KR101925130B1 - Cabin-filter for cars - Google Patents

Cabin-filter for cars Download PDF

Info

Publication number
KR101925130B1
KR101925130B1 KR1020170002060A KR20170002060A KR101925130B1 KR 101925130 B1 KR101925130 B1 KR 101925130B1 KR 1020170002060 A KR1020170002060 A KR 1020170002060A KR 20170002060 A KR20170002060 A KR 20170002060A KR 101925130 B1 KR101925130 B1 KR 101925130B1
Authority
KR
South Korea
Prior art keywords
mineral
layer
powder
inorganic
weight
Prior art date
Application number
KR1020170002060A
Other languages
Korean (ko)
Other versions
KR20180081206A (en
Inventor
천강미
Original Assignee
맑은에어텍주식회사
천강미
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 맑은에어텍주식회사, 천강미 filed Critical 맑은에어텍주식회사
Priority to KR1020170002060A priority Critical patent/KR101925130B1/en
Publication of KR20180081206A publication Critical patent/KR20180081206A/en
Application granted granted Critical
Publication of KR101925130B1 publication Critical patent/KR101925130B1/en

Abstract

본 발명은 자동차용 캐빈필터에 관한 것으로, 무기물을 포함한 혼합액에 함침시킨 부직포로 제조된 탈취층을 포함하여 구성되며, 상기 무기물을 포함한 혼합액은 물, 무기물 분말 및 바인더로 구성되거나, 또는 물, 활성탄 분말, 무기물 분말 및 바인더로 구성되거나, 또는 물, 활성탄을 포함한 무기물 분말 및 바인더로 구성되는 것을 특징으로 한다. 이와 같이 구성된 자동차용 캐빈필터는 포집과 탈취효능을 향상시키면서도 공기투과율이 양호한 효과가 있다. The present invention relates to a car cabin filter for automobiles, comprising a deodorizing layer made of a nonwoven fabric impregnated with a mixed solution containing an inorganic substance, wherein the mixed liquid containing the inorganic substance is composed of water, an inorganic powder and a binder, A powder, an inorganic powder and a binder, or an inorganic powder including water and activated carbon, and a binder. The automobile cabin filter thus configured has an effect of improving the efficiency of collection and deodorization while having a good air permeability.

Description

자동차용 캐빈필터{Cabin-filter for cars}[0001] Cabin-filter for cars [0002]

본 발명은 자동차용 캐빈필터에 관한 것으로, 더욱 상세하게는 다수겹의 웹(web)으로 된 부직포를 물, 무기물 및 바인더가 혼합된 혼합액에 함침시켜 제조한 탈취층을 포함하여 포집과 탈취효능을 향상시킨 자동차용 캐빈필터에 관한 것이다. The present invention relates to a cabin filter for automobiles, and more particularly, to a cabin filter for automobiles. More particularly, the present invention relates to a cabin filter for automobiles. More particularly, the present invention relates to a cabin filter for automobiles, To an improved cabin filter for an automobile.

일반적으로, 차량의 연료장치는 모든 운전조건하에서 엔진에 필요한 혼합기를 가장 연소하기 쉬운 상태로 공급하는 장치로서, 엔진의 성능, 특히 엔진의 출력이나 경제성을 크게 좌우하는 기능을 한다.BACKGROUND ART [0002] In general, a fueling device of a vehicle is a device that supplies a mixer necessary for an engine under all operating conditions in a state in which it is most easily combusted, and functions to greatly influence the performance of the engine, particularly, the output and economical efficiency of the engine.

이와 관련하여, 차량의 엔진의 출력과 성능의 연관성이 깊은 핵심적인 부분은 연료유입부에 이물질과 유해가스를 여과시켜주는 역할을 하는 필터이다.In this regard, a key part of the relation between the output of the engine and the performance of the vehicle is a filter that filters foreign matter and harmful gas to the fuel inlet.

또한, 자동차의 실내 공기 정화를 위하여 자동차 실내로 유입되는 공기를 여과하는 필터로서, 실내의 담배연기나 각종 VOC와 같은 유해가스 여과를 위해 일반적으로 캐빈필터가 사용된다.In addition, a cabin filter is generally used to filter air entering the automobile room for indoor air purification of automobiles, and to filter noxious gases such as tobacco smoke and various VOCs in the room.

