KR102361135B1 - Uniform formed of functional fabric with excellent moisture permeability and strength - Google Patents
Uniform formed of functional fabric with excellent moisture permeability and strength Download PDFInfo
- Publication number
- KR102361135B1 KR102361135B1 KR1020210113594A KR20210113594A KR102361135B1 KR 102361135 B1 KR102361135 B1 KR 102361135B1 KR 1020210113594 A KR1020210113594 A KR 1020210113594A KR 20210113594 A KR20210113594 A KR 20210113594A KR 102361135 B1 KR102361135 B1 KR 102361135B1
- Authority
- KR
- South Korea
- Prior art keywords
- uniform
- moisture
- permeable
- strength
- weight
- Prior art date
Abstract
Description
본 발명은 투습방수성 및 강도가 우수한 기능성 섬유원단으로 형성된 유니폼에 관한 것이다.The present invention relates to a uniform formed of a functional fiber fabric excellent in moisture permeability and waterproofness and strength.
유니폼은 학교나 관청, 회사 따위에서 정하여진 규칙에 따라 입도록 한 옷으로서, 일례로, 교복, 경찰관복, 소방관복, 군복, 위생복, 운동복, 체육복 및 청소복 등이 있다. 이러한 유니폼은 주로 학교 생활 또는 회사 생활 동안 내내 입게 되므로, 외부로부터 쉽게 오염되지 않으며, 반복적으로 세탁해도 옷감이나 옷의 형태가 상하지 않는 등의 특성이 요구된다.Uniforms are clothes made to be worn according to rules set by schools, government offices, companies, etc. For example, there are school uniforms, police uniforms, firefighters uniforms, military uniforms, sanitary clothes, sportswear, gym clothes, and cleaning clothes. Since these uniforms are mainly worn throughout school life or company life, characteristics such as not being easily contaminated from the outside and not damaging the fabric or the shape of clothes even after repeated washing are required.
특히, 이러한 유니폼은 몸으로부터 방출되는 땀과, 외부의 습기에 지속적으로 노출되어 있는데, 땀과 습기 등에 취약할 경우 냄새가 유발되고, 눅눅한 느낌에 의해 불쾌감이 발생되는 문제가 있으며, 이로 인해 반복적인 세탁이 요구됨에 따라 쉽게 손상되는 문제가 있었다. 이에 따라, 유니폼에는 물방울은 통과시키지 않지만 땀 또는 열이나 물방울이 증발되는 수증기와 같은 것을 통과시키는 투습방수성이 필수적으로 요구된다.In particular, these uniforms are continuously exposed to sweat emitted from the body and moisture from the outside. There was a problem in that it is easily damaged as washing is required. Accordingly, although water droplets do not pass through the uniform, moisture permeability and waterproofness through which sweat or heat or water vapor from which water droplets evaporate are essential.
한편, 현재까지 개발된 대부분의 투습방수성 섬유는, 섬유 소재 자체의 특성을 향상시키기 보다는, 섬유 소재의 적층 또는 배치 형태, 섬유 소재의 기공 형성 등을 통해, 투습방수성을 구현하고 있다. 일례로, 대한민국 등록특허 제10-1365027호에서는 의류의 겉감과 안감 사이에 사용되는 투습방수용 섬유 소재로서, 얇게 슬라이싱된 발포성 복수의 판이 적층 구조로 구성되고, 상기 복수의 판 각각에는 다수의 구멍이 형성되고, 적층된 인접 판들의 구멍의 위치는 서로 어긋나도록 한 것을 특징으로 하는 투습방수 기능을 갖는 섬유 소재에 대해 개시하고 있다.On the other hand, most of the moisture-permeable and waterproof fibers developed to date, rather than improving the properties of the fiber material itself, implement the moisture-permeable and waterproof through the lamination or arrangement of the fiber material, the formation of pores in the fiber material, and the like. For example, in Korean Patent Registration No. 10-1365027, as a moisture-permeable and waterproof fiber material used between the outer and lining of clothing, a plurality of thinly sliced foamable plates are configured in a laminated structure, and each of the plurality of plates has a plurality of holes. It is formed, and the position of the holes of the laminated adjacent plates is disclosed for a textile material having a moisture-permeable and waterproof function, characterized in that it is shifted from each other.
그러나, 섬유의 배치 형태 등을 변경하거나, 기공을 형성하는 정도로는 투습방수성을 높은 수준으로 향상시키는 데에 한계가 있었으며, 섬유원단의 제조 과정에 긴 시간이 소요되는 문제가 있었다. 또한, 이러한 경우에는 투습방수성을 향상시키는 것 이외에, 강도, 유연성 향상 등의 효과를 기대하기 어려웠다.However, there was a limit to improving the moisture permeability and waterproofness to a high level to the extent of changing the arrangement of the fibers or forming pores, and there was a problem that the manufacturing process of the textile fabric took a long time. In addition, in this case, in addition to improving moisture permeability and waterproofness, it was difficult to expect effects such as strength and flexibility improvement.
이에 따라, 본 출원인은 공지의 섬유원단 표면에 특정 성분이 조합된 투습방수층을 별도로 형성하여 제조된 것으로서, 간단한 공정으로 단 시간 내에 제조되면서도 투습방수성 및 강도가 현저히 우수한 기능성 섬유원단을 제조하고, 상기 기능성 섬유원단으로 유니폼을 형성함으로써, 종래 문제를 해결하고, 본 발명을 완성하였다.Accordingly, the applicant of the present applicant is manufactured by separately forming a moisture-permeable and waterproof layer in which a specific component is combined on the surface of a known textile fabric, and is manufactured in a short time with a simple process while producing a functional textile fabric that is remarkably excellent in moisture-permeability and waterproofness and strength, By forming a uniform with a functional textile fabric, the conventional problems were solved, and the present invention was completed.
본 발명의 목적은 투습방수성 및 강도가 현저히 우수한 기능성 섬유원단으로 형성된, 유니폼을 제공하는 데에 있다.It is an object of the present invention to provide a uniform, formed of a functional fiber fabric having remarkably excellent moisture permeability and waterproofness and strength.
본 발명의 목적은 상기된 바와 같은 기술적 과제로 한정되지 않으며, 이하의 설명으로부터 또 다른 기술적 과제가 도출될 수 있다. The object of the present invention is not limited to the technical problem as described above, and another technical problem may be derived from the following description.
상기 목적을 달성하기 위하여, 본 발명에서는 섬유 원단; 및 상기 섬유 원단 일면 또는 양면에 형성되는 투습방수층;을 포함하는 기능성 섬유원단으로 형성된 유니폼에 관한 것으로, 상기 투습방수층은 열가소성 폴리우레탄 수지, 기공 형성 파우더, 전분 파우더, 소듐코코일글루타메이트, 소듐코코일이세티오네이트 및 폴리에틸렌글리콜을 포함하는 투습방수 조성물로 형성된 코팅층인, 투습방수성 및 강도가 우수한 기능성 섬유원단으로 형성된 유니폼을 제공한다.In order to achieve the above object, in the present invention, a textile fabric; And a moisture-permeable and waterproof layer formed on one or both surfaces of the textile fabric; relates to a uniform formed of a functional fiber fabric comprising a, wherein the moisture-permeable and waterproof layer is a thermoplastic polyurethane resin, pore-forming powder, starch powder, sodium cocoyl glutamate, sodium cocoil It provides a uniform formed of a moisture-permeable and waterproof composition containing isethionate and polyethylene glycol, a coating layer formed of a functional fiber fabric having excellent moisture-permeable waterproofness and strength.
