KR102451229B1 - Microfiber fabric, general textile, synthetic leather and cover of mobile phone, tablet PC and home appliance using them - Google Patents

Microfiber fabric, general textile, synthetic leather and cover of mobile phone, tablet PC and home appliance using them Download PDF

Info

Publication number
KR102451229B1
KR102451229B1 KR1020210019716A KR20210019716A KR102451229B1 KR 102451229 B1 KR102451229 B1 KR 102451229B1 KR 1020210019716 A KR1020210019716 A KR 1020210019716A KR 20210019716 A KR20210019716 A KR 20210019716A KR 102451229 B1 KR102451229 B1 KR 102451229B1
Authority
KR
South Korea
Prior art keywords
polyurethane
layer
polyurethane resin
microfiber fabric
fabric
Prior art date
Application number
KR1020210019716A
Other languages
Korean (ko)
Other versions
KR20220116640A (en
Inventor
김지영
Original Assignee
(주)커버뷰
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)커버뷰 filed Critical (주)커버뷰
Priority to KR1020210019716A priority Critical patent/KR102451229B1/en
Publication of KR20220116640A publication Critical patent/KR20220116640A/en
Application granted granted Critical
Publication of KR102451229B1 publication Critical patent/KR102451229B1/en

Abstract

본 발명에 따른 폴리우레탄 극세사 원단 제작 방법은, 폴리우레탄(PU) 스킨층을 준비하는 단계, 폴리우레탄 스킨층 아래에, 폴리우레탄 스킨층에 비해 내열성이 낮은 폴리우레탄(PU) 레진층을 배치시켜 부착하는 단계, 폴리우레탄 레진층 아래에, 극세사 원단층을 배치시켜 부착하는 단계 및 폴리우레탄 스킨층, 폴리우레탄 레진층 및 극세사 원단층을 가열시켜, 폴리우레탄 레진층에 있는 폴리우레탄 레진의 일부가 극세사 원단층의 적어도 일부 영역으로 함침되도록 하는 가열 단계를 포함한다.
본 발명은 마이크로 파이버 원단 멜란지 고유의 디자인을 살릴 수 있는 커버 및 케이스 제작용 원단을 제공하고, 이를 바탕으로 멜란지 고유의 디자인을 살리고, 환경 친화성, 무독성, 발오성, 발수성, 뛰어난 내열성 및 작업 안정성을 확보할 수 있는 휴대폰이나 태블릿 또는 백색가전의 케이스 또는 커버를 제공할 수 있다.The polyurethane microfiber fabric manufacturing method according to the present invention comprises the steps of preparing a polyurethane (PU) skin layer, placing a polyurethane (PU) resin layer with low heat resistance compared to the polyurethane skin layer under the polyurethane skin layer. The step of attaching, under the polyurethane resin layer, placing and attaching a microfiber fabric layer, and heating the polyurethane skin layer, the polyurethane resin layer and the microfiber fabric layer, so that a part of the polyurethane resin in the polyurethane resin layer is and a heating step to be impregnated into at least a partial region of the microfiber fabric layer.
The present invention provides a fabric for making a cover and a case that can utilize the unique design of the microfiber fabric melange, and based on this, the original design of the melange is saved, and the environment-friendly, non-toxic, stain-repellent, water-repellent, excellent heat resistance and work stability We can provide a case or cover for a mobile phone, tablet, or white home appliance that can secure it.

Description

극세사 원단, 직물, 합성피혁 및 이를 이용한 휴대폰 또는 태블릿, 백색가전의 커버{Microfiber fabric, general textile, synthetic leather and cover of mobile phone, tablet PC and home appliance using them}Microfiber fabric, general textile, synthetic leather and cover of mobile phone, tablet PC and home appliance using them}

본 발명은 휴대폰이나 태블릿 또는 백색가전의 케이스나 소프트 커버 및 이를 제작하기 위한 극세사 원단에 관한 것이다.The present invention relates to a case or soft cover for a mobile phone, tablet, or white home appliance, and a microfiber fabric for manufacturing the same.

일반적으로 휴대폰이나 태블릿은 이용자가 휴대하면서 사용하거나 작은 가방속에 휴대할 수 있는 단말기로 현대인은 거의 필수품으로 휴대하고 다니는 것이 현실이다.In general, a mobile phone or tablet is a terminal that a user can use while carrying it or can be carried in a small bag.

이와 같은 휴대폰 및 태블릿은 휴대성으로 사람이 손으로 가지고 다니거나 가방속에 넣은 채로 이동하는 경우가 많은데, 이러한 경우 휴대폰 화면이나 표면에 손상이 갈 수 있고, 떨어뜨리는 경우 휴대폰 및 태블릿이 망가지는 경우가 존재한다. Such mobile phones and tablets are often carried by hand or carried in a bag due to their portability. In this case, the screen or surface of the mobile phone may be damaged, and if dropped, the mobile phone and tablet may be damaged. exist.

특히 대다수의 스마트폰이나 태블릿은 화면이 보이는 전면이 터치스크린으로 형성되고 이러한 터치스크린은 강화유리로 처리되고 있다. 강화유리는 긁힘, 전면으로부터의 충격에는 강한 이점이 있으나, 측면으로부터 충격에 매우 취약하여 디스플레이 패널이 강화유리로 제작된 스마트폰이나 태블릿의 경우 사용자의 사용 중 부주의에 의해 지면으로 낙하된 경우, 디스플레이 패널을 보호하고 있는 전면 패널, 또는 디스플레이 패널 자체가 깨져 버리는 등의 문제가 발생될 수 있다.In particular, most smartphones and tablets have a touch screen on the front where the screen can be seen, and these touch screens are treated with tempered glass. Tempered glass has a strong advantage in scratching and impact from the front, but it is very vulnerable to impact from the side. The front panel protecting the panel or the display panel itself may be broken.

이러한 문제점을 방지하기 위해, 사용자는 별도의 케이스나 케이스와 함께 부착되는 소프트 커버를 구매하여 휴대폰 및 태블릿을 보호하고 있다.In order to prevent such a problem, a user purchases a separate case or a soft cover attached with the case to protect the mobile phone and tablet.

