KR102541571B1 - User-Based Custom Gel Nail Stickers - Google Patents
User-Based Custom Gel Nail Stickers Download PDFInfo
- Publication number
- KR102541571B1 KR102541571B1 KR1020230008923A KR20230008923A KR102541571B1 KR 102541571 B1 KR102541571 B1 KR 102541571B1 KR 1020230008923 A KR1020230008923 A KR 1020230008923A KR 20230008923 A KR20230008923 A KR 20230008923A KR 102541571 B1 KR102541571 B1 KR 102541571B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- monomer units
- layer
- methacrylate monomer
- Prior art date
Abstract
Description
본 발명은 사용자 기반 커스텀 젤 네일 스티커에 관한 것이다.The present invention relates to user-based custom gel nail stickers.
셀프 네일 이용에 대한 관심도가 높아지고 이용자가 증가하여 셀프 네일 시장이 크게 성장하고 있다. 이용자가 자신을 표현하는 수단으로 이용하는 미용제품의 한 부문으로 자리 잡고 있다.As the interest in using self-nails increases and the number of users increases, the self-nail market is growing significantly. It has become a part of beauty products that users use as a means of expressing themselves.
이용자 스스로 본인의 손톱에 쉽게 부착과 탈착이 가능한 미용제품인 이유로 잦은 탈부착으로 인하여 손톱의 손상이 발생하고 손톱이 녹아 내리거나 손톱이 손에서 이탈하게 되는 현상이 발생한다. 장기간 부착시에는 손톱의 유분과 수분이 감소하게 되어 손톱의 갈라짐 현상도 발생하여 손톱 손상의 원인이 된다.Because it is a cosmetic product that can be easily attached and detached from the user's own nails, frequent attachment and detachment causes damage to the nail, and the nail melts or the nail separates from the hand. When attached for a long period of time, the oil and moisture of the nails are reduced, and cracking of the nails occurs, which causes nail damage.
또한, 일반적인 젤 네일 스티커는 가장 하단층의 이형필름을 제거하고 접착층이 손톱이 직접 접착하는 방식이다. 젤 네일 스티커 제거 시 접착층의 성분과 접착력으로 인하여 손톱의 손상이 발생하게 된다. 더욱이, 젤 네일 스티커 제거시에 사용되는 폴리시 리무버, 퓨어 아세톤은 손톱을 구성하고 있는 단백질인 케라틴을 녹이는 효과로 손톱이 녹아 내리는 문제가 있다.In addition, a general gel nail sticker is a method in which the release film of the lowest layer is removed and the adhesive layer is directly adhered to the nail. When removing the gel nail sticker, damage to the nail occurs due to the components and adhesive strength of the adhesive layer. Moreover, pure acetone, a polish remover used to remove gel nail stickers, has a problem of melting nails due to its effect of dissolving keratin, a protein constituting nails.
본 발명은 상기와 같은 문제점을 해결하기 위해 안출된 것으로서, 본 발명의 목적은 수용성 베이스로 만들어 젤 네일 스티커 제거시에 화학 용액의 사용을 줄여 손톱의 손상을 줄이게 하는 것이다.The present invention has been made to solve the above problems, and an object of the present invention is to reduce damage to nails by reducing the use of chemical solutions when removing gel nail stickers made of a water-soluble base.
또한, 본 발명의 다른 목적은 젤 네일 스티커의 사용시에 발생하는 유분과 수분의 감소에 대한 문제를 해결하는 것으로, 접착층에 단백질, 케라틴 및 영양성분을 함유하여 유분이 최대 90% 감소하는 것을 유분이 유지되도록 만들고, 수분 또한 높게 유지 되도록 하는 것이다.In addition, another object of the present invention is to solve the problem of reducing oil and moisture that occurs when using a gel nail sticker, and by containing protein, keratin and nutrients in the adhesive layer, the oil content is reduced by up to 90%. It is to make it stay, and the moisture is also kept high.
또한, 본 발명의 또 다른 목적은 손톱의 형태, 크기, 곡선에 맞는 젤 네일 스티커를 선택하고, 소비자 기호에 따라 색상, 디자인, 파츠를 골라 커스템 네일 스티커 제작이 가능한 젤 네일 스티커 제공 시스템을 제공하는 것이다.In addition, another object of the present invention is to select a gel nail sticker suitable for the shape, size, and curve of the nail, and to provide a gel nail sticker providing system capable of producing a custom nail sticker by selecting a color, design, and parts according to consumer preference. is to do
본 발명의 과제는 이상에서 언급한 과제들로 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.The object of the present invention is not limited to the tasks mentioned above, and other tasks not mentioned will be clearly understood by those skilled in the art from the following description.
상기 목적을 달성하기 위하여 본 발명은In order to achieve the above object, the present invention
박리필름층(10); release
상기 박리필름층(10) 상에 형성된 접착층(20); an
상기 접착층(20) 상에 형성된 베이스층(30); a
상기 베이스층(30) 상에 형성된 컬러층(40); a
상기 컬러층(40) 상에 형성된 인쇄층(50); a printed
상기 인쇄층(50) 상에 형성된 젤층(60); 및a
상기 젤층(60) 상에 형성된 이형필름층(70);을 포함하는 젤 네일 스티커(100)를 제공한다.It provides a
또한, 상기 접착층(20)은 에틸메타크릴레이트 단량체 단위 23-27 중량%, n-부틸메타크릴레이트 단량체 단위 23-27 중량%, 글리시딜메타크릴레이트 단량체 단위 23-27 중량% 및 하이드록시에틸 메타크릴레이트 단량체 단위 23-27 중량%인 제1 아크릴레이트계 공중합체 31-35 중량부; 메틸메타크릴레이트 단량체 단위 23-27 중량%, 에틸메타크릴레이트 단량체 단위 23-27 중량%, 아크릴산 단량체 단위 23-27 중량% 및 메톡시에틸메타크릴레이트 단량체 단위 23-27 중량%인 제2 아크릴레이트계 공중합체 12-16 중량부; 올레핀계 불포화기를 갖는 친수성 폴리우레탄 10-14 중량부; 분리대두단백, 귀리단백분말 및 분리완두단백이 1:1:1의 중량비율로 혼합된 제1 조성물 3-7 중량부; 레몬껍질 추출물, 사과껍질 추출물, 양파껍질 추출물, 수박껍질 추출물 및 바나나껍질 추출물이 3:3:2:1:1의 중량비율로 혼합된 제2 조성물 2-6 중량부; 비타민 혼합물 2-6 중량부; 오미자씨 오일 2-6 중량부; 복숭아씨 오일 2-6 중량부; 리모넨 0.5-4 중량부; 리날룰 0.5-4 중량부; 이소퀘르시트린 0.5-4 중량부; 나이아신아마이드 0.1-1 중량부; 폴리글리세릴-6스테아레이트 0.1-1 중량부; 폴리글리세릴-2스테아레이트 0.1-1 중량부; 프로필렌글라이콜 1-5 중량부; 세테아릴알코올 1-5 중량부; 글리세릴스테아레이트 0.5-4 중량부; 스테아릴알코올 0.1-1 중량부; 프로판다이올 1-5 중량부; 알란토인 0.1-1 중량부; 및 트로메타민 0.1-1 중량부;를 포함하는 접착층 형성용 조성물로 형성된 것을 특징으로 한다.In addition, the
또한, 상기 베이스층(30)은 메틸메타크릴레이트 단량체 단위 23-27 중량%, n-부틸메타크릴레이트 단량체 단위 23-27 중량%, 글리시딜메타크릴레이트 단량체 단위 23-27 중량% 및 하이드록시에틸 메타크릴레이트 단량체 단위 23-27 중량%인 제3 아크릴레이트계 공중합체 45-49 중량부; 중량평균분자량이 35,000-45,000인 폴리우레탄아크릴레이트 26-30 중량부; 에틸메타크릴레이트 3-7 중량부; 라우릴메타크릴레이트 2-6 중량부; 하이드록시에틸메타아크릴레이트 1-5 중량부; 메틸셀룰로오스 3-7 중량부; 프로필렌글리콜 1-5 중량부; 디메티콘 1-5 중량부; 및 소듐실리케이트 0.5-4 중량부;를 포함하는 베이스층 형성용 조성물로 형성된 것을 특징으로 한다.In addition, the
또한, 본 발명은In addition, the present invention
손톱을 깨끗하게 정리하는 단계;cleaning nails;
정리된 손톱에 전처리제를 도포한 후 건조하는 단계; 및Applying a pretreatment agent to the prepared nails and then drying; and
건조된 손톱에 박리필름층을 제거한 젤 네일 스티커를 부착시키는 단계;를 포함하고,Attaching a gel nail sticker from which the peeling film layer is removed to the dried nail;
상기 전처리제는 로즈마리추출물 및 오미자추출물을 포함하는 천연추출물 18-22 중량부; 현미, 보리, 귀리, 통밀, 호밀, 맥아, 대두, 수수, 검정콩 및 검정깨로부터 제조되는 곡물 발효분말 10-14 중량부; 아밀로스 3-7 중량부; 글리세린 3-7 중량부; 프로필렌글리콜 2-6 중량부; 부틸렌글리콜 2-6 중량부; 포스파티딜에탄올아민 3-7 중량부; 에탄올 13-17 중량부; 및 당근수 28-32 중량부;를 포함하고,18-22 parts by weight of natural extracts including rosemary extract and Schisandra chinensis extract; 10-14 parts by weight of fermented grain powder prepared from brown rice, barley, oats, whole wheat, rye, malt, soybean, sorghum, black soybean and black sesame; 3-7 parts by weight of amylose; 3-7 parts by weight of glycerin; 2-6 parts by weight of propylene glycol; 2-6 parts by weight of butylene glycol; 3-7 parts by weight of phosphatidylethanolamine; 13-17 parts by weight of ethanol; and 28-32 parts by weight of carrots;
