KR102495495B1 - Method of manufacturing a flame resistance leather - Google Patents
Method of manufacturing a flame resistance leather Download PDFInfo
- Publication number
- KR102495495B1 KR102495495B1 KR1020210067456A KR20210067456A KR102495495B1 KR 102495495 B1 KR102495495 B1 KR 102495495B1 KR 1020210067456 A KR1020210067456 A KR 1020210067456A KR 20210067456 A KR20210067456 A KR 20210067456A KR 102495495 B1 KR102495495 B1 KR 102495495B1
- Authority
- KR
- South Korea
- Prior art keywords
- leather
- flame retardant
- painting
- inorganic flame
- weight
- Prior art date
Abstract
본 발명은 난연성이 우수한 피혁의 제조방법에 관한 것이다. 보다 상세하게는 천연가죽의 도장공정에서 베이스 및 미디움 코팅시 무기계 난연제를 도장물질과 함께 도포하고, 탑 코팅시 유기계 난연제를 추가적으로 코팅함으로써 화기(Fire)에 대한 저항성을 향상시켜 난연성이 우수한 피혁의 제조방법에 관한 것이다.
이를 위해 본 발명은 (a) 크러스트 가죽을 사용하여 가죽 표면에 무기계 난연제가 포함된 혼합물을 도장처리하는 베이스 도장공정; (b) (a)공정으로 제조된 가죽에 무기계 난연제가 포함된 혼합물을 도장처리하는 미디움 도장공정; 및 (b) (b)공정으로 제조된 가죽에 유기계 난연제를 포함하는 혼합물을 코팅하여 수분에 대한 저항성을 극대화시킨 탑 도장공정을 포함하는 난연성이 우수한 피혁의 제조방법을 제공한다.The present invention relates to a method for producing leather having excellent flame retardancy. More specifically, in the coating process of natural leather, inorganic flame retardants are applied with coating materials during base and medium coating, and organic flame retardants are additionally coated during top coating to improve resistance to fire, thereby manufacturing leather with excellent flame retardancy. It's about how.
To this end, the present invention provides (a) a base painting process of painting a mixture containing an inorganic flame retardant on the surface of leather using crust leather; (b) a medium painting process of painting a mixture containing an inorganic flame retardant on the leather produced in (a) process; and (b) a top coating process in which the leather prepared in step (b) is coated with a mixture containing an organic flame retardant to maximize resistance to moisture.
Description
본 발명은 난연성이 우수한 피혁의 제조방법에 관한 것이다. 보다 상세하게는 천연가죽의 도장공정에서 베이스 및 미디움 코팅시 무기계 난연제를 도장물질과 함께 도포하고, 탑 코팅시 유기계 난연제를 추가적으로 코팅함으로써 화기(Fire)에 대한 저항성을 향상시켜 난연성이 우수한 피혁의 제조방법에 관한 것이다. The present invention relates to a method for producing leather having excellent flame retardancy. More specifically, in the coating process of natural leather, inorganic flame retardants are applied with coating materials during base and medium coating, and organic flame retardants are additionally coated during top coating to improve resistance to fire, thereby manufacturing leather with excellent flame retardancy. It's about how.
일반적으로, 피혁은 가방, 지갑, 벨트, 의류, 의자, 자동차 시트 등의 용도로 널리 활용되고 있는 소재이다. In general, leather is a material that is widely used for purposes such as bags, wallets, belts, clothes, chairs, and automobile seats.
이러한 피혁은 내열성이 낮고 인화성이 높아 고온에 매우 취약하여 고온에 노출될 경우 가죽 본래의 물성이 훼손되어 피혁제품의 가치와 기능이 상실되게 된다. 또한, 화재발생 시 쉽게 연소되고 연소되는 과정에서 유해한 성분이 배출됨에 따라 인체에 유해하다는 문제점이 있다. Such leather has low heat resistance and high inflammability, so it is very vulnerable to high temperatures, and when exposed to high temperatures, the original physical properties of leather are damaged and the value and function of leather products are lost. In addition, there is a problem that it is harmful to the human body as it is easily burned in the event of a fire and harmful components are discharged during the combustion process.
따라서, 피혁제품의 가치와 기능의 손실을 방지하고, 고온에 노출되더라도 일정 수준의 난연성이 충족될 수 있는 피혁을 개발하는 것이 요구된다. Therefore, it is required to develop leather that can prevent loss of value and function of leather products and can satisfy a certain level of flame retardancy even when exposed to high temperatures.
