KR101932079B1 - Filter for air cleaner having hybrid activated carbon powder - Google Patents

Filter for air cleaner having hybrid activated carbon powder Download PDF

Info

Publication number
KR101932079B1
KR101932079B1 KR1020160168360A KR20160168360A KR101932079B1 KR 101932079 B1 KR101932079 B1 KR 101932079B1 KR 1020160168360 A KR1020160168360 A KR 1020160168360A KR 20160168360 A KR20160168360 A KR 20160168360A KR 101932079 B1 KR101932079 B1 KR 101932079B1
Authority
KR
South Korea
Prior art keywords
urethane foam
activated carbon
carbon powder
impregnated
filter
Prior art date
Application number
KR1020160168360A
Other languages
Korean (ko)
Other versions
KR20180067747A (en
Inventor
이성우
김성훈
박석훈
Original Assignee
에스지생활안전 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 에스지생활안전 주식회사 filed Critical 에스지생활안전 주식회사
Priority to KR1020160168360A priority Critical patent/KR101932079B1/en
Publication of KR20180067747A publication Critical patent/KR20180067747A/en
Application granted granted Critical
Publication of KR101932079B1 publication Critical patent/KR101932079B1/en

Abstract

본 발명은 크기가 소형화되고 가스 흡착효과가 큰 하이브리드 활성탄 분말이 함침된 공기정화기 필터에 관한 것으로서, 본 발명의 일 실시예에 따르면, 틀을 형성하는 프레임, 상기 프레임에 장착되며, 통과되는 공기 중 미세입자를 여과하는 필터층, 상기 프레임에 장착되며, 투과되는 공기 중 유해가스를 흡착하여 제거하는 활성탄 분말이 침적된 우레탄 폼, 을 포함하는 하이브리드 활성탄 분말이 함침된 공기정화기 필터가 제공된다.The present invention relates to an air purifier filter impregnated with a hybrid activated carbon powder having a small size and a large gas adsorption effect. According to an embodiment of the present invention, there is provided an air purifier filter comprising a frame forming a frame, There is provided an air purifier filter impregnated with a hybrid activated carbon powder comprising a filter layer for filtering fine particles, and a urethane foam, which is mounted on the frame and on which activated carbon powder is adsorbed and removed from the air to be absorbed and removed.

Description

하이브리드 활성탄 분말이 함침된 공기정화기 필터{FILTER FOR AIR CLEANER HAVING HYBRID ACTIVATED CARBON POWDER}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a filter for air cleaner having a hybrid activated carbon powder impregnated therein,

본 발명은 하이브리드 활성탄 분말이 함침된 공기정화기 필터에 필터에 관한 것으로서, 보다 상세하게는, 크기가 소형화되고 가스 흡착효과가 큰 하이브리드 활성탄 분말이 함침된 공기정화기 필터에 관한 것이다.The present invention relates to an air purifier filter impregnated with a hybrid activated carbon powder, and more particularly to an air purifier filter impregnated with a hybrid activated carbon powder having a small size and a large gas adsorption effect.

근래에 환경 특히 대기오염도가 심해지면서 환경에 관한 관심이 높아지면서, 공기정화기가 많이 사용되고 있다.BACKGROUND OF THE INVENTION [0002] Air pollutants have been widely used in recent years as environment, especially air pollution, has become more and more concerned about the environment.

이러한 공기정화기(10)는 도 1에 도시된 바와 같이, 주변의 공기를 흡입하면서 필터(20)를 통해 여과시켜 공기에 포함된 유해가스나 미세먼지를 여과한 후, 이를 다시 배출하는 방식으로 운용된다.1, the air purifier 10 filters the harmful gas or fine dust contained in the air by sucking the surrounding air while filtering the air through the filter 20, do.

이러한 공기정화기에 사용되는 필터(20)를 자세하게 도시하자면, 도 2에 도시된 바와 같이, 프레임(21)과 헤파필터(22), 활성탄층(24)을 포함할 수 있다.The filter 20 used in such an air purifier may include a frame 21, a HEPA filter 22, and an activated carbon layer 24 as shown in FIG. 2 in detail.

상기 프레임(21)은, 필터(21)의 테두리를 형성하며, 그 내측에 상기 헤파필터(22)와 활성탄층(24)이 장착되고, 헤파필터(22)와 활성탄층(24)이 장착된 상태로 공기정화기(10)에 장착될 수 있다.The frame 21 forms the rim of the filter 21 and the HEPA filter 22 and the activated carbon layer 24 are mounted on the inside of the frame 21. The HEPA filter 22 and the activated carbon layer 24 are mounted Can be mounted to the air cleaner (10).

상기 헤파필터(22)는 공기중에 미세한 미세먼지를 여과하는 필터이며, 상기 헤파필터(22)의 후측에 활성탄층(24)이 구비된다.The HEPA filter 22 is a filter for filtering minute fine dust in the air, and an activated carbon layer 24 is provided on the rear side of the HEPA filter 22.

상기 활성탄층(24)은 내부에 복수개의 격벽(26)으로 구획되고, 격벽(26)으로 구획된 공간마다 활성탄 알갱이(28)가 복수개 채워져 있다.The activated carbon layer 24 is partitioned into a plurality of partition walls 26 and a plurality of activated carbon particles 28 are filled in each space partitioned by the partition walls 26.

따라서, 상기 헤파필터(22)를 통과하면서 미세먼지가 여과된 공기가 상기 활성탄층(24)을 통과하면서 유해가스등이 활성탄 알갱이(28)에 흡착되어 여과될 수 있다.Accordingly, as air passing through the HEPA filter 22 passes through the activated carbon layer 24, harmful gas can be adsorbed on the activated carbon particles 28 and filtered.

그러나, 이와 같은 종래의 필터(20)는 다음과 같은 문제점이 있다.However, such a conventional filter 20 has the following problems.

