KR102121727B1 - Pollution prevention tape for paint protection - Google Patents

Pollution prevention tape for paint protection Download PDF

Info

Publication number
KR102121727B1
KR102121727B1 KR1020180109429A KR20180109429A KR102121727B1 KR 102121727 B1 KR102121727 B1 KR 102121727B1 KR 1020180109429 A KR1020180109429 A KR 1020180109429A KR 20180109429 A KR20180109429 A KR 20180109429A KR 102121727 B1 KR102121727 B1 KR 102121727B1
Authority
KR
South Korea
Prior art keywords
polyethylene
layer
polypropylene
film
blocking film
Prior art date
Application number
KR1020180109429A
Other languages
Korean (ko)
Other versions
KR20200030778A (en
Inventor
정명준
Original Assignee
정명준
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 정명준 filed Critical 정명준
Priority to KR1020180109429A priority Critical patent/KR102121727B1/en
Publication of KR20200030778A publication Critical patent/KR20200030778A/en
Application granted granted Critical
Publication of KR102121727B1 publication Critical patent/KR102121727B1/en

Abstract

본 발명은 도장 보호용 오염 방지테이프 및 그 제조방법에 관한 것으로, 도장 작업 시 사용되는 마스킹 테이프로 자외선을 차단하고 도장 품질을 높일 수 있는 기술이다.
본 발명은 점착제층; 검정색을 제외한 색상으로 형성되어 자외선을 차단되게 하는 제1필름과, 상기 제1필름의 하부에 상기 점착제층과 접합되고 검정색으로 형성되어 온도를 유지되게 하는 제2필름으로 구성되는 자외선차단필름층; 상기 자외선차단필름층 상부에 접합되는 것으로, 폴리프로필렌(Polypropylene)이 내측에 위치하고 폴리에틸렌(Polyethylene)을 외측에 위치되게 형성되는 부직포층;으로 구성되되, 상기 부직포층은, 상기 폴리프로필렌(Polypropylene)과 폴리에틸렌(Polyethylene)의 중량비를 1:1로 되게 하고, 상기 폴리프로필렌(Polypropylene)과 폴리에틸렌(Polyethylene)을 열롤에서 일정한 두께로 연속 압연하는 열 카렌다에 의해 제조되되, 폭 방향으로 찢어짐이 쉽도록 줄무늬가 형성되며, 상기 자외선차단필름층은, 상기 부직포층과의 접합을 용이하도록 하기 위하여 상기 부직포층의 외측과 동일한 폴리에틸렌(Polyethylene) 재질을 사용하는 것을 특징으로 하는 도장 보호용 오염방지테이프를 제공한다.The present invention relates to an anti-pollution tape for coating protection and a method for manufacturing the same, and is a technology capable of blocking ultraviolet rays and increasing the quality of the coating with a masking tape used during painting.
The present invention is an adhesive layer; A UV blocking film layer composed of a first film formed in a color other than black to block UV rays, and a second film bonded to the adhesive layer under the first film and formed in black to maintain temperature; It is bonded to the top of the UV blocking film layer, polypropylene (Polypropylene) is located on the inside and polyethylene (Polyethylene) is formed to be located on the outside; consisting of; consisting of, the non-woven layer, the polypropylene (Polypropylene) and The weight ratio of polyethylene (Polyethylene) is 1:1, and the polypropylene and polyethylene are manufactured by a thermal calendar that is continuously rolled from a heat roll to a constant thickness. It is formed, and the UV-blocking film layer provides a pollution prevention tape for coating protection, characterized in that it uses the same polyethylene (Polyethylene) material as the outside of the nonwoven layer to facilitate bonding with the nonwoven layer.

Description

도장 보호용 오염 방지테이프{Pollution prevention tape for paint protection}Pollution prevention tape for paint protection

본 발명은 도장 보호용 오염 방지테이프에 관한 것으로, 도장 작업 시 사용되는 마스킹 테이프로 도장을 흡착하고, 자외선을 차단하여 도장 작업 효율을 높일 수 있는 도장 보호용 오염 방지테이프에 관한 것이다.The present invention relates to an anti-contamination tape for protecting the coating, and relates to an anti-contamination tape for protecting the coating that can adsorb the coating with a masking tape used in the coating operation and block ultraviolet rays to increase the efficiency of the coating operation.

