KR102224342B1 - A Mortar Composition of Crack-Reducing Type for High-Performance Floor and Constructing Methods Using Thereof - Google Patents

A Mortar Composition of Crack-Reducing Type for High-Performance Floor and Constructing Methods Using Thereof Download PDF

Info

Publication number
KR102224342B1
KR102224342B1 KR1020200099132A KR20200099132A KR102224342B1 KR 102224342 B1 KR102224342 B1 KR 102224342B1 KR 1020200099132 A KR1020200099132 A KR 1020200099132A KR 20200099132 A KR20200099132 A KR 20200099132A KR 102224342 B1 KR102224342 B1 KR 102224342B1
Authority
KR
South Korea
Prior art keywords
parts
weight
polyurea resin
eco
resin
Prior art date
Application number
KR1020200099132A
Other languages
Korean (ko)
Inventor
정성민
Original Assignee
정성민
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 정성민 filed Critical 정성민
Priority to KR1020200099132A priority Critical patent/KR102224342B1/en
Application granted granted Critical
Publication of KR102224342B1 publication Critical patent/KR102224342B1/en

Abstract

The present invention relates to an eco-friendly waterproofing composition containing a polyurea resin, which comprises: 3 to 20 parts by weight of an anionic emulsifying agent; 5 to 20 parts by weight of charcoal powder; 2 to 15 parts by weight of silica; 20 to 60 parts by weight of a curing agent; 1 to 10 parts by weight of octylphenol ethoxylate; 1 to 20 parts by weight of polyvinyl alcohol; 0.1 to 5 parts by weight of cellulose fibers; 3 to 20 parts by weight of nano-ceramic particles; 1 to 20 parts by weight of a thickener; 1 to 20 parts by weight of an adhesion improver; 5 to 30 parts by weight of an anti-peeling agent; and 3 to 10 parts by weight of an antioxidant with respect to 100 parts by weight of the polyurea resin, and to a construction method thereof. According to the present invention, an eco-friendly waterproofing composition, and specifically, to an eco-friendly waterproofing composition containing a polyurea resin is obtained by applying a coating agent with excellent penetrability to a microcrack and a capillary pore of a structure to a waterproofing method, thereby forming an additional protective layer, solidifying the bond between a base surface which can be easily damaged by an external load or impact, and an interface of a waterproofing agent, and improving permeability resistance, and thus, durability can be remarkably improved. Moreover, the eco-friendly waterproofing composition according to the present invention can be quickly cured compared to a waterproofing agent composition using a polymer resin such as polyurethane, thereby reducing a work time as well as forming a uniform waterproofing film by a spray dispersion method.

Description

폴리우레아 수지를 포함하는 친환경 방수제 조성물 및 이의 시공방법{A Mortar Composition of Crack-Reducing Type for High-Performance Floor and Constructing Methods Using Thereof}Eco-friendly waterproofing composition containing polyurea resin and its construction method {A Mortar Composition of Crack-Reducing Type for High-Performance Floor and Constructing Methods Using Thereof}

본 발명은 폴리우레아 수지를 포함하는 친환경 방수제 조성물에 관한 것으로서, 보다 상세하게는 구조벽, 교량, 건축물, 해양 구조물, 탱크, 철판, 바닥면 등의 바탕면에 적용 가능한 폴리우레아 수지를 포함하는 친환경 방수제 조성물에 관한 것이다.The present invention relates to an eco-friendly waterproofing composition comprising a polyurea resin, and more specifically, an eco-friendly polyurea resin that can be applied to a base surface such as structural walls, bridges, buildings, offshore structures, tanks, steel plates, and floors. It relates to a waterproofing composition.

일반적으로 방수제, 특정적으로 도막 방수제라 함은 수성 또는 유성의 액상 형태의 방수제를 각종 건축물 및 구조벽의 표면에 도포하고 수분 또는 용제가 증발되고 남은 피막을 이용하여 방수효과를 거두는 조성물을 지칭한다.In general, a waterproofing agent, specifically a coating waterproofing agent, refers to a composition in which a water-based or oil-based liquid waterproofing agent is applied to the surface of various buildings and structural walls, and a waterproofing effect is achieved by using the remaining film after moisture or solvent evaporation. .

이러한 도막 방수제는 통상적으로 건축 또는 토목 구조물의 옥상방수, 외부방수, 지하 구조물의 옹벽 내지 천정방수 또는 화장실, 욕실, 베란다 등의 실내방수 등을 위해 사용되고 있다.These coating waterproofing agents are generally used for roof waterproofing, external waterproofing, retaining wall or ceiling waterproofing of underground structures, or indoor waterproofing of toilets, bathrooms, verandas, etc. of architectural or civil structures.

현재 널리 보급된 도막 방수제로는 고무화 아스팔트, 아크릴고무 또는 아크릴 수지 등을 주성분으로 하는 에멀젼형과 클로로프렌이나 클로로설폰화 폴리에틸렌을 포함하거나 우레탄이나 에폭시수지가 주성분인 반응형이 있으며, 이들 중 가장 널리 사용되는 것이 우레탄계 도막 방수제와 고무화 아스팔트계 도막 방수제이다.Currently widely used coating waterproofing agents include an emulsion type containing rubberized asphalt, acrylic rubber, or acrylic resin as the main component, and a reactive type containing chloroprene or chlorosulfonated polyethylene, or urethane or epoxy resin as the main component. Urethane-based coating film waterproofing agents and rubberized asphalt-based coating film waterproofing agents are used.

고무화 아스팔트계 도막 방수제는 아스팔트에 스티렌 계통의 중합체, 에틸렌-비닐 아세테이트 또는 스티렌-부타디엔 라텍스 등을 혼합함으로써 아스팔트가 가질 수 없는 성질, 즉 우수한 신장율, 내균열성, 내한성, 접합성 등을 갖도록 개질시킨 것이다.Rubberized asphalt-based coating waterproofing agent is modified to have properties that asphalt cannot have by mixing a styrene-based polymer, ethylene-vinyl acetate or styrene-butadiene latex with asphalt, that is, excellent elongation, crack resistance, cold resistance, and bonding properties. will be.

또한, 도막 방수제는 내열성, 강도 및 경도를 강화시키기 위해 계면활성제나 경화촉진제 등을 첨가하기도 하며, 열가소성 엘라스토머 등을 첨가하는 경우도 있다.In addition, a surfactant or a curing accelerator may be added to the coating film waterproofing agent to enhance heat resistance, strength, and hardness, and a thermoplastic elastomer may be added thereto.

하지만, 전술한 고무화 아스팔트계 도막 방수제는 신장율, 내균열성, 접합성이 우수한 장점이 있지만, 복원력이 약하며 내화학성, 내오존성, 내자외선성이 좋지 않다.However, the above-described rubberized asphalt-based waterproofing agent has advantages of excellent elongation, crack resistance, and adhesion, but has poor resilience and poor chemical resistance, ozone resistance, and ultraviolet resistance.

특히, 스티렌부타디엔 고무를 주성분으로 하는 도막 방수제는 복원력이 매우 약하여 반복적으로 신장될 경우 열화현상이 발생되며 고유의 물리적 특성을 잃게 되는 문제점이 있다.In particular, coating waterproofing agents containing styrene butadiene rubber as a main component have a very weak resilience, and thus, when repeatedly elongated, deterioration occurs and inherent physical properties are lost.

이러한, 문제점을 극복하기 위해 대한민국 특허 제10-0731614호에는 고복원력을 갖고 내화학성, 내오존성 및 내자외선성을 향상시킬 수 있도록 수계 클로로프렌 고무와 유화 아스팔트 및 첨가제를 혼합한 도막 방수제가 개시되어 있다.In order to overcome these problems, Korean Patent No. 10-0731614 discloses a coating waterproofing agent in which water-based chloroprene rubber and emulsified asphalt and additives are mixed to have high resilience and improve chemical resistance, ozone resistance, and UV resistance. .

한편, 콘크리트 교면에 적용되는 방수공법으로는 침투식 방수공법, 시트식 방수공법 및 도막식 방수공법이 있다. 침투식 방수공법은 적용하기에 매우 간편하고 경제적인 이유로 폭넓게 사용되어 왔으나 고강도 콘크리트 교면에는 방수제가 충분히 침투되지 않아 방수성능을 기대할 수 없는 단점이 있으며, 시트식 방수공법은 저온특성이 떨어져 우리나라와 같이 사계절이 있는 나라의 경우 콘크리트 교면의 방수성능 향상에 큰 효과를 나타내지 못하는 문제점이 있다. On the other hand, as the waterproofing method applied to the concrete bridge, there are penetration type waterproofing method, sheet type waterproofing method, and coating type waterproofing method. The penetration-type waterproofing method is very simple to apply and has been widely used for economic reasons, but there is a disadvantage that waterproofing performance cannot be expected because the waterproofing agent does not sufficiently penetrate into the high-strength concrete bridge surface. In the case of a country with four seasons, there is a problem that it does not show a great effect in improving the waterproof performance of the concrete bridge surface.

따라서 최근에는 합성수지재료를 도포해서 방수도막을 형성시켜 시공하는 도막식방수공법이 선호되고 있다.Therefore, in recent years, a coating-type waterproofing method in which a synthetic resin material is applied to form a waterproof coating for construction is preferred.

도막식 방수공법을 적용한 예를 살펴보면, 대한민국 공개특허 제 1999-37809호에는, 교량 등의 표면에 에폭시 프라이머 층을 도포하고 그 위에 속건성 고분자 수지층과 지건성 고분자 수지층 및 세석골재층을 형성하는 교면 방수공법이 개시되어 있다.Looking at an example of applying the coating-type waterproofing method, Korean Patent Laid-Open No. 1999-37809, in which an epoxy primer layer is applied to the surface of a bridge, etc., and a quick-drying polymer resin layer, an oil-drying polymer resin layer, and a fine stone aggregate layer are formed thereon. The bridge surface waterproofing method is disclosed.

하지만, 상기 공개특허에 개시된 교면 방수공법에 적용된 고분자 수지층은 5초 이내에 경화되는 속건성 이어서 아스팔트 콘크리트와 아스팔트 및 에폭시 프라이머 층이 상호 융합되기도 전에 각 층이 분리되거나 크랙이 발생하는 바, 충분한 방수효과를 기대할 수 없다. 또한, 프라이머층 위에 속건성 및 지건성 고분자 수지 층과 세석골재층 등 다양한 처리층을 형성해야하는데, 이와 같이 다중층을 적층하지 않으면 각 층의 접착력이 약해져서 밀리게 되어 층분리 현상이 발생하게 되는바, 실제로 시공을 할 수 없거나 시공을 하더라도 방수효과가 떨어지는 문제점이 있다.However, the polymer resin layer applied to the bridge surface waterproofing method disclosed in the above patent is quick-drying that hardens within 5 seconds, so that each layer is separated or cracked before the asphalt concrete, asphalt, and epoxy primer layers are fused together. Can't expect. In addition, various treatment layers, such as a quick-drying and oil-drying polymer resin layer and a fine stone aggregate layer, must be formed on the primer layer.If multiple layers are not stacked in this way, the adhesive strength of each layer is weakened and the layer separation phenomenon occurs. , There is a problem that the waterproof effect is inferior even if it cannot be actually constructed or even if it is constructed.

이러한 다중층의 문제점을 보완하기 위하여 대한민국 공개특허 제 2002-76214호에서는 교량 등의 표면에 폴리우레탄수지 프라이머층을 도포한 후 그 위에 속건성 고분자 수지층을 형성하고, 그 위에 과량의 이소시아네이트를 첨가한 폴리우레탄 제조 혼합물을 도포한 후 아스팔트 접착제층과 아스팔트 콘크리트층을 차례로 적층하는 처리방법을 개시하고 있다. In order to compensate for this multi-layer problem, Korean Patent Application Publication No. 2002-76214 applies a polyurethane resin primer layer to the surface of a bridge, and then forms a quick-drying polymer resin layer thereon, and an excess of isocyanate is added thereon. Disclosed is a treatment method of sequentially laminating an asphalt adhesive layer and an asphalt concrete layer after applying a polyurethane preparation mixture.

