KR101993804B1 - Cable―veyor - Google Patents

Cable―veyor Download PDF

Info

Publication number
KR101993804B1
KR101993804B1 KR1020170094553A KR20170094553A KR101993804B1 KR 101993804 B1 KR101993804 B1 KR 101993804B1 KR 1020170094553 A KR1020170094553 A KR 1020170094553A KR 20170094553 A KR20170094553 A KR 20170094553A KR 101993804 B1 KR101993804 B1 KR 101993804B1
Authority
KR
South Korea
Prior art keywords
polyurethane
sheet
cable
layer
tpu
Prior art date
Application number
KR1020170094553A
Other languages
Korean (ko)
Other versions
KR20190011907A (en
Inventor
정봉권
Original Assignee
주식회사 수에코신소재
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 수에코신소재 filed Critical 주식회사 수에코신소재
Priority to KR1020170094553A priority Critical patent/KR101993804B1/en
Publication of KR20190011907A publication Critical patent/KR20190011907A/en
Application granted granted Critical
Publication of KR101993804B1 publication Critical patent/KR101993804B1/en

Abstract

본 발명은 무분진 및 내마모성이 우수한 케이블베어용 폴리우레탄―ptfe시트의 제조방법 및 그 제조물에 관한 것으로서 본 발명에 의해 폴리우레탄층의 열변형과 필요이상의 신장을 방지함으로써 시트두께의 불균일과 늘어남, 시트가 접히는 문제를 해결한 케이블베어용 폴리우레탄―ptfe시트의 제조방법을 제공할 수 있으며, 반복적으로 움직이는 장비에 사용되는 전선 케이블류, 공압튜브 등의 장비의 케이블류를 보호하고 장비의 결합부와 이탈 혹은 이완현상이 없는 견고하게 고정할 수 있는 무분진 자동화 케이블베어를 제공할 수 있다.The present invention relates to a method for producing a polyurethane-pheft sheet for cable bows, which is excellent in dust-free and abrasion resistance, and a method for producing the polyurethane-pheft sheet for cable bows. The present invention prevents thermal deformation of the polyurethane layer and elongation more than necessary, It is possible to provide a method of manufacturing a polyurethane-ptfe sheet for cable bails which overcomes the problem of sheet folding, and it is possible to protect cables of equipment such as wire cables and pneumatic tubes used in repeatedly moving equipment, And a dust-free automation cable bare which can be firmly fixed without deviation or relaxation.

Description

케이블베어{Cable―veyor} Cable bear {Cable-veyor}

본 발명은 케이블베어에 관한 것이다.The present invention relates to cable bearings.

자동화 장비, 공작기계, 전자기기, 산업용 로봇, 운반기계 등과 같이 반복적으로 움직이는 장비에 사용되는 전선 케이블류, 공압튜브는 뒤틀림이나 변형 혹은 마찰등에 대해 그 피복의 벗겨짐등으로 인한 손상이 될 수 있기 때문에, 케이블 및 배관호스를 보호하고 안정적으로 운용할 수 있도록 별도로 케이블 보호용 트레이 커버를 사용한다.Electrical cables and pneumatic tubes used in repeatedly moving equipment such as automation equipment, machine tools, electronic equipment, industrial robots, and conveying machines can be damaged by twisting, deformation or friction, To protect the cable and piping hose, and to ensure stable operation, use a separate cover for cable protection.

이들의 용도는 하나 또는 다중 튜브형태로 구성되어 있고 바깥쪽과 튜브 안쪽은 다양한 성능을 구현하기 위해 통상 내마모성 케이블 트레이 소재로 이루어진다.Their applications are in one or multi-tube configurations, and the outside and inside of the tube are usually made of an abrasion resistant cable tray material to provide a variety of performance.

