KR101680575B1 - Silver and Jade is the manufacturing method using the antibacterial impact sewers - Google Patents

Silver and Jade is the manufacturing method using the antibacterial impact sewers Download PDF

Info

Publication number
KR101680575B1
KR101680575B1 KR1020160035326A KR20160035326A KR101680575B1 KR 101680575 B1 KR101680575 B1 KR 101680575B1 KR 1020160035326 A KR1020160035326 A KR 1020160035326A KR 20160035326 A KR20160035326 A KR 20160035326A KR 101680575 B1 KR101680575 B1 KR 101680575B1
Authority
KR
South Korea
Prior art keywords
silver
jade
weight
parts
drain pipe
Prior art date
Application number
KR1020160035326A
Other languages
Korean (ko)
Inventor
고용배
Original Assignee
(주) 엠에스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주) 엠에스 filed Critical (주) 엠에스
Priority to KR1020160035326A priority Critical patent/KR101680575B1/en
Application granted granted Critical
Publication of KR101680575B1 publication Critical patent/KR101680575B1/en

Abstract

The present invention relates to a method of manufacturing an antibacterial and impact-resistant drain pipe by using silver and jade. More specifically, the present invention relates to a method of manufacturing an antibacterial and impact-resistant drain pipe by using silver and jade, wherein the drain pipe can provide the same benefits as antibiotics since a composition of the impact-resistant drain pipe is mixed with polyvinyl chloride resin including silver and jade such that effects of the far-infrared radiation, capability of inhibiting bacterial propagation, and sterilization and antibacterial properties can be achieved by using environment improvement materials such as silver and jade inside the drain pipe. Accordingly, the method of manufacturing an antibacterial and impact-resistant drain pipe by using silver and jade comprises: a silver preparation step; a jade preparation step; a manufacturing step of the chip by using silver and jade in which silver powder prepared in the silver preparation step and jade powder prepared in the jade preparation step are mixed with polyvinyl chloride (PVC) resin having a polymerization degree of 800 to 1,200, heated at a temperature of 180 to 230C in an extruder, and manufactured into the chip; and a drain pipe extrusion step in which the chip manufactured in the manufacturing step of the chip is stirred with a PVC resin composition for drain pipe in a mixer and then inputted back to the extruder, molds for manufacturing the drain pipe are connected, and the PVC resin composition for drain pipe are melted at a temperature of 180 to 230C and extruded into the drain pipe, wherein the PVC resin composition for drain pipe comprises 3.5 to 5 parts by weight of a composite stabilizer, 5 to 12 parts by weight of hard calcium carbonate, and 0.2 to 3 parts by weight of a lubricant with respect to 100 parts by weight of PVC resin.

Description

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an antibacterial impact sewer,

The present invention relates to a method for manufacturing an impact resistant sewage pipe using silver and jade, and more particularly, to a method for manufacturing an impact resistant sewage pipe by mixing silver and vinyl chloride resin, The present invention relates to a method for producing an antibacterial impact resistant sewage pipe using silver and jade, which is capable of providing a benefit of use as an antibiotic material by utilizing the far-infrared radiation efficiency of jade, the inhibition of bacterial propagation, and the sterilization and antibacterial ability.

Generally, a sewer pipe supplying drinking water uses a metal pipe such as a cast iron pipe or an oil pipe. Such a metal pipe is used for a long period of time, and the inner wall of the pipe is corroded by the rust generated in the inner wall of the pipe. But also the workability of the metal pipe is poor due to the heavy weight at the time of installation and transportation.

The above problems can be solved by replacing olefinic high density polyethylene (HDPE) and polyvinyl chloride (PVC) resin, which improves the impact resistance of the synthetic resin sewage pipe which is weaker in strength than the metal pipe, In case of sewage shed at low speed or long stay, harmful microorganisms such as Escherichia coli may produce odor, which may cause unpleasant odors. In severe cases, it may cause diarrhea, enteritis and food poisoning. Therefore, when sewage pipe made of synthetic resin, Have been developed.