종래에 사용되는 캐빈필터는 지지층의 역할을 하는 스펀본드 부직포의 일면에 여재로서 정전 부직포인 멜트블로운 부직포을 합지하여 사용한다. 또한 한국특허공개 제2008-0001676호에서는 스펀본드 부직포와 그 일면에 니들펀칭으로 결착된 폴리에스테르 단섬유층을 포함하여 압력손실을 낮추면서도 포집효율을 향상시키는 기술이 개시되었다.A conventionally used cabin filter is formed by laminating a meltblown nonwoven fabric, which is an electrostatic nonwoven fabric, on one surface of a spunbonded nonwoven fabric serving as a supporting layer. Korean Patent Laid-Open Publication No. 2008-0001676 discloses a technique for improving the collection efficiency while lowering the pressure loss, including a spunbond nonwoven fabric and a polyester short fiber layer bonded on one side thereof by needle punching.

그러나, 상술한 지지체상에 별도의 여재를 합지하는 자동차용 캐빈필터는 합지공정을 거쳐야 하므로 비용이 많이 발생할 뿐 아니라, 합지공정으로 인하여 차압 및 압력손실이 큰 문제가 있었다.However, since the automotive cabin filter having a separate filter material on the support body needs to be subjected to a laminating process, not only the cost is increased but also the differential pressure and pressure loss are large due to the laminating process.

또한, 공개특허공보 2007-0035344호에는 고융점사와 저융점사가 접합된 단섬유들로 이루어진 웹을 준비하고, 웹의 일면에 열을 가하여 저융점사를 용융시킴으로서, 탈취분말이 웹의 하면을 통하여 탈리되지 않도록 제조한 복합필터의 제조방법이 개시되어 있다. 그러나, 이와 같이 제조된 복합필터는 탈취분말이 고정되어 있지 않아 진동 등 외부환경에 따라 웹 내부에서 유동함으로서, 웹의 하면으로 응집되는 단점이 있고 탈취 분말에 흡착된 세균 등이 포화되면 다시 배출되어 실내 공기를 2차로 오염시키는 문제점을 갖고 있다.Japanese Unexamined Patent Application Publication No. 2007-0035344 discloses a method of preparing a web composed of short fibers having a high melting point and a low melting point bonded together and melting a low melting point web by applying heat to one surface of the web, A method of producing a composite filter manufactured so as not to be desorbed is disclosed. However, since the deodorant powder is not fixed, the composite filter thus produced flows in the web according to the external environment such as vibration, and has a disadvantage of aggregating on the lower surface of the web. When the bacteria adsorbed on the deodorizing powder are saturated, It has a problem of polluting the room air secondarily.

또한, 공개특허공보 2001-0109591호에는 활성탄소섬유와 핫멜트용 단섬유를 혼합한 웹을 제조하여 부직포 사이에 게재시킨 다음, 핫멜트용 단섬유를 융착시킨 복합 부직포의 제조방법이 개시되어 있다. 여기서, 탈취성분으로서 활성탄소섬유를 이용하므로 핫멜트용 단섬유와 혼합하여 웹 형성시 활성탄소섬유와 핫멜트용 단섬유가 서로 잘 분산되나, 캐빈필터와 같이 탈취분말을 이용하는 경우에는 웹 형성과정에서 탈취분말들이 핫멜트용 단섬유로부터 이탈되어 웹을 형성하기 어렵고, 부직포를 상하층 모두에 사용함으로서 캐빈필터에 적용시 압력손실이 높아지며, 유해가스 제거 속도가 저하되는 단점이 있다.Further, Japanese Patent Application Laid-Open No. 2001-0109591 discloses a method for producing a composite nonwoven fabric in which webs prepared by mixing activated carbon fibers and hot-melt staple fibers are placed between non-woven fabrics and then hot-melt staple fibers are fused. Since active carbon fiber is used as deodorant component, activated carbon fibers and hot-melt short fibers are dispersed well when they are mixed with hot-melt staple fibers. However, when deodorizing powders such as a cabin filter are used, It is difficult to form the web because the powders are separated from the hot-melt short fibers, and when the nonwoven fabric is used for both the upper and lower layers, the pressure loss is increased and the removal rate of harmful gas is lowered.

한국공개특허공보 제10-2007-0035344호Korean Patent Publication No. 10-2007-0035344 한국공개특허공보 제10-2001-0109591호Korean Patent Publication No. 10-2001-0109591

따라서, 본 발명의 목적은 다수겹의 웹(web)으로 된 부직포를 물, 무기물 및 바인더가 혼합된 혼합액에 함침시켜 제조한 탈취층을 포함시켜 포집과 탈취효능을 향상시킨 자동차용 캐빈필터를 제공하는 것이다. Accordingly, an object of the present invention is to provide a cabin filter for automobiles, which includes a deodorization layer prepared by impregnating a multi-layered web nonwoven fabric with a mixture of water, an inorganic substance and a binder, thereby improving the collection and deodorization efficiency .

