KR101902546B1 - Manufacturing method of composite nonwovens sheet for mask pack - Google Patents
Manufacturing method of composite nonwovens sheet for mask pack Download PDFInfo
- Publication number
- KR101902546B1 KR101902546B1 KR1020170109772A KR20170109772A KR101902546B1 KR 101902546 B1 KR101902546 B1 KR 101902546B1 KR 1020170109772 A KR1020170109772 A KR 1020170109772A KR 20170109772 A KR20170109772 A KR 20170109772A KR 101902546 B1 KR101902546 B1 KR 101902546B1
- Authority
- KR
- South Korea
- Prior art keywords
- web material
- composite
- mask pack
- nonwoven fabric
- spandex
- Prior art date
Abstract
Description
본 발명은 마스크팩용 복합부직포시트의 제조방법에 관한 것으로서, 특히 중앙부에 신축성 및 유분흡수성이 우수한 스판덱스웹(spandex web)소재를 구성하고, 상기 스판덱스웹소재 양측면에 흡수성과 촉감이 우수한 셀롤로오스웹(cellulose web)소재가 위치되게 함으로서, 신축성과 흡습성이 우수한 고품질의 마스크팩용 복합부직포시트를 제조하는 것이다.The present invention relates to a method of manufacturing a composite nonwoven fabric sheet for a mask pack, and more particularly, to a spandex web material having excellent elasticity and oil absorption at the center, a cellulose web material is placed on the surface of the non-woven fabric sheet, thereby producing a composite nonwoven fabric sheet for a mask pack having excellent stretchability and hygroscopicity.
일반적으로 마스크팩용 시트의 제조는 편물지나, 거즈형태의 직물지, 혹은 부직포 등의 소재들이 널리 사용되고 있다. BACKGROUND ART [0002] Generally, fabrics such as knitted fabrics, gauze fabrics, and nonwoven fabrics are widely used in the production of sheets for mask packs.
최근에는 부직포를 소재로 한 제품들이 널리 사용되고 있으며, 부직포시트에 피부미용성분을 흡착시켜 사용되고 있으며, 현재 마스크팩의 개발추세는 주로 마스크팩에 첨가되는 피부미용성분들을 추가하거나 기능성을 향상시키는 연구가 활발히 진행되고 있는 반면에 마스크팩시트에 대한 개발은 다소 미흡한 것이 현실이다.In recent years, nonwoven fabric-based products have been widely used, and nonwoven fabric sheets have been used by absorbing skin cosmetic ingredients. Currently, the development trend of mask packs is mainly focused on adding skin cosmetic ingredients added to mask packs, The development of the mask pack sheet is somewhat inadequate.
부직포를 이용한 마스크팩시트와 관련한 선행기술을 검토하여 보면, 특허 제10-1149061호 "마스크팩용 키토산 부직포 및 이의 제조방법"(특허문헌 1)과, 특허 제10-1296105호 "하이드로겔화된 부직포, 이의 제조방법 및 이를 이용한 마스크팩"(특허문헌 2)과, 특허 제10-1690569호 "밀착성 및 닦음성능이 우수한 미용마스크팩용 부직포의 제조방법"(특허문헌 3) 등이 제시된바 있다.[0005] In consideration of the prior art relating to a mask pack sheet using a nonwoven fabric, Patent Document No. 10-1149061 entitled " Chitosan Nonwoven Fabric for Mask Pack and Method for Producing the Same "(Patent Document 1) and Patent No. 10-1296105" Hydrogelized Nonwoven Fabric, (Patent Document 2) and Patent No. 10-1690569 entitled " Method for manufacturing a nonwoven fabric for a beauty mask pack having excellent adhesion and wiping performance "(Patent Document 3) have been proposed.
