KR101874845B1 - Conjugated fiber for melange effect and method preparing same - Google Patents
Conjugated fiber for melange effect and method preparing same Download PDFInfo
- Publication number
- KR101874845B1 KR101874845B1 KR1020160038304A KR20160038304A KR101874845B1 KR 101874845 B1 KR101874845 B1 KR 101874845B1 KR 1020160038304 A KR1020160038304 A KR 1020160038304A KR 20160038304 A KR20160038304 A KR 20160038304A KR 101874845 B1 KR101874845 B1 KR 101874845B1
- Authority
- KR
- South Korea
- Prior art keywords
- polyester
- polyamide
- based resin
- composite fiber
- cross
- Prior art date
Abstract
본 발명은 폴리아미드계 수지와 폴리에스테르계 수지로 형성되어 폴리아미드부와 폴리에스테르부로 구성되는 복합섬유에 있어서, 상기 폴리아미드부는 상대점도(RV) 2.5~3.3인 폴리아미드계 수지로 형성되고, 상기 폴리에스테르부는 고유점도(IV) 0.5~0.8dL/g인 폴리에스테르계 수지로 형성되되, 상기 복합섬유는 사이드 바이 사이드 형의 이형단면으로 형성되고, 상기 폴리아미드부와 폴리에스테르부는 섬유 제조후 분리되는 Melange용 복합섬유 및 그의 제조방법에 관한 것이다.The present invention relates to a composite fiber formed from a polyamide-based resin and a polyester-based resin and comprising a polyamide portion and a polyester portion, wherein the polyamide portion is formed of a polyamide-based resin having a relative viscosity (RV) Wherein the polyester part is formed of a polyester resin having an intrinsic viscosity (IV) of 0.5 to 0.8 dL / g, the composite fiber is formed as a side-by-side type modified cross section, and the polyamide part and the polyester part And a method for producing the same.
Description
본 발명은 폴리아미드부와 폴리에스테르부로 형성되고 복합섬유 제조 후에 폴리아미드부와 폴리에스테르부를 분리시켜 폴리아미드와 폴리에스테르의 염색성 차이를 더욱 높여 Melange용 복합섬유에 관한 것이다.The present invention relates to a composite fiber for melange which is formed of a polyamide part and a polyester part and further separates the polyamide part and the polyester part after the production of the composite fiber to further increase the difference in dyeability between the polyamide and the polyester.
통상적으로 멜란지 효과는 혼합된, 섞인 등의 의미로 서로 다른 색이 혼합하여 서리가 내린 것과 같은 효과를 내는 배색 상태를 말하는 것으로, 섬유분야에서는 다양한 색상이 혼합된 것과 같은 효과로 섬유에 부드러운 촉감을 부여하고 광택의 고급스러움을 나타내는 용어로 사용된다.Typically, the melange effect refers to a state of color that produces the same effect as a frost blended with a mixture of different colors in the sense of mixed, mixed, etc. In the field of fibers, It is used as a gloss to the quality of the gloss.
종래의 기술에서 이러한 멜란지 효과를 부여하기 위한 다양한 방법들이 제안되어왔다. Various methods for imparting such a melange effect have been proposed in the prior art.
예를 들어 대한민국 공개특허 제2003-0083577호의 "멜란지 효과가 우수한 이수축 혼섬사 및 그의 제조방법"은 "염색특성이 서로 상이한 2종(種) 이상의 섬유형성성 성분으로 구성된 2성분 복합사 또는 섬유형성성 성분과 용출성분으로 구성되며 섬유형성성 성분의 염색특성이 서로 상이한 2개 이상의 2성분 복합사가 열가소성 멀티필라멘트를 휘감고 있는 형태를 갖고, 상기 2성분 복합사는 분할 또는 용출성분 용출후에 0.001∼0.3데니어의 단사섬도를 가지며, 혼섬사 표면에 길이가 1.0mm 이상인 상기 2성분 복합사 루프가 2∼350개/m 형성되어 있으며, 길이가 1.0mm이상인 상기 2성분 복합사 루프의 95% 이상이 1.0∼2.5mm의 길이를 갖는 것을 특징으로 하는 멜란지 효과가 우수한 이수축 혼섬사"를 개시하고 있다.For example, Korean Patent Laid-Open Publication No. 2003-0083577, entitled " This method for producing a shrinkable horny yarn excellent in melange effect ", and a process for producing the shrinkable horny yarn are disclosed in "a two-component composite yarn or fiber composed of two or more kinds of fiber- Wherein at least two two-component composite yarns composed of a forming component and an eluting component and having different dyeing characteristics of the fiber-forming component are wrapped around the thermoplastic multifilament, and the two-component composite yarn has a shape of 0.001 to 0.3 Wherein at least 95% of the two-component composite yarn loops having a length of 1.0 mm or more are formed of 1.0 to 1.0 mm in length, ≪ / RTI > which has an excellent melange effect and has a length of 2 to 2.5 mm.