상기 목적을 해결하기 위하여, In order to solve the above object,

본 발명에 따른 자동차용 캐빈필터는,In the cabin filter for automobile according to the present invention,

무기물을 포함한 혼합액에 함침시킨 부직포로 제조된 탈취층을 포함하여 구성되는 것을 특징으로 한다.And a deodorizing layer made of a nonwoven fabric impregnated with a mixed solution containing an inorganic substance.

또한, 본 발명에 따른 자동차용 캐빈필터에서,Further, in the automotive cabin filter according to the present invention,

상기 무기물을 포함한 혼합액은 물, 무기물 분말 및 바인더로 구성되거나, 또는 물, 활성탄 분말, 무기물 분말 및 바인더로 구성되거나, 또는 물, 활성탄을 포함한 무기물 분말 및 바인더로 구성되는 것을 특징으로 한다.The mixed solution containing the inorganic material may be composed of water, an inorganic powder and a binder, or may be composed of water, activated carbon powder, inorganic powder and binder, or an inorganic powder containing water and activated carbon, and a binder.

또한, 본 발명에 따른 자동차용 캐빈필터에서,Further, in the automotive cabin filter according to the present invention,

상기 혼합액의 각 구성성분의 혼합비율은 물:무기물 분말:바인더=1:1:1(중량%)인 것을 특징으로 한다.The mixing ratio of each constituent component of the mixed solution is 1: 1: 1 (% by weight) of water: inorganic powder: binder.

또한, 본 발명에 따른 자동차용 캐빈필터에서,Further, in the automotive cabin filter according to the present invention,

상기 부직포는 다수겹의 웹(web)으로 구성되는 것을 특징으로 한다.The nonwoven fabric may be composed of a plurality of webs.

또한, 본 발명에 따른 자동차용 캐빈필터에서,Further, in the automotive cabin filter according to the present invention,

상기 탈취층의 상부면 또는 하부면에는 여과층이 형성되는 것을 특징으로 한다.And a filtration layer is formed on the upper surface or the lower surface of the deodorization layer.

또한, 본 발명에 따른 자동차용 캐빈필터에서,Further, in the automotive cabin filter according to the present invention,

상기 무기물은 불석광물, 이산화규소광물, 점토광물, 알루미늄수화물 및 탄산염광물로 이루어지는 것을 특징으로 한다.The inorganic material is characterized in that it is composed of a brittle mineral, a silicon dioxide mineral, a clay mineral, an aluminum hydrate and a carbonate mineral.

또한, 본 발명에 따른 자동차용 캐빈필터에서,Further, in the automotive cabin filter according to the present invention,

상기 무기물은 불석광물 50~90 중량%, 이산화규소광물 5~20 중량%, 점토광물 3~15 중량%, 알루미늄수화물 1~10 중량%, 탄산염광물 0.1~10 중량%로 이루어지는 것을 특징으로 한다.The inorganic material is characterized by comprising 50 to 90% by weight of cobalt minerals, 5 to 20% by weight of silicon dioxide minerals, 3 to 15% by weight of clay minerals, 1 to 10% by weight of aluminum hydrates and 0.1 to 10% by weight of carbonate minerals.

또한, 본 발명에 따른 자동차용 캐빈필터에서,Further, in the automotive cabin filter according to the present invention,

상기 무기물은 불석광물, 이산화규소광물, 점토광물, 알루미늄수화물, 탄산염광물을 혼합하여 가열로에 투입하고, 200~280℃ 온도에서 8~12분 동안 소성 건조시킨 다음, 소성 건조된 혼합물을 분쇄하면서 60~80℃ 온도로 열 건조 및 전기 자극을 가하여, 210~280meq/100g의 CEC(cation exchange capacity), 80~160 ㎡/g의 표면적 및 70~100nm의 나노 결정 크기를 갖는 분말로 제공되는 것을 특징으로 한다.The inorganic material is mixed with a cobalt mineral, a silicon dioxide mineral, a clay mineral, an aluminum hydrate and a carbonate mineral, and the mixture is introduced into a heating furnace, fired and dried at a temperature of 200 to 280 ° C. for 8 to 12 minutes, And then subjected to thermal drying and electrical stimulation at a temperature of 60 to 80 占 폚 to give a powder having a CEC (cation exchange capacity) of 210 to 280 meq / 100 g, a surface area of 80 to 160 m 2 / g and a nanocrystal size of 70 to 100 nm .

