KR101752634B1 - Aluminium alloy with function of far infrared ray and negative ions and deodorization and sterilization function - Google Patents
Aluminium alloy with function of far infrared ray and negative ions and deodorization and sterilization function Download PDFInfo
- Publication number
- KR101752634B1 KR101752634B1 KR1020160051003A KR20160051003A KR101752634B1 KR 101752634 B1 KR101752634 B1 KR 101752634B1 KR 1020160051003 A KR1020160051003 A KR 1020160051003A KR 20160051003 A KR20160051003 A KR 20160051003A KR 101752634 B1 KR101752634 B1 KR 101752634B1
- Authority
- KR
- South Korea
- Prior art keywords
- anion
- function
- far
- infrared ray
- deodorizing
- Prior art date
Abstract
본 발명은 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 가지는 알루미늄 합금에 관한 것으로, 보다 구체적으로는 알루미늄 합금 자체에 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 부여하고, 이러한 알루미늄 합금을 각종 제품에 적용함으로써, 해당 제품에 대한 각종 인체 유해요인(세균, 유해미생물, 유해전자파 등)을 효율적으로 억제 및 제거할 수 있도록 하며, 특히 가죽이나 섬유 등에 대한 페인트나 옻칠 등 도료로 사용하여 전자기기의 케이스, 커버, 핸드폰 케이스, 스마트폰 커버류, 각종 문 손잡이, 차량용 악세사리 등을 제조함으로써 상기 제품들에 대한 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 부여할 수 있도록 하고, 또한, 플라스틱이나 실리콘 등에 분말형태로 혼합 및 사출 성형하여 핸드폰 케이스, 스마트폰 커버류, 각종 용기, 유무선 마이크, 유무선 헤드셋, 유무선 이어폰, 전기밥솥, 후라이팬, 기타주방제품, 의료용품, 각종 팬날개(예를들면, 선풍기 날개) 등을 제조함으로써, 상기 제품들에 대한 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 부여할 수 있음에 따라, 해당 제품에 대한 각종 인체 유해요인(세균, 유해미생물, 유해전자파 등)을 효율적으로 억제 및 제거할 수 있도록 하는, 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 가지는 알루미늄 합금에 관한 것이다.The present invention relates to an aluminum alloy having an anion and far-infrared ray emitting function and a deodorizing and sterilizing function, and more specifically, to an aluminum alloy itself by giving an anion and a far-infrared ray emitting function, a deodorizing and sterilizing function, (Bacterium, harmful microorganisms, harmful electromagnetic waves, etc.) to the product, and can be used as paints such as paint or lacquer for leather or textile, , A cover, a mobile phone case, a smart phone cover, various door handles, a car accessory, and the like, thereby giving an anion and a far-infrared ray emitting function, a deodorizing and sterilizing function to the products, And by mixing and injection molding, (For example, electric fan blades) and the like are manufactured by using the anion and the anion for the products, the anion and the anion for the products, It has an anion and far infrared ray emission function that can effectively suppress and eliminate various harmful factors (bacterium, harmful microorganisms, harmful electromagnetic wave, etc.) to the product due to its ability to emit far- And an aluminum alloy having a deodorizing and sterilizing function.
Description
본 발명은 알루미늄 합금에 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 부여함으로써, 상기 알루미늄 합금이 적용된 각종 제품에 대한 각종 인체 유해요인을 효율적으로 억제 및 제거할 수 있도록 하는, 알루미늄 합금에 관한 것이다.
The present invention relates to an aluminum alloy capable of effectively suppressing and eliminating various harmful factors to various kinds of products to which the aluminum alloy is applied by imparting an anion and a far-infrared ray emitting function and a deodorizing and sterilizing function to an aluminum alloy.
일반적으로 알루미늄 합금은 그 경량성으로 인해 사용 용도가 매우 다양한 금속중 하나로써, 예를 들면, 특허문헌 1에서와 같이 각종 합성수지와 알루미늄을 혼합하여 사출성형하여 각종 제품에 대한 내구성을 향상시키는 등 다양한 분야에서 사용되고 있다.
BACKGROUND ART [0002] Aluminum alloys are widely used for various purposes because of their lightweight properties. For example, as in Patent Document 1, aluminum alloys are mixed with various synthetic resins and aluminum and injection molded to improve durability for various products Has been used in the field.
