KR101904854B1 - Method for manufacturing functional paper from coffee-grounds - Google Patents

Method for manufacturing functional paper from coffee-grounds Download PDF

Info

Publication number
KR101904854B1
KR101904854B1 KR1020170047700A KR20170047700A KR101904854B1 KR 101904854 B1 KR101904854 B1 KR 101904854B1 KR 1020170047700 A KR1020170047700 A KR 1020170047700A KR 20170047700 A KR20170047700 A KR 20170047700A KR 101904854 B1 KR101904854 B1 KR 101904854B1
Authority
KR
South Korea
Prior art keywords
raw paper
functional
paper
raw
coffee
Prior art date
Application number
KR1020170047700A
Other languages
Korean (ko)
Inventor
송중민
Original Assignee
송중민
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 송중민 filed Critical 송중민
Priority to KR1020170047700A priority Critical patent/KR101904854B1/en
Application granted granted Critical
Publication of KR101904854B1 publication Critical patent/KR101904854B1/en

Abstract

Functional paper according to the present invention includes functional raw paper containing coffee residues, first raw paper attached to one surface of the functional raw paper, and second raw paper attached to the other surface of the functional raw paper. The first raw paper and the second raw paper which are interlaced with each other with the functional raw paper interposed therebetween prevent the coffee residues from being exposed.

Description

커피찌꺼기를 이용한 기능성 종이 및 이의 제조방법{Method for manufacturing functional paper from coffee-grounds}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a functional paper using coffee grounds,

본 발명은 커피찌꺼기를 이용한 기능성 종이 및 이의 제조방법에 관한 것으로, 보다 상세하게는 종래 기술보다 위생적이고 사용 성능이 우수한 기능성 종이 및 이의 제조방법에 관한 것이다.The present invention relates to a functional paper using coffee grounds and a manufacturing method thereof, and more particularly, to a functional paper which is more hygienic than the prior art and has excellent use performance, and a method for manufacturing the functional paper.

일상 생활에서 마시는 원두 커피는 커피 원두를 분쇄한 커피 분말에 수증기의 압착이나 물을 이용하여 커피 원액을 내려 활용한다. 이때, 사용하고 버려지는 원두 커피의 찌꺼기를 재활용하여 친환경적인 생필품을 생산하기 위한 기술 개발이 다양한 방면에서 이뤄지고 있다.Coffee beans used in everyday life are made by crushing coffee beans into coffee powder, using water vapor or water to lower the amount of coffee. At this time, the development of technology for producing eco-friendly commodities using recycled waste coffee beans is being carried out in various ways.

예컨대, 화장지, 휴지, 기저귀 등의 용도로 커피찌꺼기를 사용하는 경우 커피찌꺼기의 특성인 탈취, 커피 오일 층에 의한 피부보호 및 천연 염색의 효과를 얻을 수 있는 것이다. For example, when coffee grounds are used for toilet paper, tissue paper, diapers, etc., it is possible to obtain effects of deodorization as a characteristic of coffee grounds, skin protection by a coffee oil layer and natural dyeing.

특히, 제지 분야에서 커피찌꺼기를 이용함으로써 탈취 및 방습의 기능을 얻으려는 기능성 종이의 개발이 이뤄지고 있으며, 특허 제10-1257214호(2013.04.23. 공고)에 커피찌꺼기를 이용한 기능성 펄프에 대한 기술이 개시되어 있다. Particularly, in the field of paper, the development of a functional paper for obtaining deodorizing and moisture-proofing function by using coffee grounds is being developed, and a technique for functional pulp using coffee grounds is disclosed in Patent No. 10-1257214 (published on March 23, 2013) Lt; / RTI >

그러나, 이와 같은 기술은 커피 분말 내지 찌꺼기를 종이에 포함시키기 위해 소정 크기 이하의 작은 분말로 갈아야만 하는 문제점이 있으며, 기능성 종이의 사용 시 작은 분말의 커피찌꺼기 가루가 비산되거나 사용자에게 노출되는 문제점이 있다. However, such a technique has a problem in that it needs to be replaced with a powder having a predetermined size or less to contain coffee powder or residue in paper, and there is a problem in that when using the functional paper, coffee ground powder of a small powder is scattered or exposed to a user have.

