KR101957115B1 - Seam sealing tape and manufacturing method thereof - Google Patents

Seam sealing tape and manufacturing method thereof Download PDF

Info

Publication number
KR101957115B1
KR101957115B1 KR1020180154912A KR20180154912A KR101957115B1 KR 101957115 B1 KR101957115 B1 KR 101957115B1 KR 1020180154912 A KR1020180154912 A KR 1020180154912A KR 20180154912 A KR20180154912 A KR 20180154912A KR 101957115 B1 KR101957115 B1 KR 101957115B1
Authority
KR
South Korea
Prior art keywords
adhesive
layer
waterproof film
film layer
adhesive layer
Prior art date
Application number
KR1020180154912A
Other languages
Korean (ko)
Inventor
차진섭
Original Assignee
주식회사 실론
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 실론 filed Critical 주식회사 실론
Priority to KR1020180154912A priority Critical patent/KR101957115B1/en
Application granted granted Critical
Publication of KR101957115B1 publication Critical patent/KR101957115B1/en

Abstract

The present invention, in order to prevent grin-through phenomenon near a sewing line (15) of an outdoor garment to which a seam sealing tape (100) is attached thereto, relates to: the seam sealing tape comprising a first adhesive layer (40) formed by using a hot-melt type adhesive or a solvent type adhesive into which one or more coloring agents selected from a group consisting of dyes, pigments, and paints is mixed thereinto; and the outdoor garment using the same.

Description

심실링 테이프 및 그 제조방법 { Seam sealing tape and manufacturing method thereof }[0001] SEAMING TAPE AND MANUFACTURING METHOD [0002]

본 발명은 심실링 테이프에 관한 것으로, 원단층과 방수필름층 및 착색제가 혼입된 핫멜트형 접착제 또는 용제형 접착제를 이용하여 형성되는 제 1 접착제층을 포함하는 심실링 테이프 및 이를 이용한 아웃도어용 의류에 관한 것이다. The present invention relates to a ventricular ring tape, and more particularly, to a ventricular ring tape comprising a first adhesive layer formed by using a hot melt adhesive or a solvent adhesive mixed with an outer layer, a waterproof film layer and a colorant, .

심실링 테이프(seam sealing tape)는 도 1과 같이 의복 원단(14)의 봉제선(15) 부위에 접착하는 테이프로서 외부로부터 수분이 봉제선(15)의 바늘 구멍을 통해 의복 내부로 침투하는 것을 방지하는 기능을 하게 된다. The seam sealing tape is a tape that adheres to the area of the sewing line 15 of the garment fabric 14 as shown in Fig. 1 and prevents moisture from penetrating into the inside of the garment through the needle opening of the sewing line 15 Function.

최근에는 아웃도어 의류의 착용이 확대되면서 심실링 테이프(100)의 용도가 아웃도어 의류 등으로 확대되면서 이에 대한 수요가 증가하고 있다.In recent years, the use of the ventricular ring tape 100 has expanded to outdoor clothes as the wear of outdoor clothing has expanded, and the demand for the ventricular ring tape 100 is increasing.

도 2에 도시된 바와 같이, 아웃도어 의류 등의 원단(14)의 봉제선(15) 부분에 심실링 테이프(100)를 부착하면 등산, 스키와 같은 야외 활동 시 빗물 등의 수분이 외부에서 봉제선(15)의 바늘 구멍을 통하여 침투하는 것을 방지함으로써 쾌적한 의복내 환경을 구현할 수 있다. As shown in FIG. 2, when the ventricular ring tape 100 is attached to the sewing line 15 of the fabric 14 such as outdoor clothing, moisture such as rainwater during outdoor activities such as mountain climbing and skiing, 15), it is possible to realize a comfortable environment of the clothes.

통상의 심실링 테이프(100)는 도 2에 도시된 바와 같이, 원단층(10)과, 폴리비닐클로라이드(Polyvinylchloride), 폴리에스테르(Polyester), 폴리아미드(Polyamide) 및 폴리우레탄(Polyurethane) 등으로 제조되는 방수필름층(20) 및 상기 방수필름층(20)의 하부에 접착제층(35)을 형성한 후 건조시켜서 제조하게 된다. 2, the conventional ventricular ring tape 100 comprises an outer layer 10 and a layer made of polyvinylchloride, polyester, polyamide, and polyurethane, and the like. The waterproof film layer 20 to be manufactured and the adhesive layer 35 are formed on the lower part of the waterproof film layer 20, followed by drying.

상기와 같이 제조된 심실링 테이프(100)는 안감과 겉감 사이의 봉제선(15) 상에 구비된 상태에서 봉제하고, 여기에 열풍을 가해 심실링 테이프(100)의 접착제층(35)이 용융되면서 상기 봉제선(15)에 형성된 바늘구멍을 매워줌으로써 수분이 침투하는 것을 방지하게 된다. The ventricular ring tape 100 manufactured as described above is sewed in a state where it is provided on the sewing line 15 between the lining and the outer surface and the adhesive layer 35 of the ventricular ring tape 100 is melted The needle hole formed in the sewing line 15 is worn to prevent moisture from penetrating.

상기와 같은 심실링 테이프(100)에 대한 종래기술을 살펴보면, 대한민국 등록특허공보 제10-0944767호(2010. 03. 03.)에는 이형지상에 핫멜트 접착제층 및 폴리우레탄 수지로 제조된 내열성수지 필름층이 순차 합지된 심실링테이프 제작용 원단을 제조하고, 상기 원단 중 내열성수지 필름층 상에, 표면처리제 수지 조성물이 패턴 형상으로 전사코팅된 의류봉제용 심실링 테이프(100)의 제조방법이 제시되어 있고, 대한민국 공개특허공보 제10-2012-0118226호(2012. 10. 26.)에는 소수성계 폴리우레탄 수지 성분으로 이루어지며 미세 공극이 형성되어 투습성을 갖는 필름층과, 투습성을 갖는 친수성계 폴리우레탄 수지 성분으로 이루어진 접착층이 합포되어 제조되는 심실링 테이프(100)가 제시되어 있다.[0004] In the prior art for the ventricular ring tape 100, Korean Patent Registration No. 10-0944767 (Mar. 03, 2010) discloses a heat-resistant resin film made of a hot-melt adhesive layer and a polyurethane resin A manufacturing method of a ventricular ring tape (100) for garment sewing in which a fabric for producing a ventricular ring tape in which layers are successively laminated and a surface treatment agent resin composition is transferred and coated on the heat-resistant resin film layer in the fabric is presented Korean Patent Laid-Open Publication No. 10-2012-0118226 (Oct. 26, 2012) discloses a film layer comprising hydrophobic polyurethane resin components and having micropores formed therein and having moisture permeability, and a hydrophilic poly A ventricular ring tape 100 in which an adhesive layer made of a urethane resin component is assembled is proposed.

상기와 같이 종래의 심실링 테이프(100)는 방수필름층에 의해 방수성이 부여되며, 이때 사용되는 접착제층(35)은 색상이 부여되지 않은 투명한 핫멜트 접착제를 사용하게 된다. As described above, the conventional ventricular ring tape 100 is waterproofed by the waterproof film layer, and the adhesive layer 35 used at this time uses a transparent hot-melt adhesive without color.

그런데 최근에 아웃도어 의류의 경량화가 요구됨에 따라, 상기 아웃도어 의류를 구성하는 겉감과 안감 및 투습방수성 멤브레인의 경량화를 위하여 두께가 얇은 이들 제품을 사용하게 된다. 그런데 상기와 같이 두께가 얇은 겉감과 안감 및 투습방수성 멤브레인을 사용하여 아웃도어 의류를 제조할 때, 색상이 부여되지 않은 투명한 핫멜트 접착제를 사용하여 형성된 접착제층(35)을 구비하는 심실링 테이프(100)를 부착하는 경우에 도 3과 같이 상기 심실링 테이프(100)가 부착된 봉제선(15) 부분의 아웃도어 의류의 안감의 색상이 두께가 얇은 겉감 및 투습방수성 맴브레인을 통해 외부로 비쳐보이는 그린 스루(Grin-through) 현상이 발생하게 된다. In recent years, since outdoor clothing has been required to be lightweight, thinner products such as outerwear, lining and moisture-permeable and waterproof membranes are used. However, when fabricating outdoor clothing using a thin outer layer, a lining, and a breathable and waterproofing membrane as described above, it is preferable that a ventricular ring tape 100 (100) having an adhesive layer 35 formed by using a transparent hot- The color of the lining of the outdoor garment of the portion of the sewing line 15 to which the ventricular ring tape 100 is attached is set to a thin outer layer and a greensurface portion which is visible through the breathable waterproof membrane (Grin-through) phenomenon occurs.

즉, 도 3을 살펴보면, 아웃도어 의류의 제조시 봉제선(15)에는 원단층(10)과 방수필름층(20) 및 접착제층(35)으로 구성되는 심실링 테이프(100)를 부착하게 된다. 이때 상기 아웃도어 의류를 제조하기 위한 원단은 통상적으로 겉감과 안감 및 상기 겉감과 안감 사이에 투습방수성 멤브레인이 구비된다. 3, a ventricular ring tape 100 composed of an outer layer 10, a waterproof film layer 20, and an adhesive layer 35 is attached to the sewing line 15 at the time of manufacturing outdoor clothing. At this time, the fabric for manufacturing the outdoor clothing is usually provided with a breathable and waterproof membrane between the outer and inner lining and between the outer and lining.

상기와 같이 구성되는 심실링 테이프(100)를 아웃도어 의류의 봉제선(15)에 위치시킨 후, 열풍을 가하여 상기 심실링 테이프(100)를 부착하게 된다. The ventricular ring tape 100 configured as described above is placed on the sewing line 15 of the outdoor wear and then the ventricular ring tape 100 is attached by applying hot air.

그런데 도 3에 도시된 바와 같이, 상기 심실링 테이프(100)에 열풍을 가하여 봉제선(15)에 부착할 때, 아웃도어 의류의 구비되는 투습방수성 멤브레인이 열에 의해 투명화되면서 안감의 색상이 두께가 얇은 아웃도어 의류의 겉감의 외부로 비쳐 보이는 그린 스루(Grin-Through) 현상이 발생하게 된다. 3, when the ventilation ring tape 100 is attached to the sewing line 15 by applying hot air to the ventilation ring tape 100, the moisture-permeable and waterproof membrane provided in the outdoor garment is made transparent by heat and the color of the lining is thin A grin-through phenomenon appears in the outer surface of outdoor clothes.