또한, 본 발명에 따른 자동차용 캐빈필터에서,Further, in the automotive cabin filter according to the present invention,

상기 불석광물은 캐바사이트(Chabasite), 클리노프틸로라이트(Clinoptilolite), 나트롤라이트(Natrolite), 모데나이트(Mordenite) 중에서 선택되는 어느 하나 또는 이들의 혼합물로 이루어지고, The pyroxene mineral may be any one selected from the group consisting of Chabasite, Clinoptilolite, Natrolite and Mordenite, or a mixture thereof,

상기 이산화규소광물은 석영(Quartz), 알바이트(Albite) 중에서 선택되는 어느 하나 또는 이들의 혼합물로 이루어지며,The silicon dioxide mineral may be any one selected from the group consisting of quartz and albite, or a mixture thereof,

상기 점토광물은 몬모릴로나이트(Montmorillonite), 일라이트(Iliite) 중에서 선택되는 어느 하나 또는 이들의 혼합물로 이루어지고, The clay mineral may be any one selected from the group consisting of montmorillonite and lliite, or a mixture thereof.

상기 알루미늄수화물은 보크사이트(Bauxite), 기브자이트(Gibbsite) 중에서 선택되는 어느 하나 또는 이들의 혼합물로 이루어지며,The aluminum hydrate may be any one selected from the group consisting of Bauxite and Gibbsite, or a mixture thereof.

상기 탄산염광물은 돌로마이트(Dolomite)로 이루어지는 것을 특징으로 한다.The carbonate mineral is characterized by being made of dolomite.

또한, 본 발명에 따른 자동차용 캐빈필터에서,Further, in the automotive cabin filter according to the present invention,

상기 혼합액에는 색채 또는 향취를 갖는 천연소재 추출물을 더 포함하는 것을 특징으로 한다.And the mixed solution further comprises a natural material extract having a color or a fragrance.

또한, 본 발명에 따른 자동차용 캐빈필터에서,Further, in the automotive cabin filter according to the present invention,

상기 탈취층의 일면 또는 양면에 여과층을 더 구비할 수 있으며,The deodorization layer may further include a filtration layer on one side or both sides thereof,

상기 탈취층과 여과층 사이에는 무기물을 이루는 광물이나 활성탄 분말로 이루어진 흡착층을 더 구비하는 것을 특징으로 한다.And an adsorption layer made of a mineral or activated carbon powder forming an inorganic substance is disposed between the deodorization layer and the filtration layer.

상술한 바와 같이, 본 발명에 따른 자동차용 캐빈필터는 다수겹의 웹(web)으로 된 부직포를 물, 무기물 및 바인더가 혼합된 혼합액에 함침시켜 제조한 탈취층을 포함시킴으로써 포집과 탈취효능을 향상시키면서도 공기투과율이 양호한 효과가 있다. As described above, the automotive cabin filter according to the present invention improves the collection and deodorization efficiency by including a deodorization layer formed by impregnating a multi-layered web nonwoven fabric with a mixture of water, an inorganic material and a binder The air permeability is good.

도 1은 본 발명에 따른 자동차용 캐빈필터의 개략도와 필터의 구조를 나타내는 도면.BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a schematic view of a car cabin filter according to the present invention and a structure of a filter. Fig.

이하에서는 첨부도면을 통해 본 발명의 바람직한 일 실시예를 상세하게 설명한다.
Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1은 본 발명에 따른 자동차용 캐빈필터의 개략도와 필터의 구조를 나타내는 도면이다.
BRIEF DESCRIPTION OF DRAWINGS FIG. 1 is a schematic view of a cabin filter for an automobile according to the present invention and a view showing a structure of a filter. FIG.

도 1에 도시된 바와 같이, 본 발명에 따른 자동차용 캐빈필터(1)는 무기물을 포함한 혼합액에 함침시킨 부직포로 제조된 탈취층(10)을 포함하여 구성된다. 1, the automotive cabin filter 1 according to the present invention comprises a deodorizing layer 10 made of a nonwoven fabric impregnated with a mixed solution containing an inorganic substance.

상세하게 설명하면, 탈취층(10)은 다수겹의 웹(web)으로 된 부직포를 물, 무기물 분말 및 바인더, 또는 물, 활성탄 분말, 무기물 분말 및 바인더, 또는 물, 활성탄을 포함한 무기물 분말 및 바인더가 혼합된 혼합액에 함침시켜 제조될 수 있다. 이와 같이 제조된 부직포 원단의 일면 또는 양면에 여재를 더 합지하여 여과층(20)을 형성하는 것도 바람직하다.
In detail, the deodorization layer 10 is formed by stacking a plurality of webs of a nonwoven fabric with water, an inorganic powder and a binder, or water, an activated carbon powder, an inorganic powder and a binder, or an inorganic powder including water, To the mixed solution. It is also preferable to form the filtration layer 20 by further joining filter materials on one or both sides of the nonwoven fabric fabric thus produced.