등록번호 제10-1257214호(2013.04.23. 공고)Registration No. 10-1257214 (Announcement of March 23, 2013)

본 발명은 전술한 문제점을 감안하여 안출된 것으로서, 본 발명의 목적은 커피찌꺼기를 포함한 기능성 종이의 사용 시 커피 가루가 외부에 노출되지 않도록 함으로써 사용자에게 위생적이고 우수한 사용성능을 제공하려는 것이다. SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned problems, and it is an object of the present invention to provide a user with hygienic and excellent use performance by preventing the coffee powder from being exposed to the outside when using functional paper including coffee grounds.

본 발명에 따른 기능성 종이는 커피찌꺼기를 함유하는 기능성 원지, 상기 기능성 원지의 일면에 열 압착 성형 내지 접착 성형으로 부착되어 상기 커피찌꺼기의 노출을 방지하는 제1 원지, 상기 기능성 원지의 타면에 열 압착 성형 내지 접착 성형으로 부착되어 상기 커피찌꺼기의 노출을 방지하는 제2 원지 및 상기 기능성 원지와 상기 제1 원지 및 제2 원지 사이에 하나 이상 마련되되 소정 크기 이하 직경의 다공성 표면이 마련된 커버층을 포함하며,
상기 기능성 원지, 제1 원지 및 제2 원지를 합친 중량 대비, 상기 기능성 원지에 함유된 상기 커피찌꺼기의 총 중량 비율은 상기 기능성 원지의 용도와 두께에 따라 2 내지 10 퍼센트 사이에서 선택할 수 있으며,
상기 커피찌꺼기의 분말은 상기 기능성 원지의 펄프 제조과정에서 혼합되거나 기 성형된 상기 기능성 원지에 도포될 수 있으며, 상기 제1 원지 및 제2 원지는 정보전달 및 메시지 알람을 위한 그림 내지 도안을 포함하며,
상기 커버층은 투명한 재질로 마련되어 상기 기능성 원지의 표면에 도포 또는 코팅되거나 별도의 필름으로 부착되고, 두께는 상기 기능성 원지 내지 상기 제1 원지 및 제2 원지보다 작게 마련되되 0.001mm 내지 0.005mm로 마련되는 것을 특징 특징으로 한다.The functional paper according to the present invention comprises a functional raw paper containing coffee grounds, a first raw paper adhered to one surface of the functional raw paper by thermo compression molding or adhesive molding to prevent exposure of the coffee grounds, And a cover layer provided on at least one of the functional raw paper and the first raw paper and the second raw paper and having a porous surface of a predetermined size or less in diameter, In addition,
The total weight ratio of the coffee grounds contained in the functional raw paper to the combined weight of the functional raw paper, the first raw paper and the second raw paper may be selected from 2 to 10 percent depending on the use and thickness of the functional raw paper,
The powder of the coffee grounds may be applied to the functional raw paper mixed or molded in the pulp manufacturing process of the functional raw paper, and the first raw paper and the second raw paper include figures or drawings for information transmission and message alarm ,
The cover layer is made of a transparent material and is coated or coated on the surface of the functional raw paper or is attached as a separate film. The thickness of the cover layer is smaller than the functional raw paper, the first raw paper and the second raw paper and is set to 0.001 mm to 0.005 mm .

