KR102160243B1 - Method for forming a color stereoscopic mark on a tire - Google Patents
Method for forming a color stereoscopic mark on a tire Download PDFInfo
- Publication number
- KR102160243B1 KR102160243B1 KR1020180152696A KR20180152696A KR102160243B1 KR 102160243 B1 KR102160243 B1 KR 102160243B1 KR 1020180152696 A KR1020180152696 A KR 1020180152696A KR 20180152696 A KR20180152696 A KR 20180152696A KR 102160243 B1 KR102160243 B1 KR 102160243B1
- Authority
- KR
- South Korea
- Prior art keywords
- mark
- dimensional
- tire
- urethane
- forming
- Prior art date
Abstract
본 발명의 타이어에 입체 컬러 마크를 형성하는 방법은, 타이어의 사이드월에 부착될 입체 마크가 형성된 몰드를 제작하는 단계; 상기 몰드에 컬러 잉크를 포함하는 우레탄을 주입하여 입체 마크를 성형하는 단계; 및 상기 입체 마크를 접착제로 사이드월에 부착하는 단계를 포함한다.
본 발명에 의하면, 타이어의 사이드월에 입체적인 컬러 마크를 형성할 수 있다. 또한, 투명한 우레탄을 사용하여 다양한 색상을 구현할 수 있고, 3D 프린팅을 활용하여 다양한 형상을 구현할 수 있다.The method of forming a three-dimensional color mark on a tire of the present invention comprises the steps of: manufacturing a mold having a three-dimensional mark to be attached to a side wall of the tire; Molding a three-dimensional mark by injecting urethane containing color ink into the mold; And attaching the three-dimensional mark to the sidewall with an adhesive.
According to the present invention, a three-dimensional color mark can be formed on the sidewall of a tire. In addition, various colors can be implemented using transparent urethane, and various shapes can be implemented by using 3D printing.
Description
본 발명은 타이어에 입체 컬러 마크를 형성하는 방법에 관한 것이다.The present invention relates to a method of forming a three-dimensional color mark on a tire.
고무 제품, 특히 자동차용 타이어에 마크를 사용하는 것은 이미 공지되어 있다. 예를 들면, 자동차 경주에서 타이어 사이드월에 문자(lettering) 또는 광고용 기호 내지 형상 스티커를 부착하는 것은 공지되어 있다. 마크는 스텐실(stencil)을 이용하여 타이어에 분사되거나 결합된다. 상기한 경우 모두 마크는 타이어에서 쉽게 분리되어 마크와 타이어 사이에 내구성 있는 부착이 이루어지지 않는다. 그래서 고무 제품에 견고하게 부착되는 마크에 대한 요구가 있어 왔다.It is already known to use marks in rubber products, in particular automobile tires. For example, it is known to attach letters or advertisement signs or shape stickers to tire sidewalls in automobile races. Marks are sprayed or bonded to the tire using a stencil. In all of the above cases, the mark is easily separated from the tire so that a durable attachment between the mark and the tire is not achieved. Therefore, there has been a demand for a mark that is firmly attached to rubber products.
그러한 내구성 있는 결합은 예를 들어, 마크가 새겨질 고무 제품의 일부가 도료로 채색될 때 가능하다. 예를 들면 사이드월이나 트레드 층을 적어도 한가지 색채의 선명한 안료로 채색한 타이어를 사용함으로써 차량을 더욱 잘 분간할 수 있다.Such durable bonding is possible, for example, when a part of the rubber product to be marked with is painted with paint. For example, by using tires in which the sidewall or tread layer is colored with at least one color of vivid pigment, the vehicle can be better identified.
그러나, 고무 제품 각 부분을 채색하는 방법으로 마크를 부착하는 것에는 한계가 있는데, 마크가 복잡한 기하학적 형상을 포함하거나 문자를 새기고자 할 때에 그렇다. 그러한 경우, 고무 제품에 마크를 부착하는 것은 매우 복잡하고 따라서 비용이 매우 높아질 것이다.However, there is a limit to attaching a mark as a method of coloring each part of a rubber product, and this is the case when the mark contains a complex geometric shape or when you want to engrave characters. In such a case, attaching a mark to the rubber product will be very complicated and thus the cost will be very high.
본 발명의 목적은 타이어의 사이드월에 입체적인 컬러 마크를 형성하는 방법을 제공하는 것이다.It is an object of the present invention to provide a method of forming a three-dimensional color mark on a sidewall of a tire.
