KR102300138B1 - Mask comprising surface for capturing moisture - Google Patents

Abstract

The present invention relates to a mask comprising a moisture collecting surface. Provided is a mask comprising a moisture collecting surface, which comprises: a filtering part forming a breathing space partitioned from the air and filtering foreign materials in introducing air; a collecting part prepared in the filtering part and collecting moisture; string attaching parts formed at both ends of the filtering part and in connection with wearing strings; and a drying part formed at the string attaching parts, absorbing moisture by being in connection with the capturing part, and formed to be exposed to the outer side of the string attaching parts. According to the present invention, reduction of air permeability can be prevented.

Description

A mask including a moisture-collecting surface {MASK COMPRISING SURFACE FOR CAPTURING MOISTURE}

The present invention relates to a mask including a moisture trapping surface.

Masks are used to protect the user's respiratory tract from airborne particles or unpleasant or toxic gases. Masks were mainly used at work sites or medical institutions, but in recent years, they have been widely used by the general public for the purpose of yellow dust, fine dust, and living health. The mask is used for the purpose of filtering fine dust, yellow dust, or other harmful substances in the air from entering the user's respiratory tract. These masks are generally divided into KF80, KF94, and KF99 in Korea according to their filtering function. However, even when wearing a mask with a high-performance filtration function, the adhesion to the face is not made properly, and air is often passed through the space between the mask and the face. In order to improve this, in the prior art, a metal wire is inserted into the mask to provide a structure that can be closely adhered to the shape of the user's nose and the nose area. cases still occur. In this case, in the case of a user who wears glasses or goggles, fogging may occur in the lens, which may impair visibility. In order to solve this problem, conventionally, a technique for coating a lens has been disclosed, but it is greatly affected by temperature or humidity and has a problem that the holding time is short.

Republic of Korea Registered Utility Model Publication No. 20-0492617 (2020. 11. 05)

An embodiment of the present invention aims to prevent a phenomenon in which heat exchange generated in the breathing process when wearing a mask generates moisture in the mask, and the generated moisture is absorbed or adsorbed on the mask surface to reduce air permeability.

The present invention relates to a mask including a moisture-collecting surface, comprising: a filtering unit for forming a breathing space partitioned from the atmosphere and filtering foreign substances in the incoming air; a collecting unit provided on the inside of the filtration unit and collecting moisture; It is formed at both ends of the filtering unit, a strap attachment portion to which a wear strap is connected; And formed in the attaching part of the string, connected to the collecting part to absorb moisture, and a drying part formed to be exposed to the outside from the attaching part; a mask comprising a water collecting surface is provided.

And, the collecting unit is formed of a waterproof material as one of the coating layers for coating a part of the vinyl, film, and filter unit, and is curved from the central part to both ends and extended, and the both ends are positioned low to guide the collected moisture to be delivered to the drying unit. can,

In addition, the drying unit has one end connected to the collecting unit disposed inside the filtration unit, and the other end of the drying unit is formed to be exposed to the atmosphere outside the string attachment unit, so that the moisture absorbed from the inside is absorbed in the dry season of the outside atmosphere. can be dried by

In addition, further comprising a frame disposed on the inside of the filtering unit, the frame, a vertical frame comprising a first vertical frame, a second vertical frame and a third vertical frame spaced apart from each other in the horizontal direction; and a horizontal frame including a first horizontal frame, a second horizontal frame, and a third horizontal frame spaced apart from each other in the vertical direction, and optionally including at least one of the horizontal frame and at least one of the vertical frame, the moisture collecting surface can do.

In addition, the frame may include: a rotating part provided on the foldable part on the extensibility of the frame so that it can be folded; And it may include a first coupling portion and a second coupling portion coupled to each other at the abutting point by folding.

In addition, the wearing string extends through the inside of the filter unit from the end side, and is wound and passed through the elastic winding unit in a path passing through the inside, and the elastic winding unit elastically pulls the wearing string to provide a predetermined tension on the wearing string. can be maintained.

According to an embodiment of the present invention, it is possible to provide an area that can collect moisture in the mask, and to provide a mask that can breathe more comfortably by maintaining air permeability in the mask by preferentially drying the collected moisture. can

In addition, the fabric fiber sheet for masks with improved antibacterial function of the present invention provides excellent antibacterial performance by including ingredients with excellent antibacterial function derived from natural plants, and by firmly fixing the antibacterial component to the fiber, the antibacterial function lasts for a long time effect can be provided.

1 is a view showing a front side of a mask according to an embodiment of the present invention;
2 is a view showing the rear side of the mask according to an embodiment of the present invention;
3 is a view showing a wire and a frame according to an embodiment of the present invention;
Figure 4 is a view showing a frame according to an embodiment of the present invention, Figure 4 (a) is a view showing the first vertical frame from the front side showing the position of the rotating part, the first coupling part, the second coupling part, , Figure 4 (b) is a view showing the rotational state of the first vertical frame from the side, Figure 4 (c) is a view showing the coupling between the first coupling portion and the second coupling portion,
5 is a view showing a first flow path passing through the separation space and a second flow path exhausted from the breathing space to the outside according to an embodiment of the present invention;
6 is a view showing a spacer member and a spaced space according to an embodiment of the present invention;
7 is a view showing an elastic winding unit according to an embodiment of the present invention.
8 is a cross-sectional view schematically showing a coating form of a fabric fiber sheet for a mask having an improved antibacterial function according to the present invention.
9 is a cross-sectional view schematically showing the high-moisture transfer action of the fabric fiber sheet for a mask having an improved antibacterial function according to the present invention.
10 is a view showing various embodiments of the coating layer of the fabric fiber sheet for a mask having an improved antibacterial function according to the present invention.

Hereinafter, specific embodiments of the present invention will be described with reference to the drawings. However, this is merely an example and the present invention is not limited thereto.

In the description of the present invention, if it is determined that the detailed description of the known technology related to the present invention may unnecessarily obscure the gist of the present invention, the detailed description thereof will be omitted. In addition, the terms to be described later are terms defined in consideration of functions in the present invention, which may vary according to intentions or customs of users and operators. Therefore, the definition should be made based on the content throughout this specification.

The technical spirit of the present invention is determined by the claims, and the following examples are only one means for effectively explaining the technical spirit of the present invention to those of ordinary skill in the art to which the present invention belongs.