상기 투습방수층은 상기 열가소성 폴리우레탄 수지 100 중량부에 대해, 상기 기공 형성 파우더 5 ~ 10 중량부, 상기 전분 파우더 7 ~ 15 중량부, 상기 소듐코코일글루타메이트 0.1 ~ 1 중량부, 상기 소듐코코일이세티오네이트 0.1 ~ 1 중량부 및 상기 폴리에틸렌글리콜 3 ~ 6 중량부를 포함할 수 있다.The moisture-permeable waterproof layer is based on 100 parts by weight of the thermoplastic polyurethane resin, 5 to 10 parts by weight of the pore-forming powder, 7 to 15 parts by weight of the starch powder, 0.1 to 1 parts by weight of the sodium cocoyl glutamate, the sodium cocoil It may include 0.1 to 1 parts by weight of cetionate and 3 to 6 parts by weight of the polyethylene glycol.
상기 기공 형성 파우더는 친수성 침강(precipitated) 실리카, 키틴(chitin), 알부민(albumin), 셀룰로오스(cellulose) 및 울(wool)을 포함할 수 있다.The pore-forming powder may include hydrophilic precipitated silica, chitin, albumin, cellulose, and wool.
상기 기공 형성 파우더는 평균 입경이 20 ~ 30 ㎛ 인 것일 수 있다.The pore-forming powder may have an average particle diameter of 20 to 30 μm.
상기 전분 파우더는 소듐카르복시메틸스타치 및 히드록시프로필스타치를 포함할 수 있다.The starch powder may include sodium carboxymethyl starch and hydroxypropyl starch.
상기 전분 파우더는 평균 입경이 30 ~ 40 mesh 일 수 있다.The starch powder may have an average particle diameter of 30 to 40 mesh.
상기 유니폼은 교복, 경찰관복, 소방관복, 군복, 위생복, 운동복, 체육복 및 청소복으로 이루어진 군에서 선택되는 어느 하나인 것일 수 있다. The uniform may be any one selected from the group consisting of a school uniform, a police uniform, a firefighter uniform, a military uniform, a sanitary uniform, a sportswear, a gym suit, and a cleaning suit.
본 발명의 유니폼은 공지의 섬유원단 및 상기 섬유원단의 일면 또는 양면에 형성된 투습방수층을 포함하는 기능성 섬유원단으로 형성됨에 따라, 투습방수 효과가 우수하면서도 강도가 우수하여, 장시간 사용하여도 냄새 및 불쾌감이 없고, 수명이 우수할 수 있다.The uniform of the present invention is formed of a known textile fabric and a functional textile fabric including a moisture-permeable and waterproof layer formed on one or both sides of the textile fabric. There is no such thing, and the lifespan may be excellent.
또한, 상기 섬유원단과 투습방수층의 부착성이 우수함에 따라, 상기 기능성 섬유원단으로 형성된 유니폼은 우수한 투습방수성 및 강도를 장시간 동안 유지할 수 있고, 세탁 내구성이 우수할 수 있다.In addition, as the adhesion between the textile fabric and the moisture-permeable waterproof layer is excellent, the uniform formed of the functional textile fabric can maintain excellent moisture-permeability and waterproofness and strength for a long time, and can have excellent washing durability.
아래에서는 첨부한 도면을 참조하여 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 실시예를 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다. 그리고 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings so that those of ordinary skill in the art can easily implement them. However, the present invention may be embodied in several different forms and is not limited to the embodiments described herein. And in order to clearly explain the present invention in the drawings, parts irrelevant to the description are omitted.
본 발명의 명세서 및 청구범위에 사용된 용어 또는 단어는 통상적이거나 사전적인 의미로 한정 해석되지 아니하며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.The terms or words used in the specification and claims of the present invention are not to be construed as limited in their ordinary or dictionary meanings, and the inventor can appropriately define the concept of the term in order to best describe his invention. Based on the principle, it should be interpreted as meaning and concept consistent with the technical idea of the present invention.
본 발명의 명세서 전체에 있어서, 어떤 부분이 어떤 구성 요소를 "포함" 한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성 요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것을 의미한다. In the entire specification of the present invention, when a part "includes" a component, it means that other components may be further included, rather than excluding other components, unless otherwise stated. .
본 발명의 명세서 전체에 있어서, "A 및/또는 B"는, A 또는 B, 또는 A 및 B를 의미한다.Throughout the specification of the present invention, "A and/or B" means A or B, or A and B.
이하에서 본 발명을 구체적으로 설명하였으나, 본 발명이 이에 제한되는 것은 아니다.Although the present invention has been specifically described below, the present invention is not limited thereto.
본 발명에서는 투습방수성 및 강도가 우수한 기능성 섬유원단으로 형성된 유니폼을 제공한다.The present invention provides a uniform formed of a functional fiber fabric excellent in moisture permeability and waterproofness and strength.
본 발명의 일 실시예에서는 섬유 원단; 및 상기 섬유 원단 일면 또는 양면에 형성되는 투습방수층;을 포함하되, 상기 투습방수층은 열가소성 폴리우레탄 수지, 기공 형성 파우더, 전분 파우더, 소듐코코일글루타메이트, 소듐코코일이세티오네이트 및 폴리에틸렌글리콜을 포함하는 투습방수 조성물로 형성된 코팅층인 투습방수층;을 포함하는 기능성 섬유원단으로 형성된 유니폼을 제공한다.In one embodiment of the present invention, a textile fabric; and a moisture-permeable and waterproof layer formed on one or both surfaces of the textile fabric, wherein the moisture-permeable and waterproof layer includes a thermoplastic polyurethane resin, pore-forming powder, starch powder, sodium cocoyl glutamate, sodium cocoyl ethionate and polyethylene glycol It provides a uniform formed of a functional fiber fabric comprising; a moisture-permeable waterproof layer that is a coating layer formed of a moisture-permeable and waterproof composition.
구체적으로, 본 실시예의 기능성 섬유원단은 투습방수 효과가 우수하여 장시간 사용하여도 냄새 및 불쾌감이 없고, 강도가 우수하여 수명이 우수할 수 있다. 뿐만 아니라, 본 실시예의 기능성 섬유원단은, 상기 섬유원단과 투습방수층의 부착성이 우수함에 따라, 우수한 투습방수성 및 강도를 장시간 동안 유지할 수 있고, 세탁 내구성이 우수할 수 있다.Specifically, the functional fiber fabric of this embodiment has excellent moisture-permeable and waterproof effect, so there is no smell and unpleasant feeling even after using it for a long time, and it has excellent strength and thus a lifespan can be excellent. In addition, the functional textile fabric of this embodiment has excellent adhesion between the textile fabric and the moisture-permeable and waterproof layer, so it can maintain excellent moisture-permeable waterproofness and strength for a long time, and has excellent washing durability.