선행기술문헌 : KR 등록특허공보 제10-1518699호(2015.5.8.공고) Prior art literature: KR Patent Registration No. 10-1518699 (Announced on May 8, 2015)
본 발명은 상기와 같은 문제점을 해결하기 위해 안출된 것으로, 화기에 대한 저항성을 향상시켜 난연성이 우수한 피혁을 제조하는 방법을 제공하는 데 그 목적이 있다.The present invention has been made to solve the above problems, and an object of the present invention is to provide a method for manufacturing leather with excellent flame retardancy by improving resistance to fire.
상기 목적을 달성하기 위해 안출된 본 발명에 따른 난연성이 우수한 피혁의 제조방법은 (a) 크러스트 가죽을 사용하여 가죽 표면에 무기계 난연제가 포함된 혼합물을 도장처리하는 베이스 도장공정; (b) (a)공정으로 제조된 가죽에 무기계 난연제가 포함된 혼합물을 도장처리하는 미디움 도장공정; 및 (c) (b)공정으로 제조된 가죽에 유기계 난연제를 포함하는 혼합물을 코팅하여 수분에 대한 저항성을 극대화시킨 탑 도장공정을 포함할 수 있다. A method for manufacturing leather with excellent flame retardancy according to the present invention, which was devised to achieve the above object, includes: (a) a base painting process of painting a mixture containing an inorganic flame retardant on the surface of leather using crust leather; (b) a medium painting process of painting a mixture containing an inorganic flame retardant on the leather produced in (a) process; and (c) a top painting step in which the leather prepared in step (b) is coated with a mixture containing an organic flame retardant to maximize moisture resistance.
또한, (a)공정에서 무기계 난연제가 포함된 혼합물 중 무기계 난연제는 전체 혼합물의 1~30 중량%를 사용하며, (a)공정은 1~5회 반복 수행되는 것을 특징으로 할 수 있다. In addition, in step (a), the inorganic flame retardant in the mixture containing the inorganic flame retardant is used in an amount of 1 to 30% by weight of the total mixture, and step (a) may be repeated 1 to 5 times.
또한, (b)공정은 무기계 난연제를 전체 혼합물의 1~50 중량%를 사용하며, (b)공정은 1~5회 반복 수행되는 것을 특징으로 할 수 있다. In addition, in step (b), 1 to 50% by weight of the inorganic flame retardant is used, and step (b) may be repeated 1 to 5 times.
또한, (c)공정은 유기계 난연제를 전체 혼합물의 1~30 중량%를 사용하며, (c)공정은 1~5회 반복 수행되는 것을 특징으로 할 수 있다. In addition, step (c) may be characterized in that the organic flame retardant is used in an amount of 1 to 30% by weight of the total mixture, and step (c) is repeated 1 to 5 times.
또한, 무기계 난연제는 평균입도가 1 ~ 40 마이크로 미터(㎛)이며 수산화 알루미늄(Aluminum hydroxide), 수산화 마그네슘(Magnesium hydroxide) 및 삼산화안티몬(Antimony trioxide)을 포함하는 군 중 선택된 1종 또는 그 이상을 사용하는 것을 특징으로 할 수 있다. In addition, the inorganic flame retardant has an average particle size of 1 to 40 micrometers (㎛) and uses one or more selected from the group consisting of aluminum hydroxide, magnesium hydroxide and antimony trioxide. It can be characterized by doing.
또한, 유기계 난연제는 아데노신 삼인산(ATP), 사이티딘 삼인산(CTP), 티미딘 삼인산(TTP), 구아노신 삼인산(GTP), 트리에틸 포스페이트(Triethyl phosphate) 및 암모늄 폴리포스페이트(Ammonium polyphosphate)를 포함하는 군에서 선택된 1종 또는 그 이상을 사용하는 것을 특징으로 할 수 있다. In addition, organic flame retardants include adenosine triphosphate (ATP), cytidine triphosphate (CTP), thymidine triphosphate (TTP), guanosine triphosphate (GTP), triethyl phosphate and ammonium polyphosphate. It may be characterized by using one or more selected from the group.
본 발명에 의하면 천연가죽의 도장공정에서 베이스 및 미디움 코팅시 무기계 난연제를 도장물질과 함께 도포하고, 탑 코팅시 유기계 난연제를 추가적으로 코팅함으로써 화기에 대한 저항성을 향상시켜 난연성이 우수한 피혁을 제공하는 데 그 효과가 있다.According to the present invention, in the coating process of natural leather, an inorganic flame retardant is applied with a coating material during base and medium coating, and an organic flame retardant is additionally coated during top coating to improve resistance to fire and to provide leather with excellent flame retardancy. It works.