1 is a view showing the front side of the mask 100 according to an embodiment of the present invention, Figure 2 is a view showing the rear side of the mask 100 according to an embodiment of the present invention. Here, the front side is the side exposed to the outside while the user wears the mask 100 , and the rear side is the side facing the respirator side while the user wears the mask 100 .

1 and 2 , the mask 100 includes a filtering unit 110 , a collecting unit 120 , a string attachment unit 130 , and a drying unit. Specifically, a filtering unit 110 that forms a breathing space partitioned from the atmosphere and filters foreign substances in the incoming air, a collecting unit 120 provided inside the filtering unit 110 and collecting moisture, and a filtering unit ( It is formed on both ends of the 110) and is formed in the strap attachment part 130 and the strap attachment part 130 to which the wearing strap 101 is connected, and is connected to the collecting part 120 to absorb moisture and from the strap attachment part 130. It may include a drying unit formed to be exposed to the outside.

Furthermore, in order to maintain a higher adhesion rate with the user who wears the mask 100 , the adhesion unit 140 may be provided to increase the adhesion rate with the user when wearing the mask 100 . For example, the contact unit 140 may be in close contact with the user's nose. By increasing the adhesion rate with the user by the adhesion part 140 having a predetermined area, it is possible to prevent the air in the breathing space in the mask 100 from being exhausted or introduced. That is, it is possible to implement a more improved adhesion rate compared to the contact through the line contact.

Meanwhile, the collecting unit 120 may be provided inside the filtering unit 110 . That is, it may be disposed in the breathing space, and may be made of a non-breathable material. For example, the collecting unit 120 may be formed of a waterproof material as one of vinyl, a film, and a coating layer for coating a portion of the filtering unit 110 . Moisture generated by the temperature difference between the air temperature of the breathing space and the atmosphere may be condensed on the collecting unit 120 by such a material. Preferably, it may be a material capable of forming a hydrophobic surface, and since this is a material having no absorbency, the rate at which moisture is collected on the surface of the collecting unit 120 rather than the rate at which moisture is condensed on the surface of the filtering unit 110 . can be faster,

Specifically, the collecting unit 120 may be provided at an upper end inside the filtering unit 110 . Here, the upper end means that the user may be positioned above the respirator (nose and mouth) while wearing the mask 100 . Of course, when the wire 160 maintaining a shape corresponding to the human body when wearing the mask 100 is provided in the insertion part 160a, it may be selectively formed except for a partial area. In this example, the collection part 120 will be described through an example provided without separate avoidance from the side of the wire 160 , and in this case, it may be formed in connection with the contact part 140 . Even when the user's exhalation is exhausted upward by this arrangement structure, moisture is collected by contact with the collecting unit 120 during the movement of the exhalation (air), so that the humidity is relatively low (dryness is increased) and exhausted. have. Even when the air exhausted due to a decrease in humidity is exhausted upward, the degree of fogging may be reduced in accessories such as glasses or goggles.

Furthermore, when respiration is repeatedly performed according to the above-described method, the moisture collected in the collecting unit 120 may be collected with surrounding moisture to form water droplets and flow to a lower place. The collecting part 120 is formed in a curved shape, and the central part is formed at the highest level, so that it extends to both ends and may extend downward. Accordingly, the water droplets may be moved along the moving direction M toward both ends of the collecting unit 120 . The moving direction (M) means a direction in which the water droplet is moved by its own weight, which is low in the height direction, and as a structure for inducing movement in the moving direction (M), the collecting unit 120 has a low both ends. It may be provided in a curved shape. In addition, drying units may be provided at both ends. In addition, the collecting unit 120 may have a hydrophobic property rather than a hydrophilic property so that it can be moved to both ends within a shorter time by its own weight.

The drying unit may absorb water droplets. For example, the drying unit may be made of a material having a predetermined absorption power, such as a pulp material. Accordingly, the drying unit absorbs water droplets flowing along the collecting unit 120 . Moisture absorbed by the drying unit may be completely transferred to the drying unit. This is because the relatively dry part has better absorbency on the entire area of the drying part, so it spreads from the part where water absorption starts.

One end of the drying unit of an embodiment of the present invention may be in contact with the collecting unit 120 and the other end may be exposed to the outside through the string attachment unit 130 . Here, "outside" means a breathing space and a partitioned atmosphere. Therefore, it can be relatively dry compared to the air of the exhalation. That is, since moisture is absorbed and moved to the dry side on the entire area of the drying unit, when the absorption of moisture is accumulated, the moisture may be moved to the part exposed to the outside. Moisture moved to the outside by the drying unit exposed to the outside may be continuously evaporated by the relatively dry atmosphere. That is, the moisture generated in the collecting unit 120 due to the humidity difference (or dryness difference) between the breathing space inside the mask 100 and the atmosphere may be continuously evaporated into the atmosphere.

Therefore, the moisture collected in the collecting unit 120 can be continuously discharged to the outside by evaporation, and the collecting unit 120 is composed of an area induced to cause condensation of moisture more effectively than the filtering unit 110, The humidity inside the mask 100 may be continuously reduced until it is the same as the humidity of the atmosphere.

Preferably, the area of the attaching part 130 is as wide as possible, and it is effective to expose the drying unit in an area corresponding thereto, but it may be formed of a specific image, text, etc. according to the user's selection. In the example shown in FIGS. 1 and 2 , the first drying unit 131 and the second drying unit 132 are provided in a relatively large area at the upper and lower parts, respectively, and the first drying unit 131 and the second drying unit ( A connection portion 131a connecting the 132 is provided. Here, the connection part 131a connects the first drying part 131 that is in direct contact with the collecting part 120 to the second drying part 132 formed only on the outside of the string attachment part 130 so that moisture can be moved. This is one of the examples in which the evaporation area can be further expanded through this configuration.

3 is a view showing a wire 160 and a frame according to an embodiment of the present invention.

Referring to FIG. 3 , the mask 100 may include at least two shape maintaining structures. At least one of them may be a wire 160 positioned to correspond to the user's nose, and the rest may be a frame. Here, the frame means a structure formed in at least one of horizontal and vertical directions.

First, the wire 160 may be positioned on the mask 100 . The wire 160 may be in direct or indirect contact with the user's nose to maintain a predetermined shape. Here, indirect contact means that the user's nose is in contact with the user's nose through the filtering unit 110 because it is drawn into the filtering unit 110 and not exposed to the outside. That is, the wire 160 may be attached and connected to the outside of the filter unit 110 , or at least a portion thereof may be provided to be introduced into the filter unit 160 .

