KR101712921B1 - High Grade Guss Asphalt Composition and Constructing Methods Using Thereof - Google Patents

High Grade Guss Asphalt Composition and Constructing Methods Using Thereof Download PDF

Info

Publication number
KR101712921B1
KR101712921B1 KR1020160131419A KR20160131419A KR101712921B1 KR 101712921 B1 KR101712921 B1 KR 101712921B1 KR 1020160131419 A KR1020160131419 A KR 1020160131419A KR 20160131419 A KR20160131419 A KR 20160131419A KR 101712921 B1 KR101712921 B1 KR 101712921B1
Authority
KR
South Korea
Prior art keywords
weight
parts
resin
asphalt mixture
asphalt
Prior art date
Application number
KR1020160131419A
Other languages
Korean (ko)
Inventor
김인중
Original Assignee
주식회사 지케이기술연구소
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 지케이기술연구소 filed Critical 주식회사 지케이기술연구소
Priority to KR1020160131419A priority Critical patent/KR101712921B1/en
Application granted granted Critical
Publication of KR101712921B1 publication Critical patent/KR101712921B1/en

Abstract

The present invention relates to a high-grade guss asphalt composition including: 5 to 50 parts by weight of styrene-isoprene-styrene; 5 to 50 parts by weight of styrene-butadiene-styrene; 10 to 30 parts by weight of vinyl ester resin, polyester resin, acryl resin, epoxy resin, acryl-epoxy resin, urethane resin, or polymer resin of at least one selected therefrom; 10 to 1,000 parts by weight of aggregate; 1 to 20 parts by weight of thermo-sensitive reinforcing agent; 10 to 60 parts by weight of filler; 10 to 40 parts by weight of nano ceramic particles; 1 to 15 parts by weight of surfactant; 0.1 to 5 parts by weight of antioxidant; 0.5 to 5 parts by weight of stabilizer; 0.5 to 10 parts by weight of performance improving agent; 2 to 20 parts by weight of fiber; 10 to 50 parts by weight of adhesive resin; 2 to 10 parts by weight of anti-sagging agent; and 1 to 5 parts by weight of compatibilizer with respect to 100 parts by weight of natural asphalt mixture. The high-grade guss asphalt composition according to the present invention provides the high-grade guss asphalt composition that has a high performance grade of PG 82-34 and a construction method using the same.

Description

고등급 구스 아스팔트 조성물 및 이를 이용한 시공방법{High Grade Guss Asphalt Composition and Constructing Methods Using Thereof}TECHNICAL FIELD [0001] The present invention relates to a high grade goeth asphalt composition and a construction method using the same,

본 발명은 고등급 구스 아스팔트 조성물에 관한 것으로서, 보다 상세하게는 PG 등급성능이 고등급(PG 82-34)인 공용성 등급인 고등급 구스 아스팔트 조성물 및 이를 이용한 시공방법에 관한 것이다.
The present invention relates to a high grade goeth asphalt composition, and more particularly to a high grade goeth asphalt composition having a PG grade performance of a high grade (PG 82-34) and a construction method using the same.

일반적으로, 도로포장에 주로 사용되던 종래의 가열아스팔트 혼합물은 동절기인 영하의 기온에서 시공하는 한냉지 시공공법으로는 포설할 수 없으며, 또한 하절기나 온도 및 하중의 변화가 발생하는 경우에는 굴곡현상(rutting 현상), 종단면의 요철(凹凸), 코루게이션 현상 및 레벨링 현상 등이 반복적으로 일어나 도로의 균열, 포트 홀(port hole), 골재의 박리 및 이탈 등을 일으켜 도로의 수명을 저하시킨다.In general, the conventional heated asphalt mixture used mainly for road pavement can not be installed by the cold-applied construction method which is applied at the sub-zero temperature in the winter, and when the summer season, temperature and load change occur, rutting phenomenon), irregularities of the longitudinal section, corrugation phenomenon and leveling phenomenon repeatedly occur, which causes the cracks of the road, the port hole, the peeling of the aggregate, and the deviation of the aggregate.

따라서 평균적으로 4∼5년을 주기로 재포장인 덧씌우기, 수선 등을 계속적으로 반복하게 되어 국가의 도로신설에 따른 포장예산 보다도 보수유지에 소요되는 예산을 해마다 증가시키는 주된 요인으로 작용하였다.Therefore, on average, repacking and repairs were repeated over a period of four to five years. This contributed to a yearly increase in the budget for maintenance, rather than the packaging budget for the establishment of the national road.

이러한 문제점을 극복하기 위하여 종래의 가열아스팔트 혼합물 대신에 불투수성, 내구성, 내마모성, 내충격성, 가요성, 미끄럼 저항성 및 접착성 등이 매우 우수한 구스아스팔트 혼합물이 개발되었다.In order to overcome this problem, a goosal asphalt mixture having excellent imperviousness, durability, abrasion resistance, impact resistance, flexibility, slip resistance and adhesiveness has been developed instead of the conventional heated asphalt mixture.

아스팔트 꿀레(Asphalt coule)라고도 불리는 구스아스팔트 혼합물은 특수 아스팔트 포장재로, 프랑스에서 개발되었으며 독일과 일본에서는 구스아스팔트, 영국과 미국에서는 아스팔트 매스틱 또는 매스틱 아스팔트 등으로 지칭된다.The goos asphalt mixture, also known as the asphalt coule, is a special asphalt pavement developed in France and is referred to as goose asphalt in Germany and Japan and asphalt mastic or mastic asphalt in the United Kingdom and the United States.

구스아스팔트 혼합물은 상기된 것처럼 종래의 가열아스팔트 혼합물에 비해 다양한 장점을 가지고 있는데, 시공에 있어서도 다짐이 불필요하여 인력미장공법 이나 전문피니셔에 의해 포설된다.The Goose asphalt mixture has various advantages compared to the conventional heated asphalt mixture as described above, and it is unnecessary to compaction even in the construction, so that it is installed by a work finishing method or a professional finisher.

이와 같은 구스아스팔트 혼합물을 시공하기 위한 종래의 방법을 기술하면 다음과 같다. 구스 아스팔트 혼합물은 적절한 비율로 배합된 혼합액, 골재, 모래, 석분 등을 고온(170℃∼250℃)에서 기계식 강제혼합방법을 이용하여 생산하는데, 이때 혼합액의 중량은 혼합물 전체중량의 15∼34% 정도를 차지하고, 모래 및 골재, 석분 등은 혼합물 전체중량의 85∼66%를 차지한다.A conventional method for constructing such a cusp asphalt mixture will be described below. The goosel asphalt mixture is produced by mechanically mixed mixing method at high temperature (170 ℃ ~ 250 ℃) in the mixed ratio, aggregate, sand, Of the total weight of the mixture, and the sand, aggregate, and stones account for 85 to 66% of the total weight of the mixture.

구스아스팔트 혼합물에 섞이는 혼합액은 기존의 가열아스팔트 용액과는 달리 온도나 하중변화에 의해 일어나는 단점들을 모두 극복할 수 있는 높은 결합력과 내구성 및 방수성을 갖는다.Unlike conventional heated asphalt solution, the mixed solution mixed with Goose asphalt mixture has high bonding strength, durability and waterproof property which can overcome all the disadvantages caused by temperature or load change.

특히, 많은 량의 혼합액을 넣어 고온에서 가열혼합하면, 그 혼합물은 화산에서 분출된 용암이 흘러내리는 것처럼 유동성이 매우 띄어나며 자연 냉각됨에 따라 다짐공정을 수행하지 않아도 포장층을 일체화시킬 수 있다.Particularly, when a large amount of mixed liquid is added and heated and mixed at a high temperature, the mixture becomes highly fluid as lava ejected from a volcano flows down. As the natural cooling occurs, the mixture layer can be unified without performing the compaction process.

상기와 같은 구스아스팔트 혼합물을 현장에서 직접 생산하여 시공하려는 경우에는 혼합액, 골재, 모래, 석분 등의 재료와 강제식 가열혼합기, 혼합액 정량공급장치, 골재 및 모래, 석분 등을 가열하는 가열기, 이를 정량공급하는 공급장치, 혼합액 가열장치, 연료공급장치, 전기 및 동력공급장치, 이들 전체를 통괄조정하는 품질관리장치, 기타 장비 및 공구, 잡자재 등이 필요하다.When the above-mentioned goos asphalt mixture is to be directly produced on site, it is necessary to mix materials such as mixture, aggregate, sand, and stone, a forced heating mixer, a mixed liquid quantity feeder, a heater for heating aggregate, sand, A supply device, a mixture liquid heating device, a fuel supply device, an electricity and a power supply device, a quality control device for coordinating all of them, other equipment and tools, and a job material.

상기한 바와 같이, 아스팔트 포장은 시공 후 5년이 되기 전에 주행트랙을 따라 가끔 소성변형이 생겨서 심각한 주행문제를 발생시키거나, 소성변형 문제는 없다 하더라도 시간의 흐름과 함께 포장 재료가 점차 노화되어 결국에는 심한 균열을 발생시켜 주기적으로 유지보수를 하여야 하는 문제점이 있으며, 이러한 보수 방법의 일례로서, 대한민국 특허등록 제0880030호에는 아스팔트 시멘트 60~80중량%; 식물성 오일 15~35중량%;을 포함하고, 알라파틱 폴리아미드(Aliphatic polyamides)가 포함된 것을 특징으로 하는 바인더로 이루어진 도로포장 긴급보수용 아스팔트 조성물이 개시되어 있다.As described above, the asphalt pavement is sometimes subjected to plastic deformation along the running track 5 years before the construction, causing severe driving problems, and even if there is no plastic deformation problem, the packaging material gradually ages with the passage of time There is a problem that maintenance is required periodically due to occurrence of severe cracks. As an example of such a repair method, Korean Patent Registration No. 0880030 discloses that 60 to 80% by weight of asphalt cement; And 15 to 35% by weight of a vegetable oil; and an aliphatic polyamide (Aliphatic polyamide) is contained in the asphalt composition.

또한, 현재까지 도로 및 교면포장의 보수 방법으로 2~3등급(PG64-22.76-22)의 일반 개질아스팔트 덧씌우기가 통상적으로 적용되고 있다. Also, to date, a general modified asphalt overlay of grades 2 to 3 (PG64-22.76-22) has been commonly applied as a repair method for road and bridge pavement.

그러나 상기 2~3등급의 아스팔트 포장재는 그 수명이 짧고, 부착력과 유연성이 부족하여 재료분리 및 포트홀이 빈번하게 발생하는 문제점이 있다. However, the second to third grades of asphalt pavement have a short lifetime and insufficient adhesiveness and flexibility, resulting in frequent material separation and portholes.

이에, 상기 유지보수에 따른 비용을 최소화하기 위해 아스팔트를 이용하여 포장한 도로의 소성변형을 최소화하고, 장시간 동안 노화되지 않으면서, 쉽게 박리되지 않도록 하는 아스팔트 조성물을 개발하는 것이 요구되고 있다.In order to minimize the cost due to the maintenance, it is required to minimize the plastic deformation of the road packed with the asphalt and to develop an asphalt composition that is not easily peeled off without aging for a long time.

본 발명은 전술한 문제점을 극복하기 위해 창출된 것으로서, PG 등급성능이 고등급(PG 82-34)인 공용성 등급의 구스 아스팔트 조성물 및 이를 이용한 시공방법을 제공한다.
The present invention has been made to overcome the above-described problems, and provides a goos asphalt composition having a PG grade performance of a high grade (PG 82-34) and a method of using the same.

