KR102651870B1 - Film and manufacturing method thereof - Google Patents
Film and manufacturing method thereof Download PDFInfo
- Publication number
- KR102651870B1 KR102651870B1 KR1020240033799A KR20240033799A KR102651870B1 KR 102651870 B1 KR102651870 B1 KR 102651870B1 KR 1020240033799 A KR1020240033799 A KR 1020240033799A KR 20240033799 A KR20240033799 A KR 20240033799A KR 102651870 B1 KR102651870 B1 KR 102651870B1
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- film
- additive
- manufacturing
- present
- Prior art date
Abstract
본 발명의 일 실시예에 따른 필름은 구조가 단순하며 외관이 미려한 필름 및 이의 제조방법을 제공하는 것을 목적으로 한다. 본 발명은 내부에 첨가제를 포함하여 패턴을 표현하도록 구성되는 제1층, 제1층을 보호하기 위하여 제1층의 상부에 형성되는 제2층을 포함하는 필름을 제공한다. The purpose of the film according to an embodiment of the present invention is to provide a film with a simple structure and beautiful appearance, and a method for manufacturing the same. The present invention provides a film including a first layer configured to express a pattern by including an additive therein, and a second layer formed on top of the first layer to protect the first layer.
Description
본 발명은 필름 및 이의 제조방법에 관한 것으로, 보다 상세하게는 필름을 구성하는 각 층의 구조를 개선한 필름 및 이의 제조방법에 관한 것이다. The present invention relates to a film and a method of manufacturing the same, and more specifically, to a film and a method of manufacturing the same that improve the structure of each layer constituting the film.
필름은 외관의 미려함을 위하여 범퍼, 인스트루먼트 판넬, 도어트림 판넬, 내장 트림류 등의 차량의 내외장재에 폭넓게 사용된다. Films are widely used in vehicle interior and exterior materials such as bumpers, instrument panels, door trim panels, and interior trims to enhance the exterior appearance.
특히, 필름을 이용하여 스톤 외관을 표현하기 위하여 여러가지 방법이 고안되었다. 종래에는 리얼 스톤을 필름층 내에 포함하거나, 인쇄를 통해 스톤 패턴을 구현하는 방법을 이용하였다. In particular, various methods have been devised to express the appearance of stones using films. Conventionally, methods were used to include real stones in a film layer or to implement stone patterns through printing.
이 중 리얼 스톤을 필름층 내에 포함하는 방법은 리얼 스톤에 의해 필름의 성형성이 저하되며, 비용이 많이 들었다. 또한, 스톤 패턴을 인쇄를 통해 구현하는 방법은 인쇄 공정에 의해 원가가 상승하고 인쇄에 이용하는 잉크에서 냄새가 발생하였다. Among these, the method of including real stones in the film layer reduced the formability of the film due to the real stones and was expensive. In addition, the method of implementing the stone pattern through printing increased the cost due to the printing process, and the ink used for printing produced an odor.
개시된 실시예는 구조가 단순하며 외관이 미련한 필름 및 이의 제조방법을 제공하고자 한다. The disclosed embodiments are intended to provide a film with a simple structure and a refined appearance, and a method for manufacturing the same.
상술한 기술적 과제를 달성하기 위한 기술적 수단으로서, 일 측면에 따른 필름은 내부에 첨가제를 포함하여 패턴을 구현하도록 구성되는 제1층, 상기 제1층을 보호하기 위하여 상기 제1층의 상부에 형성되는 제2층을 포함한다.As a technical means for achieving the above-described technical problem, the film according to one aspect includes an additive therein and is configured to implement a pattern, and a first layer formed on top of the first layer to protect the first layer. Includes the second floor.
또한, 상기 제1층 내의 상기 첨가제는 유색의 무기 첨가제, 유색의 유기 섬유, 유무기 첨가제로 이루어진 군으로부터 선택된 1종 이상일 수 있다. Additionally, the additive in the first layer may be one or more selected from the group consisting of colored inorganic additives, colored organic fibers, and organic and inorganic additives.