그러나 이 방법은 폴리우레탄 제조 혼합물층에 존재하는 과량의 이소시아네이트가 주위의 습기와 반응하여 오히려 결합력이 약해지는 단점이 있으며, 이러한 문제점을 방지하기 위해 현장에서 작업시 매우 주의를 요하는 까다로운 작업공정을 필요로 하게 되는 또 다른 문제점이 발생한다.However, this method has the disadvantage that the bonding strength is weakened due to the reaction of the excess isocyanate present in the polyurethane production mixture layer with the surrounding moisture. Another problem arises that becomes necessary.

본 발명은 상기와 같은 문제점을 해결하기 위해 창출한 것으로서, 구조물의 미세균열 및 모세관 공극 등에의 침투성능이 우수하여 내투수 저항성이 탁월하고, 외부하중이나 충격 등으로 손상받기 쉬운 바탕면과 방수제 계면의 결합을 공고히 함으로써 바탕면의 내구성을 대폭 향상시킬 수 있도록 하는 친환경 방수제 조성물을 제공하고자 한다.The present invention was created to solve the above problems, and has excellent penetration performance into microcracks and capillary voids of structures, so that the water permeability resistance is excellent, and the interface between the base surface and the waterproofing agent, which is susceptible to damage by external loads or impacts, etc. It is intended to provide an eco-friendly waterproofing composition that can significantly improve the durability of the base surface by solidifying the combination of the.

본 발명은The present invention

폴리우레아 수지 100중량부 기준으로,Based on 100 parts by weight of polyurea resin,

음이온 유화제 3 내지 20중량부;3 to 20 parts by weight of an anionic emulsifier;

숯가루 5 내지 20중량부;5 to 20 parts by weight of charcoal powder;

실리카 2 내지 15중량부;2 to 15 parts by weight of silica;

경화제 20 내지 60중량부;20 to 60 parts by weight of a curing agent;

옥틸페놀에톡실레이트 1 내지 10중량부;1 to 10 parts by weight of octylphenol ethoxylate;

폴리비닐알코올 1 내지 20중량부;1 to 20 parts by weight of polyvinyl alcohol;

셀룰로오스 섬유 0.1 내지 5중량부; 0.1 to 5 parts by weight of cellulose fibers;

나노세라믹 입자 3 내지 20중량부; 3 to 20 parts by weight of nanoceramic particles;

증점제 1 내지 20중량부;1 to 20 parts by weight of a thickener;

부착증진제 1 내지 20중량부;1 to 20 parts by weight of adhesion promoter;

박리방지제 5 내지 30중량부; 및5 to 30 parts by weight of an anti-peeling agent; And

산화방지제 3 내지 10중량부를 포함하는 친환경 방수제 조성물을 제공한다.It provides an eco-friendly waterproofing composition comprising 3 to 10 parts by weight of an antioxidant.

또한, Also,

본 발명은The present invention

방수제 조성물을 시공하기 위한 시공표면을 처리하는 표면처리단계;Surface treatment step of treating the construction surface for applying the waterproofing agent composition;

상기 표면처리단계가 종료된 후 프라이머를 도포하는 프라이머 도포단계;A primer application step of applying a primer after the surface treatment step is finished;

상기 프라이머 도포단계가 종료된 상단에 폴리우레아 수지 100중량부 기준으로, 음이온 유화제 3 내지 20중량부, 숯가루 5 내지 20중량부, 실리카 2 내지 15중량부, 경화제 20 내지 60중량부, 옥틸페놀에톡실레이트 1 내지 10중량부, 폴리비닐알코올 1 내지 20중량부, 셀룰로오스 섬유 0.1 내지 5중량부, 나노세라믹 입자 3 내지 20중량부, 증점제 1 내지 20중량부, 부착증진제 1 내지 20중량부, 박리방지제 5 내지 30중량부, 및 산화방지제 3 내지 10중량부 포함하는 친환경 방수제 조성물을 스프레이 방식으로 분사하는 스프레이 분사단계; 및 Based on 100 parts by weight of the polyurea resin on the upper end of the primer application step, 3 to 20 parts by weight of anionic emulsifier, 5 to 20 parts by weight of charcoal powder, 2 to 15 parts by weight of silica, 20 to 60 parts by weight of a curing agent, octylphenol Ethoxylate 1 to 10 parts by weight, polyvinyl alcohol 1 to 20 parts by weight, cellulose fiber 0.1 to 5 parts by weight, nanoceramic particles 3 to 20 parts by weight, thickener 1 to 20 parts by weight, adhesion promoter 1 to 20 parts by weight, A spray spray step of spraying an eco-friendly waterproofing composition comprising 5 to 30 parts by weight of a peeling inhibitor and 3 to 10 parts by weight of an antioxidant by a spray method; And

상기 스프레이 분사단계가 종료된 후 양생하는 양생단계를 포함하는 친환경 방수제 조성물 시공방법을 제공한다.It provides an eco-friendly waterproofing composition construction method including a curing step of curing after the spray spraying step is finished.

본 발명에 따른 친환경 방수제 조성물, 특정적으로 폴리우레아 수지를 포함하는 친환경 방수제 조성물은 구조물의 미세균열 및 모세관 공극 등에의 침투성능이 우수한 도포제를 방수공법에 적용함으로써, 추가적 보호막을 형성할 수 있고, 외부하중이나 충격 등으로 손상받기 쉬운 바탕면과 방수제 계면의 결합을 공고히 할 수 있을 뿐만 아니라 내투수 저항성을 향상시킬 수 있어 내구성을 대폭 향상시킬 수 있다.The eco-friendly waterproofing composition according to the present invention, specifically an eco-friendly waterproofing composition comprising a polyurea resin, can form an additional protective film by applying a coating agent having excellent penetration performance into microcracks of structures and capillary voids, etc. to the waterproofing method, Not only can the bonding between the surface of the surface, which is easily damaged by external loads or impacts, and the interface of the waterproofing agent, but also the water permeable resistance can be improved, greatly improving the durability.

더욱이, 본 발명에 따른 친환경 방수제 조성물은 폴리우레탄 등의 고분자 수지를 사용한 방수제 조성물과 비교하여 신속히 경화함으로써, 작업시간을 단축시킬 수 있을 뿐만 아니라, 스프레이 분산방법으로 균일한 방수도막을 형성할 수 있다.Moreover, the eco-friendly waterproofing composition according to the present invention cures quickly compared to the waterproofing composition using a polymer resin such as polyurethane, so that the working time can be shortened, and a uniform waterproofing film can be formed by the spray dispersion method. .

이하, 본 발명을 구체적으로 설명한다.Hereinafter, the present invention will be described in detail.

한 가지 관점에서, 본 발명은 폴리우레아 수지 100중량부 기준으로, 음이온 유화제 3 내지 20중량부; 숯가루 5 내지 20중량부; 실리카 2 내지 15중량부; 경화제 20 내지 60중량부; 옥틸페놀에톡실레이트 1 내지 10중량부; 폴리비닐알코올 1 내지 20중량부; 셀룰로오스 섬유 0.1 내지 5중량부; 나노세라믹 입자 3 내지 20중량부; 증점제 1 내지 20중량부; 부착증진제 1 내지 20중량부; 박리방지제 5 내지 30중량부; 및 산화방지제 3 내지 10중량부를 포함하는 친환경 방수제 조성물을 제공한다.In one aspect, the present invention, based on 100 parts by weight of the polyurea resin, 3 to 20 parts by weight of an anionic emulsifier; 5 to 20 parts by weight of charcoal powder; 2 to 15 parts by weight of silica; 20 to 60 parts by weight of a curing agent; 1 to 10 parts by weight of octylphenol ethoxylate; 1 to 20 parts by weight of polyvinyl alcohol; 0.1 to 5 parts by weight of cellulose fibers; 3 to 20 parts by weight of nanoceramic particles; 1 to 20 parts by weight of a thickener; 1 to 20 parts by weight of adhesion promoter; 5 to 30 parts by weight of an anti-peeling agent; And it provides an environmentally friendly waterproofing composition comprising 3 to 10 parts by weight of an antioxidant.

다른 관점에서, 본 발명은 방수제 조성물을 시공하기 위한 시공표면을 처리하는 표면처리단계; 상기 표면처리단계가 종료된 후 프라이머를 도포하는 프라이머 도포단계; 상기 프라이머 도포단계가 종료된 상단에 폴리우레아 수지 100중량부 기준으로, 음이온 유화제 3 내지 20중량부, 숯가루 5 내지 20중량부, 실리카 2 내지 15중량부, 경화제 20 내지 60중량부, 옥틸페놀에톡실레이트 1 내지 10중량부, 폴리비닐알코올 1 내지 20중량부, 셀룰로오스 섬유 0.1 내지 5중량부, 나노세라믹 입자 3 내지 20중량부, 증점제 1 내지 20중량부, 부착증진제 1 내지 20중량부, 박리방지제 5 내지 30중량부, 및 산화방지제 3 내지 10중량부를 포함하는 친환경 방수제 조성물을 스프레이 방식으로 분사하는 스프레이 분사단계; 및 상기 스프레이 분사단계가 종료된 후 양생하는 양생단계를 포함하는 친환경 방수제 조성물 시공방법을 제공한다.In another aspect, the present invention is a surface treatment step of treating a construction surface for constructing a waterproofing agent composition; A primer application step of applying a primer after the surface treatment step is finished; Based on 100 parts by weight of the polyurea resin on the upper end of the primer application step, 3 to 20 parts by weight of anionic emulsifier, 5 to 20 parts by weight of charcoal powder, 2 to 15 parts by weight of silica, 20 to 60 parts by weight of a curing agent, octylphenol Ethoxylate 1 to 10 parts by weight, polyvinyl alcohol 1 to 20 parts by weight, cellulose fiber 0.1 to 5 parts by weight, nanoceramic particles 3 to 20 parts by weight, thickener 1 to 20 parts by weight, adhesion promoter 1 to 20 parts by weight, A spray spray step of spraying an eco-friendly waterproofing composition comprising 5 to 30 parts by weight of a peeling inhibitor and 3 to 10 parts by weight of an antioxidant in a spray manner; And it provides an eco-friendly waterproofing composition construction method comprising a curing step of curing after the spray spraying step is finished.

본 발명에 따른 친환경 방수제 조성물, 특정적으로 폴리우레아 수지를 포함하는 친환경 방수제 조성물은 각종 구조물, 구조벽, 교량, 건축물, 해양 구조물, 탱크, 철판, 바닥면 등의 바탕면에 적용되어 방수성을 제공한다.The eco-friendly waterproofing composition according to the present invention, specifically an eco-friendly waterproofing composition containing a polyurea resin, is applied to various structures, structural walls, bridges, buildings, offshore structures, tanks, steel plates, and floor surfaces to provide waterproofness. do.

본 발명에 따른 폴리우레아는 신속히 경화가 가능하고, 내화학성, 자외선에 대한 내성이 좋아 방수수명이 길고, -50 내지 180℃의 온도범위까지의 내열성이 강하여 시공시 온도에 영향을 받지 않을 뿐만 아니라, 빠른 경화로 수직면에 일정한 도막두께를 확보하는 것이 가능하여 스프레이 분사를 통해 도막을 형성하는 방법에 적용하기 용이하다.The polyurea according to the present invention can be quickly cured, has a long waterproof life due to good chemical resistance and resistance to ultraviolet rays, and has strong heat resistance up to a temperature range of -50 to 180°C, so it is not affected by the temperature during construction. , It is possible to secure a constant film thickness on the vertical surface by fast curing, so it is easy to apply to the method of forming a coating film through spray spraying.

본 발명에 따른 친환경 방수제 조성물, 특정적으로 폴리우레아 수지를 포함하는 친환경 방수제 조성물을 구성하는 폴리우레아 수지 외 나머지 성분들의 함량은 폴리우레아 수지 100중량부 기준으로 한다.The content of the remaining components other than the polyurea resin constituting the eco-friendly waterproofing composition according to the present invention, specifically the eco-friendly waterproofing composition including the polyurea resin, is based on 100 parts by weight of the polyurea resin.

