KR102196130B1 - Packaging structure for antibacteral and antimicrobial - Google Patents

Packaging structure for antibacteral and antimicrobial Download PDF

Info

Publication number
KR102196130B1
KR102196130B1 KR1020200071517A KR20200071517A KR102196130B1 KR 102196130 B1 KR102196130 B1 KR 102196130B1 KR 1020200071517 A KR1020200071517 A KR 1020200071517A KR 20200071517 A KR20200071517 A KR 20200071517A KR 102196130 B1 KR102196130 B1 KR 102196130B1
Authority
KR
South Korea
Prior art keywords
antibacterial
antiviral
weight
parts
film
Prior art date
Application number
KR1020200071517A
Other languages
Korean (ko)
Inventor
이원정
손성구
Original Assignee
이원정
손성구
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이원정, 손성구 filed Critical 이원정
Priority to KR1020200071517A priority Critical patent/KR102196130B1/en
Application granted granted Critical
Publication of KR102196130B1 publication Critical patent/KR102196130B1/en

Abstract

The present invention provides an antibacterial and antimicrobial packaging body. The antibacterial and antimicrobial packaging body comprises: a pouch or a container type packaging material providing a space to store content; and an antibacterial and antimicrobial film provided on an inner surface of the packaging material to sterilize or pasteurize bacteria or remove viruses caused by corruption or contamination of the content.

Description

항균 및 항바이러스 포장체{Packaging structure for antibacteral and antimicrobial}Packaging structure for antibacteral and antimicrobial}

본 발명은 항균 및 항바이러스 포장체에 관한 것으로서, 보다 상세하게는 식품이나 미용제품 등을 수용하는 합성수지 재질의 포장체의 내면에 항균 및 항바이러스 기능을 제공하는 필름이 구성되어 내용물의 변질을 억제하고 항균 및 항바이러스 기능을 제공할 수 있는 항균 및 항바이러스 포장체에 관한 것이다. The present invention relates to an antibacterial and antiviral package, and more particularly, a film that provides antibacterial and antiviral functions is formed on the inner surface of a package made of synthetic resin that accommodates food or beauty products, thereby suppressing deterioration of the contents. It relates to an antibacterial and antiviral package capable of providing antibacterial and antiviral functions.

일반적으로, 식품이나 미용제품 등을 수용하는 봉지 또는 파우치나 용기 타입의 포장체는, PP나 PE 소재로 제작된 포장재의 융착 등을 이용한 밀봉을 통해 해당 내용물의 수용 및 밀봉을 가능하게 하고, 포장재가 간단히 절취되는 것을 통해 내부의 내용물 섭취나 사용을 가능하게 할 수 있다.In general, a bag or pouch or container-type package for accommodating food or beauty products is capable of receiving and sealing the contents through sealing using fusion bonding of a packaging material made of PP or PE material, and The ingestion or use of the contents of the inside can be made possible through a simple cut.

그러나 상기와 같은 포장체에 포장되는 내용물은, 여러 종류의 성분이 섞인 상태이고 이에 진공 포장되더라도, 내용물의 충전 공정에서 충전 장비나 밀봉 장비들의 낙하균이나 바이러스 및 장기간 보관이나 유통 중 온도 증의 조건이나 성분들간 화학반응 등에 의해 내용물의 조성물간 트러블이나 변질 등이 발생되어 내용물이 오염되는 문제점이 있다.However, even if the contents packaged in such a package are mixed with various kinds of ingredients and are vacuum-packed therein, falling bacteria or viruses of the filling equipment or sealing equipment in the filling process of the contents, and conditions of temperature increase during long-term storage or distribution There is a problem in that the contents are contaminated due to problems or deterioration between the compositions of the contents due to chemical reactions between the components or components.

(특허문헌 0001) 공개특허 10-2017-0006785(Patent Document 0001) Patent Publication 10-2017-0006785

(특허문헌 0002) 공개특허 10-2001-0083379(Patent Document 0002) Unexamined Patent Publication 10-2001-0083379

따라서 본 발명의 목적은 식품이나 미용제품 등을 수용하는 합성수지 재질의 포장체의 내면에 항균 및 항바이러스 기능을 제공하는 필름이 구성되어 내용물의 변질을 억제하고 항균 및 항바이러스 기능을 제공할 수 있는 항균 및 항바이러스 포장체를 제공하는 것이다.Therefore, it is an object of the present invention to provide an anti-bacterial and anti-viral function on the inner surface of a package made of synthetic resin that accommodates food or beauty products, thereby suppressing deterioration of the contents and providing anti-bacterial and anti-viral functions. It is to provide an antibacterial and antiviral package.