본 발명은
천연 아스팔트 혼합물 100중량부 기준으로,
스티렌이소프렌스티렌 5 내지 50중량부;
스티렌부타디엔스티렌 5 내지 50중량부;
비닐에스테르 수지, 폴리에스테르 수지, 아크릴 수지, 에폭시 수지, 아크릴-에폭시 수지, 우레탄 수지 또는 이들로부터 선택된 적어도 하나 이상인 고분자 수지 10 내지 30중량부;
골재 10 내지 1,000중량부;
감온성 보강제 1 내지 20중량부;
충진제 10 내지 60중량부;
나노세라믹 입자 10 내지 40중량부;
계면활성제 1 내지 15중량부;
산화방지제 0.1 내지 5중량부;
안정제 0.5 내지 5중량부;
성능개선제 0.5 내지 10중량부;
파이버 2 내지 20중량부;
점착성 수지 10 내지 50중량부;
흐름 방지제 2 내지 10중량부; 및
상용화제 1 내지 5중량부를 포함하는 고등급 구스 아스팔트 조성물에,
글리시딜 메타크릴레이트(GMA)계 수지를 천연 아스팔트 혼합물 100중량부를 기준으로 5 내지 30중량부로 더 포함하고,
벤토나이트를 천연 아스팔트 혼합물 100중량부를 기준으로 0.1 내지 5중량부로 더 포함하며,
알루민산 칼슘을 천연 아스팔트 혼합물 100중량부를 기준으로 1 내지 5중량부로 더 포함하고,
The present invention
On the basis of 100 parts by weight of the natural asphalt mixture,
5 to 50 parts by weight of styrene isoprene styrene;
5 to 50 parts by weight of styrene butadiene styrene;
10 to 30 parts by weight of a polymer resin having at least one or more selected from a vinyl ester resin, a polyester resin, an acrylic resin, an epoxy resin, an acryl-epoxy resin, a urethane resin or the like;
10 to 1,000 parts by weight of aggregate;
1 to 20 parts by weight of a thermosetting reinforcing agent;
10 to 60 parts by weight of a filler;
10 to 40 parts by weight of nano-ceramic particles;
1 to 15 parts by weight of a surfactant;
0.1 to 5 parts by weight of an antioxidant;
0.5 to 5 parts by weight of a stabilizer;
0.5 to 10 parts by weight of a performance improving agent;
2 to 20 parts by weight of fibers;
10 to 50 parts by weight of a tacky resin;
2 to 10 parts by weight of an anti-flow agent; And
And 1 to 5 parts by weight of a compatibilizing agent is added to the high grade goeth asphalt composition,
Further comprising 5 to 30 parts by weight of glycidyl methacrylate (GMA) based resin based on 100 parts by weight of the natural asphalt mixture,
Further comprising 0.1 to 5 parts by weight of bentonite based on 100 parts by weight of the natural asphalt mixture,
Further comprising 1 to 5 parts by weight of calcium aluminate based on 100 parts by weight of the natural asphalt mixture,

플루오린화나트륨을 천연 아스팔트 혼합물 100중량부를 기준으로 1 내지 5중량부로 더 포함하는 고등급 구스 아스팔트 조성물을 제공한다.
The present invention provides a high grade goeth asphalt composition further comprising 1 to 5 parts by weight of sodium fluoride based on 100 parts by weight of the natural asphalt mixture.

삭제delete

삭제delete

삭제delete

삭제delete

삭제delete

삭제delete

삭제delete

삭제delete

삭제delete

삭제delete

삭제delete

삭제delete

삭제delete

삭제delete

삭제delete

또한, 본 발명은In addition,

포장 대상표면의 이물질을 제거한 후 청소하는 이물질 제거-청소단계;
천연 아스팔트 혼합물 100중량부 기준으로, 스티렌이소프렌스티렌 5 내지 50중량부, 스티렌부타디엔스티렌 5 내지 50중량부, 비닐에스테르 수지, 폴리에스테르 수지, 아크릴 수지, 에폭시 수지, 아크릴-에폭시 수지, 우레탄 수지 또는 이들로부터 선택된 적어도 하나 이상인 고분자 수지 10 내지 30중량부, 골재 10 내지 1,000중량부, 감온성 보강제 1 내지 20중량부, 충진제 10 내지 60중량부, 나노세라믹 입자 10 내지 40중량부, 계면활성제 1 내지 15중량부, 산화방지제 0.1 내지 5중량부, 안정제 0.5 내지 5중량부, 성능개선제 0.5 내지 10중량부, 파이버 2 내지 20중량부, 점착성 수지 10 내지 50중량부, 흐름 방지제 2 내지 10중량부, 및 상용화제 1 내지 5중량부를 포함하는 고등급 구스 아스팔트 조성물에, 글리시딜 메타크릴레이트(GMA)계 수지를 천연 아스팔트 혼합물 100중량부를 기준으로 5 내지 30중량부로 더 포함하고, 벤토나이트를 천연 아스팔트 혼합물 100중량부를 기준으로 0.1 내지 5중량부로 더 포함하며, 알루민산 칼슘을 천연 아스팔트 혼합물 100중량부를 기준으로 1 내지 5중량부로 더 포함하고, 플루오린화나트륨을 천연 아스팔트 혼합물 100중량부를 기준으로 1 내지 5중량부로 더 포함하는 고등급 구스 아스팔트 조성물을 170 내지 250℃의 온도범위에서 기계식 혼합장치로 강제혼합시키는 강제혼합단계;
상기 이물질 제거-청소단계가 종료된 표면에 성가 강제혼합된 고등급 구스 아스팔트 조성물을 타설하는 타설단계; 및
상기 타설단계가 종료된 후 고등급 구스 아스팔트 조성물을 양생하는 양생단계를 포함하는 고등급 구스 아스팔트 조성물의 시공방법을 제공한다.
Removing the foreign object on the surface of the package to be cleaned and then cleaning the object;
Based on 100 parts by weight of a natural asphalt mixture, 5 to 50 parts by weight of styrene isoprene styrene, 5 to 50 parts by weight of styrene butadiene styrene, a vinyl ester resin, a polyester resin, an acrylic resin, an epoxy resin, an acryl- 10 to 30 parts by weight of a polymeric resin selected from the group consisting of an inorganic filler, an inorganic filler and an inorganic filler, 10 to 1,000 parts by weight of an aggregate, 1 to 20 parts by weight of a thermosensitive reinforcing agent, 10 to 60 parts by weight of a filler, 10 to 40 parts by weight of a nanoceramic graft, 0.1 to 5 parts by weight of an antioxidant, 0.5 to 5 parts by weight of a stabilizer, 0.5 to 10 parts by weight of a performance improver, 2 to 20 parts by weight of a fiber, 10 to 50 parts by weight of a viscous resin, 2 to 10 parts by weight of an anti- 1 to 5 parts by weight of a glycidyl methacrylate (GMA) based resin was added to a high grade goeth asphalt composition containing 100 parts by weight of a natural asphalt mixture And 5 to 30 parts by weight based on 100 parts by weight of the natural asphalt mixture, and 1 to 5 parts by weight of calcium aluminate based on 100 parts by weight of the natural asphalt mixture A forced mixing step in which a high grade goeth asphalt composition further comprising 1 to 5 parts by weight of sodium fluoride based on 100 parts by weight of a natural asphalt mixture is forcedly mixed in a mechanical mixing device at a temperature range of 170 to 250 캜;
A pouring step of pouring a high-grade goose asphalt composition which has been subjected to hot-forging mixing on a surface of which the foreign matter removal-cleaning step has been completed; And
And a curing step of curing the high grade goeth asphalt composition after the pouring step is completed.

삭제delete

삭제delete

삭제delete

본 발명에 따른 고등급 구스 아스팔트 조성물은 PG 등급성능이 고등급(PG 82-34)인 공용성 등급의 고등급 구스 아스팔트 조성물 및 이를 이용한 시공방법을 제공한다.
The high grade goeth asphalt composition according to the present invention provides a high grade goeth asphalt composition having a high PG grade performance (PG 82-34) and a method of construction using the high grade goeth asphalt composition.

이하, 본 발명을 구체적으로 설명한다.Hereinafter, the present invention will be described in detail.

한 가지 관점에서, 본 발명은 천연 아스팔트 혼합물 100중량부 기준으로, 스티렌이소프렌스티렌 5 내지 50중량부; 스티렌부타디엔스티렌 5 내지 50중량부; 비닐에스테르 수지, 폴리에스테르 수지, 아크릴 수지, 에폭시 수지, 아크릴-에폭시 수지, 우레탄 수지 또는 이들로부터 선택된 적어도 하나 이상인 고분자 수지 10 내지 30중량부; 골재 10 내지 1,000중량부; 감온성 보강제 1 내지 20중량부; 충진제 10 내지 60중량부; 나노세라믹 입자 10 내지 40중량부; 계면활성제 1 내지 15중량부; 산화방지제 0.1 내지 5중량부; 안정제 0.5 내지 5중량부; 성능개선제 0.5 내지 10중량부; 파이버 2 내지 20중량부; 점착성 수지 10 내지 50중량부; 흐름 방지제 2 내지 10중량부; 및 상용화제 1 내지 5중량부를 포함하는 고등급 구스 아스팔트 조성물을 제공한다.In one aspect, the present invention provides a process for the preparation of a natural asphalt mixture comprising, based on 100 parts by weight of a natural asphalt mixture, from 5 to 50 parts by weight of styrene isoprene styrene; 5 to 50 parts by weight of styrene butadiene styrene; 10 to 30 parts by weight of a polymer resin having at least one or more selected from a vinyl ester resin, a polyester resin, an acrylic resin, an epoxy resin, an acryl-epoxy resin, a urethane resin or the like; 10 to 1,000 parts by weight of aggregate; 1 to 20 parts by weight of a thermosetting reinforcing agent; 10 to 60 parts by weight of a filler; 10 to 40 parts by weight of nano-ceramic particles; 1 to 15 parts by weight of a surfactant; 0.1 to 5 parts by weight of an antioxidant; 0.5 to 5 parts by weight of a stabilizer; 0.5 to 10 parts by weight of a performance improving agent; 2 to 20 parts by weight of fibers; 10 to 50 parts by weight of a tacky resin; 2 to 10 parts by weight of an anti-flow agent; And 1 to 5 parts by weight of a compatibilizing agent.

다른 관점에서, 본 발명은 포장 대상표면의 이물질을 제거한 후 청소하는 이물질 제거-청소단계; 천연 아스팔트 혼합물 100중량부 기준으로, 스티렌이소프렌스티렌 5 내지 50중량부, 스티렌부타디엔스티렌 5 내지 50중량부, 비닐에스테르 수지, 폴리에스테르 수지, 아크릴 수지, 에폭시 수지, 아크릴-에폭시 수지, 우레탄 수지 또는 이들로부터 선택된 적어도 하나 이상인 고분자 수지 10 내지 30중량부, 골재 10 내지 1,000중량부, 감온성 보강제 1 내지 20중량부, 충진제 10 내지 60중량부, 나노세라믹 입자 10 내지 40중량부, 계면활성제 1 내지 15중량부, 산화방지제 0.1 내지 5중량부, 안정제 0.5 내지 5중량부, 성능개선제 0.5 내지 10중량부, 파이버 2 내지 20중량부, 점착성 수지 10 내지 50중량부, 흐름 방지제 2 내지 10중량부, 및 상용화제 1 내지 5중량부를 포함하는 고등급 구스 아스팔트 조성물을 170 내지 250℃의 온도범위에서 기계식 혼합장치로 강제혼합시키는 강제혼합단계; 상기 이물질 제거-청소단계가 종료된 표면에 성가 강제혼합된 고등급 구스 아스팔트 조성물을 타설하는 타설단계; 및 상기 타설단계가 종료된 후 고등급 구스 아스팔트 조성물을 양생하는 양생단계를 포함하는 고등급 구스 아스팔트 조성물의 시공방법을 제공한다.
In another aspect, the present invention provides a method of removing foreign objects, comprising: Based on 100 parts by weight of a natural asphalt mixture, 5 to 50 parts by weight of styrene isoprene styrene, 5 to 50 parts by weight of styrene butadiene styrene, a vinyl ester resin, a polyester resin, an acrylic resin, an epoxy resin, an acryl- 10 to 30 parts by weight of a polymeric resin selected from the group consisting of an inorganic filler, an inorganic filler and an inorganic filler, 10 to 1,000 parts by weight of an aggregate, 1 to 20 parts by weight of a thermosensitive reinforcing agent, 10 to 60 parts by weight of a filler, 10 to 40 parts by weight of a nanoceramic graft, 0.1 to 5 parts by weight of an antioxidant, 0.5 to 5 parts by weight of a stabilizer, 0.5 to 10 parts by weight of a performance improver, 2 to 20 parts by weight of a fiber, 10 to 50 parts by weight of a viscous resin, 2 to 10 parts by weight of an anti- A high grade goeth asphalt composition comprising 1 to 5 parts by weight of a steel which is forced into a mechanical mixing apparatus at a temperature range of 170 to 250 DEG C Mixing step; A pouring step of pouring a high-grade goose asphalt composition which has been subjected to hot-forging mixing on a surface of which the foreign matter removal-cleaning step has been completed; And a curing step of curing the high grade goeth asphalt composition after the pouring step is completed.