본 발명에 따른 음이온 유화제(Anionic emulsifier)는 방수제 조성물을 구성하는 각 구성성분 및 반응물 등을 용이하게 분산시키기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 음이온 유화제라면 어떠한 것을 사용하여도 무방하다.The anionic emulsifier according to the present invention is for easily dispersing each component and reactant constituting the waterproofing composition, and any conventional anionic emulsifier in the art for this purpose may be used.

바람직한 음이온 유화제로는 수지산나트륨염, 리그닌술폰산알카리금속염, 나프탈렌 설포닉 산(Naphthalene Sulfonic acid) 유도체, 클로로벤젠(Chlorobenzene) 유도체, 고급지방산알카리금속염, 알킬벤젠슬폰산염, 알파-올레핀슬폰산염, 폴리옥시에칠렌알킬페닐에텔류, 알킬아릴슬폰산나트륨류 또는 이들의 혼합물을 사용할 수 있다.Preferred anionic emulsifiers include sodium resinate salt, lignin sulfonic acid alkali metal salt, naphthalene sulfonic acid derivative, chlorobenzene derivative, higher fatty acid alkali metal salt, alkylbenzene sulfonic acid salt, alpha-olefin sulfonic acid salt, poly Oxyethylene alkylphenyl ethers, sodium alkylarylsulfonic acid, or mixtures thereof can be used.

바람직한 음이온 유화제의 사용량은 폴리우레아 수지 100중량부 기준으로 3 내지 20중량부인 것이 좋다.The preferred anionic emulsifier is preferably used in an amount of 3 to 20 parts by weight based on 100 parts by weight of the polyurea resin.

본 발명에 따른 숯가루는 높은 공극율로 인하여 친환경 방수제 조성물을 구성하는 조성물의 분산성을 향상시키는 동시에 결합력을 향상시켜 강도를 증가시키도록 하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 숯가루라면 어떠한 것을 사용하여도 무방하며, 바람직하게는 볼밀로 분말화한 숯가루를 사용하는 것이 좋다.The charcoal powder according to the present invention is to increase the strength by improving the bonding strength while improving the dispersibility of the composition constituting the eco-friendly waterproofing composition due to the high porosity. Anything may be used, and it is preferable to use charcoal powder powdered with a ball mill.

바람직한 숯가루의 사용량은 특별히 한정되는 것은 아니지만, 추천하기로는 폴리우레아 수지 100중량부 기준으로 5 내지 20중량부인 것이 좋다.A preferred amount of the charcoal powder used is not particularly limited, but is preferably 5 to 20 parts by weight based on 100 parts by weight of the polyurea resin.

본 발명에 따른 실리카는 흐름성을 방지하여 조성물의 각 성분이 상분리되는 것을 방지하고, 내부 표면적을 증가시켜 부착강도를 향상시키기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 실리카라면 어떠한 것을 사용하여도 무방하며, 그 사용량은 사용자의 선택에 따라 변경 가능하지만, 바람직하게는 폴리우레아 수지 100중량부 기준으로 2 내지 15중량부인 것이 좋다.The silica according to the present invention is intended to prevent flow properties, prevent phase separation of each component of the composition, and improve adhesion strength by increasing the inner surface area. It is also okay, and the amount can be changed according to the user's selection, but it is preferably 2 to 15 parts by weight based on 100 parts by weight of the polyurea resin.

본 발명에 따른 경화제는 친환경 방수제 조성물을 경화시키기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 경화제라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 아민혼합물 예를 들면, 폴리옥시에테르 폴리아민 혼합물, 트리에탄올아민, 메틸디에탄올아민, 트리이소프로판올 아민, 4-디메틸아미노벤조산메틸, 4-디메틸아미노벤조산에틸, 4-디메틸아미노벤조산이 소아밀, 4-디메틸아미노벤조산2-에틸헥실, 벤조산2-디메틸아미노에틸, N,N-디메틸파라톨루이딘, 4,4'-비스(디메틸아미노)벤조페논, 4,4'-비스(디에틸아미노)벤조페논 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용할 수 있다.The curing agent according to the present invention is for curing the eco-friendly waterproofing composition, and any conventional curing agent in the art having this purpose may be used, but preferably an amine mixture such as a polyoxyether polyamine mixture, triethanol Amine, methyl diethanolamine, triisopropanol amine, 4-dimethylaminobenzoic acid methyl, 4-dimethylaminobenzoic acid ethyl, 4-dimethylaminobenzoic acid isamyl, 4-dimethylaminobenzoic acid 2-ethylhexyl, benzoic acid 2-dimethylaminoethyl , N,N-dimethylparatoluidine, 4,4'-bis(dimethylamino)benzophenone, 4,4'-bis(diethylamino)benzophenone, or at least one or more mixtures selected from these may be used.

바람직한 경화제의 사용량은 폴리우레아 수지 100중량부 기준으로 20 내지 60중량부인 것이 좋다.The preferred amount of the curing agent is preferably 20 to 60 parts by weight based on 100 parts by weight of the polyurea resin.

본 발명에 따른 옥틸페놀에톡실레이트는 에톡실화된 옥틸페놀 유도체로서, 방수제 조성물에 포함되어 방수 대상면에 방수막이 용이하게 형성될 수 있도록 한다.The octylphenol ethoxylate according to the present invention is an ethoxylated octylphenol derivative, and is included in the waterproofing composition so that a waterproofing film can be easily formed on the surface to be waterproof.

바람직한 옥틸페놀에톡실레이트의 사용량은 폴리우레아 수지 100중량부 기준으로 1 내지 10중량부인 것이 좋다.The preferred amount of octylphenol ethoxylate is 1 to 10 parts by weight based on 100 parts by weight of the polyurea resin.

본 발명에 따른 폴리비닐알코올은 방수제 조성물을 구성하는 구성성분의 분산성을 좋게 할 뿐만 아니라, 초기의 끈적임 정도(tacky property)도 증가되어 초기접착력을 개선함으로써 들뜸 현상, 뒤틀림 등의 불량률을 감소시킬 수 있도록 한다.The polyvinyl alcohol according to the present invention not only improves the dispersibility of the constituents constituting the waterproofing composition, but also increases the initial tacky property to improve initial adhesion, thereby reducing defect rates such as lifting and warping. To be able to.

여기서, 상기 폴리비닐알코올은 당업계의 통상적인 폴리비닐 알코올이라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 0.1 내지 10㎛인 기공을 0.05 내지 0.4cc/g의 범위로 포함하는 폴리비닐알코올을 사용하는 것을 추천한다.Here, the polyvinyl alcohol may be any conventional polyvinyl alcohol in the art, but preferably polyvinyl alcohol containing 0.1 to 10 μm pores in the range of 0.05 to 0.4 cc/g It is recommended to do it.

바람직한 폴리비닐알코올의 사용량은 폴리우레아 수지 100중량부 기준으로 1 내지 20중량부인 것을 추천한다.It is recommended that the amount of polyvinyl alcohol used is 1 to 20 parts by weight based on 100 parts by weight of the polyurea resin.

본 발명에 따른 셀룰로오스 섬유는 친환경 방수제 조성물로 형성된 도막의 종-횡 방향으로 가해지는 응력에 의한 인장력 및/또는 경량성 등을 제공하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 셀룰로오스 섬유라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 천연 셀룰로오스 섬유를 사용하는 것이 좋고, 그 사용량은 폴리우레아 수지 100중량부 기준으로 0.1 내지 5중량부인 것이 좋다.The cellulose fiber according to the present invention is to provide tensile strength and/or light weight by stress applied in the longitudinal-transverse direction of a coating film formed of an eco-friendly waterproofing composition, and any conventional cellulose fiber in the art having this purpose Although it may be used, it is preferable to use natural cellulose fibers, and the amount thereof is preferably 0.1 to 5 parts by weight based on 100 parts by weight of the polyurea resin.

본 발명에 따른 나노세라믹 입자는 방수제 조성물의 양생 중에 표면으로 부상하여 치밀하고 경도가 높은 표면을 형성하기 때문에, 수증기와 기타 기체, 액체의 투과를 방지함은 물론, 내습성, 내구성, 내후성, 내충격성, 내약품성이 향상된다.Since the nanoceramic particles according to the present invention rise to the surface during curing of the waterproofing composition to form a dense and high hardness surface, it prevents the penetration of water vapor, other gases, and liquids, as well as moisture resistance, durability, weather resistance, and resistance. Impact resistance and chemical resistance are improved.

상기 나노세라믹 입자의 사용량은 폴리우레아 수지 100중량부 기준으로 3 내지 20중량부인 것이 좋다.The amount of the nanoceramic particles is preferably 3 to 20 parts by weight based on 100 parts by weight of the polyurea resin.

바람직한 나노세라믹 입자는 실리콘카바이드, 알루미나, 지르코니아-실리카, ZnO, TiO2 및/또는 CaCO3가 포함된다. Preferred nanoceramic particles include silicon carbide, alumina, zirconia-silica, ZnO, TiO 2 and/or CaCO 3 .

이들 세라믹입자는 평균 입경이 나노미터 범위인 것이 바람직한데, 구체적으로 상기 실리콘카바이드의 평균 입경은 300 내지 500nm, 상기 알루미나의 평균 입경은 500 내지 1000nm, 상기 지르코니아-실리카의 평균 입경은 500 내지 1000nm, 상기 ZnO의 평균 입경은 500 내지 1000nm, 상기 TiO2의 평균 입경은 100 내지 300nm, 그리고 CaCO3의 평균 입경은 500 내지 1000nm인 것이 바람직하다.These ceramic particles are preferably in the range of nanometers, specifically, the average particle diameter of the silicon carbide is 300 to 500 nm, the average particle diameter of the alumina is 500 to 1000 nm, the average particle diameter of the zirconia-silica is 500 to 1000 nm, It is preferable that the average particle diameter of ZnO is 500 to 1000 nm, the average particle diameter of TiO 2 is 100 to 300 nm, and the average particle diameter of CaCO 3 is 500 to 1000 nm.

이 중에서도 실리콘카바이드는 천연광물로 존재하지 않으므로 인공적으로 합성하며, 고온에서의 화학적 안정성 및 내식성이 뛰어나고 높은 경도를 갖는다.Among these, silicon carbide does not exist as a natural mineral, so it is artificially synthesized, has excellent chemical stability and corrosion resistance at high temperatures, and has high hardness.

본 발명에 따른 증점제는 방수제 조성물의 점도를 조절하여 조성물의 사용을 용이하게 하기 위한 것으로서, 이러한 목적을 위해 당업계에서 통상적으로 사용되는 증점제라면 특별히 한정되지 않지만, 바람직하게는 하이드록시 에틸 셀룰로오즈(HydroxyEthyl Cellulose), 소수성 우레탄변성계 증점제 또는 이들의 혼합물을 사용하는 것을 추천한다.The thickener according to the present invention is to adjust the viscosity of the waterproofing agent composition to facilitate the use of the composition, and it is not particularly limited as long as it is a thickener commonly used in the art for this purpose, but is preferably hydroxy ethyl cellulose (HydroxyEthyl Cellulose), a hydrophobic urethane-modified thickener, or a mixture thereof is recommended.

상기 증점제의 사용량은 폴리우레아 수지 100중량부 기준으로 1 내지 20중량부인 것이 바람직하다.The amount of the thickener is preferably 1 to 20 parts by weight based on 100 parts by weight of the polyurea resin.

여기서, 상기 증점제로 사용되는 하이드록시 에틸 셀룰로오즈는 보수성을 가질 수 있다.Here, hydroxy ethyl cellulose used as the thickener may have water retention properties.

본 발명에 따른 부착증진제는 방수제 조성물이 적용되는 방수 대상면에 보다 용이하게 접착할 수 있도록 하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 부착증진제라면 어떠한 것을 사용하여도 무방하지만, 추천하기로는 하이드록시 에틸 아크릴로일 포스페이트, 하이드록시 에틸 메타 아크릴레이트 포스페이트 또는 이들의 혼합물을 사용하는 것이 좋고, 그 사용량은 폴리우레아 수지 100중량부 기준으로 1 내지 20중량부인 것이 좋다.The adhesion promoter according to the present invention is intended to make it easier to adhere to the waterproofing target surface to which the waterproofing agent composition is applied, and any conventional adhesion promoter in the art having this purpose may be used, but is recommended. It is preferable to use hydroxy ethyl acryloyl phosphate, hydroxy ethyl meta acrylate phosphate, or a mixture thereof, and the amount thereof is preferably 1 to 20 parts by weight based on 100 parts by weight of the polyurea resin.