As a technique for imparting antimicrobial properties to a synthetic resin, there has been known an antibacterial polyolefin which combines an inorganic antibacterial agent containing polyethylene and zinc as active ingredients, and synthetic resins such as calcium triphosphate, hydroxyapatite, calcium hydrogen phosphate and antimicrobial compounds Is known.

On the other hand, far-infrared energy emitting materials are various. There are various products such as jade, oak charcoal, and elvan. Tourmaline was used in diluted water, and it was about to be made with adhesive-free mixed sheet. However, the far infrared ray energy emissivity of these products was about 40 to 100. The highest purity jade tested was about 100.

First, jade has various supernatural and mysterious effects as recorded in Oriental medicine's Dongbok-gog and Bon-gok gangmok. Among these efficacies, far-infrared radiation function, antibacterial activity Function, the function of removing impurities from the object (removal of heavy metals), and the function of changing hard water to soft water.

Jade is divided into nephrite and jadeite. Mineralogically, jadeite is an optical material of monoclinic whitish stone of inosilicate. The quality of nephrite is the structure of its fine structure, It is composed of silica, calcium, iron, magnesium, etc. (SiO 2 , MgO, Fe 2 O, CaO, Na 2 O, H 2 O) as main components. These ingredients are necessary for the growth of plants and animals, antibacterial, fungicidal, deodorizing effect, such as water purification functions that cause far-infrared rays

Is known to radiate a large amount of radiation.

Secondly, it is found that far infrared ray radiator far infrared ray emits far infrared rays when containing specific elements among natural minerals, and radiation energy is emitted as the content and purity of the specific elements are higher. These characteristics

Far-infrared radiation (chemical composition SiO 2 , Al 2 O 3 ) synthesis materials, which are porous crystals with about two times higher radiation intensity than natural minerals, have been developed. By adding the far infrared ray radiation synthesizing material to the epoxy coating composition, it is possible to maximize the function of the jade and to exert an excellent effect on the adsorption action of the pollution substance which is the main cause of the water pollution due to the porous property.

Third, the synthetic non-toxic inorganic antibacterial agent (SiO 2, Al2O 3, Zn, Ag) zeolite carrier: antimicrobial metal (Zn, Ag) to the (chemical composition Me2 / n, O, Al2O 3 , xSiO 2, yH 2 O) , Which is a non-toxic antimicrobial agent, is added to the main composition of epoxy coatings to exhibit strong growth inhibition and killing ability through contact with various microorganisms. Also, unlike organic antimicrobial agents, it is stable at high temperatures and has no volatility or leaching. .

Literature 1. Patent Registration No. 0969655 (registered on Jul. 05, 2010) Document 2. Patent Registration No. 0890796 (registered on Mar. 20, 2009) Document 3. Patent Registration No. 0384929 (registered on May 05, 2003) Document 4. Patent Publication No. 1995-0032428 (registered on December 20, 1995)

Accordingly, it is an object of the present invention to provide a jade powder and a silver powder having the above-described effects, which are mixed with a polyvinyl chloride (PVC) resin, The present invention aims to maximize the effective effect, the far-infrared radiation effect, the antibacterial function, the deodorizing function, the water purification function, and the beneficial effect on the human body by melt-feeding and extrusion molding into a cylindrical sewage pipe.

The present invention relates to a method for preparing silver;
The junkie stage of jade;
The silver powder prepared in the silver preparation step and the silver powder prepared in the jade preparation step are mixed with a polyvinyl chloride (PVC) resin having a polymerization degree of 800 to 1,200, heated in an extruder at 180 to 230 ° C, A step of manufacturing a chip using jade;
The housing prepared in the step of manufacturing the chips was mixed with 100 parts by weight of a polyvinyl chloride (PVC) resin,
3.5 to 5 parts by weight of a composite stabilizer, 5 to 12 parts by weight of hard calcium carbonate and 0.2 to 3 parts by weight of a lubricant were stirred with a mixer and then re-introduced into an extruder to connect a mold for sewage pipe production, A sewage pipe extrusion step of melting the polyvinyl chloride resin composition for sewage drainage at 180 to 230 캜 and extruding the sewage pipe by extrusion; .