일반적으로 필터를 쓰는 공기정화기는 실내용으로 제작된다. 그런데, 최근들어 환경에 관한 관심이 높아지면서 자동차 실내 공기환경에 대한 관심도 높아지고 있다.In general, air purifiers that use filters are made in-house. In recent years, interest in the environment has increased, and interest in the indoor air environment of the automobile is increasing.

자동차 실내는 외부 도로에서 유입되는 매연이나 질소산화물 미세먼지를 비롯하여, 자동차 실내에서 발생되는 먼지 및 세균과 포름알데히드 등의 가스성 물질로 인해 공기오염도가 높은 경향을 띈다.Car interior tends to have high air pollution due to soot and nitrogen oxide fine dust coming from outside roads, dust generated in automobile interior, gaseous substances such as bacteria and formaldehyde.

그런데, 종래의 공기정화기는 대부분 건물의 실내에서 사용되는 것을 상정하고 제작되어 그 크기가 자동차 실내에 사용하기엔 어려운 문제점이 있다.However, the conventional air purifier has a problem that it is difficult to use the air purifier in the interior of the automobile because the air purifier is generally manufactured assuming that the air purifier is used in the interior of a building.

또한, 종래의 공기정화기 필터(20)는 활성탄층(24)이 복수개의 격벽(26)으로 구획되고, 구획된 내부공간에 활성탄 알갱이(28)가 복수개 채워지는데, 이 때 구획된 공간내부에 채워진 활성탄 알갱이(28)가 중력에 의해 공간 내부의 하측에 몰려 쌓이게 되고 그 상측에 빈 곳이 발생할 수 있다. 이 때, 상기 활성탄이 비어있는 곳으로 흐르는 공기는 가스가 여과되지 못한 체 통과될 수 있어 여과성능이 하락할 수 있으며, 격벽 자체의 크기가 있어 크기 및 두께를 줄이는데 한계가 있다.In the conventional air purifier filter 20, the activated carbon layer 24 is divided into a plurality of partition walls 26, and a plurality of activated carbon particles 28 are filled in the partitioned inner space. At this time, The active carbon particles 28 are accumulated on the lower side of the space due to gravity and empty space may be formed thereon. At this time, the air flowing to the vacant space of the activated carbon can be passed through the filter without being filtered, so that the filtration performance may be lowered, and there is a limit in reducing the size and thickness due to the size of the partition wall itself.

또한, 상기 활성탄 알갱이가 외력에 의해 움직이는데, 차량용으로 사용할 경우 차량의 움직임에 의해 활성탄 알갱이가 움직일 수 있어 소음이 발생할 수 있다.In addition, when the active carbon particles are moved by an external force, the active carbon particles may move due to the movement of the vehicle, resulting in noise.

본 발명은 상기와 같은 문제점을 해결하기 위한 것으로서, 보다 소형화가 가능하고, 자세에 따라 가스 흡착 성능의 변동이 없으며, 소음이 발생될 우려가 없는 하이브리드 활성탄 분말이 함침된 공기정화기 필터를 제공하는 것이 과제이다.SUMMARY OF THE INVENTION It is an object of the present invention to provide an air purifier filter in which a hybrid activated carbon powder impregnated with a hybrid activated carbon powder which can be further downsized, has no fluctuation in gas adsorption performance according to its attitude, It is an assignment.

본 발명의 과제들은 이상에서 언급한 과제들로 제한되지 않으며, 언급되지 않는 또 다른 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.The problems of the present invention are not limited to the above-mentioned problems, and other problems not mentioned can be clearly understood by those skilled in the art from the following description.

상기와 같은 과제를 해결하기 위하여, 본 발명의 일 실시예에 따르면, 틀을 형성하는 프레임, 상기 프레임에 장착되며, 통과되는 공기 중 미세입자를 여과하는 필터층, 상기 프레임에 장착되며, 투과되는 공기 중 유해가스를 흡착하여 제거하는 활성탄 분말이 침적된 우레탄 폼을 포함하는 하이브리드 활성탄 분말이 함침된 공기정화기 필터가 제공된다.According to an aspect of the present invention, there is provided a method of fabricating a frame, comprising: forming a frame, a filter layer mounted on the frame and filtering fine particles in the air passing through the frame, There is provided an air cleaner filter impregnated with a hybrid activated carbon powder containing a urethane foam on which activated carbon powder adsorbed and removed by the harmful gas is deposited.

상기 우레탄 폼의 공기가 유입되는 측 전면에 구비되며, 투과되는 공기 중 입자가 큰 먼지를 여과하는 메쉬망, 상기 프레임에 장착되며, 상기 메쉬망의 공기가 유입되는 측 전면에 설치되고, 상기 메쉬망 및 우레탄 폼과 필터층을 프레임에 고정시키는 팬스를 더 포함할 수 있다.A mesh network provided on the side of the air inlet side of the urethane foam for filtering large dust particles in the air to be permeated, a mesh net installed on the frame, And a fence for securing the mesh and urethane foam and the filter layer to the frame.

상기 우레탄 폼은 상기 필터층의 공기가 유입되는 측 전면에 설치될 수 있다.The urethane foam may be installed on a front surface of the filter layer through which air is introduced.

상기 우레탄 폼은, 활성탄 분말을 포함하는 함침용액에 담궈져 활성탄 분말이 적셔지는 함침부, 상기 함침부에서 활성탄 분말이 함침된 우레탄 폼을 압착하여, 상기 우레탄 폼에 적셔진 여분의 함침용액을 압착배출시키고, 상기 우레탄 폼을 이송시키면서 제1온도로 1차 건조시키는 1차 건조부, 상기 1차 건조부를 거친 상기 우레탄 폼을 이송시키면서 제2온도로 가열하여 건조 및 열처리하는 2차 건조부를 포함하는 함침장치에 의해 제조될 수 있다.The urethane foam is compressed by impregnating the urethane foam impregnated with the activated carbon powder in the impregnation portion in which the activated carbon powder is dipped in the impregnation solution containing activated carbon powder and the impregnated portion is compressed in the impregnation portion, A primary drying unit for discharging the urethane foam and primarily drying the urethane foam at a first temperature while conveying the urethane foam, a secondary drying unit for heating the secondary urethane foam to the second temperature, drying and heat- Can be produced by an impregnating apparatus.

