KR102417952B1 - DGEBA-based epoxy resin composition, Organic~inorganic ceramic composite waterproofing agent composition including the same and method for manufacturing the same - Google Patents
DGEBA-based epoxy resin composition, Organic~inorganic ceramic composite waterproofing agent composition including the same and method for manufacturing the same Download PDFInfo
- Publication number
- KR102417952B1 KR102417952B1 KR1020200173079A KR20200173079A KR102417952B1 KR 102417952 B1 KR102417952 B1 KR 102417952B1 KR 1020200173079 A KR1020200173079 A KR 1020200173079A KR 20200173079 A KR20200173079 A KR 20200173079A KR 102417952 B1 KR102417952 B1 KR 102417952B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- dgeba
- epoxy resin
- based epoxy
- Prior art date
Abstract
본 발명은, 유기재인 에피크로로하이드린과 비스페놀A를 중합시킨 DGEBA계 에폭시 수지 조성물과 무기재로 이루어진 경화제를 포함하여, 시멘트 또는 모르타르와의 배합이 용이하면서도 우수한 방수성을 제공할 수 있는, DGEBA계 에폭시 수지 조성물과, 이 DGEBA계 에폭시 수지 조성물을 포함하는 유무기 세라믹 복합 방수제 조성물 및 그 제조방법을 제공한다.The present invention includes a DGEBA-based epoxy resin composition obtained by polymerizing the organic material epichlorohydrin and bisphenol A and a curing agent made of an inorganic material, which is easy to mix with cement or mortar and can provide excellent waterproofing properties, DGEBA Provided are a system epoxy resin composition, an organic-inorganic ceramic composite waterproofing agent composition comprising the DGEBA-based epoxy resin composition, and a method for manufacturing the same.
Description
본 발명은 시멘트나 모르타르의 방수용으로 사용되는 DGEBA(Diglycidyl Ether of Bisphenol A)계 에폭시 수지 조성물, 유무기 세라믹 복합 방수제 조성물 및 그 제조방법에 관한 것으로, 더욱 상세하게는 유기재인 에피크로로하이드린과 비스페놀A를 중합시킨 DGEBA계 에폭시 수지 조성물과 무기재로 이루어진 경화제를 포함하여, 시멘트 또는 모르타르와의 배합이 용이하면서도 우수한 방수성을 제공할 수 있는, DGEBA계 에폭시 수지 조성물, 이 DGEBA계 에폭시 수지 조성물을 포함하는 유무기 세라믹 복합 방수제 조성물 및 그 제조방법에 관한 것이다.The present invention relates to a DGEBA (Diglycidyl Ether of Bisphenol A)-based epoxy resin composition used for waterproofing cement or mortar, an organic-inorganic ceramic composite waterproofing agent composition, and a manufacturing method thereof, and more particularly, to an organic material epichlorohydrin and A DGEBA-based epoxy resin composition comprising a DGEBA-based epoxy resin composition polymerized with bisphenol A and a curing agent made of an inorganic material, which is easy to mix with cement or mortar and can provide excellent waterproofness, this DGEBA-based epoxy resin composition It relates to an organic-inorganic ceramic composite waterproofing agent composition and a method for manufacturing the same.
종래의 시멘트 또는 모르타르로 제조된 구조물에 대한 방수방법으로, 핏취 또는 아스팔트루우핑을 사용하여 피막을 형성하여 방법이 있는데, 이 방법은 방수층 열간 가공을 필요로 하는 번거로움과, 내후성의 불량, 경제적으로 고가인 점 등의 단점을 가진다.As a conventional waterproofing method for structures made of cement or mortar, there is a method of forming a film using pitch or asphalt roofing, which is cumbersome requiring hot working of the waterproofing layer, poor weather resistance, and economical It has disadvantages such as being expensive.
이러한 방법을 개량한 것으로서, 아스팔트 냉공법 재질인 시이트를 하지에 접착시켜 방수층을 형성시키는 시이트 방수법이 있다. 그러나, 상기 시이트 방수법은 피방수면의 습기지와 용수되는 부분의 시공상 어려움이 있고, 유연성 및 접착성은 양호하나 시멘트의 피방수면에 균열 및 하자가 발생할 때 보수 비용이 증대되는 문제가 있다.As an improvement of this method, there is a sheet waterproofing method in which a waterproofing layer is formed by bonding a sheet made of an asphalt cold-air method material to a base. However, the sheet waterproofing method has difficulties in construction of the moisture-repellent surface and the water-repellent part, and has good flexibility and adhesiveness, but there is a problem in that the repair cost increases when cracks and defects occur in the waterproofing surface of the cement. .
