KR102492401B1 - Synthetic resin woven fabric with excellent breathability and durability - Google Patents
Synthetic resin woven fabric with excellent breathability and durability Download PDFInfo
- Publication number
- KR102492401B1 KR102492401B1 KR1020200131702A KR20200131702A KR102492401B1 KR 102492401 B1 KR102492401 B1 KR 102492401B1 KR 1020200131702 A KR1020200131702 A KR 1020200131702A KR 20200131702 A KR20200131702 A KR 20200131702A KR 102492401 B1 KR102492401 B1 KR 102492401B1
- Authority
- KR
- South Korea
- Prior art keywords
- synthetic resin
- parts
- weight
- polypropylene
- durability
- Prior art date
Abstract
본 발명은 통기성과 내구성이 우수한 합성수지 직물지에 관한 것으로, 합성수지사를 위사 및 경사로 사용하여 합성수지 직물지로 재직하되 좌, 우로 일정한 간격을 가진 선택부분을 통과하는 통과위사와 통과경사를 모아주는 것에 의해 공간부가 형성되는 구조를 가지며, 상기 선택부분의 면적이 상기 직물지 전체 면적의 60 내지 90%를 차지하도록 형성된다.
상기와 같이 통기성을 갖는 공간부가 형성되는 선택부분의 면적이 직물지 전체 면적의 60 내지 90%를 차지하게 되면, 기계적 물성이나 내구성은 유지되면서도 우수한 통기성을 나타내는 합성수지 직물지가 제공된다.The present invention relates to synthetic resin fabric with excellent air permeability and durability, and uses synthetic resin yarn as weft and warp yarn to serve as synthetic resin fabric, but by collecting the passing weft and passing warp yarns passing through selected parts with regular intervals on the left and right, It has a structure in which parts are formed, and the area of the selected part is formed to occupy 60 to 90% of the total area of the woven paper.
As described above, when the area of the selected portion in which the air permeable space is formed occupies 60 to 90% of the total area of the fabric paper, the synthetic resin fabric paper exhibiting excellent air permeability while maintaining mechanical properties and durability is provided.
Description
본 발명은 통기성과 내구성이 우수한 합성수지 직물지에 관한 것으로, 더욱 상세하게는 통기성을 갖는 공간부가 형성되는 선택부분의 면적이 직물지 전체 면적의 60 내지 90%를 차지하여 기계적 물성이나 내구성은 유지되면서도 우수한 통기성을 나타내는 합성수지 직물지에 관한 것이다.The present invention relates to synthetic resin woven fabric with excellent air permeability and durability, and more particularly, the area of a selected portion where a space having air permeability is formed occupies 60 to 90% of the total area of woven fabric, thereby maintaining excellent air permeability while maintaining mechanical properties and durability. It relates to synthetic resin woven paper.
일반적으로 합성수지사로 재직되는 합성수지 직물은 위사와 경사를 순차적으로 교대 직조한 것으로서 방석이나 자동차용 시트 커버로 흔히 사용되고 있으며, 최근에는 건설현장의 안전시설물 등에 적용되고 있다.In general, synthetic resin fabrics, which are used as synthetic resin yarns, are woven alternately between weft and warp yarns, and are commonly used as cushions or seat covers for automobiles, and are recently applied to safety facilities at construction sites.
종래에 합성수지 직물은 상기한 바와 같이 위사와 경사를 서로 직교하는 상태로 촘촘히 직조하기 때문에 통풍이 원할하게 이루어지지 않는 단점이 있었으며, 특히 건설현장에서는 시야가 확보되어야하는데, 종래에 합성수지 직물은 상기의 조건을 만족시키지 못하는 문제점이 있었다.Conventionally, synthetic resin fabrics have the disadvantage of not being well ventilated because they are densely woven with weft and warp yarns orthogonal to each other as described above, and visibility must be secured, especially at construction sites. There was a problem that the condition could not be satisfied.
상기의 문제점을 해소하기 위해 위사와 경사가 일정한 간격을 유지하도록 직조하여 원활한 통기성과 시야확보의 성능을 부여하는 방법이 이용되고 있으나, 이러한 방법은 위사와 경사가 고정되지 않아 위사와 경사간의 간격으로 인해 위사나 경사가 어느 한쪽으로 쏠리는 현상이 쉽게 발생하여 직물지가 갖는 고유의 외관이 유지되지 못하고 내구성이 저하되는 문제점이 있었다.In order to solve the above problems, a method of weaving so that the weft and warp yarns are kept at regular intervals to provide smooth air permeability and visibility is used, but this method is not fixed, so the weft yarn and warp yarn Due to this, there is a problem in that the weft or warp tends to one side easily, so that the unique appearance of the woven paper cannot be maintained and durability is lowered.
또한, 건설현장의 안전시설물 등에 적용되는 종래에 합성수지 직물지는 빗물이나 자외선 등에 의해 쉽게 열화가 진행될 뿐만 아니라, 외력에 의해 발생하는 스크래치 등으로 인해 직물지의 외관이 쉽게 훼손될 뿐만 아니라, 물성의 저하가 발생하는 문제점이 있었다.In addition, conventional synthetic resin fabrics applied to safety facilities at construction sites are not only easily deteriorated by rainwater or ultraviolet rays, but also easily damaged by scratches caused by external forces, as well as deterioration of physical properties. There were problems that arose.