본 발명에 따른 박리방지제는 방수제 조성물이 방수 대상면으로부터 쉽게 박리되는 것을 방지하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 박리방지제라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 폴리인산계, 아민계, 또는 인산 에스테르계 박리방지제를 사용하는 것이 좋다.The peeling inhibitor according to the present invention is for preventing the waterproofing composition from being easily peeled off the waterproofing target surface, and any conventional peeling inhibitor having such a purpose in the art may be used, but preferably polyphosphoric acid, It is preferable to use an amine-based or phosphoric acid ester-based peeling inhibitor.

특정적으로, 상기 박리방지제는 액상형으로 비중이 1.0 이상이고 60℃ 점도가 110 cPs인 폴리인산계 박리방지제; 산가가 10 ㎎KOH/g 이하이고, 총 아민가가 140 내지 400㎎HCl/g인 아민계 박리방지제일 수 있다.Specifically, the peeling inhibitor is a polyphosphoric acid-based peeling inhibitor having a specific gravity of 1.0 or more and a viscosity of 110 cPs at 60° C. in a liquid form; It may be an amine-based peeling inhibitor having an acid value of 10 mgKOH/g or less and a total amine value of 140 to 400 mgHCl/g.

바람직한 박리방지제의 사용량은 폴리우레아 수지 100중량부 기준으로 5 내지 30중량부인 것을 추천한다.It is recommended that the preferred amount of the peeling inhibitor is 5 to 30 parts by weight based on 100 parts by weight of the polyurea resin.

본 발명에 따른 산화방지제는 방수제 조성물의 산화를 방지하기 위한 것이다.The antioxidant according to the present invention is for preventing oxidation of the waterproofing agent composition.

바람직한 산화방지제는 아민계, 비스페놀계, 모노페놀계 및 유황계 산화방지제가 사용될 수 있고, 그 사용량은 폴리우레아 수지 100중량부 기준으로 3 내지 10중량부인 것이 좋다.Preferred antioxidants may be amine-based, bisphenol-based, monophenol-based and sulfur-based antioxidants, and the amount is preferably 3 to 10 parts by weight based on 100 parts by weight of the polyurea resin.

특정적으로, 본 발명에 따른 산화방지제는 고온에서 가공이 이루어질 경우 저분자형 고분자형 페놀계 산화방지제, 예를 들면 2.2-메틸렌비스(4-메틸-6-t-부틸페놀)[2 . 2 - M e t h y l e n e b i s ( 4 - m e t h y l - 6 - t - b u t y l p h e n o l )], 2.6-디-t-부틸-4-메틸페놀(2.6-di -t-Butyl-4-methylphenol) 또는 이들의 혼합물을 사용하는 것을 추천한다.Specifically, when the antioxidant according to the present invention is processed at high temperature, a low molecular weight polymeric phenolic antioxidant, for example 2.2-methylenebis(4-methyl-6-t-butylphenol)[2. 2-M ethylenebis (4-methyl-6-t-butylphenol )], 2.6-di-t-Butyl-4-methylphenol (2.6-di -t-Butyl-4-methylphenol) or mixtures thereof I recommend you.

특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물이 용이하게 스프레이분사될 수 있도록 용제에 용해 및/또는 분산시켜 사용할 수 있는바, 이러한 경우, 상기 용제는 당업계의 통상적인 용제라면 어떠한 것을 사용하여도 무방하다.As a specific embodiment, the eco-friendly waterproofing composition according to the present invention can be used by dissolving and/or dispersing in a solvent so that the composition can be easily sprayed. In this case, the solvent is any conventional solvent in the art. It is okay to do it.

이때, 바람직한 용제, 예를 들면 물의 사용량은 특별히 한정되지 않지만, 바람직하게는 폴리우레아 수지 100중량부 기준으로 50 내지 1,000중량부인 것이 좋다.At this time, the amount of a preferred solvent, such as water, is not particularly limited, but is preferably 50 to 1,000 parts by weight based on 100 parts by weight of the polyurea resin.

본 발명에 친환경 방수제 조성물, 특정적으로 폴리우레아 수지를 포함하는 친환경 방수제 조성물은 하기의 특정 양태의 부가물을 1종 또는 1종 이상 더 포함할 수 있다.The eco-friendly waterproofing composition according to the present invention, specifically, the eco-friendly waterproofing composition including a polyurea resin may further include one or more additives of the following specific embodiments.

특정 양태로서, 본 발명에 따른 친환경 방수제 조성물, 특정적으로 폴리우레아 수지를 포함하는 친환경 방수제 조성물은 친환경 방수제 조성물의 시공 후 신속한 경화를 진행하여도 크랙 및 탈락현상을 개선하고, 조성물의 가공성, 밀착력 및 안정성 등을 제공하기 위하여 폴리비릴리덴플로라이드수지를 폴리우레아 수지 100중량부 기준으로 10 내지 30중량부로 더 포함할 수 있다.As a specific aspect, the eco-friendly waterproofing composition according to the present invention, specifically, the eco-friendly waterproofing composition containing a polyurea resin, improves cracks and dropping phenomena even after rapid curing after construction of the eco-friendly waterproofing composition, and improves the processability and adhesion of the composition. And in order to provide stability and the like, the polyvirylidene fluoride resin may further include 10 to 30 parts by weight based on 100 parts by weight of the polyurea resin.

또 다른 특정 양태로서, 본 발명에 따른 방수제 조성물은 조기강도를 발현하기 위하여 폴리우레아 수지 100중량부 기준으로 5 내지 20중량부의 폴리아민을 더 포함할 수 있다.As another specific aspect, the waterproofing agent composition according to the present invention may further include 5 to 20 parts by weight of polyamine based on 100 parts by weight of the polyurea resin in order to express early strength.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물의 양생시 수축을 방지하기 위하여 폴리우레아 수지 100중량부 기준으로 1 내지 10중량부의 네오펜틸글리콜을 더 포함할 수 있다.As another specific embodiment, the eco-friendly waterproofing composition according to the present invention may further include 1 to 10 parts by weight of neopentyl glycol based on 100 parts by weight of the polyurea resin in order to prevent shrinkage during curing of the composition.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물에 포함된 성분이 물과 용이하게 혼합되도록 폴리우레아 수지 100중량부 기준으로 0.1 내지 5중량부의 플라스터(plaster)를 더 포함할 수 있다.As another specific aspect, the eco-friendly waterproofing composition according to the present invention may further include 0.1 to 5 parts by weight of a plaster based on 100 parts by weight of the polyurea resin so that the components included in the composition are easily mixed with water.

여기서, 상기 플라스터의 사용량이 폴리우레아 수지 100중량부 기준으로 0.5 중량부 미만인 경우는 조성물에 포함된 다양한 성분이 물과 용이하게 혼합되기 어렵고, 5중량부를 초과하는 경우는 강도 및 내화학성 등이 저하되는 문제가 있다.Here, when the amount of the plaster used is less than 0.5 parts by weight based on 100 parts by weight of the polyurea resin, it is difficult for various components included in the composition to be easily mixed with water, and when it exceeds 5 parts by weight, strength and chemical resistance, etc., decrease. There is a problem.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 강도, 자외선 저항성 및 재료 분리 저항성을 개선하기 위하여 폴리우레아 수지 100중량부 기준으로 0.1 내지 5중량부의 티타늄옥사이드를 더 포함할 수 있다.As another specific aspect, the eco-friendly waterproofing composition according to the present invention may further include 0.1 to 5 parts by weight of titanium oxide based on 100 parts by weight of the polyurea resin in order to improve strength, UV resistance, and material separation resistance.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 강도, 내마모성 및 내화성을 개선하기 위하여 폴리우레아 수지 100중량부 기준으로 1 내지 15중량부의 깁사이트를 더 포함할 수 있다. As another specific aspect, the eco-friendly waterproofing composition according to the present invention may further include 1 to 15 parts by weight of gibbsite based on 100 parts by weight of the polyurea resin in order to improve strength, abrasion resistance, and fire resistance.