또 다른 방법으로는 합성고무, 합성수지 용액, 라텍스 등을 하지에 일정 두께 이상으로 도포하고 방수층을 형성시키는 방법이 있다. 그러나, 이 방법 역시 방수층의도막 형성을 위하여는 별도의 방수액을 도포하고 그 위에 시멘트 모르타르를 시공해야 하는 불편한 점이 있다.Another method is to apply synthetic rubber, synthetic resin solution, latex, etc. to the lower surface to a certain thickness or more and form a waterproof layer. However, this method is also inconvenient to apply a separate waterproofing liquid to form a coating film of the waterproofing layer and to construct a cement mortar thereon.
본 발명은, 상기의 여러 가지 결점을 개선하고자, 에피크로로하이드린과 비스페놀A를 중합시켜서 점도가 11,000~14,000센티포아즈(CPS)인 고분자 액상의 DGEBA계 에폭시 수지 조성물과, 무기재로 이루어진 저점도의 경화제를 포함하여, 분산성 및 경화성이 탁월하고 우수한 방수성을 가질 수 있는, DGEBA계 에폭시 수지 조성물과, 유무기 세라믹 복합 방수제 조성물 및 그 제조방법을 제공하는데 그 목적이 있다.The present invention, in order to improve the above various drawbacks, by polymerizing epichlorohydrin and bisphenol A, the viscosity is 11,000 to 14,000 centipoise (CPS) of a liquid polymer DGEBA-based epoxy resin composition and an inorganic material An object of the present invention is to provide a DGEBA-based epoxy resin composition, an organic-inorganic ceramic composite waterproofing agent composition, and a method for manufacturing the same, including a low-viscosity curing agent, which has excellent dispersibility and hardenability and can have excellent waterproofness.
본 발명의 일 측면은, 에폭시 당량이 184~194g/eq이고, 점도가 25℃에서 11,000~14,000센티포아즈(CPS)이고, 비중은 20℃에서 1.17~1.19이고, 색상은 1max이고, 염소함유량은 0.1~0.12%max인 DGEBA계 에폭시 수지 조성물을 제공한다.In one aspect of the present invention, the epoxy equivalent weight is 184 to 194 g / eq, the viscosity is 11,000 to 14,000 centipoise (CPS) at 25 ° C., the specific gravity is 1.17 to 1.19 at 20 ° C., the color is 1 max, and the chlorine content It provides a DGEBA-based epoxy resin composition of 0.1 to 0.12% max.
본 발명의 다른 측면은, 경량골재 4.0~6.0중량부에 대하여, 패각제 1.0중량부; 규산질 시멘트 1.0~1.2중량부; DGEBA계 에폭시 수지 조성물 20~24중량부; 및 경화제 10~12중량부; 를 포함하는 유무기 세라믹 복합 방수제 조성물을 제공한다.Another aspect of the present invention, with respect to the lightweight aggregate 4.0 to 6.0 parts by weight, 1.0 parts by weight of the shell agent; 1.0-1.2 parts by weight of siliceous cement; 20 to 24 parts by weight of a DGEBA-based epoxy resin composition; and 10 to 12 parts by weight of a curing agent; It provides an organic-inorganic ceramic composite waterproofing composition comprising a.
본 발명의 바람직한 특징에 의하면, 상기 경화제가, 디카르복실산과 디아민류와 중축합에 의해 얻어진 폴리아미드 HO(CORCONH-CH2CH2NH)n 여기서 R은 (디카르복실산의 잔기)이고, n은 (2이상의 정수), 전Amine가 310~330이고, 점도가 25℃에서 500~1,000센티포아즈(CPS)이고, 산가가 7 미만이고, 색상이 14 미만일 수 있다.According to a preferred feature of the present invention, the curing agent is a polyamide HO (CORCONH-CH 2 CH 2 NH) n obtained by polycondensation of a dicarboxylic acid and a diamine, wherein R is (a residue of a dicarboxylic acid), n is (an integer greater than or equal to 2), all amines are 310-330, viscosity is 500-1,000 centipoise (CPS) at 25°C, acid value is less than 7, and color may be less than 14.
