KR101843483B1 - Snow powder composition and mounting method of ski slope - Google Patents
Snow powder composition and mounting method of ski slope Download PDFInfo
- Publication number
- KR101843483B1 KR101843483B1 KR1020170080008A KR20170080008A KR101843483B1 KR 101843483 B1 KR101843483 B1 KR 101843483B1 KR 1020170080008 A KR1020170080008 A KR 1020170080008A KR 20170080008 A KR20170080008 A KR 20170080008A KR 101843483 B1 KR101843483 B1 KR 101843483B1
- Authority
- KR
- South Korea
- Prior art keywords
- snow
- powder composition
- ski
- snow powder
- ski slope
- Prior art date
Abstract
Description
본 발명은 스노우 파우더 조성물(snow powder composition) 및 이를 이용한 스키 슬로프(ski slope) 설치 방법에 관한 것으로서, 보다 상세하게는, 폴리아크릴산나트륨(sodium polyacrylate), 팜 왁스(palm wax)와 같은 유막 형성제 및 비누(soap)를 과립상 및 분말상으로 제조하여 혼합시킨 인공 스노우 파우더 및 상기 인공 스노우 파우더를 스키 슬로프(ski slope)에 설치하는 방법에 관한 것이다.The present invention relates to a snow powder composition and a method of installing a ski slope using the snow powder composition. More particularly, the present invention relates to a snow powder composition and a ski slope using the same, And artificial snow powder prepared by mixing and mixing soap in granular and powder form, and a method of installing the artificial snow powder on a ski slope.
최근 겨울 스포츠의 급증으로 자연 스키장이 급격히 발달하게 되었고, 이러한 현상은 전세계적으로 나타나고 있다. 그러나, 자연 스키장은 차지하는 공간이 넓고 계절적, 기후적 요소 및 비용 문제로 인하여 대개 도시에서 멀리 떨어져서 건설된다. 게다가, 자연 스키장은 특정 조건 하에서만, 즉, 영하의 온도와 눈이 오는 기후 및 특정 깊이의 눈덩이로 뒤덮이는 들판 있는 추운 겨울 동안에만 이용이 가능하다. 이러한 여러 가지 요건들은 이 스포츠의 확산 및 개발을 제한한다. The recent rapid increase in winter sports has led to the rapid development of natural ski resorts, and this phenomenon is occurring worldwide. However, natural ski areas are usually constructed far from the city due to the large space occupied by seasonal, climatic factors and costs. In addition, natural ski resorts are only available under certain conditions, ie, during cold winter, with subzero temperatures and snow climates and snowy fields covered with snow. These various requirements limit the spread and development of this sport.
따라서, 많은 국가에서 인공 눈 및 인공 스키장을 연구 개발하기 시작하였으며, 어느 정도의 성과를 이루어 오고 있다. 예를 들면, 물을 기반으로 한 물질로부터 제설 기술로 만들어진 인공눈은 자연 눈을 대체할 수 있고, 또한, 그의 성능과 품질을 향상시킬 수 있다. 단점은 비용이 많이 들고 많은 양의 물과 전력이 필요하다는 것이다. 또한, 자연 눈과 마찬가지로 온도나 계절적인 기후 조건의 영향을 받기 쉽다. 또한, 상기 인공눈은 지구 온난화로 인해 겨울에조차도 만들어진 후에 땅에 닿자마자 흔히 녹아버리게 된다. 이는 막대한 자원의 낭비일뿐만 아니라, 현재 스키장에서의 높은 조작 비용의 원인이 된다. 이는 스키 스포츠의 대중화에도 어느 정도 부정적인 영향을 끼친다. 다른 기술로는 플라스틱 스키 잔디 및 이러한 스키 잔디로 구성되는 스키장이 있다. 마치 눈 위에서처럼 스키가 그 위로 슬라이딩하게 되나, 저항이 좀 더 크다. 게다가, 스키 잔디 및 스키 잔디로 구성되는 스키장의 물리 화학적 특성은 자연 눈 및 자연 스키장의 특성보다 훨씬 열등하다. 그들은 좀처럼 실제 스키의 풍부한 감동과 성과를 제공하지 못한다. 또한, 실리카겔로 만들어지는 인공눈과 인공 스키장이 있다. 그러나, 이런 종류의 인공눈은 물과 접촉하자마자 곧 부풀어 오른다. 이는 기본적으로 상업적 용도로 사용될 수 없다.Therefore, in many countries, research and development of artificial snow and artificial ski slopes have been started and some achievements have been made. For example, artificial eyes made from water-based materials with snow removal techniques can replace natural eyes and can also improve its performance and quality. The disadvantage is that it is costly and requires a large amount of water and power. Also, like natural snow, it is susceptible to temperature and seasonal climatic conditions. In addition, the artificial snow is made even in winter due to global warming, and it is often melted as soon as it touches the ground. This is not only a huge waste of resources, but also causes high operating costs in the current ski area. This has some negative effects on the popularization of skiing sports. Other technologies include plastic ski lawns and ski slopes that consist of these ski lawns. The ski slides over it as if it were snowing, but the resistance is a bit larger. In addition, the physical and chemical properties of ski slopes, which consist of ski lawns and ski lawns, are far inferior to those of natural snow and natural ski resorts. They rarely provide a rich impression and performance of actual skiing. There are also artificial snow and artificial ski slopes made of silica gel. However, this kind of artificial eye swells up as soon as it comes into contact with water. It can not be used basically for commercial purposes.
