KR101870867B1 - Eco-friendly multi-functional floor material with no curving and excellent construct ability and manufacturing method of the same - Google Patents

Eco-friendly multi-functional floor material with no curving and excellent construct ability and manufacturing method of the same Download PDF

Info

Publication number
KR101870867B1
KR101870867B1 KR1020160075016A KR20160075016A KR101870867B1 KR 101870867 B1 KR101870867 B1 KR 101870867B1 KR 1020160075016 A KR1020160075016 A KR 1020160075016A KR 20160075016 A KR20160075016 A KR 20160075016A KR 101870867 B1 KR101870867 B1 KR 101870867B1
Authority
KR
South Korea
Prior art keywords
sheet
adhesive
fabric base
flooring
present
Prior art date
Application number
KR1020160075016A
Other languages
Korean (ko)
Other versions
KR20170141948A (en
Inventor
한창수
Original Assignee
주식회사 스타코리아
월드스타 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 스타코리아, 월드스타 주식회사 filed Critical 주식회사 스타코리아
Priority to KR1020160075016A priority Critical patent/KR101870867B1/en
Publication of KR20170141948A publication Critical patent/KR20170141948A/en
Application granted granted Critical
Publication of KR101870867B1 publication Critical patent/KR101870867B1/en

Abstract

본 발명은 커빙이 없고 시공성이 우수한 친환경 다기능 바닥재 및 그 제조 방법에 관한 것으로서, 구체적으로는 개인 위생 용품에 사용되는 흡수재를 분쇄하여 얻어진 분쇄물과 폴리올레핀계 열가소성 수지의 액상 수지를 혼합하여 일정 두께로 압착 성형함에 의해 합성 패브릭 베이스를 제조하는 단계; 상기 얻어지는 합성 패브릭 베이스의 일면에 접착제를 도포하는 단계; 상기 접착제가 도포된 상면에 PVC(polyvinyl chloride) 시트, PP(폴리프로필렌) 시트 또는 HPM(High pressure melamine) 시트를 부착하는 단계; 상기 합성 패브릭 베이스의 타면에 접착제를 도포하고 밸런싱 시트를 부착하는 단계; 및 상기 얻어지는 소재를 재단하는 단계;를 포함하는 친환경 다기능 바닥재의 제조방법 및 상기 방법으로 제조되는 친환경 다기능 바닥재를 제공한다.
본 발명에 따른 친환경 다기능 바닥재는 합판을 사용하지 않고 특수하게 제조되는 합성 패브릭 베이스를 사용하므로 고온이나 저온의 외기 조건에 의해 수축하거나 팽창하지 않아 치수 안정성이 우수하며, 수분에 대한 저항성도 우수하여 수분에 의해 수축 팽창하거나 변색되지 않는 장점이 있고, 시간의 경과에 따라 일정 부위에서 휨이 발생하는 커빙(curving) 현상이 발생하지 않으며, 단차나 접합부에서의 벌어짐 현상 등의 문제가 발생하지 않는다. 또한, 적당한 크기로 재단하여 바닥재나 벽체의 대리석 대용재로 사용할 수 있으므로 활용성이 크며, 비숙련자라도 접착제를 이용해 붙이기만 하면 시공이 완료되므로 가정에서 DIY(Do It Yourself) 작업이 가능하여 소비자의 직접 시공이 가능하고 시공 시간도 매우 절감될 수 있어 시공비를 절감할 수 있는 장점이 있다.The present invention relates to an eco-friendly multifunctional flooring material free from scouring and having excellent workability and a method for producing the same. More specifically, the present invention relates to a method for producing an eco- Fabricating a composite fabric base by press-molding a box; Applying an adhesive to one side of the resultant composite fabric base; Attaching a polyvinyl chloride (PVC) sheet, a polypropylene (PP) sheet or a high pressure melamine (HPM) sheet to the upper surface to which the adhesive is applied; Applying an adhesive to the other side of the composite fabric base and attaching a balancing sheet; And cutting the obtained material. The present invention also provides an eco-friendly multi-functional floor material produced by the method.
The environmentally-friendly multifunctional flooring according to the present invention uses a specially manufactured synthetic fabric base without using plywood, and therefore has excellent dimensional stability due to shrinkage or expansion due to high-temperature or low-temperature outdoor conditions, and is excellent in moisture resistance, The curving phenomenon in which a warp occurs in a certain region does not occur with time, and the problems such as a step or a widening at a joint portion do not occur. In addition, it can be used as flooring or wall marble flooring by cutting it to a suitable size, so it is highly usable. Even if you are a novice, you can complete DIY (Do It Yourself) It is possible to directly construct and reduce the construction time, thereby reducing the construction cost.

Description

커빙이 없고 시공성이 우수한 친환경 다기능 바닥재 및 그 제조 방법{Eco-friendly multi-functional floor material with no curving and excellent construct ability and manufacturing method of the same}BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an eco-friendly multifunctional flooring material having no curbing and excellent workability,

본 발명은 온돌 마루, 강마루 등에 사용되는 인테리어 소재의 친환경 다기능 바닥재에 관한 것으로서, 마루용 바닥재 뿐만 아니라 월 부착용 인공 대리석 대용으로도 사용될 수 있으며, 누구나 손쉽게 시공할 수 있는 친환경 다기능 바닥재의 제조 기술에 관한 것이다. The present invention relates to an environmentally-friendly multi-functional flooring material for interior materials used for flooring, flooring, and the like, and can be used not only as a flooring for floors but also as a substitute for an artificial marble for wall mounting. .

생활 수준의 향상과 실내 인테리어에 대한 요구 등으로 인해 최근에는 바닥재로서 단순한 PVC 장판이 아니라 천연 무늬목을 사용하는 친환경 인테리어 소재에 대한 요구가 증가하고 있으며, 또한 벽체로서도 기존의 단순한 페이퍼 벽지나 실크 벽지 외에 대리석 벽체에 대한 요구가 증가하고 있는 상황이다. In recent years, there has been an increasing demand for eco-friendly interior materials using natural veneer rather than simple PVC flooring as flooring due to improvement of living standards and demands for interior decoration. In addition to the existing simple paper wallpaper and silk wallpaper There is a growing demand for marble walls.

