KR102360707B1 - 친환경 염해방지 조성물을 이용한 구조물의 보수공법 - Google Patents
친환경 염해방지 조성물을 이용한 구조물의 보수공법 Download PDFInfo
- Publication number
- KR102360707B1 KR102360707B1 KR1020200098943A KR20200098943A KR102360707B1 KR 102360707 B1 KR102360707 B1 KR 102360707B1 KR 1020200098943 A KR1020200098943 A KR 1020200098943A KR 20200098943 A KR20200098943 A KR 20200098943A KR 102360707 B1 KR102360707 B1 KR 102360707B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- inhibitor
- eco
- salt damage
- agent
- Prior art date
Abstract
본 발명은 친환경 염해방지 조성물을 이용한 구조물의 보수공법에 관한 것으로, 콘크리트 구조물의 표면의 레이턴스 제거하는 단계와, 상기 레이턴스가 제거된 표면 혹은 보수재가 도포된 표면에 프라이머층을 형성하는 단계 및 상기 프라이머층을 형성한 후 염해방지제를 도포하는 단계를 포함하고, 상기 염해방지제는 에폭시-실리콘 수지 25 내지 50중량%, 강화섬유 15 내지 20중량%, 세라믹 분말 5 내지 9중량%, 자외선 안정제 5 내지 10중량%, 수축억제제 8 내지 10중량%, 증점제 6 내지 8중량%, 접착증진제 1 내지 3중량%, 박리방지제 10 내지 15중량%로 혼합된 것을 특징으로 한다.
Description
본 발명은 친환경 염해방지 조성물을 이용한 구조물의 보수공법에 관한 것이다.
콘크리트 구조물은 화학적으로 매우 안정하여 반영구적인 재료라고 인식되어져 왔으나 최근 들어 해안 및 해양과 같은 환경하에서 조기에 성능이 저하되는 현상이 발견되고 있다.
콘크리트 구조물은 초기에 주재료인 시멘트가 물과 섞이면 PH 12~13의 강알카리성 수산화칼슘을 만들기 때문에 콘크리트 내부의 철근은 알카리성 피복에 둘러싸여 있어 녹슬지 않는다. 콘크리트 구조물의 표면에 도막이 없으면 다공질의 콘크리트 표면에 염화물 등 유해한 화합물이 부착되기 쉬우며 빗물, 바람 등에 의해서도 쉽게 떨어지기 때문에 더욱 쉽게 침투하게 된다.
콘크리트 구조물의 염해(salt damage)는 주로 해수에서 유산염을 포함한 염분이 콘크리트의 모세공이나 공극으로 침투해서 콘크리트 성분과 팽창성 결정을 만드는 것과 동시에 철근이 녹슬어 팽창되어 콘크리트 구조물을 손상시키는 과정으로 진행된다. 이러한 염해에 의한 콘크리트 구조물의 노화현상은 해상이나 해안에 인접한 구조물에서 많이 나타나며 추운 산간지방과 도심지역에서 제설용 염화칼슘의 영향을 받아 촉진되기도 한다.
콘크리트 구조물에 대한 보수공법 중에 많이 이용되는 공법은 구조물의 표면에 침투형 발수제를 도포함으로써 염분과 수분이 내부로 침투하는 것을 억제하는 것이다. 특허 제10-0405022호에는 시멘트 몰타르와 혼화성이 우수한 고분자 수지를 사용한 콘크리트 보수용 몰타르 조성물이 개시되어 있다. 상기 콘크리트 몰타르 조성물은 뿜어 붙이기 보수공법의 모르타르의 경우에 보수공법의 리바운드량 및 표면 평탄화 작업시 재료손실이 크며, 표면마감시 물을 사용하므로 표면이 강도 및 내구성이 떨어지는 문제점이 있다.
특허 제10-1366514호에는 시공시간을 단축하기 위하여 프라이머의 도포없이 대기습도 100%, 콘크리트 함수비 100% 상태에서도 콘크리트 구조물의 바탕면에 직접 시공되어, 우수한 접착력, 내충격성, 통기성 및 내미끄럼성, 내화학성, 방수성, 내마모성, 불연성을 구비하며, 중성화방지, 방수, 방식, 바닥마감재로 적용가능한 프라이머가 필요없는 친환경 무기질계 도료 조성물과 이를 이용한 시공방법이 개시되어 있다. 상기 시공방법은 무기질계 도료 조성물이 수용액상과 혼합되기 위해 습윤상태를 조성하기 위한 시간이 필요하며, 외부 온도와 습도에 영향을 받기 때문에 시공시간을 일정하게 유지하기 어려운 문제점이 있다.
