KR102491115B1 - Bag filter composition containing aerogel - Google Patents
Bag filter composition containing aerogel Download PDFInfo
- Publication number
- KR102491115B1 KR102491115B1 KR1020210172955A KR20210172955A KR102491115B1 KR 102491115 B1 KR102491115 B1 KR 102491115B1 KR 1020210172955 A KR1020210172955 A KR 1020210172955A KR 20210172955 A KR20210172955 A KR 20210172955A KR 102491115 B1 KR102491115 B1 KR 102491115B1
- Authority
- KR
- South Korea
- Prior art keywords
- bag filter
- airgel
- weight
- filter composition
- polyethylene terephthalate
- Prior art date
Abstract
Description
본 발명은 에어로겔이 함유된 백필터 조성물에 관한 것으로, 더욱 상세하게는 에어로겔이 함유되어 습기에 영향을 받지 않고 마찰대전방지 성능이 우수하여 정전기로 인한 화재 및 폭발의 위험이 없으며, 우수한 내오염성을 나타내는 에어로겔이 함유된 백필터 조성물에 관한 것이다.The present invention relates to a bag filter composition containing airgel, and more particularly, since airgel is contained, it is not affected by moisture and has excellent anti-friction performance, so there is no risk of fire and explosion due to static electricity, and excellent contamination resistance It relates to a bag filter composition containing the indicated airgel.
일반적으로 산업현장에서 발생되는 오염된 공기나 물을 대기중이나 강에 그대로 배출하면 심각한 환경오염이 유발되므로 모든 업체에서는 오염된 공기나 물을 정화하여 방출하도록 의무화되어 있다.In general, if polluted air or water generated at industrial sites is discharged into the atmosphere or a river as it is, serious environmental pollution is caused, so all companies are obliged to purify and discharge the polluted air or water.
이에 따라, 업체에서는 공기나 물을 정화하는 정화 수단으로 백필터(bag filter)를 설치한다. 이와 같은 백필터는 기본적으로 흡입구와 배출구가 형성된 하우징 내부에 백(bag) 형상으로 이루어진 필터백이 설치된 형태로 이루어져서, 오염된 공기나 물이 상기 흡입구를 통해 하우징 내부로 유입되어 필터백에서 여과처리되며 처리된 공기나 물은 배출구를 통해 하우징 외부로 배출된다.Accordingly, companies install a bag filter as a purification means for purifying air or water. Such a bag filter is basically composed of a bag-shaped filter bag installed inside a housing in which an inlet and an outlet are formed, so that contaminated air or water flows into the housing through the inlet and is filtered in the filter bag. The treated air or water is discharged out of the housing through the outlet.
일반적으로, 백필터는 미세입자를 집진하는 기능을 가지고 있으며 설치비는 저렴한 반면, 합성섬유 재질로 이루어지며 사용가능 온도가 낮고 탈진 기능을 높이기 위한 운전비용이 높아 개선이 요구되고 있다.In general, the bag filter has a function of collecting fine particles and is inexpensive to install, but is made of synthetic fiber, has a low usable temperature, and high operating cost to increase the dedusting function, so improvement is required.
백필터의 제조에 사용되는 합성섬유 대부분은 공기중의 수분 흡수력이 거의 없어 절연저항이 매우 높고 분진의 양전하와 음전하에 의해 발생되는 정전기를 흘려버리지 못하고 축적하는 성질을 가지게 된다. 따라서, 공기 중에 먼지를 흡착하게 되면 흡착면이 오염되고 정전기에 의한 스파크가 발생하여 작업자의 불안감을 증복시키며, 백필터로 처리되는 오염물의 종류에 따라서는 화재나 폭발의 위험성을 내포하는 문제점이 있었다.Most of the synthetic fibers used in the manufacture of bag filters have little moisture absorption in the air, so they have very high insulation resistance and have the property of accumulating static electricity generated by the positive and negative charges of dust. Therefore, when dust is adsorbed in the air, the adsorption surface is contaminated and sparks are generated due to static electricity, which increases worker's anxiety, and poses a risk of fire or explosion depending on the type of contaminant treated by the bag filter. .
