KR102641764B1 - Diamine compound, polyimide precursor and polyimide film prepared by using same - Google Patents
Diamine compound, polyimide precursor and polyimide film prepared by using same Download PDFInfo
- Publication number
- KR102641764B1 KR102641764B1 KR1020190013487A KR20190013487A KR102641764B1 KR 102641764 B1 KR102641764 B1 KR 102641764B1 KR 1020190013487 A KR1020190013487 A KR 1020190013487A KR 20190013487 A KR20190013487 A KR 20190013487A KR 102641764 B1 KR102641764 B1 KR 102641764B1
- Authority
- KR
- South Korea
- Prior art keywords
- diamine
- formula
- polyimide
- group
- scheme
- Prior art date
Abstract
본 발명은 벤젠 고리기 3개가 연결된 구조인 p-Terphenyl구조의 양쪽에 관능기에 의해 연결된 벤젠 고리를 포함하며, 상기 벤젠 고리들이 다양한 치환기로 치환된 구조를 갖는 신규 디아민을 개시한다. 또한, 본 발명은 이러한 신규 디아민을 중합성분으로 포함함으로써, 향상된 물성을 갖는 폴리이미드 필름을 제공할 수 있다.The present invention discloses a new diamine having a structure in which three benzene ring groups are connected to each other, a p-terphenyl structure, and a benzene ring connected to both sides by functional groups, and the benzene rings are substituted with various substituents. Additionally, the present invention can provide a polyimide film with improved physical properties by including this novel diamine as a polymerization component.
Description
본 발명은 신규 디아민 화합물, 이를 이용한 폴리이미드 전구체 및 폴리이미드 필름 에 관한 것이다.The present invention relates to a new diamine compound, a polyimide precursor using the same, and a polyimide film.
최근 디스플레이 분야에서 제품의 경량화 및 소형화가 중요시 되고 있으며, 현재 사용되고 있는 유리 기판의 경우 무겁고 잘 깨지며 연속공정이 어렵다는 한계가 있기 때문에 유리 기판을 대체하여 가볍고 유연하며 연속공정이 가능한 장점을 갖는 플라스틱 기판을 핸드폰, 노트북, PDA 등에 적용하기 위한 연구가 활발히 진행되고 있다.Recently, weight reduction and miniaturization of products have become important in the display field, and the glass substrates currently used have limitations in that they are heavy, brittle, and difficult to carry out continuous processing. Instead, glass substrates are replaced with plastic substrates that are light, flexible, and capable of continuous processing. Research is being actively conducted to apply this to mobile phones, laptops, PDAs, etc.
특히, 폴리이미드(PI) 수지는 합성이 용이하고 박막형 필름을 만들 수 있으며 경화를 위한 가교기가 필요 없는 장점을 가지고 있어, 최근에 전자 제품의 경량 및 정밀화 현상으로 LCD, PDP 등 반도체 재료에 집적화 소재로 많이 적용되고 있으며, PI를 가볍고 유연한 성질을 지니는 플렉시블 디스플레이 기판(flexible plastic display board)에 사용하려는 많은 연구가 진행되고 있다.In particular, polyimide (PI) resin has the advantage of being easy to synthesize, capable of producing thin films, and not requiring a cross-linker for curing. Recently, with the phenomenon of lightness and precision in electronic products, it has been integrated into semiconductor materials such as LCDs and PDPs. It is widely applied, and much research is being conducted to use PI in flexible plastic display boards that are light and flexible.
상기 폴리이미드 수지를 필름화하여 제조한 것이 폴리이미드(PI) 필름이며, 일반적으로 폴리이미드 필름은 방향족 다이안하이드라이드와 방향족 디아민 또는 방향족 디이소시아네이트를 용액 중합하여 폴리아믹산 유도체 용액을 제조한 후, 이를 실리콘 웨이퍼나 유리 등에 코팅하고 열처리에 의해 경화시키는 방법으로 제조된다. A polyimide (PI) film is manufactured by turning the polyimide resin into a film. In general, the polyimide film is made by solution polymerizing aromatic dianhydride and aromatic diamine or aromatic diisocyanate to prepare a polyamic acid derivative solution, and then producing a polyamic acid derivative solution. It is manufactured by coating a silicon wafer or glass and hardening it through heat treatment.
고온 공정을 수반하는 플렉서블 디바이스는 고온에서의 내열성이 요구되는데, 특히 LTPS(low temperature polysilicon) 공정을 사용하는 OLED(organic light emitting diode) 디바이스의 경우 공정온도가 500℃에 근접하기도 한다. 그러나 이러한 온도에서는 내열성이 우수한 폴리이미드라 하더라도 가수분해에 의한 열분해가 일어나기 쉽다. 따라서, 플렉시블 디바이스 제조를 위해서는 고온공정에서도 가수분해에 의한 열분해가 일어나지 않는 우수한 내화학성 및 저장안정성을 나타낼 수 있는 폴리이미드 필름의 개발이 필요하다.Flexible devices involving high-temperature processes require heat resistance at high temperatures. In particular, in the case of OLED (organic light emitting diode) devices using the LTPS (low temperature polysilicon) process, the process temperature can approach 500°C. However, at these temperatures, even polyimide with excellent heat resistance is prone to thermal decomposition due to hydrolysis. Therefore, in order to manufacture flexible devices, it is necessary to develop a polyimide film that can exhibit excellent chemical resistance and storage stability without thermal decomposition due to hydrolysis even in high temperature processes.
또한, 방향족 폴리이미드는 자외선 - 가시광선 영역에서 강한 흡광도를 갖는 방향족 폴리이미드는 옅은 황색에서 진한 갈색의 강한 착색이 나타나는데 이는 투명성 및 무색 특성이 기본 요구 사항인 광전자 영역(optoelectronics area)에서의 광범위한 적용을 제한한다. 방향족 폴리이미드 수지에서 착색이 나타나는 이유는 고분자 주쇄에서 교대 전자 도너(dianhydride)와 전자 억셉터(diamine) 사이 및 내부 분자 간 전하 전달 복합체(CT-complexes)를 형성하기 때문이다.In addition, aromatic polyimide has strong absorbance in the ultraviolet-visible range and shows strong coloring from light yellow to dark brown, which makes it widely applicable in the optoelectronics area where transparency and colorless properties are basic requirements. limit. The reason coloring appears in aromatic polyimide resins is because they form intermolecular charge transfer complexes (CT-complexes) between alternating electron donors (dianhydride) and electron acceptors (diamine) in the polymer main chain.
이러한 문제를 해결하기 위해, 높은 유리전이온도(Tg)를 가지며 광학적으로 투명한 PI 필름의 개발을 위해, 기능기 도입, 부피가 큰 부착 펜던트 기, 플루오르화된 기능기 등을 고분자 주쇄로의 도입하거나, 유연한 단위 (-S-, -O-, -CH2- 등)의 도입하는 방법들이 연구되어 왔다.To solve this problem, to develop an optically transparent PI film with a high glass transition temperature (Tg), the introduction of functional groups, bulky attachment pendant groups, fluorinated functional groups, etc. into the polymer main chain or , methods for introducing flexible units (-S-, -O-, -CH 2 -, etc.) have been studied.
본 발명이 해결하고자 하는 과제는 물성이 향상된 폴리이미드를 제조할 수 있는 신규 디아민을 제공하는 것이다. The problem to be solved by the present invention is to provide a new diamine capable of producing polyimide with improved physical properties.
본 발명이 해결하고자 하는 다른 과제는 물성이 개선된 폴리이미드 필름을 제조하기 위한 폴리이미드 전구체를 제공하는 것이다.Another problem to be solved by the present invention is to provide a polyimide precursor for producing a polyimide film with improved physical properties.
본 발명이 해결하고자 하는 다른 과제는 상기 폴리이미드 전구체를 이용하는 폴리이미드 필름을 제공하는 것이다.Another problem to be solved by the present invention is to provide a polyimide film using the polyimide precursor.
또한, 본 발명은, 상기 폴리이미드 필름을 포함하는 플렉서블 디바이스 및 그 제조공정을 제공하는 것이다.Additionally, the present invention provides a flexible device including the polyimide film and a manufacturing process thereof.
본 발명의 과제를 해결하기 위해, 하기 화학식 1의 구조를 갖는 디아민을 제공한다.In order to solve the problems of the present invention, a diamine having the structure of the following formula (1) is provided.
[화학식 1][Formula 1]
상기 화학식 1에 있어서,In Formula 1,
Z는 O, S, S-S, C(=O), -C(=O)O-, - OC(=O)- CH(OH), S(=O)2, CR'R", -C(=O)NH-, -NHC(=O)- 및 이들의 조합으로 이루어진 군에서 선택된 관능기 이며, 상기 R' 및 R"는 각각 독립적으로 수소원자, 탄소수 1 내지 10의 알킬기 및 탄소수 1 내지 10의 플루오로알킬기로 이루어진 군으로부터 선택되는 것이고,Z is O, S, SS, C(=O), -C(=O)O-, - OC(=O)- CH(OH), S(=O) 2 , CR'R", -C( =O)NH-, -NHC(=O)-, and a functional group selected from the group consisting of combinations thereof, wherein R' and R" are each independently a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, and a carbon atom group having 1 to 10 carbon atoms. selected from the group consisting of fluoroalkyl groups,
R1 내지 R5는 각각 독립적으로 -F, -Cl, -Br 및 -I로부터 선택되는 할로겐 원자, 하이드록실기(-OH), 티올기(-SH), 니트로기(-NO2), 시아노기(-CN), 탄소수 1 내지 10의 치환 또는 비치환의 알킬기, 탄소수 1 내지 4의 할로게노알콕시기, 탄소수 1 내지 10의 할로게노알킬기, 탄소수 6 내지 20의 아릴기이고,R 1 to R 5 are each independently a halogen atom selected from -F, -Cl, -Br and -I, a hydroxyl group (-OH), a thiol group (-SH), a nitro group (-NO 2 ), or a cyano group. A group (-CN), a substituted or unsubstituted alkyl group having 1 to 10 carbon atoms, a halogenoalkoxy group having 1 to 4 carbon atoms, a halogenoalkyl group having 1 to 10 carbon atoms, and an aryl group having 6 to 20 carbon atoms,
n1 내지 n5는 각각 독립적으로 0 내지 4의 정수이다.n1 to n5 are each independently an integer of 0 to 4.
일 실시예에 따르면, 상기 화학식 1의 디아민이 하기 화학식 1-1 내지 1-4의 화합물 중에서 선택되는 것일 수 있다.According to one embodiment, the diamine of Formula 1 may be selected from compounds of Formulas 1-1 to 1-4 below.
[화학식 1-1][Formula 1-1]
[화학식 1-2][Formula 1-2]
[화학식 1-3][Formula 1-3]
[화학식 1-4][Formula 1-4]
상기 화학식 1-1 내지 1-4에 있어서, R1 내지 R5 및 n1 내지 n5의 정의는 화학식 1과 동일하다.In Formulas 1-1 to 1-4, the definitions of R 1 to R 5 and n1 to n5 are the same as those in Formula 1.
일 실시예에 따르면, R1 내지 R5는 각각 독립적으로 -F, -Cl, -Br 및 -I로부터 선택되는 할로겐 원자, 시아노기(-CN), 탄소수 1 내지 5의 알킬기, 탄소수 1 내지 4의 할로게노알콕시기, 탄소수 1 내지 5의 할로게노알킬기 중에서 선택되는 것일 수 있다.According to one embodiment, R 1 to R 5 are each independently a halogen atom selected from -F, -Cl, -Br and -I, a cyano group (-CN), an alkyl group having 1 to 5 carbon atoms, and a carbon number of 1 to 4. It may be selected from a halogenoalkoxy group or a halogenoalkyl group having 1 to 5 carbon atoms.
일 실시예에 따르면, 상기 화학식 1-1의 디아민은 하기 반응식 1과 같은 반응으로 제조될 수 있다.According to one embodiment, the diamine of Chemical Formula 1-1 may be prepared through a reaction shown in Scheme 1 below.
[반응식 1][Scheme 1]
상기 반응식 1에 있어서, R1 내지 R5 및 n1 내지 n5의 정의는 화학식 1과 동일하다.In Scheme 1, the definitions of R 1 to R 5 and n1 to n5 are the same as those in Chemical Formula 1.
일 실시예에 따르면, 상기 화학식 1-2의 디아민은 하기 반응식 2와 같은 반응으로 제조될 수 있다.According to one embodiment, the diamine of Chemical Formula 1-2 may be prepared through a reaction shown in Scheme 2 below.
[반응식 2][Scheme 2]
상기 반응식 2에 있어서, R1 내지 R5 및 n1 내지 n5의 정의는 화학식 1과 동일하다.In Scheme 2, the definitions of R 1 to R 5 and n1 to n5 are the same as those in Formula 1.
일 실시예에 따르면, 상기 화학식 1-3의 디아민이 하기 반응식 3과 같은 반응으로 제조될 수 있다.According to one embodiment, the diamine of Chemical Formula 1-3 may be prepared through a reaction shown in Scheme 3 below.
[반응식 3][Scheme 3]
상기 반응식 3에 있어서, R1 내지 R5 및 n1 내지 n5의 정의는 화학식 1과 동일하다.In Scheme 3, the definitions of R 1 to R 5 and n1 to n5 are the same as those in Formula 1.
일 실시예에 따르면, 상기 화학식 1-4의 디아민이 하기 반응식 4와 같은 반응으로 제조될 수 있다.According to one embodiment, the diamine of Chemical Formula 1-4 may be prepared through a reaction shown in Scheme 4 below.
[반응식 4][Scheme 4]
상기 반응식 4에 있어서, R1 내지 R5 및 n1 내지 n5의 정의는 화학식 1과 동일하다.In Scheme 4, the definitions of R 1 to R 5 and n1 to n5 are the same as those in Formula 1.
본 발명의 다른 과제를 해결하기 위해,In order to solve other problems of the present invention,
1종 이상의 디아민 및 1종 이상의 산이무수물을 포함하는 중합성분을 중합시켜 얻어지는 폴리이미드 전구체로서,A polyimide precursor obtained by polymerizing a polymerizable component containing one or more diamines and one or more acid dianhydrides,
상기 디아민이 상기 신규 디아민을 포함하는 것인 폴리이미드 전구체를 제공한다.It provides a polyimide precursor wherein the diamine includes the novel diamine.
본 발명은 또한, 폴리이미드 전구체를 이용하여 제조된 폴리이미드 필름을 제공한다.The present invention also provides a polyimide film manufactured using a polyimide precursor.
일 실시예에 따르면, 상기 폴리이미드 필름은,According to one embodiment, the polyimide film is,
상기 폴리이미드 전구체를 포함하는 폴리이미드 전구체 조성물을 캐리어 기판 상에 도포하는 단계; 및Applying a polyimide precursor composition containing the polyimide precursor onto a carrier substrate; and
상기 폴리이미드 전구체 조성물을 가열 및 경화하는 단계를 포함하는 방법으로 제조되는 것일 수 있다.It may be manufactured by a method including heating and curing the polyimide precursor composition.
일 실시예에 따르면, 면방향 굴절률이 1.73 이상이고, 두께 방향 굴절률이 1.53 이상일 수 있다.According to one embodiment, the plane direction refractive index may be 1.73 or more, and the thickness direction refractive index may be 1.53 or more.
일 실시예에 따르면, 열팽창계수(CTE)가 12 ppm/℃ 이하일 수 있다.According to one embodiment, the coefficient of thermal expansion (CTE) may be 12 ppm/°C or less.
본 발명은 또한, 폴리이미드 필름을 기판으로 포함하는 플렉서블 디바이스를 제공한다.The present invention also provides a flexible device including a polyimide film as a substrate.
본 발명은 또한, The present invention also,
상기 폴리이미드 전구체를 포함하는 폴리이미드 전구체 조성물을 캐리어 기판 상에 도포하는 단계;Applying a polyimide precursor composition containing the polyimide precursor onto a carrier substrate;
상기 폴리이미드 전구체 조성물을 가열하여 폴리아믹산을 이미드화함으로써 폴리이미드 필름을 형성하는 단계; Forming a polyimide film by heating the polyimide precursor composition to imidize the polyamic acid;
상기 폴리이미드 필름 상에 소자를 형성하는 단계; 및forming a device on the polyimide film; and
상기 소자가 형성된 폴리이미드 필름을 상기 캐리어 기판으로부터 박리하는 단계를 포함하는 플렉서블 디바이스의 제조공정을 제공한다.It provides a manufacturing process for a flexible device including the step of peeling the polyimide film on which the device is formed from the carrier substrate.
일 실시예에 따르면, 상기 제조공정이 LTPS(저온 폴리실리콘) 공정, ITO 공정 또는 Oxide 공정을 포함하는 것일 수 있다.According to one embodiment, the manufacturing process may include a LTPS (low temperature polysilicon) process, an ITO process, or an oxide process.
본 발명은 벤젠 고리기 3개가 연결된 구조인 p-Terphenyl구조의 양쪽에 관능기에 의해 연결된 벤젠 고리를 포함하며, 상기 벤젠 고리들이 다양한 치환기로 치환된 구조를 갖는 신규 디아민을 개시한다. The present invention discloses a new diamine having a structure in which three benzene ring groups are connected to each other, a p-terphenyl structure, and a benzene ring connected to both sides by functional groups, and the benzene rings are substituted with various substituents.
