KR102548315B1 - Packaging material for desiccant and moisture absorption product containing same - Google Patents
Packaging material for desiccant and moisture absorption product containing same Download PDFInfo
- Publication number
- KR102548315B1 KR102548315B1 KR1020220072740A KR20220072740A KR102548315B1 KR 102548315 B1 KR102548315 B1 KR 102548315B1 KR 1020220072740 A KR1020220072740 A KR 1020220072740A KR 20220072740 A KR20220072740 A KR 20220072740A KR 102548315 B1 KR102548315 B1 KR 102548315B1
- Authority
- KR
- South Korea
- Prior art keywords
- moisture
- moisture absorbent
- packaging material
- polyolefin
- moisture absorption
- Prior art date
Abstract
본 발명은 흡습제용 포장재 및 이를 포함하는 흡습제품을 제공하는 것이며, 구체적으로 폴리에스테르 부직포 층, 폴리올레핀 통기성 층, 폴리올레핀계 천공필름층을 포함하는 흡습제용 포장재로서,상기 각 층은 폴리우레탄계 접착제 층을 더 포함하는 것인, 흡습제용 포장재를 제공 및 이를 포함하는 흡습제품을 제공하는 것이다.The present invention provides a packaging material for a desiccant and a moisture absorbing product including the same, and specifically, a packaging material for a desiccant comprising a polyester nonwoven fabric layer, a polyolefin breathable layer, and a polyolefin perforated film layer, each layer comprising a polyurethane-based adhesive layer. It is to provide a packaging material for a moisture absorbent, which further includes, and to provide a moisture absorbent product including the same.
Description
본 발명은 흡습제용 포장재 및 이를 포함하는 흡습제품을 제공하는 것이며, 구체적으로, 투습도 및 걸리투과도가 우수하고 흡습속도 조절이 용이하면서 동시에 인장강도 또한 우수한 흡습제용 포장재를 제공하는 것이다.The present invention provides a packaging material for a moisture absorbent and a moisture absorption product including the same, and specifically, to provide a packaging material for a moisture absorbent having excellent moisture permeability and Gurley transmittance, easy moisture absorption rate control, and excellent tensile strength.
일반적으로 흡습제품은 제품의 포장 또는 운송 시 습기로부터 제품을 보호하기 위하여 포장용 박스 내에 투입되어 널리 사용되고 있으며, 종래에는 자동차 램프, 전자기 제품 등의 습도제어가 필요한 제품에도 널리 사용되고 있다.In general, hygroscopic products are widely used in packaging boxes to protect products from moisture during packaging or transportation, and are conventionally widely used in products requiring humidity control such as automobile lamps and electronic products.
상기 흡습제품은 파우치에 흡습제를 투입된 형태의 제품이 주로 사용되며, 특수 용도로는 더스트 커버 용기 내부에 흡습제를 포함하고 이를 통기성 필름으로 덮힌 제품(등록번호 10-2245735 B1)등이 사용되고 있다.As for the moisture absorbent product, a product in which a moisture absorbent is put into a pouch is mainly used, and for special use, a product containing a moisture absorbent inside a dust cover container and covering it with a breathable film (Registration No. 10-2245735 B1) is used.
상기 흡습제품에 들어가는 통기성 필름은 외부의 습기를 효과적으로 흡수할 수 있게 통기성은 우수하면서, 동시에 흡습속도는 제어하여, 상기 흡습제품이 장기간 동안 주변 습기를 흡습할 수 있는 효과적인 기능이 요구된다.The breathable film included in the moisture absorbent product has excellent air permeability so as to effectively absorb external moisture, and at the same time controls the moisture absorption rate, so that the moisture absorbent product has an effective function of absorbing ambient moisture for a long period of time.
또한, 상기 통기성 필름의 경우 자동차의 진동 및 운송에 따른 물리적인 충격에도 견딜 수 있는 물리적 강도 또한 우수한 재질을 사용해야 한다.In addition, in the case of the air permeable film, a material having excellent physical strength capable of withstanding physical shock caused by vibration and transportation of a vehicle should be used.
종래기술은 흡습제를 충진하는 흡습제품의 포장재로 PP 또는 PE 통기성 필름(부직포)에 EVA, polyurethane 등의 코팅을 하여 흡습속도를 조절하고 이 코팅제부분이 접합을 하여 파우치 형태로 만들어 접합강도(0.05kgf/mm)가 상대적으로 낮은 문제점이 있다. 또한, PP 또는 PE 통기성 필름(부직포) 자체의 모든 부분이 투습도가 일정하지 않아 일정 수준 이상의 투습도를 보증할 수 없는 문제점이 있다.The prior art is a packaging material for a moisture absorbing product that fills a moisture absorbent, and a PP or PE breathable film (non-woven fabric) is coated with EVA, polyurethane, etc. to control the moisture absorption rate, and the coating agent is bonded to form a pouch to increase the bonding strength (0.05 kgf /mm) is relatively low. In addition, there is a problem in that all parts of the PP or PE breathable film (non-woven fabric) itself cannot guarantee a certain level of moisture permeability because the moisture permeability is not constant.
상기 안출된 문제점을 해결하기 위해, 본 발명은 일정한 흡습속도를 가지며, 접합강도 또한 우수한 흡습제용 포장재를 제공하고자 한다.In order to solve the above problems, the present invention is to provide a packaging material for a moisture absorbent having a constant moisture absorption rate and excellent bonding strength.
또한, 본 발명은 통기성 필름에 추가적인 수지 코팅 없이도 접착이 용이한 흡습제용 포장재를 제공하고자 한다.In addition, the present invention is to provide a packaging material for a moisture absorbent that is easily adhered to a breathable film without additional resin coating.
또한, 본 발명은 자동차 진동 또는 외부의 물리적인 충격 등에도 견딜 수 있는 흡습제용 포장재를 제공하고자 한다.In addition, the present invention is to provide a packaging material for a moisture absorbent that can withstand automobile vibration or external physical shock.
또한, 본 발명은 상기 흡습제품용 포장제품을 사용한 흡습제 파우치를 제공하고자 한다.In addition, the present invention is to provide a moisture absorbent pouch using the packaging product for moisture absorption products.
또한, 본 발명은 상기 흡습제품용 포장제품을 사용한 더스트 커버 용기 내부에 흡습제를 포함하고 이를 통기성 필름으로 덮힌 제품을 제공하고자 한다.In addition, the present invention is to provide a product containing a moisture absorbent inside a dust cover container using the packaging product for moisture absorption products and covered with a breathable film.
상기 안출된 문제점을 해결하기 위해서, 본 발명은 폴리에스테르 부직포 층, 폴리올레핀 통기성 층, 폴리올레핀계 천공필름층을 포함하는 흡습제용 포장재으로서, 상기 각 층은 폴리우레탄계 접착제 층을 더 포함하는 것인, 흡습제용 포장재를 제공한다.In order to solve the above problems, the present invention is a packaging material for a moisture absorbent comprising a polyester nonwoven fabric layer, a polyolefin breathable layer, and a polyolefin perforated film layer, wherein each layer further comprises a polyurethane adhesive layer, the moisture absorbent packaging materials are provided.
본 발명의 일 양태에 따른, 상기 흡습제용 포장재의 걸리투과도는 500 내지 1500 초이고, 투습도는 500 내지 1,500 g/m2인 것일 수 있다.According to one aspect of the present invention, the desiccant packaging material may have a Gurley transmittance of 500 to 1500 seconds and a moisture permeability of 500 to 1,500 g/m 2 .
본 발명의 일 양태에 따른, 상기 폴리 올레핀계 천공필름은 1 내지 500 개/cm2의 천공이 형성된 폴리 올레핀계 천공필름인 것일 수 있다.According to one aspect of the present invention, the polyolefin-based perforated film may be a polyolefin-based perforated film in which 1 to 500 perforations/cm 2 are formed.
본 발명의 일 양태에 따른, 상기 폴리 올레핀계 천공필름은 8 내지 30 개/cm2의 천공이 형성된 폴리 올레핀계 천공필름인 것일 수 있다.According to one aspect of the present invention, the polyolefin-based perforated film may be a polyolefin-based perforated film in which 8 to 30 perforations/cm 2 are formed.
본 발명의 일 양태에 따른, 상기 폴리 올레핀계 천공필름은 천공의 평균 직경이 0.01 내지 2.0 mm일 수 있다.According to one aspect of the present invention, the polyolefin-based perforated film may have an average diameter of perforations of 0.01 to 2.0 mm.
본 발명의 일 양태에 따른, 상기 폴리 올레핀계 천공필름은 천공율이 0.1 내지 50%일 수 있다.According to one aspect of the present invention, the polyolefin-based perforated film may have a perforation rate of 0.1 to 50%.
본 발명의 일 양태에 따른, 상기 흡습제용 포장재의 걸리투과도는 500 내지 800 초이고, 투습도가 1,000 내지 1,500 g/m2인 것일 수 있다.According to one aspect of the present invention, the moisture absorbent packaging material may have a Gurley permeability of 500 to 800 seconds and a moisture permeability of 1,000 to 1,500 g/m 2 .
본 발명의 일 양태에 따른, 상기 흡습제용 포장재의 걸리투과도는 800 내지 1,400 초이고, 투습도가 600 내지 800 g/m2인 것일 수 있다.According to one aspect of the present invention, the packaging material for the moisture absorbent may have a Gurley transmittance of 800 to 1,400 seconds and a moisture permeability of 600 to 800 g/m 2 .
본 발명의 일 양태에 따른, 상기 폴리우레탄계 접착제는 폴리에스테르계 폴리올과 폴리에테르계 폴리올로부터 유래된 폴리우레탄 접착제인 것일 수 있다.According to one aspect of the present invention, the polyurethane adhesive may be a polyurethane adhesive derived from a polyester polyol and a polyether polyol.