상기의 문제점을 해소하기 위해 백필터로 적용되는 합성섬유에 마찰대전방지제를 혼합하는 방법이 이용되고 있으나, 마찰대전방지제를 혼합하는 방법 만으로는 대전방지 효과가 오랜기간 동안 지속되지 못하고, 대전방지제 성분이 용출되면 새로운 오염원으로 작용할 수 있는 문제점이 있었다. In order to solve the above problems, a method of mixing a tribostatic agent with synthetic fibers applied as a bag filter is used, but the antistatic effect cannot last for a long period of time only by mixing the tribostatic agent, and When eluted, there was a problem that could act as a new source of contamination.
본 발명의 목적은 에어로겔이 함유되어 습기에 영향을 받지 않고 마찰대전방지 성능이 우수하여 정전기로 인한 화재 및 폭발의 위험이 없으며, 우수한 내오염성을 나타내는 에어로겔이 함유된 백필터 조성물을 제공하는 것이다.An object of the present invention is to provide a bag filter composition containing airgel, which is not affected by moisture, has excellent anti-friction performance, is free from the risk of fire and explosion due to static electricity, and exhibits excellent contamination resistance.
본 발명의 목적은 폴리에틸렌테레프탈레이트, 에어로겔 및 가공활제로 이루어지는 것을 특징으로 하는 에어로겔이 함유된 백필터 조성물을 제공함에 의해 달성된다.An object of the present invention is achieved by providing an airgel-containing bag filter composition comprising polyethylene terephthalate, airgel, and a processing lubricant.
본 발명의 바람직한 특징에 따르면, 상기 에어로겔이 함유된 백필터 조성물은 폴리에틸렌테레프탈레이트 30 내지 98.9 중량%, 에어로겔 0.1 내지 60 중량% 및 가공활제 1 내지 10 중량%로 이루어지는 것으로 한다.According to a preferred feature of the present invention, the airgel-containing bag filter composition is composed of 30 to 98.9% by weight of polyethylene terephthalate, 0.1 to 60% by weight of airgel, and 1 to 10% by weight of a processing lubricant.
본 발명의 더 바람직한 특징에 따르면, 상기 에어로겔은 기공률이 80 내지 99%이며, 평균입경이 70 내지 80 마이크로미터인 것으로 한다.According to a more preferred feature of the present invention, the airgel has a porosity of 80 to 99% and an average particle diameter of 70 to 80 micrometers.
본 발명의 더욱 바람직한 특징에 따르면, 상기 에어로겔에 형성되는 기공의 직경은 45 내지 55 나노미터이며, 기공부피가 4 내지 6cm3인 것으로 한다.According to a more preferred feature of the present invention, the diameter of the pores formed in the airgel is 45 to 55 nanometers, and the pore volume is 4 to 6 cm 3 .
본 발명에 따른 에어로겔이 함유된 백필터 조성물은 에어로겔이 함유되어 습기에 영향을 받지 않고 마찰대전방지 성능이 우수하여 정전기로 인한 화재 및 폭발의 위험이 없으며, 우수한 내오염성을 나타내는 백필터를 제공하는 탁월한 효과를 나타낸다.The airgel-containing bag filter composition according to the present invention is not affected by moisture because it contains airgel and has excellent anti-friction performance, thereby eliminating the risk of fire and explosion due to static electricity, and providing a bag filter exhibiting excellent contamination resistance shows excellent effect.
도 1은 본 발명의 실시예 1 및 비교예 1을 통해 제조된 백필터 조성물의 방오성을 DYETEC사에 의뢰하여 측정한 실험보고서이다.1 is an experimental report obtained by requesting DYETEC to measure antifouling properties of bag filter compositions prepared in Example 1 and Comparative Example 1 of the present invention.
이하에는, 본 발명의 바람직한 실시예와 각 성분의 물성을 상세하게 설명하되, 이는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 발명을 용이하게 실시할 수 있을 정도로 상세하게 설명하기 위한 것이지, 이로 인해 본 발명의 기술적인 사상 및 범주가 한정되는 것을 의미하지는 않는다.Hereinafter, a preferred embodiment of the present invention and the physical properties of each component will be described in detail, but this is to be explained in detail so that a person having ordinary knowledge in the art to which the present invention belongs can easily practice the invention, This is not meant to limit the technical spirit and scope of the present invention.