삭제delete

삭제delete

삭제delete

본 발명에 따른 기능성 종이의 제조방법은 커피찌꺼기를 소정 크기 이하의 분말로 그라인딩 하는 단계, 상기 분말을 이용하여 펄프를 마련하는 단계, 상기 펄프를 이용하여 기능성 원지를 제작하는 단계, 상기 기능성 원지를 사이에 두고 제1 원지 및 제2 원지를 서로 합지하여 보호층을 형성하는 단계 및 상기 기능성 원지와 상기 제1 원지 및 제2 원지 사이에 하나 이상 마련되되 소정 크기 이하 직경의 다공성 표면이 마련된 커버층을 마련하는 단계를 포함하며,
상기 기능성 원지, 제1 원지 및 제2 원지를 합친 중량 대비, 상기 기능성 원지에 함유된 상기 커피찌꺼기의 총 중량 비율은 상기 기능성 원지의 용도와 두께에 따라 2 내지 10 퍼센트 사이에서 선택할 수 있으며,
상기 커피찌꺼기의 분말은 상기 기능성 원지의 펄프 제조과정에서 혼합되거나 기 성형된 상기 기능성 원지에 도포될 수 있으며, 상기 제1 원지 및 제2 원지는 정보전달 및 메시지 알람을 위한 그림 내지 도안을 포함하며,
상기 커버층은 투명한 재질로 마련되어 상기 기능성 원지의 표면에 도포 또는 코팅되거나 별도의 필름으로 부착되고, 두께는 상기 기능성 원지 내지 상기 제1 원지 및 제2 원지보다 작게 마련되되 0.001mm 내지 0.005mm로 마련되는 것을 특징으로 한다.The method for preparing a functional paper according to the present invention comprises the steps of grinding coffee grounds into a powder of a predetermined size or less, preparing pulp using the powder, fabricating a functional ground using the pulp, Forming a protective layer by laminating the first raw paper and the second raw paper between the first raw paper and the second raw paper, and forming a cover layer having a porous surface with a diameter of a predetermined size or less, And,
The total weight ratio of the coffee grounds contained in the functional raw paper to the combined weight of the functional raw paper, the first raw paper and the second raw paper may be selected from 2 to 10 percent depending on the use and thickness of the functional raw paper,
The powder of the coffee grounds may be applied to the functional raw paper mixed or molded in the pulp manufacturing process of the functional raw paper, and the first raw paper and the second raw paper include figures or drawings for information transmission and message alarm ,
The cover layer is made of a transparent material and is coated or coated on the surface of the functional raw paper or is attached as a separate film. The thickness of the cover layer is smaller than the functional raw paper, the first raw paper and the second raw paper and is set to 0.001 mm to 0.005 mm .

삭제delete

삭제delete

본 발명에 따른 기능성 종이 및 이의 제조방법은 커피찌꺼기를 포함한 기능성 종이의 사용 시 커피 가루가 외부에 노출되지 않도록 하는 기능성 종이에 활용할 수 있다.The functional paper according to the present invention and the manufacturing method thereof can be utilized as a functional paper for preventing the coffee powder from being exposed to the outside when using a functional paper including coffee grounds.

도 1은 본 발명의 실시예에 따른 기능성 종이의 분해도 및 부분확대도,
도 2는 본 발명의 다른 실시예에 따른 기능성 종이의 분해도 및 부분확대도,
도 3은 본 발명의 또 다른 실시예에 따른 기능성 종이의 분해도 및 부분확대도,
도 4는 본 발명의 실시예에 따른 기능성 종이의 설명도,
도 5는 본 발명에 따른 기능성 종이의 제조방법에 관한 순서도이다.FIG. 1 is an exploded view of a functional paper according to an embodiment of the present invention,
2 is an exploded view and partial enlarged view of a functional paper according to another embodiment of the present invention,
3 is an exploded view and partial enlarged view of a functional paper according to another embodiment of the present invention,
4 is an explanatory diagram of a functional paper according to an embodiment of the present invention,
5 is a flowchart illustrating a method for producing a functional paper according to the present invention.

이하, 첨부된 도면을 참조하면서 본 발명의 실시예에 따른 기능성 종이 및 제조방법에 관하여 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시 할 수 있도록 상세히 설명하기로 한다. 본 발명은 여기에서 설명하는 실시예들에 한정되지 않으며, 여러 가지 상이한 형태로 구현될 수 있다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Reference will now be made in detail to embodiments of the present invention, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to the like elements throughout. The present invention is not limited to the embodiments described herein, but may be embodied in various different forms.

본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 동일 또는 유사한 구성요소에 대해서는 동일한 참조부호를 붙이도록 한다. 본 발명에 따른 기능성 종이는 명칭에 한정되지 않고 다양하게 적용될 수 있으므로, 이하 설명하는 용어나 명칭에 한정될 필요는 없다. In order to clearly illustrate the present invention, parts not related to the description are omitted, and the same or similar components are denoted by the same reference numerals throughout the specification. The functional paper according to the present invention is not limited to the name and can be variously applied thereto, and thus the functional paper need not be limited to the following terms and names.

본 발명에 따른 기능성 종이는 커피찌꺼기를 함유하는 기능성 원지(200), 상기 기능성 원지(200)의 일면에 부착되는 제1 원지(100) 및 상기 기능성 원지(200)의 타면에 부착되는 제2 원지(300)를 포함한다. 이때 상기 기능성 원지(200)를 사이에 두고 상호 합지되는 상기 제1 원지(100) 및 제2 원지(300)는 상기 커피찌꺼기의 노출을 방지한다.The functional paper according to the present invention includes a functional paper 200 containing coffee grounds, a first paper 100 attached to one side of the functional paper 200, and a second paper 100 attached to the other side of the functional paper 200, (300). At this time, the first raw paper sheet 100 and the second raw paper sheet 300, which are interlaced with each other with the functional paper sheet 200 interposed therebetween, prevent the coffee grounds from being exposed.

