KR102111036B1 - Mufacturing method of sand type deodorant for companion animal toilet - Google Patents
Mufacturing method of sand type deodorant for companion animal toilet Download PDFInfo
- Publication number
- KR102111036B1 KR102111036B1 KR1020180083216A KR20180083216A KR102111036B1 KR 102111036 B1 KR102111036 B1 KR 102111036B1 KR 1020180083216 A KR1020180083216 A KR 1020180083216A KR 20180083216 A KR20180083216 A KR 20180083216A KR 102111036 B1 KR102111036 B1 KR 102111036B1
- Authority
- KR
- South Korea
- Prior art keywords
- sand
- toilet
- type deodorant
- minutes
- companion animal
- Prior art date
Abstract
본 발명은 개, 고양이 등과 같은 반려동물의 화장실에 사용되는 과정에서 반려동물의 배변 또는 배뇨에 따른 악취를 감소시키고, 화장실 변기에 버려도 막힘 현상이 발생되지 않도록 창안된 반려동물 화장실용 모래형 탈취제 제조방법 및 이로부터 제조된 모래형 탈취제에 관한 것이다.
본 발명에 따른 반려동물 화장실용 모래형 탈취제 제조방법은, a) 모래형 탈취제 제조를 위한 재료로서, 주재료와 보조 재료를 각각 준비하는 단계; b) 준비된 주재료와 보조 재료를 믹서기에서 3~7분 동안 혼합시켜서 주재료가 보조 재료에 고르게 베도록 하는 단계; c) b)단계에서 얻어진 혼합물을 5~15분 동안 치대면서 반죽하는 단계; d) c)단계에서 얻어진 반죽물을 성형기(롤러)를 통해 일정 크기로 성형가공하는 단계; e) 성형 가공물을 코팅기(표면처리기)에 넣어서 5~15분 동안 회전시키면서 표면을 처리하는 단계; f) e)단계에서 얻어진 성형가공물을 25~45℃ 에서 2~4시간 1차 건조시키는 단계; g) f)단계에서 얻어진 1차 건조물을 65~75℃ 에서 3~5시간 2차 건조시키는 단계; h) g)단계에서 얻어진 2차 건조를 거친 모래에 향료와 보존재 혼합액을 도포시키는 단계로 이루어진다.The present invention reduces the odor caused by defecation or urination of a companion animal in the process of being used in the toilet of a companion animal such as a dog, a cat, etc., and manufactures a sand type deodorant for a companion animal toilet created to prevent clogging even when discarded in the toilet. Method and sand-type deodorant prepared therefrom.
A method for manufacturing a sand type deodorant for a companion toilet for a companion animal according to the present invention comprises: a) preparing a sand type deodorant as a material for preparing a main material and an auxiliary material, respectively; b) mixing the prepared main material and auxiliary material in a blender for 3 to 7 minutes so that the main material is evenly cut into the auxiliary material; c) kneading the mixture obtained in step b) while stirring for 5-15 minutes; d) forming the dough obtained in step c) to a predetermined size through a molding machine (roller); e) processing the surface while rotating the molded object in a coating machine (surface treatment machine) for 5 to 15 minutes; f) first drying the molded product obtained in step e) at 25 to 45 ° C for 2 to 4 hours; g) a second drying step of the primary dried product obtained in step f) at 65 to 75 ° C for 3 to 5 hours; h) g) consists of applying a mixture of flavoring and preservatives to the sand that has undergone secondary drying obtained in step g).
Description
본 발명은 반려동물 화장실용 모래형 탈취제 제조방법에 관한 것으로, 특히 개, 고양이 등과 같은 반려동물의 화장실에 사용되는 과정에서 반려동물의 배변 또는 배뇨에 따른 악취를 감소시키고, 화장실 변기에 버려도 막힘 현상이 발생되지 않도록 창안된 반려동물 화장실용 모래형 탈취제 제조방법 및 이로부터 제조된 모래형 탈취제에 관한 것이다.
The present invention relates to a method for manufacturing a sand type deodorant for a companion animal restroom, in particular, in the process of being used in a companion animal restroom such as a dog, cat, etc., it reduces the odor due to defecation or urination of the companion animal and is clogged even when discarded in the toilet seat. It relates to a method for producing a sand-type deodorant for a pet toilet created to prevent this from occurring and a sand-type deodorant prepared therefrom.
일반적으로 반려동물이란 개, 고양이 등과 같은 동물을 일컫는데, 최근 들어 개나 고양이 등에 한정되지 않고 다양한 종류의 반려동물을 기르는 가정이 늘어나고 있다. In general, a companion animal refers to an animal such as a dog or a cat, but recently, households raising various types of companion animals are not limited to dogs and cats.