또한, 상기 첨가제의 입자의 직경은 0.1 내지 5mm일 수 있다. Additionally, the particle diameter of the additive may be 0.1 to 5 mm.
또한, 상기 유색의 무기 첨가제는 판상, 침상, 구상으로 구성될 수 있다. Additionally, the colored inorganic additive may be plate-shaped, needle-shaped, or spherical.
또한, 상기 유색의 유기섬유는 침상, 섬유상으로 구성될 수 있다. Additionally, the colored organic fibers may be composed of needles or fibrous shapes.
또한, 상기 유무기 첨가제는 목분, 코르크, 자개로 구성될 수 있다. Additionally, the organic and inorganic additives may be composed of wood flour, cork, and mother-of-pearl.
또한, 상기 제1층의 두께는 0.1 내지 5mm일 수 있다. . Additionally, the thickness of the first layer may be 0.1 to 5 mm. .
또한, 상기 제2층의 두께는 5*10-3 내지 1mm일 수 있다. Additionally, the thickness of the second layer may be 5*10 -3 to 1 mm.
또한, 상기 제1층과 상기 제2층 사이에 위치하며, 상기 제1층과 상기 제2층을 접착하는 제3층을 더 포함할 수 있다. In addition, it may further include a third layer located between the first layer and the second layer and adhering the first layer and the second layer.
다른 일 측면에 따른 필름의 제조방법은 제1층을 구성하는 조성물과 첨가제를 혼합하여 상기 제1층을 형성하고, 상기 제1층의 상면에 상기 제1층을 보호하기 위한 제2층을 코팅하는 것을 포함한다. A method of manufacturing a film according to another aspect includes forming the first layer by mixing a composition constituting the first layer and an additive, and coating a second layer to protect the first layer on the upper surface of the first layer. It includes doing.
또한, 상기 제1층의 형성은 상기 제1층을 구성하는 조성물과 첨가제를 혼합하여 압출 성형기에 투입하여 압출하여 형성할 수 있다. Additionally, the first layer can be formed by mixing the composition and additives constituting the first layer and extruding them into an extrusion molding machine.
또한, 상기 제1층의 형성은 상기 제1층을 구성하는 조성물과 첨가제를 혼합하여 상기 제1층을 구성하는 조성물을 용융 및/또는 분산시킬 수 있는 용제에 용해시켜 형성할 수 있다. Additionally, the first layer may be formed by mixing the composition constituting the first layer with an additive and dissolving the composition constituting the first layer in a solvent capable of melting and/or dispersing the first layer.
또한, 상기 제2층의 코팅은 상기 제2층을 구성하는 조성물을 스프레이 코팅하고 경화시키는 스프레이 코팅 방식에 의해 이루어질 수 있다. Additionally, the coating of the second layer may be performed by a spray coating method in which the composition constituting the second layer is spray coated and cured.
또한, 상기 제2층의 코팅은 상기 제2층을 구성하는 조성물을 롤을 이용하여 상기 제1층의 표면에 도포하여 이루어질 수 있다. Additionally, coating of the second layer may be achieved by applying the composition constituting the second layer to the surface of the first layer using a roll.
또한, 상기 제2층의 코팅은 열 및/또는 압력을 가해 상기 제1층과 접착하여 이루어지며, 상기 제1층과 상기 제2층 사이의 제3층이 접착제로 이용될 수 있다. Additionally, the coating of the second layer is achieved by adhering it to the first layer by applying heat and/or pressure, and a third layer between the first layer and the second layer may be used as an adhesive.
전술한 과제 해결 수단에 의하면, 외관이 미려하면서 구조가 단순하여 성형성이 뛰어난 필름을 생산할 수 있다. According to the above-described means of solving the problem, it is possible to produce a film that has an attractive appearance and a simple structure with excellent formability.