상기 젤 네일 스티커는,The gel nail sticker,
박리필름층; release film layer;
상기 박리필름층 상에 형성된 접착층; an adhesive layer formed on the release film layer;
상기 접착층 상에 형성된 베이스층; a base layer formed on the adhesive layer;
상기 베이스층(30) 상에 형성된 컬러층; a color layer formed on the
상기 컬러층 상에 형성된 인쇄층; a printing layer formed on the color layer;
상기 인쇄층 상에 형성된 젤층; 및a gel layer formed on the printing layer; and
상기 젤층 상에 형성된 이형필름층;을 포함하고,Including; a release film layer formed on the gel layer,
상기 접착층은 에틸메타크릴레이트 단량체 단위 23-27 중량%, n-부틸메타크릴레이트 단량체 단위 23-27 중량%, 글리시딜메타크릴레이트 단량체 단위 23-27 중량% 및 하이드록시에틸 메타크릴레이트 단량체 단위 23-27 중량%인 제1 아크릴레이트계 공중합체 31-35 중량부; 메틸메타크릴레이트 단량체 단위 23-27 중량%, 에틸메타크릴레이트 단량체 단위 23-27 중량%, 아크릴산 단량체 단위 23-27 중량% 및 메톡시에틸메타크릴레이트 단량체 단위 23-27 중량%인 제2 아크릴레이트계 공중합체 12-16 중량부; 올레핀계 불포화기를 갖는 친수성 폴리우레탄 10-14 중량부; 분리대두단백, 귀리단백분말 및 분리완두단백이 1:1:1의 중량비율로 혼합된 제1 조성물 3-7 중량부; 레몬껍질 추출물, 사과껍질 추출물, 양파껍질 추출물, 수박껍질 추출물 및 바나나껍질 추출물이 3:3:2:1:1의 중량비율로 혼합된 제2 조성물 2-6 중량부; 비타민 혼합물 2-6 중량부; 오미자씨 오일 2-6 중량부; 복숭아씨 오일 2-6 중량부; 리모넨 0.5-4 중량부; 리날룰 0.5-4 중량부; 이소퀘르시트린 0.5-4 중량부; 나이아신아마이드 0.1-1 중량부; 폴리글리세릴-6스테아레이트 0.1-1 중량부; 폴리글리세릴-2스테아레이트 0.1-1 중량부; 프로필렌글라이콜 1-5 중량부; 세테아릴알코올 1-5 중량부; 글리세릴스테아레이트 0.5-4 중량부; 스테아릴알코올 0.1-1 중량부; 프로판다이올 1-5 중량부; 알란토인 0.1-1 중량부; 및 트로메타민 0.1-1 중량부;를 포함하는 접착층 형성용 조성물로 형성된 것이고,The adhesive layer comprises 23-27 wt% of ethyl methacrylate monomer units, 23-27 wt% of n-butyl methacrylate monomer units, 23-27 wt% of glycidyl methacrylate monomer units, and hydroxyethyl methacrylate monomers. 31-35 parts by weight of the first acrylate-based copolymer having a unit of 23-27% by weight; A second acrylic comprising 23-27% by weight of methyl methacrylate monomer units, 23-27% by weight of ethyl methacrylate monomer units, 23-27% by weight of acrylic acid monomer units, and 23-27% by weight of methoxyethyl methacrylate monomer units 12-16 parts by weight of a late copolymer; 10-14 parts by weight of hydrophilic polyurethane having an olefinic unsaturated group; 3-7 parts by weight of a first composition in which isolated soy protein, oat protein powder, and isolated pea protein are mixed in a weight ratio of 1:1:1; 2-6 parts by weight of a second composition in which lemon peel extract, apple peel extract, onion peel extract, watermelon peel extract, and banana peel extract are mixed in a weight ratio of 3:3:2:1:1; 2-6 parts by weight of the vitamin mixture; Schisandra seed oil 2-6 parts by weight; 2-6 parts by weight of peach seed oil; 0.5-4 parts by weight of limonene; linalool 0.5-4 parts by weight; 0.5-4 parts by weight of isoquercitrin; Niacinamide 0.1-1 part by weight; 0.1-1 part by weight of polyglyceryl-6 stearate; 0.1-1 part by weight of polyglyceryl-2stearate; 1-5 parts by weight of propylene glycol; 1-5 parts by weight of cetearyl alcohol; 0.5-4 parts by weight of glyceryl stearate; 0.1-1 part by weight of stearyl alcohol; 1-5 parts by weight of propanediol; 0.1-1 part by weight of allantoin; And 0.1-1 part by weight of tromethamine; is formed of a composition for forming an adhesive layer containing,
상기 베이스층은 메틸메타크릴레이트 단량체 단위 23-27 중량%, n-부틸메타크릴레이트 단량체 단위 23-27 중량%, 글리시딜메타크릴레이트 단량체 단위 23-27 중량% 및 하이드록시에틸 메타크릴레이트 단량체 단위 23-27 중량%인 제3 아크릴레이트계 공중합체 45-49 중량부; 중량평균분자량이 35,000-45,000인 폴리우레탄아크릴레이트 26-30 중량부; 에틸메타크릴레이트 3-7 중량부; 라우릴메타크릴레이트 2-6 중량부; 하이드록시에틸메타아크릴레이트 1-5 중량부; 메틸셀룰로오스 3-7 중량부; 프로필렌글리콜 1-5 중량부; 디메티콘 1-5 중량부; 및 소듐실리케이트 0.5-4 중량부;를 포함하는 베이스층 형성용 조성물로 형성된 것을 특징으로 하는 젤 네일 스티커의 사용방법을 제공한다.The base layer comprises 23-27 wt% of methyl methacrylate monomer units, 23-27 wt% of n-butyl methacrylate monomer units, 23-27 wt% of glycidyl methacrylate monomer units, and hydroxyethyl methacrylate. 45-49 parts by weight of the third acrylate-based copolymer having 23-27% by weight of monomer units; 26-30 parts by weight of polyurethane acrylate having a weight average molecular weight of 35,000-45,000; 3-7 parts by weight of ethyl methacrylate; 2-6 parts by weight of lauryl methacrylate; 1-5 parts by weight of hydroxyethyl methacrylate; 3-7 parts by weight of methylcellulose; 1-5 parts by weight of propylene glycol; 1-5 parts by weight of dimethicone; and 0.5-4 parts by weight of sodium silicate.
또한, 상기 젤 네일 스티커를 부착시키는 단계를 수행하고난 후, 손톱에 부착된 젤 네일 스티커 위에 몰드를 부착하는 단계; 몰드가 부착된 손톱을 UV 젤램프를 사용하여 경화시키는 단계; 경화된 젤 네일 스티커로부터 몰드를 제거하는 단계; 및 몰드가 제거된 젤 네일 스티커를 성형하여 마무리하는 단계;를 더 포함하는 것을 특징으로 하는 젤 네일 스티커의 사용방법을 제공한다.In addition, after performing the step of attaching the gel nail sticker, attaching a mold on the gel nail sticker attached to the nail; curing the nail to which the mold is attached using a UV gel lamp; removing the mold from the cured gel nail sticker; and shaping and finishing the gel nail sticker from which the mold has been removed.
본 발명에 따른 젤 네일 스티커는 제거시에 손톱의 손상을 최소화하여 젤네일 스티커 이용으로 손톱 손상에 우려를 줄일 수 있게 한다. 또한 영양성분 공급으로 젤 네일 스티커 사용시에도 기존 젤 네일 스티커보다 건강한 손톱을 유지할 수 있는 효과가 있다.The gel nail sticker according to the present invention minimizes damage to the nail during removal, thereby reducing concerns about nail damage by using the gel nail sticker. In addition, by supplying nutrients, even when using gel nail stickers, it is more effective than conventional gel nail stickers to maintain healthy nails.
도 1은 본 발명의 일 측면에서 제공되는 젤 네일 스티커(100)를 모식도로 나타낸 것이고;
도 2는 본 발명의 일 측면에서 제공되는 젤 네일 스티커(100)를 사용하기 전과 사용하고 난 후 손톱을 사진으로 나타낸 것이다.1 is a schematic diagram showing a
2 is a photograph showing nails before and after using the
이하에서는 첨부된 도면을 참조하여 다양한 실시예를 보다 상세하게 설명한다. 본 명세서에 기재된 실시예는 다양하게 변형될 수 있다. 특정한 실시예가 도면에서 묘사되고 상세한 설명에서 자세하게 설명될 수 있다. 그러나 첨부된 도면에 개시된 특정한 실시 예는 다양한 실시예를 쉽게 이해하도록 하기 위한 것일 뿐이다. 따라서 첨부된 도면에 개시된 특정 실시예에 의해 기술적 사상이 제한되는 것은 아니며, 발명의 사상 및 기술 범위에 포함되는 모든 균등물 또는 대체물을 포함하는 것으로 이해되어야 한다.Hereinafter, various embodiments will be described in more detail with reference to the accompanying drawings. The embodiments described in this specification may be modified in various ways. Certain embodiments may be depicted in the drawings and described in detail in the detailed description. However, specific embodiments disclosed in the accompanying drawings are only intended to facilitate understanding of various embodiments. Therefore, the technical idea is not limited by the specific embodiments disclosed in the accompanying drawings, and it should be understood to include all equivalents or substitutes included in the spirit and technical scope of the invention.
