KR102063334B1 - Complex waterproofing method using environment-friendly rubberized asphalt and easy-sheet - Google Patents
Complex waterproofing method using environment-friendly rubberized asphalt and easy-sheet Download PDFInfo
- Publication number
- KR102063334B1 KR102063334B1 KR1020190050406A KR20190050406A KR102063334B1 KR 102063334 B1 KR102063334 B1 KR 102063334B1 KR 1020190050406 A KR1020190050406 A KR 1020190050406A KR 20190050406 A KR20190050406 A KR 20190050406A KR 102063334 B1 KR102063334 B1 KR 102063334B1
- Authority
- KR
- South Korea
- Prior art keywords
- sheet
- easy
- waterproofing material
- coating
- easy sheet
- Prior art date
Abstract
Description
본 발명은 친환경 고무아스팔트와 이지시트를 이용한 복합방수공법에 관한 것으로, 특히, 방수 시공면에 시공되는 방수층이 현장에서 한 장의 시트로 조성될 수 있게 하여 시트방수공법에서 발생하는 접합부의 터짐, 누수 등의 문제점이 원천적으로 차단되게 함과 동시에 도막방수공법에서 방수층의 균일한 두께 형성이 어렵다는 단점을 해소하여 누구나 시공을 하여도 시공이 간편하게 이루어질 수 있게 하여 시공 시의 작업실수가 배제되게 함과 동시에 시공 후의 하자가 발생하지 않도록 하는 친환경 고무아스팔트와 이지시트를 이용한 복합방수공법에 관한 것이다.The present invention relates to a composite waterproof method using an environmentally friendly rubber asphalt and easy sheet, in particular, the waterproof layer to be constructed on the waterproof construction surface can be composed of a single sheet in the field, the bursting of the joint generated in the sheet waterproof method, leak In addition, the problems such as blocking the source, etc., and at the same time to solve the disadvantage that it is difficult to form a uniform thickness of the waterproof layer in the coating film waterproofing method, so that the construction can be made easily even by anyone construction, thereby eliminating the number of work during construction and at the same time The present invention relates to a composite waterproofing method using an eco-friendly rubber asphalt and easy sheet to prevent the occurrence of later defects.
콘크리트 구조물에는 정적, 동적 하중에 의한 휨 모멘트나 진동이 발생하여 균열이 일어나며 중성화 및 노화에 의한 박리가 발생한다.In concrete structures, bending moments or vibrations occur due to static and dynamic loads, and cracks occur, and peelings due to neutralization and aging occur.
또한, 빗물 등은 콘크리트 표면에 틈이나 균열을 발생시킴과 동시에, 그 틈새로 침투하여 철근을 부식시켜 콘크리트의 균열을 촉진하며 콘크리트에 생긴 균열은 건축 토목 구조물의 수명을 단축시키는 원인이 된다.In addition, rainwater, such as cracks or cracks on the surface of the concrete, at the same time penetrates into the gap to corrode the reinforcing steel to promote the cracking of the concrete, the cracks in the concrete causes a shortening of the lifespan of civil engineering structures.
현재 국내 대표적인 방수공법은 시공방식에 따라 시트방수공법, 도막방수공법, 시트와 도막을 병합한 복합방수공법이 있다.Currently, the representative waterproofing methods in Korea include sheet waterproofing method, coating film waterproofing method, and composite waterproofing method combining sheet and coating film according to the construction method.
도막방수공법의 경우 액상을 여러 번 도포한 후 경화시켜 방수층 형성하는 공법으로, 시공성은 매우 좋으나 일정한 두께의 방수층을 형성하지 못하며 도막 두께가 얇은 부위에서는 콘크리트의 균열에 의한 파단 현상이 빈번하게 발생하며, 콘크리트 모체에서 발생되는 수증기 압력에 의한 부풀음(도 1), 꽈리(도 2), 기포 등의 현상이 자주 발생하여 미세한 누수의 원인이 되며, 중심기재로는 보강재(유리섬유, 부직포) 등을 사용하나 보강재까지 흡수력의 문제, 접합성의 불일치, 치수안정성의 문제로 인한 시공상의 어려움이 있다. In the case of coating waterproofing method, it is a method of forming a waterproof layer by hardening after applying liquid phase several times. Although it has very good workability, it does not form a waterproof layer of a certain thickness. , Swelling (Fig. 1), cold (Fig. 2), bubbles, etc. due to the water vapor pressure generated in the concrete matrix causes frequent leaks, and as the base material is a reinforcing material (glass fiber, nonwoven fabric) Although it is used, there are difficulties in construction due to problems of absorptive power, inconsistency of bonding, and problems of dimensional stability.