도 1은 본 발명의 일 실시예에 따른 필름의 단면을 도시한 도면이다.
도 2는 본 발명의 일 실시예에 따른 필름의 제조방법을 도시한 도면이다.
도 3은 본 발명의 다른 일 실시예에 따른 필름의 단면을 도시한 도면이다.
도 4는 본 발명의 다른 일 실시예에 따른 필름의 제조방법을 도시한 도면이다.
도 5는 본 발명의 일 실시예에 의해 제조된 필름의 표면 사진이다.
도 6은 본 발명의 다른 일 실시예에 의해 제조된 필름의 표면 사진이다. 1 is a diagram showing a cross section of a film according to an embodiment of the present invention.
Figure 2 is a diagram showing a method of manufacturing a film according to an embodiment of the present invention.
Figure 3 is a diagram showing a cross section of a film according to another embodiment of the present invention.
Figure 4 is a diagram showing a method of manufacturing a film according to another embodiment of the present invention.
Figure 5 is a photograph of the surface of a film manufactured according to an example of the present invention.
Figure 6 is a photograph of the surface of a film manufactured according to another example of the present invention.
명세서 전체에 걸쳐 동일 참조 부호는 동일 구성요소를 지칭한다. 본 명세서가 실시예들의 모든 요소들을 설명하는 것은 아니며, 본 발명이 속하는 기술분야에서 일반적인 내용 또는 실시예들 간에 중복되는 내용은 생략한다. Like reference numerals refer to like elements throughout the specification. This specification does not describe all elements of the embodiments, and general content or overlapping content between the embodiments in the technical field to which the present invention pertains is omitted.
명세서 전체에서, 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 포함할 수 있는 것을 의미한다. Throughout the specification, when a part "includes" a certain element, this means that it may further include other elements rather than excluding other elements, unless specifically stated to the contrary.
단수의 표현은 문맥상 명백하게 예외가 있지 않는 한, 복수의 표현들을 포함한다. Singular expressions include plural expressions unless the context clearly makes an exception.
본 명세서에서 사용한 "제1", "제2" 등과 같이 서수를 포함하는 용어는 다양한 구성요소들을 설명하는데 사용할 수 있지만, 상기 구성요소들은 상기 용어들에 의해 한정되지는 않으며, 상기 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다. 예를 들어, 본 발명의 권리범위를 벗어나지 않으면서 제1구성요소는 제2구성요소로 명명될 수 있고, 유사하게 제2구성요소도 제1구성요소로 명명될 수 있다. Terms containing ordinal numbers, such as "first", "second", etc., used in this specification can be used to describe various components, but the components are not limited by the terms, and the terms are one It is used only for the purpose of distinguishing one component from another. For example, a first component may be named a second component without departing from the scope of the present invention, and similarly, the second component may also be named a first component.
하기의 설명에서 사용된 용어 "전방", "후방", "상부" 및 "하부" 등은 도면을 기준으로 정의한 것이며, 이 용어에 의하여 각 구성요소의 형상 및 위치가 제한되는 것은 아니다. The terms “front,” “rear,” “upper,” and “lower” used in the following description are defined based on the drawings, and the shape and location of each component are not limited by these terms.
하기의 설명에서 차량은 인간, 물건 또는 동물 등과 같은 피운송체를 출발지에서 목적지로 이동시키는 다양한 장치를 의미한다. 차량은 도로 또는 선로를 주행하는 차량, 바다나 강 위로 이동하는 선박 및 공기의 작용을 이용하여 창공을 비행하는 비행기 등을 포함할 수 있다. In the following description, a vehicle refers to various devices that move a transported object, such as a human, object, or animal, from a starting point to a destination. Vehicles may include vehicles running on roads or tracks, ships moving on the sea or rivers, and airplanes flying in the sky using the action of air.
