KR102013119B1 - Incombustible sheet and manufacturing method the same and manufacturing device the same - Google Patents

Incombustible sheet and manufacturing method the same and manufacturing device the same Download PDF

Info

Publication number
KR102013119B1
KR102013119B1 KR1020180016497A KR20180016497A KR102013119B1 KR 102013119 B1 KR102013119 B1 KR 102013119B1 KR 1020180016497 A KR1020180016497 A KR 1020180016497A KR 20180016497 A KR20180016497 A KR 20180016497A KR 102013119 B1 KR102013119 B1 KR 102013119B1
Authority
KR
South Korea
Prior art keywords
paper
flame retardant
flame
adhesive
retardant
Prior art date
Application number
KR1020180016497A
Other languages
Korean (ko)
Other versions
KR20190096719A (en
Inventor
구종회
안종철
Original Assignee
(주)지피피
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)지피피 filed Critical (주)지피피
Priority to KR1020180016497A priority Critical patent/KR102013119B1/en
Publication of KR20190096719A publication Critical patent/KR20190096719A/en
Application granted granted Critical
Publication of KR102013119B1 publication Critical patent/KR102013119B1/en

Abstract

난연 시트지에 대한 발명이 개시된다. 개시된 난연 시트지는: 알루미늄박지와, 알루미늄박지의 일면에 구비되는 종이와, 알루미늄박지와 종이 사이에 구비되어 알루미늄박지와 종이를 상호 부착하도록 접착제에 난연제를 포함하여 이루어지는 난연접착제와, 종이의 외측면에 도포되는 코팅층을 포함하는 것을 특징으로 한다.Disclosed is a flame retardant sheet paper. The disclosed flame retardant sheet paper includes: an aluminum foil, a paper provided on one side of the aluminum foil, a flame retardant adhesive provided between the aluminum foil and the paper and including a flame retardant in an adhesive to adhere the aluminum foil and the paper to each other, and an outer surface of the paper. It characterized in that it comprises a coating layer applied to.

Description

난연 시트지, 그 제조방법 및 그 제조장치{INCOMBUSTIBLE SHEET AND MANUFACTURING METHOD THE SAME AND MANUFACTURING DEVICE THE SAME}Flame-retardant sheet paper, its manufacturing method and its manufacturing apparatus {INCOMBUSTIBLE SHEET AND MANUFACTURING METHOD THE SAME AND MANUFACTURING DEVICE THE SAME}

본 발명은 난연 시트지, 그 제조방법 및 그 제조장치에 관한 것으로서, 더욱 상세하게는, 알루미늄박지와 종이 사이에 접착제에 난연제가 함유된 난연접착제를 투입하여 합지하도록 하고, 종이의 외측면에 접착제에 난연제가 함유된 난연접착제를 도포하고, 그 외측에 코팅액을 추가 도포하므로 사용시 매끄러운 종이 질감을 느끼면서 화재 발생시 유독가스 발생을 줄여 환경 친화적일 수 있는 난연 시트지, 그 제조방법 및 그 제조장치에 관한 것이다.The present invention relates to a flame-retardant sheet paper, a method of manufacturing the same and an apparatus for manufacturing the same, and more particularly, a flame-retardant adhesive containing a flame retardant is added to an adhesive between aluminum foil and paper, and laminated. A flame retardant adhesive sheet containing a flame retardant is applied, and a coating solution is additionally applied to the outside thereof, so that a flame-retardant sheet paper which can be environmentally friendly by reducing the generation of toxic gases in the event of a fire while feeling a smooth paper texture during use, and a manufacturing method thereof and an apparatus thereof .

일반적으로, 아파트를 제외한 고층 건물, 영화관, 종합병원, 유흥업소 등 많은 사람이 이용하는 건물의 벽지나 커튼과 같은 내장재로는, 화염의 전파가 가능한 한 늦으면서도 유독 가스의 발생량이 적게 발생함으로써 화재발생 초기에 사람들에게 대피할 시간을 가질 수 있도록 화재 방지용 벽지 소재를 사용하도록 소방법에 규정되어 있다.In general, interior materials such as wallpaper and curtains of buildings used by many people, such as high-rise buildings, movie theaters, general hospitals, and entertainment establishments, except apartments, cause fires due to the generation of toxic gases as late as possible. Fire codes stipulate the use of fire-resistant wallpaper material so that people have time to evacuate early.

화재 방지용 벽지 소재에는 불이 붙으려 할 때 화염에 휩싸여 전부 타버리거나 불씨가 남아서 확산되지 않는 성질을 갖는 방염 벽지와, 화재 발생시 화염의 확산속도를 늦추고 유독가스의 발생을 억제하고, 타기 어려운 성질을 갖는 유리섬유 벽지등이 있다.The fire-proof wallpaper material is a flame-resistant wallpaper that has a property of being burned by a flame when it is about to catch fire, or which does not remain due to the spread of embers, and slows down the spread of the flame, suppresses the generation of toxic gases, and makes it difficult to burn. Glass fiber wallpaper having;

유리섬유 벽지는 파이버 글라스를 직조 형태로 가공하여 난연 시공을 하고자 하는 벽면에 부착하여 사용하므로 화재 발생시 유리섬유 벽지가 화염의 발생을 저지하여 화염이 벽지 내측 부분으로 전파되는 것을 차단하여 화재를 방지하게 된다.Glass fiber wallpaper is processed by weaving fiberglass in the form of weaving and attaching it to the wall to be flame-retardant. Therefore, the glass fiber wallpaper prevents the flame from occurring in case of a fire and blocks the flame from propagating to the inner part of the wallpaper to prevent fire. do.

그런데, 기존의 난연성 시트지는 화재발생시 불에 잘 타지 않지만 유독상 가스가 대량으로 발생되어 대피자의 호흡기에 치명적인 위해를 끼치는 문제점이 있었다.By the way, the existing flame-retardant sheet paper does not burn well in the event of a fire, but a large amount of toxic gas generated there was a problem causing a fatal hazard to the respiratory tract of the evacuator.

따라서, 이를 개선할 필요성이 요청된다.Therefore, there is a need for improvement.

관련 배경기술로는 등록특허공보 제10-1441192호(2014.09.05, 발명의 명칭: 난연종이의 제조방법 및 이에 의한 난연종이)가 있다.Related background arts are registered in Korean Patent Publication No. 10-1441192 (September 5, 2014, title of the invention: a method for producing flame retardant paper and flame retardant paper thereby).

본 발명은 상기와 같은 필요성에 의해 창출된 것으로서, 알루미늄박지와 종이 사이에 접착제에 난연제가 함유된 난연접착제를 투입하여 합지하도록 하고, 종이의 외측면에 접착제에 난연제가 함유된 난연접착제를 도포하고, 그 외측에 코팅액을 추가 도포하므로 사용시 매끄러운 종이 질감을 느끼면서 화재 발생시 유독가스 발생을 줄여 환경 친화적인 사용을 가능하게 하는 난연 시트지, 그 제조방법 및 그 제조장치를 제공하는 데 그 목적이 있다.The present invention has been created by the necessity as described above, and put the flame retardant adhesive containing a flame retardant in the adhesive between the aluminum foil and the paper to be laminated, and apply the flame retardant adhesive containing the flame retardant to the adhesive on the outer surface of the paper In order to provide a flame retardant sheet paper, a method of manufacturing the same, and an apparatus for manufacturing the same, a coating liquid is applied to an outer side thereof so as to feel a smooth paper texture during use and reduce the generation of toxic gases during a fire, thereby enabling environmentally friendly use.

상기한 목적을 달성하기 위하여 본 발명에 따른 난연 시트지는, 알루미늄박지; 상기 알루미늄박지의 일면에 구비되는 종이; 상기 알루미늄박지와 상기 종이 사이에 구비되어 상기 알루미늄박지와 상기 종이를 상호 부착하도록 접착제에 난연제를 포함하여 이루어지는 난연접착제; 및 상기 종이의 외측면에 도포되는 코팅층;을 포함하는 것을 특징으로 한다.In order to achieve the above object, the flame-retardant sheet paper according to the present invention is aluminum foil; Paper provided on one surface of the aluminum foil; A flame retardant adhesive provided between the aluminum foil and the paper and including a flame retardant in an adhesive to adhere the aluminum foil and the paper to each other; And a coating layer applied to the outer surface of the paper.

또한, 상기 종이의 외측면과 상기 코팅층 사이에는 상기 난연접착제가 더 포함되고, 상기 난연접착제는 접착제 40~70 중량%, 난연제 30~60 중량%를 포함하는 것을 특징으로 한다.In addition, the flame retardant adhesive is further included between the outer surface of the paper and the coating layer, the flame retardant adhesive is characterized in that it comprises an adhesive 40 to 70% by weight, flame retardant 30 to 60% by weight.

또한, 상기 접착제는 대두접착제(Soy Adhesive)를 포함하는 것을 특징으로 한다.In addition, the adhesive is characterized in that it comprises a soy adhesive (Soy Adhesive).

또한, 상기 난연제는 물유리, 인계난연제(Phosphrous-based flame retardants), 할로겐계난연제(Halogen-based flame retardants), 무기계난연제(inoragnic flame retardants)중 어느 하나 이상을 포함하는 것을 특징으로 한다.In addition, the flame retardant is characterized in that it comprises any one or more of water glass, Phosphrous-based flame retardants, halogen-based flame retardants, inorganic flame retardants.