한편, 이러한 케이스나 소프트 커버의 디자인 및 휴대감 및 손과의 접촉감을 향상시키기 위해 케이스 및 소프트 커버의 플라스틱 재질 위에 극세사 원단을 덧붙여 사용하는 방법을 제시하고 있다. On the other hand, in order to improve the design, portability, and contact feeling of the case or soft cover, a method of using a microfiber fabric on top of the plastic material of the case and the soft cover is presented.

하지만, 친환경, 무독성, 발수성, 내열성이 뛰어난 제품에 대한 요구가 증가하고 있어 이러한 특성을 갖는 케이스나 소프트 커버 및 이를 제작하기 위한 극세사 원단의 개발 필요성이 대두되고 있다.However, as the demand for environmentally friendly, non-toxic, water-repellent and heat-resistant products is increasing, the need to develop a case or soft cover having these characteristics and a microfiber fabric for manufacturing the same is emerging.

1. 대한민국 특허공개 제10-2016-0112171(고강도 내열섬유를 이용한 원단 및 그 제조방법)1. Korean Patent Laid-Open No. 10-2016-0112171 (Fabric and manufacturing method using high-strength heat-resistant fiber) 2. 대한민국 공개특허 제10-2017-0048700(휴대폰 케이스)2. Republic of Korea Patent Publication No. 10-2017-0048700 (cell phone case)

본 발명은 상술한 문제점을 해결하기 위하여 창출된 것으로, 마이크로 파이버 원단 멜란지 고유의 디자인을 살릴 수 있는 케이스 또는 커버 제작용 원단을 제공하는 것을 그 목적으로 한다.The present invention was created to solve the above problems, and an object of the present invention is to provide a fabric for manufacturing a case or cover that can utilize the unique design of the microfiber fabric melange.

또한 본 발명은 환경 친화성, 무독성, 발오성, 발수성, 뛰어난 내열성 및 작업 안정성을 확보할 수 있는 휴대폰이나 태블릿 또는 백색가전의 케이스 또는 커버를 제공하는 것을 그 목적으로 한다. Another object of the present invention is to provide a case or cover for a mobile phone, tablet, or white home appliance that can secure environmental friendliness, non-toxicity, stain repellency, water repellency, excellent heat resistance and work stability.

상기의 목적을 달성하기 위한 본 발명의 일 실시예에 따르면, 휴대폰 또는 태블릿 또는 백색가전의 케이스나 커버에 적용하기 위한 폴리우레탄 극세사 원단을 제작하는 방법은, (a) 폴리우레탄(PU) 스킨층을 준비하는 단계; (b) 상기 폴리우레탄 스킨층 아래에, 상기 폴리우레탄 스킨층에 비해 내열성이 낮은 폴리우레탄(PU) 레진층을 배치시켜 부착하는 단계; (c) 상기 폴리우레탄 레진층 아래에, 극세사 원단, 직물 및 합성 피혁중 어느 하나를 포함하는 극세사 원단층을 배치시켜 부착하는 단계; 및 (d) 상기 폴리우레탄 스킨층, 폴리우레탄 레진층 및 극세사 원단층을 가열시켜, 상기 폴리우레탄 레진층에 있는 폴리우레탄 레진의 일부가 상기 극세사 원단층의 적어도 일부 영역으로 함침되도록 하는 가열 단계;를 포함한다.According to an embodiment of the present invention for achieving the above object, the method for producing a polyurethane microfiber fabric for application to a case or cover of a mobile phone or tablet or white home appliance is (a) a polyurethane (PU) skin layer to prepare; (b) disposing and attaching a polyurethane (PU) resin layer having lower heat resistance than the polyurethane skin layer under the polyurethane skin layer; (c) disposing and attaching a microfiber fabric layer comprising any one of a microfiber fabric, a fabric, and a synthetic leather under the polyurethane resin layer; and (d) heating the polyurethane skin layer, the polyurethane resin layer, and the microfiber fabric layer so that a portion of the polyurethane resin in the polyurethane resin layer is impregnated into at least a partial region of the microfiber fabric layer; includes

일 실시예에서, 상기 (d) 단계는 엠보 가공을 통해 상기 폴리우레탄 레진층의 일부가 상기 극세사 원단층의 적어도 일부 영역으로 함침되도록 한다.In one embodiment, the step (d) allows a portion of the polyurethane resin layer to be impregnated into at least a portion of the microfiber fabric layer through embossing.

일 실시예에서, 상기 (d) 단계에서, 가열 온도는 상기 폴리우레탄 스킨층의 내열 온도보다는 낮고, 상기 폴리우레탄 레진층의 내열 온도보다는 높다.In one embodiment, in the step (d), the heating temperature is lower than the heat resistance temperature of the polyurethane skin layer, higher than the heat resistance temperature of the polyurethane resin layer.

일 실시예에서, 상기 폴리우레탄 스킨층은 투명 제1 액형 폴리우레탄 스킨층이며, 상기 폴리우레탄 레진층은 수성 또는 유성의 제1 액형 폴리우레탄 레진층이다.In one embodiment, the polyurethane skin layer is a transparent first-component polyurethane skin layer, and the polyurethane resin layer is an aqueous or oil-based first-component polyurethane resin layer.

본 발명이 다른 특징에 따르면, 휴대폰 또는 태블릿또는 백색가전의 케이스나 커버에 적용하기 위한 폴리우레탄 극세사 원단은, 폴리우레탄(PU) 스킨층; 상기 폴리우레탄 스킨층 아래에 배치되며, 상기 폴리우레탄 스킨층에 비해 내열성이 낮은 폴리우레탄(PU) 레진층; 및 상기 폴리우레탄 레진층 아래에 배치되며, 상기 폴리우레탄 레진층과 인접한 면으로부터 적어도 소정의 깊이로 상기 폴리우레탄 레진층의 폴리우레탄 레진이 함침된, 극세사 원단, 직물 및 합성 피혁중 어느 하나를 포함하는 극세사 원단층; 을 포함한다.According to another feature of the present invention, a polyurethane microfiber fabric for application to a case or cover of a mobile phone or tablet or white home appliance includes a polyurethane (PU) skin layer; a polyurethane (PU) resin layer disposed under the polyurethane skin layer and having low heat resistance compared to the polyurethane skin layer; and any one of microfiber fabric, fabric and synthetic leather, which is disposed under the polyurethane resin layer and impregnated with the polyurethane resin of the polyurethane resin layer to at least a predetermined depth from the surface adjacent to the polyurethane resin layer a microfiber fabric layer; includes