도 1은 본 발명의 바람직한 실시예에 따른 난연성이 우수한 피혁의 제조방법의 공정흐름도이다. 1 is a process flow chart of a method for producing leather having excellent flame retardancy according to a preferred embodiment of the present invention.
이하, 본 발명의 바람직한 실시예를 첨부된 도면들을 참조하여 상세히 설명한다. 우선 각 도면의 구성 요소들에 참조 부호를 부가함에 있어서, 동일한 구성 요소들에 대해서는 비록 다른 도면상에 표시되더라도 가능한 한 동일한 부호를 가지도록 하고 있음에 유의해야 한다. 또한, 본 발명을 설명함에 있어, 관련된 공지 구성 또는 기능에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명은 생략한다. 또한, 이하에서 본 발명의 바람직한 실시예를 설명할 것이나, 본 발명의 기술적 사상은 이에 한정하거나 제한되지 않고 당업자에 의해 변형되어 다양하게 실시될 수 있음은 물론이다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. First, in adding reference numerals to components of each drawing, it should be noted that the same components have the same numerals as much as possible even if they are displayed on different drawings. In addition, in describing the present invention, if it is determined that a detailed description of a related known configuration or function may obscure the gist of the present invention, the detailed description will be omitted. In addition, although preferred embodiments of the present invention will be described below, the technical idea of the present invention is not limited or limited thereto and can be modified and implemented in various ways by those skilled in the art.
도 1은 본 발명의 바람직한 실시예에 따른 난연성이 우수한 피혁의 제조방법의 공정흐름도이다. 1 is a process flow chart of a method for producing leather having excellent flame retardancy according to a preferred embodiment of the present invention.
도 1을 참조하면, 본 발명의 바람직한 실시예에 따른 난연성이 우수한 피혁의 제조방법은 베이스 도장공정(S100), 미디움 도장공정(S200), 탑 도장공정(S300)을 포함하여 이루어진다. Referring to FIG. 1, the method for manufacturing leather having excellent flame retardancy according to a preferred embodiment of the present invention includes a base painting process (S100), a medium painting process (S200), and a top painting process (S300).
본 발명에서 베이스 도장공정(S100), 미디움 도장공정(S200), 탑 도장공정(S300)은 제혁공정 후 건조과정을 거친 크러스트 가죽(Crust leather)에 난연성을 부여하기 위한 처리를 수행하는 공정이다. In the present invention, the base painting process (S100), medium painting process (S200), and top painting process (S300) are processes for imparting flame retardancy to crust leather that has been dried after the tanning process.
베이스 도장공정(S100)은 크러스트 가죽을 사용하여 가죽 표면에 무기계 난연제가 포함된 혼합물을 도장처리하는 과정이다. The base painting process (S100) is a process of painting a mixture containing an inorganic flame retardant on the surface of leather using crust leather.
구체적으로, 베이스 도장공정(S100)은 크롬 탄닝된 우피 크러스트 가죽(Crust leather)에 물, 우레탄바인더(Urethane binder), 아크릴바인더(Acrylic binder), 왁스(Wax), 무기계 난연제, 실란 커플링제(silane coupling agent) 및 레벨러(Leveller)를 포함하는 도장처리약품을 교반기를 사용하여 혼합하여 가죽에 도포한 후 100℃에서 10분 건조하는 과정이다. Specifically, in the base painting process (S100), water, urethane binder, acrylic binder, wax, inorganic flame retardant, silane coupling agent are applied to chrome tanned cow crust leather Coupling agent and leveler are mixed using a stirrer, applied to the leather, and then dried at 100 ° C for 10 minutes.
베이스 도장공정(S100)에서 무기계 난연제가 포함된 혼합물 중 무기계 난연제는 전체 혼합물의 1~30 중량%를 사용하며, 베이스 도장공정(S100)은 1~5회 반복 수행될 수 있다.In the base painting process (S100), the inorganic flame retardant in the mixture containing the inorganic flame retardant is used in an amount of 1 to 30% by weight of the total mixture, and the base painting process (S100) may be repeated 1 to 5 times.
베이스 도장공정(S100)에서 실란 커플링제는 전체 혼합물의 0.1~10 중량%를 사용하며 도장처리약품과의 혼합시에 교반기를 사용하여 100~300rpm의 속도로 혼합한다. In the base painting process (S100), the silane coupling agent is used in an amount of 0.1 to 10% by weight of the total mixture, and is mixed at a speed of 100 to 300 rpm using an agitator when mixing with the painting treatment chemical.