이러한 반려동물을 기르는 가정은 단순히 가축으로서 사육하는 종래의 입장과 달리 가족의 일원으로서 대하기 때문에 반려동물에 대한 의식주에 대하여 많은 관심과 신경을 쓰고, 나아가 여가생활 등을 함께 공유하고자 하는 욕구가 있다.Families raising these pets are treated as members of the family, unlike the conventional position of simply raising them as livestock, so there is a desire to pay much attention and attention to the consciousness of pets, and to share leisure life, etc. .
한편, 반려동물을 실내에서 키울 때 발생하는 여러 가지 문제점 중 배변과 관련된 문제점이 있는데, 배변 또는 배뇨 등과 같은 배설물을 반려동물이 지정된 장소에서 처리하게끔 훈련시키는 것이 쉽지 않은 일이고, 지정된 장소에서 처리한다고 하더라도 배변 또는 배뇨 냄새를 최소화하기 위해 수시로 청소해야 하기 때문에 매우 번거롭고 불편한 문제점이 있다.On the other hand, there are problems related to bowel movement among various problems that occur when raising a pet indoors, and it is not easy to train a pet to treat feces such as defecation or urination in a designated place, and it is handled in a designated place. Even if it has to be cleaned from time to time to minimize the smell of defecation or urination, there is a very cumbersome and uncomfortable problem.
실내에서 사육되는 고양이나 개 등의 동물의 화장실로서, 플라스틱제의 상자형의 용기에 '동물용 화장실 모래' 또는 '고양이 모래'등으로 불리우는 입상물이 부설된 것이 사용되고 있다. As a toilet for animals such as cats and dogs that are kept indoors, a plastic box-shaped container is used in which a granular material called 'animal toilet sand' or 'cat sand' is used.
동물이 배설한 뇨 등의 배설물은 이러한 변기 모래에 의해서 흡수된다. 기르는 주인은 이 뇨나 변으로 더러워진 변기 모래를 변 등과 함께 용기로부터 제거하고, 제거한 부분에 상당하는 변기 모래를 새로 보충한다.Feces such as urine excreted by animals are absorbed by the toilet sand. The owner of the cultivation removes the toilet sand soiled with diuretic or stool from the container along with the stool, and replenishes the toilet sand corresponding to the removed part.
통상, 이러한 동물용 화장실 모래 또는 '고양이 모래'로서는 액체를 흡수할 수 있는 벤토나이트나 종이, 또는 탈취력을 구비한 제올라이트 등을 직경이 수㎜ ∼수 ㎝ 정도의 대략 구형으로 성형된 것이 사용되고 있다.Typically, such animal toilet sand or 'cat sand' is formed by forming bentonite or paper capable of absorbing liquid, or zeolites having deodorizing power into approximately spherical diameters of several millimeters to several centimeters in diameter.
이것에 관해서, 최근 화장실 모래로서 동물의 배설물의 흡수력 및 탈취력이 우수한 소재인 실리카겔을 성형한 것이 제안되어 있다. 그러나, 이와 같은 화장실 모래는 동물의 뇨를 신속히 흡수하는 것을 목적으로 하여 직경이 2㎜∼6㎜ 정도의 소(小)구형으로 성형되어 있기 때문에, 플라스틱제 용기 밖으로 비산되기 쉬우며, 또한 굴러가기 쉽다. 이 때문에 동물의 발바닥에 부착되거나 하여 용기 밖으로 나온 화장실 모래는 광범위하게 확산되기 쉽다.In connection with this, recently, it has been proposed to mold silica gel, which is an excellent material for absorbing and deodorizing animal feces as toilet sand. However, since such toilet sand is molded into a small spherical shape having a diameter of about 2 mm to 6 mm for the purpose of rapidly absorbing urine from animals, it is easy to scatter out of a plastic container, and also rolls. easy. For this reason, toilet sand that is attached to the soles of animals or comes out of the container is likely to spread widely.
더욱이, 고양이 등은 배설후에 변기 모래를 발로 뒤섞는 습성이 있어, 다수의 변기 모래에서 뇨나 변 등이 발에 부착되는 경우가 있다. 더구나, 더러워진 변기 모래가 분산되기 때문에 더러워진 부분만을 완전히 제거하는 것은 곤란하다.Moreover, cats and the like have a habit of mixing toilet sand with their feet after excretion, so urine or stools may adhere to the feet in a large number of toilet sands. Moreover, it is difficult to completely remove only the soiled portion because the soil of the dirty toilet bowl is dispersed.