일 실시예에서, 상기 극세사 원단층에 함침된 상기 폴리우레탄 레진은, 상기 폴리우레탄 극세사 원단을 가열시켜, 상기 폴리우레탄 레진층의 폴리우레탄 레진 일부가 상기 극세사 원단층의 적어도 일부 영역으로 함침됨으로써 상기 폴리우레탄 레진층에서 극세사 원단층으로 함친된 것을 특징으로 한다.In one embodiment, the polyurethane resin impregnated in the microfiber fabric layer is, by heating the polyurethane microfiber fabric, a portion of the polyurethane resin of the polyurethane resin layer is impregnated into at least a partial region of the microfiber fabric layer. It is characterized in that it is impregnated with a microfiber fabric layer in a polyurethane resin layer.

일 실시예에서, 상기 극세사 원단층에 함침된 상기 폴리우레탄 레진은, 상기 폴리우레탄 극세사 원단의 엠보 가공 시, 상기 극세사 원단을 가열시켜, 상기 폴리우레탄 레진층의 폴리우레탄 레진 일부가 상기 극세사 원단층의 적어도 일부 영역으로 함침됨으로써 상기 폴리우레탄 레진층에서 극세사 원단층으로 함친된다.In one embodiment, the polyurethane resin impregnated in the microfiber fabric layer is, when embossing the polyurethane microfiber fabric, by heating the microfiber fabric, a portion of the polyurethane resin of the polyurethane resin layer is the microfiber fabric layer By being impregnated with at least a partial region of the polyurethane resin layer is impregnated with the microfiber fabric layer.

일 실시예에서, 상기 가열 온도는 상기 폴리우레탄 스킨층의 내열 온도보다는 낮고, 상기 폴리우레탄 레진층의 내열 온도보다는 높다.In one embodiment, the heating temperature is lower than the heat resistance temperature of the polyurethane skin layer, higher than the heat resistance temperature of the polyurethane resin layer.

일 실시예에서, 상기 폴리우레탄 스킨층은 투명 제1 액형 폴리우레탄 스킨층이며, 상기 폴리우레탄 레진층은 수성 또는 유성의 제1 액형 폴리우레탄 레진층이다.In one embodiment, the polyurethane skin layer is a transparent first-component polyurethane skin layer, and the polyurethane resin layer is an aqueous or oil-based first-component polyurethane resin layer.

본 발명의 또 다른 특징에 따르면, 휴대폰 또는 태블릿 또는 백색가전의 커버 제작 방법은, (a) 폴리우레탄(PU) 스킨층을 준비하는 단계; (b) 상기 폴리우레탄 스킨층 아래에, 상기 폴리우레탄 스킨층에 비해 내열성이 낮은 폴리우레탄(PU) 레진층을 배치시켜 부착하는 단계; (c) 상기 폴리우레탄 레진층 아래에, 극세사 원단, 직물 및 합성 피혁중 어느 하나를 포함하는 극세사 원단층을 배치시켜 부착하는 단계; (d) 상기 폴리우레탄 스킨층, 폴리우레탄 레진층 및 극세사 원단층을 가열시켜, 상기 폴리우레탄 레진층에 있는 폴리우레탄 레진의 일부가 상기 극세사 원단층의 적어도 일부 영역으로 함침되도록 하는 가열하여, 폴리우레탄 극세사 원단을 제작하는 단계; 및 (e) 상기 폴리우레탄 극세사 원단의 극세사 원단층 일면에 핫멜트 접착제를 통해 플라스틱 커버를 부착하는 단계;를 포함한다.According to another feature of the present invention, a method for manufacturing a cover for a mobile phone or tablet or white home appliance includes the steps of: (a) preparing a polyurethane (PU) skin layer; (b) disposing and attaching a polyurethane (PU) resin layer having lower heat resistance than the polyurethane skin layer under the polyurethane skin layer; (c) disposing and attaching a microfiber fabric layer comprising any one of a microfiber fabric, a fabric, and a synthetic leather under the polyurethane resin layer; (d) heating the polyurethane skin layer, the polyurethane resin layer and the microfiber fabric layer so that a portion of the polyurethane resin in the polyurethane resin layer is impregnated into at least a partial region of the microfiber fabric layer, poly producing a urethane microfiber fabric; and (e) attaching a plastic cover to one surface of the microfiber fabric layer of the polyurethane microfiber fabric through a hot melt adhesive.

일 실시예에서, 상기 폴리우레탄 스킨층은 제1 색상의 칼라를 포함하고, 상기 폴리우레탄 레진층은 상기 제1 색상과는 다른 제2 색상의 칼라를 포함하고, 상기 커버 제작 방법은, (f) 상기 폴리우레탄(PU) 스킨층의 일부 영역을 상기 폴리우레탄 레진층까지 깎아 제거하여 상기 폴리우레탄 레진층이 외부로 노출되도록 하는 단계;를 포함한다.In one embodiment, the polyurethane skin layer includes a color of a first color, the polyurethane resin layer includes a color of a second color different from the first color, and the method for manufacturing the cover includes (f ) removing a portion of the polyurethane (PU) skin layer to the polyurethane resin layer to expose the polyurethane resin layer to the outside; includes.