상기와 같이 아웃도어 의류에서 그린 스루 현상이 발생하게 되면, 제조된 상기 아웃도어 의류에서 심실링 테이프(100)가 부착된 부위가 미관상 좋지 않게 되며, 상기 심실링 테이프(100)의 존재가 외부로 드러나게 된다. If the green wear phenomenon occurs in the outdoor clothing as described above, a portion where the ventricular ring tape 100 is attached to the manufactured outdoor clothing becomes unfeasible, and the presence of the ventricular ring tape 100 may cause external It is revealed.

이에 따라 제조된 아웃도어 의류의 봉제선(15) 부근에서 심실링 테이프(100)의 부착 여부가 드러남에 따라 제조된 아웃도어 의류의 상품성이 떨어지게 되는 문제점이 있다. 또한 상기와 같은 그린 스루 현상을 방지하기 위하여 두꺼운 겉감과 안감 및 투습방수성 멤브레인을 사용하여 아웃도어 의류를 제조하게 되면, 경량화가 불가능하게 되고, 공기 투과성의 저하로 인하여 착용자에게 불쾌감을 주게 된다. 또한 제조된 아웃도어 의류가 뻣뻣하게 되어 촉감이 불량하게 되는 문제점이 있다.As a result, as the presence or absence of the ventricular ring tape 100 is revealed in the vicinity of the sewing line 15 of the manufactured outdoor garment, there is a problem that the commercial quality of the outdoor garment manufactured is deteriorated. In addition, when outdoor clothing is manufactured using a thick outer material, a lining and a breathable and waterproofing membrane to prevent the above-described grease penetration, it is impossible to reduce the weight, and the air permeability is reduced. In addition, there is a problem that the manufactured outdoor clothes become stiff and the touch feeling becomes poor.

본 발명은 상기와 같은 종래기술의 문제점을 해결하기 위하여 개발된 것으로, 심실링 테이프(100)가 부착되는 아웃도어 의류의 봉제선(15) 부근에서 그린 스루(Grin-through) 현상을 방지하기 위한 심실링 테이프(100) 및 이를 이용한 아웃도어용 의류에 관한 것이다. 그러나, 본 발명의 해결하고자 하는 과제는 이상에서 언급한 과제에 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 통상의 기술자에게 명확하게 이해될 수 있을 것이다.SUMMARY OF THE INVENTION The present invention has been developed in order to solve the problems of the related art as described above, and it is an object of the present invention to provide a ventilator for preventing a grease-through phenomenon in the vicinity of a sewing line 15 of an outdoor garment to which a ventricular ring tape 100 is attached. The present invention relates to a ring tape 100 and clothes for outdoor wear using the same. However, the problems to be solved by the present invention are not limited to the above-mentioned problems, and other matters not mentioned can be clearly understood by those skilled in the art from the following description.

상기 과제를 해결하기 위한 본 발명의 심실링 테이프(100)는, 원단층(10); 상기 원단층(10)의 하부에 구비되는 방수필름층(20); 및 상기 방수필름층(20)의 하부에 구비되되, 착색제가 혼입된 핫멜트형 접착제 또는 용제형 접착제로 형성되는 제 1 접착제층(40);을 포함하거나 또는 원단층(10); 상기 원단층(10)의 하부에 구비되는 방수필름층(20); 상기 방수필름층(20)의 하부에 구비되되, 착색제가 혼입되지 않은 핫멜트형 접착제 또는 용제형 접착제로 형성되는 제 2 접착제층(30); 및 상기 제 2 접착제층(30)의 하부에 구비되되, 착색제가 혼입된 핫멜트형 접착제 또는 용제형 접착제로 형성되는 제 1 접착제층(40);을 포함하는 것이 바람직하다. A ventricular ring tape (100) according to the present invention for solving the above-mentioned problems comprises an artificial layer (10); A waterproof film layer 20 provided at the lower part of the monolayer 10; And a first adhesive layer (40) formed on the lower part of the waterproof film layer (20) and made of a hot melt adhesive or a solvent adhesive mixed with a colorant; A waterproof film layer 20 provided at the lower part of the monolayer 10; A second adhesive layer 30 provided below the waterproof film layer 20, the second adhesive layer 30 being formed of a hot-melt type adhesive or a solvent type adhesive in which no colorant is mixed; And a first adhesive layer 40 provided under the second adhesive layer 30 and formed of a hot-melt type adhesive or a solvent type adhesive mixed with a coloring agent.

상기 착색제는 안료, 염료 및 도료로 이루어진 그룹으로부터 선택되는 하나 이상이며, 상기 착색제는 0.5 ~ 56 중량%로 혼입되고, 상기 제 1 접착제층(40)의 두께는 0.001 ~ 3 mm이며, 상기 방수필름층(20)의 두께는 5 ~ 70 ㎛인 것이 바람직하다. Wherein the colorant is at least one selected from the group consisting of pigments, dyes and paints, the colorant is incorporated at 0.5 to 56 wt%, the thickness of the first adhesive layer (40) is 0.001 to 3 mm, The thickness of the layer 20 is preferably 5 to 70 탆.

또한, 상기 방수필름층(20)은 가요성이 있는 필름을 사용하거나 또는 용액 캐스팅 방법으로 형성되며, 상기 원단층(10)은 직물 또는 편물로 구성되는 것이 바람직하다. 이때, 상기 직물 또는 편물은 폴리에스테르, 폴리아미드, 폴리우레탄, 폴리에틸렌, 폴리프로필렌, 폴리부타디엔, 셀룰로오스계 재생섬유, 천연섬유로 구성되는 그룹으로부터 선택되는 어느 하나 이상으로 제조되며, 상기 직물의 경사 및 위사의 밀도는 10 ~ 250 개/인치이며, 편물은 평량이 500 g/m2 이하이며, 상기 심실링 테이프(100)의 폭은 5 ~ 300 mm이고, 두께는 90 ~ 700 ㎛ 인 것이 바람직하다. In addition, the waterproof film layer 20 is formed by using a flexible film or a solution casting method, and the monolayer 10 is preferably composed of a fabric or a knitted fabric. At this time, the fabric or knitted fabric is made of at least one selected from the group consisting of polyester, polyamide, polyurethane, polyethylene, polypropylene, polybutadiene, cellulose-based regenerated fiber and natural fiber, It is preferable that the weft density is 10 to 250 / inch, the knitted fabric has a basis weight of 500 g / m 2 or less, the width of the ventricular ring tape 100 is 5 to 300 mm, and the thickness is 90 to 700 μm .

본 발명에 따른 심실링 테이프(100)의 제조방법은, 원단층(10)을 준비하는 제 1 단계; 방수필름층(20)을 준비하는 제 2 단계; 상기 원단층(10)과 방수필름층(20)을 합포하는 제 3 단계; 및 상기 접착된 방수필름층(20)의 하부에 제 1 접착제층(40)을 형성하는 제 4 단계;로 구성되되, 상기 제 1 접착제층(40)은 안료, 염료 및 도료로 이루어진 그룹으로부터 선택되는 하나 이상의 착색제가 혼입된 핫멜트형 접착제 또는 용제형 접착제를 이용하여 형성되거나, 또는 원단층(10)을 준비하는 제 1 단계; 방수필름층(20)을 준비하는 제 2 단계; 상기 원단층(10)과 방수필름층(20)을 합포하는 제 3 단계; 상기 접착된 방수필름층(20)의 하부에 착색제가 혼입되지 않은 핫멜트형 접착제 또는 용제형 접착제를 이용하여 제 2 접착제층(30)을 형성하는 제 4 단계; 및 상기 제 2 접착제층(30)의 하부에 제 1 접착제층(40)을 형성하는 제 5 단계;로 구성되되, 상기 제 1 접착제층(40)은 안료, 염료 및 도료로 이루어진 그룹으로부터 선택되는 하나 이상의 착색제가 혼입된 핫멜트형 접착제 또는 용제형 접착제를 이용하여 형성되는 것이 바람직하다. A method for manufacturing a ventricular ring tape (100) according to the present invention comprises: a first step of preparing an arcuate layer (10); A second step of preparing a waterproof film layer 20; A third step of fabricating the outer layer (10) and the waterproof film layer (20); And a fourth step of forming a first adhesive layer (40) on the lower side of the glued waterproof film layer (20), wherein the first adhesive layer (40) is selected from the group consisting of pigments, dyes and paints A hot-melt type adhesive or a solvent-type adhesive in which at least one coloring agent is mixed, or the first step of preparing the mono-layer 10; A second step of preparing a waterproof film layer 20; A third step of fabricating the outer layer (10) and the waterproof film layer (20); A fourth step of forming a second adhesive layer (30) using a hot-melt type adhesive or a solvent type adhesive in which a coloring agent is not mixed in the lower part of the glued waterproof film layer (20); And forming a first adhesive layer (40) under the second adhesive layer (30), wherein the first adhesive layer (40) is selected from the group consisting of pigments, dyes and paints It is preferable to use a hot-melt type adhesive or a solvent type adhesive into which at least one coloring agent is mixed.

본 발명에 의한 심실링 테이프(100)는 아웃도어 의류의 봉제선(15) 부위에서 상기 심실링 테이프(100)의 부착 여부가 외부로 드러나지 않도록 하며, 특히 아웃도어 의류의 안감의 색상이 심실링 테이프(100)의 외부로 비쳐 보이는 그린 스루(Grin-Through) 현상을 방지함으로써, 상기 아웃도어 의류의 상품성을 높이게 되는 효과를 갖는다. The ventricular ring tape 100 according to the present invention prevents the attachment of the ventricular ring tape 100 at the area of the sewing line 15 of the outdoor garment from being exposed to the outside, Through phenomenon that is visible to the outside of the outdoor unit 100, thereby improving the merchantability of the outdoor unit.