상기 기능성 원지(200)를 제작하기 위해서는 종래 기술에 따라 소정 크기 이하의 커피찌꺼기 분말을 펄프의 제조과정에서 혼합할 수도 있으며, 경우에 따라서는 상기 기능성 원지(200)에 커피찌꺼기의 분말을 도포하는 방법으로 상기 기능성 원지(200)를 제작할 수도 있다. In order to manufacture the functional raw paper 200, coffee ground powder having a predetermined size or less may be mixed in the process of manufacturing the pulp according to the prior art. In some cases, the functional raw paper 200 may be coated with powder of coffee ground The functional raw paper 200 may be prepared.

상기 기능성 원지(200)를 제작하는 과정은 다음과 같다.The process for fabricating the functional fabric 200 is as follows.

먼저, 커피찌꺼기가 혼합된 펄프의 제조공정에서 시작된다. 즉, 원두커피 찌거기 및 원두커피 추출물을 수거하고, 60°C 이상의 용수에 원두커피 또는 원두커피 찌거기를 투입한 뒤 농축액을 추출하고, 상기 농축액에 필요에 따라 커피 향을 첨가하여 농축액을 생성한다.First, the coffee grounds are started in the process of producing mixed pulp. That is, a coffee bean scoop and a coffee bean extract are collected, a coffee bean or a coffee bean scoop is added to a water of 60 ° C or higher, a concentrate is extracted, and a coffee aroma is added to the concentrate if necessary.

또한, 별도로 펄프 제조를 위해 나무 원료에 대한 분쇄 공정을 수행하여 원료 분쇄물을 형성하고, 상기 원료 분쇄물을 혼합하는 혼합 공정을 수행하여 혼합된 원료 분쇄물을 형성하고, 상기 혼합된 원료 분쇄물을 해리하는 해리 공정, 정제 공정, 기능성 펄프 제조를 위한 고해공정, 그리고 원두커피 찌꺼기를 활용한 펄프에 대한 용지 형성 공정을 수행하여 원두커피 찌꺼기를 활용한 용지를 생성하는 공정을 포함한다. In addition, a pulverization process for the wood raw material is separately performed to form pulverized raw materials, and a mixing process of mixing the pulverized raw materials is performed to form mixed pulverized raw materials, and the mixed pulverized raw material A refining step for dissolving the pulp, a refining step for refining the functional pulp, and a paper forming process for the pulp using the coffee ground residue to produce paper using the coffee ground residue.

또한, 커피 향이 첨가된 농축액을 분사 또는 도포하여 기능성 펄프가 제조되도록 할 수도 있다. 이러한 과정은 일부 공정이 생략 내지 변경될 수 있으며 경우에 따라서는 추가 공정이 포함될 수도 있다. 또한, 기능성 원지(200)는 다양한 방법으로 커피찌꺼기를 함유할 수 있으므로 상술한 방법 이외에도 다양한 방법으로 제작할 수 있다.In addition, the concentrated pulp added with the coffee aroma may be sprayed or applied to produce the functional pulp. This process may be omitted or changed in some processes, and in some cases, additional processes may be included. In addition, since the functional raw paper 200 may contain coffee grounds by various methods, it may be manufactured by various methods other than the above-described methods.

이와 같이 제조된 기능성 원지(200)는 커피찌꺼기를 포함하고 있으므로 탈취 효과, 코팅 기능 등의 효과를 가진다. 본 발명은 이러한 기능성 원지(200)의 사용 시 발생하는 문제점인 상기 기능성 원지(200)의 커피찌꺼기 분말이 노출되어 비산되거나 상기 기능성 원지(200)로부터 이탈되는 것을 방지하기 위해 상기 기능성 원지(200)의 양 면에 제1 원지(100) 및 제2 원지(300)를 덮어 보호층을 형성하는 것이다.The functional raw fabric 200 thus produced has effects of deodorizing effect, coating function and the like because it contains coffee grounds. The present invention is applied to the functional fabric 200 to prevent the coffee ground powder of the functional fabric 200 from being scattered or separated from the functional fabric 200 when the functional fabric 200 is used. The first raw paper sheet 100 and the second raw paper sheet 300 are covered with a protective layer.