본 발명에 따른 휴대폰 또는 태블릿 또는 백색가전의 케이스, 커버를 제작하는 방법 및 이를 위한 원단 제작 장법에 따르면, 마이크로 파이버 원단을 PU 제1 액형 핫멜트에 함침시키고 원단 표면에 투명 PU 코팅 및 엠보싱 처리함으로써 마이크로 파이버 원단 멜란지 고유의 디자인을 살릴 수 있는 커버 및 케이스 제작용 원단을 제공하고, 이를 바탕으로 멜란지 고유의 디자인을 살릴 수 있는 휴대폰, 태블릿 또는 백색가전의 커버 및 케이스를 제공할 수 있는 효과가 있다.According to the method for manufacturing a case and cover for a mobile phone or tablet or white home appliance according to the present invention, and a fabric manufacturing method for the same, microfiber fabric is impregnated in PU first liquid hot melt and transparent PU coating and embossing treatment on the fabric surface Fiber fabric It provides a fabric for making covers and cases that can make use of Melange's unique design, and based on this, it has the effect of providing covers and cases for mobile phones, tablets, or white home appliances that can make use of Melange's unique design.

또한 본 발명에 따른 휴대폰 또는 태블릿 또는 백색가전의 케이스, 커버를 제작하는 방법 및 이를 위한 원단 제작 장법에 따르면, 환경 친화성, 무독성, 발오성, 발수성, 뛰어난 내열성 및 작업 안정성을 확보할 수 있는 휴대폰이나 태블릿 또는 백색가전의 케이스 또는 커버를 제공할 수 있다.In addition, according to the method for manufacturing a case or cover for a mobile phone or tablet or white home appliance according to the present invention and a fabric manufacturing method for the same, a mobile phone capable of securing environmental friendliness, non-toxicity, stain repellency, water repellency, excellent heat resistance and work stability Alternatively, a case or cover for a tablet or white home appliance may be provided.

도 1은 본 발명에 따른 휴대폰 또는 태블릿 또는 백색가전의 원단 커버를 제작하는 과정을 나타낸 흐름도이다.
도 2는 본 발명의 일 실시예에 따른 PU 레진 함침을 통한 원단 제작 방법을 나타낸다.
도 3은 본 발명의 일 실시예에 따라 태블릿 커버를 제작한 예를 나타낸다.
도 4는 본 발명의 다른 실시예에 따라 PU 스킨층을 레이저 가공하여 커버와 다른 색상의 글자를 커버에 표시한 휴대폰 케이스를 제작한 예를 나타낸다.1 is a flowchart illustrating a process of manufacturing a fabric cover for a mobile phone or tablet or white home appliance according to the present invention.
Figure 2 shows a fabric manufacturing method through the PU resin impregnation according to an embodiment of the present invention.
3 shows an example of manufacturing a tablet cover according to an embodiment of the present invention.
4 shows an example of manufacturing a mobile phone case in which the PU skin layer is laser-processed according to another embodiment of the present invention, and letters of a different color from the cover are displayed on the cover.

이하 첨부된 도면을 참조하면서 본 발명에 따른 바람직한 실시예를 상세히 설명하기로 한다. 이에 앞서, 본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니 되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여, 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.Hereinafter, preferred embodiments according to the present invention will be described in detail with reference to the accompanying drawings. Prior to this, the terms or words used in the present specification and claims should not be construed as being limited to conventional or dictionary meanings, and the inventor should properly understand the concept of the term in order to best describe his invention. Based on the principle that it can be defined, it should be interpreted as meaning and concept consistent with the technical idea of the present invention.

따라서, 본 명세서에 기재된 실시예와 도면에 도시된 구성은 본 발명의 가장 바람직한 일 실시예에 불과할 뿐이고 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 균등물과 변형예들이 있을 수 있음을 이해하여야 한다.Therefore, the configuration shown in the embodiments and drawings described in the present specification is merely the most preferred embodiment of the present invention and does not represent all of the technical spirit of the present invention, so at the time of the present application, various It should be understood that there may be equivalents and variations.

도 1은 본 발명에 따른 휴대폰 또는 태블릿 또는 백색가전의 원단 커버를 제작하는 과정을 나타낸 흐름도이다.1 is a flowchart illustrating a process of manufacturing a fabric cover for a mobile phone or tablet or white home appliance according to the present invention.

도 2는 본 발명의 일 실시예에 따른 PU 레진 함침을 통한 원단 제작 방법을 나타낸다.Figure 2 shows a fabric manufacturing method through the PU resin impregnation according to an embodiment of the present invention.

도면을 참조하여, 본 발명에 따른 휴대폰 또는 태블릿 또는 백색가전 원단 커버를 제작하는 과정을 설명하면 다음과 같다.With reference to the drawings, a process of manufacturing a mobile phone or tablet or white home appliance fabric cover according to the present invention will be described as follows.

우선, 휴대폰 또는 태블릿 또는 백색가전의 케이스나 커버에 적용하기 위한 폴리우레탄 극세사 원단(110)을 제작한다.First, a polyurethane microfiber fabric 110 for application to a case or cover of a mobile phone or tablet or white home appliance is manufactured.

도 1 및 도 2를 참조하면, 폴리우레탄(PU) 스킨층(101)을 준비한다(S10). 이러한 폴리우레탄(PU) 스킨층은 일반적으로 도 2에 도시된 폴리우레탄 레진층(102)의 색상이 보일 수 있도록 투명한 재질인 것이 바람직하다. 1 and 2, a polyurethane (PU) skin layer 101 is prepared (S10). The polyurethane (PU) skin layer is generally preferably made of a transparent material so that the color of the polyurethane resin layer 102 shown in FIG. 2 can be seen.

그런 다음 폴리우레탄(PU) 스킨층 아래에 폴리우레탄(PU) 레진층(102)을 배치시켜 부착한다(S20). 이때 폴리우레탄(PU) 레진층(102)은 PU 스킨층(101)에 비해 내열성이 낮은 특성을 갖는 재질을 선택한다. Then, a polyurethane (PU) resin layer 102 is disposed under the polyurethane (PU) skin layer and attached (S20). In this case, the polyurethane (PU) resin layer 102 is selected from a material having low heat resistance compared to the PU skin layer 101 .

그런 다음, PU 레진층(102) 아래에 극세사 원단층(103)를 배치시켜 부착한다(S30). 이때 극세사 원단층은 극세사 원단 이외에도, 직물, 합성피혁 중 어느 하나를 이용할 수 있다.Then, the microfiber fabric layer 103 is placed under the PU resin layer 102 and attached thereto (S30). In this case, the microfiber fabric layer may use any one of fabrics and synthetic leather in addition to the microfiber fabric.