상기 특허문헌 1의 기술내용을 검토하여 보면, 천연고분자인 불용성의 키토산고분자를 수용성의 하이드로겔화 키토산으로 개질하여 마스크팩재에 적용함으로서 우수한 피부미용효과와 향상된 물성 및 기능성을 지니도록 하는 것이다.When the insoluble chitosan polymer, which is a natural polymer, is modified with water-soluble hydrogelified chitosan and applied to a mask pack material, it has an excellent skin cosmetic effect and improved physical properties and functionality.
또한 특허문헌 2의 기술내용을 검토하여 보면, 20~30℃의 상온에서 하이드로겔을 에탄올에 분산시킨 후, 물과 혼합하여 제조되는 하이드로겔 수용액을 80~90℃로 가열시켜 겔화시키는 단계, 상기 겔화된 하이드로겔 수용액에 부직포를 함침시키는 단계, 상기 하이드로겔에 함침된 부직포를 나이프 코터기를 통과시켜 일정한 두께로 하이드로겔을 함침시키는 단계, 상기 하이드로겔화된 부직포를 180~190℃에서 분당 7m의 속도로 이동시키면서 열풍 건조시키는 단계 및 상기 건조된 하이드로겔화된 부직포를 롤러에 롤링시키는 단계를 포함하는 하이드로겔화된 부직포의 제조방법에 관한 것이다.In addition, when the technical contents of Patent Document 2 are examined, it is preferable that the hydrogel is dispersed in ethanol at a room temperature of 20 to 30 ° C and then mixed with water to gelate the hydrogel aqueous solution heated to 80 to 90 ° C, Impregnating the hydrogel nonwoven fabric with a nonwoven fabric by passing the nonwoven fabric impregnated in the hydrogel through a knife coater and impregnating the hydrogel with a predetermined thickness, heating the hydrogel nonwoven fabric at a speed of 7 m / min And drying the hot-air-dried nonwoven fabric. The hydrogel nonwoven fabric is then rolled on a roller.
특허문헌 3의 기술내용을 검토하여 보면, 미용 마스팩 용 부직포시트의 제조방법이 개시되며, 그 구성은 1~ 10 denier 바람직하게는 1.2 ~ 3denier의 PET(도)/CoPET(해) 해도형 나노필라멘트를 단섬유화하는 공정, 상기 단섬유를 혼타면, 소면공정을 거친 후에 웹을 형성하는 공정, 상기 웹에서 해성분을 용출하는 공정, 상기 웹을 적층하여 부직포화 하는 공정을 포함하는 것을 특징으로 한다. 본 발명의 방법에 의하여 제조된 미용 마스크팩 용 부직포 시트는 기존 시트형 미용 마스크 팩용 부직포보다 인강강도 및 신율과 같은 물리적 물성이 우수하며, 미세직경으로 인한 비표면적이 높아 피부 밀착력이 높고 사용 후 시트 제거 시 닦음 기능 발현이 가능하게 한 것이다.A method for manufacturing a nonwoven fabric sheet for cosmetics masks is disclosed. The composition of the nonwoven fabric sheet is 1 to 10 denier, preferably 1.2 to 3 denier PET / CoPET sea-island nano- A step of forming a filament into a short fiber, a step of forming a web after the short fibers are subjected to a surface treatment, a step of eluting a marine component in the web, and a step of laminating the web to form a nonwoven fabric do. The nonwoven fabric sheet for cosmetic mask packs manufactured by the method of the present invention is superior to the conventional nonwoven fabric for mask packs for beauty masks with physical properties such as tensile strength and elongation and has a high specific surface area due to a fine diameter, The wiping function can be expressed.