여기서, 상기 깁사이트의 사용량은 1중량부 미만일 경우 성능 개선 효과가 미약할 수 있고, 상기 깁사이트의 사용량이 15중량부를 초과할 경우에는 작업성이 저하되고 제조 원가가 높아져 경제적이지 못하다.Here, when the amount of the gibbsite used is less than 1 part by weight, the performance improvement effect may be weak, and when the amount of the gibbsite used exceeds 15 parts by weight, the workability is lowered and the manufacturing cost is increased, which is not economical.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 강도, 내화성 및 내식성을 개선하기 위하여 폴리우레아 수지 100중량부 기준으로 0.1 내지 5중량부의 세륨을 더 포함할 수 있다. As another specific aspect, the eco-friendly waterproofing composition according to the present invention may further contain 0.1 to 5 parts by weight of cerium based on 100 parts by weight of the polyurea resin in order to improve strength, fire resistance, and corrosion resistance.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 점성조절을 위해서 폴리우레아 수지 100중량부 기준으로 1 내지 10중량부의 옥수수 스타치(corn starch)를 더 포함할 수 있다.As another specific aspect, the eco-friendly waterproofing composition according to the present invention may further include 1 to 10 parts by weight of corn starch based on 100 parts by weight of the polyurea resin for viscosity control.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 방수제 조성물 표면의 내부로 침투하여 염소계 유해 물질을 분해하여 제거함으로서 수밀성을 강화하기 위하여 폴리우레아 수지 100중량부 기준으로 1 내지 10중량부의 토르말린(NaX3Al6(BO3)Si6O18(OH)4)을 더 포함할 수 있다.In another specific aspect, the eco-friendly waterproofing composition according to the present invention penetrates into the interior of the waterproofing composition surface and decomposes and removes chlorine-based harmful substances, thereby enhancing water tightness, based on 100 parts by weight of a polyurea resin, of 1 to 10 parts by weight of tourmaline ( NaX 3 Al 6 (BO 3 )Si 6 O 18 (OH) 4 ) may be further included.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 습윤강도 및 마모저항성을 강화하기 위하여 폴리우레아 수지 100중량부 기준으로 1 내지 10중량부의 진크암모늄클로라이드를 더 포함할 수 있다.As another specific aspect, the eco-friendly waterproofing composition according to the present invention may further include 1 to 10 parts by weight of zinc ammonium chloride based on 100 parts by weight of the polyurea resin in order to enhance wet strength and abrasion resistance.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물의 통기성 및 흡유성 향상을 위하여 천매암 분말을 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있는데, 상기 천매암은 점토질의 퇴적층이 열수변질에 의한 가수분해 작용 및 변성, 풍화 부식 등의 과정을 거쳐 생성된 변성암의 일종으로 주 성분이 실리카, 알루미나 및 금속산화물을 포함하고 있으며, 내부에 여러 크기의 공극을 포함하고 비석(zeolite)과 거의 유사한 공극률을 갖으면서도 거포의 분율이 큰 특징을 갖고 있어 이를 친환경 방수제 조성물에 포함시키면, 상기와 같은 효과를 갖게 되며, 바람직한 천매암 분말의 평균입도는 3 내지 30㎛ 이다.As another specific embodiment, the eco-friendly waterproofing composition according to the present invention may further include 1 to 5 parts by weight of phylum powder based on 100 parts by weight of polyurea resin in order to improve the breathability and oil absorption of the composition. The sedimentary layer is a type of metamorphic rock that is formed through the process of hydrolysis and metamorphism due to hydrothermal alteration, weathering and corrosion, and its main components contain silica, alumina, and metal oxides, and contain pores of various sizes inside. zeolite) has a porosity that is almost similar to that of the foam, but has a large fraction of the foam, and if it is included in the eco-friendly waterproofing composition, the above effect will be obtained, and the average particle size of the preferred phyllite powder is 3 to 30 μm.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물이 시공되는 시공면의 공극으로 침투하여 조직을 치밀하게 유지함으로써 친환경 방수제 조성물의 들뜸방지와 내구성 및 부착 강도를 향상시키기 위하여 보크사이트 분말을 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있는데, 바람직한 보크사이트 분말의 평균입도는 1 내지 10㎛ 이다.In yet another specific aspect, the eco-friendly waterproofing composition according to the present invention contains bauxite powder in order to prevent lifting of the eco-friendly waterproofing composition and to improve durability and adhesion strength by penetrating into the pores of the construction surface on which the composition is installed and maintaining the structure densely. It may further include 1 to 5 parts by weight based on 100 parts by weight of the polyurea resin, and the average particle size of the preferred bauxite powder is 1 to 10 μm.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물의 크랙발생 및 박리방지를 위하여 디부틸프탈레이트를 폴리우레아 수지 100중량부 기준으로 2 내지 6중량부로 더 포함할 수 있다.As another specific aspect, the eco-friendly waterproofing composition according to the present invention may further include dibutylphthalate in an amount of 2 to 6 parts by weight based on 100 parts by weight of the polyurea resin in order to prevent cracking and peeling of the composition.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물의 강도, 침투력, 및 발수성 등을 향상시키기 위하여 3-메르캅토프로필트리메톡시실란을 폴리우레아 수지 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.In another specific embodiment, the eco-friendly waterproofing composition according to the present invention comprises 3-mercaptopropyltrimethoxysilane in 1 to 3 parts by weight based on 100 parts by weight of a polyurea resin in order to improve the strength, penetration, and water repellency of the composition. It may contain more.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물의 장기강도 발현 및 내구성 증진을 위하여 겔라이트 미분말을 폴리우레아 수지 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있는데, 상기 겔라이트는 황토의 187배 이상의 효과를 가진 광물질로서 상기 효과 이외에 양질의 원적외선 방출 효과도 있는 것으로서, 바람직한 평균입도는 1 내지 5㎛ 이다.As another specific embodiment, the eco-friendly waterproofing composition according to the present invention may further include 1 to 3 parts by weight of gelite fine powder based on 100 parts by weight of the polyurea resin in order to develop long-term strength and durability of the composition. Is a mineral that has an effect of 187 times or more of loess, and has a high quality far-infrared emission effect in addition to the above effect, and the preferred average particle size is 1 to 5 μm.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물을 구성하는 재료의 응결을 방지하고 일정시간 작업시간을 확보하기 위하여 구연산을 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.In another specific aspect, the eco-friendly waterproofing composition according to the present invention further comprises 1 to 5 parts by weight of citric acid based on 100 parts by weight of the polyurea resin in order to prevent condensation of the material constituting the composition and to secure a certain working time. I can.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물의 표면에 수분침투를 방지하면서 통기성을 확보하기 위하여 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부의 소디윰스테아레이트를 더 포함할 수 있는데, 그 함량이 폴리우레아 수지 100중량부 기준으로 1중량부 미만이면 목적한 수분침투 방지기능을 얻을 수 없고, 5중량부를 초과하면 조성물의 강도 저하현상이 나타나 좋지 않다.As another specific aspect, the eco-friendly waterproofing composition according to the present invention may further include 1 to 5 parts by weight of sodium stearate based on 100 parts by weight of the polyurea resin in order to prevent moisture penetration into the surface of the composition and secure breathability. However, if the content is less than 1 part by weight based on 100 parts by weight of the polyurea resin, the intended moisture penetration prevention function cannot be obtained, and if it exceeds 5 parts by weight, the strength of the composition decreases, which is not good.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물의 내수성 및 내스크래치성을 향상시키기 위하여 폴리우레아 수지 100중량부 기준으로 1 내지 6중량부의 붕산 화합물을 더 포함할 수 있는데, 상기 붕산 화합물로는 오르토붕산, 메타붕산, 사붕산, 붕산 메틸, 붕산 에틸 등을 들 수 있으며, 바람직하게는 오르토붕산을 사용하는 것이 좋다.In another specific embodiment, the eco-friendly waterproofing composition according to the present invention may further include 1 to 6 parts by weight of a boric acid compound based on 100 parts by weight of a polyurea resin in order to improve the water resistance and scratch resistance of the composition, the boric acid compound Examples of the examples include orthoboric acid, metaboric acid, tetraboric acid, methyl borate, ethyl borate, and the like, preferably orthoboric acid.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물의 건조 수축을 방지하기 위하여 폴리우레아 수지 100중량부 기준으로 1 내지 10중량부의 알루민산 칼슘을 더 포함할 수 있는데, 알루민산 칼슘이 친환경 방수제 조성물에 포함되면 팽창성을 띄게 되어 조성물의 건조수축을 방지하게 되는 것으로, 그 사용량이 폴리우레아 수지 100중량부 기준으로 1중량부 미만이면 그 효과가 미미하며, 10중량부를 초과할 경우 과다하여 작업성을 저하 시킬 수 있어 좋지 않다.As another specific aspect, the eco-friendly waterproofing composition according to the present invention may further contain 1 to 10 parts by weight of calcium aluminate based on 100 parts by weight of the polyurea resin in order to prevent the drying shrinkage of the composition. When included in the waterproofing composition, it becomes swellable to prevent drying and shrinkage of the composition.If the amount is less than 1 part by weight based on 100 parts by weight of polyurea resin, the effect is insignificant, and if it exceeds 10 parts by weight, it is excessive. It's not good because it can lower your sex.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물의 압축강도 및 휨강도를 향상시키기 위하여 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부의 메타규산나트륨을 더 포함할 수 있는데, 그 함량이 1중량부 미만이면 유동성이 낮아지고 불규칙한 기포가 형성되며, 5중량부를 초과하면 경화시간을 확보하기 어려워 좋지 않다.As another specific aspect, the eco-friendly waterproofing composition according to the present invention may further contain 1 to 5 parts by weight of sodium metasilicate based on 100 parts by weight of the polyurea resin in order to improve the compressive strength and flexural strength of the composition, If it is less than 1 part by weight, fluidity is lowered and irregular air bubbles are formed, and if it exceeds 5 parts by weight, it is difficult to secure a curing time, which is not good.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 방수제 조성물 내부에서 일체화된 필름을 형성하여 구조물, 예를 들면 콘크리트 구조물과의 접착성을 부여하고, 공극 충진에 의한 물과 유해물질의 침투를 방지 및 내마모성을 향상시키며, 작업 중의 재료 분리를 방지하는 점성을 부여하기 위하여 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부의 재유화형 분말수지를 더 포함할 수 있는데, 그 함량이 1중량부 미만이면 그 효과가 미미하고, 5중량부를 초과하면 입자의 코팅에 의해 수화작용을 방해하여 압축강도가 저하될 수 있다. As another specific aspect, the eco-friendly waterproofing composition according to the present invention forms an integrated film inside the waterproofing composition to impart adhesion to a structure, for example, a concrete structure, and prevents the penetration of water and harmful substances by filling the pores. In order to improve prevention and abrasion resistance, and to impart viscosity to prevent material separation during work, 1 to 5 parts by weight of a re-emulsified powder resin based on 100 parts by weight of the polyurea resin may be further included, the content of which is less than 1 part by weight. If it is the back, the effect is insignificant, and if it exceeds 5 parts by weight, the compressive strength may be lowered by interfering with the hydration effect by coating of the particles.

여기서, 상기 재유화형 분말수지는 경화 후 조기에 고강도가 발현되고, 이 고강도 때문에 부재의 단면을 작게 할 수 있으며, 접착력 및 내마모성, 내피로성, 내약품성 및 내충격성, 휨강도, 부착강도, 내화학성을 증가시키는 효과가 있다.Here, the re-emulsified powder resin exhibits high strength early after curing, and because of this high strength, the cross section of the member can be reduced, and adhesion and abrasion resistance, fatigue resistance, chemical resistance and impact resistance, flexural strength, adhesion strength, and chemical resistance It has an increasing effect.

상기 재유화형 분말수지는 그 종류가 특별히 한정되는 것은 아니나, 에틸렌비닐아세테이트(ethylenevinylacetate), 스티렌-부타디엔고무(styrene butadiene rubber), 에틸렌 비닐 클로라이드, 비닐 라우에이트, 초산비닐아세테이트, SBR 분말수지, 스틸렌아크릴에스터 및 폴리아크릴에스터 (polyacrylic ester)로 구성된 그룹으로부터 1종 이상이 선택되어 사용될 수 있다.The type of the re-emulsified powder resin is not particularly limited, but ethylenevinylacetate, styrene-butadiene rubber, ethylene vinyl chloride, vinyl laurate, vinyl acetate, SBR powder resin, styrene acrylic One or more selected from the group consisting of esters and polyacrylic esters may be used.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 그 조성물로 이루어진 방수 도막의 수축균열 및 균열확산 억제, 충격 파손 및 마모 억제, 피로하중에 대한 저항력 증대, 휨강도 및 인장력 등을 보완하기 위하여 폴리우레아 수지 100중량부 기준으로 1 내지 3중량부의 폴리프로필렌 섬유를 더 포함할 수 있다.In another specific aspect, the eco-friendly waterproofing composition according to the present invention is made of poly(polypropylene) to compensate for shrinkage cracking and spreading of cracks, impact breakage and abrasion, increase resistance to fatigue load, flexural strength and tensile strength, etc. of the waterproof coating made of the composition. It may further include 1 to 3 parts by weight of polypropylene fibers based on 100 parts by weight of the urea resin.