또한, 본 발명은 이러한 신규 디아민을 중합성분으로 포함함으로써, 향상된 물성을 갖는 폴리이미드 필름을 제공할 수 있다.Additionally, the present invention can provide a polyimide film with improved physical properties by including this novel diamine as a polymerization component.
본 발명은 다양한 변환을 가할 수 있고 여러 가지 실시예를 가질 수 있는 바, 특정 실시예들을 도면에 예시하고 상세한 설명에 상세하게 설명하고자 한다. 그러나, 이는 본 발명을 특정한 실시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변환, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다. 본 발명을 설명함에 있어서 관련된 공지 기술에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우 그 상세한 설명을 생략한다.Since the present invention can be modified in various ways and can have various embodiments, specific embodiments will be illustrated in the drawings and described in detail in the detailed description. However, this is not intended to limit the present invention to specific embodiments, and should be understood to include all transformations, equivalents, and substitutes included in the spirit and technical scope of the present invention. In describing the present invention, if it is determined that a detailed description of related known technologies may obscure the gist of the present invention, the detailed description will be omitted.
본 명세서에서 모든 화합물 또는 유기기는 특별한 언급이 없는 한 치환되거나 비치환된 것일 수 있다. 여기서, '치환된'이란 화합물 또는 유기기에 포함된 적어도 하나의 수소가 할로겐 원자, 탄소수 1 내지 10의 알킬기, 할로겐화알킬기, 탄소수 3 내지 30의 사이클로알킬기, 탄소수 6 내지 30의 아릴기, 하이드록시기, 탄소수 1 내지 10의 알콕시기, 카르복실산기, 알데히드기, 에폭시기, 시아노기, 니트로기, 아미노기, 술폰산기 및 이들의 유도체로 이루어진 군에서 선택되는 치환기로 대체된 것을 의미한다.In this specification, all compounds or organic groups may be substituted or unsubstituted unless otherwise specified. Here, 'substituted' means that at least one hydrogen contained in a compound or organic group is a halogen atom, an alkyl group with 1 to 10 carbon atoms, a halogenated alkyl group, a cycloalkyl group with 3 to 30 carbon atoms, an aryl group with 6 to 30 carbon atoms, or a hydroxy group. , means replaced with a substituent selected from the group consisting of an alkoxy group having 1 to 10 carbon atoms, a carboxylic acid group, an aldehyde group, an epoxy group, a cyano group, a nitro group, an amino group, a sulfonic acid group, and derivatives thereof.
본 발명은 하기 화학식 1로 표시되는 디아민을 제공한다.The present invention provides a diamine represented by the following formula (1).
[화학식 1][Formula 1]
상기 화학식 1에 있어서,In Formula 1,
Z는 O, S, S-S, C(=O), -C(=O)O-, - OC(=O)- CH(OH), S(=O)2, CR'R", -C(=O)NH-, -NHC(=O)- 및 이들의 조합으로 이루어진 군에서 선택된 관능기이며, 상기 R' 및 R"는 각각 독립적으로 수소원자, 탄소수 1 내지 10의 알킬기 및 탄소수 1 내지 10의 플루오로알킬기로 이루어진 군으로부터 선택되는 것이고,Z is O, S, S-S, C(=O), -C(=O)O-, - OC(=O)- CH(OH), S(=O)2, CR'R", -C( =O)NH-, -NHC(=O)-, and a functional group selected from the group consisting of combinations thereof, wherein R' and R" are each independently a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, and a carbon atom group having 1 to 10 carbon atoms. selected from the group consisting of fluoroalkyl groups,
R1 내지 R5는 각각 독립적으로 -F, -Cl, -Br 및 -I로부터 선택되는 할로겐 원자, 하이드록실기(-OH), 티올기(-SH), 니트로기(-NO2), 시아노기(-CN), 탄소수 1 내지 10의 치환 또는 비치환의 알킬기, 탄소수 1 내지 4의 할로게노알콕시기, 탄소수 1 내지 10의 할로게노알킬기, 탄소수 6 내지 20의 아릴기이다. R 1 to R 5 are each independently a halogen atom selected from -F, -Cl, -Br and -I, a hydroxyl group (-OH), a thiol group (-SH), a nitro group (-NO 2 ), or a cyano group. They are a cyclo group (-CN), a substituted or unsubstituted alkyl group with 1 to 10 carbon atoms, a halogenoalkoxy group with 1 to 4 carbon atoms, a halogenoalkyl group with 1 to 10 carbon atoms, and an aryl group with 6 to 20 carbon atoms.
바람직하게는, R1 내지 R5는 각각 독립적으로 -F, -Cl, -Br 및 -I로부터 선택되는 할로겐 원자, 시아노기(-CN), 탄소수 1 내지 5의 알킬기, 탄소수 1 내지 4의 할로게노알콕시기, 탄소수 1 내지 5의 할로게노알킬기 중에서 선택되는 하나 이상일 수 있고,Preferably, R 1 to R 5 are each independently a halogen atom selected from -F, -Cl, -Br and -I, a cyano group (-CN), an alkyl group having 1 to 5 carbon atoms, or a halo group having 1 to 4 carbon atoms. It may be one or more selected from a genoalkoxy group and a halogenoalkyl group having 1 to 5 carbon atoms,
n1 내지 n5는 각각 독립적으로 0 내지 4의 정수이다.n1 to n5 are each independently an integer of 0 to 4.
일 실시예에 따르면, 상기 화학식 1의 디아민이 하기 화학식 1-1 내지 1-4의 화합물 중에서 선택되는 것일 수 있다.According to one embodiment, the diamine of Formula 1 may be selected from compounds of Formulas 1-1 to 1-4 below.
[화학식 1-1][Formula 1-1]
[화학식 1-2][Formula 1-2]
[화학식 1-3][Formula 1-3]
[화학식 1-4][Formula 1-4]
상기 화학식 1-1 내지 1-4에 있어서, R1 내지 R5 및 n1 내지 n5의 정의는 화학식 1과 동일하다.In Formulas 1-1 to 1-4, the definitions of R 1 to R 5 and n1 to n5 are the same as those in Formula 1.
일 실시예에 따르면, 상기 화학식 1-1의 화합물은 하기 화합물 중에서 선택되는 것일 수 있다.According to one embodiment, the compound of Formula 1-1 may be selected from the following compounds.
일 실시예에 따르면, 상기 화학식 1-2의 화합물은 하기 화합물 중에서 선택되는 것일 수 있다.According to one embodiment, the compound of Formula 1-2 may be selected from the following compounds.
일 실시예에 따르면, 상기 화학식 1-3의 화합물은 하기 화합물 중에서 선택되는 것일 수 있다.According to one embodiment, the compound of Formula 1-3 may be selected from the following compounds.
일 실시예에 따르면, 상기 화학식 1-4의 화합물은 하기 화합물 중에서 선택되는 것일 수 있다.According to one embodiment, the compound of Formula 1-4 may be selected from the following compounds.
바람직한 실시예에 따르면, 상기 화학식 1-1의 디아민은 하기 반응식 1-1과 같은 반응으로 제조될 수 있다.According to a preferred embodiment, the diamine of Chemical Formula 1-1 may be prepared through a reaction shown in Scheme 1-1 below.
[반응식 1-1][Reaction Scheme 1-1]
상기 반응식 1-1에 있어서, R1 내지 R5 및 n1 내지 n5의 정의는 화학식 1과 동일하다.In Scheme 1-1, the definitions of R 1 to R 5 and n1 to n5 are the same as those in Formula 1.
상기 화학식 1-2의 디아민은 하기 반응식 2-1과 같은 반응으로 제조될 수 있다.The diamine of Chemical Formula 1-2 can be prepared through a reaction shown in Scheme 2-1 below.
[반응식 2-1][Reaction Scheme 2-1]
상기 반응식 2-1에 있어서, R1 내지 R5 및 n1 내지 n5의 정의는 화학식 1과 동일하다.In Scheme 2-1, the definitions of R 1 to R 5 and n1 to n5 are the same as those in Formula 1.
상기 화학식 1-3의 디아민은 하기 반응식 3-1과 같은 반응으로 제조될 수 있다.The diamine of Chemical Formula 1-3 can be prepared through a reaction shown in Scheme 3-1 below.
[반응식 3-1][Reaction Scheme 3-1]
상기 반응식 3-1에 있어서, R1 내지 R5 및 n1 내지 n5의 정의는 화학식 1과 동일하다.In Scheme 3-1, the definitions of R 1 to R 5 and n1 to n5 are the same as those in Formula 1.
상기 화학식 1-4의 디아민은 하기 반응식 4-1과 같은 반응으로 제조될 수 있다.The diamine of Chemical Formula 1-4 can be prepared through a reaction shown in Scheme 4-1 below.
[반응식 4-1][Reaction Scheme 4-1]
상기 반응식 4-1에 있어서, R1 내지 R5 및 n1 내지 n5의 정의는 화학식 1과 동일하다.In Scheme 4-1, the definitions of R 1 to R 5 and n1 to n5 are the same as those in Formula 1.
일 실시예에 따르면, 상기 구조를 갖는 디아민을 사용하여 제조된 폴리이미드 전구체의 중량평균분자량은 45,000 g/mol 이상일 수 있으며, 바람직하게는 50,000 g/mol 이상일 수 있다. 분자량이 45,000 g/mol 미만인 경우 폴리이미드 반응성 저하로 인한 용액의 점도 저하가 발생하여 고형분 대비 점도가 낮아 용액 코팅 공정 및 최종 경화 공정시 필름 두께의 제어가 용이하지 않을 수 있다. 또한 분자량이 낮으면 기계적인 물성이 저하되어 필름 강도가 낮아지는 문제가 발생할 수 있다.According to one embodiment, the weight average molecular weight of the polyimide precursor prepared using the diamine having the above structure may be 45,000 g/mol or more, and preferably 50,000 g/mol or more. If the molecular weight is less than 45,000 g/mol, the viscosity of the solution decreases due to a decrease in polyimide reactivity, and the viscosity is low compared to the solid content, so it may not be easy to control the film thickness during the solution coating process and final curing process. Additionally, if the molecular weight is low, mechanical properties may deteriorate, which may lead to lower film strength.
본 발명에 따른 폴리이미드 전구체는, 중합성분으로서 하기 화학식 2의 구조를 갖는 디아민 또는 산이무수물을 포함할 수 있다:The polyimide precursor according to the present invention may include a diamine or acid dianhydride having the structure of the following formula (2) as a polymerization component:
[화학식 2][Formula 2]
상기 화학식 2에 있어서,In Formula 2,
R5, R6는 각각 독립적으로 탄소수 1 ∼ 20 의 1 가의 유기기이고, 그리고 h 는 3∼ 200 의 정수이다.R5 and R6 are each independently a monovalent organic group having 1 to 20 carbon atoms, and h is an integer of 3 to 200.
보다 구체적으로, 상기 화학식 2의 화합물은 하기 화학식 2-1의 디아민 화합물일 수 있다.More specifically, the compound of Formula 2 may be a diamine compound of Formula 2-1 below.
[화학식 2-1][Formula 2-1]
상기 화학식 2-1에 있어서,In Formula 2-1,
R은 탄소수 1~10의 알킬기 또는 탄소수 6~24의 아릴기이고,R is an alkyl group with 1 to 10 carbon atoms or an aryl group with 6 to 24 carbon atoms,
p 및 q는 몰분율로서 p+q=100 일 때 p는 70~90, q는 10~30 이다. p and q are mole fractions, and when p+q=100, p is 70 to 90 and q is 10 to 30.
상기 화학식 2의 화합물은 상기 중합성분의 총 중량에 대해 5 내지 50 중량% 로 포함될 수 있으며, 바람직하게는 전체 중합성분 총 중량에 대해 10 내지 20 중량%로 포함할 수 있다. The compound of Formula 2 may be included in an amount of 5 to 50 wt% based on the total weight of the polymerizable components, and preferably may be included in an amount of 10 to 20 wt% based on the total weight of the total polymerizable components.
상기 화학식 2의 구조를 포함하는 중합성분이 총 중량에 대해 과도하게 첨가되면, 폴리이미드의 모듈러스(modulus)와 같은 기계적 특성이 저하될 수 있고, 막 강도가 감소함으로써, 공정상에서 필름이 찢어지는 등의 물리적 손상이 발생할 수 있다. 또한, 화학식 2의 구조를 갖는 디아민이 과도하게 첨가되는 경우, 상기 실록산 구조를 갖는 고분자로부터 유래되는 Tg가 나타날 수 있으며, 이로부터, 350℃ 이하의 낮은 공정온도에서 Tg가 나타나게 되어, 350℃ 이상의 무기막 증착 공정시 고분자의 유동현상으로 인해 필름표면에 주름이 발생하게 되어 무기막이 갈라지는 현상이 발생할 수 있다.If the polymerization component containing the structure of Formula 2 is added excessively relative to the total weight, mechanical properties such as modulus of polyimide may decrease, and film strength may decrease, resulting in tearing of the film during the process. Physical damage may occur. In addition, when diamine having the structure of Formula 2 is added excessively, Tg derived from the polymer having the siloxane structure may appear, and from this, Tg appears at a low process temperature of 350 ℃ or lower, During the inorganic film deposition process, the flow of polymers may cause wrinkles to form on the film surface, causing the inorganic film to crack.
일반적으로, 상기 화학식 2와 같은 실리콘 올리고머 구조를 포함하는 디아민 또는 산이무수물을 중합성분 중에 10 중량% 이상으로 포함하는 폴리이미드의 경우 잔류응력의 저감효과가 높아질 수 있고, 50중량% 보다 높은 조성에서는 Tg가 390℃ 보다 낮아져 내열성이 저하될 수 있다.In general, in the case of polyimide containing more than 10% by weight of diamine or acid dianhydride containing a silicone oligomer structure as shown in Formula 2, the residual stress reduction effect can be increased, and in compositions higher than 50% by weight, As Tg becomes lower than 390°C, heat resistance may decrease.
반면, 본 발명에 따른 폴리이미드는 전체 중합성분에 대해 10 중량% 이상으로 실리콘 올리고머를 포함함에도 불구하고 Tg를 390℃ 이상으로 유지할 수 있다. 따라서, 유리전이온도를 390℃ 이상으로 유지하면서, 실리콘 올리고머 구조에 의한 잔류응력의 감소효과 또한 함께 얻을 수 있다.On the other hand, the polyimide according to the present invention can maintain Tg above 390°C despite containing silicone oligomer in more than 10% by weight based on the total polymerization components. Therefore, while maintaining the glass transition temperature above 390°C, the effect of reducing residual stress due to the silicon oligomer structure can also be obtained.
상기 화학식 2의 구조를 갖는 디아민 또는 산이무수물에 포함된 실리콘 올리고머 구조의 분자량은 4000 g/mol 이상일 수 있으며, 여기서 분자량은 중량평균 분자량을 의미하며, 분자량 계산은 NMR분석 또는 산염기 적정법을 사용하여 아민 또는 이무수물과 같은 반응기의 당량을 계산하는 방식을 사용할 수 있다.The molecular weight of the silicone oligomer structure contained in the diamine or acid dianhydride having the structure of Formula 2 may be 4000 g/mol or more, where the molecular weight refers to the weight average molecular weight, and the molecular weight is calculated using NMR analysis or acid-base titration. A method of calculating the equivalent weight of a reactive group such as amine or dianhydride can be used.
상기 화학식 2의 구조를 포함하는 실리콘 올리고머 구조의 분자량이 4000 g/mol 미만인 경우에는 내열성이 저하될 수 있으며, 예를 들면, 제조된 폴리이미드의 유리전이온도(Tg)가 저하되거나, 열팽창계수가 과도하게 증가할 수 있다.If the molecular weight of the silicone oligomer structure containing the structure of Formula 2 is less than 4000 g/mol, heat resistance may decrease, for example, the glass transition temperature (Tg) of the produced polyimide may decrease or the thermal expansion coefficient may decrease. It may increase excessively.
본 발명에 따르면, 폴리이미드 매트릭스 내에 분포되어 있는 실리콘 올리고머 도메인의 크기가 나노사이즈, 예를 들어 1nm~50nm, 또는 5nm~40nm, 또는 10nm~30nm로서 연속상을 가지므로 내열성과 기계적 물성을 유지하면서 잔류 응력을 최소화할 수 있다. 이와 같은 연속상을 가지지 않는 경우에는 잔류 응력 감소효과는 있을 수 있지만 내열성과 기계적 물성이 현저히 감소하여 공정에 이용하기가 곤란하다.According to the present invention, the size of the silicon oligomer domain distributed in the polyimide matrix is nano-sized, for example, 1 nm to 50 nm, or 5 nm to 40 nm, or 10 nm to 30 nm, and has a continuous phase while maintaining heat resistance and mechanical properties. Residual stress can be minimized. If it does not have such a continuous phase, it may have a residual stress reduction effect, but heat resistance and mechanical properties are significantly reduced, making it difficult to use it in the process.
여기서 실리콘 올리고머의 도메인은 실리콘 올리고머 구조를 갖는 폴리머가 분포하는 영역을 의미하며, 그 크기는 해당 영역을 둘러싸는 원의 직경을 지칭하는 것으로 한다. Here, the domain of the silicone oligomer refers to an area where a polymer having a silicone oligomer structure is distributed, and its size refers to the diameter of a circle surrounding the area.
