KR101832793B1 - Plastic resin composition having improved anti-abrasion property and anti heat strain - Google Patents
Plastic resin composition having improved anti-abrasion property and anti heat strain Download PDFInfo
- Publication number
- KR101832793B1 KR101832793B1 KR1020170030689A KR20170030689A KR101832793B1 KR 101832793 B1 KR101832793 B1 KR 101832793B1 KR 1020170030689 A KR1020170030689 A KR 1020170030689A KR 20170030689 A KR20170030689 A KR 20170030689A KR 101832793 B1 KR101832793 B1 KR 101832793B1
- Authority
- KR
- South Korea
- Prior art keywords
- resin composition
- plastic resin
- cosmetic container
- present
- astm
- Prior art date
Abstract
Description
본 발명은 향상된 내마모성 및 내열변형성을 갖는 화장품 용기 제작용 플라스틱 수지 조성물에 관한 것이며, 더욱 구체적으로 이를 이용하여 제조된 화장품 용기의 본체 및 뚜껑의 개폐마찰에 의한 마찰 가루 발생이 획기적으로 감소된 플라스틱 수지 조성물에 관한 것이다.TECHNICAL FIELD The present invention relates to a plastic resin composition for manufacturing a cosmetic container having improved wear resistance and thermal deformation resistance, and more particularly, to a plastic resin composition for manufacturing a cosmetic container using the plastic resin ≪ / RTI >
화장품 용기 등을 제작할 때 제작시 성형의 용이성으로 인하여 다양한 플라스틱 수지 조성물이 사용되며, 특히 화장품에 함유되는 다양한 화학 성분들과의 화학 반응을 미연에 차단하기 위하여 주로 아세탈(acetal), 폴리아세탈(polyacetal) 또는 폴리포름알데하이드(polyformaldehyde)로도 알려진 플라스틱 수지인 폴리옥시메틸렌(Polyoxymethylene, POM)이 사용된다.In order to prevent the chemical reaction with various chemical components contained in cosmetics, acetal, polyacetal (polyacetal), and the like are used in order to prevent the chemical reaction with various chemical components contained in cosmetics. ) Or polyoxymethylene (POM), a plastic resin also known as polyformaldehyde.
한편, 크림 타입의 화장품은 주로 화장품이 담기는 본체와 본체를 덮는 뚜껑으로 구성되는 화장품 용기에 담기게 되며, 상기 본체와 뚜껑에는 통상적으로 대칭되는 나사산과 나사골이 형성되어 있어 이들은 나사체결 방식에 의하여 사용자에 의하여 개폐된다.Meanwhile, the cream type cosmetics are mainly contained in a cosmetic container composed of a main body containing a cosmetic product and a lid covering the main body, and the main body and the lid are usually formed with symmetrical threads and threaded screws. It is opened and closed by the user.
그러나, 폴리옥시메틸렌 등으로 제조된 본체와 뚜껑은 형태의 차이 및 첨가되는 안료 성분 등의 차이로 인하여 서로 상이한 열팽창률을 갖게 되며, 이에 따라 본체와 뚜껑이 최초 제작된 치수와 상이하게 변형되는 치수 변형을 일으키게 되며, 이와 같은 치수 변형에 따라 본체 및 뚜껑에 형성된 나사산과 나사골 간에 미세한 비대칭 부분이 발생하게 되며, 이와 같이 열팽창률의 차이에 의해 야기된 비대칭에 의하여 본체와 뚜껑의 나사 체결시 나사산과 나사골이 서로 마찰되어 심하게 마모되는 현상이 발생하게 되고 나아가 이러한 마모에 의하여 적지 않은 마모 부산물인 플라스틱 가루가 발생하게 된다.However, the body and the lid made of polyoxymethylene or the like have different thermal expansion rates due to differences in shape and pigment components added, and accordingly, the body and the lid are dimensioned to be deformed differently from the originally produced dimensions And a minute asymmetric portion is formed between the screw thread and the screw thread formed on the body and the lid due to the dimensional deformation. As a result of the asymmetry caused by the difference in thermal expansion rate, The threaded balls are abraded with each other to cause a severe wear, and further, such wear causes the plastic powder as a byproduct of the wear and tear.