상기 함침부는, 상기 함침용액을 이루는 원료 중 일부가 투입되어 교반되는 제1교반기, 제1교반기와 연결되어 제1교반기에서 교반된 원료가 유입되며, 상기 함침용액을 이루는 원료 중 나머지가 투입되어 교반되는 제2교반기, 상기 제1교반기 및 제2교반기에서 교반된 함침용액이 유입되며, 상기 우레탄 폼이 담겨 유입된 함침용액이 적셔지는 함침조를 포함할 수 있다.The impregnation part is connected to a first agitator and a first agitator, in which a part of the raw material constituting the impregnation solution is injected and agitated, the raw material stirred in the first agitator is introduced, the rest of the raw materials constituting the impregnation solution are introduced, And the impregnation tank in which the impregnation solution stirred in the first and second agitators is introduced and the impregnation solution containing the urethane foam is impregnated.

상기 1차 건조부는, 상기 함침부에서 함침된 우레탄 폼을 수평상태로 압착 이송시키면서, 여분의 용액을 압착배출시키는 적어도 한 쌍 이상의 수평 압착 롤러부, 상기 수평 압착 롤러부를 거친 후 이송되는 우레탄 폼을 가열시키는 제1가열부를 포함할 수 있다.The primary drying unit includes at least one pair of horizontal compression roller units for conveying the urethane foam impregnated in the impregnation unit in a horizontal state by pressing and discharging the excess solution, a urethane foam to be conveyed after passing through the horizontal compression roller unit, And a first heating section for heating the first heating section.

상기 2차 건조부는, 상기 우레탄 폼이 수직방향으로 상방향과 하방향으로 복수회 교번하여 이송되도록 구비되는 적어도 한 쌍 이상의 수직 롤러부, 상기 수직 롤러부에 의해 이송되는 우레탄 폼을 가열하여 열처리하는 제2가열부를 포함할 수 있다.The secondary drying unit may include at least one pair of vertical roller units arranged to vertically and vertically transfer the urethane foam in a plurality of alternating directions, and heat and heat the urethane foam conveyed by the vertical roller unit And a second heating unit.

상기 함침용액은, 분산제, 활성탄분말, 결합제, 증점제, 난연제 및 물이 혼합된 용액일 수 있다.The impregnating solution may be a mixed solution of a dispersing agent, activated carbon powder, a binder, a thickener, a flame retardant, and water.

본 발명은 상기와 같은 문제점을 해결하기 위한 것으로서, 보다 소형화가 가능하고, 자세에 따라 가스 흡착 성능의 변동이 없으며, 소음이 발생될 우려가 없는 하이브리드 활성탄 분말이 함침된 공기정화기 필터를 제공하는 것이 과제이다.SUMMARY OF THE INVENTION It is an object of the present invention to provide an air purifier filter in which a hybrid activated carbon powder impregnated with a hybrid activated carbon powder which can be further downsized, has no fluctuation in gas adsorption performance according to its attitude, It is an assignment.

본 발명의 하이브리드 활성탄 분말이 함침된 공기정화기 필터에 따르면, 첫째, 미세한 폴리우테탄 폼 조직에 활성탄 분말이 함침되므로, 격벽을 형성할 필요가 없어 두께가 보다 얇아질 수 있다.According to the air purifier filter impregnated with the hybrid activated carbon powder of the present invention, first, since the activated carbon powder is impregnated into the fine polyurethane foam structure, the thickness can be thinned because there is no need to form the partition wall.

둘째, 미세한 우테란 폼 조직에 미세한 활성탄 분말이 함침되므로 필터의 경사에 따라 활성탄 분말이 중력이나 외력에 의해 편중 되지 아니하므로 필터의 경사에 따른 유해가스 흡착 효과의 변동이 없으며, 외부의 충격에 의한 소음이 방지될 수 있다.Second, since fine activated carbon powder is impregnated into the fine Uteran foam, the activated carbon powder is not biased by gravity or external force according to the inclination of the filter. Therefore, there is no fluctuation of the harmful gas adsorption effect according to the inclination of the filter. Noise can be prevented.

본 발명의 효과들은 이상에서 언급한 효과들로 제한되지 않으며, 언급되지 않은 또 다른 효과들은 청구범위의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.The effects of the present invention are not limited to the effects mentioned above, and other effects not mentioned can be clearly understood by those skilled in the art from the description of the claims.

아래에서 설명하는 본 출원의 바람직한 실시예의 상세한 설명뿐만 아니라 위에서 설명한 요약은 첨부된 도면과 관련해서 읽을 때에 더 잘 이해될 수 있을 것이다. 본 발명을 예시하기 위한 목적으로 도면에는 바람직한 실시예들이 도시되어 있다. 그러나, 본 출원은 도시된 정확한 배치와 수단에 한정되는 것이 아님을 이해해야 한다.
도 1은 종래의 일반적인 공기정화기를 도시한 도면;
도 2는 종래의 공기정화기에 장착되는 필터를 도시한 분해사시도;
도 3은 본 발명의 일 실시예에 따른 하이브리드 활성탄 분말이 함침된 공기정화기 필터를 도시한 분해 사시도;
도 4는 도 3의 하이브리드 활성탄 분말이 함침된 공기정화기 필터의 단면도;
도 5는 도 3의 우레탄 폼에 하이브리드 활성탄 분말을 함침시키기 위한 함침장치를 도시한 도면; 그리고
도 6은 도 3의 우레탄 폼을 촬영한 사진이다.The foregoing summary, as well as the detailed description of the preferred embodiments of the present application set forth below, may be better understood when read in conjunction with the appended drawings. For the purpose of illustrating the invention, there are shown preferred embodiments in the figures. It should be understood, however, that this application is not limited to the precise arrangements and instrumentalities shown.
1 illustrates a conventional air purifier;
2 is an exploded perspective view showing a filter mounted on a conventional air purifier;
3 is an exploded perspective view illustrating an air purifier filter impregnated with a hybrid activated carbon powder according to an embodiment of the present invention;
FIG. 4 is a cross-sectional view of the air cleaner filter impregnated with the hybrid activated carbon powder of FIG. 3; FIG.
FIG. 5 is a view showing an impregnating apparatus for impregnating the urethane foam of FIG. 3 with the powder of hybrid activated carbon; And
FIG. 6 is a photograph of the urethane foam of FIG. 3; FIG.

