KR102501017B1 - Multipurpose Adhesive for Tiles - Google Patents
Multipurpose Adhesive for Tiles Download PDFInfo
- Publication number
- KR102501017B1 KR102501017B1 KR1020220150539A KR20220150539A KR102501017B1 KR 102501017 B1 KR102501017 B1 KR 102501017B1 KR 1020220150539 A KR1020220150539 A KR 1020220150539A KR 20220150539 A KR20220150539 A KR 20220150539A KR 102501017 B1 KR102501017 B1 KR 102501017B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- powder
- preparing
- acrylic
- Prior art date
Abstract
Description
본 발명은 타일용 다목적 접착제에 관한 것이다.The present invention relates to a multi-purpose adhesive for tiles.
일반적으로 건축물, 특히 주거용 건축물인 경우, 주방, 베란다, 화장실, 거실, 건물내부, 복도, 외벽 등에는 다양하게 타일이 시공되는데, 이에 따라 타일이 부착되는 바탕면도 석고보드면, 몰탈면, 타일면, 페인트면, 철판면 등 매우 다양해지고, 타일 또한 200×200 mm에서 300×600 mm, 600×600 mm, 1000×1200 mm 등으로 대형화되고, 또한 타일의 흡수율이 15%에서 1% 미만으로 매우 낮아지고 있다. In general, in the case of buildings, especially residential buildings, various tiles are installed on kitchens, verandas, bathrooms, living rooms, inside buildings, corridors, and exterior walls. , painted surface, steel plate surface, etc., and the size of the tile is also increased from 200 × 200 mm to 300 × 600 mm, 600 × 600 mm, 1000 × 1200 mm, etc., and the absorption rate of the tile ranges from 15% to less than 1%. It is getting lower.
국내 타일용 접착제는 크게 일액형 본드, 압착용 분말 시멘트, 레미탈, 에폭시의 네 가지가 있는 데, 일액형 본드의 경우 사용이 간편하나 인체에 유해하고 물에 녹는 단점이 존재하며, 압착용 분말 시멘트의 경우 고도의 기술이 필요하며 작업자의 순력도에 따라 하자 요인 발생이 크다. 또한, 레미탈의 경우 최초 건축시 주로 사용되는 비압착 시공으로 진행되는 가격경쟁력이 우수한 제품이나 시간이 지남에 따라 타일이 탈락하는 하자 발생 빈도가 높고, 에폭시의 경우 경화제를 혼합하여 사용하는 물에 강한 재질로 대형 타일에 많이 사용되나 경화속도가 빨라 시공이 어려우며 환경오염과 높은 시공비가 단점인 제품이다.Domestic tile adhesives are largely divided into four types: one-component bond, powder cement for compression, remital, and epoxy. One-component adhesive is easy to use, but it is harmful to the human body and dissolves in water. In the case of cement, a high degree of skill is required, and the occurrence of defects is large depending on the worker's net strength. In addition, in the case of Remital, it is a product with excellent price competitiveness that proceeds with non-compression construction mainly used at the time of initial construction, but there is a high frequency of defects in which tiles fall off over time, and in the case of epoxy, it is resistant to water used by mixing a hardener. As a material, it is often used for large tiles, but it is difficult to construct due to its fast curing speed, and it has disadvantages such as environmental pollution and high construction cost.
최근 폴리머계 타일 접착용 시멘트가 개발되었으나, 비흡수면에서 접착력은 유지되나, 충격, 수축, 팽창등에는 매우 취약한 상황이다. 따라서 통상 타일시공사에서는 폴리머계 타일접착용 시멘트와 에폭시 접착제를 병행하여 타일탈락을 최소화하고 있는 상황이다.Recently, polymer-based tile bonding cement has been developed, but the adhesive strength is maintained on the non-absorbent surface, but it is very vulnerable to impact, contraction, and expansion. Therefore, in general, tile construction companies use polymer-based tile bonding cement and epoxy adhesive in parallel to minimize tile loss.
이에, 타일의 종류, 시공 장소에 상관 없이 시공이 가능하며 압착 및 비압착 시공이 가능한 타일용 접착제의 개발이 요구된다.Therefore, it is required to develop adhesives for tiles that can be applied regardless of the type of tile and the place where they are applied and that can be applied by compression or non-compression.
본 발명은 상기와 같은 문제점을 해결하기 위해 안출된 것으로서, 본 발명의 목적은 압착 및 비압착 시공이 가능한 타일용 다목적 접착제를 제공하는 것이다.The present invention has been made to solve the above problems, and an object of the present invention is to provide a multi-purpose adhesive for tiles capable of compression and non-compression construction.
또한, 본 발명의 다른 목적은 타일의 종류와 크기 등에 구애받지 않고 현장 시공 가능한 타일용 다목적 접착제를 제공하는 것이다.In addition, another object of the present invention is to provide a multi-purpose adhesive for tiles that can be installed on-site regardless of the type and size of the tile.
본 발명의 과제는 이상에서 언급한 과제들로 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.The object of the present invention is not limited to the tasks mentioned above, and other tasks not mentioned will be clearly understood by those skilled in the art from the following description.
상기 목적을 달성하기 위하여 본 발명은In order to achieve the above object, the present invention
시멘트 분말을 포함하는 타일용 접착제를 제공한다.An adhesive for tiles containing cement powder is provided.
또한, 상기 타일용 접착제는 백색시멘트 36-40 중량부, 규사 18-22 중량부, 아크릴계 고분자 수지 8-12 중량부, 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 실리콘계 화합물 0.3-3 중량부, 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 탄소섬유 분산액 21-25 중량부를 포함하는 제1 조성물을 포함하고,In addition, the tile adhesive includes 36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of an acrylic polymer resin, 0.5-4 parts by weight of an acrylic mixture containing an acrylic compound, and 0.3-3 parts by weight of a silicone-based compound. A first composition comprising 3-7 parts by weight of ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fibers and 21-25 parts by weight of a carbon fiber dispersion,
상기 아크릴계 고분자 수지는 메틸메타크릴레이트 단량체 단위 23-27 중량%, n-부틸메타크릴레이트 단량체 단위 23-27 중량%, 글리시딜메타크릴레이트 단량체 단위 23-27 중량% 및 하이드록시에틸 메타크릴레이트 단량체 단위 23-27 중량%인 제1 아크릴레이트계 공중합체 및 메틸메타크릴레이트 단량체 단위 23-27 중량%, 에틸메타크릴레이트 단량체 단위 23-27 중량%, 아크릴산 단량체 단위 23-27 중량% 및 메톡시에틸메타크릴레이트 단량체 단위 23-27 중량%인 제2 아크릴레이트계 공중합체의 73-77:23-27의 중량비율로 혼합된 혼합물이고, The acrylic polymer resin contains 23-27% by weight of methyl methacrylate monomer unit, 23-27% by weight of n-butyl methacrylate monomer unit, 23-27% by weight of glycidyl methacrylate monomer unit, and hydroxyethyl methacrylate. A first acrylate-based copolymer comprising 23-27% by weight of late monomer units and 23-27% by weight of methyl methacrylate monomer units, 23-27% by weight of ethyl methacrylate monomer units, 23-27% by weight of acrylic acid monomer units and A mixture of a second acrylate-based copolymer having 23-27% by weight of methoxyethyl methacrylate monomer units in a weight ratio of 73-77:23-27,
상기 아크릴계 화합물을 포함하는 아크릴계 혼합물은 에틸메타크릴레이트, 라우릴메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 4:4:2의 중량비율로 혼합된 혼합물이고,The acrylic mixture containing the acrylic compound is a mixture in which ethyl methacrylate, lauryl methacrylate, and dimethacrylate diethylene glycol are mixed in a weight ratio of 4:4:2,
상기 실리콘계 화합물은 하기 화학식 1로 표시되는 화합물이고,The silicone-based compound is a compound represented by Formula 1 below,
상기 광석분말은 일라이트 분말 28-32 중량부, 각섬석 분말 28-32 중량부, 흑운모 분말 28-32 중량부 및 천연연옥 분말 8-12 중량부를 포함하는 것을 특징으로 한다.The ore powder is characterized by comprising 28-32 parts by weight of illite powder, 28-32 parts by weight of amphibole powder, 28-32 parts by weight of biotite powder and 8-12 parts by weight of natural nephrite powder.
<화학식 1><Formula 1>
또한, 상기 타일용 접착제는 백색시멘트 36-40 중량부, 규사 18-22 중량부, 우레탄계 고분자 수지 8-12 중량부, 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 실리콘계 화합물 0.3-3 중량부, 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 탄소섬유 분산액 21-25 중량부를 포함하는 제2 조성물을 포함하고,In addition, the tile adhesive includes 36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of a urethane-based polymer resin, 0.5-4 parts by weight of an acrylic mixture containing an acrylic compound, and 0.3-3 parts by weight of a silicone-based compound. A second composition comprising 3-7 parts by weight of ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fibers and 21-25 parts by weight of a carbon fiber dispersion,
상기 우레탄계 고분자 수지는 폴리에테르폴리올, 메틸렌 디페닐 디이소시아네이트(methylene diphenyl diisocyanate) 및 디부틸틴 디라우레이트(dibutyltin dilaurate)를 반응시켜 반응 생성물을 제조하고, 상기 반응 생성물을 아미노트리알콕시실란을 가하여 반응시켜 제조되는 실란 종결 폴리우레탄이고,The urethane-based polymer resin reacts polyether polyol, methylene diphenyl diisocyanate and dibutyltin dilaurate to prepare a reaction product, and reacts the reaction product by adding aminotrialkoxysilane It is a silane-terminated polyurethane prepared by
상기 아크릴계 화합물을 포함하는 아크릴계 혼합물은 에틸메타크릴레이트, 라우릴메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 4:4:2의 중량비율로 혼합된 혼합물이고,The acrylic mixture containing the acrylic compound is a mixture in which ethyl methacrylate, lauryl methacrylate, and dimethacrylate diethylene glycol are mixed in a weight ratio of 4:4:2,
상기 실리콘계 화합물은 상기 화학식 1로 표시되는 화합물이고,The silicon-based compound is a compound represented by Formula 1,
상기 광석분말은 일라이트 분말 28-32 중량부, 각섬석 분말 28-32 중량부, 흑운모 분말 28-32 중량부 및 천연연옥 분말 8-12 중량부를 포함하는 것을 특징으로 한다.The ore powder is characterized by comprising 28-32 parts by weight of illite powder, 28-32 parts by weight of amphibole powder, 28-32 parts by weight of biotite powder and 8-12 parts by weight of natural nephrite powder.
또한, 본 발명은In addition, the present invention
메틸메타크릴레이트 단량체, n-부틸메타크릴레이트 단량체, 글리시딜메타크릴레이트 단량체 및 하이드록시에틸 메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제1 아크릴레이트계 공중합체를 제조하는 단계; 메틸메타크릴레이트 단량체, 에틸메타크릴레이트 단량체, 아크릴산 단량체 및 메톡시에틸메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제2 아크릴레이트계 공중합체를 제조하는 단계; 및 상기 제1 아크릴레이트계 공중합체와 상기 제2 아크릴레이트계 공중합체를 73-77:23-27의 중량비율로 혼합하는 단계;를 포함하는 아크릴계 고분자 수지를 제조하는 단계;Methyl methacrylate monomer, n-butyl methacrylate monomer, glycidyl methacrylate monomer and hydroxyethyl methacrylate monomer were mixed in a weight ratio of 1:1:1:1, and a catalyst was added to 86- Preparing a first acrylate-based copolymer by reacting at a temperature of 90 ℃; Methyl methacrylate monomer, ethyl methacrylate monomer, acrylic acid monomer and methoxyethyl methacrylate monomer were mixed in a weight ratio of 1: 1: 1: 1, and a catalyst was added to react at a temperature of 86-90 ° C. preparing a second acrylate-based copolymer; and mixing the first acrylate-based copolymer and the second acrylate-based copolymer in a weight ratio of 73-77:23-27; preparing an acrylic polymer resin comprising;
폴리에테르폴리올, 메틸렌 디페닐 디이소시아네이트(methylene diphenyl diisocyanate) 및 디부틸틴 디라우레이트(dibutyltin dilaurate)를 반응시켜 반응 생성물을 제조하는 단계; 및 상기 반응 생성물을 아미노트리알콕시실란을 가하여 반응시키는 단계;를 포함하는 우레탄계 고분자 수지를 제조하는 단계;preparing a reaction product by reacting polyether polyol, methylene diphenyl diisocyanate and dibutyltin dilaurate; Preparing a urethane-based polymer resin comprising; and reacting the reaction product by adding aminotrialkoxysilane.
에틸메타크릴레이트, 라우릴메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 4:4:2의 중량비율로 혼합하여 아크릴계 화합물을 포함하는 아크릴계 혼합물을 제조하는 단계;Preparing an acrylic mixture containing an acrylic compound by mixing ethyl methacrylate, lauryl methacrylate, and dimethacrylate diethylene glycol in a weight ratio of 4:4:2;
일라이트 분말 28-32 중량부, 각섬석 분말 28-32 중량부, 흑운모 분말 28-32 중량부 및 천연연옥 분말 8-12 중량부를 혼합하여 광석분말을 제조하는 단계;Preparing ore powder by mixing 28-32 parts by weight of illite powder, 28-32 parts by weight of amphibole powder, 28-32 parts by weight of biotite powder and 8-12 parts by weight of natural nephrite powder;
일라이트 분말, 각섬석 분말, 흑운모 분말 및 천연연옥 분말을 3:3:3:1의 중량비율로 혼합한 혼합분말을 준비하는 단계; 상기 혼합분말 18-22 중량부 및 증류수 78-82 중량부를 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 84-88℃의 온도로 가열하여 추출하는 단계; 추출 후, 혼합물을 여과하여 추출액을 제조하는 단계; 및 탄소섬유 33-37 중량부 및 상기 추출액 63-67 중량부를 혼합하고 초음파조사하는 단계;를 포함하는 탄소섬유 분산액을 제조하는 단계;preparing a mixed powder obtained by mixing illite powder, amphibole powder, biotite powder, and natural nephrite powder in a weight ratio of 3:3:3:1; Preparing a mixture by mixing 18-22 parts by weight of the mixed powder and 78-82 parts by weight of distilled water; Extracting by heating the mixture at a temperature of 84-88 ° C; After extraction, filtering the mixture to prepare an extract; Preparing a carbon fiber dispersion comprising; and mixing 33-37 parts by weight of carbon fibers and 63-67 parts by weight of the extract and irradiating with ultrasonic waves;
백색시멘트 36-40 중량부, 규사 18-22 중량부, 상기 아크릴계 고분자 수지 8-12 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 상기 화학식 1로 표시되는 실리콘계 화합물 0.3-3 중량부, 상기 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 상기 탄소섬유 분산액 21-25 중량부를 혼합하여 제1 조성물을 제조하는 단계;36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of the acrylic polymer resin, 0.5-4 parts by weight of the acrylic mixture containing the acrylic compound, 0.3-3 parts by weight of the silicone compound represented by Formula 1 preparing a first composition by mixing 3-7 parts by weight of the ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fiber, and 21-25 parts by weight of the carbon fiber dispersion;
백색시멘트 36-40 중량부, 규사 18-22 중량부, 상기 우레탄계 고분자 수지 8-12 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 하기 화학식 1로 표시되는 실리콘계 화합물 0.3-3 중량부, 상기 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 상기 탄소섬유 분산액 21-25 중량부를 혼합하여 제2 조성물을 제조하는 단계;36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of the urethane-based polymer resin, 0.5-4 parts by weight of an acrylic mixture containing the acrylic compound, 0.3-3 parts by weight of a silicone-based compound represented by Formula 1 below preparing a second composition by mixing 3-7 parts by weight of the ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fiber, and 21-25 parts by weight of the carbon fiber dispersion;
상기 제1 조성물 73-77 중량부 및 상기 제2 조성물 23-27 중량부를 혼합하여 제3 조성물을 제조하는 단계;preparing a third composition by mixing 73-77 parts by weight of the first composition and 23-27 parts by weight of the second composition;
타일을 시공하기 위한 구조물의 외면을 평탄지게 정리하고, 고압수를 분사하여 이물질을 제거하는 단계;Leveling the outer surface of a structure for constructing tiles and removing foreign substances by spraying high-pressure water;
이물질이 제거된 외면에 상기 제3 조성물을 도포하는 단계; 및applying the third composition to the outer surface from which foreign substances are removed; and
도포된 제3 조성물의 외면에 타일을 부착하는 단계;를 포함하는 타일 시공방법을 제공한다.It provides a tile construction method comprising the step of attaching a tile to the outer surface of the applied third composition.
