KR101599750B1 - The manufacturing method of uncirculated a precious metal - Google Patents
The manufacturing method of uncirculated a precious metal Download PDFInfo
- Publication number
- KR101599750B1 KR101599750B1 KR1020150131482A KR20150131482A KR101599750B1 KR 101599750 B1 KR101599750 B1 KR 101599750B1 KR 1020150131482 A KR1020150131482 A KR 1020150131482A KR 20150131482 A KR20150131482 A KR 20150131482A KR 101599750 B1 KR101599750 B1 KR 101599750B1
- Authority
- KR
- South Korea
- Prior art keywords
- noble metal
- unc
- rolling
- grade
- weight
- Prior art date
Abstract
Description
본 발명은 압연기를 사용하여 준비된 주괴를 압연공정에 적용할 때, 각 중량에 맞는 정확한 두께의 귀금속 판재를 생산하기 위해 수십 개의 롤러를 설치하여 프루프(proof)급이나 미사용(UNC: uncirculated)급의 귀금속 제품의 제작시 혼용하여 생산하므로 수십 개 롤러가 필요하거나 보유한 롤러가 충분하지 않을 경우 롤러의 상하 간극을 맞추는데 많은 시간이 소요되고 제조장치의 제작비용도 많이 들었던 종래와는 달리, 미사용(UNC)급 귀금속 제품의 경우는 준비된 주괴를 압연공정에 적용시 한 개 또는 두 개의 롤러만으로도 미사용(UNC)급의 표면수준을 충분히 맞추면서도 생산단가를 낮춤과 더불어 종래보다 훨씬 용이하게 생산해 낼 수 있고, 프루프(proof)급 귀금속 제품의 경우에는 대량생산에 적합한 것인데 비해, 미사용(UNC)급 귀금속 제품의 경우는 바(bar), 코인, 메달, 엽전, 공표(소전) 형태로 하여 다품종으로 소량의 귀금속 제품을 제조하는데 적합하며, 귀금속 제품의 소둔(annealing)공정시 고가의 소둔장치를 사용하지 않고 산소토치의 불로 2 내지 3초간 노출시켜서 소둔장치를 사용하는 것과 유사한 소둔효과를 볼 수 있고, 귀금속 제품의 세정공정시 윤활유 또는 과산화수소수 등과 같은 화학약품을 사용해왔던 종래의 경우 이물질을 제거한 후 기름 및 화학약품을 제거하기 위해 후처리 작업을 해야 하므로 생산단가가 상승하고 또한 기름 및 화학약품으로 인한 환경문제가 발생하는 것과는 달리, 미사용(UNC)급 귀금속 제품의 세정공정시에는 물과 계면활성제를 사용하므로 생산단가를 줄일 수 있음과 더불어 환경문제도 개선할 수 있으며, 미사용(UNC)급 귀금속 제품의 제조방법을 소량 생산되는 프루프(proof)급 귀금속 제품의 제조에도 적용할 수 있는 미사용(UNC)급 귀금속 제품의 제조방법에 관한 기술이다.In the present invention, when an ingot prepared by using a rolling mill is applied to a rolling process, dozens of rollers are installed to produce a noble metal plate of an exact thickness corresponding to each weight, and a proof class or an uncirculated class (UNC (UNC) unlike the prior art which requires a lot of time for aligning the vertical gap of the roller and the manufacture cost of the manufacturing apparatus when dozens of rollers are needed, In the case of high-grade precious metal products, when the prepared ingot is applied to the rolling process, the production cost can be lowered while satisfying the surface level of the unused (UNC) class with only one or two rollers, (proof) grade precious metal products are suitable for mass production, whereas for un-used (UNC) grade precious metal products, It is suitable for manufacturing a small quantity of precious metal products in a wide variety of products, in the form of coin, medal, pre-war, and public announcement. Or 3 seconds, so that the annealing effect similar to that of using the annealing device can be seen. In the conventional case where the cleaning process of the noble metal product uses chemicals such as lubricating oil or hydrogen peroxide, etc., the foreign matter is removed and then the oil and the chemical are removed Unlike the increase in production costs and the environmental problems caused by oil and chemicals due to the need for post-treatment, it is possible to reduce the production cost by using water and a surfactant in the cleaning process of unclassified precious metal products Environmental problems can be improved as well as the ability to manufacture unconventional (UNC) grade precious metal products, (UNC) grade precious metal products that can be applied to the manufacture of proof grade noble metal products.
종래의 경우, 프루프(proof)급 귀금속 제품을 제조할 때, 목적한 중량의 귀금속 판재를 생산하기 위해 압연기를 사용하여 준비된 주괴를 압연공정에 적용하게 된다. 이때 압연기에 수십 개의 롤러를 설치하여 프루프(proof)급이나 미사용(UNC: uncirculated)급의 귀금속 제품의 제작시 혼용하여 생산하였다. 특히, 프루프(proof)급은 최초 압연공정시에 정확한 두께의 판재를 생산해야 하고, 이를 위해서 각 중량에 맞는 수십 개의 롤러가 필요하다. 롤러가 적을 경우에는 롤러의 상하 간극을 맞추는데 많은 시간이 소요되고 제조장치의 제작비용도 많이 드는 문제점이 있다.Conventionally, when producing a proof grade noble metal product, the ingot prepared using a rolling mill is used in the rolling process to produce a noble metal sheet of desired weight. At that time, dozens of rollers were installed in the rolling mill to produce a mixture of proof and uncirculated noble metal products. In particular, the proof grade requires a precise thickness of the sheet material during the initial rolling process, which requires dozens of rollers for each weight. When the number of rollers is small, it takes a long time to align the upper and lower gaps of the rollers, and the manufacturing cost of the manufacturing apparatus is increased.