이때, 여과층(20)의 형성 과정은, 권취롤에 감겨서 공급되는 부직포를 혼합액에 함침되도록 구성하고 함침과정이 끝난 부직포의 일면 또는 양면에 별도의 권취롤로 공급되는 여재를 합지한 후, 다수개가 수직으로 이격되게 배치된 소정온도로 달궈진 단일 롤러(미도시)를 지그재그로 통과하도록 하되 롤러의 외면을 감싸도록 밀착시켜 탈취층과 여과층이 핫멜트 방식으로 접착과 밀착이 이루어지도록 하여 형성되는 것이다.At this time, in the process of forming the filtration layer 20, the nonwoven fabric wound and wound on the take-up roll is impregnated with the mixed solution, and the filter material supplied to the one side or both sides of the impregnated non- (Not shown) which is arranged at a predetermined temperature so as to be vertically spaced apart from each other so that the deodorant layer and the filtration layer are adhered and adhered in a hot-melt manner .

이와 같은 합지방식에 의해 탈취층과 여과층을 접착과 밀착하게 되면, 한쌍의 압착롤러의 사용시 강한 압착력에 의한 탈취층의 무기물을 이루는 구성성분의 다공성이 막히거나 표면적이 적어지는 현상이 방지되게 되고, 그 결과 탈취층이 갖는 포집과 흡착효율 및 공기투과성을 저감시키는 것을 방지할 수 있게 된다.
When the deodorizing layer and the filtration layer are adhered to each other by such a laminating method, when the pair of pressing rollers is used, the phenomenon that the porosity of the component constituting the inorganic material of the deodorization layer due to the strong pressing force is blocked or the surface area is decreased is prevented As a result, it is possible to prevent the collection and absorption efficiency and air permeability of the deodorization layer from being reduced.

또한, 탈취층(10)과 여과층(20) 사이에 제올라이트 또는 후술하는 무기물을 이루는 광물이나 활성탄 등의 분말로 이루어진 흡착층(30)을 더 구비할 수도 있음은 물론이다.It is needless to say that an adsorption layer 30 made of powder such as zeolite or mineral or activated carbon which forms an inorganic material to be described later may be further provided between the deodorization layer 10 and the filtration layer 20.

이때 흡착층(30)은 분사방식으로 형성하거나 또는 접착제를 이용한 핫멜트 방식으로 분사후 압착하여 형성할 수 있다.
At this time, the adsorption layer 30 may be formed by an injection method or by spraying using a hot-melt method using an adhesive, followed by pressing.

여기서, 탈취층(10)에 사용되는 부직포가 함침되는 혼합액의 각 구성성분의 혼합비율은 물:무기물 분말:바인더=1:1:1(중량%)이다.
Here, the blending ratio of each constituent component of the mixture liquid impregnated with the nonwoven fabric used in the deodorization layer 10 is 1: 1: 1 (% by weight) of water: inorganic powder: binder.

본 발명에서 무기물 분말은 불석광물 50~90 중량%, 이산화규소광물 5~20 중량%, 점토광물 3~15 중량%, 알루미늄수화물 1~10 중량%, 탄산염광물 0.1~10 중량%, 바람직하게는 불석광물 67~80 중량%, 이산화규소광물 8~16 중량%, 점토광물 6~10 중량%, 알루미늄수화물 3~5 중량%, 탄산염광물 1~2 중량%을 혼합하여 이루어질 수 있다.
In the present invention, the inorganic powder preferably comprises 50 to 90% by weight of a cobalt mineral, 5 to 20% by weight of a silicon dioxide mineral, 3 to 15% by weight of a clay mineral, 1 to 10% by weight of an aluminum hydrate, and 0.1 to 10% A clay mineral 6 to 10 weight%, an aluminum hydrate 3 to 5 weight%, and a carbonate mineral 1 to 2 weight%.

이와 같은 무기물 분말의 제조방법은, 불석광물, 이산화규소광물, 점토광물, 알루미늄수화물, 탄산염광물을 혼합하여 가열로에 투입하고 200~280℃ 온도에서 8~12분 동안 소성 건조시킨다.The inorganic powder is prepared by mixing a cobalt mineral, a silicon dioxide mineral, a clay mineral, an aluminum hydrate, and a carbonate mineral, and heating and firing the mixture at a temperature of 200 to 280 ° C for 8 to 12 minutes.

그런 다음 소성 건조된 혼합물을, 분쇄기에서 30~70 메쉬로 분쇄하면서 60~80℃ 온도로 열 건조 및 전기 자극을 가함으로써, 210~280meq/100g의 CEC(cation exchange capacity), 80~160 ㎡/g의 표면적 및 70~100nm의 나노 결정 크기를 각각 가질 수 있다. The fired and dried mixture is then pulverized to 30 to 70 mesh in a pulverizer and heat dried and electrically stimulated at a temperature of 60 to 80 DEG C to form a powder having a cation exchange capacity (CEC) of 210 to 280 meq / g and a nanocrystal size of 70 to 100 nm, respectively.