본 발명의 목적은 통기성을 갖는 공간부가 형성되는 선택부분의 면적이 직물지 전체 면적의 60 내지 90%를 차지하여 기계적 물성이나 내구성은 유지되면서도 우수한 통기성을 나타내는 합성수지 직물지를 제공하는 것이다.An object of the present invention is to provide synthetic resin fabric paper showing excellent air permeability while maintaining mechanical properties and durability by occupying 60 to 90% of the total area of the fabric paper in which the area of the selected portion in which the air permeable space portion is formed occupies 60 to 90% of the total area of the fabric paper.
본 발명의 목적은 합성수지사를 위사 및 경사로 사용하여 합성수지 직물지로 재직하되 좌, 우로 일정한 간격을 가진 선택부분을 통과하는 통과위사와 통과경사를 모아주는 것에 의해 공간부가 형성되는 구조를 가지며, 상기 선택부분의 면적이 상기 직물지 전체 면적의 60 내지 90%를 차지하도록 형성되는 것을 특징으로 하는 통기성과 내구성이 우수한 합성수지 직물지를 제공함에 의해 달성된다.An object of the present invention is to use synthetic resin yarns as wefts and warp yarns to serve as synthetic resin fabric paper, but have a structure in which a space portion is formed by collecting passing weft yarns and passing warp yarns passing through selected portions having a constant interval on the left and right, and the selection It is achieved by providing synthetic resin fabric paper having excellent breathability and durability, characterized in that the area of the portion is formed to occupy 60 to 90% of the total area of the fabric paper.
본 발명의 바람직한 특징에 따르면, 상기 합성수지사는 폴리에스터, 폴리에틸렌, 폴리프로필렌 및 폴리아미드로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것으로 한다.According to a preferred feature of the present invention, the synthetic resin yarn is made of at least one selected from the group consisting of polyester, polyethylene, polypropylene and polyamide.
본 발명의 더 바람직한 특징에 따르면, 상기 합성수지사의 표면에는 폴리프로필렌 변성 컴파운드 조성물이 코팅되며, 상기 폴리프로필렌 변성 컴파운드 조성물은 폴리프로필렌 100 중량부, 폴리프로필렌계 변성엘라스토머 20 내지 150 중량부, 폴리스티렌계 변성엘라스토머 0.1 내지 50 중량부, 무기필러 0.1 내지 30 중량부, 산화방지제 0.1 내지 10 중량부, UV 흡수제 0.1 내지 20 중량부 및 가공활제 0.1 내지 30 중량부로 이루어지는 것으로 한다.According to a more preferred feature of the present invention, the surface of the synthetic resin yarn is coated with a polypropylene-modified compound composition, the polypropylene-modified compound composition is 100 parts by weight of polypropylene, 20 to 150 parts by weight of polypropylene-modified elastomer, polystyrene-modified 0.1 to 50 parts by weight of elastomer, 0.1 to 30 parts by weight of inorganic filler, 0.1 to 10 parts by weight of antioxidant, 0.1 to 20 parts by weight of UV absorber, and 0.1 to 30 parts by weight of processing lubricant.
본 발명의 더욱 바람직한 특징에 따르면, 상기 폴리프로필렌계 변성엘라스토머는 폴리프로필렌에틸렌 공중합 플라스토머(m-PEPP), 폴리프로필렌옥텐 공중합 플라스토머(m-POPP), 폴리프로필렌헥센 공중합 플라스토머(m-PHPP), 폴리프로필렌부텐 공중합 플라스토머(m-PBPP) 및 폴리올레핀블록코폴리머로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것으로 한다.According to a more preferred feature of the present invention, the polypropylene-modified elastomer is polypropylene ethylene copolymerization plastomer (m-PEPP), polypropylene octene copolymerization plastomer (m-POPP), polypropylene hexene copolymerization plastomer ( m-PHPP), polypropylene butene copolymerization plastomers (m-PBPP), and polyolefin block copolymers.
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 폴리스티렌계 변성엘라스토머는 폴리스티렌부타디엔공중합체(SBS), 폴리스티렌이소프렌공중합체(SIS), 폴리스티렌에틸렌부타디엔블록공중합체(SEBS), 폴리스티렌에틸렌프로필렌블록공중합체(SEPS) 및 수소부가폴리스티렌에틸렌부타디엔엘라스토머(HSEBS)로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것으로 한다.According to a more preferred feature of the present invention, the polystyrene-based modified elastomer is polystyrene butadiene copolymer (SBS), polystyrene isoprene copolymer (SIS), polystyrene ethylene butadiene block copolymer (SEBS), polystyrene ethylene propylene block copolymer (SEPS) ) and at least one selected from the group consisting of hydrogenated polystyrene ethylene butadiene elastomer (HSEBS).
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 합성수지사의 표면에는 폴리프로필렌 변성 컴파운드 조성물이 코팅된 후에 하드코팅제가 더 코팅되며, 상기 하드코팅제는 자외선 경화형 바인더 100 중량부, 광개시제 0.1 내지 10 중량부, 대전방지제 0.1 내지 10 중량부, 용매 100 내지 300 중량부 및 아크릴계 불소 화합물 0.1 내지 50 중량부로 이루어지는 것으로 한다.According to a more preferred feature of the present invention, a hard coating agent is further coated on the surface of the synthetic resin yarn after the polypropylene-modified compound composition is coated, and the hard coating agent comprises 100 parts by weight of an ultraviolet curable binder, 0.1 to 10 parts by weight of a photoinitiator, and electrification. 0.1 to 10 parts by weight of an inhibitor, 100 to 300 parts by weight of a solvent, and 0.1 to 50 parts by weight of an acrylic fluorine compound.