본 발명의 다른 측면에 따르면, 경량골재 100중량부에 대하여, 패각제 25~35중량부와 규산질 시멘트 30~35중량부 그리고 DGEBA계 에폭시 수지 조성물 20~24중량부와 경화제 10~12중량부를 넣고 혼합하여 이액형의 방수제 조성물을 제조하는 것으로서, According to another aspect of the present invention, with respect to 100 parts by weight of the lightweight aggregate, 25 to 35 parts by weight of a shell agent, 30 to 35 parts by weight of siliceous cement, 20 to 24 parts by weight of a DGEBA-based epoxy resin composition, and 10 to 12 parts by weight of a curing agent, By mixing to prepare a two-component waterproofing composition,
상기 DGEBA계 에폭시 수지 조성물은, DGEBA계 에폭시 수지 13~30중량부에 대하여, 아크릴산 에스테르(Acrylic Esters) 20~25중량부 및 메타크릴계 스티렌 20~25중량부를 혼합하여 용액 상태에서 스티렌화 된 1차 혼합물을 마련하는 단계; 스틴렌화 된 1차 혼합물에 수산기를 가지는 아마인유와 지방산을 추가하고 230℃로 가열하여 에스텔화 된 에스텔화 생성물을 마련하는 단계; 상기 에스텔화 생성물 200중량부를 방향 탄산화 수용액에 녹인 후, 스티렌 100중량부와 디-t-부틸퍼어 옥사이드 4중량부를 추가하고, 135~140℃에서 3.5~4시간 동안 가열하여 2차 혼합물을 마련하는 단계; 상기 2차 혼합물 100중량부에 대하여 스티렌 50~55중량부를 결합시켜 3차 혼합물을 마련하는 단계; 상기 3차 혼합물에 트리클로로실란과 올레핀을 첨가하고 과산화 촉매(45℃)로 반응시켜 알킬실란을 얻는 단계; 및 상기 알킬실란에 Si-O 결합시켜 얻은 화합물을 증유하여 반량 이하는 환상인 디메틸실록산이면서 가교 만상화가 일어나는 고분자량의 DGEBA계 에폭시 수지 조성물을 마련하는 단계; 를 포함하는 것을 특징으로 하는 유무기 세라믹 복합 방수제 조성물의 제조방법을 제공한다.The DGEBA-based epoxy resin composition is 1 styrenated in a solution state by mixing 20-25 parts by weight of acrylic esters and 20-25 parts by weight of methacrylic styrene with respect to 13-30 parts by weight of the DGEBA-based epoxy resin. preparing a tea mixture; preparing an esterified product by adding linseed oil and fatty acids having a hydroxyl group to the styrenated primary mixture and heating to 230°C; After dissolving 200 parts by weight of the esterification product in an aromatic carbonation aqueous solution, 100 parts by weight of styrene and 4 parts by weight of di-t-butylper oxide are added, and heated at 135 to 140° C. for 3.5 to 4 hours to prepare a secondary mixture step; preparing a tertiary mixture by combining 50 to 55 parts by weight of styrene with respect to 100 parts by weight of the secondary mixture; adding trichlorosilane and olefin to the tertiary mixture and reacting with a peroxidation catalyst (45° C.) to obtain alkylsilane; and preparing a DGEBA-based epoxy resin composition having a high molecular weight of cyclic dimethylsiloxane with less than half the weight of cyclic dimethylsiloxane by increasing the amount of the compound obtained by bonding Si-O to the alkylsilane; It provides a method for producing an organic-inorganic ceramic composite waterproofing composition comprising a.
본 발명의 바람직한 특징에 의하면, 상기 경량골재는 유해물질 중금속 검출을 제거 하기 위하여 고온(1,100~1,200℃)에서 선처리 공정으로 열처리를 먼저 한 후 사용하고, 상기 패각제는 병원성 대장균 등에 강한 살균효과를 나타내는 세라믹스 패각제를 가공 처리하여 불순물을 제거한 수세처리된 325~400메쉬의 패각제 분말을 사용할 수 있다.According to a preferred feature of the present invention, the lightweight aggregate is used after heat treatment at a high temperature (1,100 ~ 1,200 ° C) in a pre-treatment process in order to remove the detection of heavy metals from harmful substances, and the shell agent has a strong sterilizing effect on pathogenic E. coli It is possible to use a 325-400 mesh shell agent powder that has been washed with water to remove impurities by processing the indicated ceramic shell agent.
본 실시 예에 의해 제조되는 유무기 세라믹 복합 방수제 조성물은, 유기재인 DGEBA계 에폭시 수지 조성물을 무기재인 경화제와 혼합한 후 소량의 경량골재, 패각제 및 규산질 시멘트와 배합하여 방수면에 도포함으로써 건축물의 표면을 보강함과 동시에 콘크리트의 공극을 폐쇄시켜 방수효과를 극대화할 수 있는 효과가 있다.The organic-inorganic ceramic composite waterproofing composition prepared in this example is prepared by mixing an organic DGEBA-based epoxy resin composition with an inorganic curing agent, mixing it with a small amount of lightweight aggregate, a shell agent, and siliceous cement, and applying it to the waterproofing surface of the building. It has the effect of maximizing the waterproofing effect by reinforcing the surface and closing the pores of the concrete at the same time.