본 발명의 구조물의 보수공법은 친환경적인 작업환경을 제공함과 동시에 해상구조물의 내구성, 내수성 및 내오염성이 향상된 보수공법을 제공하는데 있다.
또한, 본 발명의 보수공법은 구조물의 표면을 보호하기 위한 표면처리 공정으로 균열 발생요소를 차단하여 내구성을 증진시킬 수 있는 보수공법을 제공하는데 있다.
상기 목적을 달성하기 위해 본 발명의 일 실시예에 따른 친환경 염해방지 조성물을 이용한 구조물의 보수공법은 콘크리트 구조물의 표면의 레이턴스 제거하는 단계와, 상기 레이턴스가 제거된 표면 혹은 보수재가 도포된 표면에 프라이머층을 형성하는 단계 및 상기 프라이머층을 형성한 후 염해방지제를 도포하는 단계를 포함하고, 상기 염해방지제는 에폭시-실리콘 수지 25 내지 50중량%, 강화섬유 15 내지 20중량%, 세라믹 분말 5 내지 9중량%, 자외선 안정제 5 내지 10중량%, 수축억제제 8 내지 10중량%, 증점제 6 내지 8중량%, 접착증진제 1 내지 3중량%, 박리방지제 10 내지 15중량%로 혼합된 것을 특징으로 한다.
상기 프라이머층 형성단계는 에폭시-실리콘 수지 35 내지 60중량%, 강화섬유 10 내지 18중량%, 세라믹 분말 8 내지 12중량%, 자외선 안정제 1 내지 3중량%, 수축억제제 7 내지 10중량%, 증점제 5 내지 8중량%, 접착증진제 3 내지 5중량%, 박리방지제 6 내지 9중량%를 포함하는 프라이머 조성물을 도포하는 것을 특징으로 한다.
상기 레이턴스 제거단계는 구조물 표면의 분진 및 먼지 등을 제거하기 위하여 세척단계를 포함하고, 상기 세척단계 후 구조물 표면의 균열에 보수재를 도포하는 것을 특징으로 하며, 상기 보수재는 수용성 에폭시 수지 16 내지 18중량%, 고로슬래그 20 내지 40중량%, 플라이애쉬 18 내지 20중량%, 평균 입경이 0.1 내지 0.2mm인 실리카 샌드 5 내지 7중량%, 실리콘소포제 1 내지 3중량%, 증점제 3 내지 5중량%, 방청제 0.8 내지 1중량%, 부착증진제 3 내지 6중량%, 멜라민계로 이루어진 분산제 2.5 내지 3.5중량%, 침강방지제 4 내지 6.7중량%, 경화제 6 내지 7.8중량%, 지르코닐 클로라이드 및 지르코닐 나이트레이트 하이드레이트(Zirconyl nitrate hydrate) 중 선택된 하나 0.2 내지 1중량%, 경화촉진제 0.5 내지 1중량%를 포함하는 것을 특징으로 한다.
상기와 같이 하여, 본 발명에 보수공법은 유해물질을 배출하지 않는 친환경적인 염해방지 조성물을 이용하여 균열부위에 침투성이 높고, 보수 후 방수마감 및 방수보강 처리하여 구조물의 수명을 연장할 수 있는 효과가 있다.
또한, 본 발명에 의한 구조물의 보수공법은 콘크리트 중성화 방지 및 염해 저항성을 향상시킬 수 있는 효과가 있다.
도 1은 본 발명의 일 실시예에 따른 친환경 염해방지 조성물을 이용한 구조물의 보수공법을 나타낸 흐름도이다.
이하에서는 첨부한 도면을 참조하여 본 발명을 설명하기로 한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며, 따라서 여기에서 설명하는 실시예로 한정되는 것은 아니다.
명세서 전체에서, 어떤 부분이 다른 부분과 "연결(접속, 접촉, 결합)"되어 있다고 할 때, 이는 "직접적으로 연결"되어 있는 경우뿐 아니라, 그 중간에 다른 부재를 사이에 두고 "간접적으로 연결"되어 있는 경우도 포함한다. 또한 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 구비할 수 있다는 것을 의미한다.