본 발명에 따른 에어로겔이 함유된 백필터 조성물은 폴리에틸렌테레프탈레이트, 에어로겔 및 가공활제로 이루어지며, 폴리에틸렌테레프탈레이트 30 내지 98.9 중량%, 에어로겔 0.1 내지 60 중량% 및 가공활제 1 내지 10 중량%로 이루어지는 것이 바람직하다.The airgel-containing bag filter composition according to the present invention is composed of polyethylene terephthalate, airgel, and a processing lubricant, and is composed of 30 to 98.9% by weight of polyethylene terephthalate, 0.1 to 60% by weight of airgel, and 1 to 10% by weight of a processing lubricant. desirable.
상기 폴리에틸렌테레프탈레이트는 30 내지 98.9 중량%가 함유되며, 본 발명에 따른 에어로겔이 함유된 백필터 조성물의 주재료가 되는 성분으로, 내열성과 기계적 물성이 우수한 백필터가 제공될 수 있도록 하는 역할을 한다.The polyethylene terephthalate is contained in an amount of 30 to 98.9% by weight and is a main component of the airgel-containing bag filter composition according to the present invention, and serves to provide a bag filter with excellent heat resistance and mechanical properties.
또한, 상기 폴리에틸렌테레프탈레이트는 고내열성 폴리에틸렌테레프탈레이트로 이루어질 수도 있는데, 고내열성 폴리에틸렌테레프탈레이트는 폴리에틸렌테레프탈레이트에 유기화점토 및 침강성 탄산칼슘을 혼합하여 제조될 수 있으며, 폴리에틸렌테레프탈레이트 100 중량부에 유기화점토 1 내지 10 중량부 및 침강성 탄산칼슘 1 내지 10 중량부를 혼합하여 이루어지는 것이 바람직하다.In addition, the polyethylene terephthalate may be made of highly heat-resistant polyethylene terephthalate. The high heat-resistant polyethylene terephthalate may be prepared by mixing polyethylene terephthalate with organatized clay and precipitated calcium carbonate, and 100 parts by weight of polyethylene terephthalate. It is preferably formed by mixing 1 to 10 parts by weight and 1 to 10 parts by weight of precipitated calcium carbonate.
이때, 상기 유기화점토는 몬모릴로나이트(montmorillonite), 벤토나이트(bentonite), 카올리나이트(kaolinite), 마이카(mica), 헥토라이트(hectorite), 불화헥토라이트, 사포나이트(saponite), 베이델라이트(beidellite), 논트로나이트(nontronite), 스티븐사이트(stevensite), 버미큘라이트(vermiculite), 할로사이트(halloysite), 불콘스코이트, 석코아나이트, 마가다이트, 서펜타인(serpentine), 필로실리케이트(phyllosilicate) 및 파이로필라이트(pyrophyllite)로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것이 바람직하다.At this time, the organic clay is montmorillonite, bentonite, kaolinite, mica, hectorite, fluorinated hectorite, saponite, beidellite, rice nontronite, stevensite, vermiculite, halloysite, vulkonscoite, succoanite, margadite, serpentine, phyllosilicate and pyro It is preferably made of one or more selected from the group consisting of pyrophyllite.
또한, 상기 침강성 탄산칼슘은 유기화 처리된 방해석(calcite), 아라고나이트(aragonite), 베이터라이트(vaterite) 및 백운석(dolomite)으로 이루어진 그룹에서 선택된 하나 이상으로 이루어지며, 상기 유기화 처리는 스테아르산(stearic acid), 알킬실란(alkylsilane) 및 인산(phosphoric acid)으로 이루어진 그룹에서 선택된 하나 이상으로 이루어지는 것이 바람직하다.In addition, the precipitated calcium carbonate is made of at least one selected from the group consisting of calcite, aragonite, vaterite, and dolomite, which are organically treated, and the organically treated is stearic acid (stearic acid). acid), it is preferably composed of at least one selected from the group consisting of alkylsilane and phosphoric acid.