대리석 벽체는 천연 대리석을 사용할 경우 비용 증대로 인해 천연석 보다는 인조석을 사용하는 경우가 많으며, 인조석의 경우도 중량으로 인해 시공이 어렵기 때문에 대리석 문양을 가지고 대리석 질감이 나는 벽체용 재료를 사용하는 경우가 증가하고 있다. Marble walls are often made of artificial stone rather than natural stone due to the increase in cost when natural marble is used. In case of artificial stone, it is difficult to construct due to its weight. Therefore, a case of using marble- .

바닥재의 경우 기존의 천연 무늬목 마루판의 경우 천연 무늬목이 수분에 약한 단점이 있으므로 수분에 의해 갈라짐 현상 및 백화 현상이 발생하고, 내충격성이 약하여 가구 등에 의해 스크래치가 발생하는 등 표면 손상이 발생하기 쉬우며, 시공시 마루판을 일일이 끼워 맞추고 에폭시 접착제를 사용해서 바닥에 부착해서 시공해야 하므로 공사 시간이 오래 걸리고 숙련된 기술자가 아니면 시공이 어렵다는 문제가 있다. 따라서 이러한 천연 무늬목 마루판은 자재 뿐만 아니라 시공비도 고가인 경우가 많다.In the case of a flooring material, a natural veneer floorboard has a disadvantage in that the natural veneer has a weak point in moisture, and therefore cracking and whitening occur due to moisture, scratches are generated by furniture and the like due to low impact resistance, , It is necessary to install the floorboards by attaching them to the floor using an epoxy adhesive, so that the construction time is long and there is a problem that it is difficult to construct the floorboards by skilled technicians. Therefore, such natural veneer floorboards are often expensive as well as materials.

최근에는 천연 무늬목의 질감을 가지면서 내스크래치성 및 내충격성을 증가시킨 치장 목질 마루판(예를 들어 강화마루, 강마루) 등이 사용되고 있으나, 질감이 천연 무늬목보다 떨어지고, 수분에 의한 하자 문제가 있으며, 시간의 경과에 따라 접합 부분에서 벌어짐이나 단차가 발생하여 소비자 품질 불만의 원인이 되고 있다. In recent years, stucco wood floorboards (for example, reinforced flooring, steel flooring) having increased scratch resistance and impact resistance while having a natural veneer texture have been used, but the texture is lower than that of natural veneer, , A flaring or a step is generated at the joint portion with the lapse of time, which is a cause of customer's quality dissatisfaction.

또한, 상기 치장 목질 마루판의 경우는 바닥재로만 사용될 뿐 벽체 등에는 사용되기 어렵다는 한계가 있다. In the case of the above-mentioned stained wood flooring, it is used only as a flooring material, but it is difficult to be used for walls and the like.

기존 기술로서 대한민국 등록특허 제10-1091432호는 천연 무늬목의 문양, 색상, 질감을 유지하면서 치장 목질 마루판의 문제점인 찍힘, 긁힘, 수분에 의한 수축 팽창, 치수변화 등의 문제점을 해결하기 위하여 치장 무늬목을 MDF 등의 합판 위에 접합하기 전에 무늬목을 멜라민 등의 수지 함침 소재를 사용하여 다층으로 고열 고압으로 무늬목을 가공함으로써 무늬목 세포 내의 미세한 기공을 수지 성분으로 채우도록 하여 기존 치장 목질 무늬목의 문제점을 개선하는 기술을 제안하였다. Korean Patent No. 10-1091432, as an existing technology, has been developed to solve problems such as stamping, scratching, expansion and contraction due to moisture, dimensional change, and the like, which are problems of the stained wood flooring while maintaining the pattern, color and texture of natural veneer. Is laminated on a plywood of MDF or the like using a resin impregnated material such as melamine to process the laminated wood with high temperature and high pressure to fill the fine pores in the laminated wood with the resin component to improve the problems of the existing woody wood veneer Technology.

또한, 대한민국 등록특허 제10-1441345호에서는 HPM 시트 부착 바닥재를 제조함에 있어 상부에 인쇄된 그라비아지를 적층하고, 그 하부에 베니어 합판을 적층하여 고열 고압으로 압착 성형함에 의해 수축 팽창의 치수 변형 문제를 방지하고, 내마모성, 내충격성, 내변색성, 내한성, 내열성 등의 문제를 개선하는 기술을 제안하였다. 이 기술은 인쇄된 그라비아지와 베니어 합판을 멜라민 수지 등으로 함침한 후 적층하고 나서 고열 고압으로 압착하는 방법으로 기존의 치장 목질 무늬목의 문제점을 개선할 수 있음을 설명하고 있다. In addition, Korean Patent No. 10-1441345 discloses a method for manufacturing a floor material with an HPM sheet, in which a gravure printed on an upper side is laminated, a veneer plywood is laminated on the lower side thereof, and compression- And has proposed a technique for improving problems such as abrasion resistance, impact resistance, discoloration resistance, cold resistance and heat resistance. This technology explains that the problem of existing stonework wood veneer can be improved by impregnating printed gravure paper and veneer plywood with melamine resin and then laminating and then pressing with high heat and high pressure.

그러나, 이러한 종래의 기술들은 하부에 사용되는 합판의 속성으로 인해 장기 사용시 가운데 부분에서 일어나는 커빙(curving)이 발생하고 소재의 수축 팽창으로 인해 접합 부분에서의 벌어짐 및 단차 발생 등의 문제는 해결될 수가 없었다. 또한, 바닥 공사를 함에 있어 판재 간을 서로 끼워맞추기식으로 에폭시 접착제를 이용하여 시공해야 하기 때문에 전문 작업자가 아니면 시공이 어려워 시공비가 증가하는 문제는 여전히 해결되기 어려웠다. However, due to the properties of the plywood used in the lower part of the prior art, curving occurring in the middle part occurs during long-term use, and the problems such as widening and step difference at the joint part due to contraction and expansion of the material can be solved There was no. In addition, in the floor construction, it is difficult to solve the problem that the installation cost is increased because it is difficult to construct without a professional worker because the work must be made using an epoxy adhesive in such a manner that the plates are fitted to each other.