본 발명은 마스크팩용 복합부직포시트의 제조에 관한 것으로서, 특히 마스크팩용 복합부직포시트를 제조하되, 중앙부에 신축성과 유분흡수성이 우수한 웹소재를 구성하고, 상기 웹소재 양측면에 에센스흡수성과 수분저장성이 우수한 웹소재가 위치하는 3중구조로 하여, 뛰어난 신축성으로 에센스함침후에도 변형이 없고, 리프팅과 마사지효과는 물론, 피부밀착성이 우수하여 에센스에 함유된 영양성분이 효과적으로 피부에 전달될 수 있게 한 것이다.The present invention relates to a method for producing a composite nonwoven fabric sheet for a mask pack, and more particularly to a method for producing a composite nonwoven fabric sheet for a mask pack, which comprises a web material having excellent stretchability and oil absorbency at the center thereof and having excellent essence absorbability and water retention This is a triple combination in which the web material is located. The excellent stretchability makes it possible to effectively transmit nutrients contained in the essence without deformation even after the essence impregnation, and with lifting and massage effects as well as skin adhesion.
상기 과제를 해결하기 위한 수단으로서, 본 발명은 개면한 스판덱스섬유를 소면기(carding M/C)를 통하여 얇은 시트상의 스판덱스웹(spandex web)소재를 얻고, 다시 개면한 셀롤로오스섬유를 소면기(carding M/C)를 통하여 얇은 시트상의 셀롤로오스웹(cellulose web)소재를 얻고, 상기 스판덱스웹소재 양측에 셀롤로오스웹소재를 적층한 3층구조로 복합웹소재를 얻고, 상기 복합웹소재를 연신하고, 습윤하고, 고압워터펀칭을 통하여 일체화하고, 가압롤러로 1차탈수건조하고, 열풍건조기로 2차건조하여 마스크팩용 복합부직포시트를 얻고, 상기 마스크팩용 복합부직포시트를 재단하여 마스크팩 시트를 제조하는 것이다.As a means for solving the above-mentioned problems, the present invention provides a spandex web material obtained by thinning a spandex fiber through a carding machine (M / C), re- a composite web material having a three-layer structure obtained by obtaining a thin sheet-like cellulose web material through carding M / C and laminating a cellulosic web material on both sides of the spandex web material, The composite nonwoven fabric sheet for a mask pack was cut to obtain a mask nonwoven fabric sheet, which was then cut into a mask, To produce a pack sheet.
본 발명은 개면한 스판덱스섬유를 소면기(carding M/C)를 통하여 얇은 시트상의 스판덱스웹(spandex web)소재를 얻고, 다시 개면한 셀롤로오스섬유를 소면기(carding M/C)를 통하여 얇은 시트상의 셀롤로오스웹(cellulose web)소재를 얻고, 상기 스판덱스웹소재 양측에 셀롤로오스웹소재를 적층한 3층구조로 복합웹소재를 얻고, 상기 복합웹소재를 연신하고, 습윤하고, 고압워터펀칭을 통하여 일체화하고, 가압롤러로 1차탈수건조하고, 열풍건조기로 2차건조하여 마스크팩용 복합부직포시트를 얻고, 상기 마스크팩용 복합부직포시트를 재단하여 마스크팩시트를 제조하고, 상기 마스크팩시트에 피부미용성분(에센스)을 흡착시켜 마스크팩용도로 사용케 함으로서, 뛰어난 신축성으로 에센스함침후에도 변형이 없고, 리프팅과 마사지효과는 물론, 피부밀착성이 우수하여 에센스에 함유된 영양성분이 효과적으로 피부에 전달될 수 있게 하는 등의 효과가 있는 것이다.In the present invention, a spandex web material obtained from a thin sheet is obtained through a carding machine (M / C) by using a spandex fiber made in the present invention, and the cellulosic fiber is re- A composite web material is obtained in a three-layered structure in which a sheet-like cellulose web material is obtained and laminated on both sides of the spandex web material, the composite web material is stretched, wetted, Dried by a pressure roller to obtain a composite nonwoven fabric sheet for a mask pack to obtain a mask pack sheet by cutting the composite nonwoven fabric sheet for a mask pack, It absorbs the skin cosmetic ingredient (essence) on the sheet and is used for the mask pack application. With its excellent stretchability, there is no deformation even after essence impregnation, and lifting and massage effect as well as skin adhesion are excellent The nutrients contained in the essence that would have effects such as to be able to deliver effectively on the skin.