상기 목적을 달성하기 위한 본 발명의 타이어에 입체 컬러 마크를 형성하는 방법은, 타이어의 사이드월에 부착될 입체 마크가 형성된 몰드를 제작하는 단계; 상기 몰드에 컬러 잉크를 포함하는 우레탄을 주입하여 입체 마크를 성형하는 단계; 및 상기 입체 마크를 접착제로 사이드월에 부착하는 단계를 포함한다.The method of forming a three-dimensional color mark on a tire of the present invention for achieving the above object includes: manufacturing a mold having a three-dimensional mark to be attached to a side wall of the tire; Molding a three-dimensional mark by injecting urethane containing color ink into the mold; And attaching the three-dimensional mark to the sidewall with an adhesive.
상기 몰드는 3D 프린팅에 의해 제작되는 것이 바람직하다.It is preferable that the mold is manufactured by 3D printing.
상기 우레탄은 유연하고 투명한 재질로 이루어진 것이 바람직하다.The urethane is preferably made of a flexible and transparent material.
상기 우레탄은 상온경화형 2액형 액상 우레탄인 것이 바람직하다.It is preferable that the urethane is a room temperature curing type two-component liquid urethane.
상기 입체 마크 성형 단계에서, 상기 우레탄 100 중량부에 왁스 2~5 중량부가 첨가된 것이 바람직하다.In the three-dimensional mark forming step, it is preferable that 2 to 5 parts by weight of wax are added to 100 parts by weight of the urethane.
상기 입체 마크의 두께는 0.05~5.0mm인 것이 바람직하다.It is preferable that the thickness of the three-dimensional mark is 0.05 to 5.0 mm.
상기 입체 마크 성형 단계에서, 상기 우레탄을 주입할 때 발광부재를 매립하여 입체 마크를 성형할 수 있다.In the three-dimensional mark forming step, when the urethane is injected, a three-dimensional mark may be formed by embedding a light emitting member.
상기한 본 발명에 의하면, 타이어의 사이드월에 입체적인 컬러 마크를 형성할 수 있다.According to the present invention described above, a three-dimensional color mark can be formed on the sidewall of a tire.
또한, 투명한 우레탄을 사용하여 다양한 색상을 구현할 수 있고, 3D 프린팅을 활용하여 다양한 형상을 구현할 수 있다.In addition, various colors can be implemented using transparent urethane, and various shapes can be implemented by using 3D printing.
이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 실시예에 대하여 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다.Hereinafter, embodiments of the present invention will be described in detail so that those skilled in the art can easily implement the present invention. However, the present invention may be implemented in various different forms, and is not limited to the embodiments described herein.
본 발명의 일 실시예에 따른 타이어에 입체 컬러 마크를 형성하는 방법은, 별도의 몰드에서 입체 컬러 마크를 성형한 다음 접착제로 타이어의 사이드월에 부착한다.In a method of forming a three-dimensional color mark on a tire according to an embodiment of the present invention, a three-dimensional color mark is formed in a separate mold and then attached to the sidewall of the tire with an adhesive.
우선, 타이어의 사이드월에 부착될 입체 마크가 형성된 몰드를 제작한다.First, a mold in which a three-dimensional mark to be attached to a side wall of a tire is formed is manufactured.
몰드는 소정 두께로 형성되고 임의의 입체적 형상의 마크가 음각으로 형성될 수 있다.The mold is formed to a predetermined thickness, and a mark of an arbitrary three-dimensional shape may be formed in an intaglio.
이 몰드는 몰드에 주입되는 우레탄보다 녹는점이 높은 플라스틱으로 형성될 수 있다.This mold may be formed of a plastic having a higher melting point than the urethane injected into the mold.
몰드는 3D 프린팅에 의해 제작될 수 있다. 몰드는 3D 프린팅에 일반적으로 사용되는 소재를 사용할 수 있으며, 플라스틱에 한정되지 않는다. 3D 프린팅에 의해 다양한 문자, 기호, 표장, 입체적 형상을 쉽게 구현할 수 있다.The mold can be made by 3D printing. The mold may use a material generally used for 3D printing, and is not limited to plastic. Various characters, symbols, marks, and three-dimensional shapes can be easily implemented by 3D printing.
다음으로, 몰드에 컬러 잉크를 포함하는 우레탄을 주입하여 입체 마크를 성형한다.Next, urethane containing color ink is injected into the mold to form a three-dimensional mark.
우레탄은 액상 우레탄으로서 이에 컬러 잉크가 혼합된 것을 사용한다.Urethane is a liquid urethane, and a color ink is mixed with it.