In addition, the wire 160 may be a material having a predetermined elastic restoring force to maintain the predetermined shape. For example, it may be a material including a metal material or a resin material. Of course, although not limited thereto, it is preferable that the material enters a predetermined area of plastic deformation so that elastic restoring force can be generated within the area of plastic deformation. This is to facilitate maintaining the deformed shape by elastic restoring force based on the deformed shape after the nose is deformed to correspond to a nose having a different surface shape according to the user.

Furthermore, the frame is an example, a first vertical frame 210, a second vertical frame 220 and a vertical frame including a third vertical frame 230 and a first horizontal frame 240, a second horizontal frame ( 250) and a horizontal frame including a third horizontal frame 260. This is only a few examples that the frame can be formed in various ways for each position, but is not limited thereto. The vertical frame may be provided in a vertical direction with respect to the illustrated mask 100 . The selectively applicable vertical frame may preferably include at least a first vertical frame 210 positioned at the center. This is because it may be a position where it is easy for the user to secure the breathing space (S) for breathing, and for the same reason, the first horizontal frame 240 or the second horizontal frame 250 located in the center of the horizontal frame may be located. . Of course, it is possible to selectively apply a shape in which one or more frames are connected.

And, unlike the reason that the first vertical frame 210, the first horizontal frame 240 and the second horizontal frame 250 are arranged for the reason of easy to secure the breathing space (S), the second vertical frame 220, The third vertical frame 230 and the third horizontal frame 260 may perform a function of increasing adhesion to the user's face when worn by the user through the wearing strap 101 . When the mask 100 is worn, the second vertical frame 220 , the third vertical frame 230 , and the third horizontal frame 260 are formed along both cheeks and chin of the user to form a breathing space S and an external space. It becomes possible to function to maintain the compartment of the liver more firmly. Furthermore, the frame may be coupled to the inside of the filter unit 160 of the mask 100 in a fixed manner, but may be coupled to be selectively detachable.

Figure 4 is a view showing a frame according to an embodiment of the present invention, Figure 4 (a) is a second showing the position of the rotating part 211, the first coupling part 212, the second coupling part 213 1 is a view showing the vertical frame 210 from the front side, Figure 4 (b) is a view showing the rotation state of the first vertical frame 210 from the side side, Figure 4 (c) is the first coupling portion 212 ) and a view showing a coupling portion (C) that is a coupling between the second coupling portion (213).

The frame described above may include a collapsible structure. To describe the structure as a preferred example with reference to FIGS. 4( a ), 4 ( b ) and 4 ( c ), the structure may be provided in the first vertical frame 210 . The structure may include a rotating part 211 , a first coupling part 212 , and a second coupling part 213 , and each configuration may be provided on an extension line of the first vertical frame 210 .

Specifically, the rotating part 211 may be located in the center of the first vertical frame 210, and the first body 210a and the second body 210b are divided into both sides with the rotating part 211 as the center. , a first coupling part 212 and a second coupling part 213 may be provided on the first body 210a and the second body 201b, respectively. In the case of the first coupling part 212 and the second coupling part 213, they are positioned at the same distance from the rotating part 211 so that the first body 210a and the second body 201b correspond to each other when folded. can be When the first coupling part 212 is formed in a ball-shaped protruding shape, the second coupling part 213 may be formed as a corresponding ball-shaped groove. Accordingly, the first coupling portion 212 and the second coupling portion 213 may perform folding and release of the first vertical frame 210 through the elasticity of the material.

Such folding may deform the mask 100 to be folded. That is, since the first vertical frame 210 is positioned in the vertical direction at the center of the mask 100 , when the rotating part 211 is positioned at the center of the first vertical frame 210 , an arbitrary center line formed in the horizontal direction is the reference. can be folded into Of course, the foldable structure is formed on the first vertical frame 210 as an example, but it is also possible to be provided on the second horizontal frame 250 .

In some cases, when provided in one or more of the plurality of vertical frames and the plurality of horizontal frames, the foldable structure may be provided on each vertical frame or each horizontal frame. The mask 100 can be folded inside or outside by such a folding structure, and in the case of the example shown in FIG. 4 , an example in which the mask 100 is folded inside is disclosed. In this case, the inner portion of the filtering unit 110 that covers the user's mouth and nose is folded inward, so that hygienic storage is possible. Of course, when folded to the outside, it is possible to prevent substances such as dust adsorbed on the filtering unit 110 from being blown into the atmosphere while the mask 100 is stored.

On the other hand, the frame including the first vertical frame 210 is formed by being curved, it is possible to form a breathing space (S) in the front portion of the mouth and nose. The curved shape of the first vertical frame 210 may be maintained by at least elastic traction of the wearing strap 101 among the structure between the frames and elastic traction of the wearing strap 101 . The formation of the breathing space (S) will be described in detail with reference to FIG. 5 below.

5 is a view showing a first flow path (F1) passing through the separation space (310a) and a second flow path (F2) exhausted to the outside from the breathing space (S) according to an embodiment of the present invention,

Referring to FIG. 5 , the mask 100 may further include a blocking layer 300 . The blocking layer 300 may be connected to the filtering unit 110 and may reach the blocking layer 300 through the filtering unit 110 among the paths of air sucked into the mask 100 . That is, it may be provided on the rear side based on the air intake direction. The blocking layer 300 may be connected to the filtering unit 110 and the spacer member 310 . A plurality of spacer members 310 may extend from the blocking layer 300 to form a predetermined spaced distance from the inner surface of the filtering unit 110 . Accordingly, the separation space 310a is formed by the formation of the separation distance. The separation space 310a may be a path through which air is sucked into the mask 100 . Here, the blocking layer 300 is a configuration in which air is not ventilated, and vinyl or paper is embedded in the inside of the blocking layer 300 in the form of a thin film, or the density of the fiber weave is extremely high, and it may be in a state in which ventilation is impossible.

Here, the opening and closing parts 330 may be provided in portions adjacent to both ends of the left and right sides of the filtering unit 110 . Specifically, it is preferable that the portions adjacent to both ends are provided on the side so as not to interfere with the first flow path F1 within the separation space 310a. The opening/closing part 330 may be disposed to face the ventilation part 320 formed in the blocking layer 300 . The opening/closing part 330 is configured to allow only one air flow, and will be described in more detail below.

