KR102326442B1 - A compound composite for honeycomb and honeycomb manufacturing method thereof - Google Patents
A compound composite for honeycomb and honeycomb manufacturing method thereof Download PDFInfo
- Publication number
- KR102326442B1 KR102326442B1 KR1020200022883A KR20200022883A KR102326442B1 KR 102326442 B1 KR102326442 B1 KR 102326442B1 KR 1020200022883 A KR1020200022883 A KR 1020200022883A KR 20200022883 A KR20200022883 A KR 20200022883A KR 102326442 B1 KR102326442 B1 KR 102326442B1
- Authority
- KR
- South Korea
- Prior art keywords
- honeycomb
- weight
- parts
- compound composition
- beeswax
- Prior art date
Abstract
본 발명은 꿀벌에 친화력이 있고, 고내구성, 높은 조소율을 갖는 벌집판(벌집 소초)을 제조할 수 있는 벌집판용 컴파운드 조성물과 그 컴파운드 조성물을 이용한 벌집판 제조 방법에 관한 것이다.The present invention relates to a compound composition for a honeycomb board, which has affinity to bees, which can produce a honeycomb board (honeycomb weeding) having high durability and a high roughing rate, and a method for manufacturing a honeycomb board using the compound composition.
Description
본 발명은 꿀벌에 친화력이 있고, 고내구성, 높은 조소율을 갖는 벌집판(벌집 소초)을 제조할 수 있는 벌집판용 컴파운드 조성물과 그 컴파운드 조성물을 이용한 벌집판 제조 방법에 관한 기술이다.The present invention relates to a compound composition for a honeycomb plate capable of producing a honeycomb plate (honeycomb weeding) having an affinity for bees, high durability, and a high roughing rate, and a method for manufacturing a honeycomb plate using the compound composition.
최근 소득의 증가와 더불어 삶의 질이 향상됨에 따라 수명이 연장되고 이에따른 건강식품에 대한 관심이 날로 고조되고 있다. As the quality of life is improved along with the recent increase in income, life expectancy is extended and interest in health food is increasing day by day.
이중에서 신선한 꿀은 인삼과 더불어 필수 건강식품으로 그 수요가 증가하고 있으나, 벌꿀 생산시의 농약 사용의 증가, 공해와 같은 환경 오염에 의한 미세먼지 등으로 중금속 오염이 없는 신선한 꿀의 생산량이 감소하고 있다.Among them, fresh honey is in demand as an essential health food along with ginseng, but the production of fresh honey without heavy metal pollution is decreasing due to the increase in the use of pesticides in honey production and fine dust caused by environmental pollution such as pollution. have.
중금속 오염이 없는 신선한 꿀의 공급확대를 위한 양봉 자재의 개발이 매우 중요하다. 이러한 양봉용 자재중 가장 중요한 것이 벌집 기반인 소초광으로 현재 사용되고 있는 소초광은 대부분 밀납과 파라핀을 혼합한 파라핀 소초광으로 내구성에 한계가 있어 이를 대체할 수 있는 새로운 형대의 소초광 개발이 매우 절실한 실정이다.It is very important to develop beekeeping materials to expand the supply of fresh honey without heavy metal contamination. Among these materials for beekeeping, the most important material for beekeeping is honeycomb-based Sochogwang, which is mostly paraffin Sochogwang mixed with beeswax and paraffin, and has limited durability. am.
현재 사용되고 있는 파라핀 소초광은 천연 밀랍과 파라핀을 일정 비율로 혼합하여 벌집과 유사한 형태의 롤러를 사용하여 칼렌더 방식에 의해 생산되고 있으나 이들 소초광은 철사와 같은 선을 사용하여 목재 형틀에 고정하여 사용되고 있으나 이 위에 조소한 벌집에 꿀이나 화분이 축적되면 자체 하중에 의해 변형 또는 파손되고 특히 꿀 채밀시 원심력에 의해 강도가 낮아 파손 또는 변형되는 등 내구성이 매우 낮은 단점을 지니고 있다. The paraffin ore currently used is produced by the calendar method using a roller in a shape similar to a honeycomb by mixing natural beeswax and paraffin in a certain ratio. However, if honey or pollen accumulates on the coarse honeycomb, it is deformed or damaged by its own load. In particular, it has a very low durability such as damage or deformation due to low strength due to centrifugal force during honey gathering.
따라서 이들을 대체할 수 있는 내구성이 우수하며 꿀벌에 친화력이 있고 단시간에 조소율이 높은 벌집용 소초광의 개발이 필요한 실정이다.Therefore, there is a need to develop Sochogwang for beehives that has excellent durability to replace them, is friendly to bees, and has a high sculpting rate in a short time.