또한, 대한민국 공개특허 제2006-0087684호는 카티온 염료로 염색이 가능하여 멜란지톤 신축성 직편물을 제조하는데 유용한 복합사를 제공하기 위하여, "서로 다른 2개의 폴리에스테르계 폴리머들이 복합되어 있는 폴리에스테르계 2성분 복합사에 있어서, 상기 2성분 중 한성분은 폴리에틸렌테레프탈레이트이고, 다른 한성분은 일반식(Ⅰ)의 구조를 갖는 화합물이 공중합되어 있는 카치온염료 가염형 공중합 폴리에스테르인 것을 특징으로 하는 멜란지 효과를 가진 잠재권축형 폴리에스테르 2성분 복합사"를 개시하고 있다.Korean Patent Laid-Open Publication No. 2006-0087684 discloses a polyester which is capable of dyeing with a cationic dye to provide a composite yarn useful for producing a melanchthon stretchable knitted fabric, wherein "polyester having two different polyester- Wherein the one component of the two components is polyethylene terephthalate and the other component is a cationic dye-halogenated copolymer polyester in which a compound having the structure of the general formula (I) is copolymerized Quot; latent crimped polyester two-component composite yarn having a melange effect ".
그러나, 상기 대한민국 공개특허 제2003-0083577호의 방법은 2단계로 복합사를 제조하는 것으로 그 공정이 복잡하고, 고가의 개질칩을 사용하므로 인하여 제조원가가 상승하는 문제점이 있고, 대한민국 공개특허 제2006-0087684호의 방법 또한 고가의 개질칩을 사용할 뿐 아니라 방사의 어려움이 있다는 문제점이 있다. However, the method disclosed in Korean Patent Laid-Open Publication No. 2003-0083577 has a problem in that the manufacturing cost is increased due to the use of a complicated and expensive reforming chip to produce a composite yarn in two steps, The method of No. 0087684 also has the problem of not only using expensive reforming chips but also having difficulty in spinning.
또한, 대한민국 공개특허 제2008-0008742호의 "우수한 멜란지 효과를 가지는 아세테이트섬유조폴리에스테르 공기교락사의 제조방법"은 "제 1사로 편평단면 폴리에스테르 멀티필라멘트사를 사용하고, 제 2사로 굴곡형단면 폴리에스테르 멀티필라멘트사를 사용하여 인터레이싱(INTERLACING)시키되, 제 1사와 제 2사의 총섬도가 각각 40~150데니어인 것을 사용하며 제 1사와 제 2사의 중량비가 35:65~65:35가 되도록 제조하는 것을 특징으로 하는 우수한 멜란지 효과를 나타내는 아세테이트 섬유조 폴리에스테르 공기교락사의 제조방법"을 개시하고 있으나, 이 방법은 2단계로 복합사를 생산하는 방법으로 농담효과가 떨어지는 문제점이 있다.In addition, Korean Patent Laid-Open No. 2008-0008742, "a method for producing an acetate fiber-reinforced polyester air entangled yarn having excellent melange effect ", uses" a yarn having a flat cross-section polyester multifilament yarn as a first warp yarn, The first and second yarns having a total fineness of 40 to 150 denier were used and the weight ratio of the first yarn and the second yarn was 35:65 to 65:35. A method of producing an acetate fiber-clad polyester air entangled yarn exhibiting excellent melange effect, which is characterized by the fact that the method produces a composite yarn in two steps.
본 발명은 상기와 같은 종래 기술의 문제점을 해결하기 위해 발명된 것으로 염색성이 다른 폴리아미드계 수지와 폴리에스테르계 수지를 이용한 복합섬유를 통해 자연스럽고 고급스러운 멜란지 효과를 부여할 수 있는 Melange용 복합섬유를 제공하는 것을 목적으로 한다.Disclosure of Invention Technical Problem [8] Accordingly, the present invention has been made keeping in mind the above problems occurring in the prior art, and it is an object of the present invention to provide a composite fiber using a polyamide resin and a polyester resin having different dyeability, And to provide the above-mentioned objects.