본 발명에 따른 통기성과 내구성이 우수한 합성수지 직물지는 통기성을 갖는 공간부가 형성되는 선택부분의 면적이 직물지 전체 면적의 60 내지 90%를 차지하여 기계적 물성이나 내구성은 유지되면서도 우수한 통기성을 나타내는 합성수지 직물지를 제공하는 탁월한 효과를 나타낸다.The synthetic resin fabric fabric with excellent air permeability and durability according to the present invention occupies 60 to 90% of the total area of the fabric paper, so that the area of the selected part in which the air permeable space is formed occupies 60 to 90% of the total area of the fabric paper, providing a synthetic resin fabric paper showing excellent air permeability while maintaining mechanical properties and durability. shows an excellent effect.
도 1은 본 발명에 따른 통기성과 내구성이 우수한 합성수지 직물지를 나타낸 모식적 평면도이다.
도 2는 본 발명의 일 실시예를 통해 제조된 통기성과 내구성이 우수한 합성수지 직물지를 촬영하여 나타낸 사진이다.
도 3은 본 발명의 다른 실시예를 통해 제조된 통기성과 내구성이 우수한 합성수지 직물지를 촬영하여 나타낸 사진이다.1 is a schematic plan view showing a synthetic resin fabric having excellent air permeability and durability according to the present invention.
2 is a photograph showing a synthetic resin fabric fabric with excellent air permeability and durability manufactured through an embodiment of the present invention.
Figure 3 is a photograph showing a synthetic resin fabric with excellent air permeability and durability manufactured through another embodiment of the present invention.
이하에는, 본 발명의 바람직한 실시예와 각 성분의 물성을 상세하게 설명하되, 이는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 발명을 용이하게 실시할 수 있을 정도로 상세하게 설명하기 위한 것이지, 이로 인해 본 발명의 기술적인 사상 및 범주가 한정되는 것을 의미하지는 않는다.Hereinafter, a preferred embodiment of the present invention and the physical properties of each component will be described in detail, but this is to be explained in detail so that a person having ordinary knowledge in the art to which the present invention belongs can easily practice the invention, This is not meant to limit the technical spirit and scope of the present invention.
본 발명에 따른 통기성과 내구성이 우수한 합성수지 직물지(2)는 합성수지사(1)를 위사 및 경사로 사용하여 합성수지 직물지(2)로 재직하되 좌, 우로 일정한 간격을 가진 선택부분(6)을 통과하는 통과위사(4)와 통과경사(5)를 모아주는 것에 의해 공간부(3)가 형성되는 구조를 갖는다.The synthetic resin fabric paper (2) having excellent breathability and durability according to the present invention serves as the synthetic resin fabric paper (2) by using the synthetic resin yarn (1) as the weft and the warp yarn, but passes through the selected portion (6) having regular intervals on the left and right. It has a structure in which the
이때, 상기 공간부(3)의 크기는 선택부분(6)을 지나는 통과위사(4)와 통과경사(5)가 합성수지사(1) 몇가닥을 모아서 형성되는 가에 따라 결정되는데, 더욱 상세하게는 상기의 선택부분(6)을 통과하는 통과위사(4)와 통과경사(5)가 각각 30가닥이라고 가정했을 때, 통과위사(4)와 통과경사(5)를 각각 10가닥씩을 모아주게 되면 아래 도 1과 같이 16개의 공간부(3)가 형성되는데, 상기 공간부(3)를 좁게 형성하고자 하는 경우에는 선택부분(6)을 통과하는 통과위사(4)와 통과경사(5)의 모음수를 줄여 공간부(3)의 갯수를 늘이는 대신 공간부(3)의 개별적인 넓이는 좁게 형성할 수 있다.At this time, the size of the
또한, 본 발명은 상기 선택부분(6)의 면적이 상기 직물지(2) 전체 면적의 60 내지 90%를 차지하도록 형성되는 것이 바람직한데, 선택부분(6)의 면적에 형성되는 공간부(3)의 넓이에 관계없이 선택부분(6) 자체의 면적이 직물지(2) 전체 면적의 60 내지 90%를 차지하게 되면 기계적 물성이나 내구성은 유지되면서도 우수한 통기성을 나타내는 합성수지 직물지(2)가 제공된다.In addition, in the present invention, it is preferable that the area of the
상기 선택부분(6)의 면적이 직물지(2) 전체 면적의 60% 미만인 경우에는 통기성의 향상효과가 미미하며, 상기 선택부분(6)의 면적이 직물지(2) 전체 면적의 90%를 초과하게 되면 통기성은 향상되지만 직물지(2)의 기계적 물성이나 내구성이 현저하게 저하될 수 있기 때문에 바람직하지 못하다.When the area of the optional portion (6) is less than 60% of the total area of the fabric paper (2), the effect of improving air permeability is insignificant, and the area of the optional portion (6) exceeds 90% of the total area of the fabric paper (2) If the air permeability is improved, but it is not preferable because the mechanical properties and durability of the fabric paper 2 may be significantly deteriorated.