본 발명에 따른 천연 아스팔트 혼합물은 당업계에서 통상적으로 사용되는 천연 아스팔트가 포함된 아스팔트 혼합물이라면 특별히 한정되지 않지만, 추천하기로는 천연 아스팔트와 석유계 아스팔트 등이 혼합된 것을 사용할 수 있다.The natural asphalt mixture according to the present invention is not particularly limited as long as it is an asphalt mixture containing natural asphalt commonly used in the art, but a mixture of natural asphalt and petroleum asphalt may be preferably used.

본 발명에 따른 천연 아스팔트 혼합물에 포함되는 천연 아스팔트는 트리니다드레이크(trinidad lake) 아스팔트 및/또는 트리니다드에퓨레(Trinidad epure) 아스팔트 등을 사용할 수 있다.The natural asphalt contained in the natural asphalt mixture according to the present invention may be trinidad lake asphalt and / or trinidad epure asphalt in trinidad.

여기서, 상기 천연 아스팔트는 본 발명의 아스팔트 조성물의 유동성 개선과 더불어 변형저항, 미끄럼저항 및 마찰저항 등을 증가시키는 작용을 한다.Here, the natural asphalt acts to improve the fluidity of the asphalt composition of the present invention and to increase the deformation resistance, the sliding resistance and the frictional resistance.

상기 천연 아스팔트는 천연 아스팔트 혼합물에 0.5 내지 10중량%, 바람직하게는 2 내지 5중량%로 포함되는 것이 바람직하며, 그 함량이 0.5중량% 미만일 경우에는 유동성, 변형저항 및 마찰저항의 개선효과가 미미하며, 10중량%를 초과할 경우에는 본 발명에 따른 천연 아스팔트 조성물이 연질화되고 연화점이 낮아질 수 있다. The natural asphalt is preferably contained in the natural asphalt mixture in an amount of 0.5 to 10% by weight, preferably 2 to 5% by weight. When the content is less than 0.5% by weight, the effect of improving fluidity, If it exceeds 10% by weight, the natural asphalt composition according to the present invention may be softened and the softening point may be lowered.

또한, 상기 천연 아스팔트 혼합물을 구성하는 천연 아스팔트는 당업계에서 통상적으로 사용되는 천연 아스팔트 혼합물이라면 특별히 한정되지 않지만, 바람직하게는 트리니다드레이크(Trinidad lake) 아스팔트, 트리니다드에퓨레(Trinidad epure) 아스팔트 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋고, 보다 바람직하게는 침입도 20 내지 40의 스트레이트 아스팔트와 천연 아스팔트, 예를 들면 트리니다드레이크 아스팔트 및/또는 트리니다드에퓨레 아스팔트 혼합물을 사용하는 것이 더 좋고, 더욱 바람직하게는 침입도 20 내지 40의 스트레이트 아스팔트 90 내지 99.5중량% 및 트리니다드레이크 아스팔트 또는 트리니다드에퓨레 아스팔트로 이루어진 천연 아스팔트 0.5 내지 10중량%를 혼합한 것을 사용하는 것을 추천한다.The natural asphalt constituting the natural asphalt mixture is not particularly limited as long as it is a natural asphalt mixture commonly used in the art, but is preferably a mixture of Trinidad lake asphalt, Trinidad epure asphalt, It is better to use at least one selected mixture, more preferably to use a pure asphalt with a penetration of 20 to 40 and a natural asphalt such as a mixture of pure asphalt with trinidad lake asphalt and / or trinidade, more preferably with It is recommended to use a mixture of 90 to 99.5% by weight of straight asphalt with an intrusion of 20 to 40 and 0.5 to 10% by weight of natural asphalt consisting of trinidad lake asphalt or puree asphalt.

여기서, 상기 스트레이트 아스팔트(straight asphalt)는 석유 아스팔트로 원료를 건류 또는 증류한 잔류물을 정제한 통상의 아스팔트로, 특히 침입도가 20~40인 것이 도로에 시공 시 용이성에 있어 더욱 좋다.Herein, the straight asphalt is a conventional asphalt obtained by refining the residue obtained by distillation or distillation of raw materials with petroleum asphalt. Especially, the asphalt is preferably 20 to 40 in terms of easiness in construction on the road.

상기 스트레이트 아스팔트는 천연 아스팔트 혼합물에 90 내지 99.5중량%로 포함되는 것이 바람직하다. 그 함량이 90중량% 미만일 경우에는 아스팔트 포장 후 굳는데 오랜 시간이 소요될 수 있고, 연화점이 낮아질 수 있으며, 99.5중량%를 초과할 경우에는 유동성이 저하될 수 있다.It is preferable that the straight asphalt is contained in the natural asphalt mixture in an amount of 90 to 99.5% by weight. If the content is less than 90% by weight, it may take a long time to harden after the asphalt pavement, and the softening point may be lowered. When the content exceeds 99.5% by weight, the fluidity may be lowered.

본 발명에 따른 고등급 구스 아스팔트 조성물을 구성하는 천연 아스팔트 혼합물 외 나머지 성분들의 함량은 천연 아스팔트 혼합물 100중량부 기준으로 한다.The content of the remaining components other than the natural asphalt mixture constituting the high grade goeth asphalt composition according to the present invention is based on 100 parts by weight of the natural asphalt mixture.

본 발명에 따른 스티렌이소프렌스티렌(stylene isoprene stylene; SIS)는 아스팔트 조성물의 균열 발생을 억제하고, 방수성능을 제공하는 동시에 강도를 향상시킨다.The styrene isoprene styrene (SIS) according to the present invention suppresses the occurrence of cracks in the asphalt composition, provides waterproof performance and improves strength.

바람직한 스티렌이소프렌스티렌의 사용량은 사용자의 선택에 따라 변경 가능하지만, 추천하기로는 천연 아스팔트 혼합물 100중량부의 5 내지 50중량부인 것이 바람직하다.The amount of styrene-isoprene styrene to be used may be changed according to the user's choice, but it is preferably 5 to 50 parts by weight per 100 parts by weight of the natural asphalt mixture.

본 발명에 따른 스티렌부타디엔스티렌(stylene butadien stylene; SBS)은 상기 스티렌이소프렌스티렌과 같이 아스팔트 조성물의 균열 발생을 억제하고, 방수성능을 제공하는 동시에 강도를 향상시킨다.The styrene butadiene styrene (SBS) according to the present invention inhibits cracking of the asphalt composition such as styrene isoprene styrene, and provides water resistance and strength.

바람직한 스티렌부타디엔스티렌의 사용량은 사용자의 선택에 따라 변경 가능하지만, 추천하기로는 천연 아스팔트 혼합물 100중량부 기준으로 5 내지 50중량부인 것이 바람직하다. The amount of styrene-butadiene styrene to be used may be changed according to the user's choice, but it is preferably 5 to 50 parts by weight based on 100 parts by weight of the natural asphalt mixture.

본 발명에 따른 비닐에스테르 수지, 폴리에스테르 수지, 아크릴 수지, 에폭시 수지, 아크릴-에폭시 수지, 우레탄 수지 또는 이들로부터 선택된 적어도 하나 이상인 고분자 수지는 구스 아스팔트 조성물의 방수성 및 부착성 등을 제공하는 동시에 강도를 향상시키고, 균열 발생을 억제하기 위한 것으로서, 그 사용량은 천연 아스팔트 혼합물 100중량부 기준으로 10 내지 30중량부인 것이 바람직하다.The polymer resin having at least one or more selected from the group consisting of a vinyl ester resin, a polyester resin, an acrylic resin, an epoxy resin, an acryl-epoxy resin, a urethane resin or the vinyl ester resin according to the present invention provides waterproofness and adhesiveness of the goeth asphalt composition, And the use of the asphalt mixture is preferably 10 to 30 parts by weight based on 100 parts by weight of the natural asphalt mixture.

본 발명에 따른 골재는 아스팔트, 고분자 수지 등과 같은 결합재에 의하여 뭉쳐져서 한 덩어리를 이룰 수 있는 건설용 광물질 재료이며, 화학적으로 안정하다.The aggregate according to the present invention is a construction minerals material that can be formed into a lump by binding materials such as asphalt, polymer resin and the like, and is chemically stable.

상기 골재는 모래, 자갈, 현무암, 오석, 바잘트, 기타 이와 비슷한 재료를 지칭한다.The aggregate refers to sand, gravel, basalt, calcite, bazaart, and the like.

특정적으로, 상기 골재로서 약 25mm의 입경 및 약 0.7%의 흡수율을 갖는 염기성 맥암 및/또는 약 5mm의 입경 및 5.40%의 흡수율을 갖는 보크사이트를 더 포함할 수 있다.Specifically, the aggregate may further include basic rock carcasses having a particle size of about 25 mm and an absorption rate of about 0.7% and / or bauxite having a particle size of about 5 mm and an absorption rate of 5.40%.

상기 골재는 크기에 따라 0.074mm 이상 4.76mm 미만의 것은 잔골재라 하고, 4.76mm 이상의 것은 굵은 골재라 한다. 바람직한 골재의 사용량은 천연 아스팔트 혼합물 100중량부 기준으로 10 내지 1,000중량부인 것이 좋고, 상기 골재에 포함되는 잔골재 및 굵은 골재의 혼합량은 특별히 제한되지 않으므로 필요에 따라 적절하게 조절할 수 있다.The aggregate having a size of 0.074 mm or more but less than 4.76 mm is called a fine aggregate, and a material having a diameter of 4.76 mm or more is called a coarse aggregate. The amount of the aggregate to be used is preferably 10 to 1,000 parts by weight based on 100 parts by weight of the natural asphalt mixture, and the amount of the fine aggregate and the coarse aggregate contained in the aggregate is not particularly limited and can be appropriately adjusted as needed.

본 발명에 따른 감온성 보강제는 구스 아스팔트 조성물의 감온성을 제고시켜 기온변화에 의한 구스 아스팔트 조성물의 성능변화를 저감할 수 있도록 하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 감온성 보강제라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 감압가스유의 수첨개질 공정의 공정부산물, 감압가스유의 수첨분해 공정의 공정 부산물, 조왁스 수첨 이성화 반응 공정의 공정부산물, 메탄가스 합성 공정의 공정부산물, 폴리에틸렌 합성 공정의 공정부산물, 폴리프로필렌 합성 공정의 공정부산물을 포함하며, 바람직하게는 상기 공정 부산물 중 인화점이 180℃ 이상이고, 화합물내 포화 탄화수소 함량이 80%이상인 포화 탄화수소계 화합물 중 적어도 한 가지 이상 포함하는 물질을 사용하는 것이 좋다.The thermosetting reinforcing agent according to the present invention is intended to improve the thermosensitive property of the goeth asphalt composition and to reduce the performance change of the goeth asphalt composition due to the change in temperature. Any conventional warmth- Preferably byproducts of the hydrogenation process of the reduced-pressure gas oil, process by-products of the hydrocracking process of the reduced-pressure gas oil, process by-products of the crude wax hydrogenation isomerization process, process by-products of the methane gas synthesis process, processes of the polyethylene synthesis process By-products of the polypropylene synthetic process, and preferably a material containing at least one of the above-mentioned process by-products, which has a flash point of 180 ° C or higher and a saturated hydrocarbon content of 80% or higher, It is good to do.