1차, 2차, 제1, 제2 등과 같이 서수를 포함하는 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 이러한 구성요소들은 상술한 용어에 의해 한정되지는 않는다. 상술한 용어는 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다.Terms including ordinal numbers such as primary, secondary, first, and second may be used to describe various elements, but these elements are not limited by the above-mentioned terms. The terminology described above is only used for the purpose of distinguishing one component from another.
본 명세서에서, '포함한다' 또는 '가지다' 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다. 어떤 구성요소가 다른 구성요소에 '연결되어' 있다거나 '접속되어' 있다고 언급된 때에는, 그 다른 구성요소에 직접적으로 연결되어 있거나 또는 접속되어 있을 수도 있지만, 중간에 다른 구성요소가 존재할 수도 있다고 이해되어야 할 것이다. 반면에, 어떤 구성요소가 다른 구성요소에 '직접 연결되어' 있다거나 '직접 접속되어' 있다고 언급된 때에는, 중간에 다른 구성요소가 존재하지 않는 것으로 이해되어야 할 것이다.In this specification, terms such as 'comprise' or 'having' are intended to designate that there is a feature, number, step, operation, component, part, or combination thereof described in the specification, but one or more other features It should be understood that the presence or addition of numbers, steps, operations, components, parts, or combinations thereof is not precluded. It is understood that when a component is referred to as being 'connected' or 'connected' to another component, it may be directly connected or connected to the other component, but other components may exist in the middle. It should be. On the other hand, when a component is referred to as being 'directly connected' or 'directly connected' to another component, it should be understood that no other component exists in the middle.
그 밖에도, 본 발명을 설명함에 있어서, 관련된 공지 기능 혹은 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우, 그에 대한 상세한 설명은 축약하거나 생략한다.In addition, in describing the present invention, if it is determined that a detailed description of a related known function or configuration may unnecessarily obscure the subject matter of the present invention, the detailed description thereof will be abbreviated or omitted.
본 발명은the present invention
박리필름층(10); release
상기 박리필름층(10) 상에 형성된 접착층(20); an
상기 접착층(20) 상에 형성된 베이스층(30); a
상기 베이스층(30) 상에 형성된 컬러층(40); a
상기 컬러층(40) 상에 형성된 인쇄층(50); a printed
상기 인쇄층(50) 상에 형성된 젤층(60); 및a
상기 젤층(60) 상에 형성된 이형필름층(70);을 포함하는 젤 네일 스티커(100)를 제공한다.It provides a
이때, 도 1에 본 발명의 일 측면에서 제공되는 젤 네일 스티커(100)를 모식도로 나타내었으며, 이하, 도 1을 참조하여 본 발명에 따른 젤 네일 스티커(100)에 대하여 상세히 설명한다.At this time, FIG. 1 shows a schematic diagram of a
본 발명에 따른 젤 네일 스티커(100)는 박리필름층(10)을 포함한다.The
상기 박리필름층(10)은 젤 네일 스티커(100)의 훼손 없이 접착층(20)과 분리되도록 하는 것으로, 보관시 접착층의 기능을 유지하며, 보관상자 등과 같은 패키징 부재에 접착되는 문제점을 방지하기 위한 것이다. 이와 같은 박리필름층(100)은 투명 또는 반투명재질로 다양한 재료가 적용될 수 있으며, 대표적으로는 불소표면처리 및 실리콘계열 코팅처리된 필름이 여기에 해당한다.The
본 발명에 따른 젤 네일 스티커(100)는 접착층(20)을 포함한다. 상기 접착층(20)은 상기 박리필름층(10) 상에 형성된다.The
상기 접착층(20)은 에틸메타크릴레이트 단량체 단위 23-27 중량%, n-부틸메타크릴레이트 단량체 단위 23-27 중량%, 글리시딜메타크릴레이트 단량체 단위 23-27 중량% 및 하이드록시에틸 메타크릴레이트 단량체 단위 23-27 중량%인 제1 아크릴레이트계 공중합체 31-35 중량부; 메틸메타크릴레이트 단량체 단위 23-27 중량%, 에틸메타크릴레이트 단량체 단위 23-27 중량%, 아크릴산 단량체 단위 23-27 중량% 및 메톡시에틸메타크릴레이트 단량체 단위 23-27 중량%인 제2 아크릴레이트계 공중합체 12-16 중량부; 올레핀계 불포화기를 갖는 친수성 폴리우레탄 10-14 중량부; 리대두단백, 귀리단백분말 및 분리완두단백이 1:1:1의 중량비율로 혼합된 제1 조성물 3-7 중량부; 레몬껍질 추출물, 사과껍질 추출물, 양파껍질 추출물, 수박껍질 추출물 및 바나나껍질 추출물이 3:3:2:1:1의 중량비율로 혼합된 제2 조성물 2-6 중량부; 비타민 혼합물 2-6 중량부; 오미자씨 오일 2-6 중량부; 복숭아씨 오일 2-6 중량부; 리모넨 0.5-4 중량부; 리날룰 0.5-4 중량부; 이소퀘르시트린 0.5-4 중량부; 나이아신아마이드 0.1-1 중량부; 폴리글리세릴-6스테아레이트 0.1-1 중량부; 폴리글리세릴-2스테아레이트 0.1-1 중량부; 프로필렌글라이콜 1-5 중량부; 세테아릴알코올 1-5 중량부; 글리세릴스테아레이트 0.5-4 중량부; 스테아릴알코올 0.1-1 중량부; 프로판다이올 1-5 중량부; 알란토인 0.1-1 중량부; 및 트로메타민 0.1-1 중량부;를 포함하는 접착층 형성용 조성물로 형성된 것이 바람직하고, 에틸메타크릴레이트 단량체 단위 23-27 중량%, n-부틸메타크릴레이트 단량체 단위 23-27 중량%, 글리시딜메타크릴레이트 단량체 단위 23-27 중량% 및 하이드록시에틸 메타크릴레이트 단량체 단위 23-27 중량%인 제1 아크릴레이트계 공중합체 32-34 중량부; 메틸메타크릴레이트 단량체 단위 23-27 중량%, 에틸메타크릴레이트 단량체 단위 23-27 중량%, 아크릴산 단량체 단위 23-27 중량% 및 메톡시에틸메타크릴레이트 단량체 단위 23-27 중량%인 제2 아크릴레이트계 공중합체 13-15 중량부; 올레핀계 불포화기를 갖는 친수성 폴리우레탄 11-13 중량부; 리대두단백, 귀리단백분말 및 분리완두단백이 1:1:1의 중량비율로 혼합된 제1 조성물 4-6 중량부; 레몬껍질 추출물, 사과껍질 추출물, 양파껍질 추출물, 수박껍질 추출물 및 바나나껍질 추출물이 3:3:2:1:1의 중량비율로 혼합된 제2 조성물 3-5 중량부; 비타민 혼합물 3-5 중량부; 오미자씨 오일 3-5 중량부; 복숭아씨 오일 3-5 중량부; 리모넨 1-3 중량부; 리날룰 1-3 중량부; 이소퀘르시트린 1-3 중량부; 나이아신아마이드 0.3-0.7 중량부; 폴리글리세릴-6스테아레이트 0.3-0.7 중량부; 폴리글리세릴-2스테아레이트 0.3-0.7 중량부; 프로필렌글라이콜 2-4 중량부; 세테아릴알코올 2-4 중량부; 글리세릴스테아레이트 1-3 중량부; 스테아릴알코올 0.3-0.7 중량부; 프로판다이올 2-4 중량부; 알란토인 0.3-0.7 중량부; 및 트로메타민 0.3-0.7 중량부;를 포함하는 접착층 형성용 조성물로 형성된 것이 더욱 바람직하다.The adhesive layer 20 includes 23-27 wt% of ethyl methacrylate monomer units, 23-27 wt% of n-butyl methacrylate monomer units, 23-27 wt% of glycidyl methacrylate monomer units, and hydroxyethyl meta 31-35 parts by weight of the first acrylate-based copolymer having 23-27% by weight of acrylate monomer units; A second acrylic comprising 23-27% by weight of methyl methacrylate monomer units, 23-27% by weight of ethyl methacrylate monomer units, 23-27% by weight of acrylic acid monomer units, and 23-27% by weight of methoxyethyl methacrylate monomer units 12-16 parts by weight of a late copolymer; 10-14 parts by weight of hydrophilic polyurethane having an olefinic unsaturated group; 3-7 parts by weight of a first composition in which soybean protein, oat protein powder and isolated pea protein are mixed in a weight ratio of 1:1:1; 2-6 parts by weight of a second composition in which lemon peel extract, apple peel extract, onion peel extract, watermelon peel extract, and banana peel extract are mixed in a weight ratio of 3:3:2:1:1; 2-6 parts by weight of the vitamin mixture; Schisandra seed oil 2-6 parts by weight; 2-6 parts by weight of peach seed oil; 0.5-4 parts by weight of limonene; linalool 0.5-4 parts by weight; 0.5-4 parts by weight of isoquercitrin; Niacinamide 0.1-1 part by weight; 0.1-1 part by weight of polyglyceryl-6 stearate; 0.1-1 part by weight of polyglyceryl-2stearate; 1-5 parts by weight of propylene glycol; 1-5 parts by weight of cetearyl alcohol; 0.5-4 parts by weight of glyceryl stearate; 0.1-1 part by weight of stearyl alcohol; 1-5 parts by weight of propanediol; 0.1-1 part by weight of allantoin; And 0.1-1 part by weight of tromethamine; preferably formed of a composition for forming an adhesive layer containing 23-27% by weight of ethyl methacrylate monomer units, 23-27% by weight of n-butyl methacrylate monomer units, glyc 32-34 parts by weight of a first acrylate-based copolymer comprising 23-27% by weight of cidyl methacrylate monomer units and 23-27% by weight of hydroxyethyl methacrylate monomer units; A second acrylic comprising 23-27% by weight of methyl methacrylate monomer units, 23-27% by weight of ethyl methacrylate monomer units, 23-27% by weight of acrylic acid monomer units, and 23-27% by weight of methoxyethyl methacrylate monomer units 13-15 parts by weight of a late copolymer; 11-13 parts by weight of hydrophilic polyurethane having an olefinic unsaturated group; 4-6 parts by weight of a first composition in which red soybean protein, oat protein powder and isolated pea protein are mixed in a weight ratio of 1:1:1; 3-5 parts by weight of a second composition in which lemon peel extract, apple peel extract, onion peel extract, watermelon peel extract, and banana peel extract are mixed in a weight ratio of 3:3:2:1:1; 3-5 parts by weight of the vitamin mixture; Schisandra seed oil 3-5 parts by weight; 3-5 parts by weight of peach seed oil; 1-3 parts by weight of limonene; 1-3 parts by weight of Linalool; 1-3 parts by weight of isoquercitrin; Niacinamide 0.3-0.7 parts by weight; 0.3-0.7 parts by weight of polyglyceryl-6stearate; 0.3-0.7 parts by weight of polyglyceryl-2stearate; 2-4 parts by weight of propylene glycol; 2-4 parts by weight of cetearyl alcohol; 1-3 parts by weight of glyceryl stearate; 0.3-0.7 parts by weight of stearyl alcohol; 2-4 parts by weight of propanediol; 0.3-0.7 parts by weight of allantoin; And tromethamine 0.3-0.7 parts by weight; more preferably formed of a composition for forming an adhesive layer containing.