또한, 상기 난연제는 물유리 35~60중량%, 인계난연제 15~25중량%, 할로겐계난연제 15~25중량%, 무기계난연제 10~15중량%를 포함하는 것을 특징으로 한다.In addition, the flame retardant is characterized in that it comprises water glass 35 to 60% by weight, phosphorus flame retardant 15 to 25% by weight, halogen flame retardant 15 to 25% by weight, inorganic flame retardant 10 to 15% by weight.

상기한 목적을 달성하기 위하여 본 발명에 따른 난연 시트지 제조방법은, 종이와 알루미늄박지를 준비하는 단계; 상기 종이의 이면에 난연접착제를 도포하는 단계; 상기 종이의 이면에 도포된 난연접착제에 상기 알루미늄박지를 접착하여 합지하는 단계; 및 상기 합지의 종이 외측면에 난연접착제를 도포하는 단계; 상기 합지를 건조유닛에서 건조하여 난연시트지를 제조하는 단계;를 포함하는 것을 특징으로 한다.In order to achieve the above object, a flame-retardant sheet paper manufacturing method according to the present invention comprises the steps of preparing a paper and aluminum foil; Applying a flame-retardant adhesive on the back side of the paper; Adhering and laminating the aluminum foil to a flame-retardant adhesive applied to the back side of the paper; And applying a flame retardant adhesive to the paper outer surface of the paper. And drying the lamination in a drying unit to produce a flame retardant sheet paper.

상기한 목적을 달성하기 위하여 본 발명에 따른 난연 시트지 제조방법의 변형예는, 종이와 알루미늄박지를 준비하는 단계; 상기 종이의 외측면에 난연접착제를 도포하고 건조하는 단계; 상기 종이의 이면에 난연접착제를 도포하는 단계; 상기 종이의 이면에 도포된 난연접착제에 상기 알루미늄박지를 접착하여 합지하는 단계; 및 상기 합지를 건조유닛에서 건조하여 난연시트지를 제조하는 단계;를 포함하는 것을 특징으로 한다.In order to achieve the above object, a modified example of the method for manufacturing a flame-retardant sheet paper according to the present invention includes the steps of preparing paper and aluminum foil; Applying and drying a flame-retardant adhesive on the outer surface of the paper; Applying a flame-retardant adhesive on the back side of the paper; Adhering and laminating the aluminum foil to a flame-retardant adhesive applied to the back side of the paper; And drying the paper in a drying unit to produce a flame retardant sheet paper.

또한, 상기 종이의 외측면에 도포된 상기 난연접착제 상에 코팅층을 도포하는 단계; 및 상기 건조유닛에서 상기 난연시트지를 건조한 후, 타공홀형성부를 이용하여 상기 난연시트지를 관통하는 다수개의 타공홀을 형성하는 단계; 중 적어도 어느 하나의 단계를 더 포함하는 것을 특징으로 한다.In addition, applying a coating layer on the flame-retardant adhesive applied to the outer surface of the paper; And after drying the flame retardant sheet paper in the drying unit, forming a plurality of perforated holes penetrating the flame retardant sheet paper using the perforated hole forming unit. At least any one of the steps characterized in that it further comprises.

또한, 상기 난연접착제는 접착제 40~70 중량%, 난연제 30~60 중량%를 포함하고, 상기 난연제는 물유리 35~60중량%, 인계난연제 15~25중량%, 할로겐계난연제 15~25중량%, 무기계난연제 10~15중량%를 포함하는 것을 특징으로 한다.In addition, the flame retardant adhesive agent 40 to 70% by weight of the adhesive, flame retardant 30 to 60% by weight, the flame retardant is 35 to 60% by weight of water glass, phosphorus flame retardant 15 to 25% by weight, halogen flame retardant 15 to 25% by weight, It characterized in that it comprises 10 to 15% by weight of inorganic flame retardant.

상기한 목적을 달성하기 위하여 본 발명에 따른 난연 시트지 제조장치는, 종이가 권취되어 종이를 공급하는 제1공급롤러; 알루미늄박지가 권취되어 알루미늄박지를 공급하는 제2공급롤러; 상기 종이의 이면에 난연접착제를 공급하는 난연접착제공급부; 상기 난연접착제공급부를 통해 도포된 난연접착제로 상기 종이와 상기 알루미늄박지와 상호 합지하는 압착롤러; 합지된 상기 종이와 상기 알루미늄박지에 열을 가해 건조하여 난연시트지를 제조하는 건조유닛;을 포함하는 것을 특징으로 한다.In order to achieve the above object, a flame-retardant sheet paper manufacturing apparatus according to the present invention, the first winding roller for winding the paper to supply the paper; A second feed roller for winding the aluminum foil to supply the aluminum foil; A flame-retardant adhesive supply unit for supplying a flame-retardant adhesive on the back surface of the paper; A compression roller which is laminated with the paper and the aluminum foil with a flame retardant adhesive applied through the flame retardant adhesive supply unit; And a drying unit for drying the paper and the aluminum foil by lamination to produce a flame-retardant sheet of paper.

또한, 상기 압착롤러로 상기 종이와 상기 알루미늄박지를 합지하기 전 또는 합지한 후에 상기 종이의 외측면에 난연접착제보조공급부를 통해 공급된 난연접착제를 도포롤러로 1차 코팅하고, 상기 종이의 외측면에 도포된 상기 난연접착제 상에 코팅액공급부에서 공급된 코팅액을 코팅롤러로 2차 코팅하여 코팅층을 형성하는 것을 특징으로 한다.Further, before or after laminating the paper and the aluminum foil with the pressing roller, the first side of the paper is coated with a flame retardant adhesive supplied through a flame retardant adhesive supply unit on the outer side of the paper with an application roller, and the outer side of the paper. The coating solution supplied from the coating liquid supply unit on the flame-retardant adhesive applied to the coating roller to form a coating layer by secondary coating.

또한, 상기 건조유닛을 통과한 상기 난연시트지는 탄공홀형성부에 의해 전후를 관통하는 타ㅓ공홍이 다수개 형성되므로 도포시 공기를 배출하도록 구성되고, 상기 타공홀형성부는, 상기 난연시트지에 타공홀을 관통 형성하는 타공돌기를 구비하는 제1타공롤러; 및 상기 제1타공롤러에 접하여 상기 난연시트지의 타공홀을 관통하여 돌출된 상기 타공돌기를 접촉하는 돌기접촉부를 형성하는 제2타공로러;를 포함하는 것을 특징으로 한다.In addition, the flame-retardant sheet is passed through the drying unit is formed by a plurality of tarpaulin penetrating the front and rear by the hole hole forming portion is configured to discharge the air during application, the perforated hole forming portion, the perforated hole on the flame-retardant sheet paper A first perforated roller having a perforated protrusion formed through the hole; And a second perforated roller in contact with the first perforated roller to form a protrusion contact portion contacting the perforated protrusion protruding through the perforated hole of the flame retardant sheet paper.

또한, 상기 난연접착제는 접착제 40~70 중량%, 난연제 30~60 중량%를 포함하고, 상기 난연제는 물유리 35~60중량%, 인계난연제 15~25중량%, 할로겐계난연제 15~25중량%, 무기계난연제 10~15중량%를 포함하는 것을 특징으로 한다.In addition, the flame retardant adhesive agent 40 to 70% by weight of the adhesive, flame retardant 30 to 60% by weight, the flame retardant is 35 to 60% by weight of water glass, phosphorus flame retardant 15 to 25% by weight, halogen flame retardant 15 to 25% by weight, It characterized in that it comprises 10 to 15% by weight of inorganic flame retardant.

본 발명에 따른 난연 시트지, 그 제조방법 및 그 제조장치은, 알루미늄박지와 종이 사이에 접착제에 난연제가 함유된 난연접착제를 투입하여 합지하도록 하고, 종이의 외측면에 접착제에 난연제가 함유된 난연접착제를 도포하고, 그 외측에 코팅액을 추가 도포하므로 사용시 매끄러운 종이 질감을 느끼면서 화재 발생시 유독가스 발생을 줄여 환경 친화적인 사용을 가능하게 할 수 있다.The flame retardant sheet paper according to the present invention, a method for manufacturing the same, and a device for manufacturing the same are prepared by injecting a flame retardant adhesive containing a flame retardant into an adhesive between an aluminum foil and paper, and laminating a flame retardant adhesive containing a flame retardant in the adhesive on the outer surface of the paper. Since the coating and the coating liquid is further applied to the outside thereof, it is possible to feel the smooth paper texture during use and to reduce the generation of toxic gases in the event of fire, thereby enabling environmentally friendly use.

도 1은 본 발명의 일 실시예에 따른 난연 시트지의 분리 사시도이다.
도 2는 본 발명의 일 실시예에 따른 난연 시트지의 단면도이다
도 3은 본 발명의 일 실시예에 따른 난연 시트지 제조방법의 흐름도이다.
도 4는 본 발명의 일 실시예에 따른 난연 시트지 제조방법의 변형예를 보인 흐름도이다.
도 5는 본 발명의 일 실시예에 따른 난연 시트지 제조장치의 구성도이다.
도 6은 본 발명의 일 실시예에 따른 난연 시트지 제조장치의 변형예를 보인 구성도이다.
도 7은 본 발명의 일 실시예에 따른 난연 시트지 제조장치의 타공홀형성부의 제1타공롤러에서 타공돌기를 상세하게 보인 확대도이다.1 is an exploded perspective view of a flame retardant sheet paper according to an embodiment of the present invention.
2 is a cross-sectional view of a flame retardant sheet paper according to an embodiment of the present invention.
3 is a flowchart of a method of manufacturing a flame-retardant sheet paper according to an embodiment of the present invention.
Figure 4 is a flow chart showing a modification of the method of manufacturing a flame-retardant sheet paper according to an embodiment of the present invention.
5 is a configuration of a flame-retardant sheet paper manufacturing apparatus according to an embodiment of the present invention.
Figure 6 is a block diagram showing a modification of the flame retardant sheet paper manufacturing apparatus according to an embodiment of the present invention.
Figure 7 is an enlarged view showing in detail the perforated projections in the first perforated roller of the perforated hole forming unit of the flame retardant sheet paper manufacturing apparatus according to an embodiment of the present invention.