일반적으로 이러한 경우 전선이나 내마모성이 약한 소재가 반복적인 기계 움직임으로 인해 다른 부분과 지속적으로 마찰을 하게 되면, 상기 고분자재질의 케이블 트레이 표면이 벗겨지고 마찰에 의해 분진이 발생되며, 케이블 트레이의 표면에 분진이 부착되며 이러한 분진이 자동화 장비, 반도체 장비등의 표면과 클린공정룸에 오염을 유발시켜 제품불량을 발생 시킬 수 있다.Generally, in such a case, if the wire or the weak abrasion-resistant material continuously rubs against other parts due to repetitive mechanical movements, the surface of the cable tray of the polymer material is peeled off, dust is generated by friction, Dusts are adhered and these dusts can cause contamination on the surfaces of automation equipments, semiconductor equipments, etc. and the clean process room, resulting in product failure.

일반적으로 이러한 부분을 해결하는 방법으로 공기 중에 존재하는 입자를 양이온 또는 음이온으로 이온화시켜 중화 시키는 방법인 이오나이저(Ionizer)를 사용하는 경우도 있으나, 움직이는 장비에 설치하기 용의하지 않고 지속적인 유지관리가 필요하다. 그러므로 일정구간 반복적으로 움직이는 자동화장비, 반도체 장비, 공작기계, 전자기기, 산업용 로보트, 운반기계 등에 사용되는 케이블류 및 공압튜브를 보호하고 더욱 안정적으로 유지시킴으로써 상기 케이블류의 손상을 방지하여 분진을 발생시키지 않도록 할 수 있을 뿐만 아니라, 이오나이저(Ionizer) 중화에 비해 효과적으로 유지관리 및 비용절감이 필요하고 고도화되는 시대에 맞춰 분진 및 이물질을 효과적이고 쉬운 장치가 절실히 요구되고 있는 실정이다.Generally, as an approach to solve such a problem, an ionizer, which is a method of neutralizing airborne particles by ionizing them into positive ions or negative ions, may be used. However, continuous maintenance need. Therefore, it protects the cables and pneumatic tubes used for automation equipment, semiconductor equipment, machine tools, electronic devices, industrial robots, conveying machines and the like, which are moving repeatedly, In addition, there is an urgent need for an effective and easy-to-use device for dust and foreign matter in accordance with the times when maintenance and cost reduction are more effective and more advanced than neutralization of ionizer.

대한민국특허등록제10-1709039호(2017년02월21일 공고)Korea Patent Registration No. 10-1709039 (Notice of February 21, 2017)

그러므로 본 발명은 자동화 장비, 공작기계, 전자기기, 산업용 로봇, 운반기계 등의 반복적으로 움직이는 장비에 사용되는 전선 케이블류, 공압튜브 등의 장비의 케이블류를 보호하여 분진이 발생하지 않도록 하고 케이블류와 공압튜브의 매끄럼성을 유지시키고 전기적인 안전성을 유지시키는 동시에 스파크 및 전기적인 성질에 의해 불에 잘 타지 않은 재질을 사용하여 케이블의 손상을 방지할 수 있는 다중 접착 시트 무분진 케이블용 튜브제작을 위한 다중 접착시트를 제공하는 것을 목적으로 한다. 또한 접착시트는 반복적인 피로에 견딜 수 있는 강도 및 강성을 유지하기 위해 복합화된 재료를 형성하여 제공하는 것을 목적으로 한다.Therefore, the present invention protects cables of equipment such as electric cables, pneumatic tubes and the like used in repeatedly moving equipment such as automation equipment, machine tools, electronic devices, industrial robots, and conveying machines, And multi-adhesive sheet-free dust-free cable tubing that maintains the smoothness of the pneumatic tube and maintains electrical safety while preventing damage to the cable by using materials that are not burned due to spark and electrical properties. To provide a multi-adhesive sheet. The adhesive sheet is also intended to form and provide a composite material in order to maintain strength and rigidity that can withstand repeated fatigue.

