KR19980076411A - Manufacturing method of plaster for wound disinfection - Google Patents
Manufacturing method of plaster for wound disinfection Download PDFInfo
- Publication number
- KR19980076411A KR19980076411A KR1019970013113A KR19970013113A KR19980076411A KR 19980076411 A KR19980076411 A KR 19980076411A KR 1019970013113 A KR1019970013113 A KR 1019970013113A KR 19970013113 A KR19970013113 A KR 19970013113A KR 19980076411 A KR19980076411 A KR 19980076411A
- Authority
- KR
- South Korea
- Prior art keywords
- chitin
- chitosan
- oligosaccharides
- plaster
- degree
- Prior art date
Abstract
본 발명은 상처 소독용 플라스터의 제조방법에 관한 것이다.The present invention relates to a method for producing a plaster for wound disinfection.
본 발명은 키토산, 키틴, 이들의 올리고머 또는 이들의 올리고당을 적합한 용매에 0.1% 내지 3%로 용해시켜 면직물에 침적시키고 중화, 세척, 건조하여 꺼즈를 제조하고, 제조된 꺼즈를 접착 테이프에 부착하여 플라스터를 제조하는 방법이다.The present invention is prepared by dissolving chitosan, chitin, oligomers thereof, or oligosaccharides thereof in a suitable solvent in 0.1% to 3% by immersing in cotton fabric, neutralized, washed, dried to attach the prepared to the adhesive tape It is a method for producing a plaster.
이와 같은 방법으로 제조된 플라스터는 상처를 소독하여 보호하는 효과를 갖는다.Plaster produced in this way has the effect of disinfecting and protecting the wound.
Description
본 발명은 상처 소독용 플라스터의 제조방법에 관한 것이고, 더욱 상세하게는 신체에 상처가 생겼을 때 상처를 소독하여 보호하도록 꺼즈에 키토산, 키틴, 이들의 올리고머 또는 이들의 올리고당을 처리한 플라스터의 제조방법에 관한 것이다.The present invention relates to a method for producing a plaster for wound disinfection, and more particularly, a method for preparing a plaster treated with chitosan, chitin, oligomers thereof or oligosaccharides in red to disinfect and protect the wound when a wound occurs in the body. It is about.
최근에, 자연계에 광범위하게 존재하는 천연 다당이지만 오랜기간 동안 이용되지 않은 키틴, 키토산을 응집제, 이온 교환제, 효소 고정화제, 의약품, 의용재료 등에 이용하고자 하는 많은 연구가 이루어지고 있다.Recently, many studies have been conducted to use chitin and chitosan, which are natural polysaccharides widely present in nature but have not been used for a long time, for flocculants, ion exchangers, enzyme fixatives, pharmaceuticals, and medical materials.
이와 같은 연구를 통해, 키토산 및 키틴에 항균성, 항곰팡이성이 있다는 것이 밝혀졌다.These studies have shown that chitosan and chitin have antimicrobial and antifungal properties.
이에 본 발명은 항균성, 항곰팡이성을 갖는 키토산 및 키틴을 이용하여 상처를 소독하여 보호하는 플라스터의 제조방법을 제공하는 것을 목적으로 한다.Accordingly, an object of the present invention is to provide a method for preparing a plaster that protects a wound by using chitosan and chitin having antimicrobial and antifungal properties.
본 발명은 키토산, 키틴, 이들의 올리고머 또는 이들의 올리고당을 적합한 용매에 0.1% 내지 3%로 용해시켜 면직물에 침적시키고, 중화, 세척, 건조하여 꺼즈를 제조하고, 제조된 꺼즈를 접착 테이프에 부착하여 플라스터를 제조하는 방법이다.The present invention dissolves chitosan, chitin, oligomers thereof or oligosaccharides thereof in a suitable solvent at 0.1% to 3%, soaks in cotton fabric, neutralizes, washes and dries to prepare reds, and attaches the prepared reds to the adhesive tape. To produce a plaster.
이하, 본 발명을 더욱 상세히 설명하면 다음과 같다.Hereinafter, the present invention will be described in more detail.
본 발명은 키토산, 키틴, 이들의 올리고머 또는 이들의 올리고당을 적합한 용매에 0.1 내지 3%로 용해시켜 면직물에 침적시키고 중화, 세척, 건조하여 꺼즈를 제조하고, 제조된 꺼즈를 접착 테이프에 부착하여 플라스터를 제조하는 방법으로서, 이와 같이 제조된 플라스터는 상처를 소독하는 효과를 갖는다.The present invention is prepared by dissolving chitosan, chitin, oligomers thereof, or oligosaccharides thereof in a suitable solvent in 0.1 to 3%, immersed in cotton fabric, neutralized, washed, and dried to prepare redds, and attaching the prepared todose to an adhesive tape As a method for producing the plaster thus prepared has the effect of disinfecting the wound.