또한, 본 발명은In addition, the present invention
메틸메타크릴레이트 단량체, n-부틸메타크릴레이트 단량체, 글리시딜메타크릴레이트 단량체 및 하이드록시에틸 메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제1 아크릴레이트계 공중합체를 제조하는 단계; 메틸메타크릴레이트 단량체, 에틸메타크릴레이트 단량체, 아크릴산 단량체 및 메톡시에틸메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제2 아크릴레이트계 공중합체를 제조하는 단계; 및 상기 제1 아크릴레이트계 공중합체와 상기 제2 아크릴레이트계 공중합체를 73-77:23-27의 중량비율로 혼합하는 단계;를 포함하는 아크릴계 고분자 수지를 제조하는 단계;Methyl methacrylate monomer, n-butyl methacrylate monomer, glycidyl methacrylate monomer and hydroxyethyl methacrylate monomer were mixed in a weight ratio of 1:1:1:1, and a catalyst was added to 86- Preparing a first acrylate-based copolymer by reacting at a temperature of 90 ℃; Methyl methacrylate monomer, ethyl methacrylate monomer, acrylic acid monomer and methoxyethyl methacrylate monomer were mixed in a weight ratio of 1: 1: 1: 1, and a catalyst was added to react at a temperature of 86-90 ° C. preparing a second acrylate-based copolymer; and mixing the first acrylate-based copolymer and the second acrylate-based copolymer in a weight ratio of 73-77:23-27; preparing an acrylic polymer resin comprising;
폴리에테르폴리올, 메틸렌 디페닐 디이소시아네이트(methylene diphenyl diisocyanate) 및 디부틸틴 디라우레이트(dibutyltin dilaurate)를 반응시켜 반응 생성물을 제조하는 단계; 및 상기 반응 생성물을 아미노트리알콕시실란을 가하여 반응시키는 단계;를 포함하는 우레탄계 고분자 수지를 제조하는 단계;preparing a reaction product by reacting polyether polyol, methylene diphenyl diisocyanate and dibutyltin dilaurate; Preparing a urethane-based polymer resin comprising; and reacting the reaction product by adding aminotrialkoxysilane.
에틸메타크릴레이트, 라우릴메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 4:4:2의 중량비율로 혼합하여 아크릴계 화합물을 포함하는 아크릴계 혼합물을 제조하는 단계;Preparing an acrylic mixture containing an acrylic compound by mixing ethyl methacrylate, lauryl methacrylate, and dimethacrylate diethylene glycol in a weight ratio of 4:4:2;
일라이트 분말 28-32 중량부, 각섬석 분말 28-32 중량부, 흑운모 분말 28-32 중량부 및 천연연옥 분말 8-12 중량부를 혼합하여 광석분말을 제조하는 단계;Preparing ore powder by mixing 28-32 parts by weight of illite powder, 28-32 parts by weight of amphibole powder, 28-32 parts by weight of biotite powder and 8-12 parts by weight of natural nephrite powder;
일라이트 분말, 각섬석 분말, 흑운모 분말 및 천연연옥 분말을 3:3:3:1의 중량비율로 혼합한 혼합분말을 준비하는 단계; 상기 혼합분말 18-22 중량부 및 증류수 78-82 중량부를 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 84-88℃의 온도로 가열하여 추출하는 단계; 추출 후, 혼합물을 여과하여 추출액을 제조하는 단계; 및 탄소섬유 33-37 중량부 및 상기 추출액 63-67 중량부를 혼합하고 초음파조사하는 단계;를 포함하는 탄소섬유 분산액을 제조하는 단계;preparing a mixed powder obtained by mixing illite powder, amphibole powder, biotite powder, and natural nephrite powder in a weight ratio of 3:3:3:1; Preparing a mixture by mixing 18-22 parts by weight of the mixed powder and 78-82 parts by weight of distilled water; Extracting by heating the mixture at a temperature of 84-88 ° C; After extraction, filtering the mixture to prepare an extract; Preparing a carbon fiber dispersion comprising; and mixing 33-37 parts by weight of carbon fibers and 63-67 parts by weight of the extract and irradiating with ultrasonic waves;
백색시멘트 36-40 중량부, 규사 18-22 중량부, 상기 아크릴계 고분자 수지 8-12 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 하기 화학식 1로 표시되는 실리콘계 화합물 0.3-3 중량부, 상기 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 상기 탄소섬유 분산액 21-25 중량부를 혼합하여 제1 조성물을 제조하는 단계;36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of the acrylic polymer resin, 0.5-4 parts by weight of the acrylic mixture containing the acrylic compound, 0.3-3 parts by weight of the silicone compound represented by Formula 1 below preparing a first composition by mixing 3-7 parts by weight of the ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fiber, and 21-25 parts by weight of the carbon fiber dispersion;
백색시멘트 36-40 중량부, 규사 18-22 중량부, 상기 우레탄계 고분자 수지 8-12 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 상기 화학식 1로 표시되는 실리콘계 화합물 0.3-3 중량부, 상기 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 상기 탄소섬유 분산액 21-25 중량부를 혼합하여 제2 조성물을 제조하는 단계;36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of the urethane-based polymer resin, 0.5-4 parts by weight of the acrylic mixture containing the acrylic compound, 0.3-3 parts by weight of the silicone-based compound represented by Formula 1 preparing a second composition by mixing 3-7 parts by weight of the ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fiber, and 21-25 parts by weight of the carbon fiber dispersion;
타일을 시공하기 위한 구조물의 외면을 평탄지게 정리하고, 고압수를 분사하여 이물질을 제거하는 단계;Leveling the outer surface of a structure for constructing tiles and removing foreign substances by spraying high-pressure water;
이물질이 제거된 외면에 상기 제1 조성물을 도포하는 단계;Applying the first composition to the outer surface from which foreign substances are removed;
타일의 배면에 상기 제2 조성물을 도포하는 단계; 및applying the second composition to the back surface of the tile; and
상기 제1 조성물이 도포된 외면에 상기 제2 조성물이 배면에 도포된 타일을 부착하는 단계;를 포함하는 타일 시공방법을 제공한다.It provides a tile construction method comprising the step of attaching a tile coated with the second composition to the outer surface coated with the first composition.
본 발명에 따른 타일용 접착제는 접착력과 탄성이 뛰어나 타일 시공 이후에 타일 박리 등의 현상을 방지하고 비숙련자라도 상관없이 시공 하자 발생을 현저히 낮추어서 시공성과 경제성 등을 향상시킬 수 있다.The adhesive for tiles according to the present invention has excellent adhesive strength and elasticity, preventing phenomena such as peeling off of tiles after tile construction, and remarkably reducing occurrence of construction defects regardless of unskilled users, thereby improving workability and economic feasibility.
도 1은 본 발명의 일 실시예에 따른 타일 시공방법을 순서도로 나타낸 것이고,
도 2는 본 발명에 따른 다른 일 실시예에 따른 타일 시공방법을 순서도로 나타낸 것이다.1 is a flowchart showing a tile construction method according to an embodiment of the present invention,
2 is a flowchart illustrating a tile construction method according to another embodiment of the present invention.
이하에서는 첨부된 도면을 참조하여 다양한 실시예를 보다 상세하게 설명한다. 본 명세서에 기재된 실시예는 다양하게 변형될 수 있다. 특정한 실시예가 도면에서 묘사되고 상세한 설명에서 자세하게 설명될 수 있다. 그러나 첨부된 도면에 개시된 특정한 실시 예는 다양한 실시예를 쉽게 이해하도록 하기 위한 것일 뿐이다. 따라서 첨부된 도면에 개시된 특정 실시예에 의해 기술적 사상이 제한되는 것은 아니며, 발명의 사상 및 기술 범위에 포함되는 모든 균등물 또는 대체물을 포함하는 것으로 이해되어야 한다.Hereinafter, various embodiments will be described in more detail with reference to the accompanying drawings. The embodiments described in this specification may be modified in various ways. Certain embodiments may be depicted in the drawings and described in detail in the detailed description. However, specific embodiments disclosed in the accompanying drawings are only intended to facilitate understanding of various embodiments. Therefore, the technical idea is not limited by the specific embodiments disclosed in the accompanying drawings, and it should be understood to include all equivalents or substitutes included in the spirit and technical scope of the invention.
1차, 2차, 제1, 제2 등과 같이 서수를 포함하는 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 이러한 구성요소들은 상술한 용어에 의해 한정되지는 않는다. 상술한 용어는 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다.Terms including ordinal numbers such as primary, secondary, first, and second may be used to describe various elements, but these elements are not limited by the above-mentioned terms. The terminology described above is only used for the purpose of distinguishing one component from another.
본 명세서에서, '포함한다' 또는 '가지다' 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다. 어떤 구성요소가 다른 구성요소에 '연결되어' 있다거나 '접속되어' 있다고 언급된 때에는, 그 다른 구성요소에 직접적으로 연결되어 있거나 또는 접속되어 있을 수도 있지만, 중간에 다른 구성요소가 존재할 수도 있다고 이해되어야 할 것이다. 반면에, 어떤 구성요소가 다른 구성요소에 '직접 연결되어' 있다거나 '직접 접속되어' 있다고 언급된 때에는, 중간에 다른 구성요소가 존재하지 않는 것으로 이해되어야 할 것이다.In this specification, terms such as 'comprise' or 'having' are intended to designate that there is a feature, number, step, operation, component, part, or combination thereof described in the specification, but one or more other features It should be understood that the presence or addition of numbers, steps, operations, components, parts, or combinations thereof is not precluded. It is understood that when a component is referred to as being 'connected' or 'connected' to another component, it may be directly connected or connected to the other component, but other components may exist in the middle. It should be. On the other hand, when a component is referred to as being 'directly connected' or 'directly connected' to another component, it should be understood that no other component exists in the middle.
그 밖에도, 본 발명을 설명함에 있어서, 관련된 공지 기능 혹은 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우, 그에 대한 상세한 설명은 축약하거나 생략한다.In addition, in describing the present invention, if it is determined that a detailed description of a related known function or configuration may unnecessarily obscure the subject matter of the present invention, the detailed description thereof will be abbreviated or omitted.
본 발명은 시멘트 분말을 포함하는 타일용 접착제를 제공한다.The present invention provides an adhesive for tiles containing cement powder.
이하, 본 발명에 따른 타일용 접착제를 상세히 설명한다.Hereinafter, the adhesive for tiles according to the present invention will be described in detail.
상기 타일용 접착제는 백색시멘트 36-40 중량부, 규사 18-22 중량부, 아크릴계 고분자 수지 8-12 중량부, 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 실리콘계 화합물 0.3-3 중량부, 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 탄소섬유 분산액 21-25 중량부를 포함하는 제1 조성물을 포함하는 것이 바람직하고, 백색시멘트 37-39 중량부, 규사 19-21 중량부, 아크릴계 고분자 수지 9-11 중량부, 아크릴계 화합물을 포함하는 아크릴계 혼합물 1-3 중량부, 실리콘계 화합물 0.5-1.5 중량부, 광석분말 4-6 중량부, 메틸셀룰로오스 0.3-0.7 중량부, 셀룰로오스 섬유 0.3-0.7 중량부 및 탄소섬유 분산액 22-24 중량부를 포함하는 제1 조성물을 포함하는 것이 더욱 바람직하다.The tile adhesive includes 36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of an acrylic polymer resin, 0.5-4 parts by weight of an acrylic mixture containing an acrylic compound, 0.3-3 parts by weight of a silicone compound, It is preferable to include a first composition comprising 3-7 parts by weight of ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fiber and 21-25 parts by weight of a carbon fiber dispersion, and 37-39 parts by weight of white cement 19-21 parts by weight of silica sand, 9-11 parts by weight of acrylic polymer resin, 1-3 parts by weight of an acrylic mixture containing an acrylic compound, 0.5-1.5 parts by weight of a silicon compound, 4-6 parts by weight of ore powder, 0.3 parts by weight of methylcellulose -0.7 parts by weight, 0.3-0.7 parts by weight of cellulose fibers and 22-24 parts by weight of a carbon fiber dispersion is more preferably included.