실리콘 올리고머 구조를 포함하는 부분(도메인)이 폴리이미드 매트릭스 내에 연속상으로 연결되어 있는 것이 바람직한데, 여기서 연속상이라는 것은 나노사이즈의 도메인이 균일하게 분포하고 있는 형상을 의미한다.It is preferable that the portion (domain) containing the silicon oligomer structure is connected in a continuous phase within the polyimide matrix. Here, the continuous phase means a shape in which nano-sized domains are uniformly distributed.
따라서, 본 발명은 고분자량을 갖는 실리콘 올리고머 임에도 불구하고, 폴리이미드 매트릭스 내에서 상분리 없이 균일하게 분포될 수 있어 헤이즈 특성이 저하되어 보다 투명한 특성을 갖는 폴리이미드를 얻을 수 있을 뿐만 아니라, 실리콘 올리고머 구조가 연속상으로 존재함으로 폴리이미드의 기계적 강도 및 스트레스 완화 효과를 보다 효율적으로 향상시켜 줄 수 있다. 이러한 특성으로부터, 본 발명에 따른 조성물은 열적 특성 및 광학적 특성뿐만 아니라, 코팅-경화 후 기판이 휘어지는 현상이 감소하여 평평한 폴리이미드 필름을 제공할 수 있다.Therefore, in the present invention, despite being a silicone oligomer with a high molecular weight, it can be uniformly distributed without phase separation within the polyimide matrix, thereby lowering the haze characteristics and obtaining a polyimide with more transparent characteristics, as well as a silicone oligomer structure. Since it exists in a continuous phase, the mechanical strength and stress relief effect of polyimide can be improved more efficiently. From these properties, the composition according to the present invention can provide a flat polyimide film not only with thermal properties and optical properties, but also with reduced bending of the substrate after coating-curing.
본 발명은 실리콘 올리고머 구조를 폴리이미드 구조에 삽입함으로써, 폴리이미드의 모듈러스 강도를 적절히 향상시킬 수 있고 외력에 의한 스트레스 또한 완화시켜 줄 수 있다. 이때, 실리콘 올리고머 구조를 포함하는 폴리이미드는 극성을 나타낼 수 있으며, 실록산 구조를 포함하지 않는 폴리이미드 구조와 극성 차이로 인한 상분리가 발생할 수 있으며, 이로 인해 실록산 구조가 폴리이미드 구조 전반에 불균일하게 분포될 수 있다. 이 경우에는 실록산 구조에 의한 폴리이미드의 강도 향상 및 스트레스 완화 효과와 같은 물성 향상효과를 나타내기 어려울 뿐만 아니라, 상분리로 인해 헤이즈가 증가하여 필름의 투명성이 저하될 수 있다. 특히, 실록산 구조를 포함하는 디아민이 고분자량을 갖는 경우에 이로부터 제조된 폴리이미드는 그 극성이 더욱 극명하게 나타나, 폴리이미드 간의 상분리 현상이 보다 극명하게 나타날 수 있다. 이때, 저분자량의 구조를 갖는 실록산 디아민을 사용할 경우에는 스트레스 완화 등의 효과를 나타내기 위해서는 많은 양을 첨가하여야 하며, 이는 낮은 온도에서 Tg가 발생하는 등의 공정상의 문제가 발생시킬 수 있고, 이로 인해 폴리이미드 필름의 물리적 특성이 저하될 수 있다. 이에, 고분자량의 실록산 디아민을 첨가하는 경우에는 relaxation segment가 분자 내에 크게 형성될 수 있으며, 따라서 저분자량을 첨가하는 것에 비해 적은 함량으로도 효과적으로 스트레스 완화 효과를 나타낼 수 있다. 따라서, 본 발명은 상기 고분자량을 갖는 실록산 구조를 갖는 화학식 2의 화합물을 사용함으로써, 폴리이미드 매트릭스상에 상 분리 없이 보다 고르게 분포될 수 있다.In the present invention, by inserting a silicone oligomer structure into a polyimide structure, the modulus strength of polyimide can be appropriately improved and stress caused by external force can also be alleviated. At this time, the polyimide containing the silicone oligomer structure may exhibit polarity, and phase separation may occur due to the difference in polarity from the polyimide structure not containing the siloxane structure, which causes the siloxane structure to be distributed unevenly throughout the polyimide structure. It can be. In this case, not only is it difficult to improve physical properties such as improving the strength of the polyimide and stress relieving effects due to the siloxane structure, but the transparency of the film may decrease due to increased haze due to phase separation. In particular, when the diamine containing a siloxane structure has a high molecular weight, the polarity of the polyimide produced therefrom appears more clearly, and the phase separation phenomenon between polyimides may appear more clearly. At this time, when using siloxane diamine with a low molecular weight structure, a large amount must be added to achieve effects such as stress relief, which may cause process problems such as Tg generation at low temperatures. As a result, the physical properties of the polyimide film may deteriorate. Accordingly, when adding a high molecular weight siloxane diamine, a large relaxation segment can be formed within the molecule, and therefore, a stress relief effect can be effectively achieved even with a small amount compared to adding a low molecular weight siloxane diamine. Accordingly, the present invention can be distributed more evenly on the polyimide matrix without phase separation by using the compound of formula 2 having a siloxane structure with a high molecular weight.
일 실시예에 따르면, 상기 폴리이미드 전구체를 중합하기 위해 사용되는 산이무수물은 테트라카르복실산 이무수물이 사용될 수 있으며, 예를 들면, 상기 테트라카르복실산 이무수물로서, 분자내 방향족, 지환족, 또는 지방족의 4가 유기기, 또는 이들의 조합기로서, 지방족, 지환족 또는 방향족의 4가 유기기가 가교구조를 통해 서로 연결된 4가 유기기를 포함하는 테트라카르복실산 이무수물을 사용할 수 있다. 바람직하게는 일환식 또는 다환식 방향족, 일환식 또는 다환식 지환족, 또는 이들 중 둘 이상이 단일결합 또는 관능기로 연결된 구조를 갖는 산이무수물을 포함할 수 있다. 또는, 방향족, 지환족 등의 고리구조가 단독, 또는 접합(fused)된 복소환 고리 구조, 또는 단일결합으로 연결된 구조와 같은 강직(rigid)한 구조를 갖는 4가 유기기를 포함하는 것일 수 있다:According to one embodiment, the acid dianhydride used to polymerize the polyimide precursor may be tetracarboxylic dianhydride. For example, tetracarboxylic dianhydride may include intramolecular aromatic, alicyclic, Alternatively, as an aliphatic tetravalent organic group, or a combination thereof, tetracarboxylic dianhydride containing a tetravalent organic group in which aliphatic, alicyclic, or aromatic tetravalent organic groups are linked to each other through a crosslinking structure can be used. Preferably, it may include mono- or polycyclic aromatic, mono- or polycyclic alicyclic, or an acid dianhydride having a structure in which two or more of them are connected by a single bond or functional group. Alternatively, it may contain a tetravalent organic group having a rigid structure such as a heterocyclic ring structure in which aromatic, alicyclic, etc. ring structures are singly or fused, or a structure linked by a single bond:
[화학식 3a][Formula 3a]
[화학식 3b][Formula 3b]
[화학식 3c][Formula 3c]
[화학식 3d][Formula 3d]
[화학식 3e][Formula 3e]
상기 화학식 3a 내지 3e에서, R11 내지 R17 은 각각 독립적으로 -F, -Cl, -Br 및 -I로부터 선택되는 할로겐 원자, 하이드록실기(-OH), 티올기(-SH), 니트로기(-NO2), 시아노기, 탄소수 1 내지 10의 알킬기, 탄소수 1 내지 4의 할로게노알콕시, 탄소수 1 내지 10의 할로게노알킬, 탄소수 6 내지 20의 아릴기에서 선택되는 것일 수 있고,In Formulas 3a to 3e, R 11 to R 17 are each independently a halogen atom selected from -F, -Cl, -Br and -I, a hydroxyl group (-OH), a thiol group (-SH), and a nitro group. (-NO2), cyano group, alkyl group with 1 to 10 carbon atoms, halogenoalkoxy with 1 to 4 carbon atoms, halogenoalkyl with 1 to 10 carbon atoms, and aryl group with 6 to 20 carbon atoms,
a1은 0 내지 2의 정수, a2는 0 내지 4의 정수, a3는 0 내지 8의 정수, a4 및 a5는 각각 독립적으로 0 내지 3의 정수, a6 및 a9는 각각 독립적으로 0 내지 3의 정수, 그리고 a7 및 a8은 각각 독립적으로 0 내지 7의 정수일 수 있으며,a1 is an integer from 0 to 2, a2 is an integer from 0 to 4, a3 is an integer from 0 to 8, a4 and a5 are each independently an integer from 0 to 3, a6 and a9 are each independently an integer from 0 to 3, And a7 and a8 may each independently be integers from 0 to 7,
A11 및 A12는 각각 독립적으로 단일결합, -O-, -CR'R"-(이때, R' 및 R"은 각각 독립적으로 수소원자, 탄소수 1 내지 10의 알킬기(예를 들면, 메틸기, 에틸기, 프로필기, 이소프로필기, n-부틸기, tert-부틸기, 펜틸기 등) 및 탄소수 1 내지 10의 할로알킬기(예를 들면, 트리플루오로메틸기 등)로 이루어진 군으로부터 선택되는 것임), -C(=O)-, -C(=O)O-, -C(=O)NH-, -S-, -SO-, -SO2-, -O[CH2CH2O]y-(y는 1 내지 44의 정수임), -NH(C=O)NH-, -NH(C=O)O-, 탄소수 6 내지 18의 일환식 또는 다환식의 시클로알킬렌기(예를 들면, 시클로헥실렌기 등), 탄소수 6 내지 18의 일환식 또는 다환식의 아릴렌기(예를 들면, 페닐렌기, 나프탈렌기, 플루오레닐렌기등), 및 이들의 조합으로 이루어진 군에서 선택될 수 있다. A 11 and A 12 are each independently a single bond, -O-, -CR'R"- (where R' and R" are each independently a hydrogen atom, an alkyl group having 1 to 10 carbon atoms (for example, a methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, tert-butyl group, pentyl group, etc.) and haloalkyl groups of 1 to 10 carbon atoms (e.g., trifluoromethyl group, etc.) , -C(=O)-, -C(=O)O-, -C(=O)NH-, -S-, -SO-, -SO 2 -, -O[CH 2 CH 2 O]y -(y is an integer from 1 to 44), -NH(C=O)NH-, -NH(C=O)O-, monocyclic or polycyclic cycloalkylene group having 6 to 18 carbon atoms (e.g., cyclohexylene group, etc.), monocyclic or polycyclic arylene groups having 6 to 18 carbon atoms (e.g., phenylene group, naphthalene group, fluorenylene group, etc.), and combinations thereof. .
또는, 상기 테트라카르복실산 이무수물은 하기 화학식 4a 내지 4n으로 이루어진 군으로부터 선택되는 4가 유기기를 포함하는 것일 수 있다.Alternatively, the tetracarboxylic dianhydride may contain a tetravalent organic group selected from the group consisting of the following formulas 4a to 4n.
상기 화학식 4a 내지 4n의 4가 유기기내 1 이상의 수소원자는 -F, -Cl, -Br 및 -I로부터 선택되는 할로겐 원자, 하이드록실기(-OH), 티올기(-SH), 니트로기(-NO2), 시아노기, 탄소수 1 내지 10의 알킬기, 탄소수 1 내지 4의 할로게노알콕시, 탄소수 1 내지 10의 할로게노알킬, 탄소수 6 내지 20의 아릴기에서 선택되는 치환체로 치환될 수 있다. 예를 들면, 상기 할로겐 원자는 플루오로(-F)일 수 있으며, 할로게노알킬기는 플루오로 원자를 포함하는 탄소수 1 내지 10의 플루오로알킬기로서, 플루오로메틸기, 퍼플루오로에틸기, 트리플루오로메틸기 등에서 선택되는 것일 수 있으며, 상기 알킬기는 메틸기, 에틸기, 프로필기, 이소프로필기, t-부틸기, 펜틸기, 헥실기에서 선택되는 것일 수 있고, 상기 아릴기는 페닐기, 나프탈레닐기에서 선택되는 것 일 수 있으며, 보다 바람직하게는 플루오로원자 및 플로오로알킬기 등의 플루오로 원자를 포함하는 치환기일 수 있다.One or more hydrogen atoms in the tetravalent organic group of Formulas 4a to 4n are a halogen atom selected from -F, -Cl, -Br and -I, a hydroxyl group (-OH), a thiol group (-SH), a nitro group ( -NO2), cyano group, alkyl group with 1 to 10 carbon atoms, halogenoalkoxy with 1 to 4 carbon atoms, halogenoalkyl with 1 to 10 carbon atoms, and aryl group with 6 to 20 carbon atoms. For example, the halogen atom may be fluoro (-F), and the halogenoalkyl group is a fluoroalkyl group having 1 to 10 carbon atoms containing a fluoro atom, such as a fluoromethyl group, perfluoroethyl group, and trifluoro. The alkyl group may be selected from a methyl group, ethyl group, propyl group, isopropyl group, t-butyl group, pentyl group, and hexyl group, and the aryl group may be selected from a phenyl group and a naphthalenyl group. It may be a substituent containing a fluoro atom, such as a fluoro atom or a fluoroalkyl group, more preferably.
또는, 상기 테트라카르복실산 이무수물은, 방향족 고리 또는 지방족 구조가 각각의 고리구조가 강직(rigid)한 구조, 즉, 단일 고리 구조, 각각의 고리가 단일결합으로 결합된 구조 또는 각각의 고리가 직접적으로 연결된 복소환 구조를 포함하는 4가 유기기를 포함하는 것 일 수 있다.Alternatively, the tetracarboxylic dianhydride has an aromatic ring or aliphatic structure in which each ring structure is rigid, that is, a single ring structure, a structure in which each ring is bonded by a single bond, or each ring is It may contain a tetravalent organic group containing a directly connected heterocyclic structure.
일 실시예에 따르면, 폴리이미드 전구체 중합시 상기 화학식 1디아민의 이외에 1종 이상의 디아민이 더 포함될 수 있으며, 예를 들면, 탄소수 6 내지 24의 일환식 또는 다환식 방향족 2가 유기기, 탄소수 6 내지 18의 일환식 또는 다환식 지환족 2가 유기기, 또는 이들 중 둘 이상이 단일결합이나 관능기로 연결된 구조를 포함하는 2가 유기기 선택되는 2가 유기기 구조를 포함하는 디아민을 포함할 수 있으며, 또는, 방향족, 지환족 등의 고리구조 화합물이 단독, 또는 접합(fused)된 복소환 고리 구조, 또는 단일결합으로 연결된 구조와 같은 강직(rigid)한 구조를 갖는 2가 유기기로부터 선택되는 것 일 수 있다.According to one embodiment, when polymerizing a polyimide precursor, one or more diamines may be further included in addition to the diamine of Formula 1, for example, a mono- or polycyclic aromatic divalent organic group having 6 to 24 carbon atoms, or a divalent organic group having 6 to 24 carbon atoms. It may include a diamine containing a divalent organic group structure selected from 18 mono- or polycyclic alicyclic divalent organic groups, or a divalent organic group containing a structure in which two or more of them are connected by a single bond or functional group; , or a divalent organic group having a rigid structure, such as a heterocyclic ring structure in which aromatic, alicyclic, etc. ring structures are singly or fused, or a structure linked by a single bond. It can be.
예를 들면, 상기 디아민은, 하기 화학식 5a 내지 5e 로부터 선택되는 2가 유기기를 포함하는 것일 수 있다.For example, the diamine may include a divalent organic group selected from the following formulas 5a to 5e.
[화학식 5a][Formula 5a]
[화학식 5b][Formula 5b]
[화학식 5c][Formula 5c]
[화학식 5d][Formula 5d]
[화학식 5e][Formula 5e]
상기 화학식 5a 내지 5e에서,In Formulas 5a to 5e,
R21 내지 R27은 각각 독립적으로 -F, -Cl, -Br 및 -I로부터 선택되는 할로겐 원자, 하이드록실기(-OH), 티올기(-SH), 니트로기(-NO2), 시아노기, 탄소수 1 내지 10의 알킬기, 탄소수 1 내지 4의 할로게노알콕시, 탄소수 1 내지 10의 할로게노알킬, 탄소수 6 내지 20의 아릴기로 이루어진 군에서 선택될 수 있다. R 21 to R 27 are each independently a halogen atom selected from -F, -Cl, -Br and -I, a hydroxyl group (-OH), a thiol group (-SH), a nitro group (-NO 2 ), a cyano group, It may be selected from the group consisting of an alkyl group with 1 to 10 carbon atoms, a halogenoalkoxy with 1 to 4 carbon atoms, a halogenoalkyl with 1 to 10 carbon atoms, and an aryl group with 6 to 20 carbon atoms.