상술한 바의 인공 스키장은 인공 냉각된 눈으로 이루어지는 스키장이든, 스키 잔디 스키장이든, 또는 실리카겔 인공눈에 기초한 스키장이든지 간에 자연 스키장이 갖기 쉬운 동일한 제한들을 일부 갖기 쉽다. 즉, 차지하는 영역이 크고, 비용이 많이 들며, 계절 및 기후에 의존적이며, 특정, 환경 조건을 필요로 한다. 따라서, 어느 정도, 기후의 영향을 받지 않고, 비용이 적게 들며, 온도의 제한을 받지 않으면서 실내외에서 모두 이용 가능한 진정한 의미의 인공눈 및 인공스키장은 여전히 존재하지 않는다.The artificial ski areas described above are likely to have some of the same limitations that natural ski slopes have, whether they are ski slopes with artificially cooled snow, ski slope ski slopes or silica gel artificial snow slopes. That is, the area occupied is large, expensive, seasonal and climate dependent, and requires specific, environmental conditions. Thus, there is still no true artificial snow and artificial skiing available to all, indoors and outdoors, to some extent, unaffected by climate, costly, and temperature limited.
본 발명은 상기와 같은 종래 기술의 문제점을 해결하기 위하여 안출된 것으로서, 본 발명에서 해결하고자 하는 과제는 친환경적이고, 사계절 이용 가능하고, 인체에도 무해하며, 물로 제거 가능하며, 스키 타기에 가장 좋은 눈인 인공설과 자연설을 적당히 혼합한 적정설과 유사한 특성을 나타내어 레저 스포츠 산업 발전에 기여할 수 있는 신규한 인공 스노우 파우더 조성물 및 이를 이용한 스키 슬로프 설치 방법을 제공하고자 하는 것이다. SUMMARY OF THE INVENTION The present invention has been made in order to solve the problems of the prior art as described above, and it is an object of the present invention to solve the above problems. The present invention is to provide a novel artificial snow powder composition capable of contributing to the development of the leisure sports industry by showing characteristics similar to those of a proper combination of artificial and natural scenes, and a method of installing a ski slope using the artificial snow powder composition.
이를 위해, 본 발명은 폴리아크릴산나트륨(sodium polyacrylate) 100중량부, 팜 왁스(palm wax), 파라핀, 소이 왁스 및 비즈 왁스(bees wax)로 이루어지는 군으로부터 선택되는 유막 형성제 100~400중량부 및 비누(soap) 25~100중량부를 포함하는 스노우 파우더 조성물을 제공한다. To this end, the present invention relates to a composition comprising 100 to 400 parts by weight of an oil film forming agent selected from the group consisting of 100 parts by weight of sodium polyacrylate, palm wax, paraffin, soy wax and bees wax, 25 to 100 parts by weight of a soap.
상기 폴리아크릴산나트륨은 분자량 200~600만, 점도 480~760mPa·s, pH 9.0~10.0인 것이 바람직하다.The sodium polyacrylate preferably has a molecular weight of 200 to 6,000,000, a viscosity of 480 to 760 mPa 占 퐏, and a pH of 9.0 to 10.0.
상기 폴리아크릴산나트륨은 과립상 및 분말상인 것이 바람직하다.The sodium polyacrylate is preferably granular and powdery.