즉, 상기 기능성 섬유원단으로 형성된 유니폼은 투습방수성 및 강도가 우수하면서도 세탁 내구성 및 수명이 현저히 우수할 수 있다.That is, the uniform formed of the functional fiber fabric can be excellent in moisture permeability and waterproofness and strength, while also being remarkably excellent in washing durability and lifespan.
상기 섬유원단은 공지의 모든 성분 및 형태의 섬유를 가공하여 원단 형태로 만든 것이라면, 특별히 제한되지 않는다. 구체적으로, 본 실시예의 섬유원단은 폴리에스테르 섬유, 폴리프로필렌 섬유, 폴리에틸렌 섬유, 폴리아마이드 섬유, 폴리우레탄 섬유 및 폴리스티렌 섬유로 이루어진 군에서 선택되는 하나 이상을 포함하는 섬유를 직조하여 형성된 것일 수 있으나, 이에 제한되지 않는다.The fiber fabric is not particularly limited as long as it is made in the form of a fabric by processing all known components and fibers. Specifically, the fiber fabric of this embodiment may be formed by weaving a fiber including at least one selected from the group consisting of polyester fiber, polypropylene fiber, polyethylene fiber, polyamide fiber, polyurethane fiber and polystyrene fiber, It is not limited thereto.
본 실시예의 섬유원단의 두께는 1 마이크로미터 ~ 1,000 마이크로미터일 수 있으나, 이에 제한되지 않는다.The thickness of the textile fabric of this embodiment may be 1 micrometer to 1,000 micrometers, but is not limited thereto.
상기 투습방수층은 열가소성 폴리우레탄 수지, 기공 형성 파우더, 전분 파우더, 소듐코코일글루타메이트, 소듐코코일이세티오네이트 및 폴리에틸렌글리콜을 포함하는 투습방수 조성물로 형성된 코팅층을 의미한다. 예를 들어, 상기 코팅층은, 상기 섬유원단에 상기 투습방수 조성물을 도포하여 경화시킴으로써 형성되거나, 상기 투습방수 조성물을 공지의 방법에 따라 필름으로 형성한 뒤, 이를 특정 온도 및 압력 조건에서 상기 섬유원단에 부착시킴으로써 형성될 수 있으나, 이에 제한되지 않는다.The moisture-permeable waterproof layer means a coating layer formed of a moisture-permeable waterproof composition comprising a thermoplastic polyurethane resin, pore-forming powder, starch powder, sodium cocoyl glutamate, sodium cocoyl ethionate and polyethylene glycol. For example, the coating layer is formed by applying and curing the moisture-permeable waterproof composition to the textile fabric, or after forming the moisture-permeable waterproof composition into a film according to a known method, it is the textile fabric under specific temperature and pressure conditions It may be formed by attaching to the , but is not limited thereto.
이하에서는 상기 투습방수 조성물에 상세히 설명하도록 하겠다.Hereinafter, the moisture-permeable waterproof composition will be described in detail.
본 실시예의 투습방수 조성물은 열가소성 폴리우레탄 수지를 포함한다.The moisture-permeable waterproof composition of this embodiment includes a thermoplastic polyurethane resin.
상기 열가소성 폴리우레탄 수지는 열로 녹여 제작됨으로써 압출, 진공 성형, 열접착, 고주파 가공 등에 사용이 가능하며, 내유성, 내마모성이 있고, 적정 수준의 탄성을 가지며, 단열 특성을 가질 수 있다. 즉, 본 실시예의 투습방수 조성물이 열가소성 폴리우레탄 수지를 포함함으로써, 본 실시예의 유니폼은 유연성, 회복성 및 단열성 등의 특성을 구현할 수 있다.The thermoplastic polyurethane resin is manufactured by melting with heat, so that it can be used for extrusion, vacuum molding, thermal bonding, high-frequency processing, etc., and has oil resistance, abrasion resistance, an appropriate level of elasticity, and thermal insulation properties. That is, since the moisture-permeable waterproof composition of this embodiment includes a thermoplastic polyurethane resin, the uniform of this embodiment can implement characteristics such as flexibility, recovery and heat insulation.
상기 열가소성 폴리우레탄 수지는 공지의 모든 열가소성 폴리우레탄 수지를 포함할 수 있다.The thermoplastic polyurethane resin may include all known thermoplastic polyurethane resins.
본 실시예의 투습방수 조성물은 기공 형성 파우더를 포함한다.The moisture-permeable waterproof composition of this embodiment includes a pore-forming powder.
상기 기공 형성 파우더는 상기 투습방수 조성물로 형성되는 코팅층에 기공을 형성하여 투습성 및 방수성이 동시에 구현되도록 할 수 있으며, 상기 섬유원단의 강도를 향상시키는 역할을 할 수 있다.The pore-forming powder can form pores in the coating layer formed of the moisture-permeable and waterproof composition so that moisture permeability and waterproofness can be realized at the same time, and can serve to improve the strength of the textile fabric.
본 실시예의 기공 형성 파우더는 친수성 침강(precipitated) 실리카, 키틴(chitin), 알부민(albumin), 셀룰로오스(cellulose) 및 울(wool)을 포함할 수 있다. 본 실시예에 따라, 상기 기공 형성 파우더로 친수성 침강 실리카, 키틴, 알부민, 셀룰로오스 및 울을 모두 포함할 때, 본 실시예에 따르는 기능성 섬유원단의 투습방수성, 강도, 세탁 내구성이 우수하고, 섬유원단과 투습방수층의 부착성이 우수할 수 있다.The pore-forming powder of this embodiment may include hydrophilic precipitated silica, chitin, albumin, cellulose, and wool. According to this embodiment, when hydrophilic precipitated silica, chitin, albumin, cellulose and wool are all included as the pore-forming powder, the functional textile fabric according to this embodiment has excellent moisture permeability and waterproofness, strength, and washing durability. The adhesion of the moisture-permeable and waterproof layer may be excellent.
구체적으로, 본 실시예의 기공 형성 파우더는 친수성 침강 실리카, 키틴, 알부민, 셀룰로오스 및 울을 9 ~ 10 : 1 ~ 2 : 1 ~ 2 : 1 ~ 2 : 1 의 중량비로 포함할 수 있으며, 이 경우, 본 실시예에 따르는 기능성 섬유원단의 투습방수성, 강도, 세탁 내구성은 더욱 향상되며, 섬유원단과 투습방수층의 부착성 또한 우수할 수 있다.Specifically, the pore-forming powder of this embodiment may include hydrophilic precipitated silica, chitin, albumin, cellulose and wool in a weight ratio of 9 to 10: 1 to 2: 1 to 2: 1 to 2: 1, in this case, The moisture-permeable waterproofness, strength, and washing durability of the functional textile fabric according to this embodiment are further improved, and the adhesion between the textile fabric and the moisture-permeable waterproof layer may also be excellent.