A21 및 A22는 각각 독립적으로 단일결합, -O-, -CR'R"-(이때, R' 및 R"은 각각 독립적으로 수소원자, 탄소수 1 내지 10의 알킬기(예를 들면, 메틸기, 에틸기, 프로필기, 이소프로필기, n-부틸기, tert-부틸기, 펜틸기 등) 및 탄소수 1 내지 10의 할로알킬기(예를 들면, 트리플루오로메틸기 등)로 이루어진 군으로부터 선택되는 것임), -C(=O)-, -C(=O)O-, -C(=O)NH-, -S-, -SO-, -SO2-, -O[CH2CH2O]y-(y는 1 내지 44의 정수임), -NH(C=O)NH-, -NH(C=O)O-, 탄소수 6 내지 18의 일환식 또는 다환식의 시클로알킬렌기(예를 들면, 시클로헥실렌기 등), 탄소수 6 내지 18의 일환식 또는 다환식의 아릴렌기(예를 들면, 페닐렌기, 나프탈렌기, 플루오레닐렌기등), 및 이들의 조합으로 이루어진 군에서 선택될 수 있으며,A 21 and A 22 are each independently a single bond, -O-, -CR'R"- (where R' and R" are each independently a hydrogen atom, an alkyl group having 1 to 10 carbon atoms (for example, a methyl group, ethyl group, propyl group, isopropyl group, n-butyl group, tert-butyl group, pentyl group, etc.) and haloalkyl groups of 1 to 10 carbon atoms (e.g., trifluoromethyl group, etc.) , -C(=O)-, -C(=O)O-, -C(=O)NH-, -S-, -SO-, -SO 2 -, -O[CH 2 CH 2 O] y -(y is an integer from 1 to 44), -NH(C=O)NH-, -NH(C=O)O-, monocyclic or polycyclic cycloalkylene group having 6 to 18 carbon atoms (e.g., Cyclohexylene group, etc.), monocyclic or polycyclic arylene group having 6 to 18 carbon atoms (e.g., phenylene group, naphthalene group, fluorenylene group, etc.), and combinations thereof. ,
b1은 0 내지 4의 정수이고, b2는 0 내지 6의 정수이며, b3은 0 내지 3의 정수이고, b4 및 b5는 각각 독립적으로 0 내지 4의 정수이고, b7 및 b8은 각각 독립적으로 0내지 9의 정수이고, b6 및 b9는 각각 독립적으로 0 내지 3의 정수이다.b1 is an integer from 0 to 4, b2 is an integer from 0 to 6, b3 is an integer from 0 to 3, b4 and b5 are each independently an integer from 0 to 4, and b7 and b8 are each independently an integer from 0 to 4. It is an integer of 9, and b6 and b9 are each independently integers of 0 to 3.
예를 들면, 상기 디아민은 하기 화학식 6a 내지 6p 로부터 선택되는 2가 유기기를 포함하는 것일 수 있다.For example, the diamine may include a divalent organic group selected from the following formulas 6a to 6p.
또는, 상기 디아민은 방향족 고리 또는 지방족 구조가 강직(rigid)한 사슬구조를 형성하는 2가 유기기를 포함하는 것일 수 있으며, 예를 들면, 단일 고리 구조, 각각의 고리가 단일결합으로 결합된 구조 또는 각각의 고리가 직접적으로 접합(fused)된 복소환 고리 구조를 포함하는 2가 유기기 구조를 포함할 수 있다.Alternatively, the diamine may include a divalent organic group in which an aromatic ring or an aliphatic structure forms a rigid chain structure, for example, a single ring structure, a structure in which each ring is connected by a single bond, or Each ring may contain a divalent organic group structure including a directly fused heterocyclic ring structure.
본 발명의 일 실시예에 따르면, 테트라카르복실산 이무수물의 총 함량과 상기 디아민의 함량은, 1:1.1~1.1:1 몰비로 반응될 수 있으며, 바람직하게는, 반응성 향상 및 공정성 향상을 위해, 상기 테트라카르복실산 이무수물의 총 함량이 디아민에 비해 과량으로 반응되거나, 또는 디아민의 함량이 테트라카르복실산 이무수물의 총 함량에 비해 과량으로 반응되는 것이 바람직하다.According to one embodiment of the present invention, the total content of tetracarboxylic dianhydride and the content of the diamine may be reacted at a molar ratio of 1:1.1 to 1.1:1, and preferably, to improve reactivity and improve processability, It is preferable that the total content of the tetracarboxylic dianhydride is reacted in an excessive amount compared to the diamine, or that the diamine content is reacted in an excessive amount compared to the total content of the tetracarboxylic dianhydride.
본 발명의 일 실시예에 따르면, 상기 테트라카르복실산 이무수물의 총 함량과 디아민의 함량의 몰비는 1:0.98 내지 0.98:1, 바람직하게는 1:0.99 내지 0.99:1으로 반응되는 것이 바람직할 수 있다.According to one embodiment of the present invention, the molar ratio of the total content of tetracarboxylic dianhydride and the content of diamine may be preferably 1:0.98 to 0.98:1, preferably 1:0.99 to 0.99:1. there is.
산이무수물과 다이아민계 화합물의 중합 반응은, 용액 중합 등 통상의 폴리이미드 또는 그 전구체의 중합 방법에 따라 실시될 수 있다.The polymerization reaction of an acid dianhydride and a diamine-based compound can be carried out according to a conventional polymerization method of polyimide or its precursor, such as solution polymerization.
폴리아믹산 중합반응시 사용가능한 유기용매로는, 감마-부티로락톤, 1,3-디메틸-2-이미다졸리디논, 메틸에틸케톤, 시클로헥사논, 시클로펜타논, 4-하이드록시-4-메틸-2-펜타논 등의 케톤류; 톨루엔, 크실렌, 테트라메틸벤젠 등의 방향족 탄화수소류; 에틸렌글리콜모노에틸에테르, 에틸렌글리콜모노메틸에테르, 에틸렌글리콜모노부틸에테르, 디에틸렌글리콜모노에틸에테르, 디에틸렌글리콜모노메틸에테르, 디에틸렌글리콜모노부틸에테르, 프로필렌글리콜모노메틸에테르, 프로필렌글리콜모노에틸에테르, 디프로필렌글리콜디에틸에테르, 트리에틸렌글리콜모노에틸에테르 등의 글리콜에테르류(셀로솔브); 아세트산에틸, 아세트산부틸, 에틸렌글리콜모노에틸에테르아세테이트, 에틸렌글리콜모노부틸에테르아세테이트, 디에틸렌글리콜모노에틸에테르아세테이트, 디프로필렌글리콜모노메틸에테르아세테이트, 에탄올, 프로판올, 에틸렌글리콜, 프로필렌글리콜, 카르비톨, 디메틸프로피온아마이드(dimethylpropionamide, DMPA), 디에틸프로피온아마이드(diethylpropionamide, DEPA), 디메틸아세트아미드(DMAc), N,N-디에틸아세트아미드, 디메틸포름아미드(DMF), 디에틸포름아미드(DEF), N-메틸피롤리돈(NMP), N-에틸피롤리돈(NEP), N,N-디메틸메톡시아세트아미드, 디메틸술폭사이드, 피리딘, 디메틸술폰, 헥사메틸포스포르아미드, 테트라메틸우레아, N-메틸카프로락탐, 테트라히드로퓨란, m-디옥산, P-디옥산, 1,2-디메톡시에탄, 비스(2-메톡시에틸)에테르, 1,2-비스(2-메톡시에톡시)에탄, 비스[2-(2-메톡시에톡시)]에테르, 에크아마이드(Equamide)M100, 에크아마이드(Equamide)B100 등일 수 있으며, 이들 중 1종 단독 또는 2종 이상의 혼합물이 사용될 수 있다.Organic solvents that can be used in the polyamic acid polymerization reaction include gamma-butyrolactone, 1,3-dimethyl-2-imidazolidinone, methyl ethyl ketone, cyclohexanone, cyclopentanone, and 4-hydroxy-4- Ketones such as methyl-2-pentanone; Aromatic hydrocarbons such as toluene, xylene, and tetramethylbenzene; Ethylene glycol monoethyl ether, ethylene glycol monomethyl ether, ethylene glycol monobutyl ether, Diethylene glycol monoethyl ether, Diethylene glycol monomethyl ether, Diethylene glycol monobutyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether , glycol ethers such as dipropylene glycol diethyl ether and triethylene glycol monoethyl ether (Cellosolve); Ethyl acetate, butyl acetate, ethylene glycol monoethyl ether acetate, ethylene glycol monobutyl ether acetate, diethylene glycol monoethyl ether acetate, dipropylene glycol monomethyl ether acetate, ethanol, propanol, ethylene glycol, propylene glycol, carbitol, dimethyl Propionamide (dimethylpropionamide, DMPA), diethylpropionamide (DEPA), dimethylacetamide (DMAc), N,N-diethylacetamide, dimethylformamide (DMF), diethylformamide (DEF), N -Methylpyrrolidone (NMP), N-ethylpyrrolidone (NEP), N,N-dimethylmethoxyacetamide, dimethyl sulfoxide, pyridine, dimethyl sulfone, hexamethylphosphoramide, tetramethylurea, N- Methylcaprolactam, tetrahydrofuran, m-dioxane, p-dioxane, 1,2-dimethoxyethane, bis(2-methoxyethyl)ether, 1,2-bis(2-methoxyethoxy)ethane , bis[2-(2-methoxyethoxy)]ether, Equamide M100, Equamide B100, etc., of which one type alone or a mixture of two or more types may be used.
일 실시예에 따르면, 상기 중합성분을 중합하는 유기용매로서 25℃ 분배계수 LogP가 양수인 용매를 사용할 수 있다. LogP가 양수인 유기용매를 사용함에 따라 메틸페닐실리콘 올리고머가 10중량% 이상으로 포함되는 조성에서도 Tg를 390℃이상의 높은 온도로 유지할 수 있다.According to one embodiment, a solvent having a positive partition coefficient LogP at 25°C may be used as an organic solvent for polymerizing the polymerization component. By using an organic solvent with a positive LogP, the Tg can be maintained at a high temperature of 390°C or higher even in a composition containing 10% by weight or more of methylphenyl silicon oligomer.
또한, 상기와 같은 분배계수가 양수인 유기용매는 플렉서블(flexible)한 폴리이미드 반복구조와 실리콘 올리고머와 같은 실록산 구조를 포함하는 폴리이미드 구조의 극성 차이로 인한 상분리로 인해 발생되는 백탁현상을 감소시킬 수 있다. 종래에는 이러한 상분리를 해결하기 위해 2종의 유기용매를 사용하였으나, 상기와 같은 유기용매를 사용하는 것 만으로도 백탁현상을 감소시킬 수 있어, 보다 투명한 폴리이미드 필름을 제조할 수 있다.In addition, the organic solvent with a positive distribution coefficient as described above can reduce the white clouding phenomenon caused by phase separation due to the difference in polarity between the flexible polyimide repeating structure and the polyimide structure containing a siloxane structure such as a silicone oligomer. there is. Conventionally, two types of organic solvents were used to solve this phase separation, but just using the above organic solvents can reduce the white turbidity phenomenon, making it possible to manufacture a more transparent polyimide film.
상기한 문제를 해결하기 위해 극성 용매와 비극성 용매를 혼합하여 사용하는 방법도 있으나, 극성 용매의 경우 휘발성이 높은 경향이 있으며, 따라서 제조공정상에서 미리 휘발되는 등의 문제가 발생할 수 있으며, 이 때문에 공정의 재현성이 저하되는 등의 문제가 발생할 수 있을 뿐만 아니라, 상분리 문제를 완전히 개선하지 못할 수 있어, 제조된 폴리이미드 필름의 헤이즈(Haze)가 높아져 투명도가 저하될 수 있다. In order to solve the above problem, there is a method of using a mixture of polar and non-polar solvents, but polar solvents tend to be highly volatile, and therefore problems such as pre-volatilization may occur during the manufacturing process. Not only may problems such as reduced reproducibility occur, but the phase separation problem may not be completely improved, and the haze of the produced polyimide film may increase and transparency may decrease.
보다 구체적으로는 용매의 분자가 양쪽친매성을 갖는 구조를 포함하는 용매를 사용함으로써, 극성 용매를 사용함에 따른 공정상의 문제를 해결할 수 있을 뿐만 아니라, 양쪽친매성을 갖는 분자구조로 인해 1종류의 용매만을 사용하더라도 폴리이미드를 고르게 분포시킬 수 있어 상분리로 인한 문제를 해결하는데 매우 적합하며, 이로 인해 헤이즈(Haze) 특성이 현저히 개선된 폴리이미드를 제공할 수 있다.More specifically, by using a solvent whose molecules have an amphiphilic structure, not only can the process problems caused by using a polar solvent be solved, but also one type of solvent can be produced due to the amphiphilic molecular structure. Even if only a solvent is used, polyimide can be distributed evenly, making it very suitable for solving problems caused by phase separation, and as a result, polyimide with significantly improved haze characteristics can be provided.
상기 분배계수 값이 양수인 경우에는 용매의 극성이 소수성임을 의미하는데, 본 발명자들의 연구에 따르면 분배계수 값이 양수인 특정 용매를 사용하여 폴리이미드 전구체 조성물을 제조하면, 에지백 현상이 개선되는 것을 알 수 있었다. 또한, 본 발명은 상기와 같이 Log P가 양수를 갖는 용매를 사용함으로써, 레벨링제와 같은 소재의 표면장력 및 도막의 평활성을 조절하는 첨가제를 사용하지 않고도 용액의 에지백 현상을 제어할 수 있으며, 이는 첨가제 등의 부가적인 첨가제를 사용하지 않으므로 최종 생성물에 저분자 물질이 함유되는 등의 품질 및 공정상의 문제를 제거할 수 있을 뿐만 아니라 보다 효율적으로 균일한 특성을 갖는 폴리이미드 필름을 형성할 수 있는 효과가 있다.If the distribution coefficient value is a positive number, it means that the polarity of the solvent is hydrophobic. According to the present inventors' research, it has been found that when a polyimide precursor composition is prepared using a specific solvent with a positive distribution coefficient value, the edgeback phenomenon is improved. there was. In addition, by using a solvent with a positive Log P as described above, the present invention can control the edgeback phenomenon of the solution without using additives such as leveling agents that control the surface tension of the material and the smoothness of the coating film. Because it does not use additional additives such as additives, it not only eliminates quality and process problems such as low-molecular-weight substances contained in the final product, but also forms a polyimide film with uniform characteristics more efficiently. There is.
예를 들면, 폴리이미드 전구체 조성물을 유리기판에 코팅하는 공정에 있어서, 경화시 또는 습도조건의 코팅액의 방치조건에서 코팅층의 수축으로 인한 에지백 현상이 발생할 수 있다. 이러한 코팅 용액의 에지백 현상은 필름의 두께의 편차를 초래할 수 있어, 이에 의한 필름의 내굴곡성의 부족으로 필름이 끊어지거나 컷팅시 모서리가 부스러지는 현상이 나타나 공정상의 작업성이 나쁘고 수율이 저하되는 문제가 발생할 수 있다.For example, in the process of coating a polyimide precursor composition on a glass substrate, an edgeback phenomenon may occur due to shrinkage of the coating layer during curing or when the coating solution is left under humidity conditions. The edge-back phenomenon of this coating solution can cause deviation in the thickness of the film, which causes the film to break due to lack of bending resistance of the film or the edges to crumble during cutting, which leads to poor workability in the process and lower yield. Problems may arise.
또한, 기판상에 도포된 폴리이미드 전구체 조성물에 극성을 갖는 미세 이물질이 유입되는 경우, Log P가 음수인 극성의 용매를 포함하는 폴리이미드 전구체 조성물에서는 상기 이물질이 갖는 극성에 의해 이물질의 위치를 기준으로 산발적인 코팅의 균열 또는 두께변화가 일어날 수 있으나, Log P가 양수인 소수성의 용매를 사용하는 경우에는 극성을 갖는 미세 이물질이 유입되는 경우에도 코팅의 균열로 인한 두께변화 등의 발생이 감소 또는 억제될 수 있다.In addition, when fine foreign substances with polarity are introduced into the polyimide precursor composition applied on the substrate, in the polyimide precursor composition containing a polar solvent with a negative Log P, the location of the foreign substances is based on the polarity of the foreign substances. Sporadic coating cracks or thickness changes may occur, but when using a hydrophobic solvent with a positive Log P, the occurrence of thickness changes due to coating cracks is reduced or suppressed even when polar fine foreign substances are introduced. It can be.
구체적으로, Log P가 양수인 용매를 포함하는 폴리이미드 전구체 조성물은, 하기 식 1로 정의되는 에지백율(edge back ratio)이 0% 내지 0.1% 이하일 수 있다.Specifically, the polyimide precursor composition containing a solvent in which Log P is a positive number may have an edge back ratio defined by Equation 1 below of 0% to 0.1% or less.
[식 1][Equation 1]
에지백율(%) = [(A-B)/A]×100Edge percentage (%) = [(A-B)/A]×100
상기 식 1에 있어서,In equation 1 above,
A: 기판 (100mm × 100mm) 상에 폴리이미드 전구체 조성물이 완전히 코팅된 상태에서의 면적이고,A: Area in a state where the polyimide precursor composition is completely coated on the substrate (100 mm × 100 mm),
B: 폴리이미드 전구체 조성물 또는 PI 필름이 코팅된 기판의 가장자리 끝단 에서부터 에지백 현상이 발생한 후의 면적이다.B: This is the area after the edgeback phenomenon occurs from the edge of the substrate coated with the polyimide precursor composition or PI film.