도장 보호용 오염 방지테이프는 통상 마스킹 테이프(masking tape)로 지칭되며, 도장 작업시 도장이 필요없는 부분에 부착하여 도장으로부터 보호하는데 사용하는 테이프이다.The anti-contamination tape for coating protection is commonly referred to as a masking tape, and is a tape used to protect the coating by attaching it to a portion that does not require coating during painting.

종래의 기술로 등록실용신안 20-0437378호의 "마스킹 테이프"로 개시된 바가 아있다. 종래에는 필름과, 필름에 부직포가 열융착에 의해 일체화되도록 한 것이다.It is known that the conventional technique disclosed as "masking tape" of Utility Model Registration No. 20-0437378. Conventionally, the film and the nonwoven fabric are integrated into the film by heat fusion.

그러나, 종래에는 비닐화 합성수지 필름을 사용하므로 자외선에 의한 물질 변화에 의해 잔여물이 피착물에 전이되는 문제점이 있어왔다.However, conventionally, since a vinylated synthetic resin film is used, there has been a problem in that residues are transferred to adherends due to material changes due to ultraviolet rays.

종래에는 부직포와 필름의 성분이 달라 열융착으로 일체화하기 어려운 점이 있으며 접착력이 좋지 않아 도장 작업시 박리되는 문제점이 있어왔다.Conventionally, since the components of the nonwoven fabric and the film are different, it is difficult to integrate them by heat fusion, and there has been a problem that peeling occurs during painting because of poor adhesion.

또한, 점착제가 부직포에 전이되어 부직포에 보프라기가 생기는 문제점도 있어왔다.In addition, there has been a problem that the adhesive is transferred to the non-woven fabric, and the lint is formed on the non-woven fabric.

KRKR 20-043737820-0437378 Y1Y1

본 발명은 상기의 문제를 해결하기 위한 것으로, 자외선을 차단하여 도장용 표면에 변질이 없으며, 부직포에 의해 자외선 차단하는 필름을 보호할 수 있으며, 도장 작업 및 뒤처리를 수월하게 할 수 있는 도장 보호용 오염 방지테이프를 제공하고자 한다.The present invention is to solve the above problems, there is no deterioration on the surface for painting by blocking ultraviolet rays, can protect the film to block ultraviolet rays by a non-woven fabric, pollution for painting protection that can facilitate the painting operation and post-treatment It is intended to provide a prevention tape.

상기의 과제를 해결하기 위해 본 발명은 점착제층; 검정색의 제외한 색상으로 형성되어 자외선을 차단되게 하는 제1필름과, 상기 제1필름의 하부에 상기 점착제층과 접합되고 검정색으로 형성되어 온도를 유지되게 하는 제2필름으로 구성되는 자외선차단필름층; 상기 자외선차단필름층 상부에 접합되는 것으로, 폴리프로필렌(Polypropylene)이 내측에 위치하고 폴리에틸렌(Polyethylene)을 외측에 위치되게 형성되는 부직포층;으로 구성되되, 상기 부직포층은, 상기 폴리프로필렌(Polypropylene)과 폴리에틸렌(Polyethylene)의 중량비를 1:1로 되게 하고, 상기 폴리프로필렌(Polypropylene)과 폴리에틸렌(Polyethylene)을 열롤에서 일정한 두께로 연속 압연하는 열 카렌다에 의해 제조되되, 폭 방향으로 찢어짐이 쉽도록 줄무늬가 형성되며, 상기 자외선차단필름층은, 상기 부직포층과의 접합을 용이하도록 하기 위하여 상기 부직포층의 외측과 동일한 폴리에틸렌(Polyethylene) 재질을 사용하는 것을 특징으로 하는 도장 보호용 오염방지테이프를 제공한다.The present invention to solve the above problems is an adhesive layer; An ultraviolet blocking film layer composed of a first film formed of a color except for black to block ultraviolet rays and a second film bonded to the adhesive layer under the first film and formed in black to maintain temperature; It is bonded to the top of the UV blocking film layer, polypropylene (Polypropylene) is located on the inside and polyethylene (Polyethylene) is formed to be located on the outside; consisting of; consisting of, the non-woven layer, the polypropylene (Polypropylene) and The weight ratio of polyethylene (Polyethylene) is 1:1, and the polypropylene and polyethylene are manufactured by a thermal calendar that continuously rolls from a heat roll to a constant thickness, and stripes are formed to be easily torn in the width direction. It is formed, and the UV-blocking film layer provides a pollution prevention tape for coating protection, characterized in that it uses the same polyethylene (Polyethylene) material as the outside of the nonwoven layer to facilitate bonding with the nonwoven layer.