또한, 폴리아미드계 수지는 폴리아미드부를 형성하고 폴리에스테르계 수지는 폴리에스테르부를 형성하여 복합섬유로 제조 후에 상기 폴리아미드부와 폴리에스테르부를 분리시켜 자연스러운 투톤효과가 발생되는 Melange용 복합섬유를 제공하는 것을 목적으로 한다.Further, the polyamide-based resin forms a polyamide portion, and the polyester-based resin forms a polyester portion to form a composite fiber, and then separates the polyamide portion and the polyester portion to provide a natural two-tone effect. .
또한, 폴리아미드계 수지와 폴리에스테르계 수지를 이용하여 Melange용 복합섬유의 제조방법을 제공하는 것을 목적으로 한다.Another object of the present invention is to provide a method for producing a composite fiber for melange using a polyamide-based resin and a polyester-based resin.
본 발명은 폴리아미드계 수지와 폴리에스테르계 수지로 형성되어 폴리아미드부와 폴리에스테르부로 구성되는 복합섬유에 있어서, 상기 폴리아미드부는 상대점도(RV) 2.5~3.3인 폴리아미드계 수지로 형성되고, 상기 폴리에스테르부는 고유점도(IV) 0.5~0.8dL/g인 폴리에스테르계 수지로 형성되되, 상기 복합섬유는 사이드 바이 사이드 형의 이형단면으로 형성되고, 상기 폴리아미드부와 폴리에스테르부는 섬유 제조후 분리되는 것을 특징으로 하는 Melange용 복합섬유를 제공한다.The present invention relates to a composite fiber formed from a polyamide-based resin and a polyester-based resin and comprising a polyamide portion and a polyester portion, wherein the polyamide portion is formed of a polyamide-based resin having a relative viscosity (RV) Wherein the polyester part is formed of a polyester resin having an intrinsic viscosity (IV) of 0.5 to 0.8 dL / g, the composite fiber is formed as a side-by-side type modified cross section, and the polyamide part and the polyester part The composite fiber for melange is characterized in that it is separated.
또한, 상기 복합섬유는 사이드-바이-사이드 형의 십자단면 또는 편평단면으로 형성되는 것을 특징으로 하는 Melange용 복합섬유를 제공한다.In addition, the composite fibers may be cross-sectional or side-by-side cross-section or flat cross-section.
또한, 상기 폴리아미드계 수지는 나일론 6, 나일론 66, 나일론 610 중 어느 하나인 것을 특징으로 하는 Melange용 복합섬유를 제공한다.Also, the polyamide-based resin is one of nylon 6, nylon 66, and nylon 610.
또한, 상기 폴리에스테르계 수지는 폴리에틸렌테레프탈레이트, 폴리트리메틸렌테레프탈레이트, 폴리부틸렌테레프탈레이트 중 어느 하나인 것을 특징으로 하는 Melange용 복합섬유를 제공한다.The present invention also provides a composite fiber for melange characterized in that the polyester resin is any one of polyethylene terephthalate, polytrimethylene terephthalate and polybutylene terephthalate.
또한, 상기 폴리아미드부와 폴리에스테르부는 중량비 30:70~70:30으로 형성되는 것을 특징으로 하는 Melange용 복합섬유를 제공한다.Also, the present invention provides the composite fiber for melange, wherein the polyamide portion and the polyester portion are formed in a weight ratio of 30:70 to 70:30.
또한, 본 발명은 폴리아미드계 수지와 폴리에스테르계 수지로 형성되어 폴리아미드부와 폴리에스테르부로 구성되는 복합섬유의 제조방법에 있어서, 상기 폴리아미드부는 상대점도(RV) 2.5~3.3인 폴리아미드계 수지, 상기 폴리에스테르부는 고유점도(IV) 0.5~0.8dL/g인 폴리에스테르계 수지를 사이드 바이 사이드형 복합방사구금을 통해 복합섬유로 섬유화단계; 및, 상기 복합섬유를 알카리 용액에서 폴리아미드부와 폴리에스테르부를 분리하는 분리단계를 포함하여 제조되는 것을 특징으로 하는 Melange용 복합섬유 제조방법을 제공한다.The present invention also provides a method for producing a composite fiber comprising a polyamide resin and a polyester resin and comprising a polyamide part and a polyester part, wherein the polyamide part is a polyamide resin having a relative viscosity (RV) Resin, the polyester part is fiberized with a conjugate fiber through a side-by-side composite spinneret, the polyester resin having an intrinsic viscosity (IV) of 0.5 to 0.8 dL / g; And a separating step of separating the polyamide and polyester from the composite fiber in an alkali solution.