이러한 폴리이미드 전구체 조성물 및 필름의 에지백(edge back) 현상은 폴리이미드 전구체 조성물 용액을 코팅한 후 30분 이내에 발생될 수 있으며, 특히, 가장자리부터 말려 들어가기 시작함으로써 가장자리의 두께를 두껍게 만들 수 있다.This edge back phenomenon of the polyimide precursor composition and film may occur within 30 minutes after coating the polyimide precursor composition solution, and in particular, the edge may begin to curl in from the edge, thereby increasing the thickness of the edge.
본 발명에 따른 폴리이미드 전구체 조성물을 기판에 코팅한 후 10분 이상, 예를 들면 10분 이상, 예를 들면 40분 이상의 시간 동안 습도조건에서 방치한 후의 상기 코팅된 수지 조성물 용액의 에지백율이 0.1% 이하일 수 있으며, 예를 들면, 20 ~ 30℃의 온도에서, 40% 이상의 습도조건, 보다 구체적으로는 40% 내지 80% 범위의 습도조건, 즉, 40%, 50%, 60%, 70%, 80% 각각의 습도 조건에서, 예를 들면, 50%의 습도조건에서 10 내지 50분간 방치된 이후에도 0.1% 이하의 매우 작은 에지백율을 나타낼 수 있으며, 바람직하게는 0.05%, 보다 바람직하게는 거의 0%에 가까운 에지백율을 나타낼 수 있다.상기와 같은 에지백율은 경화 이후에도 유지되는 것이며, 예를 들면, 폴리이미드 전구체 조성물을 기판에 코팅한 후 10분 이상, 예를 들면 20 ~ 30℃의 온도에서, 40% 이상의 습도조건, 보다 구체적으로는 40% 내지 80% 범위의 습도조건, 즉, 40%, 50%, 60%, 70%, 80% 각각의 습도 조건에서, 예를 들면 50%의 습도조건에서 10 내지 50분간 방치한 후 경화된 폴리이미드 필름의 에지백율이 0.1% 이하일 수 있으며, 즉, 열처리에 의한 경화 공정에서도 에지백 현상이 거의 일어나지 않거나 없을 수 있으며, 구체적으로는, 0.05%, 보다 바람직하게는 거의 0%에 가까운 에지백율을 나타낼 수 있다.After coating the polyimide precursor composition according to the present invention on a substrate and leaving it in humidity conditions for 10 minutes or more, for example, 10 minutes or more, for example, 40 minutes or more, the edge percent ratio of the coated resin composition solution is 0.1. % or less, for example, at a temperature of 20 to 30°C, humidity conditions of 40% or more, more specifically, humidity conditions in the range of 40% to 80%, that is, 40%, 50%, 60%, 70%. , 80% humidity conditions, for example, even after being left for 10 to 50 minutes at 50% humidity conditions, a very small edge whitening ratio of 0.1% or less can be displayed, preferably 0.05%, more preferably almost. It can exhibit an edge percentage close to 0%. The above edge percentage is maintained even after curing, for example, at a temperature of 20 to 30°C for more than 10 minutes after coating the polyimide precursor composition on the substrate. In humidity conditions of 40% or more, more specifically, humidity conditions in the range of 40% to 80%, that is, in each humidity condition of 40%, 50%, 60%, 70%, and 80%, for example, 50% The edge backing rate of the polyimide film cured after being left for 10 to 50 minutes in humidity conditions may be 0.1% or less, that is, the edge back phenomenon may hardly occur or may not occur even in the curing process by heat treatment, specifically, 0.05%. , More preferably, it can exhibit an edge percentage close to 0%.
본 발명에 따른 폴리이미드 전구체 조성물은 이러한 에지백(edge back) 현상을 해결함으로써, 보다 균일한 특성을 갖는 폴리이미드 필름을 수득할 수 있어 제조공정의 수율을 보다 향상시킬 수 있다.By solving this edge back phenomenon, the polyimide precursor composition according to the present invention can obtain a polyimide film with more uniform characteristics, thereby improving the yield of the manufacturing process.
또한, 본 발명에 따른 용매의 밀도는 ASTM D1475의 표준측정방법으로 측정하였을 때, 1g/cm3 이하일 수 있으며, 밀도가 1 g/cm3 이상의 값을 갖는 경우에는 상대점도가 높아질 수 있어 공정상 효율성이 감소할 수 있다.In addition, the density of the solvent according to the present invention may be 1 g/cm 3 or less when measured using the standard measurement method of ASTM D1475, and if the density is 1 g/cm 3 or more, the relative viscosity may increase, making it difficult to process. Efficiency may decrease.
상기 LogP가 양수인 용매는, 예를 들면, N,N-디에틸아세트아마이드(N,Ndiethylacetamide,DEAc), N,N-디에틸포름아마이드(N,N-diethylformamide, DEF),N-에틸피롤리돈(N-ethylpyrrolidone, NEP), 디메틸프로피온아마이드(DMPA) 및 디에틸프로피온아마이드(DEPA) 중에서 선택되는 하나 이상일 수 있다.Solvents in which the LogP is a positive number include, for example, N,N-diethylacetamide (DEAc), N,N-diethylformamide (DEF), and N-ethylpyrroli It may be one or more selected from N-ethylpyrrolidone (NEP), dimethylpropionamide (DMPA), and diethylpropionamide (DEPA).
상기 유기용매는 비점이 300℃ 이하일 수 있으며, 보다 구체적으로 분배계수 LogP 값은 0.01 내지 3, 또는 0.01 내지 2, 또는 0.1 내지 2 일 수 있다.The organic solvent may have a boiling point of 300°C or lower, and more specifically, the distribution coefficient LogP may be 0.01 to 3, or 0.01 to 2, or 0.1 to 2.
상기 분배계수는 ACD/Labs 사의 ACD/Percepta platform의 ACD/LogP module을 사용하여 계산될 수 있으며, ACD/LogP module은 분자의 2D 구조를 이용하여 QSPR(Quantitative Structure-Property Relationship) 방법론 기반의 알고리즘을 이용한다.The distribution coefficient can be calculated using the ACD/LogP module of the ACD/Percepta platform of ACD/Labs, which uses an algorithm based on the QSPR (Quantitative Structure-Property Relationship) methodology using the 2D structure of the molecule. Use it.
또한, 크실렌, 톨루엔과 같은 방향족 탄화수소를 더 사용할 수도 있으며, 또한 폴리머의 용해를 촉진시키기 위해서 상기 용매에 상기 용매 총량에 대하여 약 50 중량% 이하의 알칼리 금속염 또는 알칼리토류 금속염을 더 첨가할 수도 있다.Additionally, aromatic hydrocarbons such as xylene and toluene may be used, and in order to promote dissolution of the polymer, about 50% by weight or less of an alkali metal salt or alkaline earth metal salt may be added to the solvent based on the total amount of the solvent.
또한, 폴리아믹산 또는 폴리이미드를 합성하는 경우 과잉의 폴리아미노기 또는 산무수물기를 불활성화하기위해서, 분자 말단을 디카본산무수물 또는 모노아민을 반응시켜, 폴리이미드의 말단을 봉지하는 말단 봉지제를더 첨가할 수 있다.In addition, when synthesizing polyamic acid or polyimide, in order to inactivate excess polyamino or acid anhydride groups, an end capping agent that seals the ends of the polyimide by reacting the molecular ends with dicarbonic acid anhydride or monoamine may be added. You can.
상기 테트라카르복실산 이무수물을 디아민과 반응시키는 방법은 용액 중합 등 통상의 폴리이미드 전구체 중합 제조방법에 따라 실시할 수 있으며. 구체적으로는, 디아민을 유기 용매 중에 용해시킨 후, 결과로 수득된 혼합용액에 테트라카르복실산 이무수물을 첨가하여 중합반응시킴으로써 제조될 수 있다.The method of reacting the tetracarboxylic dianhydride with diamine can be carried out according to a typical polyimide precursor polymerization production method such as solution polymerization. Specifically, it can be prepared by dissolving diamine in an organic solvent and then adding tetracarboxylic dianhydride to the resulting mixed solution to perform a polymerization reaction.
상기 중합반응은 비활성 기체 또는 질소 기류 하에 실시될 수 있으며, 무수조건에서 실행될 수 있다.The polymerization reaction may be carried out under an inert gas or nitrogen stream and may be carried out under anhydrous conditions.
또한, 상기 중합반응시 반응온도는 -20 내지 80℃, 바람직하게는 0 내지 80℃에서 실시될 수 있다. 반응온도가 너무 높을 경우 반응성이 높아져 분자량이 커질 수 있으며, 전구체 조성물의 점도가 상승함으로써 공정상으로 불리할 수 있다.Additionally, the polymerization reaction may be carried out at a reaction temperature of -20 to 80°C, preferably 0 to 80°C. If the reaction temperature is too high, the reactivity may increase, the molecular weight may increase, and the viscosity of the precursor composition may increase, which may be disadvantageous in terms of the process.
상기한 제조방법에 따라 제조된 폴리아믹산 용액에 필름 형성 공정시의 도포성 등의 공정성을 고려하여 상기 조성물이 적절한 점도를 갖도록 하는 양으로 고형분을 포함하는 것이 바람직하다. It is preferable that the polyamic acid solution prepared according to the above-mentioned production method contains solid content in an amount that ensures that the composition has an appropriate viscosity in consideration of processability such as applicability during the film formation process.
상기 폴리아믹산을 포함하는 폴리이미드 전구체 조성물은 유기용매 중에 용해된 용액의 형태일 수 있으며, 이러한 형태를 갖는 경우, 예를 들어 폴리이미드 전구체를 유기용매 중에서 합성한 경우에는, 용액은 얻어지는 반응용액 그 자체여도 되고, 또는 이 반응 용액을 다른 용매로 희석한 것이어도 된다. 또, 폴리이미드 전구체를 고형 분말로서 얻은 경우에는, 이것을 유기 용매에 용해시켜 용액으로 한 것이어도 된다.The polyimide precursor composition containing the polyamic acid may be in the form of a solution dissolved in an organic solvent. When it has this form, for example, when the polyimide precursor is synthesized in an organic solvent, the solution is the reaction solution obtained. It may be itself, or this reaction solution may be diluted with another solvent. Additionally, when the polyimide precursor is obtained as a solid powder, it may be dissolved in an organic solvent to form a solution.
일 실시예에 따르면, 전체 폴리이미드 전구체의 함량이 8 내지 25 중량%가 되도록 유기용매를 첨가하여 조성물의 함량을 조절할 수 있으며, 바람직하게는 10 내지 25 중량%, 보다 바람직하게는 10 내지 20 중량% 이하로 조절할 수 있다.According to one embodiment, the content of the composition can be adjusted by adding an organic solvent so that the total polyimide precursor content is 8 to 25% by weight, preferably 10 to 25% by weight, more preferably 10 to 20% by weight. It can be adjusted to less than %.
또는, 상기 폴리이미드 전구체 조성물이 3,000cP 이상, 혹은 4,000cP 이상의 점도를 갖도록 조절하는 것일 수 있으며, 상기 폴리이미드 전구체 조성물의 점도는 10,000cP 이하, 바람직하게는 9,000cP 이하, 보다 바람직하게는 8,000cP 이하의 점도를 갖도록 조절하는 것이 바람직하다. 폴리이미드 전구체 조성물의 점도가 10,000cP를 초과할 경우 폴리이미드 필름 가공시 탈포의 효율성이 저하됨으로써, 공정상의 효율뿐만 아니라, 제조된 필름은 기포 발생으로 표면조도가 좋지 않아 전기적, 광학적, 기계적 특성이 저하될 수 있다. Alternatively, the polyimide precursor composition may be adjusted to have a viscosity of 3,000 cP or more, or 4,000 cP or more, and the viscosity of the polyimide precursor composition is 10,000 cP or less, preferably 9,000 cP or less, more preferably 8,000 cP. It is desirable to adjust it to have the following viscosity. If the viscosity of the polyimide precursor composition exceeds 10,000 cP, the efficiency of degassing during polyimide film processing decreases. In addition to process efficiency, the produced film has poor surface roughness due to the generation of bubbles, resulting in poor electrical, optical, and mechanical properties. may deteriorate.
이어서 상기 중합반응의 결과로 수득된 폴리이미드 전구체를 화학적 또는 열적 이미드화 방법을 이용해 이미드화 시킴으로써 투명 폴리이미드 필름을 제조할 수 있다. Next, a transparent polyimide film can be manufactured by imidizing the polyimide precursor obtained as a result of the polymerization reaction using a chemical or thermal imidization method.
일 실시예에 따르면, 폴리이미드 전구체 조성물을 캐리어 기판 상에 도포하는 단계; 및According to one embodiment, applying a polyimide precursor composition on a carrier substrate; and
상기 폴리이미드 전구체 조성물을 가열 및 경화하는 단계를 포함하는 방법으로 폴리이미드 필름을 제조할 수 있다.A polyimide film can be produced by a method that includes heating and curing the polyimide precursor composition.
이때, 상기 캐리어 기판으로는 유리, 금속기판 또는 플라스틱 기판 등이 특별한 제한 없이 사용될 수 있으며, 이 중에서도 폴리이미드 전구체에 대한 이미드화 및 경화공정 중 열 및 화학적 안정성이 우수하고, 별도의 이형제 처리 없이도, 경화 후 형성된 폴리이미드계 필름에 대해 손상 없이 용이하게 분리될 수 있는 유리 기판이 바람직할 수 있다.At this time, the carrier substrate may be a glass, metal substrate, or plastic substrate without any particular restrictions. Among these, it has excellent thermal and chemical stability during the imidization and curing process for the polyimide precursor, and does not require separate treatment with a release agent. A glass substrate that can be easily separated without damage to the polyimide-based film formed after curing may be desirable.
또, 상기 도포 공정은 통상의 도포 방법에 따라 실시될 수 있으며, 구체적으로는 스핀코팅법, 바코팅법, 롤코팅법, 에어-나이프법, 그라비아법, 리버스 롤법, 키스 롤법, 닥터 블레이드법, 스프레이법, 침지법 또는 솔질법 등이 이용될 수 있다. 이중에서도 연속 공정이 가능하며, 폴리이미드의 이미드화율을 증가시킬 수 있는 캐스팅법에 의해 실시되는 것이 보다 바람직할 수 있다.In addition, the application process can be carried out according to a normal application method, specifically, spin coating method, bar coating method, roll coating method, air-knife method, gravure method, reverse roll method, kiss roll method, doctor blade method, Spraying, dipping, or brushing methods may be used. Among these, a continuous process is possible, and it may be more preferable to carry out the casting method, which can increase the imidization rate of polyimide.
또, 상기 폴리이미드 전구체 조성물은 최종 제조되는 폴리이미드 필름이 디스플레이 기판용으로 적합한 두께를 갖도록 하는 두께 범위로 기판 위에 도포될 수 있다.Additionally, the polyimide precursor composition may be applied on the substrate in a thickness range that allows the final polyimide film to have a thickness suitable for a display substrate.
구체적으로는 10 내지 30㎛의 두께가 되도록 하는 양으로 도포될 수 있다. 상기 폴리이미드 전구체 조성물 도포 후, 경화 공정에 앞서 폴리이미드 전구체 조성물 내에 존재하는 용매를 제거하기 위한 건조공정이 선택적으로 더 실시될 수 있다.Specifically, it may be applied in an amount to achieve a thickness of 10 to 30㎛. After applying the polyimide precursor composition, a drying process to remove the solvent present in the polyimide precursor composition may optionally be further performed prior to the curing process.
상기 건조공정은 통상의 방법에 따라 실시될 수 있으며, 구체적으로 140℃이하, 혹은 80℃ 내지 140℃의 온도에서 실시될 수 있다. 건조 공정의 실시 온도가 80℃ 미만이면 건조 공정이 길어지고, 140℃를 초과할 경우 이미드화가 급격히 진행되어 균일한 두께의 폴리이미드 필름 형성이 어렵다.The drying process may be performed according to a conventional method, and may specifically be performed at a temperature of 140°C or less, or 80°C to 140°C. If the drying process temperature is less than 80°C, the drying process becomes longer, and if it exceeds 140°C, imidization progresses rapidly, making it difficult to form a polyimide film of uniform thickness.
이어서, 상기 기판에 도포된 폴리이미드 전구체 조성물은 IR오븐, 열풍오븐이나 핫 플레이트 위에서 열처리되며, 이때, 상기 열처리 온도는 300 내지 500℃, 바람직하게는 320 내지 480℃ 온도범위일 수 있으며, 상기 온도범위 내에서 다단계 가열처리로 진행될 수도 있다. 상기 열처리 공정은 20분 내지 70분 동안 진행될 수 있으며, 바람직하게는 20분 내지 60분 정도의 시간 동안 진행될 수 있다.Subsequently, the polyimide precursor composition applied to the substrate is heat-treated on an IR oven, hot air oven, or hot plate. At this time, the heat treatment temperature may be in the range of 300 to 500°C, preferably 320 to 480°C. It may be carried out as a multi-stage heat treatment within the range. The heat treatment process may be performed for 20 to 70 minutes, and preferably may be performed for 20 to 60 minutes.