이하 본 발명의 목적이 구체적으로 실현될 수 있는 본 발명의 바람직한 실시예를 첨부된 도면을 참조하여 설명한다. 본 실시예를 설명함에 있어서, 동일 구성에 대해서는 동일 명칭 및 동일 부호가 사용되며 이에 따른 부가적인 설명은 생략하기로 한다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, preferred embodiments of the present invention will be described with reference to the accompanying drawings. In describing the present embodiment, the same designations and the same reference numerals are used for the same components, and further description thereof will be omitted.

본 실시예에 따른 활성탄 분말이 함침된 공기정화기 필터(이하, 설명의 편의를 위하여 '공기정화기 필터'라 칭하기로 한다)는 도 3에 도시된 바와 같이 프레임(110), 필터층(120), 우레탄 폼(130)을 포함할 수 있다.As shown in FIG. 3, the air purifier filter (hereinafter, referred to as an 'air purifier filter') for impregnating activated carbon powder according to the present embodiment includes a frame 110, a filter layer 120, a urethane (130). ≪ / RTI >

상기 프레임(110)은 후술하는 필터층(120)과 우레탄 폼(130)이 장착되며, 각 필터층(120)이 장착된 상태로 공기정화기의 본체에 장착되는 틀을 형성할 수 있다.The frame 110 may include a filter layer 120 and a urethane foam 130 to be described later and may form a frame to be mounted on the main body of the air purifier with the filter layers 120 mounted thereon.

그리고, 상기 필터층(120)은 상기 프레임(110)에 장착되며, 공기가 통과되며, 통과되는 공기중 미세입자를 여과하는 헤파필터일 수 있다.The filter layer 120 may be a HEPA filter mounted on the frame 110 and passing air therethrough and filtering fine particles in the air passing through the filter layer 120.

그리고, 상기 우레탄 폼(130)은 상기 필터층(120)에 겹쳐서 상기 프레임(110)에 장착되며, 다공성 조직으로 이루어져 조직 사이로 공기의 투과가 가능하고, 조직에 활성탄 분말이 함침되어 투과되는 공기 중의 유해가스를 흡착하여 제거할 수 있다.The urethane foam 130 is attached to the frame 110 so as to be superimposed on the filter layer 120. The urethane foam 130 is porous and permeable to air between the tissues. The active carbon powder is impregnated into the tissue, Gas can be adsorbed and removed.

또한, 메쉬망(140)과 펜스(150)가 더 구비될 수 있다.Further, the mesh network 140 and the fence 150 may be further provided.

상기 메쉬망(140)은 상기 우레탄 폼(130)의 공기가 유입되는 측 전면에 구비되어 메쉬 사이로 공기가 유동하도록 구비되며, 비교적 큰 입자의 먼지를 여과할 수 있다.The mesh net 140 is provided on the front side of the urethane foam 130 on the air inlet side, and air is allowed to flow between the mesh net 140 and the dust of relatively large particles can be filtered.

그리고, 상기 필터층(120)과 우레탄 폼(130) 및 메쉬망(140)을 상기 프레임(110)에 고정하는 팬스(150)가 더 구비될 수 있다.Further, a fence 150 may be further provided for fixing the filter layer 120, the urethane foam 130, and the mesh net 140 to the frame 110.

따라서, 도 4에 도시된 바와 같이, 상기 공기정화기 필터를 통과하는 공기중 입자가 큰 먼지는 상기 메쉬망(140)에서 걸러지며, 유해가스는 상기 우레탄 폼(130)에서 걸러지고, 미세한 입자의 먼지는 상기 필터층(120)에서 걸러질 수 있다.Therefore, as shown in FIG. 4, large particles of air in the air passing through the air cleaner filter are filtered by the mesh net 140, noxious gas is filtered by the urethane foam 130, Dust can be filtered in the filter layer 120.

또한, 상기 우레탄 폼(130)의 미세한 조직에 미세한 분말인 활성탄 분말이 함침되어 있으므로, 종래의 격벽(26)을 형성할 필요가 없어 두께를 보다 얇게 형성할 수 있으며, 활성탄 분말이 조직에 함침되어 우레탄 폼의 기울기에 따라 이동되지 아니하므로, 다양한 자세로 활성탄 분말을 설치할 수 있으며, 우레탄 폼(130)을 통과하는 공기에 포함된 유해가스가 균일하게 제거될 수 있다. In addition, since the fine structure of the urethane foam 130 is impregnated with powder of activated carbon, which is a fine powder, it is not necessary to form the conventional partition wall 26, and the thickness can be made thinner. The activated carbon powder can be installed in various postures and the noxious gas contained in the air passing through the urethane foam 130 can be uniformly removed since it is not moved along the slope of the urethane foam.