이와 같은 공정으로 제조된 무기물 분말은 각 구성성분 광물의 다공성이 유지되어 공기투과성 효율이 양호하게 된다.The inorganic powder produced by such a process maintains the porosity of each constituent mineral so that the air permeability becomes good.

여기서 가열과정을 가열로에 의한 것을 예시하였으나 이에 국한되는 것은 아니며, 가열로로서 로터리 킬른(rotary kiln)이 사용될 수 있고, 가열에 의해 수분 3% 이하의 공극 증대 효과를 가질 수 있다. 또한 분쇄과정 역시 분쇄기에 의한 것을 예시하였으나 이에 국한되는 것은 아니며, 레이몬드 밀(raymond mill)을 사용하여 분쇄할 수도 있고, 입도구성 혼합 치환이 이루어지도록 할 수 있다.
Here, the heating process is exemplified by a heating furnace. However, the heating furnace is not limited thereto, and a rotary kiln may be used as a heating furnace, and the furnace can have a porosity increasing effect of 3% or less in moisture by heating. The crushing process is also exemplified by a crusher, but the crushing process is not limited thereto. The crushing process may be performed by using a raymond mill, or the crushing process may be performed to change the particle size of the crusher.

본 무기물 분말에는 무기물 총 중량대비 SiO2 70~75 중량%, Al2O3 13~18 중량%, CaO 4~6 중량%, K20 1~2 중량%, Na2O 1~2 중량%, MgO 0.1~1 중량%, Fe2O3 0.1~1 중량% 중에서 선택되는 어느 하나 또는 이들의 혼합물을 더 포함할 수 있다.
The inorganic powder is compared to SiO 2 70 ~ 75% by weight of the inorganic total, Al 2 O 3 13 ~ 18 wt%, CaO 4 ~ 6 wt%, K 2 0 1 ~ 2 wt%, Na 2 O 1 ~ 2 % by weight 0.1 to 1% by weight of MgO, 0.1 to 1% by weight of Fe 2 O 3, or a mixture thereof.

본 무기물에 포함되는 광물은 해당하는 광물의 범위에 속하는 다양한 종류로 이루어질 수 있다. 예를들면, 불석광물은 캐바사이트(Chabasite), 클리노프틸로라이트(Clinoptilolite, (Na,K,Ca)2-3Al3(Al,Si)2Si13O36·12H2O), 나트롤라이트(Natrolite, Na2Al2Si3O10·2H2O), 모데나이트(Mordenite, (Ca,Na2, K2)Al2Si10O24·7H2O) 중에서 선택되는 어느 하나 또는 다수의 혼합물로 이루어질 수 있고, 이산화규소광물은 석영(Quartz, SiO2), 알바이트(Albite, NaAlSi3O8) 중에서 선택되는 어느 하나 또는 이들의 혼합물로 이루어질 수 있고, 점토광물은 몬모릴로나이트(Montmorillonite,(Al,Mg)2Si4O10(OH)2·4H2O), 일라이트(Iliite, (K,H3O)Al2(Si,Al)4O10(H2O,OH)2) 중에서 선택되는 어느 하나 또는 이들의 혼합물로 이루어질 수 있다. 또한, 알루미늄수화물은 보크사이트(Bauxite, Al2O3·2H2O), 기브자이트(Gibbsite, Al(OH)3) 중에서 선택되는 어느 하나 또는 이들의 혼합물로 이루어질 수 있고, 탄산염광물은 돌로마이트(Dolomite, CaMg(CO3)2)로 이루어질 수 있다. Minerals included in this mineral may be of various types belonging to the range of minerals concerned. For example, the cobalt minerals are chabasite, clinoptilolite (Na, K, Ca) 2 -3 Al 3 (Al, Si) 2 Si 13 O 36 · 12 H 2 O), Natrolite , Na 2 Al 2 Si 3 O 10 .2H 2 O), mordenite (Ca, Na 2 , K 2) Al 2 Si 10 O 24揃 7H 2 O, and the silicon dioxide mineral may be quartz, SiO2), (it can be made in any one or a mixture selected from the group consisting of Albite, NaAlSi3O8), clay minerals are montmorillonite (montmorillonite, (Al, Mg) albayiteu 2 Si4O10 (OH) 2 · 4H 2 O), illite ( Iliite, (K, H 3 O) Al 2 (Si, Al) 4 O 10 (H 2 O, OH) 2 ) or a mixture thereof. The aluminum hydrate may be composed of any one selected from bauxite (Al 2 O 3 .2H 2 O), gibbsite (Al (OH) 3 ) or a mixture thereof. The carbonate mineral may be a dolomite (Dolomite, CaMg (CO 3 ) 2 ).