본 명세서에서 사용한 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 명세서에서, "포함하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조함한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들의 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.
본 발명이 속하는 기술분야에 있어서 통상의 지식을 가진 자가 용이하게 실시할 수 있을 정도로 본 발명의 바람직한 실시예를 도면과 함께 상세하게 설명한다.
도 1은 본 발명의 일 실시예에 따른 친환경 염해방지 조성물을 이용한 구조물의 보수공법을 나타낸 흐름도이다.
본 발명의 구조물의 보수공법은 레이턴스 제거단계(S100), 프라이머층 형성단계(S200) 및 염해방지제 도포단계(S300)을 포함한다.
상기 레이턴스 제거단계(S100)는 콘크리트 구조물 등의 표면의 레이턴스 및 이물질을 제거하기 위하여 수행한다. 상기 레이턴스 제거단계(S100)는 표면 레이턴스 및 이물질을 제거하기 위한 것으로서, 통상적인 샌드페이퍼 폴리싱 또는 그라인딩 등과 같은 다양한 표면처리 방법이 채택될 수 있다. 상기 레이턴스 제거시 분진 발생을 예방하기 위하여 습식 에어 그라인딩 하는 방법을 포함한다.
상기 레이턴스 제거단계(S100)는 살수기를 이용하여 구조물 표면의 분진 및 먼지 등을 제거하기 위하여 세척단계를 포함한다. 상기 세척시 압력이 200 내지 300 bar 인 고압 세척기를 사용할 수 있다. 상기 고압 세척기를 이용하여 세척한 후 미세 균열 혹은 망상균열 등 초기 균열에 대응할 수 있도록 보수재를 도포할 수 있다. 이때, 보수재 도포는 구조물 표면의 상태에 따라 선택적으로 적용할 수 있다.
상기 프라이머층 형성단계(S200)는 상기 레이턴스가 제거된 표면 혹은 보수재가 도포된 표면에 프라이머층을 형성한다. 상기 프라이머층에는 에폭시-실리콘 수지 35 내지 60중량%, 강화섬유 10 내지 18중량%, 세라믹 분말 8 내지 12중량%, 자외선 안정제 1 내지 3중량%, 수축억제제 7 내지 10중량%, 증점제 5 내지 8중량%, 접착증진제 3 내지 5중량%, 박리방지제 6 내지 9중량%를 포함한다.
상기 에폭시-실리콘 수지(제조사: H사, 제품명 CERAGOMER FT-EI175)는 주제의 주성분으로서 투명 하이브리드 코팅 조성물에 우수한 저장 안정성, 내화학성, 부착력 및 내열성을 부여할 수 있고, 폴리에스테르실록산(제조사: EVONIK 독일, 공급사: OTCS 제품명: TEGO Wet 270) 및 부틸아세테이트는 분산제의 기능을 부여할 수 있다.
상기 강화섬유는 유리섬유, 바잘트섬유, 탄소섬유 중 선택된 하나 이상인 것을 특징으로 한다. 상기 강화섬유는 40 내지 100mm인 장섬유인 것을 특징으로 한다.
상기 유리섬유는 신축성이 우수한 내알칼리성 유리섬유인 것을 특징으로 한다. 상기 내알칼리성 유리섬유는 알칼리성이 회복된 콘크리트에 손상되는 것을 방지하고, 굴절률이 크고 녹는점이 높아서 급격한 온도변화에 견디는 역할을 한다. 상기 바잘트섬유(basalt fiber)는 현무암을 1,500℃로 녹여 원심력을 이용해 추출된 직경 9 내지 20㎛ 크기의 무기섬유이다. 상기 바잘트섬유(basalt fiber)는 친환경적으로 독성이 없고, 인장강도가 우수하고, 고강도 및 내마모성이 큰 장점이 있다. 상기 탄소섬유는 인장강도, 압축강도, 휨강도 등의 물성이 우수한 장점이 있는 것으로, 섬유줄기부와 섬유줄기부를 중심으로 돌출된 복수개의 마디가 형성된 것을 특징으로 한다.
상기 세라믹 분말은 열에너지를 흡수 및 소멸시킴으로 열에너지 전도를 차단시키는 것으로 입도분포 5 ~ 30㎛인 것을 특징으로 하며, 상기 증점제는 벤토나이트계, 우레탄계, 아크릴계 중 선택된 어느 하나인 것을 특징으로 한다.