한편, 상기 활성탄 분말이 침적된 우레탄 폼(130)에서 외부 충격 등으로 인해 활성탄 분말이 이탈될 수 있는데, 이렇게 이탈된 활성탄 분말이 실내로 유입되는 것을 차단하기 위하여 상기 우레탄 폼(130)은 상기 필터층(120)의 공기가 유입되는 측 전면에 설치될 수 있다.Meanwhile, the activated carbon powder may be separated due to an external impact or the like in the urethane foam 130 on which the activated carbon powder is immersed. In order to prevent the powder of activated carbon from being released into the room, the urethane foam 130, (120) may be installed on the front side of the air inlet.

따라서, 상기 우레탄 폼(130)에서 이탈된 활성탄 분말은 공기의 흐름을 따라 상기 필터층(120)으로 유입되어 상기 필터층(120)에서 여과될 수 있다.Therefore, the activated carbon powder separated from the urethane foam 130 flows into the filter layer 120 along with the flow of air and can be filtered in the filter layer 120.

한편, 이하에서는 상기와 같은 우레탄 폼에 활성탄 분말을 함침하는 함침장치(200)에 대해서 설명하기로 한다.Hereinafter, the impregnating apparatus 200 for impregnating the urethane foam with activated carbon powder will be described.

본 실시예에 따른 함침장치(200)는, 도 5에 도시된 바와 같이, 함침부(210), 1차건조부(220) 및 2차 건조부(230)를 포함할 수 있다.The impregnating apparatus 200 according to the present embodiment may include an impregnating unit 210, a primary drying unit 220, and a secondary drying unit 230, as shown in FIG.

상기 함침부(210)는 활성탄 분말을 포함하는 함침용액이 상기 우레탄 폼에 적셔지는 구성요소로서, 제1교반기(212) 및 제2교반기(214)와 함침조(216)를 포함할 수 있다.The impregnation unit 210 may include a first stirrer 212, a second stirrer 214, and an impregnation tank 216, in which the impregnation solution containing activated carbon powder is immersed in the urethane foam.

이 때, 상기 함침용액은 상기 우레탄 폼(130)에 활성탄 분말을 함침시키기 위하여, 활성탄 분말을 포함하는 여러가지 성분의 원료가 혼합된 용액을 뜻한다.In this case, the impregnating solution refers to a solution in which raw materials of various components including activated carbon powder are mixed to impregnate the urethane foam 130 with activated carbon powder.

상기 제1교반기(212)는, 상기 함침용액을 이루는 원료 중 일부가 투입되어 교반되는 구성요소이며, 상기 제2교반기(214)는 상기 함침용액을 이루는 원료 중 제1교반기(212)에 투입된 원료를 제외한 나머지 원료가 투입되어 교반되며, 상기 제1교반기(212)와 연통되어 상기 제1교반기(212)에서 교반된 원료가 유입되어 같이 혼합될 수 있다.The first stirrer 212 is a component in which a part of the raw materials constituting the impregnating solution is injected and agitated. The second stirrer 214 mixes the raw materials, which are supplied to the first stirrer 212, And the raw materials in the first agitator 212 are introduced into the first agitator 212. The agitated raw materials are mixed and mixed with each other.

상기 제1교반기(212)와 제2교반기(214)에서 혼합된 함침용액은 상기 함침조(216)에 담기고, 상기 함침조(216)에서는 상기 우레탄 폼(130)이 상기 함침용액에 잠겨 적셔질 수 있다.The impregnation solution mixed in the first stirrer 212 and the second stirrer 214 is contained in the impregnation tank 216 and the urethane foam 130 is immersed in the impregnation solution in the impregnation tank 216 Can be.

상기 우레탄 폼(130)은 롤의 형태로 말린 상태로 장착되며, 풀리면서 상기 함침조(216)에서 함침용액에 잠기도록 구비될 수 있다.The urethane foam 130 may be mounted in a rolled state in the form of a roll, and may be provided to be submerged in the impregnation solution in the impregnation tank 216 while being pulverized.

한편, 1차 건조부(220)는, 상기 함침부(210)에서 활성탄 분말이 함침된 우레탄 폼(130)을 압착하여 상기 우레탄 폼(130)에 함침된 여분의 함침용액을 압착 배출시키고, 상기 우레탄 폼(130)을 이송시키면서 1차 건조시키는 구성요소로서, 상기 함침부(210)의 후단에 상기 함침부(210)와 연속적인 공정을 이루도록 구비될 수 있다.The primary drying unit 220 presses the urethane foam 130 impregnated with activated carbon powder in the impregnation unit 210 to pressurize and discharge the excess impregnation solution impregnated in the urethane foam 130, The urethane foam 130 may be a primary component to be dried while conveying the urethane foam 130, and may be provided at a rear end of the impregnation unit 210 to perform a continuous process with the impregnation unit 210.

상기 1차 건조부(220)는, 수평 압착롤러부(222) 및 제1가열부(224)를 포함할 수 있다.The primary drying unit 220 may include a horizontal pressing roller unit 222 and a first heating unit 224.

상기 수평 압착롤러부(222)는 적어도 한 쌍 이상 구비되어, 상기 함침부(210)에서 함침된 우레탄 폼(130)을 수평상태로 이송시키면서 압착하여, 상기 함침부(210)를 거친 우레탄 폼(130)에 적셔진 여분의 함침용액을 압착 배출시키는 구성요소이다.At least one pair of the horizontal compression roller units 222 are provided so that the urethane foam 130 impregnated in the impregnation unit 210 is horizontally conveyed while being pressed to form a urethane foam 130) of the impregnated solution.

상기 함침조(216)를 통과한 우레탄 폼(130)은 함침용액이 과하게 적셔진 상태로서, 그 무게가 무척 무거워 그대로 이송시킬 경우 우레탄 폼(130)이 늘어나거나 끊어지는 현상이 발생할 수 있다.The urethane foam 130 having passed through the impregnation tank 216 is in a state where the impregnation solution is excessively wetted. If the weight of the impregnation solution is too heavy, the urethane foam 130 may stretch or break.