한편, 본 발명의 목적은 이상에서 언급한 목적으로 제한되지 않으며, 언급되지 않은 다른 목적들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.On the other hand, the object of the present invention is not limited to the object mentioned above, other objects not mentioned will be clearly understood by those skilled in the art from the following description.

본 발명에 의하면, 내용물이 수용될 수 있는 공간을 제공하는 파우치나 용기 타입의 포장재와; 포장재의 내면에 구성되어 내용물의 변질이나 오염에 따른 세균을 살균 또는 멸균시키거나 바이스러스를 제거하는 항균 및 항바이러스 필름을 포함하는 항균 및 항바이러스 포장체가 제공된다.According to the present invention, a pouch or container type packaging material providing a space in which the contents can be accommodated; There is provided an antibacterial and antiviral package comprising an antibacterial and antiviral film configured on the inner surface of the packaging material to sterilize or sterilize bacteria due to deterioration or contamination of the contents, or to remove the virus.

여기서, 항균 및 항바이러스 필름은, 포장재의 내면에 면적을 가지는 필름체를 포함하고, 상기 필름체는, 기재 필름 기능을 제공하기 위한 열가소성 플라스틱 95 내지 99.5 중량% 및 항균 및 항바이러스 기능 제공을 위한 순도 85% 내지 95%의 구리 0.5 내지 5 중량%가 혼합되어 제조되는 것이 바람직하다. Here, the antibacterial and antiviral film includes a film body having an area on the inner surface of the packaging material, and the film body is 95 to 99.5% by weight of a thermoplastic plastic for providing a base film function, and for providing an antibacterial and antiviral function It is preferred that 0.5 to 5% by weight of copper having a purity of 85% to 95% are mixed and prepared.

따라서 본 발명에 의하면, 식품이나 미용제품 등을 수용하는 합성수지 재질의 포장체의 내면에 항균 및 항바이러스 기능을 제공하는 필름이 구성되어 내용물의 변질을 억제하고 항균 및 항바이러스 기능을 제공할 수 있다. Therefore, according to the present invention, a film that provides antibacterial and antiviral functions is formed on the inner surface of a package made of a synthetic resin material for accommodating food or beauty products, thereby suppressing deterioration of the contents and providing antibacterial and antiviral functions. .

한편, 본 발명의 효과는 이상에서 언급한 효과로 제한되지 않으며, 언급되지 않은 다른 효과들은 청구범위의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.On the other hand, the effects of the present invention are not limited to the above-mentioned effects, and other effects not mentioned will be clearly understood by those skilled in the art from the description of the claims.

이하, 첨부된 도면을 참조하면서 본 발명의 바람직한 실시예에 대하여 상세히 설명하기로 한다. Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

본 발명에 따른 항균 및 항바이러스 포장체는, 내용물이 수용될 수 있는 공간을 제공하는 파우치나 용기 타입의 포장재와, 포장재의 내면에 융착이나 접착 또는 부착 구성되어 내용물의 변질이나 오염에 따른 세균을 살균 또는 멸균시키거나 바이스러스를 제거하는 항균 및 항바이러스 필름 등을 포함한다.The antibacterial and antiviral package according to the present invention is composed of a pouch or container-type packaging material that provides a space in which the contents can be accommodated, and fusion, adhesion, or adhesion to the inner surface of the packaging material to prevent bacteria due to deterioration or contamination of the contents. And antibacterial and antiviral films to sterilize or sterilize or remove viruses.

포장재는, 내용물을 수용 및 보호하는 기능을 제공하는 것으로서, PE나 PP 등과 같은 합성수지 원료를 시트지나 용기로 용융 성형하는 것에 의해 파우치나 용기 타입으로 제조된다.The packaging material provides a function of accommodating and protecting contents, and is manufactured in a pouch or container type by melt-molding a synthetic resin raw material such as PE or PP into a sheet paper or a container.

포장재의 파우치나 용기 타입의 제조는, 공지의 구성과 방식에 의해 이루어질 수 있으므로, 상세한 설명은 생략하기로 한다. Since the manufacture of the pouch or container type of the packaging material may be performed by a known configuration and method, a detailed description will be omitted.

항균 및 항바이러스 필름은, 포장재의 내면에 융착, 증착, 접착 및 부착 등의 방식으로 구성되고 내용물의 변질이나 오염에 따른 세균을 살균 또는 멸균시키거나 바이러스를 제거하는 수단으로서, 포장재의 내면에 대응된 면적을 가지고 형상 변형 가능한 두께를 가지는 필름체인 것이 바람직하다.Antibacterial and antiviral films are constructed in a manner such as fusion, deposition, adhesion and attachment to the inner surface of the packaging material, and are a means to sterilize or sterilize bacteria due to deterioration or contamination of the contents, or to remove viruses, corresponding to the inner surface of the packaging material. It is preferable that the film has a thickness that can be deformed in shape with a reduced area.