본 발명의 일 양태에 따른, 상기 폴리우레탄계 접착제는 스크린 인쇄, 돗트(DOT)인쇄, 스프레이 인쇄 및 패터닝(patterning) 도포에 의해 코팅하는 것일 수 있다.According to one aspect of the present invention, the polyurethane-based adhesive may be coated by screen printing, dot (DOT) printing, spray printing, and patterning application.
본 발명의 일 양태에 따른, 상기 흡습제용 포장재를 일면 또는 양면으로 하여 흡습제를 포장한 흡습제품을 제공할 수 있다.According to one aspect of the present invention, a moisture absorbing product in which a moisture absorbing agent is packaged by using one or both sides of the moisture absorbing packaging material may be provided.
본 발명의 일 양태에 따른, 상기 흡습제는 (A) 염화마그네슘, 염화칼슘 및 탄산나트륨으로 이루어진 군으로부터 선택된 적어도 하나 또는 둘 이상의 흡습물질; (B) 산화마그네슘 및 산화칼슘으로 이루어진 군으로부터 선택된 적어도 하나 이상을 포함하는 경화성 무기물을 포함하는 것일 수 있다.According to one aspect of the present invention, the moisture absorbent is (A) at least one or two or more moisture absorbents selected from the group consisting of magnesium chloride, calcium chloride and sodium carbonate; (B) may include a curable inorganic material including at least one selected from the group consisting of magnesium oxide and calcium oxide.
본 발명의 일 양태에 따른, 상기 흡습제는 (A) 흡습물질 10 내지 50 중량% 및 (B) 경화성 무기물 50 내지 90 중량%인 것을 포함하는 흡습제품일 수 있다.According to one aspect of the present invention, the moisture absorbing agent may be a moisture absorbing product including (A) 10 to 50% by weight of a moisture absorbing material and (B) 50 to 90% by weight of a curable inorganic material.
본 발명의 일 양태에 따른, 상기 흡습제는 고분자 왁스를 더 포함하는 것일 수 있다.According to one aspect of the present invention, the moisture absorbent may further include a polymer wax.
본 발명의 일 양태에 따른, 상기 흡습제는 알칼리 금속 인산염을 더 포함하는 것일 수 있다.According to one aspect of the present invention, the moisture absorbent may further include an alkali metal phosphate.
본 발명의 일 양태에 따른, 상기 흡습제품은 흡습율이 100% 이상인, 흡습속도가 1 내지 10 %/2시간 인 것일 수 있다.According to one aspect of the present invention, the moisture absorption product may have a moisture absorption rate of 100% or more and a moisture absorption rate of 1 to 10%/2 hours.
흡습제품의 포장재로 본 발명의 흡습제용 포장재를 사용함으로써, 상기 흡습제품의 흡습속도를 효과적으로 제어할 수 있다. By using the packaging material for a moisture absorbent of the present invention as a packaging material for a moisture absorption product, the moisture absorption rate of the moisture absorption product can be effectively controlled.
또한, 상기 흡습제용 포장재에 추가적인 수지 코팅 없이도 접착이 용이하여 흡습제품의 제조공정이 단순화되는 장점이 있다.In addition, it is easy to adhere to the packaging material for the moisture absorbent without additional resin coating, thereby simplifying the manufacturing process of the moisture absorbent product.
또한, 본 발명의 흡습제용 포장재는 인장강도 및 신율이 우수하여, 외부의 충격 등에도 터지거나 찢어지지 않아, 내부의 흡습제가 외부로 토출되는 것을 막을 수 있다.In addition, the packaging material for a moisture absorbent of the present invention has excellent tensile strength and elongation, so that it does not break or tear even in the event of an external impact, and can prevent the moisture absorbent inside from being discharged to the outside.
이하 구체예 또는 실시예를 통해 본 발명을 더욱 상세히 설명한다. 다만 하기 구체예 또는 실시예는 본 발명을 상세히 설명하기 위한 하나의 참조일 뿐 본 발명이 이에 한정되는 것은 아니며, 여러 형태로 구현될 수 있다.The present invention will be described in more detail through the following specific examples or examples. However, the following specific examples or examples are only one reference for explaining the present invention in detail, but the present invention is not limited thereto, and may be implemented in various forms.
또한 달리 정의되지 않는 한, 모든 기술적 용어 및 과학적 용어는 본 발명이 속하는 당업자 중 하나에 의해 일반적으로 이해되는 의미와 동일한 의미를 갖는다. 본 발명에서 설명에 사용되는 용어는 단지 특정 구체예를 효과적으로 기술하기 위함이고 본 발명을 제한하는 것으로 의도되지 않는다.Also, unless defined otherwise, all technical and scientific terms have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Terms used in the description in the present invention are merely to effectively describe specific embodiments and are not intended to limit the present invention.
또한 명세서 및 첨부된 특허청구범위에서 사용되는 단수 형태는 문맥에서 특별한 지시가 없는 한 복수 형태도 포함하는 것으로 의도할 수 있다.Also, the singular forms used in the specification and appended claims may be intended to include the plural forms as well, unless the context dictates otherwise.
또한 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 포함할 수 있는 것을 의미한다.In addition, when a certain component is said to "include", this means that it may further include other components without excluding other components unless otherwise stated.
종래의 흡습제 파우치에 사용되는 통기성 필름(ex:Tyvek)은 흡습속도를 조절하기가 불가능해 이를 위하여 통기성 제어를 위해 EVA와 같은 수지를 코팅하여 해결하였으며, 이로 인한 공정 증가와 비용 상승을 초래하였다. 또한 상기 통기성 필름을 파우치 형태로 제공하기 위해서는 EVA 수지가 열접착에 의해 접합되는데 이는 상대적으로 낮은 접합강도를 나타내었다.The breathable film (ex: Tyvek) used in conventional moisture absorbent pouches cannot control the moisture absorption rate, so it was solved by coating a resin such as EVA to control air permeability, resulting in an increase in process and cost. In addition, in order to provide the breathable film in the form of a pouch, the EVA resin is bonded by thermal bonding, which showed relatively low bonding strength.
이에 본 발명은 폴리에스테르 부직포 층, 폴리올레핀 통기성 층, 폴리올레핀계 천공필름 층을 포함하는 흡습제용 포장재로서, 상기 각 층은 폴리우레탄계 접착제 층을 더 포함하는 것인 흡습제용 포장재를 제공함으로써, 흡습제용 포장재로 제조된 흡습제품의 흡습속도를 효과적으로 제어할 수 있으며, 특히 추가적인 고분자 수지 코팅 없이도 열접착이 가능하여 공정이 단순화되고 추가 비용이 절감되는 장점이 있다.Accordingly, the present invention provides a packaging material for a moisture absorbent including a polyester nonwoven fabric layer, a polyolefin breathable layer, and a polyolefin-based perforated film layer, wherein each layer further includes a polyurethane-based adhesive layer, thereby providing a packaging material for a moisture absorbent. It is possible to effectively control the moisture absorption rate of the moisture absorbing product made of, and in particular, it has the advantage of simplifying the process and reducing additional costs because thermal bonding is possible without additional polymer resin coating.
또한, 상기 폴리에스테르 부직포 층과 폴리올레핀 통기성 층 사이에 폴리우레탄계 접착제를 사용함으로써, 종래의 핫멜트를 이용한 열접착 또는 에폭시 접착제 등보다 더욱 단단하게 결합시킬 수 있다. 또한, 상기 폴리우레탄계 접착제는 내수성 또한 우수하여, 상기 폴리에스테르계 부직포와 폴리올레핀 통기성 층 사이에 결합되어 통기성이 우수한 장점이 있다.In addition, by using a polyurethane-based adhesive between the polyester nonwoven fabric layer and the polyolefin air permeable layer, it can be bonded more firmly than conventional hot-melt thermal bonding or epoxy adhesive. In addition, the polyurethane-based adhesive has excellent water resistance and is bonded between the polyester-based nonwoven fabric and the polyolefin breathable layer, thereby providing excellent air permeability.
또한 상기 폴리올레핀 통기성 층과 폴리올레핀계 천공필름층이 폴리우레탄계 접착제에 의해 고정됨에 따라 상기 3층의 흡습제용 포장재의 통기성은 우수하면서 내구성 및 투습성 또한 우수한 장점이 있다.In addition, since the polyolefin air permeable layer and the polyolefin perforated film layer are fixed by a polyurethane adhesive, the three-layer packaging material for a moisture absorbent has excellent air permeability, durability and moisture permeability.
본 발명의 일 양태에 따른, 상기 흡습제용 포장재의 걸리투과도(150ml 공기량)는 500 내지 1,500 초이고, 투습도는 500 내지 1,500 g/m2인 것일 수 있으며, 구체적으로, 상기 흡습제용 포장재의 걸리투과도(150ml 공기량)는 500 내지 800 초이고, 투습도가 1,000 내지 1,500 g/m2인 것일 수 있으며, 구체적으로, 상기 흡습제용 포장재의 걸리투과도는 800 내지 1,400 초이고, 투습도가 600 내지 800 g/m2인 것일 수 있다.According to one aspect of the present invention, the Gurley permeability (150ml air volume) of the packaging material for the desiccant may be 500 to 1,500 seconds, and the moisture permeability may be 500 to 1,500 g/m 2 . Specifically, the Gurley permeability of the packaging material for the desiccant (150ml air volume) may be 500 to 800 seconds, and moisture permeability may be 1,000 to 1,500 g/m 2 . Specifically, the Gurley permeability of the moisture absorbent packaging material is 800 to 1,400 seconds, and moisture permeability is 600 to 800 g/m. It could be 2 .
상기 흡습제용 포장재가 상기 걸리투과도 및 투습도를 만족함에 따라, 추가적으로 하기 후술할 흡습제와의 결합 시 흡습속도를 적절히 유지하여 장기간 동안 주변 습기를 흡습할 수 있는 장점이 있다.As the packaging material for the desiccant satisfies the Gurley permeability and moisture permeability, it has the advantage of absorbing ambient moisture for a long period of time by properly maintaining the moisture absorption rate when combined with the desiccant to be described later.