상기 포화 탄화수소는 감온성을 높이는 작용을 하기 때문에 포화 탄화수소의 함량이 많을수록 기온변화에 의한 구스 아스팔트 혼합물의 성능변화가 더욱 작다. 만약 포화 탄화수소의 함량이 비교적 적으면 상대적으로 방향족 함량이 많아져 감온성이 저하되고 동일한 효과를 가지려면 더욱 많은 량을 첨가해야 하는데 이는 원가를 높이기에 경제적이지 못하다.Since the saturated hydrocarbons have an effect of enhancing the temperature sensitivity, the performance of the goeth-asphalt mixture due to temperature changes is smaller as the content of saturated hydrocarbons increases. If the content of saturated hydrocarbons is relatively low, the aromatic content becomes relatively high and the thermosensitivity is degraded. To achieve the same effect, a larger amount of the saturated hydrocarbons should be added, which is not economical to increase the cost.

따라서 상기 부산물 중 포화 탄화수소의 함량이 80%이상인 포화 탄화수소 부산물을 선택한다. 바람직하기로는 감압가스유의 수첨분해 공정의 공정부산물과 메탄가스 합성 공정의 공정부산물 중 인화점이 230℃이고 포화 탄화수소 함량이 90%이상인 포화 탄화수소계 부산물 중 적어도 한 가지를 선택한다.Therefore, a saturated hydrocarbon by-product having a content of saturated hydrocarbons of 80% or more in the by-product is selected. Preferably, at least one of the process by-products of the hydrocracking process of the reduced-pressure gas oil and the process by-product of the methane gas synthesis process is selected from saturated hydrocarbon-based by-products having a flash point of 230 ° C and a saturated hydrocarbon content of 90% or more.

바람직한 감온성 보강제의 사용량은 특별히 한정되는 것은 아니지만, 천연 아스팔트 혼합물 100중량부 기준으로 1 내지 20중량부인 것이 좋다.The amount of the thermosensitive reinforcing agent to be used is not particularly limited, but is preferably 1 to 20 parts by weight based on 100 parts by weight of the natural asphalt mixture.

본 발명에 따른 충진제는 아스팔트 조성물의 공극채움성과, 안정도, 내마모성 및 내유동성을 향상시키는 동시에 아스팔트 조성물 상호간의 결합력을 향상시켜, 결과적으로는 마샬안정도(Marshall stability)를 증가시키는 역할을 한다.The filler according to the present invention improves the pore filling property, stability, abrasion resistance and fluidity of the asphalt composition, and improves the bonding force between the asphalt compositions, thereby increasing the Marshall stability.

바람직한 충진제는 석회분말, 포틀랜드 시멘트, 소석회, 플라이애쉬, 회수 더스트, 전기로 제강더스트, 주물더스트 및 소각재로 이루어진 그룹으로부터 선택된 하나 이상으로 이루어지는 것을 사용하는 것이 바람직하고, 그 사용량은 천연 아스팔트 혼합물 100중량부 기준으로 10 내지 60중량부를 사용하는 것을 추천한다.The preferred filler is preferably one or more selected from the group consisting of lime powder, Portland cement, slaked lime, fly ash, recovered dust, electric furnace slag, cast dust and incineration as the amount of the natural asphalt mixture It is recommended to use 10 to 60 parts by weight as a part basis.

본 발명에 따른 나노세라믹 입자는 아스팔트 조성물, 특정적으로 고등급 구스 아스팔트 조성물의 양생 중에 표면으로 부상하여 치밀하고 경도가 높은 표면을 형성하기 때문에, 수증기와 기타 기체, 액체의 투과를 방지함은 물론, 내습성, 내구성, 내후성, 내충격성, 내약품성이 향상된다.The nanoceramic particles according to the present invention float on the surface during curing of an asphalt composition, specifically a high-grade goeth asphalt composition, to form a dense and hard surface, thereby preventing permeation of water vapor and other gases and liquids , Moisture resistance, durability, weather resistance, impact resistance and chemical resistance are improved.

상기 나노세라믹 입자의 사용량은 천연 아스팔트 혼합물 100중량부 기준으로 10 내지 40중량부인 것이 좋다.The amount of the nanoceramic particles used is preferably 10 to 40 parts by weight based on 100 parts by weight of the natural asphalt mixture.

바람직한 나노세라믹 입자는 실리콘카바이드, 알루미나, 실리카, 지르코니아-실리카, ZnO, TiO2 및/또는 CaCO3가 포함된다.Preferred nanoceramic particles include silicon carbide, alumina, silica, zirconia-silica, ZnO, TiO 2 and / or CaCO 3 .

이들 세라믹입자는 평균 입경이 나노 범위인 것이 바람직한데, 구체적으로 상기 실리콘카바이드의 평균 입경은 300 내지 500nm, 상기 알루미나의 평균 입경은 500 내지 1000nm, 상기 실리카의 평균 입경은 700 내지 1500nm, 상기 지르코니아-실리카의 평균 입경은 500 내지 1000nm, 상기 ZnO의 평균 입경은 500 내지 1000nm, 상기 TiO2의 평균 입경은 100 내지 300nm, 그리고 CaCO3의 평균 입경은 500 내지 1000nm인 것이 바람직하다.Preferably, the average particle size of the ceramic particles is in the range of 300 to 500 nm, the average particle size of the alumina is 500 to 1000 nm, the average particle size of the silica is 700 to 1500 nm, the zirconia- It is preferable that the average particle size of silica is 500 to 1000 nm, the average particle size of ZnO is 500 to 1000 nm, the average particle size of TiO 2 is 100 to 300 nm, and the average particle size of CaCO 3 is 500 to 1000 nm.

이 중에서도 실리콘카바이드는 천연광물로 존재하지 않으므로 인공적으로 합성하며, 고온에서의 화학적 안정성 및 내식성이 뛰어나고 높은 경도를 갖는다. Among them, silicon carbide does not exist as natural minerals, so it is synthesized artificially, has excellent chemical stability and corrosion resistance at high temperature, and has high hardness.

본 발명에 따른 계면활성제는 음이온계면활성제로서 술폰 에스테르, 술폰산, 포스포릭 에스테르; 양이온계면활성제로서 2차 아민염, 3차 아민염; 양이온성계면활성제로서 아미노산 타입 등을 사용할 수 있다.Surfactants according to the present invention include sulfonic acid esters such as sulfonic esters, sulfonic acids, and phosphoric esters as anionic surfactants; Secondary amine salts and tertiary amine salts as cationic surfactants; As the cationic surfactant, an amino acid type or the like can be used.

바람직한 계면활성제의 사용량은 천연 아스팔트 혼합물 100중량부 기준으로 1 내지 15중량부인 것을 추천한다.The preferred amount of surfactant used is from 1 to 15 parts by weight based on 100 parts by weight of the natural asphalt mixture.

본 발명에 따른 산화방지제는 고등급 구스 아스팔트 조성물의 산화를 방지하기 위한 것이다.The antioxidant according to the present invention is intended to prevent oxidation of the high grade goeth asphalt composition.

바람직한 산화방지제는 아민계, 비스페놀계, 모노페놀계 및 유황계 산화방지제가 사용될 수 있고, 그 사용량은 천연 아스팔트 혼합물 100중량부 기준으로 0.1 내지 5중량부인 것이 좋다.The preferred antioxidant may be an amine-based, bisphenol-based, monophenol-based or sulfur-based antioxidant, and the amount of the antioxidant may be 0.1 to 5 parts by weight based on 100 parts by weight of the natural asphalt mixture.

특정적으로, 본 발명에 따른 산화방지제는 고온에서 가공이 이루어질 경우 저분자형 고분자형 페놀계 산화방지제, 예를 들면 2.2-메틸렌비스(4-메틸-6-t-부틸페놀)[2 . 2 - M e t h y l e n e b i s ( 4 - m e t h y l - 6 - t - b u t y l p h e n o l )], 2.6-디-t-부틸-4-메틸페놀(2.6-di -t-Butyl-4-methylphenol) 또는 이들의 혼합물을 사용하는 것을 추천한다.Specifically, the antioxidant according to the present invention is a low-molecular type high molecular weight phenolic antioxidant such as 2,2-methylenebis (4-methyl-6-t-butylphenol) [2. 2 - M ethylenebis (4 - methyl - 6 - t - butylphenol), 2.6 - di - t - Butyl - 4 - methylphenol or mixtures thereof I recommend you.

본 발명에 따른 안정제는 고등급 구스 아스팔트 조성물을 자외선으로부터 보호하여 안정성을 제공하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 안정제라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 아크릴 폴리올 수지, 무황변 폴리 우레아수지, 폴리이소시아네이트 또는 이들의 혼합물을 사용하는 것이 좋고, 그 사용량은 천연 아스팔트 혼합물 100중량부 기준으로 0.5 내지 10중량부인 것을 추천한다.The stabilizer according to the present invention is intended to provide stability by protecting the high-grade goeth asphalt composition from ultraviolet rays. Any conventional stabilizer in the art having such a purpose may be used, but preferably an acrylic polyol resin, A yellowing polyurea resin, a polyisocyanate or a mixture thereof is preferably used, and it is recommended that the amount thereof is 0.5 to 10 parts by weight based on 100 parts by weight of the natural asphalt mixture.

본 발명에 따른 성능개선제는 아스팔트 조성물을 구성하는 천연 아스팔트 혼합물의 기능을 향상시키기 위한 것으로서, 이러한 목적을 위해 당업계에서 통상적으로 사용되는 성능개선제, 특정적으로 아스팔트 성능개선제라면 어떠한 것을 사용하여도 무방하며, 그 사용량은 천연 아스팔트 혼합물 100중량 기준으로 0.5 내지 10중량부인 것이 바람직하다.The performance improving agent according to the present invention is intended to improve the function of the natural asphalt mixture constituting the asphalt composition. For this purpose, a performance improving agent conventionally used in the art, specifically, any asphalt performance improving agent, And the amount thereof is preferably 0.5 to 10 parts by weight based on 100 parts by weight of the natural asphalt mixture.

바람직한 성능개선제로는 성능개선제 전체 중량 기준으로 비닐아세테이트 모노머-파라핀오일 90 내지 99.5중량% 및 과산화벤조일 0.5내지 10중량%를 포함하는 것이 좋다.Preferred performance enhancers include from 90 to 99.5% by weight of vinyl acetate monomer-paraffin oil and from 0.5 to 10% by weight of benzoyl peroxide based on the total weight of the performance improver.

여기서, 상기 비닐아세테이트 모노머-파라핀오일은 비닐아세테이트 모노머 5 내지 25중량% 및 파라핀 오일 75 내지 95중량%가 혼합된 것을 사용하는 것이 바람직하다.The vinyl acetate monomer-paraffin oil may be a mixture of 5 to 25% by weight of a vinyl acetate monomer and 75 to 95% by weight of a paraffin oil.