또한, 상기 사이드 바이 사이드형 복합방사구금은 십자단면 또는 편평단면인 것을 특징으로 하는 Melange용 복합섬유 제조방법을 제공한다.In addition, the side-by-side composite spinneret has a cross-section or a flat cross-section.
본 발명은 상기와 같이 염색성에서 차이가 있는 폴리아미드계 수지와 폴리에스테르계 수지로 형성되어 폴리아미드부와 폴리에스테르부로 구성되는 복합섬유로 개질이나 별도의 후가공없이도 자연스럽고 고급스러운 멜란지 효과를 부여할 수 있는 효과가 있다.The present invention relates to a composite fiber composed of a polyamide-based resin and a polyester-based resin, which is formed of a polyamide-based resin and a polyester-based resin having different dyability as described above, and provides a natural and luxurious melange effect without modification or post- There is an effect that can be.
또한, 상기 폴리아미드계 수지는 폴리아미드부를 형성하고 폴리에스테르계 수지는 폴리에스테르부를 형성하여 복합섬유로 제조 후에 상기 폴리아미드부와 폴리에스테르부를 분리시켜 자연스러운 투톤효과가 발생되는 효과가 있다.In addition, the polyamide-based resin forms a polyamide portion, and the polyester-based resin forms a polyester portion, and after the polyamide-based resin is formed into a composite fiber, the polyamide portion and the polyester portion are separated to produce a natural two-tone effect.
또한, 본 발명의 Melange용 복합섬유는 원형단면이 아닌 이형단면형태로 제조되어 멜란지 효과뿐만 아니라 광택이 우수한 효과가 있다.In addition, the composite fiber for melange of the present invention is produced in an irregular cross-sectional shape instead of a circular cross-section, and has an effect of not only a melange effect but also an excellent gloss.
도 1은 본 발명의 Melange용 복합섬유의 제조에 사용되는 십자형 이형단면의 방사구금을 예시한 도면이다.
도 2는 본 발명의 Melange용 복합섬유의 제조에 사용되는 편평형 이형단면의 방사구금을 예시한 도면이다.
도 3은 도 1의 십자형 이형단면 방사구금을 이용하여 제조된 분리단계 전의 복합섬유를 나타낸 사진이다.
도 4는 도 3의 복합섬유를 분리단계 후의 상태를 나타낸 사진이다.BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a cross-sectional view showing a spinneret having a cross-shaped cross-section for use in the production of the composite fiber for melange of the present invention.
Fig. 2 is a view showing a spinneret having a flat cross-sectional shape used in the production of the composite fiber for melange of the present invention.
FIG. 3 is a photograph showing the composite fiber before the separation step, which is manufactured by using the cross-shaped cross-section spinneret of FIG. 1;
4 is a photograph showing the state after the step of separating the composite fibers of Fig.
이하 본 발명의 바람직한 일실시예를 상세히 설명하기로 한다. 본 발명을 설명함에 있어, 관련된 공지기능 혹은 구성에 대한 구체적인 설명은 본 발명의 요지를 모호하지 않게 하기 위하여 생략한다.Hereinafter, a preferred embodiment of the present invention will be described in detail. In the following description of the present invention, a detailed description of known functions and configurations incorporated herein will be omitted so as to avoid obscuring the subject matter of the present invention.
본 명세서에서 사용되는 정도의 용어 “약”, “실질적으로” 등은 언급된 의미에 고유한 제조 및 물질 허용오차가 제시될 때 그 수치에서 또는 그 수치에 근접한 의미로 사용되고, 본 발명의 이해를 돕기 위해 정확하거나 절대적인 수치가 언급된 개시 내용을 비양심적인 침해자가 부당하게 이용하는 것을 방지하기 위해 사용된다.The terms " about ", " substantially ", etc. used to the extent that they are used herein are intended to be taken to mean an approximation of, or approximation to, the numerical values of manufacturing and material tolerances inherent in the meanings mentioned, Accurate or absolute numbers are used to help prevent unauthorized exploitation by unauthorized intruders of the referenced disclosure.