그리고 나서 PU 스킨층(101), PU 레진층(102) 및 극세사 원단층(103)을 가열시켜, 폴리우레탄 레진층(102)에 있는 폴리우레탄 레진의 일부가 극세사 원단층(103)의 적어도 일부 영역으로 함침되도록 가열한다(S40).Then, the PU skin layer 101 , the PU resin layer 102 , and the microfiber fabric layer 103 are heated so that a part of the polyurethane resin in the polyurethane resin layer 102 is at least a part of the microfiber fabric layer 103 . The region is heated to be impregnated (S40).

이러한 과정을 통해서 극세사 원단(110)이 완성된다. 이때, 가열 단계(S40)에서 상기 가열 방법은 엠보 가열 또는 엠보 가공 방법을 이용할 수 있다. 엠보 가공을 통해 극세사 원단(110)을 엠보싱 처리하여 극세사 원단의 패턴 디자인을 그대로 살릴 수 있는 효과를 제공할 수 있다. 즉, 상기 S40 단계는 엠보 가공을 통해 폴리우레탄 레진층(102)의 일부가 극세사 원단층(103)의 소정 깊이로 함침되어 도 2에 도시된 바와 같이 폴리우레탄 레진이 함침된 원단층(103a)가 형성되게 된다.Through this process, the microfiber fabric 110 is completed. In this case, in the heating step (S40), the heating method may use an embossing heating or an embossing processing method. By embossing the microfiber fabric 110 through the embossing process, it is possible to provide an effect of keeping the pattern design of the microfiber fabric as it is. That is, in step S40, a portion of the polyurethane resin layer 102 is impregnated to a predetermined depth of the microfiber fabric layer 103 through embossing, and as shown in FIG. 2, the fabric layer 103a impregnated with the polyurethane resin. will be formed

한편, 엠보 가공 시의 가열 온도는 폴리우레탄 스킨층(101)의 내열 온도보다는 낮고, 폴리우레탄 레진층(102)의 내열 온도보다는 높은 온도로 설정하는 것이 바람직하다. 이를 통해 엠보 가공시 폴리우레탄 스킨층(101)은 변함없이 폴리우레탄 레진층(102)의 레진만 녹아 원단층(103) 속으로 함침될 수 있게 한다.On the other hand, the heating temperature at the time of embossing is lower than the heat resistance temperature of the polyurethane skin layer 101, it is preferable to set it to a temperature higher than the heat resistance temperature of the polyurethane resin layer (102). Through this, during embossing, only the resin of the polyurethane resin layer 102 is melted and the polyurethane skin layer 101 is impregnated into the fabric layer 103 without change.

엠보 가공은 엠보 롤러를 통해 수행될 수 있고 엠보 롤러의 온도를 폴리우레탄 레진의 내열 온도보다 높은 온도로 유지하면, 폴리우레탄 레진이 녹아 원단층 속으로 함침될 수 있다.Embossing can be performed through an embossing roller, and if the temperature of the embossing roller is maintained at a temperature higher than the heat-resistant temperature of the polyurethane resin, the polyurethane resin can be melted and impregnated into the fabric layer.

한편, 폴리우레탄 스킨층(101)은 제1 액형 폴리우레탄 스킨층이고, 아울러 투명한 재질로 제작하는 것이 바람직할 것이다. 그러나 폴리우레탄 스킨층(101)은 불투명한 색상을 갖는 재질로 제작될 수도 있을 것이다. 그리고 폴리우레탄 레진층(102)도 수성 또는 유성의 제1 액형 폴리우레탄 레진층인 것이 바람직하다. On the other hand, the polyurethane skin layer 101 is a first liquid polyurethane skin layer, and it will be preferable to be made of a transparent material. However, the polyurethane skin layer 101 may be made of a material having an opaque color. And it is preferable that the polyurethane resin layer 102 is also a water-based or oil-based first-component polyurethane resin layer.

도 2를 참조하면, 엠보 가공 전의 극세사 원단층(103)이 폴리우레탄 레진층(102)의 레진이 함침된 부분(103a)와 함침되지 않은 부분(103)이 소정 깊이에서 구분되게 된다. 이러한 수성 또는 유성의 폴리우레탄 레진층의 함침을 통해 극세사 원단의 특성을 살리면서도, 환경 친화성, 무독성, 방오성, 발수성, 뛰어난 내열성 및 작업 안정성을 제공하는 효과를 얻을 수 있다.Referring to FIG. 2 , the resin-impregnated portion 103a of the polyurethane resin layer 102 and the non-impregnated portion 103 of the microfiber fabric layer 103 before embossing are separated at a predetermined depth. Through the impregnation of the water-based or oil-based polyurethane resin layer, it is possible to obtain the effect of providing environmental friendliness, non-toxicity, antifouling properties, water repellency, excellent heat resistance and work stability while preserving the characteristics of the microfiber fabric.

한편, 상기 S10 단계에서 이형지 위에 일반적인 폴리우레탄 레진을 스킨층으로서 코팅하여 형성하고, S20 단계에 그 위에 내열성이 낮은 1액형 폴리우레탄 레진을 코팅하고, S30 단계에서 그 위에 극세사 원단을 접착하여 제작할 수 있다. 이러한 경우, S40 단계에서 엠보 가공을 통해 레진이 극세사 원단으로 함침된 후, 이형지를 박리하여 소정 시간 동안 숙성을 하게 할 수 있다. 여기서 숙성이란 극세사 원단을 소정 시간 뜨거운 온도에 두게 하여 굳히는 것을 말한다. 그리고 이형지는 제거된다.On the other hand, it is formed by coating a general polyurethane resin as a skin layer on the release paper in step S10, coating a one-component polyurethane resin having low heat resistance thereon in step S20, and adhering a microfiber fabric thereon in step S30. have. In this case, after the resin is impregnated with the microfiber fabric through embossing in step S40, the release paper may be peeled off and aged for a predetermined time. Here, aging refers to hardening the microfiber fabric by placing it at a hot temperature for a predetermined time. And the release paper is removed.

도 3은 본 발명의 일 실시예에 따라 태블릿 커버를 제작한 예를 나타낸다.3 shows an example of manufacturing a tablet cover according to an embodiment of the present invention.