컬러 잉크(안료)는 잉크 밀(ink mill)로 미세하게 갈아서 만든 잉크 타입의 고농축 우레탄 안료를 사용할 수 있다. 컬러 잉크는 우레탄에 대비해서 3중량% 미만을 사용한다. 3중량% 이상을 사용하면 우레탄과 경화 반응을 나타내지 못하고 겉에 묻어나게 된다.The color ink (pigment) may be an ink-type highly concentrated urethane pigment made by finely grinding with an ink mill. The color ink uses less than 3% by weight of the urethane. If more than 3% by weight is used, the curing reaction with urethane is not exhibited and the surface is buried.
우레탄은 경화되면 유연하고 투명한 재질로 이루어질 수 있다. 타이어는 차량 주행 중에 굴곡 운동을 하기 때문에, 우레탄이 유연하게 탄성적으로 변형될 수 있어야 사이드월에 부착되어 있던 입체 마크가 떨어지지 않을 수 있다. 또한, 우레탄이 투명하면 혼합되는 잉크의 컬러가 그대로 구현될 수 있다.When urethane is cured, it can be made of a flexible and transparent material. Since the tire performs bending motion while driving the vehicle, the three-dimensional mark attached to the sidewall may not fall off only when the urethane can be flexibly and elastically deformed. In addition, if the urethane is transparent, the color of the ink to be mixed can be realized as it is.
상기 우레탄은 상온경화형 2액형 액상 우레탄인 것이 바람직하다. 액상 우레탄이 상온에서 경화되기 때문에 입체 마크를 쉽게 성형할 수 있다. 예를 들어, 우레탄은 Smooth-on사에서 제조한 Clear Flex™ 95를 사용할 수 있다. 이는 투명한 우레탄 액상 고무 화합물로서 절대적인 투명도와 광저항성을 요구하는 곳에 적용될 수 있다. 낮은 점도에 의해 쉽게 혼합하고 주입할 수 있다. 또한, Clear Flex™ 95는 거의 수축 없이 상온에서 경화된다.The urethane is preferably a room temperature curing type two-component liquid urethane. Since liquid urethane is cured at room temperature, three-dimensional marks can be easily molded. For example, as urethane, Clear Flex™ 95 manufactured by Smooth-on may be used. This is a transparent urethane liquid rubber compound that can be applied to a place requiring absolute transparency and light resistance. It can be easily mixed and poured due to its low viscosity. In addition, Clear Flex™ 95 cures at room temperature with little shrinkage.
2액형 우레탄은 주제와 경화제가 서로 화학 반응을 하여 경화된다. 이와 달리, 1액형 우레탄은 공기 중에 있는 습기와 반응하여 경화된다. 2액형 우레탄에는 적당량의 희석재를 추가하고 교반기로 잘 혼합하여 사용한다.Two-component urethane is cured by chemical reaction between the main material and the hardener. In contrast, one-component urethanes cure by reacting with moisture in the air. Add an appropriate amount of diluent to the two-component urethane and mix well with a stirrer.
상기 우레탄에는 왁스가 첨가되는 것이 바람직하다. 우레탄 100 중량부에 왁스 2~5 중량부를 첨가할 수 있다. 예를 들어 왁스는 닛폰세이로 주식회사에서 제조하는 석유계 왁스인 Ozoace37을 사용할 수 있다.It is preferable that a wax is added to the urethane. 2 to 5 parts by weight of wax may be added to 100 parts by weight of urethane. For example, as the wax, Ozoace37, a petroleum wax manufactured by Nippon Seiro Co., Ltd., can be used.
Ozoace37은 탄소 농도가 높은 왁스로서 엷은 백색의 비드 타입 약품이다. 녹는점은 73~78℃이고, 오존에 의한 노화를 방지하기 위해 사용된다.Ozoace37 is a wax with high carbon concentration and is a pale white bead type chemical. Melting point is 73~78℃, and it is used to prevent aging by ozone.
왁스는 내오존성 향상을 위해 첨가되는 것인데, 왁스가 2 중량부 미만이면 오존에 의한 크랙이 성장할 수 있으며, 왁스가 5 중량부 초과이면 우레탄 표면에 백색 현상이 발생할 수 있다.Wax is added to improve ozone resistance. If the wax is less than 2 parts by weight, cracks due to ozone may grow, and if the wax is more than 5 parts by weight, whiteness may occur on the urethane surface.