Specifically, in the present embodiment, the air flow is divided into a first flow path F1 and a second flow path F2. The first flow path F1 is an air flow formed by the suction force when the user wears the mask 100 and inhaled, and the second flow path F2 is an air flow formed when the user exhales and air is discharged. it can be said Here, different air movement paths are formed in the first flow path F1 by the second flow path F2 and the blocking layer 300 . That is, the first flow path F1 and the second flow path F2 may be formed through different paths. Furthermore, the first flow path F1 may be formed to be longer than the second flow path F2 . By forming a difference in the section of the flow path to form a heat exchange section, the user (the mask 100 wearer) does not immediately drink air at a temperature created by the external environment, but drinks it through the heat exchange section.

More specifically, the first flow path F1 is introduced into the mask 100 through the filtering unit 110 , and is introduced into the inside through the filtering unit 110 of the mask 100 to filter foreign substances such as dust. can be The filtered air is introduced into the separation space (310a). The air introduced into the separation space 310a is introduced into the breathing space S through the ventilation unit 320 that is opened from the separation space 310a to the breathing space S by the suction force by inhalation.

The path of the first flow path F1 is introduced into the breathing space S through the ventilation units 320 located at both ends of the blocking layer 300 through the outer central portion of the mask 100 . Accordingly, with reference to FIG. 5 , the first flow path F1 includes a section that moves laterally.

Meanwhile, the second flow path F2 is as follows. Air is discharged into the breathing space (S) by exhaled through the nose or mouth. The discharged air is exhausted to the outside via the ventilation unit 320 and the opening/closing unit 330 . Here, the opening/closing unit 330 performs a valve function that opens when the internal pressure of the mask 100 becomes higher than the external pressure of the mask 100 and is configured to maintain an elastically closed state from the outer surface of the filter unit 110 . can Accordingly, based on the filter unit 110, when the external pressure is higher than the internal pressure, the closed state is maintained, and when the internal pressure is higher than the external pressure, it can be opened. That is, the opening/closing unit 330 may allow only one air flow from the mask 100 . Of course, the latter case corresponds to a case in which the pressure difference exceeds the elasticity of the opening and closing part 330 .

This may satisfy the condition that the opening/closing part 330 is opened because the internal pressure of the mask 100 increases when the wearer's exhalation of the mask 100 occurs. Therefore, it can be opened at the time of exhalation to exhaust air.

The above-described first flow path F1 and second flow path F2 induce a change in flow path formed by a difference in structure and pressure, and the exhausted air is directly discharged to the outside, and the incoming air is separated from the space 310a. will pass through In this structure, for example, in the case of winter when the incoming air is cold, the temperature difference between the air in the breathing space S and the air outside the mask 100 is large, so moisture may occur inside the mask 100 . When moisture is condensed on the inner surface of the mask 100, breathing may become more inconvenient, so the separation space 310a is formed to reduce or prevent moisture generation by alleviating the temperature difference. That is, as to alleviate the temperature gradient, heat exchange is primarily performed in advance in the separation space 310a, and secondary heat exchange is performed in the breathing space S, so that the moisture generation rate due to the temperature difference can be reduced.

6 is a view showing the separation member (310) and the separation space (310a) as showing the separation (A) side according to an embodiment of the present invention.

Referring to FIG. 6 , the spacer 310 may be formed as a separate member and interposed between the blocking layer 300 and the inner surface of the filtering unit 110 to form a spaced space 310a, but the blocking layer ( When the 300 ) is made of the same material as the filtering unit 110 , the spacer 310 may be formed to extend from the blocking layer 300 . Here, the extension means extending to be interposed between the blocking layer 300 and the filtering unit 110 disposed to face each other, and preferably, both ends of the blocking layer 300 and the filtering unit 110 are respectively provided. It means that it is arranged to be orthogonal and extended. In addition, a plurality of spacer members 310 may be disposed in the same manner as in the above arrangement to continuously maintain the spaced space 310a between the blocking layer 300 and the filtering unit 110 .

7 is a view showing the elastic winding unit 400 according to an embodiment of the present invention.

Referring to FIG. 7 , the mask 100 may further include an elastic winding unit 400 . The elastic winding unit 400 is connected so that a part of the wearing strap 101 is wound, so that the pulling-out and retraction of the wearing strap 101 can be elastically implemented. The elastic winding unit 400 pulls the wearing string 101 to wear the mask 100 through the elastic force of the coil spring and draws it out from the elastic winding unit 400, the wearing string drawn out from the elastic winding unit 400 (101) may generate a predetermined traction force to the wear strap 101 to elastically return. Accordingly, the wearing strap 101 can maintain the wearing state of the mask 100 by generating a continuous traction force to the user's ear or head.

Furthermore, the elastic winding unit 400 may be provided at each of both ends of the filtering unit 110 , and the wearing strap 101 may be drawn into the end side as shown in FIG. 7 . Here, the elastic winding unit 400 may provide a hollow pole (not shown) curved to a predetermined curvature so that both ends of the mask 100 do not deform due to elasticity. In addition, the second vertical frame 220 and the third vertical frame 230 may replace the function of the pole.

Hereinafter, the antibacterial function by the antibacterial treatment of the fabric sheet for mask according to the present invention will be described in more detail.

As used herein, the terms 'about', 'substantially' and the like are used in or close to the numerical value when manufacturing and material tolerances inherent in the stated meaning are presented, and provide an understanding of the present invention. To help, precise or absolute figures are used to prevent unfair use by unscrupulous infringers of the stated disclosure.

As used herein, the term 'fiber sheet' is used to include all articles manufactured by weaving or knitting, nonwoven fabrics, and fibrous webs.

8 is a cross-sectional view schematically showing the coating form of the fabric fiber sheet for a mask with improved antibacterial function according to the present invention, and FIG. 10 is a view showing various embodiments of the coating layer of the fabric fiber sheet for a mask having an improved antibacterial function according to the present invention.

As shown in FIG. 8 , a first coating layer 2000 for forming an intaglio-shaped concave-convex structure is formed on one surface of the fabric fiber sheet 1000 for a mask, thereby providing high moisture transferability and far-infrared radiation through the coating layer.

The first coating layer 2000 having the functionality as described above may include a far-infrared emitting material, a foaming agent, a water repellent agent, and a binder.

The first coating layer 2000 may be adjusted and coated on one surface of the fabric fiber sheet 1000 for a mask so that far-infrared radiation and high moisture transfer functions can be smoothly exhibited.