상기 필름체는, 기재 필름 기능을 제공하기 위한 열가소성 플라스틱 95 내지 99.5 중량% 및 항균 및 항바이러스 기능 제공을 위한 순도 85% 내지 95%의 구리 0.5 내지 5 중량%가 혼합되어 제조될 수 있다.The film body may be prepared by mixing 95 to 99.5% by weight of a thermoplastic plastic for providing a base film function and 0.5 to 5% by weight of copper having a purity of 85% to 95% for providing an antibacterial and antiviral function.

여기서, 열가소성 플라스틱은, PE, OPP, PVC, PO, PET 및 PS 중 적어도 어느 하나인 것이 좋다.Here, the thermoplastic plastic is preferably at least one of PE, OPP, PVC, PO, PET, and PS.

또한, 구리는, 항균 및 항바이러스 기능을 제공하기 위한 것으로서, 순도 85% 내지 95%를 가지는데, 85% 미만의 순도를 가지는 경우에는 항균 및 항바이러스 기능이 시간이 지날수록 크게 저하되고 95% 초과하는 순도를 가지는 경우에는 항균 및 항바이러스 기능이 시간이 지나도 변화가 없으나 용융 과정이 복잡하여 제조 비용이 많이 소요되므로 상기와 같은 수치 한정에 따른 임계적 의의를 가지는 것이 좋다.In addition, copper is intended to provide antibacterial and antiviral functions, and has a purity of 85% to 95%, but when it has a purity of less than 85%, the antibacterial and antiviral functions are greatly reduced over time and 95% If the purity is exceeded, the antibacterial and antiviral functions do not change over time, but the melting process is complicated and the manufacturing cost is high, so it is good to have a critical significance according to the above numerical limitation.

또한, 구리는 필름체와의 제조시 열가소성 플라스틱과의 중량%의 합 100 중량%에 대하여, 0.5 내지 5 중량%가 첨가 혼합되는데, 구리의 첨가량이 0.5 중량%를 미만하는 경우에는 항균 및 항바이러스 기능이 저하되고, 구리의 첨가량이 5 중량%를 초과하는 경우에는 기재 필름 기능을 제공하는 열가소성 플라tm틱의 연신율 등과 같은 제조성이 저하되는 문제점이 있으므로, 상기와 같은 수치한정에 따른 임계적 의의를 가지는 것이 좋다.In addition, copper is mixed in an amount of 0.5 to 5% by weight based on 100% by weight of the total weight% of the thermoplastic plastic in the manufacture of the film body, but when the amount of copper is less than 0.5% by weight, antibacterial and antiviral If the function is deteriorated and the amount of copper added exceeds 5% by weight, there is a problem in that manufacturability such as the elongation of the thermoplastic plastic that provides the base film function is deteriorated.Therefore, the critical significance of the numerical limitation as described above It is good to have.

따라서 항균 및 항바이러스 필름에 의하면, 구리와 열가소성 플라스틱이 혼합된 필름체가 제조되고 필름체가 포장재의 내면에 구성됨으로써, 포장재의 내면에 항균 및 항바이러스를 위한 조성물이 구성됨에 따라 포장체의 유통 중 내용물의 변질을 억제하고 변질이나 사용 중 번식된 세균이나 침투된 바이러스를 살균 또는 멸균시킬 수 있다.Therefore, according to the antibacterial and antiviral film, a film body in which copper and thermoplastic plastic are mixed is produced, and the film body is constructed on the inner surface of the packaging material, so that the composition for antibacterial and antiviral is formed on the inner surface of the packaging material. It can suppress the deterioration of the virus and sterilize or sterilize bacteria or infiltrated viruses that have grown during deterioration or use.

한편, 본 발명의 항균 및 항바이러스 필름은, 상기와 같이 제조되는 필름체의 일면 즉, 포장재에 접촉되지 않고 내용물 측에 위치되는 일면에 전체 또는 국부적으로 증착이나 도포 또는 분사 코팅 등의 방식으로 구성되어 포장재에 수용된 내용물에 존재하는 유해성 세균을 살균 또는 멸균시키거나 바이러스를 제거시키는 보조기능층을 더 포함할 수 있다.On the other hand, the antimicrobial and antiviral film of the present invention is constructed by a method such as deposition, application, spray coating, etc., entirely or locally on one side of the film body manufactured as described above, that is, on one side located on the side of the contents without contacting the packaging material. It may further include an auxiliary functional layer for sterilizing or sterilizing harmful bacteria present in the contents contained in the packaging material or removing viruses.