상기 폴리에스테르 부직포 층은 폴리에스테르계 부직포를 포함하는 것일 수 있다.The polyester nonwoven fabric layer may include a polyester nonwoven fabric.
상기 폴리에스테르계 부직포는 폴리에스테르계 단독 섬유 또는 천연섬유 또는 합성 섬유와 폴리에스테르계 섬유의 혼방으로 직조된 것일 수 있으나, 이에 제한되는 것은 아니다. 상기 천연섬유로는 면, 모, 견, 대마 등일 수 있으며, 상기 합성 섬유로는 폴리아미드 섬유, 폴리에스테르 섬유 등과 같은 합성섬유일 수 있으나 이에 제한되는 것은 아니다.The polyester-based nonwoven fabric may be woven from a single polyester fiber or a blend of natural or synthetic fibers and polyester-based fibers, but is not limited thereto. The natural fibers may be cotton, wool, silk, hemp, etc., and the synthetic fibers may be synthetic fibers such as polyamide fibers and polyester fibers, but are not limited thereto.
또한, 상기 폴리에스테르계 부직포는 포는 니들 펀칭 (needle punching), 열본딩 (thermal bonding), 스펀 본딩 (spun bondiong), 용융 블로잉 (melt blowing) 또는 스펀 편철 (spun lacing)과 같은 방식으로 제조되는 것일 수 있으나, 이에 제한되는 것은 아니다.In addition, the polyester-based nonwoven fabric is manufactured by a method such as needle punching, thermal bonding, spun bonding, melt blowing, or spun lacing. It may be, but is not limited thereto.
또한, 상기 폴리에스테르계 부직포는 평량이 10 내지 60 g/m2일 수 있으며, 구체적으로, 15 내지 50 g/m2일 수 있으며, 구체적으로, 20 내지 40 g/m2일 수 있으나, 이에 제한되는 것은 아니다.In addition, the polyester-based nonwoven fabric may have a basis weight of 10 to 60 g/m 2 , specifically, 15 to 50 g/m 2 , and specifically, 20 to 40 g/m 2 , but It is not limited.
상기 흡습제용 포장재가 상기 평량을 만족하는 폴리에스테르 부직포를 포함함에 따라 통기성이 더욱 증가하는 효과를 가질 수 있다.As the packaging material for the moisture absorbent includes a polyester nonwoven fabric satisfying the basis weight, air permeability may be further increased.
상기 폴리올레핀 통기성 필름층은 폴리올레핀 통기성 필름을 포함하는 것일 수 있다. 상기 폴리올레핀 통기성 필름의 재질은 저밀도 폴리에틸렌, 고밀도 폴리에틸렌, 선형저밀도 폴리에틸렌, 폴리프로필렌 또는 폴리부틸렌 일 수 있으나, 이에 제한되는 것은 아니다. 또한 상기 폴리올레핀 통기성 필름은 상기 폴리올레핀 수지에 무기충전제를 포함하여 제조된 것일 수 있다. 상기 폴리올레핀 통기성 필름은 폴리올레핀수지에 무기충전제를 첨가하여 압출시트를 제조한 후, 연신하여 제조하는 것일 수 있으나, 상기 제조방법에 제한되는 것은 아니다.The polyolefin breathable film layer may include a polyolefin breathable film. The material of the polyolefin breathable film may be low density polyethylene, high density polyethylene, linear low density polyethylene, polypropylene or polybutylene, but is not limited thereto. In addition, the polyolefin breathable film may be prepared by including an inorganic filler in the polyolefin resin. The polyolefin breathable film may be prepared by adding an inorganic filler to a polyolefin resin to prepare an extruded sheet and then stretching, but is not limited to the above manufacturing method.
상기 무기충전제는 탄산칼슘, 탈크, 클레이, 카올린, 실리카 및 규조토로 이루어진 군에서 선택되는 어느 하나 또는 둘 이상을 사용할 수 있다. 상기 무기충전제의 평균입경은 발명의 목적에 따라 선택하여 사용할 수 있으며, 투습도, 통기성 및 기계적 강도를 위하여 제한되지 않으나 바람직하게는 0.5~30 ㎛인 것을 사용하는 것일 수 있으나, 이에 제한되는 것은 아니다.As the inorganic filler, any one or two or more selected from the group consisting of calcium carbonate, talc, clay, kaolin, silica and diatomaceous earth may be used. The average particle diameter of the inorganic filler may be selected and used according to the purpose of the invention, and is not limited for moisture permeability, air permeability and mechanical strength, but may be preferably 0.5 to 30 μm, but is not limited thereto.
그 함량은 휨강도, 탄성 및 유연성의 향상을 위하여 상기 폴리에틸렌 수지 100 중량부에 대하여 20~40 중량부를 사용하는 것일 수 있으나, 이에 제한되는 것은 아니다.The content may be 20 to 40 parts by weight based on 100 parts by weight of the polyethylene resin to improve bending strength, elasticity and flexibility, but is not limited thereto.
상기 폴리올레핀 통기성 필름은 쉽게 찢어지지 않고, 투습, 방수능력 및 통기도를 유지하기 위하여 평량이 10~50 g/㎡인 것이 바람직하며, 또한, 상기 폴리올레핀 통기성 필름은 투습도가 100~10,000 g/㎡·24hr, 통기도가 10~5,000 sec 및 내수압이 50~100 ㎝/H2O인 물성을 갖는 것일 수 있다.The polyolefin breathable film is not easily torn and preferably has a basis weight of 10 to 50 g/m2 in order to maintain moisture permeability, waterproof ability, and air permeability, and the polyolefin breathable film has a moisture permeability of 100 to 10,000 g/m2 24 hr. , air permeability of 10 to 5,000 sec and water resistance of 50 to 100 cm/H 2 O.
또한, 본 발명의 일 양태에 따른, 상기 폴리 올레핀계 천공필름은 폴리올레핀계 필름에 1 내지 500 개/cm2의 천공이 형성된 필름인 것일 수 있으며, 구체적으로 8 내지 30 개/cm2의 천공이 형성된 필름인 것일 수 있으며, 구체적으로 8 내지 10 개/cm2의 천공이 형성된 필름인 것일 수 있으나, 이에 제한되는 것은 아니다.In addition, according to one aspect of the present invention, the polyolefin-based perforated film may be a film in which 1 to 500 perforations/cm 2 are formed in the polyolefin-based film, and specifically, 8 to 30 perforations/cm 2 are formed. It may be a formed film, specifically, it may be a film formed with 8 to 10 perforations/cm 2 , but is not limited thereto.
상기 폴리올레핀계 천공필름의 천공개수가 상기 조건을 만족함에 따라, 상기 흡습제용 포장재를 포함하는 흡습제의 흡습 속도를 효과적으로 제어할 수 있다.When the number of perforations of the polyolefin-based perforated film satisfies the above condition, it is possible to effectively control the moisture absorption rate of the moisture absorbent including the moisture absorbent packaging material.
본 발명의 일 양태에 따른, 상기 폴리 올레핀계 천공필름은 천공의 평균 직경이 0.01 내지 2.0 mm인 것일 수 있으며, 구체적으로 0.05 내지 1.5 mm일 수 있으며, 구체적으로 0.1 내지 1.0mm일 수 있으며, 구체적으로 0.3 내지 0.5 mm일 수 있으나, 이에 제한되는 것은 아니다.According to one aspect of the present invention, the polyolefin-based perforated film may have an average diameter of perforations of 0.01 to 2.0 mm, specifically 0.05 to 1.5 mm, specifically 0.1 to 1.0 mm, and specifically It may be 0.3 to 0.5 mm, but is not limited thereto.
본 발명의 일 양태에 따른, 상기 폴리 올레핀계 천공필름은 천공율이 0.1 내지 50%인 것 일 수 있으며, 구체적으로, 0.3 내지 40% 일 수 있으며, 구체적으로, 0.4 내지 30% 일 수 있으며, 구체적으로, 0.4 내지 20%일 수 있으며, 구체적으로,0.5 내지 10% 일 수 있으며, 구체적으로, 0.5 내지 5 %일 수 있으나, 이에 제한되는 것은 아니다. 이때, 천공율은 단위면적에 대한 천공 면적 전체 합의 백분율을 의미한다. 상기 천공율 범위는 상기 천공의 평균직경 범위에서 조절되는 것이며, 이들 조합에 따라 흡습속도를 더욱 효과적으로 제어할 수 있다.According to one aspect of the present invention, the polyolefin-based perforated film may have a perforation rate of 0.1 to 50%, specifically, 0.3 to 40%, specifically, 0.4 to 30%, Specifically, it may be 0.4 to 20%, specifically, it may be 0.5 to 10%, specifically, it may be 0.5 to 5%, but is not limited thereto. At this time, the perforation rate means a percentage of the total sum of the perforation area with respect to the unit area. The perforation rate range is adjusted within the range of the average diameter of the perforations, and the moisture absorption rate can be more effectively controlled according to these combinations.
본 발명의 일 양태에 따른, 상기 폴리우레탄계 접착제는 폴리에스테르계 폴리올과 폴리에테르계 폴리올로부터 유래된 폴리우레탄 접착제인 것일 수 있다.According to one aspect of the present invention, the polyurethane adhesive may be a polyurethane adhesive derived from a polyester polyol and a polyether polyol.
상기 폴리우레탄계 접착제는 폴리에테르 폴리올, 폴리에스테르 폴리올 및 이소시아네이트계 경화제, 촉진제 및 용매를 포함하며, 상기 구성으로 제조된 폴리우레탄계 접착제는 일반 접착제와는 달리 통기성이 우수한 효과를 가지고 있다.The polyurethane-based adhesive includes a polyether polyol, a polyester polyol, an isocyanate-based curing agent, an accelerator, and a solvent, and the polyurethane-based adhesive prepared with the above structure has excellent air permeability unlike general adhesives.