그러므로 본 발명에 의하면, 일면에 두께 0.1~0.4mm의 폴리우레탄(TPU)시트에 이형지가 붙여진 상태로 상부공급 롤러부를 통해 공급하고, ptfe 시트를 하부공급롤러부를 통해 연신비 1.10~1.30으로 연신하면서 공급하고, 상기 공급된 폴리우레탄시트와 ptfe시트를 실리콘롤러와 금속제 히팅롤러사이로 공급하여 폴리우레탄시트의 폴리우레탄층과 ptfe시트를 접착한 후. 상기 폴리우레탄시트의 일면에 부착된 이형지를 분리하여 권취하고, 상기 접착된 폴리우레탄―ptfe시트를 권취하는 것을 특징으로 하는 무분진 및 내마모성이 우수한 케이블베어용 폴리우레탄―ptfe시트의 제조방법이 제공된다.Therefore, according to the present invention, a release paper is supplied to a polyurethane (TPU) sheet having a thickness of 0.1 to 0.4 mm on one side through an upper feed roller unit, and a ptfe sheet is fed through a lower feed roller unit to a stretching ratio of 1.10 to 1.30 And feeding the supplied polyurethane sheet and ptfe sheet between a silicone roller and a metal heating roller to bond the polyurethane layer of the polyurethane sheet to the ptfe sheet. A method for manufacturing a polyurethane-pptfe sheet for cable bear excellent in no-dust and abrasion resistance, characterized by separating and winding up the release paper attached to one surface of the polyurethane sheet, and winding up the adhered polyurethane-pptfe sheet do.

또한, 본 발명의 케이블베어용 폴리우레탄―ptfe시트의 제조방법에서는 상기 폴리우레탄시트는 인장강도 300~600KGF/㎠이고 신도 200~800%이고, 상기 ptfe시트는 신도 100~800%로 연신된 상태이며, 상기 금속제히팅롤러는 압력 3~7KGF/㎠, 온도 150~280℃인 것을 특징으로 한다.In the process for producing a polyurethane sheet for cable bails according to the present invention, the polyurethane sheet has a tensile strength of 300 to 600 KGF / cm 2 and an elongation of 200 to 800%, and the ptfe sheet is stretched to 100 to 800% And the metal heating roller has a pressure of 3 to 7 Kgf / cm 2 and a temperature of 150 to 280 ° C.

또한, 본 발명에 의하면, 신도 100~800%인 폴리테트라플루오로에틸렌(ptfe)층과 인장강도 300~600KGF/㎠이고 신도 200~800%인 폴리우레탄(TPU)층이 적층된 것을 특징으로 하는 무분진 및 내마모성이 우수한 케이블베어용 폴리우레탄―ptfe시트가 제공된다.According to the present invention, a polytetrafluoroethylene (ptfe) layer having an elongation of 100 to 800% and a polyurethane (TPU) layer having a tensile strength of 300 to 600 KGF / cm 2 and an elongation of 200 to 800% There is provided a polyurethane-pptfe sheet for a cable bearing excellent in dust-free and abrasion resistance.

또한 본 발명에 의하면, 상기 무분진 및 내마모성이 우수한 케이블베어용 폴리우레탄―ptfe시트로 이루어진 것을 특징으로 하는 케이블베어가 제공된다.According to the present invention, there is also provided a cable bear comprising the polyurethane-pptfe sheet for cable bear excellent in no dust and abrasion resistance.

또한, 상기 케이블베어의 내부에 복합유리섬유, 카본섬유, 아라미드 섬유, 바잘트섬유 중 어느 하나 이상의 UD 또는 직물에 PVC, PE, ABS, 실리콘, 에폭시수지, 페놀수지, 폴리에스터수지, 프란수지, 멜라민 수지 중 어느 하나의 수지가 함침된 강화시트가 형성된 것을 특징으로 하는 케이블베어가 제공된다.It is also possible to use a UD or a UD of at least one of composite glass fiber, carbon fiber, aramid fiber, and bar-cut fiber in the cable bearer, or a PVC, PE, ABS, silicone, epoxy resin, phenol resin, A reinforcing sheet impregnated with any one of a melamine resin, a melamine resin, and a melamine resin is formed.

또한, 상기 케이블베어의 일단부분에 미끄럼 방지용 열가소성 폴리우레탄(TPU)층이 추가로 형성된 것을 특징으로 하는 케이블베어가 제공된다.A cable bare is also provided, wherein a non-slip thermoplastic polyurethane (TPU) layer is additionally formed at one end of the cable bear.