시트방수공법은 합성고무나 합성수지 또는 개량아스팔트를 주원료로 만든 방수시트를 콘크리트에 부착하여 방수층을 형성하는 공법으로, 기 제작된 방수시트를 토오치(Torch)등의 열융착이나 접착제를 이용하여 콘크리트 바탕면에 방수시트를 부착하여 시공하는 방수공법으로 제품이 규격화되어 있어 일정한 두께로 방수층을 형성할 수 있으므로 균일한 품질관리를 얻을 수 있으며, 내수성, 내약품성, 균열저항성이 우수하며 시공이 간단하다는 장점이 있다.Sheet waterproofing is a method of forming a waterproof layer by attaching a waterproof sheet made of synthetic rubber, synthetic resin, or improved asphalt to the concrete to form a waterproof layer.The waterproof sheet is made of concrete using heat fusion or adhesive such as Torch. As the product is standardized by attaching waterproof sheet to the base surface, it is possible to form a waterproof layer with a certain thickness, so that uniform quality control can be obtained, and it has excellent water resistance, chemical resistance, crack resistance, and easy construction. There is an advantage.
그러나, 방수시트를 시공할 때는 시트 접합부(이음부)를 열융착 방식으로 접착시키는데, 방수시트에 토오치를 사용하여 접착시켜 시공하기 때문에 시트에 열이 과도하게 전달되었을 때에는 시트 표면이 손상되거나 변형되고, 또한 미열이 가해진 부분은 용융되지 않은 상태로 미접착 부분이 생기게 되어 접착력이 약화되게 되므로, 결국에는 들뜸 및 박리 등의 하자가 발생하여 누수가 발생되는 문제점이 있으며, 또한, 아스팔트만으로 구성된 방수시트는 혹한기에 시공하는 동안 또는 시공후에 시트의 유연성이 떨어져 부러지거나, 갈라지는 현상이 발생하며, 하절기 시에는 시트에 함침된 방수제가 녹아내려 방수효과가 감소되어 방수층의 파단으로 이어진다.However, when constructing the waterproof sheet, the sheet joints (joints) are bonded by heat-sealing method. Torch is bonded to the waterproof sheet using a torch, so when the heat is excessively transferred to the sheet, the sheet surface is damaged or deformed. In addition, since the unheated portion is not melted, the unbonded portion is formed, and thus the adhesive strength is weakened. Thus, there is a problem in that a defect such as lifting and peeling occurs and water leakage occurs. The sheet breaks or breaks due to the flexibility of the sheet during or during construction in cold weather, and during summer, the waterproofing agent impregnated in the sheet melts, thereby reducing the waterproofing effect, leading to breakage of the waterproof layer.
또한, 복합방수공법의 경우 시트와 도막을 2중으로 처리하여 안정성을 확보하는 장점을 지니고 있으나 재료비, 시공비가 매우 높으며 시공성이 복잡하여 숙련공이 많이 필요하고 시트층과 도막층의 접합 불일치로 박리, 조인트 연결부가 파단되는 경우가 빈번하게 발생하여 새로운 공법을 갈망하고 있다.In addition, the composite waterproof method has the advantage of securing stability by double-treating the sheet and the coating film, but the material cost and construction cost is very high, and the workability is complicated, requiring a lot of skilled workers, peeling, joint due to the mismatch between the sheet layer and the coating layer Frequent breaks in joints are eager for new construction.
본 발명은 상기한 문제점을 해결하기 위하여 안출된 것으로, 도막방수공법에 시트방수공법이 접목될 수 있게 하되, 시공 시 1회의 도포만으로 도막방수재가 경화되는 짧은 시간에 두께가 형성되도록 하기 위하여 방수층이 형성되지 않은 편직물인 이지시트가 시공면에 포설된 후 이 이지시트에 도포된 도막방수재가 편직물인 이지시트에 함침되면서 이지시트에 의해 소망하는 도막의 두께가 형성되도록 하여 이음매나 접합부가 없이 방수층이 형성될 수 있게 하는 이지시트 및 친환경 고무아스팔트와 이지시트를 이용한 복합방수공법을 제공하는 데 그 목적이 있다.The present invention has been made in order to solve the above problems, but the sheet waterproofing method can be grafted to the coating film waterproofing method, the waterproof layer is formed so that the thickness is formed in a short time when the coating waterproofing material is cured by only one coating during construction. After the easy sheet, which is not formed, is laid on the construction surface, the coating film waterproofing material applied to the easy sheet is impregnated into the easy sheet, which is a knitted fabric, so that the desired thickness of the coating film is formed by the easy sheet. It is an object of the present invention to provide a composite waterproofing method using an easy sheet and easy rubber asphalt and easy sheet to be formed.