한편, 이와 같이 발생된 플라스틱 가루는 인체의 피부 등에 직접 도포되는 화장품에 섞이게 됨으로써 인체의 피부에 알레르기성 발진 등을 야기하는 원인이 된다.On the other hand, the plastic powder thus generated is mixed with cosmetics directly applied to the skin of a human body, thereby causing an allergic rash on the skin of the human body.
한편, 하기 특허문헌 1에서는 티트리, 명반 및 맥반석 조성물이 함유된 화장품 용기를 개시하고 있으나, 이와 같은 화장품 용기는 여전히 마찰에 의하여 가루가 발생하는 문제를 해결하지 못하는 한계를 지니고 있다.On the other hand, Patent Document 1 discloses a cosmetic container containing a tea tree, alum and a quartz composition, but such a cosmetic container still has a limitation in that it can not solve the problem that powder is generated due to friction.
따라서, 지속적인 개폐 작동에 의하더라도 마모에 의한 가루 등이 전혀 발생하지 않는 화장품 용기 제작용 플라스틱 수지 조성물의 개발이 절실히 요구되는 실정이다.Therefore, there is an urgent need to develop a plastic resin composition for producing a cosmetic container which does not cause any powder or the like due to abrasion even by continuous opening and closing operations.
[특허문헌][Patent Literature]
특허문헌 1: 대한민국 등록특허 제10-1702087호 (2017.02.02)Patent Document 1: Korean Patent No. 10-1702087 (Feb.
이에 본 발명에서는 상기 문제점을 해결하고자 폴리프로필렌(polypropylene), 실리콘 및 폴리카보네이트(polycarbonate)를 혼합한 수지 조성물을 이용하여 강한 내마모성 및 현저히 감소된 열변형율을 갖는 화장품 용기를 제작할 수 있음을 발견하였고, 본 발명은 이에 기초하여 완성되었다.Accordingly, the present invention has been made to solve the above-mentioned problems, and it has been found that a cosmetic container having strong abrasion resistance and a significantly reduced heat distortion rate can be manufactured using a resin composition obtained by mixing polypropylene, silicone and polycarbonate, The present invention has been completed on this basis.
본 발명은 상기한 해결과제를 달성하기 위한 수단으로, 실리콘 3-6 중량%;
폴리카보네이트(polycarbonate) 1-5 중량%;
아라미드섬유(aramid fiber) 0.5-5 중량%; 및
나머지 폴리프로필렌(polypropylene)으로 이루어진 화장품 용기 제작용 플라스틱 수지 조성물로서,
상기 조성물을 이용하여 제조된 화장품 용기의 마찰감소 무게는 ASTM D-1630에 따라 1,000회 마찰회전시 5㎎ 이하이고; ASTM D648에 따라 0.45 MPa 기압조건 하에 측정된 열변형 온도는 160℃ 이상이며, 1.85 MPa 기압조건 하에서는 115℃ 이상으로 유지되는 것을 특징으로 하는 화장품 용기 제작용 플라스틱 수지 조성물을 제공한다.As a means for achieving the above-mentioned object, the present invention provides a method of manufacturing a semiconductor device, comprising:
1-5% by weight of polycarbonate;
From 0.5 to 5% by weight of an aramid fiber; And
The present invention relates to a plastic resin composition for the production of a cosmetic container made of the remaining polypropylene,
The friction reducing weight of the cosmetic container made using the composition is less than or equal to 5 mg per 1,000 revolutions per minute according to ASTM D-1630; Wherein the heat distortion temperature measured under the atmospheric pressure of 0.45 MPa according to ASTM D648 is 160 DEG C or more and is maintained at 115 DEG C or more under the atmospheric pressure of 1.85 MPa.