그러므로 본 발명에 의하면 폴리우레탄층의 열변형과 필요이상의 신장을 방지함으로써 시트두께의 불균일과 늘어남, 시트가 접히는 문제를 해결한 케이블베어용 폴리우레탄―ptfe시트의 제조방법을 제공할 수 있으며, 반복적으로 움직이는 장비에 사용되는 전선 케이블류, 공압튜브 등의 장비의 케이블류를 보호하고 장비의 결합부와 이탈 혹은 이완현상이 없는 견고하게 고정할 수 있는 무분진 자동화 케이블베어를 제공할 수 있다.Therefore, according to the present invention, it is possible to provide a method for producing a polyurethane-pptfe sheet for cable bails, wherein the polyurethane layer is prevented from being thermally deformed and stretched more than necessary to prevent unevenness and elongation of sheet thickness and folding of the sheet. It is possible to provide a non-dusting automation cable bare which can protect the cables of equipment such as wire cables and pneumatic tubes used in equipment moving in the moving equipment, and can securely fix the joining parts of the equipments without loosening or releasing.

도 1은 본 발명에 따른 케이블베어용 폴리우레탄―ptfe시트의 제조장치의 사시도이며,
도 2는 본 발명에 따른 케이블베어용 폴리우레탄―ptfe시트의 제조장치의 측단면도이며,
도 3은 본 발명에 따른 케이블베어용 폴리우레탄―ptfe시트의 단면도이며,
도 4는 본 발명에 따른 케이블베어의 성형상태를 나타낸 단면도이며,
도 5는 본 발명의 또다른 일실시예에 따른 케이블베어를 나타낸 사시도이다BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a perspective view of an apparatus for producing a polyurethane-
Fig. 2 is a side cross-sectional view of a production apparatus for a polyurethane-ptfe sheet for cable bear according to the present invention,
3 is a cross-sectional view of a polyurethane-pptfe sheet for cable bear according to the present invention,
4 is a cross-sectional view showing a molding state of a cable bail according to the present invention,
5 is a perspective view showing a cable bear according to another embodiment of the present invention

이하, 첨부한 도면을 참고로 하여 본 발명의 실시예에 대하여 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 상세히 설명한다. 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다. 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 동일 또는 유사한 구성요소에 대해서는 동일한 참조부호를 부가한다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings, which will be readily apparent to those skilled in the art to which the present invention pertains. The present invention may be embodied in many different forms and is not limited to the embodiments described herein. In order to clearly illustrate the present invention, parts not related to the description are omitted, and the same reference numerals are assigned to the same or similar components throughout the specification.

도 1 내지 도 2를 참조하면, 본 발명에 따른 무분진 및 내마모성이 우수한 케이블베어용 폴리우레탄―ptfe시트의 제조방법은 일면에 두께 0.1~0.4mm의 폴리우레탄(TPU)시트(100)에 이형지가 붙여진 상태로 상부공급롤러부(200)를 통해 공급하고, ptfe시트(300)를 하부공급롤러부(400)를 통해 연신비 1.10~1.30으로 연신하면서 공급하고, 상기 공급된 폴리우레탄시트와 ptfe시트를 실리콘롤러(500)와 금속제히팅롤러(600)사이로 공급하여 폴리우레탄시트의 폴리우레탄층과 ptfe시트를 접착한 후. 상기 폴리우레탄시트의 일면에 부착된 이형지(120)를 분리하여 권취하고, 상기 접착된 폴리우레탄―ptfe시트를 권취(700)하는 것이다.Referring to FIGS. 1 and 2, a polyurethane-pptfe sheet for cable bear having excellent dust-free and abrasion resistance according to the present invention comprises a polyurethane (TPU) sheet 100 having a thickness of 0.1 to 0.4 mm, And the ptfe sheet 300 is fed through the lower feed roller unit 400 while being stretched at a stretch ratio of 1.10 to 1.30 and the ptfe sheet 300 is fed while being stretched at a stretch ratio of 1.10 to 1.30, Is fed between the silicone roller (500) and the metal heating roller (600) to bond the polyurethane layer of the polyurethane sheet and the ptfe sheet. Separating and winding the release paper 120 attached to one side of the polyurethane sheet, and winding up (700) the adhered polyurethane-phefe sheet.