본 발명에 따른 파이버는 고등급 구스 아스팔트 조성물로 형성된 교면의 종-횡 방향으로 가해지는 응력에 의한 인장력 및/또는 경량성 등을 제공하기 위한 것으로서, 이러한 목적을 갖는 파이버라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 석면, 암면, 폴리프로필렌, 폴리에스터, 유리섬유, 천연 셀룰로오즈 섬유 및 광물질섬유 중 선택된 어느 하나 이상의 혼합물을 사용하는 것이 좋고, 그 사용량은 천연 아스팔트 혼합물 100중량부 기준으로 2 내지 20중량부인 것이 좋다.The fiber according to the present invention is intended to provide a tensile force and / or lightweight by stress applied in the longitudinal-transverse direction of a cross-section formed of a high-grade goeth asphalt composition. Any fiber having such a purpose may be used Preferably, however, it is preferable to use a mixture of at least one selected from asbestos, rock wool, polypropylene, polyester, glass fiber, natural cellulose fiber and mineral fiber, and the amount thereof is 2 to 20 It is good to be in weight.

본 발명에 따른 점착성 수지는 고등급 구스 아스팔트 조성물의 점착성을 향상시키기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 수지라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 방향족 탄화수소계 석유수지, 지방족 탄화수소계 석유수지, 디시클로펜타디엔계 수지, 폴리부텐, 쿠마론-인덴 수지 등의 합성 석유수지 및 폴리터펜 수지, 터펜 페놀 수지, 로진, 로진 에스터 등의 천연계 석유수지와 이들의 수소 첨가물 등을 사용할 수 있으며, 보다 바람직하게는 연화점이 70 내지 170℃인 방향족 탄화수소계 석유수지를 사용하는 것이 좋다.The adhesive resin according to the present invention is intended to improve the tackiness of the high grade goeth asphalt composition. Any conventional resin in the art having such a purpose may be used, but preferably an aromatic hydrocarbon-based petroleum resin, an aliphatic hydrocarbon Synthetic petroleum resins such as petroleum resin, dicyclopentadiene resin, polybutene and coumarone-indene resin, and natural petroleum resins such as polyterpene resin, terpene phenol resin, rosin and rosin ester, and hydrogenated products thereof And more preferably an aromatic hydrocarbon-based petroleum resin having a softening point of 70 to 170 ° C.

상기 점착성 수지의 바람직한 사용량은 특별히 한정되지 않지만, 추천하기로는 천연 아스팔트 혼합물 100중량부 기준으로 10 내지 50중량부인 것이 좋다.The amount of the adhesive resin to be used is not particularly limited, but is preferably 10 to 50 parts by weight based on 100 parts by weight of the natural asphalt mixture.

이때, 상기 점착성 수지의 사용량이 용량이 10중량부 미만이면 골재와의 접착력이 약해질 수 있으며, 60중량부를 초과하여 사용할 경우에는 제품 가공시에 제품간에 응집 현상이 발생하게 되어 가공이 어려워지며, 이를 해결하기 위해 추가적인 가공비 상승을 초래하게 된다.If the amount of the adhesive resin is less than 10 parts by weight, the adhesive strength with the aggregate may be weakened. If the amount is more than 60 parts by weight, coagulation phenomenon occurs between the products during the processing of the product, To solve this problem, additional processing costs are increased.

본 발명에 따른 흐름방지제는 고등급 구스 아스팔트 조성물을 이용한 시공시 필요 이상의 유동성을 갖지 않도록 하기 위한 것으로서, 이러한 목적을 위해 당업계에서 통상적으로 사용되는 흐름방지제라면 어떠한 것을 사용하여도 무방하지만, 추천하기로는 폴리에틸렌(PE)왁스, 폴리프로필렌(PP)왁스, 아마이드왁스, 스테아린산 아연, 스테아린산 칼슘, 스테아린산, 마이크로 왁스 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋고, 그 사용량은 천연 아스팔트 혼합물 100중량부 기준으로 2 내지 10중량부인 것을 추천한다.The flow preventive agent according to the present invention is designed to have no more flowability than necessary when using a high grade goeth asphalt composition. For this purpose, any flow inhibitor commonly used in the art may be used, It is preferable to use at least one selected from the group consisting of polyethylene wax, polypropylene wax, amide wax, zinc stearate, calcium stearate, stearic acid, micro wax or a mixture thereof. It is recommended that the amount is 2 to 10 parts by weight.

본 발명에 따른 상용화제는 아스팔트 조성물에 포함된 천연 아스팔트 혼합물과 성능개선제 간의 상용성을 증대시키기 위한 것이다.The compatibilizer according to the present invention is intended to enhance the compatibility between the natural asphalt mixture and the performance improver contained in the asphalt composition.

바람직한 상용화제로는 폴리인산, 금속염 무기산류 또는 이들의 혼합물을 사용할 수 있고, 그 사용량은 천연 아스팔트 혼합물 100중량부 기준으로 1 내지 5중량부를 사용하는 것을 추천한다.As a preferable compatibilizer, polyphosphoric acid, metal salt inorganic acid, or mixture thereof can be used, and it is recommended to use 1 to 5 parts by weight based on 100 parts by weight of the natural asphalt mixture.

특정 양태로서, 본 발명에 따른 고등급 구스 아스팔트 조성물은 충격강도, 신율, 인장강도 및/또는 탄성력 등을 향상사키기 위하여 천연 아스팔트 혼합물 100중량부 기준으로 5 내지 30중량부의 글리시딜 메타크릴레이트(GMA)계 수지를 더 포함할 수 있다.As a specific aspect, the high grade goeth asphalt composition according to the present invention may contain 5 to 30 parts by weight of glycidyl methacrylate based on 100 parts by weight of the natural asphalt mixture to improve impact strength, elongation, tensile strength and / (GMA) based resin.

바람직한 글리시딜 메타크릴레이트계 수지는 에틸렌-글라시딜메타크릴레이트 코폴리머(EGMA), 에틸렌-부틸아크릴레이트-글라시딜메타크릴레이트 코폴리머(EBA-GMA) 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다.Preferred glycidyl methacrylate resins include ethylene-glycidyl methacrylate copolymer (EGMA), ethylene-butyl acrylate-glycidyl methacrylate copolymer (EBA-GMA), or at least one Mixtures are recommended.

다른 특정 양태로서, 본 발명에 따른 고등급 구스 아스팔트 조성물은 아스팔트 조성물을 경화시키기 위하여 천연 아스팔트 혼합물 100중량부 기준으로 2 내지 30중량부의 경화제를 더 포함할 수 있다.In another specific embodiment, the high grade goeth asphalt composition according to the present invention may further comprise 2 to 30 parts by weight of a curing agent based on 100 parts by weight of the natural asphalt mixture to cure the asphalt composition.

바람직한 경화제로는 4.4-디페닐메탄 디이소시아네이트(MDI), 핵사메틸렌테트라민, 아민류, 폴리아마이드 또는 이들의 혼합물을 사용하는 것이 좋다.As the preferred curing agent, it is preferable to use 4.4-diphenylmethane diisocyanate (MDI), hexamethylene tetramine, amines, polyamide or a mixture thereof.

특정적으로, 상기 경화제는 저수축제를 더 포함할 수 있다.Specifically, the curing agent may further comprise a water-reducing agent.

이러한 경우, 상기 저수축제는 경화제 전체 중량 기준으로 30중량%를 넘지 않는 범위에서 사용하는 것을 추천한다.In this case, it is recommended that the water-reducing agent is used in an amount not exceeding 30% by weight based on the total weight of the curing agent.

바람직한 저수축제로는 불포화 폴리에스터계 저수축제, 예를 들면 불포화 폴리에스터 수지로 이루어진 저수축제를 사용하는 것을 추천한다.As a preferable low-shrinkage agent, it is recommended to use a water-reducing agent composed of an unsaturated polyester-based water-reducing agent, for example, an unsaturated polyester resin.

또 다른 특정 양태로서, 본 발명에 따른 고등급 구스 아스팔트 조성물은 아스팔트 조성물이 시공되는 접촉면에 보다 용이하게 접착할 수 있도록 천연 아스팔트 혼합물 100중량부 기준으로 5 내지 30중량부의 부착증진제를 더 포함할 수 있다.In another specific embodiment, the high grade goeth asphalt composition according to the present invention may further comprise 5 to 30 parts by weight of adhesion promoter based on 100 parts by weight of the natural asphalt mixture so that the asphalt composition can more easily adhere to the contact surface to which it is applied have.

바람직한 부착증진제는 하이드록시 에틸 아크릴로일 포스페이트, 하이드록시 에틸 메타 아크릴레이트 포스페이트 또는 이들의 혼합물을 사용할 수 있다.Preferred adhesion promoters are hydroxyethyl acryloyl phosphate, hydroxyethyl methacrylate phosphate or mixtures thereof.

또 다른 특정 양태로서, 본 발명에 따른 아스팔트 조성물, 특정적으로 고등급 구스 아스팔트 조성물은 물을 흡수하며 팽창됨으로써, 아스팔트 공극을 메워 수분 침투를 방지하여 내구성을 향상사키는 가교된 폴리아크릴레이트 염을 천연 아스팔트 혼합물 100중량부 기준으로 20 내지 50중량부 더 포함할 수 있다.As another specific embodiment, the asphalt composition according to the present invention, specifically the high grade goeth asphalt composition, absorbs water and expands, thereby improving the durability of the asphalt pavement by preventing moisture penetration, thereby obtaining a crosslinked polyacrylate salt And 20 to 50 parts by weight based on 100 parts by weight of the natural asphalt mixture.

여기서, 상기 가교된 폴리아크릴레이트염은 아크릴레이트염의 중합체가 가교(crosslink)된 물질을 말하며, 고흡수성 폴리머의 일종으로, 가교제로 아크릴산(Acrylic acid)dl 포함된 아크릴산과 소듐아크릴레이트(sodium acrylate)의 공중합체로 이루어지며, 하기 (C3H4O2.C3H3O2Na)x 의 분자식을 갖는다.Herein, the crosslinked polyacrylate salt refers to a crosslinked polymer of an acrylate salt. The crosslinked polyacrylate salt is a kind of a superabsorbent polymer. Examples of the crosslinking agent include acrylic acid, sodium acrylate, consists of a copolymer, to (C 3 H4O 2 .C 3 H 3 O 2 Na) has a molecular formula of x.

상기의 구조로 이루어지는 가교된 폴리아크릴레이트염은 고분자 사슬 간의 가교결합(cross-linking)을 통한 3차원의 망상구조 또는 단일 사슬구조에서 친수성기의 도입에 따른 유체의 흡수현상을 나타내는 폴리머로, 일반 폴리머 재료에 비하여 흡수성이 월등히 높기 때문에 위생용품의 슬림화 및 고성능화 실현을 위한 필수적인 고기능성 재료로 사용되며, 이러한 고흡수성 폴리머인 가교된 폴리아크릴레이트염이 아스팔트 조성물에 사용되면 수분 침투시 팽창하여 아스팔트 조성물의 내부 공극을 채워 수분의 침투를 방지하고, 내구성을 증진시키게 된다.The crosslinked polyacrylate salt having the above structure is a polymer exhibiting fluid absorption phenomenon due to the introduction of a hydrophilic group in a three-dimensional network structure or a single-chain structure through cross-linking between polymer chains, It is used as a highly functional material essential for slimming down the hygienic article and realizing high performance. When the crosslinked polyacrylate salt as the superabsorbent polymer is used in the asphalt composition, it expands upon infiltration with water, so that the asphalt composition Filling the internal voids to prevent the penetration of moisture, and improving the durability.

또 다른 특정 양태로서, 본 발명에 따른 아스팔트 조성물은 포장 대상면으로부터 쉽게 박리되는 것을 방지하기 위하여 천연 아스팔트 혼합물 100중량부 기준으로 5 내지 30중량부의 박리방지제를 더 포함할 수 있다.In another specific embodiment, the asphalt composition according to the present invention may further contain 5 to 30 parts by weight of the anti-peeling agent based on 100 parts by weight of the natural asphalt mixture to prevent the peeling from the surface to be packed easily.