이하, 첨부된 도면들을 참조하여 본 발명의 일 실시예에 따른 난연 시트지, 그 제조방법 및 그 제조장치를 설명하도록 한다.Hereinafter, a flame retardant sheet paper according to an embodiment of the present invention, a manufacturing method thereof and a manufacturing apparatus thereof will be described with reference to the accompanying drawings.

이 과정에서 도면에 도시된 선들의 두께나 구성요소의 크기 등은 설명의 명료성과 편의상 과장되게 도시되어 있을 수 있다. 또한, 후술되는 용어들은 본 발명에서의 기능을 고려하여 정의된 용어들로서 이는 사용자, 운용자의 의도 또는 관례에 따라 달라질 수 있다. 그러므로, 이러한 용어들에 대한 정의는 본 명세서 전반에 걸친 내용을 토대로 내려져야 할 것이다.In this process, the thickness of the lines or the size of the components shown in the drawings may be exaggerated for clarity and convenience of description. In addition, terms to be described below are terms defined in consideration of functions in the present invention, which may vary according to the intention or convention of a user or an operator. Therefore, definitions of these terms should be made based on the contents throughout the specification.

도 1은 본 발명의 일 실시예에 따른 난연 시트지의 분리 사시도이고, 도 2는 본 발명의 일 실시예에 따른 난연 시트지의 단면도이다. 1 is an exploded perspective view of a flame retardant sheet paper according to an embodiment of the present invention, Figure 2 is a cross-sectional view of the flame retardant sheet paper according to an embodiment of the present invention.

도 3은 본 발명의 일 실시예에 따른 난연 시트지 제조방법의 흐름도이고, 도 4는 본 발명의 일 실시예에 따른 난연 시트지 제조방법의 변형예의 흐름도이다. Figure 3 is a flow chart of a flame retardant sheet paper manufacturing method according to an embodiment of the present invention, Figure 4 is a flow chart of a modification of the flame retardant sheet paper manufacturing method according to an embodiment of the present invention.

도 5는 본 발명의 일 실시예에 따른 난연 시트지 제조장치의 구성도이고, 도 6은 본 발명의 일 실시예에 따른 난연 시트지 제조장치의 변형예의 구성도이며, 도 7은 본 발명의 일 실시예에 따른 난연 시트지 제조장치의 타공홀형성부의 제1타공롤러에서 타공돌기를 상세하게 보인 확대도이다.5 is a block diagram of a flame retardant sheet paper manufacturing apparatus according to an embodiment of the present invention, Figure 6 is a block diagram of a modification of the flame retardant sheet paper manufacturing apparatus according to an embodiment of the present invention, Figure 7 is an embodiment of the present invention It is an enlarged view showing the perforation protrusion in detail in the 1st perforation roller of the perforation hole formation part of the flame-retardant sheet paper manufacturing apparatus which concerns on the example.

도 1 내지 도 2를 참조하면, 본 발명의 일 실시예에 따른 난연 시트지(1)는, 알루미늄박지(10), 종이(20), 난연접착제(30) 및 코팅층(40)을 포함한다.1 to 2, the flame retardant sheet paper 1 according to an embodiment of the present invention includes an aluminum foil 10, a paper 20, a flame retardant adhesive 30, and a coating layer 40.

알루미늄박지(10)는 알루미늄을 얇게 펼쳐서 만든 구성으로서, 알루미늄 호일(hoil)이라고도 부른다.The aluminum foil 10 is made of thin aluminum and is also called an aluminum foil.

알루미늄박지(10)는 연성과 전성이 우수한 금속재질로서 얇게 펼치더라도 쉽게 찢어지지 않는 특성을 지닌다.The aluminum foil 10 is a metal material having excellent ductility and malleability, and has a property of not being easily torn even when thinly spread.

알루미늄박지(10)는 비록 얇게 펼쳐지지만 금속재이므로 쉽게 불에 타지 않는 특성을 가지므로 난연재질로 적용할 필요성이 있다.Aluminum foil 10, although thinly spread, but because it is a metal material has a property that does not easily burn, there is a need to apply as a flame retardant material.

종이(20)는 알루미늄박지(10)의 일측면에 구비되는 구성으로서, 두껍고 찔긴 재질의 종이를 적용하는 것이 바람직하다.Paper 20 is a configuration provided on one side of the aluminum foil 10, it is preferable to apply a thick, sticking paper.

종이(20)는 시중에 유통되는 종이 중에서 어느 하나의 종류를 선택하여 사용할 수 있으나, 질기고 두꺼운 종이류를 선택하여 사용하는 것이 바람직하다.The paper 20 may be used by selecting any one type of paper on the market, but it is preferable to use a tough and thick paper.

난연접착제(30)는 알루미늄박지(10)와 종이(20) 사이에 구비되어 알루미늄박지(10)와 종이(20)를 상호 부착하도록 접착제에 난연제를 포함하여 이루어지는 불에 잘 견디는 난연기능을 지닌 접착 구성이다.The flame retardant adhesive 30 is provided between the aluminum foil 10 and the paper 20 to adhere the aluminum foil 10 and the paper 20 to each other, the adhesive having a fire-resistant flame retardant function comprising a flame retardant in the adhesive. Configuration.

난연접착제(30)는 종이(20)의 이면에 우선 도포된 후, 알루미늄박지(10)를 공급하여 후술하는 압착롤러(80)를 이용하여 압착시켜 합지할 수 있다.The flame-retardant adhesive 30 may be first coated on the back surface of the paper 20, and then may be laminated by supplying the aluminum foil 10 and compressing it by using the compression roller 80 to be described later.

코팅층(40)은 종이(20)의 외측면에 도포되는 구성이다. The coating layer 40 is a composition applied to the outer side of the paper 20.

코팅층(40)은 종이(20) 표면을 부드럽고 매끄럽게 하는 역할을 수행하면서, 불에 잘 견디게 하는 난연 특성을 증가시키는 역할을 수행한다.The coating layer 40 plays a role of smoothing and smoothing the surface of the paper 20, and serves to increase the flame retardant property of resisting fire well.

코팅층(40)은 에틸렌 비닐아세테이트 혼성 중합체(EVA 혼성 중합체)를 사용하는 것이 바랍직하다.The coating layer 40 preferably uses an ethylene vinyl acetate interpolymer (EVA interpolymer).

에틸렌 비닐아세테이트 혼성 중합체(EVA 혼성 중합체)는 충격에 매우 저항적이고 인장 균열에 매우 저항적이며, 종이(20)를 코팅하고 염화폴리비닐의 내충격성을 향상시키는 데 사용된다.Ethylene vinylacetate interpolymers (EVA interpolymers) are very resistant to impact and very resistant to tensile cracking, and are used to coat the paper 20 and to improve the impact resistance of polyvinyl chloride.

종이(20)의 외측면과 코팅층(40) 사이에는 난연접착제(30)가 더 포함될 수 있다.The flame retardant adhesive 30 may be further included between the outer surface of the paper 20 and the coating layer 40.

종이(20)의 외측면과 코팅층(40) 사이에 도포된 난연접착제(30)는 접착성분과 난연성분을 가지므로 화재시 코팅층(40)에서 차단하지 못하는 화염을 난연접착제(30)에서 차단하므로 종이(20)에 화염이 전파되어 불에 타는 것을 방지하는 역할을 수행한다.Since the flame retardant adhesive 30 applied between the outer surface of the paper 20 and the coating layer 40 has an adhesive component and a flame retardant component, since the flame prevents the flame from being blocked by the coating layer 40 in case of fire, the flame retardant adhesive 30 is blocked. Fire spreads to the paper 20 serves to prevent burning.

난연접착제(30)는 접착제 40~70 중량%, 난연제 30~60 중량%를 포함할 수 있다. 더욱더 바람직하게는 난연접착제(30)는 접착제 50~60 중량%, 난연제 40~50 중량%를 포함하는 것이 좋다.Flame retardant adhesive 30 may include an adhesive 40 to 70% by weight, flame retardant 30 to 60% by weight. Even more preferably, the flame retardant adhesive 30 may include 50 to 60 wt% of the adhesive and 40 to 50 wt% of the flame retardant.

접착제는 대두접착제(Soy Adhesive)를 포함할 수 있다.The adhesive may comprise Soy Adhesive.

대두접착제(Soy Adhesive)는 접착기능뿐만 아니라, 난연기능도 가지고 있다.Soy Adhesive has a flame retardant function as well as an adhesive function.