도 1에 도시된 바와 같이 상기 기능성 원지(200)를 사이에 두고 상기 제1 원지(100) 및 제2 원지(300)가 서로 합지되며 상기 제1 원지(100) 및 제2 원지(300)는 상기 기능성 원지(200)의 본래 기능인 탈취, 흡습 등의 기능을 발휘하도록 소정 크기의 구멍이 마련된 다공성 표면을 가진다.1, the first raw paper sheet 100 and the second raw paper sheet 300 are joined to each other with the functional paper sheet 200 interposed therebetween, and the first raw paper sheet 100 and the second raw paper sheet 300 are And has a porous surface provided with a hole of a predetermined size so as to exhibit functions such as deodorization and hygroscopicity, which are original functions of the functional groundsheet 200.

또한, 상기 제1 원지(100) 및 제2 원지(300)는 상기 기능성 원지(200)에 함침되어 있는 커피찌꺼기의 분말이 비산되거나 탈락되어 노출되는 것을 방지하기 위해 소정 크기 이하의 다공성 표면을 가질 수 있다. 바람직하게는 상기 기능성 원지(200)의 제조 과정에서 혼합 펄프에 투입하는 상기 커피찌꺼기 분말의 직경보다 작게 마련한다.The first raw paper 100 and the second raw paper 300 may have a porous surface of a predetermined size or less to prevent the powder of coffee ground impregnated in the functional raw paper 200 from being scattered or dropped and exposed . Preferably, the functional ground 200 is formed to have a diameter smaller than the diameter of the coffee ground powder to be introduced into the mixed pulp.

상기 기능성 원지(200)의 양 면에 마련되는 보호층인 상기 제1 원지(100) 및 제2 원지(300)는 상기 기능성 원지(200)의 본래 기능은 유지하되, 별도의 정보 전달, 메시지 알람, 그림 내지 도안을 포함하는 형상으로 제작될 수 도 있다. 따라서, 커피찌꺼기를 함유하는 상기 기능성 원지(200)를 다양한 용도로 활용할 수 있게 한다.The first raw paper sheet 100 and the second raw paper sheet 300 which are protective layers provided on both surfaces of the functional sheet material 200 can maintain the original function of the functional sheet material 200, , Or a shape including a figure or a figure. Therefore, the functional ground material 200 containing the coffee grounds can be utilized for various purposes.

도 1에 도시된 바와 같이 본 발명에 따른 기능성 종이의 전체 두께(L)는 0.1mm 내지 1.5mm로 마련될 수 있으며, 상기 기능성 원지(200)의 두께(L2)는 0.05mm 내지 1mm로 마련되고, 상기 제1 원지(100) 및 제2 원지(300)의 두께(L1, L3)는 각각 0.01mm 내지 0.04mm로 마련될 수 있다.1, the total thickness L of the functional paper according to the present invention may be 0.1 mm to 1.5 mm, and the thickness L2 of the functional paper 200 may be 0.05 mm to 1 mm The thicknesses L1 and L3 of the first raw paper sheet 100 and the second raw paper sheet 300 may be set to 0.01 mm to 0.04 mm, respectively.

도 2는 본 발명의 다른 실시예에 따른 도면이다. 도시된 바와 같이 상기 기능성 원지(200)와 상기 제1 원지(100) 및 제2 원지(300) 사이에 별개의 커버층(400)이 추가로 마련된다. 상기 커버층(400)은 상기 기능성 원지(200)의 표면에 도포되는 형태, 코팅되는 형태 및 별개의 필름을 포함하는 형태로 마련될 수 있다.2 is a diagram according to another embodiment of the present invention. A separate cover layer 400 is additionally provided between the functional fabric 200 and the first raw paper 100 and the second raw paper 300 as shown in FIG. The cover layer 400 may be provided on the surface of the functional paper 200, including a form to be coated on the surface of the functional paper 200, a coated form, and a separate film.

상기 커버층(400)은 바람직하게는 투명한 재질로 마련될 수 있으며, 앞서 설명한 바와 같이 상기 제1 원지(100) 및 제2 원지(300)와 같이 소정의 크기를 갖는 다공성 표면으로 마련될 수 있다.The cover layer 400 may be formed of a transparent material and may have a porous surface having a predetermined size such as the first raw paper 100 and the second raw paper 300 as described above .