삭제delete
삭제delete
삭제delete
삭제delete
본 발명에 따른 플라스틱 수지 조성물은 이를 이용하여 제작된 화장품 용기의 본체 및 뚜껑의 개폐마찰에 의한 마모 가루 발생을 획기적으로 감소시킬 수 있는 장점을 갖는다.The plastic resin composition according to the present invention has the advantage that the generation of abrasion powder due to the opening and closing friction of the body and the lid of the cosmetic container manufactured using the plastic resin composition can be remarkably reduced.
본 발명을 좀 더 구체적으로 설명하기 전에, 본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정되어서는 아니되며, 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다. 따라서, 본 명세서에 기재된 실시 예의 구성은 본 발명의 바람직한 하나의 예에 불과할 뿐이고, 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 균등물과 변형 예들이 있을 수 있음을 이해하여야 한다. Before describing the invention in more detail, it is to be understood that the words or words used in the specification and claims are not to be construed in a conventional or dictionary sense, It should be interpreted as meaning and concept consistent with the technical idea of the present invention. Therefore, the constitution of the embodiments described in the present specification is merely a preferred example of the present invention, and does not represent all the technical ideas of the present invention, so that various equivalents and variations And the like.
이하, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 본 발명을 용이하게 실시할 수 있도록, 본 발명의 바람직한 실시 예들을 상세히 설명한다.Hereinafter, preferred embodiments of the present invention will be described in detail so that those skilled in the art can easily carry out the present invention.
본 발명은 향상된 내마모성 및 낮은 열변형율을 갖는 화장품 용기 제작용 플라스틱 수지 조성물에 관한 것이며, 더욱 구체적으로 이를 이용하여 제조된 화장품 용기의 본체 및 뚜껑의 개폐마찰에 의한 마찰 가루 발생이 획기적으로 감소된 플라스틱 수지 조성물에 관한 것이다.TECHNICAL FIELD The present invention relates to a plastic resin composition for manufacturing a cosmetic container having improved wear resistance and a low thermal deformation rate, and more specifically, to a plastic resin composition for manufacturing a cosmetic container using a plastic To a resin composition.
본 발명의 일 구현 예에 따른 플라스틱 조성물은 예르 들어 화장품 용기 제작용으로 사용될 수 있으며, 폴리프로필렌(polypropylene) 90 내지 95 중량%; 실리콘 3 내지 6 중량%; 및 폴리카보네이트(polycarbonate) 1 내지 5 중량%;를 포함할 수 있다.The plastic composition according to one embodiment of the present invention can be used for making cosmetic containers, and comprises 90 to 95% by weight of polypropylene; 3 to 6% by weight of silicone; And 1 to 5% by weight of polycarbonate.
본 발명은 종래에 화장품 용기 제작용으로 주로 사용되던 소재인 POM을 대체할 수 있음에 특징이 있다.The present invention is characterized in that it can replace POM which is a material conventionally used for manufacturing a cosmetic container.
즉, 본 발명은 종래의 POM 수지가 지녔던 개폐 작동에 의한 마모 가루 발생을 방지하기 위하여 POM을 사용하지 않고 폴리프로필렌을 사용하였으며, 특히 내마모성 및 내화학성을 획기적으로 향상시키기 위하여 폴리프로필렌과 함께 실리콘 및 폴리카보네이트를 혼합하는 점에 특징이 있다.That is, the present invention uses polypropylene instead of POM in order to prevent the generation of abrasion powder by the opening and closing operation of the conventional POM resin. Particularly, in order to remarkably improve the abrasion resistance and chemical resistance, It is characterized by mixing polycarbonate.
폴리프로필렌은 본 발명에 따른 수지 조성물의 주성분에 해당하며, 물성이 폴리에틸렌과 매우 비슷하지만 비중은 더욱 작아 가벼운 특징이 있다(약 0.9 내지 0.92). The polypropylene corresponds to the main component of the resin composition according to the present invention, and has a light weight (about 0.9 to 0.92) because the physical properties thereof are very similar to those of polyethylene but are smaller in specific gravity.