현재 밀랍 소초광을 대체하여 개발된 것이 플라스틱 소초광으로 미국에서는 플라스틱을 재료로 밀랍 소초와 유사한 모양의 플라스틱 소초광을 생산하여 판매하고 있다. 그러나 이들 소초광은 닫힌 형태로 조소율이 낮으며 밀랍 소초에 비해 가격이 비싼 단점을 지니고 있다. 또한 독일 등에서도 이와 유사한 플라스틱 소촉광이 개발되어 사용되고 있으나 동일한 단점을 지니고 있고 국내에서는 내구성이 우수한 폴리카보네이트 수지를 원료로기존 개발된 플라스틱 소초와는 달리 벌집 형태의 육각형이 서로 교파된 개방형태의 플라스틱 소초가 개발되어 일부 사용되었으나 조소율이 낮고 특히 밀랍 소초에 비해 가격이 월등히 비싸 현재 극히 일부만 사용되고 있는 실정이다.Plastic Sochogwang is currently being developed to replace beeswax Sochogwang, and in the United States, plastics are produced and sold in a shape similar to that of Beeswax Sochogwang. However, these sochogwangs have the disadvantages that they have a low sculpting rate in a closed shape and are more expensive than waxy sochos. In addition, similar plastic small candles have been developed and used in Germany, etc., but have the same disadvantages. In Korea, unlike the conventionally developed plastic candle candles using polycarbonate resin with excellent durability, it is an open plastic in which honeycomb-shaped hexagons are intersected with each other. Socho was developed and used in part, but the carving rate is low and, in particular, the price is much higher than that of beeswax grass, so only a small part of it is currently used.
따라서 대부분 중국에서 수입되고 있는 밀랍 소초와 가격경쟁력이 있고 내구성이 우수하여 사용기간을 대폭 늘리수 있으며 안전하게 채밀이 가능하고 밀랍 소초와 거의 동일한 수준의 조소율을 유지할 수 있는 새로운 형태의 사출성형에 의한 대량 생산이 가능한 꿀벌 친화형 고 내구성 플라스틱 벌집판 제조가 필요한 시점이 된 것이다. 이러한 필요성에 기인해 본 발명이 제안되게 되었다.Therefore, it is cost-competitive with the most imported beeswax from China and has excellent durability, so it can be used for a long time, can be harvested safely, and is produced by injection molding of a new type that can maintain the cutting rate at almost the same level as that of beeswax. The time has come for the manufacture of bee-friendly, high-durability plastic honeycomb boards that can be mass-produced. Due to this necessity, the present invention has been proposed.
본 발명은 고내구성, 높은 조소율, 꿀벌에 친화력이 있는 플라스틱 벌집판을 제조할 수 있는 벌집판용 컴파운드 조성물 제공을 목적으로 한다.An object of the present invention is to provide a compound composition for a honeycomb plate capable of manufacturing a plastic honeycomb plate having high durability, high sculpting rate, and affinity to bees.
또한, 본 발명은 고내구성, 높은 조소율, 꿀벌에 친화력이 있는 하니콤 구조의 플라스틱 벌집판 제조를 목적으로 한다. In addition, an object of the present invention is to manufacture a plastic honeycomb plate having a honeycomb structure having high durability, high sculpting rate, and affinity to bees.
상기 과제를 해결하기 위한 본 발명의 벌집판용 컴파운드 조성물은,The compound composition for a honeycomb board of the present invention for solving the above problems,
플라스틱 수지 70~80 중량부, 목분 10~20 중량부를 포함하는 것을 특징으로 한다.It is characterized in that it contains 70 to 80 parts by weight of plastic resin and 10 to 20 parts by weight of wood flour.
또한, 상기 과제를 해결하기 위한 본 발명의 벌집판 제조 방법은,In addition, the honeycomb plate manufacturing method of the present invention for solving the above problems,
벌집 소초(벌집판) 제조에 필요한 컴파운드 조성물을 가열 및 혼련하여 반죽을 형성하는 반죽단계(S100)와;A kneading step (S100) of forming a dough by heating and kneading the compound composition required for the production of honeycomb sorghum (honeycomb plate);
상기 반죽을 성형기를 통해 압출하여 허니콤 구조의 펠렛을 형성하는 펠렛형성단계(S200)와;a pellet forming step (S200) of extruding the dough through a molding machine to form pellets having a honeycomb structure;
상기 펠렛을 일정 크기로 커팅하는 커팅단계(S300)를 포함하고,Including a cutting step (S300) of cutting the pellets to a predetermined size,
상기 상기 컴파운드 조성물은 플라스틱 수지 70~80 중량부, 밀납 5~20 중량부, 목분 5~10 중량부를 포함하는 것을 특징으로 한다.The compound composition is characterized in that it comprises 70 to 80 parts by weight of plastic resin, 5 to 20 parts by weight of beeswax, and 5 to 10 parts by weight of wood flour.
본 발명에 의한 벌집판용 컴파운드 조성물은 내구성이 우수하고, 조소율이 높고, 환경 친화적(꿀벌 친화적)인 벌집판을 제조할 수 있도록 하는 장점을 제공한다. The compound composition for a honeycomb board according to the present invention provides advantages of being able to manufacture a honeycomb board having excellent durability, a high sculpting rate, and an environment-friendly (bee-friendly) honeycomb board.
본 발명에 의한 벌집판 제조방법은 치수안정성, 높은 조소율, 용이한 가공성을 제공하는 장점이 있다. The method for manufacturing a honeycomb board according to the present invention has advantages of providing dimensional stability, high roughing rate, and easy workability.
도 1은 본 발명에 따른 벌집판 제조방법 순서도1 is a flowchart of a method for manufacturing a honeycomb plate according to the present invention;
이하 도면을 참조하여 본 발명에 따른 벌집판용 컴파운드 조성물과 벌집판 제조 방법에 대해 상세히 설명한다. Hereinafter, a compound composition for a honeycomb board and a method for manufacturing a honeycomb board according to the present invention will be described in detail with reference to the drawings.