상기 접착층 형성용 조성물은 제1 아크릴레이트계 공중합체, 제2 아크릴레이트계 공중합체 및 올레핀계 불포화기를 갖는 친수성 폴리우레탄을 포함하여 접착층이 구현되고, 제거에 용이하다.The composition for forming an adhesive layer includes a first acrylate-based copolymer, a second acrylate-based copolymer, and a hydrophilic polyurethane having an olefin-based unsaturated group, so that an adhesive layer is realized and easily removed.
상기 올레핀계 불포화기를 갖는 친수성 폴리우레탄은 폴리이소시아네이트와 히드록실-관능성 폴리알킬렌 옥사이드의 반응에 의해 수득가능하다.The hydrophilic polyurethane having olefinically unsaturated groups is obtainable by reaction of a polyisocyanate with a hydroxyl-functional polyalkylene oxide.
이러한 폴리알킬렌 옥사이드는 바람직하게는 존재하는 옥살킬렌 단위를 기준으로 50 중량％ 이상, 보다 바람직하게는 60 중량％ 이상의 에틸렌 옥사이드 함량을 갖는다.These polyalkylene oxides preferably have an ethylene oxide content of at least 50% by weight, more preferably at least 60% by weight, based on the oxalkylen units present.
이들 폴리알킬렌 옥사이드가 폴리올 또는 아민, 예컨대 물 (디올로서 간주됨), 에틸렌 글리콜, 프로필렌 글리콜, 부틸렌 글리콜, 글리세롤, 트리메틸올프로판(TMP), 소르비톨, 펜타에리트리톨, 트리에탄올아민, 암모니아 또는 에틸렌디아민으로 개시하여, 50-100 중량％, 바람직하게는 60-82 중량％의 에틸렌 옥사이드 함량을 갖는 에틸렌 옥사이드 및 프로필렌 옥사이드의 공중합체를 포함하는 것이 특히 바람직하다.These polyalkylene oxides are polyols or amines such as water (considered as diols), ethylene glycol, propylene glycol, butylene glycol, glycerol, trimethylolpropane (TMP), sorbitol, pentaerythritol, triethanolamine, ammonia or ethylene Particular preference is given to comprising copolymers of ethylene oxide and propylene oxide, initiated with diamines, having an ethylene oxide content of 50-100% by weight, preferably 60-82% by weight.
이들 폴리알킬렌 옥사이드의 몰질량은 바람직하게는 Mn = 2,000-20,000 g/몰, 보다 바람직하게는 4,000-8,500 g/몰이다.The molar mass of these polyalkylene oxides is preferably Mn = 2,000-20,000 g/mol, more preferably 4,000-8,500 g/mol.
OH 관능가는 바람직하게는 2-6, 보다 바람직하게는 3-6, 가장 바람직하게는 3-4이다.The OH functionality is preferably 2-6, more preferably 3-6, most preferably 3-4.
상기 폴리이소시아네이트는 예를 들면, 올레핀계 불포화 이소시아네이트, 예컨대 MOI (이소시아네이토에틸메타크릴레이트), TMI (3-이소프로페닐-α,α-디메틸벤질 이소시아네이트) 또는 알릴 이소시아네이트가 포함된다.The polyisocyanates include, for example, olefinically unsaturated isocyanates such as MOI (isocyanatoethyl methacrylate), TMI (3-isopropenyl-α,α-dimethylbenzyl isocyanate) or allyl isocyanate.
또한 올레핀계 불포화 디- 또는 폴리이소시아네이트 대신에 또는 부가하여 포화 디- 또는 폴리이소시아네이트를 사용하고 후속적으로 불포화기 이외에 1개 이상의 이소시아네이트-반응성 기를 갖는 화합물과의 반응에 의해 올레핀계 불포화 기를 도입하는 것도 가능하다.It is also possible to use a saturated di- or polyisocyanate instead of or in addition to an olefinically unsaturated di- or polyisocyanate and subsequently introduce an olefinically unsaturated group by reaction with a compound having at least one isocyanate-reactive group in addition to the unsaturated group. possible.
바람직하게는, 폴리알킬렌 옥사이드의 OH 기를 기준으로 1.6-30배 당량의 디이소시아네이트의 반응에 의해 예비중합체를 제조한다. NCO/OH 비율은 바람직하게는 4:1-12:1의 범위, 보다 바람직하게는 2:1이다.Preferably, the prepolymer is prepared by reaction of 1.6 to 30 equivalents of diisocyanate based on the OH groups of the polyalkylene oxide. The NCO/OH ratio is preferably in the range of 4:1-12:1, more preferably 2:1.
바람직하게는 아민 또는 주석 화합물과 같은 촉매 및/또는 벤조일 클로라이드, 이소프탈로일 클로라이드, 디부틸포스페이트, 3-클로로프로피온산 또는 메틸 토실레이트와 같은 안정화제를 제조 중에 첨가할 수 있다.Catalysts such as preferably amines or tin compounds and/or stabilizers such as benzoyl chloride, isophthaloyl chloride, dibutylphosphate, 3-chloropropionic acid or methyl tosylate may be added during preparation.
반응 온도는 20-120℃의 범위, 바람직하게는 60-100℃의 범위이다.The reaction temperature is in the range of 20-120°C, preferably in the range of 60-100°C.
과량의 미반응 이소시아네이트는 후속적으로, 바람직하게는 박막 증류에 의해 제거될 수 있다.Excess unreacted isocyanate can subsequently be removed, preferably by thin film distillation.
상기 디이소시아네이트의 예로는 HDI, IPDI, 비스이소시아네이토시클로헥실메탄, 2,2,4-트리메틸헥사메틸렌디이소시아네이트, 비스이소시아네이토메틸시클로헥산, 비스이소시아네이토메틸트리시클로데칸, 크실릴렌 디이소시아네이트, 테트라메틸크실릴렌 디이소시아네이트, 노르보르난 디이소시아네이트, 시클로헥산 디이소시아네이트, 디이소시아네이토도데칸, 2,4-TDI, 2,6-TDI, 2,2-, 2,4- 또는 4,4-MDI, 4,4'-디이소시아네이토-3,3'-디메틸비페닐, 3,4'-디이소시아네이토디페닐 에테르, 1,5-나프틸렌 디이소시아네이트 또는 이들의 혼합물이 있다.Examples of the diisocyanate include HDI, IPDI, bisisocyanatocyclohexylmethane, 2,2,4-trimethylhexamethylenediisocyanate, bisisocyanatomethylcyclohexane, bisisocyanatomethyltricyclodecane, xylylene Diisocyanate, tetramethylxylylene diisocyanate, norbornane diisocyanate, cyclohexane diisocyanate, diisocyanatododecane, 2,4-TDI, 2,6-TDI, 2,2-, 2,4- or 4,4-MDI, 4,4'-diisocyanato-3,3'-dimethylbiphenyl, 3,4'-diisocyanatodiphenyl ether, 1,5-naphthylene diisocyanate or mixtures thereof there is.