상기 자외선 안정제는 300~400㎚의 자외선을 흡수하여 열로 변환시키는 살리실산 에스테르계, 벤조페논계, 벤조트리아졸계, 시아노아크릴레이트계 등의 자외선 흡수제 또는 힌더드 아민계의 광안정제 등을 포함하는 군에서 1종 또는 2종 이상을 혼합하여 사용할 수 있다.
상기 수축억제제는 다당류와 비정질 실리카를 포함할 수 있다. 상기 다당류는 개질된 셀룰로오스, 변성 또는 개질되지 않은 전분, 검, 로커스트 빈, 알지네이트부터 선택될 수 있으며, 특히 숙시노글라이칸, 구아 검, 아라비아 고무, 크 산탄 검, 란산검, 젤란 검 또는 라르복시 메틸 렐룰로스를 포함할 수 있다. 상기 비정질 실리카는 무정형 실리카이고, 분말 또는 액상으로 사용될 수 있다.
상기 접착증진제는 방수보강제 조성물을 구성하는 물질들이 서로 용이하게 결합되게 하고 도막의 내수성, 내구성을 향상시키기 위한 것으로, 글리시독시프로필 메틸디에톡시 실란(Glycidoxy propyl methyldiethoxy silane), 감마메타아크릴옥시 프로필트리에톡시실란(gamma-Methacryloxy propyl triethoxy silane), 감마글리시독시 프로필 트리에톡시 실란(gamma-Glycidoxypropyl trimethoxy silane), 감마아미노프로필 트리에톡시 실란(gamma-Amino propyl triethoxy silane), 비닐트리메톡시 실란(Vinyltrimethoxy silane) 중 선택된 어느 하나를 사용할 수 있다.
상기 박리방지제로 아세트산이 6 내지 9중량%을 포함하는 것을 특징으로 한다. 상기 기타 첨가제에는 착색제, 자외선 차단제, 무기물 충진제, 유화제, 계면활성제, 점도조절제, 산화방지제 등에서 선택되는 1종 이상의 재료가 포함되는 것을 특징으로 한다.
상기 염해방지제 도포단계(S300)는 프라이머층이 양생된 후 염해방지제 조성물을 도포한다. 상기 염해방지제는 에폭시-실리콘 수지 25 내지 50중량%, 강화섬유 15 내지 20중량%, 세라믹 분말 5 내지 9중량%, 자외선 안정제 5 내지 10중량%, 수축억제제 8 내지 10중량%, 증점제 6 내지 8중량%, 접착증진제 1 내지 3중량%, 박리방지제 10 내지 15중량%인 것을 특징으로 한다. 상기 강화섬유는 5 내지 35 mm 인 단섬유인 것을 특징으로 한다.
상기 프라이머층과 염해방지제 도포층에 사용된 재료는 유해물질 배출이 없는 친환경 조성물로서, 친환경적인 작업환경을 제공할 수 있다. 또한, 친환경적이면서 균열부위에 침투성이 높고, 자외선차단, 염화물이온, 이산화탄소, 수분 등 화학적 침투에 대한 저항성을 확보하고 오염을 방지할 수 있다.
상기 프라이머층 형성단계(S200)는 보수단계(S250)를 더 포함한다. 상기 보수단계(S250)는 구조물 이물질 제거 과정에서 부식이 많이 진행되어 균열부위가 큰 경우 보수재로 보수한 후 프라이머층을 형성한다.
상기 보수단계(S250)는 철근이 노출되는 경우 철근 표면의 녹제거제를 도포하여 열풍건조하는 것(S251)을 더 포함한다. 이때 녹제거제는 금속표면처리제 11 내지 25중량%, 킬레이트제 4 내지 7 중량%, 침전제 1 내지 3 중량%, 실리카 8 내지 14 중량%, 경수연화제 6 내지 8 중량%, 계면활성제 1 내지 3 중량%, 소포제 2 내지 5 중량%, 폴리아크릴산 2 내지 5 중량%, 물 30 내지 60 중량%로 혼합된 것을 특징으로 한다.