이때, 사용되는 기술 용어 및 과학 용어에 있어서 다른 정의가 없다면, 이 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 통상적으로 이해하고 있는 의미를 가지며, 하기의 설명에서 본 발명의 요지를 불필요하게 흐릴 수 있는 공지 기능 및 구성에 대한 설명은 생략한다. At this time, unless there are other definitions in the technical terms and scientific terms used, it has the meaning commonly understood by those of ordinary skill in the art to which this invention belongs, and in the following description, the subject matter of the present invention may be unnecessarily obscured. Descriptions of possible known functions and configurations will be omitted.
본 발명에 따른 벌집판용 컴파운드 조성물은 벌들이 생활하며 꿀을 생산할 수 있도록 하는 벌집에 사용되는 벌집판(일명 소초라고도 함)을 제조하기 위해 사용되는 조성물인 것을 특징으로 한다.The compound composition for a honeycomb board according to the present invention is characterized in that it is a composition used for manufacturing a honeycomb board (also called socho) used in a honeycomb that allows bees to live and produce honey.
본 발명에 따른 벌집판용 컴파운드 조성물은 기본적으로 플라스틱 수지와 밀납과 목분을 포함하는데, 구체적으로,플라스틱 수지 70~80 중량부, 밀납 5~20 중량부, 목분 5~10 중량부를 포함하는 것을 특징으로 한다.The compound composition for a honeycomb board according to the present invention basically includes a plastic resin, beeswax, and wood flour, specifically, 70 to 80 parts by weight of a plastic resin, 5 to 20 parts by weight of beeswax, and 5 to 10 parts by weight of wood flour. do.
본 발명에 의한 벌집판용 컴파운드 조성물은 플라스틱 수지와 밀납과 목분을 포함하고 있어 고 내구성, 높은 조소율, 친환경성, 꿀벌 친화형,낮은 제조단가, 가공의 용이성을 제공한다. The compound composition for a honeycomb board according to the present invention contains a plastic resin, beeswax, and wood flour, and thus provides high durability, high sculpting rate, eco-friendliness, bee-friendly, low manufacturing cost, and ease of processing.
상기 플라스틱 수지는 일반적인 플라스틱 합성수지를 의미하며, 벌집판용 컴파운드 조성물 조성 시 70~80 중량부로 혼합되며, 제조되는 벌집판(소초)의 기본적 강도를 유지하기 위한 기본 원료가 된다.The plastic resin means a general plastic synthetic resin, and is mixed in an amount of 70 to 80 parts by weight when the compound composition for honeycomb board is composed, and becomes a basic raw material for maintaining the basic strength of the honeycomb board (socho) to be manufactured.
상기 밀납은 벌집에서 가열압착법·용제추출법 등에 의해 채취하는 동물성 고체랍으로 주성분은 멜리실알코올의 팔미트산 에스터와 세로트산이며, 이 밖에 여러 가지 지방산·알코올 및 고급탄화수소 등이 함유되어 있다. The beeswax is an animal solid wax that is collected from a honeycomb by hot pressing and solvent extraction. The main components are palmitic acid ester of melicyl alcohol and serotic acid, and in addition, various fatty acids, alcohols, and higher hydrocarbons are contained.
밀납은 점착성이 있는 비결정성 물질로 제과, 각종 약제의 기초제, 화장품 등에 사용되며, 이 밖에 전기의 절연제, 광택제, 방수제, 색연필 등의 제조에도 사용되고, 마룻바닥의 도료나, 양초의 원료로도 사용된다. Beeswax is an amorphous substance with adhesive properties and is used in confectionery, base agent for various pharmaceuticals, cosmetics, etc. In addition, it is also used in the manufacture of electrical insulation, varnish, waterproofing agent, colored pencils, etc. is also used
상기 밀납은 벌집에서 채취되는 벌의 분비물인 것이어서 밀납이 포함된 벌집판용 컴파운드 조성물로 벌집판(소초)을 제조하면, 환경 친화 조건 및 꿀벌의 용이한 조소 조건을 확보(꿀벌 친화력 확보 의미)하여 조소 과정의 거부감이 없고 가공이 용이한 장점이 있다. The beeswax is a secretion of bees collected from a beehive, so when a honeycomb plate (sweet grass) is prepared with a compound composition for a honeycomb plate containing beeswax, environmental friendly conditions and conditions for easy sculpting of bees are secured (meaning securing bee affinity) and sculpting There is no objection to the process and it has the advantage of easy processing.
이러한 장점에 의해, 벌집판(소초) 제조 시, 밀랍을 코팅하는 공정을 별도로 거치지 않아도 밀랍 코팅효과를 확보하여 결과적으로 벌집판 생산단가를 현저히 낮출 수 있는 장점이 있다. Due to these advantages, there is an advantage in that the honeycomb plate production cost can be significantly lowered as a result by securing the beeswax coating effect without going through a separate process for coating the beeswax when the honeycomb plate (socho) is manufactured.
즉, 통상적으로 밀랍을 코팅하는 과정을 거치는 종래의 벌집판 제조 방법과 차별성을 띠며, 본 발명의 벌집판용 컴파운두 조성물에 밀납을 포함시키게 되면 벌집 조소에 적합한 높은 조소율을 나타내면서도 높은 치수안정성을 나타낼 수 있는 장점이 있다. That is, it is differentiated from the conventional honeycomb plate manufacturing method, which usually goes through a process of coating beeswax, and when beeswax is included in the compound head composition for a honeycomb plate of the present invention, high dimensional stability is achieved while exhibiting a high sculpting rate suitable for honeycomb sculpting. There are advantages that can be shown.
