KR101925987B1 - A production method of wall painting tile - Google Patents

A production method of wall painting tile Download PDF

Info

Publication number
KR101925987B1
KR101925987B1 KR1020180090264A KR20180090264A KR101925987B1 KR 101925987 B1 KR101925987 B1 KR 101925987B1 KR 1020180090264 A KR1020180090264 A KR 1020180090264A KR 20180090264 A KR20180090264 A KR 20180090264A KR 101925987 B1 KR101925987 B1 KR 101925987B1
Authority
KR
South Korea
Prior art keywords
layer
weight
picture
tile
tile body
Prior art date
Application number
KR1020180090264A
Other languages
Korean (ko)
Inventor
김주홍
박정숙
Original Assignee
박정숙
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 박정숙 filed Critical 박정숙
Priority to KR1020180090264A priority Critical patent/KR101925987B1/en
Application granted granted Critical
Publication of KR101925987B1 publication Critical patent/KR101925987B1/en

Abstract

The present invention relates to a method of manufacturing a painting tile for a wall. A fiber layer, in which a polyester synthetic fiber yarn and a cotton yarn are mixed and woven in a certain ratio, is provided on a surface of a tile body through an adhesive coating layer of a certain thickness. Therefore, the tensile strength of the tile body is further improved by adhesion of the fiber layer, and the durability of the tile body can be further increased. A canvas type picture is formed on the surface of the tile body by a manual operation, rather than a formatted picture of a printing type such that a beautiful canvas-shaped picture for a wall can be appreciated. Particularly, a crosslinking agent and a curing agent are mixed with a transparent modifying acrylic polymer applied to the surface of the tile body at a certain ratio such that the durability of adhesion is excellent, the fiber layer is not wrinkled, and the cotton yarn is not laddered. By applying a transparent coating layer having a certain thickness on the surface of the picture layer at least twice or more, the picture layer is permanently preserved while preventing the picture layer from being scratched and discolored by ultraviolet rays, erased, and peeled off. Further, the color and visibility of the picture layer can be excellent.

Description

벽화용 그림 타일 제작방법{A PRODUCTION METHOD OF WALL PAINTING TILE}{A PRODUCTION METHOD OF WALL PAINTING TILE}

본 발명은 벽화용 타일 제작방법에 관한 것으로, 이는 특히 타일 본체의 표면에 일정 두께의 접착 도포층을 개재하여 면사에 폴리에스터 합성 섬유사가 일정한 비율로 혼합 직조된 섬유층을 착설하여, 상기 섬유층의 부착에 의해 타일 본체의 인장 강도가 가일층 향상되고, 상기 타일 본체의 내구성을 가일층 증대시킬 수 있음은 물론, 상기 타일 본체의 표면에 프린팅 방식의 정형화된 그림이 아닌 캔버스(canvas) 타입의 그림을 수작업에 의해 자유롭게 형성하고, 이에 띠라서 미려한 캔버스 형태의 벽화용 그림을 감상할 수 있는 벽화용 그림타일 제작방법에 관한 것이다.More particularly, the present invention relates to a method for producing a wall tile, in which a fiber layer, in which a polyester synthetic fiber yarn is mixed and woven at a predetermined ratio, is applied to a surface of a tile body through a bonding layer of a certain thickness, The tensile strength of the tile body can be improved to a great extent, the durability of the tile body can be increased, and a canvas-type picture other than printing formatted pictures can be manually hand- The present invention relates to a method of manufacturing a painting tile for a wall painting,

일반적으로 알려져있는 타일은, 도기 또는 자기를 원료로 하여 제조되며, 이때 타일의 기본 소지가 되는 점토등을 적당량의 물과 혼합하여 반죽상태로 하고 내 부의 공기를 충분히 제거한 후, 이를 판상화하여 적당한 크기 및 형상을 갖도록 성형한 다음, 결정수를 제외한 수분이 내부에 남아 있지 않을 때까지 저온에서 충분히 건조시키고 건조 완료된 판상의 성형물을 대략 900℃의 온도에서 1차 소성하고 냉각한 다음, 상기 성형물의 표면에 유약을 적용시켜 건조한 후, 이를 1300℃의 온도로 2차 소성하여 제조되는 것이다.Generally known tiles are made of ceramics or porcelain as a raw material. At this time, the clay which is the basic material of the tile is mixed with an appropriate amount of water to make a kneaded state, the inner air is sufficiently removed, And then sufficiently dried at a low temperature until moisture other than the crystal water is left in the inside, and the dried plate-shaped product is firstly sintered at a temperature of about 900 DEG C and cooled. After that, Dried by applying a glaze to the surface thereof, and then fired at a temperature of 1300 ° C.

상기와 같은 타일의 표면에 벽화등의 그림이 형성되어 있는 타일을 제조하는 경우에는, 상기와 같이 1차 소성이 완료된 판상의 타일 표면에 연소성의 물질을 사용하여 밑그림을 그리고, 상기 그 밑그림을 바탕으로 하여 소성후에 각기 다른 색상으로 표현되는 안료가 혼합되어 있는 유약을 사용하여 그림을 그려넣은 다음 소성후에 투명성이 보장되는 유약을 코팅하여 2차 소성(열처리)을 하는 것이다.In the case of manufacturing a tile in which a picture such as a wall painting is formed on the surface of the tile as described above, a sidewall is formed on the surface of the plate-like tile on which the first sintering has been completed as described above, After the firing, a picture is drawn using a glaze mixed with pigments expressed in different colors, and then a second firing (heat treatment) is performed by coating a glaze which is ensured in transparency after firing.

이와 같은 기술과 관련된 종래의 벽화 타일의 제작방법에 있어서는 대한민국 등록특허 제 10-1074535호에 알려져 있다.A conventional method of producing a mural tile related to such a technique is known from Korean Patent Registration No. 10-1074535.