여기서, 상기 폴리프로필렌 섬유는 표준길이 약 5 내지 8㎜, 바람직하게는 표준길이 약 6㎜인 것을 사용하는 것이 좋다.Here, it is preferable to use the polypropylene fibers having a standard length of about 5 to 8 mm, preferably a standard length of about 6 mm.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 동절기 응결 지연 현상을 차단하고, 강도 증진 및 점성을 증가시켜 폴리우레아 수지의 흐름성을 향상시키기 위하여 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부의 황산알루미늄을 더 포함할 수 있다.As another specific aspect, the eco-friendly waterproofing composition according to the present invention is 1 to 5 based on 100 parts by weight of the polyurea resin in order to block the delay of condensation in winter, increase strength and increase viscosity to improve the flowability of the polyurea resin. It may further include aluminum sulfate in parts by weight.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물의 균열을 저감시키기 강도 발현성을 향상시키기 위하여 폴리우레아 수지 100중량부 기준으로 1 내지 3중량부의 활성마그네시아(MgO)를 더 포함할 수 있다.In another specific aspect, the eco-friendly waterproofing composition according to the present invention may further include 1 to 3 parts by weight of active magnesia (MgO) based on 100 parts by weight of a polyurea resin in order to reduce cracking of the composition and improve strength expression. have.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물내의 거대 기공을 빠른 속도로 제거하여 수평 작업시 깨끗한 마감면을 얻고 소요강도를 확보하기 위하여 폴리우레아 수지 100중량부 기준으로 1 내지 3중량부의 알루미늄스테아레이트를 더 포함할 수 있다.In another specific aspect, the eco-friendly waterproofing composition according to the present invention removes the large pores in the composition at a high speed to obtain a clean finish surface during horizontal work and to secure the required strength, 1 to 3 parts by weight based on 100 parts by weight of a polyurea resin. It may further include negative aluminum stearate.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 친환경 방수제 조성물의 발수성을 향상시키기 위하여 폴리우레아 수지 100중량부 기준으로 0.1 내지 5중량부의 칼륨메틸실리코네이트를 더 포함할 수 있으며, 상기 칼륨메틸실리코네이트의 사용량이 0.1중량부 미만이면 발수성의 효과가 미미하며, 5중량부를 초과하면 상용성이 저하된다.As another specific embodiment, the eco-friendly waterproofing composition according to the present invention may further include 0.1 to 5 parts by weight of potassium methylsiliconate based on 100 parts by weight of the polyurea resin in order to improve the water repellency of the eco-friendly waterproofing composition, and the potassium methyl If the amount of silicate is less than 0.1 parts by weight, the effect of water repellency is insignificant, and if it exceeds 5 parts by weight, compatibility is lowered.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물이 도포되는 대상물이 염해 또는 중성화 등의 성능저하 요인에 의해 부식 및 피복 탈락 등이 발생하는 것을 방지하기 위해 메틸트리메톡시실란(MTMS(methyltrimethoxysilane))을 더 포함할 수 있는데, 그 사용량은 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부가 좋다.In another specific aspect, the eco-friendly waterproofing composition according to the present invention is methyltrimethoxysilane (MTMS (MTMS) to prevent corrosion and coating dropout due to deterioration of performance such as salt damage or neutralization of the object to which the composition is applied. methyltrimethoxysilane)), the amount of which is preferably 1 to 5 parts by weight based on 100 parts by weight of the polyurea resin.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 조성물의 재료분리 저항성, 작업성 및 동결융해 내구성 등을 향상시키기 위하여 이미다졸린베타인을 폴리우레아 수지 100중량부 기준으로 0.1 내지 2중량부로 더 포함할 수 있다.In another specific aspect, the eco-friendly waterproofing composition according to the present invention further comprises 0.1 to 2 parts by weight of imidazoline betaine based on 100 parts by weight of the polyurea resin in order to improve the material separation resistance, workability and freeze-thaw durability of the composition. Can include.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 친환경 방수제 조성물의 부착성능을 향상시키기 위하여 노말부틸아크릴레이트(n-butyl acrylate)를 폴리우레아 수지 100중량부 기준으로 1 내지 10중량부로 더 포함할 수 있는데, 폴리우레아 수지 100중량부 기준으로 1중량부 미만이면 부착력이 저하되며, 10중량부를 초과하면 경제적이지 못하여 좋지 않다.As another specific aspect, the eco-friendly waterproofing composition according to the present invention further comprises 1 to 10 parts by weight of n-butyl acrylate based on 100 parts by weight of the polyurea resin in order to improve the adhesion performance of the eco-friendly waterproofing composition. However, if it is less than 1 part by weight based on 100 parts by weight of the polyurea resin, the adhesion is lowered, and if it exceeds 10 parts by weight, it is not good because it is not economical.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 친환경 방수제 조성물의 강도, 내크리프성, 내마모성, 내화성 등을 개선하기 위하여 멀라이트(mullite)를 폴리우레아 수지 100중량부 기준으로 1 내지 5량부로 더 포함할 수 있는데, 상기 멀라이트는 사방정계에 속하는 광물질로서 무색 또는 담홍색을 띄며, 산화알루미늄과 이산화규소를 많이 함유하고 있는데, 폴리우레아 수지 100중량부 기준으로 1중량부 미만이면 강도, 내마모성 및 내화성 등의 개선효과가 미미하며, 5중량부를 초과하면 작업성이 저하되어 좋지 않다.In another specific aspect, the eco-friendly waterproofing composition according to the present invention contains 1 to 5 amounts of mullite based on 100 parts by weight of a polyurea resin in order to improve the strength, creep resistance, abrasion resistance, and fire resistance of the eco-friendly waterproofing composition. The mullite is a mineral belonging to the orthorhombic system, and has a colorless or pink color, and contains a lot of aluminum oxide and silicon dioxide.If less than 1 part by weight based on 100 parts by weight of a polyurea resin, strength and abrasion resistance And the improvement effect such as fire resistance is insignificant, and if it exceeds 5 parts by weight, workability is deteriorated, which is not good.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 친환경 방수제 조성물의 경화속도를 조절하고, 방수성 및 내식성을 개선하기 위하여 규불화마그네슘을 폴리우레아 수지 100중량부 기준으로 0.5 내지 3중량부로 더 포함할 수 있다. In another specific aspect, the eco-friendly waterproofing composition according to the present invention further comprises 0.5 to 3 parts by weight of magnesium silicate based on 100 parts by weight of the polyurea resin in order to control the curing rate of the eco-friendly waterproofing composition and improve waterproof and corrosion resistance. can do.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 친환경 방수제 조성물의 내구성, 내마모성 및 분산성을 향상시키기 위하여 스테아린산칼슘을 폴리우레아 수지 100중량부 기준으로 0.1 내지 2중량부로 더 포함할 수 있다.As another specific embodiment, the eco-friendly waterproofing composition according to the present invention may further include 0.1 to 2 parts by weight of calcium stearate based on 100 parts by weight of the polyurea resin in order to improve the durability, abrasion resistance, and dispersibility of the eco-friendly waterproofing composition.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 친환경 방수제 조성물의 경화성을 향상시키기 위하여 트리페닐포스파인(triphenyphosphine)을 폴리우레아 수지 100중량부 기준으로 0.1 내지 3중량부로 더 포함할 수 있다.As another specific embodiment, the eco-friendly waterproofing composition according to the present invention may further include triphenylphosphine in an amount of 0.1 to 3 parts by weight based on 100 parts by weight of the polyurea resin in order to improve the curability of the eco-friendly waterproofing composition.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 친환경 방수제 조성물의 발색을 억제하고, 투명성을 향상시키기 위하여 글리시딜 네오데카노에이트(Glycidyl neodecanoate)을 폴리우레아 수지 100중량부 기준으로 3 내지 10중량부로 더 포함할 수 있다.In another specific embodiment, the eco-friendly waterproofing composition according to the present invention is 3 to 3 to about 100 parts by weight of a polyurea resin in order to inhibit the color development of the eco-friendly waterproofing composition and improve transparency. It may further contain 10 parts by weight.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 균일한 도막을 형성시키기 위하여 글리시딜 디옥틸프탈레이트(DOP, DiOctyl Phthalate)을 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.As another specific aspect, the eco-friendly waterproofing composition according to the present invention further comprises 1 to 5 parts by weight based on 100 parts by weight of the polyurea resin glycidyl dioctyl phthalate (DOP) in order to form a uniform coating film. I can.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 친환경 방수제 조성물의 혼합시 반응속도를 빠르게 하고, 흡착 및 접착 성능을 향상시키기 위하여 2-브로모피리딘(2-bromopyridine)을 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.As another specific aspect, the eco-friendly waterproofing composition according to the present invention is 100 weight of polyurea resin in order to speed up the reaction rate when mixing the eco-friendly waterproofing composition, and to improve adsorption and adhesion performance. It may further include 1 to 5 parts by weight based on parts.

또 다른 특정 양태로서, 본 발명에 따른 친환경 방수제 조성물은 친환경 방수제 조성물의 내열성, 탄성회복력, 및 내주름성 등을 향상시키기 위하여 디이소노닐프탈레이트(Di-Isononyl Phthalate, (DINP))를 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.In another specific aspect, the eco-friendly waterproofing composition according to the present invention is a polyurea resin using Di-Isononyl Phthalate (DINP) to improve heat resistance, elastic recovery, and wrinkle resistance of the eco-friendly waterproofing composition. It may further include 1 to 5 parts by weight based on 100 parts by weight.

이러한 구성을 갖는 본 발명에 따른 친환경 방수제 조성물은 경화가 초속경으로 신속하게 이루어질 수 있으므로, 수직면에 분사하여도 흘러내림 없이 균일한 도막 두께를 형성할 수 있기 때문에 스프레이 분사 방법을 이용한 도막형성방법을 사용하는 것이 좋다.Since the eco-friendly waterproofing composition according to the present invention having such a configuration can be rapidly cured at an ultra-fast diameter, it is possible to form a uniform coating thickness without flowing down even when sprayed on a vertical surface.Therefore, a coating film forming method using a spray spraying method is used. It is good to use.

특히, 상기 방수제 조성물에 포함된 폴리우레아 수지는 가사경화시간이 수 분 이내로서 경화가 초속경이 이루어져 방수제 조성물이 주변의 습기와 반응할 충분한 시간을 가질 수 없어 수분과 온도에 영향을 받지 않아 적용 가능한 환경의 범위가 넓게 확장될 수 있다.In particular, the polyurea resin contained in the waterproofing composition has a potency curing time within several minutes, and the curing is performed at an initial speed, so that the waterproofing composition cannot have sufficient time to react with the surrounding moisture, so it is not affected by moisture and temperature, so it can be applied. The scope of the environment can be extended widely.

이와 같은 구성을 갖는 본 발명에 따른 친환경 방수제 조성물, 특정적으로 폴리우레아 수지를 포함하는 친환경 방수제 조성물을 이용한 시공방법은 당업계의 통상적인 시공방법이라면 어떠한 것을 사용하여도 무방하지만, 이러한 일례를 설명하면 다음과 같다.The eco-friendly waterproofing composition according to the present invention having such a configuration, specifically, the construction method using the eco-friendly waterproofing composition containing a polyurea resin may be any conventional construction method in the art, but this example will be described. Then it looks like this:

본 발명에 따른 친환경 방수제 조성물의 시공방법은 방수제 조성물을 시공하기 위한 시공표면을 처리하는 표면처리단계;The construction method of the eco-friendly waterproofing composition according to the present invention comprises: a surface treatment step of treating a construction surface for applying the waterproofing composition;

상기 표면처리단계가 종료된 후 프라이머를 도포하는 프라이머 도포단계;A primer application step of applying a primer after the surface treatment step is finished;

상기 프라이머 도포단계가 종료된 상단에 폴리우레아 수지 100중량부 기준으로, 음이온 유화제 3 내지 20중량부, 숯가루 5 내지 20중량부, 실리카 2 내지 15중량부, 경화제 20 내지 60중량부, 옥틸페놀에톡실레이트 1 내지 10중량부, 폴리비닐알코올 1 내지 20중량부, 셀룰로오스 섬유 0.1 내지 5중량부, 나노세라믹 입자 3 내지 20중량부, 증점제 1 내지 20중량부, 부착증진제 1 내지 20중량부, 박리방지제 5 내지 30중량부, 및 산화방지제 3 내지 10중량부를 포함하는 친환경 방수제 조성물을 스프레이 방식으로 분사하는 스프레이 분사단계; 및Based on 100 parts by weight of the polyurea resin on the upper end of the primer application step, 3 to 20 parts by weight of anionic emulsifier, 5 to 20 parts by weight of charcoal powder, 2 to 15 parts by weight of silica, 20 to 60 parts by weight of a curing agent, octylphenol Ethoxylate 1 to 10 parts by weight, polyvinyl alcohol 1 to 20 parts by weight, cellulose fiber 0.1 to 5 parts by weight, nanoceramic particles 3 to 20 parts by weight, thickener 1 to 20 parts by weight, adhesion promoter 1 to 20 parts by weight, A spray spray step of spraying an eco-friendly waterproofing composition comprising 5 to 30 parts by weight of a peeling inhibitor and 3 to 10 parts by weight of an antioxidant in a spray manner; And

상기 스프레이 분사단계가 종료된 후 양생하는 양생단계를 포함한다.And a curing step of curing after the spray spraying step is finished.

여기서, 상기 친환경 방수제 조성물 시공방법은 상기 양성단계가 종료된 그 상단에 탑코팅하는 탑코팅단계를 더 포함할 수 있다. 이때, 상기 탑코팅은 당업계에서 통상적으로 사용하는 탑코팅이라면 어떠한 것을 사용하여도 무방하다.Here, the method of constructing the eco-friendly waterproofing composition may further include a top coating step of top coating the top of the formation step is completed. At this time, the top coating may be any of the top coatings commonly used in the art.

또한, 본 발명에 따른 프라이머 도포단계의 프라이머는 당업계에서 통상적으로 사용하는 프라이머, 예를 들면 에폭시 프라이머라면 어떠한 것을 사용하여도 무방하다.In addition, the primer in the primer application step according to the present invention may be used as long as it is a primer commonly used in the art, for example, an epoxy primer.

한편, 본 발명에 따른 친환경 방수제 조성물을 이용한 방수막을 형성하기 위한 스프레이 분사단계는 당업계의 통상적인 스프레이 분사방법을 이용한 것이라면 어떠한 것이라도 무방하다.On the other hand, the spray spraying step for forming a waterproof film using the eco-friendly waterproofing composition according to the present invention may be any one using a conventional spray spraying method in the art.

이하에서 실시예를 통하여 본 발명을 구체적으로 설명하기로 한다. 그러나 하기의 실시예는 오로지 본 발명을 구체적으로 설명하기 위한 것으로 이들 실시예에 의해 본 발명의 범위를 한정하는 것은 아니다.Hereinafter, the present invention will be described in detail through examples. However, the following examples are for illustrative purposes only and are not intended to limit the scope of the present invention by these examples.