이러한 밀랍은 컴파운드 조성물에 5 내지 20 중량부 포함될 수 있는데, 밀랍이 상기 범위보다 다량 첨가되는 경우 제조되는 벌집판(소초)이 높은 치수안정성을 나타내기 어려운 문제점이 있으며, 밀랍이 상기 범위 보다 적게 첨가되는 경우 제조되는 벌집판(소초)의 조소율을 담보하기 어려운 문제점이 있다. 5 to 20 parts by weight of such beeswax may be included in the compound composition, but when the amount of beeswax is added in a larger amount than the above range, there is a problem in that it is difficult for the honeycomb board (socho) manufactured to exhibit high dimensional stability, and the beeswax is added in less than the above range If it is, there is a problem in that it is difficult to guarantee the sculpting rate of the honeycomb plate (socho) to be manufactured.
상기 목분은 목재를 이용한 건축용 자재 생산 시 발생하는 부산물로서 통상적인 의미의 목분일 수 있으나, 더욱 구체적으로는 소나무, 은행나무, 향나무, 편백나무, 측백나무, 계피나무, 잣나무 중 적어도 하나 이상을 건조 후 분쇄하여 분말화한 것일 수 있으며, 이러한 목분은 입자의 크기가 0.05 내지 1 ㎜일 수 있다.The wood powder is a by-product generated during the production of building materials using wood and may be wood powder in a conventional sense, but more specifically, at least one of pine, ginkgo, juniper, cypress, arborvitae, cinnamon, and cypress is dried It may be pulverized and then pulverized, and such wood powder may have a particle size of 0.05 to 1 mm.
이러한 목분이 포함된 벌집판용 컴파운드 조성물로 벌집판(소초)을 제조하면, 벌지판(소초)에 목재의 질감을 나타내어 제조된 벌집판(소초) 사용 시 목재의 질감을 살릴 수 있는 장점이 있다. When a honeycomb board (socho) is prepared with a compound composition for a honeycomb board containing such wood powder, there is an advantage in that the texture of wood can be saved when using a honeycomb board (socho) manufactured by expressing the texture of wood on the honeycomb board (socho).
나아가, 이러한 목분에 의해 제조된 벌지판(소초)은 기계적 강도를 향상시킬 수 있으며 특히 목재의 특성이 있어 온도 조절 기능을 부여할 뿐만 아니라, 환경 친화적, 꿀벌 친화적으로 조소율을 높이는 장점이 있다. Furthermore, the bulge board (socho) manufactured by such wood powder can improve mechanical strength, and has the advantage of not only giving a temperature control function due to the characteristics of wood in particular, but also increasing the sculpting rate in an environment-friendly and bee-friendly manner.
이러한 목분은 벌집판용 컴파운드 조성물 조성 시, 5~10 중량부로 혼합될 수 있다.Such wood powder may be mixed in an amount of 5 to 10 parts by weight when the compound composition for honeycomb board is formulated.
특히, 본 발명의 벌집판용 컴파운드 조성물은 밀납과 목분을 동시에 포함하는데, 밀랍의 윤활성으로 인해 목분의 분산성을 향상시켜 대면적에서도 균질한 혼합비를 나타내며, 결과적으로 밀랍과 목분이 균일하게 분산되어 높은 조소율을 갖는 벌집판(소초)을 제조할 수 있는 장점이 있다. In particular, the compound composition for honeycomb board of the present invention contains beeswax and wood flour at the same time. Due to the lubricity of the beeswax, the dispersibility of the wood flour is improved to show a homogeneous mixing ratio even in a large area. There is an advantage of being able to manufacture a honeycomb plate (socho) having a roughening rate.
상기 벌집판용 컴파운드 조성물은 조성 시, 플라스틱 수지 70~80 중량부, 밀납 5~20 중량부, 목분 5~10 중량부로 혼합되는데, 바람직하게는 플라스틱 수지 70~80 중량부에 대해 밀납과 목분의 중량합이 10 내지 30 중량부가 되도록 한다.The compound composition for the honeycomb board is mixed in 70 to 80 parts by weight of plastic resin, 5 to 20 parts by weight of beeswax, and 5 to 10 parts by weight of wood flour, preferably, the weight of beeswax and wood flour based on 70 to 80 parts by weight of plastic resin. Let the sum be 10 to 30 parts by weight.
만일, 밀랍과 목분이 상기 범위 보다 소량 첨가되는 경우, 제조되는 벌집판(소초)의 균질한 조성을 기대하기 어려우며, 밀랍과 목분이 상기 범위 보다 다량 첨가되는 경우 제조되는 벌집판(소초)의 내구성을 도모하기 어려운 문제점이 있다. If beeswax and wood powder are added in a smaller amount than the above range, it is difficult to expect a homogeneous composition of the prepared honeycomb board (socho), and when beeswax and wood powder are added in a larger amount than the above range, the durability of the manufactured honeycomb board (socho) is improved. There are problems that are difficult to solve.