한편, 제올라이트나 강의 모래 등은 뇨를 흡수하는 것이 아니고, 또한 벤토나이트나 펄프 등은 흡수력이 떨어질뿐만 아니라 탈취력도 없다. 더구나, 동물, 특히 고양이의 배설물은 악취가 심하여, 변기를 설치해 두는 방전체나 일반 쓰레기통에 버릴 경우 냄새가 나게 되고, 그 결과 불쾌감을 일으킨다.On the other hand, zeolite and sand of rivers do not absorb urine, and bentonite and pulp, etc., have not only poor absorption but also no deodorizing power. Moreover, the feces of animals, especially cats, have a bad odor, and when they are thrown into a discharging body or a regular trash box where a toilet is installed, it smells, resulting in an unpleasant feeling.
또한, 수분의 흡수가 여의치 않으며, 물에 잘 풀어지지 않으므로 변기에 버리기도 어려운 실정이다. 이에 따라 화장실 변기에 버려도 막힘 현상이 발생되지 않는 반려동물 화장실용 모래형 탈취제의 개발이 시급히 요구되고 있는 실정이다.
In addition, the absorption of water is not easy, and it is difficult to throw it into the toilet because it does not easily dissolve in water. Accordingly, there is an urgent need to develop a sand-type deodorant for a companion animal restroom that does not cause clogging even when discarded in the toilet.
본 발명은 상기한 종래 기술의 문제점을 감안하여 안출된 것으로서, 본 발명의 목적은 반려동물의 배변 또는 배뇨에 따른 악취를 크게 감소시키는 것이 가능한 반려동물 화장실용 모래형 탈취제 제조방법을 제공하는 데 있다.The present invention has been devised in view of the above-mentioned problems of the prior art, and an object of the present invention is to provide a method for manufacturing a sand type deodorant for a companion animal toilet capable of greatly reducing odor caused by defecation or urination of a companion animal. .
본 발명의 다른 목적은 화장실 변기에 그대로 버리는 것이 가능하고, 변기에 버려도 막힘 현상이 발생되지 않는 반려동물 화장실용 모래형 탈취제 제조방법을 제공하는 데 있다.Another object of the present invention is to provide a method for manufacturing a sand type deodorant for a companion animal toilet that can be discarded as it is in the toilet and does not cause clogging even when discarded in the toilet.
본 발명의 또 다른 목적은 플라스틱제 용기 밖으로 잘 비산되지 않고, 사용과정에서 쉽게 굴러가지 않는 반려동물 화장실용 모래형 탈취제 제조방법을 제공하는 데 있다.
Another object of the present invention is to provide a method for manufacturing a sand type deodorant for a pet toilet that is not easily scattered out of a plastic container and does not easily roll in use.
상기한 본 발명의 목적을 달성하기 위해, a) 모래형 탈취제 제조를 위한 재료로서, 주재료와 보조 재료를 각각 준비하는 단계; b) 준비된 주재료와 보조 재료를 믹서기에서 3~7분 동안 혼합시켜서 주재료가 보조 재료에 고르게 베도록 하는 단계; c) b)단계에서 얻어진 혼합물을 5~15분 동안 치대면서 반죽하는 단계; d) c)단계에서 얻어진 반죽물을 성형기를 통해 일정 크기로 성형가공하는 단계; e) 성형 가공물을 코팅기에 넣어서 5~15분 동안 회전시키면서 표면을 처리하는 단계; f) e)단계에서 얻어진 성형가공물을 25~45℃ 에서 2~4시간 1차 건조시키는 단계; g) f)단계에서 얻어진 1차 건조물을 65~75℃ 에서 3~5시간 2차 건조시키는 단계; h) g)단계에서 얻어진 2차 건조를 거친 모래에 향료와 보존재 혼합액을 도포시키는 단계로 이루어지는 반려동물 화장실용 모래형 탈취제 제조방법이 제공된다.In order to achieve the above object of the present invention, a) as a material for the production of sand-type deodorant, preparing a main material and an auxiliary material, respectively; b) mixing the prepared main material and auxiliary material in a blender for 3 to 7 minutes so that the main material is evenly cut into the auxiliary material; c) kneading the mixture obtained in step b) while stirring for 5-15 minutes; d) forming the dough obtained in step c) to a predetermined size through a molding machine; e) processing the surface of the molded product by putting it in a coating machine and rotating it for 5 to 15 minutes; f) first drying the molded product obtained in step e) at 25 to 45 ° C for 2 to 4 hours; g) a second drying step of the primary dried product obtained in step f) at 65 to 75 ° C for 3 to 5 hours; h) A method for manufacturing a sand type deodorant for a pet toilet is provided, which comprises applying a mixture of a perfume and a preservative to the sand that has undergone secondary drying obtained in step g).