[실시예 1][Example 1]

폴리우레아 수지 100g, 리그닌술폰산알카리금속염 12g, 숯가루 12g, 실리카 8g, 4-디메틸아미노벤조산메틸 40g, 옥틸페놀에톡실레이트 5g, 평균 5㎛ 기공을 약 0.1cc/g의 범위로 포함하는 폴리비닐알코올 10g, 천연 셀룰로오스 섬유 3g, 평균입경이 400nm인 실리콘카바이드 12g, 하이드록시 에틸 셀룰로오즈 10g, 하이드록시 에틸 아크릴로일 포스페이트 10g, 액상형으로 비중이 1.0 이상이고 60℃ 점도가 110 cPs인 폴리인산계 박리방지제 20g, 및 2.2-메틸렌비스(4-메틸-6-t-부틸페놀) 6g을 혼합하여 친환경 방수제 조성물을 제조하였다.Polyurea resin 100 g, lignin sulfonic acid alkali metal salt 12 g, charcoal powder 12 g, silica 8 g, methyl 4-dimethylaminobenzoate 40 g, octylphenol ethoxylate 5 g, polyvinyl containing an average of 5 μm pores in the range of about 0.1 cc/g 10g of alcohol, 3g of natural cellulose fiber, 12g of silicon carbide with an average particle diameter of 400nm, 10g of hydroxyethyl cellulose, 10g of hydroxyethyl acryloyl phosphate, polyphosphoric acid peeling with a specific gravity of 1.0 or more and a viscosity of 110 cPs at 60℃ An eco-friendly waterproofing composition was prepared by mixing 20 g of an inhibitor and 6 g of 2.2-methylenebis(4-methyl-6-t-butylphenol).

[실시예 2][Example 2]

실시예 1과 동일한 방법으로 실시하되, 물 100g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 100 g of water.

[실시예 3][Example 3]

실시예 1과 동일한 방법으로 실시하되, 폴리비닐리덴플로라이드수지 20g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 20 g of a polyvinylidene fluoride resin.

[실시예 4][Example 4]

실시예 1과 동일한 방법으로 실시하되, 폴리아민을 12g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 12 g of polyamine.

[실시예 5][Example 5]

실시예 1과 동일한 방법으로 실시하되, 네오펜틸글리콜 5g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 5 g of neopentyl glycol.

[실시예 6][Example 6]

실시예 1과 동일한 방법으로 실시하되, 플라스터 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of plaster.

[실시예 7][Example 7]

실시예 1과 동일한 방법으로 실시하되, 티타늄옥사이드 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of titanium oxide.

[실시예 8][Example 8]

실시예 1과 동일한 방법으로 실시하되, 깁사이트 8g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 8 g of gibbsite.

[실시예 9][Example 9]

실시예 1과 동일한 방법으로 실시하되, 세륨 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of cerium.

[실시예 10][Example 10]

실시예 1과 동일한 방법으로 실시하되, 옥수수 스타치 6g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 6 g of corn starch.

[실시예 11][Example 11]

실시예 1과 동일한 방법으로 실시하되, 토르말린 6g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 6 g of tourmaline.

[실시예 12][Example 12]

실시예 1과 동일한 방법으로 실시하되, 진크암모늄클로라이드 6g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but further added 6 g of zinc ammonium chloride.

[실시예 13][Example 13]

실시예 1과 동일한 방법으로 실시하되, 평균입도가 5㎛인 천매암 분말 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of cheonmaeam powder having an average particle size of 5 μm.

[실시예 14][Example 14]

실시예 1과 동일한 방법으로 실시하되, 평균입도가 3㎛인 보크사이트 분말 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of bauxite powder having an average particle size of 3 μm.

[실시예 15][Example 15]

실시예 1과 동일한 방법으로 실시하되, 디부틸프탈레이트 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of dibutylphthalate.

[실시예 16][Example 16]

실시예 1과 동일한 방법으로 실시하되, 3-메르캅토프로필트리메톡시실란 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of 3-mercaptopropyltrimethoxysilane.

[실시예 17][Example 17]

실시예 1과 동일한 방법으로 실시하되, 평균입도가 3㎛인 겔라이트 미분말 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but further added 2 g of fine gelite powder having an average particle size of 3 μm.

[실시예 18][Example 18]

실시예 1과 동일한 방법으로 실시하되, 구연산 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of citric acid.

[실시예 19][Example 19]

실시예 1과 동일한 방법으로 실시하되, 소디윰스테아레이트 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of sodium stearate.

[실시예 20][Example 20]

실시예 1과 동일한 방법으로 실시하되, 오르토붕산 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of orthoboric acid.

[실시예 21][Example 21]

실시예 1과 동일한 방법으로 실시하되, 알루민산 칼슘 4g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 4 g of calcium aluminate.

[실시예 22][Example 22]

실시예 1과 동일한 방법으로 실시하되, 메타규산나트륨 4g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 4 g of sodium metasilicate.

[실시예 23][Example 23]

실시예 1과 동일한 방법으로 실시하되, 스틸렌아크릴에스터 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of styrene acrylic ester.

[실시예 24][Example 24]

실시예 1과 동일한 방법으로 실시하되, 표준길이 약 6㎜인 폴리프로필렌 섬유 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of polypropylene fibers having a standard length of about 6 mm.

[실시예 25][Example 25]

실시예 1과 동일한 방법으로 실시하되, 황산알루미늄 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of aluminum sulfate.

[실시예 26][Example 26]

실시예 1과 동일한 방법으로 실시하되, 활성마그네시아 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of active magnesia.

[실시예 27][Example 27]

실시예 1과 동일한 방법으로 실시하되, 알루미늄스테아레이트 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of aluminum stearate.

[실시예 28][Example 28]

실시예 1과 동일한 방법으로 실시하되, 칼륨메틸실리코네이트 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of potassium methylsiliconate.

[실시예 29][Example 29]

실시예 1과 동일한 방법으로 실시하되, 메틸트리메톡시실란 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of methyltrimethoxysilane.

[실시예 30][Example 30]

실시예 1과 동일한 방법으로 실시하되, 이미다졸린베타인 1g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 1 g of imidazoline betaine.

[실시예 31][Example 31]

실시예 1과 동일한 방법으로 실시하되, 노말부틸아크릴레이트 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of normal butyl acrylate.

[실시예 32][Example 32]

실시예 1과 동일한 방법으로 실시하되, 멀라이트 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of mullite.

[실시예 33][Example 33]

실시예 1과 동일한 방법으로 실시하되, 규불화마그네슘 1g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 1 g of magnesium silicide.

[실시예 34][Example 34]

실시예 1과 동일한 방법으로 실시하되, 스테아린산칼슘 1g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 1 g of calcium stearate.

[실시예 35][Example 35]

실시예 1과 동일한 방법으로 실시하되, 트리페닐포스파인 2g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 2 g of triphenylphosphine.

[실시예 36][Example 36]

실시예 1과 동일한 방법으로 실시하되, 글리시딜 네오데카노에이트 6g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but further added 6 g of glycidyl neodecanoate.

[실시예 37][Example 37]

실시예 1과 동일한 방법으로 실시하되, 글리시딜 디옥틸프탈레이트 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of glycidyl dioctylphthalate.

[실시예 38][Example 38]

실시예 1과 동일한 방법으로 실시하되, 2-브로모피리딘 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of 2-bromopyridine.

[실시예 39][Example 39]

실시예 1과 동일한 방법으로 실시하되, 디이소노닐프탈레이트 3g을 더 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding 3 g of diisononylphthalate.

[실시예 40][Example 40]

실시예 1과 동일한 방법으로 실시하되, 실시예 2 내지 실시예 39 따라 부가된 부가물을 모두 부가하여 실시하였다.It was carried out in the same manner as in Example 1, but was carried out by adding all of the additives added according to Examples 2 to 39.

[실 험][Experiment]

실시예에 따라 제조된 조성물을 콘크리트 면에 건조두께 5mm가 되도록 스프레이 분사하여 도막층을 형성한 후 기계적 물성, 예를 들면 오염물질 용출정도, 균열추종성, 가사경화시간, 경화시간 등을 측정하였다.The composition prepared according to the example was spray-sprayed to a concrete surface to a dry thickness of 5 mm to form a coating layer, and then mechanical properties such as contaminant elution degree, crack followability, pot life curing time, curing time, and the like were measured.

그 결과를 표 1로 나타냈다. The results are shown in Table 1.

오염물질 용출Contaminant elution 균열추종성(mm)Crack followability (mm) 가사경화시간(분)Housework curing time (minutes) 경화 시간(hr)Curing time (hr) 실시예 1Example 1 없음none 1.71.7 2020 44 실시예 2Example 2 없음none 1.91.9 2828 55 실시예 3Example 3 없음none 2.12.1 2323 66 실시예 4Example 4 없음none 1.81.8 2424 33 실시예 6Example 6 없음none 2.22.2 2222 55 실시예 7Example 7 없음none 2.12.1 2121 44 실시예 8Example 8 없음none 2.42.4 1717 44 실시예 9Example 9 없음none 1.71.7 2121 55 실시예 10Example 10 없음none 1.91.9 2424 66 실시예 11Example 11 없음none 1.61.6 2323 33 실시예 12Example 12 없음none 1.71.7 2121 55 실시예 13Example 13 없음none 2.12.1 2323 44 실시예 14Example 14 없음none 1.81.8 2121 55 실시예 15Example 15 없음none 2.72.7 2525 44 실시예 16Example 16 없음none 2.42.4 2121 55 실시예 17Example 17 없음none 2.72.7 2222 66 실시예 18Example 18 없음none 2.32.3 2323 33 실시예 19Example 19 없음none 2.82.8 2121 55 실시예 20Example 20 없음none 2.22.2 2323 55 실시예 21Example 21 없음none 2.12.1 1919 44 실시예 22Example 22 없음none 2.42.4 2121 55 실시예 23Example 23 없음none 2.72.7 1919 55 실시예 24Example 24 없음none 2.92.9 2121 66 실시예 25Example 25 없음none 2.62.6 2020 33 실시예 26Example 26 없음none 2.72.7 2323 44 실시예 27Example 27 없음none 1.51.5 2424 55 실시예 28Example 28 없음none 2.02.0 2121 44 실시예 29Example 29 없음none 1.81.8 2222 55 실시예 30Example 30 없음none 2.22.2 2121 66 실시예 31Example 31 없음none 2.12.1 2222 44 실시예 32Example 32 없음none 2.32.3 2222 55 실시예 33Example 33 없음none 1.81.8 2323 44 실시예 34Example 34 없음none 2.12.1 2323 55 실시예 35Example 35 없음none 2.22.2 2525 55 실시예 36Example 36 없음none 2.72.7 2323 66 실시예 37Example 37 없음none 2.62.6 2323 55 실시예 38Example 38 없음none 2.82.8 2121 55 실시예 39Example 39 없음none 2.72.7 2323 55 실시예 40Example 40 없음none 2.82.8 2222 66

표 1에 나타난 바와 같이, 실시예들에 따라 제조된 친환경 방수제 조성물은 오염물질의 용출이 없고, 균열 추종성이 좋으며, 경화시간이 매우 신속하여 초속경을 요구하는 방수도막 형성에 용이한 것으로 나타났다. As shown in Table 1, the eco-friendly waterproofing composition prepared according to the examples showed no elution of contaminants, good crack followability, and very fast curing time, and thus it was found that it was easy to form a waterproof coating requiring an ultra-fast diameter.

이상에서 설명한 바와 같이, 본 발명이 속하는 기술 분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예는 모두 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위의 의미 및 범위 그리고 그 등가개념으로부터 도출되는 모두 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.As described above, those skilled in the art to which the present invention pertains will understand that the present invention can be implemented in other specific forms without changing the technical spirit or essential features thereof. Therefore, all of the embodiments described above are illustrative and should be understood as non-limiting. The scope of the present invention should be construed as including all changed or modified forms derived from the meaning and scope of the claims to be described later rather than the above detailed description and equivalent concepts thereof.

