KR101990825B1 - High-dom typed pot lip of manufacturing method - Google Patents

High-dom typed pot lip of manufacturing method Download PDF

Info

Publication number
KR101990825B1
KR101990825B1 KR1020180107536A KR20180107536A KR101990825B1 KR 101990825 B1 KR101990825 B1 KR 101990825B1 KR 1020180107536 A KR1020180107536 A KR 1020180107536A KR 20180107536 A KR20180107536 A KR 20180107536A KR 101990825 B1 KR101990825 B1 KR 101990825B1
Authority
KR
South Korea
Prior art keywords
glass plate
glass
glass sheet
lid
curved
Prior art date
Application number
KR1020180107536A
Other languages
Korean (ko)
Inventor
정하선
Original Assignee
정하선
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 정하선 filed Critical 정하선
Priority to KR1020180107536A priority Critical patent/KR101990825B1/en
Application granted granted Critical
Publication of KR101990825B1 publication Critical patent/KR101990825B1/en

Abstract

The present invention relates to a high-dome shaped lid made of tempered glass for a cooking vessel, which is made of tempered glass to remove a need to insert a stainless steel finishing ring into a circumferential part in order to reinforce the circumferential part so as to provide a neat appearance and be hygienic, and is relatively deeply curved to have a high dome shape so as to be useful for quickly and uniformly cooking food; a novel method for easily manufacturing the same; and a glass forming mold used for manufacturing the lid for a cooking vessel. According to the present invention, the method for manufacturing a lid for a cooking vessel comprises: a process (1) of designing and cutting an ordinary glass sheet; a process (2) of grinding a cut surface of the glass sheet cut in the process (1); a process (3) of perforating a handle mounting hole on the central part of the glass sheet whose cut surface is ground in the process (2); a process (4) of softening the glass sheet having the handle mounting hole perforated in the process (3) to curve the softened glass sheet in a dome shape; a process (5) of quenching the glass sheet curved in the dome shape in the process (4) to temper the glass sheet; and a process (6) of mounting a handle in the handle mounting hole of the glass sheet tempered in the process (5).

Description

강화유리로 이루어진 하이돔 형태의 조리용기뚜껑 제조방법{High-dom typed pot lip of manufacturing method}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a high-

본 발명은 강화유리로 이루어져서 둘레부에 스텐레스 마감링을 끼울 필요가 없으므로 외관도 깔끔하고 위생적이며, 상대적으로 깊게 만곡성형되어 하이돔 형태를 가지기 때문에 음식물을 신속하고 고르게 조리하는데 도움이 되는 강화유리로 이루어진 하이돔 형태의 조리용기뚜껑을 용이하게 제조할 수 있는 방법에 관한 것이다. The present invention is made of a tempered glass, and it is not necessary to insert a stainless steel finish ring in the periphery thereof, so that it is clean, sanitary, and has a high-dome shape with relatively deep curvature, To a method for easily manufacturing a cooking vessel lid in the form of a high dome.

흔히, 냄비나 구이판과 같은 조리용기의 뚜껑은 금속재로 이루어지거나 유리로 제조된다. 유리로 제조된 조리용기뚜껑은 뚜껑을 열지 않고도 조리용기에 담긴 음식물의 상태를 확인할 수 있는 장점이 있는데, 종래의 유리로 된 조리용기 뚜껑은 유리판의 둘레부에 스텐레스 마감링이 결합되고, 중앙부에는 손잡이가 결합되어 이루어진다.Often, the lid of a cooking vessel, such as a pot or grill, is made of metal or made of glass. The cooking lid made of glass has an advantage in that the state of food contained in the cooking liquor can be confirmed without opening the lid. The conventional lid of the cooking lid made of glass has a stainless steel finish ring at the periphery of the glass plate, Handles are combined.

그런데 이러한 종래의 유리로 된 조리용기 뚜껑은 스텐레스 마감링과 유리판 사이에 음식찌꺼지가 끼어서 잘 닦아지지 않으므로, 보기에도 좋지 좋고 비위생적인 단점을 가진다.However, such a conventional cookware lid made of glass has disadvantages in that it is good and unhygienic because it is not wiped off because the food residue is stuck between the stainless steel finishing ring and the glass plate.