상기 합성수지사(1)는 폴리에스터, 폴리에틸렌, 폴리프로필렌 및 폴리아미드로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것이 바람직하며, 상기에 나열된 합성수지사(1)의 표면에 폴리프로필렌 변성 컴파운드 조성물이 코팅되어 이루어지는 것이 더욱 바람직하다.The synthetic resin yarn (1) is preferably made of at least one selected from the group consisting of polyester, polyethylene, polypropylene and polyamide, and the surface of the synthetic resin yarn (1) listed above is coated with a modified polypropylene compound composition. it is more preferable
상기와 같이 폴리프로필렌 변성 컴파운드 조성물이 코팅된 합성수지사(1)는 가공성, 내구성 및 내후성과 같은 물성이 향상된다.As described above, the synthetic resin yarn 1 coated with the polypropylene-modified compound composition has improved properties such as processability, durability, and weather resistance.
이때, 상기 폴리프로필렌 변성 컴파운드 조성물은 폴리프로필렌 100 중량부, 폴리프로필렌계 변성엘라스토머 20 내지 150 중량부, 폴리스티렌계 변성엘라스토머 0.1 내지 50 중량부, 무기필러 0.1 내지 30 중량부, 산화방지제 0.1 내지 10 중량부, UV 흡수제 0.1 내지 20 중량부 및 가공활제 0.1 내지 30 중량부로 이루어진다.In this case, the polypropylene-modified compound composition includes 100 parts by weight of polypropylene, 20 to 150 parts by weight of polypropylene-modified elastomer, 0.1 to 50 parts by weight of polystyrene-modified elastomer, 0.1 to 30 parts by weight of inorganic filler, and 0.1 to 10 parts by weight of antioxidant. Part, composed of 0.1 to 20 parts by weight of UV absorber and 0.1 to 30 parts by weight of processing lubricant.
상기 폴리프로필렌은 일반호모폴리프로필렌, 하이크리스탈폴리프로필렌 공중합체, 하이크리스탈블록폴리프로필렌 공중합체, 랜덤코폴리프로필렌 및 부틸터셔리폴리프로필렌 삼중합체로 이루어진 그룹에서 선택된 하나 이상으로 이루어질 수 있으며, 용융지수(Melt Index; MI)(230℃/2.16Kg, ASTM D1238)가 1.0 g/10min 내지 5.0 g/10min인 수지 또는 MI(230℃/2.16Kg, ASTM D1238)가 7g/10min 내지 30g/10min인 수지를 사용하여 압출 T-Dies 공법으로 제조될 수 있다.The polypropylene may be made of one or more selected from the group consisting of general homopolypropylene, high-crystal polypropylene copolymer, high-crystal block polypropylene copolymer, random co-polypropylene, and butyl tertiary polypropylene terpolymer, and the melt index (Melt Index; MI) (230°C/2.16Kg, ASTM D1238) of 1.0 g/10min to 5.0 g/10min or MI (230°C/2.16Kg, ASTM D1238) of 7g/10min to 30g/10min It can be manufactured by the extrusion T-Dies method using.
또한, 상기 폴리프로필렌 수지는 굴곡탄성율(ASTM D790, kg/㎠)은 6,500 내지 11,000 kg/㎠이며, 용융점(ASTM D3418, ℃)은 130 내지 150 이고, 연화점(ASTM D1525, ℃)은 110 내지 140 이며, 신장율(ASTM D638, %)은 500% 이하인 것을 사용하는 것이 바람직하다.In addition, the polypropylene resin has a flexural modulus (ASTM D790, kg/cm2) of 6,500 to 11,000 kg/cm2, a melting point (ASTM D3418, °C) of 130 to 150, and a softening point (ASTM D1525, °C) of 110 to 140 And, the elongation rate (ASTM D638, %) is preferably 500% or less.
상기 폴리프로필렌계 변성 엘라스토머 수지는 메탈로젠 촉매법으로 제조한 폴리프로필렌에틸렌 공중합 플라스토머, 폴리프로필렌옥텐 공중합 플라스토머, 폴리프로필렌헥센 공중합 플라스토머, 폴리프로필렌부텐 공중합 플라스토머 및 폴리올레핀블록코폴리머로 이루어진 군에서 선택된 하나 이상을 포함하여 이루어지는데, 이러한 폴리프로필렌계 변성 엘라스토머는 본 발명에 따른 통기성과 내구성이 우수한 합성수지 직물지(2)를 구성하는 합성수지사(1)에 탄성과 내한성을 향상시켜주는 역할을 한다.The polypropylene-modified elastomer resins are polypropylene ethylene copolymerization plastomers, polypropylene octene copolymerization plastomers, polypropylene hexene copolymerization plastomers, polypropylene butene copolymerization plastomers and polyolefin block co-plastomers prepared by the metallogen catalyst method. It includes at least one selected from the group consisting of polymers, and the polypropylene-modified elastomer improves elasticity and cold resistance of the synthetic resin yarn 1 constituting the synthetic resin fabric fabric 2 having excellent air permeability and durability according to the present invention. play a role in giving
상기 폴리스티렌계 변성엘라스토머는 폴리스티렌부타디엔공중합체(SBS), 폴리스티렌이소프렌공중합체(SIS), 폴리스티렌에틸렌부타디엔블록공중합체(SEBS), 폴리스티렌에틸렌프로필렌블록공중합체(SEPS) 및 수소부가폴리스티렌에틸렌부타디엔엘라스토머(HSEBS)로 이루어진 그룹에서 선택된 하나 이상을 포함하여 이루어지는것이 바람직한데, 상기 본 발명에 따른 통기성과 내구성이 우수한 합성수지 직물지(2)를 구성하는 합성수지사(1)에 인장성, 인열성, 유연성 및 굴곡강도를 향상시켜 주는 역할을 한다.The polystyrene-modified elastomers include polystyrene butadiene copolymer (SBS), polystyrene isoprene copolymer (SIS), polystyrene ethylene butadiene block copolymer (SEBS), polystyrene ethylene propylene block copolymer (SEPS) and hydrogenated polystyrene ethylene butadiene elastomer (HSEBS). ) It is preferable to include at least one selected from the group consisting of, the tensile strength, tear resistance, flexibility and flexural strength of the synthetic resin yarn (1) constituting the synthetic resin fabric paper (2) having excellent air permeability and durability according to the present invention. plays a role in enhancing
상기 무기필러는 탄산칼슘, 탈크, 클레이, 마그네사이트, 수산화알루미늄 및 수산화마그네슘으로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것이 바람직한데, 상기 무기필러의 함량이 30 중량부를 초과하게 되면 쵸크마크가 발생할 확률이 높아지고 비중이 높아져 본 발명에 따른 통기성과 내구성이 우수한 합성수지 직물지(2)의 중량을 지나치게 증가시킬 수 있다.The inorganic filler is preferably composed of at least one selected from the group consisting of calcium carbonate, talc, clay, magnesite, aluminum hydroxide and magnesium hydroxide. When the content of the inorganic filler exceeds 30 parts by weight, the probability of occurrence of chalk marks increases. As the specific gravity increases, the weight of the synthetic resin fabric paper 2 having excellent breathability and durability according to the present invention may be excessively increased.
