KR102100140B1 - Medical pressure band with excellent heat conduction property and cool feeling property - Google Patents
Medical pressure band with excellent heat conduction property and cool feeling property Download PDFInfo
- Publication number
- KR102100140B1 KR102100140B1 KR1020180045891A KR20180045891A KR102100140B1 KR 102100140 B1 KR102100140 B1 KR 102100140B1 KR 1020180045891 A KR1020180045891 A KR 1020180045891A KR 20180045891 A KR20180045891 A KR 20180045891A KR 102100140 B1 KR102100140 B1 KR 102100140B1
- Authority
- KR
- South Korea
- Prior art keywords
- core
- yarn
- sheath
- sheath type
- yarns
- Prior art date
Abstract
본 발명에 따른 의료용 압박밴드는 원사들이 경편 조직 및 위편 조직 중에서 선택된 하나의 조직으로 제편된 편물 구조를 구비하며, 상기 원사들은 심사가 1차 효과사와 2차 효과사에 의해 차례로 2회 커버링되어 있는 더블 커버링 원사이고, 상기 심사는 스판덱스 원사이고, 상기 2차 효과사는 폴리에스터 폴리머인 코어부와 친수성기를 갖는 흡수성 폴리머인 쉬스부가 복합방사되어 있는 코어-쉬스형(Core-sheath type) 복합섬유를 포함하는 것을 특징으로 한다.
본 발명에 따른 의료용 압박밴드는 인체에서 배출되는 수분 및 땀을 빨리 흡수 후 확신시킬 수 있어서 우수한 열전도성과 접촉 냉감성을 발현함과 동시에 통기성과 착용감을 향상시켜 준다.The medical compression band according to the present invention has a knitting structure in which the yarns are divided into one tissue selected from warp tissue and gastric tissue, wherein the yarns are covered twice by the primary and secondary effectors in turn. It is a double covering yarn, the screening is a spandex yarn, and the secondary effect yarn includes a core-sheath type composite fiber in which a core portion, which is a polyester polymer, and a sheath portion, which is an absorbent polymer having a hydrophilic group, are compound-spun. It is characterized by.
The medical compression band according to the present invention can quickly and confidently absorb moisture and sweat discharged from the human body, thereby exhibiting excellent thermal conductivity and contact coldness, while improving breathability and wearing comfort.
Description
본 발명은 열전도성 및 접촉 냉감성이 우수한 의료용 압박밴드에 관한 것으로서, 더욱 상세하게는 부종에 의해 생길 수 있는 팔이나 다리의 만성염증에 압박을 가하여 치료하는 부종 치료용 압박밴드 등으로 사용되며, 양호한 탄력성과 함께 우수한 열전도성과 접촉 냉감성을 구비하여 착용감과 통기성이 개선된 의료용 압박밴드에 관한 것이다.The present invention relates to a medical compression band excellent in thermal conductivity and contact cold feeling, and more specifically, it is used as a compression band for treating edema by applying pressure to chronic inflammation of the arm or leg that may be caused by edema, The present invention relates to a medical compression band with improved elasticity and breathability by providing excellent elasticity and excellent thermal conductivity and contact coldness.
이하, 본 발명에서 "더블 커버링" 이라는 용어는 심사(C)를 1차 효과사(E1)로 1차 커버링하여 싱글 커버링사를 제조한 다음, 상기 싱글 커버링사를 2차 효과사(E2)로 2차 커버링하는 것을 의미한다.Hereinafter, in the present invention, the term "double covering" refers to the first covering of the examination (C) with the primary effect yarn (E1) to prepare a single covering yarn, and then the single covering yarn to the secondary effect yarn (E2). It means secondary covering.
의료용 압박붕대는 부종에 의해 생길 수 있는 팔이나 다리의 만성염증에 압박을 가해 치료하는 부종 치료용 압박밴드로 사용되거나, 골절환자의 깁스 시술시 골절 환부에 부목을 단 후 감아서 고정시키는 압박밴드 등으로 사용되고 있다.The medical compression bandage is used as a compression band for treating edema by applying pressure to the chronic inflammation of the arm or leg that may be caused by edema, or a compression band that is fixed by wrapping a splint on the fractured area during the cast of a fractured patient. Etc.