또한, 본 실시 예에 의한 방수제 조성물은, 수중에서 용이하게 분산될 수 있는 저점도의 액체로 시멘트와 배합이 용이할 뿐만 아니라 시멘트나 모르타르 등 수분침투가 용이한 다공질의 면에 균일하게 침투되어 완전한 방수효과를 나타낼 수 있다.In addition, the waterproofing agent composition according to the present embodiment is a low-viscosity liquid that can be easily dispersed in water, and not only is easy to mix with cement, but also uniformly penetrates into a porous surface that easily penetrates moisture, such as cement or mortar, so that it is completely It can show the waterproof effect.
도 1은 본 발명의 일 실시 예에 의한 유무기 세라믹 복합 방수제 조성물을 제조하는 방법을 순서대로 나타낸 플로우차트이다.1 is a flowchart sequentially showing a method for preparing an organic-inorganic ceramic composite waterproofing agent composition according to an embodiment of the present invention.
이하, 본 발명의 바람직한 실시 예를 설명한다. 그러나, 본 발명의 범위가 이하 설명하는 실시 예로 한정되지 않고 청구 범위에 기재된 바에 의해 정의되며, 본 발명의 분야에서 통상의 지식을 가진 자가 청구 범위에 기재된 권리 범위 내에서 다양한 변형과 개작을 할 수 있다.Hereinafter, preferred embodiments of the present invention will be described. However, the scope of the present invention is not limited to the embodiments described below, it is defined by the claims, and a person of ordinary skill in the art can make various modifications and adaptations within the scope of the rights described in the claims. have.
본 발명의 일 실시 예에 따른 유무기 세라믹 복합 방수제 조성물은 DGEBA계 에폭시 수지와 경화제를 포함하는 이액형의 방수제이다. 이때, DGBEA계 에폭시 수지와 경화제의 혼합비율은 2:1(경화제가 1)이 될 수 있다.The organic-inorganic ceramic composite waterproofing composition according to an embodiment of the present invention is a two-component waterproofing agent comprising a DGEBA-based epoxy resin and a curing agent. At this time, the mixing ratio of the DGBEA-based epoxy resin and the curing agent may be 2:1 (curing agent 1).
상기 DGEBA계 에폭시 수지는 유기제인 에피크로로 하이드린(Epichloro hydrin) 액상수지로서, 성상의 비스페놀A(Bisphenol A)를 중합시킨 수지이다. 이러한 DGEBA계 에폭시 수지는, 에폭시 당량이 184~194g/eq이고, 25℃에서 점도가 11,000~14,000센티포아즈(CPS)이고, 비중은 200℃에서 1.17~1.19이고, 색상은 1max이고, 염소함유량은 0.1~0.12%max이다.The DGEBA-based epoxy resin is an organic epichloro hydrin liquid resin, and is a resin obtained by polymerizing bisphenol A (Bisphenol A). This DGEBA-based epoxy resin has an epoxy equivalent of 184 to 194 g/eq, a viscosity of 11,000 to 14,000 centipoise (CPS) at 25° C., a specific gravity of 1.17 to 1.19 at 200° C., a color of 1 max, and a chlorine content is 0.1~0.12%max.
상기 경화제는 방수제 조성물의 경화성을 확보하기 위한 것으로서, 바람직하게는 디카르복실산과 디아민류와 중축합에 의해 얻어진 폴리아미드 HO(CORCONH-CH2CH2NH)n일 수 있다. 여기에서, R은 (디카르복실산의 잔기)이고, n은 (2이상의 정수)인 것이며. 이러한 경화제는, 전Amine가 310 내지 330이고, 점도가 25℃에서 500~1,000 센티포아즈(CPS)이고, 산가가 7 미만이고, 색상이 14 미만이다.The curing agent is for securing the curability of the waterproofing agent composition, and preferably, polyamide HO(CORCONH-CH 2 CH 2 NH)n obtained by polycondensation with dicarboxylic acid and diamines may be used. where R is (a residue of a dicarboxylic acid), and n is an integer of 2 or more. This curing agent has a total amine of 310 to 330, a viscosity of 500 to 1,000 centipoise (CPS) at 25° C., an acid value of less than 7, and a color of less than 14.
본 실시 예의 방수제 조성물은, 최종 시공 현장에서, 경량골재와 패각제 및 규산질 시멘트를 혼합하여 배합할 때, DGEBA계 에폭시수지와 경화제를 2:1의 비율로 혼합하여 제조한 후 사용하게 된다.The waterproofing agent composition of this embodiment is used after preparing by mixing the DGEBA-based epoxy resin and the curing agent in a ratio of 2:1 when mixing and mixing the lightweight aggregate, the shell agent, and the siliceous cement at the final construction site.