상기와 같은 성분으로 이루어지는 침강성 탄산칼슘은 평균입자 크기가 20 내지 200 나노미터이며, 밀도가 18 내지 22g/cc를 나타낸다.The precipitated calcium carbonate composed of the above components has an average particle size of 20 to 200 nanometers and a density of 18 to 22 g/cc.
상기와 같이 유기화점토 및 침강성 탄산칼슘이 혼합되면 폴리에틸렌테레프탈레이트의 내열성이 월등하게 향상될 뿐만 아니라, 백화현상을 개선하여 백필터 내열성과 상품성을 향상시킬 수 있다.As described above, when the organic clay and the precipitated calcium carbonate are mixed, not only the heat resistance of polyethylene terephthalate is significantly improved, but also the bag filter heat resistance and marketability can be improved by improving the whitening phenomenon.
상기 폴리에틸렌테레프탈레이트의 함량이 30 중량% 미만이면 백필터의 기계적 물성이 저하될 수 있으며, 상기 폴리에틸렌테레프탈레이트의 함량이 98.9 중량%를 초과하게 되면 에어로겔의 함량이 지나치게 줄어들어 백필터의 마찰대전방지 성능이 저하된다.If the content of polyethylene terephthalate is less than 30% by weight, the mechanical properties of the bag filter may be deteriorated, and if the content of polyethylene terephthalate exceeds 98.9% by weight, the content of airgel is excessively reduced, thereby reducing tribostatic performance of the bag filter. this is lowered
상기 에어로겔은 0.1 내지 60 중량%가 함유되며, 본 발명에 따른 백필터 조성물이 습기에 영향을 받지 않도록 하며, 백필터 조성물의 마찰대전방지 성능을 향상시켜 정전기로 인한 화재 및 폭발의 위험이 없으며, 우수한 내오염성을 나타낼 수 있도록 하는 역할을 한다.The airgel contains 0.1 to 60% by weight, prevents the bag filter composition according to the present invention from being affected by moisture, and improves the tribostatic performance of the bag filter composition so that there is no risk of fire and explosion due to static electricity, It plays a role to show excellent stain resistance.
이때, 상기 에어로겔은 이산화규소가 함유되며, 기공률이 80 내지 99%이며, 평균입경이 70 내지 80 마이크로미터이고, 기공의 직경은 45 내지 55 나노미터이며, 기공부피가 4 내지 6cm3이고, 일도는 0.2 내지 0.3g/cm3이고 내부 표면적이 1000m2/g인 것을 사용하는 것이 바람직하다.At this time, the airgel contains silicon dioxide, has a porosity of 80 to 99%, an average particle diameter of 70 to 80 micrometers, a pore diameter of 45 to 55 nanometers, a pore volume of 4 to 6 cm 3 , and one degree is 0.2 to 0.3 g/cm 3 , and it is preferable to use one having an internal surface area of 1000 m 2 /g.
상기 에어로겔의 함량이 0.1 중량% 미만이면 상기의 효과가 미미하며, 상기 에어로겔의 함량이 60 중량%를 초과하게 되면 상기의 효과는 크게 향상되지 않으면서 폴리에틸렌테레프탈레이트의 함량이 지나치게 줄어들어 백필터의 기계적 물성이 저하될 수 있다.If the content of the airgel is less than 0.1% by weight, the above effect is insignificant, and if the content of the airgel exceeds 60% by weight, the above effect is not greatly improved, but the content of polyethylene terephthalate is excessively reduced, resulting in mechanical damage to the bag filter. properties may deteriorate.
상기 가공활제는 1 내지 10 중량%가 함유되며, 상기 폴리에틸렌테레프탈레이트와 상기 에어로겔의 혼합물을 융융방사 등의 과정을 통해 섬유화하는 경우에 성형성을 향상시키는 역할을 한다.The processing lubricant is contained in an amount of 1 to 10% by weight, and serves to improve moldability when the mixture of the polyethylene terephthalate and the airgel is fibrous through a process such as melt spinning.