한편, 최근에는 생활수준의 향상 및 좀 더 건강한 삶을 위하여, 방부, 살균 및 탈취기능 등의 다양한 기능이 부여된 제품에 대한 관심과 소비가 늘어나고 있지만, 이러한 상황에도 불구하고 일반적인 알루미늄 합금에는 탈취 및 살균기능이 미비한 문제점이 있었다.
In recent years, interest and consumption of products having various functions such as preservation, sterilization and deodorization functions have been increasing for the improvement of living standards and for a healthier life. However, in spite of this situation, There is a problem that the sterilizing function is insufficient.
즉, 일반적인 알루미늄 합금이 적용된 각종 제품의 경우, 탈취 및 살균기능이 미비함에 따라 각종 세균 및 유해미생물들의 서식 환경을 제공하여 인체에 심각한 유해요인으로 작용할 수 있으며, 각종 전자파 등을 발생시키는 제품의 경우, 상기와 같은 세균 및 유해미생물들 뿐만 아니라 유해 전자파가 방출되어 남성 호르몬수치의 감소, 혈액순환의 방해 등 또 다른 인체 유해요인으로 작용하는 문제점이 있다.
In other words, various kinds of products to which general aluminum alloy is applied have poor deodorizing and sterilizing functions, and thus they provide a habitat environment for various bacteria and harmful microorganisms, which can act as serious harmful factors to the human body. In the case of products that generate various electromagnetic waves , There is a problem that harmful electromagnetic waves are released as well as the above-mentioned bacteria and harmful microorganisms, and thus they are another human harmful factors such as decrease of male hormone levels and obstruction of blood circulation.
따라서, 본 발명은 상술한 문제점을 해결하기 위한 것으로, 알루미늄 합금 자체에 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 부여하고, 이러한 알루미늄 합금을 각종 제품에 적용함으로써, 해당 제품에 대한 각종 인체 유해요인(세균, 유해미생물, 유해전자파 등)을 효율적으로 억제 및 제거할 수 있도록 함을 과제로 한다.
SUMMARY OF THE INVENTION Accordingly, the present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to provide an aluminum alloy itself with an anion and far-infrared ray emitting function, a deodorizing and sterilizing function, and applying such an aluminum alloy to various products, (Bacteria, harmful microorganisms, harmful electromagnetic waves, etc.) can be effectively suppressed and removed.
본 발명은 알루미늄 합금에 있어서, 알루미늄, 은 및 광물을 포함하여 이루어지는 것을 특징으로 하는, 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 가지는 알루미늄 합금을 과제의 해결 수단으로 한다.
The present invention provides an aluminum alloy having an anion and far-infrared ray emitting function and an aluminum alloy having a deodorizing and sterilizing function, which comprises aluminum, silver and a mineral.
좀 더 구체적으로 상기 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 가지는 알루미늄 합금은, 알루미늄 87.5 ~ 97 중량%, 아연 0.3 ~ 0.7 중량%, 칼슘 0.3 ~ 0.7 중량%, 은 0.01 ~ 0.03 중량% 및 광물 2.39 ~ 11.07 중량%로 이루어지는 것이 바람직하다.
More specifically, the aluminum alloy having an anion and far-infrared ray emitting function and a deodorizing and sterilizing function is composed of 87.5 to 97 wt% of aluminum, 0.3 to 0.7 wt% of zinc, 0.3 to 0.7 wt% of calcium, 0.01 to 0.03 wt% of silver, 2.39 to 11.07% by weight.
그리고, 상기 광물은, 칠보석, 토르말린, 황토, 견운모, 자수정, 생광석, 실리카, 죽탄, 의왕석, 귀양석, 흑요석 또는 맥반석 중에서 단독 또는 2종 이상 병용하여 사용하는 것이 바람직하다.
It is preferable that the above-mentioned minerals are used alone or in combination of two or more kinds of chalcopyrite, tourmaline, loess, sericite, amethyst, biotite, silica, bamboo, quartz,
아울러, 상기와 같은 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 가지는 알루미늄 합금은, 가죽이나 섬유 등에 대한 페인트나 옻칠 등 도료로 사용하여 전자기기의 케이스, 커버, 핸드폰 케이스, 스마트폰 커버류, 각종 문 손잡이, 차량용 악세사리 등을 제조함으로써 상기 제품들에 대한 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 부여할 수 있도록 하거나, 또는 플라스틱이나 실리콘 등에 분말형태로 혼합하고 사출 성형하여 핸드폰 케이스, 스마트폰 커버류, 각종 용기, 유무선 마이크, 유무선 헤드셋, 유무선 이어폰, 전기밥솥, 후라이팬, 기타주방제품, 의료용품, 각종 팬날개(예를들면, 선풍기 날개) 등을 제조함으로써, 상기 제품들에 대한 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 부여할 수 있도록 하는 것이 바람직하다.