본 발명에서 a)단계에서의 주재료는 중량%로, 펄프 파우더(pulp powder) : 70~80%, 칼슘카보네이트(calcium carbonate) : 10~20%, 탄산수소나트륨(Sodium Bicarbonate) : 5~10%를 3~7분 동안 용기(容器)내에서 혼합하고, 보조 재료는 중량%로, 정제수 : 97~99%, 카르복시메틸 셀룰로오스(Carboxymethyl Cellulose) : 0.1~1%, 구아검(Guar Gum): 0.1~1%, 폴리비닐알코올 (Polyvinyl alcohol): 0.1~1%를 용기내에서 혼합한 후에 2~4시간 숙성시킨다.In the present invention, the main material in step a) is weight%, pulp powder: 70-80%, calcium carbonate: 10-20%, sodium bicarbonate: 5-10% Is mixed in a container for 3-7 minutes, the auxiliary material is weight%, purified water: 97-99%, Carboxymethyl Cellulose: 0.1-1%, Guar Gum: 0.1 ~ 1%, Polyvinyl alcohol: 0.1 ~ 1% is mixed in a container and aged for 2 ~ 4 hours.
상기한 바와 같은 본 발명의 반려동물 화장실용 모래형 탈취제 제조방법에 따르면, 다음과 같은 효과가 있다.According to the method for manufacturing a sand-type deodorant for a pet toilet of the present invention as described above, it has the following effects.
첫째, 반려동물의 화장실 내부에 향을 발산시켜서 반려동물의 배변 또는 배뇨에 따른 악취를 크게 감소시킨다.First, the odor caused by the defecation or urination of the companion animal is greatly reduced by emitting incense inside the companion animal's toilet.
둘째, 모래형 탈취제는 펄프(종이) 가공품으로 물에 잘 녹으므로 변이나 오줌이 묻은 모래나 수거된 탈취제는 화장실 변기에 그대로 버리는 것이 가능하며, 변기에 버려도 막힘 현상이 발생되지 않는다.Second, the sand-type deodorant is a pulp (paper) processed product that dissolves well in water, so it is possible to discard the sand or urine-stained sand or collected deodorant as it is in the toilet bowl, and no clogging occurs even when discarded in the toilet.
셋째, 모래형 탈취제가 10~15㎜ 정도의 크기에 비정형(非定型) 형태로 되어있고 일반 고양이 모래 대비 무게가 있어서 플라스틱제 용기 밖으로 잘 비산되지 않고, 사용과정에서 쉽게 굴러가지 않는다.Third, the sand-type deodorant is about 10 ~ 15㎜ in size and has an irregular shape and weighs more than ordinary cat sand, so it is not easily scattered out of the plastic container and does not roll easily during use.
도 1은 본 발명의 일 실시예에 따른 반려동물 화장실용 모래형 탈취제 제조방법의 공정 흐름도.
도 2는 본 발명에 따라 제조된 반려동물 화장실용 모래형 탈취제가 플라스틱제 용기에 담겨진 상태를 나타낸 사진,
도 3은 본 발명에 따라 제조된 반려동물 화장실용 모래형 탈취제가 그릇에 담겨진 상태를 나타낸 사진.1 is a process flow diagram of a method for manufacturing a sand type deodorant for a companion toilet according to an embodiment of the present invention.
Figure 2 is a photograph showing a state in which a sand-type deodorant for a pet toilet made in accordance with the present invention is contained in a plastic container,
3 is a photograph showing a state in which a sand-type deodorant for a companion toilet made in accordance with the present invention is contained in a bowl.
이하, 본 발명의 바람직한 실시예에 따른 반려동물 화장실용 모래형 탈취제 제조방법을 상세히 설명하기로 한다. Hereinafter, a method of manufacturing a sand type deodorant for a companion toilet according to a preferred embodiment of the present invention will be described in detail.
이하에서 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니되며, 발명자는 그 자신의 발명을 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야 할 것이다.The terms or words used in the following should not be interpreted as being limited to ordinary or lexical meanings, and the inventor is based on the principle that the concept of terms can be properly defined to explain his or her invention in the best way. It should be interpreted as meanings and concepts consistent with the technical spirit of the present invention.
도 1은 본 발명의 일 실시예에 따른 반려동물 화장실용 모래형 탈취제 제조방법의 공정 흐름도로서, 이를 참조하면, 우선, 모래형 탈취제 제조를 위한 재료로서, 주재료와 보조 재료를 각각 준비한다(S11).1 is a process flow diagram of a method for manufacturing a sand-type deodorant for a companion toilet according to an embodiment of the present invention. Referring to this, first, as a material for the production of a sand-type deodorant, a main material and an auxiliary material are respectively prepared (S11). ).