상기한 목적은, 바탕면의 이물질을 제거하고 세척하는 바탕면 정리단계와; 상기 바탕면 정리단계에 의해 정리된 콘크리트 바탕면에 합성고무계 프라이머를 도포하여 프라이머층을 형성하는 프라이머 도포단계와; 상기 프라이머 도포단계가 실시된 후, 370 ~ 410 데니아의 굵기를 가지는 폴리에틸렌(Polyethylene) 원사로 이루어진 다수 개의 제1번사(102)가 가로방향으로 편직되는 연결용 루프가 세로방향을 따라 일정 간격 반복 형성되며, 세로방향으로는 배열되는 370 ~ 410 데니아의 굵기를 가지는 폴리에틸렌(Polyethylene) 원사로 이루어진 제2번사(104)가 지그재그 방향으로 이동하면서 제1번사(102)의 연결용 루프에 상호 연결하는 연결고리를 형성함과 동시에 편직되고, 편직과 동시에 180 ~ 220℃로 열처리되어 이루어진 이지시트(100)를 포설하는 이지시트(100) 포설단계와; 상기 바탕면에 포설된 이지시트(100)에 액상의 아스팔트계 방수재와 경화제가 17kg : 100 ~ 200cc로 혼합된 도막방수재를 도포하여 이지시트(100)에 도막방수재가 함침되게 하는 방수재 도포단계와; 상기 방수재 도포단계에 의해 이지시트에 도막방수재가 함침된 후 2 ~ 3시간 경과하여 경화되면, 보호몰탈을 타설하거나 보호재 또는 PE필름을 부착하는 보호층 형성단계를 포함하는 것을 특징으로 하는 친환경 고무아스팔트와 이지시트를 이용한 복합방수공법에 의해 달성된다.The above object, the base surface cleansing step of removing and cleaning the foreign matter on the base surface; A primer coating step of forming a primer layer by applying a synthetic rubber primer to the concrete base surface cleaned by the base surface cleaning step; After the primer coating step is performed, a plurality of
그리고, 상기 이지시트(100)는 1㎡당 150 ~ 180g의 중량의 편직물이며, 상기 아스팔트계 방수재는 1,000cps 이상의 점도와 600% 이사의 신장율을 가지며, 고형분이 80% 이상인 고무아스팔트인 것이 바람직하다.The
본 발명에 따른 이지시트 및 친환경 고무아스팔트와 이지시트를 이용한 복합방수공법에 의하면, 이지시트와 이 이지시트에 함침되는 도막방수재에 의하여 도막방수공법의 문제점인 두께형성이 용이하게 이루어지고, 소망하는 두께(2.1mm ~ 3mm)는 경화제와 액상의 아스팔트계 방수재의 혼합비를 통하여 형성할 수 있는 장점을 가지며, 시공면 전체에 걸쳐 이지시트를 포설하고 방수재를 도포함으로써, 접합부가 없는 방수층을 형성할 수 있다는 장점을 통하여 종래와 같이 접합부 및 조인트의 부실공사로 인한 방수시공 후 발생하는 접합부 및 조인트의 박리, 탈리 등의 문제점을 해결할 수 있는 효과를 가진다.According to the composite waterproofing method using the easy sheet and the eco-friendly rubber asphalt and the easy sheet according to the present invention, by the easy sheet and the coating film waterproofing material impregnated in the easy sheet, it is easy to form the thickness of the coating film waterproofing method, and the desired Thickness (2.1mm ~ 3mm) has the advantage that can be formed through the mixing ratio of the hardening agent and the liquid asphalt-based waterproofing material, by forming an easy sheet over the entire construction surface and applying a waterproofing material, it is possible to form a waterproof layer without joints Through the advantage that there is an effect that can solve problems such as peeling, detachment of the joint and joint generated after the waterproof construction due to poor construction of the joint and joint as in the prior art.