도 1은 본 발명의 Melange용 복합섬유의 제조에 사용되는 십자형 이형단면의 방사구금을 예시한 도면이고, 도 2는 본 발명의 Melange용 복합섬유의 제조에 사용되는 편평형 이형단면의 방사구금을 예시한 도면이며, 도 3은 도 1의 십자형 이형단면 방사구금을 이용하여 제조된 분리단계 전의 복합섬유를 나타낸 사진이고, 도 4는 도 3의 복합섬유를 분리단계 후의 상태를 나타낸 사진이다.FIG. 1 is a cross-sectional view showing a cross-section of a cruciform shaped cross section used in the production of the composite fiber for melange of the present invention, and FIG. 2 is a cross-sectional view showing a spinneret having a flat cross- FIG. 3 is a photograph showing the composite fiber before the separation step, which is manufactured by using the spinneret having a cross-shaped modified cross section shown in FIG. 1, and FIG. 4 is a photograph showing a state after the separation step of the composite fiber of FIG.
본 발명은 폴리아미드계 수지와 폴리에스테르계 수지로 형성되어 폴리아미드부와 폴리에스테르부로 구성되는 복합섬유로 폴리아미드계 수지와 폴리에스테르계 수지의 염색성의 차이를 통해 Melange용 복합섬유에 관한 것이다.The present invention relates to a composite fiber composed of a polyamide-based resin and a polyester-based resin and composed of a polyamide portion and a polyester portion, and relates to a composite fiber for melange through a difference in dyeability between a polyamide-based resin and a polyester-
일반적으로 고분자 수지는 상대점도 또는 고유점도 등의 점도에 따라 분자량, 고분자의 융점, 강도 등의 물성을 판단할 수 있는 값으로 본 발명의 상기 폴리아미드계 수지는 상대점도(RV)가 2.5~3.3인 것이 바람직하며, 폴리에스테르계 수지는 고유점도(IV) 0.5~0.8dL/g인 것이 바람직할 것이다.Generally, the polymer resin is a value that can determine the physical properties such as molecular weight, melting point and strength of the polymer according to viscosity such as relative viscosity or intrinsic viscosity. The polyamide resin of the present invention has a relative viscosity (RV) of 2.5 to 3.3 , And the polyester resin preferably has an intrinsic viscosity (IV) of 0.5 to 0.8 dL / g.
본 발명에서 사용할 수 있는 상기 폴리아미드계 수지는 나일론 6, 나일론 66, 나일론 610 등 현재 출시중이거나 개발된 폴리아미드계 수지는 어느 것이나 사용할 수 있으며, 바람직하게는 나일론 6이나 나일론 66을 사용할 수 있을 것이다.The polyamide-based resin that can be used in the present invention may be any of polyamide-based resins currently in development or developed, such as nylon 6, nylon 66, and nylon 610, and preferably nylon 6 or nylon 66 will be.
또한, 본 발명에서 사용할 수 있는 상기 폴리에스테르계 수지는 폴리에틸렌테레프탈레이트(Polyethylene Terephthalate, PET), 폴리트리메틸렌테레프탈레이트(Polytrimethylene Terephthalate, PTT), 폴리부틸렌테레프탈레이트(Polybutylene Terephthalate, PBT) 등 폴리아미드계 수지와 같이 현재 출시중이거나 개발된 폴리에스테르계 수지를 사용할 수 있으나 바람직하게는 폴리에틸렌테레프탈레이트을 사용할 수 있을 것이다.The polyester resin that can be used in the present invention may be selected from the group consisting of polyethyleneterephthalate (PET), polytrimethylene terephthalate (PTT), polybutylene terephthalate (PBT) Based resin may be used, but polyethylene terephthalate may be preferably used.
본 발명의 폴리아미드계 수지와 폴리에스테르계 수지로 형성되어 폴리아미드부와 폴리에스테르부로 구성되는 복합섬유는 사이드 바이 사이드 형의 이형단면으로 형성되고 상기 폴리아미드부와 폴리에스테르부는 복합섬유 제조 후에 분리되어 종래와는 다른 멜란지 효과가 부여된다.The composite fiber formed of the polyamide-based resin and the polyester-based resin of the present invention, which is composed of the polyamide portion and the polyester portion, is formed as a side-by-side type modified cross section, and the polyamide portion and the polyester portion are separated Thereby giving a melange effect different from the conventional one.
상기 복합섬유의 이형단면은 삼각단면, 사각단면, 편평단면, 십자단면 등 다양한 형태로 형성할 수 있으며, 가장 바람직하게는 사이드-바이-사이드 형의 십자단면 또는 편평단면으로 형성되는 것이다.The modified cross-section of the composite fiber may be formed in various shapes such as a triangular cross-section, a square cross-section, a flat cross-section, and a cross cross-section, and is most preferably formed as a cross-section or a flat cross-section of a side-by-side structure.