또한 그린 스루(Grin-Through) 현상을 방지함으로써 아웃도어 의류의 제조시 두께가 얇은 겉감과 안감 및 투습방수성 멤브레인의 적용이 가능하게 됨에 따라 아웃도어 의류의 경량화와 공기 투과도 및 촉감을 개선할 수 있게 된다. 그리고 제조된 아웃도어 의류의 전체적인 기능과 품질을 향상시키는 효과를 갖는다. In addition, by preventing the green-through phenomenon, it is possible to apply a thin outer surface, lining and breathable and waterproof membrane in the manufacture of outdoor clothes, thereby improving the lightness of outdoor clothing, improving air permeability and feel do. And has an effect of improving the overall function and quality of the outdoor clothing manufactured.

도 1은 종래기술에 따른 심실링 테이프(100)를 의류의 봉제부에 적용한 것을 나타내는 모식도이며,
도 2는 종래기술에 따른 심실링 테이프(100)를 적용한 의류를 나타내는 모식도이며,
도 3은 아웃도어 의류에서 그린 스루 현상을 설명하기 위한 모식도이며,
도 4는 본 발명의 제 1 실시예에 따른 심실링 테이프(100)의 단면도이며,
도 5는 본 발명의 제 2 실시예에 따른 심실링 테이프(100)의 단면도이며,
도 6은 본 발명에 따른 방수필름층(20)의 형성을 위하여 이형지(31)의 상부에 방수필름층(20) 제조용 캐스팅 도프(33)를 캐스팅하는 공정을 나타내는 공정도이다.1 is a schematic view showing application of a prior art ventricular ring tape 100 to a sewing portion of a garment,
2 is a schematic view showing a garment to which a ventricular ring tape 100 according to the related art is applied,
3 is a schematic view for explaining a green through phenomenon in an outdoor garment,
4 is a cross-sectional view of a ventricular ring tape 100 according to a first embodiment of the present invention,
5 is a cross-sectional view of a ventricular ring tape 100 according to a second embodiment of the present invention,
6 is a process diagram showing a process of casting a casting dope 33 for manufacturing a waterproof film layer 20 on the release paper 31 for forming a waterproof film layer 20 according to the present invention.

본 출원에서 “포함한다”, “가지다” 또는 “구비하다” 등의 용어는 명세서 상에 기재된 특징, 숫자, 단계, 구성요소, 부분품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부분품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.The use of the terms "comprises", "having", or "having" in this application is intended to specify the presence of stated features, integers, steps, components, parts, or combinations thereof, But do not preclude the presence or addition of features, numbers, steps, operations, components, parts, or combinations thereof.

또한, 다르게 정의되지 않는 한 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미를 가지고 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련기술의 문맥상 가지는 의미와 일치하는 의미를 가지는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다. Also, unless otherwise defined, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Terms such as those defined in commonly used dictionaries are to be interpreted as having a meaning consistent with the contextual meaning of the related art and are to be interpreted as either ideal or overly formal in the sense of the present application Do not.

최근의 아웃도어 의류 제조용 원단은 경량성 및 공기투과도를 개선하기 위하여 두께가 얇은 겉감과 안감 및 투습방수성 멤브레인을 주로 사용하며, 이에 따라 제조된 아웃도어 의류에 도 3과 같은 그린 스루 현상이 빈번하게 발생하게 된다. Recently, outdoor fabrics for outerwear fabrication mainly use a thin outer cloth, a lining and a breathable and waterproof membrane in order to improve light weight and air permeability, and the grease penetration phenomenon as shown in Fig. .

이하에서는 본 발명에 따른 그린 스루 현상을 방지하기 위한 심실링 테이프(100)에 대하여 첨부도면을 참조하여 상세히 설명한다. 도 4는 본 발명의 제 1 실시예에 따른 심실링 테이프(100)의 단면도이며, 도 5는 본 발명의 제 2 실시예에 따른 심실링 테이프(100)의 단면도이다.Hereinafter, a ventricular ring tape 100 for preventing a grease penetration phenomenon according to the present invention will be described in detail with reference to the accompanying drawings. FIG. 4 is a cross-sectional view of a ventricular ring tape 100 according to a first embodiment of the present invention, and FIG. 5 is a sectional view of a ventricular ring tape 100 according to a second embodiment of the present invention.

도 4에 도시한 바와 같이, 본 발명의 제 1 실시예에 따른 아웃도어 의류 제조용 심실링 테이프(100)는, 크게 원단층(10)과 방수필름층(20)및 제 1 접착제층(40)이 합포되어 구성된다. 4, the ventricular ring tape 100 for manufacturing outdoor clothing according to the first embodiment of the present invention mainly comprises an outer layer 10, a waterproof film layer 20 and a first adhesive layer 40, .

상기 원단층(10)은 심실링 테이프(100)의 제조 후에 부착되는 아웃도어 의류의 안감의 원단과 동일한 색상의 원단을 사용함으로써, 심실링 테이프(100)의 부착 여부가 외부로 드러나지 않도록 하는 것이 바람직하다.The outer layer 10 is made of the same color as the fabric of the lining of the outdoor garment attached after manufacture of the ventricular ring tape 100 so that the attachment of the ventricular ring tape 100 is not exposed to the outside desirable.

상기와 같은 원단층(10)은 직물 또는 편물로 구성될 수 있으며, 상기 원단층(10)은 폴리에스테르, 폴리아미드, 폴리우레탄, 폴리에틸렌, 폴리프로필렌, 폴리부타디엔, 셀룰로오스계 재생섬유, 천연섬유로 구성되는 그룹으로부터 선택되는 어느 하나 이상으로 제조될 수 있다. The monolayer 10 may be fabric or knitted. The monolayer 10 may be made of polyester, polyamide, polyurethane, polyethylene, polypropylene, polybutadiene, cellulose-based regenerated fibers, And may be made of any one or more selected from the group consisting of

특히, 상기 원단층(10)을 직물로 구성하는 경우에 경사 및 위사의 밀도는 10 ~ 250 개/인치인 것이 바람직하다. 상기 경사 및 위사의 밀도가 10 개/인치 미만인 경우에는 직물의 조직이 성글지 못하여 심실링 테이프(100)의 제조가 어렵고, 250 개/인치를 초과하는 경우에는 상기 원단층(10)의 조직이 경화되어 심실링 테이프(100)의 제조후 그 사용이 불가하게 된다. In particular, when the monolayer 10 is composed of a fabric, the density of warp and weft is preferably 10 to 250 / inch. If the density of the warp and weft is less than 10 pcs / inch, the fabric of the fabric is unstable and the manufacture of the ventricular ring tape 100 is difficult. If the density of the warp and weft exceeds 250 pcs / inch, Cured to make its use after manufacture of the ventricular ring tape 100 impossible.

또한 본 발명의 다른 실시예에 의하면, 상기 원단층(10)은 편물로 구성하는 것도 가능하다. 이때 상기 편물은 평량이 500 g/m2 이하인 것이 바람직하다. 상기 편물의 평량이 500 g/m2 을 초과하는 경우에는 제조되는 심실링 테이프(100)의 무게가 무거워져서 제조되는 아웃도어 의류의 경량화가 어렵게 된다. 따라서 원단층(10)을 구성하는 편물의 평량은 500 g/m2 이하인 것이 바람직하다.According to another embodiment of the present invention, the monolayer 10 may be formed of a knitted fabric. The knitted fabric preferably has a basis weight of 500 g / m 2 or less. When the basis weight of the knitted fabric exceeds 500 g / m 2 , the weight of the ventricular ring tape 100 to be manufactured becomes heavy, which makes it difficult to reduce the weight of the outdoor garment produced. Therefore, the basis weight of the knitted fabric constituting the monolayer 10 is preferably 500 g / m 2 or less.

상기와 같이 원단층(10)을 편물로 구상하는 경우에는 특히 싱글 저지(single jersey) 또는 트리코트(tricot) 조직을 갖는 편성물이 가장 바람직하며, 그 이유는 상기 싱글저지 또는 트리코트 조직을 갖는 편성물이 신축성과 유연성 및 드레이프성이 우수하기 때문에 부착 부위에서 주름이 발생하지 않으므로, 심실링 테이프(100)의 부착 여부가 눈에 잘 띄지 않게 되는 장점이 있기 때문이다.In the case of circularly knitting the artificial layer 10 as described above, a knitted fabric having a single jersey or a tricot structure is most preferable because the knitted fabric having a single jersey or a tricot structure This is because elasticity, flexibility, and drape property are excellent, so that there is no wrinkle at the attachment site, so that it is advantageous that the attachment of the ventricular ring tape 100 is not conspicuous.

상기 원단층(10)의 하부에는 도 4에 도시된 바와 같이, 방수필름층(20)이 구비된다. 상기 방수필름층(20)은 필름 제조용 수지 즉, 폴리우레탄, 폴리에스테르, 폴리아미드, 폴리테트라플루오로에틸렌, 폴리비닐클로라이드 중 어느 하나로 구성되는 것이 바람직하다.As shown in FIG. 4, a waterproof film layer 20 is provided under the artificial layer 10. The waterproof film layer 20 is preferably composed of any one of resin for producing a film, that is, polyurethane, polyester, polyamide, polytetrafluoroethylene and polyvinyl chloride.

상기 방수필름층(20)은 기제조된 가요성이 있는 필름을 사용할 수 있다. 즉, 상기 폴리우레탄, 폴리에스테르, 폴리아미드, 폴리테트라플루오로에틸렌 및 폴리비닐클로라이드 등의 필름 제조용 수지 중에서 선택되는 수지를 이용하여 제조된 가요성이 있는 필름의 상부에 접착제를 코팅 한 후, 원단층(10)을 접착함으로써 상기 원단층(10과 방수필름층(20)의 합포가 가능하다.The waterproof film layer 20 may be made of a flexible film prepared in advance. That is, after an adhesive is coated on the upper portion of a flexible film produced using a resin selected from resins for producing films such as polyurethane, polyester, polyamide, polytetrafluoroethylene and polyvinyl chloride, By adhering the monolayer 10, the monolayer 10 and the waterproof film layer 20 can be laminated.