바람직한 박리방지제는 폴리인산계, 아민계, 또는 인산 에스테르계 박리방지제를 사용하는 것이 좋다.As the preferable peeling inhibitor, it is preferable to use a polyphosphoric acid type, an amine type, or a phosphoric acid ester type peeling inhibitor.

특정적으로, 상기 박리방지제는 액상형으로 비중이 1.0 이상이고 60℃ 점도가 110 cPs인 폴리인산계 박리방지제; 산가가 10 ㎎KOH/g 이하이고, 총 아민가가 140 내지 400㎎HCl/g인 아민계 박리방지제일 수 있다.Specifically, the anti-peeling agent is a liquid phase anti-peeling agent having a specific gravity of 1.0 or more and a viscosity at 60 DEG C of 110 cPs; The acid value is 10 mgKOH / g or less, and the total amine value is 140 to 400 mg HCl / g.

또 다른 특정 양태로서, 본 발명에 따른 아스팔트 조성물은 건조층의 표면 택키(tacky)를 방지하여 차량 통행으로 인한 표면오염을 방지하기 위한 왁스를 천연 아스팔트 혼합물 100중량부 기준으로 2 내지 5중량부 더 포함할 수 있다.As another specific embodiment, the asphalt composition according to the present invention may further comprise 2 to 5 parts by weight of wax based on 100 parts by weight of the natural asphalt mixture to prevent surface tacky of the dry layer to prevent surface contamination due to vehicle passage .

바람직한 왁스로는 폴리에틸렌 왁스 또는 폴리프로필렌 왁스 또는 이들의 혼합물을 사용하는 것이 좋다.As the preferable wax, polyethylene wax or polypropylene wax or a mixture thereof is preferably used.

또 다른 특정 양태로서, 본 발명에 따른 고등급 구스 아스팔트 조성물은 폐 아스팔트를 더 포함할 수 있다.In another specific embodiment, the high grade goeth asphalt composition according to the present invention may further comprise waste asphalt.

상기 폐 아스팔트는 종래에 포장용으로 사용된 아스팔트가 노후화되거나 파손되어 교체할 경우 발생되는 것을 주로 사용하며, 그 사용량은 천연 아스팔트 혼합물 100중량부 기준으로 50 내지 150중량부인 것을 추천한다.It is recommended that the waste asphalt is produced when the asphalt conventionally used for packaging is aged or broken and replaced with 50 to 150 parts by weight based on 100 parts by weight of the natural asphalt mixture.

또 다른 특정 양태로서, 본 발명에 따른 아스팔트 조성물은 고분자 개질제를 더 포함할 수 있다.In another specific embodiment, the asphalt composition according to the present invention may further comprise a polymer modifier.

여기서, 상기 고분자 개질제는 당업계에서 통상적으로 사용하는 고분자 개질제라면 어떠한 것을 사용하여도 무방하며, 그 사용량은 천연 아스팔트 혼합물 100중량부 기준으로 2 내지 40중량부인 것을 추천한다.The polymer modifier may be any polymer modifier generally used in the art, and it is recommended that the modifier is used in an amount of 2 to 40 parts by weight based on 100 parts by weight of the natural asphalt mixture.

상기 고분자 개질제의 일 양태로서, 본 발명에서는 생고무, 니트릴고무, 스티렌부타디엔고무, 부타디엔고무 및 이들의 혼합물로 이루어진 군으로부터 선택된 고분자 수지를 포함하는 개질제를 사용하는 것이 좋다.As an embodiment of the polymer modifier, it is preferable to use a modifier comprising a polymer resin selected from the group consisting of crude rubber, nitrile rubber, styrene butadiene rubber, butadiene rubber, and mixtures thereof.

또 다른 특정 양태로서, 본 발명에 따른 고등급 구스 아스팔트 조성물은 균열발생을 억제하고, 접착력 및 내구성을 향상시키기 위하여 천연 아스팔트 혼합물 100중량부 기준으로 5 내지 20중량부의 바이오 수지를 더 포함할 수 있다.In another specific embodiment, the high grade goeth asphalt composition according to the present invention may further comprise 5 to 20 parts by weight of a bio-resin based on 100 parts by weight of the natural asphalt mixture in order to suppress cracking, improve adhesion and durability .

바람직한 바이오 수지는 유변성 알키드 수지, 유변성 우레탄 수지, 유변성 우레탄 수지의 지방산 에스테르, 유변성 에폭시 수지, 유변성 에폭시 수지의 지방산 에스테르, 바이오 폴리에틸렌 수지, L-폴리락트산 또는 이들의 혼합물로 이루어진 것을 사용하는 것이 좋고, 추천하기로는 유변성 알키드 수지를 사용하는 것이 좋다.Preferable bio-resins include those made of a rubidic alkyd resin, a rubidic urethane resin, a fatty acid ester of a rubidic urethane resin, a rubidic epoxy resin, a fatty acid ester of a rubidic epoxy resin, a biopolyethylene resin, L-polylactic acid or a mixture thereof It is recommended to use a rubidic alkyd resin.

여기서, 상기 유변성은 지방산 등의 유성분을 분자 중에 함유하는 수지를 지칭하는 것으로서, 이러한 유변성 수지를 사용하게 되면 분산성, 기계적 성질, 경화성, 피막 형성성을 제어하기 용이하다.Here, the rheological property refers to a resin containing a oil component such as a fatty acid in a molecule. When such a rheological resin is used, it is easy to control the dispersibility, the mechanical properties, the curability, and the film formability.

특정적으로, 상기 바이오 수지는 식물성 오일, 예를 들면 식물 또는 식물의 씨로부터 추출된 오일로, 쌀 기름, 팜 오일, 코코넛 오일, 피마자 오일, 포도씨 오일, 호호바 오일, 홍화 오일, 마카데미아너츠 오일, 올리브씨 오일, 및 이들의 혼합 오일과 혼합하여 사용할 수 있다.Specifically, the bio-resin is an oil extracted from a vegetable oil, for example, a plant or a plant seed, and is preferably selected from the group consisting of rice oil, palm oil, coconut oil, castor oil, grape seed oil, jojoba oil, safflower oil, Oil, olive seed oil, and mixed oil thereof.

이때, 상기 바이오 수지와 식물성 오일의 혼합비는 사용자의 선택에 따라 변경 가능하지만, 추천하기로는 바이오 수지와 식물성 오일의 중량비율로서 1:9 내지 9:1인 것이 좋다.At this time, the mixing ratio of the bio resin and the vegetable oil can be changed according to the user's choice, but it is recommended that the weight ratio of the bio resin and the vegetable oil is 1: 9 to 9: 1.

또 다른 특정 양태로서, 본 발명에 따른 고등급 구스 아스팔트 조성물은 아스팔트의 점탄성을 높이기 위하여 천연 아스팔트 혼합물 100중량부 기준으로 0.1 내지 1중량부의 소듐 벤조 에이트(sodium benzoate)를 더 포함할 수 있는데, 소듐 벤조 에이트가 0.1중량부 보다 적을 경우 효과가 미미하며, 1중량부를 초과할 경우 과량이 되어 물성을 저하시킬 수 있다.In another specific embodiment, the high grade goeth asphalt composition according to the present invention may further comprise 0.1 to 1 part by weight of sodium benzoate based on 100 parts by weight of the natural asphalt mixture in order to increase the viscoelasticity of the asphalt, When the amount of the benzoate is less than 0.1 parts by weight, the effect is insignificant. When the amount of the benzoate exceeds 1 part by weight, the amount of the benzoate is excessive and the physical properties may be deteriorated.

또 다른 특정 양태로서, 본 발명에 따른 구스 아스팔트 조성물은 포장되는 아스팔트 조성물의 박리 방지를 위하여 천연 아스팔트 혼합물 100중량부 기준으로 0.1 내지 2중량부의 다이머산(Dimer acid)을 더 포함 할 수 있다.In another specific embodiment, the goeth asphalt composition according to the present invention may further comprise 0.1 to 2 parts by weight of dimer acid based on 100 parts by weight of the natural asphalt mixture in order to prevent peeling of the asphalt composition to be packed.

상기 다이머산은 그 유래 및 형태가 크게 제한되지 않으나, 식물유 지방산의 이량체인 것이 바람직하고, 식물류 지방산은 올레익산, 리놀레익산, 스테아릭산 및 팔미틱산으로 이루어진 군에서 선택되는 1종 이상으로 구성될 수 있다.The dimeric acid is not particularly limited in its origin and form, but is preferably an amount of vegetable oil fatty acid. The vegetable fatty acid may be at least one selected from the group consisting of oleic acid, linoleic acid, stearic acid and palmitic acid have.

또 다른 특정 양태로서, 본 발명에 따른 고등급 구스 아스팔트 조성물은 점도 조절 및 강도증진을 위하여 테트라에틸렌펜타민(Tetraethylenepentamine; TEPA)을 천연 아스팔트 혼합물 100중량부 기준으로 1 내지 10중량부 더 포함할 수 있는데, 테트라에틸렌펜타민이 1중량부 미만이면 그 효과가 미미하며, 10중량부를 초과하면 그 양이 과다하여 구스 아스팔트 조성물의 물성에 좋지 않은 영향을 줄 수 있다.In another specific embodiment, the high grade goeth asphalt composition according to the present invention may contain 1 to 10 parts by weight of tetraethylenepentamine (TEPA) based on 100 parts by weight of the natural asphalt mixture for viscosity control and strength enhancement If the amount of tetraethylenepentamine is less than 1 part by weight, the effect is insignificant. If the amount is more than 10 parts by weight, the amount of tetraethylenepentamine is excessive, which may adversely affect the physical properties of the goeth asphalt composition.

또 다른 특정 양태로서, 본 발명에 따른 고등급 구스 아스팔트 조성물은 조성물의 수밀성과 투수계수를 개선하기 위하여 천연 아스팔트 혼합물 100중량부를 기준으로 0.1 내지 5중량부의 벤토나이트를 더 포함할 수 있는데, 벤토나이트가 0.1중량부 보다 적을 경우 효과가 미미하며, 5중량부를 초과할 경우 과량이 되어 물성을 저하시킬 수 있다.In another specific embodiment, the high grade goeth asphalt composition according to the present invention may further comprise 0.1 to 5 parts by weight of bentonite based on 100 parts by weight of the natural asphalt mixture to improve watertightness and permeability of the composition, wherein the bentonite is 0.1 When the amount is less than 5 parts by weight, the effect is insignificant. When the amount is more than 5 parts by weight, the amount is excessive and the physical properties may be deteriorated.

또 다른 양태로서, 본 발명에 따른 고등급 구스 아스팔트 조성물은 조성물의 건조 수축을 방지하기 위하여 천연 아스팔트 혼합물 100중량부를 기준으로 1 내지 5중량부의 알루민산 칼슘을 더 포함할 수 있는데, 알루민산 칼슘은 조성물에 포함되면 팽창성을 띠게 되어 건초수축을 방지하게 되는데, 사용량이 1중량부 보다 적을 경우에는 효과가 미미하며, 5중량부를 초과할 경우 과다하여 작업성을 저하 시킬수 있다.In another aspect, the high grade goeth asphalt composition according to the present invention may further comprise 1 to 5 parts by weight of calcium aluminate based on 100 parts by weight of the natural asphalt mixture to prevent drying and shrinking of the composition. If the amount is less than 1 part by weight, the effect is insignificant. If the amount is more than 5 parts by weight, the workability may be deteriorated.