실란 커플링제는 무기계 난연제와 바인더와의 결합력을 향상시키는 효과를 가지며, 0.1 중량% 미만에서는 효과가 없으며, 10 중량% 초과 시에는 더 이상의 증진 효과가 없다. The silane coupling agent has an effect of improving the bonding strength between the inorganic flame retardant and the binder, and has no effect when less than 0.1% by weight, and no further enhancing effect when greater than 10% by weight.
실란 커플링제는 Vinyltriethoxysilane, 3-Glycidoxypropyl triethoxysilane, 3-Glycidoxypropyl trimethoxysilane, 3-Glycidoxypropyl methyldimethoxysilane 및 2-(3,4 epoxycyclohexyl) ethyltrimethoxysilane을 포함하는 군에서 선택된 1종 또는 그 이상을 사용할 수 있다.As the silane coupling agent, one or more selected from the group consisting of Vinyltriethoxysilane, 3-Glycidoxypropyl triethoxysilane, 3-Glycidoxypropyl trimethoxysilane, 3-Glycidoxypropyl methyldimethoxysilane and 2-(3,4 epoxycyclohexyl) ethyltrimethoxysilane may be used.
비중이 높은 무기계 난연제는 도장처리약품과의 혼합 시 자연 침강의 문제가 발생될 수 있어 비교적 빠른 혼합 속도로 교반해주어야 하며, 100 rpm 미만에서는 충분한 혼합이 되지 않으며 300 rpm 초과시에는 거품이 발생될 우려가 있으므로, 100~300rpm의 교반속도로 혼합하도록 한다. Inorganic flame retardants with high specific gravity may cause natural sedimentation when mixed with paint treatment chemicals, so they must be stirred at a relatively fast mixing speed. Therefore, mix at a stirring speed of 100 to 300 rpm.
베이스 도장공정(S100)에서 미디움 도장공정(S200)과 달리 무기계 난연제의 함량이 1~30 중량% 범위를 유지해야하는 이유는 30 중량% 초과 적용시 가죽과의 접착력이 약화되어 접착 강도가 떨어지는 문제가 발생하며, 1 중량% 미만인 경우에는 난연효과를 부여하기 어렵기 때문이다. Unlike the medium painting process (S200) in the base painting process (S100), the reason why the content of the inorganic flame retardant should be maintained in the range of 1 to 30% by weight is that when applied in excess of 30% by weight, the adhesive strength with leather is weakened and the adhesive strength is lowered. This is because it is difficult to impart a flame retardant effect when it is less than 1% by weight.
또한, 상기 무기계 난연제는 도장층의 두께를 감안하여 평균입도 1 ~ 40 마이크로 미터(㎛)의 것을 사용한다.In addition, the inorganic flame retardant is used with an average particle size of 1 to 40 micrometers (㎛) in consideration of the thickness of the coating layer.
일례로, 상기 무기계 난연제는 수산화 알루미늄(Aluminum hydroxide), 수산화 마그네슘(Magnesium hydroxide) 및 삼산화안티몬(Antimony trioxide)을 포함하는 군에서 선택된 1종 또는 그 이상을 사용할 수 있다. 이러한 무기계 난연제는 화기로부터 불꽃의 확산 및 연기 발생을 지연시키는 역할을 한다.For example, the inorganic flame retardant may use one or more selected from the group consisting of aluminum hydroxide, magnesium hydroxide, and antimony trioxide. These inorganic flame retardants serve to delay the spread of flame and the generation of smoke from firearms.
미디움 도장공정(S200)은 베이스 도장공정(S100)으로 제조된 가죽에 무기계 난연제가 포함된 혼합물을 도장처리하는 과정이다.The medium painting process (S200) is a process of painting a mixture containing an inorganic flame retardant on the leather manufactured in the base painting process (S100).
구체적으로, 미디움 도장공정(S200)은 물, 우레탄바인더(Urethane binder), 아크릴바인더(Acrylic binder), 왁스(Wax), 무기계 난연제, 실란 커플링제(silane coupling agent) 및 레벨러(Leveller)를 포함하는 도장처리약품을 교반기를 사용하여 혼합하여 도포한 후 100℃에서 10분간 건조하는 과정이다. Specifically, the medium painting process (S200) includes water, a urethane binder, an acrylic binder, a wax, an inorganic flame retardant, a silane coupling agent, and a leveler. It is a process of mixing and applying paint treatment chemicals using an agitator and then drying them at 100℃ for 10 minutes.