종래 의료용 압박붕대로는 심사인 스판덱스 원사가 효과사인 나일론 6 원사 또는 나일론 66 원사로 커버링되어 있는 커버링 원사로 직조된 편물 또는 직물이 널리 사용되어 왔으나, 상기 종래 의료용 압박붕대는 인체에서 배출되는 땀을 빨리 흡수 후 확산시키는 기능이 떨어져서 열전도성 및 접촉 냉감성이 불량하였고, 그로 인해 통기성 및 착용감이 떨어지는 문제가 있었다.As a conventional medical compression bandage, knitted fabrics or fabrics woven from a covering yarn covered with
한편, 또 다른 종래 의료용 압박붕대로서 대한민국 공개특허 제10-2011-0052009호에서는 가연사(DTY 원사 : Draw Textured Yarn)로 직조된 직물 형태의 의료용 압박붕대를 게재하고 있으나, 상기 종래 의료용 압박붕대의 경우 피부질환을 일으킬 수 있는 스판덱스 원사(고무사)를 사용하지 않고도 어느 정도 탄력성을 얻을 수 있는 효과는 있지만, 탄력성이 다소 부족함과 동시에 인체에서 배출되는 땀을 빨리 흡수 후 확산시키는 기능이 떨어져서 열전도성 및 접촉 냉감성이 불량한 문제점이 있었다.On the other hand, as another conventional medical compression bandage, Korean Patent Publication No. 10-2011-0052009 discloses a medical compression bandage in the form of a woven fabric made of false twisted yarn (DTY yarn: Draw Textured Yarn). In this case, there is an effect of obtaining a certain degree of elasticity without using a spandex yarn (rubber yarn), which can cause skin diseases, but the elasticity is somewhat insufficient, and at the same time, the ability to quickly absorb and diffuse sweat discharged from the human body is reduced and the thermal conductivity is reduced. And poor contact cooling.
또 다른 종래 의료용 압박붕대로서 대한민국 공개특허 제10-2010-0012625호에서는 표면사와 이면사 사이에 쿠션사를 반복으로 삽입한 경편지인 의료용 쿠션붕대를 게재하고 있으나, 인체에서 배출되는 땀을 빨리 흡수 후 확산시키는 기능이 떨어져서 열전도성 및 접촉 냉감성이 불량한 문제가 있었다.As another conventional medical pressure bandage, Korean Patent Publication No. 10-2010-0012625 discloses a medical cushion bandage, which is a warp letter that repeatedly inserts a cushion yarn between the surface yarn and the back yarn, but after quickly absorbing sweat discharged from the human body There was a problem in that the heat spreading property and the contact coldness were poor because the function of diffusing was poor.
본 발명의 과제는 양호한 탄력성을 구비하면서 인체에서 배출되는 수분 및 땀을 빨리 흡수 후 확산시킬 수 있어서 열전도성 및 접촉 냉감성, 통기성 및 착용감이 우수한 의료용 압박밴드를 제공하는 것이다.An object of the present invention is to provide a medical compression band excellent in thermal conductivity and contact coldness, breathability, and fit because it can absorb and diffuse moisture and sweat discharged from the human body while having good elasticity.
이와 같은 과제를 달성하기 위해서 본 발명에서는 심사인 스팍덱스 원사에 1차 효과사와 2차 효과사가 차례로 커버링되어 있는 더블 커버링 원사로 직조된 직물 또는 편물로 의료용 압박밴드를 제조한다.In order to achieve the above object, in the present invention, a medical compression band is manufactured from a woven fabric or a knitted fabric of a double covering yarn in which primary and secondary secondary yarns are sequentially covered to a screener's spandex yarn.