한편, 조리시에 음식물이 고르게 잘 익도록 하기 위해서는 조리용기 뚜껑의 역할도 중요한데, 조리용기 뚜껑이 평면형태로 이루어진 것에 비해 중앙부가 상향으로 돌출된 만곡된 형상으로 이루어지면, 조리용기 내부의 열기가 중앙부에서 상승되어 조리뚜껑에 부딪혀서 조리뚜껑의 저면을 따라 둘레부로 이동되고 다시 중앙에서 상승되는 순환이 이루어지므로 음식물이 전체적으로 고르게 잘 익으면서도 조리시간도 단축되어 에너지도 절감되는 효과를 얻을 수 있다. 따라서 중앙부가 상향으로 돌출되도록 만곡성형된 유리냄비뚜껑이 제공되고 있다.Meanwhile, in order for the food to be uniformly cooked at the time of cooking, the role of the cooking vessel lid is also important. When the cooking vessel lid is formed in a curved shape with the central portion projecting upward compared with the flat cooking vessel, The food is lifted up at the central portion and strikes against the cooking lid, and is moved along the bottom surface of the cooking lid to the peripheral portion and then raised from the center. Thus, the cooking time is shortened while energy is also reduced. Accordingly, a glass pot lid which is curved and formed so that the central portion protrudes upward is provided.

그런데 유리를 이용하여 중앙부가 상향으로 돌출된 만곡된 형태의 조리용기 뚜껑을 만들기 위해서는 평판 형태의 유리판을 곡면을 갖도록 만곡성형하여야 하는데, 종래에는 도 1에 도시된 바와 같이 대략 45°로 경사진 경사면을 가지는 원반형태의 하부금형(9)에 평판형태의 유리판을 올려놓고 유리판을 만곡성형하기 때문에, 성형시 유리판이 하부금형에 상대적으로 넓은 면적으로 접촉되어 유리판의 표면이 매끄러운 곡면을 가지도록 성형되지 못한다.However, in order to make a curved cooking lid protruding upward in the center by using glass, a flat plate-shaped glass plate should be curved so as to have a curved surface. Conventionally, as shown in FIG. 1, The glass plate is brought into contact with a relatively large area of the lower mold at the time of molding so that the surface of the glass plate is not molded so as to have a smooth curved surface can not do it.

그리고 이러한 이유로 인해 종래에는 유리판을 상대적으로 깊이 있게 만곡변형시키기 곤란한 문제점이 있으며, 따라서 비교적 깊은 깊이로 만곡된 하이돔 형태의 조리용기뚜껑을 제조하기도 곤란하였다. For this reason, conventionally, there is a problem that it is difficult to deform the glass plate with a relatively deep depth, and thus it is also difficult to manufacture a high-dome cooking container lid having a relatively deep depth.

대한민국 공개특허 제10-2012-0065759호(2012. 06. 21.)Korean Patent Publication No. 10-2012-0065759 (June 21, 2012)

본 발명은 상기와 같은 문제점에 착안하여 제안된 것으로서, 강화유리로 이루어져서 둘레부를 보강을 위해 스텐레스 마감링을 끼울 필요가 없으므로 외관도 깔끔하고 위생적이며, 상대적으로 깊게 만곡성형되어 하이돔 형태를 가지기 때문에 음식물을 신속하고 고르게 조리하는데 도움이 되는 강화유리로 이루어진 하이돔 형태의 조리용기뚜껑과, 이를 용이하게 제조할 수 있는 새로운 방법 및 이러한 조리용기뚜껑의 제조에 사용되는 유리성형금형을 제공하는 것이다.SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned problems, and it is an object of the present invention to provide a high dome shape, which is made of tempered glass and has a high dome shape because it does not need to insert a stainless steel finish ring for reinforcing the periphery, A high-dome cooking vessel lid made of tempered glass to help quickly and uniformly cook the cooking cavity lid, a new method for easily manufacturing the lid, and a glass forming die used for manufacturing such a cooking vessel lid.