주재료는 중량%로, 펄프 파우더(pulp powder) : 70~80%, 칼슘카보네이트(calcium carbonate) : 10~20%, 탄산수소나트륨(Sodium Bicarbonate) : 5~10%를 3~7분, 보다 바람직하게는 5분 정도 용기(容器)내에서 혼합한다. Main material is weight%, pulp powder: 70 ~ 80%, calcium carbonate: 10-20%, sodium bicarbonate: 5-10%, 3-7 minutes, more preferable The mixture is mixed in a container for about 5 minutes.
이때, 펄프 파우더와 칼슘카보네이트, 탄산수소나트륨의 혼합비율을 위와 같이 한정한 것은, 펄프 파우더의 혼합 비율이 70% 미만시, 사용후 수세식 변기에 버릴 시 잘 풀어지지 않고 풀어지는 시간이 오래 소요되기 때문이고, 펄프 파우더의 혼합 비율이 80% 초과시, 표면이 많이 거칠고 포장상태에서 모양이 잘 깨어지는 현상이 일어나기 때문이다.At this time, when the mixing ratio of the pulp powder, calcium carbonate, and sodium hydrogen carbonate is limited as above, when the mixing ratio of the pulp powder is less than 70%, it takes a long time to dissolve and dissolve when discarded in a flush toilet after use. This is because when the mixing ratio of the pulp powder exceeds 80%, the surface is very rough and the shape is broken well in the packaging state.
또한, 칼슘카보네이트의 혼합 비율이 10% 미만시, 포장 보관시 모양 깨어짐 현상이 높아지기 때문이고, 칼슘카보네이트의 혼합 비율이 20% 초과시, 비즈가 너무 단단해져서 물에 풀어지기 힘들어 수세식 변기가 막힐 확률이 높아지기 때문이다.In addition, when the mixing ratio of calcium carbonate is less than 10%, the shape is broken during packaging storage, and when the mixing ratio of calcium carbonate exceeds 20%, the beads are too hard to be released into the water, so there is a possibility that the flush toilet will be blocked. Because it is high.
또한, 탄산수소나트륨의 혼합 비율이 5% 미만시, 냄새 억제 효과가 떨어지기 때문이고, 탄산수소나트륨의 혼합 비율이 10% 초과시 표면에 공극(孔隙)이 늘어나기 때문이다.Also, when the mixing ratio of sodium hydrogen carbonate is less than 5%, the odor suppressing effect is deteriorated, and when the mixing ratio of sodium hydrogen carbonate exceeds 10%, voids on the surface increase.
보조 재료는 중량%로, 정제수 : 97~99%, 카르복시메틸 셀룰로오스(Carboxymethyl Cellulose) : 0.1~1%, 구아검(Guar Gum): 0.1~1%, 폴리비닐알코올 (Polyvinyl alcohol): 0.1~1%를 용기내에서 혼합한 후에 2~4시간, 보다 바람직하게는 3시간 숙성시킨다.Auxiliary material by weight, purified water: 97-99%, Carboxymethyl Cellulose: 0.1-1%, Guar Gum: 0.1-1%, Polyvinyl alcohol: 0.1-1 After mixing% in a container, it is aged 2-4 hours, more preferably 3 hours.
이후, 주재료와 보조 재료를 서로 동일한 비율로 믹서기에서 3~7분, 보다 바람직하게는 5분 정도 혼합시켜서 주재료가 보조 재료에 고르게 베도록 한다(S12).Thereafter, the main material and the auxiliary material are mixed in the same proportion in the blender for 3 to 7 minutes, more preferably for about 5 minutes, so that the main material is evenly cut into the auxiliary material (S12).
이후, 혼합물을 5~15분, 보다 바람직하게는 10분 정도 밀가루 반죽처럼 치대면서 반죽을 한다(S13).Thereafter, the mixture is kneaded while stirring like a flour dough for 5 to 15 minutes, more preferably 10 minutes (S13).
이후, 반죽물을 성형기(롤러)를 통해 일정 크기로 성형가공한다(S14). 이때, 탈취제는 약 10~15㎜, 모래는 약 5~10㎜ 크기가 적당하다.Thereafter, the dough is molded into a predetermined size through a molding machine (roller) (S14). At this time, the deodorant is about 10 ~ 15㎜, sand is about 5 ~ 10㎜ size is suitable.