이와 같은 본 발명에 따른 무기물의 혼합 물질은 각 성분들의 매우 큰 표면적과 미크론 이하의 결정크기 및 큰 다공크기에 기인하여 냄새 등의 흡착효율이 크기 때문에, 공기중 암모니아(NH3), 포름알데히드(HCHO) 및 휘발성유기화합물(VOC)의 저감에 기여할 수 있으며, 이로 인해 실내 환경의 오염 방지에 기여한다. 특히 많은 세공을 가지는 있어 흡착 표면적이 매우 큰 불석광물 등에 의해 양이온을 치환하는 능력이 우수하여 유해물질의 흡착에 이용될 수 있고, 중금속 양이온을 손쉽게 치환함으로써 유해한 중금속의 제거에도 탁월한 성능을 발휘할 수 있다. 또한 광물로부터 원적외선을 방출함으로써, 이로운 주변 환경을 제공할 수 있게 된다.
Since the mixed material of the inorganic material according to the present invention has a large adsorption efficiency due to the odor due to the very large surface area of each component, the crystal size of less than micron and the large porous size, it is difficult to remove ammonia (NH 3 ), formaldehyde HCHO) and volatile organic compounds (VOC), thereby contributing to prevention of contamination of the indoor environment. Especially, it has excellent ability to replace cations due to the presence of a large amount of pores, and can be used for the adsorption of harmful substances. By substituting heavy metal cations easily, it is possible to exhibit excellent performance for removal of harmful heavy metals . By emitting far infrared rays from the minerals, it is possible to provide favorable surrounding environment.

또한, 본 발명에 따른 자동차용 캐빈필터의 색채를 더한 시각적 효과 또는 인체에 유효한 향취 등을 위해 상술한 무기물 혼합액에 천연소재 추출물을 더 포함시킬 수 있다.
In addition, the natural material extract may be further included in the above-described inorganic material mixture for visual effects added to the color of the cabin filter for automobiles according to the present invention, or fragrance effective on the human body.

제조된 캐빈필터는 주름을 형성하도록 접어 필터 표면적을 확대시키는 것이 바람직하다.
The manufactured cabin filter is preferably folded to form a wrinkle to enlarge the filter surface area.

이상에서 본 발명의 실시 예에 대하여 상세하게 설명하였지만 본 발명의 권리범위는 이에 한정되는 것은 아니고 다음의 청구범위에서 정의하고 있는 본 발명의 기본 개념을 이용한 당업자의 여러 변형 및 개량 형태 또한 본 발명의 권리범위에 속하는 것이다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, It belongs to the scope of right.

1: 캐빈필터 10:탈취층
20:여과층 30:흡착층1: cabin filter 10: deodorization layer
20: filtration layer 30: adsorption layer

Claims (11)