delete

delete

delete

The present invention relates to a method for preparing silver;
The junkie stage of jade;
The silver powder prepared in the silver preparation step and the silver powder prepared in the jade preparation step are mixed with a polyvinyl chloride (PVC) resin having a polymerization degree of 800 to 1,200, heated in an extruder at 180 to 230 ° C, A step of manufacturing a chip using jade;
The housing prepared in the step of manufacturing the chips was mixed with 100 parts by weight of a polyvinyl chloride (PVC) resin,
3.5 to 5 parts by weight of a composite stabilizer, 5 to 12 parts by weight of hard calcium carbonate and 0.2 to 3 parts by weight of a lubricant were stirred with a mixer and then re-introduced into an extruder to connect a mold for sewage pipe production, A sewage pipe extrusion step of melting the polyvinyl chloride resin composition for sewage drainage at 180 to 230 캜 and extruding the sewage pipe by extrusion;
Cooling the sewer pipe extruded in the extruding step, moving to a head forming mold, heating the head forming mold to 50 to 120 캜 to form a pipe expanding part at one end of the sewage pipe, and forming a packing groove in the expanding pipe part; .

delete

delete

delete

delete

The present invention relates to a method for manufacturing a honeycomb structure by mixing powder of silver powder of 700 to 1,200 mash with a polyvinyl chloride (PVC) resin having a powder purity of 200 to 600 mash and a powder purity of 95 to 99% and a moisture content of 0.03 to 0.5% And then extruded from an extruder and extruded into a cylindrical sewer pipe to simultaneously exhibit an antibacterial function, a deodorizing function and a water purifying function for killing bacteria caused by far-infrared radiation, and exhibiting a beneficial effect on the human body Effect.

1 is a sectional view of a sewage pipe according to the present invention,
2 is a partial enlarged cross-sectional view of the sewage pipe of the present invention
FIG. 3 is an enlarged cross-sectional view of a sewage pipe according to the present invention,
4 is a block diagram for explaining the sewage pipe coating method of the present invention

Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

FIG. 1 is a cross-sectional view of a sewage pipe according to the present invention in an extruded state, FIG. 2 is a partially enlarged sectional view of a sewer pipe according to the present invention, and FIG. 3 is an enlarged cross- will be.

Based on 100 parts by weight of a polyvinyl chloride (PVC) resin having a degree of polymerization of 800 to 1,200,

0.05 to 100 parts by weight of silver powder and 5 to 15 parts by weight of jade powder are mixed with a mixer, heated to 180 to 230 캜, molded into chips in an extruder,

A polyvinyl chloride resin composition for sewerage piping comprising 3.5 to 5 parts by weight of a complex stabilizer, 5 to 12 parts by weight of hard calcium carbonate and 0.2 to 3 parts by weight of a lubricant was added to 100 parts by weight of the chip and a polyvinyl chloride (PVC) After the stirrer, a mold for sewage pipe production is connected, the polyvinyl chloride resin composition for sewage pipe is melted at 180 to 230 캜, and the sewage pipe 10 made of the tube body 11 is formed by extrusion,

A pipe portion 20 is formed at one end of the sewage pipe 10 and a packing groove 30 is formed in the pipe portion 20 and the packing 40 is connected to the packing groove 30, (10) so as to maintain watertightness in the watertight container (20).

The silver powder was ground to a size of 300 to 1,200 mesh,

The jade is milled to a size of 200 to 600 mesh and processed to have a purity of 95 to 99% and a moisture content of 0.03 to 0.5%.

The jade has a radiant energy of 0.93 W / m < 2 > at a wavelength of 5 to 20 mu m and a medium-diameter fiber having a hardness of about 5 to about 5.5 using a FT-IR spectrum.

Additives such as heat stabilizers, ultraviolet stabilizers, and processing improvers which are usually added when forming the tubular body 11 can be added as needed, and they are not particularly limited and may be appropriately selected according to those skilled in the art Additives and processing aids can be selected. Therefore, detailed description thereof will be omitted in the present invention.