도 3을 참조하면, 위 단계 S40까지의 과정을 통해 얻은 극세사 원단(110)을 이용하여 플라스틱 커버를 접착하여 케이스 또는 커버를 제작할 수 있게 된다.Referring to FIG. 3 , a case or cover can be manufactured by adhering a plastic cover using the microfiber fabric 110 obtained through the process up to step S40 above.

도 1을 참조하면, 극세사 원단(110) 아래에 이형 핫멜트를 코팅한 후 플라스틱 커버를 핫멜트에 부착한다(S50). 일 실시예에서, 사출 완료된 플라스틱에 이형 핫멜트가 부착된 극세사 원단(110)을 열로 접착한다. 그러면 핫멜트가 식으면서 극세사 원단(110)과 플라스틱 재질의 커버 또는 케이스가 접착되어 극세사 원단이 적용된 커버나 케이스가 제작되게 된다. Referring to FIG. 1 , after coating the release hot melt under the microfiber fabric 110 , a plastic cover is attached to the hot melt ( S50 ). In one embodiment, the microfiber fabric 110 to which the release hot melt is attached to the injection-completed plastic is thermally bonded. Then, as the hot melt cools, the microfiber fabric 110 and the plastic cover or case are adhered, so that a cover or case to which the microfiber fabric is applied is manufactured.

도 4는 본 발명의 다른 실시예에 따라 PU 스킨층을 레이저 가공하여 커버와 다른 색상의 글자를 커버에 표시한 휴대폰 케이스를 제작한 예를 나타낸다.4 shows an example of manufacturing a mobile phone case in which the PU skin layer is laser-processed according to another embodiment of the present invention, and letters of a different color from the cover are displayed on the cover.

도 1 및 도 4를 참조하면, PU 스킨층(101)의 재질을 투명한 재질이 아닌 제1 색상의 칼라를 포함하는 재질로 만들고, PU 레진층(102)은 제1 색상과는 다른 제2 색상의 칼라를 포함하는 재질로 만든 후, PU 스킨층(101)의 일부 영역을 PU 레진층(102)까지 레이저 가공 등을 통해 깎아 제거하여, PU 레진층(102)의 색상이 깎은 공간을 통해 PU 스킨층(101) 외부로 노출되게 한다(S60). 1 and 4, the material of the PU skin layer 101 is made of a material containing a color of a first color rather than a transparent material, and the PU resin layer 102 has a second color different from the first color. After making it with a material containing the color of the PU skin layer 101, a portion of the PU skin layer 101 is removed through laser processing, etc. up to the PU resin layer 102, and the color of the PU resin layer 102 is cut through the PU through the space. The skin layer 101 is exposed to the outside (S60).

예를 들어, PU 스킨층(101)의 표면에 제작사나 소유자의 이름을 새길 수 있도록 레이저고 가공하면, PU 레진층(102)이 가공된 영역을 통해 드러나게 되어, 도 4의 예에서와 같이, 서로 다른 색상의 PU 스킨층(101)과 PU 레진층(102)를 통해 케이스 자체에서 다양한 색상의 무늬나 글자를 새길 수 있는 효과를 제공하게 된다.For example, when laser processing is performed so that the name of the manufacturer or owner can be engraved on the surface of the PU skin layer 101, the PU resin layer 102 is exposed through the processed area, as in the example of FIG. Through the PU skin layer 101 and the PU resin layer 102 of different colors, it is possible to provide the effect of engraving patterns or characters of various colors on the case itself.

본 발명에 따른 휴대폰 또는 태블릿 또는 백색가전의 케이스, 커버를 제작하는 방법 및 이를 위한 원단 제작 장법에 따르면, 마이크로 파이버 원단을 PU 제1 액형 핫멜트에 함침시키고 원단 표면에 투명 PU 코팅 및 엠보싱 처리함으로써 마이크로 파이버 원단 멜란지 고유의 디자인을 살릴 수 있는 커버 및 케이스 제작용 원단을 제공하고, 이를 바탕으로 멜란지 고유의 디자인을 살릴 수 있는 휴대폰 및 태블릿 또는 백색가전의 커버 및 케이스를 제공할 수 있는 효과가 있다.According to the method for manufacturing a case and cover for a mobile phone or tablet or white home appliance according to the present invention, and a fabric manufacturing method for the same, microfiber fabric is impregnated in PU first liquid hot melt and transparent PU coating and embossing treatment on the fabric surface Fiber fabric It provides a fabric for making covers and cases that can make use of Melange's unique design, and based on this, it has the effect of providing covers and cases for mobile phones and tablets or white home appliances that can utilize Melange's unique design.

또한 본 발명에 따른 휴대폰 또는 태블릿 또는 백색가전의 케이스, 커버를 제작하는 방법 및 이를 위한 원단 제작 장법에 따르면, 환경 친화성, 무독성, 발오성, 발수성, 뛰어난 내열성 및 작업 안정성을 확보할 수 있는 휴대폰이나 태블릿 또는 백색가전의 케이스 또는 커버를 제공할 수 있다.In addition, according to the method for manufacturing a case or cover for a mobile phone or tablet or white home appliance according to the present invention and a fabric manufacturing method for the same, a mobile phone capable of securing environmental friendliness, non-toxicity, stain repellency, water repellency, excellent heat resistance and work stability Alternatively, a case or cover for a tablet or white home appliance may be provided.

이상과 같이, 본 발명은 비록 한정된 실시예와 도면에 의해 설명되었으나, 본 발명은 이것에 의해 한정되지 않으며 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 본 발명의 기술 사상과 아래에 기재될 청구범위의 균등 범위 내에서 다양한 수정 및 변형이 가능함은 물론이다.As described above, although the present invention has been described with reference to limited embodiments and drawings, the present invention is not limited thereto, and the technical spirit of the present invention and the following by those of ordinary skill in the art to which the present invention pertains. It goes without saying that various modifications and variations are possible within the equivalent scope of the claims to be described.