이와 같이 구성되는 본 발명에 의한 유무기 세라믹 복합 방수제 조성물의 제조방법에 대해 아래의 일 실시 예를 들어 구체적으로 설명하기로 한다.A method of manufacturing the organic-inorganic ceramic composite waterproofing agent composition according to the present invention configured as described above will be described in detail with reference to an example below.
도 1을 참조하면, 본 실시 예의 방수제 조성물을 제조하기 위해서는, 먼저 DGEBA계 에폭시 수지 조성물(S60)을 마련한다.Referring to FIG. 1 , in order to prepare the waterproofing agent composition of this embodiment, first, a DGEBA-based epoxy resin composition (S60) is prepared.
이를 위해, DGEBA계 에폭시 수지 13~30중량부에 대하여, 아크릴산 에스테르(Acrylic Esters) 20~25중량부 및 메타크릴계 스티렌 20~25중량부를 혼합하여 용액 상태에서 스티렌화 된 1차 혼합물을 마련한다(S10).To this end, with respect to 13 to 30 parts by weight of the DGEBA-based epoxy resin, 20 to 25 parts by weight of acrylic esters and 20 to 25 parts by weight of methacrylic styrene are mixed to prepare a styrenated primary mixture in a solution state (S10).
상기 아크릴산 에스테르는 내후성이 우수한 킬복실기와 접착성이 우수한 에폭시기를 가지는데, 이러한 킬복실기와 에폭시기의 혼합에 의한 자기반응으로 방수제 조성물의 내후성, 접착성, 방수성, 내수성 및 내화학성을 향상시키는 역할을 하게 된다.The acrylic acid ester has a killboxyl group with excellent weather resistance and an epoxy group with excellent adhesion, and the self-reaction caused by the mixing of the killboxyl group and the epoxy group serves to improve the weather resistance, adhesion, waterproofness, water resistance and chemical resistance of the waterproofing agent composition. will do
이러한 아크릴산 에스테르가 20중량부 미만이면 상기의 여러가지 특성을 향상시키는 효과가 제대로 구현되지 못하게 되고, 상기 아크릴산 에스테르의 함량이 25중량부를 초과하면 경화지연 문제가 발생할 수 있다.If the amount of the acrylic acid ester is less than 20 parts by weight, the effect of improving the various properties may not be properly implemented, and if the content of the acrylic acid ester exceeds 25 parts by weight, a curing delay problem may occur.
다음으로, 스틴렌화 된 1차 혼합물에 수산기를 가지는 아마인유와 지방산을 추가하고 230℃로 가열하여 에스텔화 된 에스텔화 생성물을 마련한다(S20).Next, linseed oil and fatty acids having a hydroxyl group are added to the styrenated primary mixture and heated to 230° C. to prepare an esterified esterified product (S20).
다음으로, 상기 에스텔화 생성물 200중량부를 방향 탄산화 수용액에 녹인 후, 스티렌 100중량부와 디-t-부틸퍼어 옥사이드 4중량부를 추가하고, 135~140℃에서 3.5~4시간 동안 가열하여 2차 혼합물을 마련한다(S30).Next, after dissolving 200 parts by weight of the esterification product in an aqueous aromatic carbonation solution, 100 parts by weight of styrene and 4 parts by weight of di-t-butylperoxide are added, and the second mixture is heated at 135 to 140° C. for 3.5 to 4 hours. to prepare (S30).
다음으로, 상기 2차 혼합물 100중량부에 대하여 스티렌 50~55중량부를 결합시켜 3차 혼합물을 마련한다(S40). 이때, 상기 3차 혼합물은, 음이온으로 PH가 6.5~7.5이고, 활성분 95~98중량%와 인계면 활성제 2~5중량%로 수용화될 수 있다.Next, 50 to 55 parts by weight of styrene are combined with respect to 100 parts by weight of the secondary mixture to prepare a tertiary mixture (S40). At this time, the tertiary mixture, as an anion, has a pH of 6.5 to 7.5, and may be solubilized with 95 to 98% by weight of active ingredient and 2 to 5% by weight of phosphorus surfactant.
다음으로, 상기 3차 혼합물에 트리클로로실란과 올레핀을 첨가하고 과산화 촉매(45℃)로 반응시켜 알킬실란을 얻는다(S50). 그리고, 상기 알킬실란에 Si-O 결합시켜 얻은 화합물을 증유하면, 반량 이하는 환상인 디메틸실록산이면서 가교 만상화가 일어나는 고분자량의 DGEBA계 에폭시 수지 조성물을 마련할 수 있다(S60).Next, trichlorosilane and olefin are added to the tertiary mixture and reacted with a peroxidation catalyst (45° C.) to obtain alkylsilane (S50). And, if the compound obtained by bonding the Si-O to the alkylsilane is increased, a DGEBA-based epoxy resin composition having a high molecular weight in which crosslinking occurs while half weight is cyclic dimethylsiloxane can be prepared (S60).