본 발명에서 사용된 키토산 및 키틴은 오징어뼈나 게 껍질에서 추출하거나 시판품을 그대로 사용한다.Chitosan and chitin used in the present invention is extracted from the squid bone or crab shell or use a commercially available product.
상기의 키토산은 중합도가 300 내지 23000인 것을 사용하고, 키틴은 300 내지 30000의 중합도를 갖는 것을 사용하는 것이 바람직하다.It is preferable to use the thing whose polymerization degree is 300-23000 as said chitosan, and the thing which has a polymerization degree of 300-30000 as chitin.
또한, 키토산 및 키틴의 올리고머 또는 이들의 올리고당을 제조하는 방법은 하기와 같다.In addition, a method for producing oligomers of chitosan and chitin or oligosaccharides thereof is as follows.
키토산 올리고머는 키틴을 농염산으로 가수분해하여 탈아세틸화도가 50 내지 96%이고, 중합도가 20 내지 25000 정도인 것으로 제조한다.The chitosan oligomer is prepared by hydrolyzing chitin with concentrated hydrochloric acid to have a degree of deacetylation of 50 to 96% and a degree of polymerization of about 20 to 25000.
키틴 올리고머는 키틴을 농염산으로 가수분해하여 중합도 20 내지 300 정도로 제조된 키토산을 무수아세트산으로 N-아세틸화하여 제조한다.The chitin oligomer is prepared by hydrolyzing chitin with concentrated hydrochloric acid to N-acetylate chitosan prepared with a degree of polymerization of 20 to 300 with acetic anhydride.
키토산 올리고당 또는 키틴 올리고당은 키토산 또는 키틴을 5N 내지 9N의 농염산으로 50 내지 100℃에서 4 내지 24시간 가수분해하여 중합도가 1 내지 20 정도를 제조한다.The chitosan oligosaccharides or chitin oligosaccharides are hydrolyzed chitosan or chitin with concentrated hydrochloric acid of 5N to 9N at 50 to 100 ° C. for 4 to 24 hours to prepare a degree of polymerization of about 1 to 20.
상기의 키틴, 키토산, 이들의 올리고머 및 이들의 올리고당의 중합도는 세포 접촉 투과성에 영향을 미치기 때문에 상기 각각의 범위를 벗어나는 경우에는 효과가 감소된다.Since the degree of polymerization of chitin, chitosan, oligomers thereof, and oligosaccharides thereof affects cell contact permeability, the effect is reduced when outside the respective ranges.
또한, 상기에서 키토산, 키틴, 이들의 올리고머 또는 이들의 올리고당을 적합한 용매에 0.1 내지 3%로 용해시키는 경우 적합한 용매로는 다음과 같은 것이 사용된다.In addition, in the case of dissolving chitosan, chitin, oligomers thereof or oligosaccharides thereof in 0.1 to 3% in a suitable solvent, the following are used as a suitable solvent.
키틴 또는 키틴의 올리고머의 경우에는 용매로서 트리클로로초산 또는 디클로로초산과 클로로화 탄화수소 혼합용액을 사용하여 키틴 또는 키틴의 올리고머를 0.1 내지 3%로 용해시키고, 이 용액에 면직물을 담그어 처리한 후 이 처리된 면직물을 약알칼리성 용액으로 중화하고, 다시 증류수로 세척하여 풍건함으로써 꺼즈를 제조한다.In the case of chitin or oligomer of chitin, the chitin or chitin oligomer is dissolved in 0.1 to 3% using a mixed solution of trichloroacetic acid or dichloroacetic acid and chlorolated hydrocarbon as a solvent, and the cotton fabric is immersed in this solution, followed by treatment. The cotton fabric is neutralized with a weakly alkaline solution, washed again with distilled water, and air dried to prepare redds.