폴리프로필렌은 고밀도 폴리에틸렌과 비교하면 연화 온도가 현저하게 높고 인장강도, 굽힘강도, 강성 등이 크며 비교적 저가인 장점이 있으나 내한성 및 내충격성이 약한 단점을 갖는다.Polypropylene is remarkably high in softening temperature, tensile strength, bending strength, rigidity, and comparatively low in cost compared to high density polyethylene, but has a disadvantage of low cold resistance and low impact resistance.
본 발명에 따른 조성물에서 폴리프로필렌은 90 내지 95 중량%의 비율로 포함되고 내화학성을 높이는 기능을 발휘하며, 90 중량% 미만으로 포함되는 경우는 플라스틱 성형성이 저하되고 내화학성이 낮아지며 다른 성분의 함량이 늘어나게 되어 비경제적이고, 95 중량%를 초과하는 경우는 내마모성 및 내충격성이 저하되고 열변형률이 높아지는 문제가 있다.In the composition according to the present invention, polypropylene is contained in a proportion of 90 to 95% by weight and exhibits a function of improving chemical resistance. When it is contained in an amount of less than 90% by weight, plastic moldability is lowered, chemical resistance is lowered, If the content exceeds 95% by weight, the abrasion resistance and impact resistance are lowered and the heat distortion rate is increased.
한편, 상기 실리콘(silicone)은 플라스틱의 내마모성 및 내충격성을 향상시키고 열변형성 낮추는 기능을 발휘한다.On the other hand, the silicone improves the abrasion resistance and the impact resistance of the plastic and exhibits the function of lowering the thermal deformation.
본 발명에서는 무초산 실리콘을 사용하는 것이 바람직하다.In the present invention, it is preferable to use non-nitric acid.
실리콘은 3 내지 6 중량%의 비율로 포함되며, 3 중량% 미만으로 포함되는 경우는 내마모성 향상 및 열변형 저감 효과가 낮아지는 문제가 있으며, 6 중량%를 초과하는 경우는 수지의 성형성이 저하되는 문제가 있다.Silicon is contained in a proportion of 3 to 6% by weight. When it is contained in an amount of less than 3% by weight, there is a problem that wear resistance is improved and the effect of reducing heat distortion is lowered. There is a problem.
폴리카보네이트는 본 발명에서 내마모성 및 내충격성을 더욱 향상시키고, 특히 화장품 용기에 광택성을 부여하는 기능을 발휘한다.The polycarbonate further improves abrasion resistance and impact resistance in the present invention, and particularly exhibits a function of imparting gloss to the cosmetic container.
폴리카보네이트는 1 내지 5 중량%의 비율로 포함되며, 1 중량% 미만으로 포함되는 경우는 내마모성 및 내충격성이 저하되는 문제가 있으며, 5 중량%를 초과하는 경우는 비경제적이고 성형성이 저하되는 문제가 있다.Polycarbonate is contained in a proportion of 1 to 5% by weight. When it is contained in an amount of less than 1% by weight, abrasion resistance and impact resistance are deteriorated. When it exceeds 5% by weight, .
본 발명의 다른 구현 예에 따른 플라스틱 수지 조성물은 아라미드섬유(aramid fiber)를 0.5 내지 5 중량%의 비율로 더욱 포함할 수 있다.The plastic resin composition according to another embodiment of the present invention may further include an aramid fiber in an amount of 0.5 to 5% by weight.
이때, 상기 아라미드 섬유는 플라스틱의 내마모성을 더욱 향상시킴으로써 본체와 뚜껑의 지속적인 개폐 동작에 의해도 마모 가루가 전혀 발생하지 않게 하는 기능을 발휘한다.At this time, the aramid fiber further improves the abrasion resistance of the plastic, thereby exhibiting a function of preventing the abrasion powder from being generated at all by the continuous opening and closing operations of the main body and the lid.