이렇게 제조된 본 실시 예의 DGEBA계 에폭시 수지 조성물은 Si-O 결합을 분해하지 않고서는 순수 증유할 수 없는 화합물이므로 후술하는 무기계 조성물과 혼용하여 사용할 수 있다.The DGEBA-based epoxy resin composition of this embodiment prepared in this way is a compound that cannot be pure without decomposing the Si-O bond, so it can be used in combination with an inorganic composition to be described later.
다음으로, 경량골재 100중량부에 대하여 패각제 25~35중량부와 규산질 시멘트 30~35중량부를 혼합한다. 그리고, 앞서 공정을 통해 마련된 DGEBA계 에폭시 수지 조성물과 경화제를 함께 넣고 혼합하여 본 실시 예의 이액형의 방수제 조성물을 제조할 수 있다(S70).Next, 25 to 35 parts by weight of the shell agent and 30 to 35 parts by weight of siliceous cement are mixed with respect to 100 parts by weight of the lightweight aggregate. Then, the DGEBA-based epoxy resin composition prepared through the above process and the curing agent are put together and mixed to prepare the two-component waterproofing agent composition of this embodiment (S70).
또한, 시공을 간편하게 하기 위해서 DGEBA계 에폭시 수지 조성물과 경화제는 별도로 보관하고 운송한 후, 시공시 상기의 경량골재, 패각제 및 규산질 시멘트의 혼합물과의 혼합 공정을 진행할 수 있다.In addition, in order to simplify the construction, the DGEBA-based epoxy resin composition and the curing agent are separately stored and transported, and then the mixing process with the above-mentioned lightweight aggregate, shell agent, and siliceous cement mixture may be performed during construction.
이때, 바람직하게는 경량골재 4.0~6.0중량부에 대하여, 패각제 1.0중량부와 규산질 시멘트 1.0~1.2중량부의 비율로 혼합하고, 여기에 DGEBA계 에폭시 수지 조성물 20~24중량부와 경화제 10~12중량부를 더 포함할 수 있다. At this time, preferably, with respect to 4.0 to 6.0 parts by weight of the lightweight aggregate, 1.0 parts by weight of the shell agent and 1.0 to 1.2 parts by weight of the siliceous cement are mixed, and 20 to 24 parts by weight of the DGEBA-based epoxy resin composition and 10 to 12 parts by weight of the curing agent. It may further include parts by weight.
상기 경량골재는 고온(1,100~1,200℃)에서 소성하는 열처리 공정을 먼저 한 후 사용한다. 이렇게 열처리된 경량골재는 유해물질의 용출이 검출되지 않고, 하부지지 구조의 축소, 철근, 철골 등의 자재 절감이 가능하며, 우수한 단열성 및 내열성을 가진다. 이에 본 실시 예의 방수제 조성물이 에너지 절감형 건축물의 소재로 기능할 수 있도록 하고, 우수한 습도조절 및 흡음성능을 가지도록 할 수 있다.The lightweight aggregate is used after first performing a heat treatment process of firing at a high temperature (1,100 ~ 1,200 ℃). The heat-treated lightweight aggregate does not detect the elution of harmful substances, can reduce the lower support structure, save materials such as reinforcing bars and steel frames, and has excellent thermal insulation and heat resistance. Accordingly, the waterproofing composition of this embodiment can function as a material for an energy-saving building, and can have excellent humidity control and sound absorption performance.
본 실시 예의 열처리된 경량골재는, 바람직하게 SiO2 50~55%, AL2O3 15~19%, Fe2O3 7.10~7.30%, CaO3 18~20%, MgO 1.30~35%, K2O 1.35~1.38%, Na2O 0.8~0.95%, TiO2 0.80~83%, P2O5 1.50~1.60%, B2O2 0.03~0.05%, Cr2O3 0.04~0.05%, V2O5 0.03~0.05%, ZrO2 0.03~0.05%, PbO 0.06~0.08%, MnO 0.10~12%, 무기재 30~45%의 중량비로 이루어질 수 있다.The heat-treated lightweight aggregate of this embodiment is preferably SiO 2 50 to 55%, AL 2 O 3 15 to 19%, Fe 2 O 3 7.10 to 7.30%, CaO 3 18 to 20%, MgO 1.30 to 35%, K 2 O 1.35~1.38%, Na 2 O 0.8~0.95%, TiO 2 0.80~83%, P 2 O 5 1.50~1.60%, B 2 O 2 0.03~0.05%, Cr 2 O 3 0.04~0.05%, V 2 O 5 0.03 to 0.05%, ZrO 2 0.03 to 0.05%, PbO 0.06 to 0.08%, MnO 0.10 to 12%, and may be composed of a weight ratio of 30 to 45% of inorganic material.