<기타 선행기술 문헌><Other Prior Art Documents>

1. 대한민국 등록특허 제10-0732541호1. Korean Patent No. 10-0732541

2. 대한민국 등록특허 제10-0913438호2. Korean Patent No. 10-0913438

3. 대한민국 등록특허 제10-1299918호3. Korean Patent No. 10-1299918

4. 대한민국 등록특허 제10-1608692호4. Korean Patent No. 10-1608692

5. 대한민국 공개특허 제10-2016-0009247호5. Korean Patent Publication No. 10-2016-0009247

6. 대한민국 공개특허 제10-2016-0002437호6. Korean Patent Publication No. 10-2016-0002437

본 발명은 상기와 같은 종래 기술의 문제점을 해결하기 위해 개발된 것으로서, 무늬목이나 대리석의 문양을 갖는 데코 타일형 바닥재를 제조함에 있어서, 열이나 저온에 의한 변형이나 물에 의한 변색이 일어나지 않으며 시간이 경과한 후에도 커빙이나 단차, 접합분 분리 등의 불량이 발생하지 않을 뿐만 아니라, 시공이 쉬어 비숙련자도 쉽게 작업할 수 있어 DIY(Do It Yourself) 시공이 가능하며, 특히 인테리어 바닥재 뿐만 아니라 인테리어 벽체로도 다양하게 활용할 수 있는 친환경 다기능 바닥재를 제조하는 방법과 상기 방법에 의해 제조되는 친환경 다기능 바닥재를 제공하고자 한다. DISCLOSURE Technical Problem The present invention has been developed in order to solve the problems of the related art as described above, and it is an object of the present invention to provide a decorative tile flooring having a pattern of veneer or marble, (Do It Yourself) can be done easily because it is easy to work even for the unskilled person because it is not only not causing defects such as curbing, step difference and separation of joints after elapsing, The present invention also provides a method for producing an environmentally friendly multifunctional flooring material which can be utilized in various ways and an environmentally friendly multifunctional flooring material produced by the above method.

상기 과제를 달성하기 위하여 본 발명은In order to achieve the above object,

(a) 개인 위생 용품에 사용되는 흡수재를 분쇄하여 얻어진 분쇄물과 폴리올레핀계 열가소성 수지의 액상 수지를 혼합하여 일정 두께로 압착 성형함에 의해 합성 패브릭 베이스를 제조하는 단계;(a) preparing a synthetic fabric base by mixing a pulverized material obtained by pulverizing an absorbent material used in personal hygiene products with a liquid resin of a polyolefin thermoplastic resin, and compression-molding the pulverized material to a predetermined thickness;

(b) 상기 얻어지는 합성 패브릭 베이스의 일면에 접착제를 도포하는 단계; (b) applying an adhesive to one side of the resultant composite fabric base;

(c) 상기 접착제가 도포된 상면에 PVC(polyvinyl chloride) 시트, PP(폴리프로필렌) 시트 또는 HPM(High pressure melamine) 시트를 부착하는 단계; (c) attaching a polyvinyl chloride (PVC) sheet, a polypropylene (PP) sheet or a high pressure melamine (HPM) sheet to the top surface to which the adhesive is applied;

(d) 상기 합성 패브릭 베이스의 타면에 접착제를 도포하고 밸런싱 시트를 부착하는 단계; 및 (d) applying an adhesive to the other side of the composite fabric base and attaching a balancing sheet; And

(e) 상기 얻어지는 소재를 재단하는 단계;(e) cutting the obtained material;

를 포함하는 것을 특징으로 하는 친환경 다기능 바닥재의 제조 방법을 제공한다. The present invention also provides a method for manufacturing an environmentally friendly multi-functional floor material.

본 발명의 일 실시예에서, 상기 개인 위생 용품에 사용되는 흡수재는 목재 펄프 섬유, 목재 플러프 섬유 및 합성 목재 펄프 섬유 중에서 선택되는 1종 또는 2종 이상의 혼합물로서, 상기 분쇄물은 직경이 1~50미크론이고 길이가 1~100미크론에 포함되는 것을 특징으로 한다. In one embodiment of the present invention, the absorbent material used in the personal care article is one or a mixture of two or more materials selected from wood pulp fibers, wood fluff fibers and synthetic wood pulp fibers, 50 microns in length and 1 to 100 microns in length.

또한, 본 발명의 일 실시예에서, 상기 폴리올레핀계 열가소성 수지는 폴리프로필렌인 것을 특징으로 한다. Further, in an embodiment of the present invention, the polyolefin-based thermoplastic resin is polypropylene.

또한, 본 발명의 일 실시예에서, 상기 접착제는 수성 EVA(Ethylene-vinyl acetate) 수지를 포함하는 접착제를 사용하는 것을 특징으로 한다. Further, in one embodiment of the present invention, the adhesive is characterized by using an adhesive containing an aqueous ethylene-vinyl acetate (EVA) resin.

또한, 상기 과제를 달성하기 위하여 본 발명은In order to achieve the above object,

상기 본 발명에 따른 방법에 의해 제조되며, Which is produced by the process according to the present invention,

상기 (a)의 방법에 의해 제조되는 합성 패브릭 베이스를 포함하고, A composite fabric base fabricated by the method of (a)

상기 합성 패브릭 베이스의 일면에 접착제를 포함하며, Wherein the synthetic fabric base comprises an adhesive on one side,

상기 접착제가 도포된 상면에 PVC(polyvinyl chloride) 시트, PP(폴리프로필렌) 시트 또는 HPM(High pressure melamine) 시트를 포함하고, A polyvinyl chloride (PVC) sheet, a polypropylene (PP) sheet or a high pressure melamine (HPM) sheet on the upper surface to which the adhesive is applied,

상기 합성 패브릭 베이스의 타면에 도포된 접착제 및 이에 부착된 밸런싱 시트를 포함하는 것을 특징으로 하는 친환경 다기능 바닥재를 제공한다. And an adhesive applied to the other surface of the synthetic fabric base and a balancing sheet attached thereto.