무기물을 포함한 혼합액에 함침시킨 부직포로 제조된 탈취층을 포함하여 구성되고,
상기 무기물은 불석광물, 이산화규소광물, 점토광물, 알루미늄수화물 및 탄산염광물로 이루어지는 것을 특징으로 하는 자동차용 캐빈필터.
And a deodorizing layer made of a nonwoven fabric impregnated with a mixed solution containing an inorganic substance,
Wherein the inorganic material is composed of a cobalt mineral, a silicon dioxide mineral, a clay mineral, an aluminum hydrate and a carbonate mineral.
제 1항에 있어서,
상기 무기물을 포함한 혼합액은 물, 무기물 분말 및 바인더로 구성되거나, 또는 물, 활성탄 분말, 무기물 분말 및 바인더로 구성되거나, 또는 물, 활성탄을 포함한 무기물 분말 및 바인더로 구성되는 것을 특징으로 하는 자동차용 캐빈필터.
The method according to claim 1,
Wherein the mixed liquid containing the inorganic material is composed of water, an inorganic powder and a binder, or is composed of water, an activated carbon powder, an inorganic powder and a binder or an inorganic powder containing water and activated carbon and a binder. filter.
제 2항에 있어서,
상기 혼합액의 각 구성성분의 혼합비율은 물:무기물 분말:바인더=1:1:1(중량%)인 것을 특징으로 하는 자동차용 캐빈필터.
3. The method of claim 2,
Wherein the mixing ratio of each constituent component of the mixed liquid is 1: 1: 1 (weight%) of water: inorganic powder: binder.
제 1항에 있어서,
상기 부직포는 다수겹의 웹(web)으로 구성되는 것을 특징으로 하는 자동차용 캐빈필터.
The method according to claim 1,
Wherein the nonwoven fabric is composed of a plurality of webs.
제 1항에 있어서,
상기 탈취층의 일면 또는 양면에는 여과층이 형성되는 것을 특징으로 하는 자동차용 캐빈필터.
The method according to claim 1,
Wherein a filter layer is formed on one side or both sides of the deodorization layer.
삭제delete 제 1항에 있어서,
상기 무기물은 불석광물 50~90 중량%, 이산화규소광물 5~20 중량%, 점토광물 3~15 중량%, 알루미늄수화물 1~10 중량%, 탄산염광물 0.1~10 중량%로 이루어지는 것을 특징으로 하는 자동차용 캐빈필터.
The method according to claim 1,
Wherein the inorganic material is composed of 50 to 90% by weight of a cobalt mineral, 5 to 20% by weight of a silicon dioxide mineral, 3 to 15% by weight of a clay mineral, 1 to 10% by weight of an aluminum hydrate, and 0.1 to 10% Cabin filter for.
제 1항에 있어서,
상기 무기물은 불석광물, 이산화규소광물, 점토광물, 알루미늄수화물, 탄산염광물을 혼합하여 가열로에 투입하고, 200~280℃ 온도에서 8~12분 동안 소성 건조시킨 다음, 소성 건조된 혼합물을 분쇄하면서 60~80℃ 온도로 열 건조 및 전기 자극을 가하여, 210~280meq/100g의 CEC(cation exchange capacity), 80~160 ㎡/g의 표면적 및 70~100nm의 나노 결정 크기를 갖는 분말로 제공되는 것을 특징으로 하는 자동차용 캐빈필터.
The method according to claim 1,
The inorganic material is mixed with a cobalt mineral, a silicon dioxide mineral, a clay mineral, an aluminum hydrate and a carbonate mineral, and the mixture is introduced into a heating furnace, fired and dried at a temperature of 200 to 280 ° C. for 8 to 12 minutes, And then subjected to thermal drying and electrical stimulation at a temperature of 60 to 80 占 폚 to give a powder having a CEC (cation exchange capacity) of 210 to 280 meq / 100 g, a surface area of 80 to 160 m 2 / g and a nanocrystal size of 70 to 100 nm Features a car cabin filter.
제 1항에 있어서,
상기 불석광물은 캐바사이트(Chabasite), 클리노프틸로라이트(Clinoptilolite), 나트롤라이트(Natrolite), 모데나이트(Mordenite) 중에서 선택되는 어느 하나 또는 이들의 혼합물로 이루어지고,
상기 이산화규소광물은 석영(Quartz), 알바이트(Albite) 중에서 선택되는 어느 하나 또는 이들의 혼합물로 이루어지며,
상기 점토광물은 몬모릴로나이트(Montmorillonite), 일라이트(Iliite) 중에서 선택되는 어느 하나 또는 이들의 혼합물로 이루어지고,
상기 알루미늄수화물은 보크사이트(Bauxite), 기브자이트(Gibbsite) 중에서 선택되는 어느 하나 또는 이들의 혼합물로 이루어지며,
상기 탄산염광물은 돌로마이트(Dolomite)로 이루어지는 것을 특징으로 하는 자동차용 캐빈필터.
The method according to claim 1,
The pyroxene mineral may be any one selected from the group consisting of Chabasite, Clinoptilolite, Natrolite and Mordenite, or a mixture thereof,
The silicon dioxide mineral may be any one selected from the group consisting of quartz and albite, or a mixture thereof,
The clay mineral may be any one selected from the group consisting of montmorillonite and lliite, or a mixture thereof.
The aluminum hydrate may be any one selected from the group consisting of Bauxite and Gibbsite, or a mixture thereof.
Wherein the carbonate mineral is dolomite.
제 1항에 있어서,
상기 혼합액에는 색채 또는 향취를 갖는 천연소재 추출물을 더 포함하는 것을 특징으로 하는 자동차용 캐빈필터.
The method according to claim 1,
Wherein the mixed liquid further comprises a natural material extract having a color or a fragrance.
제 1항에 있어서,
상기 탈취층의 일면 또는 양면에 여과층을 더 구비할 수 있으며,
상기 탈취층과 여과층 사이에는 무기물을 이루는 광물이나 활성탄 분말로 이루어진 흡착층을 더 구비하는 것을 특징으로 하는 자동차용 캐빈필터.The method according to claim 1,
The deodorization layer may further include a filtration layer on one side or both sides thereof,
Further comprising an adsorption layer between the deodorization layer and the filtration layer, the adsorption layer being composed of minerals or powder of activated carbon.
KR1020170002060A 2017-01-05 2017-01-05 Cabin-filter for cars KR101925130B1 (en)