또한, 도로 또는 선로를 주행하는 차량은 적어도 하나의 차륜의 회전에 따라 소정의 방향으로 이동할 수 있으며, 예를 들어 삼륜 또는 사륜 자동차, 건설기계, 이륜 자동차, 원동기 장치, 자전거 및 선로를 주행하는 열차를 포함할 수 있다. In addition, vehicles running on roads or tracks can move in a predetermined direction according to the rotation of at least one wheel, for example, three- or four-wheeled vehicles, construction machinery, two-wheeled vehicles, prime movers, bicycles, and trains running on tracks. may include.
이하에서는 본 발명에 따른 실시예를 첨부된 도면을 참조하여 상세히 설명한다. Hereinafter, embodiments according to the present invention will be described in detail with reference to the attached drawings.
도 1은 본 발명의 일 실시예에 따른 필름의 단면을 도시한 도면이다. 1 is a diagram showing a cross section of a film according to an embodiment of the present invention.
도 1에 도시된 바와 같이, 개시된 발명에 따른 필름은 내부에 첨가제를 포함하여 패턴을 구현하도록 구성되는 제1층(20)과, 제1층(20)을 보호하기 위하여 제1층(20)의 상부에 형성되는 제2층(10)을 포함한다. 제1층(20)은 외관을 구현하기 위한 층이다. 개시된 발명의 일 실시예에는 제1층(20)을 통해 외관에 스톤 패턴을 구현하고자 한다. 제2층(10)은 제1층(20)을 보호하기 위한 층이다. As shown in FIG. 1, the film according to the disclosed invention includes a first layer 20 configured to implement a pattern by including an additive therein, and a first layer 20 to protect the first layer 20. It includes a second layer 10 formed on the top of. The first layer 20 is a layer for implementing the exterior. In one embodiment of the disclosed invention, a stone pattern is intended to be implemented on the exterior through the first layer 20. The second layer 10 is a layer to protect the first layer 20.
제1층(20)으로는 ABS 수지(Acrylonitrile-Butadiene-Styrene resin), 폴리프로필렌 수지(PP; Polypropylene resin), 폴리카보네이트 수지(PC; Polycarbonate resin), PMMA 수지(Poly methyl methacrylate resin), PET 수지(Polyethylene terephthalate resin), PBT(Polybutylene terephthalate resin)로 이루어진 군으로부터 선택된 1종이상일 수 있다. The first layer 20 includes Acrylonitrile-Butadiene-Styrene resin (ABS), Polypropylene resin (PP), Polycarbonate resin (PC), Poly methyl methacrylate resin (PMMA), and PET resin. It may be one or more types selected from the group consisting of (Polyethylene terephthalate resin) and PBT (Polybutylene terephthalate resin).
제1층(20) 내의 첨가제(30)는 유색의 무기 첨가제(30b), 유색의 유기 섬유(30a), 유무기 첨가제(30c)로 이루어진 군으로부터 선택된 1종이상일 수 있다. 유색의 무기 첨가제(30c)는 판상, 침상, 구상으로 구성될 수 있다. 유색의 유기섬유(30a)는 침상, 섬유상으로 구성될 수 있다. 유무기 첨가제(30c)는 목분, 코르크, 자개로 구성될 수 있다. The additive 30 in the first layer 20 may be one or more types selected from the group consisting of colored inorganic additives 30b, colored organic fibers 30a, and organic and inorganic additives 30c. The colored inorganic additive 30c may be plate-shaped, needle-shaped, or spherical. The colored organic fibers 30a may be composed of needle-like or fibrous shapes. The organic and inorganic additive 30c may be composed of wood flour, cork, and mother-of-pearl.