본 실시예의 기공 형성 파우더는 평균 입경이 20 ~ 30 ㎛, 구체적으로는 25 ~ 30 ㎛ 인 것일 수 있으며, 이 경우, 본 실시예의 기능성 섬유원단의 투습방수성, 강도, 세탁 내구성 및 부착성은 더욱 향상될 수 있다.The pore-forming powder of this embodiment may have an average particle diameter of 20 to 30 µm, specifically 25 to 30 µm, in this case, the moisture permeability, strength, washing durability and adhesion of the functional textile fabric of this embodiment will be further improved. can
만약, 본 실시예의 기공 형성 파우더의 평균 입경이 20 ㎛ 미만일 경우에는, 상기 기공 형성 파우더 간의 응집이 발생될 수 있고, 상기 기공 형성 파우더에 의해 형성된 기공이 미세하여, 투습방수성이 저하될 수 있으며, 섬유원단에 대한 투습방수층의 부착성이 저하될 수 있다. 반면, 본 실시예의 기공 형성 파우더의 평균 입경이 30 ㎛ 초과일 경우에는, 섬유원단에 대한 투습방수층의 부착성이 저하되고, 상기 기공 형성 파우더에 의해 형성된 기공이 커, 방수 성능이 현저히 저하될 수 있다.If the average particle diameter of the pore-forming powder of this embodiment is less than 20 μm, agglomeration may occur between the pore-forming powders, and the pores formed by the pore-forming powder are fine, and moisture permeability and waterproofness may be reduced, The adhesion of the moisture-permeable waterproof layer to the textile fabric may be reduced. On the other hand, when the average particle diameter of the pore-forming powder of this embodiment is more than 30 μm, the adhesion of the moisture-permeable waterproof layer to the textile fabric is lowered, the pores formed by the pore-forming powder are large, and the waterproof performance can be significantly reduced. have.
본 실시예의 투습방수 조성물은 상기 열가소성 폴리우레탄 수지 100 중량부에 대해 상기 기공 형성 파우더를 5 ~ 10 중량부, 구체적으로 6 ~ 9 중량부로 포함할 수 있다.The moisture-permeable waterproof composition of this embodiment may include 5 to 10 parts by weight of the pore-forming powder, specifically 6 to 9 parts by weight, based on 100 parts by weight of the thermoplastic polyurethane resin.
만약, 본 실시예의 투습방수 조성물이 상기 열가소성 폴리우레탄 수지 100 중량부에 대해 상기 기공 형성 파우더를 5 중량부 미만으로 포함할 경우에는, 기능성 섬유원단의 투습방수성, 강도가 저하될 수 있다. 반면, 본 실시예의 투습방수 조성물이 상기 열가소성 폴리우레탄 수지 100 중량부에 대해 상기 기공 형성 파우더를 10 중량부 초과로 포함할 경우에는, 섬유원단과 투습방수층의 부착성이 저하되고, 투습방수성이 저하될 수 있다.If the moisture-permeable and waterproof composition of this embodiment contains less than 5 parts by weight of the pore-forming powder with respect to 100 parts by weight of the thermoplastic polyurethane resin, the moisture-permeable waterproofness and strength of the functional textile fabric may be reduced. On the other hand, when the moisture-permeable waterproof composition of this embodiment contains more than 10 parts by weight of the pore-forming powder with respect to 100 parts by weight of the thermoplastic polyurethane resin, the adhesion between the textile fabric and the moisture-permeable waterproof layer is reduced, and the moisture-permeable waterproofness is lowered can be
본 실시예의 투습방수 조성물은 전분 파우더를 포함한다.The moisture-permeable and waterproof composition of this embodiment includes starch powder.
상기 전분 파우더는 상기 기능성 섬유원단의 강도를 높이면서도 유연하게 하며, 계면활성 효과를 구현하여 각 성분들이 균일하게 혼합된 도막 형태의 투습방수층을 형성하도록 할 수 있다. The starch powder increases the strength and flexibility of the functional textile fabric, and implements a surfactant effect to form a moisture-permeable waterproof layer in the form of a coating film in which each component is uniformly mixed.
구체적으로, 본 실시예의 전분 파우더는 소듐카르복시메틸스타치 및 히드록시프로필스타치를 포함할 수 있으며, 상기 두 종류의 전분 유도체를 모두 포함함으로써, 상기 두 종류의 전분 유도체 중 하나를 포함하는 경우 보다, 본 실시예의 기능성 섬유원단은 강도가 좋으면서도 유연할 수 있다.Specifically, the starch powder of this embodiment may include sodium carboxymethyl starch and hydroxypropyl starch, and by including both types of starch derivatives, compared to the case of including one of the two types of starch derivatives, The functional fiber fabric of this embodiment may have good strength and flexibility.
더 구체적으로, 본 실시예의 전분 파우더는 소듐카르복시메틸스타치 및 히드록시프로필스타치를 1 : 5 ~ 9 의 중량비로 포함할 수 있으며, 이 경우, 본 실시예의 기능성 섬유원단의 투습방수성, 강도, 세탁 내구성 및 부착성은 더욱 향상될 수 있다.More specifically, the starch powder of this embodiment may include sodium carboxymethyl starch and hydroxypropyl starch in a weight ratio of 1: 5 to 9, and in this case, the moisture permeability and waterproofness, strength, and washing of the functional textile fabric of this embodiment. Durability and adhesion can be further improved.
가장 구체적으로, 본 실시예의 전분 파우더는 소듐카르복시메틸스타치 및 히드록시프로필스타치를 1 : 6 ~ 8 의 중량비로 포함할 수 있으며, 이 경우, 본 실시예의 기능성 섬유원단의 투습방수성, 강도, 세탁 내구성 및 부착성은 현저히 우수할 수 있다.Most specifically, the starch powder of this embodiment may include sodium carboxymethyl starch and hydroxypropyl starch in a weight ratio of 1: 6 to 8, and in this case, the moisture permeability and waterproofness, strength, and washing properties of the functional textile fabric of this embodiment. Durability and adhesion may be remarkably excellent.
본 실시예의 전분 파우더는 평균 입경이 30 ~ 40 mesh 일 수 있다. 특히, 본 실시예에서는 기공 형성 파우더 보다, 전분 파우더의 입경을 더욱 크게 함으로써, 기공 형성 파우더에 의해 형성된 기공이 전분 파우더에 의해 막히는 현상을 방지할 수 있다.The starch powder of this embodiment may have an average particle diameter of 30 to 40 mesh. In particular, in this embodiment, by making the particle size of the starch powder larger than that of the pore-forming powder, it is possible to prevent the pores formed by the pore-forming powder from being blocked by the starch powder.