상기 폴리에스테르 폴리올은 다염기산 및 다가알콜류가 반응하여 제조된다. 상기 다염기산으로는 방향족 다염기산으로 프탈산, 이소프탈산, 테레프탈산, 디카르복실산이 있으며 지방족으로는 숙신산, 아디프산, 아젤라인산, 세바식산 등을 사용할 수 있다.The polyester polyol is prepared by reacting a polybasic acid and a polyhydric alcohol. Examples of the polybasic acid include phthalic acid, isophthalic acid, terephthalic acid, and dicarboxylic acid as aromatic polybasic acids, and succinic acid, adipic acid, azelaic acid, and sebacic acid may be used as aliphatic acids.
또한, 상기 다가알콜류로는 에틸렌글리콜, 프로필렌글리콜, 디에틸렌글리콜, 트리에틸렌글리콜, 1.4부탄디올, 1.3부탄디올, 네오펜틸글리콜, 펜타메틸렌글리콜, 헥사메틸렌글리콜, 헵타메틸렌글리콜 등을 사용할 수 있다.In addition, ethylene glycol, propylene glycol, diethylene glycol, triethylene glycol, 1.4 butanediol, 1.3 butanediol, neopentyl glycol, pentamethylene glycol, hexamethylene glycol, heptamethylene glycol and the like can be used as the polyhydric alcohol.
상기 다염기산과 다가알코올을 200 내지 250℃에서 축중합시킴으로서 상기의 폴리에스테르폴리올을 제조할 수 있다.The polyester polyol may be prepared by condensation polymerization of the polybasic acid and the polyhydric alcohol at 200 to 250°C.
본 발명에 따르면, 상기 폴리에스테르폴리올은 폴리프로필렌글리콜, 폴리에틸렌글리콜, 폴리카프로락톤글리콜, 폴리테트라메틸렌글리콜, 폴리카르보네이트글리콜류로 이루어진 군에서 선택된 어느 하나 이상을 사용할 수 있다.According to the present invention, the polyester polyol may use at least one selected from the group consisting of polypropylene glycol, polyethylene glycol, polycaprolactone glycol, polytetramethylene glycol, and polycarbonate glycols.
이들 폴리올들은 폴리올 분자당 하이드록시 작용기가 3개 이하인 것을 사용하며 주로 2개인 것을 위주로 하는 것이 바람직하다.These polyols use three or less hydroxyl functional groups per polyol molecule, preferably two.
본 발명에 따르면, 상기 폴리올은 수평균분자량 400 내지 6,000 g/mol인 것을 사용하는 것이 바람직하며, 보다 바람직하게는 1,000 내지 4,000 g/mol사이 분자량을 갖는 폴리올을 주로 사용할 수 있으며, 이들 폴리올의 공중합체 또는 이들의 혼합물로 조성될 수도 있다.According to the present invention, it is preferable to use polyols having a number average molecular weight of 400 to 6,000 g/mol, and more preferably polyols having a molecular weight between 1,000 and 4,000 g/mol may be mainly used, and the air of these polyols It may be composed of a polymer or a mixture thereof.
본 발명에 따르면, 상기 수지조성물을 구성하는 이소시아네이트계 경화제는 상기 폴리올에 부가반응시키기 위한 것으로, 종류로는 방향족 이소시아네이트화합물, 지방족 또는 지환족 이소시아네이트화합물 등이 있다.According to the present invention, the isocyanate-based curing agent constituting the resin composition is for an addition reaction to the polyol, and includes aromatic isocyanate compounds, aliphatic or alicyclic isocyanate compounds, and the like.
상기 지방족 이소시아네이트 화합물로는 헥사메틸렌 디이소시아네이트, 이소프로필렌 디이소시아네이트, 메틸렌 디이소시아네이트, 크실렌 디이소시아네이트로 이루어진 군에서 선택되는 어느 하나 이상을 사용할 수 있으며, 상기 지환족 이소시아네이트로는 이소포론 디이소시아네이트, 메틸시클로헥산 디이소시아네이트, 시클로헥산-1.4-디이소시아네이트로 이루어진 군에서 선택되는 어느 하나 이상일 수 있다. 또한, 상기 방향족 이소시아네이트로서는 톨릴렌 디이소시아네이트, 1.5-나프틸렌 디시소시아네이트, 4.4-디페닐메탄 디이소시사네이트, 1.3-페닐렌 디이소시아네이트로 이루어진 군에서 선택되는 어느 하나 이상을 사용할 수 있으나 이에 제한되는 것은 아니다.As the aliphatic isocyanate compound, at least one selected from the group consisting of hexamethylene diisocyanate, isopropylene diisocyanate, methylene diisocyanate, and xylene diisocyanate may be used, and as the alicyclic isocyanate, isophorone diisocyanate, methylcyclo It may be at least one selected from the group consisting of hexane diisocyanate and cyclohexane-1.4-diisocyanate. In addition, as the aromatic isocyanate, at least one selected from the group consisting of tolylene diisocyanate, 1.5-naphthylene diisocyanate, 4.4-diphenylmethane diisocyanate, and 1.3-phenylene diisocyanate may be used, but is limited thereto it is not going to be
본 발명의 일 양태에 따른, 상기 폴리우레탄계 접착제는 폴리에테르 폴리올과 폴리에스테르 폴리올이 1: 1 내지 4의 중량비로 혼합된 폴리우레탄 접착제 수지 100 중량부에 대하여, 이소시아네이트계 경화제가 5 내지 40 중량부와 반응하여 제조된 폴리우레탄 접착제를 포함하는 것일 수 있다.According to one aspect of the present invention, the polyurethane adhesive contains 5 to 40 parts by weight of an isocyanate-based curing agent based on 100 parts by weight of a polyurethane adhesive resin in which polyether polyol and polyester polyol are mixed in a weight ratio of 1: 1 to 4. It may be to include a polyurethane adhesive prepared by reacting with.
상기 3단 구성의 흡습제용 포장재를 상기 폴리우레탄계 접착제를 사용하여 접착함에 따라, 통기성은 우수하면서 투습도는 제어할 수 있는 효과를 가질 수 있으며, 특히 내구성 및 인장강도와 같은 물리적 강도가 우수해지는 장점이 있다. As the three-stage moisture absorbent packaging material is bonded using the polyurethane-based adhesive, it is possible to have an effect of controlling moisture permeability while having excellent air permeability, and in particular, the advantage of excellent physical strength such as durability and tensile strength there is.
본 발명의 일 양태에 따른, 상기 폴리우레탄계 접착제는 스크린 인쇄, 돗트(DOT)인쇄, 스프레이 인쇄 및 패터닝(patterning) 도포 등에 의해 코팅하는 것일 수 있으나, 이에 제한되는 것은 아니다.According to one aspect of the present invention, the polyurethane-based adhesive may be coated by screen printing, dot (DOT) printing, spray printing and patterning application, but is not limited thereto.
상기 패터닝 도포는 메쉬형태의 그라비아 인쇄나 또는 메쉬 롤 인쇄방법을 사용하여 메쉬형태로 도포하는 방식으로 제조될 수 있으며, 상기 스프레이 도포는 상기 폴리우레탄계 접착제를 전체적으로 도포할 수 있으면, 방법에는 제한되지 않는다. The patterning application may be made by applying in a mesh shape using a mesh type gravure printing or mesh roll printing method, and the spray application is not limited to the method as long as the polyurethane-based adhesive can be applied as a whole. .
상기 스프레이 도포를 통해 상기 각 층의 사이에 닷 형태로 도포됨에 따라, 전반적인 접착제 도포방식 보다 통기성이 더욱 우수해지는 장점이 존재한다.As it is applied in a dot form between the respective layers through the spray application, there is an advantage in that air permeability is more excellent than the overall adhesive application method.
본 발명의 일 양태에 따른, 상기 흡습제용 포장재를 일면 또는 양면으로 하여 흡습제를 포장한 흡습제품을 제공할 수 있다.According to one aspect of the present invention, a moisture absorbing product in which a moisture absorbing agent is packaged by using one or both sides of the moisture absorbing packaging material may be provided.
상기 흡습제품은 상기 흡습제용 포장재에 흡습제를 포함하는 흡습제 파우치 형태일 수 있으며, 더스트 커버 용기 내부에 흡습제를 포함하고 이를 상기 흡습제 통기성 필름으로 덮힌 제품일 수도 있으나, 상기 사용방식은 제한되지 않는다.The moisture absorbent product may be in the form of a moisture absorbent pouch containing a moisture absorbent in a packaging material for the moisture absorbent, or may be a product including a moisture absorbent inside a dust cover container and covered with the moisture absorbent breathable film, but the method of use is not limited.
본 발명의 일 양태에 따른, 상기 흡습제에 대하여 자세하게 설명한다.According to one aspect of the present invention, the moisture absorbent will be described in detail.
상기 흡습제는 분말형 및 과립형일 수 있으나, 이에 제한되는 것은 아니다. The moisture absorbent may be in powder form or granular form, but is not limited thereto.
상기 흡습제의 구성은 The composition of the absorbent is
(A) 염화마그네슘, 염화칼슘 및 탄산나트륨으로 이루어진 군으로부터 선택된 적어도 하나 또는 둘 이상의 흡습물질;(A) at least one or two or more hygroscopic substances selected from the group consisting of magnesium chloride, calcium chloride and sodium carbonate;
(B) 산화마그네슘 및 산화칼슘으로 이루어진 군으로부터 선택된 적어도 하나 이상을 포함하는 경화성 무기물을 포함하는 것일 수 있다.(B) may include a curable inorganic material including at least one selected from the group consisting of magnesium oxide and calcium oxide.
또한 , 본 발명의 일 양태에 따른, 상기 흡습제는 (A) 흡습물질 : (B) 경화성 무기물의 중량비가 1 : 0.1 내지 2 인 비율일 수 있으며, 바람직하게는 1: 0.2 내지 1.5 인 비율일 수 있으며, 더욱 바람직하게는 0.4 내지 1.5 인 비율일 수 있다. In addition, according to one aspect of the present invention, the moisture absorbent may have a weight ratio of (A) hygroscopic material: (B) curable inorganic material of 1: 0.1 to 2, preferably 1: 0.2 to 1.5. And, more preferably, it may be a ratio of 0.4 to 1.5.