그 기술적인 구성은, 1차 소성이 완료된 타일기재의 상면에 소망하는 모양으로 제1도료로 밑그림을 형성시키고, 상기 밑그림을 경계로 밑그림보다 높게 표현하고자 하는 색상을 갖는 제2도료로 상기 밑그림보다 제2도료가 높도록 채색하며, 상기 제2도료의 상면에 오일을 도포하고 도포된 오일 상면에 세라믹분말을 도포한 후, 상기 타일기재를 900~1250℃에서 15~30분간 소성하는 것이다.The technical construction is such that a sketch is formed on the upper surface of the tile substrate having been subjected to the first firing with a first paint in a desired shape and a second paint having a hue that is higher than the sketch Coating the upper surface of the second paint with oil, applying the ceramic powder to the upper surface of the coated oil, and then firing the tile substrate at 900 to 1250 ° C for 15 to 30 minutes.

상기와 같이 타일기재의 표면에 벽화등의 그림이 형성된 타일은 별도의 2차 소성(열처리)에 의해 제작이 극히 어렵게 됨은 물론, 상기와 같이 2차소성(열처리)후에는 벽화용 타일의 표면에서 표현하고자 하는 벽화 등의 그림이 가열(열처리)에 의해 명료하게 표현이 않되는 경우가 빈번하게 발생되는 문제점이 있는 것이다.As described above, a tile having a figure such as a wall or the like formed on the surface of the tile substrate is extremely difficult to manufacture by a second secondary firing (heat treatment), and after the second firing (heat treatment) There is a problem that a picture such as a murals to be expressed frequently is not clearly expressed by heating (heat treatment).

한편, UV프린터기를 이용하여 일반타일의 표면에 직접 이미지를 프린트하여, 타일에 이미지를 표현 후 완성한 벽화용 타일을 설치면(벽면, 바닥면 등)에 퍼즐처럼 하나씩 조합하여 부착 시공함으로써, 색체와 색감이 훨씬 뛰어난 벽화를 생성할 수 있는 직접 프린팅 방식의 벽화용 타일 및 그 제조방법이 대한민국 등록 특허 제 10-0622413호에 알려져 있다.On the other hand, an image is directly printed on the surface of a general tile using a UV printer, and the finished tile is displayed on the tile, and the completed tile is mounted on the installation surface (wall surface, floor surface, A tile for wall painting of a direct printing type which can produce a wall color much superior in color and a method for manufacturing the same are known from Korean Patent No. 10-0622413.

이는, 벽화용 이미지 원본을 벽화크기만큼 확대 한 후, 타일의 단위크기 만큼씩 분할하여 출력데이터 편집을 완료하고, 타일의 표면에 에폭시수지 도료를 스프레이 도포한 후에 고온, 건조시키는 전처리 과정과, 상기 에폭시수지 도포층 표면에 UV프린터기로 직접 이미지를 프린팅하며, 프린팅 한 이미지층에 우레탄수지 도료를 코팅하여 고온, 건조시키는 것이다.This preprocessing process is a process of enlarging the original image for freshening by the size of the freshening, dividing the freshener image by the unit size of the tile, completing the output data editing, spraying the epoxy resin paint on the surface of the tile, The image is printed directly on the surface of the epoxy resin coating layer with a UV printer, the urethane resin coating is coated on the printed image layer, and the resultant is heated and dried.

그러나, 소성된 타일의 표면에 단순히 UV프린터기를 통하여 인쇄되는 이미지층은 외부의 환경에 의해 쉽게 벗겨지게 됨은 물론, 상기 타일에 외력이 가해지게 되면 타일이 쉽게 파손되는 커다란 문제점이 있는 것이다.However, the image layer printed on the surface of the fired tile simply through the UV printer is easily peeled off by the external environment, and the tile is easily broken when an external force is applied to the tile.

1. 대한민국 등록 특허공보 제 10-1074535호(2011년 10월 11일 등록)1. Korean Registered Patent No. 10-1074535 (registered on October 11, 2011) 2. 대한민국 등록 특허공보 제 10-0622413호(2006년 09월 04일 등록)2. Korean Patent Registration No. 10-0622413 (registered on September 04, 2006)

본 발명의 기술적 과제는 상기와 같은 종래의 문제점들을 개선하기 위한 것으로, 그 목적은 타일 본체의 표면에 일정 두께의 접착 도포층을 개재하여 면사에 폴리에스터 합성 섬유사가 일정한 비율로 혼합 직조된 섬유층을 착설하여, 상기 섬유층의 부착에 의해 타일 본체의 인장 강도가 가일층 향상되고, 상기 타일 본체의 내구성을 가일층 증대시킬 수 있음은 물론, 상기 타일 본체의 표면에 프린팅 방식의 정형화된 그림이 아닌 캔버스(canvas) 타입의 그림을 수작업에 의해 자유롭게 형성하고, 이에 띠라서 미려한 캔버스 형태의 벽화용 그림을 감상할 수 있으며, 상기 타일 본체의 표면에 도포되는 투명한 변성 아크릴폴리머에 가교제 및 경화제가 일정비율 혼합되어, 접착 내구성이 우수하면서, 섬유층의 구김이 없고, 면사의 올이 풀리지 않도록 하며, 상기 그림층 표면에 일정 두께의 투명 코팅층을 적어도 2회 이상 도포하여, 상기 그림층이 긁힘, 자외선에 의한 변색 및 탈색, 지워짐과 볏겨지는 현상을 방지하면서, 그림층의 보존 수명이 영구적이며, 그림층의 색상과 선명도가 우수하게 될 수 있는 벽화용 그림 타일 제작방법을 제공 하는데 있다.SUMMARY OF THE INVENTION The present invention has been made in order to solve the above problems, and it is an object of the present invention to provide a method for producing a polyester fiber composite yarn, The tensile strength of the tile body can be further improved by the attachment of the fibrous layer and the durability of the tile body can be increased even more. In addition, the surface of the tile body can be coated with a canvas ) Type can be freely formed by hand, so that a beautiful canvas-like murals can be appreciated. A crosslinking agent and a curing agent are mixed with a transparent modifying acrylic polymer applied on the surface of the tile body at a certain ratio, The durability of adhesion is excellent, the fiber layer is not wrinkled, the yarn is not loosened, The shelf life of the picture layer is permanent, while the transparent layer of a certain thickness is applied on the surface of the picture layer at least twice to prevent the picture layer from being discolored or discolored due to scratching, ultraviolet rays, The present invention also provides a method of manufacturing a painting tile for a mural that can have excellent color and sharpness of a layer.