When the first coating layer 2000 is formed with a surface area of less than 30% on one surface of the fabric fiber sheet 1000 for a mask, the functionality of far-infrared radiation and high moisture transfer function may be reduced, and the fabric fiber sheet for a mask (1000) When the surface area exceeds 90% on one surface, it is preferable to apply 30 to 90% of the surface area on one surface of the fabric fabric sheet 1000 for a mask because the texture and physical properties of the fabric sheet for mask may be reduced and the coating layer may be peeled off.

The far-infrared radiation material of the first coating layer 2000 has its own energy according to the molecular structure and vibration of atoms, and transmits energy to our body, and this energy stimulates the muscles of our body and improves blood circulation. It helps, increases the oxygen content in the blood, and increases the vitality of our body.

Such far-infrared rays deliver energy to the muscle layer, activate muscle movement, and express a function of reducing muscle fatigue.

As the far infrared ray emitting material, an inorganic material emitting at least one far infrared ray consisting of silicon oxide, magnesium, alumina, sodium, calcium, and iron oxide may be used.

The inorganic material emits far-infrared rays and has a beneficial function to the human body. The silicon oxide has a function of removing wastes and excess sebum in the skin pores, the magnesium promotes the excretion of wastes and helps to bind collagen, the alumina improves blood circulation, and the sodium controls the osmotic pressure and moisture in the body has a function of smoothing out, the calcium helps the body's detoxification, and acts on the iron oxide collagen binding.

In addition, in order for the functions of silicon oxide, magnesium, alumina, sodium, calcium, and iron oxide, which are the far-infrared emitting materials, to be smoothly performed with each other, silicon oxide, magnesium, alumina, sodium, calcium, and iron oxide are each contained in an amount of 0.5 wt% or more in the far-infrared emitting material. It is preferable to include each.

The water repellent is not particularly limited to a non-hydrophilic resin having a property of repelling without absorbing moisture such as sweat, and any water repellent that can be used in textiles for clothing may be used.

The first coating layer 2000 formed on the fabric fiber sheet 1000 for the mask to form an uneven structure contains a water repellent and when moisture such as sweat comes into contact with the coating layer as shown in FIG. 9 , the coating layer due to the water repellent contained in the coating layer It is not absorbed by the mask and is pushed out into the fabric fiber sheet 1000 for which the coating layer is not formed.

Moisture such as sweat pushed out from the first coating layer 2000 is absorbed by the fabric fiber sheet 1000 for a mask, and the first coating layer 2000 that comes into contact with the skin always maintains a dry state, so that comfort is maintained. Therefore, it is preferable that the fabric fiber sheet for a mask with improved antibacterial function of the present invention is used so that the first coating layer 2000 is in contact with the skin.

As the water repellent, at least one selected from the group consisting of a fluorine-based water repellent, a silicone water repellent, an acrylic water repellent, a polyethylene water repellent, a polypropylene water repellent, a polyamide water repellent, a polyester water repellent, and a polymethyl water repellent may be used. , it is preferable to selectively use a fluorine-based water repellent, a silicone-based water repellent, and an acrylic water repellent having excellent processability.

The water repellent may be used together with a solvent, a thickener, etc. in order to increase processability.

As the foaming agent, the first coating layer 2000 containing the far-infrared emitting material and the water repellent is inflated to make the fiber sheet into a concave-convex structure.

In the present invention, as the foaming agent, at least one selected from the group consisting of a silicone foaming agent, a polyurethane foaming agent, a polystyrene foaming agent, a polyethylene foaming agent, a polyvinyl chloride foaming agent, and a polyacrylic foaming agent may be used.

The far-infrared emitting material, water repellent, and foaming agent are mixed together with a binder to form the first coating layer 2000 .

As the binder, any binder used for textile products may be used, and for example, an acrylic binder, a silicone-based bar binder, a polyurethane-based binder, and the like may be used without limitation. Among the above binders, it is preferable to use an acrylic binder that has little skin irritation and is easy to use.

The first coating layer 2000 formed of the far-infrared emitting material, the water repellent, the foaming agent, and the binder as described above is based on 100 parts by weight of the far-infrared emitting material, 150 to 250 parts by weight of the foaming agent, 25 to 50 parts by weight of the water repellent, 250 to 350 parts by weight of the binder. It is preferable to include wealth.

The far-infrared emitting material is preferably contained in about 10 to 20% by weight of the total weight of the coating layer. If the content of the far-infrared emitting material is less than 10% by weight, the amount of far-infrared radiation may be insufficient, and since the amount of far-infrared radiation is not significantly increased if it exceeds 20% by weight, economic efficiency may be deteriorated.

If the content of the foaming agent is less than 150 parts by weight based on 100 parts by weight of the far-infrared emitting material, the high moisture transfer function may be deteriorated due to the insignificant uneven structure of the fiber sheet. It is preferable that 150 to 250 parts by weight of the foaming agent is included because it may be separated.

In addition, if the content of the water repellent is less than 25 parts by weight based on 100 parts by weight of the far-infrared emitting material, the water repellency function of the coating layer may be insufficient and the high moisture transfer function may be deteriorated. If it exceeds 50 parts by weight, the function of the water repellent is effective compared to the content Since it does not rise, it is preferable that 25-50 parts by weight is included.

In addition, if the content of the binder is less than 250 parts by weight based on 100 parts by weight of the far-infrared emitting material, the adhesion of the coating layer may be insufficient and the coating layer may be separated from the fiber sheet. It is preferable that 250 to 350 parts by weight is included because the tactile feel of the product may be reduced.

The first coating layer 2000 may further include a general pigment or a thermochromic pigment in order to enhance the aesthetic feeling of the fiber sheet.

When the fabric fiber sheet 1000 for a mask is dyed, the coating layer may further include a general pigment of the same color or a different color as the fabric fabric sheet for a mask to consider the design elements of the fabric fabric sheet for a mask of the present invention. .

In addition, a thermochromic pigment may be further included in the coating layer to further enhance esthetics.

The thermochromic pigment is a pigment whose color appears or disappears in a specific temperature range, and when heat is absorbed, the structure of the compound is changed to develop or discolor, and when heat is blocked, the color returns to the original compound structure and color is lost or discolored. In general, the raw material of these thermochromic pigments is an electron-donating chromatic organic compound and consists of a donor that emits electrons and an acceptor that accepts electrons.

The interaction of these components gives color to the crystal phase. When heat is applied, the acceptor is separated and there is no interaction, so the color disappears.