상기와 같이 제조된 폴리이미드 필름의 경화 직후 잔류응력은 40MPa 이하일 수 있으며, 상기 폴리이미드 필름을 상기 폴리이미드 필름을 25℃ 50% 습도 조건에서 3시간 방치한 후의 잔류응력 변화값이 5MPa 이하일 수 있다. The residual stress immediately after curing of the polyimide film prepared as described above may be 40 MPa or less, and the residual stress change value after leaving the polyimide film for 3 hours at 25°C and 50% humidity may be 5 MPa or less. .
상기 폴리이미드 필름의 황색도는 15 이하일 수 있으며, 바람직하게는 13 이하일 수 있다. 또한, 상기 폴리이미드 필름의 헤이즈(Haze)는 2이하일 수 있고, 바람직하게는 1 이하일 수 있다.The yellowness of the polyimide film may be 15 or less, and preferably 13 or less. Additionally, the haze of the polyimide film may be 2 or less, and preferably 1 or less.
또한, 상기 폴리이미드 필름의 450 nm에서의 투과도는 75% 이상일 수 있으며, 550 nm에서의 투과도는 85% 이상 일 수 있고, 630 nm에서의 투과도는 90% 이상일 수 있다.Additionally, the transmittance of the polyimide film at 450 nm may be 75% or more, the transmittance at 550 nm may be 85% or more, and the transmittance at 630 nm may be 90% or more.
또한, 상기 폴리이미드 필름의 532nm에서의 면방향 굴절률은 1.73 이상일 수 있으며, 바람직하게는 1.74 이상일 수 있고, 두께 방향 굴절률은 1.53 이상, 바람직하게는 1.54 이상일 수 있다.Additionally, the in-plane refractive index at 532 nm of the polyimide film may be 1.73 or more, preferably 1.74 or more, and the thickness direction refractive index may be 1.53 or more, preferably 1.54 or more.
상기 폴리이미드 필름은 내열성이 높을 수 있으며, 예를 들면, 질량감소가 1% 일어나는 열분해온도(Td_1%)가 500℃ 이상일 수 있다. The polyimide film may have high heat resistance, and for example, the thermal decomposition temperature (Td_1%) at which 1% mass loss occurs may be 500°C or higher.
상기 폴리이미드 필름은 모듈러스가 3 내지 6 GPa일 수 있다. 상기 모듈러스(탄성율)이 0.1Gpa 미만이면, 필름의 강성이 낮아 외부 충격에 쉽게 깨지기 쉽고, 상기 탄성율이 6 GPa을 초과하면, 커버레이 필름의 강성은 우수하지만 충분한 유연성을 확보할 수 없는 문제가 발생할 수 있다.The polyimide film may have a modulus of 3 to 6 GPa. If the modulus (modulus of elasticity) is less than 0.1 GPa, the rigidity of the film is low and it is easily broken by external impact. If the modulus of elasticity is more than 6 GPa, the rigidity of the coverlay film is excellent, but a problem of not being able to secure sufficient flexibility may occur. You can.
또한, 상기 폴리이미드 필름의 연신율은 20% 이상이며, 바람직하게는 50% 이상이며, 인장강도가 130 MPa 이상, 바람직하게는 140 MPa이상일 수 있다.Additionally, the elongation of the polyimide film may be 20% or more, preferably 50% or more, and the tensile strength may be 130 MPa or more, preferably 140 MPa or more.
또한, 본 발명에 따른 폴리이미드 필름은 온도변화에 따른 열안정성이 우수할 수 있으며, 예를 들면, 100℃ 내지 350℃ 온도범위에서 가열 및 냉각 공정을 n+1회 거친 후의 열팽창계수가 -10 내지 100 ppm/℃의 값을 가질 수 있으며, 바람직하게는 -7 내지 90 ppm/℃의 값, 보다 바람직하게는 80 ppm/℃ 이하일 수 있다(이때, n은 0이상의 정수).In addition, the polyimide film according to the present invention may have excellent thermal stability according to temperature changes, for example, the thermal expansion coefficient after going through n+1 heating and cooling processes in the temperature range of 100°C to 350°C is -10. It may have a value of from 100 ppm/℃, preferably -7 to 90 ppm/℃, and more preferably 80 ppm/℃ or less (where n is an integer of 0 or more).
예를 들면, 본 발명에 따른 폴리이미드 필름은 12 ppm/℃ 이하의 CTE값을 가질 수 있으며, 바람직하게는 0 내지 12 ppm/℃의 값을 갖는 것일 수 있다. For example, the polyimide film according to the present invention may have a CTE value of 12 ppm/℃ or less, and preferably may have a value of 0 to 12 ppm/℃.
본 발명의 폴리이미드 필름은 열팽창율이 12ppm/℃ 이하로 낮기 때문에, 온도변화에 의한 필름의 팽창 및 수축 현상이 최소화될 수 있으며, 따라서, 이러한 팽창 및 수축 현상에 의해 발생할 수 있는 기판의 휨과 같은 현상을 감소시킴으로써 유리 기판과 박리되는 등의 공정상의 문제점을 최소화할 수 있다.Since the polyimide film of the present invention has a low thermal expansion rate of 12ppm/℃ or less, the expansion and contraction of the film due to temperature changes can be minimized, and therefore, the bending and shrinkage of the substrate that may occur due to such expansion and contraction phenomena can be minimized. By reducing the same phenomenon, process problems such as delamination from the glass substrate can be minimized.
또한, 본 발명에 따른 폴리이미드 필름은 두께방향 위상차(Rth)가 -150nm 내지 +150nm의 값, 바람직하게는 -130nm 내지 +130nm을 가짐으로써 광학적 등방성을 나타낼 수 있어 시감성이 향상될 수 있다.In addition, the polyimide film according to the present invention can exhibit optical isotropy by having a thickness direction retardation (Rth) of -150 nm to +150 nm, preferably -130 nm to +130 nm, thereby improving visibility.
일 실시예에 따르면, 상기 폴리이미드 필름은 캐리어 기판과의 접착력이 5 gf/in 이상일 수 있으며, 바람직하게는 10 gf/in 이상일 수 있다.According to one embodiment, the polyimide film may have an adhesive force with the carrier substrate of 5 gf/in or more, preferably 10 gf/in or more.
또한, 본 발명은, In addition, the present invention,
상기 폴리이미드 전구체 조성물을 캐리어 기판상에 도포하는 단계;Applying the polyimide precursor composition on a carrier substrate;
상기 폴리이미드 전구체 조성물을 가열하여 폴리아믹산을 이미드화함으로써 폴리이미드 필름을 형성하는 단계; Forming a polyimide film by heating the polyimide precursor composition to imidize the polyamic acid;
상기 폴리이미드 필름 상에 소자를 형성하는 단계; 및forming a device on the polyimide film; and
상기 소자가 형성된 폴리이미드 필름을 상기 캐리어 기판으로부터 박리하는 단계를 포함하는 플렉서블 디바이스의 제조공정을 제공한다.It provides a manufacturing process for a flexible device including the step of peeling the polyimide film on which the device is formed from the carrier substrate.
특히, 상기 플렉서블 디바이스의 제조공정은 LTPS(low temperature polysilicon) 공정, ITO 공정 또는 Oxide 공정을 포함할 수 있다. In particular, the manufacturing process of the flexible device may include a low temperature polysilicon (LTPS) process, an ITO process, or an oxide process.
예를 들면, 폴리이미드 필름상에 SiO2를 포함하는 차단층을 형성하는 단계; For example, forming a blocking layer containing SiO 2 on a polyimide film;
상기 차단층 상에 a-Si(Amorphous silicon)박막을 증착하는 단계;Depositing an a-Si (amorphous silicon) thin film on the blocking layer;
상기 증착된 a-Si박막을 450±50℃의 온도에서 열처리하는 탈수소 어닐링 단계; 및A dehydrogen annealing step of heat treating the deposited a-Si thin film at a temperature of 450±50°C; and
상기 a-Si 박막을 엑시머 레이저 등으로 결정화시키는 단계를 포함하는 LTPS 박막제조공정 이후, 레이저 박리 등으로 캐리어 기판과 폴리이미드 필름을 박리함으로써, LTPS층을 포함하는 플렉서블 디바이스를 얻을 수 있다.After the LTPS thin film manufacturing process including the step of crystallizing the a-Si thin film with an excimer laser, etc., a flexible device including an LTPS layer can be obtained by peeling off the carrier substrate and the polyimide film using laser peeling, etc.
산화물 박막 공정은 실리콘을 이용한 공정에 비해 낮은 온도에서 열처리될 수 있으며, 예를 들면, ITO TFT공정의 열처리 온도는 240℃±50℃일 수 있고, Oxide TFT공정의 열처리 온도는 350℃±50℃일 수 있다.The oxide thin film process can be heat treated at a lower temperature than the process using silicon. For example, the heat treatment temperature for the ITO TFT process can be 240℃±50℃, and the heat treatment temperature for the oxide TFT process can be 350℃±50℃. It can be.
이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 실시예에 대하여 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다.Hereinafter, embodiments of the present invention will be described in detail so that those skilled in the art can easily implement it. However, the present invention may be implemented in many different forms and is not limited to the embodiments described herein.
<합성예 1><Synthesis Example 1>
하기 반응식 1-1과 같은 방법으로 화학식 1-1의 화합물을 제조하였다. The compound of Chemical Formula 1-1 was prepared in the same manner as Scheme 1-1 below.
[반응식 1-1][Reaction Scheme 1-1]
구체적으로, 보로닉애시드를 포함한 출발물질과 브롬을 포함한 출발물질을 테트라히드로퓨란 용매에 용해시키고, 포타슘카보네이트 3당량을 물에 용해시켜서 같이 가열 교반시켰다. 촉매로 테트라키스팔라듐 트리페닐포스핀을 5mol% 사용하였다. TLC를 통해 반응을 확인하였다. 반응이 종료되면 유기층과 수층을 분리해 무수 마그네슘설페이트를 사용해 유기층의 수분을 제거하였다. 감압증류장치를 통해 용매를 증발시키고 컬럼 크로마토그래피를 통해 정제하여 화학식 1-ⅰ의 화합물을 제조하였다.Specifically, the starting material containing boronic acid and the starting material containing bromine were dissolved in a tetrahydrofuran solvent, and 3 equivalents of potassium carbonate were dissolved in water and heated and stirred together. 5 mol% of tetrakispalladium triphenylphosphine was used as a catalyst. The reaction was confirmed through TLC. When the reaction was completed, the organic layer and the aqueous layer were separated, and the moisture in the organic layer was removed using anhydrous magnesium sulfate. The solvent was evaporated through a vacuum distillation device and purified through column chromatography to prepare a compound of Formula 1-i.
상기 카복실릭애시드를 포함하는 화학식 1-ⅰ의 화합물을 무수 톨루엔 용매에 용해시킨 후 티오닐클로라이드(SOCl2)를 천천히 적가하였다. 출발물질이 사라질 때까지 가열 교반한 후, 감압증류를 통해 용매를 제거하고 화학식 1-ⅱ의 화합물을 얻었다. The compound of Formula 1-i containing the carboxylic acid was dissolved in anhydrous toluene solvent, and then thionyl chloride (SOCl 2 ) was slowly added dropwise. After heating and stirring until the starting material disappeared, the solvent was removed through reduced pressure distillation, and the compound of Formula 1-ii was obtained.
상기 화학식 1-ⅱ의 화합물을 포함한 출발물질과 히드록시기 및 니트로기를 포함한 출발물질을 테트라히드로퓨란 용매에 용해시키고 포타슘카보네이트 2당량을 넣어 가열 교반시켜 화학식 1-ⅲ의 화합물을 제조하였다. 반응은 TLC를 통해 확인하고 반응이 종료되면 물을 첨가해 염을 제거한다. 유기층은 무수 마그네슘설페이트를 사용해 수분을 제거하고, 감압 증류장치를 통해 용매를 증발시킨다. 컬럼 크로마토그래피를 통해 정제하였다.The starting material containing the compound of Formula 1-ii and the starting material containing a hydroxy group and a nitro group were dissolved in a tetrahydrofuran solvent, and 2 equivalents of potassium carbonate were added and heated and stirred to prepare a compound of Formula 1-iii. The reaction is confirmed through TLC, and when the reaction is completed, water is added to remove the salt. Moisture is removed from the organic layer using anhydrous magnesium sulfate, and the solvent is evaporated through a reduced pressure distillation device. It was purified through column chromatography.
니트로기를 포함한 화학식 1-ⅲ의 출발물질을 에탄올 용매에 넣고 Pd/C를 3wt% 첨가하였다. 이 후 하이드라진 10당량을 천천히 적가한 후 가열하였다. 반응은 TLC를 통해 확인하고 반응이 종료된 후 상온으로 식혀 필터하였다. 얻어진 고체를 테트라히드로퓨란 용매에 완전히 용해시킨 후 셀라이트를 사용해 다시 필터하여 사용한 Pd/C를 제거하였다. 용매는 감압 증류장치를 통해 제거하고 얻어진 고체를 필터하여 화학식 1-1의 화합물을 얻었다.The starting material of Chemical Formula 1-ⅲ containing a nitro group was placed in an ethanol solvent, and 3 wt% of Pd/C was added. Afterwards, 10 equivalents of hydrazine was slowly added dropwise and heated. The reaction was confirmed through TLC, and after the reaction was completed, it was cooled to room temperature and filtered. The obtained solid was completely dissolved in tetrahydrofuran solvent and then filtered again using Celite to remove the used Pd/C. The solvent was removed through a reduced-pressure distillation device, and the obtained solid was filtered to obtain the compound of Formula 1-1.
<합성예 2><Synthesis Example 2>
하기 반응식 2-1와 같은 방법으로 화학식 1-2의 화합물을 제조하였다. The compound of Chemical Formula 1-2 was prepared in the same manner as Scheme 2-1 below.
[반응식 2-1][Reaction Scheme 2-1]
구체적으로, 보로닉애시드를 포함한 출발물질과 브롬을 포함한 출발물질을 테트라히드로퓨란 용매에 용해시키고, 포타슘카보네이트 3당량을 물에 용해시켜서 같이 가열 교반시켰다. 촉매로 테트라키스팔라듐 트리페닐포스핀을 5mol% 사용하였다. TLC를 통해 반응을 확인하였다. 반응이 종료되면 유기층과 수층을 분리해 무수 마그네슘설페이트를 사용해 유기층의 수분을 제거하였다. 감압증류장치를 통해 용매를 증발시키고 컬럼 크로마토그래피를 통해 정제하여 화학식 2-ⅰ의 화합물을 제조하였다.Specifically, the starting material containing boronic acid and the starting material containing bromine were dissolved in a tetrahydrofuran solvent, and 3 equivalents of potassium carbonate were dissolved in water and heated and stirred together. 5 mol% of tetrakispalladium triphenylphosphine was used as a catalyst. The reaction was confirmed through TLC. When the reaction was completed, the organic layer and the aqueous layer were separated, and the moisture in the organic layer was removed using anhydrous magnesium sulfate. The solvent was evaporated through a vacuum distillation device and purified through column chromatography to prepare a compound of formula 2-i.
상기 카복실릭애시드를 포함하는 화학식 2-ⅰ의 화합물을 무수 톨루엔 용매에 용해시킨 후 티오닐클로라이드(SOCl2)를 천천히 적가하였다. 출발물질이 사라질 때까지 가열 교반한 후, 감압증류를 통해 용매를 제거하고 화학식 2-ⅱ의 화합물을 얻었다. The compound of Formula 2-i containing the carboxylic acid was dissolved in anhydrous toluene solvent, and then thionyl chloride (SOCl 2 ) was slowly added dropwise. After heating and stirring until the starting material disappeared, the solvent was removed through reduced pressure distillation, and the compound of Formula 2-ii was obtained.
상기 화학식 2-ⅱ의 화합물을 포함한 출발물질과 아민기 및 니트로기를 포함한 출발물질을 테트라히드로퓨란 용매에 용해시키고 포타슘카보네이트 2당량을 넣어 가열 교반시켜 화학식 2-ⅲ의 화합물을 제조하였다. 반응은 TLC를 통해 확인하고 반응이 종료되면 물을 첨가해 염을 제거한다. 유기층은 무수 마그네슘설페이트를 사용해 수분을 제거하고, 감압 증류장치를 통해 용매를 증발시킨다. 컬럼 크로마토그래피를 통해 정제하였다.The starting material containing the compound of Formula 2-ii and the starting material containing an amine group and a nitro group were dissolved in a tetrahydrofuran solvent, and 2 equivalents of potassium carbonate were added and heated and stirred to prepare a compound of Formula 2-iii. The reaction is confirmed through TLC, and when the reaction is completed, water is added to remove the salt. Moisture is removed from the organic layer using anhydrous magnesium sulfate, and the solvent is evaporated through a reduced pressure distillation device. It was purified through column chromatography.
니트로기를 포함한 화학식 2-ⅲ의 출발물질을 에탄올 용매에 넣고 Pd/C를 3wt % 첨가하였다. 이 후 하이드라진 10당량을 천천히 적가한 후 가열하였다. 반응은 TLC를 통해 확인하고 반응이 종료된 후 상온으로 식혀 필터하였다. 얻어진 고체를 테트라히드로퓨란 용매에 완전히 용해시킨 후 셀라이트를 사용해 다시 필터하여 사용한 Pd/C를 제거하였다. 용매는 감압 증류장치를 통해 제거하고 얻어진 고체를 필터하여 화학식 1-2의 화합물을 얻었다.The starting material of formula 2-iii containing a nitro group was placed in ethanol solvent and 3 wt % of Pd/C was added. Afterwards, 10 equivalents of hydrazine was slowly added dropwise and heated. The reaction was confirmed through TLC, and after the reaction was completed, it was cooled to room temperature and filtered. The obtained solid was completely dissolved in tetrahydrofuran solvent and then filtered again using Celite to remove the used Pd/C. The solvent was removed through a reduced-pressure distillation device, and the obtained solid was filtered to obtain the compound of Formula 1-2.