상기 폴리우레탄(TPU)시트는 폴리우레탄(TPU)층(110)의 일면에 두께 0.1~0.4mm의 이형지(120)가 붙은 폴리우레탄(TPU)시트(100)로서 본 발명의 케이블베어용 폴리우레탄―ptfe시트의 일면을 형성하는 것이다. 상기 폴리우레탄(TPU)시트는 신도가 인장강도 300~600KGF/㎠이고 신도 200~800%인 것으로서 신도가 높아 폴리우레탄(TPU)시트만을 롤러로 공급하는 경우에 히팅롤러의 열에 의해 폴리우레탄층이 열변형을 하게 되고 필요이상으로 신장하게 되어 열에 의해 두께의 불균일과 늘어남이 발생하고, 이로 인해 시트가 접히는 문제가 발생하게 되므로 폴리우레탄(TPU)시트의 일면에 이형지를 붙여 상부공급롤러로 공급하여 성형시 폴리우레탄층의 열변형을 방지하고 고정시켜 주는 역할을 하게 된다.The polyurethane (TPU) sheet is a polyurethane (TPU) sheet 100 having a release paper 120 of 0.1 to 0.4 mm thickness on one side of a polyurethane (TPU) layer 110, -Ptfe < / RTI > sheet. The polyurethane (TPU) sheet has a tensile strength of 300 to 600 KGF / cm 2 and an elongation of 200 to 800%, and has a high elongation, so that when the polyurethane (TPU) (TPU) sheets are attached to one side of the sheet and then fed to the upper feed rollers so that the sheet is fed to the upper feed rollers Thereby preventing thermal deformation of the polyurethane layer during molding and fixing the polyurethane layer.

상기 폴리우레탄(TPU)시트의 일면에 붙은 이형지는 추후 실리콘롤러와 금속제히팅 롤러사이에서 폴리우레탄시트의 폴리우레탄층과 ptfe시트가 접착된 후에 이형지를 분리하게 된다.The releasing paper on one side of the polyurethane (TPU) sheet separates the releasing paper after the polyurethane layer of the polyurethane sheet and the ptfe sheet are adhered between the silicone roller and the metal heating roller.

상기 ptfe시트는 저온 프라즈마를 이용하여 표면에 다수의 미세기공이 형성된 것을 사용하는 것이 접착력이 향상되는데, 특히 신도 100~800%인 ptfe(폴리테트라플루오로에틸렌) 시트를 사용하는 것이 폴리우레탄(TPU)가 열에 의해 녹아 압력으로 접착하여 접착력에 더 바람직하다. The use of a ptfe (polytetrafluoroethylene) sheet having an elongation of 100% to 800% is preferable because the polyurethane (TPU (polytetrafluoroethylene) sheet) ) Is melted by heat and adhered by pressure, which is more preferable for adhesive force.

상기 ptfe시트는 하부공급롤러부를 통해 공급하는데, 연신비 1.10~1.30으로 연신하여 실리콘롤러와 금속제히팅롤러 사이에서 폴리우레탄시트의 폴리우레탄층과 접착할 때 폴리우레탄층과의 접착을 보다 원활하고 견고하게 행하도록 한다.The ptfe sheet is fed through the lower feed roller portion and stretched at a stretching ratio of 1.10 to 1.30 to bond the polyurethane layer to the polyurethane layer of the polyurethane sheet between the silicone roller and the metal heating roller to smoothly and firmly adhere to the polyurethane layer .

이렇게 공급된 상기 폴리우레탄시트와 ptfe시트는 실리콘롤러와 금속제히팅롤러사이로 공급하여 폴리우레탄시트의 폴리우레탄층과 ptfe시트를 열과 압력에 의해 접착되어지게 한다. 상기 실리콘롤러도 고온의 열을 발산하게 할 수도 있다. 상기 금속제히팅롤러는 압력 3~7KGF/㎠, 온도 150~280℃인 것을 사용하는 것이 폴리우레탄층과 ptfe시트가 견고하게 접착되도록 할 수 있다. 접착된 폴리우레탄―ptfe시트는 필요에 따라 원형 혹은 일자형태의 컷팅 날에 의해 일정한 폭으로 재단된다.The polyurethane sheet and the ptfe sheet thus fed are fed between the silicone roller and the metal heating roller to bond the polyurethane layer and the ptfe sheet of the polyurethane sheet by heat and pressure. The silicone roller may also cause high temperature heat to be dissipated. The metal heating roller has a pressure of 3 to 7 Kgf / cm 2 and a temperature of 150 to 280 ° C so that the polyurethane layer and the ptfe sheet can be firmly adhered to each other. The bonded polyurethane-pptfe sheet is cut to a certain width by a cutting blade in the shape of a circle or a line if necessary.