상기 유막 형성제는 팜 왁스인 것이 바람직하다.The oil film forming agent is preferably palm wax.
상기 팜 왁스는 팜 오일을 경화시킨 과립상인 것이 바람직하다.The palm wax is preferably a granular phase obtained by hardening palm oil.
상기 비누는 과립상 및 분말상인 것이 바람직하다.The soap is preferably granular and powdery.
또한, 본 발명은 본 발명의 상기 스노우 파우더 조성물을 스키 슬로프에 살포한 후, 미립자 수분을 분사하여 스노우 파우더를 활성화시키는 스키 슬로프 설치 방법을 제공한다.In addition, the present invention provides a method of installing a ski slope in which the snow powder composition of the present invention is sprayed on a ski slope and sprayed with water of a minute particle to activate the snow powder.
본 발명의 인공 스노우 파우더 및 이를 이용한 스키 슬로프 설치 방법은 조성물에 포함되는 성분이 친환경적이고, 슬로프만 존재한다면 시기나 장소의 제한이 없이 설치가 가능하고, 소량 삼키더라도 인체에 전혀 무해하며, 폐장시 물로 제거 가능한 특징이 있으므로 레저 스포츠 산업상 매우 유용한 발명이다.The artificial snow powder of the present invention and the method of installing a ski slope can be installed without limitations in terms of time or place if the components contained in the composition are environmentally friendly and only a slope exists. Even if a small amount of the slope is swallowed, It is a very useful invention in the leisure sports industry due to its water-removable characteristics.
도 1은 본 발명의 스노우 파우더를 지면에 살포한 모습을 나타낸 것이다.
도 2는 본 발명의 스노우 파우더 조성물의 열에 대한 안정성을 나타낸 결과이다.
도 3은 본 발명의 스노우 파우더 조성물의 염분에 대한 안정성을 나타낸 결과이다.
도 4는 본 발명의 스노우 파우더 조성물의 보습성을 나타낸 결과이다.
도 5는 본 발명의 스노우 파우더 조성물의 pH 영향을 나타낸 결과이다.1 shows a snow powder of the present invention sprayed on the ground.
2 shows the heat stability of the snow powder composition of the present invention.
3 is a graph showing the stability of the snow powder composition of the present invention against salinity.
Fig. 4 shows the moisture retention of the snow powder composition of the present invention.
Figure 5 shows the effect of pH on the snow powder composition of the present invention.
이하, 본 발명을 상세하게 설명한다.Hereinafter, the present invention will be described in detail.
본 발명의 발명자는 기존 자연설을 대체하기 위하여 개발된 바 있는 인공설의 문제점을 해결하기 위하여 연구를 거듭한 결과, 친환경적이고, 슬로프만 존재한다면 시기나 장소의 제한 없이 이용 가능하고, 스키 타기에 가장 좋은 형태인 인공설과 자연설을 적당히 혼합한 적정설과 유사한 형태로써 이를 소량 삼키더라도 인체에 전혀 무해하며, 폐장시 물로 제거 가능한 특징이 있는 신규한 인공설 조성물의 개발을 완료하여 이를 스키 슬로프에 성공적으로 설치할 수 있음을 확인하고 본 발명을 완성하였다.The inventor of the present invention has conducted studies to solve the problems of artificial theories which have been developed to replace existing natural scenes. As a result, the inventors of the present invention have found that they are eco-friendly and can be used without restriction of time or place if only slopes exist, It is a form similar to that of a fairly mixed form of artificial and natural texts. It is completely harmless to the human body even when a small amount of it is swallowed. And completed the present invention.
스키의 원리는 얼음에 압력을 가하면 얼음이 녹게 되고, 얼음 표면과 접촉 표면 사이에 물이 들어가고, 이 얼음은 표면의 홈을 메워주는 역할을 하여 마찰력을 감소시킴으로써 경사도에 따른 관성력으로 스키가 아래로 밀려나가는 원리이다. 따라서, 스키가 잘 미끄러지려면 반드시 마찰력이 필요하며, 스키면과 지면 사이에 발생한 마찰력이 열을 일으키고, 이 열로 순간적으로 눈이 녹으면서 스키가 미끄러져 내려가게 된다. The principle of skiing is that the ice is melted when the ice is pressurized, the water enters between the ice surface and the contact surface, and this ice serves to fill the grooves of the surface, thereby reducing the frictional force, It is a principle to be pushed out. Therefore, in order for a ski to slide well, a friction force is required, and friction generated between the ski surface and the ground causes heat, and the ski instantly slips down as the snow melts instantaneously.