<합성예 3><Synthesis Example 3>
하기 반응식 3-1과 같은 방법으로 화학식 1-3의 화합물을 제조하였다. A compound of Chemical Formula 1-3 was prepared in the same manner as Scheme 3-1 below.
[반응식 3-1][Reaction Scheme 3-1]
구체적으로, 보로닉애시드를 포함한 출발물질과 브롬을 포함한 출발물질을 테트라히드로퓨란 용매에 용해시키고, 포타슘카보네이트 3당량을 물에 용해시켜서 같이 가열 교반시켰다. 촉매로 테트라키스팔라듐 트리페닐포스핀을 5mol % 사용하였다. TLC를 통해 반응을 확인하였다. 반응이 종료되면 유기층과 수층을 분리해 무수 마그네슘설페이트를 사용해 유기층의 수분을 제거하였다. 감압증류장치를 통해 용매를 증발시키고 컬럼 크로마토그래피를 통해 정제하여 화학식 3-ⅰ의 화합물을 제조하였다.Specifically, the starting material containing boronic acid and the starting material containing bromine were dissolved in a tetrahydrofuran solvent, and 3 equivalents of potassium carbonate were dissolved in water and heated and stirred together. 5 mol % of tetrakispalladium triphenylphosphine was used as a catalyst. The reaction was confirmed through TLC. When the reaction was completed, the organic layer and the aqueous layer were separated, and the moisture in the organic layer was removed using anhydrous magnesium sulfate. The solvent was evaporated through a vacuum distillation device and purified through column chromatography to prepare a compound of formula 3-i.
상기 화학식 3-ⅰ의 화합물을 포함한 출발물질과 카복실릭애시드 및 니트로기를 포함한 출발물질을 테트라히드로퓨란 용매에 용해시키고 포타슘카보네이트 2당량을 넣어 가열 교반시켜 화학식 3-ⅱ의 화합물을 제조하였다. 반응은 TLC를 통해 확인하고 반응이 종료되면 물을 첨가해 염을 제거한다. 유기층은 무수 마그네슘설페이트를 사용해 수분을 제거하고, 감압 증류장치를 통해 용매를 증발시킨다. 컬럼 크로마토그래피를 통해 정제하였다.The starting material containing the compound of Formula 3-i and the starting material containing carboxylic acid and nitro group were dissolved in tetrahydrofuran solvent, and 2 equivalents of potassium carbonate were added and heated and stirred to prepare the compound of Formula 3-ii. The reaction is confirmed through TLC, and when the reaction is completed, water is added to remove the salt. Moisture is removed from the organic layer using anhydrous magnesium sulfate, and the solvent is evaporated through a reduced pressure distillation device. It was purified through column chromatography.
니트로기를 포함한 화학식 3-ⅱ의 화합물을 에탄올 용매에 넣고 Pd/C를 3wt % 첨가하였다. 이 후 하이드라진 10당량을 천천히 적가한 후 가열하였다. 반응은 TLC를 통해 확인하고 반응이 종료된 후 상온으로 식혀 필터하였다. 얻어진 고체를 테트라히드로퓨란 용매에 완전히 용해시킨 후 셀라이트를 사용해 다시 필터하여 사용한 Pd/C를 제거하였다. 용매는 감압 증류장치를 통해 제거하고 얻어진 고체를 필터하여 화학식 1-3의 화합물을 얻었다.The compound of formula 3-ii containing a nitro group was placed in ethanol solvent and 3 wt % of Pd/C was added. Afterwards, 10 equivalents of hydrazine was slowly added dropwise and heated. The reaction was confirmed through TLC, and after the reaction was completed, it was cooled to room temperature and filtered. The obtained solid was completely dissolved in tetrahydrofuran solvent and then filtered again using Celite to remove the used Pd/C. The solvent was removed through a reduced-pressure distillation device, and the obtained solid was filtered to obtain a compound of Formula 1-3.
<합성예 4><Synthesis Example 4>
하기 반응식 4-1과 같은 방법으로 화학식 1-4의 화합물을 제조하였다. The compound of Chemical Formula 1-4 was prepared in the same manner as Scheme 4-1 below.
[반응식 4-1][Reaction Scheme 4-1]
구체적으로, 보로닉애시드를 포함한 출발물질과 브롬을 포함한 출발물질을 테트라히드로퓨란 용매에 용해시키고, 포타슘카보네이트 3당량을 물에 용해시켜서 같이 가열 교반시켰다. 촉매로 테트라키스팔라듐 트리페닐포스핀을 5mol % 사용하였다. TLC를 통해 반응을 확인하였다. 반응이 종료되면 유기층과 수층을 분리해 무수 마그네슘설페이트를 사용해 유기층의 수분을 제거하였다. 감압증류장치를 통해 용매를 증발시키고 컬럼 크로마토그래피를 통해 정제하여 화학식 4-ⅰ의 화합물을 제조하였다.Specifically, the starting material containing boronic acid and the starting material containing bromine were dissolved in a tetrahydrofuran solvent, and 3 equivalents of potassium carbonate were dissolved in water and heated and stirred together. 5 mol % of tetrakispalladium triphenylphosphine was used as a catalyst. The reaction was confirmed through TLC. When the reaction was completed, the organic layer and the aqueous layer were separated, and the moisture in the organic layer was removed using anhydrous magnesium sulfate. The solvent was evaporated through a reduced pressure distillation device and purified through column chromatography to prepare a compound of formula 4-i.
상기 화학식 4-ⅰ의 화합물과 카복실릭애시드 및 니트로기를 포함한 출발물질을 테트라히드로퓨란 용매에 용해시키고 포타슘카보네이트 2당량을 넣어 가열 교반시켜 화학식 4-ⅱ의 화합물을 제조하였다. 반응은 TLC를 통해 확인하고 반응이 종료되면 물을 첨가해 염을 제거한다. 유기층은 무수 마그네슘설페이트를 사용해 수분을 제거하고, 감압 증류장치를 통해 용매를 증발시킨다. 컬럼 크로마토그래피를 통해 정제하였다.The compound of Formula 4-i and the starting material containing carboxylic acid and nitro group were dissolved in tetrahydrofuran solvent, and 2 equivalents of potassium carbonate were added and heated and stirred to prepare the compound of Formula 4-ii. The reaction is confirmed through TLC, and when the reaction is completed, water is added to remove the salt. Moisture is removed from the organic layer using anhydrous magnesium sulfate, and the solvent is evaporated through a reduced pressure distillation device. It was purified through column chromatography.
니트로기를 포함한 화학식 4-ⅱ의 화합물을 에탄올 용매에 넣고 Pd/C를 3wt % 첨가하였다. 이 후 하이드라진 10당량을 천천히 적가한 후 가열하였다. 반응은 TLC를 통해 확인하고 반응이 종료된 후 상온으로 식혀 필터하였다. 얻어진 고체를 테트라히드로퓨란 용매에 완전히 용해시킨 후 셀라이트를 사용해 다시 필터하여 사용한 Pd/C를 제거하였다. 용매는 감압 증류장치를 통해 제거하고 얻어진 고체를 필터하여 화학식 1-4의 화합물을 얻었다.The compound of formula 4-ii containing a nitro group was placed in ethanol solvent and 3 wt % of Pd/C was added. Afterwards, 10 equivalents of hydrazine was slowly added dropwise and heated. The reaction was confirmed through TLC, and after the reaction was completed, it was cooled to room temperature and filtered. The obtained solid was completely dissolved in tetrahydrofuran solvent and then filtered again using Celite to remove the used Pd/C. The solvent was removed through a reduced-pressure distillation device, and the obtained solid was filtered to obtain a compound of Formula 1-4.
<제조예 1><Manufacturing Example 1>
합성예 1의 방법으로 하기 화합물 1의 디아민을 제조하였다.The diamine of Compound 1 below was prepared by the method of Synthesis Example 1.
HR LC/MS/MS m/z calcd for C34H22N4O4 (M+): 550.1641; found: 550.1644HR LC/MS/MS m/z calcd for C 34 H 22 N 4 O 4 (M+): 550.1641; found: 550.1644
<제조예 2><Production Example 2>
합성예 1의 방법으로 하기 화합물 2의 디아민을 제조하였다.The diamine of Compound 2 below was prepared by the method of Synthesis Example 1.
HR LC/MS/MS m/z calcd for C36H32N2O4 (M+): 556.2362; found: 556.2364HR LC/MS/MS m/z calcd for C 36 H 32 N 2 O 4 (M+): 556.2362; found: 556.2364
<실시예 3><Example 3>
합성예 1의 방법으로 하기 화합물 3의 디아민을 제조하였다.The diamine of Compound 3 below was prepared by the method of Synthesis Example 1.
HR LC/MS/MS m/z calcd for C37H31F3N2O4 (M+): 624.2236; found: 624.2240HR LC/MS/MS m/z calcd for C 37 H 31 F 3 N 2 O 4 (M+): 624.2236; found: 624.2240
<제조예 4><Production Example 4>
합성예 1의 방법으로 하기 화합물 4의 디아민을 제조하였다.The diamine of Compound 4 below was prepared by the method of Synthesis Example 1.
HR LC/MS/MS m/z calcd for C37H22N6O4 (M+): 614.1703; found: 614.1705HR LC/MS/MS m/z calcd for C 37 H 22 N 6 O 4 (M+): 614.1703; found: 614.1705
<제조예 5><Production Example 5>
합성예 2의 방법으로 하기 화합물 5의 디아민을 제조하였다.The diamine of Compound 5 below was prepared by the method of Synthesis Example 2.
HR LC/MS/MS m/z calcd for C36H34N4O2 (M+): 554.2682; found: 554.2683HR LC/MS/MS m/z calcd for C 36 H 34 N 4 O 2 (M+): 554.2682; found: 554.2683
<제조예 6><Production Example 6>
합성예 2의 방법으로 하기 화합물 6의 디아민을 제조하였다.The diamine of Compound 6 below was prepared by the method of Synthesis Example 2.
HR LC/MS/MS m/z calcd for C33H26F2N4O2 (M+): 548.2024; found: 548.2027HR LC/MS/MS m/z calcd for C 33 H 26 F 2 N 4 O 2 (M+): 548.2024; found: 548.2027
<제조예 7><Production Example 7>
합성예 2의 방법으로 하기 화합물 7의 디아민을 제조하였다.The diamine of Compound 7 below was prepared by the method of Synthesis Example 2.
HR LC/MS/MS m/z calcd for C36H22F12N4O2 (M+): 770.1551; found: 770.1554HR LC/MS/MS m/z calcd for C 36 H 22 F 12 N 4 O 2 (M+): 770.1551; found: 770.1554
<제조예 8><Production Example 8>
합성예 2의 방법으로 하기 화합물 8의 디아민을 제조하였다.The diamine of Compound 8 below was prepared by the method of Synthesis Example 2.
HR LC/MS/MS m/z calcd for C33H24F4N4O2 (M+): 584.1835; found: 584.1837HR LC/MS/MS m/z calcd for C 33 H 24 F 4 N 4 O 2 (M+): 584.1835; found: 584.1837
<제조예 9><Production Example 9>
합성예 3의 방법으로 하기 화합물 9의 디아민을 제조하였다.Diamine of compound 9 below was prepared by the method of Synthesis Example 3.
HR LC/MS/MS m/z calcd for C32H22F2N2O4 (M+): 536.1548; found: 536.1550HR LC/MS/MS m/z calcd for C 32 H 22 F 2 N 2 O 4 (M+): 536.1548; found: 536.1550
<제조예 10><Production Example 10>
합성예 3의 방법으로 하기 화합물 10의 디아민을 제조하였다.Diamine of compound 10 below was prepared by the method of Synthesis Example 3.
HR LC/MS/MS m/z calcd for C34H21FN4O4 (M+): 568.1547; found: 568.1549HR LC/MS/MS m/z calcd for C 34 H 21 FN 4 O 4 (M+): 568.1547; found: 568.1549
<제조예 11><Production Example 11>
합성예 3의 방법으로 하기 화합물 11의 디아민을 제조하였다.The diamine of Compound 11 below was prepared by the method of Synthesis Example 3.
HR LC/MS/MS m/z calcd for C36H20F12N2O4 (M+): 772.1231; found: 772.1234HR LC/MS/MS m/z calcd for C 36 H 20 F 12 N 2 O 4 (M+): 772.1231; found: 772.1234
<제조예 12><Production Example 12>
합성예 3의 방법으로 하기 화합물 12의 디아민을 제조하였다.The diamine of Compound 12 below was prepared by the method of Synthesis Example 3.
HR LC/MS/MS m/z calcd for C33H22F4N2O4 (M+): 586.1516; found: 586.1518HR LC/MS/MS m/z calcd for C 33 H 22 F 4 N 2 O 4 (M+): 586.1516; found: 586.1518
<제조예 13><Production Example 13>
합성예 4의 방법으로 하기 화합물 13의 디아민을 제조하였다.The diamine of Compound 13 below was prepared by the method of Synthesis Example 4.
HR LC/MS/MS m/z calcd for C34H24F6N4O2 (M+): 634.1803; found: 634.1806HR LC/MS/MS m/z calcd for C 34 H 24 F 6 N 4 O 2 (M+): 634.1803; found: 634.1806
<제조예 14><Production Example 14>
합성예 4의 방법으로 하기 화합물 14의 디아민을 제조하였다.The diamine of Compound 14 below was prepared by the method of Synthesis Example 4.
HR LC/MS/MS m/z calcd for C33H26Cl2N4O2 (M+): 580.1433; found: 580.1434HR LC/MS/MS m/z calcd for C 33 H 26 Cl 2 N 4 O 2 (M+): 580.1433; found: 580.1434
<제조예 15><Production Example 15>
합성예 4의 방법으로 하기 화합물 15의 디아민을 제조하였다.The diamine of Compound 15 below was prepared by the method of Synthesis Example 4.
HR LC/MS/MS m/z calcd for C34H22F2N6O2 (M+): 584.1772; found: 584.1775HR LC/MS/MS m/z calcd for C 34 H 22 F 2 N 6 O 2 (M+): 584.1772; found: 584.1775
<제조예 16><Production Example 16>
합성예 4의 방법으로 하기 화합물 16의 디아민을 제조하였다.The diamine of Compound 16 below was prepared by the method of Synthesis Example 4.
HR LC/MS/MS m/z calcd for C35H30Cl2N4O2 (M+): 608.1746; found: 608.1749HR LC/MS/MS m/z calcd for C 35 H 30 Cl 2 N 4 O 2 (M+): 608.1746; found: 608.1749
<비교예 1><Comparative Example 1>
질소 기류가 흐르는 교반기 내에 유기용매 DEAc를 채운 후, 반응기의 온도를 25℃로 유지한 상태에서 TFMB(2,2'-Bis(trifluoromethyl)benzidine) 1.672mol을 같은 온도에서 첨가하여 용해시켰다. 상기 TFMB가 첨가된 용액에 BPDA 1.672mol을 같은 온도에서 첨가하여 24시간동안 교반하여 폴리이미드 전구체 조성물을 얻었다.After filling the organic solvent DEAc in a stirrer with a nitrogen stream flowing, 1.672 mol of TFMB (2,2'-Bis(trifluoromethyl)benzidine) was added and dissolved at the same temperature while maintaining the temperature of the reactor at 25°C. 1.672 mol of BPDA was added to the solution containing TFMB at the same temperature and stirred for 24 hours to obtain a polyimide precursor composition.
<비교예 2><Comparative Example 2>
질소 기류가 흐르는 교반기 내에 유기용매 DEAc를 채운 후, 반응기의 온도를 25℃로 유지한 상태에서 BAPT 1.537 mol을 같은 온도에서 첨가하여 용해시켰다. 상기 BAPB가 첨가된 용액에 BPDA 1.537 mol을 같은 온도에서 첨가하여 24시간동안 교반하여 폴리이미드 전구체 조성물을 얻었다.After filling the organic solvent DEAc in a stirrer with a nitrogen stream flowing, while maintaining the temperature of the reactor at 25°C, 1.537 mol of BAPT was added and dissolved at the same temperature. 1.537 mol of BPDA was added to the solution containing BAPB at the same temperature and stirred for 24 hours to obtain a polyimide precursor composition.
<실시예 1><Example 1>
질소 기류가 흐르는 교반기 내에 유기용매 DEAc를 채운 후, 반응기의 온도를 25℃로 유지한 상태에서 상기 화합물 1의 디아민 0.973mol을 같은 온도에서 첨가하여 용해시켰다. 상기 화합물 1의 디아민이 첨가된 용액에 BPDA 0.973 mol을 같은 온도에서 첨가하여 24시간동안 교반하여 폴리이미드 전구체 조성물을 얻었다.After filling the organic solvent DEAc in a stirrer with a nitrogen stream flowing, while maintaining the temperature of the reactor at 25°C, 0.973 mol of the diamine of Compound 1 was added and dissolved at the same temperature. 0.973 mol of BPDA was added to the diamine solution of Compound 1 at the same temperature and stirred for 24 hours to obtain a polyimide precursor composition.