상기 아크릴계 고분자 수지는 메틸메타크릴레이트 단량체 단위 23-27 중량%, n-부틸메타크릴레이트 단량체 단위 23-27 중량%, 글리시딜메타크릴레이트 단량체 단위 23-27 중량% 및 하이드록시에틸 메타크릴레이트 단량체 단위 23-27 중량%인 제1 아크릴레이트계 공중합체 및 메틸메타크릴레이트 단량체 단위 23-27 중량%, 에틸메타크릴레이트 단량체 단위 23-27 중량%, 아크릴산 단량체 단위 23-27 중량% 및 메톡시에틸메타크릴레이트 단량체 단위 23-27 중량%인 제2 아크릴레이트계 공중합체의 73-77:23-27의 중량비율로 혼합된 혼합물인 것이 바람직하다. 상기 아크릴계 고분자 수지로 상기 조성의 제1 아크릴레이트계 공중합체 및 제2 아크릴레이트계 공중합체를 포함하여 우수한 부착강도 및 부착유지력을 나타낼 수 있다.The acrylic polymer resin contains 23-27% by weight of methyl methacrylate monomer unit, 23-27% by weight of n-butyl methacrylate monomer unit, 23-27% by weight of glycidyl methacrylate monomer unit, and hydroxyethyl methacrylate. A first acrylate-based copolymer comprising 23-27% by weight of late monomer units and 23-27% by weight of methyl methacrylate monomer units, 23-27% by weight of ethyl methacrylate monomer units, 23-27% by weight of acrylic acid monomer units and It is preferable that the second acrylate-based copolymer having 23-27% by weight of methoxyethyl methacrylate monomer unit is mixed in a weight ratio of 73-77:23-27. The acrylic polymer resin may exhibit excellent adhesion strength and adhesion retention, including the first acrylate-based copolymer and the second acrylate-based copolymer of the above composition.
상기 아크릴계 화합물을 포함하는 아크릴계 혼합물은 에틸메타크릴레이트, 라우릴메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 4:4:2의 중량비율로 혼합된 혼합물이고, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물로 에틸메타크릴레이트, 라우릴메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜의 혼합물을 포함하여 더욱 우수한 부착강도와 유지력을 나타낸다.The acrylic mixture containing the acrylic compound is a mixture in which ethyl methacrylate, lauryl methacrylate, and dimethacrylate diethylene glycol are mixed in a weight ratio of 4:4:2, and the acrylic mixture containing the acrylic compound Contains a mixture of ethyl methacrylate, lauryl methacrylate, and dimethacrylate diethylene glycol to show better adhesion strength and retention.
상기 실리콘계 화합물은 하기 화학식 1로 표시되는 실리콘메타크릴레이트를 사용하는 것이 바람직하며, 실리콘메타크릴레이트를 포함하여 도포되는 타일과의 접착력을 높여주고, 내구성을 더 높여줄 수 있다. As the silicon-based compound, it is preferable to use silicon methacrylate represented by Chemical Formula 1 below, and including silicon methacrylate can increase adhesion with the applied tile and further enhance durability.
<화학식 1><Formula 1>
상기 광석분말은 일라이트 분말 28-32 중량부, 각섬석 분말 28-32 중량부, 흑운모 분말 28-32 중량부 및 천연연옥 분말 8-12 중량부를 포함하는 것이 바람직하다.The ore powder preferably includes 28-32 parts by weight of illite powder, 28-32 parts by weight of amphibole powder, 28-32 parts by weight of biotite powder, and 8-12 parts by weight of natural nephrite powder.
일라이트(illite)는 대표적인 천연점토 광물질로서 다공성 운모 미네랄이며, 얇은 판상의 구조로 요곡성과 탄성을 가지고 있어 탄성과 흡착성이 뛰어나다. 또한, 40℃에서 방사율 93%, 3.71 x 102의 원적외선을 방사한다. 그밖에 항균작용 및 중금속 흡착 성능을 갖고 있다. 상기 일라이트 분말은 29-31 중량부를 포함하는 것이 더욱 바람직하다.Illite is a porous mica mineral as a representative natural clay mineral, and has excellent elasticity and adsorption due to its thin plate-like structure and has concavity and elasticity. In addition, it emits far-infrared rays of 3.71 x 102 with an emissivity of 93% at 40℃. In addition, it has antibacterial action and heavy metal adsorption performance. More preferably, the illite powder includes 29-31 parts by weight.
각섬석(amphibloe)은 칼슘, 마그네슘 및 철을 주성분으로 하고 알루미늄을 약간 함유하는 검은색의 광물질로 곱돌이라고도 한다. 이러한 각섬석은 열이 가해질 경우 원적외선 및 무기산 등을 다량 방출하는 것으로 밝혀졌다. 특히 인체에 유익한 9∼10 마이크론의 원적외선(방사율 92%)을 방출한다. 상기 각섬석 분말은 29-31 중량부를 포함하는 것이 더욱 바람직하다.Amphibole is a black mineral containing calcium, magnesium, and iron as main components and a little aluminum, and is also called a gobstone. It has been found that amphibole emits a large amount of far-infrared rays and inorganic acids when heat is applied. In particular, it emits 9-10 micron far-infrared rays (92% emissivity) that are beneficial to the human body. More preferably, the amphibole powder contains 29-31 parts by weight.
흑운모(biotite)는 40도의 온도에서 원적외선 방사율이 93%이다. 이러한 광물질 등은 각각 살균작용, 액체분자 미세화, 원적외선 방사, 산소보충기능, 인체흡수능력 향상, 산성중화기능, 흡착기능 등 다양한 기능을 지니고 있는 것으 로 알려져 있다. 특히 상기한 광물질에서 방사된 원적외선에서 방출하는 파장은 수분과 단백질 분자에 닿을 경우에 세포를 1분에 2,000번씩 미세하게 공명, 공진시켜 세포노화를 방지하는 기능을 가지고 있다. 상기 흑운모 분말은 29-31 중량부를 포함하는 것이 더욱 바람직하다.Biotite has a far-infrared emissivity of 93% at a temperature of 40 degrees. These minerals are known to have various functions such as sterilization, micronization of liquid molecules, far-infrared radiation, oxygen replenishment function, improvement of human body absorption capacity, acid neutralization function, and adsorption function. In particular, the wavelengths emitted from the far-infrared rays emitted from the above minerals have a function of preventing cell aging by finely resonating and resonating cells 2,000 times per minute when they come into contact with moisture and protein molecules. More preferably, the biotite powder contains 29-31 parts by weight.
천연연옥은 춘천옥이라고도 하며, 탈취, 건강증진기능, 단열기능, 항균기능, 원적외선방사기능, 음이온방출기능 등을 갖는 것으로 알려진 물질로서, 오래전부터 인체에 가까이 두면 건강 증진에 도움이 된다고 알려진 물질이다. 상기 천연연옥을 적용하여 항균기능을 발현시킬 수 있다. 상기 천연연욕 분말은 9-11 중량부를 포함하는 것이 더욱 바람직하다.Natural nephrite, also called chuncheonok, is a substance known to have deodorizing, health promotion, insulation, antibacterial, far-infrared radiation, and negative ion emission functions. Antibacterial function can be expressed by applying the natural nephrite. More preferably, the natural smoke bath powder contains 9-11 parts by weight.
상기 탄소섬유 분산액은, 일라이트 분말, 각섬석 분말, 흑운모 분말 및 천연연옥 분말을 3:3:3:1의 중량비율로 혼합한 혼합분말을 준비하는 단계; 상기 혼합분말 18-22 중량부 및 증류수 78-82 중량부를 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 84-88℃의 온도로 가열하여 추출하는 단계; 추출 후, 혼합물을 여과하여 추출액을 제조하는 단계; 및 탄소섬유 33-37 중량부 및 상기 추출액 63-67 중량부를 혼합하고 초음파조사하는 단계;를 수행하여 제조되는 것을 사용하는 것이 바람직하다.The carbon fiber dispersion is prepared by mixing illite powder, amphibole powder, biotite powder, and natural nephrite powder in a weight ratio of 3: 3: 3: 1; Preparing a mixture by mixing 18-22 parts by weight of the mixed powder and 78-82 parts by weight of distilled water; Extracting by heating the mixture at a temperature of 84-88 ° C; After extraction, filtering the mixture to prepare an extract; And mixing 33-37 parts by weight of carbon fiber and 63-67 parts by weight of the extract and irradiating with ultrasonic waves;
또한, 상기 타일용 접착제는 백색시멘트 36-38 중량부, 규사 18-22 중량부, 우레탄계 고분자 수지 8-12 중량부, 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 실리콘계 화합물 0.3-3 중량부, 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 탄소섬유 분산액 21-25 중량부를 포함하는 제2 조성물을 포함하는 것이 바람직하고, 백색시멘트 37-39 중량부, 규사 19-21 중량부, 우레탄계 고분자 수지 9-11 중량부, 아크릴계 화합물을 포함하는 아크릴계 혼합물 1-3 중량부, 실리콘계 화합물 0.5-1.5 중량부, 광석분말 4-6 중량부, 메틸셀룰로오스 0.3-0.7 중량부, 셀룰로오스 섬유 0.3-0.7 중량부 및 탄소섬유 분산액 22-24 중량부를 포함하는 제1 조성물을 포함하는 것이 더욱 바람직하다.In addition, the tile adhesive includes 36-38 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of a urethane-based polymer resin, 0.5-4 parts by weight of an acrylic mixture containing an acrylic compound, and 0.3-3 parts by weight of a silicone-based compound. It is preferable to include a second composition comprising 3-7 parts by weight of ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fiber and 21-25 parts by weight of carbon fiber dispersion, white cement 37-1 part by weight 39 parts by weight, 19-21 parts by weight of silica sand, 9-11 parts by weight of urethane polymer resin, 1-3 parts by weight of an acrylic mixture containing an acrylic compound, 0.5-1.5 parts by weight of a silicone compound, 4-6 parts by weight of ore powder, methyl It is more preferable to include a first composition comprising 0.3-0.7 parts by weight of cellulose, 0.3-0.7 parts by weight of cellulose fibers and 22-24 parts by weight of a carbon fiber dispersion.
상기 우레탄계 고분자 수지는 폴리에테르폴리올, 메틸렌 디페닐 디이소시아네이트(methylene diphenyl diisocyanate) 및 디부틸틴 디라우레이트(dibutyltin dilaurate)를 반응시켜 반응 생성물을 제조하고, 상기 반응 생성물을 아미노트리알콕시실란을 가하여 반응시켜 제조되는 실란 종결 폴리우레탄을 사용하는 것이 바람직하다. 상기 우레탄계 고분자 수지를 포함하여 접착력과 더불어 탄성을 확보할 수 있고, 타일 박리 등의 현상을 방지할 수 있다.The urethane-based polymer resin reacts polyether polyol, methylene diphenyl diisocyanate and dibutyltin dilaurate to prepare a reaction product, and reacts the reaction product by adding aminotrialkoxysilane Preference is given to using silane-terminated polyurethanes prepared by Including the urethane-based polymer resin, adhesion and elasticity can be secured, and phenomena such as peeling of tiles can be prevented.
또한, 본 발명은In addition, the present invention
메틸메타크릴레이트 단량체, n-부틸메타크릴레이트 단량체, 글리시딜메타크릴레이트 단량체 및 하이드록시에틸 메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제1 아크릴레이트계 공중합체를 제조하는 단계; 메틸메타크릴레이트 단량체, 에틸메타크릴레이트 단량체, 아크릴산 단량체 및 메톡시에틸메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제2 아크릴레이트계 공중합체를 제조하는 단계; 및 상기 제1 아크릴레이트계 공중합체와 상기 제2 아크릴레이트계 공중합체를 73-77:23-27의 중량비율로 혼합하는 단계;를 포함하는 아크릴계 고분자 수지를 제조하는 단계;Methyl methacrylate monomer, n-butyl methacrylate monomer, glycidyl methacrylate monomer and hydroxyethyl methacrylate monomer were mixed in a weight ratio of 1:1:1:1, and a catalyst was added to 86- Preparing a first acrylate-based copolymer by reacting at a temperature of 90 ℃; Methyl methacrylate monomer, ethyl methacrylate monomer, acrylic acid monomer and methoxyethyl methacrylate monomer were mixed in a weight ratio of 1: 1: 1: 1, and a catalyst was added to react at a temperature of 86-90 ° C. preparing a second acrylate-based copolymer; and mixing the first acrylate-based copolymer and the second acrylate-based copolymer in a weight ratio of 73-77:23-27; preparing an acrylic polymer resin comprising;
폴리에테르폴리올, 메틸렌 디페닐 디이소시아네이트(methylene diphenyl diisocyanate) 및 디부틸틴 디라우레이트(dibutyltin dilaurate)를 반응시켜 반응 생성물을 제조하는 단계; 및 상기 반응 생성물을 아미노트리알콕시실란을 가하여 반응시키는 단계;를 포함하는 우레탄계 고분자 수지를 제조하는 단계;preparing a reaction product by reacting polyether polyol, methylene diphenyl diisocyanate and dibutyltin dilaurate; Preparing a urethane-based polymer resin comprising; and reacting the reaction product by adding aminotrialkoxysilane.
에틸메타크릴레이트, 라우릴메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 4:4:2의 중량비율로 혼합하여 아크릴계 화합물을 포함하는 아크릴계 혼합물을 제조하는 단계;Preparing an acrylic mixture containing an acrylic compound by mixing ethyl methacrylate, lauryl methacrylate, and dimethacrylate diethylene glycol in a weight ratio of 4:4:2;
일라이트 분말 28-32 중량부, 각섬석 분말 28-32 중량부, 흑운모 분말 28-32 중량부 및 천연연옥 분말 8-12 중량부를 혼합하여 광석분말을 제조하는 단계;Preparing ore powder by mixing 28-32 parts by weight of illite powder, 28-32 parts by weight of amphibole powder, 28-32 parts by weight of biotite powder and 8-12 parts by weight of natural nephrite powder;
일라이트 분말, 각섬석 분말, 흑운모 분말 및 천연연옥 분말을 3:3:3:1의 중량비율로 혼합한 혼합분말을 준비하는 단계; 상기 혼합분말 18-22 중량부 및 증류수 78-82 중량부를 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 84-88℃의 온도로 가열하여 추출하는 단계; 추출 후, 혼합물을 여과하여 추출액을 제조하는 단계; 및 탄소섬유 33-37 중량부 및 상기 추출액 63-67 중량부를 혼합하고 초음파조사하는 단계;를 포함하는 탄소섬유 분산액을 제조하는 단계;preparing a mixed powder obtained by mixing illite powder, amphibole powder, biotite powder, and natural nephrite powder in a weight ratio of 3:3:3:1; Preparing a mixture by mixing 18-22 parts by weight of the mixed powder and 78-82 parts by weight of distilled water; Extracting by heating the mixture at a temperature of 84-88 ° C; After extraction, filtering the mixture to prepare an extract; Preparing a carbon fiber dispersion comprising; and mixing 33-37 parts by weight of carbon fibers and 63-67 parts by weight of the extract and irradiating with ultrasonic waves;
백색시멘트 36-40 중량부, 규사 18-22 중량부, 상기 아크릴계 고분자 수지 8-12 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 상기 화학식 1로 표시되는 실리콘계 화합물 0.3-3 중량부, 상기 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 상기 탄소섬유 분산액 21-25 중량부를 혼합하여 제1 조성물을 제조하는 단계;36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of the acrylic polymer resin, 0.5-4 parts by weight of the acrylic mixture containing the acrylic compound, 0.3-3 parts by weight of the silicone compound represented by Formula 1 preparing a first composition by mixing 3-7 parts by weight of the ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fiber, and 21-25 parts by weight of the carbon fiber dispersion;
백색시멘트 36-40 중량부, 규사 18-22 중량부, 상기 우레탄계 고분자 수지 8-12 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 상기 화학식 1로 표시되는 실리콘계 화합물 0.3-3 중량부, 상기 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 상기 탄소섬유 분산액 21-25 중량부를 혼합하여 제2 조성물을 제조하는 단계;36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of the urethane-based polymer resin, 0.5-4 parts by weight of the acrylic mixture containing the acrylic compound, 0.3-3 parts by weight of the silicone-based compound represented by Formula 1 preparing a second composition by mixing 3-7 parts by weight of the ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fiber, and 21-25 parts by weight of the carbon fiber dispersion;
상기 제1 조성물 73-77 중량부 및 상기 제2 조성물 23-27 중량부를 혼합하여 제3 조성물을 제조하는 단계;preparing a third composition by mixing 73-77 parts by weight of the first composition and 23-27 parts by weight of the second composition;
타일을 시공하기 위한 구조물의 외면을 평탄지게 정리하고, 고압수를 분사하여 이물질을 제거하는 단계;Leveling the outer surface of a structure for constructing tiles and removing foreign substances by spraying high-pressure water;
이물질이 제거된 외면에 상기 제3 조성물을 도포하는 단계; 및applying the third composition to the outer surface from which foreign substances are removed; and
도포된 제3 조성물의 외면에 타일을 부착하는 단계;를 포함하는 타일 시공방법을 제공한다.It provides a tile construction method comprising the step of attaching a tile to the outer surface of the applied third composition.