본 발명의 일 특징에 따르면, (1) 일반 유리판을 재단하여 절단하는 과정;According to an aspect of the present invention, there is provided a method of manufacturing a glass plate, comprising the steps of: (1) cutting and cutting a plain glass plate;

(2) 상기 (1)과정에서 절단된 유리판의 절단면을 연마하는 과정; (3) 상기 (2)과정에서 절단면이 연마된 유리판의 중앙부에 손잡이장착공을 천공하는 과정; (4) 상기 (3)과정에서 손잡이장착공이 천공된 유리판을 연화시켜서 돔형태로 만곡성형하는 과정; (5) 상기 (4)과정에서 돔형태로 만곡성형된 유리판을 급랭시켜 강화시키는 과정; 및 (6) 상기 (5)과정에서 강화된 유리판의 손잡이장착공에 손잡이를 장착하는 과정;을 포함하는 것을 특징으로 조리용기뚜껑 제조방법 및 이에 의해 제조된 조리용기뚜껑이 제공된다. (2) polishing the cut surface of the glass sheet cut in the step (1); (3) a process of drilling a handle mounting hole at a central portion of a glass plate having a cutting surface polished in the step (2); (4) softening the glass plate in which the handle mounting hole is perforated in the step (3) to form a dome shape; (5) a process of quenching and tempering a glass plate curved in a dome shape in the process (4); And (6) attaching the handle to the handle mounting hole of the glass plate reinforced in the step (5). The method of manufacturing the lid of the cooking lid and the lid of the cooking lid manufactured thereby are provided.

본 발명의 다른 특징에 따르면, 상기 (4)과정은 원반형상을 가지는 하부금형(10)에 상기 유리판을 올려놓고, 유리판을 올려놓은 하부금형(10)을 가열로에 넣어서 유리판을 연화시키면서, 상부금형(20)으로 유리판을 눌려서 이루어지며,According to another aspect of the present invention, in the step (4), the glass plate is placed on the lower mold 10 having a disk shape, and the lower mold 10 on which the glass plate is placed is placed in a heating furnace to soften the glass plate, Is formed by pressing a glass plate with a mold (20)

상기 하부금형(10)은 외측으로 갈수록 상향으로 돌출되는 경사면을 갖는 중앙급경사부(12); 및 상기 중앙급경사부(12)의 둘레부에 구비되어 외측으로 갈수록 상향으로 돌출되는 경사면을 가지되 상기 중앙급경사부(12)에 비해 완만한 경사면을 가지는 완경사둘레부(14);로 이루어진다.The lower mold (10) has a central steep sloping portion (12) having an inclined surface protruding upward toward the outer side; And a mild circumferential portion 14 provided at a circumferential portion of the central steep sloping portion 12 and having a sloping surface protruding upward toward the outer side and having a sloped surface that is gentler than the central steep sloping portion 12.

삭제delete

이상과 같은 구성을 가지는 본 발명은 다음과 같은 효과를 가진다.The present invention having the above-described configuration has the following effects.

첫째, 강화유리로 이루어져서 둘레부를 보강하기 위해 둘레부에 스텐레스 마감링을 끼울 필요가 없다. 따라서 뚜껑이 손잡이를 제외하고는 전체적으로 유리소재로 이루어지므로 보기에 깔끔하며, 종래와 같이 마감링과 유리 사이에 음식물이 끼워서 지저분해지지도 않으므로 위생적이고, 세척도 용이한 장점을 가진다.First, it is made of tempered glass and it is not necessary to insert a stainless steel finish ring in the periphery to reinforce the periphery. Therefore, the lid is made of a glass material as a whole except for the handle, so that it is neat in appearance and hygienic since the food is sandwiched between the finish ring and the glass as in the prior art.