상기 금속표면처리제는 트리카르보닐 화합물, 변성에폭시수지, 블록이소시아네이트, 아미노수지를 포함한다. 상기 금소교면처리제는 트리카르보닐 화합물 10 내지 15중량%, 변성에폭시수지 15 내지 25중량%, 블록이소시아네이트 50 내지 70중량%, 아미노수지 5 내지 10중량%를 포함하는 것을 특징으로 한다. 상기 트리카르보닐 화합물은 10중량% 이하에서는 표면처리제에 의해 형성되는 피막의 내식성 및 가요성이 저하되고 15중량% 이상에서는 가요성 및 내산성이 저하된다. 상기 변성에폭시수지는 15 내지 25중량%의 범위를 벗어나면 피막의 내식성, 도포막 밀착성, 가요성 및 내산성이 크게 저하된다. 상기 블록이소시아네이트는 50 내지 70중량%의 범위를 벗어나면 피막의 내식성, 도포막 밀착성, 가요성 및 내산성이 저하된다. 상기 아미노수지는 5 내지 10중량%의 범위를 벗어나면 피막의 가요성 및 내산성이 저하된다.
상기 킬레이트제는 아민의 산화분해를 억제시켜 내산화성을 향상시키는 용도로 사용되며, 한 개의 리드간드가 금속 이온과 두 자리 이상에서 배위결합을 하여 생긴 착이온인 킬레이트를 형성시킬 수 있는 모든 화합물을 포함한다. 상기 킬레이트제는 인산(Phosphoric acid) 및 이의 수소 양이온이 알칼리금속 양이온으로 치환된 염(예를 들어, 소듐포스페이트(Sodium phosphate)), 에티드로닉산(Etidronic acid, 1-hydroxyethane 1, 1-diphosphonic acid, HEDP) 및 이의 수소 양이온이 알칼리금속 양이온으로 치환된 염(예를들어, HEDP-Na), 에틸렌다이아민 테트라메틸렌포스포닉산(Ethylenediamine tetramethylene phosphonic acid, EDTMP) 및 이의 수소 양이온이 알칼리금속 양이온으로 치환된 염(예를 들어, EDTMP-Na), 에틸렌다이아민테트라아세트산(Ethylenediaminetetraacetic acid, EDTA) 및 이의 수소 양이온이 알칼리금속 양이온으로 치환된 염(예를 들어, EDTA-Na), 펜테틱산(Diethylenetriaminpentaacetic acid, DTPA) 및 이의 수소 양이온이 알칼리금속 양이온으로 치환된 염(예를 들어, DTPA-Na), 다이멀캡토수시닉산(Dimercaptosuccinic acid, DMSA) 및 이의 수소 양이온이 알칼리금속 양이온으로 치환된 염(예를 들어, DMSA-Na), 아미도트리스메틸렌포스포닉산(Aminotrismethylenephosphonic acid) 및 이의 수소 양이온이 알칼리금속 양이온으로 치환된 염, 다이에틸렌트라이아민 펜타메틸렌포스포닉산(Diethylenetriaminepentamethylene phoshpnonic acid, DTPMP) 및 이의 수소 양이온이 알칼리금속 양이온으로 치환된 염, 다이소듐 테트라설파이드(Disodium tetrasulfide) 등을 포함할 수 있다.
상기 침전제는 황화나트륨(Na2S) 또는 수산화칼슘(Ca(OH)2)인 것을 특징으로 한다.
상기 실리카는 수분산성 실리카를 포함하는 것이 바람직하다. 상기 실리카는 나트륨 등의 불순물이 적은 구상 실리카, 쇄상 실리카, 알루미늄 변형(modified) 실리카 등을 들 수 있다.
상기 경수연화제는 Na+의 1:1 배합보다 영역이 적은 울트라계 인산염이고 무정형 물질이며 복잡한 고분자 이온과 강한 결합력을 가지고 분산, 침전 방지 작업이 탁월하여 산성 영역에서 pH(수소이온농도, 이온수지) 완충작용이 강한 물질로서 6 내지 8 중량% 포함되는 것이 바람직하다.
상기 계면활성제는 철 적층물(iron deposit)의 표면 아래로 도달하도록 하는 통로를 형성하여 녹이 잘 벗겨지도록 도와주는 것으로 1 내지 3 중량%가 포함되는 것이 바람직하다.