It is made of such an electron-donating chromatic organic compound and an electron-accepting compound, and is sensitive to the external environment, especially to oxygen or humidity in the air. It is preferable to use it in the form of microcapsules through a process called micro encapsulation.

As described above, by further including a thermochromic pigment in the first coating layer, the color of the coating layer is discolored at a certain temperature, so that various aesthetic properties can be imparted to the fabric fiber sheet for a mask of the present invention.

Since the general pigment or thermochromic pigment included in the first coating layer should be included within a range that does not impair the functionality of the coating layer, the general pigment or thermochromic pigment is included in 80 to 120 parts by weight based on 100 parts by weight of the far-infrared emitting material. desirable.

The first coating layer 2000 may be applied to the fiber sheet in various forms as shown in FIG. Alternatively, it may be applied in the form of a grid pattern as shown in Fig. 3(c), and may be formed in a design form having a wave pattern or an amorphous pattern as well as the formally designed form of Fig. 3 .

In the present invention, as shown in FIG. 8 , the second coating layer 3000 is formed on the entire surface of the fiber sheet 1000 including the first coating layer 2000 .

The second coating layer 3000 includes an antibacterial composition comprising an ethanol extract of the leaves of Streptonia and an ethanol extract of the leaves of Fanpacho.

The antibacterial composition may be one comprising the ethanol extract of the leaves of Streptonia and the ethanol extract of the leaves of chamomile chamomile in a weight ratio of 4:6 to 6:4.

The Strelitzia (scientific name: Strelitzia nicolai, English name: White bird of paradise) is a kind of bird of paradise native to South Africa, with white flowers of the family Pachoceae. It is also called the White Bird of Paradise or Wild Banana, and it is the largest species among the Birds of Paradise. It grows up to 12m in height and 4m in width, and several stems come out to form a tumble. The gray, straight stems are woody, similar to those of a palm, and there are traces of fallen leaves on the surface. Glossy gray-green leaves of 2m or more hanging on the stem with long thick petioles are arranged in a fan shape like the pilgrim tree, which is a member of the same family.

The present inventors have found that the ethanol extract of the Stresia leaf has an excellent antibacterial action. It was confirmed by the following experimental examples that the ethanol extract of Stregia leaf has excellent antibacterial activity.

The ethanol extract of the Stresia leaf may be used by slicing the Stresia leaf and extracting it with ethanol.

The Ravenala madagascariensis is the only species of the genus Ravenala and inhabits Madagascar. This genus is a close continuation of the genus Bird of Paradise in South Africa and the genus Narrow serrata in South America. It grows to about 10-20m in height, and the stem is erect. At first it is herbaceous, but later it becomes woody, and the stem is round. It got its name because the spot where the leaves fell rises in the shape of a thick stem, and the glossy, dark green leaves at the tip spread to the left and right like an open fan. The leaves are banana leaf-shaped and leathery, and the length is about 2.5m. The flowers are white and the seeds are blue. It is edible because it contains a large amount of starch.

The present inventors have found that the ethanol extract of the leaf of fenugreek leaves has an excellent antibacterial action. The excellent antibacterial activity of the ethanol extract from the leaf of chamomile leaf was confirmed in the following experimental examples.

As described above, it was confirmed in the experimental examples below that the mixture of the ethanol extract of Stresia leaf and the ethanol extract of the leaf of S. oleracea provides significantly superior antibacterial activity than the ethanol extract of the leaf of Stresia or the ethanol extract of the leaf of S.

In addition, the antimicrobial composition may further include a copolymer represented by the following formula (1).

[Formula 1]

where m and n are mole fractions,

m is 0.3 to 0.7, n is 0.3 to 0.7, and m+n is 1.

The copolymer represented by Chemical Formula 1 performs a function of allowing the antimicrobial components of the antimicrobial composition to be better adsorbed to the textile fabric and to be well fixed during subsequent use. And, it performs a function of improving the durability of the fiber sheet by fixing chlorine ions.

The polymer of Formula 1 may have a weight average molecular weight of 50,000 to 300,000, more preferably 150,000 to 250,000.

The antibacterial composition includes 90 to 97% by weight of a mixture of ethanol extract of Stregia leaf and ethanol extract of P. oleraceae contained in a weight ratio of 4:6 to 6:4, and 3 of the copolymer represented by Formula 1 to 10% by weight.

In addition, the antibacterial composition contains 90 to 93% by weight of a mixture of the ethanol extract of Stregia leaf and the leaf ethanol extract of S. oleracea contained in a weight ratio of 4:6 to 6:4, and 3 to 3 to the copolymer represented by Formula 1 7% by weight, and 3 to 7% by weight of the polar organic solvent. As the polar organic solvent, for example, dimethyl formamide (DMF) may be used.

The second coating layer 3000 is Gram-positive bacteria Staphylococcus aureus ( Staphylococcus aureus ), Bacillus bacteria ( Bacillus cereus ) and tooth decay-causing bacteria ( Streptococcus mutans ); Gram-negative bacteria Escherichia coli and Pseudomonas aeruginosa ; and yeasts, Candida albicans ) and dandruff-causing bacteria ( Malassezia furfur );

In the present invention, the application of the second coating layer 3000 including the antimicrobial composition may be performed by various methods known in the art. That is, it may be carried out in a manner such as spraying or dipping. Specifically, the antimicrobial composition may be sprayed on the entire surface of the fiber sheet on which the first coating layer is formed and dried, or the fiber sheet may be dipped in the antimicrobial composition and impregnated with the antimicrobial composition, and then taken out and dried.

Thereafter, a heat treatment process may be performed at 100 to 190° C., and the antibacterial composition may be more firmly fixed to the surface of the bedding fabric by heat treatment.

Hereinafter, the present invention will be described in more detail through Preparation Examples and Examples. However, the following examples are provided to explain the present invention in more detail, and the scope of the present invention is not limited by the following examples. The following examples can be appropriately modified and changed by those skilled in the art within the scope of the present invention.

Preparation Example 1: ethanol extract of Stregia leaf

The dried Stregia leaves were finely pulverized into 5-10 mesh to prepare Stresia leaf powder. Next, 10 L of ethanol having a concentration of 60% (v/v) was mixed with 1 kg of the straria leaf powder, and then, using a stirrer, the extract solution was prepared by stirring at 60-80° C. at a stirring speed of 300 rpm for 2 hours. did.