이때, 도 1에 본 발명의 일 실시예에 따른 타일 시공방법을 순서도로 나타내었으며, 이하, 도 1을 참조하여 본 발명에 따른 타일 시공방법을 각 단계별로 상세히 설명한다.At this time, FIG. 1 shows a tile construction method according to an embodiment of the present invention as a flow chart, and hereinafter, the tile construction method according to the present invention will be described in detail step by step with reference to FIG. 1 .
먼저, 본 발명에 따른 타일 시공방법은 아크릴계 고분자 수지를 제조하는 단계를 포함한다. 상기 아크릴계 고분자 수지를 제조하는 단계는, 메틸메타크릴레이트 단량체, n-부틸메타크릴레이트 단량체, 글리시딜메타크릴레이트 단량체 및 하이드록시에틸 메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제1 아크릴레이트계 공중합체를 제조하는 단계; 메틸메타크릴레이트 단량체, 에틸메타크릴레이트 단량체, 아크릴산 단량체 및 메톡시에틸메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제2 아크릴레이트계 공중합체를 제조하는 단계; 및 상기 제1 아크릴레이트계 공중합체와 상기 제2 아크릴레이트계 공중합체를 73-77:23-27의 중량비율로 혼합하는 단계;를 포함한다.First, the tile construction method according to the present invention includes preparing an acrylic polymer resin. In the step of preparing the acrylic polymer resin, the weight ratio of methyl methacrylate monomer, n-butyl methacrylate monomer, glycidyl methacrylate monomer and hydroxyethyl methacrylate monomer is 1: 1: 1: 1 preparing a first acrylate-based copolymer by adding a catalyst and reacting at a temperature of 86-90 ° C; Methyl methacrylate monomer, ethyl methacrylate monomer, acrylic acid monomer and methoxyethyl methacrylate monomer were mixed in a weight ratio of 1: 1: 1: 1, and a catalyst was added to react at a temperature of 86-90 ° C. preparing a second acrylate-based copolymer; and mixing the first acrylate-based copolymer and the second acrylate-based copolymer in a weight ratio of 73-77:23-27.
다음으로, 본 발명에 따른 타일 시공방법은 우레탄계 고분자 수지를 제조하는 단계를 포함한다. 상기 우레탄계 고분자 수지를 제조하는 단계는, 폴리에테르폴리올, 메틸렌 디페닐 디이소시아네이트(methylene diphenyl diisocyanate) 및 디부틸틴 디라우레이트(dibutyltin dilaurate)를 반응시켜 반응 생성물을 제조하는 단계; 및 상기 반응 생성물을 아미노트리알콕시실란을 가하여 반응시키는 단계;를 포함한다.Next, the tile construction method according to the present invention includes preparing a urethane-based polymer resin. Preparing the urethane-based polymer resin may include preparing a reaction product by reacting polyether polyol, methylene diphenyl diisocyanate, and dibutyltin dilaurate; and reacting the reaction product by adding aminotrialkoxysilane.
다음으로, 본 발명에 따른 타일 시공방법은 에틸메타크릴레이트, 라우릴메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 4:4:2의 중량비율로 혼합하여 아크릴계 화합물을 포함하는 아크릴계 혼합물을 제조하는 단계를 포함한다.Next, in the tile construction method according to the present invention, ethyl methacrylate, lauryl methacrylate, and dimethacrylate diethylene glycol are mixed in a weight ratio of 4: 4: 2 to prepare an acrylic mixture containing an acrylic compound It includes steps to
다음으로, 본 발명에 따른 타일 시공방법은 일라이트 분말 28-32 중량부, 각섬석 분말 28-32 중량부, 흑운모 분말 28-32 중량부 및 천연연옥 분말 8-12 중량부를 혼합하여 광석분말을 제조하는 단계를 포함한다.Next, in the tile construction method according to the present invention, ore powder is prepared by mixing 28-32 parts by weight of illite powder, 28-32 parts by weight of amphibole powder, 28-32 parts by weight of biotite powder, and 8-12 parts by weight of natural nephrite powder. It includes steps to
다음으로, 본 발명에 따른 타일 시공방법은 탄소섬유 분산액을 제조하는 단계를 포함한다. 상기 탄소섬유 분산액을 제조하는 단계는, 일라이트 분말, 각섬석 분말, 흑운모 분말 및 천연연옥 분말을 3:3:3:1의 중량비율로 혼합한 혼합분말을 준비하는 단계; 상기 혼합분말 18-22 중량부 및 증류수 78-82 중량부를 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 84-88℃의 온도로 가열하여 추출하는 단계; 추출 후, 혼합물을 여과하여 추출액을 제조하는 단계; 및 탄소섬유 33-37 중량부 및 상기 추출액 63-67 중량부를 혼합하고 초음파조사하는 단계;를 포함한다.Next, the tile construction method according to the present invention includes preparing a carbon fiber dispersion. The preparing of the carbon fiber dispersion may include preparing a mixed powder obtained by mixing illite powder, amphibolite powder, biotite powder, and natural nephrite powder in a weight ratio of 3:3:3:1; Preparing a mixture by mixing 18-22 parts by weight of the mixed powder and 78-82 parts by weight of distilled water; Extracting by heating the mixture at a temperature of 84-88 ° C; After extraction, filtering the mixture to prepare an extract; and mixing 33-37 parts by weight of carbon fiber and 63-67 parts by weight of the extract and irradiating with ultrasonic waves.
본 발명에서는 단순히 물이 아닌 용매로 탄소섬유 분산액을 적용함으로써 조성물 내 물질들 간의 결합력을 높이고 타일과 구조물 간의 접착력을 향상시킬 수 있다. 더욱이, 탄소섬유 분산액에 적용되는 물은 일라이트, 각섬석, 흑운모 및 천연연옥의 혼합분말을 가열 추출하여 제조되는 물을 사용함으로써 항균 기능을 부여할 수 있다.In the present invention, by applying the carbon fiber dispersion as a solvent other than water, it is possible to increase the bonding strength between materials in the composition and improve the bonding strength between the tile and the structure. Furthermore, water applied to the carbon fiber dispersion may impart an antibacterial function by using water prepared by heating and extracting a mixed powder of illite, amphibole, biotite, and natural nephrite.
다음으로, 본 발명에 따른 타일 시공방법은 백색시멘트 36-40 중량부, 규사 18-22 중량부, 상기 아크릴계 고분자 수지 8-12 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 상기 화학식 1로 표시되는 실리콘계 화합물 0.3-3 중량부, 상기 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 상기 탄소섬유 분산액 21-25 중량부를 혼합하여 제1 조성물을 제조하는 단계를 포함한다.Next, the tile construction method according to the present invention includes 36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of the acrylic polymer resin, 0.5-4 parts by weight of an acrylic mixture containing the acrylic compound, 0.3-3 parts by weight of the silicon-based compound represented by Formula 1, 3-7 parts by weight of the ore powder, 0.1-1 part by weight of methylcellulose, 0.1-1 part by weight of cellulose fibers and 21-25 parts by weight of the carbon fiber dispersion were mixed. and preparing the first composition.
백색시멘트 37-39 중량부, 규사 19-21 중량부, 상기 아크릴계 고분자 수지 9-11 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 1-3 중량부, 상기 화학식 1로 표시되는 실리콘계 화합물 0.5-1.5 중량부, 상기 광석분말 4-6 중량부, 메틸셀룰로오스 0.3-0.7 중량부, 셀룰로오스 섬유 0.3-0.7 중량부 및 상기 탄소섬유 분산액 22-24 중량부를 혼합하는 것이 더욱 바람직하다.37-39 parts by weight of white cement, 19-21 parts by weight of silica sand, 9-11 parts by weight of the acrylic polymer resin, 1-3 parts by weight of the acrylic mixture containing the acrylic compound, 0.5-1.5 parts by weight of the silicone compound represented by Formula 1 It is more preferable to mix 4-6 parts by weight of the ore powder, 0.3-0.7 parts by weight of methyl cellulose, 0.3-0.7 parts by weight of cellulose fibers and 22-24 parts by weight of the carbon fiber dispersion.
다음으로, 본 발명에 따른 타일 시공방법은 백색시멘트 36-40 중량부, 규사 18-22 중량부, 상기 우레탄계 고분자 수지 8-12 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 상기 화학식 1로 표시되는 실리콘계 화합물 0.3-3 중량부, 상기 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 상기 탄소섬유 분산액 21-25 중량부를 혼합하여 제2 조성물을 제조하는 단계를 포함한다.Next, the tile construction method according to the present invention includes 36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of the urethane-based polymer resin, 0.5-4 parts by weight of an acrylic mixture containing the acrylic compound, 0.3-3 parts by weight of the silicon-based compound represented by Formula 1, 3-7 parts by weight of the ore powder, 0.1-1 part by weight of methylcellulose, 0.1-1 part by weight of cellulose fibers and 21-25 parts by weight of the carbon fiber dispersion were mixed. and preparing a second composition.
백색시멘트 37-39 중량부, 규사 19-21 중량부, 상기 우레탄계 고분자 수지 9-11 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 1-3 중량부, 상기 화학식 1로 표시되는 실리콘계 화합물 0.5-1.5 중량부, 상기 광석분말 4-6 중량부, 메틸셀룰로오스 0.3-0.7 중량부, 셀룰로오스 섬유 0.3-0.7 중량부 및 상기 탄소섬유 분산액 22-24 중량부를 혼합하는 것이 더욱 바람직하다.37-39 parts by weight of white cement, 19-21 parts by weight of silica sand, 9-11 parts by weight of the urethane-based polymer resin, 1-3 parts by weight of the acrylic mixture containing the acrylic compound, 0.5-1.5 parts by weight of the silicone-based compound represented by Formula 1 It is more preferable to mix 4-6 parts by weight of the ore powder, 0.3-0.7 parts by weight of methyl cellulose, 0.3-0.7 parts by weight of cellulose fibers and 22-24 parts by weight of the carbon fiber dispersion.
다음으로, 본 발명에 따른 타일 시공방법은 상기 제1 조성물 73-77 중량부 및 상기 제2 조성물 23-27 중량부를 혼합하여 제3 조성물을 제조하는 단계를 포함한다.Next, the tile construction method according to the present invention includes preparing a third composition by mixing 73-77 parts by weight of the first composition and 23-27 parts by weight of the second composition.
상기 제1 조성물 74-76 중량부 및 상기 제2 조성물 24-26 중량부를 혼합하여 제3 조성물을 제조하는 것이 더욱 바람직하다. 상기 제1 조성물과 제2 조성물을 혼합하되, 3:1의 중량비율로 혼합하여 제조함으로써 우수한 부착강도와 부착유지력을 얻을 수 있다.It is more preferable to prepare a third composition by mixing 74-76 parts by weight of the first composition and 24-26 parts by weight of the second composition. Excellent adhesion strength and adhesion retention can be obtained by mixing the first composition and the second composition, but mixing them in a weight ratio of 3:1.
다음으로, 본 발명에 따른 타일 시공방법은 타일을 시공하기 위한 구조물의 외면을 평탄지게 정리하고, 고압수를 분사하여 이물질을 제거하는 단계를 포함한다.Next, the tile construction method according to the present invention includes the steps of flattening the outer surface of a structure for constructing tiles and removing foreign substances by spraying high-pressure water.
타일을 시공하기 위한 구조물의 외면에 브러시 또는 그라인더를 이용하여 평편하게 정리한다. 그리고 콤프레셔로 토출되는 고압의 물이나 공기로 이물질을 깨끗하게 제거한다.Use a brush or grinder to flatten the outer surface of the structure for tile construction. Then, foreign substances are removed cleanly with high-pressure water or air discharged from the compressor.
다음으로, 본 발명에 따른 타일 시공방법은 이물질이 제거된 외면에 상기 제3 조성물을 도포하는 단계를 포함한다.Next, the tile construction method according to the present invention includes applying the third composition to the outer surface from which foreign substances are removed.
상기 단계에서는 구조물의 외면에 제3 조성물을 미장한다.In this step, a third composition is plastered on the outer surface of the structure.
다음으로, 본 발명에 따른 타일 시공방법은 도포된 제3 조성물의 외면에 타일을 부착하는 단계를 포함한다.Next, the tile construction method according to the present invention includes attaching a tile to the outer surface of the applied third composition.
최종적으로 타일을 부착하여 시공한다.Finally, the tiles are installed and installed.