상기 원단층(10)과 기제조된 가요성이 있는 필름을 이용한 방수필름층(20)의 합포시 사용되는 접착제는 통상의 열가소성 접착제 즉, 폴리초산비닐, 폴리염화비닐, 폴리스티렌 등이 사용가능하나, 본 발명에서는 특히 용제형 폴리우레탄 접착제가 바람직하다. 상기 용제형 폴리우레탄 접착제는 상기 원단층(10)과 방수필름층(20)에 쉽게 젖으며, 또한 원단층(10) 및 방수필름층(20)의 표면과 쉽게 공유결합을 형성하게 되므로 접착강도가 우수한 특징을 갖는다. The adhesive used in the preparation of the waterproof film layer 20 using the flexible layer and the original layer 10 may be conventional thermoplastic adhesives such as polyvinyl acetate, polyvinyl chloride, and polystyrene. In the present invention, a solvent-type polyurethane adhesive is particularly preferred. The solvent type polyurethane adhesive is easily wetted with the outer layer 10 and the waterproof film layer 20 and easily forms a covalent bond with the surface of the outer layer 10 and the waterproof film layer 20, .

상기 원단층(10)과 방수필름층(20)의 합포 공정은 먼저 가요성이 있는 필름을 이용한 방수필름층(20)의 일측면에 용제형 폴리우레탄 접착제를 도포한 후 상기 용제형 폴리우레탄 접착제가 도포된 일측면에 원단층(10)을 접착함으로써 합포하게 된다. In the process of padding the outer layer 10 and the waterproof film layer 20, a solvent type polyurethane adhesive is first applied to one side of the waterproof film layer 20 using a flexible film, and then the solvent type polyurethane adhesive By adhering the monofilaments 10 to one side to which the adhesive layer 10 is applied.

상기 용제형 폴리우레탄 접착제는 상기 방수필름층(20)의 일측면에 도포되고, 상기 용제형 폴리우레탄 접착제가 도포된 방수필름층(20)은 원단층(10)과 합포된 후, 열풍으로 유기용제를 휘발함으로써 합포 공정이 완료된다.The solvent type polyurethane adhesive is applied to one side of the waterproof film layer 20 and the waterproof film layer 20 coated with the solvent type polyurethane adhesive is coated with the ultrafine layer 10 and then heated Volatilization of the solvent completes the consolidation process.

상기 합포 공정에서 사용되는 용제형 폴리우레탄 접착제는 통상적으로 엠이케이(MEK)나 디엠에프(DMF)와 같은 유기용제에 녹여 접착제로 사용하며, 표면이 매우 부드러우며 마찰저항성이 양호하고, 신축성, 유연성, 굴곡성, 내약품성 등 여러 가지 장점을 가지고 있기 때문에 직물의 코팅, 도료, 접착제 등 다양한 용도로 폭넓게 사용되고 있다.The solvent-type polyurethane adhesive used in the pouring process is usually dissolved in an organic solvent such as MEK or DMF to be used as an adhesive. The adhesive is very soft on the surface, good in friction resistance, Flexibility, flexibility and chemical resistance, it has been widely used for various applications such as coatings for fabrics, paints, and adhesives.

상기 합포 공정에서 방수필름층(20)에 도포되는 용제형 폴리우레탄 접착제의 양은 10 ∼ 30 g/m2 가 되는 것이 바람직하다. 즉, 상기 도포되는 용제형 폴리우레탄 접착제의 양이 30 g/㎡을 초과하게 되면 원단층(10)의 텍스처가 지나치게 경질화되어 촉감이 저하된다. 반대로 용제형 폴리우레탄 접착제의 양이 10 g/㎡ 미만으로 도포되면 원단층(10)과 방수필름층(20)간의 결합강도가 불충분하여 세탁을 견디기에 충분한 내구성을 얻을 수 없게 된다. The amount of the solvent-type polyurethane adhesive to be applied to the waterproof film layer 20 in the pouring process is preferably 10 to 30 g / m 2 . That is, when the amount of the solvent-based polyurethane adhesive applied is more than 30 g / m 2, the texture of the artificial layer 10 becomes excessively hard and the touch is reduced. On the contrary, if the amount of the solvent-based polyurethane adhesive is less than 10 g / m 2, the bond strength between the ultrafine layer 10 and the waterproof film layer 20 is insufficient, and durability sufficient to withstand washing can not be obtained.

본 발명의 일실시예에 따르면 상기 용제형 폴리우레탄 접착제를 유기용매에 용해하여 방수필름층(20)에 도포시 점도는 1,000 ∼ 20,000 cps 인 것이 가장 바람직하다. According to one embodiment of the present invention, it is most preferable that the solvent-type polyurethane adhesive is dissolved in an organic solvent and the viscosity of the adhesive is 1,000 to 20,000 cps when applied to the waterproof film layer 20.

또한 본 발명의 다른 실시예에 따르면, 상기 방수필름층(20)을 제조하기 위한 상기 필름 제조용 수지를 적절한 용매에 용해하여 제조된 방수필름층(20) 제조용 캐스팅 도프(dope, 33)를 이형지(31) 상으로 캐스팅함으로써 상기 방수필름층(20)을 제조하는 용액 캐스팅 방법이 가능하다. According to another embodiment of the present invention, a casting dope 33 for manufacturing the waterproof film layer 20, which is prepared by dissolving the film-forming resin for producing the waterproof film layer 20 in an appropriate solvent, 31) to form the waterproof film layer 20 is possible.

즉, 도 6에 도시된 바와 같이, 회전하는 복수의 로울러(12) 상에 이형지(31)를 이동시키면서, 상기 이동되는 이형지(31)의 상부에 상기 방수필름층(20) 제조용 캐스팅 도프(33)를 도포하게 된다. 이때 상기 방수필름층(20) 제조용 캐스팅 도프(33)는 상기 필름 제조용 수지를 적절한 용매에 용해하거나, 또는 상기 필름 제조용 수지의 중합시 단량체를 용매에 용해하여 중합하는 용액 중합에 의해 제조될 수 있다.6, a casting dope 33 for manufacturing the waterproof film layer 20 is formed on the upper side of the release paper 31 while the release paper 31 is moved on the plurality of rollers 12 that are rotating. ). The casting dope 33 for producing the waterproof film layer 20 may be prepared by solution polymerization in which the film-forming resin is dissolved in an appropriate solvent, or a monomer is dissolved in a solvent upon polymerization of the film-forming resin .

상기와 같이 이형지(31) 상에 도포된 방수필름층(20) 제조용 캐스팅 도프(33)는 로울러(12)를 따라 이동되면서 상기 로울러(12)의 상부 일측에 구비되는 나이프(25)를 거치게 된다. 이 때 상기 나이프(25)의 높낮이 정도에 따라 이형지(31)에 도포되는 방수필름층(20) 제조용 캐스팅 도프(33)의 두께를 조절함으로써 형성되는 방수필름층(20)의 두께를 조절하게 된다. 이후에는 원단층(10)과 방수필름층(20)을 합포한 다음 상기 이형지(31)를 박리함으로써 원단에 방수필름층(20)이 형성되게 된다. The casting dope 33 for forming the waterproof film layer 20 coated on the release paper 31 is moved along the roller 12 and passes through the knife 25 provided at one side of the upper portion of the roller 12 . The thickness of the waterproof film layer 20 formed by adjusting the thickness of the casting dope 33 for manufacturing the waterproof film layer 20 applied to the release paper 31 is adjusted according to the height of the knife 25 . Thereafter, the waterproof film layer 20 is formed on the fabric by separating the release paper 31 after the monolayer 10 and the waterproof film layer 20 are formed.

상기와 같이 용액 캐스팅 방법에 의해 형성되는 방수필름층(20)은 이형지(31)에 도포한 후, 상기 방수필름층(20) 제조용 캐스팅 도프(33)에 포함된 용매가 휘발하여 완전히 건조되기 전에 원단층(20)과 합포를 하게 된다. 이때 가압롤러를 통과시킨 후, 2~5일간 숙성을 하면 방수필름층(20)에 원단층(10)이 접착이 되어 방수성능을 발휘할 정도로 내구성을 가지게 된다. 이후에 상기 방수필름층(20)의 하부에 제 1, 2 접착제층을 형성하기 위하여 이형지(31)는 박리하게 된다. After the waterproof film layer 20 formed by the solution casting method is applied to the release paper 31 and then the solvent contained in the casting dope 33 for manufacturing the waterproof film layer 20 is volatilized and completely dried It is mixed with the monolayer 20. At this time, if the aging is performed for 2 to 5 days after passing through the pressure roller, the monolayer 10 is adhered to the waterproof film layer 20 and durability is obtained so as to exhibit waterproof performance. Thereafter, the release paper 31 is peeled off to form the first and second adhesive layers on the lower part of the waterproof film layer 20.

상기 방수필름층(20)을 형성하기 위한 필름 제조용 수지중 폴리우레탄은 M.E.K(Methyl Ethyl ketone) 또는 M.I.B.K(Methyl Iso Butyl ketone)를 이용하여 방수필름층(20) 제조용 캐스팅 도프(33)의 제조가 가능하며, 폴리에스테르는 페놀, o-클로로페놀, m-클로로페놀, 니트로벤젠 등에 용해하여 방수필름층(20) 제조용 캐스팅 도프(33)의 제조가 가능하다. 또한 폴라아미드는 m-크레졸, n-메틸-2-피롤리돈(NMP), 디메틸포름아미드(DMF), 디메틸아세트아미드(DMAc), 디메틸설폭사이드(DMSO) 등에 용해가 가능하며, 폴리테트라플루오로에틸렌은 케톤 또는 극성 용매에 용해가 가능하며, 폴리비닐클로라이드는 케톤, 아세톤, 사이클로 핵사논 등의 용매를 이용하여 방수필름층(20) 제조용 캐스팅 도프(33)의 제조가 가능하다. The production of the casting dope 33 for producing the waterproof film layer 20 by using MEK (Methyl Ethyl Ketone) or MIBK (Methyl Iso Butyl Ketone) in the resin for producing the waterproof film layer 20 And the polyester can be dissolved in phenol, o - chlorophenol, m - chlorophenol, nitrobenzene and the like to produce a casting dope 33 for producing the waterproof film layer 20. The polyamide is soluble in m -cresol, n-methyl-2-pyrrolidone (NMP), dimethylformamide (DMF), dimethylacetamide (DMAc), dimethylsulfoxide (DMSO) Ethylene can be dissolved in a ketone or a polar solvent, and polyvinyl chloride can be prepared by casting dope 33 for producing a waterproof film layer 20 using a solvent such as ketone, acetone, or cyclohexanone.