이후, 성형 가공물을 코팅기(표면처리기)에 넣어서 5~15분, 보다 바람직하게는 10분 동안 회전시키면서 표면을 매끄럽게 처리하고 모양을 탄탄하게 가공한다(S15).Thereafter, the molded object is put into a coating machine (surface treatment machine), and the surface is smoothly processed and the shape is firmly processed while rotating for 5 to 15 minutes, more preferably 10 minutes (S15).
이후, 성형가공물을 25~45℃, 보다 바람직하게는 35℃에서 2~4시간, 보다 바람직하게는 3시간 동안 1차 건조시키며(S16), 이는 가공물의 색상이나 형상의 변형을 줄이고, 매끈한 표면을 유지하기 위함이다.Thereafter, the molded article is first dried at 25 to 45 ° C, more preferably at 35 ° C for 2 to 4 hours, and more preferably at 3 hours (S16), which reduces the deformation of the color or shape of the workpiece and provides a smooth surface. It is to maintain.
이후, 1차 건조물을 65~75℃, 보다 바람직하게는 70℃의 고온에서 3~5시간, 보다 바람직하게는 4시간 동안 2차 건조시키며(S17), 이는 수분 함유율을 5% 이하로 낮추어 세균의 번식을 줄이고, 고온 살균처리에 의해 곰팡이와 세균의 증식을 줄이기 위함이다.Subsequently, the primary dried product is dried at a high temperature of 65 to 75 ° C., more preferably at 70 ° C. for 3 to 5 hours, and more preferably at 4 ° C. for 2 hours (S17), which lowers the moisture content to 5% or less. This is to reduce the propagation and reduce the growth of mold and bacteria by high temperature sterilization.
위와 같은 과정을 거쳐서 전술한 회색 색상의 '고양이 모래'가 얻어지고, 이러한 '고양이 모래'는 별도로 보관하다가 포장 및 출고가 가능하며, 본 발명에서는 2차 건조를 거친 모래에 향료와 보존재 혼합액을 도포시켜서(S18), 도 2 및 도 3에 도시된 바와 같은 모래형 탈취제를 얻었으며, 이와 같이 얻어진 모래형 탈취제를 포장 및 출고한다.Through the above process, the above-mentioned 'cat sand' of gray color is obtained, and these 'cat sands' can be stored and packaged separately, and in the present invention, a mixture of spices and preservatives is added to sand that has undergone secondary drying. By applying (S18), a sand type deodorant as shown in FIGS. 2 and 3 was obtained, and the sand type deodorant thus obtained is packaged and shipped.
이때, 변질을 막기 위한 보존제 혼합액으로서 물 100중량부에 에탄올 : 3~7중량부, 1,2헥산다이올(1,2-Hexanediol) : 0.1~1중량부, 향료 증발을 억제해주고 2차 건조물 안쪽까지 향료와 보존제를 퍼지해주는 습윤제 역할을 하는 디프로필렌 글라이콜(Dipropylene Glycol) : 3~5중량부를 혼합하여 사용하며, 이러한 보존제 혼합액을 상기 에탄올의 비율(3~7중량부)와 같은 향료(perfume)와 함께 사용한다.At this time, as a preservative mixture to prevent deterioration, 100 parts by weight of water, ethanol: 3 to 7 parts by weight, 1,2-hexane diol (1,2-Hexanediol): 0.1 to 1 parts by weight, suppressing evaporation of the fragrance and secondary drying Dipropylene Glycol, which acts as a wetting agent to purge fragrance and preservatives to the inside: 3 to 5 parts by weight is used by mixing, and these preservative mixtures are fragrances such as the ratio of ethanol (3 to 7 parts by weight) Used with (perfume).
도 3을 참조하면, 본 발명에 따른 '고양이 모래' 또는 모래형 탈취제는 비정형(非定型) 형태를 가지며, 이에 따라 플라스틱제 용기 밖으로 잘 비산되지 않고, 사용 과정에서 쉽게 굴러가지 않게 된다. Referring to FIG. 3, the 'cat sand' or sand-type deodorant according to the present invention has an amorphous shape, and thus does not scatter well outside the plastic container, and does not easily roll in the process of use.
한편, 상기와 같은 과정에서 디프로필렌 글라이콜(Dipropylene Glycol)은, 향료가 모래 탈취제에 고르게 도포된 후 펄프와 칼슘카보네이트로 구성된 모래층이 안쪽까지 고르게 흡수되도록 돕고, 동시에 향이 오래도록 지속 될 수 있도록 잡아 주는 역할을 한다. On the other hand, in the process as described above, dipropylene glycol (Dipropylene Glycol), the fragrance is evenly applied to the sand deodorant, and then help the sand layer composed of pulp and calcium carbonate to be evenly absorbed to the inside, and at the same time hold the fragrance for a long time The Lord plays a role.