둘째, 유리판을 비교적 깊게 만곡성형시켜서, 뚜껑이 하이돔 형태를 가지기 때문에, 조리시 조리용기 내부의 열기가 중앙부에서 상승되어 뚜껑의 만곡된 저면을 따라 외측으로 이동되어 다시 중앙에서 상승되는 순환이 이루어지므로 음식이 신속하면서 고르게 조리된다. 따라서 조리시간도 단축되고, 조리시 소비되는 에너지도 절감된다.Secondly, since the glass plate is relatively deeply curved and the lid has a high dome shape, the heat inside the cooking container is raised at the central portion during cooking, moved outward along the curved bottom surface of the lid, The food is cooked quickly and uniformly. Therefore, the cooking time is shortened and the energy consumed in cooking is also reduced.

셋째, 유리판을 하이돔 형태로 만곡성형시에 중앙급경사부와 중앙급경사부의 둘레부에 구비되어 중앙급경사부에 비해 완만한 경사면을 가지는 완경사둘레부로 이루어진 하부금형을 이용하여 유리판을 만곡성형하기 때문에, 유리판을 상대적으로 깊은 깊이로 만곡성형하여 하이돔 형태로 성형하면서도 유리판이 하부금형과 최소한으로 접촉되기 때문에, 유리판의 표면 손상이 최소화되고 표면이 매끈한 형태를 갖도록 유리판을 하이돔 형태로 만곡시킬 수 있는 장점을 가진다. Third, since the glass plate is curved and formed by using the lower metal mold having the center steep slope portion at the time of curved molding of the glass plate in the form of a high dome and the circumferential portion of the center of gravity slope at the circumferential portion of the central steep slope portion, Since the glass plate is minimally contacted with the lower mold while the glass plate is formed into a high dome shape by curving the glass plate at a relatively deep depth, it is possible to minimize the surface damage of the glass plate and to bend the glass plate into a high dome shape .

또한, 유리판의 만곡성형시에 유리판이 하부금형의 중앙급경사부와는 접촉되지 않기 때문에, 유리판을 강화시키기 위해 하부금형에 구비된 노즐을 통해 에어를 분사시키면 에어가 유리판과 원활하게 분사되어 유리판의 냉각이 한층 더 신속하게 이루어지므로 유리판도 원활하게 잘 강화되는 효과도 얻을 수 있다.In addition, since the glass plate does not come into contact with the center sharpened portion of the lower mold at the time of curving the glass plate, air is injected through the nozzle provided in the lower mold to strengthen the glass plate, The cooling can be performed more quickly, so that the glass plate can be smoothly strengthened well.

도 1은 종래 유리판 만곡성형용 하부금형의 단면도
도 2는 본 발명에서 사용되는 유리판 만곡성형용 하부금형의 단면도
도 3은 상기 하부금형을 사용하여 유리판을 만곡성형하는 과정을 보인 단면도
도 4는 상기 과정에 의해 제조된 하이돔 형태의 유리판1 is a cross-sectional view of a conventional lower mold for curved glass plate
Fig. 2 is a cross-sectional view of the lower mold for curved glass plate used in the present invention
3 is a cross-sectional view showing a process of curving and forming a glass plate using the lower mold
FIG. 4 is a graph showing the relationship between the high-dome type glass plate

이하에서, 본 발명을 구체적인 실시예를 통해 좀 더 구체적으로 설명한다. Hereinafter, the present invention will be described more specifically with reference to specific examples.

본 발명은 하이돔 형태의 조리용기뚜껑에 관한 것으로서, 도 2는 본 실시예에서 사용되는 유리판 만곡성형용 하부금형의 단면도이고, 도 3은 이러한 하부금형을 사용하여 유리판을 만곡성형하는 과정을 보인 단면도이며, 도 4는 이러한 과정을 거쳐서 성형된 하이돔 형태의 유리판(2)을 보인 사진이다. 2 is a cross-sectional view of a lower mold for bending a glass plate used in the present embodiment, and Fig. 3 is a view showing a process of curving and forming a glass plate using such a lower mold. And FIG. 4 is a photograph showing a glass plate 2 of high-dome shape formed through such a process.