상기 타일은 장석 20 중량부, 규석 20 중량부, 토르말린 10 중량부, 도석 10 중량부, 고령토 10 중량부, 활석 10 중량부, 석회석 10 중량부 및 이산화티타늄 10 중량부를 혼합한 제1 조성물 100 중량부에 물 40 중량부를 볼밀에 넣고 볼밀에서 24시간 분쇄하여 유액 조성물을 준비하는 단계; 시멘트 80 중량부, 폐도자기분말 10 중량부, 상기 유액 조성물 7 중량부 및 규산소다 3 중량부를 혼합한 제2 조성물 100 중량부에 물 40 중량부를 혼합하여 시멘트 조성물을 준비하는 단계; 상기 시멘트 조성물을 이용하여 타일을 성형하여 제조하는 단계; 상기 타일을 120℃의 온도에서 1차 건조하는 단계; 1차 건조된 타일에 상기 유액 조성물을 도포하여 코팅하는 단계; 유액 조성물이 코팅된 타일을 180℃의 온도에서 2차 건조하는 단계; 및 2차 건조된 타일을 1100℃의 온도에서 7시간 동안 소성시키는 단계;를 포함하는 타일을 제조하는 단계;를 수행하여 제조되는 것을 사용한다.The tile contains 20 parts by weight of feldspar, 20 parts by weight of silica stone, 10 parts by weight of tourmaline, 10 parts by weight of pottery stone, 10 parts by weight of kaolin, 10 parts by weight of talc, 10 parts by weight of limestone, and 10 parts by weight of a first composition mixed with 10 parts by weight of titanium dioxide. Preparing an emulsion composition by putting 40 parts by weight of water in a ball mill and grinding it in a ball mill for 24 hours; Preparing a cement composition by mixing 40 parts by weight of water with 100 parts by weight of a second composition in which 80 parts by weight of cement, 10 parts by weight of waste ceramic powder, 7 parts by weight of the emulsion composition and 3 parts by weight of sodium silicate are mixed; Forming and manufacturing a tile using the cement composition; primary drying of the tile at a temperature of 120° C.; Applying and coating the emulsion composition on the primarily dried tile; Secondary drying of the tile coated with the emulsion composition at a temperature of 180 ° C; and calcining the secondarily dried tile at a temperature of 1100° C. for 7 hours.
또한, 본 발명은In addition, the present invention
메틸메타크릴레이트 단량체, n-부틸메타크릴레이트 단량체, 글리시딜메타크릴레이트 단량체 및 하이드록시에틸 메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제1 아크릴레이트계 공중합체를 제조하는 단계; 메틸메타크릴레이트 단량체, 에틸메타크릴레이트 단량체, 아크릴산 단량체 및 메톡시에틸메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제2 아크릴레이트계 공중합체를 제조하는 단계; 및 상기 제1 아크릴레이트계 공중합체와 상기 제2 아크릴레이트계 공중합체를 73-77:23-27의 중량비율로 혼합하는 단계;를 포함하는 아크릴계 고분자 수지를 제조하는 단계;Methyl methacrylate monomer, n-butyl methacrylate monomer, glycidyl methacrylate monomer and hydroxyethyl methacrylate monomer were mixed in a weight ratio of 1:1:1:1, and a catalyst was added to 86- Preparing a first acrylate-based copolymer by reacting at a temperature of 90 ℃; Methyl methacrylate monomer, ethyl methacrylate monomer, acrylic acid monomer and methoxyethyl methacrylate monomer were mixed in a weight ratio of 1: 1: 1: 1, and a catalyst was added to react at a temperature of 86-90 ° C. preparing a second acrylate-based copolymer; and mixing the first acrylate-based copolymer and the second acrylate-based copolymer in a weight ratio of 73-77:23-27; preparing an acrylic polymer resin comprising;
폴리에테르폴리올, 메틸렌 디페닐 디이소시아네이트(methylene diphenyl diisocyanate) 및 디부틸틴 디라우레이트(dibutyltin dilaurate)를 반응시켜 반응 생성물을 제조하는 단계; 및 상기 반응 생성물을 아미노트리알콕시실란을 가하여 반응시키는 단계;를 포함하는 우레탄계 고분자 수지를 제조하는 단계;preparing a reaction product by reacting polyether polyol, methylene diphenyl diisocyanate and dibutyltin dilaurate; Preparing a urethane-based polymer resin comprising; and reacting the reaction product by adding aminotrialkoxysilane.
에틸메타크릴레이트, 라우릴메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 4:4:2의 중량비율로 혼합하여 아크릴계 화합물을 포함하는 아크릴계 혼합물을 제조하는 단계;Preparing an acrylic mixture containing an acrylic compound by mixing ethyl methacrylate, lauryl methacrylate, and dimethacrylate diethylene glycol in a weight ratio of 4:4:2;
일라이트 분말 28-32 중량부, 각섬석 분말 28-32 중량부, 흑운모 분말 28-32 중량부 및 천연연옥 분말 8-12 중량부를 혼합하여 광석분말을 제조하는 단계;Preparing ore powder by mixing 28-32 parts by weight of illite powder, 28-32 parts by weight of amphibole powder, 28-32 parts by weight of biotite powder and 8-12 parts by weight of natural nephrite powder;
일라이트 분말, 각섬석 분말, 흑운모 분말 및 천연연옥 분말을 3:3:3:1의 중량비율로 혼합한 혼합분말을 준비하는 단계; 상기 혼합분말 18-22 중량부 및 증류수 78-82 중량부를 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 84-88℃의 온도로 가열하여 추출하는 단계; 추출 후, 혼합물을 여과하여 추출액을 제조하는 단계; 및 탄소섬유 33-37 중량부 및 상기 추출액 63-67 중량부를 혼합하고 초음파조사하는 단계;를 포함하는 탄소섬유 분산액을 제조하는 단계;preparing a mixed powder obtained by mixing illite powder, amphibole powder, biotite powder, and natural nephrite powder in a weight ratio of 3:3:3:1; Preparing a mixture by mixing 18-22 parts by weight of the mixed powder and 78-82 parts by weight of distilled water; Extracting by heating the mixture at a temperature of 84-88 ° C; After extraction, filtering the mixture to prepare an extract; Preparing a carbon fiber dispersion comprising; and mixing 33-37 parts by weight of carbon fibers and 63-67 parts by weight of the extract and irradiating with ultrasonic waves;
백색시멘트 36-40 중량부, 규사 18-22 중량부, 상기 아크릴계 고분자 수지 8-12 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 상기 화학식 1로 표시되는 실리콘계 화합물 0.3-3 중량부, 상기 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 상기 탄소섬유 분산액 21-25 중량부를 혼합하여 제1 조성물을 제조하는 단계;36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of the acrylic polymer resin, 0.5-4 parts by weight of the acrylic mixture containing the acrylic compound, 0.3-3 parts by weight of the silicone compound represented by Formula 1 preparing a first composition by mixing 3-7 parts by weight of the ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fiber, and 21-25 parts by weight of the carbon fiber dispersion;
백색시멘트 36-40 중량부, 규사 18-22 중량부, 상기 우레탄계 고분자 수지 8-12 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 상기 화학식 1로 표시되는 실리콘계 화합물 0.3-3 중량부, 상기 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 상기 탄소섬유 분산액 21-25 중량부를 혼합하여 제2 조성물을 제조하는 단계;36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of the urethane-based polymer resin, 0.5-4 parts by weight of the acrylic mixture containing the acrylic compound, 0.3-3 parts by weight of the silicone-based compound represented by Formula 1 preparing a second composition by mixing 3-7 parts by weight of the ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fiber, and 21-25 parts by weight of the carbon fiber dispersion;
타일을 시공하기 위한 구조물의 외면을 평탄지게 정리하고, 고압수를 분사하여 이물질을 제거하는 단계;Leveling the outer surface of a structure for constructing tiles and removing foreign substances by spraying high-pressure water;
이물질이 제거된 외면에 상기 제1 조성물을 도포하는 단계;Applying the first composition to the outer surface from which foreign substances are removed;
타일의 배면에 상기 제2 조성물을 도포하는 단계; 및applying the second composition to the back surface of the tile; and
상기 제1 조성물이 도포된 외면에 상기 제2 조성물이 배면에 도포된 타일을 부착하는 단계;를 포함하는 타일 시공방법을 제공한다.It provides a tile construction method comprising the step of attaching a tile coated with the second composition to the outer surface coated with the first composition.
이때, 도 2에 본 발명의 일 실시예에 따른 타일 시공방법을 순서도로 나타내었으며, 이하, 도 2를 참조하여 본 발명에 따른 타일 시공방법을 각 단계별로 상세히 설명한다.At this time, FIG. 2 shows a tile construction method according to an embodiment of the present invention as a flowchart, and the tile construction method according to the present invention will be described in detail step by step with reference to FIG. 2 .
먼저, 본 발명에 따른 타일 시공방법은 아크릴계 고분자 수지를 제조하는 단계를 포함한다. 상기 아크릴계 고분자 수지를 제조하는 단계는, 메틸메타크릴레이트 단량체, n-부틸메타크릴레이트 단량체, 글리시딜메타크릴레이트 단량체 및 하이드록시에틸 메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제1 아크릴레이트계 공중합체를 제조하는 단계; 메틸메타크릴레이트 단량체, 에틸메타크릴레이트 단량체, 아크릴산 단량체 및 메톡시에틸메타크릴레이트 단량체를 1:1:1:1의 중량비율로 혼합하고, 촉매를 투입하여 86-90℃의 온도에서 반응시켜 제2 아크릴레이트계 공중합체를 제조하는 단계; 및 상기 제1 아크릴레이트계 공중합체와 상기 제2 아크릴레이트계 공중합체를 73-77:23-27의 중량비율로 혼합하는 단계;를 포함한다.First, the tile construction method according to the present invention includes preparing an acrylic polymer resin. In the step of preparing the acrylic polymer resin, the weight ratio of methyl methacrylate monomer, n-butyl methacrylate monomer, glycidyl methacrylate monomer and hydroxyethyl methacrylate monomer is 1: 1: 1: 1 preparing a first acrylate-based copolymer by adding a catalyst and reacting at a temperature of 86-90 ° C; Methyl methacrylate monomer, ethyl methacrylate monomer, acrylic acid monomer and methoxyethyl methacrylate monomer were mixed in a weight ratio of 1: 1: 1: 1, and a catalyst was added to react at a temperature of 86-90 ° C. preparing a second acrylate-based copolymer; and mixing the first acrylate-based copolymer and the second acrylate-based copolymer in a weight ratio of 73-77:23-27.
다음으로, 본 발명에 따른 타일 시공방법은 우레탄계 고분자 수지를 제조하는 단계를 포함한다. 상기 우레탄계 고분자 수지를 제조하는 단계는, 폴리에테르폴리올, 메틸렌 디페닐 디이소시아네이트(methylene diphenyl diisocyanate) 및 디부틸틴 디라우레이트(dibutyltin dilaurate)를 반응시켜 반응 생성물을 제조하는 단계; 및 상기 반응 생성물을 아미노트리알콕시실란을 가하여 반응시키는 단계;를 포함한다.Next, the tile construction method according to the present invention includes preparing a urethane-based polymer resin. Preparing the urethane-based polymer resin may include preparing a reaction product by reacting polyether polyol, methylene diphenyl diisocyanate, and dibutyltin dilaurate; and reacting the reaction product by adding aminotrialkoxysilane.
다음으로, 본 발명에 따른 타일 시공방법은 에틸메타크릴레이트, 라우릴메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 4:4:2의 중량비율로 혼합하여 아크릴계 화합물을 포함하는 아크릴계 혼합물을 제조하는 단계를 포함한다.Next, in the tile construction method according to the present invention, ethyl methacrylate, lauryl methacrylate, and dimethacrylate diethylene glycol are mixed in a weight ratio of 4: 4: 2 to prepare an acrylic mixture containing an acrylic compound It includes steps to
다음으로, 본 발명에 따른 타일 시공방법은 일라이트 분말 28-32 중량부, 각섬석 분말 28-32 중량부, 흑운모 분말 28-32 중량부 및 천연연옥 분말 8-12 중량부를 혼합하여 광석분말을 제조하는 단계를 포함한다.Next, in the tile construction method according to the present invention, ore powder is prepared by mixing 28-32 parts by weight of illite powder, 28-32 parts by weight of amphibole powder, 28-32 parts by weight of biotite powder, and 8-12 parts by weight of natural nephrite powder. It includes steps to
다음으로, 본 발명에 따른 타일 시공방법은 탄소섬유 분산액을 제조하는 단계를 포함한다. 상기 탄소섬유 분산액을 제조하는 단계는, 일라이트 분말, 각섬석 분말, 흑운모 분말 및 천연연옥 분말을 3:3:3:1의 중량비율로 혼합한 혼합분말을 준비하는 단계; 상기 혼합분말 18-22 중량부 및 증류수 78-82 중량부를 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 84-88℃의 온도로 가열하여 추출하는 단계; 추출 후, 혼합물을 여과하여 추출액을 제조하는 단계; 및 탄소섬유 33-37 중량부 및 상기 추출액 63-67 중량부를 혼합하고 초음파조사하는 단계;를 포함한다.Next, the tile construction method according to the present invention includes preparing a carbon fiber dispersion. The preparing of the carbon fiber dispersion may include preparing a mixed powder obtained by mixing illite powder, amphibolite powder, biotite powder, and natural nephrite powder in a weight ratio of 3:3:3:1; Preparing a mixture by mixing 18-22 parts by weight of the mixed powder and 78-82 parts by weight of distilled water; Extracting by heating the mixture at a temperature of 84-88 ° C; After extraction, filtering the mixture to prepare an extract; and mixing 33-37 parts by weight of carbon fiber and 63-67 parts by weight of the extract and irradiating with ultrasonic waves.
본 발명에서는 단순히 물이 아닌 용매로 탄소섬유 분산액을 적용함으로써 조성물 내 물질들 간의 결합력을 높이고 타일과 구조물 간의 접착력을 향상시킬 수 있다. 더욱이, 탄소섬유 분산액에 적용되는 물은 일라이트, 각섬석, 흑운모 및 천연연옥의 혼합분말을 가열 추출하여 제조되는 물을 사용함으로써 항균 기능을 부여할 수 있다.In the present invention, by applying the carbon fiber dispersion as a solvent other than water, it is possible to increase the bonding strength between materials in the composition and improve the bonding strength between the tile and the structure. Furthermore, water applied to the carbon fiber dispersion may impart an antibacterial function by using water prepared by heating and extracting a mixed powder of illite, amphibole, biotite, and natural nephrite.
다음으로, 본 발명에 따른 타일 시공방법은 백색시멘트 36-40 중량부, 규사 18-22 중량부, 상기 아크릴계 고분자 수지 8-12 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 상기 화학식 1로 표시되는 실리콘계 화합물 0.3-3 중량부, 상기 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 상기 탄소섬유 분산액 21-25 중량부를 혼합하여 제1 조성물을 제조하는 단계를 포함한다.Next, the tile construction method according to the present invention includes 36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of the acrylic polymer resin, 0.5-4 parts by weight of an acrylic mixture containing the acrylic compound, 0.3-3 parts by weight of the silicon-based compound represented by Formula 1, 3-7 parts by weight of the ore powder, 0.1-1 part by weight of methylcellulose, 0.1-1 part by weight of cellulose fibers and 21-25 parts by weight of the carbon fiber dispersion were mixed. and preparing the first composition.