이때, 상기 2차 효과사로는 폴리에스터 폴리머인 코어부와 친수성기를 갖는 흡수성 폴리머인 쉬스부가 복합방사되어 있는 코어-쉬스형(Core-sheath type) 복합섬유가 포함된 원사를 사용하고, 상기 1차 효과사로는 상기 코어-쉬스형(Core-sheath type) 복합섬유를 포함하는 원사를 사용할 수도 있고, 나일론 6 원사 또는 나일론 66 원사를 단독으로 사용할 수도 있다.In this case, as the secondary effect yarn, a yarn containing a core-sheath type composite fiber in which a core portion, which is a polyester polymer, and a sheath portion, which is an absorbent polymer having a hydrophilic group, is compositely spun, is used. As the effect yarn, a yarn including the core-sheath type composite fiber may be used, or a
본 발명에 따른 의료용 압박밴드는 인체에서 배출되는 수분 및 땀을 빨리 흡수 후 확신시킬 수 있어서 우수한 열전도성과 접촉 냉감성을 발현함과 동시에 통기성과 착용감을 향상시켜 준다.The medical compression band according to the present invention can quickly and confidently absorb moisture and sweat discharged from the human body, thereby exhibiting excellent thermal conductivity and contact coldness, while improving breathability and wearing comfort.
도 1은 코어-쉬스형 복합섬유의 단면도.
도 2는 더블 커버링 원사를 제조하는 공정 개략도.1 is a cross-sectional view of a core-sheath type composite fiber.
2 is a schematic diagram of a process for manufacturing a double covering yarn.
이하, 첨부한 도면 등을 참조하여 본 발명을 상세하게 설명한다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.
본 발명의 의료용 압박밴드는 원사들이 경편 또는 위편으로 제편된 편물구조를 구비하고, 상기 원사들은 심사가 1차 효과사와 2차 효과사에 의해 차례로 2회 커버링 되어 있는 더블 커버링 원사이다.The medical compression band of the present invention is a double covering yarn in which the yarns are knitted with knitted or knitted fabrics, and the yarns are covered twice in turn by the primary and secondary effectors.
상기 심사는 스판덱스 원사이고, 상기 2차 효과사는 폴리에스터 폴리머인 코어부와 친수성기를 갖는 흡수성 폴리머인 쉬스부가 복합방사되어 있는 코어-쉬스형(Core-sheath type) 복합섬유를 포함하고 있다.The screening is a spandex yarn, and the secondary effect yarn includes a core-sheath type composite fiber in which a core portion of a polyester polymer and a sheath portion of an absorbent polymer having a hydrophilic group are compositely spun.
구체적으로, 상기 2차 효과사는 (ⅰ) 전부가 상기 코어-쉬스형 복합섬유로 이루어질 수도 있고, (ⅱ) 일부만 상기 코어-쉬스형 복합섬유로 이루어지고 나머지 일부는 나일론 6 원사 또는 나일론 66 원사 등의 나일론 원사로 이루어질 수도 있다. Specifically, all of the secondary effect yarns (i) may be composed of the core-sheath type composite fiber, (ii) a part of the core-sheath type composite fiber, and the other part is
상기 1차 효과사는 (ⅰ) 일부만 상기 코어-쉬스형 복합섬유이고 나머지 일부는 나일론 원사일 수도 있고, (ⅱ) 전부가 나일론 원사일 수도 있다.The primary effect yarn may be (i) a part of the core-sheath type composite fiber and the other part may be a nylon yarn, or (ii) all may be a nylon yarn.
상기 코어-쉬스형 복합섬유의 쉬스부(Y)를 구성하는 친수성기를 갖는 흡수성 폴리머는 에틸렌-비닐알콜계 공중합 폴리머 등이다.The absorbent polymer having a hydrophilic group constituting the sheath portion (Y) of the core-sheath type composite fiber is an ethylene-vinyl alcohol copolymer or the like.
상기 코어-쉬스형 복합섬유의 섬도는 심사인 스판덱스 원사의 섬도보다 상대적으로 굵은 것이 열전도도 및 접촉 냉감성을 개선하는데 바람직하다.The fineness of the core-sheath type composite fiber is relatively thicker than the fineness of the spandex yarn as a screening agent, and it is preferable to improve the thermal conductivity and contact coldness.