대두접착제(Soy Adhesive)는 콩으로부터 추출하여 사용하는 것으로서 섭취 가능한 식품으로부터 취득하므로 친환경적이고, 불에 탈 때 유독가스의 배출을 최소화할 수 있어 최근에 접착제로 각광받는 소재이다.Soy Adhesive is extracted from soybeans and is used in foods to consume. Soy Adhesive is eco-friendly and minimizes the emission of toxic gases when burning.

난연제는 물유리, 인계난연제(Phosphrous-based flame retardants), 할로겐계난연제(Halogen-based flame retardants), 무기계난연제(inoragnic flame retardants) 중 어느 하나 이상을 포함할 수 있다.Flame retardants may include any one or more of water glass, Phosphrous-based flame retardants, halogen-based flame retardants, and inorganic flame retardants.

난연제는 물유리 35~60중량%, 인계난연제 15~25중량%, 할로겐계난연제 15~25중량%, 무기계난연제 10~15중량%를 포함할 수 있다.The flame retardant may include water glass 35 to 60% by weight, phosphorus flame retardant 15 to 25% by weight, halogen flame retardant 15 to 25% by weight, inorganic flame retardant 10 to 15% by weight.

물유리는 규산나트륨, 규산칼륨, 규산소다칼륨과 같은 한 종류 이상의 규산연물질 수용액으로서, 규산염물질의 함량이 2~90중량%인 것을 특징으로 한다. Water glass is an aqueous solution of at least one type of soft silicate material such as sodium silicate, potassium silicate, potassium potassium silicate, and is characterized in that the content of silicate material is 2 to 90% by weight.

인계난연제는 적인(Red phosphate)을 포함할 수 있다.Phosphorus-based flame retardants may include red phosphate.

무기계난연제는 수산화알루미늄(Aluminum hydroxide), 규사 중 적어도 어느 하나를 포함할 수 있다.The inorganic flame retardant may include at least one of aluminum hydroxide and silica sand.

한편, 난연시트지(1)는 후술하는 타공홀형성부(150)에 의해 일측에서 타측으로 관통되는 타공홀(2)이 다수개 형성되므로 피부착물에 부착시 공기의 배출을 도와줄 수 있다. 물론, 난연시트지(1)는 타공홀(2)이 형성되지 않고 사용될 수도 있다.On the other hand, since the flame-retardant sheet 1 is formed by a plurality of perforation holes (2) penetrating from one side to the other side by the perforation hole forming unit 150 to be described later can help the discharge of air when attached to the skin complex. Of course, the flame retardant sheet 1 may be used without the perforation hole 2 formed.

그러므로, 난연시트지(10)는 불연 내외장재로서, 건축물의 벽면 또는 천장 등의 피부착물에 부착시, 접착부위에서 공기층이 발생되더라도, 타공홀(2)을 통해 배출됨으로써, 난연시트지(1)는 피부착물에 틈새없이 견고하게 부착될 수 있다. 타공홀형성부(150)의 세부 구성은 아래에 기재된 사항을 참조 및 적용하도록 한다.Therefore, the flame-retardant sheet paper 10 is a non-flammable interior and exterior materials, and when attached to a skin complex such as a wall or a ceiling of a building, even if an air layer is generated at the adhesive part, the flame-retardant sheet paper 1 is discharged through the perforated hole 2, thereby the skin-deposited sheet 1 is It can be firmly attached without gaps. Detailed configuration of the perforation hole forming unit 150 to refer to and apply the items described below.

도 3을 참조하면, 본 발명의 일 실시예에 따른 난연 시트지 제조방법은, 종이(20)와 알루미늄박지(10)를 준비하는 단계(S10)와, 종이(10)의 이면에 난연접착제(30)를 도포하는 단계(S20)와, 종이(20)의 이면에 도포된 난연접착제(30)에 알루미늄박지(10)를 접착하여 합지하는 단계(S30)와, 합지된 종이 외측면에 난연접착제(30)를 도포하는 단계(S40)와, 합지를 건조유닛(130)에서 건조하여 난연시트지(1)를 제조하는 단계(S60)를 포함한다.Referring to Figure 3, the flame-retardant sheet paper manufacturing method according to an embodiment of the present invention, the step of preparing a paper 20 and aluminum foil 10 (S10), the flame-retardant adhesive 30 on the back surface of the paper 10 ) (S20) and the step of adhering the aluminum foil (10) to the flame retardant adhesive 30 applied to the back surface of the paper 20 (S30) and the flame-retardant adhesive on the laminated paper outer surface ( 30) applying a step (S40), and drying the paper in the drying unit 130 includes a step (S60) for producing a flame-retardant sheet (1).

도 4를 참조하면, 본 발명의 일 실시예에 따른 난연 시트지 제조방법의 변형예는, 종이(20)와 알루미늄박지(10)를 준비하는 단계(S10)와, 종이(20)의 외측면에 난연접착제(30)를 도포하고 건조하는 단계(S40)와, 종이(20)의 이면에 난연접착제(30)를 도포하는 단계(S20)와, 종이(20)의 이면에 도포된 난연접착제(30)에 알루미늄박지(10)를 접착하여 합지하는 단계(S30)와, 합지를 건조유닛(130)에서 건조하여 난연시트지(1)를 제조하는 단계(S60)를 포함한다.Referring to Figure 4, a modification of the flame-retardant sheet paper manufacturing method according to an embodiment of the present invention, the step of preparing the paper 20 and the aluminum foil 10 (S10) and the outer surface of the paper 20 Step (S40) of applying and drying the flame-retardant adhesive 30, the step (S20) of applying the flame-retardant adhesive 30 on the back surface of the paper 20, and the flame-retardant adhesive 30 applied to the back surface of the paper 20 And bonding the aluminum foil 10 to the laminate (S30), and drying the laminate in the drying unit 130 to produce a flame retardant sheet 1 (S60).

한편, 종이(20)의 외측면에 도포된 난연접착제(30) 상에 코팅층(30)을 도포하는 단계(S50)를 더 포함할 수 있다.On the other hand, it may further comprise the step (S50) of applying a coating layer 30 on the flame-retardant adhesive 30 applied to the outer surface of the paper 20.

난연접착제(30)는 알루미늄박지(10)와 종이(20) 사이에 구비되어 알루미늄박지(10)와 종이(20)를 상호 부착하도록 접착제에 난연제를 포함하여 이루어지는 불에 잘 견디는 난연기능을 지닌 접착 구성이다.The flame retardant adhesive 30 is provided between the aluminum foil 10 and the paper 20 to adhere the aluminum foil 10 and the paper 20 to each other, the adhesive having a fire-resistant flame retardant function comprising a flame retardant in the adhesive. Configuration.

난연접착제(30)는 종이(20)의 이면에 우선 도포된 후, 알루미늄박지(10)를 공급하여 후술하는 압착롤러(80)를 이용하여 압착시켜 합지할 수 있다.The flame-retardant adhesive 30 may be first coated on the back surface of the paper 20, and then may be laminated by supplying the aluminum foil 10 and compressing it by using the compression roller 80 to be described later.

코팅층(40)은 종이(20)의 외측면에 도포되는 구성이다. The coating layer 40 is a composition applied to the outer side of the paper 20.

코팅층(40)은 종이(20) 표면을 부드럽고 매끄럽게 하는 역할을 수행하면서, 불에 잘 견디게 하는 난연 특성을 증가시키는 역할을 수행한다.The coating layer 40 plays a role of smoothing and smoothing the surface of the paper 20, and serves to increase the flame retardant property of resisting fire well.

코팅층(40)은 에틸렌 비닐아세테이트 혼성 중합체(EVA 혼성 중합체)를 사용하는 것이 바랍직하다.The coating layer 40 preferably uses an ethylene vinyl acetate interpolymer (EVA interpolymer).

에틸렌 비닐아세테이트 혼성 중합체(EVA 혼성 중합체)는 충격에 매우 저항적이고 인장 균열에 매우 저항적이며, 종이(20)를 코팅하고 염화폴리비닐의 내충격성을 향상시키는 데 사용된다.Ethylene vinylacetate interpolymers (EVA interpolymers) are very resistant to impact and very resistant to tensile cracking, and are used to coat the paper 20 and to improve the impact resistance of polyvinyl chloride.

종이(20)의 외측면과 코팅층(40) 사이에는 난연접착제(30)가 더 포함될 수 있다.The flame retardant adhesive 30 may be further included between the outer surface of the paper 20 and the coating layer 40.

단계 "S30"에서, 종이(20)의 외측면과 코팅층(40) 사이에 도포된 난연접착제(30)는 접착성분과 난연성분을 가지므로 화재시 코팅층(40)에서 차단하지 못하는 화염을 난연접착제(30)에서 차단하므로 종이(20)에 화염이 전파되어 불에 타는 것을 방지하는 역할을 수행한다.In step "S30", the flame retardant adhesive 30 applied between the outer surface of the paper 20 and the coating layer 40 has an adhesive component and a flame retardant component, so the flame retardant adhesive does not block in the coating layer 40 in case of fire. Block 30 so that the flame propagates to the paper 20 serves to prevent burning.

난연접착제(30)는 접착제 40~70 중량%, 난연제 30~60 중량%를 포함할 수 있다. 더욱더 바람직하게는 난연접착제(30)는 접착제 50~60 중량%, 난연제 40~50 중량%를 포함하는 것이 좋다.Flame retardant adhesive 30 may include an adhesive 40 to 70% by weight, flame retardant 30 to 60% by weight. Even more preferably, the flame retardant adhesive 30 may include 50 to 60 wt% of the adhesive and 40 to 50 wt% of the flame retardant.