그리고, 종래의 경우, 귀금속 제품을 제조할 때, 세정공정시 윤활유 또는 과산화수소수 등과 같은 화학약품을 사용해왔는데, 이 경우 귀금속 제품에서 이물질을 제거한 후 기름 및 화학약품을 제거하기 위해 후처리 작업을 해야 한다. 그러므로 생산단가가 상승하고 또한 기름 및 화학약품으로 인한 환경문제가 발생하는 문제점을 갖고 있다.In the past, when manufacturing precious metal products, in the cleaning process, chemicals such as lubricating oil or hydrogen peroxide were used. In this case, after removing foreign matters from the precious metal products, the post-treatment must be performed to remove oil and chemicals do. Therefore, the production cost is increased and environmental problems due to oil and chemicals are generated.
따라서 미사용(UNC)급 귀금속 제품의 경우는 준비된 주괴를 압연공정에 적용시 한 개 또는 두 개의 롤러만으로도 미사용(UNC)급의 표면수준을 충분히 맞추면서도 생산단가를 낮춤과 더불어 종래보다 훨씬 용이하게 생산해 낼 수 있고, 미사용(UNC)급 귀금속 제품의 경우는 바(bar), 코인, 메달, 엽전, 공표(소전) 형태로 하여 다품종으로 소량의 귀금속 제품을 제조하는데 적합하며, 귀금속 제품의 소둔(annealing)공정시 고가의 소둔장치를 사용하지 않고 산소토치의 불로 2 내지 3초간 노출시켜서 소둔장치를 사용하는 것과 유사한 소둔효과를 볼 수 있고, 미사용(UNC)급 귀금속 제품의 세정공정시에는 물과 계면활성제를 사용하므로 생산단가를 줄일 수 있음과 더불어 환경문제도 개선할 수 있는 미사용(UNC)급 귀금속 제품의 제조방법의 개발이 절실히 요구되고 있는 실정이다. Therefore, in the case of unused (UNC) grade precious metal products, when the prepared ingot is applied to the rolling process, one or two rollers can be used to lower the cost of production even though the surface level of unused (UNC) (UNC) grade precious metal products are suitable for manufacturing a small quantity of precious metal products in a variety of products in the form of bar, coin, medal, pre-war, and public announcement (annealing) ) In the process, an annealing effect similar to that of using an annealing device can be seen by exposing the furnace for 2 to 3 seconds without using an expensive annealing device. In the cleaning process of a UNC grade noble metal product, (UNC) grade precious metal product which can reduce the production cost by using the active agent and can also improve the environmental problem, In fact.
이에 본 발명은 상기 문제점들을 해결하기 위하여 착상된 것으로서, 압연기를 사용하여 준비된 주괴를 압연공정에 적용할 때, 각 중량에 맞는 정확한 두께의 귀금속 판재를 생산하기 위해 수십 개의 롤러를 설치하여 프루프(proof)급이나 미사용(UNC: uncirculated)급의 귀금속 제품의 제작시 혼용하여 생산하므로 수십 개 롤러가 필요하거나 보유한 롤러가 충분하지 않을 경우 롤러의 상하 간극을 맞추는데 많은 시간이 소요되고 제조장치의 제작비용도 많이 들었던 종래와는 달리, 미사용(UNC)급 귀금속 제품의 경우는 준비된 주괴를 압연공정에 적용시 한 개 또는 두 개의 롤러만으로도 미사용(UNC)급의 표면수준을 충분히 맞추면서도 생산단가를 낮춤과 더불어 종래보다 훨씬 용이하게 생산해 낼 수 있는 미사용(UNC)급 귀금속 제품의 제조방법을 제공하는 데 그 목적이 있다. Accordingly, when applying an ingot prepared using a rolling mill to a rolling process, dozens of rollers are installed to produce a precious metal plate of an exact thickness corresponding to each weight, ) Or uncirculated (UNC: grade) noble metal products, it takes a long time to adjust the gap between the rollers when the number of rollers is required or the number of rollers is not sufficient. Unlike the conventional method, uncoloured (UNC) grade precious metal products, when applied to the rolling process, can be manufactured with only one or two rollers, while satisfying the surface level of unused (UNC) (UNC) grade precious metal product which can be manufactured much more easily than the conventional ones. There is a purpose.
또한 본 발명의 목적은 프루프(proof)급 귀금속 제품의 경우에는 대량생산에 적합한 것인데 비해, 미사용(UNC)급 귀금속 제품의 경우는 바(bar), 코인, 메달, 엽전, 공표(소전) 형태로 하여 다품종으로 소량의 귀금속 제품을 제조하는데 적합한 미사용(UNC)급 귀금속 제품의 제조방법을 제공하는 데 있다.In addition, while the object of the present invention is to mass-produce a proof grade noble metal product, the case of a UNC grade noble metal product is in the form of bar, coin, medal, (UNC) grade precious metal products suitable for producing small quantities of noble metal products in a wide variety of products.
또한 본 발명의 목적은 귀금속 제품의 소둔(annealing)공정시 고가의 소둔장치를 사용하지 않고 산소토치의 불로 2 내지 3초간 노출시켜서 소둔장치를 사용하는 것과 유사한 소둔효과를 볼 수 있는 미사용(UNC)급 귀금속 제품의 제조방법을 제공하는 데 있다.It is also an object of the present invention to provide a method of annealing a noble metal product by using an unshown (UNC) annealing method similar to that of using an annealing device by exposing an oxygen torch for 2 to 3 seconds without using an expensive annealing device, And to provide a method for manufacturing a precious metal product.