삭제delete

삭제delete

삭제delete

삭제delete

삭제delete

본 과제의 해결 수단에 제공된 구성에 의하면, 부직포를 사용함으로써 도장을 흡착하여 테이프 제거시 도장 흡착한 면이 깨지지 않아 뒤처리가 깔끔하며, 자외선차단필름을 추가함으로써 야외에서 햇빛으로 인한 물질 변화가 적어 장시간 사용하더라도 잔여물이 피착물에 전이되지 않는다.According to the configuration provided in the solution of the present invention, the non-woven fabric is used to adsorb the coating so that when the tape is removed, the surface adsorbed is not broken, and the post-treatment is clean. Even when used, the residue does not transfer to the adherend.

도 1은 본원발명의 실시예에 따른 도장 보호용 오염방지테이프의 단면도이다.
도 2는 본원발명의 실시예에 따른 도장 보호용 오염방지테이프 제조방법의 실시예이다.1 is a cross-sectional view of a pollution prevention tape for protecting a coating according to an embodiment of the present invention.
Figure 2 is an embodiment of a method for manufacturing a pollution prevention tape for protecting a coating according to an embodiment of the present invention.

이하에서는 본 발명의 실시예를 첨부한 도면을 참조하여 설명하고자 한다. 하기 설명 및 첨부 도면에 나타난 바는 본 발명의 전반적인 이해를 위해 제시된 것이므로 본 발명의 기술적 범위가 그것들에 한정되는 것은 아니다 그리고 본 발명의 요지를 불필요하게 흐릴 수 있는 공지 구성 및 기능에 대한 상세한 설명은 생략하기로 한다.Hereinafter, embodiments of the present invention will be described with reference to the accompanying drawings. Since the following description and the accompanying drawings are presented for an overall understanding of the present invention, the technical scope of the present invention is not limited to them, and detailed descriptions of well-known configurations and functions that may unnecessarily obscure the subject matter of the present invention are provided. It will be omitted.

도 1은 본원발명의 실시예에 따른 도장 보호용 오염방지테이프의 단면도이다.1 is a cross-sectional view of a pollution prevention tape for protecting a coating according to an embodiment of the present invention.

도 1을 참조하면, 본 발명인 도장 보호용 오염방지테이프는 크게 점착제층(100), 자외선차단필름층(200), 부직포층(300)을 포함하여 이루어진다.Referring to Figure 1, the present inventor's paint protection pollution prevention tape is largely made of the pressure-sensitive adhesive layer 100, a UV blocking film layer 200, a non-woven fabric layer 300.

상기 점착제층(100)은 도장면에 점착할 수 있는 층이다.The pressure-sensitive adhesive layer 100 is a layer that can adhere to the painted surface.

상기 자외선차단필름층(200)은 상기 점착제층(100) 상부에 형성된 것으로, 자외선을 차단하여 도장용 표면의 변질을 방지하기 위한 층이다.The UV blocking film layer 200 is formed on the pressure-sensitive adhesive layer 100, and is a layer for blocking ultraviolet rays to prevent deterioration of the surface for painting.

상기 자외선차단필름층(200)은 2개의 필름층으로 구성하는데, 검정색을 제외한 색상으로 형성하여 자외선을 차단되게 하고 온도를 유지할 수 있는 제1필름(220)과, 상기 제1필름(220)의 하부에 상기 점착제층(100)과 접합되고 검정색으로 형성되어 자외선을 차단하면서도 온도유지를 통한 도장용 표면의 변질을 방지되게 하는 제2필름(240)으로 구성된다.The UV blocking film layer 200 is composed of two film layers, formed of a color other than black to block ultraviolet rays and maintain temperature, of the first film 220 and the first film 220. It is composed of a second film 240 that is bonded to the pressure-sensitive adhesive layer 100 at the bottom and is formed in black to block ultraviolet rays while preventing deterioration of the surface for painting through temperature maintenance.