상기 폴리아미드계 수지(100)와 폴리에스테르계 수지(200)를 도 1과 같은 복합방사구금을 통해 사이드-바이-사이드 형의 십자단면으로 복합섬유를 형성할 경우 방사 시에 발생되는 스웰링(swelling) 현상으로 도 3, 4에서와 같이 폴리아미드부와 폴리에스테르부는 각각 삼각단면의 섬유로 형성되고 분리되어 복합섬유는 실크섬유와 같은 고급스러운 광택을 갖게 된다.When the polyamide-based resin (100) and the polyester-based resin (200) are formed into cross-sectionally cross-sectioned cross-sections through a composite spinneret as shown in Fig. 1, swelling swelling phenomenon, the polyamide part and the polyester part are respectively formed and separated into triangular cross-section fibers as shown in Figs. 3 and 4, so that the composite fiber has a luxurious luster like silk fiber.
또는, 도 2와 같이 복합방사구금을 통해 사이드-바이-사이드 형의 편평단면으로 복합섬유를 형성할 경우 상기 폴리아미드계 수지(100)와 폴리에스테르계 수지(200)는 각각 사각단면의 섬유로 형성되고 분리되어 복합섬유는 색다른 광택을 갖게 된다.2, the polyamide-based
상기 폴리아미드계 수지와 폴리에스테르계 수지는 중량비 30:70~70:30으로 복합섬유를 형성하여 폴리아미드계 수지의 장점과 폴리에스테르계 수지의 장점을 모두 가지도록 형성할 수 있을 것이다.The polyamide-based resin and the polyester-based resin may be formed so as to have the advantages of the polyamide-based resin and the advantages of the polyester-based resin by forming the composite fiber at a weight ratio of 30:70 to 70:30.
상기와 같이 폴리아미드계 수지와 폴리에스테르계 수지로 형성되어 폴리아미드부와 폴리에스테르부로 구성되는 본 발명에 따른 Melange용 복합섬유는 상대점도(RV) 2.5~3.3인 폴리아미드계 수지와 고유점도(IV) 0.5~0.8dL/g인 폴리에스테르계 수지를 사이드 바이 사이드형 복합방사구금을 통해 복합섬유로 섬유화단계와 상기 복합섬유를 알카리 용액에서 폴리아미드부와 폴리에스테르부를 분리하는 분리단계를 포함하여 제조할 수 있을 것이다.The composite fiber for melange according to the present invention, which is formed of a polyamide-based resin and a polyester-based resin and is composed of a polyamide portion and a polyester portion, has a polyamide-based resin having a relative viscosity (RV) IV) 0.5 to 0.8 dL / g to a composite fiber through a side-by-side composite spinneret and a separation step of separating the composite fiber from the polyamide part and the polyester part in an alkali solution .
상기 폴리아미드계 수지는 대략 250~280℃에서 용융하고, 상기 폴리에스테르계 수지는 대략 270~310℃에서 용융하여 방사할 수 있으며, 상기 섬유화단계는 일반적인 복합섬유를 섬유로 제조하는 단계로 방사, 연신 등의 공정을 통해 실시할 수 있을 것이다.The polyamide-based resin melts at about 250 to 280 ° C, and the polyester-based resin can melt and spin at about 270 to 310 ° C. In the fiberization step, Stretching, and the like.
상기 섬유화단계 중 연신은 방사된 복합섬유을 1.5~2.5의 연신비로 연신할 수 있으며, 본 발명의 복합섬유의 사용목적에 따라 반연신사 또는 연신사로 제조할 수 있을 것이다. The drawn composite fiber may be stretched at a stretching ratio of 1.5 to 2.5, and the composite fiber of the present invention may be produced as a semi-stretched or drawn yarn according to the purpose of use.
또한, 제조되는 복합섬유의 광택을 향상시키기 위해 상기 사이드 바이 사이드형 복합방사구금은 위에서 설명된 바와 같이 십자단면 또는 평편단면인 것이 바람직할 것이다.Further, in order to improve the gloss of the composite fiber to be produced, the side-by-side composite spinneret preferably has a cross-section or a flat cross-section as described above.
상기 분리단계는 복합섬유를 알카리 용액에서 폴리아미드부와 폴리에스테르부를 분리하는 단계로 70~100℃, 0.1~1%의 NaOH 또는 KOH 알카리 수용액에 15~60분간 복합섬유를 처리하여 실시할 수 있을 것이다.The separation step is a step of separating the polyamide part and the polyester part in the alkali solution of the composite fiber, and may be carried out by treating the composite fiber in an aqueous solution of 0.1 to 1% NaOH or KOH alkali solution at 70 to 100 ° C for 15 to 60 minutes will be.