백색시멘트 37-39 중량부, 규사 19-21 중량부, 상기 아크릴계 고분자 수지 9-11 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 1-3 중량부, 상기 화학식 1로 표시되는 실리콘계 화합물 0.5-1.5 중량부, 상기 광석분말 4-6 중량부, 메틸셀룰로오스 0.3-0.7 중량부, 셀룰로오스 섬유 0.3-0.7 중량부 및 상기 탄소섬유 분산액 22-24 중량부를 혼합하는 것이 더욱 바람직하다.37-39 parts by weight of white cement, 19-21 parts by weight of silica sand, 9-11 parts by weight of the acrylic polymer resin, 1-3 parts by weight of the acrylic mixture containing the acrylic compound, 0.5-1.5 parts by weight of the silicone compound represented by Formula 1 It is more preferable to mix 4-6 parts by weight of the ore powder, 0.3-0.7 parts by weight of methyl cellulose, 0.3-0.7 parts by weight of cellulose fibers and 22-24 parts by weight of the carbon fiber dispersion.
다음으로, 본 발명에 따른 타일 시공방법은 백색시멘트 36-40 중량부, 규사 18-22 중량부, 상기 우레탄계 고분자 수지 8-12 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 상기 화학식 1로 표시되는 실리콘계 화합물 0.3-3 중량부, 상기 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 상기 탄소섬유 분산액 21-25 중량부를 혼합하여 제2 조성물을 제조하는 단계를 포함한다.Next, the tile construction method according to the present invention includes 36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of the urethane-based polymer resin, 0.5-4 parts by weight of an acrylic mixture containing the acrylic compound, 0.3-3 parts by weight of the silicon-based compound represented by Formula 1, 3-7 parts by weight of the ore powder, 0.1-1 part by weight of methylcellulose, 0.1-1 part by weight of cellulose fibers and 21-25 parts by weight of the carbon fiber dispersion were mixed. and preparing a second composition.
백색시멘트 37-39 중량부, 규사 19-21 중량부, 상기 우레탄계 고분자 수지 9-11 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 1-3 중량부, 상기 화학식 1로 표시되는 실리콘계 화합물 0.5-1.5 중량부, 상기 광석분말 4-6 중량부, 메틸셀룰로오스 0.3-0.7 중량부, 셀룰로오스 섬유 0.3-0.7 중량부 및 상기 탄소섬유 분산액 22-24 중량부를 혼합하는 것이 더욱 바람직하다.37-39 parts by weight of white cement, 19-21 parts by weight of silica sand, 9-11 parts by weight of the urethane-based polymer resin, 1-3 parts by weight of the acrylic mixture containing the acrylic compound, 0.5-1.5 parts by weight of the silicone-based compound represented by Formula 1 It is more preferable to mix 4-6 parts by weight of the ore powder, 0.3-0.7 parts by weight of methyl cellulose, 0.3-0.7 parts by weight of cellulose fibers and 22-24 parts by weight of the carbon fiber dispersion.
다음으로, 본 발명에 따른 타일 시공방법은 타일을 시공하기 위한 구조물의 외면을 평탄지게 정리하고, 고압수를 분사하여 이물질을 제거하는 단계를 포함한다.Next, the tile construction method according to the present invention includes the steps of flattening the outer surface of a structure for constructing tiles and removing foreign substances by spraying high-pressure water.
타일을 시공하기 위한 구조물의 외면에 브러시 또는 그라인더를 이용하여 평편하게 정리한다. 그리고 콤프레셔로 토출되는 고압의 물이나 공기로 이물질을 깨끗하게 제거한다.Use a brush or grinder to flatten the outer surface of the structure for tile construction. Then, foreign substances are removed cleanly with high-pressure water or air discharged from the compressor.
다음으로, 본 발명에 따른 타일 시공방법은 이물질이 제거된 외면에 상기 제1 조성물을 도포하는 단계를 포함한다.Next, the tile construction method according to the present invention includes applying the first composition to the outer surface from which foreign substances are removed.
상기 단계에서는 구조물의 외면에 제1 조성물을 미장한다. 상기 제1 조성물은 아크릴계 고분자 수지를 포함하는 접착제 조성물로, 제2 조성물과 구분하여 적용함으로써 더욱 높은 접착력을 나타낼 수 있다.In this step, the first composition is plastered on the outer surface of the structure. The first composition is an adhesive composition containing an acrylic polymer resin, and may exhibit higher adhesive strength by being applied separately from the second composition.
다음으로, 본 발명에 따른 타일 시공방법은 타일의 배면에 상기 제2 조성물을 도포하는 단계를 포함한다.Next, the tile construction method according to the present invention includes applying the second composition to the rear surface of the tile.
상기 단계에서는 타일의 배면, 즉, 구조물 외면과 접하는 면에 제2 조성물을 도포한다. 상기 제2 조성물은 우레탄계 고분자 수지를 포함하는 접착제 조성물로, 제1 조성물과 구분하여 적용함으로써 더욱 높은 접착력과 더불어 탄성을 나타내어 타일 시공 이후에 타일 박리 등의 현상을 방지할 수 있다.In this step, the second composition is applied to the rear surface of the tile, that is, the surface in contact with the outer surface of the structure. The second composition is an adhesive composition containing a urethane-based polymer resin, and is applied separately from the first composition to exhibit higher adhesive strength and elasticity, thereby preventing phenomena such as peeling off of tiles after tile construction.
상기 타일은 장석 20 중량부, 규석 20 중량부, 토르말린 10 중량부, 도석 10 중량부, 고령토 10 중량부, 활석 10 중량부, 석회석 10 중량부 및 이산화티타늄 10 중량부를 혼합한 제1 조성물 100 중량부에 물 40 중량부를 볼밀에 넣고 볼밀에서 24시간 분쇄하여 유액 조성물을 준비하는 단계; 시멘트 80 중량부, 폐도자기분말 10 중량부, 상기 유액 조성물 7 중량부 및 규산소다 3 중량부를 혼합한 제2 조성물 100 중량부에 물 40 중량부를 혼합하여 시멘트 조성물을 준비하는 단계; 상기 시멘트 조성물을 이용하여 타일을 성형하여 제조하는 단계; 상기 타일을 120℃의 온도에서 1차 건조하는 단계; 1차 건조된 타일에 상기 유액 조성물을 도포하여 코팅하는 단계; 유액 조성물이 코팅된 타일을 180℃의 온도에서 2차 건조하는 단계; 및 2차 건조된 타일을 1100℃의 온도에서 7시간 동안 소성시키는 단계;를 포함하는 타일을 제조하는 단계;를 수행하여 제조되는 것을 사용한다.The tile contains 20 parts by weight of feldspar, 20 parts by weight of silica stone, 10 parts by weight of tourmaline, 10 parts by weight of pottery stone, 10 parts by weight of kaolin, 10 parts by weight of talc, 10 parts by weight of limestone, and 10 parts by weight of a first composition mixed with 10 parts by weight of titanium dioxide. Preparing an emulsion composition by putting 40 parts by weight of water in a ball mill and grinding it in a ball mill for 24 hours; Preparing a cement composition by mixing 40 parts by weight of water with 100 parts by weight of a second composition in which 80 parts by weight of cement, 10 parts by weight of waste ceramic powder, 7 parts by weight of the emulsion composition and 3 parts by weight of sodium silicate are mixed; Forming and manufacturing a tile using the cement composition; primary drying of the tile at a temperature of 120° C.; Applying and coating the emulsion composition on the primarily dried tile; Secondary drying of the tile coated with the emulsion composition at a temperature of 180 ° C; and calcining the secondarily dried tile at a temperature of 1100° C. for 7 hours.
다음으로, 본 발명에 따른 타일 시공방법은 상기 제1 조성물이 도포된 외면에 상기 제2 조성물이 배면에 도포된 타일을 부착하는 단계를 포함한다.Next, the tile construction method according to the present invention includes attaching a tile coated with the second composition on the outer surface coated with the first composition to the rear surface.
최종적으로 타일을 부착하여 시공한다.Finally, the tiles are installed and installed.
이하, 본 발명을 하기의 실시예에 의해 보다 상세하게 설명한다.Hereinafter, the present invention will be described in more detail by the following examples.
단, 하기 실시예는 본 발명의 내용을 예시하는 것일 뿐 발명의 범위가 실시예 및 실험예에 의해 한정되는 것은 아니다.However, the following examples are merely illustrative of the content of the present invention, but the scope of the invention is not limited by the examples and experimental examples.
<제조예 1> 아크릴계 고분자 수지의 제조<Preparation Example 1> Preparation of acrylic polymer resin
4구 플라스크에 메틸메타크릴레이트 25 중량부 및 n-부틸메타크릴레이트 25 중량부를 투입하고 교반하면서 글리시딜메타크릴레이트 25 중량부와 하이드록시에틸 메타크릴레이트 25 중량부를 순차적으로 투입하고, 촉매로 아조비스이소부티로니트릴(AIBN) 0.01 중량부를 적하 투입하여 88℃까지 승온시켰다. 온도가 일정하게 되었을 때 90분 동안 유지시켰다. 반응이 종결된 후 투명한 액체 상태의 제1 아크릴레이트계 공중합체를 수득하였다. 25 parts by weight of methyl methacrylate and 25 parts by weight of n-butyl methacrylate were added to a four-necked flask, and while stirring, 25 parts by weight of glycidyl methacrylate and 25 parts by weight of hydroxyethyl methacrylate were sequentially added, and the catalyst 0.01 part by weight of azobisisobutyronitrile (AIBN) was added dropwise to the furnace, and the temperature was raised to 88°C. When the temperature became constant, it was held for 90 minutes. After the reaction was completed, a first acrylate-based copolymer in a transparent liquid state was obtained.
다른 4구 플라스크에 메틸메타크릴레이트 25 중량부 및 에틸메타크릴레이트 25 중량부를 투입하고 교반하면서 아크릴산 25 중량부와 메톡시에틸메타크릴레이트 25 중량부를 순차적으로 투입하고, 촉매로 아조비스이소부티로니트릴(AIBN) 0.01 중량부를 적하 투입하여 88℃까지 승온시켰다. 온도가 일정하게 되었을 때 90분 동안 유지시켰다. 반응이 종결된 후 투명한 액체 상태의 제2 아크릴레이트계 공중합체를 수득하였다. 25 parts by weight of methyl methacrylate and 25 parts by weight of ethyl methacrylate were added to another four-necked flask, and 25 parts by weight of acrylic acid and 25 parts by weight of methoxyethyl methacrylate were sequentially added while stirring, and azobisisobutyro as a catalyst 0.01 part by weight of nitrile (AIBN) was added dropwise and the temperature was raised to 88°C. When the temperature became constant, it was held for 90 minutes. After the reaction was completed, a second acrylate-based copolymer in a transparent liquid state was obtained.
상기 제1 아크릴레이트계 공중합체와 제2 아크릴레이트계 공중합체를 75:25의 중량비율로 혼합하여 아크릴계 고분자 수지를 제조하였다.An acrylic polymer resin was prepared by mixing the first acrylate-based copolymer and the second acrylate-based copolymer in a weight ratio of 75:25.
<제조예 2> 우레탄계 고분자 수지의 제조<Preparation Example 2> Preparation of urethane-based polymer resin
4구 플라스크에 분자량 4,000의 폴리에테르폴리올 500 g에 메틸렌 디페닐 디이소시아네이트 37.2 g 및 디부틸틴 디라우레이트 2 ppm을 투입하고 질소분위기 하 75℃의 온도에서 4시간 동안 교반하여 반응시켜 반응 생성물을 제조하였다. 반응 생성물에 아미노트리알콕시실란을 첨가하여 65℃의 온도에서 반응시켜 NCO기를 실란으로 캡핑되도록 하여 실란 종결 폴리우레탄인 우레탄계 고분자 수지를 제조하였다. In a four-necked flask, 37.2 g of methylene diphenyl diisocyanate and 2 ppm of dibutyltin dilaurate were added to 500 g of polyether polyol having a molecular weight of 4,000, and stirred and reacted for 4 hours at a temperature of 75 ° C. under a nitrogen atmosphere to obtain a reaction product. manufactured. Aminotrialkoxysilane was added to the reaction product and reacted at a temperature of 65° C. to cap the NCO group with silane to prepare a silane-terminated polyurethane, urethane-based polymer resin.
<제조예 3> 아크릴계 화합물을 포함하는 아크릴계 혼합물의 제조<Preparation Example 3> Preparation of an acrylic mixture containing an acrylic compound
에틸메타크릴레이트, 라우릴메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 4:4:2의 중량비율로 혼합하여 아크릴계 화합물을 포함하는 아크릴계 혼합물을 제조하였다.Ethyl methacrylate, lauryl methacrylate, and dimethacrylate diethylene glycol were mixed in a weight ratio of 4:4:2 to prepare an acrylic mixture containing an acrylic compound.
<제조예 4> 광석분말의 제조<Production Example 4> Production of ore powder
일라이트 분말 30 중량부, 각섬석 분말 30 중량부, 흑운모 분말 30 중량부 및 천연연옥 분말 10 중량부를 혼합하여 광석분말을 제조하였다.Ore powder was prepared by mixing 30 parts by weight of illite powder, 30 parts by weight of amphibole powder, 30 parts by weight of biotite powder, and 10 parts by weight of natural nephrite powder.
<제조예 5> 탄소섬유 분산액의 제조<Preparation Example 5> Preparation of carbon fiber dispersion
일라이트 분말, 각섬석 분말, 흑운모 분말 및 천연연옥 분말을 3:3:3:1의 중량비율로 혼합한 혼합분말을 준비한 후, 상기 혼합분말 20 중량부 및 증류수 80 중량부를 혼합하여 혼합물을 제조하였다. 이후, 86℃의 온도로 가열하여 추출하고, 추출 후, 혼합물을 여과하여 추출액을 제조하였다. 탄소섬유 35 중량부 및 상기 추출액 65 중량부를 혼합하고 초음파조사하여 탄소섬유 분산액을 제조하였다.After preparing a mixed powder obtained by mixing illite powder, amphibole powder, biotite powder, and natural nephrite powder in a weight ratio of 3: 3: 3: 1, 20 parts by weight of the mixed powder and 80 parts by weight of distilled water were mixed to prepare a mixture. . Thereafter, extraction was performed by heating at a temperature of 86° C., and after extraction, the mixture was filtered to prepare an extract. A carbon fiber dispersion was prepared by mixing 35 parts by weight of carbon fibers and 65 parts by weight of the extract and irradiating with ultrasonic waves.