이렇게 폴리우레탄층과 ptfe시트를 접착한 후. 상기 폴리우레탄시트의 일면에 부착된 이형지를 분리하여 권취하고, 상기 접착된 폴리우레탄―ptfe시트를 권취하여 본 발명의 폴리우레탄―ptfe시트를 제조하게 된다.After bonding the polyurethane layer and ptfe sheet. The releasing paper attached to one surface of the polyurethane sheet is separated and wound up, and the polyurethane-pptfe sheet is wound up to produce the polyurethane-pptfe sheet of the present invention.

또한 본 발명에 의해 신도 100~800%인 폴리테트라플루오로에틸렌(ptfe)층과 인장강도 300~600KGF/㎠이고 신도 200~800%인 폴리우레탄(TPU)층이 적층된 것을 특징으로 하는 무분진 및 내마모성이 우수한 케이블베어용 폴리우레탄―ptfe시트가 제공된다.According to the present invention, a polytetrafluoroethylene (ptfe) layer having an elongation of 100 to 800% and a polyurethane (TPU) layer having a tensile strength of 300 to 600 KGF / cm 2 and an elongation of 200 to 800% And a polyurethane-pptfe sheet for a cable bare excellent in abrasion resistance are provided.

도 3에 도시된 바와 같이 본 발명의 무분진 및 내마모성이 우수한 케이블베어용 폴리우레탄―ptfe시트(10)는 저온 프라즈마를 이용하여 표면에 다수의 미세기공이 형성된 신도 100~800%인 폴리테트라플루오로에틸렌(ptfe)층(300)과 신도 200~800%인 점착성있는 폴리우레탄(TPU)층(110)이 적층된 것으로서 연신 및 개질화를 통하여 접착력이 우수한 특징을 가진다.As shown in FIG. 3, the polyurethane-pptfe sheet 10 of the present invention having excellent dust-free and abrasion resistance is made of polytetrafluoroethylene (PTFE) having 100 to 800% elongation having many micropores formed on the surface thereof by using low-temperature plasma. (TPU) layer 110 having an elongation of 200 to 800%, which is excellent in adhesion strength through stretching and reforming. The poly (ethylene terephthalate) (PTFE) layer 300 and the tacky polyurethane (TPU)

상기 ptfe(폴리테트라플루오로에틸렌)층은 작은 단위체들을 사슬 혹은 그물 형태로 화학결합된 고분자소재로서 미세기공이 형성되어 있는 다공성 구조로 이루어져 있으며, 내열성, 내화학성이 뛰어나고 마찰계수가 매우 낮기 때문에, 내피와 외피에 적용하여 전선 및 공압 튜브등의 수업이 반복되는 장비에 마찰에 의한 손상을 방지할 수 있고, 분진을 최소화 할 수 있다.The ptfe (polytetrafluoroethylene) layer is a polymer material chemically bonded to a small unit in a chain or net form and has a porous structure in which micropores are formed. Since it has excellent heat resistance, chemical resistance and very low coefficient of friction, It can be applied to the inner skin and the outer skin to prevent damage caused by friction to equipment such as electric wires and pneumatic tubes repeatedly, and dust can be minimized.

또한 본 발명에 의하면 상기 무분진 및 내마모성이 우수한 케이블베어용 폴리우레탄―ptfe시트로 이루어진 것을 특징으로 하는 케이블베어가 제공된다. In addition, according to the present invention, there is provided a cable bear comprising the polyurethane-pptfe sheet for cable bear excellent in no dust and abrasion resistance.