그리고, 종래 도막방수공법에서 도막방수층 형성 후 자외선에 노출된 상태로 도막층이 경화되면서 발생하는 기포나 꽈리 및 방수막이 터지는 현상은 통기성이 뛰어난 이지시트에 의하여 기포발생의 우려를 해결하여 안정적인 도막층의 형성을 유도할 수 있으며, 특히, 시공 현장에서 한 장의 방수시트로 방수층을 형성한 것과 같은 효과를 얻을 수 있게 됨으로써, 종래 일정한 두께의 방수층 형성, 이음매 발생 및 파단, 방수층의 파단, 기포, 꽈리 등 우려되는 모든 문제점을 동시에 해결할 수 있게 되어 향후의 하자발생이 최소화되어 건물수명의 연장에 의한 제반적인 비용의 절감효과를 얻도록 하는 효과를 가진다.In the conventional film waterproofing method, bubbles, cracks, and waterproof films that occur when the coating layer is cured while being exposed to ultraviolet rays after the formation of the coating waterproof layer are solved by the easy-sheet that is highly breathable. It is possible to induce the formation of, and in particular, it is possible to obtain the same effect as forming a waterproof layer with a single sheet of waterproof sheet at the construction site, thereby forming a waterproof layer of a certain thickness, generation and break of seams, breaking of the waterproof layer, bubbles, glass All problems of concern can be solved at the same time, thus minimizing future defects, thereby reducing the overall cost of building by extending the life of the building.
도 1은 종래 도막층이 자연경화되면서 통기성부족으로 인한 방수층과 섬유직포 보강재가 함께 부풀음 발생된 상태의 사진.
도 2는 종래 도막층이 자연경화되면서 발생된 부풀음 사진.
도 3은 PE 매쉬망에 본 발명에 따른 도막방수재를 함침시킨 시편의 인장시험 성적서.
도 4는 부직포에 본 발명에 따른 도막방수재를 함침시킨 시편의 인장시험 성적서.
도 5는 본 발명에 따른 이지시트(100)에 본 발명에 따른 도막방수재를 함침시킨 시편의 인장시험 성적서.
도 6은 본 발명에 따른 이지시트의 구조를 촬영한 사진Figure 1 is a photograph of a state in which the conventional coating layer is naturally swelling together with the waterproof layer and the textile fabric reinforcement due to lack of breathability.
Figure 2 is a swelling photo generated while the conventional coating film layer cured naturally.
Figure 3 is a tensile test report of the specimen impregnated with a coating waterproofing material according to the present invention in a PE mesh.
Figure 4 is a tensile test report of the specimen impregnated with a non-woven fabric coating waterproofing material according to the present invention.
5 is a tensile test report of the test piece impregnated with a coating film waterproofing material according to the present invention in the
Figure 6 is a picture taken the structure of the easy sheet according to the present invention
본 발명에 따른 친환경 고무아스팔트와 이지시트를 이용한 복합방수공법을 도 3 내지 도 6을 참조하여 설명하면 다음과 같다.The composite waterproof method using the eco-friendly rubber asphalt and easy sheet according to the present invention will be described with reference to FIGS.