접착제는 대두접착제(Soy Adhesive)를 포함할 수 있다.The adhesive may comprise Soy Adhesive.

대두접착제(Soy Adhesive)는 접착기능뿐만 아니라, 난연기능도 가지고 있다.Soy Adhesive has a flame retardant function as well as an adhesive function.

대두접착제(Soy Adhesive)는 콩으로부터 추출하여 사용하는 것으로서 섭취 가능한 식품으로부터 취득하므로 친환경적이고, 불에 탈 때 유독가스의 배출을 최소화할 수 있어 최근에 접착제로 각광받는 소재이다.Soy Adhesive is extracted from soybeans and is used in foods to consume. Soy Adhesive is eco-friendly and minimizes the emission of toxic gases when burning.

난연제는 물유리, 인계난연제(Phosphrous-based flame retardants), 할로겐계난연제(Halogen-based flame retardants), 무기계난연제(inoragnic flame retardants) 중 어느 하나 이상을 포함할 수 있다.Flame retardants may include any one or more of water glass, Phosphrous-based flame retardants, halogen-based flame retardants, and inorganic flame retardants.

난연제는 물유리 35~60중량%, 인계난연제 15~25중량%, 할로겐계난연제 15~25중량%, 무기계난연제 10~15중량%를 포함할 수 있다.The flame retardant may include water glass 35 to 60% by weight, phosphorus flame retardant 15 to 25% by weight, halogen flame retardant 15 to 25% by weight, inorganic flame retardant 10 to 15% by weight.

물유리는 규산나트륨, 규산칼륨, 규산소다칼륨과 같은 한 종류 이상의 규산연물질 수용액으로서, 규산염물질의 함량이 2~90중량%인 것을 특징으로 한다. Water glass is an aqueous solution of at least one type of soft silicate material such as sodium silicate, potassium silicate, potassium potassium silicate, and is characterized in that the content of silicate material is 2 to 90% by weight.

인계난연제는 적인(Red phosphate)을 포함할 수 있다.Phosphorus-based flame retardants may include red phosphate.

무기계난연제는 수산화알루미늄(Aluminum hydroxide), 규사 중 적어도 어느 하나를 포함할 수 있다.The inorganic flame retardant may include at least one of aluminum hydroxide and silica sand.

또한, 본 발명의 일 실시예에 따른 난연 시트지 제조방법은, 건조유닛(140)에서 난연시트지(1)를 건조한 후, 타공홀형성부(150)를 이용하여 난연시트지(1)를 관통하는 다수개의 타공홀(2)을 형성하는 단계(S70)를 더 포함할 수 있다.In addition, the flame-retardant sheet paper manufacturing method according to an embodiment of the present invention, after drying the flame-retardant sheet paper 1 in the drying unit 140, a plurality of penetrating through the flame-retardant sheet paper 1 using the perforated hole forming unit 150 It may further comprise the step (S70) of forming the two perforation holes (2).

단계 "S70"은 건조유닛(140)을 통과하여 배출되는 난연시트지(1)가 권취롤러(140)에 리와인드(권취) 되기 전에 난연시트지(1)에 가로 및 세로방향으로 타공홀형성부(150)를 이용하여 다수개의 타공홀(2)을 형성하므로 난연시트지(1)를 벽체 등의 피부착물에 부착할 때, 공기가 잘 배출되도록 하여 난연시트지(1)가 피부착물에서 들뜨는 현상을 방지하도록 해준다.Step "S70" is a perforated hole forming unit 150 in the horizontal and vertical direction on the flame retardant sheet (1) before the flame retardant sheet 1 discharged through the drying unit 140 is rewinded (winding) to the take-up roller 140 Since a plurality of perforated holes (2) are formed using a), when the flame retardant sheet (1) is attached to a skin deposit such as a wall, air is well discharged to prevent the flame retardant sheet (1) from being lifted from the skin deposit. Do it.

도 5 내지 도 7을 참조하면, 타공홀형성부(150)는, 난연시트지(1)에 타공홀(2)을 관통 형성하는 타공돌기(153)를 구비하는 제1타공롤러(152)와, 제1타공롤러(152)에 접하여 난연시트지(1)의 타공홀(2)을 관통하여 돌출된 타공돌기(153)가 접촉되는 돌기접촉부(155)를 형성하는 제2타공롤러(154)를 포함할 수 있다.5 to 7, the perforated hole forming unit 150 includes a first perforated roller 152 having a perforated protrusion 153 formed to penetrate the perforated hole 2 in the flame retardant sheet 1, And a second perforated roller 154 which contacts the first perforated roller 152 to form a protrusion contact portion 155 to contact the perforated protrusion 153 protruding through the perforated hole 2 of the flame retardant sheet 1. can do.

돌기접촉부(155)는 타공돌기(153)의 전체 길이 또는 일부 길이가 수용되는 깊이를 갖도록 구성될 수 있다. 이 경우, 돌기접촉부(155)는 도 5 및 도 6에 도시된 바와 같이, 타공돌기(153)의 직경에 대응하는 원형홈으로 형성된다. The protrusion contact part 155 may be configured to have a depth in which the entire length or the partial length of the perforation protrusion 153 is accommodated. In this case, the protrusion contact portion 155 is formed as a circular groove corresponding to the diameter of the perforation protrusion 153, as shown in Figs.

또한, 돌기접촉부(155)는 칼날부(156)의 전체 길이 또는 일부 길이가 수용되는 깊이를 갖도록 구성될 수 있다. 이 경우, 돌기접촉부(155)는 도 7에 도시된 바와 같이, 칼날부(156) 만 삽입되도록 링 형태의 고리홈으로 형성되며, 돌기접촉부(155)의 단면은 칼날부(156)의 단면에 대응하도록 삼각형상의 홈으로 형성될 수 있다.In addition, the protrusion contact portion 155 may be configured to have a depth in which the entire length or a partial length of the blade portion 156 is accommodated. In this case, the protrusion contact portion 155 is formed as a ring-shaped ring groove so that only the blade portion 156 is inserted, as shown in Figure 7, the cross section of the protrusion contact portion 155 to the cross section of the blade portion 156 It may be formed as a triangular groove to correspond.

제1타공롤러(152)는 둘레면에 가로 및 세로방향으로 다수개의 타공돌기(153)를 설정길이로 돌출 형성된다.The first perforated roller 152 is formed to protrude a plurality of perforation protrusions 153 in a set length in the horizontal and vertical direction on the circumferential surface.

제2타공롤러(154)는 타공돌기(153)가 돌기접촉부(155)에 대응되어 끼워지도록 가로 및 세로방향으로 설징깊이로 함몰 형성된다.The second perforation roller 154 is formed to be recessed deeply in the horizontal and vertical directions so that the perforation protrusion 153 is fitted to correspond to the protrusion contact portion 155.

난연시트지(1)는 제1,제2타공롤러(152)(154) 사이에 접하여 밀착 이동되고, 제1타공롤러(152)의 타공돌기(153)에 의해 타공홀(2)이 타공 형성되면서 이동하여 권취롤러(140)에 권취될 수 있다.The flame-retardant sheet paper 1 is brought into close contact with the first and second perforated rollers 152 and 154, and the perforated hole 2 is perforated by the perforated protrusion 153 of the first perforated roller 152. It may be wound around the winding roller 140 by moving.

도 7에 도시된 바와 같이, 타공돌기(153)는 단부에 칼날부(156)를 구비한다. 타공돌기(153)는 칼날부(156)의 중심으로 함몰홈부(157)가 형성되며, 함몰홈부(157)는 칼날부(156)에서 절단된 난연시트지(1)의 제거부위를 수용했다가 제1타공롤러(152)가 회전하면서 분리 제거되도록 해준다.As shown in FIG. 7, the perforation protrusion 153 has a blade portion 156 at an end thereof. The perforated protrusion 153 has a recessed groove 157 formed at the center of the blade 156, and the recessed groove 157 accommodates the removal portion of the flame-retardant sheet paper 1 cut at the blade 156. 1 punching roller 152 is rotated to be removed to remove.

칼날부(156)의 외주면은 길이방향으로 직선으로 형성되고, 칼날부(156)의 내주면은 단부로 갈수록 점차적으로 협소해지면서 날카롭도록 경사지게 형성된다.The outer circumferential surface of the blade portion 156 is formed in a straight line in the longitudinal direction, and the inner circumferential surface of the blade portion 156 is formed to be sharply inclined while gradually narrowing toward the end portion.

도 5 내지 도 7을 참조하면, 본 발명의 일 실시예에 따른 난연 시트지 제조장치는, 종이(20)가 권취되어 종이(20)를 공급하는 제1공급롤러(50)와, 알루미늄박지(10)가 권취되어 알루미늄박지(10)를 공급하는 제2공급롤러(60)와, 종이(20)의 이면에 난연접착제(30)를 공급하는 난연접착제공급부(70)와, 난연접착제공급부(70)를 통해 도포된 난연잡착제(30)로 종이(20)와 알루미늄박지(10)를 상호 압착하여 합지하는 압착롤러(80)와, 합지된 종이(20)와 알루미늄박지(10)에 열을 가해 건조하여 난연시트지(1)를 제조하는 건조유닛(130)을 포함한다.5 to 7, a flame retardant sheet paper manufacturing apparatus according to an embodiment of the present invention, the paper 20 is wound around the first supply roller 50 to supply the paper 20, aluminum foil 10 ) Is wound around the second supply roller 60 for supplying the aluminum foil 10, the flame retardant adhesive supply unit 70 for supplying the flame retardant adhesive 30 to the back surface of the paper 20, and the flame retardant adhesive supply unit 70. The paper 20 and the aluminum foil 10 are press-bonded to each other by laminating the paper 20 and the aluminum foil 10 with the flame-retardant adhesive applied through the coating, and the heat is applied to the laminated paper 20 and the aluminum foil 10. It comprises a drying unit 130 to dry to produce a flame-retardant sheet (1).