상기 커버층(400)은 상기 기능성 원지(200)와 상기 제1 원지(100) 및 제2 원지(300)를 접착하는 기능을 수행할 수 있다. 이때, 상기 커버층(400)은 접착성을 가지는 물질을 함유하거나 도포될 수 있으며, 상기 커버층(400)의 두께는 상기 기능성 원지(200) 내지 상기 제1 원지(100) 및 제2 원지(300)의 두께보다 상대적으로 작은 크기를 가지며 바람직하게는 0.001mm 내지 0.005mm의 두께로 마련될 수 있다.The cover layer 400 may function to adhere the first raw paper 100 and the second raw paper 300 to the functional raw paper 200. The cover layer 400 may include or be coated with a material having adhesiveness and the thickness of the cover layer 400 may be determined by the thickness of the functional sheet 200 to the first sheet 100, 300, and preferably has a thickness of 0.001 mm to 0.005 mm.

도 3은 본 발명의 또 다른 실시예에 따른 도면이다. 도시된 바와 같이 상기 기능성 원지(200)의 양면에는 앞서 설명한 두 장의 커버층(400)이 마련된다. 따라서 상기 제1 원지(100) 및 제2 원지(300)가 생략되고 상기 커버층(400)을 이용하여 상기 기능성 원지(200)의 본래 기능을 확보하고 커피찌꺼기의 분말이 비산되거나 노출되는 것을 방지할 수 있다. 3 is a diagram according to another embodiment of the present invention. As shown in the figure, the two sheets of cover layer 400 described above are provided on both sides of the functional sheet 200. Therefore, the first raw paper 100 and the second raw paper 300 are omitted, and the original function of the functional raw paper 200 is secured by using the cover layer 400 to prevent the powder of the coffee residue from being scattered or exposed can do.

도 4는 본 발명의 실시예에 따른 상기 기능성 원지(200) 및 이를 양 면에서 보호하는 상기 제1 원지(100) 및 제2 원지(300)의 분해 사시도이다. 도시된 바와 같이 상기 기능성 원지(200)를 사이에 두고 합지되되 열 압착의 방식 내지 압축력을 이용한 압착 방식 등 다양한 방법으로 견고하게 밀착시킨다.4 is an exploded perspective view of the first raw paper 100 and the second raw paper 300 that protect the functional raw paper 200 according to the embodiment of the present invention and both sides thereof. As shown in the figure, the functional raw paper 200 is sandwiched between the rolls, and is tightly adhered by various methods such as a thermocompression method or a compression method using a compressive force.

상기 기능성 원지(200), 제1 원지(100) 및 제2 원지(300)를 합친 중량 대비, 상기 기능성 원지(200)에 함유된 상기 커피찌꺼기의 총 중량 비율은 2 퍼센트 내지 10퍼센트로 마련하며 바람직하게는 5퍼센트로 마련한다. 또한, 상기 기능성 원지(200)의 용도와 두께에 따라 사용자가 상기 중량 비를 선택할 수 있도록 마련한다. The ratio of the total weight of the coffee grounds contained in the functional raw paper 200 to the combined weight of the functional raw paper 200, the first raw paper 100 and the second raw paper 300 is set to 2 to 10 percent Preferably 5 percent. In addition, the user can select the weight ratio according to the use and thickness of the functional fabric 200.

본 발명에 따른 기능성 종이의 제조방법은 커피찌꺼기를 소정 크기 이하의 분말로 그라인딩 하는 단계(S100), 상기 분말을 이용하여 펄프를 마련하는 단계(S200), 상기 펄프를 이용하여 기능성 원지(200)를 제작하는 단계(S300) 및 상기 기능성 원지(200)의 표면에 보호층(100, 300)을 형성하는 단계(S400) 포함한다.The method for preparing a functional paper according to the present invention includes grinding a coffee grounds into a powder having a predetermined size or less (S100), preparing pulp using the powder (S200) (S300), and forming a protective layer (100, 300) on the surface of the functional fabric (400).

상기 보호층(100,300)을 형성하는 단계(S400)는 상기 기능성 원지(200)를 사이에 두고 제1 원지(100) 및 제2 원지(300)를 서로 합지하여 형성한다. 또한, 상기 기능성 원지(200)의 양면에는 하나 이상의 커버층(400)이 더 마련될 수 있으며, 이때 상기 제1 원지(100) 및 제2 원지(300)는 생략될 수도 있다.In the step S400 of forming the protective layers 100 and 300, the first raw paper 100 and the second raw paper 300 are formed by interposing the functional raw paper 200 therebetween. In addition, one or more cover layers 400 may be further provided on both sides of the functional paper 200, and the first paper 100 and the second paper 300 may be omitted.