이때, 상기 가공활제의 성분은 특별히 한정되지 않고, 상기와 같이 폴리에틸렌테레프탈레이트와 에어로겔 혼합물의 가공성을 향상시킬 수 있는 성분이면 특별히 한정되지 않고 어떠한 것이든 사용가능하다.At this time, the component of the processing lubricant is not particularly limited, and as long as it is a component that can improve the processability of the mixture of polyethylene terephthalate and airgel as described above, it is not particularly limited and any component can be used.
상기 가공활제의 함량이 1 중량% 미만이면 상기의 효과가 미미하며, 상기 가공활제의 함량이 10 중량%를 초과하게 되면 상기의 효과는 크게 향상되지 않으면서 상대적으로 상기 폴리에틸렌테레프탈레이트와 상기 에어로겔의 함량이 지나치게 줄어들기 때문에 바람직하지 못하다.If the content of the processing lubricant is less than 1% by weight, the above effect is insignificant, and if the content of the processing lubricant exceeds 10% by weight, the above effect is not greatly improved and relatively the polyethylene terephthalate and the airgel This is undesirable because the content is excessively reduced.
상기의 성분으로 이루어지는 백필터 조성물은 폴리에틸렌테레프탈레이트, 에어로겔 및 가공활제를 혼합하여 혼합물을 제조하고, 제조된 혼합물을 스핀펌프와 압출기를 통과시킨 후에, 방사노즐을 통해 필라멘트로 방사하고, 방사된 필라멘트는 냉각하여 고화한 후에 이젝터(Ejector)를 통하여 방사속도 약 4,500m/min 속도로 연신하여 분리성이 좋은 다공성 특수 컨베이어 벨트상에 일정한 중량으로 적층하여 부직포 형태의 웹으로 형성하고, 컨베이어 벨트 상에 안착된 웹은 1차 칼렌더 롤에 의해 열압착하고, 열접착 온도를 190℃로 설정하여 프리 본딩된 웹을 니들펀칭 하는 과정으로 제조된다.The bag filter composition composed of the above components is prepared by mixing polyethylene terephthalate, airgel and a processing lubricant, and after passing the prepared mixture through a spin pump and an extruder, spinning into filaments through a spinning nozzle, the spun filaments After cooling and solidifying, it is stretched at a spinning speed of about 4,500 m/min through an ejector, laminated with a certain weight on a porous special conveyor belt with good separability, and formed into a non-woven web, and on the conveyor belt The seated web is prepared by thermocompression bonding with a primary calender roll, setting the thermal bonding temperature to 190° C., and needle punching the pre-bonded web.
상기의 과정을 통해 제조된 백필터 조성물은 상단이 개구된 자루형상으로 이루어지며, 하우징 내부에 백필터가 단순하게 삽입될 뿐인 것으로 하우징 내에서의 팩필터가 이격되도록 되어 있다. 이때, 하우징 내에서의 백필터는 개구된 상단 둘레부만 고정링에 일체로 결합되며 이 고정링은 하우징 격판의 설치공 둘레부에 걸려지나 경우에 따라서는 집진기 구조물에 착탈 가능하게 결합될 수 있다.The bag filter composition prepared through the above process is made in the shape of a bag with an open top, and the bag filter is simply inserted into the housing so that the pack filter in the housing is spaced apart. At this time, only the upper circumference of the bag filter in the housing is integrally coupled to the fixing ring, and the fixing ring is caught on the circumference of the installation hole of the housing diaphragm, but can be detachably coupled to the dust collector structure in some cases. .
더욱 상세하게는, 유입구 및 배출구가 하우징의 측방으로 중간부에는 유입구와 배출구를 연통시키며 상기 백필터가 설치되어 형성되는데, 상기의 백피터는 상단이 개구된 자루형상으로 이루어지며, 내부에 단순히 삽입될 뿐이다 이때, 백필터의 개구된 상단 둘레부분만 고정링에 일체로 결합되며 이 고정링은 케이지 격판의 설치공 둘레부에 걸려지나 경우에 따라서는 장착되는 케이지에 착탈가능하게 결합될 수 있다.More specifically, the inlet and outlet are formed by connecting the inlet and outlet to the middle of the housing and the bag filter is installed. The bag filter is formed in the shape of a bag with an open top and is simply inserted into the inside. At this time, only the upper circumference of the open top of the bag filter is integrally coupled to the fixing ring, and the fixing ring is caught on the circumference of the installation hole of the cage diaphragm, but may be detachably coupled to the cage to be mounted in some cases.