상기 산화방지제는 1,1,1-트리스(2-메틸-4-히드록시-5-터셔리-부틸페닐)부탄, 1,3,5-트리메틸-2,4,6-트리스(3,5-디-터셔리-부틸-4-히드록시벤질)벤젠, 테트라키스-[메틸렌-3-(3'5'-디-터셔리-부틸-4-히드록시페닐)프로피네이트], 비스[3,3'-비스-(4'-하이드록시-3'-터셔리-부틸페닐)부틸릭엑시드]글리콜에스테르, 1,3,5-트리스(3',5'-디-터셔리-부틸-4'히드록시벤질)-SEC-트리아진-2,4,6-트리온, 3,5-디-터셔리-부틸-4-히드록시히드로시나메이트 옥타데실, 트리스(2,4-디-터셔리-부틸페닐)포스페이트, 시클로 네오펜탄테트라일 비스(2,4-디-터셔리-부틸페닐)포스페이트 및 1,2-비스(3,5-디-터셔리-부틸-4-히드록시히드로시나모일)히드라진으로 이루어진 그룹에서 선택된 하나 이상을 포함하여 이루어지는 것이 바람직한데, 본 발명에 따른 통기성과 내구성이 우수한 합성수지 직물지(2)를 구성하는 합성수지사(1)의 노화를 방지하는 역할을 한다.The antioxidant is 1,1,1-tris (2-methyl-4-hydroxy-5-tertiary-butylphenyl) butane, 1,3,5-trimethyl-2,4,6-tris (3,5 -di-tert-butyl-4-hydroxybenzyl)benzene, tetrakis-[methylene-3-(3'5'-di-tert-butyl-4-hydroxyphenyl)propinate], bis[3 ,3'-bis-(4'-hydroxy-3'-tert-butylphenyl)butylic acid]glycol ester, 1,3,5-tris(3',5'-di-tert-butyl- 4'hydroxybenzyl)-SEC-triazine-2,4,6-trione, 3,5-di-tert-butyl-4-hydroxyhydrocinnamate octadecyl, tris(2,4-di- tert-butylphenyl)phosphate, cyclo neopentanetetrayl bis(2,4-di-tert-butylphenyl)phosphate and 1,2-bis(3,5-di-tert-butyl-4-hydroxy It is preferable to include at least one selected from the group consisting of hydrocinamoyl) hydrazine, which serves to prevent aging of the synthetic resin yarn 1 constituting the synthetic resin fabric fabric 2 having excellent air permeability and durability according to the present invention. .
상기 UV 흡수제는 벤조페논계, 페닐실리케이트, 비스(2,2,6,6-테트라메틸-4-피페리디닐)세바케이트, 2-(3'-5'-디-터셔리-부틸-2'-히드록시페닐)-5-클로로벤조트리아졸, 2-(3,5-디-터셔리-페닐-2-히드록시페닐)벤조트리아졸, 2-(2'-히드록시-5-메틸페닐)벤조트리아졸, 2-(3'-터셔리-부틸-2'-히드록시-5'-메틸페닐)-5-클로로벤조트리아졸 및 힌다드아민계로 이루어진 그룹에서 선택된 하나 이상을 포함하여 이루어지는 것이 바람직한데, 자외선으로 인해 본 발명에 따른 통기성과 내구성이 우수한 합성수지 직물지(2)가 변색 및 노화되는 것을 억제하는 역할을 한다.The UV absorber is benzophenone, phenyl silicate, bis (2,2,6,6-tetramethyl-4-piperidinyl) sebacate, 2- (3'-5'-di-tert-butyl-2 '-hydroxyphenyl) -5-chlorobenzotriazole, 2- (3,5-di-tert-phenyl-2-hydroxyphenyl) benzotriazole, 2- (2'-hydroxy-5-methylphenyl ) benzotriazole, 2-(3'-tertiary-butyl-2'-hydroxy-5'-methylphenyl)-5-chlorobenzotriazole, and hindadamine-based containing at least one selected from the group consisting of Preferably, it serves to suppress discoloration and aging of the synthetic resin fabric paper 2 having excellent air permeability and durability according to the present invention due to ultraviolet rays.