도 1 : 본 발명의 제조공정도
도 2 : 본 발명에 사용되는 스판덱스웹소재의 상태도
도 3 : 본 발명에 사용되는 셀롤로오스웹소재의 상태도
도 4 : 본 발명에서 스판덱스웹소재 양측면에 셀롤로오스웹소재를 적층시켜 제조한 복합웹소재의 상태도
도 5 : 도 4의 복합웹소재를 이용하여 제조한 마스크팩용 복합부직포시트의 상태도
도 6 : 도 5의 마스크팩용 복합부직포시트를 재단하여 제조한 마스크팩시트의 상태도Figure 1: Manufacturing process diagram of the present invention
2: State diagram of the spandex web material used in the present invention
3: State diagram of cellulosic web material used in the present invention
Figure 4: State of composite web material prepared by laminating cellulosic web material on both sides of spandex web material in the present invention
Figure 5: State of composite nonwoven fabric sheet for mask packs manufactured using composite web material of Figure 4
6: State of the mask pack sheet produced by cutting the composite nonwoven fabric sheet for a mask pack of Fig. 5
이하 본 발명의 실시예를 첨부도면에 따라 상세히 설명한다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings.
본 발명은 마스크팩용 복합부직포시트의 제조에 관한 것으로서, 스판덱스섬유로 스판덱스웹(spandex web)소재를 얻고, 상기 스판덱스웹소재 양측에 셀롤로오스섬유로 제조된 셀롤로오스웹(cellulose web)소재를 적층한 다음 고압워터펀칭하고, 가압건조하여 마스크팩용 복합부직포시트를 제조하고, 제조된 마스크팩용 복합부직포시트를 원하는 모양으로 재단하여 마스크팩시트로 사용할 수 있게 한 것이다.The present invention relates to the production of a composite nonwoven fabric sheet for a mask pack, which comprises a spandex web material obtained from spandex fibers, a cellulose web material made of cellulosic fibers on both sides of the spandex web material, Pressure water punching, pressure drying to produce a composite nonwoven fabric sheet for a mask pack, and the resulting composite nonwoven fabric sheet for a mask pack can be cut into a desired shape and used as a mask pack sheet.
본 발명에 사용되는 스판덱스섬유는 장섬유(filament)형태의 스판덱스섬유를 30~60㎜정도의 길이로 절단한 단섬유(stable fiber)형태의 스판덱스섬유를 사용하며, 셀롤로오스섬유의 경우에도, 발명에서는 주로 재생셀롤로오스섬유를 하되, 재생셀롤로오스섬유 역시 30~60㎜정도의 길이로 절단한 단섬유를 사용하며, 원사공장에서 제조된 솜형태의 소재를 구매하여 사용한다. The spandex fiber used in the present invention is a spandex fiber in the form of a staple fiber obtained by cutting a filament spandex fiber into a length of about 30 to 60 mm. In the case of the cellulosic fiber, In the invention, regenerated cellulosic fibers are mainly used, and regenerated cellulose fibers are also cut to a length of about 30 to 60 mm. Cotton-like materials produced in yarn factories are used for the purchase.
구매된 스판덱스섬유 및 셀롤로오스섬유는 압축된 상태로 유통이 되므로 개면을 통하여 솜풀기하여 원활한 소면작업이 될 수 있게 한다.The purchased spandex fiber and cellulosic fiber are flowed in a compressed state, so that they can be unwound through the opening to make a smooth surface operation.
본 발명에 적용되는 스판덱스섬유의 섬도는 0.7~0.9데니어, 셀롤로오스섬유는 1~1.3데니어가 적합하다.The fineness of the spandex fiber according to the present invention is preferably 0.7 to 0.9 denier, and the cellulosic fiber is preferably 1 to 1.3 denier.