A manufacturing method according to the present invention comprises: preparing silver (S10);

Preparing a jade (S20);

The silver powder prepared in the preparation step (S10) and the silver powder prepared in the preparation step (S20) are mixed with a polyvinyl chloride (PVC) resin having a polymerization degree of 800 to 1,200 and heated at 180 to 230 캜 in an extruder A step (S30) of manufacturing chips using silver and silver to be manufactured into chips;

The chip produced in the step of manufacturing the chip (S30) is composed of 3.5 to 5 parts by weight of a complex stabilizer, 5 to 12 parts by weight of hard calcium carbonate and 0.2 to 3 parts by weight of a lubricant, based on 100 parts by weight of polyvinyl chloride (PVC) After the polyvinyl chloride resin composition for sewage drainage is stirred with a mixer, the mold for sewage pipe production is connected, the polyvinyl chloride resin composition for sewage drainage is melted at 180 to 230 ° C, and the sewage pipe 10 made of the pipe body 11 is extruded A sewage pipe extrusion step (S40) for extrusion molding;

An expansion step of heating the expansion metal mold to a temperature of 0 to 0 DEG C by extruding and cooling the sewage pipe 10 and then moving to the expansion metal mold and molding the expansion part 20 at one end of the sewage pipe 10 at the expansion metal mold S50); Lt; / RTI >

The silver preparation step S10 for processing the silver is milled to a size of 300 to 1,200 mesh and is composed of 0.05 to 100.5% by weight of the total weight of the polyethylene.

The step (S20) of processing the jade to form jigs to form chips by mixing with the processed silver is carried out in a size of 200 to 600 mesh, and has a purity of 95 to 99% and a moisture content of 0.03 to 0.5% 15 parts by weight.

The oxide is FT-IR radiation with energy of 0.93 W / ㎡ contrast emissivity in 5~20㎛ heukchae using the spectrum, the hardness is from 5 to 5.5, the chemical composition of SiO 2, Fe 2 O 3, CaO, MgO, K 2 O and Na 2 O. When the amount is less than 5 parts by weight, the effect of the present invention is insignificant, and when it is used in an amount of more than 15% by weight, have.

When the silver powder is in the range of 300 to 1,200 mesh and the jade 200 to 600 mesh is composed of a powder having a very small particle size, in particular, when the particle size of jade is small, the amount of the various beneficial ingredients is reduced. The reduction and stirring with the resin can not be performed.

In the manufacturing step S30 and the sewage pipe extrusion step S40, the complex stabilizer is added so that the powdery silver and jade having a higher weight than the polyvinyl chloride (PVC) resin can be easily stirred.

Then, the chip is molded in the step of manufacturing the chip (S30) so that the silver and the jade are uniformly infiltrated. The chip is re-introduced in the sewage pipe extrusion step (S40) and melted and stirred once again, So that the state of silver and jade can be evenly distributed.

The antibacterial sewage pipe using silver and jade according to the present invention can be used for piping used for drinking water since the tubular body 11 of the sewage pipe 10 contains silver and jade.

The antimicrobial sewage pipes using silver and jade complement each other's antibacterial power of silver and jade and provide various beneficial actions through very good antibacterial action and far-infrared radiation.

That is, the silver provides antimicrobial action against yellow staphylococci, E. coli, and pneumococci, and jade exhibits antimicrobial action against fungi and far-infrared ray emissivity.

Here, the sewage pipe 10 containing the silver and the jade is manufactured and tested for the antibacterial activity, which provides the following characteristics.

Sample name: silver nano and ox-containing sewer pipe

Strain used: 1. Staphylococcus aureus ATCC 6538

2. Escherichia coli ATCC 25922

3. Pneumococcus pneumoniae - Klebsiella pneunomiae ATCC 4352

Bacterial reduction rate (%): [(Mb - Mc) / Mb] X 100

Growth rate (F): Mb / Ma (31.6 times or more)

Ma: Number of viable cells immediately after inoculation of control flask (average value of 3 samples)

Mb: Number of viable cells after 18 hours of culture (average value of 3 samples)

Mc: Number of viable cells after 18 hours of culture (average value of 3 samples)

On the other hand, in the test results according to the above test method, the antibacterial activity against all three strains (KS K 0639) was 99.9%.