미디움 도장공정(S200)은 무기계 난연제를 전체 혼합물의 1~50 중량%를 사용하며, 미디움 도장공정(S200)은 1~5회 반복 수행될 수 있다. In the medium painting process (S200), 1 to 50% by weight of the inorganic flame retardant is used, and the medium painting process (S200) may be repeated 1 to 5 times.
무기계 난연제를 전체 혼합물의 50 중량% 초과 적용시에는 표면의 접착력 약화 및 필름의 물성이 약화되는 문제가 있으며, 1 중량 미만의 함량에서는 난연효과를 부여하기 어려운 문제가 있다. When the inorganic flame retardant is applied in excess of 50% by weight of the total mixture, there is a problem of weakening the adhesion of the surface and the physical properties of the film, and it is difficult to impart a flame retardant effect at an amount of less than 1 weight.
또한, 상기 무기계 난연제는 도장층의 두께를 감안하여 1 ~ 40 마이크로 미터(㎛)의 평균 입도를 가지는 수산화 알루미늄(Aluminum hydroxide), 수산화 마그네슘(Magnesium hydroxide) 및 삼산화안티몬(Antimony trioxide)을 포함하는 군에서 선택된 1종 또는 그 이상을 사용할 수 있다. In addition, the inorganic flame retardant is a group containing aluminum hydroxide, magnesium hydroxide and antimony trioxide having an average particle size of 1 to 40 micrometers (㎛) in consideration of the thickness of the coating layer. One or more selected from may be used.
미디움 도장공정(S200)에서 실란 커플링제는 전체 혼합물의 0.1~10 중량%를 사용하며 도장처리약품과의 혼합시에 교반기를 사용하여 100 ~ 300rpm의 속도로 혼합한다. In the medium painting process (S200), the silane coupling agent is used in an amount of 0.1 to 10% by weight of the total mixture, and is mixed at a speed of 100 to 300 rpm using an agitator when mixing with the painting treatment chemical.
미디움 도장공정(S200)에서 투입되는 실란 커플링제는 무기계 난연제와 바인더와의 결합력을 향상시키는 효과를 가지며, 0.1 중량% 미만에서는 효과가 없으며, 10 중량% 초과 시에는 더 이상의 증진 효과가 없다. The silane coupling agent introduced in the medium coating process (S200) has an effect of improving the bonding strength between the inorganic flame retardant and the binder, has no effect when less than 0.1% by weight, and no further enhancing effect when greater than 10% by weight.
비중이 높은 무기계 난연제는 도장처리약품과의 혼합 시 자연 침강의 문제가 발생될 수 있어 비교적 빠른 혼합 속도로 교반해주어야 하며, 100 rpm 미만에서는 충분한 혼합이 되지 않으며 300 rpm 초과시에는 거품이 발생될 우려가 있으므로, 100~300rpm의 교반속도로 혼합하도록 한다. Inorganic flame retardants with high specific gravity may cause natural sedimentation when mixed with paint treatment chemicals, so they must be stirred at a relatively fast mixing speed. Therefore, mix at a stirring speed of 100 to 300 rpm.
탑 도장공정(S300)은 미디움 도장공정(S200)으로 제조된 가죽에 유기계 난연제를 포함하는 도장처리약품을 코팅하여 화기에 대한 저항성을 극대화시킨 과정이다. The top painting process (S300) is a process of maximizing resistance to fire by coating the leather manufactured in the medium painting process (S200) with a painting treatment agent containing an organic flame retardant.
구체적으로, 탑 도장공정(S300)은 물, PU계 락카(Lacquor), 및 유기계 난연제를 포함하는 도장처리약품을 혼합하여 미디움 도장공정(S200)으로 제조된 가죽에 도포한 후 100℃에서 10분 건조하는 과정이다. Specifically, in the top painting process (S300), a paint treatment agent containing water, PU-based lacquer, and an organic flame retardant is mixed and applied to the leather manufactured by the medium painting process (S200), followed by 10 minutes at 100 ° C. It is a drying process.
또한, 탑 도장공정(S300)은 유기계 난연제를 전체 혼합물의 1~30 중량%를 사용하며, 탑 도장공정(S300)은 1~5회 반복 수행될 수 있다.In addition, in the top painting process (S300), 1 to 30% by weight of the organic flame retardant is used, and the top painting process (S300) may be repeated 1 to 5 times.
유기계 난연제의 함량이 30 중량% 초과 적용시, 표면의 접착력 약화 및 필름의 물성이 약화되는 문제가 있으며, 1 중량% 미만의 함량에서는 난연효과를 부여하기 어려운 문제점이 있다.When the content of the organic flame retardant is applied in excess of 30% by weight, there is a problem in that the adhesion of the surface and the physical properties of the film are weakened, and it is difficult to impart a flame retardant effect at an amount of less than 1% by weight.