위에서 살핀 바와 같이, 기제조된 가요성 필름 또는 용액 캐스팅 방법에 의해 형성되는 방수필름층(20)의 두께는 5 ~ 70 ㎛인 것이 바람직하며, 특히, 상기 방수필름층(20)의 인장강도는 5 Mpa 이상, 신도는 200~700 %이며, 모듈러스는 2 MPa 이상, 연화점의 범위는 120 ~ 190 ℃ 인 것이 특히 바람직하다. As described above, the thickness of the waterproof film layer 20 formed by the previously prepared flexible film or solution casting method is preferably 5 to 70 탆, and in particular, the tensile strength of the waterproof film layer 20 is 5 MPa or more, elongation is 200 to 700%, modulus is 2 MPa or more, and softening point is 120 to 190 ° C.

상기와 같은 두께 및 물성을 갖는 방수필름층(20)을 사용하여 제조되는 심실링 테이프(100)는 방수성 및 방풍성이 뛰어나며, 또한 경량성 등이 우수한 아웃도어 의류의 제조가 가능하게 된다. 그리고 상기와 같은 방수필름층(20)으로 제조되는 심실링 테이프(100)를 부착하는 경우에 봉제선(15)으로 부터 아웃도어 의류의 유연성이 저하되지 아니하여 활동성이 편하고, 이에 따라 다양한 기능성 의류 제품의 제조가 가능하게 된다.The ventricular ring tape 100 manufactured using the waterproof film layer 20 having the above-described thickness and physical properties is capable of producing an outdoor garment excellent in waterproof property, windproof property, and light weight. In the case of attaching the ventricular ring tape 100 made of the waterproof film layer 20 as described above, the flexibility of the outdoor clothing is not deteriorated from the sewing line 15, so that the activity is easy, Can be manufactured.

상기와 같이 원단층(10)과 방수필름층(20)이 합포된 후에는 상기 방수필름층(20)의 하부면에 제 1 접착제층(40)을 형성하게 된다. The first adhesive layer 40 is formed on the lower surface of the waterproof film layer 20 after the outer layer 10 and the waterproof film layer 20 are formed as described above.

본 발명에서 상기 제 1 접착제층(40)의 형성은 핫멜트형 접착제 또는 용제형 접착제를 이용하여 형성하는 것이 가능하다. In the present invention, the first adhesive layer 40 may be formed using a hot-melt type adhesive or a solvent type adhesive.

상기 핫멜트형 접착제를 이용하여 제 1 접착제층(40)을 형성하는 방법은 상기 핫멜트형 접착제에 열을 가하여 용융시킨 후, 원단층(10)과 합포된 방수필름층(20)의 하부에 캐스팅함으로써 가능하다. 즉, 상기 핫멜트 접착제는 압출용 T-다이 즉, 압출기에 투입하고, 실린더 히터에 의한 열과 스크류를 회전시켜 발생하는 마찰열과 압력을 가해 상기 핫멜트 접착제를 용융함으로써 코팅하는 것이 바람직하다. The method of forming the first adhesive layer 40 using the hot-melt type adhesive is the same as that of the first embodiment except that the hot-melt type adhesive is melted by applying heat to the lower layer of the waterproof film layer 20, It is possible. That is, it is preferable to apply the hot-melt adhesive to a T-die for extrusion, that is, an extruder, and apply heat and friction generated by rotating the screw and the cylinder heater to apply pressure to melt the hot-melt adhesive.

또한 용제형 접착제를 이용하여 제 1 접착제층(40)을 형성하는 방법은 상기 용제형 접착제를 적절한 유기용매에 용해하거나 또는 용매내에서 중합한 접착제를 원단층(10)과 합포된 방수필름층(20)의 하부에 캐스팅함으로써 가능하다. The method of forming the first adhesive layer 40 using a solvent type adhesive is the same as that of the first embodiment except that the solvent type adhesive is dissolved in an appropriate organic solvent or an adhesive polymerized in a solvent is applied to the waterproof film layer 20).

상기 용제형 접착제의 코팅 방식은 용제형 접착제 수지를 적절한 유기용매에 용해하여 캐스팅 도프(dope)를 형성하고, 상기 캐스팅 도프를 나이프 코팅설비를 이용하여 상기 방수필름층(20)의 일측면에 캐스팅 함으로써 제 1 접착제층(40)의 형성이 가능하다. In the coating method of the solvent type adhesive, a casting dope is formed by dissolving a solvent type adhesive resin in an appropriate organic solvent, and casting dope is cast on one side of the waterproof film layer 20 using a knife coating facility The first adhesive layer 40 can be formed.

상기와 같이 핫멜트형 접착제 또는 용제형 접착제를 이용하여 형성되는 제 1 접착제층(40)은 원단층(10)과 합포된 방수필름층(20)의 하부에 5 ~ 50 g/㎡의 양으로 도포한다.  The first adhesive layer 40 formed using the hot melt type adhesive or the solvent type adhesive is applied to the lower side of the waterproof film layer 20 adhered with the artificial layer 10 in an amount of 5 to 50 g / do.

상기와 같이 핫멜트형 접착제 또는 용제형 접착제를 도포한 후, 필요에 따라 온도 30 ~ 50℃ 및 상대습도 50 ~ 100%의 조건에서 12 ~ 48시간 동안 숙성시킴으로써 제 1 접착제층(40)이 형성된다. After the application of the hot-melt type adhesive or the solvent type adhesive as described above, the first adhesive layer 40 is formed by aging for 12 to 48 hours at a temperature of 30 to 50 ° C and a relative humidity of 50 to 100% .

이때 상기 제 1 접착제층(40)의 두께는 0.001 ~ 3 mm 인 것이 바람직하다. 즉, 상기 제 1 접착제층(40)의 두께가 0.001 mm 미만으로 형성되는 경우에는 심실링 테이프(100)와 원단(14) 간의 접착력이 떨어지고 3 mm를 초과하는 경우에는 제조된 의류 제품의 촉감이 저하된다. At this time, the thickness of the first adhesive layer 40 is preferably 0.001 to 3 mm. That is, when the thickness of the first adhesive layer 40 is less than 0.001 mm, the adhesive force between the ventricular ring tape 100 and the distal end 14 is lowered. If the thickness is more than 3 mm, .

또한 상기 핫멜트형 접착제 또는 용제형 접착제는 폴리에스테르, 폴리아미드, 폴리에스테르계 폴리우레탄, 폴리에테르계 폴리우레탄, 폴리카프로락톤계 폴리우레탄으로 구성되는 그룹에서 선택되는 어느 하나 이상일 수 있다. The hot-melt type adhesive or the solvent type adhesive may be any one or more selected from the group consisting of polyester, polyamide, polyester-based polyurethane, polyether-based polyurethane, and polycaprolactone-based polyurethane.

본 발명의 제 1 실시예에 따르면, 상기와 같은 제 1 접착제층(40)을 구성하는 핫멜트형 접착제 또는 용제형 접착제에는 착색제를 혼입함으로서 심실링 테이프(100)의 그린 스루 현상을 방지할 수 있게 된다.According to the first embodiment of the present invention, it is possible to prevent the green-through phenomenon of the ventricular ring tape 100 by mixing a colorant into the hot-melt type adhesive agent or the solvent type adhesive constituting the first adhesive layer 40, do.

즉, 본 발명에 따르면, 상기 제 1 접착제층(40)의 형성시 사용되는 핫멜트형 접착제 또는 용제형 접착제는 착색제 즉, 염료, 안료 및 도료 등으로 구성되는 그룹으로부터 선택되는 어느 하나 이상을 혼입하여 색상을 부여함으로써 착색을 하는 것이 바람직하다. That is, according to the present invention, the hot-melt type adhesive agent or the solvent type adhesive agent used in forming the first adhesive layer 40 may be prepared by mixing at least one selected from the group consisting of a colorant, a dye, a pigment, It is preferable to perform coloration by imparting hue.

즉, 종래의 심실링 테이프(100)의 제조시 사용되는 핫멜트형 접착제 또는 용제형 접착제는 착색이 되지 아니하여 투명한 색상으로 접착제층(35)을 형성하게 된다. That is, the hot melt type adhesive or the solvent type adhesive used in manufacturing the conventional ventricular ring tape 100 is not colored and forms the adhesive layer 35 in a transparent color.

상기와 같이 투명한 색상의 핫멜트형 접착제 또는 용제형 접착제를 이용하여 접착제층(35)을 형성하게 되면, 의류에 부착된 후 아웃도어 의류의 안감의 색상이 심실링 테이프(100)를 통해 투영되게 된다. 따라서 아웃도어 의류의 제조 후 상기 아웃도어 의류에 부착된 심실링 테이프(100)의 존재가 드러나게 됨으로써 아웃도어 의류의 상품성이 떨어지게 되고, 디자인이 제약되게 된다. When the adhesive layer 35 is formed using the transparent hot melt adhesive or the solvent adhesive, the color of the lining of the outdoor garment after being attached to the garment is projected through the ventricular ring tape 100 . Accordingly, the presence of the ventricular ring tape 100 attached to the outdoor garment after the manufacture of the outdoor garment is revealed, thereby deteriorating the merchantability of the outdoor garment and limiting the design.

따라서 본 발명에서는 상기 제 1 접착제층(40)에 사용되는 핫멜트형 접착제 또는 용제형 접착제에 착색제를 혼입함으로써 그린 스루 현상을 방지할 수 있게 된다. Therefore, in the present invention, it is possible to prevent a green through phenomenon by incorporating a coloring agent into a hot-melt type adhesive agent or a solvent type adhesive agent used in the first adhesive layer 40.