이와 같은 스키의 작동 원리에 착안하여, 본 발명의 발명자는 자연설과 유사한 미끄럼성과 마찰력을 나타내는데 적합한 성분을 조합하여 스키타기에 가장 좋은 설질인 자연설과 인공성을 적당히 혼합한 적정설과 거의 유사한 특성을 나타내는 인공 스노우 파우더를 개발하였다.In view of the operation principle of the ski, the inventors of the present invention have found that the combination of the components suitable for showing the sliding property and the frictional force similar to those of the natural skiing is similar to the optimal skiing style in which natural snow and artificiality, Artificial snow powder.
본 발명은 폴리아크릴산나트륨(sodium polyacrylate) 100중량부, 팜 왁스(palm wax), 파라핀, 소이 왁스 및 비즈 왁스(bees wax)로 이루어지는 군으로부터 선택되는 유막 형성제 100~400중량부 및 비누(soap) 25~200중량부를 포함하는 스노우 파우더 조성물을 제공한다.The present invention relates to a composition comprising 100 to 400 parts by weight of an oil film forming agent selected from the group consisting of 100 parts by weight of sodium polyacrylate, palm wax, paraffin, soy wax and bees wax, ) ≪ / RTI >
상기 폴리아크릴산나트륨은 자연설과 같은 시각 효과를 제공하고, 응집성 및 다져짐 작용에 관여하며, 입자의 마찰력에 의한 미끄러짐의 적정 제어 작용을 하는 성분이다. 상기 폴리아크릴산나트륨은 분자량 200~600만, 점도 480~760mPa·s, pH 9.0~10.0의 특성을 갖는다. 또한, 상기 폴리아크릴산나트륨은 과립상 및 분말상일 수 있으며, 과립상과 분말상의 혼합상인 것이 가장 바람직하다. 과립상의 경우 60메쉬에 걸리는 정도의 크기이며, 분말상의 경우에는 60메쉬를 통과하는 크기일 수 있다. The sodium polyacrylate is a component that provides a visual effect such as natural stigma, participates in cohesion and agglomeration, and has an appropriate control effect of slip due to the frictional force of the particles. The sodium polyacrylate has a molecular weight of 200 to 6,000,000, a viscosity of 480 to 760 mPa 占 퐏, and a pH of 9.0 to 10.0. In addition, the sodium polyacrylate may be granular or powdery, and most preferably a mixture of granular and powdery phases. It may be about 60 meshes in the case of granules and 60 meshes in the case of powders.
상기 유막 형성제는 인공설의 시각적인 효과를 자연설과 유사하게 하며, 스키면과의 마찰에 의한 융해로 유막을 형성하여 자연설과 유사한 미끄러짐 효과를 나타낸다. 상기 유막 형성제는 팜 왁스(palm wax), 파라핀, 소이 왁스 및 비즈 왁스(bees wax)로 이루어지는 군으로부터 선택될 수 있으며, 팜 왁스인 것이 바람직하다. 상기 팜 왁스는 팜 오일을 경화시켜 과립상으로 제조될 수 있다. 과립상의 제조 방법은 본 발명의 기술 분야에서 통상의 지식을 가진 자에게 자명한 사항이다. The oil film forming agent makes the visual effect of artificial hair similar to that of natural scenery, and forms an oil film by melting due to friction with the ski surface, thereby exhibiting a slip effect similar to that of natural scenery. The oil film forming agent may be selected from the group consisting of palm wax, paraffin, soy wax and bees wax, and is preferably palm wax. The palm wax may be prepared into a granular form by hardening the palm oil. The preparation method of the granular phase is obvious to those skilled in the art.