상기 (A) 흡습물질과 상기 (B) 경화성 무기물을 상기 중량비로 포함한 흡습제는 흡습효과는 우수하면서 동시에 낮은 방출율을 가지는 현저한 효과를 발휘할 수 있다. The moisture absorbent containing the hygroscopic material (A) and the curable inorganic material (B) in the above weight ratio can exhibit a remarkable effect having a low release rate while having an excellent moisture absorption effect.
상기 흡습제에 있어서, 흡습성을 부여하기 위하여 (A) 염화마그네슘, 염화칼슘 및 탄산나트륨으로 이루어진 군으로부터 선택된 적어도 하나 이상을 포함하는 흡습물질을 포함하며, 이외에도 본 발명의 기술분야에서 공지된 생석회 등의 흡습물질을 추가로 포함하여 사용할 수도 있다. (A) 상기 흡습물질에 있어서는, 우수한 흡습성과 낮은 방출율의 측면에서 염화마그네슘을 사용하는 것이 보다 바람직하다.In the hygroscopic agent, in order to impart hygroscopicity, (A) a hygroscopic material containing at least one selected from the group consisting of magnesium chloride, calcium chloride and sodium carbonate is included, and in addition to hygroscopic materials such as quicklime known in the art, It may be used by including additionally. (A) As for the hygroscopic material, it is more preferable to use magnesium chloride in view of excellent hygroscopicity and low release rate.
본 발명의 일 실시예에 따르면, 상기 염화마그네슘은 흡습제 내용물 전체 중량에 대하여 10 내지 50중량%, 바람직하게는 20 내지 45중량%, 보다 바람직하게는 25 내지 40 중량%로 포함될 수 있다. 상기 범위에서 우수한 흡습율을 구현할 뿐만 아니라, 습기를 흡수하는 속도를 최적화함으로, 과도한 흡습에 의한 흡습 지속성이 떨어지거나 흡습된 습기가 재방출되는 것을 효율적으로 억제하는 측면에서 효과적이다.According to one embodiment of the present invention, the magnesium chloride may be included in 10 to 50% by weight, preferably 20 to 45% by weight, more preferably 25 to 40% by weight based on the total weight of the content of the moisture absorbent. In addition to realizing an excellent moisture absorption rate within the above range, by optimizing the rate of absorbing moisture, it is effective in effectively suppressing deterioration in moisture absorption continuity due to excessive moisture absorption or re-release of absorbed moisture.
또한, 상기 흡습제가 습기를 흡습하면서 경화되도록 하여 조해성으로 인해 액화되는 것을 방지하기 위하여, (B) 산화마그네슘 및 산화칼슘으로 이루어진 군으로부터 선택된 적어도 하나 이상을 포함하는 경화성 무기물을 포함한다. In addition, (B) a curable inorganic material containing at least one selected from the group consisting of magnesium oxide and calcium oxide is included to prevent the desiccant from becoming liquefied due to deliquescence by allowing the absorbent to harden while absorbing moisture.
더욱이, 상기 경화성 무기물이 비중이 상이한 2종의 산화마그네슘을 포함함으로써, 램프 내부 습기의 흡습 속도를 최적화하고 장기간 지속적인 흡습성능을 구현할 뿐만 아니라, 외기 또는 자동차 엔진열에 의하여 급격히 상승된 온도에서 흡습된 수분이 재방출되지 않도록 하는 현저한 효과를 가질 수 있다. Moreover, since the curable inorganic material contains two types of magnesium oxide having different specific gravity, the moisture absorption rate of the moisture inside the lamp is optimized and continuous moisture absorption performance is realized for a long period of time, as well as moisture absorbed at a rapidly elevated temperature by outside air or automobile engine heat. This can have a significant effect of preventing re-emission.
본 발명의 일 실시예에 따르면, 상기 비중이 상이한 2종의 산화마그네슘은 상기 자동차 램프용 흡습제 내용물 전체 중량에 대하여 50 내지 90 중량%로 포함될 수 있고, 바람직하게는 55 내지 70 중량%로 포함될 수 있다.According to one embodiment of the present invention, the two types of magnesium oxide having different specific gravity may be included in 50 to 90% by weight, preferably 55 to 70% by weight, based on the total weight of the contents of the moisture absorbent for the automobile lamp. there is.
상기 비중이 상이한 2종의 산화마그네슘은 고비중 산화마그네슘과 저비중 산화마그네슘으로 이루어질 수 있다. 이때, 본 발명의 고비중, 저비중은 겉보기 비중을 측정하여 상대적인 값을 기준으로 구분된 것을 의미한다. 구체적으로 상기 고비중 산화마그네슘은 비중이 3 내지 8, 바람직하게는 4 내지 7일 수 있고 상기 저비중 산화마그네슘은 비중이 0.1 내지 0.9, 바람직하게는 0.3 내지 0.7인 것일 수 있다. The two types of magnesium oxide having different specific gravity may be composed of high specific gravity magnesium oxide and low specific gravity magnesium oxide. At this time, the high specific gravity and low specific gravity of the present invention mean that the apparent specific gravity is measured and classified based on the relative value. Specifically, the high specific gravity magnesium oxide may have a specific gravity of 3 to 8, preferably 4 to 7, and the low specific gravity magnesium oxide may have a specific gravity of 0.1 to 0.9, preferably 0.3 to 0.7.
상기 비중이 상이한 2종의 산화마그네슘은 고비중 산화마그네슘과 저비중 산화마그네슘의 비중 비율(저비중/고비중)은 0.01 내지 0.3, 구체적으로 0.05 내지 0.2인 것일 수 있다. 상기 범위에서 흡습성능, 내방출성이 더욱 향상될 수 있고, 그에 따라 수명 증대, 흡습으로 인한 팽창 억제 측면에서 더욱 효과적이다.The two types of magnesium oxide having different specific gravity may have a specific gravity ratio (low specific gravity/high specific gravity) of high specific gravity magnesium oxide and low specific gravity magnesium oxide of 0.01 to 0.3, specifically 0.05 to 0.2. Within the above range, moisture absorption performance and release resistance can be further improved, and accordingly, it is more effective in terms of life extension and expansion inhibition due to moisture absorption.
상기 비중이 상이한 2종의 산화마그네슘은 상술한 비중 범위를 갖는 고비중 산화마그네슘과 저비중 산화마그네슘의 혼합 조성비는 크게 제한되지는 않으나, 구체적인 일예로 1 : 0.5 내지 2, 바람직하게는 1 : 0.7 내지 1.5, 보다 바람직하게는 1 : 1 내지 1.4의 혼합비율로 혼합한 것을 사용할 수 있다. 상기 범위에서 흡습성능, 내방출성, 수명 증대, 흡습으로 인한 팽창 억제 측면에서 더욱 효과적이다.The mixing composition ratio of the two types of magnesium oxide having different specific gravity is not particularly limited, but, as a specific example, 1: 0.5 to 2, preferably 1: 0.7. to 1.5, more preferably 1: 1 to 1.4 may be used. In the above range, it is more effective in terms of moisture absorption performance, release resistance, life extension, and inhibition of expansion due to moisture absorption.
본 발명의 일 실시예에 따른 흡습제는 흡습에 의하여 경화 시, 물 분자가 산화마그네슘의 결정구조에 참여하여, 침상형의 결정구조로 변화하면서, 수분을 흡수하고, 또한 침상구조의 공간에 수분입자가 들어가게 되어, 흡습성이 더욱 향상될 수 있다.When the moisture absorbent according to an embodiment of the present invention is cured by moisture absorption, water molecules participate in the crystal structure of magnesium oxide, change to an acicular crystal structure, absorb moisture, and also absorb moisture in the space of the acicular structure. is included, and the hygroscopicity can be further improved.
또한 상기 고비중 산화마그네슘과 저비중 산화마그네슘의 수화반응 속도를 이용하여, 장기간에 걸쳐 흡습율이 일정하게 지속될 수 있고, 내방출성 효과가 더욱 향상될 수 있어 바람직하다. 또한, 부피팽창을 억제하여, 통기성 포장재 등의 포장재 손상을 방지하는 효과를 가질 수 있다.In addition, by using the hydration reaction rate of the high specific gravity magnesium oxide and the low specific gravity magnesium oxide, the moisture absorption rate can be maintained constant over a long period of time, and the release resistance effect can be further improved, which is preferable. In addition, it may have an effect of preventing damage to packaging materials such as air permeable packaging materials by suppressing volume expansion.
또한 본 발명의 또 다른 양태로, 상기 흡습제는 (A) 흡습물질; (B) 경화성 무기물; 및 (C) 고분자 왁스;를 포함하여 완성할 수 있다. In another aspect of the present invention, the moisture absorbing agent may include (A) a moisture absorbing material; (B) curable inorganics; And (C) polymer wax; can be completed by including.
본 발명의 상기 흡습제는 (A) 흡습물질; (B) 경화성 무기물; 및 (C) 고분자 왁스;를 포함함으로서, 흡습율이 우수할 뿐만 아니라, 고온 저습의 환경 조건에서 흡습된 수분의 재방출을 최소화하며 또한 계속적인 흡습성을 확보할 수 있다.The moisture absorbent of the present invention includes (A) a moisture absorbent; (B) curable inorganics; And (C) polymer wax; by including, not only is the moisture absorption rate excellent, but also minimizes the re-release of moisture absorbed under environmental conditions of high temperature and low humidity, and also ensures continuous moisture absorption.
상기 (C) 고분자 왁스를 더 포함함으로써, 상기 흡습제가 흡습 팽창 후 스폰지와 같은 연질의 특성을 부가할 수 있다.By further including the (C) polymer wax, the absorbent may have a soft property like a sponge after expanding by absorbing moisture.