본 발명에서 "하이돔 형태"는 유리판이 돔형태를 가지도록 비교적 깊게 만곡성형되어 중앙부가 상향으로 많이 돌출되어 비교적 높이가 높은 돔형태를 가진다는 것을 의미하는 것이며, 그 높이가 특정한 수치로 한정되는 개념은 아니다. In the present invention, the term " high dome type "means that the glass plate is relatively deeply curved so as to have a dome shape, and the central portion thereof protrudes upward so as to have a relatively high dome shape. It is not a concept.

이러한 본 발명은 다음과 같은 방법으로 제조된다. The present invention is produced by the following method.

1) 유리판을 재단 및 절단하는 과정1) The process of cutting and cutting the glass plate

일반 유리판을 원하는 크기로 재단하여 절단한다. 바람직하게는 후술하는 돔성형과정에서 유리판이 만곡되어 단부의 직경이 축소되므로 이를 감안하여 유리판을 재단 및 절단한다. Cut the glass plate to the desired size and cut it. Preferably, the glass plate is bent and the diameter of the end portion is reduced in the dome forming process described later, so that the glass plate is cut and cut in consideration of this.

일반적으로 조리용기는 원형 또는 사각형으로 이루어지므로 이러한 조리용기의 형태에 따라 뚜껑도 원형 또는 사각형으로 제조되어야 한다, 따라서 본 과정에서는 유리판을 사각 또는 원형으로 재단하여 절단한다. Generally, since the cooking vessel is formed of a circular or square shape, the lid must also be formed in a circular or square shape according to the shape of the cooking vessel. Therefore, in this procedure, the glass plate is cut into a rectangular or circular shape and cut.

2) 유리판의 절단면 연마과정2) Polishing process of cut surface of glass plate

절단된 유리판의 절단면을 연마하여 다듬어서 광택처리한다.The cut surface of the cut glass plate is polished and polished.

3) 손잡이장착구멍 천공과정3) Handle mounting hole drilling process

절단한 유리판의 중앙부에 뚜껑의 손잡이를 장착하기 위한 손잡이장착구멍(4)을 천공한다. A handle mounting hole (4) for mounting the handle of the lid is formed at the center of the cut glass plate.

4) 유리판 만곡성형과정4) Bending process of glass plate

손잡이장착구멍(4)을 천공한 유리판을 가열로에 넣어 유리판을 돔형태로 만곡성형시킨다. 본 과정에서는 유리판을 도 2에 도시된 바와 같은 하부금형(10)에 올려놓은 상태에서 가열로에 넣고 가열하여 유리판을 연화시키며, 도 3에 도시된 바와 같이, 상부금형(30)으로 연화된 유리판을 가압하여 유리판을 돔형상으로 성형한다. 이때 가열로의 온도를 700~750℃로 올려서 유리판을 급가열하여 연화시키는데, 유리판이 연화되어 상, 하부금형(10,20) 사이에서 변형됨에 따라 돔형상으로 만곡성형된다.A glass plate in which the handle mounting hole 4 is drilled is placed in a heating furnace, and the glass plate is curved and formed into a dome shape. In this process, the glass plate is placed in a heating furnace with the glass plate placed on the lower mold 10 as shown in FIG. 2 and heated to soften the glass plate. As shown in FIG. 3, The glass plate is molded into a dome shape. At this time, the temperature of the heating furnace is raised to 700 to 750 ° C to soften the glass plate by rapid heating. As the glass plate is softened and deformed between the upper and lower molds 10 and 20, the glass plate is curved into a dome shape.

본 과정에서 사용하는 하부금형(10)은 전체적으로 원반형상을 가지는데, 도 2, 3에 도시된 바와 같이, 외측으로 갈수록 상향으로 돌출되는 경사면을 가지는 중앙급경사부(12)와, 중앙급경사부(12)의 둘레부에 구비되어 외측으로 갈수록 상향으로 돌출되는 경사면을 가지되 상기 중앙급경사부(12)에 비해 상대적으로 완만한 경사면을 이루는 완경사둘레부(14)로 이루어진다. As shown in FIGS. 2 and 3, the lower mold 10 used in this process has a disc shape as a whole, and includes a central steep sloping portion 12 having an inclined surface protruding upward toward the outside, and a central steep sloping portion 12, and has a sloped surface protruding upward toward the outer side, and a mild circumferential portion 14 having a relatively sloped surface relative to the central steep sloped portion 12.