In addition, the aluminum alloy having an anion and far-infrared ray emitting function and a deodorizing and sterilizing function as described above can be used as paints such as leather or textile for paint or lacquer, and is used as a coating material for electronic devices such as cases, covers, mobile phone cases, smart phone covers, Handles, automobile accessories, and the like, thereby imparting negative ion and far infrared ray emission functions, deodorizing and sterilizing functions to the products, mixing them in powder form in plastic or silicon, and injection molding to manufacture mobile phone cases, smart phone covers, (For example, fan blades) of various kinds of containers, wired and wireless microphones, wired / wireless headsets, wired / wireless headphones, electric rice cookers, frying pans, other kitchen products, medical supplies, Function and deodorization and sterilization function can be imparted.
본 발명은 가죽이나 섬유 등에 대한 페인트나 옻칠 등 도료로 사용하여 전자기기의 케이스, 커버, 핸드폰 케이스, 스마트폰 커버류, 각종 문 손잡이, 차량용 악세사리 등을 제조함으로써 상기 제품들에 대한 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 부여할 수 있으며, 또한, 본 발명은 플라스틱이나 실리콘 등에 분말형태로 혼합 및 사출 성형하여 핸드폰 케이스, 스마트폰 커버류, 각종 용기, 유무선 마이크, 유무선 헤드셋, 유무선 이어폰, 전기밥솥, 후라이팬, 기타주방제품, 의료용품, 각종 팬날개(예를들면, 선풍기 날개) 등을 제조함으로써, 상기 제품들에 대한 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 부여할 수 있음에 따라, 해당 제품에 대한 각종 인체 유해요인(세균, 유해미생물, 유해전자파 등)을 효율적으로 억제 및 제거할 수 있도록 하는 효과가 있다.
The present invention relates to an anion and a far-infrared ray emission function for the above products by manufacturing a case, a cover, a mobile phone case, a smart phone cover, various door handles, a vehicle accessory, etc., The present invention can be applied to a plastic or silicon powder or the like to be mixed and injection molded into a cell phone case, a smartphone cover, various containers, wired / wireless microphones, wired / wireless headsets, wired / wireless earphones, Since the anion and far-infrared ray emitting function and the deodorizing and sterilizing function can be imparted to the products by producing various kinds of fan wings (for example, fan blades) and the like, Effective suppression and removal of harmful factors (bacteria, harmful microorganisms, harmful electromagnetic waves, etc.) on products There is an effect to be able to.
상기의 효과를 달성하기 위한 본 발명은 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 가지는 알루미늄 합금에 관한 것으로서, 본 발명의 기술적 구성을 이해하는데 필요한 부분만이 설명되며 그 이외 부분의 설명은 본 발명의 요지를 흩트리지 않도록 생략될 것이라는 것을 유의하여야 한다.
In order to achieve the above-mentioned effects, the present invention relates to an aluminum alloy having an anion and far-infrared ray emitting function and a deodorizing and sterilizing function, and only the parts necessary for understanding the technical structure of the present invention are explained, It will be omitted so as not to disturb the gist of the present invention.
이하, 본 발명에 따른 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 가지는 알루미늄 합금을 상세히 설명하면 다음과 같다.
Hereinafter, an aluminum alloy having an anion and far-infrared ray emitting function and a deodorizing and sterilizing function according to the present invention will be described in detail.
먼저, 본 발명에 따른 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 가지는 알루미늄 합금은, 알루미늄, 은 및 광물을 포함하여 이루어진다.
First, an aluminum alloy having an anion and far-infrared ray emitting function and a deodorizing and sterilizing function according to the present invention comprises aluminum, silver and a mineral.
좀 더 구체적으로 본 발명에 따른 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 가지는 알루미늄 합금은, 알루미늄 87.5 ~ 97 중량%, 아연 0.3 ~ 0.7 중량%, 칼슘 0.3 ~ 0.7 중량%, 은 0.01 ~ 0.03 중량% 및 광물 2.39 ~ 11.07 중량%로 이루어진다.
More specifically, the aluminum alloy having an anion and far-infrared ray emitting function and a deodorizing and sterilizing function according to the present invention comprises 87.5 to 97% by weight of aluminum, 0.3 to 0.7% by weight of zinc, 0.3 to 0.7% by weight of calcium, 0.01 to 0.03% % And 2.39 to 11.07% by weight of minerals.