Claims (5)

폴리우레아 수지 100중량부 기준으로,
음이온 유화제 3 내지 20중량부;
숯가루 5 내지 20중량부;
실리카 2 내지 15중량부;
경화제 20 내지 60중량부;
옥틸페놀에톡실레이트 1 내지 10중량부;
폴리비닐알코올 1 내지 20중량부;
셀룰로오스 섬유 0.1 내지 5중량부;
나노세라믹 입자 3 내지 20중량부;
증점제 1 내지 20중량부;
부착증진제 1 내지 20중량부;
박리방지제 5 내지 30중량부; 및
산화방지제 3 내지 10중량부를 포함하는 친환경 방수제 조성물에,
폴리비닐리덴플로라이드수지를 폴리우레아 수지 100중량부 기준으로 5 내지 20중량부로 더 포함하고,
네오펜틸글리콜을 폴리우레아 수지 100중량부 기준으로 1 내지 10중량부로 더 포함하며,
티타늄옥사이드를 폴리우레아 수지 100중량부 기준으로 0.1 내지 5중량부로 더 포함하고,
세륨을 폴리우레아 수지 100중량부 기준으로 0.1 내지 5중량부로 더 포함하며,
진크암모늄클로라이드를 폴리우레아 수지 100중량부 기준으로 1 내지 10중량부로 더 포함하고,
천매암 분말을 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함하며,
보크사이트 분말을 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함하고,
디부틸프탈레이트를 폴리우레아 수지 100중량부 기준으로 2 내지 6중량부로 더 포함하며,
3-메르캅토프로필트리메톡시실란을 폴리우레아 수지 100중량부 기준으로 1 내지 3중량부로 더 포함하고,
겔라이트 미분말을 폴리우레아 수지 100중량부 기준으로 1 내지 3중량부로 더 포함하며,
구연산을 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함하고,
소디윰스테아레이트를 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함하며,
붕산 화합물을 폴리우레아 수지 100중량부 기준으로 1 내지 6중량부로 더 포함하고,
황산알루미늄을 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함하며,
노말부틸아크릴레이트를 폴리우레아 수지 100중량부 기준으로 1 내지 10중량부로 더 포함하고,
멀라이트를 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함하며,
규불화마그네슘을 폴리우레아 수지 100중량부 기준으로 0.5 내지 3중량부로 더 포함하고,
트리페닐포스파인을 폴리우레아 수지 100중량부 기준으로 0.1 내지 3중량부로 더 포함하며,
글리시딜 네오데카노에이트를 폴리우레아 수지 100중량부 기준으로 3 내지 10중량부로 더 포함하고,
2-브로모피리딘을 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함하는 친환경 방수제 조성물.
Based on 100 parts by weight of polyurea resin,
3 to 20 parts by weight of an anionic emulsifier;
5 to 20 parts by weight of charcoal powder;
2 to 15 parts by weight of silica;
20 to 60 parts by weight of a curing agent;
1 to 10 parts by weight of octylphenol ethoxylate;
1 to 20 parts by weight of polyvinyl alcohol;
0.1 to 5 parts by weight of cellulose fibers;
3 to 20 parts by weight of nanoceramic particles;
1 to 20 parts by weight of a thickener;
1 to 20 parts by weight of adhesion promoter;
5 to 30 parts by weight of an anti-peeling agent; And
In an eco-friendly waterproofing composition comprising 3 to 10 parts by weight of an antioxidant,
Further comprising a polyvinylidene fluoride resin in an amount of 5 to 20 parts by weight based on 100 parts by weight of the polyurea resin,
Neopentyl glycol further comprises 1 to 10 parts by weight based on 100 parts by weight of the polyurea resin,
Further comprising 0.1 to 5 parts by weight of titanium oxide based on 100 parts by weight of the polyurea resin,
Cerium is further included in an amount of 0.1 to 5 parts by weight based on 100 parts by weight of the polyurea resin,
Zinc ammonium chloride is further included in an amount of 1 to 10 parts by weight based on 100 parts by weight of the polyurea resin,
It further comprises 1 to 5 parts by weight based on 100 parts by weight of the polyurea resin, the phyllite powder,
Further comprising 1 to 5 parts by weight of bauxite powder based on 100 parts by weight of the polyurea resin,
Dibutylphthalate further comprises 2 to 6 parts by weight based on 100 parts by weight of the polyurea resin,
3-mercaptopropyltrimethoxysilane further comprises 1 to 3 parts by weight based on 100 parts by weight of the polyurea resin,
Further comprising 1 to 3 parts by weight of gelite fine powder based on 100 parts by weight of the polyurea resin,
Citric acid is further included in an amount of 1 to 5 parts by weight based on 100 parts by weight of the polyurea resin,
Sodium stearate further comprises 1 to 5 parts by weight based on 100 parts by weight of the polyurea resin,
A boric acid compound is further included in an amount of 1 to 6 parts by weight based on 100 parts by weight of the polyurea resin,
Further comprising 1 to 5 parts by weight of aluminum sulfate based on 100 parts by weight of the polyurea resin,
Further comprising 1 to 10 parts by weight of normal butyl acrylate based on 100 parts by weight of the polyurea resin,
Further comprising 1 to 5 parts by weight of mullite based on 100 parts by weight of the polyurea resin,
Further comprising 0.5 to 3 parts by weight of magnesium silicide based on 100 parts by weight of the polyurea resin,
Further comprising 0.1 to 3 parts by weight of triphenyl phosphine based on 100 parts by weight of the polyurea resin,
Further comprising 3 to 10 parts by weight of glycidyl neodecanoate based on 100 parts by weight of the polyurea resin,
Eco-friendly waterproofing composition further comprising 1 to 5 parts by weight of 2-bromopyridine based on 100 parts by weight of the polyurea resin.
 삭제delete 삭제delete 방수제 조성물을 시공하기 위한 시공표면을 처리하는 표면처리단계;
상기 표면처리단계가 종료된 후 프라이머를 도포하는 프라이머 도포단계;
상기 프라이머 도포단계가 종료된 상단에 폴리우레아 수지 100중량부 기준으로, 음이온 유화제 3 내지 20중량부, 숯가루 5 내지 20중량부, 실리카 2 내지 15중량부, 경화제 20 내지 60중량부, 옥틸페놀에톡실레이트 1 내지 10중량부, 폴리비닐알코올 1 내지 20중량부, 셀룰로오스 섬유 0.1 내지 5중량부, 나노세라믹 입자 3 내지 20중량부, 증점제 1 내지 20중량부, 부착증진제 1 내지 20중량부, 박리방지제 5 내지 30중량부, 및 산화방지제 3 내지 10중량부를 포함하는 친환경 방수제 조성물에, 폴리비닐리덴플로라이드수지를 폴리우레아 수지 100중량부 기준으로 5 내지 20중량부로 더 포함하고, 네오펜틸글리콜을 폴리우레아 수지 100중량부 기준으로 1 내지 10중량부로 더 포함하며, 티타늄옥사이드를 폴리우레아 수지 100중량부 기준으로 0.1 내지 5중량부로 더 포함하고, 세륨을 폴리우레아 수지 100중량부 기준으로 0.1 내지 5중량부로 더 포함하며, 진크암모늄클로라이드를 폴리우레아 수지 100중량부 기준으로 1 내지 10중량부로 더 포함하고, 천매암 분말을 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 보크사이트 분말을 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함하고, 디부틸프탈레이트를 폴리우레아 수지 100중량부 기준으로 2 내지 6중량부로 더 포함하며, 3-메르캅토프로필트리메톡시실란을 폴리우레아 수지 100중량부 기준으로 1 내지 3중량부로 더 포함하고, 겔라이트 미분말을 폴리우레아 수지 100중량부 기준으로 1 내지 3중량부로 더 포함하며, 구연산을 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함하고, 소디윰스테아레이트를 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 붕산 화합물을 폴리우레아 수지 100중량부 기준으로 1 내지 6중량부로 더 포함하고, 황산알루미늄을 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 노말부틸아크릴레이트를 폴리우레아 수지 100중량부 기준으로 1 내지 10중량부로 더 포함하고, 멀라이트를 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 규불화마그네슘을 폴리우레아 수지 100중량부 기준으로 0.5 내지 3중량부로 더 포함하고, 트리페닐포스파인을 폴리우레아 수지 100중량부 기준으로 0.1 내지 3중량부로 더 포함하며, 글리시딜 네오데카노에이트를 폴리우레아 수지 100중량부 기준으로 3 내지 10중량부로 더 포함하고, 2-브로모피리딘을 폴리우레아 수지 100중량부 기준으로 1 내지 5중량부로 더 포함하는 친환경 방수제 조성물을 스프레이 방식으로 분사하는 스프레이 분사단계; 및
상기 스프레이 분사단계가 종료된 후 양생하는 양생단계를 포함하는 친환경 방수제 조성물 시공방법.
Surface treatment step of treating the construction surface for applying the waterproofing agent composition;
A primer application step of applying a primer after the surface treatment step is finished;
Based on 100 parts by weight of the polyurea resin on the upper end of the primer application step, 3 to 20 parts by weight of anionic emulsifier, 5 to 20 parts by weight of charcoal powder, 2 to 15 parts by weight of silica, 20 to 60 parts by weight of a curing agent, octylphenol Ethoxylate 1 to 10 parts by weight, polyvinyl alcohol 1 to 20 parts by weight, cellulose fiber 0.1 to 5 parts by weight, nanoceramic particles 3 to 20 parts by weight, thickener 1 to 20 parts by weight, adhesion promoter 1 to 20 parts by weight, In an eco-friendly waterproofing composition comprising 5 to 30 parts by weight of a peeling inhibitor and 3 to 10 parts by weight of an antioxidant, further comprising 5 to 20 parts by weight of a polyvinylidene fluoride resin based on 100 parts by weight of a polyurea resin, and neopentyl glycol It further comprises 1 to 10 parts by weight based on 100 parts by weight of the polyurea resin, and further comprises 0.1 to 5 parts by weight based on 100 parts by weight of the polyurea resin, and 0.1 to 5 parts by weight of cerium based on 100 parts by weight of the polyurea resin. It further comprises 5 parts by weight, further comprises 1 to 10 parts by weight of zinc ammonium chloride based on 100 parts by weight of the polyurea resin, further comprises 1 to 5 parts by weight based on 100 parts by weight of the polyurea resin, and bauxite Powder is further included in an amount of 1 to 5 parts by weight based on 100 parts by weight of a polyurea resin, and dibutylphthalate is further included in an amount of 2 to 6 parts by weight based on 100 parts by weight of a polyurea resin, and 3-mercaptopropyltrimethoxysilane. 1 to 3 parts by weight based on 100 parts by weight of the polyurea resin, further comprising 1 to 3 parts by weight based on 100 parts by weight of the polyurea resin, and 1 to 3 parts by weight of citric acid based on 100 parts by weight of the polyurea resin. It further comprises 5 parts by weight, further comprises 1 to 5 parts by weight of sodium stearate based on 100 parts by weight of the polyurea resin, and further comprises 1 to 6 parts by weight based on 100 parts by weight of the polyurea resin, and sulfuric acid Aluminum is further included in an amount of 1 to 5 parts by weight based on 100 parts by weight of a polyurea resin, and normal butyl arc Relate is further included in 1 to 10 parts by weight based on 100 parts by weight of polyurea resin, mullite is further included in 1 to 5 parts by weight based on 100 parts by weight of polyurea resin, and magnesium silicide is 100 parts by weight of polyurea resin It further comprises 0.5 to 3 parts by weight based on, further comprises 0.1 to 3 parts by weight based on 100 parts by weight of the polyurea resin, triphenyl phosphine, and 3 based on 100 parts by weight of the polyurea resin glycidyl neodecanoate. A spray spray step of spraying an eco-friendly waterproofing composition further comprising from 1 to 5 parts by weight based on 100 parts by weight of the polyurea resin, further comprising from 10 parts by weight to 10 parts by weight; And
An eco-friendly waterproofing composition construction method comprising a curing step of curing after the spray spraying step is finished.
 제4항 있어서,
상기 양생단계가 종료된 그 상단에 탑코팅하는 탑코팅단계를 더 포함하는 친환경 방수제 조성물 시공방법.


The method of claim 4,
An eco-friendly waterproofing composition construction method further comprising a top coating step of top coating the top of the curing step is completed.
KR1020200099132A 2020-08-07 2020-08-07 A Mortar Composition of Crack-Reducing Type for High-Performance Floor and Constructing Methods Using Thereof KR102224342B1 (en)