상기 가공활제는 스테아르산아연, 올레아미드, 에루카아미드, 스테아르아미드, 베헨아미드, 지방산아민 및 불소수지로 이루어진 군에서 선택된 하나 이상을 포함하여 이루어지는데, 상기의 성분으로 이루어지는 가공활제는 압출기 실린더 및 스크류와 폴리프로필렌 변성 컴파운드 조성물 간의 마찰계수를 낮춰주기 때문에 압출공정을 등을 통해 합성수지사(1)의 표면에 폴리프로필렌 변성 컴파운드 조성물을 코팅하는 공정의 효율성을 향상시킬 수 있다.The processing lubricant comprises at least one selected from the group consisting of zinc stearate, oleamide, erucamide, stearamide, behenamide, fatty acid amine, and fluororesin. Since the friction coefficient between the screw and the polypropylene-modified compound composition is lowered, the efficiency of the process of coating the polypropylene-modified compound composition on the surface of the synthetic resin yarn 1 through an extrusion process can be improved.
이때, 상기 가공활제의 함량이 3.0 중량부를 초과하게 되면 폴리프로필렌 변성 컴파운드 조성물의 접착력이 감소하여 본 발명에 따른 합성수지 직물지(2)에 견고하게 코팅될 수 없게 된다.At this time, when the content of the processing lubricant exceeds 3.0 parts by weight, the adhesive strength of the polypropylene-modified compound composition decreases, so that it cannot be firmly coated on the synthetic resin fabric paper 2 according to the present invention.
또한, 상기의 성분으로 이루어지는 폴리프로필렌 변성 컴파운드 조성물이 코팅된 합성수지사(1)의 표면에는 하드코팅제가 더 코팅될 수도 있는데, 하드코팅제가 코팅되면 내오염성이 향상될 뿐만 아니라, 대전방지로 인해 먼지 등이 달라붙는 것이 억제되고, 외력에 의한 스크래치 등의 발생이 억제되어 내구성이 향상된 합성수지 직물지(2)를 제공할 수 있다.In addition, a hard coating agent may be further coated on the surface of the synthetic resin yarn 1 coated with the polypropylene-modified compound composition composed of the above components. When the hard coating agent is coated, stain resistance is improved and dust is prevented due to antistatic. It is possible to provide a synthetic resin fabric paper 2 with improved durability by suppressing sticking of the back and suppressing occurrence of scratches due to external force.
상기 하드코팅제는 자외선 경화형 바인더 100 중량부, 광개시제 0.1 내지 10 중량부, 대전방지제 0.1 내지 10 중량부, 용매 100 내지 300 중량부 및 아크릴계 불소 화합물 0.1 내지 50 중량부로 이루어지는 것이 바람직하다.The hard coating agent preferably consists of 100 parts by weight of an ultraviolet curable binder, 0.1 to 10 parts by weight of a photoinitiator, 0.1 to 10 parts by weight of an antistatic agent, 100 to 300 parts by weight of a solvent, and 0.1 to 50 parts by weight of an acrylic fluorine compound.
상기 자외선 경화가 가능한 바인더는 우레탄 아크릴레이트계, 에폭시 아크릴레이트계, 실리콘 아크릴레이트계, 폴리에스터 아크릴레이트계, 멜라민 아크릴레이트계 또는 실리카-아크릴 하이브리드계 등의 올리고머를 사용하거나, 대전방지제나 유기 또는 무기 입자 등의 화합물과의 상용성을 고려하여 1~6개의 관능기를 갖는 모노머를 사용하는 것이 바람직하다. 상기 모노머는 디펜타에리스리톨헥사아크릴레이트, 펜타에리스리톨트리아크릴레이트, 1,6-헥산 디올디아크릴레이트 트리프로필렌글리콜트리아크릴레이트, 트리메티롤프로판트리아크릴레이트, 폴리에틸렌글리콜디아크릴레트, 하이드록시프로필아크릴레이트, 하이드록시에틸아크릴레이트, 라우릴메타아크릴레이트, 하이드록시프로필메타아크릴레이트, 하이드록시에틸메타아크릴레이트, 스티렌 및 N-비닐피롤리돈으로 이루어진 그룹에서 선택된 하나를 사용하는 것이 바람직하다.The UV-curable binder uses oligomers such as urethane acrylate, epoxy acrylate, silicone acrylate, polyester acrylate, melamine acrylate, or silica-acrylic hybrid, or an antistatic agent, organic or It is preferable to use a monomer having 1 to 6 functional groups in consideration of compatibility with compounds such as inorganic particles. The monomers include dipentaerythritol hexaacrylate, pentaerythritol triacrylate, 1,6-hexane diol diacrylate, tripropylene glycol triacrylate, trimethylolpropane triacrylate, polyethylene glycol diacrylate, and hydroxypropyl acryl. It is preferable to use one selected from the group consisting of lactate, hydroxyethyl acrylate, lauryl methacrylate, hydroxypropyl methacrylate, hydroxyethyl methacrylate, styrene and N-vinylpyrrolidone.
상기 광개시제는 자외선의 조사에 의해 하드코팅제가 경화될 수 있도록 하는 역할을 하는데, α-하이드록시사이크로헥실페닐메타논, 1-하이드록시사이클로헥실페닐케톤, 2-하이드록시-2-메틸-1페닐프로판-1-온, 하이드록시메틸아세토페논 및 벤조페논으로 이루어진 그룹에서 선택된 하나 이상을 포함하는 것이 바람직하다.The photoinitiator serves to cure the hard coating agent by irradiation of ultraviolet rays, and α-hydroxycyclohexylphenylmethanone, 1-hydroxycyclohexylphenylketone, 2-hydroxy-2-methyl-1 It is preferable to include at least one selected from the group consisting of phenylpropan-1-one, hydroxymethylacetophenone, and benzophenone.