한편, 상부금형(20)도 도시된 바와 같이, 만곡된 저면을 가지는데, 바람직하게는 상부금형(20)의 저면은 중앙부만 부분적으로 유리판에 접촉되도록 그 형태가 조절된다. The upper mold 20 also has a curved bottom surface. Preferably, the bottom surface of the upper mold 20 is shaped so that only the center portion is partially in contact with the glass plate.

따라서 상기 하부금형(10)에 유리판을 올려놓고 상부금형(20)으로 유리판을 누르면, 도 3에 도시된 바와 같이, 연화된 유리판의 하측으로 향하는 면의 둘레부 일부만 하부금형(10)과 닿게 되고, 유리판을 깊게 만곡성형시켜도 유리판의 하측으로 항햐는 면이 중앙급경사부(12)와 닿지 않으므로 유리판을 상대적으로 깊에 만곡성형시켜서 하이돔 형태로 성형할 수 있다. Therefore, when the glass plate is placed on the lower mold 10 and the glass plate is pressed by the upper mold 20, only a part of the periphery of the downwardly facing surface of the softened glass plate is contacted with the lower mold 10 , Even if the glass plate is formed to be deeply curved, the surface of the glass plate which does not contact the lower side of the glass plate does not contact the central steepening portion 12, so that the glass plate can be formed into a high dome shape by curving the glass plate relatively deeply.

또한, 이때 상부금형(20)도 중앙부 일부가 유리판의 상측으로 향하는 면과 부분적으로 닿게 된다. At this time, part of the center portion of the upper mold 20 also partially touches the upper surface of the glass plate.

즉, 본 발명에서는 하부금형(10)의 중앙부위가 완경사둘레부(14)에 비해 급경사면을 가지는 중앙급경사부(12)로 이루어져서 유리판이 깊게 만곡성형되어도 유리판이 중앙급경사부(12)와 닿지 않기 때문에, 유리판이 하부금형(10)에 접촉되는 면적이 최소화된다. 따라서 유리판을 상대적으로 깊게 만곡성형시켜도 유리판의 표면에 손상이 가급적 발생되지 않으므로 유리판을 매끄러운 표면을 가지는 하이돔 형태로 용이하게 성형할 수 있다. 또한, 상부금형(20)의 저면도 유리판과 부분적으로 접촉되기 때문에 유리판 표면의 손상이 최소화된다.That is, in the present invention, the central portion of the lower mold 10 is composed of the central steep sloping portion 12 having a steeply sloped surface compared to the mild circumferential portion 14 so that the glass plate touches the central steep sloping portion 12 The area in which the glass plate contacts the lower mold 10 is minimized. Therefore, even if the glass sheet is curved relatively deeply, damage to the surface of the glass sheet is not generated as much as possible, so that the glass sheet can be easily formed into a high-dome shape having a smooth surface. In addition, since the bottom surface of the upper mold 20 is also partially in contact with the glass plate, damage to the glass plate surface is minimized.

바람직하게는 상기 중앙급경사부(12)는 경사도가 55~60°정도이고, 완경사둘레부(14)는 45° 정도의 경사도를 가지며, 하부금형이 이러한 규격을 가질 때 높이가 4~5cm 정도 되도록 비교적 높이가 높은 하이돔 형태로 유리판을 성형할 수 있다. 그리고 유리판이 4~~5cm 정도의 높이를 가지는 경우에, 보기에도 좋으며, 후술하는 바와 같이, 조리시 조리용기 내부의 열순환이 원활하게 이루어진다. Preferably, the central steep sloping portion 12 has an inclination of about 55 to 60 degrees, the soft rubber circumferential portion 14 has an inclination of about 45 degrees, and the height of the lower mold is about 4 to 5 cm The glass plate can be formed in a high-dome shape having a relatively high height. In the case where the glass plate has a height of about 4 to 5 cm, it may be seen. As will be described later, the inside of the cooking container is smoothly circulated thermally.