개시된 발명에 따르면, 제1층(20)의 두께는 0.1 내지 5mm일 수 있다. 제1층(20)이 0.1mm 이하인 경우에는 필름 성형 시 제1층(20) 표면에 주름이 발생하거나 제1층(20) 내부의 첨가제(30)의 입자에 의해 표면 품질이 저하될 수 있다. 이와 반대로 제1층(20)의 두께가 5mmm를 초과하는 경우에는 성형성이 떨어지면 작업성이 확보되기 어렵다. 이에 개시된 발명의 일 실시예에 따르면 제1층(20)의 두께를 0.1 내지 5mm로 하는 것이 바람직하다. According to the disclosed invention, the thickness of the first layer 20 may be 0.1 to 5 mm. If the first layer 20 is 0.1 mm or less, wrinkles may occur on the surface of the first layer 20 during film molding, or the surface quality may deteriorate due to particles of the additive 30 inside the first layer 20. . On the contrary, when the thickness of the first layer 20 exceeds 5 mmm, it is difficult to secure workability as formability is reduced. According to one embodiment of the invention disclosed herein, it is preferable that the thickness of the first layer 20 is 0.1 to 5 mm.
개시된 발명에 따르면, 제1층(20) 내의 첨가제(30)의 입자의 직경은 0.1 내지 5mm 일 수 있다. 첨가제(30)의 입자의 직경이 0.1mm 이하인 경우에는 외관에 스톤 패턴이 표현되지 않을 수 있다. 이와 반대로 입자의 직경이 5mm를 초과하는 경우에는 성형성이 떨어지며, 입자가 분산되지 않을 수 있다. 이에 개시된 발명의 일 실시예에 따르면 첨가제(30)의 입자의 직경을 0.1 내지 5mm로 하는 것이 바람직하다. According to the disclosed invention, the diameter of the particles of the additive 30 in the first layer 20 may be 0.1 to 5 mm. If the particle diameter of the additive 30 is 0.1 mm or less, the stone pattern may not be expressed on the exterior. On the contrary, if the diameter of the particles exceeds 5 mm, the moldability is poor and the particles may not be dispersed. According to one embodiment of the invention disclosed herein, it is preferable that the particle diameter of the additive 30 is 0.1 to 5 mm.
개시된 발명에 따르면, 제2층(10)의 두께는 5*10-3 내지 1mm일 수 있다. 5*10-3 mm 이하인 경우에는 제2층(10)의 보호 기능이 저하된다. 이와 반대로 제2층(10)의 두께가 1mm를 초과하는 경우에는 성형성이 확보되지 않는다는 문제가 있다. 이에 개시된 발명의 일 실시예에 따르면 제2층(10)의 두께는 5*10-3 내지 1mm일 수 있다. According to the disclosed invention, the thickness of the second layer 10 may be 5*10 -3 to 1 mm. If it is 5*10 -3 mm or less, the protective function of the second layer 10 is reduced. On the contrary, if the thickness of the second layer 10 exceeds 1 mm, there is a problem that formability is not secured. According to one embodiment of the disclosed invention, the thickness of the second layer 10 may be 5*10 -3 to 1 mm.
이와 같이, 개시된 발명에 의한 필름은 제1층(20) 내부에 포함된 첨가제(30)에 의해 스톤 패턴이 구현될 수 있다. 종래에는 필름층 이외에 별도의 리얼 스톤층을 포함하거나 인쇄층을 포함하였던 것을 하나의 층으로 구현하여 외관의 미려함과 동시에 성형성을 확보할 수 있다. 또한, 하나의 층으로 구현되기 때문에 제조과정에서 발생하는 원가를 절감할 수 있다. In this way, the film according to the disclosed invention can have a stone pattern implemented by the additive 30 included in the first layer 20. In the past, in addition to the film layer, a separate real stone layer or a printing layer was implemented as a single layer to ensure a beautiful appearance and at the same time formability. Additionally, because it is implemented as a single layer, costs incurred during the manufacturing process can be reduced.
도 2는 본 발명의 일 실시예에 따른 필름의 제조방법을 도시한 도면이다. Figure 2 is a diagram showing a method of manufacturing a film according to an embodiment of the present invention.