그리고, 상기 패각제는 굴 껍질을 수세처리하고 분쇄기로 분쇄한 325메쉬의 분말을 사용할 수 있다. 상기 굴 껍질은 미세다공질의 구조를 가지고 있어 시멘트 제조에 필요한 석회물질인 생석회(CaO)의 원료로 매우 적합하므로, 규산질 시멘트와 혼합하여 사용하기 좋다. 또한, 주성분과 광물상이 천연 석회석과 동일하므로, 건축용 자재에 사용되는 본 발명의 방수제 조성물의 재료로서의 활용 가치가 높다.In addition, the shell agent may use a powder of 325 mesh that is washed with oyster shells and pulverized with a grinder. Since the oyster shell has a microporous structure, it is very suitable as a raw material for quicklime (CaO), a lime material necessary for manufacturing cement, so it is good to mix it with siliceous cement. In addition, since the main component and the mineral phase are the same as that of natural limestone, the utilization value as a material of the waterproofing agent composition of the present invention used for building materials is high.
본 발명의 유무기 세라믹 복합 방수제 조성물은, 상기에서 설명한 조성과 방법으로 제조되어, 콘크리트의 미세 균열 및 모세관 공극 등에 침투 성능이 우수하다. 따라서, 이를 방수공법에 적용함으로 방수제 계면의 결합을 공고히 할 수 있으므로 내투수 저항성을 향상시켜 콘크리트 구조물의 내구성을 향상 시킬 수 있다.The organic-inorganic ceramic composite waterproofing agent composition of the present invention is prepared by the composition and method described above, and has excellent penetration performance in microcracks and capillary pores of concrete. Therefore, by applying this to the waterproofing method, the bond between the waterproofing agent interface can be solidified, so that the permeability resistance can be improved, thereby improving the durability of the concrete structure.
또한, 본 발명에 따른 유무기 세라믹 복합 방수제 조성물은, 건축 구조물 표면에 피복되어 치밀하고 균열방지효과를 제공하고, 우수한 접착성 및 탈락현상, 내수성, 내후성, 내구성으로 외부에서 침투되는 물을 차단하는 효과가 탁월하다.In addition, the organic-inorganic ceramic composite waterproofing composition according to the present invention is coated on the surface of a building structure to provide a dense and crack-preventing effect, and to block water penetrating from the outside with excellent adhesion and drop-off phenomenon, water resistance, weather resistance, and durability The effect is excellent.
이상에서 본 발명의 일 실시 예에 대하여 설명하였지만 본 발명의 권리 범위는 이에 한정되는 것이 아니며, 이외에 다양한 형태로 변형 실시가 가능한 것으로 본 발명의 기술적 사상을 벗어나지 않는 한, 변형되는 실시 예 또한 모두 본 발명의 권리 범위에 속하는 것으로 해석되어야 한다.Although one embodiment of the present invention has been described above, the scope of the present invention is not limited thereto, and as long as it does not depart from the technical spirit of the present invention, the scope of the present invention is not limited thereto. It should be construed as belonging to the scope of the right of the invention.