101 : PU 스킨층 102 : PU 레진층
103 : 극세사 원단층 103a : 레진이 함침된 극세사 원단층
110 : 폴리우레탄 극세사 원단101: PU skin layer 102: PU resin layer
103: microfiber fabric layer 103a: resin-impregnated microfiber fabric layer
110: polyurethane microfiber fabric

Claims (11)

휴대폰 또는 태블릿 또는 백색가전의 케이스나 커버에 적용하기 위한 폴리우레탄 극세사 원단을 제작하는 방법에 있어서,
(a) 폴리우레탄(PU) 스킨층을 준비하는 단계;
(b) 상기 폴리우레탄 스킨층 아래에, 상기 폴리우레탄 스킨층에 비해 내열성이 낮은 폴리우레탄(PU) 레진층을 배치시켜 부착하는 단계;
(c) 상기 폴리우레탄 레진층 아래에, 극세사 원단, 직물 및 합성 피혁중 어느 하나를 포함하는 극세사 원단층을 배치시켜 부착하는 단계; 및
(d) 상기 폴리우레탄 스킨층, 폴리우레탄 레진층 및 극세사 원단층을 가열시켜, 상기 폴리우레탄 레진층에 있는 폴리우레탄 레진의 일부가 상기 극세사 원단층의 적어도 일부 영역으로 함침되도록 하여, 상기 원단의 일부층은 상기 폴리우레탄 레진으로 함침되고 상기 원단층의 나머지층은 상기 폴리우레탄 레진으로 함침되지 않도록 하는 가열 단계;
를 포함하며,
상기 (d) 단계는 엠보 가공을 통해 상기 폴리우레탄 레진층의 일부가 상기 극세사 원단층의 적어도 일부 영역 안 소정 깊이로 함침되도록 하여, 폴리우레탄 레진이 함침된 원단층이 형성되도록 하며,
상기 (d) 단계에서, 가열 온도는 상기 폴리우레탄 스킨층의 내열 온도보다는 낮고, 상기 폴리우레탄 레진층의 내열 온도보다는 높은 것을 특징으로 하는 원단 제작 방법.
In a method for producing a polyurethane microfiber fabric for application to a case or cover of a mobile phone or tablet or white home appliance,
(a) preparing a polyurethane (PU) skin layer;
(b) disposing and attaching a polyurethane (PU) resin layer having lower heat resistance than the polyurethane skin layer under the polyurethane skin layer;
(c) disposing and attaching a microfiber fabric layer comprising any one of a microfiber fabric, a fabric, and a synthetic leather under the polyurethane resin layer; and
(d) heating the polyurethane skin layer, the polyurethane resin layer and the microfiber fabric layer so that a portion of the polyurethane resin in the polyurethane resin layer is impregnated into at least a partial region of the microfiber fabric layer, A heating step in which some layers are impregnated with the polyurethane resin and the remaining layers of the fabric layer are not impregnated with the polyurethane resin;
includes,
In step (d), a portion of the polyurethane resin layer is impregnated to a predetermined depth in at least a partial region of the microfiber fabric layer through embossing, so that a fabric layer impregnated with a polyurethane resin is formed,
In the step (d), the heating temperature is lower than the heat resistance temperature of the polyurethane skin layer, fabric manufacturing method, characterized in that higher than the heat resistance temperature of the polyurethane resin layer.
 삭제delete 삭제delete 제1 항에 있어서,
상기 폴리우레탄 스킨층은 투명 제1 액형 폴리우레탄 스킨층이며, 상기 폴리우레탄 레진층은 수성 또는 유성의 제1 액형 폴리우레탄 레진층인 것을 특징으로 하는 원단 제작 방법.
The method of claim 1,
The polyurethane skin layer is a transparent first-component polyurethane skin layer, and the polyurethane resin layer is an aqueous or oil-based first-component polyurethane resin layer.
 휴대폰 또는 태블릿 또는 백색가전의 케이스나 커버에 적용하기 위한 폴리우레탄 극세사 원단에 있어서,
폴리우레탄(PU) 스킨층;
상기 폴리우레탄 스킨층 아래에 배치되며, 상기 폴리우레탄 스킨층에 비해 내열성이 낮은 폴리우레탄(PU) 레진층; 및
상기 폴리우레탄 레진층 아래에 배치되며, 상기 폴리우레탄 레진층과 인접한 면으로부터 적어도 소정의 깊이로 상기 폴리우레탄 레진층의 폴리우레탄 레진이 함침된, 극세사 원단, 직물 및 합성 피혁중 어느 하나를 포함하는 극세사 원단층;
을 포함하며,
상기 극세사 원단층에 함침된 상기 폴리우레탄 레진은,
상기 폴리우레탄 극세사 원단을 엠보 가공을 통해 가열시켜, 상기 폴리우레탄 레진층의 폴리우레탄 레진 일부가 상기 폴리우레탄 레진층에서 극세사 원단층 방향으로 상기 극세사 원단층의 적어도 일부 영역 안 소정 깊이로 함침되도록 하여, 상기 원단의 일부층은 상기 폴리우레탄 레진으로 함침되고 상기 원단층의 나머지층은 상기 폴리우레탄 레진으로 함침되지 않도록 함으로써 , 폴리우레탄 레진이 함침된 원단층이 형성되며,
상기 가열 온도는 상기 폴리우레탄 스킨층의 내열 온도보다는 낮고, 상기 폴리우레탄 레진층의 내열 온도보다는 높은 것을 특징으로 하는 폴리우레탄 극세사 원단.
In a polyurethane microfiber fabric for application to a case or cover of a mobile phone or tablet or white home appliance,
polyurethane (PU) skin layer;
a polyurethane (PU) resin layer disposed under the polyurethane skin layer and having low heat resistance compared to the polyurethane skin layer; and
It is disposed under the polyurethane resin layer, and the polyurethane resin of the polyurethane resin layer is impregnated to at least a predetermined depth from the surface adjacent to the polyurethane resin layer, including any one of microfiber fabric, fabric and synthetic leather microfiber fabric layer;
includes,
The polyurethane resin impregnated in the microfiber fabric layer,
By heating the polyurethane microfiber fabric through embossing, a portion of the polyurethane resin of the polyurethane resin layer is impregnated to a predetermined depth in at least a portion of the microfiber fabric layer in the direction from the polyurethane resin layer to the microfiber fabric layer. , A part layer of the fabric is impregnated with the polyurethane resin and the remaining layers of the fabric layer are not impregnated with the polyurethane resin, thereby forming a fabric layer impregnated with a polyurethane resin,