본 발명에 따른 기능성 종이의 제조방법은 상기 기능성 원지(200)와 상기 제1 원지(100) 및 제2 원지(300) 사이에 하나 이상의 커버층(400)을 마련하는 단계를 더 포함할 수 있으며, 상기 커버층(400)은 소정 크기의 직경을 가지는 다공성 표면으로 마련될 수 있다. The method of manufacturing a functional paper according to the present invention may further comprise the step of providing at least one cover layer 400 between the functional fabric 200 and the first raw paper 100 and the second raw paper 300 , The cover layer 400 may be provided with a porous surface having a predetermined diameter.

또한, 상기 기능성 원지(200), 제1 원지(100) 및 제2 원지(300)를 합친 중량 대비, 상기 기능성 원지(200)에 함유된 상기 커피찌꺼기의 총 중량 비율은 2 퍼센트 내지 10퍼센트로 마련하며 바람직하게는 5퍼센트로 마련한다. 또한, 상기 기능성 원지(200)의 용도와 두께에 따라 사용자가 상기 중량 비를 선택할 수 있도록 마련한다. The ratio of the total weight of the coffee grounds contained in the functional raw paper 200 to the combined weight of the functional raw paper 200, the first raw paper 100 and the second raw paper 300 is 2 to 10 percent And is preferably set at 5 percent. In addition, the user can select the weight ratio according to the use and thickness of the functional fabric 200.

이상에서 설명한 본 발명은 전술한 실시예 및 첨부된 도면에 의해 한정되지 않으며, 본 발명의 기술적 사상 내에서의 단순 치환, 변형 및 변경은 당 분야에서의 통상의 지식을 가진 자에게 명백한 것이다.The present invention described above is not limited to the above-described embodiments and the accompanying drawings, and simple substitution, modification and alteration within the technical spirit of the present invention will be apparent to those skilled in the art.

본 발명에 따른 기능성 종이는 커피찌꺼기를 함유하는 기능성 원지에서 커피찌꺼기 분말의 노출을 방지할 수 있는 기능성 종이에 이용될 수 있다.The functional paper according to the present invention can be used in a functional paper capable of preventing the exposure of the coffee ground powder in the functional paper containing the coffee grounds.

100: 제1 원지(보호층) 200: 기능성 원지
300: 제2 원지(보호층) 400: 커버 층
S100: 커피찌꺼기 분쇄단계
S200: 혼합펄프 제작단계
S300: 기능성 원지 제작단계
S400: 보호층 형성단계100: first raw paper (protective layer) 200: functional raw paper
300: second paper (protective layer) 400: cover layer
S100: Coffee ground crushing step
S200: Mixed pulp production step
S300: Functional paper making step
S400: Step of forming protective layer

Claims (7)