본 발명에 따른 친환경 다기능 바닥재의 특징 및 장점을 설명하면 다음과 같다. The features and advantages of the eco-friendly multi-functional flooring according to the present invention will be described below.

1. 먼저, 본 발명에 따른 친환경 다기능 바닥재는 휘발성 유기화합물이나 인체에 유해한 성분의 유출이 전혀 없어 친환경적이다. 1. First, the environmentally-friendly multifunctional flooring according to the present invention is environment-friendly because there is no leakage of volatile organic compounds or harmful components to human body.

2. 또한, 본 발명에 따른 친환경 다기능 바닥재는 기존의 판재나 합판을 사용하지 않고 특수하게 제조되는 합성 패브릭 베이스를 사용하기 때문에 고온이나 저온의 외기 조건에 의해 수축하거나 팽창하지 않아 치수 안정성이 우수하다. 2. Since the environmentally-friendly multifunctional flooring according to the present invention uses a specially manufactured synthetic fabric base without using a conventional plate or plywood, it is excellent in dimensional stability because it does not shrink or expand due to high temperature or low temperature outdoor conditions .

3. 또한, 본 발명에 따른 친환경 다기능 바닥재는 수분에 대한 저항성도 우수하여 수분에 의해 수축 팽창하거나 백화 현상이 발생하지 않는다. 3. The environmentally-friendly multifunctional flooring according to the present invention is also excellent in resistance to moisture, so that it does not shrink or expand due to moisture or bleaching.

4. 또한, 본 발명에 따른 친환경 다기능 바닥재는 항균성도 우수하며, 특히 판재나 합판을 사용하지 않고 특수하게 제작된 합성 패브릭 베이스를 사용하므로 시간의 경과에 따라 일정 부위에서 휨이 발생하는 커빙(curving) 현상이 발생하지 않으며, 단차나 접합부에서의 벌어짐 현상 등의 문제가 발생하지 않는다. 4. The environmentally-friendly multifunctional flooring according to the present invention is also excellent in antibacterial property. In particular, since it uses a specially manufactured synthetic fabric base without using plate materials or plywood, curving ) Phenomenon does not occur, and problems such as a step or a widening phenomenon at the joint portion do not occur.

5. 또한, 적당한 크기로 재단하여 바닥재나 벽체의 대리석 대용재로 사용할 수 있으므로 활용성이 크며, 또한 비숙련자라도 접착제를 이용해 붙이기만 하면 시공이 완료되므로 가정에서 DIY(Do It Yourself) 작업이 가능하여 소비자의 직접 시공이 가능하고 시공 시간도 매우 절감될 수 있어 시공비를 절감할 수 있는 장점이 있다. 5. It can also be used as a flooring or wall marble flooring by cutting it to a suitable size. It is also highly usable, and even if you are a novice, you can do it by doing DIY (Do It Yourself) So that it is possible to directly construct a consumer and the construction time can be greatly reduced, thereby reducing the construction cost.

도 1은 본 발명의 일 실시예에 따른 친환경 다기능 바닥재를 제조하는 과정을 나타낸 것이다.
도 2a 내지 도 2c는 본 발명의 일 실시예에 따른 친환경 다기능 바닥재의 측면을 나타낸 몇 가지 예이다.
도 3은 본 발명의 일 실시예에 따른 친환경 다기능 바닥재를 인테리어 바닥재로 사용하는 것을 나타낸 것이다.
도 4는 본 발명의 일 실시예에 따른 친환경 다기능 바닥재를 인테리어 벽체 재료로 사용하는 것을 나타낸 것이다. FIG. 1 illustrates a process for manufacturing an environmentally-friendly multi-functional floor material according to an embodiment of the present invention.
2A to 2C are several examples of side views of an environmentally friendly multi-functional floor material according to an embodiment of the present invention.
3 illustrates the use of an environmentally-friendly multi-functional floor material according to an embodiment of the present invention as an interior floor material.
4 illustrates the use of an eco-friendly multi-functional flooring material according to an embodiment of the present invention as an interior wall material.

이하에서는 첨부된 도면을 참조하여 본 발명에 대하여 더욱 구체적으로 설명한다.Hereinafter, the present invention will be described in more detail with reference to the accompanying drawings.

도 1은 본 발명의 일 실시예에 따른 친환경 다기능 바닥재를 제조하는 과정을 순서대로 나타낸 것이다. 또한, 도 2a 내지 도 2c는 본 발명의 일 실시예에 따른 친환경 다기능 바닥재의 측면을 나타낸 몇 가지 예이다.FIG. 1 is a flowchart illustrating a process for manufacturing an environmentally-friendly multi-functional floor material according to an embodiment of the present invention. 2A to 2C are several examples showing side views of an environmentally-friendly multi-functional floor material according to an embodiment of the present invention.