보조기능층은, 상기 필름체의 일면 중 내용물과 접촉되는 부분에 전체 또는 국부적으로 내용물의 변질 등에 따라 존재하는 세균을 살균 또는 멸균시키거나 바이러스를 제거하는 기능을 제공하는 것으로서, 필름체에 무기산화물이 증착되어 형성되는 배리어층과, 배리어층 상부에 항균 및 항바이러스성 물질이 증착되어 형성되는 항균 및 항바이러스층 등을 포함한다.The auxiliary functional layer is to provide a function of sterilizing or sterilizing bacteria or removing viruses present in a part of the film body that is in contact with the contents, either entirely or locally, and is an inorganic oxide on the film body. And a barrier layer formed by the deposition, and an antibacterial and antiviral layer formed by depositing an antibacterial and antiviral material on the barrier layer.

배리어층은, 무기산화물의 투명한 치밀막으로 형성되어 촉매 기능을 제공하고 포장재의 개봉 후 외부 조명 등으로부터 복사 에너지를 흡수하여 후술된 항균 및 항바이러스층에 의한 내용물의 항균 및 항바이러스 기능이 극대화되도록 하는 것으로서, 무기산화물은 실리카, 알루미나, 지르코니아 및 이들의 조합에서 선택된 적어도 어느 하나를 포함하고, 두께가 5nm 내지 10nm인 것이 바람직하다.The barrier layer is formed of a transparent dense film of inorganic oxide to provide a catalytic function and absorb radiant energy from external lighting after opening the packaging material to maximize the antibacterial and antiviral functions of the contents by the antibacterial and antiviral layers described below. As such, the inorganic oxide includes at least one selected from silica, alumina, zirconia, and combinations thereof, and preferably has a thickness of 5 nm to 10 nm.

여기서, 배리어층은, 두께가 5nm에 미만하는 경우에는 항균 및 항바이러스 기능이 저하되고 10nm를 초과하는 경우에는 필름체가 포장재의 형상 변형을 따라 가변되는 것에 장애가 발생되므로, 상기와 같은 두께 한정에 의한 임계적 의의를 가지는 것이 좋다. Here, when the thickness of the barrier layer is less than 5 nm, the antibacterial and antiviral functions are deteriorated, and when the thickness exceeds 10 nm, it is difficult to change the shape of the packaging material. It is good to have critical significance.

한편, 본 발명에 있어서, 필름체에 배리어층이 구성되어 광원 등으로부터 촉매 기능이 제공되는 경우, 필름체는, 배리어층을 통해 투과되거나 반사되는 빛이 내용물을 향해 광범위하게 확산되도록 하기 위한 확산블록이 돌출 형성되는 것이 좋다.Meanwhile, in the present invention, when a barrier layer is formed on the film body to provide a catalytic function from a light source, etc., the film body is a diffusion block for allowing light transmitted or reflected through the barrier layer to diffuse widely toward the contents. It is good that this protrusion is formed.

여기서, 확산블록은, 나이테 형상과 같이 다수개의 볼록한 띠들이 점차 큰 지름을 가지면서 연속적으로 배열되는 구조를 가질 수 있으며, 필름체의 일면으로부터 내용물을 향해 투과 또는 반사되는 빛이 원형 고리 형상을 가지면서 투과 또는 반사되도록 하는 것이 좋다.Here, the diffusion block may have a structure in which a plurality of convex bands gradually have a large diameter, such as a ring shape, and are continuously arranged, and light transmitted or reflected from one side of the film body toward the contents has a circular ring shape. It is better to be transmitted or reflected.

또한, 필름체는, 소정의 두께를 가지는 경우, 필름체의 제조시 발포 압출이나 발포 사출 등과 같은 발포 성형에 의해 내부에 빛의 산란시키면서 반사되도록 하기 위한 소정 크기의 기포들이 형성되는 것이 바람직하다.In addition, when the film body has a predetermined thickness, it is preferable that bubbles of a predetermined size are formed so as to be reflected while scattering light inside by foam molding such as foam extrusion or foam injection when the film body is manufactured.

항균 및 항바이러스층은, 치밀막으로 형성되어 항균 기능을 제공하는 것으로서, 은나노, 게르마늄, 셀레늄, 아연 및 트리클로산을 포함하고, 두께가 10nm 내지 20nm인 것이 바람직하다.The antibacterial and antiviral layer is formed as a dense film to provide an antibacterial function, and includes silver nano, germanium, selenium, zinc and triclosan, and preferably has a thickness of 10 nm to 20 nm.

여기서, 항균 및 항바이러스층은, 두께가 10nm에 미만하는 경우에는 금속 성분의 조성물이 막으로 형성되지 않아 충분한 반응성을 가질 수 없고 20nm를 초과하는 경우에는 공정시간이 많이 필요할 뿐만 아니라 필름체의 두께가 두꺼워져 포장재의 형상 변형을 따라 가변되지 않고 들뜨게 되어 제조성이 저하되는 문제점이 있으므로, 상기와 같은 두께 한정에 의한 임계적 의의를 가지는 것이 좋다.Here, when the thickness of the antibacterial and antiviral layer is less than 10 nm, the composition of the metal component is not formed as a film, so it cannot have sufficient reactivity, and when it exceeds 20 nm, it requires a lot of processing time as well as the thickness of the film body. Since the thickness is thick and does not change according to the shape deformation of the packaging material, but is lifted, there is a problem in that manufacturability is deteriorated, so it is good to have a critical significance by limiting the thickness as described above.