<실시예 1> 타일용 접착제의 제조-1<Example 1> Preparation of tile adhesive-1
백색시멘트 38 중량부, 규사 20 중량부, 상기 제조예 1에서 제조된 아크릴계 고분자 수지 10 중량부, 상기 제조예 3에서 제조된 아크릴계 화합물을 포함하는 아크릴계 혼합물 2 중량부, 상기 화학식 1로 표시되는 실리콘계 화합물 1 중량부, 상기 제조예 4에서 제조된 광석분말 5 중량부, 메틸셀룰로오스 0.5 중량부, 셀룰로오스 섬유 0.5 중량부 및 상기 제조예 5에서 제조된 탄소섬유 분산액 23 중량부를 혼합하여 타일용 접착제를 제조하였다.38 parts by weight of white cement, 20 parts by weight of silica sand, 10 parts by weight of the acrylic polymer resin prepared in Preparation Example 1, 2 parts by weight of the acrylic mixture containing the acrylic compound prepared in Preparation Example 3, silicone represented by Formula 1 1 part by weight of the compound, 5 parts by weight of the ore powder prepared in Preparation Example 4, 0.5 parts by weight of methylcellulose, 0.5 parts by weight of cellulose fibers, and 23 parts by weight of the carbon fiber dispersion prepared in Preparation Example 5 were mixed to prepare an adhesive for tiles. did
<실시예 2> 타일용 접착제의 제조-2<Example 2> Preparation of tile adhesive-2
백색시멘트 38 중량부, 규사 20 중량부, 상기 제조예 2에서 제조된 우레탄계 고분자 수지 10 중량부, 상기 제조예 3에서 제조된 아크릴계 화합물을 포함하는 아크릴계 혼합물 2 중량부, 상기 화학식 1로 표시되는 실리콘계 화합물 1 중량부, 상기 제조예 4에서 제조된 광석분말 5 중량부, 메틸셀룰로오스 0.5 중량부, 셀룰로오스 섬유 0.5 중량부 및 상기 제조예 5에서 제조된 탄소섬유 분산액 23 중량부를 혼합하여 타일용 접착제를 제조하였다.38 parts by weight of white cement, 20 parts by weight of silica sand, 10 parts by weight of the urethane-based polymer resin prepared in Preparation Example 2, 2 parts by weight of the acrylic mixture containing the acrylic compound prepared in Preparation Example 3, Silicone represented by Formula 1 1 part by weight of the compound, 5 parts by weight of the ore powder prepared in Preparation Example 4, 0.5 parts by weight of methylcellulose, 0.5 parts by weight of cellulose fibers, and 23 parts by weight of the carbon fiber dispersion prepared in Preparation Example 5 were mixed to prepare an adhesive for tiles. did
<실시예 3> 타일용 접착제의 제조-3<Example 3> Preparation of tile adhesive-3
상기 실시예 1에서 제조된 타일용 접착제 75 중량부 및 상기 실시예 2에서 제조된 타일용 접착제 25 중량부를 혼합하여 타일용 접착제를 제조하였다.A tile adhesive was prepared by mixing 75 parts by weight of the tile adhesive prepared in Example 1 and 25 parts by weight of the tile adhesive prepared in Example 2.
<실험예 1> 물성 분석<Experimental Example 1> Physical property analysis
상기 실시예 1, 실시예 2 및 실시예 3에서 제조된 타일용 접착제를 사용하여 타일을 시공하는 경우 부착강도 등의 물성을 확인하기 위하여, 아래와 같은 시험을 수행하였다.In order to confirm physical properties such as adhesive strength when constructing tiles using the tile adhesives prepared in Examples 1, 2, and 3, the following tests were performed.
1. 부착강도 및 부착가능시간1. Attachment strength and attachment time
바탕재로 도자기질 타일을 40×40 mm로 절단하여 사용하였다.Porcelain tiles cut into 40 × 40 mm were used as the base material.
KS L 1593의 철제 도포용 보조틀에 평활면을 위로 하여 바탕재 5매를 틈이 없이 삽입 고정하고, 공시 접착제의 적당량을 취하고 표준 빗으로 도포한다. 접착제의 도포 조작을 할 때에는 바탕재에 KS A1527에 규정하는 테이프를 나비 7 mm 덮이도록 부착하고 적당량의 접착제를 올려놓고, 주걱 등을 사용하여 두께 7 mm로 도포한 후, 표준빗을 각도 약 60°로 세워서 양속으로 단번에 자기 앞으로 당겨 접착제를 5매의 바탕재로 균일하게 도포한다. 테이프는 접착제 도포 후, 즉시 서서히 벗겨낸다.Insert and fix 5 sheets of base material without gaps with the smooth surface facing up on the steel application frame of KS L 1593, take an appropriate amount of the test adhesive and apply it with a standard comb. When applying the adhesive, attach the tape specified in KS A1527 to the base material so that it covers the width of 7 mm, place an appropriate amount of adhesive, apply it with a spatula, etc. to a thickness of 7 mm, and then use a standard comb at an angle of about 60° Stand upright and pull it in front of you at once with both hands to apply the adhesive evenly to the base material of 5 sheets. The tape is slowly peeled off immediately after application of the adhesive.
접착제 도포 후 원칙적으로 5분 후에 미리 40×40 mm의 크기로 절단한 도자기질 타일을 접착제가 도포된 바탕재의 중앙에 가만히 올려놓고 다시 그 위에 무게 1 kg의 추를 약 30초간 올려놓은 후, 추를 제거하여 7일간 양생한다. In principle, 5 minutes after applying the adhesive, place the porcelain tile cut into a size of 40 × 40 mm in advance on the center of the base material to which the adhesive is applied, and place a weight of 1 kg on it again for about 30 seconds. Remove and cure for 7 days.
단, 실시예 4로 실시예 1과 실시예 2의 접착제를 각각 사용하기 위해, 깨끗한 바닥면에 실시예 1의 접착제를 약 4 mm 두께로 도포하고, 바탕재에는 실시예 2의 접착제를 약 3 mm 두께로 도포한 후 동일한 방법으로 양생하였다.However, in order to use the adhesives of Example 1 and Example 2 as Example 4, the adhesive of Example 1 was applied to a thickness of about 4 mm on a clean floor surface, and the adhesive of Example 2 was applied to the base material by about 3 mm. After applying to a thickness of mm, it was cured in the same way.
양생 4일에서 6일 사이에 KS L 1593에서 규전한 철편을 표준 상태 속에서 에폭시 수지계 접착제 등으로 타일에 접착한다(시험체를 작성할 때 타일의 시유 면을 샌드 페이퍼 등으로 거칠게 하여 두면 좋다.).Between the 4th and 6th day of curing, attach the iron piece that has been tempered according to KS L 1593 to the tile with an epoxy resin-based adhesive, etc. in a standard state (when preparing a specimen, it is good to roughen the glazed surface of the tile with sandpaper, etc.).
시험기는 파괴하중이 시험기 용량이 15-85％에 들 수 있는 인장 시험기로서, 인장속도를 3 mm/min로 조절할 수 있는 것으로 한다.The testing machine is a tensile testing machine in which the breaking load can be 15-85% of the testing machine capacity, and the tensile speed can be adjusted to 3 mm/min.
부착강도는 시험체를 양생한 후, 지그를 사용하여 시험기에 장치하고, 인장속도 3 mm/min로 인장시험을 하고 끊어질 때까지의 최대하중을 측정하고 끊어진 상태를 기록한다. 또한 인장시험은 양생종료 후 즉시 한다.For adhesion strength, after curing the specimen, place it in a tester using a jig, conduct a tensile test at a tensile speed of 3 mm/min, measure the maximum load until it breaks, and record the broken state. In addition, the tensile test is performed immediately after curing is completed.
부착강도는 F=P/A의 식으로 계산하며, 여기서 F는 부착강도(kgf/cm2), P는 최대하중(kgf), A는 타일의 면적(cm2)을 의미한다. 부착강도는 5시험체의 평균치로 표시한다.The bond strength is calculated by the formula F=P/A, where F is the bond strength (kgf/cm 2 ), P is the maximum load (kgf), and A is the area of the tile (cm 2 ). The adhesive strength is expressed as the average value of 5 specimens.
부착가능시간은 표준 접착강도를 만족하는 최장의 시간으로 한다.The attachable time is the longest time that satisfies the standard adhesive strength.
2. 휨변형 시험 (ISO 13007 : Part 2 / Part 4 4.5절)2. Bending test (ISO 13007: Part 2 / Part 4 Section 4.5)
시험기계는 2 mm/min의 비율로 시험체에 가압이 가능한 기계로 하고, 플로우 테이블은 300×45×3 mm의 공시체가 맞도록 준비하였다.The test machine was a machine capable of pressurizing the specimen at a rate of 2 mm/min, and the flow table was prepared to fit a specimen of 300 × 45 × 3 mm.
시험체로 몰탈용 플로우 테이블에 몰드를 단단하게 고정하고, 시료를 채우고 몰탈용 플로우 장치로 진동을 70번 사용하여 채운다.Firmly fix the mold on the mortar flow table with the test body, fill the sample, and use the mortar flow device to vibrate 70 times.
플로우 테이블에서 몰드를 조심스럽게 들어내어, 제거한다.The mold is carefully lifted off the flow table and removed.
공시체 모양에 맞는 몰드를 시료 위에서 눌러 공시체가 모양이 300×45×3 mm의 사각형태가 되도록 한다. 몰드에서 넘치는 재료를 제거하고, 48시간 후 탈형한다.A mold suitable for the shape of the specimen is pressed on the sample so that the specimen has a square shape of 300 × 45 × 3 mm. Remove excess material from the mold and demold after 48 hours.
공시체를 탈형하고, 밀폐된 플라스틱 그릇에 넣고 실링한다. 23±2℃ 12일 양생 후 플라스틱 그릇에서 꺼내어 20±2℃, 습도 60±5%의 조건에서 14일 양생한다. The specimen is demolded, placed in an airtight plastic bowl and sealed. After curing for 12 days at 23±2℃, take it out of the plastic bowl and cure for 14 days at 20±2℃ and humidity of 60±5%.
양생이 끝난 후 공시체 3곳의 두께를 측정하여(시험체를 4등분한 점들을 측정) 각 지점의 측정값이 평균값에서 3±0.1mm 이상의 오차가 나면, 공시체를 버린다.After curing is completed, measure the thickness of the specimen at 3 places (measure the points where the specimen is divided into 4 parts), and if the measured value at each point has an error of more than 3±0.1mm from the average value, discard the specimen.
공시체의 중간을 시험기로 2mm/min의 비율로 하중을 주어 mm 단위로 시작점부터 휨변형을 측정하며, 0.1 mm까지 변형치를 측정한다. A load is applied to the middle of the specimen at a rate of 2 mm/min with a tester, and the bending deformation is measured from the starting point in mm units, and the deformation value is measured up to 0.1 mm.
그 결과를 하기 표 1에 나타내었다.The results are shown in Table 1 below.
* 실시예 4는 부착강도 및 부착가능시간만 측정되었음* In Example 4, only the adhesion strength and the possible adhesion time were measured
상기 표 1에 나타낸 바와 같이, 본 발명에 따른 실시예 1 및 실시예 2에서 제조되는 타일용 접착제를 적용하는 경우 부착강도, 부착가능시간 및 휨변형시험에서 우수한 결과를 얻을 수 있음을 확인하였다.As shown in Table 1, it was confirmed that excellent results can be obtained in the adhesion strength, adhesion time and bending deformation test when the tile adhesives prepared in Examples 1 and 2 according to the present invention are applied.
특히, 상기 실시예 3의 타일용 접착제는 우수한 성능을 나타내었으며, 나아가서는 실시예 4와 같이 본 발명에 따른 2개의 타일용 접착제를 이용하여 타일을 시공하는 경우 더욱 우수한 성능을 나타냄을 확인하였다.In particular, it was confirmed that the tile adhesive of Example 3 exhibited excellent performance, and furthermore, as in Example 4, when tiles were constructed using the two tile adhesives according to the present invention, even better performance was exhibited.