성형된 입체 마크의 두께는 0.05~5.0mm인 것이 바람직하다. 기존 사이드월 전사지의 두께가 0.05mm이므로, 마크 두께가 0.05mm 미만이면 입체감이 떨어진다. 마크 두께가 5.0mm 초과이면, 고속주행 및 코너링시에 사이드월이 접힐 때 노면에 닿을 수 있고, 조기 박리 가능성이 높아질 수 있다.It is preferable that the thickness of the molded three-dimensional mark is 0.05 to 5.0 mm. Since the thickness of the existing sidewall transfer paper is 0.05mm, if the mark thickness is less than 0.05mm, the three-dimensional effect is deteriorated. If the mark thickness is more than 5.0mm, the sidewall may contact the road surface when the sidewall is folded during high-speed driving and cornering, and the possibility of early peeling may increase.
마지막으로, 성형된 입체 마크를 접착제로 사이드월에 부착한다. 마크 부착시 사용되는 접착제는 아크릴계 순간접착제 또는 합성 고무 베이스의 감압성 접착제(Pressure Sensitive Adhesive)가 사용될 수 있다.Finally, the molded three-dimensional mark is attached to the sidewall with an adhesive. The adhesive used for attaching the mark may be an acrylic instant adhesive or a synthetic rubber-based pressure sensitive adhesive.
한편, 상기 입체 마크 성형 단계에서, 상기 우레탄을 주입할 때 발광부재를 매립하여 입체 마크를 성형할 수도 있다.Meanwhile, in the three-dimensional mark forming step, when the urethane is injected, a three-dimensional mark may be formed by embedding a light emitting member.
컬러 입체 마크는 그 두께와 잉크의 함유량을 조절하여 반투명하게 형성할 수 있으며, 마크 내부에 발광부재를 매립함으로써 타이어에 부착된 상태에서 발광부재가 더욱 잘 식별될 수 있다.The color three-dimensional mark can be formed to be translucent by adjusting its thickness and ink content, and by embedding the light emitting member in the mark, the light emitting member can be better identified while attached to the tire.
발광부재로는 야광소재로 형성된 것이나, LED와 태양광 전지패널 등을 액상 우레탄 속에 삽입하여 굳힐 수 있다. 그러면, 입체 마크가 발광부재를 보호하는 역할도 하게 된다.The light emitting member is formed of a luminous material, but can be hardened by inserting an LED and a solar panel into liquid urethane. Then, the three-dimensional mark also serves to protect the light emitting member.
유연한 솔라 패널(flexible solar panel)에 전도성 카본 블랙(conductive carbon black)을 포함하는 투명 고무를 도포하고, 우측에 유연한 솔라 패널(flexible solar panel)을 부착하고, 좌측에 유연한 PCB에 부착된 LED를 부착하여 전기가 통하도록 연결한다. 유연한 솔라 패널(flexible solar panel)을 덮는 컬러 우레탄 두께가 0.05mm 이하로 형성되면, 솔라 패널이 발전할 수 있다.A transparent rubber containing conductive carbon black is applied to the flexible solar panel, the flexible solar panel is attached to the right, and the LED attached to the flexible PCB is attached to the left. And connect it so that electricity can flow. If the color urethane thickness covering the flexible solar panel is formed to be less than 0.05mm, the solar panel can develop.
한편, 타이어의 사이드월에는 노화방지제를 사용하는데, 노화방지제는 노화 방지에는 유리하지만 표면이 갈색으로(누렇게) 변하는 갈변 현상이 발생할 수 있다. 종래의 경우, 갈변 방지를 위해 별도의 고무를 개발하여 사이드월에 부착한 다음 그 위에 컬러 고무를 부착하였다.On the other hand, an anti-aging agent is used for the sidewall of the tire, and although the anti-aging agent is advantageous for anti-aging, browning may occur in which the surface turns brown (yellow). In the conventional case, to prevent browning, a separate rubber was developed and attached to the sidewall, and then colored rubber was attached thereon.
반면에, 본 발명의 경우 사이드월 고무보다 노화 속도가 느린 우레탄 고무를 사용하기 때문에 갈변 현상이 발생하지 않는다. 또한, 사이드월 고무와 우레탄 고무 사이에 접착제를 도포함에 따라, 사이드월에서 올라오는 노화방지제가 접착물질을 통과하는데 오랜 시간이 걸리기 때문에, 갈변 현상을 더욱 방지할 수 있다.On the other hand, in the case of the present invention, since the urethane rubber having a slower aging rate than the sidewall rubber is used, browning does not occur. In addition, as the adhesive is applied between the sidewall rubber and the urethane rubber, since it takes a long time for the anti-aging agent rising from the sidewall to pass through the adhesive material, browning can be further prevented.