건조유닛(130)에서 이송된 난연시트지(1)는 권취롤러(140)에 감겨서 제품으로 판매된다.The flame retardant sheet 1 transferred from the drying unit 130 is wound on a winding roller 140 and sold as a product.

한편, 압착롤러(80)로 종이(20)와 알루미늄박지(10)를 합지하기 전 또는 합지한 후에 종이(10)의 외측면에 난연접착제보조공급부(90)를 통해 공급된 난연접착제(30)를 도포롤러(100)로 1차 코팅한다.Meanwhile, the flame-retardant adhesive 30 supplied through the flame-retardant adhesive auxiliary supply unit 90 to the outer surface of the paper 10 before or after laminating the paper 20 and the aluminum foil 10 with the pressing roller 80. Is first coated with a coating roller (100).

연이어, 종이(20)의 외측면에 도포된 난연접착제(30) 상에 코팅액공급부(110)에서 공급된 코팅액을 코팅롤러(120)로 2차 코팅하여 코팅층(40)을 형성할 수 있다.Subsequently, the coating liquid supplied from the coating liquid supply unit 110 on the flame-retardant adhesive 30 applied to the outer surface of the paper 20 may be secondarily coated with the coating roller 120 to form the coating layer 40.

난연접착제공급부(70)는 난연접착제 수용액을 저장하도록 상측이 개방된 저장조(71)과, 저장조(71) 상에 회전 가능하게 설치되어 난연접착제 수용액을 둘레에 묻혀서 이송하는 종이(20)의 이면에 도포하는 점착롤러(72)를 포함한다.The flame-retardant adhesive supply unit 70 is provided on the back side of the paper 20 to which the upper side is opened so as to store the flame-retardant adhesive solution, and is rotatably installed on the storage tank 71 to bury the flame-retardant adhesive solution around and transport it. The adhesive roller 72 to apply is included.

난연접착제보조공급부(90)는 난연접착제 수용액을 저장하도록 상측이 개방되고, 도포롤러(100) 하측에 구비된 저장조이다.The flame-retardant adhesive auxiliary supply unit 90 is an upper side open to store the flame-retardant adhesive solution, and is a storage tank provided below the coating roller 100.

코팅액공급부(110)는 코팅액을 저장하도록 상측이 개방되고, 코팅롤러(120) 하측에 구비된 저장조이다.The coating liquid supply unit 110 is a storage tank provided at the upper side to store the coating liquid and provided below the coating roller 120.

건조유닛(130)은 난연시트지(10)를 터널부위로 통과시키면서 간조유닛(130) 내부에 구비된 히팅기구를 이용하여 난연시트지(10)에 잔류된 수분을 증발시켜 건조하도록 한다.The drying unit 130 allows the flame retardant sheet 10 to pass through the tunnel portion to evaporate moisture remaining in the flame retardant sheet 10 using a heating mechanism provided in the low water unit 130.

난연시트지910)는 히팅롤러(Heating roller)를 이용하여 합지시키면서 건조시킬 수도 있다.Flame retardant sheet 910 may be dried while laminating using a heating roller (Heating roller).

난연접착제(30)는 알루미늄박지(10)와 종이(20) 사이에 구비되어 알루미늄박지(10)와 종이(20)를 상호 부착하도록 접착제에 난연제를 포함하여 이루어지는 불에 잘 견디는 난연기능을 지닌 접착 구성이다.The flame retardant adhesive 30 is provided between the aluminum foil 10 and the paper 20 to adhere the aluminum foil 10 and the paper 20 to each other, the adhesive having a fire-resistant flame retardant function comprising a flame retardant in the adhesive. Configuration.

난연접착제(30)는 종이(20)의 이면에 우선 도포된 후, 알루미늄박지(10)를 공급하여 후술하는 압착롤러(80)를 이용하여 압착시켜 합지할 수 있다.The flame-retardant adhesive 30 may be first coated on the back surface of the paper 20, and then may be laminated by supplying the aluminum foil 10 and compressing it by using the compression roller 80 to be described later.

코팅층(40)은 종이(20)의 외측면에 도포되는 구성이다. The coating layer 40 is a composition applied to the outer side of the paper 20.

코팅층(40)은 종이(20) 표면을 부드럽고 매끄럽게 하는 역할을 수행하면서, 불에 잘 견디게 하는 난연 특성을 증가시키는 역할을 수행한다.The coating layer 40 plays a role of smoothing and smoothing the surface of the paper 20, and serves to increase the flame retardant property of resisting fire well.

코팅층(40)은 에틸렌 비닐아세테이트 혼성 중합체(EVA 혼성 중합체)를 사용하는 것이 바랍직하다.The coating layer 40 preferably uses an ethylene vinyl acetate interpolymer (EVA interpolymer).

에틸렌 비닐아세테이트 혼성 중합체(EVA 혼성 중합체)는 충격에 매우 저항적이고 인장 균열에 매우 저항적이며, 종이(20)를 코팅하고 염화폴리비닐의 내충격성을 향상시키는 데 사용된다.Ethylene vinylacetate interpolymers (EVA interpolymers) are very resistant to impact and very resistant to tensile cracking, and are used to coat the paper 20 and to improve the impact resistance of polyvinyl chloride.

종이(20)의 외측면과 코팅층(40) 사이에는 난연접착제(30)가 더 포함될 수 있다.The flame retardant adhesive 30 may be further included between the outer surface of the paper 20 and the coating layer 40.

종이(20)의 외측면과 코팅층(40) 사이에 도포된 난연접착제(30)는 접착성분과 난연성분을 가지므로 화재시 코팅층(40)에서 차단하지 못하는 화염을 난연접착제(30)에서 차단하므로 종이(20)에 화염이 전파되어 불에 타는 것을 방지하는 역할을 수행한다.Since the flame retardant adhesive 30 applied between the outer surface of the paper 20 and the coating layer 40 has an adhesive component and a flame retardant component, since the flame prevents the flame from being blocked by the coating layer 40 in case of fire, the flame retardant adhesive 30 is blocked. Fire spreads to the paper 20 serves to prevent burning.

난연접착제(30)는 접착제 40~70 중량%, 난연제 30~60 중량%를 포함할 수 있다. 더욱더 바람직하게는 난연접착제(30)는 접착제 50~60 중량%, 난연제 40~50 중량%를 포함하는 것이 좋다.Flame retardant adhesive 30 may include an adhesive 40 to 70% by weight, flame retardant 30 to 60% by weight. Even more preferably, the flame retardant adhesive 30 may include 50 to 60 wt% of the adhesive and 40 to 50 wt% of the flame retardant.

접착제는 대두접착제(Soy Adhesive)를 포함할 수 있다.The adhesive may comprise Soy Adhesive.

대두접착제(Soy Adhesive)는 접착기능뿐만 아니라, 난연기능도 가지고 있다.Soy Adhesive has a flame retardant function as well as an adhesive function.

대두접착제(Soy Adhesive)는 콩으로부터 추출하여 사용하는 것으로서 섭취 가능한 식품으로부터 취득하므로 친환경적이고, 불에 탈 때 유독가스의 배출을 최소화할 수 있어 최근에 접착제로 각광받는 소재이다.Soy Adhesive is extracted from soybeans and is used in foods to consume. Soy Adhesive is eco-friendly and minimizes the emission of toxic gases when burning.

난연제는 물유리, 인계난연제(Phosphrous-based flame retardants), 할로겐계난연제(Halogen-based flame retardants), 무기계난연제(inoragnic flame retardants) 중 어느 하나 이상을 포함할 수 있다.Flame retardants may include any one or more of water glass, Phosphrous-based flame retardants, halogen-based flame retardants, and inorganic flame retardants.

난연제는 물유리 35~60중량%, 인계난연제 15~25중량%, 할로겐계난연제 15~25중량%, 무기계난연제 10~15중량%를 포함할 수 있다.The flame retardant may include water glass 35 to 60% by weight, phosphorus flame retardant 15 to 25% by weight, halogen flame retardant 15 to 25% by weight, inorganic flame retardant 10 to 15% by weight.

물유리는 규산나트륨, 규산칼륨, 규산소다칼륨과 같은 한 종류 이상의 규산연물질 수용액으로서, 규산염물질의 함량이 2~90중량%인 것을 특징으로 한다. Water glass is an aqueous solution of at least one type of soft silicate material such as sodium silicate, potassium silicate, potassium potassium silicate, and is characterized in that the content of silicate material is 2 to 90% by weight.

인계난연제는 적인(Red phosphate)을 포함할 수 있다.Phosphorus-based flame retardants may include red phosphate.

무기계난연제는 수산화알루미늄(Aluminum hydroxide), 규사 중 적어도 어느 하나를 포함할 수 있다.The inorganic flame retardant may include at least one of aluminum hydroxide and silica sand.