한편, 본 발명의 다른 구현 예에 따른 플라스틱 수지 조성물은 가소제(plasticizers), 산화방지제(antioxidants), 열안정제(heat stabilizers), 자외선안정제(UV stabilizer), 난연제(flame retardents), 활제, 대전방지제, 및 충격보강제로 이루어진 군으로부터 선택된 성분을 0.5 내지 5 중량%의 비율로 더욱 포함할 수 있다.Meanwhile, the plastic resin composition according to another embodiment of the present invention may include plasticizers, antioxidants, heat stabilizers, UV stabilizers, flame retardants, lubricants, antistatic agents, And an impact modifier in a proportion of 0.5 to 5% by weight.
가소제는 수지 조성물에 유연성을 부여하고 가공 작업성을 향상시킴과 동시에 팽창성을 증가시키는 기능을 발휘한다.The plasticizer imparts flexibility to the resin composition, improves the workability of the processing, and exhibits the function of increasing the expandability.
산화방지제는 플라스틱과 산소의 접촉에 의한 화학반응을 억제 또는 차단시킴으로써 플라스틱이 산화반응에 의하여 분해되어 고유물성을 상실하는 것을 방지한다.The antioxidant inhibits or blocks the chemical reaction caused by the contact between the plastic and the oxygen, thereby preventing the plastic from being decomposed by the oxidation reaction and losing its inherent properties.
열안정제는 고온에서 조성물을 혼합 또는 성형할 경우 발생할 수 있는 플라스틱 수지의 열적 분해를 억제 또는 차단하는 기능을 발휘한다.The heat stabilizer has a function of inhibiting or blocking the thermal decomposition of the plastic resin which may occur when the composition is mixed or molded at a high temperature.
자외선안정제는 자외선에 의하여 플라스틱 수지가 분해되어 색변 또는 기계적 성질이 상실되는 것을 억제 또는 차단시키는 기능을 발휘한다.The ultraviolet light stabilizer exerts a function of inhibiting or blocking the loss of color or mechanical properties of the plastic resin due to decomposition by ultraviolet rays.
난연제는 플라스틱 수지의 가연성을 감소시키는 기능을 발휘한다.The flame retardant exhibits a function of reducing the flammability of the plastic resin.
활제는 카렌다 가공, 성형, 압출 중에 플라스틱과 접촉하는 금형 등의 금속표면을 윤활시켜 유동을 도움으로써 가공성을 향상시키는 기능을 발휘한다.The lubricant functions to enhance workability by lubrication of a metal surface such as a mold which contacts plastic during calendering, molding and extrusion, thereby helping to flow.
대전방지제는 플라스틱 표면에 형성되는 정전기 발생을 억제 또는 제거하는 기능을 발휘한다.The antistatic agent exerts a function of suppressing or eliminating the generation of static electricity formed on the plastic surface.
충격 보강제는 플라스틱의 내충격성을 더욱 향상시키는 기능을 발휘한다.The impact modifier exhibits a function of further improving the impact resistance of the plastic.
상기 가소제(plasticizers), 산화방지제(antioxidants), 열안정제(heat stabilizers), 자외선안정제(UV stabilizer), 난연제(flame retardents), 활제, 대전방지제, 및 충격보강제로는 플라스틱 기술분야에 통상적으로 사용되는 공지의 물질을 선택하여 사용하는 것이 가능하다.The plasticizers, antioxidants, heat stabilizers, UV stabilizers, flame retardants, lubricants, antistatic agents and impact modifiers are commonly used in the plastics arts It is possible to select and use a known substance.
본 발명의 상기 다양한 구현 예에 따른 수지 조성물을 이용하여 제조된 플라스틱 시편은 ASTM D-1630에 따라 1,000회 마찰회전시 마찰로 감소되는 시편의 무게가 5㎎ 이하인 특성을 지닌다.The plastic specimen produced using the resin composition according to various embodiments of the present invention has a characteristic that the weight of the specimen reduced to friction by 1,000 rubbing rotations according to ASTM D-1630 is 5 mg or less.