상기 유막 형성제는 본 발명의 스노우 파우더 조성물 성분 중 폴리아크릴산나트륨 100중량부에 대하여 100~400중량부로 혼합된다. 상기 함량이 100중량부 미만인 경우에는 유막 형성력이 약화되어 스키면의 미끄러짐 현상이 약하고, 상기 함량이 400중량부를 초과하는 경우에는 자연설에 비하여 지나치게 미끄러운 현상이 나타날 뿐만 아니라 본 발명의 스노우 파우더의 응집과 다져짐 현상이 현저히 저하되는 문제점이 있다.The oil film forming agent is mixed in 100 to 400 parts by weight with respect to 100 parts by weight of sodium polyacrylate in the snow powder composition component of the present invention. When the content is less than 100 parts by weight, the oil-film forming ability is weakened and slippage of the ski surface is weak. When the content is more than 400 parts by weight, not only is the slippery phenomenon more pronounced than in natural scenery, There is a problem that the compacting phenomenon remarkably deteriorates.
스테아르산은 가장 널리 알려진 지방산으로 옥타데칸산이라고도 하며, 식물에서 추출한 지방산의 일종으로 기름과 같은 느낌으로서 비누의 주재료가 된다. Stearic acid is the most widely known fatty acid, also known as octadecanoic acid, and is a kind of fatty acid extracted from plants, and it is the main ingredient of soap as oil.
한편, 비누는 스테아르산에 NaOH가 첨가되어 제조되는 것이므로 물과 만나면 이 성분들이 녹게되며, 결정상의 팜 왁스와 비누가 배합 살포된 상태에서 비눗물이나 물을 분사하면 팜 왁스를 일부 녹여 물에 노출된 비누처럼 유막과 수막이 동시에 형성되어 미끄럼을 극대화할 수 있다. 또한, 스키의 원리 즉, 중력의 작용에 의해 플레이트가 무게를 가해 경사면을 미끄러지면 눈 입자가 압력과 마찰열이 발생해 녹아내려 마찰력이 감소하는 것과 마찬가지로 팜 왁스가 열을 받아 유막을 형성하여 마찰력이 줄어들게 된다. Since the soap is prepared by adding NaOH to stearic acid, when these ingredients are mixed with water, the components are dissolved. When the soap is mixed with the palm wax of the crystalline phase, if soapy water or water is sprayed, the palm wax is partially melted and exposed to water Like oil soap, oil film and water film can be formed at the same time, maximizing slip. In addition, the principle of skiing, that is, when the plate is weighted by the action of gravity, when the slope slides, snow particles are generated by pressure and frictional heat and melted down to decrease the frictional force, and the palm wax is heated to form an oil film, .
또한, 그래뉼 왁스는 자연설을 전혀 기대할 수 없는 여름이나 중동지역에서도 녹지 않고 결정이나 분말형태를 유지할 수 있을 뿐만 아니라 중동지역과 같이 태양의 복사열과 플레이트의 마찰열로 인해 그래뉼 왁스 표면이 녹을 경우 유막을 형성하여 별도로 물을 분사하지 않더라도 미끄럼을 극대화할 수 있다. 이와 같이 스노우 파우더 조성물 중 비누를 사용하지 않더라도 충분한 미끄럼 효과를 얻을 수 있는 경우 비누를 생략할 수 있다. In addition, granule wax is not soluble in the summer or the Middle East, where natural stalks can not be expected at all. It can not only maintain the shape of crystals and powder, but also form the oil film when the granular wax surface melts due to the heat of solar radiation and frictional heat of the plate, So that the slip can be maximized even if no water is injected separately. When the snow powder composition can provide a sufficient sliding effect without using the soap, the soap can be omitted.
상기 비누는 수산화나트륨과 스테아르산을 비누화 반응시켜 제조되는 것이며, 미끄러짐 증가, 응집력 증가, 다져짐 증가의 효과를 나타낸다. 또한, 수분 살포시 융해 작용이 일어나서 유막 형성제의 융해에 의하여 미끄러짐 현상을 향상시킬 수 있다. 상기 비누는 과립상 및 분말상인 것이 바람직하며, 비눗물 살포시엔 생략해도 무방하다. The soap is produced by saponifying sodium hydroxide and stearic acid, and exhibits an effect of increasing slip, increasing cohesion, and increasing compaction. In addition, a melting action occurs during the spraying of water, and the slipping phenomenon can be improved by melting of the oil film forming agent. The soap is preferably granular and powdery, and may be omitted when spraying soapy water.
상기와 같은 조성 및 함량으로 본 발명의 스노우 파우더 조성물을 제조할 수 있으며, 상기 각 성분이 혼합된 스노우 파우더 조성물은 스키 슬로프와 같은 원하는 지면에 연중 상시 살포되어 자연설 및 인공설을 대체할 수 있다. The snow powder composition of the present invention can be prepared by the above composition and content. The snow powder composition in which the above components are mixed can be sprayed all over the year on a desired surface such as a ski slope, thereby replacing natural and artificial snow.