상기 부직포층(300)은 상기 자외선차단필름층(200) 상부에 접합되는 것으로, 도료를 흡수할 수 있는 것으로, 폴리프로필렌(PP:Polypropylene)이 내측에 위치하고 폴리에틸렌(PE:Polyethylene)을 외측에 위치되도록 형성된 층이다.The non-woven fabric layer 300 is bonded to the upper portion of the UV blocking film layer 200, and can absorb paint. Polypropylene (PP) is located inside and polyethylene (PE:Polyethylene) is located outside. It is a layer formed as much as possible.

도 2는 본원발명의 실시예에 따른 도장 보호용 오염방지테이프 제조방법의 실시예이다.Figure 2 is an embodiment of a method for manufacturing a pollution prevention tape for protecting a coating according to an embodiment of the present invention.

도 2를 참조하면, 도장 보호용 오염방지테이프 제조방법은 앞서 상술한 도장 보호용 오염방지테이프의 구성인 점착제층(100), 자외선차단필름층(200), 부직포층(300)을 제조하고 상호 일체화하기 위한 것에 특징이 있다.Referring to FIG. 2, the method for manufacturing the anti-contamination tape for coating protection is prepared by integrating the adhesive layer 100, the UV-blocking film layer 200, and the non-woven fabric layer 300, which are the components of the anti-contamination tape for coating protection, as described above There are features for.

먼저, 점착제층(100)은 무기용제 접착제 또는 유기용제 접착제 다 가능하며, 예시로 리무발 아크릴 테이프를 사용한다. 리무발 아크릴 테이프는 도장면에 테이핑 후 제거시 도장면 표면에 점착제 잔여물이 없는 이점이 있다.First, the pressure-sensitive adhesive layer 100 may be an inorganic solvent adhesive or an organic solvent adhesive, and a limu acrylic tape is used as an example. Limubal acrylic tape has the advantage that there is no adhesive residue on the surface of the painted surface when removed after taping on the painted surface.

그리고, 자외선차단필름층(200)은 상기 부직포층(300)에 접합되고 검은색을 제외하고 색상을 띄며 자외선을 차단되게 하는 제1필름(220)과, 상기 제1필름(220)의 하부에 상기 점착제층(100)과 접합되고 검정색으로 형성되어 자외선을 차단하면서도 온도를 유지되게 하는 제2필름(240)을 일체가 되게 제조한다.In addition, the UV blocking film layer 200 is bonded to the nonwoven fabric layer 300 and has a color except black and blocks the ultraviolet rays. The first film 220 and the lower portion of the first film 220 The second film 240, which is bonded to the pressure-sensitive adhesive layer 100 and formed in black to block ultraviolet rays and maintain the temperature, is integrally manufactured.

상기 제1필름(220)은 부직포층(300)에 투영되므로 외부에서 색상으로 식별 가능다. 색상별로 적용하여 도장 섹터별 구분을 가능하게 하는 용도로 사용할 수 있다. 또한 상기 제1필름(220)은 백색 또는 하늘색을 사용할 수 있으며, 검정색 제외한 색상은 어떠한 것도 적용 가능하다.Since the first film 220 is projected onto the nonwoven layer 300, it can be identified by color from the outside. It can be used for the purpose of enabling classification by coating sector by applying by color. Also, the first film 220 may use white or light blue, and any color except black may be applied.

여기서, 자외선차단필름층(200)은 폴리에틸렌(Polyethylene) 재질을 사용하여 상기 부직포층(300)의 외측 성분과 동일하게 하며 상호 접착이 쉽도록 하는 것이 바람직하다.Here, the UV blocking film layer 200 is preferably the same as the outer component of the nonwoven fabric layer 300 by using a polyethylene material, so that it is easy to mutually adhere.

상기 부직포층(300)은 폴리프로필렌(Polypropylene)을 내측에 위치하고 폴리에틸렌(Polyethylene)을 외측에 위치되게 제조한다. The nonwoven layer 300 is manufactured such that polypropylene is located inside and polyethylene is located outside.