<실시예 2><Example 2>
질소 기류가 흐르는 교반기 내에 유기용매 DEAc를 채운 후, 반응기의 온도를 25℃로 유지한 상태에서 상기 화합물 2의 디아민 0.962mol을 같은 온도에서 첨가하여 용해시켰다. 상기 화합물 2의 디아민이 첨가된 용액에 BPDA 0.962mol을 같은 온도에서 첨가하여 24시간동안 교반하여 폴리이미드 전구체 조성물을 얻었다.After filling the organic solvent DEAc in a stirrer with a nitrogen stream flowing, while maintaining the temperature of the reactor at 25°C, 0.962 mol of the diamine of Compound 2 was added and dissolved at the same temperature. 0.962 mol of BPDA was added to the diamine solution of Compound 2 at the same temperature and stirred for 24 hours to obtain a polyimide precursor composition.
<실시예 3><Example 3>
질소 기류가 흐르는 교반기 내에 유기용매 DEAc를 채운 후, 반응기의 온도를 25℃로 유지한 상태에서 상기 화합물 5의 디아민 0.965mol을 같은 온도에서 첨가하여 용해시켰다. 상기 화합물 5의 디아민이 첨가된 용액에 BPDA 0.965mol을 같은 온도에서 첨가하여 24시간동안 교반하여 폴리이미드 전구체 조성물을 얻었다.After filling the organic solvent DEAc in a stirrer with a nitrogen stream flowing, while maintaining the temperature of the reactor at 25°C, 0.965 mol of the diamine of Compound 5 was added and dissolved at the same temperature. 0.965 mol of BPDA was added to the diamine solution of Compound 5 at the same temperature and stirred for 24 hours to obtain a polyimide precursor composition.
<실시예 4><Example 4>
질소 기류가 흐르는 교반기 내에 유기용매 DEAc를 채운 후, 반응기의 온도를 25℃로 유지한 상태에서 상기 화합물 8의 디아민 0.916mol을 같은 온도에서 첨가하여 용해시켰다. 상기 화합물 8의 디아민이 첨가된 용액에 BPDA 0.916mol을 같은 온도에서 첨가하여 24시간동안 교반하여 폴리이미드 전구체 조성물을 얻었다.After filling the organic solvent DEAc in a stirrer with a nitrogen stream flowing, while maintaining the temperature of the reactor at 25°C, 0.916 mol of the diamine of Compound 8 was added and dissolved at the same temperature. 0.916 mol of BPDA was added to the diamine solution of Compound 8 at the same temperature and stirred for 24 hours to obtain a polyimide precursor composition.
<실시예 5><Example 5>
질소 기류가 흐르는 교반기 내에 유기용매 DEAc를 채운 후, 반응기의 온도를 25℃로 유지한 상태에서 상기 화합물 10의 디아민 0.942mol을 같은 온도에서 첨가하여 용해시켰다. 상기 화합물 10의 디아민이 첨가된 용액에 BPDA 0.942mol을 같은 온도에서 첨가하여 24시간동안 교반하여 폴리이미드 전구체 조성물을 얻었다.After filling the organic solvent DEAc in a stirrer with a nitrogen stream flowing, while maintaining the temperature of the reactor at 25°C, 0.942 mol of the diamine of compound 10 was added and dissolved at the same temperature. 0.942 mol of BPDA was added to the diamine solution of Compound 10 at the same temperature and stirred for 24 hours to obtain a polyimide precursor composition.
<실시예 6><Example 6>
질소 기류가 흐르는 교반기 내에 유기용매 DEAc를 채운 후, 반응기의 온도를 25℃로 유지한 상태에서 상기 화합물 11의 디아민 0.693 mol을 같은 온도에서 첨가하여 용해시켰다. 상기 화합물 11의 디아민이 첨가된 용액에 BPDA 0.693 mol을 같은 온도에서 첨가하여 24시간동안 교반하여 폴리이미드 전구체 조성물을 얻었다.After filling the organic solvent DEAc in a stirrer with a nitrogen stream flowing, while maintaining the temperature of the reactor at 25°C, 0.693 mol of the diamine of Compound 11 was added and dissolved at the same temperature. 0.693 mol of BPDA was added to the diamine solution of Compound 11 at the same temperature and stirred for 24 hours to obtain a polyimide precursor composition.
<실시예 7><Example 7>
질소 기류가 흐르는 교반기 내에 유기용매 DEAc를 채운 후, 반응기의 온도를 25℃로 유지한 상태에서 상기 화합물 13의 디아민 0.844 mol을 같은 온도에서 첨가하여 용해시켰다. 상기 화합물 13의 디아민이 첨가된 용액에 BPDA 0.844 mol을 같은 온도에서 첨가하여 24시간동안 교반하여 폴리이미드 전구체 조성물을 얻었다.After filling the organic solvent DEAc in a stirrer with a nitrogen stream flowing, while maintaining the temperature of the reactor at 25°C, 0.844 mol of the diamine of Compound 13 was added and dissolved at the same temperature. 0.844 mol of BPDA was added to the diamine solution of Compound 13 at the same temperature and stirred for 24 hours to obtain a polyimide precursor composition.
<실시예 8><Example 8>
질소 기류가 흐르는 교반기 내에 유기용매 DEAc를 채운 후, 반응기의 온도를 25℃로 유지한 상태에서 상기 화합물 16의 디아민 0.880mol을 같은 온도에서 첨가하여 용해시켰다. 상기 화합물 16의 디아민이 첨가된 용액에 BPDA 0.880mol을 같은 온도에서 첨가하여 24시간동안 교반하여 폴리이미드 전구체 조성물을 얻었다.After filling the organic solvent DEAc in a stirrer with a nitrogen stream flowing, while maintaining the temperature of the reactor at 25°C, 0.880 mol of the diamine of Compound 16 was added and dissolved at the same temperature. 0.880 mol of BPDA was added to the diamine solution of Compound 16 at the same temperature and stirred for 24 hours to obtain a polyimide precursor composition.
<실험예 1> <Experimental Example 1>
실시예 1 내지 8 및 비교예 1, 2에서 제조된 각각의 폴리이미드 전구체 용액을 유리기판 상에 스핀 코팅하였다. 폴리이미드 전구체 용액이 도포된 유리 기판을 오븐에 넣고 5℃/min의 속도로 가열하였으며, 80℃에서 30분, 300℃에서 30분을 유지하여 경화 공정을 진행하여 폴리이미드 필름을 제조하였다. Each of the polyimide precursor solutions prepared in Examples 1 to 8 and Comparative Examples 1 and 2 were spin-coated on a glass substrate. The glass substrate coated with the polyimide precursor solution was placed in an oven and heated at a rate of 5°C/min, and a curing process was performed by maintaining the temperature at 80°C for 30 minutes and 300°C for 30 minutes to prepare a polyimide film.
각각의 필름에 대한 물성을 측정하여 하기 표 1에 나타내었다.The physical properties of each film were measured and shown in Table 1 below.
<투과도><Transmittance>
투과도는 JIS K 7105에 의거하여 투과율계(모델명 HR-100, Murakami Color Research Laboratory 제조)로 450nm 파장에 대한 투과율을 측정하였다.Transmittance was measured at a wavelength of 450 nm using a transmittance meter (model name HR-100, manufactured by Murakami Color Research Laboratory) in accordance with JIS K 7105.
<굴절률 측정> <Measurement of refractive index>
상기 제조된 폴리이미드 필름을 박리하여 프리즘커플러(SPA-3DR) 측정장비를 이용하여 532nm 파장에서 면방향 및 두께방향 굴절률을 측정하였다.The polyimide film prepared above was peeled off and the refractive index in the plane direction and thickness direction was measured at a wavelength of 532 nm using a prism coupler (SPA-3DR) measuring device.
<유리전이온도(Tg) 및 열팽창계수(CTE)><Glass transition temperature (Tg) and coefficient of thermal expansion (CTE)>
필름을 5 x 20 mm 크기로 준비한 뒤 악세서리를 이용하여 시료를 로딩한다. 실제 측정되는 필름의 길이는 16mm로 동일하게 하였다. 필름을 당기는 힘을 0.02N으로 설정하고 100 내지 350℃ 온도 범위에서 5℃/min 의 승온 속도로 1차 승온 공정을 진행한 후, 350 내지 100℃의 온도 범위에서 4℃/min 의 냉각 속도로 냉각(cooling) 공정을 진행하여 열팽창 변화 양상을 TMA(TA 사의 Q400)로 측정하였다.Prepare a film with a size of 5 x 20 mm and load the sample using the accessory. The actual length of the film measured was the same at 16 mm. The force pulling the film was set to 0.02N and the first temperature increase process was performed at a temperature increase rate of 5°C/min in the temperature range of 100 to 350°C, followed by a cooling rate of 4°C/min in the temperature range of 350 to 100°C. A cooling process was performed and the thermal expansion change pattern was measured using TMA (Q400 from TA).
<열분해 온도(Td_1%) 측정><Measurement of thermal decomposition temperature (Td_1%)>
열중량 분석 장치(TGA, TG-DTA2000)를 이용하여, 질소 중 승온 속도 10℃/분으로의 승온하면서 폴리이미드 필름의 초기 중량이 1% 감소했을 때의 온도를 측정하였다.Using a thermogravimetric analysis device (TGA, TG-DTA2000), the temperature when the initial weight of the polyimide film decreased by 1% was measured while increasing the temperature in nitrogen at a temperature increase rate of 10°C/min.
표 1의 결과로부터, 본 발명에 따른 디아민을 포함하는 실시예 1 내지 8의 폴리이미드는 비교예 1및 2에 비해 두께방향 및 면방향의 굴절률이 높게 나타나는 것을 알 수 있다. From the results in Table 1, it can be seen that the polyimides of Examples 1 to 8 containing diamine according to the present invention have higher refractive indices in the thickness direction and the surface direction compared to Comparative Examples 1 and 2.
일반적으로 고투과 폴리이미드 필름의 경우 굴절률이 n=1.65 이하 인데, 폴리이미드층으로 빛이 방출될 때, 상기 무기막을 포함하는 상부층의 굴절율(n=1.8 이상)과 폴리이미드층의 굴절률의 차이에 의해 방출 효율이 감소할 수 있다.Generally, in the case of a high-transmission polyimide film, the refractive index is n = 1.65 or less. When light is emitted into the polyimide layer, the refractive index of the upper layer containing the inorganic film (n = 1.8 or more) and the refractive index of the polyimide layer are changed. Emission efficiency may be reduced.
본 발명에 따른 디아민을 포함하는 폴리이미드 필름은 내열성과 같은 물성특성을 최대한 유지시키면서, 면방향 및 두께방향 굴절률을 향상시킴으로써, 상부층과의 굴절률 차이를 줄여줌으로써 내부에서 소멸되는 빛의 양을 감소시킬 수 있어 플렉서블 디스플레이 소자에서 기판층으로의 빛 방출(bottom emission) 효율을 증대시킬 수 있다.The polyimide film containing diamine according to the present invention can reduce the amount of light extinguished inside by reducing the difference in refractive index with the upper layer by improving the refractive index in the plane direction and the thickness direction while maintaining physical properties such as heat resistance as much as possible. This can increase the efficiency of light emission from the flexible display device to the substrate layer.
또한, 본 발명의 폴리이미드 필름은 열팽창율이 12ppm/℃ 이하로 낮기 때문에, 온도변화에의한 필름의 팽창 및 수축 현상이 최소화시킴으로써, 유리 기판과 박리되는 등의 공정상의 문제점을 최소화할 수 있다.In addition, since the polyimide film of the present invention has a low thermal expansion rate of 12ppm/℃ or less, the expansion and contraction of the film due to temperature changes are minimized, thereby minimizing process problems such as delamination from the glass substrate. .
이상으로 본 발명 내용의 특정한 부분을 상세히 기술하였는바, 당업계의 통상의 지식을 가진 자에게 있어서, 이러한 구체적 기술은 단지 바람직한 실시 양태일 뿐이며, 이에 의해 본 발명의 범위가 제한되는 것이 아닌 점은 명백할 것이다. 따라서 본 발명의 실질적인 범위는 첨부된 청구항들과 그것들의 등가물에 의하여 정의된다고 할 것이다. As the specific parts of the present invention have been described in detail above, it is clear to those skilled in the art that these specific techniques are merely preferred embodiments and do not limit the scope of the present invention. something to do. Accordingly, the actual scope of the present invention will be defined by the appended claims and their equivalents.
Claims (15)
[화학식 1-1]
[화학식 1-2]
[화학식 1-3]
[화학식 1-4]
상기 화학식 1-1 내지 1-4에 있어서,
R1 내지 R5는 각각 독립적으로 -F, -Cl, -Br 및 -I로부터 선택되는 할로겐 원자, 시아노기(-CN), 탄소수 1 내지 5의 알킬기, 탄소수 1 내지 5의 할로게노알킬기이고,
n1 내지 n5는 각각 독립적으로 0 내지 4의 정수이고, n1+n2+n3+n4+n5는 0이 아니다.Diamine having a structure selected from the following formulas 1-1 to 1-4:
[Formula 1-1]
[Formula 1-2]
[Formula 1-3]
[Formula 1-4]
In Formulas 1-1 to 1-4,
R 1 to R 5 are each independently a halogen atom selected from -F, -Cl, -Br and -I, a cyano group (-CN), an alkyl group with 1 to 5 carbon atoms, or a halogenoalkyl group with 1 to 5 carbon atoms,
n1 to n5 are each independently an integer from 0 to 4, and n1+n2+n3+n4+n5 is not 0.
[반응식 1]
상기 반응식 1에 있어서, R1 내지 R5 및 n1 내지 n5의 정의는 제1항에서 정의된 것과 동일하다.Method for producing diamine of Chemical Formula 1-1 through the reaction shown in Scheme 1 below:
[Scheme 1]
In Scheme 1, the definitions of R 1 to R 5 and n1 to n5 are the same as those defined in claim 1.
[반응식 2]
상기 반응식 2에 있어서, R1 내지 R5 및 n1 내지 n5의 정의는 제1항에서 정의된 것과 동일하다.Method for producing diamine of Chemical Formula 1-2 through the reaction shown in Scheme 2 below:
[Scheme 2]
In Scheme 2, the definitions of R 1 to R 5 and n1 to n5 are the same as those defined in claim 1.
[반응식 3]
상기 반응식 3에 있어서, R1 내지 R5 및 n1 내지 n5의 정의는 제1항에서 정의된 것과 동일하다.Method for producing diamine of Chemical Formula 1-3 through the reaction shown in Scheme 3 below:
[Scheme 3]
In Scheme 3, the definitions of R 1 to R 5 and n1 to n5 are the same as those defined in claim 1.
[반응식 4]
상기 반응식 4에 있어서, R1 내지 R5 및 n1 내지 n5의 정의는 제1항에서 정의된 것과 동일하다.Method for producing diamine of the following formula 1-4 through the reaction shown in the following reaction formula 4:
[Scheme 4]
In Scheme 4, the definitions of R 1 to R 5 and n1 to n5 are the same as those defined in claim 1.
상기 디아민이 제1항의 디아민을 포함하는 것인 폴리이미드 전구체.A polyimide precursor obtained by polymerizing a polymerization component containing one or more diamines and one or more acid dianhydrides,
A polyimide precursor wherein the diamine includes the diamine of claim 1.
상기 폴리이미드 필름은 면방향 굴절률이 1.73 이상이고, 두께 방향 굴절률이 1.53 이상인 폴리이미드 필름.According to clause 9,
The polyimide film has a plane direction refractive index of 1.73 or more and a thickness direction refractive index of 1.53 or more.
상기 폴리이미드 필름은 열팽창계수(CTE)가 12 ppm/℃ 이하인 폴리이미드 필름.According to clause 9,
The polyimide film has a coefficient of thermal expansion (CTE) of 12 ppm/℃ or less.
상기 폴리이미드 전구체 조성물을 가열 및 경화하는 단계를 포함하는 폴리이미드 필름 제조 방법.Applying a polyimide precursor composition containing the polyimide precursor according to claim 8 on a carrier substrate; and
A method of producing a polyimide film comprising heating and curing the polyimide precursor composition.
상기 폴리이미드 전구체 조성물을 가열하여 폴리아믹산을 이미드화함으로써 폴리이미드 필름을 형성하는 단계;
상기 폴리이미드 필름 상에 소자를 형성하는 단계; 및
상기 소자가 형성된 폴리이미드 필름을 상기 캐리어 기판으로부터 박리하는 단계를 포함하는 플렉서블 디바이스의 제조공정.Applying a polyimide precursor composition containing the polyimide precursor of claim 8 on a carrier substrate;
Forming a polyimide film by heating the polyimide precursor composition to imidize polyamic acid;
forming a device on the polyimide film; and
A manufacturing process of a flexible device comprising the step of peeling the polyimide film on which the device is formed from the carrier substrate.
상기 제조공정이 LTPS(저온 폴리실리콘) 공정, ITO 공정 또는 Oxide 공정을 포함하는 것인 플렉서블 디바이스의 제조공정.
According to clause 14,
A manufacturing process of a flexible device, wherein the manufacturing process includes a LTPS (low temperature polysilicon) process, an ITO process, or an oxide process.