상기 고분자 왁스는 폴리에틸렌 왁스, 폴리프로필렌 왁스, 폴리아미드 왁스, 카노바 왁스, 파라핀 왁스 및 폴리테트라플루오로에틸렌 왁스로 이루어진 군으로부터 선택된 적어도 하나 이상인 고분자 왁스를 추가적으로 포함할 수 있다. 상기 고분자 왁스로 폴리에틸렌 왁스의 경우, 상업화된 예로 SFC사의 LH 1200 등을 사용할 수 있다. 상기 고분자 왁스는, 예를 들어 자동차 램프 내부의 온도가증가하는 경우와 같이 상기 흡습제의 환경 온도가 증가하는 경우, 고점도의 액상으로 변화하여 흡습된 수분의 방출을 억제하는 기능을 하며 또한 제품의 흡습율을 조절하는 기능을 병행한다.The polymer wax may further include at least one polymer wax selected from the group consisting of polyethylene wax, polypropylene wax, polyamide wax, carnova wax, paraffin wax, and polytetrafluoroethylene wax. In the case of polyethylene wax as the polymer wax, commercially available examples such as SFC's LH 1200 may be used. The polymer wax functions to suppress the release of moisture absorbed by changing into a high-viscosity liquid phase when the environmental temperature of the absorbent increases, for example, when the temperature inside a car lamp increases. In parallel with the function of regulating the rate.
본 발명의 일 양태에 있어서, 상기 흡습제는 (A) 흡습물질 10 중량% 내지 70 중량%, (B) 경화성 무기물 10 중량% 내지 50 중량%; 및 (C) 고분자 왁스 5 중량% 내지 50 중량%를 포함하는 것일 수 있다.In one aspect of the present invention, the moisture absorbent includes (A) 10% to 70% by weight of a moisture absorbing material, (B) 10% to 50% by weight of a curable inorganic material; and (C) 5% to 50% by weight of polymer wax.
상기 흡습제의 함량이 상기 함량일 때, 흡습효과가 우수하며, 수분 재방출량이 저하될 수 있다.When the content of the moisture absorbent is the above content, the moisture absorption effect is excellent, and the amount of water re-release may be reduced.
상기 함량에 따른 효과에 대하여 구체적으로 설명한다.The effect according to the content will be described in detail.
상기 흡습제에 대하여 (A) 흡습물질은 10 중량% 내지 70 중량%을 포함할 수 있으며, 바람직하게는 15 중량% 내지 65% 중량을 포함할 수 있으며, 더욱 바람직하게는 20 중량 % 내지 60% 중량을 포함할 수 있으나 이에 제한되는 것은 아니다.Regarding the moisture absorbent, (A) the moisture absorbent may include 10% to 70% by weight, preferably 15% to 65% by weight, and more preferably 20% to 60% by weight. It may include, but is not limited thereto.
상기 (A) 흡습물질의 함량이 상기 범위일 때 흡습제의 흡습효과가 우수하며, 과도한 수분 흡습을 인하여 제조된 흡습제가 액상화 되는 현상을 억제할 수 있어 제품의 안정성을 높일 수 있다. When the content of the hygroscopic material (A) is within the above range, the moisture absorption effect of the moisture absorbent is excellent, and the liquefaction of the moisture absorbent produced due to excessive moisture absorption can be suppressed, thereby increasing product stability.
상기 흡습제에 대하여 (B) 경화성 무기물은 10 중량% 내지 50 중량%을 포함할 수 있으며, 바람직하게는 15 중량% 내지 45% 중량을 포함할 수 있으며, 더욱 바람직하게는 10 중량% 내지 40 중량%을 포함할 수 있으나 이에 제한되는 것은 아니다. With respect to the moisture absorbent, (B) the curable inorganic material may include 10% to 50% by weight, preferably 15% to 45% by weight, and more preferably 10% to 40% by weight. It may include, but is not limited thereto.
상기 (B) 경화성 무기물의 함량이 상기 범위일 때 조해성 흡습제의 분리를 억제할 수 있으면서 동시에 상기 흡습제가 우수한 흡습율을 유지할 수 있는 장점이 있다.When the content of the curable inorganic material (B) is within the above range, there is an advantage in that the separation of the deliquescent desiccant can be suppressed and at the same time, the desiccant can maintain an excellent moisture absorption rate.
상기 흡습제에 대하여 (C) 고분자 왁스는 바람직하게 5 중량% 내지 40 중량%으로 포함할 수 있으며, 바람직하게는 10 중량% 내지 35중량 %를 포함할 수 있으며, 더욱 바람직하게는 15 중량% 내지 30중량%를 포함할 수 있으나, 이에 제한되는 것은 아니다. With respect to the moisture absorbent, (C) polymer wax may preferably be included in an amount of 5% to 40% by weight, preferably 10% to 35% by weight, more preferably 15% to 30% by weight Weight % may include, but is not limited thereto.
상기 (C) 고분자 왁스의 함량이 상기 범위일 때 흡습제에 흡습된 수분의 방출율을 억제 할 수 있는 상기 흡습제의 우수한 흡습율 및 흡습 속도를 가질 수 있다. When the content of the (C) polymer wax is within the above range, the moisture absorbent may have excellent moisture absorption rate and moisture absorption rate capable of suppressing the release rate of moisture absorbed in the moisture absorbent.
본 발명의 일 양태에 따른, 상기 흡습제는 알칼리 금속 인산염을 더 포함하는 것일 수 있다. According to one aspect of the present invention, the moisture absorbent may further include an alkali metal phosphate.
상기 알칼리 금속 인산염은 리튬, 소듐 및 포타슘 등으로부터 선택되는 알칼리 금속이온을 포함할 수 있다.The alkali metal phosphate may include an alkali metal ion selected from lithium, sodium and potassium.
바람직하게는 소듐 금속이온을 포함하는 알칼리 금속 인산염을 포함할 수 있다. 구체적인 예를 들어, 상기 알칼리 금속 인산염은 모노소듐 포스페이트(monosodium phosphate), 다이소듐 포스페이트(disodium phosphate) 및 트리소듐 포스페이트(trisodium phosphate)등으로 이루어지는 군으로부터 선택되는 어느 하나 또는 둘 이상을 포함할 수 있으나, 반드시 이에 제한되는 것은 아니다. Preferably, an alkali metal phosphate containing sodium metal ion may be included. For example, the alkali metal phosphate may include any one or two or more selected from the group consisting of monosodium phosphate, disodium phosphate, and trisodium phosphate. , but is not necessarily limited thereto.
상기 알칼리 금속 인산염을 포함할 경우, 상기 흡습물질, 상기 경화성 무기물 및 상기 고분자 왁스와 함께 혼합하였을 때, 수분을 흡습함으로 인해 발생되는 팽창을 효율적으로 억제할 수 있을 뿐만 아니라, 고습도의 조건에서 습도 제어성능이 탁월하여 흡습효과를 오랫동안 구현할 수 있는 장기 내구성을 확보할 수 있다.When the alkali metal phosphate is included, when mixed with the hygroscopic material, the curable inorganic material, and the polymer wax, expansion caused by moisture absorption can be effectively suppressed, and humidity is controlled under high humidity conditions. Its excellent performance ensures long-term durability that can realize the moisture absorption effect for a long time.
본 발명의 일 양태에 따라, 상기 알칼리 금속 인산염은 상기 흡습제 100 중량에 대하여, 1 내지 30중량부가 포함될 수 있으며, 바람직하게는 2 내지 25중량부, 더 바람직하게는 5 내지 25중량부가 포함될 수 있다. 상기와 같은 함량으로 포함할 경우, 흡습 시 팽창률을 더욱 향상시킬 수 있고, 이로써 흡습제품의 파손 및 내용물 누출 등을 방지하는 측면에서 더욱 효과적이다.According to one aspect of the present invention, the alkali metal phosphate may be included in an amount of 1 to 30 parts by weight, preferably 2 to 25 parts by weight, and more preferably 5 to 25 parts by weight, based on 100 parts by weight of the moisture absorbent. . When included in the above content, it is possible to further improve the expansion rate upon moisture absorption, thereby being more effective in terms of preventing damage to the moisture absorbing product and leakage of contents.
본 발명의 일 양태에 따라, 상기 흡습제는 (A)흡습물질, (B)경화성 무기물, (C)고분자 왁스 및 알칼리 금속 인산염을 모두 포함함으로써, 향상된 흡습율뿐만 아니라, 습도 조절이 요구되는 환경, 특히 극한의 다습한 조건에서도 탁월한 습도 제어성능을 구현하며, 지속적인 흡습성능을 확보할 수 있다. 나아가, 흡습에 따른 팽창으로 인한 추가적인 손상이 발생을 방지하는 안정성을 확보할 수 있는 면에서 더욱 효과적이다.According to one aspect of the present invention, the moisture absorbent includes (A) a hygroscopic material, (B) a curable inorganic material, (C) a polymer wax, and an alkali metal phosphate, thereby improving moisture absorption as well as an environment requiring humidity control, In particular, it realizes excellent humidity control performance even in extreme high humidity conditions and can secure continuous moisture absorption performance. Furthermore, it is more effective in terms of securing stability that prevents the occurrence of additional damage due to expansion due to moisture absorption.
본 발명의 일 양태에 따라, 상기 흡습제는 고분자 첨가제를 더 포함할 수 있다. 상기 고분자 첨가제는 카르복실기 및 수산화기 등에서 선택되는 어느 하나 또는 둘 이상의 기능기를 갖는 음이온성 고분자일 수 있다. 일 구체예로, 알긴산, 알지네이트, 카라기난, 젤라틴, 히알루론산, 폴리아크릴산, 폴리아크릴레이트, 폴리메타크릴산, 폴리메타크릴레이트, 전분, 산화전분, 셀룰로오스 및 카르복실메틸셀룰로오스 등으로 이루어지는 군으로부터 선택되는 어느 하나 또는 둘 이상의 고분자 첨가제를 더 포함할 수 있으나, 이에 제한되는 것은 아니다. 또한, A101, NAP701 등과 같은 응집제를 더 포함할 수 있으나, 이에 제한되는 것은 아니다.According to one aspect of the present invention, the moisture absorbent may further include a polymer additive. The polymer additive may be an anionic polymer having one or two or more functional groups selected from a carboxyl group and a hydroxyl group. In one embodiment, selected from the group consisting of alginic acid, alginate, carrageenan, gelatin, hyaluronic acid, polyacrylic acid, polyacrylate, polymethacrylic acid, polymethacrylate, starch, oxidized starch, cellulose, carboxylmethylcellulose, etc. It may further include any one or two or more polymeric additives that are, but is not limited thereto. In addition, it may further include a coagulant such as A101, NAP701, etc., but is not limited thereto.