상기 알루미늄은 경량성이 우수한 공지된 소재로써 인체에 무해한 소재이다. 한편, 알루미늄의 혼합량이 87.5 중량% 미만이 될 경우에는 광물의 혼합량이나 기타 아연 등과 같은 다른 소재의 혼합량이 증가하여 금속재 부품의 물성(경량성이나 내구성 등)이 저하될 우려가 있으며, 알루미늄의 혼합량이 97 중량%를 초과할 경우에는 기타 다른 소재의 혼합량이 너무 적어지게 되므로 성형성 등이 저하될 우려가 있다.
The above-mentioned aluminum is a well-known material excellent in light weight and is harmless to the human body. On the other hand, when the mixing amount of aluminum is less than 87.5% by weight, there is a possibility that the physical properties (light weight and durability) of the metallic parts are lowered due to an increase in the mixing amount of the mineral and other materials such as zinc, If the content exceeds 97% by weight, the amount of the other materials to be mixed becomes too small, and the moldability may be deteriorated.
상기 아연은 가공성을 높이는 작용을 하며, 아연의 혼합량이 0.3 중량% 미만이 될 경우에는 가공성이 저하할 우려가 있고, 아연의 혼합량이 0.7 중량%를 초과할 경우에는 제조 후 부식균열을 일으킬 우려가 있다.
If the mixing amount of zinc is less than 0.3% by weight, the workability may be lowered. If the mixing amount of zinc is more than 0.7% by weight, there is a fear of causing corrosion cracks have.
상기 칼슘은 성형이 용이하게 이루어지는 작용을 하는 것으로, 칼슘 또는 산화칼슘을 적용할 수 있으며, 그 혼합량이 0.3 중량% 미만이 될 경우에는 성형 용이성이 저하될 우려가 있으며, 0.7 중량%를 초과할 경우에는 상대적으로 아연 등과 같은 금속 소재의 혼합량이 적어짐에 따라 가공성이 저하할 우려가 있다.
Calcium or calcium oxide can be applied. When the amount of calcium is less than 0.3% by weight, the ease of molding may be deteriorated. When the amount exceeds 0.7% by weight There is a possibility that the workability is lowered as the amount of metal material such as zinc is relatively decreased.
상기 은은 탈취 및 살균기능을 더욱 향상시키기 위해 첨가되는 것으로, 그 혼합량이 0.01 중량% 미만일 경우 상기 효과가 미비해질 우려가 있으며, 0.03 중량%를 초과할 경우, 사용량 대비 탈취 및 살균기능의 향상효율이 미비하여 비경제적일 우려가 있다.
The silver is added to further improve the deodorizing and sterilizing function. When the mixing amount is less than 0.01% by weight, the above effect may be insufficient. When the mixing amount is more than 0.03% by weight, the efficiency of deodorization and sterilization There is a possibility that it is uneconomical.
상기 광물은 음이온 및 원적외선을 발산하는 천연광물로써 칠보석, 토르말린, 황토, 견운모, 자수정, 생광석, 실리카, 죽탄, 의왕석, 귀양석, 흑요석 또는 맥반석 중에서 단독 또는 2종 이상 병용하여 사용하며, 그 사용량이 2.39 중량% 미만일 경우 음이온 및 원적외선 발산효과가 미비해질 우려가 있으며, 11.07 중량%를 초과할 경우 사용량 대비 상기 기능의 증가율이 미비하여 비경제적일 우려가 있다.
These minerals are natural minerals that emit anions and far infrared rays. They are used alone or in combination of two or more of the following types of jewels, tourmaline, loess, sericite, amethyst, ore, silica, bamboo, quartz, If the amount is less than 2.39% by weight, the anion and far-infrared rays may be less effective. If the amount is more than 11.07% by weight, the rate of increase of the function is insufficient.
이하 본 발명의 구성을 아래 실시예에 의거하여 더욱 상세히 설명하겠는바 본 발명이 하기의 실시예에 의해서만 반드시 한정되는 것은 아니다.
Hereinafter, the structure of the present invention will be described in more detail with reference to the following examples, but the present invention is not limited thereto.
1. 알루미늄 합금의 제조
1. Manufacture of aluminum alloy
(실시예 1)(Example 1)
알루미늄 87.5 중량%, 칠보석 11.07 중량%, 아연 0.7 중량%, 은 0.03 중량% 및 칼슘 0.7 중량%로 알루미늄 합금을 제조하였다.