또한 본 발명의 목적은 귀금속 제품의 세정공정시 윤활유 또는 과산화수소수 등과 같은 화학약품을 사용해왔던 종래의 경우 이물질을 제거한 후 기름 및 화학약품을 제거하기 위해 후처리 작업을 해야 하므로 생산단가가 상승하고 또한 기름 및 화학약품으로 인한 환경문제가 발생하는 것과는 달리, 미사용(UNC)급 귀금속 제품의 세정공정시에는 물과 계면활성제를 사용하므로 생산단가를 줄일 수 있음과 더불어 환경문제도 개선할 수 있는 미사용(UNC)급 귀금속 제품의 제조방법을 제공하는 데 있다.It is another object of the present invention to provide a method and apparatus for cleaning a noble metal product by using a chemical agent such as a lubricating oil or hydrogen peroxide solution in a conventional cleaning process to remove oil and chemicals, Unlike environmental problems caused by oil and chemicals, water and surfactants are used in the cleaning process of UNC grade noble metal products, which can reduce the production cost, UNC) grade precious metal products.
또한 본 발명의 목적은 미사용(UNC)급 귀금속 제품의 제조방법을 소량 생산되는 프루프(proof)급 귀금속 제품의 제조에도 적용할 수 있는 미사용(UNC)급 귀금속 제품의 제조방법을 제공하는 데 있다.It is another object of the present invention to provide a method for manufacturing a UNC grade noble metal product which can be applied to the production of a proof grade noble metal product which is produced in a small amount.
상기 목적을 달성하기 위한 본 발명의 바람직한 실시예에 따른 미사용(UNC)급 귀금속 제품의 제조방법은 백금, 금, 은 중에서 선택되는 귀금속 주괴(ingot)를 준비하는 단계(a)와; 상기 준비된 귀금속 주괴가 압연기(rolling mill)의 롤러 사이를 통과할 때, 3 내지 10 마력(hp)의 파워(power)로 수차례 압연을 하여 각 중량별로 판재 작업을 하는 압연 단계(b)와; 상기 압연한 후, 타발기를 사용하여 판재에 0.5 내지 1ton으로 전단응력을 발생시켜 소정의 형상 및 치수로 절단하는 타발 단계(c)와; 상기 타발된 목표대상물의 표면에 손상이 가지 않도록 하면서 가장자리의 이바리(burr)를 제거하면서 저울을 사용하여 중량을 목적 중량으로 맞추는 중량 맞춤 단계(d)와; 상기 맞추어진 목표대상물에 산소토치의 불을 2 내지 3초간 가하여 열처리하는 소둔 단계(e)와; 상기 소둔된 목표대상물인 소전을 볼 형태의 쇠가 들어 있는 세척기에 물과 계면활성제를 넣고 세척기를 회전시켜 쇠 볼과 소전을 마찰시켜 세척하는 세정 단계(f); 을 포함함을 특징으로 한다.According to another aspect of the present invention, there is provided a method of manufacturing a noble metal (UNC) grade noble metal product, comprising: (a) preparing a noble metal ingot selected from platinum, gold, and silver; A rolling step (b) of rolling the noble metal ingot several times at a power of 3 to 10 hp when the noble metal ingot passes between rollers of a rolling mill to perform plate work for each weight; (C) a step (c) of forming a shear stress at 0.5 to 1 ton on the plate using a rudder after the rolling, and cutting the plate into a predetermined shape and dimensions; A weight adjusting step (d) of adjusting a weight to a target weight by using a balance while removing burrs of edges while preventing damage to the surface of the punched target object; An annealing step (e) of applying a heat of an oxygen torch to the aligned target object for 2 to 3 seconds and performing a heat treatment; (F) a cleaning step (f) in which water and a surfactant are put into a dish-type washing machine having a spherical shape as a target object to be annealed, and the dish was rotated by rotating the dishwasher; .
또한, 상기 목적을 달성하기 위한 본 발명의 바람직한 실시예에 따른 미사용(UNC)급 귀금속 제품의 제조방법은 백금, 금, 은 중에서 선택되는 귀금속 주괴(ingot)를 준비하는 단계(a)와; 상기 준비된 귀금속 주괴가 압연기(rolling mill)의 롤러 사이를 통과할 때, 3 내지 10 마력(hp)의 파워(power)로 수차례 압연을 하여 각 중량별로 판재 작업을 하는 압연 단계(b)와; 상기 압연한 후, 타발기를 사용하여 판재에 0.5 내지 1ton으로 전단응력을 발생시켜 소정의 형상 및 치수로 절단하는 타발 단계(c)와; 상기 타발된 목표대상물의 표면에 손상이 가지 않도록 하면서 가장자리의 이바리(burr)를 제거하면서 저울을 사용하여 중량을 목적 중량으로 맞추는 중량 맞춤 단계(d)와; 상기 맞추어진 목표대상물에 산소토치의 불을 2 내지 3초간 가하여 열처리하는 소둔 단계(e)와; 상기 소둔된 목표대상물인 소전을 볼 형태의 쇠가 들어 있는 세척기에 물과 계면활성제를 넣고 세척기를 회전시켜 쇠 볼과 소전을 마찰시켜 세척하는 세정 단계(f)와; 상기 세정된 소전에 압연기(press)를 사용하여 150 내지 500ton의 압력을 가하여 금형에 의해 소전의 표면을 성형하는 압사 단계(g); 을 포함함을 특징으로 한다.According to another aspect of the present invention, there is provided a method of manufacturing a noble metal (UNC) grade noble metal product, comprising: (a) preparing a noble metal ingot selected from platinum, gold, and silver; A rolling step (b) of rolling the noble metal ingot several times at a power of 3 to 10 hp when the noble metal ingot passes between rollers of a rolling mill to perform plate work for each weight; (C) a step (c) of forming a shear stress at 0.5 to 1 ton on the plate using a rudder after the rolling, and cutting the plate into a predetermined shape and dimensions; A weight adjusting step (d) of adjusting a weight to a target weight by using a balance while removing burrs of edges while preventing damage to the surface of the punched target object; An annealing step (e) of applying a heat of an oxygen torch to the aligned target object for 2 to 3 seconds and performing a heat treatment; (F) a cleaning step (f) in which water and a surfactant are put in a washing machine containing a metal in the shape of a ball and the rinse wheel is rotated to rub and clean the metal balls with each other; A pressing step (g) of applying a pressure of 150 to 500 ton by using a mill to the cleaned preform to mold the surface of the preform by a mold; .