Claims (5)
상기 타일용 접착제는 백색시멘트 36-40 중량부, 규사 18-22 중량부, 아크릴계 고분자 수지 8-12 중량부, 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 실리콘계 화합물 0.3-3 중량부, 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 탄소섬유 분산액 21-25 중량부를 포함하는 제1 조성물을 포함하고,
상기 아크릴계 고분자 수지는 메틸메타크릴레이트 단량체 단위 23-27 중량%, n-부틸메타크릴레이트 단량체 단위 23-27 중량%, 글리시딜메타크릴레이트 단량체 단위 23-27 중량% 및 하이드록시에틸 메타크릴레이트 단량체 단위 23-27 중량%인 제1 아크릴레이트계 공중합체 및 메틸메타크릴레이트 단량체 단위 23-27 중량%, 에틸메타크릴레이트 단량체 단위 23-27 중량%, 아크릴산 단량체 단위 23-27 중량% 및 메톡시에틸메타크릴레이트 단량체 단위 23-27 중량%인 제2 아크릴레이트계 공중합체의 73-77:23-27의 중량비율로 혼합된 혼합물이고,
상기 아크릴계 화합물을 포함하는 아크릴계 혼합물은 에틸메타크릴레이트, 라우릴메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 4:4:2의 중량비율로 혼합된 혼합물이고,
상기 실리콘계 화합물은 하기 화학식 1로 표시되는 화합물이고,
상기 광석분말은 일라이트 분말 28-32 중량부, 각섬석 분말 28-32 중량부, 흑운모 분말 28-32 중량부 및 천연연옥 분말 8-12 중량부를 포함하고,
상기 탄소섬유 분산액은,
일라이트 분말, 각섬석 분말, 흑운모 분말 및 천연연옥 분말을 3:3:3:1의 중량비율로 혼합한 혼합분말을 준비하는 단계; 상기 혼합분말 18-22 중량부 및 증류수 78-82 중량부를 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 84-88℃의 온도로 가열하여 추출하는 단계; 추출 후, 혼합물을 여과하여 추출액을 제조하는 단계; 및 탄소섬유 33-37 중량부 및 상기 추출액 63-67 중량부를 혼합하고 초음파조사하는 단계;를 수행하여 제조되는 것을 특징으로 하는 타일용 접착제:
<화학식 1>
The tile adhesive includes 36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of an acrylic polymer resin, 0.5-4 parts by weight of an acrylic mixture containing an acrylic compound, 0.3-3 parts by weight of a silicone compound, A first composition comprising 3-7 parts by weight of ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fiber and 21-25 parts by weight of a carbon fiber dispersion,
The acrylic polymer resin contains 23-27% by weight of methyl methacrylate monomer unit, 23-27% by weight of n-butyl methacrylate monomer unit, 23-27% by weight of glycidyl methacrylate monomer unit, and hydroxyethyl methacrylate. A first acrylate-based copolymer comprising 23-27% by weight of late monomer units and 23-27% by weight of methyl methacrylate monomer units, 23-27% by weight of ethyl methacrylate monomer units, 23-27% by weight of acrylic acid monomer units and A mixture of a second acrylate-based copolymer having 23-27% by weight of methoxyethyl methacrylate monomer units in a weight ratio of 73-77:23-27,
The acrylic mixture containing the acrylic compound is a mixture in which ethyl methacrylate, lauryl methacrylate, and dimethacrylate diethylene glycol are mixed in a weight ratio of 4:4:2,
The silicone-based compound is a compound represented by Formula 1 below,
The ore powder includes 28-32 parts by weight of illite powder, 28-32 parts by weight of amphibole powder, 28-32 parts by weight of biotite powder and 8-12 parts by weight of natural nephrite powder,
The carbon fiber dispersion,
preparing a mixed powder obtained by mixing illite powder, amphibole powder, biotite powder, and natural nephrite powder in a weight ratio of 3:3:3:1; Preparing a mixture by mixing 18-22 parts by weight of the mixed powder and 78-82 parts by weight of distilled water; Extracting by heating the mixture at a temperature of 84-88 ° C; After extraction, filtering the mixture to prepare an extract; and mixing 33-37 parts by weight of carbon fiber and 63-67 parts by weight of the extract and irradiating with ultrasonic waves;
<Formula 1>
상기 타일용 접착제는 백색시멘트 36-40 중량부, 규사 18-22 중량부, 우레탄계 고분자 수지 8-12 중량부, 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 실리콘계 화합물 0.3-3 중량부, 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 탄소섬유 분산액 21-25 중량부를 포함하는 제2 조성물을 포함하고,
상기 우레탄계 고분자 수지는 폴리에테르폴리올, 메틸렌 디페닐 디이소시아네이트(methylene diphenyl diisocyanate) 및 디부틸틴 디라우레이트(dibutyltin dilaurate)를 반응시켜 반응 생성물을 제조하고, 상기 반응 생성물을 아미노트리알콕시실란을 가하여 반응시켜 제조되는 실란 종결 폴리우레탄이고,
상기 아크릴계 화합물을 포함하는 아크릴계 혼합물은 에틸메타크릴레이트, 라우릴메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 4:4:2의 중량비율로 혼합된 혼합물이고,
상기 실리콘계 화합물은 하기 화학식 1로 표시되는 화합물이고,
상기 광석분말은 일라이트 분말 28-32 중량부, 각섬석 분말 28-32 중량부, 흑운모 분말 28-32 중량부 및 천연연옥 분말 8-12 중량부를 포함하고,
상기 탄소섬유 분산액은,
일라이트 분말, 각섬석 분말, 흑운모 분말 및 천연연옥 분말을 3:3:3:1의 중량비율로 혼합한 혼합분말을 준비하는 단계; 상기 혼합분말 18-22 중량부 및 증류수 78-82 중량부를 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 84-88℃의 온도로 가열하여 추출하는 단계; 추출 후, 혼합물을 여과하여 추출액을 제조하는 단계; 및 탄소섬유 33-37 중량부 및 상기 추출액 63-67 중량부를 혼합하고 초음파조사하는 단계;를 수행하여 제조되는 것을 특징으로 하는 타일용 접착제:
<화학식 1>
The tile adhesive includes 36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of a urethane polymer resin, 0.5-4 parts by weight of an acrylic mixture containing an acrylic compound, 0.3-3 parts by weight of a silicone compound, A second composition comprising 3-7 parts by weight of ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fiber and 21-25 parts by weight of a carbon fiber dispersion,
The urethane-based polymer resin reacts polyether polyol, methylene diphenyl diisocyanate and dibutyltin dilaurate to prepare a reaction product, and reacts the reaction product by adding aminotrialkoxysilane It is a silane-terminated polyurethane prepared by
The acrylic mixture containing the acrylic compound is a mixture in which ethyl methacrylate, lauryl methacrylate, and dimethacrylate diethylene glycol are mixed in a weight ratio of 4:4:2,
The silicone-based compound is a compound represented by Formula 1 below,
The ore powder includes 28-32 parts by weight of illite powder, 28-32 parts by weight of amphibole powder, 28-32 parts by weight of biotite powder and 8-12 parts by weight of natural nephrite powder,
The carbon fiber dispersion,
preparing a mixed powder obtained by mixing illite powder, amphibole powder, biotite powder, and natural nephrite powder in a weight ratio of 3:3:3:1; Preparing a mixture by mixing 18-22 parts by weight of the mixed powder and 78-82 parts by weight of distilled water; Extracting by heating the mixture at a temperature of 84-88 ° C; After extraction, filtering the mixture to prepare an extract; and mixing 33-37 parts by weight of carbon fiber and 63-67 parts by weight of the extract and irradiating with ultrasonic waves;
<Formula 1>
폴리에테르폴리올, 메틸렌 디페닐 디이소시아네이트(methylene diphenyl diisocyanate) 및 디부틸틴 디라우레이트(dibutyltin dilaurate)를 반응시켜 반응 생성물을 제조하는 단계; 및 상기 반응 생성물을 아미노트리알콕시실란을 가하여 반응시키는 단계;를 포함하는 우레탄계 고분자 수지를 제조하는 단계;
에틸메타크릴레이트, 라우릴메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 4:4:2의 중량비율로 혼합하여 아크릴계 화합물을 포함하는 아크릴계 혼합물을 제조하는 단계;
일라이트 분말 28-32 중량부, 각섬석 분말 28-32 중량부, 흑운모 분말 28-32 중량부 및 천연연옥 분말 8-12 중량부를 혼합하여 광석분말을 제조하는 단계;
일라이트 분말, 각섬석 분말, 흑운모 분말 및 천연연옥 분말을 3:3:3:1의 중량비율로 혼합한 혼합분말을 준비하는 단계; 상기 혼합분말 18-22 중량부 및 증류수 78-82 중량부를 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 84-88℃의 온도로 가열하여 추출하는 단계; 추출 후, 혼합물을 여과하여 추출액을 제조하는 단계; 및 탄소섬유 33-37 중량부 및 상기 추출액 63-67 중량부를 혼합하고 초음파조사하는 단계;를 포함하는 탄소섬유 분산액을 제조하는 단계;
백색시멘트 36-40 중량부, 규사 18-22 중량부, 상기 아크릴계 고분자 수지 8-12 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 하기 화학식 1로 표시되는 실리콘계 화합물 0.3-3 중량부, 상기 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 상기 탄소섬유 분산액 21-25 중량부를 혼합하여 제1 조성물을 제조하는 단계;
백색시멘트 36-40 중량부, 규사 18-22 중량부, 상기 우레탄계 고분자 수지 8-12 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 하기 화학식 1로 표시되는 실리콘계 화합물 0.3-3 중량부, 상기 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 상기 탄소섬유 분산액 21-25 중량부를 혼합하여 제2 조성물을 제조하는 단계;
상기 제1 조성물 73-77 중량부 및 상기 제2 조성물 23-27 중량부를 혼합하여 제3 조성물을 제조하는 단계;
타일을 시공하기 위한 구조물의 외면을 평탄지게 정리하고, 고압수를 분사하여 이물질을 제거하는 단계;
이물질이 제거된 외면에 상기 제3 조성물을 도포하는 단계; 및
도포된 제3 조성물의 외면에 타일을 부착하는 단계;를 포함하는 타일 시공방법:
<화학식 1>
preparing a reaction product by reacting polyether polyol, methylene diphenyl diisocyanate and dibutyltin dilaurate; Preparing a urethane-based polymer resin comprising; and reacting the reaction product by adding aminotrialkoxysilane.
Preparing an acrylic mixture containing an acrylic compound by mixing ethyl methacrylate, lauryl methacrylate, and dimethacrylate diethylene glycol in a weight ratio of 4:4:2;
Preparing ore powder by mixing 28-32 parts by weight of illite powder, 28-32 parts by weight of amphibole powder, 28-32 parts by weight of biotite powder and 8-12 parts by weight of natural nephrite powder;
preparing a mixed powder obtained by mixing illite powder, amphibole powder, biotite powder, and natural nephrite powder in a weight ratio of 3:3:3:1; Preparing a mixture by mixing 18-22 parts by weight of the mixed powder and 78-82 parts by weight of distilled water; Extracting by heating the mixture at a temperature of 84-88 ° C; After extraction, filtering the mixture to prepare an extract; Preparing a carbon fiber dispersion comprising; and mixing 33-37 parts by weight of carbon fibers and 63-67 parts by weight of the extract and irradiating with ultrasonic waves;
36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of the acrylic polymer resin, 0.5-4 parts by weight of the acrylic mixture containing the acrylic compound, 0.3-3 parts by weight of the silicone compound represented by Formula 1 below preparing a first composition by mixing 3-7 parts by weight of the ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fiber, and 21-25 parts by weight of the carbon fiber dispersion;
36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of the urethane-based polymer resin, 0.5-4 parts by weight of an acrylic mixture containing the acrylic compound, 0.3-3 parts by weight of a silicone-based compound represented by Formula 1 below preparing a second composition by mixing 3-7 parts by weight of the ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fiber, and 21-25 parts by weight of the carbon fiber dispersion;
preparing a third composition by mixing 73-77 parts by weight of the first composition and 23-27 parts by weight of the second composition;
Leveling the outer surface of a structure for constructing tiles and removing foreign substances by spraying high-pressure water;
applying the third composition to the outer surface from which foreign substances are removed; and
A tile construction method comprising: attaching a tile to the outer surface of the applied third composition:
<Formula 1>
폴리에테르폴리올, 메틸렌 디페닐 디이소시아네이트(methylene diphenyl diisocyanate) 및 디부틸틴 디라우레이트(dibutyltin dilaurate)를 반응시켜 반응 생성물을 제조하는 단계; 및 상기 반응 생성물을 아미노트리알콕시실란을 가하여 반응시키는 단계;를 포함하는 우레탄계 고분자 수지를 제조하는 단계;
에틸메타크릴레이트, 라우릴메타크릴레이트 및 디메타크릴레이트 디에틸렌글리콜이 4:4:2의 중량비율로 혼합하여 아크릴계 화합물을 포함하는 아크릴계 혼합물을 제조하는 단계;
일라이트 분말 28-32 중량부, 각섬석 분말 28-32 중량부, 흑운모 분말 28-32 중량부 및 천연연옥 분말 8-12 중량부를 혼합하여 광석분말을 제조하는 단계;
일라이트 분말, 각섬석 분말, 흑운모 분말 및 천연연옥 분말을 3:3:3:1의 중량비율로 혼합한 혼합분말을 준비하는 단계; 상기 혼합분말 18-22 중량부 및 증류수 78-82 중량부를 혼합하여 혼합물을 제조하는 단계; 상기 혼합물을 84-88℃의 온도로 가열하여 추출하는 단계; 추출 후, 혼합물을 여과하여 추출액을 제조하는 단계; 및 탄소섬유 33-37 중량부 및 상기 추출액 63-67 중량부를 혼합하고 초음파조사하는 단계;를 포함하는 탄소섬유 분산액을 제조하는 단계;
백색시멘트 36-40 중량부, 규사 18-22 중량부, 상기 아크릴계 고분자 수지 8-12 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 하기 화학식 1로 표시되는 실리콘계 화합물 0.3-3 중량부, 상기 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 상기 탄소섬유 분산액 21-25 중량부를 혼합하여 제1 조성물을 제조하는 단계;
백색시멘트 36-40 중량부, 규사 18-22 중량부, 상기 우레탄계 고분자 수지 8-12 중량부, 상기 아크릴계 화합물을 포함하는 아크릴계 혼합물 0.5-4 중량부, 하기 화학식 1로 표시되는 실리콘계 화합물 0.3-3 중량부, 상기 광석분말 3-7 중량부, 메틸셀룰로오스 0.1-1 중량부, 셀룰로오스 섬유 0.1-1 중량부 및 상기 탄소섬유 분산액 21-25 중량부를 혼합하여 제2 조성물을 제조하는 단계;
타일을 시공하기 위한 구조물의 외면을 평탄지게 정리하고, 고압수를 분사하여 이물질을 제거하는 단계;
이물질이 제거된 외면에 상기 제1 조성물을 도포하는 단계;
타일의 배면에 상기 제2 조성물을 도포하는 단계; 및
상기 제1 조성물이 도포된 외면에 상기 제2 조성물이 배면에 도포된 타일을 부착하는 단계;를 포함하는 타일 시공방법:
<화학식 1>
preparing a reaction product by reacting polyether polyol, methylene diphenyl diisocyanate and dibutyltin dilaurate; Preparing a urethane-based polymer resin comprising; and reacting the reaction product by adding aminotrialkoxysilane.
Preparing an acrylic mixture containing an acrylic compound by mixing ethyl methacrylate, lauryl methacrylate, and dimethacrylate diethylene glycol in a weight ratio of 4:4:2;
Preparing ore powder by mixing 28-32 parts by weight of illite powder, 28-32 parts by weight of amphibole powder, 28-32 parts by weight of biotite powder and 8-12 parts by weight of natural nephrite powder;
preparing a mixed powder obtained by mixing illite powder, amphibole powder, biotite powder, and natural nephrite powder in a weight ratio of 3:3:3:1; Preparing a mixture by mixing 18-22 parts by weight of the mixed powder and 78-82 parts by weight of distilled water; Extracting by heating the mixture at a temperature of 84-88 ° C; After extraction, filtering the mixture to prepare an extract; Preparing a carbon fiber dispersion comprising; and mixing 33-37 parts by weight of carbon fibers and 63-67 parts by weight of the extract and irradiating with ultrasonic waves;
36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of the acrylic polymer resin, 0.5-4 parts by weight of the acrylic mixture containing the acrylic compound, 0.3-3 parts by weight of the silicone compound represented by Formula 1 below preparing a first composition by mixing 3-7 parts by weight of the ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fiber, and 21-25 parts by weight of the carbon fiber dispersion;
36-40 parts by weight of white cement, 18-22 parts by weight of silica sand, 8-12 parts by weight of the urethane-based polymer resin, 0.5-4 parts by weight of an acrylic mixture containing the acrylic compound, 0.3-3 parts by weight of a silicone-based compound represented by Formula 1 below preparing a second composition by mixing 3-7 parts by weight of the ore powder, 0.1-1 part by weight of methyl cellulose, 0.1-1 part by weight of cellulose fiber, and 21-25 parts by weight of the carbon fiber dispersion;
Leveling the outer surface of a structure for constructing tiles and removing foreign substances by spraying high-pressure water;
Applying the first composition to the outer surface from which foreign substances are removed;
applying the second composition to the back surface of the tile; and
A tile construction method comprising: attaching a tile coated with the second composition to the outer surface coated with the first composition;
<Formula 1>