또한, 항균 및 항바이러스층은, 은나노 100 중량부에, 게르마늄 70 내지 90 중량부, 셀레늄 50 내지 70 중량부, 아연 30 내지 50 중량부 및 트리클로산 3 내지 5 중량부 등을 포함한다.In addition, the antibacterial and antiviral layer contains 100 parts by weight of silver nano, 70 to 90 parts by weight of germanium, 50 to 70 parts by weight of selenium, 30 to 50 parts by weight of zinc, 3 to 5 parts by weight of triclosan, and the like.

은나노는, 내용물의 변질에 따른 세균을 살균하거나 침투된 바이러스를 제거 시키기 위한 것으로서, 나노 입자를 가지는 것이 바람직하다.Silver nano is intended to sterilize bacteria due to deterioration of the contents or to remove infiltrating viruses, and it is preferable to have nanoparticles.

게르마늄은, 내용물의 살균 및 바이러스 제거 기능 이외에 내용물에 원적외선을 방사하여 독소를 제거하기 위한 것으로서, 은나노 100 중량부에 대하여 70 내지 90 중량부가 첨가 및 혼합되는데, 70 중량부에 미만하는 경우에는 살균이나 바이러스 제거 및 독소 제거 기능이 저하되고, 90 중량부를 초과하는 경우에는 발열 등으로 인하여 오히려 내용물의 변질을 초래하므로, 상기와 같은 중량부 한정에 의한 임계적 의의를 가지는 것이 좋다.Germanium is for removing toxins by radiating far-infrared rays to the contents in addition to the function of sterilizing and removing viruses of the contents.70 to 90 parts by weight are added and mixed with respect to 100 parts by weight of silver nano, but if less than 70 parts by weight, sterilization or Virus removal and toxin removal functions are deteriorated, and if it exceeds 90 parts by weight, the contents are rather deteriorated due to heat or the like, so it is good to have a critical significance by limiting the parts by weight as described above.

셀레늄은, 내용물의 활성산소를 제거하기 위한 것으로서, 은나노 100 중량부에 대하여 50 내지 70 중량부가 첨가 및 혼합되는데, 50 중량부에 미만하는 경우에는 활성산소 제거 기능이 저하되고, 70 중량부를 초과하는 경우에는 단백질 분해에 의한 냄새 발생 등의 문제점이 있으므로, 상기와 같은 중량부 한정에 의한 임계적 의의를 가지는 것이 좋다.Selenium is for removing active oxygen from the contents, and 50 to 70 parts by weight are added and mixed with respect to 100 parts by weight of silver nano, but if it is less than 50 parts by weight, the active oxygen removal function is lowered, and exceeding 70 parts by weight. In this case, since there is a problem such as odor generation due to protein decomposition, it is preferable to have a critical significance by limiting the weight part as described above.

아연은, 항균, 항바이러스 및 항염증 등의 기능을 제공하기 위한 것으로서, 은나노 100 중량부에 대하여 30 내지 50 중량부가 첨가 및 혼합되는데, 30 중량부에 미만하는 경우에는 항균 및 항염증 기능이 저하되고, 50 중량부를 초과하는 경우에는 오히려 필름체에 포함된 구리의 살균 및 멸균 기능을 상쇄시키게 되므로, 상기와 같은 중량부 한정에 의한 임계적 의의를 가지는 것이 좋다.Zinc is to provide functions such as antibacterial, antiviral and anti-inflammatory, and 30 to 50 parts by weight are added and mixed with respect to 100 parts by weight of silver nano, but if it is less than 30 parts by weight, antibacterial and anti-inflammatory functions are lowered. In the case of exceeding 50 parts by weight, the sterilization and sterilization functions of copper contained in the film body are rather offset, so it is good to have a critical significance by limiting the parts by weight as described above.