상기 본 발명에 있어서, 상기 압사 단계(g) 이후에, 상기 목표대상물인 소전을 마무리 손질하는 마무리 작업 단계(g-1); 을 더 포함함을 특징으로 한다.In the present invention, the finishing work step (g-1) finishing the finish as the target object after the pressing step (g); Further comprising:
상기 본 발명에 있어서, 상기 목표대상물은 바(bar), 코인, 메달, 엽전, 공표(소전) 형태로 제품화되는 것을 특징으로 한다.In the present invention, the target object is commercialized in the form of a bar, a coin, a medal, a pre-war, or a public exhibition.
상기 본 발명에 있어서, 상기 단계(d)에서, 상기 이바리(burr)를 제거하는 깎기 도구는 줄(file), 갈기, 연삭기(grinder) 중의 어느 하나인 것을 포함함을 특징으로 한다.
상기 본 발명에 있어서, 상기 단계(g-1)에서, 상기 이바리(burr)를 제거하는 깎기 도구는 줄(file), 갈기, 연삭기(grinder) 중의 어느 하나인 것을 포함함을 특징으로 한다.According to the present invention, in the step (d), the cutting tool for removing the burr may be one of a file, a grinder, and a grinder.
According to the present invention, in the step (g-1), the cutting tool for removing the burr may be any one of a file, a mane, and a grinder.
상기 본 발명에 있어서, 상기 미사용(UNC)급 귀금속 제품의 제조방법은 소량 생산되는 프루프(proof)급 귀금속 제품의 제조에도 적용할 수 있는 것을 포함함을 특징으로 한다.In the present invention, the method of manufacturing a UNC grade noble metal product includes a method of manufacturing a noble metal product, which is produced in a small amount.
본 발명에 따른 미사용(UNC)급 귀금속 제품의 제조방법은 다음과 같은 효과를 나타낸다.The method of manufacturing a UNC grade noble metal product according to the present invention has the following effects.
첫째, 본 발명은 압연기를 사용하여 준비된 주괴를 압연공정에 적용할 때, 각 중량에 맞는 정확한 두께의 귀금속 판재를 생산하기 위해 수십 개의 롤러를 설치하여 프루프(proof)급이나 미사용(UNC: uncirculated)급의 귀금속 제품의 제작시 혼용하여 생산하므로 수십 개 롤러가 필요하거나 보유한 롤러가 충분하지 않을 경우 롤러의 상하 간극을 맞추는데 많은 시간이 소요되고 제조장치의 제작비용도 많이 들었던 종래와는 달리, 미사용(UNC)급 귀금속 제품의 경우는 준비된 주괴를 압연공정에 적용시 한 개 또는 두 개의 롤러만으로도 미사용(UNC)급의 표면수준을 충분히 맞추면서도 생산단가를 낮춤과 더불어 종래보다 훨씬 용이하게 생산해 낼 수 있다. First, when applying an ingot prepared using a rolling mill to a rolling process, dozens of rollers are installed to produce a proof grade or an uncirculated (UNC) shape to produce a noble metal sheet of an exact thickness corresponding to each weight, It is necessary to use several tens of rollers or a roller that is not sufficient, unlike the prior art which requires much time to adjust the gap between the rollers and the production cost of the manufacturing apparatus UNC) grade noble metal products can be manufactured much easier than conventional ones by adjusting the surface level of unused (UNC) grade with only one or two rollers when the prepared ingot is applied to the rolling process, while lowering the production cost .
둘째, 본 발명은 프루프(proof)급 귀금속 제품의 경우에는 대량생산에 적용하는 것에 비해, 미사용(UNC)급 귀금속 제품의 경우는 바(bar), 코인, 메달, 엽전, 공표(소전) 형태로 하여 다품종으로 소량의 귀금속 제품을 제조하는데 적합하다.Second, the present invention is applicable to mass production of proof grade noble metal products, and to bar-type, coin, medal, pre-war, and unpublished forms in the case of unclassified (UNC) Making it suitable for producing small quantities of noble metal products in a variety of products.
셋째, 본 발명은 귀금속 제품의 소둔(annealing)공정시 고가의 소둔장치를 사용하지 않고 산소토치의 불로 2 내지 3초간 노출시켜서 소둔장치를 사용하는 것과 유사한 소둔효과를 볼 수 있다.Third, the present invention can exhibit an annealing effect similar to that of using an annealing device by exposing an oxygen torch for 2 to 3 seconds without using an expensive annealing device during annealing of a noble metal product.