또한, 본 발명은 상기 타일 본체에 착설되는 섬유층에 의해 컬러 물감의 흡수가 용이하게 이루어져 캔버스에 직접 그려지는 그림과 같은 선명한 상태의 그림층을 얻을 수 있으며, 소성 가공하여 제작되는 타일 본체에 벽화용 그림층의 제작 후 별도의 열처리 공정이 전혀 필요 없이도 상기 벽화용 타일을 손쉽고, 용이하게 제작할 수 있는 벽화용 그림 타일 제작방법을 제공 하는데 있다.In addition, the present invention can easily absorb the color paints by the fibrous layer laid on the tile body to obtain a picture layer in a clear state such as a picture drawn directly on the canvas, It is an object of the present invention to provide a method for manufacturing a painting tile for a wall painting, which can easily and easily produce the wall tile without any additional heat treatment step after the production of the picture layer.

상기 목적을 달성하기 위한 기술적인 구성으로서 본 발명은, 벽화가 소성 가공된 판상(板狀)의 다수의 타일로 나누어져 형성되는 그림층을 형성하고, 상기 그림층의 표면에는 투명 코팅층을 적층 형성하여 제작되는 벽화용 그림 타일의 제작방법에 있어서,In order to achieve the above object, the present invention provides a method of forming a picture layer formed by dividing a plate into a plurality of plate-shaped tiles in which murals are processed, and forming a transparent coating layer on the picture layer A method of manufacturing a painting tile for a wall painting,

벽면에 착설되는 타일 본체의 표면에 접착제를 스프레이에 의해 건조후 20 ~ 25μm의 도막 두께가 형성되도록 접착 도포층을 형성하는 단계;Forming an adhesive coating layer on the surface of the tile body to form a coating film thickness of 20 to 25 占 퐉 after drying the adhesive agent on the surface of the tile body by spraying;

면(cotton)사에 폴리에스터 합성 섬유사가 6~8 : 4~2의 비율로 혼합되어 직조되는 섬유층을 상기 타일 본체의 크기로 컷팅하여 착설하는 단계;Cutting a fiber layer of polyester synthetic fiber yarns mixed at a ratio of 6: 8: 4 to 2 into a size of the tile body;

상기 접착제를 개재하여 타일 본체에 착설되는 섬유층을 초기 접착력 증대를 위하여 110~150℃의 온도로 10분간 열풍 가열하는 단계;Heating the fiber layer laid on the tile body through the adhesive agent for 10 minutes at a temperature of 110 to 150 DEG C for the purpose of increasing initial adhesion;

상기 타일 본체의 표면에 착설되는 섬유층에는 습기, 온도변화에 따른 채색용 물감의 벗겨짐, 변색 방지 및 방수 기능을 위하여 밑그림용 물감 분말 7.5 중량% 알콜 15.7중량%, 투명 실리콘 70.5중량%, 경화제 6.3 중량%가 충분히 혼합되어 5℃~25℃의 온도를 유지하면서 도포되어 밑그림층을 형성하는 단계;The fibrous layer laid on the surface of the tile body is provided with moisture, peeling of the coloring paint due to temperature change, 15.7 wt.% Of alcohol, 7.5 wt.% Of transparent silicone, and 6.3 wt.% Of curing agent are thoroughly mixed and coated at a temperature of 5 ° C to 25 ° C to form a sketch layer for waterproof function.

상기 섬유층에 형성되는 밑그림층에 형광안료(螢光顔料)로 이루어진 컬러물감 70~75중량%, 우레탄 20~25중량% 및 빠른 경화를 위한 경화제 5중량%가 혼합되어 수공에 의해 상기 밑그림층에 직접 그려지는 그림층 제작단계;70 to 75% by weight of a color pigment consisting of a fluorescent pigment (fluorescent pigment), 20 to 25% by weight of urethane and 5% by weight of a curing agent for fast curing are mixed in a sketch layer formed on the fibrous layer, Directly drawn picture layering phase;

상기 그림층의 표면에 방수를 위한 투명 실리콘 75.5중량%, 알콜 15.7중량%, 경화제 8.8 중량%가 혼합되어 상기 그림층 표면에 1회 도포시 50-60㎛의 두께가 되도록 하여 적어도 2회 이상 도포하여 100-120㎛ 두께를 갖도록 하여 투명 코팅층 형성단계;를 포함하여 제작되는 것을 특징으로 하는 벽화용 그림 타일의 제작방법을 마련함에 의한다.75.5% by weight of transparent silicone for waterproofing, 15.7% by weight of alcohol and 8.8% by weight of a curing agent are mixed on the surface of the picture layer to coat the surface of the picture layer with a coating thickness of 50-60 占 퐉 at least twice And forming a transparent coating layer having a thickness of 100-120 [micro] m to provide a painting tile for a wall painting.

또한, 본 발명은 상기 타일 본체의 표면에 도포되는 접착 도포층은 투명한 변성 아크릴폴리머 55~65중량%, 증류수 30~40중량%, 폴리이소시아네이트로 이루어진 가교제(架橋劑) 4.15중량%에 방향족 폴리아민계의 경화제 0.5중량%, 부착력을 높이는 역할을 하는 가소제(可塑劑) 0.35중량% 혼합되는 것을 특징으로 한다.The adhesive coating layer applied on the surface of the tile body is composed of 55 to 65% by weight of a transparent modified acrylic polymer, 30 to 40% by weight of distilled water, 4.15% by weight of a crosslinking agent composed of polyisocyanate, 0.5% by weight of a curing agent, and 0.35% by weight of a plasticizer acting as an adhesive force.

또한, 본 발명은 상기 그림층의 표면에 도포되는 투명 코팅층은, 방수를 위한 투명 실리콘 75.5중량%, 알콜 15.7중량%, 경화제 8.8 중량%가 혼합되어 도포되는 것을 특징으로 한다.In the present invention, the transparent coating layer applied to the surface of the picture layer is coated with 75.5% by weight of transparent silicone for waterproofing, 15.7% by weight of alcohol and 8.8% by weight of a curing agent.