본 발명의 의료용 압박밴드를 구성하는 더블 커버링 원사를 제조하는 방법 일례를 살펴보면, 도 2에 도시된 바와 같이 크릴에 거치된 보빈(B1)으로부터 심사(C)를 인출하여 장력조절장치(2)를 거치면서 장력을 균일하게 조절한 후 1차 스핀들(3)의 내부 중공부 내로 통과시키면서 상부 방향으로 안내함과 동시에 1차 스핀들(3)에 끼워진 보빈(B2)으로부터 1차 효과사(E1)를 인출하여 상기 심사(C)에 1차 커버링하여 싱글 커버링사를 형성하고, 계속해서 상기 싱글 커버링사를 2차 스핀들(3')의 내부 중공부로 통과시키면서 상부 방향으로 안내함과 동시에 2차 스핀들(3')에 끼워진 보빈(B3)로부터 2차 효과사(E2)를 인출하여 상기 싱글 커버링사를 커버링하여 더블 커버링 원사를 제조한다.Looking at an example of a method of manufacturing a double covering yarn constituting the medical compression band of the present invention, as shown in Figure 2, the tension control device (2) by drawing the examination (C) from the bobbin (B1) mounted on the krill After uniformly adjusting the tension while passing through, the first effect yarn (E1) from the bobbin (B2) fitted to the primary spindle (3) is guided upward while passing through the inner hollow portion of the primary spindle (3). Withdrawal and primary covering to the screening (C) to form a single covering yarn, and continuously passing the single covering yarn through the hollow portion of the secondary spindle 3 ', guiding it upward and simultaneously the secondary spindle ( The secondary effect yarn E2 is taken out from the bobbin B3 fitted in 3 ') to cover the single covering yarn to manufacture a double covering yarn.
이하, 실시예 및 비교실시예를 통하여 본 발명을 보다 구체적으로 살펴본다.Hereinafter, the present invention will be described in more detail through Examples and Comparative Examples.
그러나, 본 발명의 보호범위를 하기 실시예만으로 한정되는 것은 아니다.However, the protection scope of the present invention is not limited to the following examples.
실시예 1Example 1
스판덱스 원사(심사)가 (ⅰ) 나일론 66(1차 효과사)와 (ⅱ) 코어-쉬스형 복합섬유(2차 효과사)에 의해 차례로 커버링되어 있는 더블 커버링 원사로 위편 조직으로 제편하여 의료용 압박밴드를 제조하였다.Spandex yarn (screening) is a double-covering yarn covered in turn by (i) nylon 66 (primary effect yarn) and (ii) core-sheath type composite fiber (secondary effect yarn), which is divided into upper tissues for medical compression. A band was prepared.
상기 코어-쉬스형 복합섬유(2차 효과사)는 코어부(X)가 폴리에스터 폴리머이고 쉬스부(Y)가 에틸렌-비닐알콜계 공중합 폴리머로 구성하였다.The core-sheath type composite fiber (secondary effect yarn) is composed of a core part (X) of a polyester polymer and a sheath part (Y) of an ethylene-vinyl alcohol-based copolymer polymer.
실시예 2Example 2
스판덱스 원사(심사)가 (ⅰ) 나일론 66(1차 효과사)와 (ⅱ) 나일론 66 원사와 코어-쉬스형 복합섬유의 혼섬사(2차 효과사)에 의해 차례로 커버링되어 있는 더블 커버링 원사로 위편조직으로 제편하여 의료용 압박밴드를 제조하였다.The spandex yarn (screening) is a double-covering yarn, which is in turn covered by (i) nylon 66 (primary effect yarn) and (ii) nylon 66 yarn and a core-sheath composite fiber blend yarn (secondary effect yarn). A medical compression band was prepared by knitting with a gastric tissue.
상기 코어-쉬스형 복합섬유(2차 효과사)는 코어부(X)가 폴리에스터 폴리머이고 쉬스부(Y)가 에틸렌-비닐알콜계 공중합 폴리머로 구성하였다.The core-sheath type composite fiber (secondary effect yarn) is composed of a core part (X) of a polyester polymer and a sheath part (Y) of an ethylene-vinyl alcohol-based copolymer polymer.