본 발명 친환경 고무아스팔트와 이지시트를 이용한 복합방수공법에서 중요한 구성요소인 이지시트(100)의 구성을 살펴보면 다음과 같다.Looking at the configuration of the
도 6은 본 발명에 따른 이지시트(100)의 구조를 도시한 사진으로서, 도시된 바와 같이 본 발명의 이지시트(100)는 폴리에틸렌(Polyethylene, PE)으로 이루어진 제1번사(102)와 제2번사(104)가 편직되어 이루어진 편직물이다.Figure 6 is a picture showing the structure of the
즉, 상기 제1번사(102)와 제2번사(104)는 370 ~ 410 데니아의 굵기를 가지는 폴리에틸렌(Polyethylene) 원사로 이루어지며, 다수 개의 제1번사(102)는 가로방향으로 연결용 루프를 형성하고, 이 가로방향으로 형성된 연결용 루프는 세로방향을 따라 일정 간격 반복 형성된다.That is, the
그리고, 상기 제1번사(102)의 연결용 루프에 편직되는 제2번사(104)는 세로방향으로는 배열되어 지그재그 방향으로 이동하면서 연결고리를 형성하면서 제1번사(102)의 연결용 루프에 상호 연결되는 구조로 편직된다.In addition, the
상기한 바와 같이 편직된 제1번사(102)와 제2번사(104)는 편직이 완료됨과 동시에 180 ~ 220℃로 열처리 가공하여 폴리에틸렌(Polyethylene, PE)으로 이루어진 제1번사(102)와 제2번사(104)가 편직되면서 원사의 재질적 특성에 의하여 복원되려하는 복원력이 제거되게 하여 이지시트(100)가 편평한 상태를 유지하게 하되, 이지시트(100)를 편직하는 망의 목수는 제1번사(102)는 8개이고 제2번사(104)는 10개이며, 편직된 상기 이지시트(100)는 1㎡당 150 ~ 180g의 중량이 되도록 편직하는 것이 바람직하다.The
한편, 본 발명에 따른 친환경 고무아스팔트와 이지시트를 이용한 복합방수공법은 방수시공을 하고자 하는 바탕면의 이물질을 제거하고 세척하는 바탕면 정리단계를 실시하고, 상기 바탕면 정리단계에 의해 정리된 콘크리트 바탕면에는 합성고무계 프라이머를 도포하여 프라이머층을 형성하는 프라이머 도포단계를 실시한다.On the other hand, the composite waterproofing method using the eco-friendly rubber asphalt and easy sheet according to the present invention is carried out the base surface cleaning step to remove and wash the foreign matter of the base surface to be waterproof construction, the concrete arranged by the base surface cleaning step The base surface is subjected to a primer coating step of forming a primer layer by applying a synthetic rubber primer.
그리고, 상기 프라이머 도포단계가 실시된 후, 상기한 이지시트(100)를 바탕면에 포설하는 이지시트(100) 포설단계를 실시하는 바, 이때, 상기 이지시트(100)를 포설하는 방법은 길이방향을 따라 하나의 이지시트(100)만이 포설되게 한 후, 후술하게 될 방수재 도포단계에 의하여 도막방수재를 포설된 이지시트(100)에 도포할 수도 있으며, 상기 이지시트(100)를 길이방향을 따라 연장되도록 포설한 후, 측면 방향으로는 또 다른 이지시트(100)를 연접하여 포설하되, 서로 오버랩(overlap)되도록 포설한 후, 후술하게 될 방수재 도포단계에 의하여 도막방수재를 포설된 이지시트(100) 전체에 도포할 수도 있는 것으로, 상기한 이지시트(100) 포설단계는 작업조건에 따라 선택적으로 채택할 수 있는 것이므로 본 발명은 여기에 한정되지 않고 다양하게 채택변경할 수 있다.Then, after the primer coating step is carried out, the step of laying the
상기한 바와 같이 이지시트(100) 포설단계에 의하여 이지시트(100)가 바탕면에 포설되면, 상기 바탕면에 포설된 이지시트(100)에 액상의 아스팔트계 방수재와 경화제가 17kg : 100 ~ 200cc로 혼합된 도막방수재를 도포하여 이지시트(100)에 도막방수재가 함침되게 하는 방수재 도포단계를 실시한다.When the
여기서, 상기 아스팔트계 방수재는 1,000cps 이상의 점도와 600% 이상의 신장율을 가지며, 고형분이 80% 이상인 고무아스팔트인 것이 바람직하다.Here, the asphalt-based waterproofing material has a viscosity of at least 1,000 cps and an elongation of at least 600%, preferably solid rubber of at least 80%.