개시된 발명에 의한 필름은 제1층(20)을 구성하는 조성물과 첨가제(30)를 혼합하여 제1층(20)을 형성하고(100, 110), 제1층(20)의 상면에 제1층(20)을 보호하기 위한 제2층(10)을 코팅하여(200) 제조된다. The film according to the disclosed invention forms the first layer 20 by mixing the composition constituting the first layer 20 and the additive 30 (100, 110), and a first layer 20 is formed on the upper surface of the first layer 20. It is manufactured by coating (200) a second layer (10) to protect the layer (20).
제1층(20)은 압출 성형 방식(100)이나 솔루션 캐스팅 방식(110)으로 형성될 수 있다.The first layer 20 may be formed using an extrusion molding method 100 or a solution casting method 110.
압출 성형 방식(100)은 제1층(20)을 구성하는 조성물과 첨가제(30)를 혼합하여 압출 성형기에 투입하여 압출하여 제1층(20)을 형성할 수 있다. 압출 성형 방식은 압출 성형기에 투입한 이후에 용융 및 혼합 과정을 거칠 수 있다. 또한, 압출 성형기 말단에 T 다이를 부착하여 용융되는 소재를 통과하여 필름을 제조할 수 있다. In the extrusion molding method 100, the composition constituting the first layer 20 and the additive 30 are mixed and put into an extrusion molding machine and extruded to form the first layer 20. In the extrusion molding method, the material may undergo a melting and mixing process after being placed in an extrusion molding machine. Additionally, a T die can be attached to the end of the extrusion molding machine to produce a film by passing the molten material.
솔루션 캐스팅 방식(110)은 제1층(20)을 구성하는 조성물과 첨가제(30)를 혼합하여 제1층(20)을 구성하는 조성물을 용융 및/또는 분산시킬 수 있는 용제에 용해시켜 제1층(20)을 형성할 수 있다. 보다 구체적으로 제1층(20)을 구성하는 조성물과 첨가제(30)를 혼합하여 용제에 용해시켜 성형판 위에서 용제를 휘발시켜 필름을 제조한다. 이 때 성형판은 필름 형상을 유지할 수 있는 판재가 사용될 수 있다. 일 예로 강철 벨트가 사용될 수 있다. The solution casting method 110 mixes the composition constituting the first layer 20 with the additive 30 and dissolves the composition constituting the first layer 20 in a solvent capable of melting and/or dispersing the first layer 20. A layer 20 can be formed. More specifically, the composition constituting the first layer 20 and the additive 30 are mixed, dissolved in a solvent, and the solvent is volatilized on a molding plate to produce a film. At this time, a plate material capable of maintaining the film shape may be used as the molded plate. As an example, a steel belt may be used.
제1층(20)을 제조한 후, 제1층(20)의 상면에 제2층(10)을 코팅한다(200). After manufacturing the first layer 20, the second layer 10 is coated on the upper surface of the first layer 20 (200).
제2층(10)의 코팅(200)은 제2층(10)을 구성하는 조성물을 스프레이 코팅하고 경화시키는 스프레이 코팅 방식으로 진행될 수 있다. 스프레이 코팅은 제2층(10)을 구성하는 수지를 용제에 분산하여, 스프레이 도장을 진행한다. 이후, 경화시켜 투명 또는 불투명한 제2층(10)을 형성할 수 있다. 이 때 경화는 자외선, 전자빔, 열건조 등의 방법을 이용하여 진행될 수 있다. Coating 200 of the second layer 10 may be performed by a spray coating method in which the composition constituting the second layer 10 is spray-coated and cured. Spray coating is performed by dispersing the resin constituting the second layer 10 in a solvent and spray painting. Afterwards, it can be cured to form a transparent or opaque second layer 10. At this time, curing may be carried out using methods such as ultraviolet rays, electron beams, and heat drying.