상기 대전방지제는 나노사이즈 졸 상태의 전도성 고분자 또는 이온성 대전방지제를 사용하여 하드코팅제의 투명성과 영구적인 대전방지효과가 유지될 수 있도록 하는 것이 바람직한데, 졸 상태의 전도성 고분자는 폴리아닐린, 폴리피롤, 폴리티오펜 및 폴리에틸렌디옥시티오펜으로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것이 바람직하며, 상기 이온성 대전방지제는 트리노르말부틸메틸암모늄비스트리플로우르메탄설포닐이미드, 알킬이미다졸리움, 알킬포스포늄, N-알킬피리디늄, N,N'-디알킬이미다졸리움 또는 그 유도체 등으로 이루어진 양이온, 브로마이드 또는 헥사플로로포스페이트 등을 사용하는 것이 바람직하다.The antistatic agent is preferably a nano-sized sol-state conductive polymer or an ionic anti-static agent so that the transparency and permanent antistatic effect of the hard coating can be maintained. The sol-state conductive polymer is polyaniline, polypyrrole, It is preferably composed of at least one selected from the group consisting of thiophene and polyethylenedioxythiophene, and the ionic antistatic agent is trinormalbutylmethylammonium bistrifluoromethanesulfonylimide, alkylimidazolium, alkylphosphonium, It is preferable to use a cation composed of N-alkylpyridinium, N,N'-dialkylimidazolium or a derivative thereof, bromide or hexafluorophosphate or the like.
상기 용매는 상기 바인더 성분의 용해성과, 유기 또는 무기 입자의 분산성을 향상시키는 역할을 하는데, 프로필렌글리콜모노프로필에테르, 프로필렌글리콜모노메틸에테르, 에틸렌글리콜모노에틸에테르, 에틸렌글리콜모노프로필에테르, 에틸렌글리콜모노부틸에테르, 디에틸렌글리콜모노메틸에테르, 디에틸렌글리콜모노에틸에테르, 디에틸렌글리콜모노부틸에테르, 디에틸렌글리콜모노프로필에테르, 디에틸렌글리콜-2-에틸헥실에테르 등의 에테르류, 또는 이소프로필알콜, 에틸알콜, 부틸알콜 등의 알콜류, 메틸에틸케톤, 아세톤 등의 케톤류 또는 톨루엔 자일렌 등의 방향족류 그 외에도 에틸아세테이트, 부틸아세테이트 등의 아세테이트류, N-메틸 피롤리돈 등의 아마이드류 등을 포함하거나 이들의 혼합물을 포함하는 것을 사용하는 것이 바람직하다.The solvent serves to improve the solubility of the binder component and the dispersibility of organic or inorganic particles, propylene glycol monopropyl ether, propylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monopropyl ether, ethylene glycol Ethers such as monobutyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, diethylene glycol monopropyl ether, diethylene glycol-2-ethylhexyl ether, or isopropyl alcohol , alcohols such as ethyl alcohol and butyl alcohol, ketones such as methyl ethyl ketone and acetone, aromatics such as toluene xylene, acetates such as ethyl acetate and butyl acetate, and amides such as N-methylpyrrolidone. It is preferred to use one containing or a mixture thereof.
상기 아크릴계 불소 화합물은 하드코팅제에 방오성 및 내구성을 부여하는 역할을 하는데, 상용화된 것을 사용할 수 있으며, 구체적으로는 다이킨(Daikin)사의 제품명 Optsol DAC 등을 사용할 수 있다.The acrylic fluorine compound plays a role in imparting antifouling properties and durability to the hard coating agent, and a commercially available one may be used. Specifically, Daikin's product name Optsol DAC may be used.
따라서, 본 발명에 따른 통기성과 내구성이 우수한 합성수지 직물지(2)는 통기성을 갖는 공간부(3)가 형성되는 선택부분(6)의 면적이 직물지(2) 전체 면적의 60 내지 90%를 차지하여 기계적 물성이나 내구성은 유지되면서도 우수한 통기성을 나타낸다.Therefore, in the synthetic resin fabric fabric 2 having excellent air permeability and durability according to the present invention, the area of the selected
또한, 본 발명에 따른 통기성과 내구성이 우수한 합성수지 직물지(2)는 상기 합성수지사(1)의 표면에 폴리프로필렌 변성 컴파운드 조성물이 코팅되어 가공성, 내구성 및 내후성과 같은 물성이 우수하다.In addition, the synthetic resin fabric fabric 2 having excellent air permeability and durability according to the present invention is coated with a polypropylene modified compound composition on the surface of the synthetic resin yarn 1, and thus has excellent physical properties such as processability, durability and weather resistance.
또한, 본 발명에 따른 통기성과 내구성이 우수한 합성수지 직물지(2)는 상기 폴리프로필렌 변성 컴파운드 조성물이 코팅된 합성수지사(1)의 표면에 하드코팅제를 더 코팅하여 내오염성이 향상될 뿐만 아니라, 대전방지로 인해 먼지 등이 달라붙는 것이 억제되고, 외력에 의한 스크래치 등의 발생이 억제되어 내구성이 우수하다.In addition, the synthetic resin fabric paper 2 having excellent air permeability and durability according to the present invention is further coated with a hard coating agent on the surface of the synthetic resin yarn 1 coated with the polypropylene-modified compound composition, so that stain resistance is improved and antistatic Due to this, the adhesion of dust and the like is suppressed, and the occurrence of scratches and the like due to external force is suppressed, resulting in excellent durability.