즉, 상기 이지시트(100)는 도막방수재가 함침된 후 두께가 용이하게 형성되도록 하기 위하여 도시된 바와 같이 제1번사(102)와 제2번사(104)가 편직된 상태에서도 연결용 루프와 연결고리가 일정한 두께를 형성하면서 그 사이에 빈 공간이 형성되도록 한 것으로서, 아스팔트계 방수재의 점도가 1,000cps 이하일 경우 흐름성이 높아지므로, 이지시트(100)에 함침된 도막방수재가 이지시트(100)에 함침되는 함침률은 증가하지만, 상대적으로 고형분이 80% 이하로 조성되므로, 경화과정에서 수축하는 현상이 크게 발생하며, 이때, 이지시트(100)에 함침된 도막방수재가 어느 한 방향으로 편중되게 수축될 경우 균일하게 두께가 형성되지 못할 수도 있으며, 특히, 계절, 기후, 작업환경에 따라 경화과정에서 수축되는 수축률이 크게 달라지게 되어 작업이 불편하게 이루어질 수 있는 단점이 발생하게 된다.That is, the
따라서, 본 발명에서는 이지시트(100)에 함침되는 도막방수재가 본 발명의 이지시트(100)에 적합한 흐름성을 갖게 함과 동시에 이에 따라, 예측 가능한 수축률을 갖게 함으로써, 두께 형성이 용이하게 이루어지게 하면서 수축에 의한 두께의 편차가 배제되도록 아스팔트계 방수재는의 점도가 1,000cps 이상으로 유지되게 하는 것이 바람직하다.Therefore, in the present invention, the coating film waterproofing material impregnated in the
다시 말하면, 상기 아스팔트계 방수재인 고무아스팔트는 상기한 바와 같이 1,000cps 이상의 점도와 600% 이상의 신장율을 가지며, 고형분이 80% 이상이며, 이지시트(100)에 함침되는 도막방수재는 상기한 아스팔트계 방수재와 경화제를 17kg : 100 ~ 200cc로 혼합하여 경화속도와 점도 및 흐름성이 작업에 적합하게 됨으로써, 두께 형성이 용이하게 이루어지게 하면서 수축에 의한 두께의 편차가 배제될 수 있게 되는 것이다.In other words, the rubber asphalt as the asphalt-based waterproofing material has a viscosity of 1,000 cps or more and an elongation rate of 600% or more as described above, the solid content is 80% or more, and the coating waterproof material impregnated in the
상기한 바와 같이 방수재 도포단계에 의해 이지시트에 도막방수재가 함침된 후 2 ~ 3시간 경과하여 도막방수재가 경화되면, 그 상부에는 보호몰탈을 타설하거나 보호재 또는 PE필름을 부착하는 보호층 형성단계를 실시하여 방수층이 보호될 수 있게 한다.After the waterproofing material is impregnated in the easy sheet by the waterproofing material coating step as described above, if the coating waterproofing material is cured for 2 to 3 hours, a protective layer forming step of placing a protective mortar or attaching a protective material or PE film to the upper part is performed. To ensure that the waterproofing layer is protected.
따라서, 본 발명에 따른 친환경 고무아스팔트와 이지시트를 이용한 복합방수공법은 시공면 전체가 하나의 시트로 방수층을 형성할 수 있게 한 것으로서, 도막방수공법에서 방수층의 두께형성이 곤란하였던 문제점을 극복하여 2.1mm ~ 3.0mm까지의 방수층 두께형성이 용이하며, 시트방수공법에서 시트와 시트간에 형성되는 접합부가 배제됨으로써, 접합부에서 발생하는 터짐이나 누수 등의 문제점을 완벽하게 해소할 수 있다.Therefore, the composite waterproofing method using the eco-friendly rubber asphalt and easy sheet according to the present invention allows the entire construction surface to form a waterproofing layer with a single sheet, overcoming the problem that the thickness formation of the waterproofing layer was difficult in the coating waterproofing method. It is easy to form a waterproof layer thickness of 2.1mm ~ 3.0mm, and the joint formed between the sheet and the sheet is excluded from the sheet waterproofing method, it is possible to completely solve the problems such as burst or leaks generated in the joint.
도 3은 PE 매쉬망에 본 발명에 따른 도막방수재를 함침시킨 시편의 인장시험 성적서이고, 도 4는 부직포에 본 발명에 따른 도막방수재를 함침시킨 시편의 인장시험 성적서이고, 도 5는 본 발명에 따른 이지시트(100)에 본 발명에 따른 도막방수재를 함침시킨 시편의 인장시험 성적서이다.3 is a tensile test report of the test piece impregnated with the coating waterproof material according to the present invention in a PE mesh net, Figure 4 is a tensile test report of the test piece impregnated with a coating waterproof material according to the present invention in a nonwoven fabric, Figure 5 is a present invention Tensile test report of the specimen impregnated with a coating film waterproofing material according to the present invention.