따라서, 밀랍과 목분이 상기 범위 내로 포함되는 경우, 제조되는 벌집판(소초)는 높은 치수안정성 및 가공성이 용이할 뿐 만 아니라, 벌집판(소초) 제조 비용이 저렴해지는 장점이 있다.Therefore, when beeswax and wood flour are included within the above range, the manufactured honeycomb board (scourge) has advantages in that the manufacturing cost of the honeycomb board (socho) is low as well as high dimensional stability and easy workability.
본 발명의 벌집판용 컴파운드 조성물은 리그닌을 더 포함할 수 있으며 1~12 중량부로 혼합되어 벌집판용 컴파운드 조성물을 구성한다.The compound composition for a honeycomb board of the present invention may further include lignin and is mixed in an amount of 1 to 12 parts by weight to constitute the compound composition for a honeycomb board.
상기 리그닌은 목재에서 추출된 유기화합물로서, 목재를 이용한 펄프 제지 가공 공정에서 테르펜유를 추출하고 남은 잔류물로부터 획득할 수 있다. The lignin is an organic compound extracted from wood, and may be obtained from a residue remaining after terpene oil is extracted in a pulp and paper processing process using wood.
이러한 리그닌이 포함된 벌집판용 컴파운드 조성물로 벌집판(소초)를 제조하면, 색깔의 구현은 물론 목재의 질감을 더욱 강화할 수 있다. 즉, 리그닌은 상술한 목분과 혼합되어 결착됨으로써 제조된 벌집판(소초)의 목재 질감을 더욱 향상시킬 수 있는 장점이 있다. When a honeycomb board (socho) is prepared with a compound composition for a honeycomb board containing such lignin, it is possible to realize color as well as further enhance the texture of wood. That is, lignin has the advantage of being able to further improve the wood texture of the honeycomb board (socho) manufactured by mixing and binding with the above-mentioned wood powder.
이러한 리그닌은 벌집판용 컴파운드 조성물 조성 시, 1~12 중량부로 혼합될 수 있는데, 리그닌이 상기 범위 이상으로 포함되면 제조된 벌집판(소초)의 내구성이 낮아진다. 따라서 리그닌이 벌집판용 컴파운드 조성물 조성 시, 1~12 중량부, 바람직하게는 5~8 중량부로 혼합되면 목분에 의한 목재의 질감을 더욱 강화하여 환경 친화적, 꿀벌 친화적 양봉용 벌집판(소초)으로의 이용 적합도가 높아지는 장점이 있다. Such lignin may be mixed in an amount of 1 to 12 parts by weight in the composition of the compound composition for honeycomb board, but when lignin is included in the above range, durability of the prepared honeycomb board (socho) is lowered. Therefore, when the lignin is mixed in 1 to 12 parts by weight, preferably 5 to 8 parts by weight, when the compound composition for the honeycomb board is composed, the texture of the wood by wood powder is further strengthened and used as an environmentally friendly, bee-friendly beekeeping honeycomb board (socho) It has the advantage of increasing the fit.
본 발명의 벌집판용 컴파운드 조성물은 탈취 기능을 하는 첨가제 1~5 중량부를 더 포함할 수 있다.The compound composition for a honeycomb board of the present invention may further include 1 to 5 parts by weight of an additive having a deodorizing function.
상기 탈취 기능을 하는 첨가제는 탈크, 활성탄, 맥반석, 제올라이트, 활성알루미나 중에서 선택되는 적어도 하나 이상을 포함한다.The additive having the deodorizing function includes at least one selected from talc, activated carbon, elvan, zeolite, and activated alumina.
탈취 기능을 하도록 사용되는 상기 첨가제는 본 발명의 벌집판용 컴파운드 조성물에 포함된 밀랍 및 목분과 결착되어 제조된 벌집판에 물리적 충격 등이 가해질 때 벌집판으로부터 이탈되어 유실되는 것이 방지된다. The additive used to perform a deodorizing function is prevented from being separated from the honeycomb plate and lost when a physical impact or the like is applied to the honeycomb plate manufactured by binding with the beeswax and wood powder contained in the compound composition for the honeycomb plate of the present invention.
첨가제를 구성하는 탈크, 활성탄, 맥반석, 제올라이트, 활성알루미나 등은 입경이 100 내지 3000 ㎛, 바람직하게는 100 내지 1000 ㎛로 분말화 되어 이용할 수 있으며, 분말화된 탈크, 활성탄, 맥반석, 제올라이트, 활성알루미나 등에 형성된 기공의 평균 직경은 300 내지 1500 ㎚ 정도이다. Talc, activated carbon, elvan stone, zeolite, activated alumina, etc. constituting the additive may be powdered to a particle size of 100 to 3000 μm, preferably 100 to 1000 μm, and powdered talc, activated carbon, elvan, zeolite, active The average diameter of pores formed on alumina or the like is about 300 to 1500 nm.
따라서 입자크기 및 평균 기공의 직경이 상기 범위를 만족하는 경우, 탈취 효과를 나타내면서도 상술한 밀랍 및 목분과 결착되어 제조된 벌집판에 물리적 충격 등이 가해질 때 유실되는 것을 예방할 수 있다. Therefore, when the particle size and the average pore diameter satisfy the above ranges, it is possible to prevent loss when a physical impact or the like is applied to the honeycomb plate manufactured by binding with the above-described beeswax and wood flour while exhibiting a deodorizing effect.