트리클로산은,방균 기능을 제공하기 위한 것으로서, 은나노 100 중량부에 대하여 3 내지 5 중량부가 첨가 및 혼합되는데, 3 중량부에 미만하는 경우에는 방균 기능이 저하되어 포장재의 개봉후 온도 등에 의해 변질되어 진균이나 곰팡이가 발생되는 것을 억제하는 효과가 저하되고, 5 중량부를 초과하는 경우에는 오히려 다른 물질과의 반응에 따라 장시간 사용 중 발암물질로 변질되는 문제점이 있으므로, 상기와 같은 중량부 한정에 의한 임계적 의의를 가지는 것이 좋다. Triclosan is to provide an antibacterial function, and 3 to 5 parts by weight are added and mixed with respect to 100 parts by weight of silver nano, but if it is less than 3 parts by weight, the antibacterial function is deteriorated and the packaging material is deteriorated by temperature after opening. The effect of suppressing the occurrence of mold or mold decreases, and if it exceeds 5 parts by weight, it is rather deteriorated into a carcinogen during long-time use due to a reaction with other substances. It is good to have significance.

따라서 보조기능층에 의하면, 내용물에 접촉되는 항균 및 항바이러스를 위한 조성물이 구성됨에 따라 포장체를 이용한 유통 중 내용물의 변질을 억제하고 변질이나 사용 중 번식된 세균이나 침투된 바이러스를 제거할 수 있다.Therefore, according to the auxiliary functional layer, as the composition for antibacterial and antiviral in contact with the contents is composed, it is possible to suppress the deterioration of the contents during distribution using the package, and to remove the bacteria or infiltrated viruses that have grown during deterioration or use. .

이하, 상술한 바와 같은 구성을 가지는 포장체의 작용과 효과를 구체적인 실시예를 통해 설명하기로 한다.Hereinafter, the action and effect of the package having the configuration as described above will be described through specific embodiments.

합성수지 재질의 용융을 통하여 포장재가 파우치나 용기 타입으로 제조된 후 포장재의 내면에 항균 및 항바이러스 필름이 구성된다.After the packaging material is manufactured in a pouch or container type through melting of the synthetic resin material, an antibacterial and antiviral film is formed on the inner surface of the packaging material.

여기서, 항균 및 항바이러스 필름은 열가소성 플라스틱 99 중량% 및 순도 95%의 구리 1 중량%가 혼합되어 제조된다.Here, the antibacterial and antiviral film is prepared by mixing 99% by weight of a thermoplastic plastic and 1% by weight of copper having a purity of 95%.

합성수지 재질의 용융을 통하여 포장재가 파우치나 용기 타입으로 제조된 후 포장재의 내면에 항균 및 항바이러스 필름이 구성된다.After the packaging material is manufactured in a pouch or container type through melting of the synthetic resin material, an antibacterial and antiviral film is formed on the inner surface of the packaging material.

여기서, 항균 및 항바이러스 필름은 열가소성 플라스틱 97 중량% 및 순도 90%의 구리 3 중량%가 혼합되어 제조된다.Here, the antibacterial and antiviral film is prepared by mixing 97% by weight of a thermoplastic plastic and 3% by weight of copper having a purity of 90%.

합성수지 재질의 용융을 통하여 포장재가 파우치나 용기 타입으로 제조된 후 포장재의 내면에 항균 및 항바이러스 필름이 구성된다.After the packaging material is manufactured into a pouch or container type through melting of the synthetic resin material, an antibacterial and antiviral film is formed on the inner surface of the packaging material.

여기서, 항균 및 항바이러스 필름은 열가소성 플라스틱 95 중량% 및 순도 85%의 구리 5 중량%가 혼합되어 제조된다.Here, the antibacterial and antiviral film is prepared by mixing 95% by weight of a thermoplastic plastic and 5% by weight of copper having a purity of 85%.

합성수지 재질의 용융을 통하여 포장재가 파우치나 용기 타입으로 제조된 후 포장재의 내면에 항균 및 항바이러스 필름이 구성된다.After the packaging material is manufactured in a pouch or container type through melting of the synthetic resin material, an antibacterial and antiviral film is formed on the inner surface of the packaging material.

여기서, 항균 및 항바이러스 필름은 열가소성 플라스틱 99 중량% 및 순도 95%의 구리 1 중량%가 혼합되어 제조된다.Here, the antibacterial and antiviral film is prepared by mixing 99% by weight of a thermoplastic plastic and 1% by weight of copper having a purity of 95%.

또한, 항균 및 항바이러스 필름의 일면에 배리어층과 항균 및 항바이러스층으로 구분되는 보조기능층이 구성된다.In addition, an auxiliary functional layer divided into a barrier layer and an antibacterial and antiviral layer is formed on one side of the antibacterial and antiviral film.

여기서, 배리어층은 두께가 5nm이고, 항균 및 항바이러스층은 두게가 10nm이며 은나노 100 중량부에 게르마늄 70 중량부, 셀레늄 50 중량부, 아연 30 중량부 및 트리클로산 3 중량부를 포함한다.Here, the barrier layer has a thickness of 5 nm, the antibacterial and antiviral layer has a thickness of 10 nm, and contains 70 parts by weight of germanium, 50 parts by weight of selenium, 30 parts by weight of zinc, and 3 parts by weight of triclosan in 100 parts by weight of silver nano.