도 3에 도시된 바와 같이 PE 매쉬망 시편은 인장강도가 낮으며 연신율이 너무 높아 도막방수재가 경화되는 과정에서 편중된 수축력에 의해 균일한 두께형성이 불편할 뿐만 아니라, PE 매쉬망은 직조된 구조로서 자체적으로 두께 형성이 어렵다는 문제점이 있다.As shown in FIG. 3, the PE mesh net specimen has a low tensile strength and a high elongation, so that the uniform thickness formation is inconvenient due to the shrinkage force biased during the curing of the coating waterproof material, and the PE mesh mesh is a woven structure. There is a problem that it is difficult to form the thickness itself.
도 4에 도시된 바와 같이 부직포 시편은 함침시간이 증가하고, 이에 따라 경화시간도 증가하게 되며, 부직포 상부에 도포되어 부직포에 함침된 상태에서의 도막방수재가 프라이머층과 접착될 때, 그 접착성능이 기대한 만큼 이루어지지 않을 뿐만 아니라, 인장강도가 높은 반면에 연신율이 낮은 시험결과에서 알 수 있듯이 바탕면의 거동에 대한 대응성이 낮으므로 시공 후 파단되는 문제점이 발생하게 된다.As shown in FIG. 4, the impregnation time of the nonwoven fabric specimen is increased, and accordingly, the curing time is increased. Not only is this not achieved as expected, but as the tensile strength and low elongation test results show, the responsiveness to the behavior of the ground surface is low, causing problems after construction.
도 5는 본 발명에 따른 이지시트(100)에 도막방수재를 함침시킨 시편의 인장시험 성적서로서, 시편의 크기 및 규격에 따른 인장강도의 편차가 크지 않으므로 일정한 인장강도를 가지며, 특히 연신율도 높아서 바탕면의 거동에 대한 대응성이 우수하다.5 is a tensile test report of the specimen impregnated with a coating film waterproofing material in the
특히, 상술한 바와 같이 이지시트(100)가 편직물로 제작되고, 제1번사(102)와 제2번사(104)가 편직되는 과정에서 연결용 루프와 연결고리의 틈새로 도막방수재가 침투 또는 함침되는 구조이므로, 함침된 도막방수재가 바탕면에 도포된 프라이머층과 접촉면적이 확대되면서 접착률이 크게 증가하여 안정적으로 방수층을 형성할 수 있는 장점을 가진다. Particularly, as described above, the
100 : 이지시트
102 : 제1번사 104 : 제2번사100: Easy Sheet
102: the first company 104: the second company
Claims (3)
상기 이지시트(100)는 편직과 동시에 180 ~ 220℃로 열처리되며, 1㎡당 150 ~ 180g의 중량의 편직물이고,
상기 방수재 도포단계의 도막방수재는, 1,000cps 이상의 점도와 600% 이상의 점도를 가지며, 고형분이 80% 이상인 액상의 아스팔트계 방수재와 경화제가 17kg : 100 ~ 200cc로 혼합된 것을 특징으로 하는 친환경 고무아스팔트와 이지시트를 이용한 복합방수공법.
A base surface cleaning step of removing and washing foreign substances on the base surface, a primer applying step of forming a primer layer by applying a synthetic rubber primer to the concrete base surface cleaned by the base surface cleaning step, and applying the primer After that, a plurality of first yarns 102 made of polyethylene yarns having a thickness of 370 to 410 deniers are repeatedly formed at regular intervals along the longitudinal direction, and the connecting loops are knitted in the horizontal direction. The second yarn 104 made of polyethylene yarn having a thickness of 370 to 410 denier arranged moves in the zigzag direction to form a connecting ring interconnecting the connecting loop of the first yarn 102. The step of laying the easy sheet 100 for laying the knitted easy sheet 100, and applying a coating film waterproofing material to the easy sheet 100 installed on the base surface When the waterproofing material coating step, and after curing for 2 to 3 hours after the coating sheet waterproofing material is impregnated in the easy sheet by the waterproofing material applying step, the environment-friendly comprising a protective layer forming step of pouring a protective mortar or attaching a protective material or PE film In the composite waterproof method using rubber asphalt and easy sheet,
The easy sheet 100 is knitted and heat treated at 180 to 220 ° C. at the same time, and is a knitted fabric having a weight of 150 to 180 g per 1 m 2,
The waterproof coating material of the waterproofing material coating step has a viscosity of at least 1,000 cps and a viscosity of 600% or more, and an eco-friendly rubber asphalt, characterized in that a liquid asphalt-based waterproofing material and a hardener having a solid content of 80% or more are mixed in 17kg: 100 to 200cc. Composite waterproof method using easy sheet.