그러나, 상기한 종류의 지방족 디이소시아네이트는 생성 폴리우레탄의 가수분해 생성물이 일반적으로 독물학자에 의해 안정한 것으로 인정되기 때문에 바람직하다.However, aliphatic diisocyanates of the type described above are preferred because the resulting polyurethane hydrolysis products are generally recognized by toxicologists as stable.
이어서, 그에 따라 함유된 이소시아네이트-관능성 예비중합체를 불포화기 이외에 1개 이상의 이소시아네이트-반응성 기를 갖는 화합물과 반응시킨다. 바람직한 이소시아네이트-반응성 기는 아미노 또는 히드록실 관능기, 바람직하게는 히드록실 관능기이다.The isocyanate-functional prepolymer thus contained is then reacted with a compound having at least one isocyanate-reactive group in addition to the unsaturated group. Preferred isocyanate-reactive groups are amino or hydroxyl functions, preferably hydroxyl functions.
NCO 기 대 NCO-반응성 기의 당량비는 바람직하게는 1.5-1.0:1의 범위이다. 과량의 NCO-반응성 기는 피해야만 하거나, 또는 불포화 단량체는 남게 될 것이다. 이러한 화합물이 부족한 경우에, 잔류하는 유리 NCO 기는 적용 전에 물 또는 모노올, 예컨대 메탄올, 에탄올 또는 이소프로판올과의 반응에 의해 제거된다.The equivalent ratio of NCO groups to NCO-reactive groups is preferably in the range of 1.5-1.0:1. Excessive NCO-reactive groups must be avoided or unsaturated monomers will remain. In case of a shortage of these compounds, the remaining free NCO groups are removed prior to application by reaction with water or a monool such as methanol, ethanol or isopropanol.
올레핀계 불포화 기 및 1개 이상의 이소시아네이트-반응성 기를 갖는 바람직한 화합물은 바람직하게는 히드록시 아크릴레이트 및 -메타크릴레이트, 예컨대 히드록시에틸 아크릴레이트, 히드록시에틸 메타크릴레이트, 히드록시프로필 아크릴레이트, 히드록시프로필 메타크릴레이트, 히드록시부틸 아크릴레이트, 히드록시부틸 메타크릴레이트, 글리세롤 디아크릴레이트, 글리세롤 디메타크릴레이트, 글리세롤 모노아크릴레이트 모노메타크릴레이트, 글리세롤 모노알릴 에테르 메타크릴레이트, TMP 디아크릴레이트, TMP 디메타크릴레이트, 펜타에리트리톨 트리아크릴레이트, 펜타에리트리톨 트리메타크릴레이트 및 이들의 임의의 바람직한 혼합물이다.Preferred compounds having an olefinically unsaturated group and at least one isocyanate-reactive group are preferably hydroxy acrylates and -methacrylates such as hydroxyethyl acrylate, hydroxyethyl methacrylate, hydroxypropyl acrylate, hydroxyethyl acrylate, Roxypropyl Methacrylate, Hydroxybutyl Acrylate, Hydroxybutyl Methacrylate, Glycerol Diacrylate, Glycerol Dimethacrylate, Glycerol Monoacrylate Monomethacrylate, Glycerol Monoallyl Ether Methacrylate, TMP Diacryl rate, TMP dimethacrylate, pentaerythritol triacrylate, pentaerythritol trimethacrylate, and any desired mixtures thereof.
올레핀계 불포화 기를 갖는 친수성 폴리우레탄으로의 전환은, 바람직하게는 중합 억제제, 예컨대 히드로퀴논, 히드로퀴논 모노알킬 에테르, 디-tert-부틸크레졸 또는 메틸렌비스(tert-부틸크레졸), 및 OH-NCO 반응의 촉매, 예컨대 주석 화합물 또는 아민의 존재하에 20-80℃의 온도에서 수행된다.Conversion to a hydrophilic polyurethane having olefinically unsaturated groups is preferably carried out using a polymerization inhibitor, such as hydroquinone, hydroquinone monoalkyl ether, di-tert-butylcresol or methylenebis(tert-butylcresol), and a catalyst for the OH-NCO reaction. , for example in the presence of a tin compound or an amine at a temperature of 20-80°C.
상기 제1 조성물, 제2 조성물, 비타민 혼합물, 오미자씨 오일, 복숭아씨 오일, 리모넨, 리날룰 등의 영양성분을 포함하여 젤 네일 스티커 제거 후에 발생하는 손톱의 손상이 거의 없을 뿐만 아니라, 영양성분 공급에 용이하다. 또한 손톱의 손상도를 낮추고 유분과 수분을 유지할 수 있다.Including nutrients such as the first composition, the second composition, the vitamin mixture, Schisandra seed oil, peach seed oil, limonene, and linalool, there is little damage to the nails that occurs after removing the gel nail sticker, and nutritional ingredients are supplied. easy to In addition, it can lower the degree of damage to nails and maintain oil and moisture.
상기 비타민 혼합물은 비타민 A 90-110 중량부, 비타민 B1 40-50 중량부, 비타민 B2 65-85 중량부, 비타민 B3 390-410 중량부, 비타민 B4 80-100 중량부, 비타민 B6 20-40 중량부, 비타민 D 150-170 중량부 및 비타민 E 790-810 중량부를 포함하는 것이 바람직하다.The vitamin mixture contains 90-110 parts by weight of vitamin A, 40-50 parts by weight of vitamin B1, 65-85 parts by weight of vitamin B2, 390-410 parts by weight of vitamin B3, 80-100 parts by weight of vitamin B4, and 20-40 parts by weight of vitamin B6. 150-170 parts by weight of vitamin D and 790-810 parts by weight of vitamin E are preferred.
상기 오미자씨 오일 및 복숭아씨 오일은, 오미자 및 복숭아를 파쇄한 후 세척하여 오미자씨 및 복숭아씨를 분리하는 단계; 분리된 오미자씨 및 복숭아씨를 분쇄하여 오미자씨분말 및 복숭아씨분말을 준비하는 단계; 상기 오미자씨분말 및 복숭아씨분말을 1:1의 중량비율로 혼합하여 제2 혼합분말을 준비하는 단계; 상기 제2 혼합분말 및 헥산을 혼합하고, 28-32℃의 온도에서 2-4일 동안 교반하여 추출물을 제조하는 단계; 및 상기 추출물을 여과하고 감압농축한 후 원심분리하여 이물질을 제거한 후, 감압증류하는 단계;를 포함하는 오미자씨 오일 및 복숭아씨 오일을 제조하는 단계;를 수행하여 제조한 것을 사용하는 것이 바람직하다.The Schisandra seed oil and peach seed oil are separated from Schisandra seeds and peach seeds by washing after crushing Schisandra seeds and peaches; Preparing Schisandra seed powder and peach seed powder by grinding the separated Schizandra seeds and peach seeds; Preparing a second mixed powder by mixing the Schizandra seed powder and peach seed powder in a weight ratio of 1: 1; Preparing an extract by mixing the second mixed powder and hexane and stirring at a temperature of 28-32 ° C for 2-4 days; It is preferable to use those prepared by carrying out; preparing Schisandra seed oil and peach seed oil comprising; filtering and concentrating the extract under reduced pressure, centrifuging to remove foreign substances, and then distilling under reduced pressure.
본 발명에 따른 젤 네일 스티커(100)는 베이스층(30)을 포함한다. 상기 베이스층(30)은 상기 접착층(20) 상에 형성된다.The
상기 베이스층(30)은 메틸메타크릴레이트 단량체 단위 23-27 중량%, n-부틸메타크릴레이트 단량체 단위 23-27 중량%, 글리시딜메타크릴레이트 단량체 단위 23-27 중량% 및 하이드록시에틸 메타크릴레이트 단량체 단위 23-27 중량%인 제3 아크릴레이트계 공중합체 45-49 중량부; 중량평균분자량이 35,000-45,000인 폴리우레탄아크릴레이트 26-30 중량부; 에틸메타크릴레이트 3-7 중량부; 라우릴메타크릴레이트 2-6 중량부; 하이드록시에틸메타아크릴레이트 1-5 중량부; 메틸셀룰로오스 3-7 중량부; 프로필렌글리콜 1-5 중량부; 디메티콘 1-5 중량부; 및 소듐실리케이트 0.5-4 중량부;를 포함하는 베이스층 형성용 조성물로 형성된 것이 바람직하고, 메틸메타크릴레이트 단량체 단위 23-27 중량%, n-부틸메타크릴레이트 단량체 단위 23-27 중량%, 글리시딜메타크릴레이트 단량체 단위 23-27 중량% 및 하이드록시에틸 메타크릴레이트 단량체 단위 23-27 중량%인 제3 아크릴레이트계 공중합체 46-48 중량부; 중량평균분자량이 35,000-45,000인 폴리우레탄아크릴레이트 27-29 중량부; 에틸메타크릴레이트 4-6 중량부; 라우릴메타크릴레이트 3-5 중량부; 하이드록시에틸메타아크릴레이트 2-4 중량부; 메틸셀룰로오스 4-6 중량부; 프로필렌글리콜 2-4 중량부; 디메티콘 2-4 중량부; 및 소듐실리케이트 1-3 중량부;를 포함하는 베이스층 형성용 조성물로 형성된 것이 더욱 바람직하다.The base layer 30 includes 23-27% by weight of methyl methacrylate monomer units, 23-27% by weight of n-butyl methacrylate monomer units, 23-27% by weight of glycidyl methacrylate monomer units, and hydroxyethyl 45-49 parts by weight of the third acrylate-based copolymer comprising 23-27% by weight of methacrylate monomer units; 26-30 parts by weight of polyurethane acrylate having a weight average molecular weight of 35,000-45,000; 3-7 parts by weight of ethyl methacrylate; 2-6 parts by weight of lauryl methacrylate; 1-5 parts by weight of hydroxyethyl methacrylate; 3-7 parts by weight of methylcellulose; 1-5 parts by weight of propylene glycol; 1-5 parts by weight of dimethicone; and 0.5-4 parts by weight of sodium silicate. 46-48 parts by weight of a third acrylate-based copolymer comprising 23-27% by weight of cidyl methacrylate monomer units and 23-27% by weight of hydroxyethyl methacrylate monomer units; 27-29 parts by weight of polyurethane acrylate having a weight average molecular weight of 35,000-45,000; 4-6 parts by weight of ethyl methacrylate; 3-5 parts by weight of lauryl methacrylate; 2-4 parts by weight of hydroxyethyl methacrylate; 4-6 parts by weight of methylcellulose; 2-4 parts by weight of propylene glycol; 2-4 parts by weight of dimethicone; And 1-3 parts by weight of sodium silicate; more preferably formed of a composition for forming a base layer comprising.