상기 분리단계 전에 상기 복합섬유를 ATY, DTY, ITY 등으로 사가공하는 사가공단계가 더 포함될 수 있을 것이다.The composite fiber may be further processed by ATY, DTY, ITY or the like before the separation step.
상기 사가공단계는 복합섬유의 다양한 사용목적에 따라 적합한 사가공을 선택하여 실시할 수 있을 것이다.The yarn processing step may be carried out by selecting a suitable yarn according to various purposes of the conjugated fiber.
아래에서 본 발명에 따른 실시예로 본 발명의 Melange용 복합섬유를 제조하였다. 본 발명이 이들 실시예에 한정되는 것은 아니다. The composite fiber for melange of the present invention was produced in the following Examples according to the present invention. But the present invention is not limited to these examples.
실시예 1 내지 3Examples 1 to 3
상기 폴리아미드계 수지는 약 260~270℃에서 용융하고, 상기 폴리에스테르계 수지는 약 280~300℃에서 용융하고 방사속도는 약 2,000m/min으로 방사하였고, 약 2.0연신비로 연신하여 복합섬유를 제조하였다.The polyamide based resin melted at about 260 to 270 DEG C, the polyester based resin was melted at about 280 to 300 DEG C, the spinning speed was about 2,000 m / min, stretched at a draw ratio of about 2.0, .
상기 제조된 복합섬유를 DTY(Draw Textured Yarn)로 제조 후에 100℃의 가성소다 약 0.5%의 NaOH 용액에서 30분간 처리하여 폴리아미드부와 폴리에스테르부를 분리하는 분리단계를 실시하여 본 발명의 Melange용 복합섬유를 제조하였다.The composite fiber thus prepared was made into DTY (Draw Textured Yarn), and then subjected to a separation step of separating the polyamide portion and the polyester portion by treatment with caustic soda of about 0.5% NaOH solution at 100 캜 for 30 minutes, To prepare composite fibers.
상기에서 제조된 본 발명의 Melange용 복합섬유를 카티온 염료를 사용하여 염색하였다.The composite fiber of the present invention prepared above was dyed using a cationic dye.
상기 폴리아미드계 수지와 폴리에스테르계 수지의 조성과 조건은 표 1에 나타내었다. 도 3은 실시예 1의 연신 후의 복합섬유 상태를 나타낸 사진이고, 도 4는 실시예 1의 염색 후의 복합섬유 상태를 나타낸 사진이다.The composition and conditions of the polyamide-based resin and the polyester-based resin are shown in Table 1. Fig. 3 is a photograph showing the state of the composite fibers after stretching in Example 1, and Fig. 4 is a photograph showing the state of the composite fibers after dyeing in Example 1. Fig.
도 3에서는 폴리아미드부와 폴리에스테르부가 분리되지 않은 상태인 것을 알 수 있으나, 분리단계 후인 도 4에서는 폴리아미드부와 폴리에스테르부가 완벽히 분리된 것을 알 수 있으며, 폴리아미드부가 카티온 염료로 염색된 상태임을 알 수 있다.In FIG. 3, it can be seen that the polyamide moiety and the polyester moiety are not separated. However, in FIG. 4 after the separation step, it can be seen that the polyamide moiety and the polyester moiety are completely separated and the polyamide moiety and the polyester moiety are stained with the polyamide moiety cationic dye State.
비교예 1 내지 3Comparative Examples 1 to 3
상기 실시예 1 내지 3과 동일하게 제조하였으며, 표 1과 같은 조성과 조건으로 복합섬유를 제조하였다.The composite fibers were prepared in the same manner as in Examples 1 to 3, and the composite fibers were prepared according to the composition and conditions as shown in Table 1.
◈ 실시예 및 비교예의 평가◈ Evaluation of Examples and Comparative Examples
실시예 1 내지 3과 비교예 1 내지 3의 공정성, 광택, 멜란지 효과, 청량감을 평가하여 표 2에 나타내었다.The fairness, gloss, melange effect and refreshing feeling of Examples 1 to 3 and Comparative Examples 1 to 3 were evaluated and shown in Table 2.