상기 부직포층(300)은 테이프로 사용하는 것을 고려할 때 폭 방향(CD)으로 줄무늬를 형성하여 폭 방향으로 찢어짐이 쉽도록 제작하는 것이 바람직하다.When considering the use of the nonwoven fabric layer 300 as a tape, it is preferable to form a stripe in the width direction (CD) so that it is easy to tear in the width direction.

상기 부직포층(300)의 내측에 폴리프로필렌(Polypropylene)은 폴리에틸렌분자 사슬의 탄소에 하나씩 걸러 메틸기(CH3)가 붙은 것이며, 규칙적으로 짧은 가지가 달린 형태를 하고 있으며 폴리에틸렌(Polyethylene) 보다 상대적으로 경질이므로 강도를 높일 수 있다. 그리고, 외측에 폴리에틸렌(Polyethylene)은 착색이 잘되며 상기 자외선차단필름층(520)과 같은 재질에 의해 접착을 쉽게 할 수 있는 이점이 있다.Polypropylene inside the non-woven fabric layer 300 is one by which methyl groups (CH3) are attached to the carbon of the polyethylene molecule chain one by one, and it has a regular shape with short branches and is relatively harder than polyethylene. Strength can be increased. In addition, polyethylene on the outside is well colored and has the advantage of being easily adhered by a material such as the UV blocking film layer 520.

여기서 상기 폴리프로필렌(Polypropylene)과 폴리에틸렌(Polyethylene)은 중량비를 1:1로 되게 하고, 상기 폴리프로필렌(Polypropylene)과 상기 폴리에틸렌(Polyethylene)을 열롤에서 일정한 두께로 연속 압연하는 열 카렌다에 의해 상기 부직포층(300)이 제조되는 것을 특징으로 한다. 상기 부직포층(300)은 열카렌다에 의해 누름작업이 진행되어 차후 상기 점착제층(100)의 점착성분을 흡수하는 것을 방지할 수 있고, 부직포층(300)의 자체에 보프라기가 발생하는 것을 방지할 수 있다. Here, the polypropylene (Polypropylene) and polyethylene (Polyethylene) to a weight ratio of 1:1, the polypropylene (Polypropylene) and the polyethylene (Polyethylene) by a heat calendar continuously rolling in a constant thickness in a heat roll the non-woven fabric layer It is characterized in that the 300 is produced. The non-woven fabric layer 300 can be prevented from absorbing the adhesive component of the pressure-sensitive adhesive layer 100 after the pressing operation is progressed by a thermal calendar, and preventing the generation of lint-free fabric itself from the non-woven fabric layer 300 can do.

한편, 자외선차단필름층(200)을 기준으로 일면에는 부직포층(300)을 부착하고, 상기 자외선차단필름층(200)의 타면에는 점착제층(100)을 부착하는 것에서 특징이 있으며, 여기서 점착제층(100)은 접합하는 기술은 공지의 기술로 상세한 설명은 생략하며, 특히 자외선차단필름층(200)과 부직포층(300)을 접합에 대해 설명하면 다음과 같다.Meanwhile, the non-woven fabric layer 300 is attached to one surface based on the UV-blocking film layer 200, and the adhesive layer 100 is attached to the other surface of the UV-blocking film layer 200. (100) is a technique known for bonding, and a detailed description thereof is omitted. In particular, the description will be given as to the bonding of the UV blocking film layer 200 and the nonwoven fabric layer 300.

상기 부직포층(300)과 상기 자외선차단필름층(200) 사이에는 폴리에틸렌(Polyethylene)의 열융착에 의해 상기 자외선차단필름층(200)과 상기 부직포층(300)을 접합한다. 접합방법은 상기 자외선차단필름층(200)과 상기 부직포층(300) 사이에 열융착되게 하는 상기 폴리에틸렌(Polyethylene)을 T-다이(die)에 의해 공급되도록 하여 동일 성분으로 하여 접착을 용이하게 한다.The UV blocking film layer 200 and the nonwoven fabric layer 300 are bonded between the nonwoven fabric layer 300 and the UV blocking film layer 200 by heat fusion of polyethylene. The bonding method allows the polyethylene to be heat-sealed between the UV-blocking film layer 200 and the nonwoven fabric layer 300 by T-die so that it is easily bonded with the same component. .