상기 베이스층 형성용 조성물은 제3 아크릴레이트계 공중합체, 폴리우레탄아크릴레이트, 에틸메타크릴레이트, 라우릴메타크릴레이트, 하이드록시에틸메타아크릴레이트를 포함하여 베이스층이 구현되고, 제거에 용이하다.The composition for forming the base layer includes a third acrylate-based copolymer, polyurethane acrylate, ethyl methacrylate, lauryl methacrylate, and hydroxyethyl methacrylate to implement a base layer and is easy to remove. .
본 발명에 따른 젤 네일 스티커(100)는 컬러층(40)을 포함한다. 상기 컬러층(40)은 상기 베이스층(30) 상에 형성된다.The
상기 컬러층(40)은 젤 네일 스티커(100)의 배경색상을 표현해주기 위한 것으로, 다양한 색상을 유지하는 안료를 도포하거나, UV 경화수지에 안료를 혼합하여 적용할 수 있다.The
본 발명에 따른 젤 네일 스티커(100)는 인쇄층(50)을 포함한다. 상기 인쇄층(50)은 상기 컬러층(40) 상에 형성된다.The
상기 인쇄층(30)은 다양한 인쇄기법을 이용한 무늬 표현, 운모, 미립자 등의 심미성을 위한 다양한 재료를 도포하거나 첨가하여 인쇄할 수 있다. 여기서, 상기 인쇄층(30)을 형성하기 위한 인쇄방법으로는 실크스크린 인쇄, 플렉소그래픽 인쇄, 그라비아 인쇄, 디지털 인쇄, 디지털 플렉소그래픽 인쇄, 오프셋 인쇄, UV인쇄, 홀로그래픽 적층인쇄, 핫스탬핑 적층인쇄, 금박 또는 은박 적층인쇄, 글리터 인쇄 중 어느 하나가 적용될 수 있으나, 이를 한정하는 것은 아니며, 다양한 기법의 인쇄방법이 적용될 수 있다.The printed
본 발명에 따른 젤 네일 스티커(100)는 젤층(60)을 포함한다. 상기 젤층(60)은 상기 인쇄층(50) 상에 형성된다.The
상기 젤층(60)은 UV 경화수지 5-60 중량% 및 열경화수지 40-95 중량%를 포함하여 자외선에 의해 경화되도록 하는 것이다.The
이 때, 상기 UV 경화수지가 60 중량% 초과의 양으로 사용되거나 열경화수지가 40 중량% 미만의 양으로 사용될 경우 경화성이 저하되며, 상기 UV 경화수지가5 중량% 미만의 양으로 사용되거나 열경화수지가 95 중량% 초과의 양으로 사용될 경우에는 고경화성으로 유연성이 저하되는 단점이 있다.At this time, when the UV curable resin is used in an amount of more than 60% by weight or the thermosetting resin is used in an amount of less than 40% by weight, the curability is lowered, and when the UV curable resin is used in an amount of less than 5% by weight or the heat curing resin is used in an amount of less than 5% by weight When the cured resin is used in an amount of more than 95% by weight, there is a disadvantage in that flexibility is lowered due to high curability.
또한, 상기 UV 경화수지에는 올리고머인 UV 경화수지의 점도를 조절하기 위해 반응성 모노머 희석제 10-30 중량부를 더 혼합할 수 있으며, 상기와 같은 희석제는 2-에틸헥실(메타)아크릴레이트, 2-디카프로락톤 에틸 아크릴레이트, 싸이클로헥실(메타)아크릴레이트, 페녹시에틸(메타)아크릴레이트, 아이소보닐(메타)아크릴레이트, 아크릴로일몰포린, N-비닐피로리돈, N-비닐카프로락탐, 디메틸아미노에틸(메타)아크릴레이트, 트리프로필렌글리콜디(메타)아크릴레이트, 싸이클로펜테닐(메타)아크릴레이트, 트리싸이클로 데칸디메타놀디(메타)아크릴레이트 및 트리메틸올프로판트리(메타)아크릴레이트로 이루어진 군 중에서 1종 또는 2종 이상을 혼합하여 적용하게 된다.In addition, 10-30 parts by weight of a reactive monomer diluent may be further mixed with the UV curable resin to adjust the viscosity of the UV curable resin, which is an oligomer. Prolactone ethyl acrylate, cyclohexyl (meth)acrylate, phenoxyethyl (meth)acrylate, isobornyl (meth)acrylate, acryloylmorpholine, N-vinylpyrrolidone, N-vinylcaprolactam, dimethyl Consisting of aminoethyl (meth)acrylate, tripropylene glycoldi (meth)acrylate, cyclopentenyl (meth)acrylate, tricyclodecanedimethanoldi (meth)acrylate and trimethylolpropanetri (meth)acrylate One type or a mixture of two or more types from the group is applied.
상기 젤층(60)은 에폭시 수지, 아크릴 수지, 폴리에스테르 수지, 셀롤로오스, 테르펜, 모노머, 올리고머, 우레탄 아크릴레이트, 에폭시 아크릴레이트, 폴리에스테르 아크릴레이트, 우레탄 아크릴레이트, 에폭시 아크릴레이트, 폴리에스테르 아크릴레이트 및 셀롤로오스로 이루어진 군에서 선택된 하나 이상의 수지를 추가로 포함하는 것을 특징으로 한다. The
또한, 상기 젤층(60)은 심미감을 위해, 운모, 미립자 등과 같은 부재를 더 포함할 수 있다.In addition, the
본 발명에 따른 젤 네일 스티커(100)는 이형필름층(70)을 포함한다. 상기 이형필름층(70)은 상기 젤층(60) 상에 형성된다.The
상기 이형필름층(70)은 투명한 필름으로 젤 네일 스티커(100)의 최상단에 위치하며 긁힘 등의 외부충격으로부터 보호하는 역할을 하게 되며, 손톱에 제품을 부착한 후 사용자에 의해 제거될 수 있다.The
또한, 본 발명은In addition, the present invention
손톱을 깨끗하게 정리하는 단계;cleaning nails;
정리된 손톱에 전처리제를 도포한 후 건조하는 단계; 및Applying a pretreatment agent to the prepared nails and then drying; and
건조된 손톱에 박리필름층을 제거한 젤 네일 스티커를 부착시키는 단계;를 포함하는 젤 네일 스티커의 사용방법을 제공한다.It provides a method of using a gel nail sticker including the step of attaching a gel nail sticker from which the peeling film layer is removed to the dried nail.
이하, 본 발명에 따른 젤 네일 스티커의 사용방법에 대하여 각 단계별로 상세히 설명한다.Hereinafter, the method of using the gel nail sticker according to the present invention will be described in detail for each step.
먼저, 본 발명에 따른 젤 네일 스티커의 사용방법은 손톱을 깨끗하게 정리하는 단계를 포함한다.First, the method of using the gel nail sticker according to the present invention includes the step of cleaning the nails.
상기 단계에서는 손톱을 정리한다. 세정액으로 세척할 수 있다.In this step, the nails are trimmed. It can be washed with a cleaning solution.
본 발명에 따른 젤 네일 스티커의 사용방법은 정리된 손톱에 전처리제를 도포한 후 건조하는 단계를 포함한다.The method of using the gel nail sticker according to the present invention includes applying a pretreatment agent to the prepared nails and then drying them.