따라서, 상기 수평 압착롤러부(222)는 상기 함침용액이 함침된 우레탄 폼(130)을 수평상태로 이송시키면서 압착하여, 중력의 영향을 최소화 하면서, 상기 우레탄 폼(130)에 적셔진 여분의 함침용액을 압착 배출함으로써 무게를 최소화 시키는 것이다.Therefore, the horizontal compression roller unit 222 compresses the urethane foam 130 impregnated with the impregnation solution while horizontally conveying the same, thereby minimizing the influence of gravity. Thus, the urethane foam 130, The solution is compressed and discharged to minimize weight.

또한, 상기 제1가열부(224)는 상기 수평 압착롤러부(222)를 통과한 우레탄 폼(130)을 제1온도로 1차 건조시켜 무게를 더욱 줄일 수 있다.The first heating unit 224 may further reduce the weight by first drying the urethane foam 130 having passed through the horizontal compression roller unit 222 to a first temperature.

이 때, 상기 제1온도는 120도 이상 180도 미만일 수 있다.At this time, the first temperature may be 120 degrees or less and 180 degrees or less.

상기 1차 건조부(220)에서 1차 건조된 우레탄 폼(130)은 롤에 말려 권취된 상태로 2차 건조부(230)로 향할 수 있다.The urethane foam 130 primarily dried in the primary drying unit 220 may be directed to the secondary drying unit 230 while being wound on a roll.

상기 2차 건조부(230)는 상기 1차 건조부(220)를 마친 우레탄 폼(130)을 이송시키면서 제2온도로 가열하여 건조 및 열처리 하는 구성요소이다.The secondary drying unit 230 is a component that heats the urethane foam 130 that has completed the primary drying unit 220 to a second temperature and dries and heat-treats the same.

즉, 상기 1차 건조부(220)에서 1차 건조된 후 롤에 말린 우레탄 폼(130)을 장착한 후 상기 2차 건조부(230)를 거치도록 각 롤러에 권취시킬 수 있다.That is, after the primary drying unit 220 is primarily dried, the dried urethane foam 130 may be mounted on the rolls and then wound on the rollers to pass through the secondary drying unit 230.

상기 2차 건조부(230)는 수직 롤러부(232) 및 제2가열부(234)를 포함할 수 있다.The secondary drying unit 230 may include a vertical roller unit 232 and a second heating unit 234.

상기 수직 롤러부(232)는 상기 우레탄 폼(130)이 수직방향으로 상방향과 하방향으로 복수회 교번하여 이송되도록 구비되는 한 쌍 이상의 롤러가 수평방향으로 일정간격 이격되어 상하 방향으로 배치될 수 있다. The vertical roller part 232 may be disposed in the vertical direction so that the urethane foam 130 is vertically and vertically conveyed in a plurality of alternating directions. have.

이는 상기 우레탄 폼(130)을 건조할 때 공간을 보다 적게 차지하게 하기 위함이다.This is to make the urethane foam 130 occupy less space when it is dried.

또한, 상기 제2가열부(234)는 상기 수직 롤러부(232)에 의해 이송되는 우레탄 폼(130)을 가열하여 2차 건조하여 완전히 건조시킴과 동시에 함침된 활성탄 분말이 보다 견고하게 함침상태를 유지하도록 열처리 할 수 있다.The second heating part 234 heats the urethane foam 130 conveyed by the vertical roller part 232 to dry it completely and dry the impregnated activated carbon powder more firmly, Heat treatment can be performed.

이때, 상기 제2가열부(234)는 제2온도로 가열할 수 있으며, 상기 제2온도는 섭싸 40도 에서 섭씨 120도 사이일 수 있다.At this time, the second heating part 234 may be heated to a second temperature, and the second temperature may be between 40 degrees Celsius and 120 degrees Celsius.

한편, 이하에서는 상기 우레탄 폼에 활성탄 분말을 함침하기 위한 함침용액에 대해서 설명하기로 한다.Hereinafter, the impregnation solution for impregnating the urethane foam with the activated carbon powder will be described.

상기 함침용액은, 활성탄분말, 분산제, 결합제, 증점제, 난연제 및 물이 혼합된 용액일 수 있다.The impregnating solution may be a mixed solution of activated carbon powder, a dispersant, a binder, a thickener, a flame retardant, and water.

이 때, 상기 활성탄 분말은 미립화된 활성탄 가루로서 예를 들어 Granscar 1800이 적용될 수 있고, 상기 분산제는 함침 용액내에 상기 활성탄 분말등의 원료가 골고루 분산되도록 하는 원료로서 예를 들어 고형분 18%의 Gransperse M-60등이 적용될 수 있다. 또한, 상기 결합제는 활성탄 분말을 우레탄 폼 조직에 부착시키는 구성요소로서 고형분38%의 Grantex CP가 적용될 수 있고, 증점재는 함침용액의 점도를 증가시키는 구성요소로서 고형분 28% Grantex-288의 5%용액 등이 적용될 수 있다. 또한, 상기 난연제는 내화성을 증가시키는 원료로서 Phos chek P/30이 적용될 수 있다.In this case, the activated carbon powder may be Granscar 1800, for example, as an atomized activated carbon powder. The dispersant may be, for example, Gransperse M having a solid content of 18% as a raw material for dispersing the raw materials such as activated carbon powder uniformly in the impregnation solution -60 can be applied. The binder may be Grantex CP having a solid content of 38% as a component for attaching the activated carbon powder to the urethane foam structure, and the thickening material may be a component for increasing the viscosity of the impregnation solution, such as a solid content of 28%, Grantex- Solution or the like may be applied. Further, Phos chek P / 30 may be applied as a raw material for increasing the fire resistance of the flame retardant.

또한 필요에 따라 결합력을 증강시키는 용도로서 흡착제가 더 혼합될 수 있다. 상기 흡착제는 WSRN-80 등의 수용성 레진이 적용될 수 있다.If necessary, an adsorbent may be further mixed to increase the binding force. The adsorbent may be a water-soluble resin such as WSRN-80.