상기 소포제는 유해한 기포를 제거하는데 사용되는 것으로 휘발성이 적고 확산력이 큰 특성이 있다. 소포제는 2 내지 5 중량%가 포함되는 것이 바람직하다.
상기 폴리아크릴산은 녹 방지 철근 피막 형성약품 원료로서 2 내지 5 중량%가 포함되는 것이 바람직하다.
상기 보수단계(S250)는 균열부위에 보수재를 충진(S253)하여 보수한다. 상기 보수재는 수용성 에폭시 수지 16 내지 18중량%, 고로슬래그 20 내지 40중량%, 플라이애쉬 18 내지 20중량%, 평균 입경이 0.1 내지 0.2mm인 실리카 샌드 5 내지 7중량%, 실리콘소포제 1 내지 3중량%, 증점제 3 내지 5중량%, 방청제 0.8 내지 1중량%, 부착증진제 3 내지 6중량%, 멜라민계로 이루어진 분산제 2.5 내지 3.5중량%, 침강방지제 4 내지 6.7중량%, 경화제 6 내지 7.8중량%, 지르코닐 클로라이드 및 지르코닐 나이트레이트 하이드레이트(Zirconyl nitrate hydrate) 중 선택된 하나 0.2 내지 1중량%, 경화촉진제 0.5 내지 1중량%를 포함한다. 상기 침투보강제는 물배합비가 60 내지 80%인 것을 특징으로 한다. 물배합비는 물을 침투보강제로 중량을 나눈 값으로 배합비가 높아질수록 묽어진다.
상기 수용성 에폭시 수지는 에폭시 당량이 100 내지 500 g/eq이며, 중량평균분자량(Mw)이 3000 내지 100000이며, 점도가 25℃에서 500 내지 20000 cps인 것을 특징으로 한다.
상기 고로슬래그는 용광로에서 선철을 제조할 때에 부산물로서 생성되는 것으로, 고온의 용융슬래그를 대기중에서 냉각하는서냉슬래그와 압력수로 급냉하는 수쇄슬래그로 나누어 지며, 수쇄슬래그는 유리질(비정질)이며 알칼리자극에 의해 경화하는성질(잠재수경성)을 갖는다. 상기 고로슬래그미분말은 수쇄슬래그를 볼밀 등에서 건조?미분쇄한 후, 분급기에서 소정의 분말도의 것을 선별하여 제조되며, 용도에 따라 석고를 첨가한 것도 제조된다. 상기 고로슬래그는 콘크리트 및 모르타르의 혼화재로서 사용되는 콘크리트용 고로슬래그 미분말(Ground graulated blast-furnace slag for use in concrete)일 수 있으며, 상기 콘크리트용 고로슬래그 미분말은 4,0000 내지 6,000㎠/g 의 분말도를 가지도록 분쇄처리된 것을 특징으로 한다. 상기 고로슬래그 분말은 20 내지 40중량% 포함되는 것을 특징으로 한다.
상기 플라이애쉬는 석탁이나 중유를 보일러 연료로 사용하는 화력발전소에서 연료의 연소과정에서 발생되는 회분을 굴뚝에서 전기 집진기로 포집한 연소재이다. 상기 플라이애쉬는 고로슬래그 분말보다 입도가 작은 것을 특징으로 하고, 바람직하게는 2,0000 내지 3,000㎠/g의 분말도를 가지도록 분쇄처리된 것을 특징으로 한다. 상기 플라이애쉬는 고로슬래그 분말과 혼합되어 가공성이 향상되고 강도 및 수밀성을 향상시키기 위하여 바람직하게는 18 내지 20중량% 포함되는 것을 특징으로 한다.
상기 증점제는 하이드록시 에틸 셀룰로오스(HydroxyEthyl Cellulose), 소수성 우레탄변성계 증점제 또는 이들의 혼합물이 인 것으로 바람직하게는 3 내지 5중량% 포함되는 것을 특징으로 한다.
상기 방청제는 시공면의 부식을 방지하기 위하여 크롬산 스트론튬, 크롬산 칼슘, 크롬산 바륨, 크롬산아연칼륨, 사염기산 크롬산 아연, 아연말, 인산아연, 유기니트로 화합물 아연염, 규산염 칼슘, 사산화삼납, 아연 칼륨 또는 이들의 혼합물이 0.8 내지 1중량% 포함되는 것을 특징으로 한다.