도 1에 도시된 바와 같이, 본 발명에 따른 친환경 다기능 바닥재는, As shown in FIG. 1, the eco-friendly multi-

(a) 개인 위생 용품에 사용되는 흡수재를 분쇄하여 얻어진 분쇄물과 폴리올레핀계 열가소성 수지의 액상 수지를 혼합하여 일정 두께로 압착 성형함에 의해 합성 패브릭 베이스를 제조하는 단계;(a) preparing a synthetic fabric base by mixing a pulverized material obtained by pulverizing an absorbent material used in personal hygiene products with a liquid resin of a polyolefin thermoplastic resin, and compression-molding the pulverized material to a predetermined thickness;

(b) 상기 얻어지는 합성 패브릭 베이스의 일면에 접착제를 도포하는 단계; (b) applying an adhesive to one side of the resultant composite fabric base;

(c) 상기 접착제가 도포된 상면에 PVC(polyvinyl chloride) 시트, PP(폴리프로필렌) 시트 또는 HPM(High pressure melamine) 시트를 부착하는 단계; (c) attaching a polyvinyl chloride (PVC) sheet, a polypropylene (PP) sheet or a high pressure melamine (HPM) sheet to the top surface to which the adhesive is applied;

(d) 상기 합성 패브릭 베이스의 타면에 접착제를 도포하고 밸런싱 시트를 부착하는 단계; 및 (d) applying an adhesive to the other side of the composite fabric base and attaching a balancing sheet; And

(e) 상기 얻어지는 소재를 재단하는 단계;(e) cutting the obtained material;

를 포함하는 제조 방법에 의해 제조되는 것을 특징으로 한다.&Lt; / RTI &gt;

먼저, 상기 (a)단계에서 상기 개인 위생 용품에 사용되는 흡수재란 유아용 기저귀, 배변 훈련용 팬티, 요실금용 가먼트, 생리대 등을 포함할 수 있다. 이러한 개인 위생 용품은 그 내부에 천연 목재 펄프로 이루어진 흡수재를 포함하고 있는데, 본 발명에서는 이러한 흡수재를 분쇄하여 폴리올레핀계 열가소성 수지와 혼합한 후 일정 두께로 성형한다. First, the absorbent material used in the personal care article in the step (a) may include an infant diaper, a training pant, a urinal incontinence garment, a sanitary napkin, and the like. In the present invention, such an absorbent material is pulverized and mixed with a polyolefin-based thermoplastic resin, and then molded into a certain thickness.

구체적으로, 상기 개인 위생 용품에 사용되는 흡수재는 목재 펄프 섬유, 목재 플러프 섬유 및 합성 목재 펄프 섬유 중에서 선택되는 1종 또는 2종 이상의 혼합물로서, 상기 분쇄물은 직경이 1~50미크론이고 길이가 1~100미크론에 포함되는 것을 사용할 수 있다. Specifically, the absorbent material used in the personal hygiene article may be one or a mixture of two or more materials selected from wood pulp fibers, wood fluff fibers and synthetic wood pulp fibers, the pulverized material having a diameter of 1 to 50 microns and a length of 1 to 100 microns may be used.

또한, 본 발명에서 사용되는 상기 폴리올레핀계 열가소성 수지의 대표적인 예로는 폴리프로필렌 또는 폴리에틸렌을 들 수 있으며, 더욱 바람직하게는 폴리프로필렌 수지를 사용한다. Further, typical examples of the polyolefin-based thermoplastic resin used in the present invention include polypropylene or polyethylene, more preferably a polypropylene resin.

상기 폴리올레핀계 열가소성 수지를 가열하여 얻은 액상 수지와 상기 흡수재를 분쇄하여 얻은 분쇄물을 일정 비율로 혼합하고 여기에 경화제, 증점제, 촉진제, 충진재, 난연제, 항균제 등 각종 첨가제를 혼합하여 일정 두께로 압착 성형하여 합성 패브릭 베이스를 제조한다. The liquid resin obtained by heating the polyolefin thermoplastic resin and the pulverized material obtained by pulverizing the absorbent material are mixed at a predetermined ratio and various additives such as a hardener, a thickener, an accelerator, a filler, a flame retardant, and an antibacterial agent are mixed with the pulverizer, To produce a synthetic fabric base.

여기에서 상기 충진재로는 실리카 또는 알루미나 등의 표면 강화 충진재가 사용될 수 있고, 상기 난연재로는 수산화 알루미늄, 포스포릭에스테르, 할로겐탄화수소, 산화안티몬, 인산화합물 등이 단독 또는 혼합물로 포함될 수 있다. As the filler, a surface reinforcing filler such as silica or alumina may be used. As the flame retardant, aluminum hydroxide, phosphoric ester, halogen hydrocarbon, antimony oxide, phosphoric acid compound or the like may be included singly or as a mixture.

아울러, 기능성을 부여하기 위하여 전기석, 일라이트, 화산석, 운모, 게르마늄, 맥반석 등을 추가로 포함할 수 있다. 이러한 성분은 음이온 및 원적외선을 방출하여 생체 리듬을 활성화시키고 인체를 건강하게 유지할 수 있도록 하는 역할을 한다. In addition, tourmaline, ilite, volcanic stone, mica, germanium, elvan, etc. may be added to impart functionality. These ingredients release negative ions and far infrared rays to activate the biorhythm and keep the body healthy.

상기 폴리올레핀계 열가소성 수지와 상기 흡수재 분쇄물의 혼합 비율은 상기 폴리올레핀계 열가소성 수지 100 중량부를 기준으로 상기 흡수재 분쇄물이 약 50~300의 중량부로 혼합하는 것이 바람직하며, 이외에 각종 첨가제는 약 0.1~10 중량부로 혼합될 수 있다. 이렇게 조성물을 혼합한 후 일정 두께로 압출하고 건조 및 경화시켜 상기 합성 패브릭 베이스를 제조한다. The blend ratio of the polyolefin thermoplastic resin and the pulverizer is preferably about 50 to 300 parts by weight based on 100 parts by weight of the polyolefin thermoplastic resin. Lt; / RTI &gt; The composition is mixed, extruded to a certain thickness, dried and cured to prepare the synthetic fabric base.

본 발명에서는 상기 흡수재 분쇄물 외에 합성 하이드로겔 중합체와 같은 합성 재료를 추가로 포함하여 사용할 수 있다. In the present invention, a synthetic material such as a synthetic hydrogel polymer may be further used in addition to the above-mentioned pulverized material of the absorbent material.