5) 유리강화과정5) Glass strengthening process

상기 과정에서 성형된 하이돔 형태의 유리판(2)을 급랭시켜서 하이돔 형태의 유리판(2)을 강화시킨다. 이 과정은 하이돔 형태의 유리판(2)이 거치된 상태의 상, 하부금형(10,20)을 가열로에서 인출시켜서, 하이돔 형태의 유리판(2)을 공기로 급냉시켜 이루어진다. In the above process, the formed high-dome glass plate 2 is quenched to reinforce the high-dome glass plate 2. In this process, the upper and lower dies 10, 20 in a state in which the glass plate 2 in the form of a high dome is mounted are drawn out from the heating furnace, and the glass plate 2 in the form of a high dome is quenched with air.

도시된 바와 같이, 상기 상, 하부금형(10,20)에는 하이돔 형태의 유리판(2)에 공기를 분사시키기 위한 급기노즐(13,23)이 촘촘히 배열되고, 급기노즐(13,23)에는 공기가 저장된 공기탱크가 연결되어, 급기노즐(13,23)을 통해 하이돔 형태의 유리판(2)에 공기가 분사된다. As shown in the drawing, the upper and lower dies 10 and 20 are closely arranged with air supply nozzles 13 and 23 for injecting air into a high-dome glass plate 2, and air supply nozzles 13 and 23 Air is stored in the air tank, and air is injected into the high-dome glass plate 2 through the air supply nozzles 13,

특히, 본 발명에서는 전술한 바와 같이, 하부금형(10)의 중앙부를 이루는 급경사중앙부(12)가 하이돔 형태의 유리판(2)에 닿지 않기 때문에, 하부금형(10)의 급기노즐(13)을 통해 분사되는 공기가 하이돔 형태의 유리판(2)에 원활하게 분사되고, 이에 따라 유리의 냉각이 한층 더 신속하게 이루어진다. Particularly, in the present invention, as described above, since the steep slanting center portion 12 forming the central portion of the lower mold 10 does not touch the glass plate 2 of the high dome type, the supply nozzle 13 of the lower mold 10 Air is injected smoothly into the high-dome glass plate 2, whereby the cooling of the glass is performed more rapidly.

이와 같이 하이돔 형태의 유리판(2)이 급랭됨에 따라 유리판이 강화된다. 도 3은 이러한 강화과정을 거친 하이돔 형태의 유리판(2)을 보인 사진이다.As the high-dome glass plate 2 is rapidly cooled, the glass plate is strengthened. FIG. 3 is a photograph showing a glass plate 2 of a high dome type having undergone such strengthening process.

6) 손잡이장착과정6) Handle mounting process

상기와 같이 강화처리된 하이돔 형태의 유리판(2)에 손잡이(미도시)를 장착하여 조리용기뚜껑을 완성한다. A handle (not shown) is attached to the high-dome glass plate 2 reinforced as described above to complete the cooking lid.

이상과 같은 구성을 가지는 본 발명은 유리판을 표면 손상없이 하이돔 형태로 깊게 만곡성형하여 조리용기뚜껑을 만들 수 있다. 따라서 일반 유리판을 이용하여 외관이 미려한 하이돔 형태의 강화유리로 된 조리용기뚜껑을 용이하게 제조할 수 있으며, 특히, 본 발명에 의해 제조되는 조리용기뚜껑은 강화유리로 이루어져서 둘레부가 쉽게 손상되지 않기 때문에 둘레부를 보강하기 위해 스텐레스 마감링을 끼울 필요가 없다. 따라서 유리로 된 조리용기뚜껑에 있어서 스텐레스 마감링과 유리 사이에 음식물이 끼어서 지저분해지는 문제가 발생되지 않는다.According to the present invention having the above-described structure, the glass plate can be formed into a high-dome shape by deeply curving and forming a lid of a cooking vessel without surface damage. Therefore, it is possible to easily manufacture a cooking vessel lid made of a tempered glass of a high dome type having an excellent appearance using an ordinary glass plate. In particular, the cooking vessel lid manufactured by the present invention is made of tempered glass, Therefore, it is not necessary to insert the stainless steel finish ring to reinforce the circumference. Therefore, there is no problem that the food is caught between the stainless steel finish ring and the glass in the lid of the glass-made cooking container, thereby becoming dirty.