In addition, the increase in fungal bacteria did not occur in the cultivation of Aspergillus niger ATCC 6275 for 2 weeks in the degree of viscocity (AATCC 30 TM Ⅲ) against the fungus of the nano sewage pipe 10.

As described above, the antibacterial sewage pipe using silver and jade according to the present invention has an excellent antimicrobial action for reducing various kinds of bacteria harmful to human body, and also has an excellent effect on the removal of fungus.

While the present invention has been described in connection with what is presently considered to be practical exemplary embodiments, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the scope of the appended claims.

The present invention relates to a method for improving the radiation efficiency of far-infrared rays of silver and silver, which is environment improving material, from the inner surface of a sewer pipe by mixing polyvinyl chloride resin including silver and jade, It is a very useful invention.

10: sewage pipe 11: pipe body
20: expansion part 30: packing groove
40: Packing

Claims (5)

A silver preparation step S10;
Junk step S20 of the jade;
The silver powder prepared in the preparing step (S10) and the silver powder prepared in the jade preparing step (S20) are mixed with a polyvinyl chloride (PVC) resin having a polymerization degree of 800 to 1,200, heated in an extruder at 180 to 230 캜, A step (S30) of manufacturing chips using silver and silver which are manufactured to be made of silver and silver;
With respect to 100 parts by weight of the chip and the polyvinyl chloride (PVC) resin produced in the step (S30) of manufacturing the chip,
3.5 to 5 parts by weight of a composite stabilizer, 5 to 12 parts by weight of hard calcium carbonate and 0.2 to 3 parts by weight of a lubricant were stirred with a mixer and then re-introduced into an extruder to connect a mold for sewage pipe production, A sewage pipe extrusion step (S40) for melting the polyvinyl chloride resin composition for sewage drainage at 180 to 230 캜 and extruding the sewage pipe (10) by extrusion; Wherein the method comprises the steps of:
A silver preparation step S10;
Junk step S20 of the jade;
The silver powder prepared in the preparing step (S10) and the silver powder prepared in the jade preparing step (S20) are mixed with a polyvinyl chloride (PVC) resin having a polymerization degree of 800 to 1,200, heated in an extruder at 180 to 230 캜, A step (S30) of manufacturing chips using silver and silver which are manufactured to be made of silver and silver;
With respect to 100 parts by weight of the chip and the polyvinyl chloride (PVC) resin produced in the step (S30) of manufacturing the chip,
3.5 to 5 parts by weight of a composite stabilizer, 5 to 12 parts by weight of hard calcium carbonate and 0.2 to 3 parts by weight of a lubricant were stirred with a mixer and then re-introduced into an extruder to connect a mold for sewage pipe production, A sewage pipe extrusion step (S40) for extruding the sewage pipe (10) by extruding the polyvinyl chloride resin composition for sewage drainage at 180 to 230 캜;
After the sewage pipe 10 extruded in the extrusion step is cooled, the mold is moved to a head forming mold, and the head forming mold is heated to 50 to 120 캜 to form an expanding portion 20 at one end of the sewage pipe 10, (S50) of forming a packing groove (30) in the container (20); Wherein the method comprises the steps of:
The method according to claim 1,
Wherein the jade powder in the jade preparation step (S20) is pulverized into a size of 200 to 600 mesh and has a purity of 95 to 99% and a moisture content of 0.03 to 0.5%.
The method according to claim 1,
In the preparation step (S20) of the jade, the jade powder is characterized in that the emissivity of the jade based on the FT-IR spectrum is in the range of 5 to 20 탆 at a radiation energy of 0.93 W / m 2 and a hardness of 5 to 5.5. (METHOD FOR PREPARING ANTIBACTERIAL SHOCK HOSE.
The method according to claim 1,
Wherein the silver powder is milled to a size of 300 to 1,200 mesh in the silver preparation step (S10) so as to provide antimicrobiality by mixing the powder with jade.
KR1020160035326A 2016-03-24 2016-03-24 Silver and Jade is the manufacturing method using the antibacterial impact sewers KR101680575B1 (en)