상기와 같이 제 1 접착제층(40)을 구성하는 핫멜트형 접착제 또는 용제형 접착제에 색상이 부여되게 되면 심실링 테이프(100)의 존재가 외부로 드러나지 않게 됨으로써 디자인의 자유도가 넓어 지고, 아웃도어 의류의 상품성이 높아지게 되는 효과를 갖게 된다.As described above, when the hot melt adhesive or the solvent adhesive constituting the first adhesive layer 40 is colored, the presence of the ventricular ring tape 100 is not exposed to the outside, so that the degree of freedom of design is increased, The merchantability of the product is increased.

즉, 상기와 같이 착색제가 혼입된 핫멜트형 접착제 또는 용제형 접착제로 형성된 제 1 접착제층(40)을 포함하는 심실링 테이프(100)를 의류의 봉제선(15)에 위치시킨 후, 열풍을 가하게 되면 상기 제 1 접착제층(40)이 용융되어 아웃도어 의류의 봉제선(15)에 부착되게 된다. 이때 부착되는 아웃도어 의류의 안감 조직 사이로 용융된 제 1 접착제층(40)의 핫멜트형 접착제 또는 용제형 접착제가 침투함으로써, 아웃도어 의류의 겉감면에 나타나는 그린 스루 현상을 방지할 수 있게 된다.That is, when the ventricular ring tape 100 including the first adhesive layer 40 formed of the hot-melt adhesive or the solvent adhesive mixed with the coloring agent is placed on the sewing line 15 of the garment and hot air is applied The first adhesive layer 40 is melted and attached to the sewing line 15 of the outdoor wear. The hot melt adhesive or the solvent type adhesive of the melted first adhesive layer 40 penetrates between the lining structures of the attached outdoor clothes, thereby preventing the occurrence of the grease penetration appearing on the outer surface of the outdoor garment.

상기 제 1 접착제층(40)을 형성하는 핫멜트형 접착제 또는 용제형 접착제에 혼입되는 착색제의 색상은 안감 대비 옅은 색상인 것이 바람직하며, 상기와 같이 안감 대비 옅은 색상으로 착색된 핫멜트형 접착제 또는 용제형 접착제를 이용하여 형성되는 제 1 접착제층(40)은 부착후에 아웃도어 의류의 안감의 색상이 투영되지 아니하여 그린 스루 현상이 방지된다.The color of the colorant mixed into the hot-melt type adhesive agent or the solvent type adhesive forming the first adhesive layer 40 is preferably lighter than lining, and may be a hot-melt type adhesive or a solvent type The first adhesive layer 40 formed by using the adhesive prevents the color of the lining of the outdoor garment from being projected after the attachment so that the grease penetration phenomenon is prevented.

상기와 같은 핫멜트형 접착제 또는 용제형 접착제에 착색제를 혼입하는 방법은 마스터 배치 또는 액상의 착색제를 상기 접착제에 혼입함으로써 가능하다. 이때 상기 투입되는 착색제는 핫멜트형 접착제 또는 용제형 접착제 대비 0.5 ~ 56 중량%로 혼입되는 것이 바람직하다. 즉, 착색제가 0.5 중량% 미만으로 혼입되는 경우에는 색상의 차단효과가 발현되지 아니하여, 그린 스루 현상의 방지가 어렵게 된다. 또한 착색제의 혼입량이 56 중량%를 초과하는 경우에는 핫멜트형 접착제 또는 용제형 접착제의 점도가 상승하여 작업이 용이하지 않고 접착력 저하되는 문제가 발생하게 된다. 또한 상기와 같이 착색제가 혼입된 핫멜트 접착제의 용융점도는 160 ℃에서 측정시 제조 공정성 측면에서 50 ~ 410,000 mPas 인 것이 바람직하며, 또한 용제형 접착제의 경우에는 캐스팅 도프의 점도는 1,000 ~ 20,000 cps인 것이 바람직하다. The method of incorporating the colorant into the hot melt type adhesive or the solvent type adhesive as described above can be achieved by incorporating a master batch or a liquid coloring agent into the adhesive. At this time, it is preferable that the added colorant is incorporated at 0.5 to 56 wt% of the hot-melt type adhesive or the solvent type adhesive. That is, when the colorant is incorporated in an amount of less than 0.5% by weight, the color blocking effect is not exhibited and it is difficult to prevent the grease penetration phenomenon. When the mixing amount of the colorant is more than 56% by weight, the viscosity of the hot-melt type adhesive agent or the solvent type adhesive agent is increased and the work is not easy and the adhesive strength is lowered. In addition, the melt viscosity of the hot-melt adhesive mixed with the colorant as described above is preferably 50 to 410,000 mPas in view of the production processability when measured at 160 ° C, and the viscosity of the casting dope is 1,000 to 20,000 cps in the case of the solvent- desirable.

본 발명의 제 1 실시예에 따른 심실링 테이프(100)는 상기와 같이 원단층(10)과 방수필름층(20) 및 상기 방수필름층(20)의 하부에 착색제가 일정량 혼입된 핫멜트형 접착제 또는 용제형 접착제로 형성되는 제 1 접착제층(40)을 구비하게 된다.The ventricular ring tape 100 according to the first embodiment of the present invention can be applied to the lower layer of the outer layer 10, the waterproof film layer 20 and the waterproof film layer 20 as described above by using a hot melt adhesive Or a first adhesive layer 40 formed of a solvent type adhesive.

상기와 같이 제조된 심실링 테이프(100)는 필요에 따라 숙성을 거친 후에 권취함으로서, 본 발명의 제 1 실시예에 따른 심실링 테이프(100)가 제조된다. The ventricular ring tape 100 manufactured as described above is wound after being aged if necessary, thereby manufacturing the ventricular ring tape 100 according to the first embodiment of the present invention.

또한 본 발명의 제 2 실시예에 따르면, 상기 심실링 테이프(100)는 도 5와 같이 원단층(10), 방수필름층(20), 착색제가 혼입되지 않은 핫멜트형 접착제 또는 용제형 접착제로 형성되는 제 2 접착제층(30) 및 착색제가 혼입된 핫멜트형 접착제 또는 용제형 접착제로 형성되는 제 1 접착제층(40)으로 구성되는 것을 특징으로 한다. According to a second embodiment of the present invention, the ventricular ring tape 100 is formed of an outer layer 10, a waterproof film layer 20, a hot-melt type adhesive without a coloring agent, or a solvent type adhesive And a first adhesive layer (40) formed of a hot-melt type adhesive or a solvent type adhesive mixed with a coloring agent.

상기 본 발명의 제 2 실시예에 따른 심실링 테이프(100)에서 원단층(10)과 방수필름층(20)은 제 1 실시예와 동일하므로, 그 설명을 생략한다.In the ventricular ring tape 100 according to the second embodiment of the present invention, the distal layer 10 and the waterproof film layer 20 are the same as those in the first embodiment, and a description thereof will be omitted.

도 5에 도시된 바와 같이, 본 발명의 제 2 실시예에서 제 2 접착제층(30)은 착색제가 혼입되지 않은 통상의 핫멜트형 접착제 또는 용제형 접착제로 형성되며, 상기 방수필름층(20)의 하부에 형성된다. 상기 제 2 접착제층(30)은 심실링 테이프(100)에 구비됨으로서, 열풍을 가해 심실링 테이프(100)를 의류에 부착후 상기 착색제가 혼입된 핫멜트형 접착제 또는 용제형 접착제로 형성되는 제 1 접착제층(40)이 심실링 테이프(100)의 변부로 드러나지 않도록 한다. 5, in the second embodiment of the present invention, the second adhesive layer 30 is formed of a conventional hot-melt type adhesive or a solvent type adhesive in which no colorant is mixed, Respectively. The second adhesive layer 30 is provided on the ventricular ring tape 100 so that the ventricular ring tape 100 is adhered to the clothes by applying hot air to the clothes and then the hot- Thereby preventing the adhesive layer 40 from being exposed at the side of the ventricular ring tape 100.

즉, 상기 본 발명의 제 1 실시예와 같이, 착색제가 혼입된 핫멜트형 접착제 또는 용제형 접착제로 제 1 접착제층(40)만을 구성하는 경우에, 심실링 테이프(100)를 박막으로 제조되게 되면 심실링 테이프를 의류에 부착한 후 상기 심실링 테이프(100)의 변부에서 상기 제 1 접착제층(40)이 외부로 드러나게 될 수 있다.That is, in the case where only the first adhesive layer 40 is composed of a hot-melt type adhesive or a solvent type adhesive mixed with a colorant as in the first embodiment of the present invention, when the ventricular ring tape 100 is made into a thin film The first adhesive layer 40 may be exposed to the outside at the edge of the ventricular ring tape 100 after the ventricular ring tape is attached to the garment.

따라서 상기 제 2 실시예와 같이, 착색제가 혼입되지 않은 핫멜트형 접착제 또는 용제형 접착제를 이용하여 형성된 제 2 접착제층(30)의 하부에 착색제가 혼입된 핫멜트형 접착제 또는 용제형 접착제로 형성되는 제 1 접착제층(40)을 구비하게 되면, 상기 제 2 접착제층(30)에 의해 심실링 테이프(100)의 변부에서 상기 제 1 접착제층(40)의 존재가 드러나지 않게 된다. Therefore, as in the second embodiment, a hot-melt type adhesive agent or a solvent-type adhesive agent mixed with a colorant is used in the lower part of the second adhesive layer 30 formed by using a hot-melt type adhesive agent or a solvent type adhesive agent, 1 adhesive layer 40 prevents the presence of the first adhesive layer 40 from being exposed at the edge of the ventricular ring tape 100 by the second adhesive layer 30. [

상기와 같이 제조된 제 1 접착제층(40) 및 제 2 접착제층(30)이 형성된 심실링 테이프(100)는 이후에 권취함으로서, 본 발명의 제 2 실시예에 따른 심실링 테이프(100)가 제조된다. 이때 필요에 따라 숙성 공정을 추가할 수 있다.The ventricular ring tape 100 formed with the first adhesive layer 40 and the second adhesive layer 30 manufactured as described above is wound thereafter so that the ventricular ring tape 100 according to the second embodiment of the present invention . At this time, an aging process can be added as needed.