이하에서는, 본 발명에 따른 에어로겔이 함유된 백필터 조성물의 제조방법 및 그 제조방법으로 제조된 백필터의 물성을 실시예를 들어 설명하기로 한다.Hereinafter, the manufacturing method of the airgel-containing bag filter composition according to the present invention and the physical properties of the bag filter manufactured by the manufacturing method will be described with examples.
<실시예 1><Example 1>
폴리에틸렌테레프탈레이트 60 중량%, 에어로겔(이산화규소가 함유되며, 내부에 공기가 90% 이상, 기공율 90%, 평균입경이 75㎛, 밀도 0.25g/cm3, 내부 표면적 1000m2/g, 기공직경 50nm 및 기공 부피 5cm3) 35 중량% 및 가공활제(PurgexTM 3057 Plus) 5 중량%를 혼합하여 혼합물을 제조하고, 상기 혼합물을 스핀펌프와 압출기를 통과시킨 후에, 방사노즐을 통해 필라멘트로 방사하고, 방사된 필라멘트는 냉각하여 고화한 후에 이젝터(Ejector)를 통하여 방사속도 약 4,500m/min 속도로 연신하여 분리성이 좋은 다공성 특수 컨베이어 벨트상에 일정한 중량으로 적층하여 부직포 형태의 웹으로 형성하고, 컨베이어 벨트 상에 안착된 웹은 1차 칼렌더 롤에 의해 열압착하고, 열접착 온도를 190℃로 설정하여 프리 본딩된 웹을 니들펀칭 하는 과정을 통해 에어로겔이 함유된 백필터 조성물을 제조하였다.Polyethylene terephthalate 60% by weight, airgel (contains silicon dioxide, air inside is 90% or more, porosity 90%, average particle diameter 75㎛, density 0.25g/cm 3 , internal surface area 1000m 2 /g, pore diameter 50nm And pore volume 5cm 3 ) 35% by weight and processing lubricant (PurgexTM 3057 Plus) 5% by weight to prepare a mixture, and after passing the mixture through a spin pump and an extruder, spinning into a filament through a spinning nozzle, spinning After cooling and solidifying, the filament is stretched at a spinning speed of about 4,500 m/min through an ejector, laminated with a certain weight on a special porous conveyor belt with good separability, and formed into a non-woven web, and the conveyor belt A bag filter composition containing airgel was prepared through the process of thermocompressing the web seated on the bed with a primary calender roll, setting the thermosealing temperature to 190° C., and needle punching the pre-bonded web.
<비교예 1><Comparative Example 1>
폴리에틸렌테레프탈레이트를 스핀펌프와 압출기를 통과시킨 후에, 방사노즐을 통해 필라멘트로 방사하고, 방사된 필라멘트는 냉각하여 고화한 후에 이젝터(Ejector)를 통하여 방사속도 약 4,500m/min 속도로 연신하여 분리성이 좋은 다공성 특수 컨베이어 벨트상에 일정한 중량으로 적층하여 부직포 형태의 웹으로 형성하고, 컨베이어 벨트 상에 안착된 웹은 1차 칼렌더 롤에 의해 열압착하고, 열접착 온도를 190℃로 설정하여 프리 본딩된 웹을 니들펀칭 하는 과정을 통해 백필터 조성물을 제조하였다.After passing polyethylene terephthalate through a spin pump and an extruder, it is spun into filaments through a spinning nozzle, and the spun filaments are cooled and solidified and then stretched through an ejector at a spinning speed of about 4,500 m/min to achieve separability. It is laminated with a certain weight on this good porous special conveyor belt to form a web in the form of a non-woven fabric, and the web seated on the conveyor belt is thermally compressed by a primary calender roll, and pre-bonded by setting the thermal bonding temperature to 190 ° C. A bag filter composition was prepared through a process of needle punching the web.