또 다른 양태로서, 본 발명에 따른 고등급 구스 아스팔트 조성물은 조성물의 충진성 및 내구성을 향상시키기 위하여 천연 아스팔트 혼합물 100중량부를 기준으로 1 내지 5중량부의 플루오린화나트륨을 더 포함할 수 있는데, 플루오린화 나트륨은 1차적으로 충진제로서의 역할도 하지만, 2차적으로는 내구성을 향상시키는 역할을 하는 것으로, 상기와 같은 함량 범위에서 그 효과를 얻을 수 있다.In another embodiment, the high grade goeth asphalt composition according to the present invention may further comprise 1 to 5 parts by weight of sodium fluoride based on 100 parts by weight of the natural asphalt mixture to improve the filling and durability of the composition, Sodium plays a role primarily as a filler, but secondarily plays a role in improving durability, and the effect can be obtained in the above content range.

또 다른 양태로서, 본 발명에 따른 고등급 구스 아스팔트 조성물은 조성물의 내부에 폴리머 필름을 형성하여, 휨, 인장 및 부착강도를 증진시킬 뿐만 아니라 폴리머 필름막으로 인하여 내구성을 개선하기 위하여 천연 아스팔트 혼합물 100중량부를 기준으로 1 내지 5중량부의 스티렌-부타디엔 수지를 더 포함할 수 있는데, 사용량이 1중량부 보다 적을 경우에는 효과가 미미하며, 5중량부를 초과할 경우 과다하여 경제성이 떨어질 수 있다.
In another embodiment, the high grade goeth asphalt composition according to the present invention is formed by forming a polymer film inside a composition to improve warpage, tensile and adhesion strength, and to improve durability due to a polymer film, If the amount is less than 1 part by weight, the effect is insignificant. If the amount is more than 5 parts by weight, the economical efficiency may be lowered.

이와 같은 구성을 갖는 본 발명에 따른 고등급 구스 아스팔트 조성물의 시공방법을 설명하면 다음과 같다.The construction method of the high grade goeth asphalt composition according to the present invention having such a structure will be described as follows.

여기서, 상기 고등급 구스 아스팔트 조성물의 시공방법은 특별히 한정되지 않지만, 바람직하게는 포장 대상표면의 이물질을 제거한 후 청소하는 이물질 제거-청소단계;Here, the method of applying the high-grade goeth asphalt composition is not particularly limited, but preferably includes a foreign matter removal-cleaning step of removing foreign substances on the surface to be packaged and cleaning the foreign matter;

천연 아스팔트 혼합물 100중량부 기준으로, 스티렌이소프렌스티렌 5 내지 50중량부, 스티렌부타디엔스티렌 5 내지 50중량부, 비닐에스테르 수지, 폴리에스테르 수지, 아크릴 수지, 에폭시 수지, 아크릴-에폭시 수지, 우레탄 수지 또는 이들로부터 선택된 적어도 하나 이상인 고분자 수지 10 내지 30중량부, 골재 10 내지 1,000중량부, 감온성 보강제 1 내지 20중량부, 충진제 10 내지 60중량부, 나노세라믹 입자 10 내지 40중량부, 계면활성제 1 내지 15중량부, 산화방지제 0.1 내지 5중량부, 안정제 0.5 내지 5중량부, 성능개선제 0.5 내지 10중량부, 파이버 2 내지 20중량부, 점착성 수지 10 내지 50중량부, 흐름 방지제 2 내지 10중량부, 및 상용화제 1 내지 5중량부를 포함하는 고등급 구스 아스팔트 조성물을 170 내지 250℃의 온도범위에서 기계식 혼합장치로 강제혼합시키는 강제혼합단계;Based on 100 parts by weight of a natural asphalt mixture, 5 to 50 parts by weight of styrene isoprene styrene, 5 to 50 parts by weight of styrene butadiene styrene, a vinyl ester resin, a polyester resin, an acrylic resin, an epoxy resin, an acryl- 10 to 30 parts by weight of a polymeric resin selected from the group consisting of an inorganic filler, an inorganic filler and an inorganic filler, 10 to 1,000 parts by weight of an aggregate, 1 to 20 parts by weight of a thermosensitive reinforcing agent, 10 to 60 parts by weight of a filler, 10 to 40 parts by weight of a nanoceramic graft, 0.1 to 5 parts by weight of an antioxidant, 0.5 to 5 parts by weight of a stabilizer, 0.5 to 10 parts by weight of a performance improver, 2 to 20 parts by weight of a fiber, 10 to 50 parts by weight of a viscous resin, 2 to 10 parts by weight of an anti- A high grade goeth asphalt composition comprising 1 to 5 parts by weight of a steel which is forced into a mechanical mixing apparatus at a temperature range of 170 to 250 DEG C Mixing step;

상기 이물질 제거-청소단계가 종료된 표면에 성가 강제혼합된 고등급 구스 아스팔트 조성물을 타설하는 타설단계; 및 A pouring step of pouring a high-grade goose asphalt composition which has been subjected to hot-forging mixing on a surface of which the foreign matter removal-cleaning step has been completed; And

상기 타설단계가 종료된 후 고등급 구스 아스팔트 조성물을 양생하는 양생단계를 포함한다.And a curing step of curing the high grade goeth asphalt composition after the pouring step is completed.

이하에서 실시예를 통하여 본 발명을 구체적으로 설명하기로 한다. 그러나 하기의 실시예는 오로지 본 발명을 구체적으로 설명하기 위한 것으로 이들 실시예에 의해 본 발명의 범위를 한정하는 것은 아니다.
Hereinafter, the present invention will be described in detail by way of examples. However, the following examples are for illustrative purposes only and are not intended to limit the scope of the present invention.

[실시예 1][Example 1]

침입도 30의 스트레이트 아스팔트 97g 및 트리니다드레이크 아스팔트로 이루어진 천연 아스팔트 3g의 혼합물로 이루어진 아스팔트 혼합물 100g, 스티렌이소프렌스티렌 25g, 스티렌부타디엔스티렌 25g, 아크릴 수지 15g, 굵은 골재 300g, 인화점이 약 180℃ 이상이고, 감압가스유의 수첨개질 공정의 공정부산물 중 탄화수소 함량이 80% 이상인 포화탄화수소를 포함하는 감온성 보강제 10g, 포틀랜드 시멘트 40g, 경균입경이 400nm인 실리콘카바이드 20g, 술폰 에스테르 8g, 2.6-디-t-부틸-4-메틸페놀 2g, 무황변 폴리 우레아수지 3, 비닐아세테이트 모노머-파라핀오일 4.75g과 과산화벤조일 0.25g의 혼합물로 이루어진 성능개선제 5g, 천연 셀룰로오즈 섬유 10g, 쿠마론-인덴 수지 20g, 아마이드왁스 5g, 폴리인산 2.5g을 혼합하여 고등급 구스 아스팔트 조성물을 제조하였다.
100 g of an asphalt mixture consisting of 97 g of straight asphalt with an intrusion degree of 30 and 3 g of natural asphalt consisting of trinidad lake asphalt, 25 g of styrene isoprene styrene, 25 g of styrene butadiene styrene, 15 g of acrylic resin, 300 g of coarse aggregate, 10 g of a thermosensitive reinforcing agent containing saturated hydrocarbons having a hydrocarbon content of 80% or more in the by-product of the hydrocracking process of the reduced pressure gas oil, 40 g of Portland cement, 20 g of silicon carbide having a mushroom particle diameter of 400 nm, 8 g of a sulfone ester, 5 g of a performance improver consisting of 2 g of 4-methylphenol, 3 g of non-yellowing polyurea resin 3, 4.75 g of vinyl acetate monomer-paraffin oil and 0.25 g of benzoyl peroxide, 10 g of natural cellulose fibers, 20 g of coumarone- And 2.5 g of polyphosphoric acid were mixed to prepare a high grade goeth asphalt composition.

[실시예 2][Example 2]

실시예 1과 동일한 방법으로 실시하되, 에틸렌-글라시딜메타크릴레이트 코폴리머 20g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated except that 20 g of ethylene-glycidyl methacrylate copolymer was added.

[실시예 3][Example 3]

실시예 1과 동일한 방법으로 실시하되, 4.4-디페닐메탄 디이소시아네이트 15g을 더 부가하여 사용하여 실시하였다.
The procedure of Example 1 was repeated except that 15 g of 4.4-diphenylmethane diisocyanate was further added.

[실시예 4][Example 4]

실시예 3과 동일한 방법으로 실시하되, 불포화 폴리에스터 수지 2g을 더 부가하여 실시하였다.
The procedure of Example 3 was repeated, except that 2 g of the unsaturated polyester resin was further added.

[실시예 5][Example 5]

실시예 1과 동일한 방법으로 실시하되, 하이드록시 에틸 아크릴로일 포스페이트 12g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated except that 12 g of hydroxyethyl acryloyl phosphate was further added.

[실시예 6][Example 6]

실시예 1과 동일한 방법으로 실시하되, 가교된 폴리아크릴레이트 염 35g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated except that 35 g of crosslinked polyacrylate salt was further added.

[실시예 7][Example 7]

실시예 1과 동일한 방법으로 실시하되, 액상형으로 비중이 1.0 이상이고 60℃ 점도가 110 cPs인 폴리인산계 박리방지제 15g을 더 부가하여 실시하였다.
15 g of a polyphosphoric acid-based anti-peeling agent having a specific gravity of 1.0 or more and a viscosity of 60 c of 110 cPs was further added in the same manner as in Example 1.

[실시예 8][Example 8]

실시예 1과 동일한 방법으로 실시하되, 폴리에틸렌 왁스 3g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 3 g of polyethylene wax was further added.

[실시예 9][Example 9]

실시예 1과 동일한 방법으로 실시하되, 폐 아스팔트 100g를 더 부가하여 실시하였다.
The same procedure as in Example 1 was carried out except that 100 g of waste asphalt was further added.

[실시예 10][Example 10]

실시예 1과 동일한 방법으로 실시하되, 니트릴고무 20g을 더 부가하여 실시하였다.
The same procedure as in Example 1 was carried out except that 20 g of nitrile rubber was further added.

[실시예 11][Example 11]

실시예 1과 동일한 방법으로 실시하되, 유변성 알키드 수지 10g을 더 부가하여 실시하였다.
Was carried out in the same manner as in Example 1 except that 10 g of a rubidic alkyd resin was further added.

[실시예 12][Example 12]

실시예 1과 동일한 방법으로 실시하되, 소듐 벤조 에이트 0.5g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 0.5 g of sodium benzoate was further added.

[실시예 13][Example 13]

실시예 1과 동일한 방법으로 실시하되, 다이머산 1g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 1 g of dimeric acid was further added.

[실시예 14][Example 14]

실시예 1과 동일한 방법으로 실시하되, 테트라에틸렌펜타민 5g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 5 g of tetraethylene pentamine was further added.

[실시예 15][Example 15]

실시예 1과 동일한 방법으로 실시하되, 벤토나이트 3g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 3 g of bentonite was further added.

[실시예 16][Example 16]

실시예 1과 동일한 방법으로 실시하되, 알루민산 칼슘 2g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 2 g of calcium aluminate was further added.

[실시예 17][Example 17]

실시예 1과 동일한 방법으로 실시하되, 플루오린화나트륨 3g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated, except that 3 g of sodium fluoride was further added.

[실시예 18][Example 18]

실시예 1과 동일한 방법으로 실시하되, 스티렌-부타디엔 수지 3g을 더 부가하여 실시하였다.
The procedure of Example 1 was repeated except that 3 g of styrene-butadiene resin was further added.

[실 험][Experiment]

실시예들에 따라 제조된 조성물을 이용하여 약 60mm 두께의 아스팔트층을 제조한 후 공극률, 부착성, 동적안정도, 간접인장강도, 변형강도, 압축강도 등을 측정하여 표 1로 나타냈다. Table 1 shows the porosity, adhesion, dynamic stability, indirect tensile strength, deformation strength, compressive strength and the like of the asphalt layer having a thickness of about 60 mm using the composition prepared according to the examples.