상기 전처리제는 로즈마리추출물 및 오미자추출물을 포함하는 천연추출물 18-22 중량부; 현미, 보리, 귀리, 통밀, 호밀, 맥아, 대두, 수수, 검정콩 및 검정깨로부터 제조되는 곡물 발효분말 10-14 중량부; 아밀로스 3-7 중량부; 글리세린 3-7 중량부; 프로필렌글리콜 2-6 중량부; 부틸렌글리콜 2-6 중량부; 포스파티딜에탄올아민 3-7 중량부; 에탄올 13-17 중량부; 및 당근수 28-32 중량부;를 포함하는 것이 바람직하고, 로즈마리추출물 및 오미자추출물을 포함하는 천연추출물 19-21 중량부; 현미, 보리, 귀리, 통밀, 호밀, 맥아, 대두, 수수, 검정콩 및 검정깨로부터 제조되는 곡물 발효분말 11-13 중량부; 아밀로스 4-6 중량부; 글리세린 4-6 중량부; 프로필렌글리콜 3-5 중량부; 부틸렌글리콜 3-5 중량부; 포스파티딜에탄올아민 4-6 중량부; 에탄올 14-16 중량부; 및 당근수 29-31 중량부;를 포함하는 것이 더욱 바람직하다.18-22 parts by weight of natural extracts including rosemary extract and Schisandra chinensis extract; 10-14 parts by weight of fermented grain powder prepared from brown rice, barley, oats, whole wheat, rye, malt, soybean, sorghum, black soybean and black sesame; 3-7 parts by weight of amylose; 3-7 parts by weight of glycerin; 2-6 parts by weight of propylene glycol; 2-6 parts by weight of butylene glycol; 3-7 parts by weight of phosphatidylethanolamine; 13-17 parts by weight of ethanol; And 28-32 parts by weight of carrots; preferably containing, 19-21 parts by weight of natural extracts including rosemary extract and Schisandra chinensis extract; 11-13 parts by weight of fermented grain powder prepared from brown rice, barley, oats, whole wheat, rye, malt, soybean, sorghum, black soybean and black sesame; 4-6 parts by weight of amylose; 4-6 parts by weight of glycerin; 3-5 parts by weight of propylene glycol; 3-5 parts by weight of butylene glycol; 4-6 parts by weight of phosphatidylethanolamine; 14-16 parts by weight of ethanol; It is more preferable to include; and 29-31 parts by weight of carrots.
본 발명에 따른 젤 네일 스티커 사용방법은 전처리제를 손톱에 도포하여 손톱에 발생한 미세 흠집 등을 개선하고 젤 네일 스티커의 부착력을 향상시킬 수 있다. 더욱이 추가 영양성분을 공급하여 손톱의 수분 유지를 도와준다.In the method of using the gel nail sticker according to the present invention, a pretreatment agent is applied to the nail to improve fine scratches on the nail and improve the adhesive strength of the gel nail sticker. Moreover, it provides additional nutrients to help keep nails hydrated.
상기 천연추출물은, 로즈마리 및 오미자를 세척하고, 적절한 크기로 자른 뒤 동결건조시키고, 분쇄하여 로즈마리분말 및 오미자분말을 준비하는 단계; 상기 로즈마리분말 및 오미자분말을 1:1의 중량비율로 혼합하여 혼합분말을 준비하는 단계; 상기 혼합분말 및 물을 혼합하고, 교반을 수행하며 95-105℃의 온도에서 10-14시간 동안 1차 열수추출을 수행하는 단계; 1차 열수추출을 수행하고난 후, 여과지로 여과한 다음 그 여액을 동결건조하여 제1 추출물을 제조하는 단계; 1차 열수추출을 수행하고난 후, 여과지로 여과한 다음 남은 고형물을 다시 물과 혼합하고, 135-145℃의 온도에서 4-8시간 동안 2차 열수추출을 수행하는 단계; 2차 열수추출 후, 여과지로 여과한 다음 그 여액을 동결건조하여 제2 추출물을 제조하는 단계; 및 상기 제1 추출물 및 제2 추출물을 혼합하는 단계;를 수행하여 제조되는 것을 사용한다.The natural extracts are prepared by washing rosemary and Schisandra chinensis, cutting them into appropriate sizes, freeze-drying, and grinding to prepare rosemary powder and Schisandra chinensis powder; preparing a mixed powder by mixing the rosemary powder and Schisandra chinensis powder in a weight ratio of 1:1; mixing the mixed powder and water, performing primary hot water extraction at a temperature of 95-105 ° C. for 10-14 hours while stirring; After performing the first hot water extraction, filtering with filter paper and then freeze-drying the filtrate to prepare a first extract; After performing the first hot water extraction, filtering with a filter paper, mixing the remaining solids with water again, and performing a second hot water extraction at a temperature of 135-145 ° C. for 4-8 hours; After the second hot water extraction, filtering with filter paper and then freeze-drying the filtrate to prepare a second extract; and mixing the first extract and the second extract.
상기 곡물 발효분말은, 현미, 보리, 귀리, 통밀, 호밀, 맥아, 대두, 수수, 검정콩 및 검정깨를 세척한 후, 멸균기에 넣어 123-127℃의 온도로 멸균하는 단계; 멸균된 현미, 보리, 귀리, 통밀, 호밀, 맥아, 대두, 수수, 검정콩 및 검정깨를 1:1:1:1:1:1:1:1:1:1의 중량비율로 혼합하여 혼합물을 제조하고, 상기 혼합물을 98-100℃의 온도에서 볶는 단계; 볶아진 혼합물 98-102 중량부 및 농도 10 중량%의 소금물 98-102 중량부를 혼합한 후, 여기에 락토바실러스균 1 중량부를 첨가하여 혼합물을 제조하는 단계; 상기 혼합물을 항온 발효조에 넣어 40-44℃의 온도에서 22-26시간 동안 발효시키는 단계; 및 발효시킨 후 혼합물을 여과하고, 여과되어 얻어지는 발효곡물을 건조시킨 후 분쇄하는 단계;를 수행하여 제조되는 것을 사용한다.The fermented grain powder is, after washing brown rice, barley, oats, whole wheat, rye, malt, soybean, sorghum, black beans and black sesame seeds, sterilizing them at a temperature of 123-127 ℃ in a sterilizer; Mix sterilized brown rice, barley, oats, whole wheat, rye, malt, soybean, sorghum, black soybean and black sesame in a weight ratio of 1:1:1:1:1:1:1:1:1:1 to obtain a mixture Preparing and roasting the mixture at a temperature of 98-100 ℃; Preparing a mixture by mixing 98-102 parts by weight of the roasted mixture and 98-102 parts by weight of salt water having a concentration of 10% by weight, and then adding 1 part by weight of Lactobacillus bacteria thereto; Fermenting the mixture at a temperature of 40-44 ° C. for 22-26 hours in a constant temperature fermentation tank; and filtering the mixture after fermentation, drying the fermented grains obtained by filtration, and then grinding them.
당근은 90%의 물을 함유한 수분 함량이 높은 채소로, 비타민 A, K와 미네랄을 함유하여 거칠어진 피부를 빠르게 회복시켜주는 영양성분이 풍부하다. 또한, 당근의 수분은 피부의 보습에 좋은 영향을 준다. 상기 당근수는 수용성 원료로 당근이 가진 풍부한 수분과 미네랄을 녹여낸 원료로서 일반적으로 화장료 조성물에 적용되는 정제수를 대신하여 사용한다.Carrots are vegetables with high water content, containing 90% of water, and are rich in nutrients that quickly restore rough skin by containing vitamins A, K and minerals. In addition, the moisture of carrots has a good effect on moisturizing the skin. The carrot water is a water-soluble raw material in which the rich moisture and minerals of carrots are dissolved, and is generally used instead of purified water applied to cosmetic compositions.
본 발명에 따른 젤 네일 스티커의 사용방법은 건조된 손톱에 박리필름층을 제거한 젤 네일 스티커를 부착시키는 단계를 포함한다.The method of using the gel nail sticker according to the present invention includes attaching the gel nail sticker from which the release film layer is removed to the dried nail.
상기 젤 네일 스티커는 전술한 바와 같으므로 이하에서 상세한 설명을 생략한다.Since the gel nail sticker is as described above, a detailed description thereof will be omitted.
또한, 본 발명에 따른 젤 네일 스티커의 사용방법은,In addition, the method of using the gel nail sticker according to the present invention,
상기 젤 네일 스티커를 부착시키는 단계를 수행하고난 후,After performing the step of attaching the gel nail sticker,
손톱에 부착된 젤 네일 스티커 위에 몰드를 부착하는 단계;attaching a mold on a gel nail sticker attached to a nail;
몰드가 부착된 손톱을 UV 젤램프를 사용하여 경화시키는 단계;curing the nail to which the mold is attached using a UV gel lamp;
경화된 젤 네일 스티커로부터 몰드를 제거하는 단계; 및removing the mold from the cured gel nail sticker; and
몰드가 제거된 젤 네일 스티커를 성형하여 마무리하는 단계;를 포함한다.and shaping and finishing the gel nail sticker from which the mold has been removed.
상기 몰드는 당분야에서 사용하는 몰드로서 그 종류에 특별한 제한은 없다. 예를 들어, 플라스틱이나, 실리콘, 펄프 등을 사용해 다양한 사이즈 및 손톱 모양으로 성형하여 자연스럽고 아름답고 긴 길이를 가진 자연 손톱을 본따 만들 수 있다. 이 때 손톱 연장을 위한 몰드는 손톱 모양 및 길이에 따라 다양한 사이즈, 길이, 모양으로 사용할 수 있으며, 이에 따라 원하는 손톱 연장을 이룰 수 있다.The mold is a mold used in the art, and there is no particular limitation on its type. For example, plastic, silicone, pulp, etc. can be molded into various sizes and nail shapes to imitate natural, beautiful, and long lengths of natural nails. At this time, the mold for nail extension can be used in various sizes, lengths, and shapes according to the shape and length of the nail, and accordingly, desired nail extension can be achieved.