합성수지 재질의 용융을 통하여 포장재가 파우치나 용기 타입으로 제조된 후 포장재의 내면에 항균 및 항바이러스 필름이 구성된다.After the packaging material is manufactured in a pouch or container type through melting of the synthetic resin material, an antibacterial and antiviral film is formed on the inner surface of the packaging material.

여기서, 항균 및 항바이러스 필름은 열가소성 플라스틱 97 중량% 및 순도 90%의 구리 3 중량%가 혼합되어 제조된다.Here, the antibacterial and antiviral film is prepared by mixing 97% by weight of a thermoplastic plastic and 3% by weight of copper having a purity of 90%.

또한, 항균 및 항바이러스 필름의 일면에 배리어층과 항균 및 항바이러스층으로 구분되는 보조기능층이 구성된다.In addition, an auxiliary functional layer divided into a barrier layer and an antibacterial and antiviral layer is formed on one side of the antibacterial and antiviral film.

여기서, 배리어층은 두께가 8nm이고, 항균 및 항바이러스층은 두게가 15nm이며 은나노 100 중량부에 게르마늄 80 중량부, 셀레늄 60 중량부, 아연 40 중량부 및 트리클로산 4 중량부를 포함한다.Here, the barrier layer has a thickness of 8 nm, the antibacterial and antiviral layer has a thickness of 15 nm, and contains 80 parts by weight of germanium, 60 parts by weight of selenium, 40 parts by weight of zinc, and 4 parts by weight of triclosan in 100 parts by weight of silver nano.

합성수지 재질의 용융을 통하여 포장재가 파우치나 용기 타입으로 제조된 후 포장재의 내면에 항균 및 항바이러스 필름이 구성된다.After the packaging material is manufactured in a pouch or container type through melting of the synthetic resin material, an antibacterial and antiviral film is formed on the inner surface of the packaging material.

여기서, 항균 및 항바이러스 필름은 열가소성 플라스틱 95 중량% 및 순도 85%의 구리 5 중량%가 혼합되어 제조된다.Here, the antibacterial and antiviral film is prepared by mixing 95% by weight of a thermoplastic plastic and 5% by weight of copper having a purity of 85%.

또한, 항균 및 항바이러스 필름의 일면에 배리어층과 항균 및 항바이러스층으로 구분되는 보조기능층이 구성된다.In addition, an auxiliary functional layer divided into a barrier layer and an antibacterial and antiviral layer is formed on one side of the antibacterial and antiviral film.

여기서, 배리어층은 두께가 10nm이고, 항균 및 항바이러스층은 두게가 20nm이며 은나노 100 중량부에 게르마늄 90 중량부, 셀레늄 70 중량부, 아연 50 중량부 및 트리클로산 5 중량부를 포함한다.Here, the barrier layer has a thickness of 10 nm, the antibacterial and antiviral layer has a thickness of 20 nm, and contains 90 parts by weight of germanium, 70 parts by weight of selenium, 50 parts by weight of zinc, and 5 parts by weight of triclosan in 100 parts by weight of silver nano.

상기 실시예 1 내지 6에 따라 제조된 포장체의 참고예 또는 평가예로서, A사에서 판매중인 종래의 포장체에 B사에서 판매 중인 항균 필름을 부착하였다.As a reference or evaluation example of the package prepared according to Examples 1 to 6, an antibacterial film sold by Company B was attached to a conventional package sold by Company A.

이후, 상기와 같은 실시예 1 내지 실시예 4의 포장체의 항균력을 평기하기 위하여 황색포도상구균과 대장균을 균주액을 준비하고 초기 균수를 측정하였으며, 포장체의 포장재와 필름을 15cm * 15cm의 크기로 준비한 후 각 시험용 균주액을 1ml를 적하하고 커버 필름으로 커버한 상태에서 실내 온도 및 습도에서 형광등을 조사하면서 24시간 동안 정치 배양 후 세균수를 측정하여 표 1에 나타내었다. Thereafter, in order to evaluate the antibacterial activity of the packages of Examples 1 to 4 as described above, a strain solution was prepared for Staphylococcus aureus and E. coli, and the initial number of bacteria was measured, and the packaging material and film of the package were 15cm * 15cm in size. After preparation, 1 ml of each test strain solution was added dropwise, and the number of bacteria was measured after stationary culture for 24 hours while irradiating a fluorescent lamp at room temperature and humidity while covering with a cover film.