또한, 보존제는 위의 향료와 같이 고르게 퍼져서 안쪽까지 스며 들면서 세균과 곰팡이가 증식하는 것을 억제해 준다.
In addition, the preservative spreads evenly like the above flavoring, and prevents the growth of bacteria and fungi while penetrating to the inside.
이하에서는 하기 실시예에 의하여 본 발명을 보다 구체적으로 설명한다.
Hereinafter, the present invention will be described in more detail by the following examples.
(실시예) (Example)
1) 주재료로서 펄프 파우더 : 75 중량%, 칼슘카보네이트 : 20 중량%, 탄산수소나트륨 : 7.5 중량%를 5분 정도 용기내에서 혼합하였다. 또한, 보조 재료로서 정제수 : 98중량%, 카르복시메틸 셀룰로오스 : 0.5 중량%, 구아검(Guar Gum): 0.5 중량%, 폴리비닐알코올 : 0.5 중량%를 용기내에서 혼합한 후에 3시간 숙성시켰다.1) As a main material, pulp powder: 75% by weight, calcium carbonate: 20% by weight, and sodium hydrogen carbonate: 7.5% by weight were mixed in a container for about 5 minutes. In addition, purified water: 98% by weight, carboxymethyl cellulose: 0.5% by weight, Guar Gum: 0.5% by weight, polyvinyl alcohol: 0.5% by weight in a container, and aged for 3 hours.
2) 주재료와 보조 재료를 서로 동일한 비율로 믹서기에서 5분 정도 혼합시켜서 주재료가 보조 재료에 고르게 베도록 하였다.2) The main material and the auxiliary material were mixed at the same ratio in the blender for about 5 minutes so that the main material was evenly cut into the auxiliary material.
3) 혼합물을 10분 정도 밀가루 반죽처럼 치대면서 반죽을 하였다.3) The mixture was kneaded for about 10 minutes while striking like flour.
4) 반죽물을 성형기(롤러)를 통해 약 10㎜ 크기로 성형가공하였다.4) The dough was molded into a size of about 10 mm through a molding machine (roller).
5) 성형 가공물을 코팅기(표면처리기)에 넣어서 10분 동안 회전시키면서 표면을 매끄럽게 처리하고 모양을 탄탄하게 가공하였다.5) The molded product was put into a coating machine (surface treatment machine) and rotated for 10 minutes to smoothly treat the surface and to process the shape firmly.
6) 성형가공물을 35℃에서 3시간 동안 1차 건조시켰다.6) The molded product was first dried at 35 ° C for 3 hours.
7) 1차 건조물을 70℃의 고온에서 4시간 동안 2차 건조시켰다.7) The primary dried product was dried at a high temperature of 70 ° C. for 4 hours.
8) 2차 건조를 거친 보존제 혼합액으로서 에탄올 : 5중량부, 1,2헥산다이올(1,2-Hexanediol) : 0.5중량부, 디프로필렌 글라이콜(Dipropylene Glycol) : 4중량부를 혼합한 후, 이 보존제 혼합액을 5중량부의 향료(perfume)와 함께 도포시켜서, 도 2 및 도 3에 도시된 바와 같은 모래형 탈취제를 얻었다.8) As a preservative mixture that has undergone secondary drying, ethanol: 5 parts by weight, 1,2-hexane diol (1,2-Hexanediol): 0.5 parts by weight, Dipropylene Glycol (Dipropylene Glycol): 4 parts by weight after mixing , This preservative mixture was applied with 5 parts by weight of perfume to obtain a sand type deodorant as shown in FIGS. 2 and 3.
이때, 1차 건조이전에 얻어진 '고양이 모래'는 별도로 보관하다가 약 5㎜ 크기로 가공하여 포장 및 출고가 가능하다.
At this time, the 'cat sand' obtained before the first drying can be stored separately and processed to a size of about 5 mm for packaging and shipping.
상기와 같은 공정을 통해 제조된 모래형 탈취제는 뚜껑에 적당량을 담아 고양이와 같은 반려동물의 화장실에 뿌려주며, 화장실 내부에 향을 발산시켜서 반려동물의 배변 또는 배뇨에 따른 악취를 크게 감소시키며, 향기가 약해지면 적당량을 추가해서 보충해준다.The sand-type deodorant manufactured through the above process contains an appropriate amount on the lid and sprinkles it in the toilet of a companion animal, such as a cat, and radiates incense inside the toilet to greatly reduce the odor caused by defecation or urination of the companion animal, and the fragrance When is weak, add an appropriate amount to supplement.