개면된 스판덱스섬유 및 셀롤로오스섬유를 별도의 소면기(carding M/C)에 투입하여, 얇은 시트상의 스판덱스웹소재(10)와 셀롤로오스웹소재(20)를 얻는다.The opened spandex fiber and the cellulosic fiber are put into a separate carding machine (carding M / C) to obtain a thin sheet-like
소면공정에서 얻어진 웹소재는 스판덱스웹소재(10)를 중심으로 상하부에 셀롤로오스웹소재(20)를 적층하여 3층구조의 복합웹소재(30)를 얻는다.In the web material obtained in the process of the cotton process, the
이때 스판덱스웹소재(10)를 기준으로 상하부에 셀롤로오스웹소재(20)를 적층하는 것은 형태안정성과 기능성 때문이다.The lamination of the
즉 신축성과 탄성이 우수한 스판덱스웹소재(10)를 기준으로 양측에 셀롤로오스웹소재(20)가 위치되게 함으로서, 스판덱스웹소재(10)의 신축성을 이용할때, 양측에 위치한 셀롤로오스웹소재(20)가 피동적으로 신축되게 함으로서, 소재의 틀림을 방지케 함과 동시에, 피부미용성분(에센스)의 흡착성 및 수분저장성이 우수한 셀롤로오스섬유가 외면에 위치되게 하고, 피부미용성분에 함유된 유분흡수성과 수분보호기능이 우수한 스판덱스섬유가 내면에 위치되게 하여 마스크팩효과를 높이기 위한 것이다.In other words, when the elasticity of the
상기에서 얻어진 복합웹소재(30)는 연신과정을 통하여 복합웹소재(30)의 두께를 줄이면서 각 섬유소재들이 전면에 걸쳐 고르게 분포되게 한다.The
연신과정을 거친 복합웹소재(30)는 습윤과정을 통하여 복합웹소재 중량대비 7~10%정도의 수분이 함유되게 하여, 고압워터펀칭과정에서 섬유의 반발력을 최소화함과 동시에 섬유간의 원활한 결속이 이루어질 수 있게 하는 것이다.The
연신, 습윤과정을 마친 복합웹소재(10)는 고압워터펀칭과정을 통하여 3단으로 적층된 웹소재의 단섬유들이 서로 엉키면서 결속되어 형태안정성이 부여되게 한다.After the stretching and wetting processes, the
고압워터펀칭과정을 통하여 다층으로 적층된 복합웹소재의 단섬유들이 서로 결속된 상태에서 가압롤러를 통하여 가열가압하여 부풀어오른 상태, 즉 벌키성 상태의 복합웹소재(30)를 부직포형태로 얇고 평활한 상태로 가공한 다음, 열풍건조하여 마스크팩용 복합부직포시트(40)를 제조한다.The
상기 공정에서 가압롤러의 온도는 120~130℃로 가열되게 함으로서, 고압워터펀칭과정에서 흡착된 물을 탈수함과 동시에 예비건조되게 하며, 열풍건조는 열풍건조기를 이용하되, 110~140℃에서 완전건조한다.In this process, the temperature of the pressurizing roller is heated to 120 to 130 ° C so that the adsorbed water is dewatered and preliminarily dried in the high pressure water punching process. The hot air drying is performed using a hot air drier at 110 to 140 ° C Dry.
상기 과정에서 제조된 마스크팩용 복합부직포시트(40)의 중량은 45~55g/㎡, 두께는 0.2~0.4㎜로 유지되게 한다.The weight of the composite
상기에서 중량이 45g/㎡이하이면 밀도가 성글어 피부미용성분 및 수분흡착율이 반감되고, 55g/㎡이상이면 밀도가 높아 유연성이 떨어지게 된다.When the weight is less than 45 g / m 2, the skin cosmetic ingredients and moisture adsorption rate are reduced by half, and when the weight is more than 55 g / m 2, the density is high and the flexibility is low.