Figure 112020060613585-pat00001
Figure 112020060613585-pat00001

따라서 표 1에 의하면, 실시예 1 내지 실시예 6은 실시예 7에 비하여, 황색포도상구균, 대장균, 고초균 및 녹농균 등 모두에서 항균 활성치가 매우 높은 것을 알 수 있다.Therefore, according to Table 1, it can be seen that the antibacterial activity values of Examples 1 to 6 are very high in all of Staphylococcus aureus, Escherichia coli, Bacillus aeruginosa and Pseudomonas aeruginosa compared to Example 7.

이에, 상술한 바에 의하면, 포장재의 내면에 항균 및 항바이러스 필름이 구성됨에 따라, 상기 필름에 의해 내용물이 변질되거나 또는 개봉후 내용물에 세균이 증식되거나 바이러스가 침투되더라도 이를 살균 및 제거할 수 있다.Accordingly, according to the above, as the antibacterial and antiviral film is formed on the inner surface of the packaging material, even if the contents are deteriorated by the film, or bacteria are multiplied or virus penetrates the contents after opening, it can be sterilized and removed.

또한, 상기 필름의 보조기능층으로부터 항균 및 항바이러스 기능이 부가적으로 더 제공될 수 있다. In addition, antibacterial and antiviral functions may be additionally provided from the auxiliary functional layer of the film.

상술한 본 발명에서는 구체적인 실시예에 관해 설명하였으나, 여러 가지 변형이 본 발명의 범위에서 벗어나지 않고 실시될 수 있다. 따라서 발명의 범위는 설명된 실시예에 의하여 정할 것이 아니고 청구 범위와 청구 범위의 균등한 것에 의해 정해져야 한다.In the above-described present invention, specific embodiments have been described, but various modifications may be implemented without departing from the scope of the present invention. Therefore, the scope of the invention should not be determined by the described embodiments, but should be defined by the claims and the equivalents of the claims.

Claims (5)

내용물이 수용될 수 있는 공간을 제공하는 파우치나 용기 타입의 포장재와;
포장재의 내면에 구성되어 내용물의 변질이나 오염에 따른 세균을 살균 또는 멸균시키거나 바이스러스를 제거하는 항균 및 항바이러스 필름을 포함하고,
항균 및 항바이러스 필름은,
포장재의 내면에 면적을 가지는 필름체와, 필름체에 구성되는 보조기능층을 포함하며,
상기 필름체는,
기재 필름 기능을 제공하기 위한 열가소성 플라스틱 95 내지 99.5 중량% 및 항균 및 항바이러스 기능 제공을 위한 순도 85% 내지 95%의 구리 0.5 내지 5 중량%가 혼합되어 제조되고,
보조기능층은,
필름체에 항균 및 항바이러스성 물질이 증착되어 형성되는 항균 및 항바이러스층을 포함하며,
항균 및 항바이러스층은,
두께가 10nm 내지 20nm이고,
은나노 100 중량부에,
게르마늄 70 내지 90 중량부, 셀레늄 50 내지 70 중량부, 아연 30 내지 50 중량부 및 트리클로산 3 내지 5 중량부를 포함하는 것을 특징으로 하는 항균 및 항바이러스 포장체.A pouch or container type packaging material that provides a space in which the contents can be accommodated;
It includes an antibacterial and antiviral film that is configured on the inner surface of the packaging material to sterilize or sterilize bacteria due to deterioration or contamination of the contents, or to remove viruses,
Antibacterial and antiviral film,
It includes a film body having an area on the inner surface of the packaging material, and an auxiliary functional layer configured on the film body,
The film body,
95 to 99.5% by weight of a thermoplastic plastic for providing a base film function and 0.5 to 5% by weight of copper having a purity of 85% to 95% for providing an antibacterial and antiviral function are mixed and manufactured,
The auxiliary functional layer,
It includes an antibacterial and antiviral layer formed by depositing an antibacterial and antiviral material on the film body,
The antibacterial and antiviral layer,
The thickness is 10 nm to 20 nm,
100 parts by weight of silver nano,
An antibacterial and antiviral package comprising 70 to 90 parts by weight of germanium, 50 to 70 parts by weight of selenium, 30 to 50 parts by weight of zinc, and 3 to 5 parts by weight of triclosan. 삭제delete 삭제delete 제1항에 있어서, 상기 보조기능층은,
배리어층을 포함하고,
배리어층은,
실리카, 알루미나, 지르코니아 및 이들의 조합에서 선택된 적어도 어느 하나를 포함하고,
두께가 5nm 내지 10nm인 것을 특징으로 하는 항균 및 항바이러스 포장체.
The method of claim 1, wherein the auxiliary functional layer,
Including a barrier layer,
The barrier layer,
Including at least any one selected from silica, alumina, zirconia, and combinations thereof,
Antibacterial and antiviral package, characterized in that the thickness is 5nm to 10nm.
 삭제delete
KR1020200071517A 2020-06-12 2020-06-12 Packaging structure for antibacteral and antimicrobial KR102196130B1 (en)