상기 부착증진제는 아크릴 포스페이트계 부착 증진제, 예를 들면 하이드록시 에틸 아크릴로일포스페이트, 하이드록시 에틸 메타 아크릴레이트 포스페이트 또는 이들로부터 선택된 적어도 하나 이상의 혼합물이 3 내지 6중량% 포함되는 것을 특징으로 한다.
상기 분산제는 침투보강제 조성물의 부착력을 향상시키고, 균일하게 분산시키기 위한 것으로 유기산, 아로마틱 오일, 지방족 오일, 동 식물성 기름, 캐스터 오일, 면실유, 미네랄 오일 및 이들의 혼합물로 이루어진 군으로부터 선택된 것을 2.5 내지 3.5중량% 포함되도록 하는 것을 특징으로 한다.
상기 침강방지제는 각 조성물이 용이하게 혼합되고 그 상태를 유지하도록 하는 것으로 합성 흄 실리카계로서 디메틸 디클로로실란(Dimethyldichlorosilane)으로 처리되어 있는 것을 사용하거나 수용성 에복시 수지에 사용할 수 있는 어떠한 침강방지제를 사용하여도 무방하다. 상기 침강방지제는 4 내지 6.7중량%가 포함되는 것을 특징으로 한다.
상기 경화제는 선형 지방족 폴리아민, 방향족 폴리아민, 산무수물 및 이미다졸이 6 내지 7.8중량% 포함되는 것을 특징으로 한다.
상기 경화촉진제는 페놀, 노닐페놀, 3급아민, 머켑탄류, 디부틸디아세테이트, 디부틸렌디라우레이트, 모노부틸렌옥사이드, 모노부틸렌클로라이드디하이드록사이드 등의 1종 이상을 선택한 것으로 0.5 내지 1중량% 포함되는 것을 특징으로 한다.
이하, 본 발명을 하기의 실시예, 비교예에 의거하여 좀 더 상세하게 설명한다.
단, 하기의 실시예는 본 발명을 예시하기 위한 것일 뿐, 본 발명이 하기 실시예에 의해 한정되는 것이 아니고, 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 치환 및 균등한 타 실시예로 변경할 수 있음은 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 있어서 명백할 것이다.
실시예 1
에폭시-실리콘 수지 60중량%, 70mm의 유리섬유와 바질트섬유가 2:1로 혼합된 강화섬유 10중량%, 세라믹 분말 8중량%, 자외선 안정제 1중량%, 수축억제제 7중량%, 증점제 5중량%, 접착증진제 3중량%, 박리방지제 6중량%를 포함하는 프라이머층을 형성한다.
에폭시-실리콘 수지 45중량%, 15mm의 유리섬유와 탄소섬유가 1:1로 혼합된 강화섬유 20중량%, 세라믹 분말 5중량%, 자외선 안정제 5중량%, 수축억제제 8중량%, 증점제 6중량%, 접착증진제 1중량%, 박리방지제 10중량%를 포함하는 염해방지제를 제조한다.
실시예2
균열부위에 보수재 1000kgf와 물750kgf가 혼합된 것을 충진하고 양생 후 실시예1의 프라이머층을 형성한 후 염해방지제를 도포하였다.
표1은 실시예1 내지 실시예2에 대하여 각각 외관, 염화물 차단성, 부착강도, 중성화 저항성, 습기투과저항성, 염소이온 침투저항성을 시험하였다.
시험방법 | 실시예1 | 실시예2 | |
외관 | KS F 4936 | 이상없음 | 이상없음 |
부착강도(N/mm2) | KS F 4936 | 1.96 | 1.91 |
중성화 촉진 시험(30일)(㎜) | KS F 4936 | 0.34 | 0.4 |
투수량(g) | KS F 4042 | 0.17 | 0.19 |
염소이온 침투저항성 (Coulomb) |
KS F 2711 | 149 | 156 |
외관에는 표면 주름, 잔갈림, 핀홀, 변형, 벗겨짐 및 변색이 나타났는지를 육안으로 관찰하였다. 부착강도는 KS F 4936 시험방법에는 1.0 N/㎟ 이상이며, 실시예1 내지 2는 1.91~1.96 N/㎟ 으로 우수한 결과를 확인하였다.