1 ; 합성수지사, 2 ; 직물지
3 ; 공간부, 4 ; 통과위사
5 ; 통과경사, 6 ; 선택부분One ; synthetic resin yarn, 2; textile paper
3 ; space part, 4; passing weft
5 ; through slope, 6 ; selection
Claims (6)
상기 선택부분의 면적이 상기 직물지 전체 면적의 60 내지 90%를 차지하도록 형성되며,
상기 합성수지사의 표면에는 폴리프로필렌 변성 컴파운드 조성물이 코팅된 후에 하드코팅제가 더 코팅되고,
상기 하드코팅제는 자외선 경화형 바인더 100 중량부, 광개시제 0.1 내지 10 중량부, 대전방지제 0.1 내지 10 중량부, 용매 100 내지 300 중량부 및 아크릴계 불소 화합물 0.1 내지 50 중량부로 이루어지는 것을 특징으로 하는 통기성과 내구성이 우수한 합성수지 직물지.
Synthetic resin yarns are used as wefts and warp yarns to serve as synthetic resin fabrics, but have a structure in which a space portion is formed by collecting passing wefts and passing warp yarns passing through selected parts with regular intervals on the left and right,
The area of the selected portion is formed to occupy 60 to 90% of the total area of the woven paper,
After the polypropylene modified compound composition is coated on the surface of the synthetic resin yarn, a hard coating agent is further coated,
The hard coating agent has breathability and durability, characterized in that it consists of 100 parts by weight of an ultraviolet curable binder, 0.1 to 10 parts by weight of a photoinitiator, 0.1 to 10 parts by weight of an antistatic agent, 100 to 300 parts by weight of a solvent, and 0.1 to 50 parts by weight of an acrylic fluorine compound. Excellent synthetic resin woven paper.
상기 합성수지사는 폴리에스터, 폴리에틸렌, 폴리프로필렌 및 폴리아미드로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것을 특징으로 하는 통기성과 내구성이 우수한 합성수지 직물지.
The method of claim 1,
The synthetic resin yarn is made of one or more selected from the group consisting of polyester, polyethylene, polypropylene and polyamide, characterized in that the breathable and durable synthetic resin fabric paper.
상기 폴리프로필렌 변성 컴파운드 조성물은 폴리프로필렌 100 중량부, 폴리프로필렌계 변성엘라스토머 20 내지 150 중량부, 폴리스티렌계 변성엘라스토머 0.1 내지 50 중량부, 무기필러 0.1 내지 30 중량부, 산화방지제 0.1 내지 10 중량부, UV 흡수제 0.1 내지 20 중량부 및 가공활제 0.1 내지 30 중량부로 이루어지는 것을 특징으로 하는 통기성과 내구성이 우수한 합성수지 직물지.
The method of claim 1,
The polypropylene-modified compound composition includes 100 parts by weight of polypropylene, 20 to 150 parts by weight of a polypropylene-modified elastomer, 0.1 to 50 parts by weight of a polystyrene-modified elastomer, 0.1 to 30 parts by weight of an inorganic filler, 0.1 to 10 parts by weight of an antioxidant, A synthetic resin fabric having excellent breathability and durability, characterized in that it consists of 0.1 to 20 parts by weight of a UV absorber and 0.1 to 30 parts by weight of a processing lubricant.
상기 폴리프로필렌계 변성엘라스토머는 폴리프로필렌에틸렌 공중합 플라스토머(m-PEPP), 폴리프로필렌옥텐 공중합 플라스토머(m-POPP), 폴리프로필렌헥센 공중합 플라스토머(m-PHPP), 폴리프로필렌부텐 공중합 플라스토머(m-PBPP) 및 폴리올레핀블록코폴리머로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것을 특징으로 하는 통기성과 내구성이 우수한 합성수지 직물지.
The method of claim 3,
The polypropylene-modified elastomer is polypropylene ethylene copolymerization plastomer (m-PEPP), polypropylene octene copolymerization plastomer (m-POPP), polypropylene hexene copolymerization plastomer (m-PHPP), polypropylene butene copolymerization A synthetic resin fabric with excellent air permeability and durability, characterized in that it consists of at least one selected from the group consisting of plastomer (m-PBPP) and polyolefin block copolymer.
상기 폴리스티렌계 변성엘라스토머는 폴리스티렌부타디엔공중합체(SBS), 폴리스티렌이소프렌공중합체(SIS), 폴리스티렌에틸렌부타디엔블록공중합체(SEBS), 폴리스티렌에틸렌프로필렌블록공중합체(SEPS) 및 수소부가폴리스티렌에틸렌부타디엔엘라스토머(HSEBS)로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것을 특징으로 하는 통기성과 내구성이 우수한 합성수지 직물지.
The method of claim 3,
The polystyrene-modified elastomers include polystyrene butadiene copolymer (SBS), polystyrene isoprene copolymer (SIS), polystyrene ethylene butadiene block copolymer (SEBS), polystyrene ethylene propylene block copolymer (SEPS) and hydrogenated polystyrene ethylene butadiene elastomer (HSEBS). ) Excellent breathability and durability synthetic resin fabric paper, characterized in that consisting of one or more selected from the group consisting of.