또한, 유기계 난연제는 아데노신 삼인산(ATP), 사이티딘 삼인산(CTP), 티미딘 삼인산(TTP), 구아노신 삼인산(GTP), 트리에틸 포스페이트(Triethyl phosphate) 및 암모늄 폴리포스페이트(Ammonium polyphosphate)를 포함하는 군에서 1종 또는 그 이상을 선택 혼합하여 탑 코팅 공정에 적용할 수 있다.In addition, organic flame retardants include adenosine triphosphate (ATP), cytidine triphosphate (CTP), thymidine triphosphate (TTP), guanosine triphosphate (GTP), triethyl phosphate and ammonium polyphosphate. One or more of them may be selectively mixed and applied to the top coating process.
또한, 앞선 베이스 도장공정(S100) 및 미디움 도장공정(S200)과 달리, 탑 도장공정(S300)에서 유기계 난연제를 사용하는 이유는 무기계 난연제의 경우 파우더 상으로 특유의 색상과 입자의 표면 노출로 인해 가장 밖에 적용되는 탑 도장공정(S300)에는 적용하기 어려우나 유기계 난연제의 경우 액상으로, 색상의 변화가 적으며, 표면 상태에 영향이 없는 장점을 가지고 있기 때문이다. In addition, unlike the previous base painting process (S100) and medium painting process (S200), the reason why organic flame retardants are used in the top painting process (S300) is that inorganic flame retardants are in powder form due to the unique color and surface exposure of particles. This is because it is difficult to apply to the top coating process (S300), which is most applied outside, but in the case of organic flame retardants, they are liquid, have little color change, and have the advantage of not affecting the surface state.
이하에서는, 본 발명의 바람직한 실시예를 상세히 설명하겠는 바, 본 발명의 실시예에 한정되는 것은 아니며, 피혁 제품의 전반적인 공정에 적용 가능함을 밝혀둔다. Hereinafter, a preferred embodiment of the present invention will be described in detail, but it is not limited to the embodiment of the present invention, and it is revealed that it is applicable to the overall process of leather products.
1. 난연성이 우수한 피혁의 제조1. Manufacture of leather with excellent flame retardancy
[실시예1][Example 1]
크롬 탄닝된 우피 크러스트 가죽(Crust leather)에 베이스 도장공정(Base coating)에서 물 50g, 우레탄바인더(Urethane binder) 200g, 아크릴바인더(Acrylic binder) 550g, 왁스(Wax) 50g, 무기계 난연제 100g, 실란 커플링제 10g 및 레벨러(Leveller) 50g을 교반기를 사용하여 교반속도 200 rpm으로 혼합하여 롤코팅(Roll coating) 방법을 통해 도포한 후 100도씨에서 10분 건조하는 공정을 2회 반복 진행하고, 미디움 도장공정(Medium coating)에서 물 50g, 우레탄바인더(Urethane binder) 550g, 아크릴바인더(Acrylic binder) 200g, 왁스(Wax) 50g, 무기계 난연제 100g, 실란 커플링제 10g 및 레벨러(Leveller) 50g을 교반기를 사용하여 교반속도 200 rpm으로 혼합하여 롤코팅(Roll coating) 방법을 통해 도포한 후 100도씨에서 10분간 건조하는 공정을 3회 반복 진행하며, 탑 도장공정(Top coating)에서 물 400g, PU계 락카(Lacquor) 500g 및 유기계 난연제 100g을 혼합하여 도포한 후 100도씨에서 10분 건조하는 공정을 진행하여 난연성이 우수한 천연피혁을 제조하였다. 50g of water, 200g of Urethane binder, 550g of Acrylic binder, 50g of Wax, 100g of inorganic flame retardant, silane couple 10 g of ringing agent and 50 g of leveler are mixed at a stirring speed of 200 rpm using a stirrer, applied through a roll coating method, and then the process of drying at 100 ° C for 10 minutes is repeated twice, and the medium painting process In (Medium coating), 50g of water, 550g of Urethane binder, 200g of Acrylic binder, 50g of Wax, 100g of inorganic flame retardant, 10g of silane coupling agent and 50g of Leveler are stirred using an agitator After mixing at a speed of 200 rpm and applying through the roll coating method, the process of drying at 100 ° C for 10 minutes is repeated three times, and in the top coating process, 400 g of water and PU-based lacquer After mixing and applying 500 g and 100 g of an organic flame retardant, a process of drying at 100 ° C for 10 minutes was performed to prepare natural leather with excellent flame retardancy.