상술한 바와 같이, 벌집판용 컴파운드 조성물은 조성 시, 첨가제는 1 내지 5 중량부 포함될 수 있는데, 이러한 범위로 포함되는 경우, 탈취효과를 확보하면서도 제조되는 벌집판(소초)의 기계적 물성 저하를 막을 수 있는 장점이 있다. As described above, the compound composition for honeycomb board may contain 1 to 5 parts by weight of additives during composition. there are advantages to
이상에서 설명한 본 발명인 벌집판용 컴파운드 조성물은 벌집판 제조에 이용되는데 폐쇄형 벌집판(소초), 개방형 벌집판(소초), 하니컴 벌집판(소초) 등의 제조 원료로 사용될 수 있으며, 내구성과 대량생산을 목표로 하는 환경 친화적, 꿀벌 친화적인 벌집판 제조에 유용하게 사용될 수 있다. The compound composition for a honeycomb board according to the present invention described above is used for manufacturing a honeycomb board. It can be used as a raw material for manufacturing a closed honeycomb board (socho), an open honeycomb board (socho), a honeycomb honeycomb board (socho), etc., and has durability and mass production. It can be usefully used in the manufacture of environmentally friendly, bee-friendly honeycomb plates that aim at
이하에서는 본 발명인 벌들이 생활하며 꿀을 생산할 수 있도록 하는 벌집판 제조 방법에 대해 설명한다.Hereinafter, a method for manufacturing a honeycomb board that allows bees to live and produce honey according to the present invention will be described.
본 발명의 벌집판 제조 방법은 상술한 벌집판용 컴파운드 조성물이 이용된다.In the method for manufacturing a honeycomb board of the present invention, the above-described compound composition for a honeycomb board is used.
본 발명에 따른 벌집판 제조 방법은, 도 1에 도시된 바와 같이,As shown in FIG. 1, the method for manufacturing a honeycomb board according to the present invention comprises:
벌집판(소초) 제조에 필요한 컴파운드 조성물을 가열 및 혼련하여 반죽을 형성하는 반죽단계(S100)와;A kneading step (S100) of forming a dough by heating and kneading the compound composition necessary for manufacturing a honeycomb plate (socho);
상기 반죽을 성형기를 통해 압출하여 허니콤 구조의 펠렛을 형성하는 펠렛형성단계(S200)와;a pellet forming step (S200) of extruding the dough through a molding machine to form pellets having a honeycomb structure;
상기 펠렛을 일정 크기로 커팅하는 커팅단계(S300)를 포함한다.and a cutting step (S300) of cutting the pellets to a predetermined size.
본 발명의 벌집판 제조 방법은 추가적으로 커팅단계(S300) 이후에 일정 크기로 커팅된 펠렛 표면에 밀납을 코팅하는 밀납코팅단계(S400)를 더 포함할 수 있다.The honeycomb plate manufacturing method of the present invention may further include a beeswax coating step (S400) of additionally coating the surface of the pellets cut to a predetermined size after the cutting step (S300).
상기 반죽단계(S100)는 벌집판 제조를 위한 기조 원료를 혼합하여 반죽하는 과정으로서, 벌집판(소초) 제조에 필요한 컴파운드 조성물을 가열 및 혼련하여 반죽을 형성한다.The kneading step (S100) is a process of mixing and kneading a base material for manufacturing a honeycomb board, and heating and kneading a compound composition necessary for manufacturing a honeycomb board (socho) to form a dough.
상기 반죽단계(S100)에서 사용되는 벌집판(소초) 제조에 필요한 컴파운드 조성물로서 상술한 플라스틱 수지 70~80 중량부, 밀납 5~20 중량부, 목분 5~10 중량부를 포함하는 조성물로서, 플라스틱 수지, 밀납, 목분에 대한 특징은 벌집판용 컴파운두 조성물 부분에서 상세히 설명한 바 구체적 설명은 생략한다.A composition comprising 70 to 80 parts by weight of the above-mentioned plastic resin, 5 to 20 parts by weight of beeswax, 5 to 10 parts by weight of wood flour as a compound composition necessary for manufacturing the honeycomb board (socho) used in the kneading step (S100), a plastic resin , beeswax, and wood flour have been described in detail in the compound head composition for honeycomb board, and detailed descriptions thereof will be omitted.
또한, 상기 반죽단계(S100)에서 사용되는 벌집판(소초) 제조에 필요한 컴파운드 조성물은 리그닌 1~12 중량부를 더 포함할 수 있으며, 리그닌에 대한 특징은 벌집판용 컴파운두 조성물 부분에서 상세히 설명한 바 구체적 설명은 생략한다.In addition, the compound composition necessary for manufacturing the honeycomb board (socho) used in the kneading step (S100) may further include 1 to 12 parts by weight of lignin, and the characteristics of lignin are described in detail in the compound head composition for honeycomb board. A description is omitted.
또한, 상기 반죽단계(S100)에서 사용되는 벌집판(소초) 제조에 필요한 컴파운드 조성물은 탈취 기능을 하는 첨가제를 더 포함할 수 있으며, 상기 탈취 기능을 하는 첨가제는 활성탄, 맥반석, 제올라이트, 활성알루미나 중에서 선택되는 적어도 하나 이상인 것을 특징으로 하며, 활성탄, 맥반석, 제올라이트, 활성알루미나 중에서 선택되는 적어도 하나 이상인 첨가제의 특징은 벌집판용 컴파운두 조성물 부분에서 상세히 설명한 바 구체적 설명은 생략한다.In addition, the compound composition necessary for manufacturing the honeycomb board (socho) used in the kneading step (S100) may further include an additive having a deodorizing function, and the additive having a deodorizing function is activated carbon, elvan, zeolite, and activated alumina. Characteristics of at least one additive selected from activated carbon, elvan stone, zeolite, and activated alumina are described in detail in the compound head composition for honeycomb board, and detailed descriptions thereof will be omitted.