Next, the extract solution was first filtered using a non-woven filter paper, and then the first filtrate was second filtered using a diatomaceous earth filter so that no precipitate was formed.

The recovered secondary filtrate was concentrated under reduced pressure at 60° C. using a concentrator to obtain 2 kg of an ethanol extract of Stregia leaf.

Preparation Example 2: Preparation of an ethanol extract from the leaves of chamomile

After shredding the leaves of Japanese sagebrush, 10 L of ethanol having a concentration of 60% by volume was mixed with 1 kg of ethanol, and then, using a stirrer, the extract solution was prepared by stirring at 60-80°C at a stirring speed of 300rpm for 3 hours.

Next, the extract solution was first filtered using a non-woven filter paper, and then the first filtrate was second filtered using a diatomaceous earth filter so that no precipitate was formed. The filtrate was concentrated under reduced pressure at 60° C. using a concentrator to obtain 2 kg of an ethanol extract from the leaves of fenugreek.

Preparation Example 3: Synthesis of the copolymer of Formula 1

3-[[2-(Methacryloyloxy)ethyl]dimethylamino]propionate (3-[[2-(Methacryloyloxy)ethyl]dimethylammonio]propionate, CAS No.24249-95- 4) and 3-(trimethoxysilyl)propyl methacrylate (3-(Trimethoxysilyl)propyl methacrylate) were added in a molar ratio of 0.5:0.5, and 0.5 parts by weight of normal mercaptan was mixed with 100 parts by weight of the total monomer to uniformly made.

The polymerization solution prepared above was put into a 20 L reactor at a rate of 10 L/hr and polymerized at a temperature of 100°C, and unreacted monomers and reaction solvent were removed at a temperature of 150°C in a volatilization tank, followed by washing, dehydration, and drying. Thus, a copolymer of Formula 1 having a weight average molecular weight of 220,000 was obtained.

[Formula 1]

In the above formula, m and n are mole fractions, and m=0.5 and n=0.5.

Example 1: Manufacture of fiber sheet with improved antibacterial function

A first coating layer composition was prepared by mixing 15% by weight of a far-infrared emitting material, 30% by weight of a polyacrylic foaming agent, 5% by weight of a polymethyl-based water repellent, 45% by weight of an acrylic binder, and 5% by weight of other additives such as admixtures and dispersants.

The far-infrared emitting material was mixed with silicon oxide, magnesium, alumina, sodium, calcium, and iron oxide in the same weight.

The first coating layer composition was printed on one side of a fiber sheet made of 90% by weight of polyester fiber and 10% by weight of polyurethane fiber by roll printing to form a first coating layer having a hexagonal dot shape. The first coating layer was coated on about 68% of the surface area of one surface of the fiber sheet.

An antibacterial composition prepared by mixing the ethanol extract of the Stresia leaf prepared in Preparation Example 1 and the ethanol extract of the leaf chamomile leaf prepared in Preparation Example 2 in a weight ratio of 1:1 was prepared.

The fiber sheet on which the first coating layer was formed was immersed in the antimicrobial composition for 5 hours to coat the antimicrobial composition and dried. Thereafter, heat treatment was performed at a temperature of about 110° C. for about 40 seconds to form a second coating layer.

Example 2: Manufacture of fiber sheet with improved antibacterial function

A fiber sheet having a first coating layer prepared in the same manner as in Example 1 was used.

95% by weight of a mixture obtained by mixing the ethanol extract of Stregia leaf prepared in Preparation Example 1 and the ethanol extract of fenugreek leaf prepared in Preparation Example 2 in a weight ratio of 1:1 and the copolymer of Formula 1 prepared in Preparation Example 3 was added in an amount of 5% by weight to prepare an antibacterial solution composition.

The fiber sheet on which the first coating layer was formed was immersed in the antimicrobial composition for 5 hours to coat the antimicrobial composition and dried. Thereafter, heat treatment was performed at a temperature of about 110° C. for about 40 seconds to form a second coating layer.

Comparative Example 1: Fabrication of a fiber sheet

A fiber sheet having a first coating layer was prepared in the same manner as in Example 1. However, unlike Example 1, the second coating layer was not formed.

Test Example 1: Safety evaluation of fiber sheet with improved antibacterial function

The safety of the ethanol extract of Stregia leaf and the ethanol extract of Fanpaco leaf prepared in Preparation Examples 1 and 2 was tested through a 48-hour patch test using Guinea Pig. The degree of irritation was evaluated and the results are shown in Table 1 below.

<Evaluation criteria>

○: Non-irritating (no erythema and edema)

△: mild irritation (very mild erythema and edema)

×: moderate irritation (moderate edema and obvious erythema)

As shown in Table 1, it was confirmed that the ethanol extract of Stregia leaf and the leaf ethanol extract of Japanese cypress leaf extract prepared in Preparation Examples 1 and 2 were safe for the skin.

Test Example 2: Measurement of antibacterial activity of plant extracts

The ethanol extract of Stresia leaf of Preparation Example 1, the leaf ethanol extract of Preparation Example 2, and the ethanol extract of the leaves of Preparation Example 1 and the ethanol extract of the leaf of Preparation Example 2 of Banana grasshopper leaf in a weight ratio of 1:1 The antibacterial activity of the mixed extract was measured.

Representative food poisoning bacteria (Bacillus cereus, Bacillus subtilis, Campylobacter jejuni, Escherichia coli, Escherichia coli O-157, Listeria monocytogenes, Pseudomonas aeruginosa, Staphylococcus aureus, Salmonella enteritidis, Salmonella thypimurium, Vibrio parahaemolyticus) were used.

The bacteria were inoculated with 50 μl of the culture in 10 ml of sterile TSB medium and subcultured at 30° C. for 24±1 hours. The concentration of this culture was maintained at an Abs 0.6±0.1 at an absorption wavelength of 655 nm in a microplate reader. ^{The subcultured test bacteria were diluted 10 -3} times with sterile distilled water, and the disc diffusion method was performed. That is, the diluted strain is put on a sterile cotton swab and spread on a plate medium with a thickness of 4 mm, and a sterilized 8 mm (thickness 1 mm) paper is raised, the ethanol extract of the Stresia leaf of Preparation Example 1, and the ethanol extract of the leaf of Japanese pea leaf of Preparation Example 2 , and 50 μl of the extract obtained by mixing the ethanol extract of Stregia leaf of Preparation Example 1 and the ethanol extract of the leaf chamomile leaf of Preparation Example 2 in a weight ratio of 1:1, respectively, was injected. After sufficient inhalation for about 20 minutes, culture was performed for 24±1 hours and growth rings were confirmed.