여기서, 동적안정도는 소성변형 저항성 평가로 Kim Test에 의한 변형강도 시험과 시험을 통해 측정하고, 간접인강도는 균열 저항성을 평가하기 위해 진행되었고, 압축강도는 아스팔트 압축강도시험기를 이용하여 측정하였다.
Here, the dynamic stability was measured by the deformation strength test and the test by Kim Test in the evaluation of the plastic deformation resistance, and the indirect tensile strength was measured in order to evaluate the crack resistance. The compressive strength was measured by using the asphalt compressive strength tester.

공극률Porosity 부착성Attachment 동적안정도
(pass/mm)
Dynamic stability
(pass / mm)
간접인장강도
(ITS)
Indirect tensile strength
(ITS)
변형강도
(Mpa)
Deformation strength
(Mpa)
압축강도(MPa)Compressive strength (MPa)
3일간3 days 7일간7 days 28일간28 days 실시예 1Example 1 0.5%0.5% 좋음good 13341334 0.860.86 5.645.64 22.322.3 25.725.7 7878 실시예 2Example 2 0.7%0.7% 좋음good 12631263 0.880.88 5.735.73 23.123.1 25.825.8 7979 실시예 3Example 3 0.5%0.5% 좋음good 13251325 0.840.84 5.595.59 27.827.8 31.531.5 7676 실시예 4Example 4 0.6%0.6% 좋음good 15551555 0.960.96 5.585.58 27.127.1 30.930.9 8080 실시예 5Example 5 0.7%0.7% 좋음good 14791479 0.850.85 6.026.02 28.228.2 31.231.2 7878 실시예 6Example 6 0.6%0.6% 좋음good 13851385 0.880.88 6.316.31 28.928.9 31.431.4 8181 실시예 7Example 7 0.4%0.4% 좋음good 12451245 0.850.85 5.875.87 28.128.1 31.631.6 8484 실시예 8Example 8 0.4%0.4% 좋음good 16321632 0.880.88 6.036.03 29.529.5 31.831.8 7979 실시예 9Example 9 0.6%0.6% 좋음good 15491549 0.860.86 5.985.98 23.323.3 24.924.9 7777 실시예 10Example 10 0.7%0.7% 좋음good 11481148 0.890.89 5.975.97 22.722.7 25.725.7 7878 실시예 11Example 11 0.6%0.6% 좋음good 13751375 0.870.87 5.675.67 29.329.3 31.131.1 8181 실시예 12Example 12 0.6%0.6% 좋음good 15531553 0.860.86 5.695.69 28.228.2 31.331.3 7777 실시예 13Example 13 0.7%0.7% 좋음good 17841784 0.860.86 5.605.60 23.123.1 27.227.2 7878 실시예 14Example 14 0.7%0.7% 좋음good 16391639 0.870.87 5.875.87 21.521.5 27.827.8 7979 실시예 15Example 15 0.3%0.3% 좋음good 17821782 0.880.88 5.645.64 28.328.3 32.132.1 7979 실시예 16Example 16 0.4%0.4% 좋음good 14341434 0.890.89 5.945.94 28.228.2 31.331.3 7979 실시예 17Example 17 0.5%0.5% 좋음good 13841384 0.870.87 5.815.81 24.824.8 29.929.9 8080 실시예 18Example 18 0.4%0.4% 좋음good 14591459 0.900.90 5.905.90 21.521.5 28.4528.45 7979

표 1에 나타낸 바와 같이, 고등급 구스 아스팔트 조성물을 사용한 실시예 1 내지 실시예 18의 공극률, 부착성, 동적안정도, 간접인장강도 및 변형강도가 좋고, 압축강도는 28일이 경과한 시점에서 75메가파스칼 이상으로서, 상시 실시예의 모든 콘크리트 조성물이 고강도인 것을 확인할 수 있었다.
As shown in Table 1, the porosity, adhesion, dynamic stability, indirect tensile strength and deformation strength of Examples 1 to 18 using the high grade goeth asphalt composition were good and the compressive strength was 75 It was confirmed that all of the concrete compositions of the present invention had higher strength than the megapascals.

이상에서 설명한 바와 같이, 본 발명이 속하는 기술 분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예는 모두 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위의 의미 및 범위 그리고 그 등가개념으로부터 도출되는 모두 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.As described above, those skilled in the art will understand that the present invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. It is therefore to be understood that the embodiments described above are all illustrative and not restrictive. The scope of the present invention should be construed as being included in the scope of the present invention without departing from the spirit and scope of the present invention as defined by the appended claims and their equivalents.

Claims (5)

천연 아스팔트 혼합물 100중량부 기준으로,
스티렌이소프렌스티렌 5 내지 50중량부;
스티렌부타디엔스티렌 5 내지 50중량부;
비닐에스테르 수지, 폴리에스테르 수지, 아크릴 수지, 에폭시 수지, 아크릴-에폭시 수지, 우레탄 수지 또는 이들로부터 선택된 적어도 하나 이상인 고분자 수지 10 내지 30중량부;
골재 10 내지 1,000중량부;
감온성 보강제 1 내지 20중량부;
충진제 10 내지 60중량부;
나노세라믹 입자 10 내지 40중량부;
계면활성제 1 내지 15중량부;
산화방지제 0.1 내지 5중량부;
안정제 0.5 내지 5중량부;
성능개선제 0.5 내지 10중량부;
파이버 2 내지 20중량부;
점착성 수지 10 내지 50중량부;
흐름 방지제 2 내지 10중량부; 및
상용화제 1 내지 5중량부를 포함하는 고등급 구스 아스팔트 조성물에,
글리시딜 메타크릴레이트(GMA)계 수지를 천연 아스팔트 혼합물 100중량부를 기준으로 5 내지 30중량부로 더 포함하고,
벤토나이트를 천연 아스팔트 혼합물 100중량부를 기준으로 0.1 내지 5중량부로 더 포함하며,
알루민산 칼슘을 천연 아스팔트 혼합물 100중량부를 기준으로 1 내지 5중량부로 더 포함하고,
플루오린화나트륨을 천연 아스팔트 혼합물 100중량부를 기준으로 1 내지 5중량부로 더 포함하는 고등급 구스 아스팔트 조성물.
On the basis of 100 parts by weight of the natural asphalt mixture,
5 to 50 parts by weight of styrene isoprene styrene;
5 to 50 parts by weight of styrene butadiene styrene;
10 to 30 parts by weight of a polymer resin having at least one or more selected from a vinyl ester resin, a polyester resin, an acrylic resin, an epoxy resin, an acryl-epoxy resin, a urethane resin or the like;
10 to 1,000 parts by weight of aggregate;
1 to 20 parts by weight of a thermosetting reinforcing agent;
10 to 60 parts by weight of a filler;
10 to 40 parts by weight of nano-ceramic particles;
1 to 15 parts by weight of a surfactant;
0.1 to 5 parts by weight of an antioxidant;
0.5 to 5 parts by weight of a stabilizer;
0.5 to 10 parts by weight of a performance improving agent;
2 to 20 parts by weight of fibers;
10 to 50 parts by weight of a tacky resin;
2 to 10 parts by weight of an anti-flow agent; And
And 1 to 5 parts by weight of a compatibilizing agent is added to the high grade goeth asphalt composition,
Further comprising 5 to 30 parts by weight of glycidyl methacrylate (GMA) based resin based on 100 parts by weight of the natural asphalt mixture,
Further comprising 0.1 to 5 parts by weight of bentonite based on 100 parts by weight of the natural asphalt mixture,
Further comprising 1 to 5 parts by weight of calcium aluminate based on 100 parts by weight of the natural asphalt mixture,
Wherein the sodium fluoride further comprises 1 to 5 parts by weight based on 100 parts by weight of the natural asphalt mixture.
삭제delete 삭제delete 삭제delete 포장 대상표면의 이물질을 제거한 후 청소하는 이물질 제거-청소단계;
천연 아스팔트 혼합물 100중량부 기준으로, 스티렌이소프렌스티렌 5 내지 50중량부, 스티렌부타디엔스티렌 5 내지 50중량부, 비닐에스테르 수지, 폴리에스테르 수지, 아크릴 수지, 에폭시 수지, 아크릴-에폭시 수지, 우레탄 수지 또는 이들로부터 선택된 적어도 하나 이상인 고분자 수지 10 내지 30중량부, 골재 10 내지 1,000중량부, 감온성 보강제 1 내지 20중량부, 충진제 10 내지 60중량부, 나노세라믹 입자 10 내지 40중량부, 계면활성제 1 내지 15중량부, 산화방지제 0.1 내지 5중량부, 안정제 0.5 내지 5중량부, 성능개선제 0.5 내지 10중량부, 파이버 2 내지 20중량부, 점착성 수지 10 내지 50중량부, 흐름 방지제 2 내지 10중량부, 및 상용화제 1 내지 5중량부를 포함하는 고등급 구스 아스팔트 조성물에, 글리시딜 메타크릴레이트(GMA)계 수지를 천연 아스팔트 혼합물 100중량부를 기준으로 5 내지 30중량부로 더 포함하고, 벤토나이트를 천연 아스팔트 혼합물 100중량부를 기준으로 0.1 내지 5중량부로 더 포함하며, 알루민산 칼슘을 천연 아스팔트 혼합물 100중량부를 기준으로 1 내지 5중량부로 더 포함하고, 플루오린화나트륨을 천연 아스팔트 혼합물 100중량부를 기준으로 1 내지 5중량부로 더 포함하는 고등급 구스 아스팔트 조성물을 170 내지 250℃의 온도범위에서 기계식 혼합장치로 강제혼합시키는 강제혼합단계;
상기 이물질 제거-청소단계가 종료된 표면에 성가 강제혼합된 고등급 구스 아스팔트 조성물을 타설하는 타설단계; 및
상기 타설단계가 종료된 후 고등급 구스 아스팔트 조성물을 양생하는 양생단계를 포함하는 고등급 구스 아스팔트 조성물의 시공방법.
Removing the foreign object on the surface of the package to be cleaned and then cleaning the object;
Based on 100 parts by weight of a natural asphalt mixture, 5 to 50 parts by weight of styrene isoprene styrene, 5 to 50 parts by weight of styrene butadiene styrene, a vinyl ester resin, a polyester resin, an acrylic resin, an epoxy resin, an acryl- 10 to 30 parts by weight of a polymeric resin selected from the group consisting of an inorganic filler, an inorganic filler and an inorganic filler, 10 to 1,000 parts by weight of an aggregate, 1 to 20 parts by weight of a thermosensitive reinforcing agent, 10 to 60 parts by weight of a filler, 10 to 40 parts by weight of a nanoceramic graft, 0.1 to 5 parts by weight of an antioxidant, 0.5 to 5 parts by weight of a stabilizer, 0.5 to 10 parts by weight of a performance improver, 2 to 20 parts by weight of a fiber, 10 to 50 parts by weight of a viscous resin, 2 to 10 parts by weight of an anti- 1 to 5 parts by weight of a glycidyl methacrylate (GMA) based resin was added to a high grade goeth asphalt composition containing 100 parts by weight of a natural asphalt mixture And 5 to 30 parts by weight based on 100 parts by weight of the natural asphalt mixture, and 1 to 5 parts by weight of calcium aluminate based on 100 parts by weight of the natural asphalt mixture A forced mixing step in which a high grade goeth asphalt composition further comprising 1 to 5 parts by weight of sodium fluoride based on 100 parts by weight of a natural asphalt mixture is forcedly mixed in a mechanical mixing device at a temperature range of 170 to 250 캜;
A pouring step of pouring a high-grade goose asphalt composition which has been subjected to hot-forging mixing on a surface of which the foreign matter removal-cleaning step has been completed; And
And a curing step of curing the high grade goeth asphalt composition after the pouring step is completed.
KR1020160131419A 2016-10-11 2016-10-11 High Grade Guss Asphalt Composition and Constructing Methods Using Thereof KR101712921B1 (en)