KR101653564B1 - 초속경 도로보수용 몰탈 조성물 및 그 제조방법 - Google Patents
초속경 도로보수용 몰탈 조성물 및 그 제조방법 Download PDFInfo
- Publication number
- KR101653564B1 KR101653564B1 KR1020130128018A KR20130128018A KR101653564B1 KR 101653564 B1 KR101653564 B1 KR 101653564B1 KR 1020130128018 A KR1020130128018 A KR 1020130128018A KR 20130128018 A KR20130128018 A KR 20130128018A KR 101653564 B1 KR101653564 B1 KR 101653564B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- aggregate
- mortar composition
- mortar
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
본 발명에 따른 초속경 도로보수용 몰탈 조성물은, 인산염 10 내지 20 중량%, 규산칼슘 3 내지 6 중량%, 실리카흄 15 내지 25 중량%, 무기결합재 20 내지 59 중량%, 산화알루미늄 5 내지 10 중량% 및 산화마그네슘 5 내지 10 중량%를 포함한다.
상기한 본 발명에 따른 초속경 도로보수용 몰탈 조성물은 기존의 포틀랜드 시멘트와 같은 석회 성분이 포함되어 있지 않아 친환경적으로 도로를 보수할 수 있고, 겨울철 양생 시간의 지연문제를 해결할 수 있으며, 기존의 포틀랜드 시멘트보다 경화시간을 빠르게 진행되므로 도로의 결손부위를 단시간에 보수할 수 있어 경제적이고 안정성이 우수한 효과가 있다.
Description
시험항목 | 시험결과 | 시험방법 | |
휨강도(N/㎟) |
3시간 | 3.8 | KS F-4042:2007 |
1일 | 8.7 | ||
3일 | 11.4 | ||
7일 | 14.2 | ||
28일 | 15.7 | ||
압축강도(N/㎟) |
3시간 | 11.2 | |
1일 | 33.0 | ||
3일 | 48.7 | ||
7일 | 59.7 | ||
28일 | 69.2 | ||
부착강도(N/㎟) |
표준조건 | 2.1 | |
온냉반복 후 | 1.9 | ||
내알칼리성(N/㎟) | 62.7 | ||
중성화 저항성(mm) | 1.6 | ||
투수량(g) | 5.2 | ||
물흡수계수(kg/㎡·h0 .5) | 0.27 | ||
습기투과저항성(m) | 1.5 | ||
염화이온침투저항성(coulombs) | 812 | ||
길이변화율(%) | -0.11 |
Claims (10)
상기 무기결합재는 플라이 애시 및 골재의 혼합물이고,
상기 골재는 바텀 애시 골재, 제강 슬래그 골재, 동제련 슬래그 골재 및 니켈제련 슬래그 골재 중 하나 또는 2 이상의 골재인 것을 특징으로 하는 초속경 도로보수용 몰탈 조성물.
상기 실리카흄은 밀도가 2.0 내지 2.2g/cm3 이고, 비표면적이 150,000 내지 200,000cm2/g의 분말도를 가지는 것을 특징으로 하는 초속경 도로보수용 몰탈 조성물.
상기 실리카흄은 평균 입경이 0.2 내지 0.5㎛인 것을 특징으로 하는 초속경 도로보수용 몰탈 조성물.
상기 저급 규석은 입자의 크기가 212㎛ 이하(평균 입경이 50㎛)로 30~50 중량%의 범위를 가지며, 212㎛ 이상의 입자가 50~70 중량%의 범위를 가지는 것을 특징으로 하는 초속경 도로보수용 몰탈 조성물.