본 발명인 벽화용 그림 타일의 제작방법의 실시 형태에 따르면, 타일 본체의 표면에 일정 두께의 접착 도포층을 개재하여 면사에 폴리에스터 합성 섬유사가 일정한 비율로 혼합 직조된 섬유층을 착설하여, 상기 섬유층의 부착에 의해 타일 본체의 인장 강도가 가일층 향상되고, 상기 타일 본체의 내구성을 가일층 증대시킬 수 있음은 물론, 상기 타일 본체의 표면에 프린팅 방식의 정형화된 그림이 아닌 캔버스(canvas) 타입의 그림을 수작업에 의해 자유롭게 형성하고, 이에 띠라서 미려한 캔버스 형태의 벽화용 그림을 감상할 수 있으며, 상기 타일 본체의 표면에 도포되는 투명한 변성 아크릴폴리머에 가교제 및 경화제가 일정비율 혼합되어, 접착 내구성이 우수하면서, 섬유층의 구김이 없고, 면사의 올이 풀리지 않도록 하며, 상기 그림층 표면에 일정 두께의 투명 코팅층을 적어도 2회 이상 도포하여, 상기 그림층이 긁힘, 자외선에 의한 변색 및 탈색, 지워짐과 볏겨지는 현상을 방지하면서, 그림층의 보존 수명이 영구적이며, 그림층의 색상과 선명도가 우수하게 되는 효과가 있다.According to the embodiment of the method for producing a painting tile for painting of the present invention, a fiber layer in which a polyester synthetic fiber yarn is mixed and woven at a predetermined ratio is formed on the surface of a tile body through an adhesive coating layer of a certain thickness, It is possible to improve the tensile strength of the tile body to a considerable extent, to increase the durability of the tile body, and to provide a canvas-type image on the surface of the tile body, And a transparent canvas-shaped wall painting can be appreciated. The transparent and modified acrylic polymer applied on the surface of the tile body is mixed with a crosslinking agent and a curing agent in a certain ratio, The fiber layer is not wrinkled and the cotton yarn is not loosened, The transparent layer of the paint layer is applied at least twice to prevent the paint layer from being discolored or discolored due to scratches, ultraviolet rays, and being crushed and crumbled, and the preservation life of the paint layer is permanent and the color and clarity of the picture layer is excellent There is an effect to be done.

또한, 본 발명은 상기 타일 본체에 착설되는 섬유층에 의해 컬러 물감의 흡수가 용이하게 이루어져 캔버스에 직접 그려지는 그림과 같은 선명한 상태의 그림층을 얻을 수 있으며, 소성 가공하여 제작되는 타일 본체에 벽화용 그림층의 제작 후 별도의 열처리 공정이 전혀 필요 없이도 상기 벽화용 타일을 손쉽고, 용이하게 제작할 수 있는 효과가 있다.In addition, the present invention can easily absorb the color paints by the fibrous layer laid on the tile body to obtain a picture layer in a clear state such as a picture drawn directly on the canvas, It is possible to easily and easily manufacture the wall tile without any additional heat treatment step after the production of the picture layer.

도 1은 본 발명의 의한 벽화용 그림 타일 제작방법을 설명하기 위한 플로우챠트.
도 2는 본 발명에 의해 제작되는 벽화용 그림 타일의 정단면 구조도.
도 3은 본 발명에 의해 제작된 벽화용 그림 타일의 설치상태 사진.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a flow chart for explaining a method of manufacturing a painting tile for a wall painting according to the present invention; FIG.
Fig. 2 is a front cross-sectional view of a painting tile for wall painting produced by the present invention; Fig.
FIG. 3 is a photograph of the installation state of a painting tile for a wall made by the present invention. FIG.

이하, 본 발명의 장점 및 특징, 그리고 그것들을 달성하는 기술적 구성은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. 그러나 본 발명은, 이하에서 개시되는 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것으로, 본 발명은 청구항의 범주에 의해 정의될 뿐이다. 또한, 본 발명을 설명함에 있어 관련된 공지 기술 등이 본 발명의 요지를 흐리게 할 수 있다고 판단되는 경우 그에 관한 자세한 설명은 생략하기로 한다.BRIEF DESCRIPTION OF THE DRAWINGS The above and other features and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings. The present invention may, however, be embodied in many different forms and should not be construed as being limited to the exemplary embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete and will fully convey the concept of the invention to those skilled in the art. And the present invention is only defined by the scope of the claims. In the following description, well-known functions or constructions are not described in detail since they would obscure the invention in unnecessary detail.

도 1은 본 발명의 의한 벽화용 그림 타일 제작방법을 설명하기 위한 플로우챠트이고, 도 2는 본 발명에 의해 제작되는 벽화용 그림 타일의 정단면 구조도이며, 도 3은 본 발명에 의해 제작된 벽화용 그림 타일의 설치상태 사진이다.FIG. 1 is a flow chart for explaining a method of manufacturing a painting tile for a wall painting according to the present invention, FIG. 2 is a front sectional view of a painting tile for wall painting produced by the present invention, This is a photograph of the installation state of the drawing tile.

즉, 본 발명은 벽면에 소성 가공된 판상(板狀)의 다수의 타일 본체로 나누어져 형성되는 그림층을 형성한 후, 상기 그림층의 표면에는 투명 코팅층을 적층 형성하여 벽화용 그림 타일을 제작한다.That is, according to the present invention, a picture layer formed by dividing a plurality of plate-shaped tile bodies subjected to plastic working on a wall surface is formed, and then a transparent coating layer is formed on the surface of the picture layer, do.

이때, 상기 벽면에 착설되는 타일 본체(110)의 표면에는 접착제를 스프레이에 의해 건조후의 20 ~ 25μm의 도막 두께가 형성되도록 접착 도포층(120)을 형성한 후, 상기 접착 도포층(120)에는 섬유층(130)을 착설한다.At this time, an adhesive coating layer 120 is formed on the surface of the tile body 110 to form a coating film thickness of 20 to 25 μm after drying by spraying on the surface of the tile body 110, The fibrous layer 130 is formed.