이때, 상기 반죽단계(S100)는 250-290℃, 구체적으로 260℃ 내지 280℃ 에서 수행될수 있으며, 상기 온도 범위에서 재료를 혼련하는 경우, 고열에 의한 조성물의 화학적 변화를 예방할 수 있으면서도, 조성물을 균일하게 혼련할 수 있다. At this time, the kneading step (S100) may be carried out at 250-290 ℃, specifically 260 to 280 ℃, when kneading the material in the above temperature range, while it is possible to prevent chemical change of the composition due to high heat, the composition It can be kneaded uniformly.
이러한 반죽단계(S100)는 5 분 내지 30 분 동안 수행될 수 있으나, 조성물을 균일하게 혼련할 수 있는 범위 내인 경우 제한이 없다.This kneading step (S100) may be performed for 5 to 30 minutes, but there is no limitation if the composition is within a range that can be uniformly kneaded.
상기 펠렛형성단계(S200)는 반죽을 성형기를 통해 압출하여 허니콤 구조의 펠렛을 형성하는 과정이다.The pellet forming step (S200) is a process of forming pellets of a honeycomb structure by extruding the dough through a molding machine.
상기 성형기는 반죽을 투입하면 허니콤 구조의 펠렛을 압출 성형하는 펠렛 다이일 수 있다.The molding machine may be a pellet die for extruding pellets having a honeycomb structure when the dough is added.
성형기에 반죽 투입 시, 접착력을 확보하기 위하여 소량의 밀랍을 추가 투입할 수 있으며 펠렛형성단계(S200)를 통해 형성되는 펠렛의 두께는 2 내지 100 ㎜일수 있으나, 사용용도 및 사용 환경 등을 고려하여 적절히 조절될 수 있다. When kneading the dough into the molding machine, a small amount of beeswax can be added to ensure adhesion, and the thickness of the pellets formed through the pellet forming step (S200) may be 2 to 100 mm, but considering the purpose of use and the environment, etc. can be appropriately adjusted.
상기 커팅단계(S300)는 형성된 펠렛을 일정 크기로 커팅하는 과정으로서, 커팅되는 펠렛의 크기는 사용용도 및 사용 환경 등을 고려하여 적절히 조절될 수 있다. The cutting step (S300) is a process of cutting the formed pellets to a predetermined size, and the size of the pellets to be cut may be appropriately adjusted in consideration of the intended use and the environment of use.
또한, 본 발명의 벌집판 제조 방법은 추가적으로 커팅단계(S300) 이후에 일정 크기로 커팅된 펠렛 표면에 밀납을 코팅하는 밀납코팅단계(S400)를 더 포함할 수 있는데, 밀납코팅단계(S400)를 더 포함시키는 이유는 제조되는 벌집판의 친환경성 및 꿀벌 친화성을 더욱 향상시키기 위함이다.In addition, the honeycomb plate manufacturing method of the present invention may further include a beeswax coating step (S400) of coating beeswax on the surface of the pellets cut to a predetermined size after the cutting step (S300). The reason for further inclusion is to further improve the eco-friendliness and bee-friendly properties of the manufactured honeycomb plate.
즉, 상술한 벌집판용 컴파운드 조성물 부분에서 언급한 바와 같이, 벌집판용 컴파운드 조성물에는 이미 밀납 성분이 포함되어 있어, 커팅단계(S300)를 통해 제조된 벌집판은 어느 정도 환경 친화 조건 및 꿀벌의 용이한 조소 조건을 확보(꿀벌 친화력 확보 의미)하고 있게 되는데, 커팅된 벌집판 표면에 밀납을 추가 코팅하게 되면 환경 친화 조건 및 꿀벌의 용이한 조소 조건이 더욱 향상되는 효과가 있다.That is, as mentioned in the above-mentioned compound composition for honeycomb board, the compound composition for honeycomb board already contains a beeswax component. Sculpture conditions are secured (meaning securing bee affinity), and if beeswax is additionally coated on the surface of the cut honeycomb plate, environmental friendly conditions and easy sculpting conditions for bees are further improved.
이상에서 본 발명에 대한 기술사상을 첨부도면과 함께 서술하였지만, 이는 본 발명의 바람직한 실시예를 예시적으로 설명한 것이지 본 발명을 한정하는 것은 아니다. 또한, 이 기술분야의 통상의 지식을 가진 자라면 누구나 본 발명의 기술사상의 범주를 이탈하지 않는 범위 내에서 다양한 변형 및 모방이 가능함은 명백한 사실이다.Although the technical idea of the present invention has been described together with the accompanying drawings, the preferred embodiment of the present invention is illustratively described and does not limit the present invention. In addition, it is a clear fact that anyone with ordinary skill in the art can make various modifications and imitations without departing from the scope of the technical idea of the present invention.