중성화 촉진 시험은 30일간 열화 정도를 측정하였다. 중성화 정도가 적다는 의미는 콘크리트 구조체의 열화 정도가 적은 것을 의미하고, 중성화 정도의 품질 기준은 10㎜ 이다. 본 발명의 실시예1 내지 2는 품질 기준에 비교하면 우수한 결과를 얻을 수 있었다.
투수량은 KS F 4042 시험방법에 따라 측정하였다. 콘크리트 내부로 불순물이나 물이 침투하면 구조물 파손을 초래하는 문제를 발생시키는데 실시예1 내지 2의 투수량은 낮게 나타났다.
또한, 염소이온 침투저항성은 ‘전기 전도도에 의한 콘크리트의 염소이온 침투 저항성 시험 방법’의 규정에 따라 지금 100mm, 두께 50mm의 시편으로 시험을 하였다. 180일 수중 양생이후, 3%의 NaCl 수용액과 0.3 M NaOH 수용액을 가진 셀에 60V 전압을 인가하여 30분 간격으로 6시간까지 통과한 전류량을 측정하였다. 실시예1 내지 2는 염소이온 투과 저항성을 우수하게 나타내었다.
이 외에도 전술한 본 발명의 설명은 예시를 위한 것이며, 본 발명이 속하는 기술분야의 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 쉽게 변형 가능하다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다. 예를 들어, 단일형으로 설명된 각 구성요소는 분산 또는 분할되어 실시될 수 있으며, 마찬가지로 분산 또는 반할된 것으로 설명된 구성요소들도 통상의 기술자가 이해하는 범위 안에서 결합된 형태로 실시 될 수 있다.
본 발명의 범위는 후술하는 특허청구범위에 의하여 나타내어지며 특허청구범위의 의미 및 범위 그리고 그 균등 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.
Claims (3)
- 콘크리트 구조물의 표면의 레이턴스 제거하는 단계;
상기 레이턴스가 제거된 표면 혹은 보수재가 도포된 표면에 프라이머층을 형성하는 단계; 및
상기 프라이머층을 형성한 후 염해방지제를 도포하는 단계;를 포함하고,
상기 염해방지제는 에폭시-실리콘 수지 25 내지 50중량%, 강화섬유 15 내지 20중량%, 세라믹 분말 5 내지 9중량%, 자외선 안정제 5 내지 10중량%, 수축억제제 8 내지 10중량%, 증점제 6 내지 8중량%, 접착증진제 1 내지 3중량%, 박리방지제 10 내지 15중량%로 혼합된 것을 특징으로 하는 친환경 염해방지 조성물을 이용한 구조물의 보수공법.
- 제 1 항에 있어서,
상기 프라이머층 형성단계는 에폭시-실리콘 수지 35 내지 60중량%, 강화섬유 10 내지 18중량%, 세라믹 분말 8 내지 12중량%, 자외선 안정제 1 내지 3중량%, 수축억제제 7 내지 10중량%, 증점제 5 내지 8중량%, 접착증진제 3 내지 5중량%, 박리방지제 6 내지 9중량%를 포함하는 프라이머 조성물을 도포하는 것을 특징으로 하는 친환경 염해방지 조성물을 이용한 구조물의 보수공법.
- 제 1 항에 있어서,
상기 레이턴스 제거단계는 구조물 표면의 분진 및 먼지 등을 제거하기 위하여 세척단계를 포함하고,
상기 세척단계 후 구조물 표면의 균열에 보수재를 도포하는 것을 특징으로 하며,
상기 보수재는 수용성 에폭시 수지 16 내지 18중량%, 고로슬래그 20 내지 40중량%, 플라이애쉬 18 내지 20중량%, 평균 입경이 0.1 내지 0.2mm인 실리카 샌드 5 내지 7중량%, 실리콘소포제 1 내지 3중량%, 증점제 3 내지 5중량%, 방청제 0.8 내지 1중량%, 부착증진제 3 내지 6중량%, 멜라민계로 이루어진 분산제 2.5 내지 3.5중량%, 침강방지제 4 내지 6.7중량%, 경화제 6 내지 7.8중량%, 지르코닐 클로라이드 및 지르코닐 나이트레이트 하이드레이트(Zirconyl nitrate hydrate) 중 선택된 하나 0.2 내지 1중량%, 경화촉진제 0.5 내지 1중량%를 포함하는 것을 특징으로 하는 친환경 염해방지 조성물을 이용한 구조물의 보수공법.