본 발명의 일 양태에 따라, 상기 고분자 첨가제는 흡습제 100중량부에 대하여, 0.1 내지 10중량부 포함될 수 있다. 바람직하게는 0.01 내지 5중량부 포함될 수 있으나, 이에 제한되지 않는다. 상기와 같은 함량으로 포함될 경우, 본 발명의 목적으로 하는 흡습성능은 물론 흡습 후 내부 물질의 안정적인 고화와 동시에 팽창 억제 효율을 더욱 향상시킬 수 있다.According to one aspect of the present invention, the polymer additive may be included in an amount of 0.1 to 10 parts by weight based on 100 parts by weight of the moisture absorbent. Preferably, it may be included in an amount of 0.01 to 5 parts by weight, but is not limited thereto. When included in the above content, the desired moisture absorption performance of the present invention as well as stable solidification of the internal material after moisture absorption and expansion suppression efficiency can be further improved.
앞서 서술한 흡습제 포장 필름에 상기 흡습제를 포장하여 흡습제품을 제조함에 따라, 상기 흡습제품의 흡습속도를 효과적으로 제어할 수 있다. 또한, 상기 흡습제품이 우수한 내구성을 가질 수 있어, 운송 및 보관 등에 있어서 외부 충격으로 인한 흡습제가 외부로 토출되는 현상을 억제할 수 있다.As the moisture absorbing product is manufactured by packaging the moisture absorbing agent in the aforementioned moisture absorbing agent packaging film, the moisture absorption rate of the moisture absorbing product can be effectively controlled. In addition, since the moisture absorbing product may have excellent durability, it is possible to suppress a phenomenon in which the moisture absorbing agent is discharged to the outside due to external impact during transportation and storage.
본 발명의 일 양태에 따른, 상기 흡습제품은 흡습율이 100% 이상일 수 있으며, 구체적으로 120%일 수 있으며, 구체적으로 150%일 수 있으나, 이에 제한되는 것은 아니다.According to one aspect of the present invention, the moisture absorption product may have a moisture absorption rate of 100% or more, specifically 120%, and specifically 150%, but is not limited thereto.
본 발명의 일 양태에 따른, 상기 흡습제품의 흡습속도는 흡습속도가 1 내지 10 %/2시간 일 수 있으며, 구체적으로 1 내지 8 %/2시간 일 수 있으며, 구체적으로 1 내지 6 %/2시간 일 수 있으나, 이에 제한되는 것은 아니다. According to one aspect of the present invention, the moisture absorption rate of the moisture absorption product may be 1 to 10%/2 hours, specifically 1 to 8%/2 hours, and specifically 1 to 6%/2 hours It may be time, but is not limited thereto.
이하 실시예 및 비교예를 바탕으로 본 발명을 더욱 상세히 설명한다. 다만 하기 실시예 및 비교예는 본 발명을 더욱 상세히 설명하기 위한 하나의 예시일 뿐, 본 발명이 하기 실시예 및 비교예에 의해 제한되는 것은 아니다.The present invention will be described in more detail based on the following Examples and Comparative Examples. However, the following Examples and Comparative Examples are only one example for explaining the present invention in more detail, and the present invention is not limited by the following Examples and Comparative Examples.
<흡습필름 성능 평가><Hygroscopic film performance evaluation>
1. 걸리 투과도1. Gurley permeability
공기 150ml가 투과되는 시간을 걸리 밀도계(Gurley densometer, KP-M4350, 기배이앤티사)를 사용하여 측정하였다.The time for 150 ml of air to pass through was measured using a Gurley densometer (KP-M4350, Kibae E&T Co.).
2. 인장강도2. Tensile strength
상기 인장강도는 ISO 1924-2에 따라 측정한 값이다. The tensile strength is a value measured according to ISO 1924-2.
<흡습제품 성능 평가><Evaluation of moisture absorption product performance>
3. 흡습율3. Moisture Absorption
상기 흡습율은 항온항습기를 이용하여 50±2 ℃ 온도 및 95±5 % 상대습도 하에의 만습조건에서 시편의 흡습율을 측정하며, 흡습율은 하기의 식 1과 같이 계산하였다. The moisture absorptive rate was measured by using a thermo-hygrostat under a high humidity condition at a temperature of 50 ± 2 ° C and a relative humidity of 95 ± 5%, and the moisture absorptive rate was calculated as in Equation 1 below.
[식 1][Equation 1]
4. 흡습속도4. Moisture Absorption Rate
항온항습기를 이용하여 50±2 ℃ 온도 및 95±5 % 상대습도 하에서 시편을 2시간 동안 노출시킨 후 흡습속도를 측정하였으며, 흡습속도는 하기 식 2 으로 산출하였다. After exposing the specimen for 2 hours under a temperature of 50 ± 2 ℃ and 95 ± 5% relative humidity using a thermo-hygrostat, the moisture absorption rate was measured, and the moisture absorption rate was calculated by the following formula 2.
[식 2][Equation 2]
5. 방출률 5. Emission rate
열풍건조기를 이용하여 80±2 ℃ 온도 하에서 만습된 시편을 2시간, 24시간 동안 노출시킨 후 방출률을 측정하였으며, 방출률은 하기 식 3 으로 산출하였다.The release rate was measured after exposing the wet specimen for 2 hours and 24 hours under a temperature of 80 ± 2 ° C using a hot air dryer, and the release rate was calculated by Equation 3 below.
[식 3][Equation 3]
<흡습제 제조예><Examples of producing a moisture absorbent>
혼합기를 이용하여 흡습물질로 염화마그네슘(Aldrich, 순도 94%) 40 중량%, 경화성 무기물로 산화마그네슘(KONOSHIMA CHEMICAL사, STARMAG 50, 입도 30 ㎛) 40 중량% 및 폴리에틸렌 왁스(SFC사, LH1200, 연화점 109±3℃) 20 중량%를 균일하게 혼합하여, 흡습제 35g를 제조하였다.Using a mixer, 40% by weight of magnesium chloride (Aldrich, purity 94%) as a hygroscopic material, 40% by weight of magnesium oxide (KONOSHIMA CHEMICAL, STARMAG 50, particle size 30 ㎛) and polyethylene wax (SFC, LH1200, softening point) as a curable inorganic material 109±3° C.) 20% by weight was uniformly mixed to prepare 35 g of a moisture absorbent.
<실시예 1><Example 1>
폴리에스터 스펀본드 부직포(평량 30g/m2, CAS No. 25038-59-9)의 일면 상에 폴리우레탄 접착제를 도포하고, 상기 도포된 접착제 상에 폴리프로필렌 필름(CAS No. 9003-07-0)을 접착하였다. 이후, 상기 폴리프로필렌 필름 상에 폴리우레탄 접착제를 도포하고, 상기 도포된 접착제 상에 평균 20개/cm2의 천공을 가지는 폴리프로필렌 천공필름(CAS No. 9003-07-0, 주조 PP 필름, 두께 25 um)를 접착하여 3중 무지 필름을 제조하였다. 상기 3중 무지 필름제조는 건식라미네이션 공정으로 제조되었다.A polyurethane adhesive is applied on one side of a polyester spunbond nonwoven fabric (basic weight 30 g/m 2 , CAS No. 25038-59-9), and a polypropylene film (CAS No. 9003-07-0) is applied on the applied adhesive. ) was attached. Then, a polyurethane adhesive is applied on the polypropylene film, and a polypropylene perforated film (CAS No. 9003-07-0 , cast PP film, thickness 25 um) to prepare a triple plain film. The triple plain film was manufactured by a dry lamination process.
<실시예 2><Example 2>
실시예 1에서 상기 20 내지 25개/cm2의 천공을 가지는 폴리프로필렌 천공필름 대신에 8 내지 10개/cm2의 천공을 가지는 폴리프로필렌 천공필름(CAS No. 9003-07-0, 주조 PP 필름, 두께 25 um)을 사용한 것을 제외하고는 동일하게 실시하였다.In Example 1, a polypropylene perforated film (CAS No. 9003-07-0, cast PP film) having 8 to 10 perforations/cm 2 instead of the perforated polypropylene film having perforations of 20 to 25 per cm 2 , thickness 25 um) was carried out in the same manner except for using.
<실시예 3><Example 3>
길이 130㎜와 너비 100㎜의 실시예 1의 통기성 포장재에 상기 흡습제를 투입한 후, 열씰링기를 이용하여 160 ℃ 이상 온도에서 가공하여 흡습제 파우치를 제조하였다. After the moisture absorbent was added to the air permeable packaging material of Example 1 having a length of 130 mm and a width of 100 mm, a moisture absorbent pouch was prepared by processing at a temperature of 160° C. or higher using a heat sealing machine.
<실시예 4><Example 4>
길이 130㎜와 너비 100㎜의 실시예 2의 통기성 포장재에 상기 흡습제를 투입한 후, 열씰링기를 이용하여 160 ℃ 이상 온도에서 가공하여 흡습제 파우치를 제조하였다. After the moisture absorbent was added to the air permeable packaging material of Example 2 having a length of 130 mm and a width of 100 mm, a moisture absorbent pouch was prepared by processing at a temperature of 160° C. or higher using a heat sealing machine.
<비교예 1><Comparative Example 1>
타이벡(Dupont 제공 원단) 필름을 사용하였다. Tyvek (fabric provided by Dupont) film was used.
<비교예 2><Comparative Example 2>
상기 비교예 1에서 타이벡 필름을 EVA로 코팅한 것을 제외하고는 동일하게 실시하였다. The same procedure as in Comparative Example 1 was performed except that the Tyvek film was coated with EVA.