제2층(10)의 코팅(200)은 제2층(10)을 구성하는 롤을 이용하여 제1층(20)의 표면에 도포하여 이루어질 수 있다. 보다 구체적으로, 제2층(10)을 구성하는 수지를 용제에 분산하여, 롤을 이용하여 일정한 두께로 제1층(20)의 표면에 도포할 수 있다. The coating 200 of the second layer 10 may be applied to the surface of the first layer 20 using a roll constituting the second layer 10. More specifically, the resin constituting the second layer 10 can be dispersed in a solvent and applied to the surface of the first layer 20 at a constant thickness using a roll.
제2층(10)의 코팅은 열 및/또는 압력을 가해 제1층(20)과 접착하여 이루어질 수 있다. 보다 구체적으로, 제조된 제2층(10)을 열 및/또는 압력을 가해 제1층(20)과 접착한다. 이 때, 제1층(20)과 제2층(10)의 재질이 상이한 경우 별도의 접착층이 추가될 수 있다. 이에 대해서는 후술한다. Coating of the second layer 10 may be achieved by adhering it to the first layer 20 by applying heat and/or pressure. More specifically, the manufactured second layer 10 is adhered to the first layer 20 by applying heat and/or pressure. At this time, if the first layer 20 and the second layer 10 are made of different materials, a separate adhesive layer may be added. This will be described later.
압출 성형 방식이나 솔루션 캐스팅 방식으로 제1층(20)을 제조한 후, 제2층(10)의 두께를 조절하거나 제조공정에 차이를 두어 거친 스톤 패턴을 구현할 수도 있고, 매끄러운 스톤 패턴을 구현할 수도 있다. 이때 제2층(10)의 제조 공정의 차이로는 평탄화 작업을 거치느냐의 유무가 있을 수 있다. After manufacturing the first layer 20 by extrusion molding or solution casting, a rough stone pattern or a smooth stone pattern can be realized by adjusting the thickness of the second layer 10 or varying the manufacturing process. there is. At this time, differences in the manufacturing process of the second layer 10 may include whether or not a planarization process is performed.
도 3은 본 발명의 다른 일 실시예에 따른 필름의 단면을 도시한 도면이다. Figure 3 is a diagram showing a cross section of a film according to another embodiment of the present invention.
도 3에서, " ' "가 붙은 도면부호의 경우 도 1에 도시된 실시예와 동일한 구성요소를 의미한다. In FIG. 3, reference numerals with " ' " indicate the same components as the embodiment shown in FIG. 1.
도 3에 도시된 실시예에 의하면 제1층(20')과 제2층(10') 사이에 제3층(40)이 마련될 수 있다. 제3층(40)은 제1층(20')과 제2층(10')을 접착하기 위한 접착층일 수 있다. 특히, 제1층(20')과 제2층(10')의 소재가 상이한 경우, 제3층(40)은 제1층(20')과 제2층(10')을 접착하기 위하여 사용될 수 있다. According to the embodiment shown in FIG. 3, the third layer 40 may be provided between the first layer 20' and the second layer 10'. The third layer 40 may be an adhesive layer for adhering the first layer 20' and the second layer 10'. In particular, when the first layer 20' and the second layer 10' are made of different materials, the third layer 40 is used to bond the first layer 20' and the second layer 10'. You can.
도 4는 본 발명의 다른 일 실시예에 따른 필름의 제조방법을 도시한 도면이다. Figure 4 is a diagram showing a method of manufacturing a film according to another embodiment of the present invention.