본 발명의 타이어에 의하면, 타이어의 사이드월에 입체적인 컬러 마크를 형성할 수 있다.According to the tire of the present invention, a three-dimensional color mark can be formed on the side wall of the tire.
또한, 투명한 우레탄을 사용하여 다양한 색상을 구현할 수 있고, 3D 프린팅을 활용하여 다양한 형상을 구현할 수 있다.In addition, various colors can be implemented using transparent urethane, and various shapes can be implemented by using 3D printing.
이상, 본 발명을 예시적으로 설명하였으며, 본 발명이 속하는 기술 분야에서 통상의 지식을 가지는 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 변형이 가능할 것이다. 따라서, 본 명세서에 개시된 실시예들은 본 발명을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 사상과 범위가 한정되는 것은 아니다. 본 발명의 보호범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술은 본 발명의 권리범위에 포함하는 것으로 해석되어야 할 것이다.In the above, the present invention has been exemplarily described, and those of ordinary skill in the technical field to which the present invention pertains will be able to make various modifications without departing from the essential characteristics of the present invention. Accordingly, the embodiments disclosed in the present specification are not intended to limit the present invention, but to explain the present invention, and the spirit and scope of the present invention are not limited by these embodiments. The scope of protection of the present invention should be interpreted by the following claims, and all technologies within the scope equivalent thereto should be interpreted as being included in the scope of the present invention.
Claims (7)
상기 몰드에 컬러 잉크를 포함하는 우레탄을 주입하여 입체 마크를 성형하는 단계;
상기 입체 마크를 접착제로 사이드월에 부착하는 단계를 포함하고,
상기 입체 마크 성형 단계에서, 상기 우레탄을 주입할 때 발광부재로서 LED와 태양광 전지패널을 우레탄 속에 매립되도록 삽입하되, 상기 LED와 태양광 전지패널은 유연한 솔라 패널에 전도성 카본 블랙을 포함하는 투명 고무를 도포하고, 유연한 솔라 패널과 유연한 PCB에 부착된 LED를 전기가 통하도록 연결하는 것을 특징으로 하는 타이어에 입체 컬러 마크를 형성하는 방법.Manufacturing a mold in which a three-dimensional mark to be attached to a sidewall of a tire is formed;
Molding a three-dimensional mark by injecting urethane containing color ink into the mold;
Including the step of attaching the three-dimensional mark to the side wall with an adhesive,
In the step of forming the three-dimensional mark, when the urethane is injected, the LED and the solar panel are inserted to be embedded in the urethane as a light emitting member, but the LED and the solar panel are transparent rubber containing conductive carbon black in a flexible solar panel. A method of forming a three-dimensional color mark on a tire, comprising applying and connecting the flexible solar panel and the LED attached to the flexible PCB to conduct electricity.
상기 몰드는 3D 프린팅에 의해 제작되는 것을 특징으로 하는 타이어에 입체 컬러 마크를 형성하는 방법.The method of claim 1,
The method of forming a three-dimensional color mark on a tire, characterized in that the mold is produced by 3D printing.
상기 우레탄은 유연하고 투명한 재질로 이루어진 것을 특징으로 하는 타이어에 입체 컬러 마크를 형성하는 방법.The method of claim 2,
The urethane is a method of forming a three-dimensional color mark on a tire, characterized in that made of a flexible and transparent material.
상기 우레탄은 상온경화형 2액형 액상 우레탄인 것을 특징으로 하는 타이어에 입체 컬러 마크를 형성하는 방법.The method of claim 3,
The urethane is a room temperature curing type two-component liquid urethane method for forming a three-dimensional color mark on a tire, characterized in that.
상기 입체 마크 성형 단계에서, 상기 우레탄 100 중량부에 왁스 2~5 중량부가 첨가된 것을 특징으로 하는 타이어에 입체 컬러 마크를 형성하는 방법.The method of claim 4,
In the three-dimensional mark forming step, a method of forming a three-dimensional color mark on a tire, characterized in that 2 to 5 parts by weight of wax is added to 100 parts by weight of the urethane.
상기 입체 마크의 두께는 0.05~5.0mm인 것을 특징으로 하는 타이어에 입체 컬러 마크를 형성하는 방법.The method according to any one of claims 1 to 5,
The method of forming a three-dimensional color mark on a tire, characterized in that the thickness of the three-dimensional mark is 0.05 ~ 5.0mm.