이때, 상기 활성탄은 전체의 20~26%비율로 혼합될 수 있고, 분산제는 1~4%로 혼합될 수 있다. 그리고, 증점제는 0.6~0.9% 혼합될 수 있고, 결합제는 2~6%, 난연제는 1.5~2.0% 혼합될 수 있다. 또한 물은 전체의 60~70% 사이일 수 있다. 또한, 필요에 따라 흡착제가 0.3~0.7% 혼합될 수 있다.At this time, the activated carbon may be mixed in a proportion of 20 to 26% of the total, and the dispersing agent may be mixed in 1 to 4%. The thickener may be mixed with 0.6 to 0.9%, the binder to 2 to 6%, and the flame retardant to 1.5 to 2.0%. Water can also be between 60 and 70% of the total. Further, 0.3 to 0.7% of the adsorbent may be mixed as needed.

물론, 상기와 같은 함침용액에 포함되는 원료의 종류 및 배합비율은 당업자의 사정에 의해 변경이 가능한 것이다.Of course, the kinds and the mixing ratios of the raw materials included in the impregnation solution as described above can be changed by a person skilled in the art.

한편, 이하에서는 전술한 함침장치로서 상기 우레탄 폼에 활성탄 분말을 함침하는 과정에 대해서 설명하기로 한다.Hereinafter, the process of impregnating the urethane foam with activated carbon powder as the above-described impregnation apparatus will be described.

먼저, 분산제와 물을 제2교반기(214)에 투입한 후 소정시간동안 교반한다. 그리고, 활성탄 분말과 물을 상기 제2교반기(214)에 투입한 후 소정시간동안 교반한 후에 결합제와 증점제를 제2교반기(214)에 투입한다.First, the dispersant and water are introduced into a second stirrer 214 and stirred for a predetermined time. Then, the activated carbon powder and water are introduced into the second agitator 214, stirred for a predetermined time, and then the binder and the thickener are introduced into the second agitator 214.

그리고, 난연제와 물을 제1교반기(212)에 투입한 후 소정시간동안 상기 제2교반기(214)와는 별도로 교반시킬 수 있다. 이 때, 난연제의 부착력 유지를 위하여 수용성 레진을 필요에 따라 첨가할 수 있다.Then, the flame retardant and water may be added to the first stirrer 212 and stirred for a predetermined time separately from the second stirrer 214. At this time, a water-soluble resin may be added as needed to maintain the adhesion of the flame retardant.

그리고, 상기 제1교반기(212)에서 교반된 난연제와 물의 혼합물을 제2교반기(214)에 유입시킨 후, 상기 제2교반기(214)에서 교반되는 혼합물과 함께 소정시간동안 교반시킨 후에 교반이 완료된 함침용액을 함침조에 공급할 수 있다.After the mixture of the flame retardant and water stirred in the first stirrer 212 is introduced into the second stirrer 214 and then stirred together with the mixture to be stirred in the second stirrer 214 for a predetermined time, The impregnating solution can be supplied to the impregnation bath.

이 때, 각 원료를 교반하는 교반시간 및 교반속도는 당업자의 실시형태 및 조건에 따라 서로 상이하게 조절할 수 있다.At this time, the stirring time and the stirring speed for stirring the respective raw materials can be adjusted differently according to the embodiments and conditions of those skilled in the art.

이상의 과정을 거친 함침용액에 함침된 우레탄 폼(130)은 도 6에 도시된 바와 같이, 활성탄 분말 및 함침용액 성분이 조직내에 함침되어 공기가 통과되면서 유해가스 성분이 조직에 함침된 활성탄 분말에 함침될 수 있다.As shown in FIG. 6, the urethane foam 130 impregnated with the impregnation solution has impregnated the active carbon powder and the impregnating solution component into the tissue, .

이상과 같이 본 발명에 따른 바람직한 실시예를 살펴보았으며, 앞서 설명된 실시예 이외에도 본 발명이 그 취지나 범주에서 벗어남이 없이 다른 특정 형태로 구체화 될 수 있다는 사실은 해당 기술에 통상의 지식을 가진 이들에게는 자명한 것이다. 그러므로, 상술된 실시예는 제한적인 것이 아니라 예시적인 것으로 여겨져야 하고, 이에 따라 본 발명은 상술한 설명에 한정되지 않고 첨부된 청구항의 범주 및 그 동등 범위 내에서 변경될 수도 있다.It will be apparent to those skilled in the art that the present invention can be embodied in other specific forms without departing from the spirit or scope of the invention as defined in the appended claims. It is obvious to them. Therefore, the above-described embodiments are to be considered as illustrative rather than restrictive, and the present invention is not limited to the above description, but may be modified within the scope of the appended claims and equivalents thereof.

100: 공기정화기 필터 110: 프레임
120: 필터층 130: 우레탄 폼
140: 메쉬망 150: 펜스
200: 함침장치 210: 함침부
212: 제1교반기 214: 제2교반기
216: 함침조 220: 1차 건조부
222: 수평 압착롤러부 224: 제1건조부
230: 2차 건조부 232: 수직 롤러부
234: 제2건조부100: air purifier filter 110: frame
120: filter layer 130: urethane foam
140: mesh net 150: fence
200: Impregnating device 210: Impregnating part
212: first stirrer 214: second stirrer
216: impregnation tank 220: primary drying unit
222: Horizontal pressing roller unit 224: First drying unit
230: secondary drying unit 232: vertical roller unit
234: Second drying section

Claims (8)