The heating temperature is lower than the heat resistance temperature of the polyurethane skin layer, polyurethane microfiber fabric, characterized in that higher than the heat resistance temperature of the polyurethane resin layer.
 삭제delete 제5 항에 있어서,
상기 극세사 원단층에 함침된 상기 폴리우레탄 레진은,
상기 폴리우레탄 극세사 원단의 엠보 가공 시, 상기 극세사 원단을 가열시켜, 상기 폴리우레탄 레진층의 폴리우레탄 레진 일부가 상기 극세사 원단층의 적어도 일부 영역으로 함침됨으로써 상기 폴리우레탄 레진층에서 극세사 원단층으로 함친된 것을 특징으로 하는 폴리우레탄 극세사 원단.
6. The method of claim 5,
The polyurethane resin impregnated in the microfiber fabric layer,
During embossing of the polyurethane microfiber fabric, by heating the microfiber fabric, a portion of the polyurethane resin of the polyurethane resin layer is impregnated into at least a partial region of the microfiber fabric layer, thereby impregnated with the microfiber fabric layer in the polyurethane resin layer Polyurethane microfiber fabric, characterized in that
 삭제delete 제5 항에 있어서,
상기 폴리우레탄 스킨층은 투명 제1 액형 폴리우레탄 스킨층이며, 상기 폴리우레탄 레진층은 수성 또는 유성의 제1 액형 폴리우레탄 레진층인 것을 특징으로 하는 폴리우레탄 극세사 원단.
6. The method of claim 5,
The polyurethane skin layer is a transparent first-component polyurethane skin layer, and the polyurethane resin layer is a polyurethane microfiber fabric, characterized in that it is an aqueous or oil-based first-component polyurethane resin layer.
 휴대폰 또는 태블릿 또는 백색가전의 커버 제작 방법에 있어서,
(a) 폴리우레탄(PU) 스킨층을 준비하는 단계;
(b) 상기 폴리우레탄 스킨층 아래에, 상기 폴리우레탄 스킨층에 비해 내열성이 낮은 폴리우레탄(PU) 레진층을 배치시켜 부착하는 단계;
(c) 상기 폴리우레탄 레진층 아래에, 극세사 원단, 직물 및 합성 피혁중 어느 하나를 포함하는 극세사 원단층을 배치시켜 부착하는 단계;
(d) 상기 폴리우레탄 스킨층, 폴리우레탄 레진층 및 극세사 원단층을 가열시켜, 상기 폴리우레탄 레진층에 있는 폴리우레탄 레진의 일부가 상기 극세사 원단층의 적어도 일부 영역으로 함침되도록 하여, 상기 원단의 일부층은 상기 폴리우레탄 레진으로 함침되고 상기 원단층의 나머지층은 상기 폴리우레탄 레진으로 함침되지 않도록 가열하여, 폴리우레탄 극세사 원단을 제작하는 단계; 및
(e) 상기 폴리우레탄 극세사 원단의 극세사 원단층 일면에 핫멜트 접착제를 통해 플라스틱 커버를 부착하는 단계;를
포함하며,
상기 (d) 단계는 엠보 가공을 통해 상기 폴리우레탄 레진층의 일부가 상기 극세사 원단층의 적어도 일부 영역 안 소정 깊이로 함침되도록 하여, 폴리우레탄 레진이 함침된 원단층이 형성되고,
상기 폴리우레탄 스킨층은 제1 색상의 칼라를 포함하고, 상기 폴리우레탄 레진층은 상기 제1 색상과는 다른 제2 색상의 칼라를 포함하고,
상기 커버 제작 방법은,
(f) 상기 폴리우레탄(PU) 스킨층의 일부 영역을 상기 폴리우레탄 레진층까지 깎아 제거하여 상기 폴리우레탄 레진층이 외부로 노출되도록 하는 단계;를
포함하며,
상기 가열 온도는 상기 폴리우레탄 스킨층의 내열 온도보다는 낮고, 상기 폴리우레탄 레진층의 내열 온도보다는 높은 것을 특징으로 하는 커버 제작 방법.
In the method for manufacturing a cover of a mobile phone or tablet or white home appliance,
(a) preparing a polyurethane (PU) skin layer;
(b) disposing and attaching a polyurethane (PU) resin layer having lower heat resistance than the polyurethane skin layer under the polyurethane skin layer;
(c) disposing and attaching a microfiber fabric layer comprising any one of a microfiber fabric, a fabric, and a synthetic leather under the polyurethane resin layer;
(d) heating the polyurethane skin layer, the polyurethane resin layer and the microfiber fabric layer so that a portion of the polyurethane resin in the polyurethane resin layer is impregnated into at least a partial region of the microfiber fabric layer, Some layers are impregnated with the polyurethane resin and the remaining layers of the fabric layer are heated so as not to be impregnated with the polyurethane resin, producing a polyurethane microfiber fabric; and
(e) attaching a plastic cover through a hot melt adhesive to one surface of the microfiber fabric layer of the polyurethane microfiber fabric;
includes,
In step (d), a portion of the polyurethane resin layer is impregnated to a predetermined depth in at least a partial region of the microfiber fabric layer through embossing, so that the fabric layer impregnated with the polyurethane resin is formed,
The polyurethane skin layer includes a color of a first color, and the polyurethane resin layer includes a color of a second color different from the first color,
The method of making the cover,
(f) removing a partial area of the polyurethane (PU) skin layer to the polyurethane resin layer to expose the polyurethane resin layer to the outside;
includes,
The heating temperature is lower than the heat resistance temperature of the polyurethane skin layer, the cover manufacturing method, characterized in that higher than the heat resistance temperature of the polyurethane resin layer.
 삭제delete
KR1020210019716A 2021-02-15 2021-02-15 Microfiber fabric, general textile, synthetic leather and cover of mobile phone, tablet PC and home appliance using them KR102451229B1 (en)