즉, 본 발명에 따른 조성물을 이용하여 화장품 용기 등의 본체 및 뚜껑을 제조하는 경우 지속적인 나사 개폐작동에 의하더라도 마모 가루가 전혀 발생하지 않는 획기적인 장점을 갖는다.That is, when a body and a lid such as a cosmetic container are manufactured using the composition according to the present invention, there is an epoch-making advantage that wear powder is not generated at all even when the screw is opened and closed.
또한, 본 발명의 상기 다양한 구현 예에 따른 수지 조성물을 이용하여 제조된 시편은 ASTM D648에 의하여 0.45 MPa 기압조건 하에 측정된 열변형 온도가 160℃ 이상이며, ASTM D648에 의하여 1.85 MPa 기압조건 하에 측정된 열변형 온도가 115℃ 이상인 특징을 갖는다.The specimen prepared using the resin composition according to the various embodiments of the present invention has a heat distortion temperature of 160 ° C or more measured under 0.45 MPa atmospheric pressure according to ASTM D648 and measured under a pressure of 1.85 MPa according to ASTM D648 Lt; RTI ID = 0.0 > 115 C < / RTI >
즉, 본 발명에 따른 조성물을 이용하여 화장품 용기 등의 본체 및 뚜껑을 제조하는 경우 본체와 뚜껑에 안료 등 서로 상이한 성분이 함유되거나 형태가 상이하더라도 열에 따른 팽창률의 변화가 거의 없게 되어 형태 변형에 따른 나사산과 나사골의 불일치에 의하여 마모 가루가 발생되는 것이 더욱 방지되는 장점을 갖는다.That is, when a body and a lid of a cosmetic container or the like are manufactured using the composition according to the present invention, even if different components such as a pigment are contained in the body and the lid, or the form is different, there is almost no change in the expansion ratio due to heat, There is an advantage that the generation of abrasive powder by the inconsistency between the thread and the thread is further prevented.
이하 다양한 실시 예 및 비교 예를 통하여 본 발명을 좀 더 구체적으로 살펴보지만, 하기 예에 본 발명의 범주가 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to various examples and comparative examples, but the scope of the present invention is not limited to the following examples.
[실시 예 1][Example 1]
폴리프로필렌(polypropylene) 950g, 실리콘 50g 및 폴리카보네이트(polycarbonate) 30g을 믹서에 넣고 혼합하여 플라스틱 수지 조성물을 제조하였다.950 g of polypropylene, 50 g of silicone, and 30 g of polycarbonate were put in a mixer and mixed to prepare a plastic resin composition.
[실시 예 4] - 아라미드섬유(aramid fiber) 추가[Example 4] - Addition of aramid fiber (aramid fiber)
삭제delete
삭제delete
삭제delete
삭제delete
폴리프로필렌(polypropylene) 950g, 실리콘 50g, 폴리카보네이트(polycarbonate) 30g 및 아라미드섬유(aramid fiber) 30g을 믹서에 넣고 혼합하여 플라스틱 수지 조성물을 제조하였다.950 g of polypropylene, 50 g of silicone, 30 g of polycarbonate and 30 g of aramid fiber were put into a mixer and mixed to prepare a plastic resin composition.
[비교 예 1][Comparative Example 1]
삭제delete
삭제delete
폴리프로필렌(polypropylene) 1,000g 및 폴리카보네이트(polycarbonate) 30g을 믹서에 넣고 혼합하여 플라스틱 수지 조성물을 제조하였다.1,000 g of polypropylene and 30 g of polycarbonate were put into a mixer and mixed to prepare a plastic resin composition.
[비교 예 2][Comparative Example 2]
폴리프로필렌(polypropylene) 1,000g 및 실리콘 30g을 믹서에 넣고 혼합하여 플라스틱 수지 조성물을 제조하였다.1,000 g of polypropylene and 30 g of silicone were put in a mixer and mixed to prepare a plastic resin composition.