도 4에 도시된 바와 같이, 개시된 발명에 의한 필름은 제1층(20')을 형성하고(100), 제1층(20')의 상면에 제3층(40)을 형성하고(300), 제3층(40)의 상면에 제2층(10')을 코팅하여(200) 제조된다. 제1층(20')의 형성은 전술한 바와 같이, 압출 성형 방식(100)이나 솔루션 캐스팅 방식(110)을 이용하여 형성할 수 있다. As shown in FIG. 4, the film according to the disclosed invention forms a first layer 20' (100) and a third layer 40 is formed on the upper surface of the first layer 20' (300). , It is manufactured by coating the second layer 10' on the upper surface of the third layer 40 (200). As described above, the first layer 20' can be formed using the extrusion molding method 100 or the solution casting method 110.
도 5는 본 발명의 일 실시예에 의해 제조된 필름의 표면 사진이며, 도 6은 본 발명의 다른 일 실시예에 의해 제조된 필름의 표면 사진이다. Figure 5 is a photograph of the surface of a film manufactured according to an example of the present invention, and Figure 6 is a photograph of the surface of a film manufactured according to another example of the present invention.
도 5의 경우 거친 스톤 패턴이 구현된 것을 확인할 수 있고, 도 6의 경우 매끄러운 스톤 패턴이 구현된 것을 확인할 수 있다. 이와 같이 제2층의 두께 조절 또는 제조공정 차이로 각각의 필름에 대해 상이한 질감을 표현하는 것이 가능하다. In the case of Figure 5, it can be seen that a rough stone pattern has been implemented, and in the case of Figure 6, it can be confirmed that a smooth stone pattern has been implemented. In this way, it is possible to express different textures for each film by adjusting the thickness of the second layer or differences in the manufacturing process.
이상에서와 같이 첨부된 도면과 표를 참조하여 개시된 실시예들을 설명하였다. 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고도, 개시된 실시예들과 다른 형태로 본 발명이 실시될 수 있음을 이해할 것이다. 개시된 실시예들은 예시적인 것이며, 한정적으로 해석되어서는 안 된다. As described above, the disclosed embodiments have been described with reference to the attached drawings and tables. A person skilled in the art to which the present invention pertains will understand that the present invention can be practiced in forms different from the disclosed embodiments without changing the technical idea or essential features of the present invention. The disclosed embodiments are illustrative and should not be construed as limiting.
10, 10': 제2층 20, 20': 제1층
30, 30': 첨가제 40: 제3층10, 10': 2nd floor 20, 20': 1st floor
30, 30': Additive 40: Third layer
Claims (5)
상기 제1층을 보호하기 위하여 상기 제1층의 상부에 형성되는 제2층;
을 포함하고,
상기 제1층 내의 상기 첨가제는 유색의 유기 섬유 및 유무기 첨가제 중 적어도 하나이며,
상기 유색의 유기섬유는 침상, 섬유상으로 구성되고, 상기 유무기 첨가제는 목분, 코르크, 자개로 구성되고,
상기 첨가제에 의해 스톤 패턴이 구현되는, 필름.A first layer configured to implement a pattern by including an additive therein;
a second layer formed on top of the first layer to protect the first layer;
Including,
The additive in the first layer is at least one of colored organic fibers and an organic-inorganic additive,
The colored organic fibers are composed of needles and fibers, and the organic and inorganic additives are composed of wood flour, cork, and mother-of-pearl,
A film in which a stone pattern is implemented by the additive.
상기 첨가제의 입자의 직경은 0.1 내지 5mm인 필름. According to paragraph 1,
A film wherein the particle diameter of the additive is 0.1 to 5 mm.
상기 제1층의 두께는 0.1 내지 5mm인 필름. According to paragraph 1,
A film wherein the first layer has a thickness of 0.1 to 5 mm.
상기 제2층의 두께는 5*10-3 내지 1mm인 필름. According to paragraph 1,
A film wherein the second layer has a thickness of 5*10 -3 to 1 mm.
상기 제1층과 상기 제2층 사이에 위치하며, 상기 제1층과 상기 제2층을 접착하는 제3층을 더 포함하는 필름. According to paragraph 1,
The film further includes a third layer located between the first layer and the second layer and adhering the first layer and the second layer.