The antibacterial activity of the extracts was evaluated by measuring the size of the translucency including the filter paper (diameter 8mm), and the results are shown in Table 2 below.

Co., Ltd. ^a : ATCC American Type Culture Collection, KCTC Center for Biological Resources, Korea Research Institute of Bioscience and Biotechnology; KCCM Korea Sprout Association

^b : size of transparencies (diameter mm)

As can be seen in Table 2 above, both the Stregia alcohol extract prepared in Preparation Example 1 and the chamomile leaf extract prepared in Preparation Example 2 exhibited excellent antibacterial activity against all bacteria.

In particular, the mixed extracts of the ethanol extract of Stregia leaf and the ethanol extract of the leaf of Panaxafolia showed much superior antibacterial activity than the respective extracts.

Test Example 3: Measurement of antibacterial activity of fiber sheet

The antibacterial activity of the antibacterial fiber sheets prepared in Examples 1 and 2 and Comparative Example 1 was measured.

Representative food poisoning bacteria (Bacillus cereus, Bacillus subtilis, Campylobacter jejuni, Escherichia coli, Escherichia coli O-157, Listeria monocytogenes, Pseudomonas aeruginosa, Staphylococcus aureus, Salmonella enteritidis, Salmonella thypimurium, Vibrio parahaemolyticus) were used.

The bacteria were inoculated with 50 μl of the culture in 10 ml of sterile TSB medium and subcultured at 30° C. for 24±1 hours. The concentration of this culture was maintained at an Abs 0.6±0.1 at an absorption wavelength of 655 nm in a microplate reader. ^{The subcultured test bacteria were diluted 10 -3} times with sterile distilled water, and the disc diffusion method was performed. That is, the diluted strain is put on a sterile cotton swab and spread on a plate medium with a thickness of 4 mm, and the antibacterial fiber fabrics prepared in Examples 1 and 2 and Comparative Example 1 are cut into circles with a diameter of 8 mm and raised, and then cultured for 24±1 hours. and the growth ring was confirmed.

The antibacterial activity of the antibacterial fabrics of Examples 1 and 2 and Comparative Example 1 was evaluated by measuring the size of the transparent band including the antibacterial fabric (diameter 8mm), and the results are shown in Table 3 below.

Co., Ltd. ^a : ATCC American Type Culture Collection, KCTC Center for Biological Resources, Korea Research Institute of Bioscience and Biotechnology; KCCM Korea Sprout Association

^b : size of transparencies (diameter mm)

As can be seen in Table 3, the fiber sheet of Example 1 exhibited excellent antibacterial activity against all bacteria by the formation of the second coating layer.

In particular, the fiber sheet of Example 2 exhibited superior antibacterial activity against all bacteria by forming a second coating layer further comprising the copolymer compound of Formula 1. These results suggest that the fiber sheet of Example 2, in which the second coating layer further containing the copolymer compound of Formula 1 was formed, exhibits better antibacterial activity because the antibacterial active ingredient is better fixed to the fabric by the copolymer.

On the other hand, in the fiber sheet of Comparative Example 1 in which the second coating layer, which is an antibacterial coating layer, was not formed, a transparent band showing antibacterial activity was not observed, and thus it was confirmed that there was no antibacterial function.

Although representative embodiments of the present invention have been described in detail above, those of ordinary skill in the art to which the present invention pertains will understand that various modifications are possible without departing from the scope of the present invention with respect to the above-described embodiments. . Therefore, the scope of the present invention should not be limited to the described embodiments, and should be defined by the claims described below as well as the claims and equivalents.

100: mask
101: wear strap
105: connection part
110: filtration unit
120: collection unit
130: string attachment part
131: first drying unit
131a: connection part
132: second drying unit
140: adhesion part
160: wire
160a: insertion part
210: first vertical frame
210a: first body
210b: second body
211: rotating part
212: first coupling part
213: second coupling part
220: second vertical frame
230: third vertical frame
240: first horizontal frame
250: second horizontal frame
260: third horizontal frame
300: blocking layer
310: spacer member
310a: separation space
320: ventilation
330: opening and closing part
400: elastic winding part
1000: fiber sheet
2000: first coating layer
3000: second coating layer
A : Separation part
B : guide structure
C: coupling part
S: breathing space
R: Rotation direction
F1: 1st Euro
F2: 2nd Euro

Claims (6)

a filtration unit that forms a breathing space separated from the atmosphere and filters foreign substances in the incoming air;
a collecting unit provided inside the filtering unit and collecting moisture;
a string attachment portion formed at both ends of the filtering unit and to which a wearing string is connected; and
Is formed in the attachment part of the string, is connected to the collecting part to absorb the moisture, and a drying unit formed so as to be exposed to the outside from the attachment part;
The collection unit,
It is formed of a waterproof material as one of the coating layers for coating a part of vinyl, film, and the filter part,
A mask including a moisture collecting surface that extends from the central portion to both ends and is curved to guide the moisture collected by lowering the both ends to be transferred to the drying unit. delete The method according to claim 1,
The drying unit has one end connected to the collecting unit disposed inside the filtering unit, and the other end of the drying unit is formed to be exposed to the atmosphere outside the string attachment unit, and the moisture absorbed from the inside is removed from the outside of the drying unit. A mask including a moisture-collecting surface that is dried by atmospheric dry air. The method according to claim 1,
Further comprising a frame disposed on the inside of the filter unit,
The frame is
a vertical frame including a first vertical frame, a second vertical frame and a third vertical frame spaced apart from each other in the horizontal direction; and a first horizontal frame spaced apart from each other in the vertical direction, a horizontal frame including a second horizontal frame and a third horizontal frame, the mask including a moisture collecting surface. 5. The method according to claim 4,
The frame is
a rotating part provided on the folding part on the extension line of the frame so that it can be folded; and
A mask including a moisture collecting surface, comprising a first coupling part and a second coupling part coupled to each other at a point in contact with each other by the folding. The method according to claim 1,
The wearing strap is
It extends through the inside of the filter unit from the end side, and is wound and passed through the elastic winding unit in the path passing through the inside,
The elastic winding part elastically pulls the wearing strap to maintain a predetermined tension on the wear strap, the mask including a moisture collecting surface.

Images