상기 타일 본체(110)의 표면에 착설되는 섬유층(130)은, 면(cotton)사에 내마모성 및 내구성의 향상을 위하여 폴리에스터 합성 섬유사를 혼합하여 직조하게 되며, 이때 상기 면사 : 폴리에스터 합성 섬유사는 6~8 : 4~2의 비율로 혼합되어 직조되어 상기 타일 본체(110)의 크기로 컷팅하여 착설된다.The fiber layer 130 to be laid on the surface of the tile body 110 is made by mixing polyester synthetic fiber yarns to improve the abrasion resistance and durability of the cotton yarn, Are mixed and knitted at a ratio of 6: 8: 4 to 2, and cut into a size of the tile body (110).

상기 면사의 혼합 비율이 6 이하일 경우에는 상대적으로 폴리에스터 합성 섬유사의 혼합비율이 4 이상으로 되어, 후술하는 밑그림층과 그림층의 형성시 섬유층(130)에 컬러 물감등의 흡수가 제대로 이루어지지 않음은 물론, 이에 따라서 상기 밑그림층과 그림층이 쉽게 박리(剝離)되는 현상이 발생하게 되고, 상기 면사의 혼합 비율이 8 이상일 경우에는, 폴리에스터 합성 섬유사의 혼합비율이 2 이하로 직조되어, 컬러 물감등의 흡수가 우수한 반면에 상기 타일 본체(110)의 표면에 착설되는 섬유층(130)의 내마모성 및 내구성이 극히 취약하게 되며, 따라서 면사의 올이 쉽게 풀리게 되거나 끊어지게 되고, 상기와 같이 타일 본체(110)의 표면에 착설되는 섬유층(130)에 손상이 발생하게 되는 것으로, 본 발명에서와 같이 면사 : 폴리에스터 합성 섬유사는 6~8 : 4~2의 비율로 혼합되어 직조됨이 가장 바람직하다.When the blend ratio of the cotton yarn is 6 or less, the blending ratio of the polyester synthetic fiber yarn is relatively higher than 4, and the color layer is not absorbed to the fiber layer 130 when the sagging layer and the drawing layer are formed When the blend ratio of the cotton yarn is 8 or more, the blending ratio of the polyester synthetic fiber yarn is weighed to 2 or less so that the color The durability and abrasion resistance of the fiber layer 130 to be laid on the surface of the tile body 110 is extremely weak, so that the cotton yarn is easily loosened or broken, The fiber yarn 130 is damaged at the surface of the polyester yarn 110. As in the present invention, the cotton yarn: polyester synthetic fiber yarn is 6 to 8: 4 to 2 Are mixed in a ratio being most preferred it is woven.

한편, 상기 타일 본체(110)의 표면에 섬유층(130)의 부착시 사전에 접착제에 의해 접착 도포층(120)을 형성하게 되며, 이때 상기 타일 본체(110)의 표면에 도포되는 접착제는 섬유층(130)과의 우수한 접착은 물론, 상기 섬유층(130)이 타일 본체로부터 쉽게 벗겨지지 않도록 하기 위하여, 내구성이 우수하면서, 섬유층의 구김이 잘 없고, 면사의 올이 잘 풀리지 않도록 투명한 변성 아크릴폴리머 55~65중량%, 증류수 30~40중량%, 폴리이소시아네이트로 이루어진 가교제(架橋劑) 4.15중량%에 내열성, 내약품성이 우수한 방향족폴리아민계의 경화제 0.5중량% 및 부착력을 높이는 역할을 하는 가소제(可塑劑) 0.35중량% 가 혼합되어, 건조후의 20 ~ 25μm의 도막 두께가 형성되도록 접착 도포층(120)을 형성한다.The adhesive layer 120 is formed on the surface of the tile body 110 by an adhesive before the adhesive layer 130 is attached to the surface of the tile body 110. The adhesive applied to the surface of the tile body 110 may be a fiber layer 130, and to prevent the fiber layer 130 from being easily peeled off from the tile body, the fiber layer 130 is excellent in durability and is not easily wrinkled in the fiber layer, and the transparent modified acrylic polymer 55 - 0.5% by weight of an aromatic polyamine curing agent having excellent heat resistance and chemical resistance, and a plasticizer having a role of enhancing the adhesion strength, in an amount of 65% by weight, distilled water 30% by weight to 40% by weight and a polyisocyanate crosslinking agent 4.15% 0.35% by weight are mixed to form an adhesive application layer 120 so that a film thickness of 20 to 25 μm after drying is formed.

상기 접착 도포층(120)을 형성하는 접착제는 섬유층과 소성 가공된 타일 본체와의 우수한 접착력 유지를 위하여 , 투명한 변성 아크릴폴리머 55중량% 이하일 경우, 섬유층 섬유와의 접착 탄성력이 저하되어 섬유층의 구김 및 균열이 발생하고, 이에 따라서 외부의 온도변화 등에 의해 섬유층의 접착력을 유지하기 어렵게 됨은 물론, 상기 투명한 변성 아크릴폴리머 65중량% 이상일 경우에는, 이와 함께 혼합되는 증류수가 30중량% 이하로 혼합되어 접착제의 점성을 제대로 유지할 수 없게 되며, 따라서 접착력이 저하되는 것으로, 상기 접착 도포층(120)을 형성하는 접착제에는 투명한 변성 아크릴폴리머 55~65중량%에 대하여 증류수 30~40중량%를 혼합함이 바람직하다.In order to maintain an excellent adhesive strength between the fiber layer and the plastic tile body, the adhesive forming the adhesive coating layer 120 has an adhesive strength lower than 55% by weight of the transparent modified acrylic polymer, It is difficult to maintain the adhesive force of the fibrous layer due to external temperature change or the like. In addition, when the transparent modified acrylic polymer is at least 65 wt%, the distilled water mixed with the transparent modified acrylic polymer is mixed with not more than 30 wt% It is impossible to properly maintain the viscosity and therefore the adhesive strength is lowered. It is preferable to mix 30 to 40% by weight of distilled water with respect to 55 to 65% by weight of the transparent modified acrylic polymer as the adhesive forming the adhesive coating layer 120 .