상기 몰드는 젤네일 스티커를 손톱 모양에 따라 UV 젤램프로 경화시킨 다음 제거하는 것을 특징으로 한다. 이에 따라, 상기 몰드는 반영구적으로 재사용할 수 있다는 장점이 있다. The mold is characterized in that the gel nail sticker is cured with a UV gel lamp according to the shape of the nail and then removed. Accordingly, there is an advantage in that the mold can be reused semi-permanently.
상기 UV 젤램프를 이용한 경화시간은 통상적인 경화시간으로 이에 특별한 제한은 없다. 예를 들어, 20-50분 동안 경화할 수 있다.The curing time using the UV gel lamp is a typical curing time and is not particularly limited thereto. For example, it can cure for 20-50 minutes.
상기 몰드를 제거한 다음 젤 네일 스티커의 이형필름층 또는 이형필름층이 제거된 젤층을 유광 또는 무광 액상 UV 젤로 덮고 한번 더 UV 젤램프로 경화하여 젤 네일 스티커의 젤층을 매끈하게 만들어주어 젤층의 끈끈함을 없애고 지속력을 높여줄 수 있다.After removing the mold, the release film layer of the gel nail sticker or the gel layer from which the release film layer is removed is covered with a glossy or matte liquid UV gel and cured with a UV gel lamp once more to make the gel layer of the gel nail sticker smooth, thereby reducing the stickiness of the gel layer. It can be removed and its durability can be increased.
또한, 본 발명은In addition, the present invention
손톱의 형태, 크기 및 곡선 이미지를 형성하는 단계; Forming an image of the shape, size and curve of the nail;
소비자 기호에 따른 색상 및 디자인을 선택하는 단계; 및Selecting color and design according to consumer preference; and
형성된 이미지, 소비자가 선택한 색상 및 디자인을 바탕으로 젤 네일 스티커를 제공하는 단계;를 포함하는 젤 네일 스티커 제공 시스템을 제공한다.Providing a gel nail sticker based on the formed image and the color and design selected by the consumer;
도 2에 본 발명에 따른 실시예 1의 젤 네일 스티커를 손톱에 적용하기 전 사진과 적용 및 제거 후 사진을 나타내었고, 비교예 1의 일반적인 젤 네일 스티커를 손톱에 적용하기 전 사진과 적용 및 제거 후 사진을 나타내었다.2 shows pictures before applying the gel nail sticker of Example 1 according to the present invention to nails and pictures after application and removal, and pictures before applying and applying and removing the general gel nail sticker of Comparative Example 1 to nails. After the picture was shown.
도 2에 나타낸 바와 같이 본 발명에 따른 젤 네일 스티커는 손톱의 손상이 거의 없음을 확인할 수 있었다.As shown in FIG. 2, it was confirmed that the gel nail sticker according to the present invention hardly damaged the nail.
Claims (2)
소비자 기호에 따른 색상 및 디자인을 선택하는 단계; 및
형성된 이미지, 소비자가 선택한 색상 및 디자인을 바탕으로 젤 네일 스티커를 제공하는 단계;를 포함하고,
상기 젤 네일 스티커는,
박리필름층;
상기 박리필름층 상에 형성된 접착층;
상기 접착층 상에 형성된 베이스층;
상기 베이스층 상에 형성된 컬러층;
상기 컬러층 상에 형성된 인쇄층;
상기 인쇄층 상에 형성된 젤층; 및
상기 젤층 상에 형성된 이형필름층;을 포함하고,
상기 접착층은 에틸메타크릴레이트 단량체 단위 23-27 중량%, n-부틸메타크릴레이트 단량체 단위 23-27 중량%, 글리시딜메타크릴레이트 단량체 단위 23-27 중량% 및 하이드록시에틸 메타크릴레이트 단량체 단위 23-27 중량%인 제1 아크릴레이트계 공중합체 31-35 중량부; 메틸메타크릴레이트 단량체 단위 23-27 중량%, 에틸메타크릴레이트 단량체 단위 23-27 중량%, 아크릴산 단량체 단위 23-27 중량% 및 메톡시에틸메타크릴레이트 단량체 단위 23-27 중량%인 제2 아크릴레이트계 공중합체 12-16 중량부; 올레핀계 불포화기를 갖는 친수성 폴리우레탄 10-14 중량부; 분리대두단백, 귀리단백분말 및 분리완두단백이 1:1:1의 중량비율로 혼합된 제1 조성물 3-7 중량부; 레몬껍질 추출물, 사과껍질 추출물, 양파껍질 추출물, 수박껍질 추출물 및 바나나껍질 추출물이 3:3:2:1:1의 중량비율로 혼합된 제2 조성물 2-6 중량부; 비타민 혼합물 2-6 중량부; 오미자씨 오일 2-6 중량부; 복숭아씨 오일 2-6 중량부; 리모넨 0.5-4 중량부; 리날룰 0.5-4 중량부; 이소퀘르시트린 0.5-4 중량부; 나이아신아마이드 0.1-1 중량부; 폴리글리세릴-6스테아레이트 0.1-1 중량부; 폴리글리세릴-2스테아레이트 0.1-1 중량부; 프로필렌글라이콜 1-5 중량부; 세테아릴알코올 1-5 중량부; 글리세릴스테아레이트 0.5-4 중량부; 스테아릴알코올 0.1-1 중량부; 프로판다이올 1-5 중량부; 알란토인 0.1-1 중량부; 및 트로메타민 0.1-1 중량부;를 포함하는 접착층 형성용 조성물로 형성된 것이고,
상기 베이스층은 메틸메타크릴레이트 단량체 단위 23-27 중량%, n-부틸메타크릴레이트 단량체 단위 23-27 중량%, 글리시딜메타크릴레이트 단량체 단위 23-27 중량% 및 하이드록시에틸 메타크릴레이트 단량체 단위 23-27 중량%인 제3 아크릴레이트계 공중합체 45-49 중량부; 중량평균분자량이 35,000-45,000인 폴리우레탄아크릴레이트 26-30 중량부; 에틸메타크릴레이트 3-7 중량부; 라우릴메타크릴레이트 2-6 중량부; 하이드록시에틸메타아크릴레이트 1-5 중량부; 메틸셀룰로오스 3-7 중량부; 프로필렌글리콜 1-5 중량부; 디메티콘 1-5 중량부; 및 소듐실리케이트 0.5-4 중량부;를 포함하는 베이스층 형성용 조성물로 형성된 것을 특징으로 하는 젤 네일 스티커 제공 시스템.Forming an image of the shape, size and curve of the nail;
Selecting color and design according to consumer preference; and
Providing a gel nail sticker based on the formed image and the color and design selected by the consumer;
The gel nail sticker,
release film layer;
an adhesive layer formed on the release film layer;
a base layer formed on the adhesive layer;
a color layer formed on the base layer;
a printing layer formed on the color layer;
a gel layer formed on the printing layer; and
Including; a release film layer formed on the gel layer,
The adhesive layer contains 23-27 wt% of ethyl methacrylate monomer units, 23-27 wt% of n-butyl methacrylate monomer units, 23-27 wt% of glycidyl methacrylate monomer units, and hydroxyethyl methacrylate monomers. 31-35 parts by weight of the first acrylate-based copolymer having a unit of 23-27% by weight; A second acrylic comprising 23-27% by weight of methyl methacrylate monomer units, 23-27% by weight of ethyl methacrylate monomer units, 23-27% by weight of acrylic acid monomer units, and 23-27% by weight of methoxyethyl methacrylate monomer units 12-16 parts by weight of a late copolymer; 10-14 parts by weight of hydrophilic polyurethane having an olefinic unsaturated group; 3-7 parts by weight of a first composition in which isolated soy protein, oat protein powder, and isolated pea protein are mixed in a weight ratio of 1:1:1; 2-6 parts by weight of a second composition in which lemon peel extract, apple peel extract, onion peel extract, watermelon peel extract, and banana peel extract are mixed in a weight ratio of 3:3:2:1:1; 2-6 parts by weight of the vitamin mixture; Schisandra seed oil 2-6 parts by weight; 2-6 parts by weight of peach seed oil; 0.5-4 parts by weight of limonene; linalool 0.5-4 parts by weight; 0.5-4 parts by weight of isoquercitrin; Niacinamide 0.1-1 part by weight; 0.1-1 part by weight of polyglyceryl-6 stearate; 0.1-1 part by weight of polyglyceryl-2stearate; 1-5 parts by weight of propylene glycol; 1-5 parts by weight of cetearyl alcohol; 0.5-4 parts by weight of glyceryl stearate; 0.1-1 part by weight of stearyl alcohol; 1-5 parts by weight of propanediol; 0.1-1 part by weight of allantoin; And 0.1-1 part by weight of tromethamine; is formed of a composition for forming an adhesive layer containing,
The base layer includes 23-27 wt% of methyl methacrylate monomer units, 23-27 wt% of n-butyl methacrylate monomer units, 23-27 wt% of glycidyl methacrylate monomer units, and hydroxyethyl methacrylate. 45-49 parts by weight of the third acrylate-based copolymer having 23-27% by weight of monomer units; 26-30 parts by weight of polyurethane acrylate having a weight average molecular weight of 35,000-45,000; 3-7 parts by weight of ethyl methacrylate; 2-6 parts by weight of lauryl methacrylate; 1-5 parts by weight of hydroxyethyl methacrylate; 3-7 parts by weight of methylcellulose; 1-5 parts by weight of propylene glycol; 1-5 parts by weight of dimethicone; and 0.5-4 parts by weight of sodium silicate.