한편, 건조유닛(140)을 통과한 난연시트지(1)는 타공홀형성부(150)에 의해 전후로 관통되는 타공홀(2)이 다수개 형성되어 피부착물에 부착시 공기의 배출을 도와줄 수 있다.On the other hand, the flame-retardant sheet (1) passed through the drying unit 140 is formed with a plurality of perforation holes (2) which are penetrated back and forth by the perforation hole forming unit 150 can help the discharge of air when attached to the skin deposits have.

이와같이, 난연시트지(10)는 건축물의 불연 내외장재로서, 벽면 또는 천장 등의 피부착물에 부착시, 접착부위에서 공기층이 발생되더라도, 타공홀(2)을 통해 외부로 배출됨으로써, 난연시트지(1)는 피부착물에 틈새없이 견고하게 부착될 수 있다.As described above, the flame-retardant sheet paper 10 is a non-flammable interior and exterior material of a building, and when attached to a skin surface such as a wall or a ceiling, even if an air layer is generated at the adhesive part, the flame-retardant sheet paper 1 is discharged to the outside through the perforation hole 2, It can be firmly attached to the skin complex without gaps.

도 5 내지 도 7을 참조하면, 타공홀형성부(150)는, 난연시트지(1)에 타공홀(2)을 관통 형성하는 타공돌기(153)를 구비하는 제1타공롤러(152)와, 제1타공롤러(152)에 접하여 난연시트지(1)의 타공홀(2)을 관통하여 돌출된 타공돌기(153)가 접촉되는 돌기접촉부(155)를 형성하는 제2타공롤러(154)를 포함할 수 있다.5 to 7, the perforated hole forming unit 150 includes a first perforated roller 152 having a perforated protrusion 153 formed to penetrate the perforated hole 2 in the flame retardant sheet 1, And a second perforated roller 154 which contacts the first perforated roller 152 to form a protrusion contact portion 155 to contact the perforated protrusion 153 protruding through the perforated hole 2 of the flame retardant sheet 1. can do.

돌기접촉부(155)는 타공돌기(153)의 전체 길이 또는 일부 길이가 수용되는 깊이를 갖도록 구성될 수 있다. 이 경우, 돌기접촉부(155)는 도 5 및 도 6에 도시된 바와 같이, 타공돌기(153)의 직경에 대응하는 원형홈으로 형성된다. The protrusion contact part 155 may be configured to have a depth in which the entire length or the partial length of the perforation protrusion 153 is accommodated. In this case, the protrusion contact portion 155 is formed as a circular groove corresponding to the diameter of the perforation protrusion 153, as shown in Figs.

또한, 돌기접촉부(155)는 칼날부(156)의 전체 길이 또는 일부 길이가 수용되는 깊이를 갖도록 구성될 수 있다. 이 경우, 돌기접촉부(155)는 도 7에 도시된 바와 같이, 칼날부(156) 만 삽입되도록 링 형태의 고리홈으로 형성되며, 돌기접촉부(155)의 단면은 칼날부(156)의 단면에 대응하도록 삼각형상의 홈으로 형성될 수 있다.In addition, the protrusion contact portion 155 may be configured to have a depth in which the entire length or a partial length of the blade portion 156 is accommodated. In this case, the protrusion contact portion 155 is formed as a ring-shaped ring groove so that only the blade portion 156 is inserted, as shown in Figure 7, the cross section of the protrusion contact portion 155 to the cross section of the blade portion 156 It may be formed as a triangular groove to correspond.

제1타공롤러(152)는 둘레면에 가로 및 세로방향으로 다수개의 타공돌기(153)를 설정길이로 돌출 형성된다.The first perforated roller 152 is formed to protrude a plurality of perforation protrusions 153 in a set length in the horizontal and vertical direction on the circumferential surface.

제2타공롤러(154)는 타공돌기(153)가 돌기접촉부(155)에 대응되어 끼워지도록 가로 및 세로방향으로 설징깊이로 함몰 형성된다.The second perforation roller 154 is formed to be recessed deeply in the horizontal and vertical directions so that the perforation protrusion 153 is fitted to correspond to the protrusion contact portion 155.

난연시트지(1)는 제1,제2타공롤러(152)(154) 사이에 접하여 밀착 이동되고, 제1타공롤러(152)의 타공돌기(153)에 의해 타공홀(2)이 타공 형성되면서 이동하여 권취롤러(140)에 권취될 수 있다.The flame-retardant sheet paper 1 is brought into close contact with the first and second perforated rollers 152 and 154, and the perforated hole 2 is perforated by the perforated protrusion 153 of the first perforated roller 152. It may be wound around the winding roller 140 by moving.

도 7에 도시된 바와 같이, 타공돌기(153)는 단부에 칼날부(156)를 구비한다. 타공돌기(153)는 칼날부(156)의 중심으로 함몰홈부(157)가 형성되며, 함몰홈부(157)는 칼날부(156)에서 절단된 난연시트지(1)의 제거부위를 수용했다가 제1타공롤러(152)가 회전하면서 분리 제거되도록 해준다.As shown in FIG. 7, the perforation protrusion 153 has a blade portion 156 at an end thereof. The perforated protrusion 153 has a recessed groove 157 formed at the center of the blade 156, and the recessed groove 157 accommodates the removal portion of the flame-retardant sheet paper 1 cut at the blade 156. 1 punching roller 152 is rotated to be removed to remove.

칼날부(156)의 외주면은 길이방향으로 직선으로 형성되고, 칼날부(156)의 내주면은 단부로 갈수록 점차적으로 협소해지면서 날카롭도록 경사지게 형성된다.The outer circumferential surface of the blade portion 156 is formed in a straight line in the longitudinal direction, and the inner circumferential surface of the blade portion 156 is formed to be sharply inclined while gradually narrowing toward the end portion.

따라서, 본 발명의 일 실시예에 따른 난연 시트지, 그 제조방법 및 그 제조장치은, 알루미늄박지와 종이 사이에 접착제에 난연제가 함유된 난연접착제를 투입하여 합지하도록 하고, 종이의 외측면에 접착제에 난연제가 함유된 난연접착제를 도포하고, 그 외측에 코팅액을 추가 도포하므로 사용시 매끄러운 종이 질감을 느끼면서 화재 발생시 유독가스 발생을 줄여 환경 친화적인 사용을 가능하게 한다.Therefore, the flame-retardant sheet paper according to an embodiment of the present invention, a method for manufacturing the same, and a device for manufacturing the same, and put the flame-retardant adhesive containing a flame-retardant in the adhesive between the aluminum foil and the paper to be laminated, and the flame retardant to the adhesive on the outer surface of the paper It is possible to apply a flame retardant adhesive containing, and to further apply a coating liquid on the outside, so as to feel a smooth paper texture during use while reducing the generation of toxic gases in the event of a fire enables an environmentally friendly use.

본 발명은 도면에 도시된 실시예를 참고로 하여 설명되었으나, 이는 예시적인 것에 불과하며, 당해 기술이 속하는 분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능하다는 점을 이해할 것이다.Although the present invention has been described with reference to the embodiments shown in the drawings, this is merely exemplary, and those skilled in the art to which the art belongs can make various modifications and other equivalent embodiments therefrom. Will understand.

따라서, 본 발명의 진정한 기술적 보호범위는 아래의 특허청구범위에 의해서 정하여져야 할 것이다.Therefore, the true technical protection scope of the present invention will be defined by the claims below.

1 : 난연시트지 2 : 타공홀
10 : 알루미늄박지 20 : 종이
30 : 난연접착제 40 : 코팅층
50 : 제1공급롤러 60 : 제2공급롤러
70 : 난연접착제공급부 80 : 압착롤러
90 : 난연접착제보조공급부 100 : 도포롤러
110 : 코팅액공급부 120 : 코팅롤러
130 : 건조유닛 140 : 권취롤러
150 : 타공홀형성부 152 : 제1타공롤러
153 : 타공돌기 154 : 제2타공롤러
155 : 돌기접촉부 156 : 칼날부
157 : 함몰홈부
S10~S70 : 난연 시트지 제조방법의 단계들이다.1: flame retardant sheet 2: perforation hole
10: aluminum foil 20: paper
30: flame retardant adhesive 40: coating layer
50: first feed roller 60: second feed roller
70: flame retardant adhesive supply unit 80: compression roller
90: flame retardant adhesive auxiliary supply unit 100: coating roller
110: coating liquid supply unit 120: coating roller
130: drying unit 140: winding roller
150: perforation hole forming unit 152: first perforation roller
153: punching projection 154: second punching roller
155: protrusion contact portion 156: blade portion
157: recessed groove
S10 ~ S70: The steps of the flame-retardant sheet paper manufacturing method.