넷째, 본 발명은 귀금속 제품의 세정공정시 윤활유 또는 과산화수소수 등과 같은 화학약품을 사용해왔던 종래의 경우 이물질을 제거한 후 기름 및 화학약품을 제거하기 위해 후처리 작업을 해야 하므로 생산단가가 상승하고 또한 기름 및 화학약품으로 인한 환경문제가 발생하는 것과는 달리, 미사용(UNC)급 귀금속 제품의 세정공정시에는 물과 계면활성제를 사용하므로 생산단가를 줄일 수 있음과 더불어 환경문제도 개선할 수 있다.Fourth, the present invention requires a post-treatment to remove oil and chemicals after removing foreign matter in the conventional case where a chemical such as lubricating oil or hydrogen peroxide is used in a cleaning process of a noble metal product, And environmental problems caused by chemical agents, water and surfactants are used in the cleaning process of unclassified precious metal products, so that the production cost can be reduced and the environmental problems can be improved.
다섯째, 본 발명은 미사용(UNC)급 귀금속 제품의 제조방법을 소량 생산되는 프루프(proof)급 귀금속 제품의 제조에도 적용할 수 있다. Fifth, the present invention can be applied to the production of unprotected (UNC) grade precious metal products by the production of proof-grade precious metal products produced in small quantities.
도 1은 본 발명의 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조 흐름도.
도 2는 본 발명의 다른 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조 흐름도.
도 3은 본 발명의 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조 흐름 중에서, 압연 작업을 하는 광경을 나타낸 사진 도면.
도 4는 본 발명의 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조 흐름 중에서, 타발 작업을 하는 광경을 나타낸 사진 도면.
도 5는 본 발명의 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조 흐름 중에서, 이바리(burr)를 제거하면서 저울을 사용하여 중량을 맞추는 작업을 하는 광경을 나타낸 사진 도면.
도 6은 본 발명의 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조 흐름 중에서, 세정 작업을 하는 광경을 나타낸 사진 도면.
도 7은 본 발명의 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조 흐름 중에서, 압사 작업을 하는 광경을 나타낸 사진 도면.
도 8은 본 발명의 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조 흐름 중에서, 코인형 금형의 형태와 래핑 작업을 하는 광경을 나타낸 사진 도면. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a flow diagram of a process for manufacturing a UNC grade noble metal product in accordance with an embodiment of the present invention.
2 is a flow chart of a manufacturing process of an unused (UNC) grade noble metal product according to another embodiment of the present invention.
FIG. 3 is a photograph showing a scene for performing a rolling operation in a production flow of a UNC grade noble metal product according to an embodiment of the present invention. FIG.
FIG. 4 is a photograph showing a scene of a punching operation in a manufacturing flow of an unused (UNC) grade noble metal product according to an embodiment of the present invention. FIG.
FIG. 5 is a photographic view showing a scene in which, in a production flow of a UNC grade noble metal product according to an embodiment of the present invention, a work is performed using a balance while removing the burr.
FIG. 6 is a photograph showing a scene for performing a cleaning operation in a production flow of an unused (UNC) grade noble metal product according to an embodiment of the present invention. FIG.
FIG. 7 is a photograph showing a scene for performing a pressing operation in a production flow of an unused (UNC) grade noble metal product according to an embodiment of the present invention. FIG.
FIG. 8 is a photograph showing a shape of a coin-type mold and a scene for performing a lapping operation, in a manufacturing flow of a UNC grade noble metal product according to an embodiment of the present invention. FIG.
이하 첨부된 도면과 함께 본 발명의 바람직한 실시 예를 살펴보면 다음과 같은데, 본 발명을 설명함에 있어서 관련된 공지기술 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명은 생략할 것이며, 후술되는 용어들은 본 발명에서의 기능을 고려하여 정의된 용어들로서 이는 사용자, 운용자의 의도 또는 관례 등에 따라 달라질 수 있으므로, 그 정의는 본 발명인 미사용(UNC)급 귀금속 제품의 제조방법을 설명하는 본 명세서 전반에 걸친 내용을 토대로 내려져야 할 것이다. Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. In the following description of the present invention, when it is determined that a detailed description of related art or configuration may unnecessarily obscure the gist of the present invention, The description below will be omitted, and the terms described below are defined in consideration of the functions of the present invention. This may be changed according to the intention or custom of the user, the operator, and the like, And should be based on the contents of this specification which describe the method.
이하, 본 발명의 바람직한 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조방법을 첨부된 도면을 참조하여 상세히 설명한다.Hereinafter, a method of manufacturing a UNC grade noble metal product according to a preferred embodiment of the present invention will be described in detail with reference to the accompanying drawings.