실시예 3Example 3
스판덱스 원사(심사)가 (ⅰ) 나일론 6 원사와 코어-쉬스형 복합섬유의 혼섬사(1차 효과사)와 (ⅱ) 코어-쉬스형 복합섬유(2차 효과사)에 의해 차례로 커버링되어 있는 더블 커버링 원사로 위편조직으로 제편하여 의료용 압박밴드를 제조하였다.The spandex yarn (reinforced yarn) is in turn covered with (6)
상기 코어-쉬스형 복합섬유(2차 효과사)는 코어부(X)가 폴리에스터 폴리머수지이고 쉬스부(Y)가 에틸렌-비닐알콜계 공중합 폴리머로 구성하였다.In the core-sheath type composite fiber (secondary effect yarn), the core part (X) is a polyester polymer resin and the sheath part (Y) is composed of an ethylene-vinyl alcohol-based copolymer polymer.
비교실시예 1Comparative Example 1
스판덱스 원사(심사)가 (ⅰ) 나일론 66(1차 효과사)와 (ⅱ) 나일론 66 원사(2차 효과사)에 의해 차례로 커버링되어 있는 더블 커버링 원사로 위편조직으로 제편하여 의료용 압박밴드를 제조하였다.Spandex yarn (screening) is a double-covering yarn covered in turn by (나일론) nylon 66 (primary effect yarn) and (ii) nylon 66 yarn (secondary effect yarn), which is divided into upper tissues to produce a medical compression band. Did.
상기 코어-쉬스형 복합섬유(2차 효과사)는 코어부(X)가 폴리에스터 폴리머이고 쉬스부(Y)가 에틸렌-비닐알콜계 공중합 폴리머로 구성하였다.The core-sheath type composite fiber (secondary effect yarn) is composed of a core part (X) of a polyester polymer and a sheath part (Y) of an ethylene-vinyl alcohol-based copolymer polymer.
실시예 1 내지 실시예 3으로 제조한 의료용 압박밴드와 비교실시예 1로 제조한 의료용 압박밴드를 실온 20℃에 3일 동안 보관한 후 이를 사람의 피부에 접촉시켰을 때 순간적인 열의 이동량을 측정한 각 시료의 최대열흡수속도(Q·max)를 비교해본 결과, 실시예 1 내지 실시예 3으로 제조한 의료용 압박밴드들 각각의 최대열흡수속도는 0.15J/㎠·sec 이상으로서 접촉 냉감성이 우수하였으나, 비교실시예 1로 제조한 의료용 압박밴드의 최대열흡수속도는 0.1J/㎠·sec 미만으로서 접촉 냉감성이 불량하였다The medical compression bands prepared in Examples 1 to 3 and the medical compression bands prepared in Comparative Example 1 were stored at room temperature at 20 ° C. for 3 days, and then the instantaneous heat transfer amount was measured when they were in contact with human skin. As a result of comparing the maximum heat absorption rate (Q · max) of each sample, the maximum heat absorption rate of each of the medical compression bands prepared in Examples 1 to 3 was 0.15 J / cm 2 · sec or more, and the contact cold sensitivity Although excellent, the maximum heat absorption rate of the medical compression band prepared in Comparative Example 1 was less than 0.1 J / cm 2 · sec, resulting in poor contact cooling.
X : 코어-쉬스형 복합섬유의 코어부 Y : 코어-쉬스형 복합섬유의 쉬스부
1 : 사이드 크릴(Side creel) 2 : 장력조절장치
3 : 1차 스핀들 3' : 2차 스핀들
4 : 어댑터(Adapter) 5 : 커버링사 권취장치
6 : 사 가이드(Yarn Guide) C : 심사
E1 : 1차 효과사 E2 : 2차 효과사
B1 : 심사(C)가 권취된 보빈
B2 : 1차 효과사(E1)가 권취된 보빈
B3 : 2차 효과사(E2)가 권취된 보빈X: Core part of core-sheath type composite fiber Y: Sheath part of core-sheath type composite fiber
1: Side creel 2: Tension control device
3: 1st spindle 3 ': 2nd spindle
4: Adapter 5: Winding device for covering yarn
6: Yarn Guide C: Judging
E1: Primary effector E2: Secondary effector
B1: Bobbin in which examination (C) was taken
B2: bobbin with primary effector (E1) wound
B3: Bobbin with secondary effector (E2) wound
Claims (7)
The compression band of claim 1, wherein the fineness of the core-sheathed composite fiber included in the double-covering yarn is relatively thicker than that of the spandex yarn as the screening agent.