본 발명에서 심실링 테이프(100)의 두께는 90 ~ 700 ㎛인 것이 바람직하다. 즉, 심실링 테이프(100)의 두께가 90 ㎛ 미만의 경우에는 상기 심실링 테이프(100)의 두께가 얇아서 아웃도어 의류의 제조시 촉감은 우수하게 되나 가공성이 낮고, 방수필름층(20)의 성형성 및 두께 평활도가 취약하게 된다. 또한 상기 심실링 테이프(100)의 두께가 700 ㎛를 초과하는 경우에는 단가가 상승하므로 가격 경쟁력이 떨어진다.In the present invention, the thickness of the ventricular ring tape 100 is preferably 90 to 700 탆. That is, when the thickness of the ventricular ring tape 100 is less than 90 탆, the thickness of the ventricular ring tape 100 is thin, Resulting in poor moldability and thickness smoothness. If the thickness of the ventricular ring tape 100 exceeds 700 mu m, the price increases and the price competitiveness decreases.

또한 본 발명에서 심실링 테이프(100)의 폭은 5 ~ 300 mm인 것이 바람직하나. 제조되는 아웃도어의 의류에 따라 요구되는 폭으로 적절하게 슬리팅 또는 컷팅하여 사용될 수 있다. In the present invention, the width of the ventricular ring tape 100 is preferably 5 to 300 mm. It can be used by appropriately slitting or cutting to the width required according to the clothes of the outdoor manufactured.

이하에서는 본 발명의 심실링 테이프(100)의 제조방법에 대하여 설명한다. Hereinafter, a method of manufacturing the ventricular ring tape 100 of the present invention will be described.

본 발명의 제 1 실시예에 따른 심실링 테이프(100)는 먼저 제 1 단계로서 원단층(10)을 준비하게 된다. 그 이후에는 제 2 단계로서 상기 원단층(10)에 합포되는 방수필름층(20)을 준비한다. The ventricular ring tape 100 according to the first embodiment of the present invention first prepares the distal layer 10 as a first step. Thereafter, as a second step, a waterproof film layer 20 to be applied to the monolayer 10 is prepared.

상기와 같이 준비된 상기 원단층(10)과 방수필름층(20)은 합포 공정을 통해 합포하게 된다(제 3 단계). 상기 합포 공정은 위에서 살핀 바와 같이, 상기 필름 제조용 수지로 제조된 가요성이 있는 필름을 방수필름층(20)으로 이용하여 합포가 가능하다. 또한 상기 필름 제조용 수지 즉, 폴리우레탄, 폴리에스테르, 폴리아미드, 폴리테트라플루오로에틸렌, 폴리비닐클로라이드 중 어느 하나의 수지를 적절한 용매에 용해하거나, 또는 상기 필름 제조용 수지의 중합시 용액 중합을 통해 방수필름층(20) 제조용 캐스팅 도프(33)를 제조한 후, 이를 이형지(31)의 상부에 캐스팅한 후 원단층(10)과의 합포가 가능하다. The prepared monolayer layer 10 and the waterproof film layer 20 are assembled through a foaming process (third step). As described above, the film forming process can be carried out using the flexible film made of the film-forming resin as the waterproof film layer 20. The resin for film production, that is, any one of polyurethane, polyester, polyamide, polytetrafluoroethylene and polyvinyl chloride may be dissolved in an appropriate solvent, or may be waterproofed by solution polymerization during polymerization of the film- The casting dope 33 for producing the film layer 20 can be manufactured and then cast on the release paper 31 and then mixed with the artificial layer 10.

상기와 같이 합포된 원단층(10)과 방수필름층(20)은 이후에 상기 방수필름층(20)의 하부에 제 1 접착제층(40)을 형성하는 제 4 단계;를 거치게 된다. The synthetic resin layer 10 and the waterproof film layer 20 thus formed are then subjected to a fourth step of forming a first adhesive layer 40 below the waterproof film layer 20.

이때 상기 방수필름층(20)의 하부에 형성되는 제 1 접착제층(40)은 안료, 염료 및 도료로 이루어진 그룹으로부터 선택되는 하나 이상의 착색제가 0.5 ~ 56 중량%로 혼입된 핫멜트형 접착제 또는 용제형 접착제를 사용하여 형성하는 것이 바람직하다. At this time, the first adhesive layer 40 formed on the lower part of the waterproof film layer 20 may be a hot-melt type adhesive or a solvent type adhesive in which 0.5 to 56% by weight of at least one coloring agent selected from the group consisting of pigments, dyes, It is preferable to use an adhesive.

상기와 같이 방수필름층(20)의 하부에 착색제가 혼입된 핫멜트형 접착제 또는 용제형 접착제를 이용하여 제 1 접착제층(40)을 형성함으로써, 본 발명의 제 1 실시예에 따른 그린 스루 현상을 방지하는 심실링 테이프(100)의 제조가 완료된다. As described above, the first adhesive layer 40 is formed by using the hot-melt type adhesive agent or the solvent type adhesive agent in which the coloring agent is mixed in the lower part of the waterproof film layer 20 so that the grease penetration phenomenon according to the first embodiment of the present invention The manufacture of the ventricular ring tape 100 is completed.

또한 본 발명의 제 2 실시예에 따른 심실링 테이프(100)는 상기 제 1 실시예에 따른 심실링 테이프(100)의 제조방법의 제 3 단계에서 원단층(10)과 방수필름층(20)을 합포한 후, 상기 방수필름층(20)의 하부에 착색제가 혼입되지 않은 핫멜트형 접착제 또는 용제형 접착제를 이용하여 제 2 접착제층(30)을 형성한다(제 4 단계). The ventricular ring tape 100 according to the second embodiment of the present invention can be applied to the outer layer 10 and the waterproof film layer 20 in the third step of the method of manufacturing the ventricular ring tape 100 according to the first embodiment, A second adhesive layer 30 is formed by using a hot-melt type adhesive or a solvent type adhesive in which a colorant is not mixed in the lower part of the waterproof film layer 20 (step 4).

이후에 상기 제 2 접착제층(30)의 하부에 착색제 즉, 염료, 안료 및 도료로 이루어진 그룹으로부터 선택되는 하나 이상의 착색제가 혼입된 핫멜트형 접착제 또는 용제형 접착제를 이용하여 제 1 접착제층(40)을 형성함으로써(제 5 단계), 본 발명의 제 2 실시예에 따른 그린 스루 현상을 방지하는 심실링 테이프(100)의 제조가 완료된다. A first adhesive layer 40 is formed on the lower side of the second adhesive layer 30 by using a hot-melt type adhesive or a solvent type adhesive in which a coloring agent, that is, at least one coloring agent selected from the group consisting of a dye, (Fifth step), the manufacture of the ventricular ring tape 100 for preventing the grease penetration phenomenon according to the second embodiment of the present invention is completed.

상기와 같이 제조되는 본 발명의 심실링 테이프(100)는 아웃도어 의류의 제조에 사용될 수 있다. The ventricular ring tape 100 of the present invention manufactured as described above can be used in the manufacture of outdoor clothing.

즉, 본 발명에 따른 아웃도어 의류의 제조방법은 먼저 아웃도어 의류 제조용 원단을 준비하는 단계를 포함한다. 통상적으로 상기 아웃도어 의류 제조용 원단은 겉감과 안감 사이에 투습방수성 멤브레인을 포함함으로써 투습방수 기능을 갖는 원단을 사용하게 된다. That is, the method of manufacturing an outdoor garment according to the present invention includes preparing a fabric for outdoor garment production. Generally, the fabric for manufacturing outdoor clothing includes a moisture-permeable and waterproof membrane between a cloth and a lining so that a fabric having moisture-permeable and waterproof function is used.

일반적으로 투습방수 기능을 갖는 원단은 의류 내부의 땀 등의 수증기는 외부로 통과시켜 배출하고, 외부의 비 등의 수분은 의류의 내부로 스며들지 않게 하여, 비나 눈에 젖지 않고(waterproof) 땀은 배출시켜(breathable) 착용자의 체온조절을 돕고, 쾌적감을 유지하도록 하는 원단 소재를 가리킨다. Generally, the cloth having the moisture permeable and waterproof function is used to prevent water vapor such as sweat inside the clothes from passing through to the outside and to prevent the moisture such as outside rain from penetrating into the inside of the clothes, Refers to a fabric material that is breathable to help control the temperature of the wearer and maintain a pleasant sensation.

상기 아웃도어 의류 제조용 원단의 재질은, 폴리에스터(polyester), 폴리아미드(polyamide), 폴리비닐클로라이드(polyvinylchloride), 폴리케톤(polyketone), 폴리술폰(polysulfone), 폴리카보네이트(polycarbonate), 플루오로폴리머(fluoropolymer), 폴리아크릴레이트(polyacrylate), 폴리우레탄(polyurethane), 및 폴리프로필렌(polypropylene) 중에서 하나 이상일 수 있다.The fabric of the outer garment manufacturing fabric may be a polyester, a polyamide, a polyvinylchloride, a polyketone, a polysulfone, a polycarbonate, a fluoropolymer a fluoropolymer, a polyacrylate, a polyurethane, and a polypropylene.

상기와 같이 준비된 아웃도어 의류 제조용 원단을 바지, 자켓 또는 점퍼 등의 의류 형상으로 재 단하여 재단물을 제조하게 된다. 이후에는 상기와 같이 제조된 재단물을 봉제함으로써 의류 형상으로 제조하게 된다. The prepared fabric for outdoor clothing is cut into a garment such as a pants, a jacket or a jumper to produce a cut. Thereafter, the cut material produced as described above is sewn to produce a garment shape.

일반적으로 아웃도어 의류는 디자인에 따라 전면, 후면, 측면, 팔 등 각각의 부위의 원단을 재단하여 재단물을 제조한 후, 이들을 봉제하여 의류 형상으로 제조하게 된다. Generally, outdoor garments are cut into fabric of front, rear, side, arm, etc. according to the design, and the cut material is manufactured, and then the garments are sewn to produce clothes.

상기와 같이 제조된 의류는 봉제선(15) 부위에 본 발명의 제 1 실시예에 따른 심실링 테이프(100)를 부착한 후 열풍을 가하여 접착함으로써 마무리하게 되면, 상기 봉제선(15) 부위로 수분이 침투하는 것을 방지하게 되어 아웃도어 의류의 제조가 완료되게 된다. When the ventricular ring tape 100 according to the first embodiment of the present invention is attached to the sewing line 15 at the site of the garment so that the hot air is applied to the sewing line 15 to adhere the sewing line 15 to the sewing line 15, So that the manufacture of the outdoor garment is completed.