도 1은 본 발명의 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조 흐름도이고, 도 2는 본 발명의 다른 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조 흐름도이며, 도 3은 본 발명의 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조 흐름 중에서, 압연 작업을 하는 광경을 나타낸 사진 도면이고, 도 4는 본 발명의 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조 흐름 중에서, 타발 작업을 하는 광경을 나타낸 사진 도면이며, 도 5는 본 발명의 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조 흐름 중에서, 이바리(burr)를 제거하면서 저울을 사용하여 중량을 맞추는 작업을 하는 광경을 나타낸 사진 도면이고, 도 6은 본 발명의 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조 흐름 중에서, 세정 작업을 하는 광경을 나타낸 사진 도면이며, 도 7은 본 발명의 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조 흐름 중에서, 압사 작업을 하는 광경을 나타낸 사진 도면이고, 도 8은 본 발명의 일실시예에 따른 미사용(UNC)급 귀금속 제품의 제조 흐름 중에서, 코인형 금형의 형태와 래핑 작업을 하는 광경을 나타낸 사진 도면이다.FIG. 1 is a flow chart for manufacturing a UNC grade noble metal product according to an embodiment of the present invention, FIG. 2 is a flowchart for manufacturing a UNC grade noble metal product according to another embodiment of the present invention, FIG. (UNC) grade noble metal product according to an embodiment of the present invention. FIG. 4 is a photograph showing a scene of performing a rolling operation in a production flow of an unused (UNC) grade noble metal product according to an embodiment of the present invention. FIG. 5 is a photograph showing a scene for performing a punching operation in a manufacturing flow, and FIG. 5 is a flowchart showing a manufacturing process of an unused (UNC) grade noble metal product according to an embodiment of the present invention by using a balance while removing the burr FIG. 6 is a photograph showing a scene for performing a cleaning operation in a production flow of an unused (UNC) grade noble metal product according to an embodiment of the present invention, and FIG. 7 is a photographFIG. 8 is a photograph showing a scene for performing a pressing operation in a production flow of a UNC grade noble metal product according to an embodiment of the present invention. FIG. 8 is a view showing the manufacturing process of a UNC grade noble metal product according to an embodiment of the present invention. Fig. 8 is a photographic view showing the shape of the coin-type mold and the sight of the lapping operation in the flow.
도 1에 도시한 바와 같이, 미사용(UNC)급 귀금속 제품의 제조방법은 백금, 금, 은 중에서 선택되는 귀금속 주괴(ingot)를 준비하는 단계(a)와; 상기 준비된 귀금속 주괴가 압연기(rolling mill)(10)의 롤러(11) 사이를 통과할 때, 3 내지 10 마력(hp)의 파워(power)로 수차례 압연을 하여 각 중량별로 판재(12) 작업을 하는 압연 단계(b)와; 상기 압연한 후, 타발기(20)를 사용하여 판재(12)에 0.5 내지 1ton으로 전단응력을 발생시켜 소정의 형상 및 치수로 절단하는 타발 단계(c)와; 상기 타발된 목표대상물(30)의 표면에 손상이 가지 않도록 하면서 가장자리의 이바리(burr)(31)를 제거하면서 저울(40)을 사용하여 중량을 목적 중량으로 맞추는 중량 맞춤 단계(d)와; 상기 맞추어진 목표대상물(30)에 산소토치의 불을 2 내지 3초간 가하여 열처리하는 소둔 단계(e)와; 상기 소둔된 목표대상물(30)인 소전을 볼 형태의 쇠가 들어 있는 세척기(50)에 물과 계면활성제를 넣고 세척기를 회전시켜 쇠 볼(51)과 소전을 마찰시켜 세척하는 세정 단계(f); 로 구성된다.As shown in FIG. 1, a method of manufacturing a UNC grade noble metal product includes the steps of (a) preparing a noble metal ingot selected from platinum, gold, and silver; When the noble metal ingot is passed between the
또한, 도 2에 도시한 바와 같이, 미사용(UNC)급 귀금속 제품의 제조방법은 백금, 금, 은 중에서 선택되는 귀금속 주괴(ingot)를 준비하는 단계(a)와; 상기 준비된 귀금속 주괴가 압연기(rolling mill)(10)의 롤러(11) 사이를 통과할 때, 3 내지 10 마력(hp)의 파워(power)로 수차례 압연을 하여 각 중량별로 판재(12) 작업을 하는 압연 단계(b)와; 상기 압연한 후, 타발기(20)를 사용하여 판재(12)에 0.5 내지 1ton으로 전단응력을 발생시켜 소정의 형상 및 치수로 절단하는 타발 단계(c)와; 상기 타발된 목표대상물(30)의 표면에 손상이 가지 않도록 하면서 가장자리의 이바리(burr)(31)를 제거하면서 저울(40)을 사용하여 중량을 목적 중량으로 맞추는 중량 맞춤 단계(d)와; 상기 맞추어진 목표대상물(30)에 산소토치의 불을 2 내지 3초간 가하여 열처리하는 소둔 단계(e)와; 상기 소둔된 목표대상물(30)인 소전을 볼 형태의 쇠가 들어 있는 세척기(50)에 물과 계면활성제를 넣고 세척기를 회전시켜 쇠 볼(51)과 소전을 마찰시켜 세척하는 세정 단계(f)와; 상기 세정된 소전에 압연기(press)를 사용하여 150 내지 500ton의 압력을 가하여 금형(60)에 의해 소전의 표면을 성형하는 압사 단계(g); 로 구성된다.Also, as shown in FIG. 2, a method of manufacturing an unused (UNC) grade noble metal product includes the steps of (a) preparing a noble metal ingot selected from platinum, gold, and silver; When the noble metal ingot is passed between the
또한, 상기 압사 단계(g) 이후에, 상기 목표대상물인 소전을 마무리 손질하는 마무리 작업 단계(g-1)가 더 구성된다.Further, after the pressing step (g), a final finishing work step (g-1) finishing the target object is constructed.
도 1과 도 2에 도시한 바와 같이, 상기 미사용(UNC)급 귀금속 제품의 제조방법을 구성하는 기술적 단계들의 기능을 살펴보면 다음과 같다.As shown in FIG. 1 and FIG. 2, the functions of the technical steps constituting the manufacturing method of the unused (UNC) grade precious metal product will be described as follows.