S10: 1차 혼합물 마련 S20: 에스텔화 생성물 마련
S30: 2차 혼합물 마련 S40: 3차 혼합물 마련
S50: 알칸실란을 얻음 S60: DGEBA계 에폭시 수지 조성물 마련
S70: 재료를 혼합하여 방수세 조성물 제조S10: Prepare the first mixture S20: Prepare the esterification product
S30: Prepare the secondary mixture S40: Prepare the tertiary mixture
S50: Obtained alkanesilane S60: Prepared DGEBA-based epoxy resin composition
S70: Mixing materials to prepare a waterproofing composition
Claims (8)
상기 DGEBA계 에폭시 수지 조성물은,
DGEBA계 에폭시 수지 13~30중량부에 대하여, 아크릴산 에스테르(Acrylic Esters) 20~25중량부 및 메타크릴계 스티렌 20~25중량부를 혼합하여 용액 상태에서 스티렌화 된 1차 혼합물을 마련하는 단계;
스틴렌화 된 1차 혼합물에 수산기를 가지는 아마인유와 지방산을 추가하고 230℃로 가열하여 에스텔화 된 에스텔화 생성물을 마련하는 단계;
상기 에스텔화 생성물 200중량부를 방향 탄산화 수용액에 녹인 후, 스티렌 100중량부와 디-t-부틸퍼어 옥사이드 4중량부를 추가하고, 135~140℃에서 3.5~4시간 동안 가열하여 2차 혼합물을 마련하는 단계;
상기 2차 혼합물 100중량부에 대하여 스티렌 50~55중량부를 결합시켜 3차 혼합물을 마련하는 단계;
상기 3차 혼합물에 트리클로로실란과 올레핀을 첨가하고 과산화 촉매(45℃)로 반응시켜 알킬실란을 얻는 단계; 및
상기 알킬실란에 Si-O 결합시켜 얻은 화합물을 증유하여 반량 이하는 환상인 디메틸실록산이면서 가교 만상화가 일어나는 고분자량의 DGEBA계 에폭시 수지 조성물을 마련하는 단계; 를 포함하는 것을 특징으로 하는 유무기 세라믹 복합 방수제 조성물의 제조방법.Based on 100 parts by weight of the lightweight aggregate, 25 to 35 parts by weight of a shell agent, 30 to 35 parts by weight of siliceous cement, 20 to 24 parts by weight of a DGEBA (Diglycidyl Ether of Bisphenol A)-based epoxy resin composition, and 10 to 12 parts by weight of a hardener, and mix To prepare a two-component waterproofing composition,
The DGEBA-based epoxy resin composition,
Preparing a styrenated primary mixture in a solution state by mixing 20-25 parts by weight of acrylic esters and 20-25 parts by weight of methacrylic styrene with respect to 13-30 parts by weight of the DGEBA-based epoxy resin;
preparing an esterified product by adding linseed oil and fatty acids having a hydroxyl group to the styrenated primary mixture and heating to 230°C;
After dissolving 200 parts by weight of the esterification product in an aromatic carbonation aqueous solution, 100 parts by weight of styrene and 4 parts by weight of di-t-butylper oxide are added, and heated at 135 to 140° C. for 3.5 to 4 hours to prepare a secondary mixture step;
preparing a tertiary mixture by combining 50 to 55 parts by weight of styrene with respect to 100 parts by weight of the secondary mixture;
adding trichlorosilane and olefin to the tertiary mixture and reacting with a peroxidation catalyst (45° C.) to obtain alkylsilane; and
preparing a DGEBA-based epoxy resin composition having a high molecular weight of cyclic dimethylsiloxane with less than half the weight of cyclic dimethylsiloxane by increasing the amount of the compound obtained by bonding Si-O to the alkylsilane; Method for producing an organic-inorganic ceramic composite waterproofing composition comprising a.
상기 경량골재는 유해물질 중금속 검출을 제거 하기 위하여 고온(1,100~1,200℃)에서 선처리 공정으로 열처리를 먼저 한 후 사용하고,
상기 패각제는 병원성 대장균에 강한 살균효과를 나타내는 세라믹스 패각제를 가공 처리하여 불순물을 제거한 수세처리된 325~400메쉬의 패각제 분말을 사용하는 것을 특징으로 하는 유무기 세라믹 복합 방수제 조성물의 제조방법. 6. The method of claim 5,
The lightweight aggregate is used after heat treatment at a high temperature (1,100 ~ 1,200 ° C) in a pre-treatment process to remove the detection of heavy metals from harmful substances,
The shell agent is a method of manufacturing an organic-inorganic ceramic composite waterproofing composition, characterized in that using a 325-400 mesh shell agent powder washed with water to remove impurities by processing a ceramic shell agent that has a strong sterilization effect on pathogenic E. coli.
상기 경화제가, 디카르복실산과 디아민류와 중축합에 의해 얻어진 폴리아미드 HO(CORCONH-CH2CH2NH)n 여기서 R은 (디카르복실산의 잔기)이고, n은 (2이상의 정수), 전Amine가 310~330이고, 점도가 25℃에서 500~1,000센티포아즈(CPS)이고, 산가가 7 미만이고, 색상이 14 미만인 것을 특징으로 하는 유무기 세라믹 복합 방수제 조성물의 제조방법.6. The method of claim 5,
The curing agent is polyamide HO (CORCONH-CH 2 CH 2 NH) n obtained by polycondensation with dicarboxylic acid and diamines, wherein R is (residue of dicarboxylic acid), n is (an integer of 2 or more), A method of producing an organic-inorganic ceramic composite waterproofing composition, characterized in that the total amine is 310 to 330, the viscosity is 500 to 1,000 centipoise (CPS) at 25° C., the acid value is less than 7, and the color is less than 14.