도 4에 도시된 바와 같이 상기 폴리우레탄―ptfe시트로 케이블베어가 형성되는데, 케이블베어(20)는 슬리팅된 한쌍의 폴리우레탄―ptfe시트를 ptfe층(300)이 서로 마주보도록 여러쌍 배열되고 그 외층에 광폭의 폴리우레탄―ptfe시트를 폴리우레탄층(110)이 서로 마주보도록 배열하여 전체로서 접착된 것으로서, 슬리팅된 한쌍의 폴리우레탄―ptfe시트는 ptfe층이 서로 마주보도록 형성되어 ptfe층이 분리됨으로써 그 내부에 공간을 형성하게 되고 그 공간에 케이블을 수납할 수 있도록 하며, 외층의 광폭의 폴리우레탄―ptfe시트는 폴리우레탄층이 서로 마주보도록 배열하고 접착하여 이루어진 것이다.As shown in FIG. 4, a cable bear is formed of the polyurethane-ptfe sheet, wherein the cable bear 20 has a pair of slitted polyurethane-ptfe sheets arranged in pairs such that the ptfe layers 300 face each other A wide polyurethane-pptfe sheet is arranged on the outer layer so that the polyurethane layers 110 are arranged so as to face each other, and a pair of slitted polyurethane-pptfe sheets are formed such that the ptfe layers are opposed to each other, So that a space can be formed in the space, and the cable can be housed in the space. The wide polyurethane foam sheet of the outer layer is formed by arranging and bonding the polyurethane layers so as to face each other.

또한, 상기 케이블베어의 강도 및 강성을 보강하기 위한 것으로서 복합유리섬유, 카본섬유, 아라미드 섬유, 바잘트섬유 중 어느 하나 이상의 UD 또는 직물에 PVC, PE, ABS, 실리콘, 에폭시수지, 페놀수지, 폴리에스터수지, 프란수지, 멜라민 수지 중 어느 하나의 수지가 함침된 강화시트가 형성될 수 있다. 상기 UD는 상기 섬유를 일방향으로 펼쳐진 형태 또는 스프레드 토우 시트 형태로 사용 되어 질 수 있다. 상기 강화시트는 상기 케이블베어의 케이블이 수납되는 슬리팅된 한쌍의 폴리우레탄―ptfe시트층의 내부의 공간에 삽입되어 형성됨으로써 케이블베어의 강도 및 강성을 보강할 수 있다. 또한 전선의 곡율 반경을 일정하게 유지시켜 줌으로써 전선의 피로누적에 의한 마찰 감소 및 전선 및 케이블베어의 수명을 오랫동안 유지시킬 수 있다.In order to reinforce the strength and rigidity of the cable bear, the UD or the fabric of any one or more of the composite glass fiber, the carbon fiber, the aramid fiber and the Vasartite fiber may be made of PVC, PE, ABS, silicone, epoxy resin, A reinforcing sheet impregnated with any one of an ester resin, a flan resin, and a melamine resin may be formed. The UD may be used in a unidirectional or spread-tow sheet form. The reinforcing sheet is inserted and formed in a space inside a pair of slitted polyurethane foam sheets in which the cables of the cable bear are housed, thereby reinforcing the strength and rigidity of the cable bear. By keeping the curvature radius of the wire constant, it is possible to reduce the friction by accumulating the fatigue of the wire and to maintain the life of the cable and the cable bear for a long time.

또한 본 발명에서는 도 5에 도시된 바와 같이 상기 케이블베어의 일단부분에 미끄럼 방지용 열가소성 폴리우레탄(TPU)층이 추가로 형성된 것을 특징으로 하는 케이블베어가 제공될 수 있다. Further, in the present invention, as shown in FIG. 5, a cable bearing may be provided, wherein a non-slip thermoplastic polyurethane (TPU) layer is further formed on one end of the cable bear.