또한, 본 발명에 따른 모래형 탈취제는 펄프(종이) 가공품으로 물에 잘 녹으므로 변이나 오줌이 묻은 모래나 수거된 탈취제는 화장실 변기에 그대로 버리는 것이 가능하며, 변기에 버려도 막힘 현상이 발생되지 않는다.In addition, the sand-type deodorant according to the present invention is a pulp (paper) processed product, so it is well soluble in water, so sand or collected deodorant can be discarded as it is in the toilet bowl, and clogging does not occur even when discarded in the toilet bowl. .
또한, 본 발명에 따른 '고양이 모래' 또는 모래형 탈취제는 비정형(非定型) 형태를 가짐에 따라 플라스틱제 용기 밖으로 잘 비산되지 않고, 사용과정에서 쉽게 굴러가지 않게 된다.
In addition, the 'cat sand' or sand type deodorant according to the present invention is not easily scattered out of the plastic container as it has an irregular shape, and does not easily roll in the process of use.
이와 같이 본 발명에 따른 반려동물 화장실용 모래형 탈취제 제조방법을 예시된 도면을 참조로 설명하였으나, 본 명세서에 개시된 실시예와 도면에 의해 본 발명은 한정되지 않으며 그 발명의 기술사상 범위 내에서 당업자에 의해 다양한 변형이 이루어질 수 있음은 물론이다.As described above, the method for manufacturing a sand type deodorant for a companion toilet according to the present invention has been described with reference to the exemplified drawings, but the present invention is not limited by the examples and drawings disclosed herein, and those skilled in the art within the technical scope of the present invention Of course, various modifications can be made.
Claims (3)
b) 준비된 주재료와 보조 재료를 믹서기에서 3~7분 동안 혼합시켜서 주재료가 보조 재료에 고르게 베도록 하는 단계;
c) b)단계에서 얻어진 혼합물을 5~15분 동안 치대면서 반죽하는 단계;
d) c)단계에서 얻어진 반죽물을 성형기를 통해 일정 크기로 성형가공하는 단계;
e) 성형 가공물을 코팅기에 넣어서 5~15분 동안 회전시키면서 표면을 처리하는 단계;
f) e)단계에서 얻어진 성형가공물을 25~45℃ 에서 2~4시간 1차 건조시키는 단계;
g) f)단계에서 얻어진 1차 건조물을 65~75℃ 에서 3~5시간 2차 건조시키는 단계;
h) g)단계에서 얻어진 2차 건조를 거친 모래에 향료와 보존재 혼합액을 도포시키는 단계로 이루어지되,
a)단계에서의 주재료는 중량%로, 펄프 파우더(pulp powder) : 70~80%, 칼슘카보네이트(calcium carbonate) : 10~20%, 탄산수소나트륨(Sodium Bicarbonate) : 5~10%를 3~7분 동안 용기(容器)내에서 혼합하고,
보조 재료는 중량%로, 정제수 : 97~99%, 카르복시메틸 셀룰로오스(Carboxymethyl Cellulose) : 0.1~1%, 구아검(Guar Gum): 0.1~1%, 폴리비닐알코올(Polyvinyl alcohol): 0.1~1%를 용기내에서 혼합한 후에 2~4시간 숙성시키는 것을 특징으로 하는 반려동물 화장실용 모래형 탈취제 제조방법.a) as a material for the production of a sand type deodorant, preparing a main material and an auxiliary material, respectively;
b) mixing the prepared main material and auxiliary material in a blender for 3 to 7 minutes so that the main material is evenly cut into the auxiliary material;
c) kneading the mixture obtained in step b) while stirring for 5-15 minutes;
d) forming the dough obtained in step c) to a predetermined size through a molding machine;
e) processing the surface of the molded product by putting it in a coating machine and rotating it for 5 to 15 minutes;
f) first drying the molded product obtained in step e) at 25 to 45 ° C for 2 to 4 hours;
g) a second drying step of the primary dried product obtained in step f) at 65 to 75 ° C for 3 to 5 hours;
h) It consists of a step of applying a mixture of a perfume and a preservative to the sand that has undergone the secondary drying obtained in step g),
The main material in step a) is weight%, pulp powder: 70 ~ 80%, calcium carbonate: 10-20%, sodium bicarbonate: 5-10% 3 ~ Mix in a container for 7 minutes,
Auxiliary material is weight%, purified water: 97 ~ 99%, Carboxymethyl Cellulose: 0.1 ~ 1%, Guar Gum: 0.1 ~ 1%, Polyvinyl alcohol: 0.1 ~ 1 Method for manufacturing a sand type deodorant for a pet toilet, characterized in that it is aged 2-4 hours after mixing in a container.