커피찌꺼기를 함유하는 기능성 원지;
상기 기능성 원지의 일면에 열 압착 성형 내지 접착 성형으로 부착되어 상기 커피찌꺼기의 노출을 방지하는 제1 원지;
상기 기능성 원지의 타면에 열 압착 성형 내지 접착 성형으로 부착되어 상기 커피찌꺼기의 노출을 방지하는 제2 원지; 및
상기 기능성 원지와 상기 제1 원지 및 제2 원지 사이에 하나 이상 마련되되 소정 크기 이하 직경의 다공성 표면이 마련된 커버층; 을 포함하며,
상기 기능성 원지, 제1 원지 및 제2 원지를 합친 중량 대비, 상기 기능성 원지에 함유된 상기 커피찌꺼기의 총 중량 비율은 상기 기능성 원지의 용도와 두께에 따라 2 내지 10 퍼센트 사이에서 선택할 수 있으며,
상기 커피찌꺼기의 분말은 상기 기능성 원지의 펄프 제조과정에서 혼합되거나 기 성형된 상기 기능성 원지에 도포될 수 있으며,
상기 제1 원지 및 제2 원지는 정보전달 및 메시지 알람을 위한 그림 내지 도안을 포함하며,
상기 커버층은 투명한 재질로 마련되어 상기 기능성 원지의 표면에 도포 또는 코팅되거나 별도의 필름으로 부착되고, 두께는 상기 기능성 원지 내지 상기 제1 원지 및 제2 원지보다 작게 마련되되 0.001mm 내지 0.005mm로 마련되는 것을 특징으로 하는 기능성 종이.
Functional grounds containing coffee grounds;
A first raw paper adhered to one side of the functional raw paper by thermo compression molding or adhesive molding to prevent exposure of the coffee residue;
A second raw paper adhered to the other surface of the functional raw paper by thermo compression molding or adhesive molding to prevent exposure of the coffee grounds; And
A cover layer provided on at least one surface of the functional fabric, between the first raw paper and the second raw paper, and having a porous surface with a diameter of a predetermined size or less; / RTI >
The total weight ratio of the coffee grounds contained in the functional raw paper to the combined weight of the functional raw paper, the first raw paper and the second raw paper may be selected from 2 to 10 percent depending on the use and thickness of the functional raw paper,
The powder of the coffee grounds may be applied to the functional raw paper mixed or molded in the pulp manufacturing process of the functional raw paper,
The first original and the second original include a picture or a figure for information transmission and a message alarm,
The cover layer is made of a transparent material and is coated or coated on the surface of the functional raw paper or is attached as a separate film. The thickness of the cover layer is smaller than the functional raw paper, the first raw paper and the second raw paper and is set to 0.001 mm to 0.005 mm Wherein the functional paper is a paper.
삭제delete 삭제delete 삭제delete 기능성 종이의 제조방법에 있어서,
커피찌꺼기를 소정 크기 이하의 분말로 그라인딩 하는 단계;
상기 분말을 이용하여 펄프를 마련하는 단계;
상기 펄프를 이용하여 기능성 원지를 제작하는 단계;
상기 기능성 원지를 사이에 두고 제1 원지 및 제2 원지를 서로 합지하여 보호층을 형성하는 단계; 및
상기 기능성 원지와 상기 제1 원지 및 제2 원지 사이에 하나 이상 마련되되 소정 크기 이하 직경의 다공성 표면이 마련된 커버층을 마련하는 단계; 를 포함하며,
상기 기능성 원지, 제1 원지 및 제2 원지를 합친 중량 대비, 상기 기능성 원지에 함유된 상기 커피찌꺼기의 총 중량 비율은 상기 기능성 원지의 용도와 두께에 따라 2 내지 10 퍼센트 사이에서 선택할 수 있으며,
상기 커피찌꺼기의 분말은 상기 기능성 원지의 펄프 제조과정에서 혼합되거나 기 성형된 상기 기능성 원지에 도포될 수 있으며,
상기 제1 원지 및 제2 원지는 정보전달 및 메시지 알람을 위한 그림 내지 도안을 포함하며,
상기 커버층은 투명한 재질로 마련되어 상기 기능성 원지의 표면에 도포 또는 코팅되거나 별도의 필름으로 부착되고, 두께는 상기 기능성 원지 내지 상기 제1 원지 및 제2 원지보다 작게 마련되되 0.001mm 내지 0.005mm로 마련되는 것을 특징으로 하는 기능성 종이의 제조방법.
In the method for producing a functional paper,
Grinding the coffee grounds to powder of a predetermined size or less;
Providing a pulp with the powder;
Preparing a functional paper using the pulp;
Forming a protective layer by laminating the first raw paper and the second raw paper with the functional raw paper interposed therebetween; And
Providing a cover layer having at least one porous surface with a diameter of a predetermined size or less between the functional fabric and the first raw paper and the second raw paper; / RTI >
The total weight ratio of the coffee grounds contained in the functional raw paper to the combined weight of the functional raw paper, the first raw paper and the second raw paper may be selected from 2 to 10 percent depending on the use and thickness of the functional raw paper,
The powder of the coffee grounds may be applied to the functional raw paper mixed or molded in the pulp manufacturing process of the functional raw paper,
The first original and the second original include a picture or a figure for information transmission and a message alarm,
The cover layer is made of a transparent material and is coated or coated on the surface of the functional raw paper or is attached as a separate film. The thickness of the cover layer is smaller than the functional raw paper, the first raw paper and the second raw paper and is set to 0.001 mm to 0.005 mm Wherein the functional paper has a thickness of 100 mu m or less.
삭제delete 삭제delete
KR1020170047700A 2017-04-13 2017-04-13 Method for manufacturing functional paper from coffee-grounds KR101904854B1 (en)