뿐만 아니라 본 발명에 의해 제조되는 조리용기뚜껑은 하이돔 형태를 가지기 때문에, 조리시 조리용기 내부의 열기가 중앙부에서 상승되어 뚜껑의 만곡된 저면을 따라 외측으로 이동되고 다시 중앙에서 상승되는 순환이 원활히 이루어지므로 조리가 신속하면서도 고르게 잘 익게 된다. 따라서 조리시간이 단축되고, 이에 따라 조리시 소비되는 에너지도 절감된다.In addition, since the cooking lid manufactured by the present invention has a high dome shape, the heat inside the cooking liquor during the cooking is raised at the central portion, moved outward along the curved bottom surface of the lid, So that the cooking is quick and evenly ripened. Therefore, the cooking time is shortened, and thus the energy consumed in cooking is also reduced.

Claims (5)

(1) 일반 유리판(2)을 재단하여 절단하는 과정;
(2) 상기 (1)과정에서 절단된 유리판의 절단면을 연마하는 과정;
(3) 상기 (2)과정에서 절단면이 연마된 유리판(2)의 중앙부에 손잡이장착공(4)을 천공하는 과정;
(4) 상기 (3)과정에서 손잡이장착공(4)이 천공된 유리판(2)을 가열로의 온도를 700~750℃로 올려서 유리판(2)을 급가열하여 연화시켜서 돔형태로 만곡성형하되, 원반형상을 가지며, 외측으로 갈수록 상향으로 돌출되는 경사면을 갖는 중앙급경사부(12) 및 상기 중앙급경사부(12)의 둘레부에 구비되어 외측으로 갈수록 상향으로 돌출되는 경사면을 가지되 상기 중앙급경사부(12)에 비해 완만한 경사면을 이루는 완경사둘레부(14)로 이루어진 하부금형(10)에 상기 유리판(2)을 올려놓고, 유리판(2)을 올려놓은 하부금형(10)을 가열로에 넣어서 유리판(2)을 연화시키면서, 상부금형(20)으로 유리판(2)을 눌러서 만곡성형하는 과정;
(5) 상기 (4)과정에서 돔형태로 만곡성형된 유리판(2)을 급랭시켜 강화시키는 과정; 및
(6) 상기 (5)과정에서 강화된 유리판(2)의 손잡이장착공(4)에 손잡이를 장착하는 과정;을 포함하는 것을 특징으로 조리용기 뚜껑제조방법.
(1) Cutting and cutting a plain glass sheet (2);
(2) polishing the cut surface of the glass sheet cut in the step (1);
(3) a step of drilling the handle mounting hole 4 at the center of the glass sheet 2 having the cut surface polished in the step (2);
(4) In the step (3), the glass plate 2 with the handle mounting holes 4 is heated to 700-750 ° C. to heat the glass plate 2 so that the glass plate 2 is softened and curved in a dome shape A central steep sloping portion 12 having a disk shape and having an inclined surface protruding upward toward the outside and a sloping surface provided on the circumferential portion of the central steep sloping portion 12 and protruding upward toward the outside, The glass plate 2 is placed on a lower mold 10 made of a soft circumferential portion 14 having a gentle slope as compared with the portion 12 and the lower mold 10 on which the glass plate 2 is placed is placed in a heating furnace Pressing the glass plate 2 with the upper mold 20 while curving the glass plate 2 by softening the glass plate 2;
(5) a process of quenching and strengthening the glass plate 2 curved in a dome shape in the process (4); And
(6) A method for manufacturing a lid of a cooking container, comprising the steps of: (a) fitting a handle to a handle mounting hole (4) of a glass plate (2) reinforced in the step (5).
삭제delete 삭제delete 삭제delete 삭제delete
KR1020180107536A 2018-09-10 2018-09-10 High-dom typed pot lip of manufacturing method KR101990825B1 (en)