<비교예 3><Comparative Example 3>
길이 130㎜와 너비 100㎜의 비교예 1의 통기성 포장재에 상기 흡습제를 투입한 후, 열씰링기를 이용하여 120℃의 온도에서 가공하여 흡습제 파우치를 제조하였다. After the moisture absorbent was added to the air permeable packaging material of Comparative Example 1 having a length of 130 mm and a width of 100 mm, a moisture absorbent pouch was prepared by processing at a temperature of 120° C. using a heat sealing machine.
<비교예 4><Comparative Example 4>
길이 130㎜와 너비 100㎜의 비교예 2의 통기성 포장재에 상기 흡습제를 투입한 후, 열씰링기를 이용하여 120℃ 내외의 온도에서 가공하여 흡습제 파우치를 제조하였다. After the moisture absorbent was added to the air permeable packaging material of Comparative Example 2 having a length of 130 mm and a width of 100 mm, a moisture absorbent pouch was prepared by processing at a temperature around 120° C. using a heat sealing machine.
하기 표 1은 실시예 1 내지 2 및 비교예 1 내지 2의 3중 무지 필름의 최대하중, 인장강도, 최대변위 및 연신율을 나타낸 표이며, 하기 표2는 투습도 및 걸리 투과도를 나타낸 표이다. 또한 하기 표 3은 실시예 3, 실시예 4 및 비교예 4의 흡수율을 나타낸 표이며, 표 4는 흡습속도, 표 5는 방출률을 나타낸 표이다.Table 1 below is a table showing the maximum load, tensile strength, maximum displacement and elongation of the triple plain films of Examples 1 and 2 and Comparative Examples 1 and 2, and Table 2 below is a table showing the water vapor permeability and Gurley permeability. In addition, Table 3 below is a table showing water absorption rates of Examples 3, 4 and Comparative Example 4, Table 4 is a moisture absorption rate, and Table 5 is a table showing release rates.
실시예 1 내지 2는 비교예 1보다 기계적 강도뿐만 아니라 연신율이 매우 우수한 것을 확인할 수 있다. 또한, 실시예 1 내지 2에서는 투습률 및 걸리투과도가 매우 적절한 것을 확인할 수 있다.It can be seen that Examples 1 and 2 have very excellent elongation as well as mechanical strength compared to Comparative Example 1. In addition, in Examples 1 and 2, it can be confirmed that the moisture permeability and Gurley transmittance are very appropriate.
이어서, 상기 실시예 1, 2 및 비교예 1의 흡습필름을 포함하는 흡습제품을 제조하여 흡습률, 흡습속도 및 방출율을 관찰하였다. Subsequently, moisture absorption products including the moisture absorption films of Examples 1 and 2 and Comparative Example 1 were prepared and moisture absorption rate, moisture absorption rate and release rate were observed.
실시예 3, 4의 경우 비교예 4와 흡습율은 비슷하였으나, 흡습속도는 비교예 4보다 낮은 것으로 확인되었다. 또한, 상기 흡습제품이 만습 상태까지 걸리는 흡습기간은 실시예3은 24일, 실시예4는 49일, 비교예4는 15일 정도로 확인되었다. 이는 동일한 흡습제를 포함하더라도 흡습제용 포장재의 종류에 따라 흡습속도를 제어하여 장기간 동안 흡습효과를 유지할 수 있음을 확인할 수 있었다.In the case of Examples 3 and 4, the moisture absorption rate was similar to that of Comparative Example 4, but the moisture absorption rate was confirmed to be lower than that of Comparative Example 4. In addition, the moisture absorption period for the moisture absorption product to full moisture was confirmed to be 24 days in Example 3, 49 days in Example 4, and 15 days in Comparative Example 4. It was confirmed that even if the same moisture absorbent was included, the moisture absorption effect could be maintained for a long period of time by controlling the moisture absorption rate according to the type of packaging material for the moisture absorbent.
이는 상기 흡습제품이 자주 교체하기 곤란하여 장기간 동안 흡습효과를 유지해야 되는 자동차 램프 내부, 선박 또는 창고 등에 사용하기에 매우 적절한 것을 알 수 있다. It can be seen that the moisture absorbing product is very suitable for use in automobile lamps, ships, warehouses, etc., where it is difficult to frequently replace the moisture absorbing product and the moisture absorption effect must be maintained for a long period of time.
비교예 2의 흡습필름으로는 열접착이 잘 안되어서 흡습제품을 제조할 수 없었다.With the moisture absorbing film of Comparative Example 2, it was not possible to manufacture a moisture absorbing product due to poor thermal bonding.
이상과 같이 본 발명에서는 특정된 사항들과 한정된 실시예 및 도면에 의해 설명되었으나 이는 본 발명의 보다 전반적인 이해를 돕기 위해서 제공된 것일 뿐, 본 발명은 상기의 실시예에 한정되는 것은 아니며, 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 이러한 기재로부터 다양한 수정 및 변형이 가능하다. As described above, the present invention has been described by specific details and limited embodiments and drawings, but this is only provided to help a more general understanding of the present invention, the present invention is not limited to the above embodiments, and the present invention Those skilled in the art can make various modifications and variations from these descriptions.
따라서, 본 발명의 사상은 설명된 실시예에 국한되어 정해져서는 아니되며, 후술하는 특허청구범위뿐 아니라 이 특허청구범위와 균등하거나 등가적 변형이 있는 모든 것들은 본 발명 사상의 범주에 속한다고 할 것이다.Therefore, the spirit of the present invention should not be limited to the described embodiments, and it will be said that not only the claims to be described later, but also all modifications equivalent or equivalent to these claims belong to the scope of the present invention. .
Claims (12)
폴리올레핀 통기성 층,
폴리올레핀계 천공필름 층을 포함하는 흡습제용 포장재로서,
상기 각 층은 폴리우레탄계 접착제 층을 더 포함하는 것이며,
상기 폴리 올레핀계 천공필름은 복수의 천공을 가지며,
상기 폴리 올레핀계 천공필름은 1 내지 500 개/cm2의 천공이 형성된 폴리 올레핀계 천공필름인 것이며,
상기 흡습제용 포장재의 걸리투과도는 500 내지 800 미만 초이며,
상기 흡습제용 포장재의 투습도는 500 내지 1500 g/m2.day인, 흡습제용 포장재.a layer of polyester non-woven fabric;
a polyolefin breathable layer;
A packaging material for a moisture absorbent comprising a polyolefin-based perforated film layer,
Each of the above layers further includes a polyurethane-based adhesive layer,
The polyolefin-based perforated film has a plurality of perforations,
The polyolefin-based perforated film is a polyolefin-based perforated film in which 1 to 500 perforations / cm 2 are formed,
The Gurley permeability of the packaging material for the moisture absorbent is 500 to less than 800 seconds,
The moisture permeability of the packaging material for the moisture absorbent is 500 to 1500 g / m 2 .day, the packaging material for the moisture absorbent.
상기 폴리 올레핀계 천공필름은 8 내지 30 개/cm2의 천공이 형성된 폴리 올레핀계 천공필름인 것인, 흡습제용 포장재.According to claim 2,
The polyolefin-based perforated film is a polyolefin-based perforated film in which 8 to 30 perforations / cm 2 are formed, a packaging material for a moisture absorbent.
상기 폴리 올레핀계 천공필름은 천공율이 0.1 내지 50%인, 흡습제용 포장재.According to claim 3,
The polyolefin-based perforated film has a perforation rate of 0.1 to 50%, a packaging material for a moisture absorbent.
상기 폴리우레탄계 접착제는 폴리에스테르계 폴리올과 폴리에테르계 폴리올로부터 유래된 폴리우레탄 접착제인 것인, 흡습제용 포장재.According to claim 1,
The polyurethane-based adhesive is a polyurethane adhesive derived from a polyester-based polyol and a polyether-based polyol, a packaging material for a moisture absorbent.
상기 폴리우레탄계 접착제는 스크린 인쇄, 돗트(DOT)인쇄, 스프레이 인쇄 및 패터닝(patterning) 도포에 의해 코팅하는 것인, 흡습제용 포장재.According to claim 1,
The polyurethane-based adhesive is a packaging material for a moisture absorbent that is coated by screen printing, dot (DOT) printing, spray printing and patterning (patterning) application.
상기 흡습제는
(A) 염화마그네슘, 염화칼슘 및 탄산나트륨으로 이루어진 군으로부터 선택된 적어도 하나 또는 둘 이상의 흡습물질;
(B) 산화마그네슘 및 산화칼슘으로 이루어진 군으로부터 선택된 적어도 하나 이상을 포함하는 경화성 무기물을 포함하는 것인 흡습제품.According to claim 7,
The moisture absorbent
(A) at least one or two or more hygroscopic substances selected from the group consisting of magnesium chloride, calcium chloride and sodium carbonate;
(B) A moisture absorbent product comprising a curable inorganic material containing at least one selected from the group consisting of magnesium oxide and calcium oxide.
상기 흡습제는 (A) 흡습물질 10 내지 50 중량% 및 (B) 경화성 무기물 50 내지 90 중량%인 것을 포함하는 흡습제품.According to claim 8,
The moisture absorbing agent includes (A) 10 to 50% by weight of a moisture absorbing material and (B) 50 to 90% by weight of a curable inorganic material.
상기 흡습제는 고분자 왁스를 더 포함하는 것인 흡습제품.According to claim 8,
The moisture absorbent product further comprises a polymer wax.
상기 흡습제는 알칼리 금속 인산염을 더 포함하는 것인 흡습제품.According to claim 8,
The moisture absorbent product further comprises an alkali metal phosphate.
상기 흡습제품은 흡습율이 100% 이상인, 흡습속도가 1 내지 10 %/2시간 인 흡습제품.
According to claim 8,
The moisture absorption product has a moisture absorption rate of 100% or more and a moisture absorption rate of 1 to 10%/2 hours.