[비교 예 3][Comparative Example 3]
POM 1,030g을 믹서에 넣고 혼합하여 플라스틱 수지 조성물을 제조하였다.1,030 g of POM were put into a mixer and mixed to prepare a plastic resin composition.
[비교 예 4][Comparative Example 4]
POM 950g 및 실리콘 80g을 믹서에 넣고 혼합하여 플라스틱 수지 조성물을 제조하였다.950 g of POM and 80 g of silicone were put in a mixer and mixed to prepare a plastic resin composition.
[비교 예 5][Comparative Example 5]
POM 950g 및 폴리카보네이트(polycarbonate) 80g을 믹서에 넣고 혼합하여 플라스틱 수지 조성물을 제조하였다.950 g of POM and 80 g of polycarbonate were put into a mixer and mixed to prepare a plastic resin composition.
[테스트용 시편 제작][Test Specimen Production]
상기 실시 예 1,4와 비교 예 1 내지 5에 의하여 제조된 플라스틱 조성물을 시편 성형용 캐스트에 넣고 성형하여 가로×세로×높이가 10㎝×10㎝×1㎝인 사각 판 형상의 테스트용 플라스틱 시편을 제작하였다.The plastic composition prepared in Examples 1 and 4 and Comparative Examples 1 to 5 was placed in a casting mold for forming a specimen and molded into a square plate type test plastic specimen having a size of 10 cm x 10 cm x 1 cm Respectively.
[내충격성 테스트 1][Impact resistance test 1]
상기 시편을 이용하여 내충격성을 테스트하였고, 그 결과를 하기 표 1에 나타내었다. 내충격성 시험은 ASTM D 256에 따라 아이조드 충격강도(J/m)를 테스트하는 방법으로 수행하였다.The impact resistance was tested using the above specimens. The results are shown in Table 1 below. The impact resistance test was carried out by testing the Izod impact strength (J / m) according to ASTM D 256.
상기 표 1의 결과를 살펴보면, 본 발명에 따른 플라스틱 조성물을 이용하여 제조된 시편의 내충격성이 비교예 1 내지 5의 시편에 비하여 매우 우수함을 확인할 수 있다.The results of Table 1 show that the test pieces prepared by using the plastic composition according to the present invention are superior in impact resistance to the test pieces of Comparative Examples 1 to 5.
[내충격성 테스트 2][Impact resistance test 2]
상기 시편에 깊이 및 폭이 1㎜이고 길이가 20㎝인 직선 노치(notch)를 동일하게 인위적으로 형성하고, 노치가 형성된 노치 시편을 이용하여 내충격성을 테스트하였고, 그 결과를 하기 표 2에 나타내었다. 내충격성 시험은 ASTM D 256에 따라 아이조드 충격강도(J/m)를 테스트하는 방법으로 수행하였다.A straight notch having a depth and a width of 1 mm and a length of 20 cm was similarly artificially formed on the specimen and the impact resistance was tested using a notched specimen having a notch. . The impact resistance test was carried out by testing the Izod impact strength (J / m) according to ASTM D 256.
상기 표 2의 결과를 살펴보면, 본 발명에 따른 플라스틱 조성물을 이용하여 제조된 시편은 노치가 발생한 경우에도 내충격성이 비교예 1 내지 5의 시편에 비하여 매우 우수함을 확인할 수 있다.It can be seen from the results of Table 2 that the specimens prepared using the plastic composition according to the present invention are superior in impact resistance to the specimens of Comparative Examples 1 to 5 even when the notches are formed.
[내마모성 테스트][Abrasion resistance test]
상기 시편을 이용하여 ASTM D-1630에 따라 1,000회 마찰회전시 마찰로 감소되는 시편의 무게를 측정하였으며, 그 결과를 하기 표 3에 나타내었다. The specimens were weighed in accordance with ASTM D-1630 by friction during 1,000 rubbing rotations. The results are shown in Table 3 below.