또한, 상기와 같이 섬유층이 접착되어 적층 되도록 하는 접착 도포층(120)은 건조후의 도막 두께가 20μm 이하일 경우, 접착 도포층의 두께가 너무 얇게 되어 섬유층(130)이 타일 본체(110)로부터 쉽게 벗겨지게 되며, 상기 접착 도포층(120)의 건조후의 도막 두께가 25μm 이상일 경우에는 일정 두께이상으로 두껍게 도포가 되어 타일과 접착 도포츠의 불완전 양생이 되어, 상기 타일 본체가 접착 도포층으로부터 쉽게 탈락 될 수 있는 것으로, 상기 접착 도포층(120)은 본 발명에서와 같이 건조후의 20 ~ 25μm의 도막 두께가 형성 되도록 하는 것이 바람직하다. When the thickness of the adhesive layer 120 after the drying is 20 μm or less, the thickness of the adhesive layer is too thin, so that the fiber layer 130 easily peels off from the tile body 110 When the thickness of the adhesive coating layer 120 after the drying of the adhesive coating layer 120 is 25 μm or more, the thickness of the adhesive coating layer 120 is increased to a certain thickness or more to incompletely cure the tile and the adhesive coating, Preferably, the adhesive coating layer 120 is formed to have a film thickness of 20 to 25 mu m after drying as in the present invention.

그리고, 상기 접착 도포층(120)에 착설되는 섬유층(130)은, 110~150℃의 온도로 10분간 열풍 가열하여 상기 섬유층(130)의 접착력이 우수하게 됨은 물론, 섬유층의 초기 접착력을 증대시킬 수 있도록 한다.The fiber layer 130 to be adhered to the adhesive application layer 120 is heated at a temperature of 110 to 150 ° C. for 10 minutes to improve the adhesion of the fiber layer 130 and to increase the initial adhesive strength of the fiber layer .

상기와 같이, 타일 본체(110)의 표면에 일정 두께의 접착 도포층(120)을 개재하여 면사에 폴리에스터 합성 섬유사가 혼합 직조된 섬유층(130)을 착설하여, 상기 섬유층의 부착에 의해 타일 본체의 인장강도가 가일층 향상되고, 타일 본체의 내구성을 증대시킬 수 있음은 물론, 상기 타일 본체의 표면에 프린팅 방식의 정형화된 그림이 아닌 캔버스(canvas) 타입의 그림을 수작업에 의해 자유롭게 형성하고, 이에 띠라서 미려한 캔버스 형태의 벽화용 그림을 감상할 수 있는 것이다. As described above, a fiber layer 130 in which a polyester synthetic fiber yarn is mixed and woven on a cotton yarn is provided on the surface of the tile body 110 with the adhesive coating layer 120 having a certain thickness interposed therebetween, And the canvas type image is formed on the surface of the tile body by manual operation instead of the standardized printing type image, and the tensile strength of the tile body can be increased. You can enjoy beautiful canvas paintings for murals.

계속해서, 상기 타일 본체(110)의 표면에 착설되는 섬유층(130)에는 밑그림용 물감 분말 7.5 중량%, 알콜 15.7중량%, 투명 실리콘 70.5중량%, 경화제 6.3 중량%가 충분히 혼합되는 밑그림층(140)을 형성하여, 외부의 습기, 겨울 및 여름등의 온도변화에 따른 채색용 물감의 벗겨짐, 변색을 방지하면서 방수 기능을 향상시킬 수 있다.Subsequently, the fiber layer 130 provided on the surface of the tile body 110 is provided with a sketch layer 140 (see FIG. 1) in which 7.5 wt% of powder for sketching, 15.7 wt% of alcohol, 70.5 wt% of transparent silicone, ) Can be formed to improve the waterproof function while preventing peeling and discoloration of the paint for coloring due to changes in temperature such as outside moisture, winter and summer.

바로 이때, 상기 밑그림층(140)을 형성시 투명 실리콘이 70.5중량% 이상일 경우에는, 상기 실리콘이 섬유층의 섬유를 너무 두껍게 코팅하여 컬러물감을 통한 그림층의 제작시 채색 작업이 제대로 이루어지지 않게 되며, 상기 실리콘에 혼합되는 알콜이 15.7중량% 이하 및 밑그림용 물감 분말 7.5 중량% 이하로 형성되어, 밑그림층(140)을 제대로 형성할 수 없으며, 상기 투명 실리콘이 70.5중량% 이하일 경우 섬유층의 섬유층에 얇게 코팅되어 겨울 및 여름철의 온도 변화에 의해 채색용 물감의 벗겨짐, 변색이 발생하게 되고, 상기 섬유를 제대로 보호할 수 없으며, 상기 섬유층의 방수성이 저하되는 것이다.At this time, if the transparent silicone is 70.5% by weight or more when the sagging layer 140 is formed, the silicone is too thick to coat the fibers of the fiber layer, so that the coloring operation is not properly performed when the color layer is formed 15.7% by weight of the alcohol mixed in the silicone and 7.5% by weight or less of the color powder for the sketch, so that the sketch layer 140 can not be formed properly. When the transparent silicone is 70.5% by weight or less, It is thinly coated and peeling and discoloration of the paint for coloring occurs due to a change in temperature during winter and summer, the fiber can not be protected properly, and the water resistance of the fiber layer is lowered.

상기와 같이 타일 본체(110)의 표면에 착설되는 섬유층(130)에 밑그림층(140)을 형성시 겨울 및 여름의 평균 온도에 알맞게 5℃~25℃의 온도를 유지하면서 섬유층(130)의 표면에 도포하여 외부의 온도 변화에 의해 변형 및 벗겨짐이 방지되는 최적화된 밑그림층(140)을 형성하게 된다.When the sketch layer 140 is formed on the fiber layer 130 formed on the surface of the tile body 110 as described above, the surface temperature of the fiber layer 130 is maintained at a temperature of 5 ° C to 25 ° C, Thereby forming an optimized sagging layer 140 which is prevented from being deformed and peeled off due to external temperature changes.