상기 합성 하이드로겔 중합체는 변성 셀룰로오스계 중합체를 사용할 수 있으며, 상기 흡수재 분쇄물로 이루어진 천연 재료와 상기 폴리프로필렌 수지 간의 혼용성을 향상시키고 내수성을 더욱 증진시키는 역할을 한다.The synthetic hydrogel polymer can use a modified cellulose polymer and improve the compatibility between the natural material composed of the pulverized material of the absorbent material and the polypropylene resin and further improve the water resistance.

상기 변성 셀룰로오스계 중합체로는 메틸셀룰로오스, 카르복시메틸셀룰로오스, 히드록시프로필셀룰로오스 등에서 선택되는 1종 또는 2종 이상의 혼합물을 사용할 수 있으며, 사용 비율은 상기 흡수재 분쇄물 중량의 1~20 중량%의 범위에서 포함되는 것이 바람직하다. The modified cellulose polymer may be a mixture of one or more selected from methyl cellulose, carboxymethyl cellulose and hydroxypropyl cellulose. The proportion of the modified cellulose polymer is 1 to 20% by weight of the weight of the pulverized material .

이와 같이 제조되는 합성 패브릭 베이스는 고온 또는 저온 조건에서 치수 변화가 거의 일어나지 않는 장점이 있고, 일면으로 휨 변형도 발생하지 않는 장점이 있다. The composite fabric base thus manufactured has an advantage that the dimensional change hardly occurs at a high temperature or a low temperature condition, and there is an advantage that no bending deformation occurs on one side.

이어서, 상기 방법으로 얻어지는 합성 패브릭 베이스의 일면, 구체적으로는 표면 방향 면에 접착제를 도포한다. Then, an adhesive is applied to one surface of the synthetic fabric base obtained by the above method, specifically, the surface direction surface.

상기 접착제는 구체적으로 핫멜트 접착제로서 수성 EVA(Ethylene-vinyl acetate) 수지를 포함하는 접착제를 사용할 수 있다. As the adhesive, specifically, an adhesive containing an aqueous ethylene-vinyl acetate (EVA) resin may be used as a hot-melt adhesive.

구체적으로는 EVA 수지, 점착부여제, 왁스, 산화방지제 등을 혼합하여 사용할 수 있으며, 더욱 구체적으로는 EVA 수지 100 중량부에 대하여 점착부여제 90~110 중량부, 왁스 10~30 중량부, 산화 방지제 1~5 중량부를 혼합하여 사용할 수 있다. Concretely, EVA resin, tackifier, wax, antioxidant and the like can be mixed and used. More specifically, 90 to 110 parts by weight of the tackifier, 10 to 30 parts by weight of the tackifier, 10 to 30 parts by weight of the tackifier, And 1 to 5 parts by weight of an inhibitor may be mixed and used.

상기 EVA 수지를 포함하는 접착제는 응집력과 접착성을 높게 유지하는 장점이 있고 형태 유지력을 높게 유지하도록 하는 효과가 있다. The adhesive containing the EVA resin has an advantage of maintaining the cohesive force and adhesiveness at a high level, and has an effect of keeping the shape retention force high.

이어서, 상기 접착제가 도포된 상면에 데코 시트를 부착한다. Then, a decorative sheet is attached to the upper surface to which the adhesive is applied.

본 발명에서 사용되는 데코 시트의 예로서는 HPM(High pressure melamine) 시트(30)를 예로 들 수 있다. An example of the decor sheet used in the present invention is HPM (High Pressure Melamine) sheet 30.

상기 HPM 시트는 다른 말로 고압 멜라민 수지 합침판으로서, 최하층에 멜라민 수지 함침 언더레이지, 중간층에 멜라민 수지 함침 인쇄지 및 최상층에 멜라민 수지 함침 오버레이지를 적층하여 일정 두께(예를 들어 0.2~0.5mm)로 성형한 것으로서, 상기 인쇄지 무늬가 대리석 무늬를 가지므로 바닥재 뿐만 아니라 벽체 재료로서 사용되기도 적합한 장점이 있다. The HPM sheet is, in other words, a laminate of a high-pressure melamine resin laminated to a melamine resin impregnated underlay paper in the lowermost layer, a melamine resin impregnated printing paper in the middle layer, and a melamine resin impregnated overlay paper in the uppermost layer and has a thickness (for example, 0.2 to 0.5 mm) Since the printing paper pattern has a marble pattern, it is advantageous to be used not only as a floor material but also as a wall material.

본 발명에서 상기 데코 시트로 사용될 수 있는 또 다른 재료로는 PP(폴리프로필렌) 시트(31)를 들 수 있다. 상기 폴리프로필렌 시트는 그 표면이 원목 무늬를 갖도록 가공된 것으로서 표면이 원목 느낌이 나는 것을 특징으로 한다. As another material that can be used as the decor sheet in the present invention, a PP (polypropylene) sheet 31 can be mentioned. The polypropylene sheet is processed so that its surface has a log pattern, and the surface of the polypropylene sheet has a natural wood feel.

또한, 본 발명에서 상기 데코 시트로 사용될 수 있는 또 다른 재료로는 PVC(폴리염화비닐) 시트(32)를 들 수 있다. 상기 폴리염화비닐 시트는 그 표면이 원목 무늬를 갖도록 가공된 것으로서 표면이 비닐 느낌이 나는 비교적 저가 용도로 사용될 수 있다. In addition, PVC (polyvinyl chloride) sheet 32 is another material that can be used as the decor sheet in the present invention. The polyvinyl chloride sheet is processed so that its surface has a lumber pattern and can be used for a comparatively low-cost application in which the surface has a vinyl feel.

이어서, 상기 합성 패브릭 베이스의 타면, 구체적으로는 표면 방향의 반대 방향 면, 즉 바닥면에 접착제(40)를 도포하고 여기에 밸런싱 시트(50)를 부착한다. 이 때 사용되는 접착제는 상기 (b)단계에서 사용되는 것과 동일한 것을 사용하거나 다른 것을 사용할 수도 있다. Then, the adhesive 40 is applied to the other surface of the composite fabric base, specifically, the surface opposite to the surface, that is, the bottom surface, and the balancing sheet 50 is attached thereto. The adhesive used at this time may be the same as that used in the step (b), or may be another one.