[실시예2][Example 2]
크롬 탄닝된 우피 크러스트 가죽(Crust leather)에 베이스 도장공정(Base coating)에서 물 150g, 우레탄바인더(Urethane binder) 200g, 아크릴바인더(Acrylic binder) 550g, 왁스(Wax) 50g 및 레벨러(Leveller) 50g을 혼합하여 롤코팅(Roll coating) 방법을 통해 도포한 후 100도씨에서 10분 건조하는 공정을 2회 반복 진행하고, 미디움 도장공정(Medium coating)에서 물 150g, 우레탄바인더(Urethane binder) 550g, 아크릴바인더(Acrylic binder) 200g, 왁스(Wax) 50g 및 레벨러(Leveller) 50g을 혼합하여 롤코팅(Roll coating) 방법을 통해 도포한 후 100도씨에서 10분간 건조하는 공정을 3회 반복 진행하며, 탑 도장공정(Top coating)에서 물 400g, PU계 락카(Lacquor) 500g 및 유기계 난연제 100g을 혼합하여 도포한 후 100도씨에서 10분 건조하는 공정을 진행하여 난연성이 우수한 천연피혁을 제조하였다. 150g of water, 200g of Urethane binder, 550g of Acrylic binder, 50g of Wax and 50g of Leveler were applied to chrome tanned cowhide crust leather in the base coating process. After mixing and applying through the roll coating method, the process of drying at 100 ° C for 10 minutes is repeated twice, and in the medium coating process, 150 g of water, 550 g of urethane binder, and acrylic binder (Acrylic binder) 200g, wax (Wax) 50g, and leveler (Leveler) 50g are mixed and applied through the roll coating method, and then the process of drying at 100 degrees Celsius for 10 minutes is repeated three times, and the top painting process In (Top coating), 400 g of water, 500 g of PU-based lacquer, and 100 g of organic flame retardant were mixed and applied, followed by drying at 100 ° C for 10 minutes to prepare natural leather with excellent flame retardancy.
[비교예1][Comparative Example 1]
상기 실시예 1과 동일한 방법에 의해 천연가죽을 제조하되, 베이스 도장(Base coating) 및 미디움 도장(Medium coating) 공정에서 무기계 난연제를 제외하고 도장공정을 진행하였으며, 탑 도장(Top coating)공정에서 유기계 난연제를 제외한 도장공정에 의해 제조한 천연가죽을 대조구인 비교예 1로 사용하였다.Natural leather was manufactured by the same method as in Example 1, but the coating process was performed except for the inorganic flame retardant in the base coating and medium coating processes, and the organic-based coating process was performed in the top coating process. Natural leather prepared by the painting process excluding the flame retardant was used as a control, Comparative Example 1.
2. 고내구성 보온성 피혁의 물성평가2. Evaluation of physical properties of high-durability and heat-retaining leather
실시예 1, 2 및 비교예 1의 고내구성 보온성 피혁을 사용하여 보온성, 내마모성, 발수도 등의 물성을 측정한 결과를 아래 표 1에 나타내었다.Table 1 below shows the results of measuring physical properties such as heat retention, abrasion resistance, and water repellency using the highly durable heat-retaining leathers of Examples 1 and 2 and Comparative Example 1.
표 1에서 보는 바와 같이, 실시예 1과 2에 의해 제조된 난연성 피혁은 비교예 1에 비해 모두 난연성이 우수한 것으로 나타났다.As shown in Table 1, the flame retardant leathers prepared in Examples 1 and 2 were all excellent in flame retardancy compared to Comparative Example 1.
또한, 실시예 1의 베이스 및 미디움 도장공정에서 무기계 난연제를 사용한 경우 실시예 2보다 우수한 난연성을 나타내었다.In addition, when an inorganic flame retardant was used in the base and medium coating process of Example 1, flame retardancy was superior to that of Example 2.
이와 같이 본 발명은 안전화, 소방화 등의 특수 목적용 가죽 제품 소재에 적합하도록 난연성을 가짐으로써 다양한 용도로의 활용이 기대된다.As such, the present invention is expected to be used for various purposes by having flame retardancy to be suitable for special purpose leather products such as safety shoes and fire boots.