첫 번째로는, 주괴(ingot)를 준비하는 단계(a)로서, 백금, 금, 은 중에서 선택되는 귀금속 주괴(ingot)를 준비하는 것이다.The first step is to prepare the ingot of noble metal selected from platinum, gold and silver as the step (a) of preparing the ingot.
두 번째로는, 압연 단계(b)로서, 도 3에 도시한 바와 같이, 상기 준비된 귀금속 주괴가 압연기(rolling mill)(10)의 롤러(11) 사이를 통과할 때, 3 내지 10 마력(hp)의 파워(power)로 수차례 압연을 하여 각 중량별로 판재(12) 작업을 하는 것이다. 여기서, 상기 롤러의 파워(power)는 5 마력(hp)이 가장 바람직하다.3, when the prepared noble metal ingot passes between the
세 번째로는, 타발 단계(c)로서, 도 4에 도시한 바와 같이, 상기 압연한 후, 타발기(20)를 사용하여 판재(12)에 0.5 내지 1ton으로 전단응력을 발생시켜 소정의 형상 및 치수로 절단하는 것이다. 여기서, 상기 타발기의 전단응력은 0.5 ton이 가장 바람직하다.4, after the rolling, a shear stress is generated in the
네 번째로는, 중량 맞춤 단계(d)로서, 도 5에 도시한 바와 같이, 상기 타발된 목표대상물(30)의 표면에 손상이 가지 않도록 하면서 가장자리의 이바리(burr)(31)를 제거하면서 저울(40)을 사용하여 중량을 목적 중량으로 맞추는 것이다. 여기서, 상기 이바리(burr)를 제거하는 깎기 도구(70)는 줄(file), 갈기, 연삭기(grinder) 중의 어느 하나인 것을 포함하는 것이다. Fourth, as the weight fitting step (d), as shown in FIG. 5, the
또한, 상기 중량 맞춤 단계에서, 일부러 과도한 중량으로 제품을 생산한 후, 가장자리를 깎아내어 목적 중량을 맞추는 것이다. 이 경우 롤러를 한 개 내지 두개만을 갖고 작업하기 위해서 목적 중량보다 약간 많은 중량의 제품을 만들어 가장 자리를 깎아내는 것이다. 금제품의 경우, 소량의 중량만 미달되어도 금액으로 따지면 크기 때문에 중량에 예민하다. 그래서 의도적으로 중량을 소량 과도하게 한 후 깎아내는 것이다. In addition, in the weight adjusting step, after the product is produced with an excessive weight, the edge is shaved to achieve the desired weight. In this case, to work with only one or two rollers, a product with a weight slightly larger than the target weight is made and the edge is cut off. In the case of gold products, even if only a small amount of weight is exceeded, it is sensitive to weight because it is large in amount. So, intentionally, after a small amount of excess weight is to shave.
그러므로 의도적으로 약간 많은 중량으로 초벌 생산하여 깎아내므로 롤러를 한 개 내지 두개만 설비하여도 충분한 것이며, 이바리(burr)를 제거하는 것이 미관상의 목적일 경우가 종래의 방법이었는데, 본 발명은 생산 공정 중간에 이바리(burr)를 오히려 의도적으로 발생하게 하여 깎아내어 중량을 맞추는 것이다. 또한, 미관상 목적으로 이바리(burr)를 제거하는 과정은 본 공정의 마지막 단계에서 실시하는 것이다.Therefore, it is sufficient to provide only one or two rollers by intentionally producing a large amount of weight and then carving it out. It is a conventional method to remove the burr to remove the burr. However, In the middle of the process, the burr is intentionally generated, and the burr is weighed. In addition, the process of removing the burr for cosmetic purposes is carried out at the end of the process.
다섯 번째로는, 소둔 단계(e)로서, 상기 맞추어진 목표대상물에 산소토치의 불을 2 내지 3초간 가하여 열처리하는 것이다.Fifthly, in the annealing step (e), a fire of the oxygen torch is applied to the aligned target object for 2 to 3 seconds, followed by heat treatment.
여섯 번째로는, 세정 단계(f)로서, 도 6에 도시한 바와 같이, 상기 소둔된 목표대상물(30)인 소전을 볼 형태의 쇠가 들어 있는 세척기(50)에 물과 계면활성제를 넣고 세척기(50)를 회전시켜 쇠 볼(51)과 소전을 마찰시켜 세척하는 것이다.Sixth, as a cleaning step (f), water and a surfactant are put into a
일곱 번째로는, 압사 단계(g)로서, 도 7에 도시한 바와 같이, 상기 세정된 소전에 압연기(press)를 사용하여 150 내지 500ton의 압력을 가하여 금형(60)에 의해 소전의 표면을 성형하는 것이다. 여기서, 상기 압연기(press)의 압력은 150 ton과 300 ton이 가장 바람직한 것이다. 또한, 목표대상물이 들어있는 가락지(30)는 금형(上)과 금형(下) 사이에 놓는 기구이며, 목표대상물이 들어있는 가락지(30) 안쪽에 목적 형상이 있고, 그 곳에 목적대상물인 소전(공표)을 장입하고, 금형(上)과 금형(下)을 누르는 것이다. 상기의 경우, 목표대상물(30)을 바로 금형(上)과 금형(下)을 누르는 것도 가능할 것이다.7, as the pressing step (g), a pressure of 150 to 500 tons is applied to the cleaned pre-press using a rolling machine, and the surface of the preform is formed by the
또한, 여덟 번째로는, 마무리 작업 단계(g-1)로서, 상기 압사 단계(g) 이후에, 상기 목표대상물인 소전을 마무리 손질하여 마무리 작업을 하는 것이다. 여기서, 상기 마무리 작업 단계에서 이바리(burr)가 발생하는 경우는 압사단계의 압력이 너무 과도할 경우에 발생하는 것이기 때문에, 합당한 압력을 가하는 경우 거의 이바리(burr)가 발생하지 않는 것이다. 프루프(proof)급 제품의 경우는 세심하게 압력 조절을 해야 하나, 일반적으로 미사용(unc)급 생산시에는 적당하게 압력을 가하고 이바리(burr)을 처리를 하는 것이다. 상기 단계에서 미관상 목적으로 이바리(burr)를 제거하는 것이다. 주의할 점은 이바리(burr) 제거를 위해 깎아낼 경우, 중량이 미달되므로 이 단계에서 이바리(burr)의 제거는 깎지 않고 문대는 것이다.In the eighth, as the finishing work step (g-1), after completion of the pressing step (g), finishing work is performed by finishing the target object as the target object. Here, in the case where the burr is generated in the finishing work step, since the burr is generated when the pressure in the pressing step is excessively high, almost no burr is generated when a proper pressure is applied. In the case of proof-class products, the pressure must be carefully controlled, but in general, it is necessary to pressurize the burr with moderate pressure during production. In this step, the burr is removed for cosmetic purposes. Note that if the burr is scraped for removal, the burr will be removed at this stage because the weight is not sufficient.