틀을 형성하는 프레임;
상기 프레임에 장착되며, 통과되는 공기 중 미세입자를 여과하는 필터층; 및
상기 프레임에 장착되며, 투과되는 공기 중 유해가스를 흡착하여 제거하는 활성탄 분말이 함침된 우레탄 폼을 포함하고;
상기 우레탄 폼은,
활성탄 분말을 포함하는 함침용액에 담궈져 활성탄 분말이 적셔지는 함침부;
상기 함침부에서 활성탄 분말이 함침된 우레탄 폼을 압착하여, 상기 우레탄 폼에 적셔진 여분의 함침용액을 압착배출시키고, 상기 우레탄 폼을 이송시키면서 제1온도로 1차 건조시키는 1차 건조부;
상기 1차 건조부를 거친 상기 우레탄 폼을 이송시키면서 제2온도로 가열하여 건조 및 열처리하는 2차 건조부;
를 포함하는 함침장치에 의해 제조되며,
상기 2차 건조부는,
상기 우레탄 폼이 수직방향으로 상방향과 하방향으로 복수회 교번하여 이송되도록 구비되는 적어도 한 쌍 이상의 수직 롤러부;
상기 수직 롤러부에 의해 이송되는 우레탄 폼을 가열하여 열처리하는 제2가열부;
를 포함하는 하이브리드 활성탄 분말이 함침된 공기정화기 필터.
A frame forming a frame;
A filter layer mounted on the frame for filtering fine particles in the air passing through; And
A urethane foam mounted on the frame and impregnated with activated carbon powder to absorb and remove noxious gas from the air to be permeated;
The urethane foam,
An impregnation unit immersed in an impregnation solution containing activated carbon powder to wet the activated carbon powder;
A primary drying unit for pressing the urethane foam impregnated with the activated carbon powder in the impregnating unit to pressurize and discharge the excess impregnation solution soaked in the urethane foam and to primarily dry the urethane foam while transferring the urethane foam;
A secondary drying unit for heating and drying the urethane foam through the primary drying unit to a second temperature while transferring the urethane foam;
≪ / RTI >
The secondary drying unit includes:
At least one pair of vertical roller parts arranged such that the urethane foam is conveyed alternately upward and downward in the vertical direction;
A second heating unit for heating and heat treating the urethane foam fed by the vertical roller unit;
Wherein the filter is impregnated with the hybrid activated carbon powder.
제1항에 있어서,
상기 우레탄 폼의 공기가 유입되는 측 전면에 구비되며, 투과되는 공기 중 입자가 큰 먼지를 여과하는 메쉬망;
상기 프레임에 장착되며, 상기 메쉬망의 공기가 유입되는 측 전면에 설치되고, 상기 메쉬망 및 우레탄 폼과 필터층을 프레임에 고정시키는 팬스;
를 더 포함하는 하이브리드 활성탄 분말이 함침된 공기정화기 필터.The method according to claim 1,
A mesh net provided on the side of the urethane foam on the air inlet side for filtering large particles of the air to be permeated;
A fence mounted on the frame and installed on a front surface of the mesh net on the air inlet side for fixing the mesh net and the urethane foam and the filter layer to the frame;
Wherein the filter is impregnated with a hybrid activated carbon powder. 제1항에 있어서,
상기 우레탄 폼은 상기 필터층의 공기가 유입되는 측 전면에 설치되는 하이브리드 활성탄 분말이 함침된 공기정화기 필터.The method according to claim 1,
Wherein the urethane foam is impregnated with a hybrid activated carbon powder installed on a side surface of the filter layer through which air flows. 삭제delete 제1항에 있어서,
상기 함침부는,
상기 함침용액을 이루는 원료 중 일부가 투입되어 교반되는 제1교반기;
제1교반기와 연결되어 제1교반기에서 교반된 원료가 유입되며, 상기 함침용액을 이루는 원료 중 나머지가 투입되어 교반되는 제2교반기;
상기 제1교반기 및 제2교반기에서 교반된 함침용액이 유입되며, 상기 우레탄 폼이 담겨져 유입된 함침용액이 적셔지는 함침조;
를 포함하는 하이브리드 활성탄 분말이 함침된 공기정화기 필터.The method according to claim 1,
Wherein the impregnating unit comprises:
A first agitator in which a part of the raw material constituting the impregnation solution is injected and stirred;
A second agitator connected to the first agitator for introducing the agitated raw material in the first agitator, and the rest of the raw material constituting the impregnating solution is introduced and stirred;
An impregnation tank into which the impregnated solution stirred in the first and second stirrers is introduced and in which the impregnated solution containing the urethane foam is impregnated;
Wherein the filter is impregnated with the hybrid activated carbon powder. 제1항에 있어서,
상기 1차 건조부는,
상기 함침부에서 함침된 우레탄 폼을 수평상태로 압착 이송시키면서, 여분의 용액을 압착배출시키는 적어도 한 쌍 이상의 수평 압착 롤러부;
상기 수평 압착 롤러부를 거친 후 이송되는 우레탄 폼을 가열시키는 제1가열부;
를 포함하는 하이브리드 활성탄 분말이 함침된 공기정화기 필터.
The method according to claim 1,
The primary drying unit includes:
At least one pair of horizontal compression roller parts for conveying the urethane foam impregnated in the impregnation part in a horizontal state by pressing and discharging the excess solution;
A first heating unit for heating the urethane foam fed through the horizontal pressing roller unit;
Wherein the filter is impregnated with the hybrid activated carbon powder.
삭제delete 제1항에 있어서,
상기 함침용액은,
분산제, 활성탄분말, 결합제, 증점제, 난연제 및 물이 혼합된 용액인 하이브리드 활성탄 분말이 함침된 공기정화기 필터.The method according to claim 1,
The impregnating solution may contain,
An air purifier filter impregnated with a hybrid activated carbon powder, which is a mixed solution of a dispersant, an activated carbon powder, a binder, a thickener, a flame retardant and water.
KR1020160168360A 2016-12-12 2016-12-12 Filter for air cleaner having hybrid activated carbon powder KR101932079B1 (en)