상기와 같이 아웃도어 의류 등의 제조시 사용되는 본 발명의 제 1 실시예에 따른 심실링 테이프(100)는 원단층(10); 상기 원단층(10)의 하부에 구비되는 방수필름층(20) 및 상기 방수필름층(20)의 하부에 구비되는 제 1 접착제층(40);으로 구성되되, 상기 제 1 접착제층(40)은 그린 스루 현상을 방지하기 위하여 안료, 염료 및 도료로 이루어진 그룹으로부터 선택되는 하나 이상의 착색제가 혼입된 핫멜트형 접착제 또는 용제형 접착제를 이용하여 형성하는 것이 바람직하다. As described above, the ventricular ring tape 100 according to the first embodiment of the present invention used in the manufacture of outdoor clothing or the like includes an artificial layer 10; A waterproof film layer 20 provided below the outer layer 10 and a first adhesive layer 40 provided below the waterproof film layer 20, Is preferably formed using a hot-melt type adhesive or a solvent type adhesive in which at least one coloring agent selected from the group consisting of pigments, dyes, and paints is mixed to prevent a grease penetration phenomenon.

또한 상기와 같이 아웃도어 의류 등의 제조시 사용되는 본 발명의 제 2 실시예에 따른 심실링 테이프(100)는 원단층(10); 상기 원단층(10)의 하부에 구비되는 방수필름층(20); 상기 방수필름층(20)의 하부에 착색제가 혼입되지 않은 핫멜트형 접착제 또는 용제형 접착제를 이용하여 형성되는 제 2 접착제층(30); 및 상기 제 2 접착제층(30)의 하부에 구비되는 제 1 접착제층(40);으로 구성되되, 상기 제 1 접착제층(40)은 그린 스루 현상을 방지하기 위하여 안료, 염료 및 도료로 이루어진 그룹으로부터 선택되는 하나 이상의 착색제가 혼입된 핫멜트형 접착제 또는 용제형 접착제를 이용하여 형성하는 것이 바람직하다.In addition, the ventricular ring tape 100 according to the second embodiment of the present invention used in the manufacture of outdoor clothing and the like as described above includes an artificial layer 10; A waterproof film layer 20 provided at the lower part of the monolayer 10; A second adhesive layer 30 formed by using a hot-melt type adhesive or a solvent type adhesive in which a colorant is not mixed in the lower part of the waterproof film layer 20; And a first adhesive layer 40 provided under the second adhesive layer 30. The first adhesive layer 40 may be formed of a pigment, Or a solvent-type adhesive in which at least one coloring agent selected from the group consisting of a coloring agent and a coloring agent is mixed.

본 발명은 도면에 도시된 실험예를 참고로 설명되었으나 이는 예시적인 것에 불과하며, 당해 기술분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 다른 실험예가 가능하다는 점을 이해할 것이다. 또한 본 발명이 속하는 기술분야의 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 쉽게 변형이 가능하다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 하고, 본 발명의 진정한 기술적 보호 범위는 첨부된 청구범위의 기술적 사상에 의하여 정해져야 할 것이다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it will be understood by those of ordinary skill in the art that various changes in form and details may be made therein without departing from the scope of the present invention. It will also be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the appended claims. It is therefore to be understood that the embodiments described above are intended to be illustrative and not restrictive in all aspects and that the true scope of protection of the present invention should be determined by the spirit of the appended claims.

100 : 심실링 테이프
10 : 원단층
20 : 방수필름층
25 : 나이프
31 : 이형지
33 : 방수필름층 제조용 캐스팅 도프
30 : 제 2 접착제층
40 : 제 1 접착제층100: ventricular ring tape
10: Single layer
20: Waterproof film layer
25: Knife
31: release paper
33: casting dope for manufacturing waterproof film layer
30: second adhesive layer
40: first adhesive layer

Claims (15)

삭제delete 삭제delete 원단층(10);
상기 원단층(10)의 하부에 구비되는 방수필름층(20);
제 1 접착제층(40)이 외부로 드러나는 것을 방지하기 위하여 상기 방수필름층(20)의 하부에 구비되되, 착색제가 혼입되지 않은 핫멜트형 접착제 또는 용제형 접착제로 형성되는 제 2 접착제층(30); 및
상기 제 2 접착제층(30)의 하부에 5 ~ 50 g/m2 으로 구비되되, 착색제가 0.5 ~ 56 중량%로 혼입된 핫멜트형 접착제 또는 용제형 접착제로 형성되는 제 1 접착제층(40);을 포함하는 심실링 테이프(100).
An artificial layer 10;
A waterproof film layer 20 provided at the lower part of the monolayer 10;
A second adhesive layer 30 provided below the waterproof film layer 20 to prevent the first adhesive layer 40 from being exposed to the outside, the adhesive layer 30 being formed of a hot-melt type adhesive agent or a solvent type adhesive agent, ; And
A first adhesive layer 40 formed at a lower portion of the second adhesive layer 30 at 5 to 50 g / m 2 and formed of a hot-melt type adhesive or a solvent type adhesive mixed with 0.5 to 56 wt% of a coloring agent; (100). ≪ / RTI >
청구항 3에 있어서,
상기 착색제는 안료, 염료 및 도료로 이루어진 그룹으로부터 선택되는 하나 이상인 것을 특징으로 하는 심실링 테이프(100).

The method of claim 3,
Wherein the colorant is at least one selected from the group consisting of pigments, dyes, and paints.

삭제delete 청구항 3에 있어서,
상기 제 1 접착제층(40)의 두께는 0.001 ~ 3 mm인 것을 특징으로 하는 심실링 테이프(100).
The method of claim 3,
Wherein the thickness of the first adhesive layer (40) is 0.001 to 3 mm.
청구항 3에 있어서,
상기 방수필름층(20)의 두께는 5 ~ 70 ㎛인 것을 특징으로 하는 심실링 테이프(100).
The method of claim 3,
Wherein the thickness of the waterproof film layer (20) is 5 to 70 占 퐉.
청구항 3에 있어서,
상기 방수필름층(20)은 가요성이 있는 필름을 사용하거나 또는 용액 캐스팅 방법으로 형성되는 것을 특징으로 하는 심실링 테이프(100).
The method of claim 3,
Wherein the waterproof film layer (20) is formed by a flexible film or by a solution casting method.
청구항 3에 있어서,
상기 원단층(10)은 직물 또는 편물로 구성되는 것을 특징으로 하는 심실링 테이프(100).
The method of claim 3,
Wherein the monolayer (10) comprises a fabric or a knitted fabric.
청구항 9에 있어서,
상기 직물 또는 편물은 폴리에스테르, 폴리아미드, 폴리우레탄, 폴리에틸렌, 폴리프로필렌, 폴리부타디엔, 셀룰로오스계 재생섬유, 천연섬유로 구성되는 그룹으로부터 선택되는 어느 하나 이상으로 제조되는 것을 특징으로 하는 심실링 테이프(100).
The method of claim 9,
Wherein the woven or knitted fabric is made of at least one selected from the group consisting of polyester, polyamide, polyurethane, polyethylene, polypropylene, polybutadiene, cellulose-based regenerated fiber, 100).
청구항 9에 있어서,
상기 직물의 경사 및 위사의 밀도는 10 ~ 250 개/인치인 것을 특징으로 하는 심실링 테이프(100).
The method of claim 9,
Wherein the fabric has a warp and weft density of 10 to 250 yarns / inch.
청구항 9에 있어서,
상기 편물은 평량이 500 g/m2 이하인 것을 특징으로 하는 심실링 테이프(100).
The method of claim 9,
Wherein the knitted fabric has a basis weight of 500 g / m 2 or less.
청구항 3에 있어서,
상기 심실링 테이프(100)의 폭은 5 ~ 300 mm이고, 두께는 90 ~ 700 ㎛ 인 것을 특징으로 하는 심실링 테이프(100).

The method of claim 3,
Wherein the thickness of the ventricular ring tape (100) is 5 to 300 mm and the thickness is 90 to 700 탆.

삭제delete 원단층(10)을 준비하는 제 1 단계;
방수필름층(20)을 준비하는 제 2 단계;
상기 원단층(10)과 방수필름층(20)을 합포하는 제 3 단계;
제 1 접착제층(40)이 외부로 드러나는 것을 방지하기 위하여 상기 합포된 방수필름층(20)의 하부에 착색제가 혼입되지 않은 핫멜트형 접착제 또는 용제형 접착제를 이용하여 제 2 접착제층(30)을 형성하는 제 4 단계; 및
상기 제 2 접착제층(30)의 하부에 제 1 접착제층(40)을 형성하는 제 5 단계;로 구성되되,
상기 제 1 접착제층(40)은 안료, 염료 및 도료로 이루어진 그룹으로부터 선택되는 하나 이상의 착색제가 0.5 ~ 56 중량%로 혼입된 핫멜트형 접착제 또는 용제형 접착제를 이용하여 5 ~ 50 g/m2으로 형성되는 것을 특징으로 하는 심실링 테이프(100)의 제조방법.
A first step of preparing the monolayer 10;
A second step of preparing a waterproof film layer 20;
A third step of fabricating the outer layer (10) and the waterproof film layer (20);
In order to prevent the first adhesive layer 40 from being exposed to the outside, a second adhesive layer 30 is formed using a hot-melt type adhesive agent or a solvent type adhesive agent in which a colorant is not mixed in the lower part of the waterproof film layer 20 A fourth step of forming; And
And a fifth step of forming a first adhesive layer (40) below the second adhesive layer (30)
The first adhesive layer 40 may be formed to a thickness of 5 to 50 g / m < 2 > using hot melt adhesive or solvent adhesive mixed with 0.5 to 56% by weight of at least one colorant selected from the group consisting of pigments, dyes, (100). ≪ RTI ID = 0.0 > 11. < / RTI >
KR1020180154912A 2018-12-05 2018-12-05 Seam sealing tape and manufacturing method thereof KR101957115B1 (en)