따라서, 이상과 같이 제조된 도장 보호용 오염 방지테이프는 부직포층(100)이 폴리프로필렌(Polypropylene)과 폴리에틸렌(Polyethylene)으로 구성되어 강도를 가지면서 자외선차단필름층(200)과 부착이 용이하고, 자외선차단필름층(200)에 의해 도장용 표면의 변질을 방지할 수 있다.Therefore, the anti-fouling tape for coating protection manufactured as described above is made of polypropylene and polyethylene, and thus has strength, and is easily attached to the UV blocking film layer 200, and ultraviolet light. The blocking film layer 200 can prevent the deterioration of the surface for painting.

또한, 도장 작업 시 부직포층(100)이 최외측에 있어 도료를 흡수하면서 도료로부터 자외선차단필름층(200)을 보호하여 변형 또는 깨짐을 방지할 수 있으며 차후 뒤처리가 깔끔하다.In addition, during the painting operation, the nonwoven fabric layer 100 is on the outermost side and absorbs the paint while protecting the UV blocking film layer 200 from the paint to prevent deformation or cracking, and subsequent post-treatment is neat.

이상에서 설명한 본 발명은 상기한 실시예에 한정되지 않고, 이하의 특허청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 누구든지 다양하게 변경하여 실시할 수 있는 범위까지 특허청구범위의 보호범위에 속하는 것으로 보아야 할 것이다.The present invention described above is not limited to the above-described embodiments, and can be variously changed by anyone having ordinary knowledge in the technical field to which the present invention pertains without departing from the gist of the present invention claimed in the claims below. It should be regarded as belonging to the protection scope of the claims to the extent possible.

100: 점착제층
200: 자외선차단필름층
220: 제1필름
240: 제2필름
300: 부직포층100: adhesive layer
200: UV blocking film layer
220: 1st film
240: second film
300: non-woven fabric layer

Claims (6)

삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 점착제층;
검정색을 제외한 색상으로 형성되어 자외선을 차단되게 하는 제1필름과, 상기 제1필름의 하부에 상기 점착제층과 접합되고 검정색으로 형성되어 온도를 유지되게 하는 제2필름으로 구성되는 자외선차단필름층;
상기 자외선차단필름층 상부에 접합되는 것으로, 폴리프로필렌(Polypropylene)이 내측에 위치하고 폴리에틸렌(Polyethylene)을 외측에 위치되게 형성되는 부직포층;으로 구성되되,
상기 부직포층은,
상기 폴리프로필렌(Polypropylene)과 폴리에틸렌(Polyethylene)의 중량비를 1:1로 되게 하고, 상기 폴리프로필렌(Polypropylene)과 폴리에틸렌(Polyethylene)을 열롤에서 일정한 두께로 연속 압연하는 열 카렌다에 의해 제조되되, 폭 방향으로 찢어짐이 쉽도록 줄무늬가 형성되며,
상기 자외선차단필름층은,
상기 부직포층과의 접합을 용이하도록 하기 위하여 상기 부직포층의 외측과 동일한 폴리에틸렌(Polyethylene) 재질을 사용하는 것을 특징으로 하는 도장 보호용 오염방지테이프.Adhesive layer;
A UV blocking film layer composed of a first film formed in a color other than black to block UV rays, and a second film bonded to the adhesive layer under the first film and formed in black to maintain temperature;
It is to be bonded to the upper portion of the UV blocking film layer, polypropylene (Polypropylene) is located on the inside and polyethylene (Polyethylene) is formed to be located on the outside; consisting of;
The nonwoven layer,
The weight ratio of the polypropylene (Polypropylene) and polyethylene (Polyethylene) is 1:1, and the polypropylene (Polypropylene) and polyethylene (Polyethylene) are manufactured by a thermal calendar that is continuously rolled with a constant thickness in a heat roll, in the width direction. Stripes are formed to facilitate tearing,
The UV blocking film layer,
In order to facilitate the bonding with the nonwoven fabric layer, a pollution prevention tape for coating protection, characterized in that the same material as the outside of the nonwoven fabric layer is used.
KR1020180109429A 2018-09-13 2018-09-13 Pollution prevention tape for paint protection KR102121727B1 (en)