상기 밸런싱 시트(50)는 시공 대상 바닥면과의 밀착성 및 평활도를 향상시키며 하부에서 올라오는 습기를 차단하는 역할을 한다. 본 발명에서 사용될 수 있는 밸런싱 시트로는 PET 시트 또는 PVC 시트 등의 합성 수지재 시트를 들 수 있다. The balancing sheet 50 improves the adhesion and smoothness of the floor surface to be applied and blocks the moisture coming from the bottom. Examples of the balancing sheet that can be used in the present invention include synthetic resin sheet such as PET sheet or PVC sheet.

이어서, 상기 얻어지는 소재를 적당한 크기로 재단함에 의해 바닥재의 제조가 완료된다. Subsequently, the obtained material is cut to an appropriate size to complete the production of the flooring.

본 발명에 따라 제조되는 상기 바닥재의 구조는 상기 (a)의 방법에 의해 제조되는 합성 패브릭 베이스를 포함하고, 상기 합성 패브릭 베이스의 일면에 접착제를 포함하며, 상기 접착제가 도포된 상면에 PVC(polyvinyl chloride) 시트, PP(폴리프로필렌) 시트 또는 HPM(High pressure melamine) 시트를 포함하고, 상기 합성 패브릭 베이스의 타면에 도포된 접착제 및 이에 부착된 밸런싱 시트를 포함하는 것을 특징으로 한다. The structure of the bottom material manufactured according to the present invention includes a synthetic fabric base produced by the method of (a), and the adhesive fabric is provided on one side of the synthetic fabric base, and PVC (polyvinyl and a balancing sheet attached to the other side of the synthetic fabric base, wherein the adhesive comprises a sheet of polypropylene (PP), a sheet of polypropylene (PP), or a sheet of high pressure melamine (HPM).

이러한 본 발명에 따른 바닥재는 기존에 대량으로 폐기되는 개인 위생 용품 흡수재를 재활용할 수 있으므로 친환경적이라는 장점이 있다. The flooring according to the present invention has an advantage of being eco-friendly because it can recycle a personal hygiene article absorber which is mass-disused in the past.

또한, 넓은 판재 형상으로 제조되며, 용도에 맞게 재단하여 사용할 수 있는 장점이 있다. In addition, it is manufactured in a wide plate shape and can be cut and used according to the application.

도 3은 본 발명의 일 실시예에 따른 친환경 다기능 바닥재를 인테리어 바닥재로 사용하는 것을 나타낸 것이다. 3 illustrates the use of an environmentally-friendly multi-functional floor material according to an embodiment of the present invention as an interior floor material.

도 3에 도시된 바와 같이, 바닥재의 용도로 사용할 경우에는 폭이 비교적 좁고 길이가 긴 직사각형 형태로 재단하여 사용할 수 있으며, 대리석 바닥재와 같은 느낌이 나도록 하기 위한 용도로서는 정사각형 형태로 재단하여 상호간에 접합하기만 하면 된다. As shown in FIG. 3, when it is used as a flooring material, it can be cut and used in a rectangular shape having a relatively narrow width and a long length. In order to make the marble flooring feel the same, All you have to do.

도 4는 본 발명의 일 실시예에 따른 친환경 다기능 바닥재를 인테리어 벽체 재료로 사용하는 것을 나타낸 것이다. 4 illustrates the use of an eco-friendly multi-functional flooring material according to an embodiment of the present invention as an interior wall material.

도 4에 도시된 바와 같이, 벽체 재료로 사용할 경우에는 대리석 벽체의 느낌이 나도록 하기 위해 정사각형 형태로 재단하고 일정 틈을 준 상태로 벽에 접합하기만 하면 된다. As shown in FIG. 4, when used as a wall material, it is only necessary to cut it into a square shape and to bond it to a wall in a state of a predetermined gap so as to give a feeling of a marble wall.

이와 같이, 본 발명에 따른 바닥재는 기존의 아파트나 주택, 사무실 등의 바닥재 뿐만 아니라, 벽체의 대리석 대용 소재로서도 사용될 수 있는 등 다양한 기능을 갖는다.As described above, the flooring according to the present invention has various functions such as being able to be used not only as a floor material for an existing apartment, a house, an office, but also as a marble substitute for a wall.

이상, 본 발명에 따른 친환경 다기능 바닥재 및 그 제조 방법에 관하여 설명하였다. 상기 설명된 바와 같이, 본 발명에 따른 친환경 다기능 바닥재는 합판을 사용하지 않고 특수하게 제조되는 합성 패브릭 베이스를 사용하므로 고온이나 저온의 외기 조건에 의해 수축하거나 팽창하지 않아 치수 안정성이 우수하며, 수분에 대한 저항성도 우수하여 수분에 의해 수축 팽창하거나 변색되지 않는 장점이 있고, 시간의 경과에 따라 일정 부위에서 휨이 발생하는 커빙(curving) 현상이 발생하지 않으며, 단차나 접합부에서의 벌어짐 현상 등의 문제가 발생하지 않는다. 또한, 적당한 크기로 재단하여 바닥재나 벽체의 대리석 대용재로 사용할 수 있으므로 활용성이 크며, 비숙련자라도 접착제를 이용해 붙이기만 하면 시공이 완료되므로 가정에서 DIY(Do It Yourself) 작업이 가능하여 소비자의 직접 시공이 가능하고 시공 시간도 매우 절감될 수 있어 시공비를 절감할 수 있는 장점이 있다. The eco-friendly multi-functional flooring according to the present invention and the manufacturing method thereof have been described above. As described above, the eco-friendly multifunctional flooring according to the present invention uses a specially manufactured synthetic fabric base without using a plywood, and thus has excellent dimensional stability because it does not shrink or expand due to high temperature or low temperature outdoor conditions. It is advantageous in that it is not shrunk or swelled due to moisture because it is excellent in resistance to moisture, and curving phenomenon in which a bending occurs in a certain region does not occur with time, and problems such as a step or a widening at a joint . In addition, it can be used as flooring or wall marble flooring by cutting it to a suitable size, so it is highly usable. Even if you are a novice, you can complete DIY (Do It Yourself) It is possible to directly construct and reduce the construction time, thereby reducing the construction cost.