키토산 또는 키토산 올리고머의 경우에는 용매로서 1 내지 5% 초산 용액을 사용하여 키토산 또는 키토산 올리고머를 0.1 내지 3%로 용해시키고, 이 용액에 면직물을 담그어 처리한 후 이 처리된 면직물을 약알카리성 용액으로 중화하고 증류수로 세척하여 풍건함으로써 꺼즈를 제조한다.In the case of chitosan or chitosan oligomers, the chitosan or chitosan oligomer is dissolved in 0.1 to 3% using a 1 to 5% acetic acid solution as a solvent, and the cotton fabric is immersed in this solution and neutralized with a weakly alkaline solution. To prepare the reds by washing with distilled water and air-dried.
키틴 올리고당 또는 키토산 올리고당은 용매로서 증류수를 사용하여 키틴 올리고당 또는 키토산 올리고당을 0.1 내지 3%로 용해시키고, 면직물을 담그어 처리한 후 풍건함으로써 꺼즈를 제조한다.Chitin oligosaccharides or chitosan oligosaccharides are prepared by dissolving chitin oligosaccharides or chitosan oligosaccharides in an amount of 0.1 to 3% using distilled water as a solvent, dipping and then treating cotton fabrics.
이와 같이 제조된 꺼즈를 1㎝×1.5㎝로 잘라서 접착 테이프에 부착하여 플라스터를 제조한다.The prepared sod was cut into 1 cm x 1.5 cm and attached to an adhesive tape to prepare a plaster.
[실시예 1]Example 1
키틴 분말 2g을 7N-염산 용액 200g에 현탁시키고, 질소 기류 중에서 100℃로 4시간 반응시키고, 이 용액을 3N-가성소다 용액으로 중화시켜 침전시킨 후 여과하고 증류수로 세척, 다시 아세톤으로 세척하여 건조함으로써 분말상의 키토산 올리고머를 제조하였다. 이와 같이 제조된 키토산 올리고머를 1% 초산 용액에 0.1%로 용해시키고 면직물을 침전시키고 건조한 다음 다시 1% 가성소다 용액으로 중화하고 증류수로 세척, 건조함으로써 키토산이 처리된 꺼즈를 제조하였다. 이 꺼즈를 1㎝×1.5㎝로 잘라서 접착 테이프에 부착하여 플라스터를 제조하였다.2 g of chitin powder was suspended in 200 g of 7N hydrochloric acid solution, reacted at 100 DEG C for 4 hours in a stream of nitrogen, neutralized with 3N caustic soda solution, precipitated, filtered, washed with distilled water, washed with acetone and dried. Thus, a powdery chitosan oligomer was produced. Chitosan oligomers prepared as described above were dissolved in 1% acetic acid solution at 0.1%, precipitated cotton fabric, dried, neutralized with 1% caustic soda solution, washed with distilled water, and dried to prepare chitosan-treated oeds. This toad was cut into 1 cm x 1.5 cm and attached to an adhesive tape to prepare a plaster.
[실시예 2]Example 2
키토산 분말 1g을 0.5% 아세트산 용액 100g에 분산 용해시킨 후 무수 아세트산 1g을 가하여 N-아세틸화하여 증류수로 세척하고 건조하여 키틴 올리고머를 제조하였다. 제조된 키틴 올리고머를 트리클로로 아세트산에 0.1%로 용해시킨다는 것만 제외하고 실시예 1과 동일하게 플라스터를 제조하였다.1 g of chitosan powder was dispersed and dissolved in 100 g of 0.5% acetic acid solution, 1 g of acetic anhydride was added thereto, followed by N-acetylation, washing with distilled water, and drying to prepare a chitin oligomer. The plaster was prepared in the same manner as in Example 1 except that the prepared chitin oligomer was dissolved in trichloro acetic acid at 0.1%.
[실시예 3]Example 3
키토산 올리고당 또는 키틴 올리고당을 증류수에 0.1%로 용해시켜 면직물을 처리한다는 것만 제외하고 실시예 1과 동일한 방법으로 키토산 올리고당 또는 키틴 올리고당이 처리된 플라스터를 제조하였다.Chitosan oligosaccharides or chitin oligosaccharides were prepared in the same manner as in Example 1 except that chitosan oligosaccharides or chitin oligosaccharides were dissolved in distilled water at 0.1% to treat cotton fabrics.
이와 같이 키토산, 키틴, 이들의 올리고머 또는 이들의 올리고당이 처리된 플라스터는 키토산, 키틴이 가지고 있는 항균성과 항곰팡이성으로 상처를 소독하는 효과를 갖는다.The plaster treated with chitosan, chitin, oligomers thereof or oligosaccharides thereof has the effect of disinfecting wounds with antibacterial and antifungal properties of chitosan and chitin.
Claims (7)