An aluminum alloy was prepared from 87.5% by weight of aluminum, 11.07% by weight of fullerenes, 0.7% by weight of zinc, 0.03% by weight of silver and 0.7% by weight of calcium.
(실시예 2)(Example 2)
알루미늄 97 중량%, 토르말린 2.39 중량%, 아연 0.3 중량%, 은 0.01 중량% 및 산화칼슘 0.3 중량%로 알루미늄 합금을 제조하였다.
An aluminum alloy was prepared from 97 wt% aluminum, 2.39 wt% tourmaline, 0.3 wt% zinc, 0.01 wt% silver and 0.3 wt% calcium oxide.
(비교예 1)(Comparative Example 1)
알루미늄 99.7 중량%, 아연 0.3 중량%로 알루미늄 합금을 제조하였다.An aluminum alloy was prepared with 99.7 wt% aluminum and 0.3 wt% zinc.
(비교예 2)(Comparative Example 2)
알루미늄 99.4 중량%, 아연 0.3 중량% 및 산화칼슘 0.3 중량%로 알루미늄 합금을 제조하였다.An aluminum alloy was prepared from 99.4 wt% aluminum, 0.3 wt% zinc and 0.3 wt% calcium oxide.
2. 음이온 및 원적외선 발산 성능 및 살균성 평가
2. Evaluation of anion and far-infrared radiation performance and sterilization
(1) 음이온 발생 성능
(1) Negative ion generation performance
KFIA-FI-1042에 기준하여 측정하되, 전하입자 측정 장치를 이용하여 실내온도 26℃, 습도 36%, 대기중 음이온수 102/cc 조건에서 시험하였고, 측정대상물에서 발생되는 음이온을 측정하여 단위체적당 ION수로 표시하여 측정하였으며, 그 결과는 아래 [표 1]과 같다.
The test was conducted under the conditions of room temperature of 26 ° C, humidity of 36%, and number of atmospheric anions of 102 / cc using a charge particle measuring device under the measurement of KFIA-FI-1042. The anions generated in the measurement object were measured, ION number, and the results are shown in Table 1 below.
발생되지 않음Anion
Not Occurred
발생되지 않음Anion
Not Occurred
상기 [표 1]에서와 같이 본 발명의 실시예 1, 2에 따른 알루미늄 합금은 음이온 발생효율이 우수함을 알 수 있다.
As shown in Table 1, the aluminum alloys according to Examples 1 and 2 of the present invention show excellent anion generation efficiency.
(2) 원적외선 방사 성능
(2) Far-infrared radiation performance
KFIA-FI-1005에 기준하여 측정하되, FT-IR Spectrometer을 이용한 BLACK BODY 대비 측정으로써 실내온도 37℃에서 측정하였으며, 그 결과는 아래 [표 2]와 같다.
The measurement was performed based on KFIA-FI-1005, using a FT-IR spectrometer, and measured at a room temperature of 37 ° C. The results are shown in Table 2 below.
(5 ~ 20㎛)Emissivity
(5 to 20 占 퐉)
원적외선
방사되지 않음
Far infrared ray
Not radiated
원적외선
방사되지 않음
Far infrared ray
Not radiated
(W/m2·㎛, 37℃)Radiant energy
(W / m 2占 퐉, 37 占 폚)
상기 [표 2]에서와 같이 본 발명의 실시예 1, 2에 따른 알루미늄 합금은 원적외선 방사효율이 우수함을 알 수 있다.
As shown in Table 2, the aluminum alloys according to Examples 1 and 2 of the present invention have excellent far-infrared radiation efficiency.
(3) 살균 성능
(3) Sterilization performance
JIS Z 2801에 기준하여 측정하되, 표준필름은 Stomacher 400 POLY-BAG을 사용하였고, 시험균액을 35±1℃, 90% R.H.에서 24시간 정치 배양 후 균수를 측정하였으며, 균주는 Staphy lococcus aureus ATCC 6538P(균주 1)와 Escherichia coli ATCC 8739(균주 2)를 사용하였고, 그 결과는 아래 [표 3]과 같다.
Stomacher 400 POLY-BAG was used as a standard film, and the number of bacteria was measured after the test bacteria were incubated for 24 hours at 35 ± 1 ° C. and 90% RH. Staphylococcus aureus ATCC 6538P (Strain 1) and Escherichia coli ATCC 8739 (strain 2) were used. The results are shown in Table 3 below.