계속해서, 상기 섬유층(130)에 형성되는 밑그림층(140)에는 형광안료(螢光顔料)로 이루어진 컬러물감 70~75중량%, 우레탄 20~25중량% 및 빠른 경화를 위한 경화제 5중량%가 혼합되어 수공에 의해 상기 밑그림층(140)에 직접 그려지는 그림층(150)을 제작하게 되며, 상기 그림층(150)의 형성시 형광안료(물감)에 의해 어두운 한밤중에 빛의 조사시 발광되어 채색된 그림층(150)을 육안으로 감상할 수 있도록 하며, 상기 그림층을 형성하는 컬러물감이 75 중량% 이상일 경우, 이에 혼합되는 우레탄은 20 중량% 이하로 형성되어 상기 컬러물감의 부착성, 내마모성이 극히 취약하게 되고, 상기 컬러물감이 70중량% 이하일 경우에는 상대적으로 우레탄은 25 중량% 이상으로 형성되어, 적은양의 컬러물감 혼합에 의해 선명한 그림층의 형성이 어렵게 되며, 우레탄 자체의 특성상 시간이 오래 경과하여 경화가 이루어져 이에 혼합된 컬러물감의 건조시간이 길어지게 되어 작업성이 저하되는 것으로, 본 발명은 컬러물감 70~75중량%, 우레탄 20~25중량%에 빠른 경화를 위한 경화제 5중량%가 혼합됨이 바람직한 것이다.Subsequently, 70 to 75% by weight of a color pigment made of a fluorescent pigment (fluorescent pigment), 20 to 25% by weight of urethane and 5% by weight of a curing agent for quick curing are added to the sketch layer 140 formed on the fiber layer 130 A picture layer 150 which is directly drawn on the sketch layer 140 is formed by hand-painting. When the picture layer 150 is formed, a fluorescent pigment (light) The coloring layer 150 can be visually appreciated. When the coloring layer forming the coloring layer is not less than 75% by weight, the amount of the urethane mixed therewith is less than 20% by weight, The abrasion resistance becomes extremely weak. When the color paint is less than 70% by weight, the urethane is relatively more than 25% by weight, and it is difficult to form a clear picture layer by mixing a small amount of color paints.The present invention relates to a curing agent for fast curing, which comprises 70 to 75% by weight of color paints and 20 to 25% by weight of urethane, By weight is preferably mixed.

한편, 상기와 같이 섬유층(130)에 그림을 수작업에 의해 자유롭게 형성한 그림층(150)의 표면에는, 투명 실리콘 75.5중량%, 알콜 15.7중량%, 경화제 8.8 중량%가 혼합되어 일정두께 도포된 투명 코팅층(160)을 형성하게 되며, 이때 상기 투명 실리콘이 75.5중량% 이하일 경우에는, 상기 그림층(150) 표면에 투명 실리콘이 얇게 코팅되어 외부의 극심한 온도 변화에 따른 그림층의 균열 및 벗겨짐, 변색이 빈번히 발생하게 되고, 상기 그림층의 방수성이 저하되며, 상기 투명 실리콘이 75.5중량% 이상일 경우 상기 투명 실리콘의 경화시 외부의 충격등에 의해 상기 투명 코팅층(160)이 쉽게 깨지거나, 변색이 발생하게 되는 것으로, 본 발명에서와 같이 상기 투명 코팅층(160)은 투명 실리콘 75.5중량%에 알콜 15.7중량% 및 빠른 경화를 위하여 경화제 8.8 중량%가 혼합되어 도포됨이 바람직하다.On the other hand, on the surface of the picture layer 150 formed by hand painting the picture layer 130 as described above, 75.5% by weight of transparent silicone, 15.7% by weight of alcohol and 8.8% by weight of a curing agent are mixed, Coating layer 160 is formed on the surface of the picture layer 150. When the transparent silicon layer is not more than 75.5% by weight, transparent silicon is thinly coated on the surface of the picture layer 150 so that cracks and peeling, If the transparent silicone is 75.5% by weight or more, the transparent coating layer 160 is easily broken or discolored due to an external impact when the transparent silicone is cured. As in the present invention, the transparent coating layer 160 is formed by mixing 15.5 wt% of alcohol with 75.5 wt% of transparent silicone and 8.8 wt% of a curing agent for rapid curing It is preferred.

바로 이때, 상기와 같이 그림층(150)의 표면에 코팅되는 투명 코팅층(160)은, 상기 그림층 표면에 1회 도포시 약 50-60㎛의 두께가 되도록 하여 적어도 2회 이상 도포하여 100-120㎛ 두께를 갖도록 하여, 2회 이상의 도포작업에 의해 균일하면서 내마모성이 우수한 상태의 투명 코팅층(160)을 얻을 수 있으며, 상기 투명 코팅층(160)의 두께가 100㎛ 이하일 경우에는 그림층(150)이 긁힘, 자외선에 의한 변색 및 탈색, 지워짐과 볏겨지는 현상이 빈번하게 발생되고, 상기 투명 코팅층(160)의 두께가 120㎛ 이상일 경우에는 외부의 충격등에 의해 상기 투명 코팅층(160)이 쉽게 깨지거나, 상기 그림층의 색상과 선명도가 떨어지게 되는 것으로, 본 발명에서와 같이 상기 투명 코팅층(160)은 그림층 표면에 1회 도포시 약 50-60㎛의 두께가 되도록 하여 적어도 2회 이상 도포하여 100-120㎛ 두께를 갖도록 하여, 상기 그림층(150)의 보존 수명이 영구적이며, 그림층의 색상과 선명도가 우수하도록 하는 것이다.At this time, the transparent coating layer 160 coated on the surface of the picture layer 150 is applied at least twice to the surface of the picture layer so as to have a thickness of about 50-60 μm, A transparent coating layer 160 having a uniform thickness and excellent abrasion resistance can be obtained by two or more coating operations. When the thickness of the transparent coating layer 160 is 100 탆 or less, When the thickness of the transparent coating layer 160 is 120 μm or more, the transparent coating layer 160 easily breaks due to an external impact or the like, , The color and clarity of the picture layer are deteriorated. As in the present invention, the transparent coating layer 160 is applied at least two times to a thickness of about 50-60 [mu] m, The thickness of the picture layer 150 is made permanent and the color and sharpness of the picture layer are excellent.