따라서, 본 발명은 전술한 스노우 파우더 조성물을 스키 슬로프에 살포한 후, 분무기 또는 스프링클러 등을 이용하여 미립의 수분을 골고루 분사하여 스노우 파우더를 활성화시키는 스키 슬로프 설치 방법을 제공한다.Accordingly, the present invention provides a method of installing a ski slope in which the above-described snow powder composition is sprayed on a ski slope, spraying fine water evenly using an atomizer, a sprinkler, or the like to activate the snow powder.
본 발명의 스노우 파우더 살포 두께는 통상적으로 20~60cm일 수 있으며, 사용 조건에 따라 증감될 수도 있다. 원하는 지면에 살포된 후, 분무기나 스프링클러를 사용하여 미립자의 물을 분사함으로써 스노우 파우더를 활성화시키면 스키 타기에 가장 좋은 자연설과 인공설이 잘 배합된 적정설과 동일한 조건의 스키 인공 슬로프가 완성된다. The snow powder spraying thickness of the present invention may be generally 20 to 60 cm, and may be increased or decreased depending on conditions of use. After spraying on the desired surface, spraying the water of the particulate matter using a sprayer or sprinkler activates the snow powder, and the ski artificial slope is completed with the same conditions as the optimal snowflakes with the best combination of natural and artificial snow.
이하에서는, 구체적인 실시예를 통하여 본 발명을 더욱 상세하게 설명한다. 하기 실시예는 본 발명의 바람직한 하나의 구체예를 기재한 것이며, 하기 실시예에 기재된 사항에 의하여 본 발명의 권리범위가 한정되어 해석되는 것이 아님이 명백하다.Hereinafter, the present invention will be described in more detail with reference to specific examples. The following examples illustrate one preferred embodiment of the present invention and are not to be construed as limiting the scope of the present invention by the matters described in the following examples.
[[ 실시예Example ]]
1. One. 스노우Snow 파우더 조성물의 열에 대한 안정성 Stability of the powder composition against heat
분자량 200~600만, 점도 480~760mPa·s 및 pH 9.0~10.0의 물성을 갖는 분말 및 과립상 폴리아크릴산나트륨 100g, 과립상 팜 왁스 100g 및 분말상 비누 25g의 혼합물을 0.2 및 0.5% 수용액으로 제조하였다. 각각의 수용액을 1시간 동안 40, 60, 80 및 100℃로 가열하였다. 식힌 후 25℃에서 30rpm으로 각각의 점도를 측정하였다. 도 2에 나타낸 바와 같이, 본 발명의 스노우 파우더 조성물의 점도는 온도에 관계없이 매우 안정함을 확인하였다.A mixture of 100 g of powdery and granular sodium polyacrylate having a molecular weight of 200 to 6,000,000, a viscosity of 480 to 760 mPa 및 and a pH of 9.0 to 10.0, 100 g of granular palm wax and 25 g of powdery soap was prepared in 0.2 and 0.5% aqueous solution . Each aqueous solution was heated to 40, 60, 80 and 100 < 0 > C for 1 hour. After cooling, the respective viscosities were measured at 25 DEG C and 30 rpm. As shown in FIG. 2, it was confirmed that the viscosity of the snow powder composition of the present invention was very stable regardless of the temperature.
2. 2. 스노우Snow 파우더 조성물의 염분에 의한 영향 Influence of salt composition of powder composition
실시예 1로부터 제조된 스노우 파우더 조성물의 0.2 및 0.5% 수용액에 일정 농도의 염분을 첨가하였다. 25℃에서 30rpm으로 각각의 점도를 측정하였다. 도 3에 나타낸 바와 같이, 본 발명의 스노우 파우더 조성물의 점도는 염분 증가와 함께 감소하였으나 감소율은 미약함을 확인하였다.A constant concentration of salt was added to the 0.2 and 0.5% aqueous solutions of the snow powder compositions prepared from Example 1. The respective viscosities were measured at 25 DEG C and 30 rpm. As shown in FIG. 3, the viscosity of the snow powder composition of the present invention was decreased with increasing salinity, but it was confirmed that the decrease rate was insignificant.