Claims (13)

알루미늄박지;
상기 알루미늄박지의 일면에 구비되는 종이;
상기 알루미늄박지와 상기 종이 사이에 구비되어 상기 알루미늄박지와 상기 종이를 상호 부착하도록 접착제에 난연제를 포함하여 이루어지는 난연접착제; 및
상기 종이의 외측면에 도포되는 코팅층;을 포함하고,
상기 난연제는 물유리, 인계난연제(Phosphrous-based flame retardants), 할로겐계난연제(Halogen-based flame retardants), 무기계난연제(inoragnic flame retardants)중 어느 하나 이상을 포함하며,
상기 난연제는 물유리 35~60중량%, 인계난연제 15~25중량%, 할로겐계난연제 15~25중량%, 무기계난연제 10~15중량%를 포함하는 것을 특징으로 하는 난연 시트지.
Aluminum foil;
Paper provided on one surface of the aluminum foil;
A flame retardant adhesive provided between the aluminum foil and the paper and including a flame retardant in an adhesive to adhere the aluminum foil and the paper to each other; And
And a coating layer applied to the outer surface of the paper.
The flame retardant includes any one or more of water glass, Phosphrous-based flame retardants, halogen-based flame retardants, inorganic flame retardants,
The flame retardant is a flame retardant sheet paper comprising 35 to 60% by weight of water glass, 15 to 25% by weight of phosphorus flame retardant, 15 to 25% by weight of halogen flame retardant, 10 to 15% by weight of inorganic flame retardant.
제 1항에 있어서,
상기 종이의 외측면과 상기 코팅층 사이에는 상기 난연접착제가 더 포함되고,
상기 난연접착제는 접착제 40~70 중량%, 난연제 30~60 중량%를 포함하는 것을 특징으로 하는 난연 시트지.
The method of claim 1,
The flame retardant adhesive is further included between the outer surface of the paper and the coating layer,
The flame-retardant adhesive agent is a flame-retardant sheet paper, characterized in that the adhesive comprises 40 to 70% by weight, flame retardant 30 to 60% by weight.
제 2항에 있어서,
상기 접착제는 대두접착제(Soy Adhesive)를 포함하는 것을 특징으로 하는 난연 시트지.
The method of claim 2,
The adhesive is flame retardant sheet paper, characterized in that it comprises a soy adhesive (Soy Adhesive).
삭제delete 삭제delete 종이와 알루미늄박지를 준비하는 단계;
상기 종이의 이면에 난연접착제를 도포하는 단계;
상기 종이의 이면에 도포된 난연접착제에 상기 알루미늄박지를 접착하여 합지하는 단계; 및
상기 합지의 종이 외측면에 난연접착제를 도포하는 단계;
상기 합지를 건조유닛에서 건조하여 난연시트지를 제조하는 단계;를 포함하고,
상기 난연접착제는 접착제 40~70 중량%, 난연제 30~60 중량%를 포함하고,
상기 난연제는 물유리 35~60중량%, 인계난연제 15~25중량%, 할로겐계난연제 15~25중량%, 무기계난연제 10~15중량%를 포함하는 것을 특징으로 하는 난연 시트지 제조방법.
Preparing paper and aluminum foil;
Applying a flame-retardant adhesive on the back side of the paper;
Adhering and laminating the aluminum foil to a flame-retardant adhesive applied to the back side of the paper; And
Applying a flame-retardant adhesive to the paper outer surface of the paper;
And drying the paper in a drying unit to produce a flame retardant sheet paper.
The flame retardant adhesive agent comprises an adhesive 40 to 70% by weight, flame retardant 30 to 60% by weight,
The flame retardant is 35 to 60% by weight of water glass, phosphorus flame retardant 15 to 25% by weight, halogen flame retardant 15 to 25% by weight, inorganic flame retardant manufacturing method characterized in that it comprises 10 to 15% by weight.
종이와 알루미늄박지를 준비하는 단계;
상기 종이의 외측면에 난연접착제를 도포하고 건조하는 단계;
상기 종이의 이면에 난연접착제를 도포하는 단계;
상기 종이의 이면에 도포된 난연접착제에 상기 알루미늄박지를 접착하여 합지하는 단계; 및
상기 합지를 건조유닛에서 건조하여 난연시트지를 제조하는 단계;를 포함하고,
상기 난연접착제는 접착제 40~70 중량%, 난연제 30~60 중량%를 포함하고,
상기 난연제는 물유리 35~60중량%, 인계난연제 15~25중량%, 할로겐계난연제 15~25중량%, 무기계난연제 10~15중량%를 포함하는 것을 특징으로 하는 난연 시트지 제조방법.
Preparing paper and aluminum foil;
Applying and drying a flame-retardant adhesive on the outer surface of the paper;
Applying a flame-retardant adhesive on the back side of the paper;
Adhering and laminating the aluminum foil to a flame-retardant adhesive applied to the back side of the paper; And
And drying the paper in a drying unit to produce a flame retardant sheet paper.
The flame retardant adhesive agent comprises an adhesive 40 to 70% by weight, flame retardant 30 to 60% by weight,
The flame retardant is 35 to 60% by weight of water glass, phosphorus flame retardant 15 to 25% by weight, halogen flame retardant 15 to 25% by weight, inorganic flame retardant manufacturing method characterized in that it comprises 10 to 15% by weight.
제 6항 또는 제 7항에 있어서,
상기 종이의 외측면에 도포된 상기 난연접착제 상에 코팅층을 도포하는 단계; 및
상기 건조유닛에서 상기 난연시트지를 건조한 후, 타공홀형성부를 이용하여 상기 난연시트지를 관통하는 다수개의 타공홀을 형성하는 단계;
중 적어도 어느 하나의 단계를 더 포함하는 것을 특징으로 하는 난연 시트지 제조방법.
The method according to claim 6 or 7,
Applying a coating layer on the flame retardant adhesive applied to an outer surface of the paper; And
Drying the flame retardant sheet paper in the drying unit, and then forming a plurality of perforated holes penetrating the flame retardant sheet paper by using the perforated hole forming unit;
Flame retardant sheet paper manufacturing method characterized in that it further comprises at least one step.
삭제delete 종이가 권취되어 종이를 공급하는 제1공급롤러;
알루미늄박지가 권취되어 알루미늄박지를 공급하는 제2공급롤러;
상기 종이의 이면에 난연접착제를 공급하는 난연접착제공급부;
상기 난연접착제공급부를 통해 도포된 난연접착제로 상기 종이와 상기 알루미늄박지와 상호 합지하는 압착롤러;
합지된 상기 종이와 상기 알루미늄박지에 열을 가해 건조하여 난연시트지를 제조하는 건조유닛;을 포함하고,
상기 압착롤러로 상기 종이와 상기 알루미늄박지를 합지하기 전 또는 합지한 후에 상기 종이의 외측면에 난연접착제보조공급부를 통해 공급된 난연접착제를 도포롤러로 1차 코팅하고,
상기 종이의 외측면에 도포된 상기 난연접착제 상에 코팅액공급부에서 공급된 코팅액을 코팅롤러로 2차 코팅하여 코팅층을 형성하는 것을 특징으로 하는 난연 시트지 제조장치.
A first feed roller which winds the paper and supplies the paper;
A second feed roller for winding the aluminum foil to supply the aluminum foil;
A flame-retardant adhesive supply unit for supplying a flame-retardant adhesive on the back surface of the paper;
A compression roller which is laminated with the paper and the aluminum foil with a flame retardant adhesive applied through the flame retardant adhesive supply unit;
And a drying unit for drying the paper and the aluminum foil by lamination to produce a flame-retardant sheet paper.
Before or after laminating the paper and the aluminum foil with the pressing roller, firstly coating the flame-retardant adhesive supplied through the flame-retardant adhesive supply unit on the outer surface of the paper with a coating roller,
Flame retardant sheet paper manufacturing apparatus, characterized in that to form a coating layer by coating the coating liquid supplied from the coating liquid supply unit on the flame-retardant adhesive applied to the outer surface of the paper with a coating roller.
삭제delete 제 10항에 있어서,
상기 건조유닛을 통과한 상기 난연시트지는 타공홀형성부에 의해 타공홀이 다수개 형성되어 상기 난연시트지를 피부착물에 부착시 공기의 배출을 도와주고,
상기 타공홀형성부는,
상기 난연시트지에 타공홀을 관통 형성하도록 타공돌기를 구비하는 제1타공롤러; 및
상기 제1타공롤러에 접하여 상기 난연시트지의 타공홀을 관통하여 돌출된 상기 타공돌기를 접촉하는 돌기접촉부를 형성하는 제2타공롤러;를
포함하는 것을 특징으로 하는 난연 시트지 제조장치.
The method of claim 10,
The flame-retardant sheet paper passing through the drying unit is formed with a plurality of perforated holes by the hole-hole forming portion to help the discharge of air when attaching the flame-retardant sheet paper to the skin complex,
The perforation hole forming unit,
A first perforated roller having a perforated protrusion to penetrate the perforated hole in the flame retardant sheet paper; And
A second perforated roller in contact with the first perforated roller and forming a protrusion contact portion contacting the perforated protrusion protruding through the perforated hole of the flame retardant sheet paper;
Flame retardant sheet paper manufacturing apparatus comprising a.
제 10항 또는 제 12항에 있어서,
상기 난연접착제는 접착제 40~70 중량%, 난연제 30~60 중량%를 포함하고,
상기 난연제는 물유리 35~60중량%, 인계난연제 15~25중량%, 할로겐계난연제 15~25중량%, 무기계난연제 10~15중량%를 포함하는 것을 특징으로 하는 난연 시트지 제조장치.
The method of claim 10 or 12,
The flame retardant adhesive agent comprises an adhesive 40 to 70% by weight, flame retardant 30 to 60% by weight,
The flame retardant is 35 to 60% by weight of water glass, phosphorus flame retardant 15 to 25% by weight, halogen flame retardant 15 to 25% by weight, flame retardant sheet paper manufacturing apparatus comprising a 10 to 15% by weight inorganic flame retardant.
KR1020180016497A 2018-02-09 2018-02-09 Incombustible sheet and manufacturing method the same and manufacturing device the same KR102013119B1 (en)