본 실시예의 투습방수 조성물은 상기 열가소성 폴리우레탄 수지 100 중량부에 대해 상기 전분 파우더 7 ~ 15 중량부, 구체적으로는 10 ~ 12 중량부로 포함할 수 있다.The moisture-permeable waterproof composition of this embodiment may include 7 to 15 parts by weight of the starch powder, specifically 10 to 12 parts by weight, based on 100 parts by weight of the thermoplastic polyurethane resin.
만약, 본 실시예의 투습방수 조성물이 상기 열가소성 폴리우레탄 수지 100 중량부에 대해 상기 전분 파우더를 7 중량부 미만으로 포함할 경우에는, 기능성 섬유원단의 강도 및 유연성이 저하될 수 있다. 반면, 본 실시예의 투습방수 조성물이 상기 열가소성 폴리우레탄 수지 100 중량부에 대해 상기 전분 파우더를 15 중량부 초과로 포함할 경우에는, 섬유원단과 투습방수층의 부착성이 저하되고, 투습방수성 및 세탁 내구성이 저하될 수 있다.If the moisture-permeable waterproof composition of this embodiment contains less than 7 parts by weight of the starch powder based on 100 parts by weight of the thermoplastic polyurethane resin, the strength and flexibility of the functional fiber fabric may be reduced. On the other hand, when the moisture-permeable and waterproof composition of this embodiment contains more than 15 parts by weight of the starch powder with respect to 100 parts by weight of the thermoplastic polyurethane resin, the adhesion between the textile fabric and the moisture-permeable waterproof layer is reduced, moisture-permeable waterproofness and washing durability This may be lowered.
본 실시예의 투습방수 조성물은 소듐코코일글루타메이트를 포함한다.The moisture-permeable waterproof composition of this embodiment contains sodium cocoyl glutamate.
상기 소듐코코일글루타메이트는 상기 투습방수 조성물의 분산성을 높이고, 각 성분들의 혼용을 도울 수 있다. 뿐만 아니라, 상기 소듐코코일글루타메이트는 투습방수층 표면을 친수화시켜, 땀이나 수증기가 표면에 결로되는 현상을 최소화하여, 투습방수 효과를 극대화시킬 수 있다.The sodium cocoyl glutamate may increase the dispersibility of the moisture-permeable and waterproof composition, and may help mixing of each component. In addition, the sodium cocoyl glutamate hydrophilicizes the surface of the moisture-permeable waterproofing layer, thereby minimizing the phenomenon of sweat or water vapor condensing on the surface, thereby maximizing the moisture-permeable waterproofing effect.
본 실시예의 투습방수 조성물은 상기 열가소성 폴리우레탄 수지 100 중량부에 대해 상기 소듐코코일글루타메이트 0.1 ~ 1 중량부, 구체적으로는 0.5 ~ 0. 7 중량부를 포함할 수 있다.The moisture-permeable waterproof composition of this embodiment may contain 0.1 to 1 parts by weight of sodium cocoyl glutamate, specifically 0.5 to 0.7 parts by weight, based on 100 parts by weight of the thermoplastic polyurethane resin.
만약, 본 실시예의 투습방수 조성물이 상기 열가소성 폴리우레탄 수지 100 중량부에 대해 상기 소듐코코일글루타메이트를 0.1 중량부 미만으로 포함할 경우, 분산성 및 각 성분의 혼용성이 저하되어 전반적인 성능이 저하될 수 있다. 반면, 본 실시예의 투습방수 조성물이 상기 열가소성 폴리우레탄 수지 100 중량부에 대해 상기 소듐코코일글루타메이트를 1 중량부 초과로 포함할 경우, 강도 및 세탁 내구성이 저하될 수 있다. If the moisture-permeable waterproof composition of this embodiment contains less than 0.1 parts by weight of sodium cocoyl glutamate with respect to 100 parts by weight of the thermoplastic polyurethane resin, dispersibility and miscibility of each component are lowered, so that the overall performance will be lowered. can On the other hand, when the moisture-permeable waterproof composition of this embodiment contains more than 1 part by weight of sodium cocoyl glutamate based on 100 parts by weight of the thermoplastic polyurethane resin, strength and washing durability may be reduced.
본 실시예의 투습방수 조성물은 소듐코코일이세티오네이트를 포함한다.The moisture-permeable and waterproof composition of this embodiment includes sodium cocoyl ethionate.
상기 소듐코코일이세티오네이트는 상기 소듐코코일글루타메이트와 함께, 상기 투습방수 조성물의 분산성을 높이고, 각 성분들의 혼용을 도울 수 있다. 뿐만 아니라, 상기 소듐코코일이세티오네이트는 투습방수층 표면을 친수화시켜, 땀이나 수증기가 표면에 결로되는 현상을 최소화하여, 투습방수 효과를 극대화시킬 수 있다.The sodium cocoyl ethionate, together with the sodium cocoyl glutamate, increases the dispersibility of the moisture-permeable and waterproof composition, and may help mixing of each component. In addition, the sodium cocoyl ethionate hydrophilicizes the surface of the moisture-permeable waterproofing layer, thereby minimizing the phenomenon of sweat or water vapor condensing on the surface, thereby maximizing the moisture-permeable waterproofing effect.
본 실시예의 투습방수 조성물은 상기 열가소성 폴리우레탄 수지 100 중량부에 대해 상기 소듐코코일이세티오네이트 0.1 ~ 1 중량부, 구체적으로는 0.2 ~ 0.5 중량부를 포함할 수 있다.The moisture-permeable waterproof composition of this embodiment may include 0.1 to 1 parts by weight of sodium cocoyl ethionate, specifically 0.2 to 0.5 parts by weight, based on 100 parts by weight of the thermoplastic polyurethane resin.
만약, 본 실시예의 투습방수 조성물이 상기 열가소성 폴리우레탄 수지 100 중량부에 대해 상기 소듐코코일이세티오네이트를 0.1 중량부 미만으로 포함할 경우, 분산성 및 각 성분의 혼용성이 저하되어 전반적인 성능이 저하될 수 있다. 반면, 본 실시예의 투습방수 조성물이 상기 열가소성 폴리우레탄 수지 100 중량부에 대해 상기 소듐코코일이세티오네이트를 1 중량부 초과로 포함할 경우, 강도 및 세탁 내구성이 저하될 수 있다.If the moisture-permeable waterproof composition of this embodiment contains less than 0.1 parts by weight of sodium cocoyl ethionate based on 100 parts by weight of the thermoplastic polyurethane resin, dispersibility and compatibility of each component are lowered to reduce overall performance This may be lowered. On the other hand, when the moisture-permeable waterproof composition of this embodiment contains more than 1 part by weight of sodium cocoylethionate based on 100 parts by weight of the thermoplastic polyurethane resin, strength and washing durability may be reduced.
본 실시예의 투습방수 조성물은 폴리에틸렌글리콜을 포함한다.The moisture-permeable waterproof composition of this embodiment contains polyethylene glycol.