이상의 설명은 본 발명의 기술 사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위 내에서 다양한 수정, 변경 및 치환이 가능할 것이다. 따라서, 본 발명에 개시된 실시예 및 첨부된 도면들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예 및 첨부된 도면에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.The above description is merely an example of the technical idea of the present invention, and those skilled in the art can make various modifications, changes, and substitutions without departing from the essential characteristics of the present invention. will be. Therefore, the embodiments disclosed in the present invention and the accompanying drawings are not intended to limit the technical idea of the present invention, but to explain, and the scope of the technical idea of the present invention is not limited by these embodiments and the accompanying drawings. . The protection scope of the present invention should be construed according to the claims below, and all technical ideas within the equivalent range should be construed as being included in the scope of the present invention.
S100 : 베이스 도장
S200 : 미디움 도장
S300 : 탑 도장S100: Base painting
S200 : Medium painting
S300: Top painting
Claims (6)
(b) (a)공정으로 제조된 가죽에 무기계 난연제가 포함된 혼합물을 도장처리하는 미디움 도장공정; 및
(c) (b)공정으로 제조된 가죽에 유기계 난연제를 포함하는 혼합물을 코팅하여 수분에 대한 저항성을 극대화시킨 탑 도장공정
을 포함하고,
(a)공정에서 무기계 난연제가 포함된 혼합물 중 무기계 난연제는 전체 혼합물의 1~30 중량%를 사용하며, (a)공정은 1~5회 반복 수행되고,
(b)공정은 무기계 난연제를 전체 혼합물의 1~50 중량%를 사용하며, (b)공정은 1~5회 반복 수행되며,
(c)공정은 유기계 난연제를 전체 혼합물의 1~30 중량%를 사용하며, (c)공정은 1~5회 반복 수행되고,
무기계 난연제는 평균입도가 1 ~ 40 마이크로 미터(㎛)이며 수산화 알루미늄(Aluminum hydroxide), 수산화 마그네슘(Magnesium hydroxide) 및 삼산화안티몬(Antimony trioxide)을 포함하는 군 중 선택된 1종 또는 그 이상을 사용하고,
유기계 난연제는 아데노신 삼인산(ATP), 사이티딘 삼인산(CTP), 티미딘 삼인산(TTP), 구아노신 삼인산(GTP), 트리에틸 포스페이트(Triethyl phosphate) 및 암모늄 폴리포스페이트(Ammonium polyphosphate)를 포함하는 군에서 선택된 1종 또는그 이상을 사용하는 것
을 특징으로 하고,
(a) 베이스도장공정 및 (b) 미디움도장공정에서는 실란커플링제를 전체 혼합물의 0.1~10 중량%를 사용하고
실란커플링제는
Vinyltriethoxysilane, 3-Glycidoxypropyl riethoxysilane, 3-Glycidoxypropyl trimethoxysilane, 3-Glycidoxypropyl methyldimethoxysilane 및 2-(3,4 epoxycyclohexyl) ethyltrimethoxysilane을 포함하는 군에서 선택된 1종 또는 그 이상을 사용하는 것
을 특징으로 하는 난연성이 우수한 피혁의 제조방법.
(a) a base painting process of painting a mixture containing an inorganic flame retardant on the surface of leather using crust leather;
(b) a medium painting process of painting a mixture containing an inorganic flame retardant on the leather produced in (a) process; and
(c) Top painting process in which the leather manufactured in (b) process is coated with a mixture containing an organic flame retardant to maximize resistance to moisture
including,
In the process (a), the inorganic flame retardant in the mixture containing the inorganic flame retardant is used in an amount of 1 to 30% by weight of the total mixture, and the process (a) is repeated 1 to 5 times,
Step (b) uses 1 to 50% by weight of the total mixture of inorganic flame retardants, and step (b) is repeated 1 to 5 times,
(c) process uses 1 to 30% by weight of the total mixture of organic flame retardants, (c) process is repeated 1 to 5 times,
The inorganic flame retardant has an average particle size of 1 to 40 micrometers (㎛) and uses one or more selected from the group consisting of aluminum hydroxide, magnesium hydroxide and antimony trioxide,
Organic flame retardants are in the group containing adenosine triphosphate (ATP), cytidine triphosphate (CTP), thymidine triphosphate (TTP), guanosine triphosphate (GTP), triethyl phosphate and ammonium polyphosphate. Use of one or more selected species
characterized by,
In the (a) base painting process and (b) medium painting process, 0.1 to 10% by weight of the silane coupling agent is used and
Silane coupling agent
Using one or more selected from the group consisting of Vinyltriethoxysilane, 3-Glycidoxypropyl riethoxysilane, 3-Glycidoxypropyl trimethoxysilane, 3-Glycidoxypropyl methyldimethoxysilane and 2-(3,4 epoxycyclohexyl) ethyltrimethoxysilane
Method for producing leather with excellent flame retardancy, characterized by