S100 : 반죽단계
S200 : 펠렛형성단계
S300 : 커팅단계
S400 : 밀납코팅단계S100: kneading step
S200: pellet forming step
S300 : Cutting step
S400: Beeswax coating step
Claims (9)
플라스틱 수지 70~80 중량부, 밀납 5~20 중량부, 목분 5~10 중량부를 포함하는 것을 특징으로 하는 벌집판용 컴파운드 조성물.
In a compound composition for a honeycomb plate for producing a honeycomb plate that allows bees to live and produce honey,
A compound composition for a honeycomb board, comprising 70 to 80 parts by weight of a plastic resin, 5 to 20 parts by weight of beeswax, and 5 to 10 parts by weight of wood flour.
리그닌 1~12 중량부를 더 포함하되,
상기 리그닌은 목재에서 추출된 유기화합물인 것을 특징으로 하는 벌집판용 컴파운드 조성물.
According to claim 1,
Further comprising 1 to 12 parts by weight of lignin,
The compound composition for honeycomb board, characterized in that the lignin is an organic compound extracted from wood.
탈취 기능을 하는 첨가제 1~5 중량부를 더 포함하되,
상기 탈취 기능을 하는 첨가제는 활성탄, 맥반석, 제올라이트, 활성알루미나 중에서 선택되는 적어도 하나 이상인 것을 특징으로 하는 벌집판용 컴파운드 조성물.
3. The method of claim 1 or 2,
Further comprising 1 to 5 parts by weight of an additive having a deodorizing function,
The additive for the deodorizing function is a compound composition for honeycomb board, characterized in that at least one selected from activated carbon, elvan, zeolite, and activated alumina.
상기 목분은,
소나무, 은행나무, 향나무, 편백나무, 측백나무, 계피나무, 잣나무 중 적어도 하나 이상을 건조 후 분쇄하여 분말화한 것이고,
상기 목분의 입자 크기는 0.05 내지 1 ㎜인 것을 특징으로 하는 벌집판용 컴파운드 조성물.
According to claim 1,
The wood powder is
At least one of pine, ginkgo, juniper, cypress, arborvitae, cinnamon, and cypress is dried and then pulverized into powder,
The compound composition for honeycomb board, characterized in that the particle size of the wood powder is 0.05 to 1 mm.
벌집 소초(벌집판) 제조에 필요한 컴파운드 조성물을 가열 및 혼련하여 반죽을 형성하는 반죽단계(S100)와;
상기 반죽을 성형기를 통해 압출하여 허니콤 구조의 펠렛을 형성하는 펠렛형성단계(S200)와;
상기 펠렛을 일정 크기로 커팅하는 커팅단계(S300)를 포함하고,
상기 컴파운드 조성물은 플라스틱 수지 70~80 중량부, 밀납 5~20 중량부, 목분 5~10 중량부를 포함하는 것을 특징으로 하는 벌집판 제조 방법.
In a method for manufacturing a honeycomb board that allows bees to live and produce honey,
A kneading step (S100) of forming a dough by heating and kneading the compound composition necessary for the production of honeycomb sorghum (honeycomb plate);
a pellet forming step (S200) of extruding the dough through a molding machine to form pellets having a honeycomb structure;
Including a cutting step (S300) of cutting the pellets to a predetermined size,
The compound composition comprises 70 to 80 parts by weight of plastic resin, 5 to 20 parts by weight of beeswax, and 5 to 10 parts by weight of wood flour.
상기 컴파운드 조성물은 리그닌 1~12 중량부를 더 포함하되,
상기 리그닌은 목재에서 추출된 유기화합물인 것을 특징으로 하는 벌집판 제조 방법.
6. The method of claim 5,
The compound composition further comprises 1 to 12 parts by weight of lignin,
The lignin is a method for producing a honeycomb board, characterized in that the organic compound extracted from wood.
상기 컴파운드 조성물은 탈취 기능을 하는 첨가제 1~5 중량부를 더 포함하되,
상기 탈취 기능을 하는 첨가제는 활성탄, 맥반석, 제올라이트, 활성알루미나 중에서 선택되는 적어도 하나 이상인 것을 특징으로 하는 벌집판 제조 방법.
7. The method of claim 5 or 6,
The compound composition further comprises 1 to 5 parts by weight of an additive having a deodorizing function,
The additive for the deodorizing function is at least one selected from activated carbon, elvan, zeolite, and activated alumina.
상기 목분은,
소나무, 은행나무, 향나무, 편백나무, 측백나무, 계피나무, 잣나무 중 적어도 하나 이상을 건조 후 분쇄하여 분말화한 것이고,
상기 목분의 입자 크기는 0.05 내지 1 ㎜인 것을 특징으로 하는 벌집판 제조 방법.
6. The method of claim 5,
The wood powder is
At least one of pine, ginkgo, juniper, cypress, arborvitae, cinnamon, and cypress is dried and then pulverized into powder,
The method for manufacturing a honeycomb board, characterized in that the particle size of the wood powder is 0.05 to 1 mm.
상기 커팅단계(S300)이후에 일정 크기로 커팅된 펠렛 표면에 밀납을 코팅하는 밀납코팅단계(S400)를 더 포함하는 것을 특징으로 하는 벌집판 제조 방법.
6. The method of claim 5,
After the cutting step (S300), the honeycomb plate manufacturing method further comprising a beeswax coating step (S400) of coating the surface of the pellets cut to a predetermined size with beeswax.