상기 폴리에틸렌글리콜은 친수성이 좋아, 투습성을 향상시키는 역할을 할 수 있다. The polyethylene glycol has good hydrophilicity, and may serve to improve moisture permeability.
본 실시예의 투습방수 조성물은 상기 열가소성 폴리우레탄 수지 100 중량부에 대해 상기 폴리에틸렌글리콜 3 ~ 6 중량부, 구체적으로는 4 ~ 5 중량부를 포함할 수 있다.The moisture-permeable waterproof composition of this embodiment may include 3 to 6 parts by weight of the polyethylene glycol, specifically 4 to 5 parts by weight, based on 100 parts by weight of the thermoplastic polyurethane resin.
만약, 본 실시예의 투습방수 조성물이 상기 열가소성 폴리우레탄 수지 100 중량부에 대해 상기 폴리에틸렌글리콜을 3 중량부 미만으로 포함할 경우, 투습성의 향상 정도가 미미할 수 있다. 반면, 본 실시예의 투습방수 조성물이 상기 열가소성 폴리우레탄 수지 100 중량부에 대해 상기 폴리에틸렌글리콜을 6 중량부 초과로 포함할 경우, 방수성이 저하되고, 세탁 내구성 및 강도가 저하될 수 있다.If the moisture-permeable waterproof composition of this embodiment contains less than 3 parts by weight of the polyethylene glycol based on 100 parts by weight of the thermoplastic polyurethane resin, the degree of improvement in moisture permeability may be insignificant. On the other hand, when the moisture-permeable waterproof composition of this embodiment contains more than 6 parts by weight of the polyethylene glycol with respect to 100 parts by weight of the thermoplastic polyurethane resin, waterproofness may be reduced, and washing durability and strength may be reduced.
상기 투습방수 조성물은 상기된 성분 이외에 공지의 첨가제를 포함할 수 있다. 예를 들어, 상기 첨가제는 유화제, 유화안정제, 보조 계면활성제, 유기용매, 소포제, 색소, 안료, 염료, 분산제, 산화방지제, 노화방지제, 정전기 방지제, 유연화제 등을 포함할 수 있으나, 이에 제한되지 않는다.The moisture-permeable waterproof composition may include known additives in addition to the above-described components. For example, the additive may include, but is not limited to, an emulsifier, an emulsion stabilizer, an auxiliary surfactant, an organic solvent, an antifoaming agent, a pigment, a pigment, a dye, a dispersant, an antioxidant, an antioxidant, an antistatic agent, a softener, etc. does not
또한, 본 실시예에서는 상기 기능성 섬유원단으로 형성된 유니폼을 제공한다. 상기 유니폼은 교복, 경찰관복, 소방관복, 군복, 위생복, 운동복, 체육복 및 청소복으로 이루어진 군에서 선택되는 어느 하나인 것일 수 있다.In addition, this embodiment provides a uniform formed of the functional fiber fabric. The uniform may be any one selected from the group consisting of a school uniform, a police uniform, a firefighter uniform, a military uniform, a sanitary uniform, a sportswear, a gym suit, and a cleaning suit.
본 실시예의 유니폼은 상기 기능성 섬유원단으로 형성됨으로써, 투습방수성, 강도 및 세탁 내구성이 우수하여, 사용 수명이 향상될 수 있다. 뿐만 아니라, 투습방수성이 우수하여 사용 시 쾌적하며, 강도가 우수하여 외부 외력에 의해 쉽게 손상되지 않을 수 있다.The uniform of this embodiment is formed of the functional fiber fabric, and thus has excellent moisture permeability and waterproofness, strength and washing durability, so that the service life can be improved. In addition, it is comfortable to use due to its excellent moisture permeability and waterproofness, and it may not be easily damaged by external external forces due to its excellent strength.
이하 실시예, 비교예, 및 실험예를 통하여 본 발명의 투습방수성 및 강도가 우수한 기능성 섬유원단으로 형성된 유니폼에 대해 구체적으로 설명하기로 한다. 이들 실시예는 단지 본 발명을 예시하기 위한 것이므로, 본 발명의 범위가 이들 실시예에 의해 제한되는 것으로 해석되지는 않는다.Hereinafter, through Examples, Comparative Examples, and Experimental Examples, the uniform formed of the functional fiber fabric having excellent moisture permeability, waterproofness and strength of the present invention will be described in detail. These examples are only for illustrating the present invention, and therefore, the scope of the present invention is not to be construed as being limited by these examples.
[ 실시예 ][Example]
실시예 1Example 1
폴리에스테르 섬유를 직조하여 제조된 섬유원단의 양면에, 표 1[단위 : 중량부]에 따르는 투습방수 조성물로 형성된 접착필름을 적층하고, 열 융착시켜, 투습방수층이 형성된, 기능성 섬유 원단을 제조하였다.On both sides of the textile fabric manufactured by weaving polyester fibers, an adhesive film formed of a moisture-permeable and waterproof composition according to Table 1 [unit: parts by weight] was laminated and heat-sealed to form a moisture-permeable waterproof layer, a functional fiber fabric was prepared .
구체적으로, 상기 투습방수 조성물을 펠레타이징한 수지를 압출하여, 50 ㎛(평균 두께)로 성형하여 접착필름를 준비하고, 섬유원단에 접착필름을 적층한 후 160℃에서 열융착하여, 폴리에스테르 섬유를 직조하여 제조된 섬유원단의 양면에 투습방수층이 형성된, 기능성 섬유원단을 제조하였다.Specifically, the moisture-permeable waterproof composition is extruded from the pelletized resin, molded to 50 μm (average thickness) to prepare an adhesive film, and the adhesive film is laminated on the fiber fabric and then heat-sealed at 160° C., polyester fiber A functional fiber fabric was prepared in which moisture-permeable and waterproof layers were formed on both sides of the fabric fabric manufactured by weaving it.
상기 표 1에서, 상기 기공 형성 파우더는 친수성 침강 실리카, 키틴, 알부민, 셀룰로오스 및 울이 9 : 1 : 2 : 2 : 1 의 중량비로 혼합된 것을 사용하였으며, 평균 입경이 25 ~ 30 ㎛ 인 것을 사용하였다. 또한, 상기 전분 파우더는 소듐카르복시메틸스타치 및 히드록시프로필스타치가 1 : 8 의 중량비로 혼합된 것을 사용하였으며, 평균 입경이 30 ~ 40 mesh 인 것을 사용하였다.In Table 1, the pore-forming powder used was a mixture of hydrophilic precipitated silica, chitin, albumin, cellulose and wool in a weight ratio of 9: 1: 2: 2: 1, and an average particle diameter of 25 to 30 μm was used. did In addition, as the starch powder, a mixture of sodium carboxymethyl starch and hydroxypropyl starch in a weight ratio of 1:8 was used, and an average particle diameter of 30 to 40 mesh was used.