상기 표 3의 결과를 살펴보면, 본 발명에 따른 플라스틱 조성물을 이용하여 제조된 시편은 비교예 1 내지 5의 시편에 비하여 내마모성이 매우 우수함을 확인할 수 있다.The results of Table 3 indicate that the specimens prepared using the plastic composition according to the present invention are superior in abrasion resistance to the specimens of Comparative Examples 1 to 5.
[열변형 온도 테스트][Thermal Deformation Temperature Test]
상기 시편을 이용하여 ASTM D648에 의하여 0.45 MPa 기압조건 및 1.85 MPa 기압조건 하에서 각각 열변형이 개시되는 온도를 측정하였으며, 그 결과를 하기 표 4에 나타내었다.The temperature at which the thermal deformation was initiated under the atmospheric pressure of 0.45 MPa and the pressure of 1.85 MPa was measured according to ASTM D648 using the above specimen. The results are shown in Table 4 below.
상기 표 4의 결과를 살펴보면, 본 발명에 따른 플라스틱 조성물을 이용하여 제조된 시편은 비교예 1 내지 5의 시편에 비하여 열변형에 대한 저항성이 매우 높음을 확인할 수 있다.The results of Table 4 show that the specimens prepared using the plastic composition according to the present invention are highly resistant to thermal deformation compared with the specimens of Comparative Examples 1 to 5.
[내화학성 테스트][Chemical resistance test]
상기 시편을 이용하여 내화학성을 테스트하였고, 그 결과를 하기 표 5에 나타내었다. 내화학성 시험은 염수(염분 농도 10중량%) 침전법 및 염산 용액(HCl 10%) 침전법을 이용하여 수행되었으며, 침전 시간에 따라 지속적으로 꺼내어 표면 손상이 발생하는 시간을 체크하였다.The chemical resistance was tested using the above specimens, and the results are shown in Table 5 below. The chemical resistance test was conducted by precipitation method of saline (salt concentration 10% by weight) and hydrochloric acid solution (HCl 10%) precipitation method.
상기 표 5의 결과를 살펴보면, 본 발명에 따른 플라스틱 조성물을 이용하여 제조된 시편은 비교예 1 내지 5의 시편에 비하여 염수 및 염산용액 모두에 대하여 내화학성이 매우 우수함을 확인할 수 있다.The results of Table 5 indicate that the test pieces prepared using the plastic composition according to the present invention have excellent chemical resistance to both the salt water and the hydrochloric acid solution as compared with the test pieces of Comparative Examples 1 to 5.
Claims (5)
폴리카보네이트(polycarbonate) 1-5 중량%;
아라미드섬유(aramid fiber) 0.5-5 중량%; 및
나머지 폴리프로필렌(polypropylene)으로 이루어진 화장품 용기 제작용 플라스틱 수지 조성물로서,
상기 조성물을 이용하여 제조된 화장품 용기의 마찰감소 무게는 ASTM D-1630에 따라 1,000회 마찰회전시 5㎎ 이하이고; ASTM D648에 따라 0.45 MPa 기압조건 하에 측정된 열변형 온도는 160℃ 이상이며, 1.85 MPa 기압조건 하에서는 115℃ 이상으로 유지되는 것을 특징으로 하는 화장품 용기 제작용 플라스틱 수지 조성물.3-6 wt% silicone;
1-5% by weight of polycarbonate;
From 0.5 to 5% by weight of an aramid fiber; And
The present invention relates to a plastic resin composition for the production of a cosmetic container made of the remaining polypropylene,
The friction reducing weight of the cosmetic container made using the composition is less than or equal to 5 mg per 1,000 revolutions per minute according to ASTM D-1630; Wherein the heat distortion temperature measured at 0.45 MPa atmospheric pressure according to ASTM D648 is 160 DEG C or higher and is maintained at 115 DEG C or higher under an atmospheric pressure of 1.85 MPa.