* 공정성 평가: 1등급 생산량/전체 생산량*100= 수율(중량기준)* Fairness assessment: grade 1 production / overall yield * 100 = yield (by weight)
* 광택, 청량감 및 멜란지 효과: 5명의 전문가에 의해 상대적인 관능평가 실시* Gloss, refreshing and melange effect: Relative sensory evaluation performed by 5 experts
표 2에서와 같이 본 발명의 Melange용 복합섬유(실시예 1내지 3)은 비교예 1 내지 3에 비해 멜란지 효과가 매우 우수한 것을 알 수 있으며, 실시예 1, 2의 광택보다 실시예 3의 광택이 우수한 것을 보아 십자단면 보다 편평단면이 광택이 더 좋은 것을 알 수 있으나 청량감의 경우에는 삽자단면이 더 우수한 것을 알 수 있을 것이다.As can be seen from Table 2, the melange composite fibers of the present invention (Examples 1 to 3) have a remarkably superior melange effect as compared with Comparative Examples 1 to 3, and the gloss of Example 3 It can be seen that the flat section of the cross section is better in gloss than the cross section, but in the case of the cool feeling, the cross section is better.
<도면의 주요부분에 대한 설명>
100 : 폴리아미드계 수지 200 : 폴리에스테르계 수지DESCRIPTION OF THE EMBODIMENTS
100: polyamide resin 200: polyester resin
Claims (7)
상기 폴리아미드부는 상대점도(RV) 2.5~3.3인 폴리아미드계 수지로 형성되고, 상기 폴리에스테르부는 고유점도(IV) 0.5~0.8dL/g인 폴리에스테르계 수지로 형성되되,
상기 복합섬유는 사이드 바이 사이드 형의 십자단면으로 형성되고, 상기 폴리아미드부와 폴리에스테르부는 섬유 제조 후 폴리아미드부와 폴리에스테르부는 각각 삼각단면의 섬유로 분리되는 것을 특징으로 하는 Melange용 복합섬유.A composite fiber comprising a polyamide-based resin and a polyester-based resin, the composite fiber comprising a polyamide portion and a polyester portion,
Wherein the polyamide portion is formed of a polyamide resin having a relative viscosity (RV) of 2.5 to 3.3, and the polyester portion is formed of a polyester resin having an intrinsic viscosity (IV) of 0.5 to 0.8 dL / g,
Wherein the composite fiber is formed as a cross-section of a side-by-side type, and the polyamide portion and the polyester portion are separated into triangular cross-section fibers after the production of the fiber, respectively.
상기 폴리아미드계 수지는 나일론 6, 나일론 66, 나일론 610 중 어느 하나인 것을 특징으로 하는 Melange용 복합섬유.The method according to claim 1,
Wherein the polyamide based resin is any one of nylon 6, nylon 66, and nylon 610.
상기 폴리에스테르계 수지는 폴리에틸렌테레프탈레이트, 폴리트리메틸렌테레프탈레이트, 폴리부틸렌테레프탈레이트 중 어느 하나인 것을 특징으로 하는 Melange용 복합섬유.The method according to claim 1,
Wherein the polyester-based resin is any one of polyethylene terephthalate, polytrimethylene terephthalate, and polybutylene terephthalate.
상기 폴리아미드부와 폴리에스테르부는 중량비 30:70~70:30으로 형성되는 것을 특징으로 하는 Melange용 복합섬유.The method according to claim 1,
Wherein the polyamide portion and the polyester portion are formed in a weight ratio of 30:70 to 70:30.
상기 폴리아미드부는 상대점도(RV) 2.5~3.3인 폴리아미드계 수지, 상기 폴리에스테르부는 고유점도(IV) 0.5~0.8dL/g인 폴리에스테르계 수지를 십자단면의 사이드 바이 사이드형 복합방사구금을 통해 복합섬유로 섬유화단계;
상기 복합섬유를 알카리 용액에서 폴리아미드부와 폴리에스테르부가 각각 삼각단면의 섬유로 분리되는 분리단계를 포함하여 제조되는 것을 특징으로 하는 Melange용 복합섬유 제조방법.A method for producing a composite fiber comprising a polyamide-based resin and a polyester-based resin, the composite fiber comprising a polyamide portion and a polyester portion,
Wherein the polyamide portion is a polyamide-based resin having a relative viscosity (RV) of 2.5 to 3.3, and the polyester portion is a polyester-based resin having an intrinsic viscosity (IV) of 0.5 to 0.8 dL / g as a cross- Through fiberization step to composite fiber;
And separating the composite fiber into an alkali solution and separating the polyamide part and the polyester part into triangular cross-section fibers, respectively.
상기 사이드 바이 사이드형 복합방사구금은 십자단면 또는 편평단면인 것을 특징으로 하는 Melange용 복합섬유 제조방법.The method according to claim 6,
Wherein the side-by-side composite spinneret has a cross-section or a flat cross-section.