실시예 2 내지 3Examples 2-3
투습방수 조성물에서, 기공 형성 파우더로 표 2[단위 : 중량비]에 따라 각 성분이 혼합된 것을 사용한 것을 제외하고는, 실시예 1과 동일하게 실시하였다. 이때, 표 2에, 실시예 1의 기공 형성 파우더를 구성하는 각 성분의 중량비도 함께 나타내었다.In the moisture-permeable waterproof composition, it was carried out in the same manner as in Example 1, except that each component was mixed according to Table 2 [unit: weight ratio] as the pore-forming powder. At this time, in Table 2, the weight ratio of each component constituting the pore-forming powder of Example 1 is also shown.
실시예 4 내지 7Examples 4 to 7
투습방수 조성물에서, 전분 파우더로 표 3[단위 : 중량비]에 따라 각 성분이 혼합된 것을 사용한 것을 제외하고는, 실시예 1과 동일하게 실시하였다. 이때, 표 2에, 실시예 1의 전분 파우더를 구성하는 각 성분의 중량비도 함께 나타내었다.In the moisture-permeable and waterproof composition, it was carried out in the same manner as in Example 1, except that the starch powder in which each component was mixed according to Table 3 [unit: weight ratio] was used. At this time, in Table 2, the weight ratio of each component constituting the starch powder of Example 1 is also shown.
[ 비교예 ][ Comparative Example ]
비교예 1 내지 12Comparative Examples 1 to 12
표 4[단위 : 중량부]에 따라 각 성분을 혼합하여 투습방수 조성물을 제조한 것을 제외하고는, 실시예 1과 동일하게 실시하였다.It was carried out in the same manner as in Example 1, except that a moisture-permeable waterproof composition was prepared by mixing each component according to Table 4 [unit: parts by weight].
교
예
1rain
school
Yes
One
교
예
2rain
school
Yes
2
교
예
3rain
school
Yes
3
교
예
4rain
school
Yes
4
교
예
5rain
school
Yes
5
교
예
6rain
school
Yes
6
교
예
7rain
school
Yes
7
교
예
8rain
school
Yes
8
교
예
9rain
school
Yes
9
교
예
10rain
school
Yes
10
교
예
11rain
school
Yes
11
교
예
12rain
school
Yes
12
폴리우레탄 수지thermoplastic
polyurethane resin
글루타메이트Sodium Cocoil
glutamate
이세티오네이트Sodium Cocoil
Isethionate
비교예 13 내지 17Comparative Examples 13 to 17
투습방수 조성물로, 기공 형성 파우더로 표 5에서'○' 표기된 성분만을 포함하는 것을 제외하고는, 실시예 1과 동일하게 실시하였다. As a moisture-permeable and waterproof composition, it was carried out in the same manner as in Example 1, except that only the components marked with '○' in Table 5 as pore-forming powder were included.
비교예 18 내지 19Comparative Examples 18 to 19
투습방수 조성물로, 전분 파우더로 표 6에서, '○' 표기된 성분만을 포함하는 것을 제외하고는, 실시예 1과 동일하게 실시하였다As a moisture-permeable waterproof composition, it was carried out in the same manner as in Example 1, except that in Table 6, only the ingredients marked with '○' were included as starch powder.
[ 실험예 ][Experimental example]
실험예 1 : 투습방수성 평가Experimental Example 1: Water vapor permeability and waterproof evaluation
(1) 투습도 및 세탁 내구성 평가(1) Water vapor permeability and washing durability evaluation
실시예 및 비교예의 섬유원단에 대하여 ASTM E96-2000(INVERTED CUP WATER METHOD) 방법에 따라 투습도를 측정하였고, 그 결과를 하기 표 7[단위 : g/m2*24]에 나타내었다.For the textile fabrics of Examples and Comparative Examples, the moisture permeability was measured according to the ASTM E96-2000 (INVERTED CUP WATER METHOD) method, and the results are shown in Table 7 [unit: g/m 2 *24] below.
또한, 세탁 내구성의 평가를 위해, 세탁전 투습도를 측정한 다음, 약 30 회 세탁(상온, 헹굼 2회, 탈수 10분, 중성세제 사용)한 뒤, 투습도를 측정하여, 그 결과를 함께 나타내었다. 이때, 표 7에서, 세탁전과 세탁후의 투습도 차이가 적을수록 세탁 내구성이 우수함을 의미한다.In addition, for the evaluation of washing durability, the moisture permeability was measured before washing, and then washed about 30 times (at room temperature, rinsed twice, dehydrated for 10 minutes, using a neutral detergent), and then the moisture permeability was measured, and the results are shown together. . At this time, in Table 7, the smaller the difference in moisture permeability before and after washing, the better the washing durability.
표 7을 보면, 본 실시예에 따를 경우, 투습도가 우수함을 확인할 수 있다. 특히, 본 실시예에 따를 경우, 세탁전과 세탁후의 투습도에 차이가 거의 없는 바, 투습도가 우수함과 동시에 세탁 내구성이 우수함을 알 수 있다.Referring to Table 7, it can be confirmed that, according to the present embodiment, the moisture permeability is excellent. In particular, according to this embodiment, there is little difference in the moisture permeability before and after washing, it can be seen that the moisture permeability is excellent and washing durability is excellent at the same time.
(2) 내수성 평가(2) Water resistance evaluation
실시예 및 비교예의 섬유원단에 대하여, KS K0592 방법에 따라 내수도를 측정하고, 그 결과를 표 8[단위 : mmH2O]에 나타내었다.For the textile fabrics of Examples and Comparative Examples, water resistance was measured according to KS K0592 method, and the results are shown in Table 8 [unit: mmH 2 O].
표 8을 보면, 본 실시예에 따를 경우, 내수성이 우수함을 알 수 있다.Referring to Table 8, it can be seen that, according to the present embodiment, the water resistance is excellent.
즉, 본 실시예에 따르는 기능성 섬유원단은 투습방수 효과가 우수하면서도 세탁 내구성이 우수함을 알 수 있다.That is, it can be seen that the functional fiber fabric according to the present embodiment has excellent moisture permeability and waterproof effect and excellent washing durability.
실험예 2 : 강도 평가Experimental Example 2: Strength evaluation
실시예 및 비교예의 섬유원단을 인장시험기(Instorn) 측정설비를 이용하여, KSK 0743법에 의해, 시험 편 폭 5 cm 및 간격 10 cm의 시험편을 인장속도 500 mm/min의 조건으로 인장하여 최대 하중을 구하고, 그 결과를 표 9[단위 : Kgf/5cm]에 나타내었다.Using a tensile tester (Instorn) measuring equipment for the textile fabrics of Examples and Comparative Examples, a test piece with a width of 5 cm and an interval of 10 cm was pulled under the condition of a tensile speed of 500 mm/min by KSK 0743 method to obtain the maximum load , and the results are shown in Table 9 [unit: Kgf/5 cm].
표 9를 보면, 본 실시예에 따를 경우, 인장강도가 우수함을 알 수 있다.Referring to Table 9, it can be seen that, according to the present embodiment, the tensile strength is excellent.