또한 두께가 0.2㎜이하이면 마스크팩시트에 피부미용성분의 흡착량이 반감될 뿐 아니라, 형태유지가 어려워 사용에 불편함이 있고, 0.4㎜이상이면 흡착성은 증진되나, 밀착성이 떨어지기 때문에 바람직하지 않다.If the thickness is 0.2 mm or less, the amount of skin cosmetic ingredients adsorbed on the mask pack sheet is reduced by half, and shape maintenance is difficult, which is inconvenient for use. On the other hand, if the thickness is 0.4 mm or more, the adsorption property is improved, .
상기에서 제조된 마스크팩용 복합부직포시트(40)는 롤상태로 권취한 다음 포장하고 상품화하여 별도의 재단공정을 통하여 마스크팩시트(50)를 제조하거나, 연속공정을 통하여 원하는 형태로 재단하여 마스크팩시트(50)를 제조할 수 있다.The composite
상기에서 제조된 마스크팩시트(50)에 피부미용성분(에센스)과 함께 필요한 기능성 성분을 흡착시켜 마스크팩 용도로 사용하게 된다.The
본 발명에서 제조된 마스크팩용 복합부직포시트(40)는 제조과정에서 설명한 바와 같이 섬도 0.7~0.8데니어 스판덱스섬유를 소면(carding)하여 제조한 스판덱스웹소재(10) 상하부에, 섬도 1~1.3데니어 셀롤로오스섬유를 소면(carding)하여 제조한 셀롤로오스웹소재(20)를 적층하여 복합웹소재(30)를 얻고, 상기 복합웹소재(30)를 연신, 습윤, 고압워터펀칭, 롤러가압건조, 열풍건조하여 제조한 것이다.The composite
따라서 마스크팩용 복합부직포시트(40)는 내면에 신축성과 탄성이 풍부하고, 유분흡수성과 수분저장성이 우수한 스판덱스섬유가 위치하고 있고, 스판덱스섬유 양측면에 흡수성과 수분저장이 우수한 천연소재의 셀롤로오스섬유가 위치하고 있어, 마스크팩시트(50)로 재단한 다음, 피부미용성분(에센스)과 함께 기능성 성분을 흡착시키게 되면 다음과 같이 작용하게 된다.Therefore, the composite
즉 내면에 위치하는 스판덱스섬유가 피부미용성분, 즉 에센스에 함유된 유분과 수분을 효과적으로 흡수하게 되고, 양측면에 위치하는 셀롤로오스섬유가 피부미용성분과 기능성 성분, 즉 에센스성분과 수분을 흡수하여 저장하게 된다.That is, the spandex fiber located on the inner surface effectively absorbs the skin cosmetic ingredient, i.e. oil and moisture contained in the essence, and the cellulosic fibers located on both sides absorb the skin cosmetic ingredient and the functional ingredient, i.e., essence ingredient and moisture .
특히 마스크팩시트(50) 내면에 위치하는 스판덱스웹소재(10)의 탄성과 신축성에 의해 피부미용성분을 흡착시키더라도 마스크팩시트(50)가 처지거나 변형되는 현상없이 형태안정성을 유지할 수 있다.In particular, even if the skin cosmetic ingredients are adsorbed by the elasticity and stretchability of the
또한 마스크팩시트(50)를 얼굴에 붙일때 원하는 방향으로 가볍게 당긴 다음 피부에 밀착시켜 주면 늘어났던 스판덱스섬유가 수축하게 되므로 리프팅과 마사지효과를 기대할 수 있고, 피부와의 접촉성을 향상시켜 피부미용성분의 흡수를 높일 수 있다.In addition, when the
(10)--스판덱스웹소재 (20)--셀롤로오스웹소재
(30)--복합웹소재 (40)--복합부직포시트
(50)--마스크팩시트(10) - Spandex web material (20) - Cellulose web material
(30) - Composite web material (40) - Composite nonwoven sheet
(50) - mask pack sheet
Claims (2)