상기 케이블베어는 폴리우레탄(TPU)과 ptfe 시트가 하나 또는 다중으로 결합된 상태로서 장비에 조립하는 경우 기존에는 별도의 알루미늄, 플라스틱등의 결합부(800)에 케이블베어가 견고하게 고정되도록 하기 위해 실리콘시트, 링, 패드 등을 넣고 조립하여 고정하였으나, 이 경우 미끄럼성이 강한 ptfe층의 특성상 영구적으로 고정되지 못하고 결합부로부터 이탈하거나 케이블베어와 고정체의 연결부위가 느슨해질 수 있어 인해 장비의 문제를 야기할 수 있기 때문에 연결부위에 대해 지속적으로 유지 및 관리해야 하는 문제점이 있었다. 이를 해결하기 위하여 본 발명에서는 도 5와 같이 케이블베어의 일단부분에 미끄럼 방지용 열가소성 폴리우레탄(TPU)(900)을 150~ 270℃의 융착기에 의해 열융착 시킴으로서 케이블베어의 ptfe층과 추가 형성된 폴리우레탄(TPU)층이 완전하게 접착되도록 하여 장비의 결합부가 이탈 혹은 이완현상이 없이 장기간동안 케이블베어를 견고하게 고정할 수 있게 된다. When the cable bear is assembled with the polyurethane (TPU) and the ptfe sheet in a single or multi-ply state, the cable bear is conventionally fixed so that the cable bear is firmly fixed to the joint portion 800 of aluminum or plastic However, in this case, due to the characteristic of the slip resistant ptfe layer, it can not be permanently fixed and the connection portion between the cable bear and the fixing body may be loosened. There has been a problem in that it is necessary to constantly maintain and manage the connection site. In order to solve this problem, in the present invention, as shown in FIG. 5, a thermoplastic polyurethane (TPU) 900 for anti-slip is thermally fused at one end of a cable bear by a welder at 150 to 270 ° C., (TPU) layer is fully adhered, so that the cable bear can be firmly fixed for a long period without releasing or loosening of the coupling part of the equipment.

10 : 폴리우레탄-ptfe 시트
20 : 케이블 베어
100 : 이형지가 붙은 폴리우레탄(TPU)시트
110 : TPU층 120 : 이형지
200 : 상부공급롤러부 300 : ptfe시트
400 : 하부공급롤러부 500 : 실리콘롤러
600 : 금속재히팅롤러 700 : 폴리우레탄―ptfe시트 권취롤
800 : 결합부 900 : 열가소성 폴리우레탄(TPU)10: polyurethane-pptfe sheet
20: Cable Bear
100: Polyurethane (TPU) sheet with release paper
110: TPU layer 120: release paper
200: upper feed roller part 300: ptfe sheet
400: lower feed roller unit 500: silicone roller
600: metal heating roller 700: polyurethane-pptfe sheet winding roll
800: Coupling part 900: Thermoplastic polyurethane (TPU)

Claims (6)

삭제delete 삭제delete 신도 100~800%인 폴리테트라플루오로에틸렌(ptfe)층과 인장강도 300~600KGF/㎠이고 신도 200~800%인 폴리우레탄(TPU)층이 적층된 케이블베어용 폴리우레탄―ptfe시트로 이루어지고, 그 내부에 복합유리섬유, 카본섬유, 아라미드 섬유, 바잘트섬유 중 어느 하나 이상의 섬유의 일방향으로 펼쳐진 형태, 스프레드 토우 시트 형태 및 직물 중 어느 하나에 PVC, PE, ABS, 실리콘, 에폭시수지, 페놀수지, 폴리에스터수지, 프란수지, 멜라민 수지 중 어느 하나의 수지가 함침된 강화시트가 형성된 것을 특징으로 하는 케이블베어.(Polytetrafluoroethylene) layer having a stretch ratio of 100 to 800% and a polyurethane (TPU) layer having a tensile strength of 300 to 600 KGF / cm 2 and an elongation of 200 to 800% PE, ABS, silicone, epoxy resin, phenol, or the like in any one of a unfolded shape, a spreadsheet form, and a fabric of one or more fibers of a composite glass fiber, a carbon fiber, an aramid fiber, Wherein a reinforcing sheet impregnated with any one of a resin, a polyester resin, a flan resin, and a melamine resin is formed. 삭제delete 삭제delete 제 3항에 있어서,
상기 케이블베어의 일단부분에 미끄럼 방지용 열가소성 폴리우레탄(TPU)층이 추가로 형성된 것을 특징으로 하는 케이블베어.The method of claim 3,
Further comprising a non-slip thermoplastic polyurethane (TPU) layer on one end of the cable bear.
KR1020170094553A 2017-07-26 2017-07-26 Cable―veyor KR101993804B1 (en)