실험예 3 : 부착성 평가Experimental Example 3: Adhesion evaluation
실시예 및 비교예의 섬유원단의 접착력을 평가하고, 그 결과를 표 10[단위 : kg/cm]에 나타내었다.The adhesive strength of the textile fabrics of Examples and Comparative Examples was evaluated, and the results are shown in Table 10 [unit: kg/cm].
구체적으로, 섬유원단과 투습방수층의 접착력을 ASTM D903 방법에 따라, 5 회 반복한 후, 그 평균값을 표 10에 나타내었다.Specifically, the adhesive strength of the textile fabric and the moisture-permeable waterproof layer was repeated 5 times according to the ASTM D903 method, and the average values thereof are shown in Table 10.
표 10을 보면, 본 실시예의 기능성 섬유원단은, 기재에 해당되는 섬유원단과 투습방수층 간의 접착력이 우수함을 알 수 있다.Referring to Table 10, it can be seen that the functional textile fabric of this embodiment has excellent adhesion between the textile fabric corresponding to the substrate and the moisture-permeable waterproof layer.
전술한 바와 같이, 본 발명의 설명은 예시를 위한 것이며, 본 발명이 속하는 기술분야의 통상의 기술을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 쉽게 변형이 가능하다는 것을 이해할 수 있을 것이다. 그러므로, 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며, 한정적이 아닌 것으로 이해해야만 한다. 예를 들어, 단일형으로 설명되어 있는 각 구성 요소는 분산되어 실시될 수도 있으며, 마찬가지로 분산된 것으로 설명되어 있는 구성 요소들도 결합된 형태로 실시될 수 있다.As described above, the description of the present invention is for illustration, and those of ordinary skill in the art to which the present invention pertains can easily transform into other specific forms without changing the technical spirit or essential features of the present invention. You will understand. Therefore, it should be understood that the embodiments described above are illustrative in all respects and not restrictive. For example, each component described as a single type may be implemented in a dispersed form, and likewise components described as distributed may also be implemented in a combined form.
본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위에 의하여 나타내어지며, 특허청구범위의 의미 및 범위 그리고 그 균등 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.The scope of the present invention is indicated by the following claims rather than the above detailed description, and all changes or modifications derived from the meaning and scope of the claims and their equivalents should be interpreted as being included in the scope of the present invention. do.
Claims (7)
상기 섬유 원단 일면 또는 양면에 형성되는 투습방수층;을 포함하는 기능성 섬유원단으로 형성된 유니폼에 관한 것으로,
상기 투습방수층은
열가소성 폴리우레탄 수지, 기공 형성 파우더, 전분 파우더, 소듐코코일글루타메이트, 소듐코코일이세티오네이트 및 폴리에틸렌글리콜을 포함하는 투습방수 조성물로 형성된 코팅층인 것을 특징으로 하는, 투습방수성 및 강도가 우수한 기능성 섬유원단으로 형성된 유니폼.
textile fabric; and
It relates to a uniform formed of a functional fiber fabric comprising; a moisture-permeable and waterproof layer formed on one or both sides of the fiber fabric,
The moisture-permeable waterproof layer is
Functional fiber with excellent moisture permeability and strength, characterized in that it is a coating layer formed of a moisture-permeable and waterproof composition comprising a thermoplastic polyurethane resin, pore-forming powder, starch powder, sodium cocoyl glutamate, sodium cocoyl ethionate and polyethylene glycol Uniform made of fabric.
상기 투습방수층은
상기 열가소성 폴리우레탄 수지 100 중량부에 대해, 상기 기공 형성 파우더 5 ~ 10 중량부, 상기 전분 파우더 7 ~ 15 중량부, 상기 소듐코코일글루타메이트 0.1 ~ 1 중량부, 상기 소듐코코일이세티오네이트 0.1 ~ 1 중량부 및 상기 폴리에틸렌글리콜 3 ~ 6 중량부를 포함하는 것을 특징으로 하는, 투습방수성 및 강도가 우수한 기능성 섬유원단으로 형성된 유니폼.
The method of claim 1,
The moisture-permeable waterproof layer is
With respect to 100 parts by weight of the thermoplastic polyurethane resin, 5 to 10 parts by weight of the pore-forming powder, 7 to 15 parts by weight of the starch powder, 0.1 to 1 part by weight of the sodium cocoyl glutamate, 0.1 parts by weight of the sodium cocoyl ethionate - 1 part by weight and 3 to 6 parts by weight of the polyethylene glycol, characterized in that the uniform formed of a functional fiber fabric excellent in moisture permeability and waterproof strength and strength.
상기 기공 형성 파우더는
친수성 침강(precipitated) 실리카, 키틴(chitin), 알부민(albumin), 셀룰로오스(cellulose) 및 울(wool)을 포함하는 것을 특징으로 하는, 투습방수성 및 강도가 우수한 기능성 섬유원단으로 형성된 유니폼.
The method of claim 1,
The pore-forming powder is
Hydrophilic precipitated (precipitated) silica, chitin (chitin), albumin (albumin), cellulose (cellulose) and a uniform formed of a functional fiber fabric excellent in strength and moisture permeability, waterproof, characterized in that it contains wool (wool).
상기 기공 형성 파우더는
평균 입경이 20 ~ 30 ㎛ 인 것을 특징으로 하는, 투습방수성 및 강도가 우수한 기능성 섬유원단으로 형성된 유니폼.
The method of claim 1,
The pore-forming powder is
Uniform formed of functional fiber fabric with excellent moisture permeability, waterproofness and strength, characterized in that the average particle diameter is 20 ~ 30 ㎛.
상기 전분 파우더는
소듐카르복시메틸스타치 및 히드록시프로필스타치를 포함하는 것을 특징으로 하는, 투습방수성 및 강도가 우수한 기능성 섬유원단으로 형성된 유니폼.
The method of claim 1,
The starch powder is
A uniform formed of a functional fiber fabric with excellent moisture permeability, waterproofness and strength, characterized in that it contains sodium carboxymethyl starch and hydroxypropyl starch.
상기 전분 파우더는
평균 입경이 30 ~ 40 mesh 인 것을 특징으로 하는, 투습방수성 및 강도가 우수한 기능성 섬유원단으로 형성된 유니폼.
The method of claim 1,
The starch powder is
Uniform formed of functional fiber fabric with excellent moisture permeability, waterproofness and strength, characterized in that the average particle diameter is 30 ~ 40 mesh.
상기 유니폼은
교복, 경찰관복, 소방관복, 군복, 위생복, 운동복, 체육복 및 청소복으로 이루어진 군에서 선택되는 어느 하나인 것을 특징으로 하는, 투습방수성 및 강도가 우수한 기능성 섬유원단으로 형성된 유니폼.
The method of claim 1,
The uniform is
Uniform formed of a functional fiber fabric with excellent moisture permeability and waterproofness, characterized in that it is any one selected from the group consisting of school uniform, police uniform, firefighter uniform, military uniform, sanitary uniform, sportswear, gym uniform and cleaning clothes.