본 발명을 첨부 도면과 전술된 바람직한 실시예를 참조하여 설명하였으나, 본 발명은 그에 한정되지 않으며, 후술되는 청구범위에 의해 한정된다. 따라서, 본 기술분야의 통상의 지식을 가진 자라면 후술되는 청구범위의 기술적 사상에서 벗어나지 않는 범위 내에서 본 발명을 다양하게 변형 및 수정할 수 있다.Although the present invention has been described with reference to the accompanying drawings and the preferred embodiments described above, the present invention is not limited thereto but is limited by the following claims. Accordingly, those skilled in the art will appreciate that various modifications and changes may be made thereto without departing from the spirit of the following claims.

110...타일 본체
120...접착 도포층
130...섬유층
140...밑그림층
150...그림층
160...투명 코팅층110 ... tile body
120 ... adhesive application layer
130 ... fibrous layer
140 ... Sketch layer
150 ... picture layer
160 ... transparent coating layer

Claims (3)

벽화가 소성 가공된 판상(板狀)의 다수의 타일로 나누어져 형성되는 그림층을 형성하고, 상기 그림층의 표면에는 투명 코팅층을 적층 형성하여 제작되는 벽화용 그림 타일의 제작방법에 있어서,
벽면에 착설되는 타일 본체(110)의 표면에 접착제를 스프레이에 의해 건조후의 20 ~ 25μm의 도막 두께가 형성되도록 접착 도포층(120)을 형성하는 단계;
면(cotton)사에 폴리에스터 합성 섬유사가 6~8 : 4~2의 비율로 혼합되어 직조되는 섬유층(130)을 상기 타일 본체의 크기로 컷팅하여 착설하는 단계;
상기 타일 본체(110)에 착설되는 섬유층(130)을 초기 접착력 증대를 위하여 110~150℃의 온도로 10분간 열풍 가열하는 단계;
상기 타일 본체(110)의 표면에 착설되는 섬유층(130)에는 습기, 온도변화에 따른 채색용 물감의 벗겨짐, 변색 방지 및 방수 기능을 위하여 밑그림용 물감 분말 7.5 중량%, 알콜 15.7중량%, 투명 실리콘 70.5중량%, 경화제 6.3중량%가 혼합되어 5℃~25℃의 온도를 유지하면서 도포되어 밑그림층(140)을 형성하는 단계;
상기 섬유층(130)에 형성되는 밑그림층(140)에 형광안료(螢光顔料)로 이루어진 컬러물감 70~75중량%, 우레탄 20~25중량% 및 빠른 경화를 위한 경화제 5중량%가 혼합되어 수공에 의해 상기 밑그림층(140)에 직접 그려지는 그림층(150) 제작단계;
상기 그림층(150)의 표면에 방수를 위한 투명 실리콘 75.5중량%, 알콜 15.7중량%, 경화제 8.8 중량%가 혼합되어 상기 그림층(150) 표면에 1회 도포시 50-60㎛의 두께가 되도록 하여 적어도 2회 이상 도포하여 100-120㎛ 두께를 갖도록 하여 투명 코팅층(160)을 형성단계;를 포함하여 제작되는 것을 특징으로 하는 벽화용 그림 타일의 제작방법.
A method of manufacturing a painting tile for a wall painting which is formed by forming a picture layer formed by dividing a mural into a plurality of plate-shaped tiles and laminating a transparent coating layer on the surface of the picture layer,
Forming an adhesive coating layer (120) on the surface of the tile body (110) to form a coating film thickness of 20 to 25 占 퐉 after drying by spraying an adhesive;
Cutting a fiber layer (130) which is woven by mixing polyester synthetic fiber yarns at a ratio of 6 to 8: 4 to 2 to a size of the tile body;
Heating the fiber layer (130) installed on the tile body (110) at a temperature of 110 to 150 ° C for 10 minutes to increase initial adhesion;
The fibrous layer 130 provided on the surface of the tile body 110 is provided with moisture, peeling of the coloring paint due to temperature change, And 7.5% by weight of coloring powder for drawing, 15.7% by weight of alcohol, 70.5% by weight of transparent silicone and 6.3% by weight of a curing agent are mixed to form a sketch layer 140 while maintaining the temperature at 5 ° C to 25 ° C ;
70 to 75% by weight of a color pigment made of a fluorescent pigment (fluorescent pigment), 20 to 25% by weight of urethane and 5% by weight of a curing agent for quick curing are mixed in a sketch layer 140 formed on the fiber layer 130, Forming a picture layer (150) directly on the sketch layer (140);
75.5% by weight of transparent silicone for waterproofing, 15.7% by weight of alcohol and 8.8% by weight of curing agent are mixed on the surface of the picture layer 150 so that the thickness of the picture layer 150 is 50-60 μm when applied on the surface of the picture layer 150 Forming a transparent coating layer (160) by applying at least two times or more and having a thickness of 100-120 mu m.
제 1항에 있어서,
상기 타일 본체(110)의 표면에 도포되는 접착 도포층(120)은 투명한 변성 아크릴폴리머 55~65중량%, 증류수 30~40중량%, 폴리이소시아네이트로 이루어진 가교제(架橋劑) 4.15중량%에 방향족폴리아민계의 경화제 0.5중량%, 부착력을 높이는 역할을 하는 가소제(可塑劑) 0.35중량% 혼합되는 것을 특징으로 하는 벽화용 그림 타일의 제작방법.
The method according to claim 1,
The adhesive coating layer 120 applied to the surface of the tile body 110 is composed of 55 to 65 wt% of a transparent modified acrylic polymer, 30 to 40 wt% of distilled water, 4.15 wt% of a crosslinking agent composed of polyisocyanate, 0.5 wt% of a curing agent of the system, and 0.35 wt% of a plasticizer acting as an adhesive force.
제 1항에 있어서,
상기 그림층(150)의 표면에 도포되는 투명 코팅층(160)은, 방수를 위한 투명 실리콘 75.5중량%, 알콜 15.7중량%, 빠른 경화를 위한 경화제 8.8 중량%가 혼합되어 도포되는 것을 특징으로 하는 벽화용 그림 타일의 제작방법.The method according to claim 1,
Wherein the transparent coating layer 160 applied to the surface of the picture layer 150 is a mixture of 75.5% by weight of transparent silicone for waterproofing, 15.7% by weight of alcohol and 8.8% by weight of a curing agent for quick curing, How to make a painting tile for.
KR1020180090264A 2018-08-02 2018-08-02 A production method of wall painting tile KR101925987B1 (en)