3. 3. 스노우Snow 파우더 조성물의 보습성 Moisturizing property of powder composition
실시예 1로부터 제조된 스노우 파우더 조성물과 대조군으로서 구아검 및 CMC-Na의 0.05, 0.1 및 0.5% 수용액을 각각 제조하였다. 실온에서 준비된 각 용액들을 2cm×15cm의 종이필터에 40분 동안 담군 후, 각 수용액들이 종이필터에 빨려 올라긴 길이를 측정하였다. 도 4에 나타난 바와 같이, 각 성분의 흡수된 높이는 농도에 비례하여 감소하였으며, 이와 같은 효과는 보습성의 증대를 의미하는데, 본 발명의 스노우 파우더 조성물의 경우 대조군과 비교하여 가장 강력한 보습성을 가지는 것으로 확인되었다.0.05, 0.1 and 0.5% aqueous solutions of guar gum and CMC-Na, respectively, were prepared as the control and snow powder compositions prepared from Example 1, respectively. Each solution prepared at room temperature was immersed in a paper filter of 2 cm x 15 cm for 40 minutes, and each aqueous solution was sucked into a paper filter to measure its length. As shown in FIG. 4, the absorbed height of each component decreased in proportion to the concentration. Such an effect indicates an increase in moisturizing property. In the case of the snow powder composition of the present invention, .
4. 4. 스노우Snow 파우더 조성물의 pH 안정성 PH stability of powder composition
실시예 1로부터 제조된 스노우 파우더 조성물 0.5% 수용액, 대조군으로서 구아검 1% 수용액 및 CMC-Na 1% 수용액을 각각 제조하였다. 각 수용액에 일정 pH로 조절한 HCl 희석액 또는 NaOH 희석액을 첨가하였다. 25℃에서 30rpm으로 각각의 점도를 측정하였다. 도 5에 나타난 바와 같이, 본 발명의 스노우 파우더 조성물은 대조군과 대비하여 절반 정도의 농도에도 불구하고, 높은 점도를 가짐을 확인할 수 있다.A 0.5% aqueous solution of snow powder prepared in Example 1, a 1% aqueous solution of guar gum and a 1% aqueous solution of CMC-Na as control were prepared. To each aqueous solution was added a diluted HCl or NaOH solution adjusted to a constant pH. The respective viscosities were measured at 25 DEG C and 30 rpm. As shown in FIG. 5, the snow powder composition of the present invention has a high viscosity in spite of the concentration of about half that of the control group.
5. 5. 스노우Snow 파우더 조성물의 미끄러짐 특성 비교 Comparison of Slip Characteristics of Powder Compositions
본 발명의 스노우 파우더 조성물을 경사도 20°, 슬로프 길이 1m인 모형 슬로프에 3cm 두께로 살포하고 물을 분무하여 활성화시켰다. 대조군으로서 동일한 모혈 슬로프에 자연설을 덮고, 무게 1kg의 추를 장착한 모형 보드(2cm×10cm)의 미끄러짐 정도를 비교하였다. 모형 슬로프의 상부에 모형 보드를 두고 10N의 힘을 가하여 미끄러져 내려오는 길이를 측정하여 아래 표 1에 나타내었다.The snow powder composition of the present invention was sprayed on a model slope having a slope of 20 DEG and a slope length of 1 m to a thickness of 3 cm and sprayed with water to activate the snow powder composition. As a control group, the slippage of a model board (2 cm x 10 cm) equipped with a weight of 1 kg was compared with that of the same wrestling slope. The model board is placed on the top of the model slope, and the length of sliding down by applying a force of 10 N is measured and shown in Table 1 below.
표 1에 나타난 바와 같이, 본 발명의 스노우 파우더 조성물은 자연설과 유사한 미끄러짐 현상을 보임을 확인하였다.As shown in Table 1, it was confirmed that the snow powder composition of the present invention showed a slip phenomenon similar to that of natural snow.
Claims (7)
상기 폴리아크릴산나트륨 및 상기 비누는 과립상 및 분말상인 것을 특징으로 하는 스노우 파우더 조성물.100 parts by weight of sodium polyacrylate; 100 to 400 parts by weight of an oil film forming agent selected from the group consisting of palm wax, paraffin, soy wax and bees wax; And 25 to 100 parts by weight of a soap,
Wherein the sodium polyacrylate and the soap are granular and powdery.