상기 실시예 1 및 비교예 1을 통해 제조된 백필터 조성물의 마찰대전방지 성능을 측정하여 아래 표 1에 나타내었다.The tribostatic performance of the bag filter composition prepared in Example 1 and Comparative Example 1 was measured and shown in Table 1 below.
{단, 마찰대전방지 성능은 EMK-5000(Electrostatic Measuring Kit)와 ETD-8000(Electrostaic Test Device)를 이용하여 제조된 백필터 조성물의 전정기 전압(V)을 측정하는 방법을 이용하였으며, 각각 8회 측정 후, 평균값으로 나타내었다.}{However, for tribostatic performance, a method of measuring the electrostatic voltage (V) of the bag filter composition prepared using EMK-5000 (Electrostatic Measuring Kit) and ETD-8000 (Electrostatic Test Device) was used, each 8 times After measurement, it was expressed as an average value.}
<표 1><Table 1>
상기 표 1에 나타낸 것처럼, 본 발명의 실시예 1을 통해 제조된 에어로겔이 함유된 백필터 조성물을 비교예 1을 통해 제조된 백필터 조성물에 비해 정전기의 전압이 현저히 낮은 것을 알 수 있다.As shown in Table 1, it can be seen that the bag filter composition containing airgel prepared in Example 1 of the present invention has significantly lower static voltage than the bag filter composition prepared in Comparative Example 1.
또한, 상기 실시예 1 및 비교예 1을 통해 제조된 백필터 조성물의 방오성을 DYETEC에 의뢰하여 측정한 실험보고서를 아래 도 1에 나타내었다.In addition, an experimental report obtained by requesting DYETEC to measure the antifouling properties of the bag filter compositions prepared in Example 1 and Comparative Example 1 is shown in FIG. 1 below.
{단, #1:실시예 1, #2:비교예 1이다.}{However, #1: Example 1, #2: Comparative Example 1.}
아래 도 1에 나타낸 것처럼, 본 발명의 실시예 1을 통해 제조된 백필터 조성물은 방오성이 월등하게 개선되는 것을 알 수 있다.As shown in FIG. 1 below, it can be seen that the antifouling property of the bag filter composition prepared in Example 1 of the present invention is significantly improved.
따라서, 본 발명에 따른 에어로겔이 함유된 백필터 조성물은 에어로겔이 함유되어 습기에 영향을 받지 않고 마찰대전방지 성능이 우수하여 정전기로 인한 화재 및 폭발의 위험이 없으며, 우수한 내오염성을 나타낸다.Therefore, the airgel-containing bag filter composition according to the present invention contains airgel, is not affected by moisture, has excellent tribostatic performance, has no risk of fire and explosion due to static electricity, and exhibits excellent contamination resistance.
Claims (4)
상기 고내열성 폴리에틸렌테레프탈레이트는 폴리에틸렌테레프탈레이트 100 중량부에 유기화점토 1 내지 10 중량부 및 침강성 탄산칼슘 1 내지 10 중량부를 혼합하여 이루어지는 것을 특징으로 하는 에어로겔이 함유된 백필터 조성물.
30 to 98.9% by weight of high heat-resistant polyethylene terephthalate, 0.1 to 60% by weight of airgel, and 1 to 10% by weight of a processing lubricant,
The high heat-resistant polyethylene terephthalate is a bag filter composition containing airgel, characterized in that made by mixing 1 to 10 parts by weight of organic clay and 1 to 10 parts by weight of precipitated calcium carbonate in 100 parts by weight of polyethylene terephthalate.
상기 에어로겔은 기공률이 80 내지 99%이며, 평균입경이 70 내지 80 마이크로미터인 것을 특징으로 하는 에어로겔이 함유된 백필터 조성물.
The method of claim 1,
The airgel has a porosity of 80 to 99% and an average particle diameter of 70 to 80 micrometers.
상기 에어로겔에 형성되는 기공의 직경은 45 내지 55 나노미터이며, 기공부피가 4 내지 6cm3인 것을 특징으로 하는 에어로겔이 함유된 백필터 조성물.
The method of claim 3,
The airgel-containing bag filter composition, characterized in that the diameter of the pores formed in the airgel is 45 to 55 nanometers, and the pore volume is 4 to 6 cm 3 .