10: 합성 패브릭 베이스 20: 접착제
30: HPM 시트 31: PP 시트
32: PVC 시트 40: 접착제
50: 밸런싱 시트10: Synthetic fabric base 20: Adhesive
30: HPM sheet 31: PP sheet
32: PVC sheet 40: Adhesive
50: Balancing sheet

Claims (5)

(a) 개인 위생 용품에 사용되는 흡수재를 분쇄하여 얻어진 분쇄물과 폴리올레핀계 열가소성 수지의 액상 수지를 혼합하여 일정 두께로 압착 성형함에 의해 합성 패브릭 베이스를 제조하는 단계;
(b) 상기 얻어지는 합성 패브릭 베이스의 일면에 접착제를 도포하는 단계;
(c) 상기 접착제가 도포된 상면에 PVC(polyvinyl chloride) 시트, PP(폴리프로필렌) 시트 또는 HPM(High pressure melamine) 시트로 이루어진 데코 시트를 부착하는 단계;
(d) 상기 합성 패브릭 베이스의 타면에 접착제를 도포하고 밸런싱 시트를 부착하는 단계; 및
(e) 상기 (d)단계에서 얻어지는 합성 패브릭 베이스의 타면에 밸런싱 시트가 부착된 소재를 재단하는 단계;를 포함하는 것을 특징으로 하며,
상기 개인 위생 용품에 사용되는 흡수재는 목재 펄프 섬유, 목재 플러프 섬유 및 합성 목재 펄프 섬유 중에서 선택되는 1종 또는 2종 이상의 혼합물로서, 상기 분쇄물은 직경이 1~50미크론이고 길이가 1~100미크론에 포함되는 것을 특징으로 하고,
상기 (a) 단계에서 상기 분쇄물 외에 메틸셀룰로오스, 카르복시메틸 셀룰로오스, 히드록시프로필셀룰로오스 중에서 선택되는 1종 또는 2종 이상의 혼합물로 이루어진 변성 셀룰로오스 중합체로 이루어진 합성 하이드로겔 중합체가 추가로 사용되며, 상기 합성 하이드로겔 중합체의 사용 비율은 상기 분쇄물 중량의 1~20 중량%의 범위로 포함되는 것을 특징으로 하며,
상기 (d) 단계에서 상기 접착제는 수성 EVA(Ethylene-vinyl acetate) 수지를 포함하는 접착제를 사용하는 것을 특징으로 하는
친환경 다기능 바닥재의 제조 방법.
(a) preparing a synthetic fabric base by mixing a pulverized material obtained by pulverizing an absorbent material used for personal hygiene products with a liquid resin of a polyolefin thermoplastic resin, and compression-molding the pulverized material to a predetermined thickness;
(b) applying an adhesive to one side of the resultant composite fabric base;
(c) attaching a decorative sheet made of a polyvinyl chloride (PVC) sheet, a polypropylene (PP) sheet or a high pressure melamine (HPM) sheet to the top surface to which the adhesive is applied;
(d) applying an adhesive to the other side of the composite fabric base and attaching a balancing sheet; And
(e) cutting the material to which the balancing sheet is attached on the other side of the synthetic fabric base obtained in the step (d)
The absorbent material used in the personal care article is one or a mixture of two or more materials selected from wood pulp fibers, wood fluff fibers and synthetic wood pulp fibers, the pulverized material having a diameter of 1 to 50 microns and a length of 1 to 100 It is characterized by being included in micron,
In step (a), a synthetic hydrogel polymer composed of a modified cellulose polymer composed of one or more selected from methyl cellulose, The use ratio of the hydrogel polymer is in the range of 1 to 20% by weight of the weight of the pulverized material,
In the step (d), the adhesive may be an adhesive containing an aqueous ethylene-vinyl acetate (EVA) resin.
A method for manufacturing an environmentally friendly multifunctional flooring material.
삭제delete 청구항 1에 있어서, 상기 폴리올레핀계 열가소성 수지는 폴리프로필렌인 것을 특징으로 하는 친환경 다기능 바닥재의 제조 방법.
The method according to claim 1, wherein the polyolefin-based thermoplastic resin is polypropylene.
삭제delete 청구항 1의 방법에 의해 제조되며,
상기 (a)의 방법에 의해 제조되는 합성 패브릭 베이스를 포함하고,
상기 합성 패브릭 베이스의 일면에 수성 EVA(Ethylene-vinyl acetate) 수지를 포함하는 접착제를 포함하며,
상기 접착제가 도포된 상면에 PVC(polyvinyl chloride) 시트, PP(폴리프로필렌) 시트 또는 HPM(High pressure melamine) 시트로 이루어진 데코 시트를 포함하고,
상기 합성 패브릭 베이스의 타면에 도포된 접착제 및 이에 부착된 밸런싱 시트를 포함하는 것을 특징으로 하는 친환경 다기능 바닥재. A process for the preparation of a compound according to claim 1,
A composite fabric base fabricated by the method of (a)
An adhesive comprising an aqueous ethylene-vinyl acetate (EVA) resin on one side of the composite fabric base,
A decorative sheet made of a polyvinyl chloride (PVC) sheet, a polypropylene (PP) sheet or a high pressure melamine (HPM) sheet on the upper surface to which the adhesive is applied,
An adhesive applied on the other side of the composite fabric base, and a balancing sheet attached thereto.
KR1020160075016A 2016-06-16 2016-06-16 Eco-friendly multi-functional floor material with no curving and excellent construct ability and manufacturing method of the same KR101870867B1 (en)