균주 1
Strain 1
(세균수/cm2)Initial number of bacteria
(Number of bacteria / cm 2 )
(log)Antimicrobial activity value
(log)
균주 2
Strain 2
(세균수/cm2)Initial number of bacteria
(Number of bacteria / cm 2 )
(log)Antimicrobial activity value
(log)
상기 [표 3]에서와 같이 본 발명의 실시예 1, 2에 따른 알루미늄 합금은 살균기능이 우수함을 알 수 있다. 아울러 상기 음이온 및 원적외선 방출기능과 은에 의해 탈취성능이 구현됨은 자명할 것이다.
As shown in Table 3, the aluminum alloy according to Examples 1 and 2 of the present invention has excellent sterilizing function. It is also apparent that the deodorizing performance is realized by the anion and far-infrared ray emitting function and silver.
즉, 본 발명은 상기와 같은 이온 및 원적외선 방출기능과 탈취 및 살균기능을 바탕으로 가죽이나 섬유 등에 대한 페인트나 옻칠 등 도료로 사용하여 전자기기의 케이스, 커버, 핸드폰 케이스, 스마트폰 커버류, 각종 문 손잡이, 차량용 악세사리 등을 제조함으로써 상기 제품들에 대한 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 부여할 수 있으며, 또한, 본 발명은 플라스틱이나 실리콘 등에 분말형태로 혼합 및 사출 성형하여 핸드폰 케이스, 스마트폰 커버류, 각종 용기, 유무선 마이크, 유무선 헤드셋, 유무선 이어폰, 전기밥솥, 후라이팬, 기타주방제품, 의료용품, 각종 팬날개(예를들면, 선풍기 날개) 등을 제조함으로써, 상기 제품들에 대한 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 부여할 수 있음에 따라, 해당 제품에 대한 각종 인체 유해요인(세균, 유해미생물, 유해전자파 등)을 효율적으로 억제 및 제거할 수 있음을 알 수 있다.
That is, the present invention can be applied to paints such as paint or lacquer for leather or textile based on ion and far-infrared ray emitting function and deodorizing and sterilizing function as described above, Handles, vehicle accessories, and the like. The present invention can be applied to an anion and a far-infrared ray emitting function, a deodorizing and sterilizing function, (For example, fan blades) and the like are manufactured by manufacturing the earphone, the earphone, the phone cover, various containers, wired / wireless microphone, wired / wireless headset, wired / wireless earphone, rice cooker, frying pan, And the ability to emit far-infrared rays and provide deodorization and sterilization functions, It can be seen that it is possible to effectively suppress and eliminate the hazards (germs, microorganisms, harmful electromagnetic radiation, etc.).
상술한 바와 같이, 본 발명에 따른 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 가지는 알루미늄 합금은 상기의 바람직한 실시 예를 통해 설명하고, 그 우수성을 확인하였지만 해당 기술 분야의 당업자라면 하기의 특허 청구 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다.As described above, the aluminum alloy having an anion and far-infrared ray emitting function and a deodorizing and sterilizing function according to the present invention has been described through the preferred embodiments and its superiority has been confirmed. However, those skilled in the art It will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined in the appended claims.
Claims (3)
알루미늄, 은 및 광물을 포함하여 이루어지되,
알루미늄 87.5 ~ 97 중량%, 아연 0.3 ~ 0.7 중량%, 칼슘 0.3 ~ 0.7 중량%, 은 0.01 ~ 0.03 중량% 및 광물 2.39 ~ 11.07 중량%로 이루어지며,
상기 광물은, 칠보석, 토르말린, 황토, 견운모, 자수정, 생광석, 실리카, 죽탄, 의왕석, 귀양석, 흑요석 또는 맥반석 중에서 단독 또는 2종 이상 병용하여 사용하는 것을 특징으로 하는, 음이온 및 원적외선 방출기능과 탈취 및 살균기능을 가지는 알루미늄 합금.In the aluminum alloy,
Aluminum, silver and minerals,
Wherein the composition comprises 87.5 to 97% by weight of aluminum, 0.3 to 0.7% by weight of zinc, 0.3 to 0.7% by weight of calcium, 0.01 to 0.03% by weight of silver and 2.39 to 11.07%
Wherein the mineral is anionic and far-infrared radiation, characterized in that the mineral is used alone or in combination of two or more of chylook, tourmaline, loess, sericite, amethyst, biotite, silica, bamboo, quartz, Aluminum alloy with function and deodorizing and sterilizing function.