상기 줄(file)은 세로면 위로 솟은 작고 많은 절삭 날을 가진 막대나 봉 모양의 경화강 공구이며, 물체(특히 금속)를 다듬질하거나 성형 작업하는데 사용되며, 보통 손으로 공작물을 문질러 연삭이나 절삭을 한다. 줄은 단면, 절삭날의 모양, 그리고 줄눈의 거칠기(㎝당 줄 눈수)에 따라 분류된다. 단면의 종류에는 최소한 20가지가 있는데, 가장 일반적인 것으로는 폭 - 두께 비가 다른 직4각형·정4각형·3각형·원형·쥐꼬리형·반원형 등이 있다. 줄눈의 모양에는 홑눈·겹눈·래습(rasp) 등 일반적으로 3가지 종류가 있다. 홑눈 줄에는 줄눈이 작업면의 대각선으로 평행하게 나 있으며, 겹눈 줄에는 서로 교차한다. 래습 줄눈은 서로 떨어져 있고 윗부분이 둥근데, 줄 표면을 펀치로 쳐서 조그맣게 솟아오르게 함으로써 만들 수 있다. 래습 줄(또는 래습)은 보통 매우 거칠어서 나무나 무른 금속에 주로 사용된다. 줄눈의 거칠기나 간격에 따른 분류는 홑눈 줄과 겹눈 줄에 국한되는데 거친날 줄, 굵은날 줄, 성긴날 줄, 중간날 줄, 다듬질 줄, 고운 다듬질 줄 등 6가지 주요형태가 있다. ㎝당 줄 눈수는 모양과 크기에 따라 매우 다르다.The file is a bar or rod shaped hardened steel tool with a small number of cutting edges that protrude vertically and is used for finishing or shaping objects (especially metals) and usually grinding or cutting the workpiece by hand do. Rows are classified according to the section, the shape of the cutting edge, and the roughness of the joint (the number of lines per cm). There are at least 20 types of cross sections. The most common ones are rectangular quadrangle, quadrilateral, triangle, round, ridge-tail, semicircle with different width-thickness ratios. There are three types of joints in general, such as single, double, and rasp. On the uneven line, the joints are parallel to the diagonal line of the working surface, and the compound lines cross each other. The razor joints can be made by spacing each other and rounding the top, punching the surface of the line and making it rise so little. Lathes (or rags) are usually very rough and are often used for wood or loose metals. Classification according to the roughness and spacing of the joints is limited to the one and the odd line. There are six main types such as a rough line, a thick line, a sparse line, a middle line, a finishing line and a fine finishing line. The line number per cm is very different depending on the shape and size.
또한, 상기 연삭기(grinding machine)는 단단하고 미세한 입자를 결합하여 제작한 연삭숫돌을 고속으로 회전시켜, 가공물의 원통면이나, 평면을 극히 소량씩 가공하는 정밀 가공방법이며 연삭을 하는 기계인 것이다.In addition, the grinding machine is a precision machining method for grinding a cylindrical surface or a flat surface of a workpiece by rotating the grindstone produced by combining hard and fine particles at a high speed, and grinding.
또한, 상기 목표대상물은 바(bar), 코인, 메달, 엽전, 공표(소전) 형태로 제품화되는 것이다. 여기서, 도 8에 도시한 바와 같이, 상기 코인 형태의 제품은 코인형 금형을 사용하며, 금형(60)의 디자인은 목적 디자인의 반대형상으로 되어 있어야 하고, 그렇게 할 경우에만 압사단계 후 목적한 디자인으로 각인되는 것이다. 또한, 랩핑 공정을 통해 금형의 표면에 광택을 내는 것이며, 상기 랩핑 공정이 잘 되어야 귀금속 제품의 광택이 좋게 나타나는 것이다.In addition, the target object is commercialized in the form of a bar, a coin, a medal, a pre-exhibition, or a public exhibition. Here, as shown in FIG. 8, the coin-shaped product uses a coin-type metal mold, and the design of the
또한, 상기 미사용(UNC)급 귀금속 제품의 제조방법은 소량 생산되는 프루프(proof)급 귀금속 제품의 제조에도 적용할 수 있는 것이다. In addition, the method of manufacturing a UNC grade noble metal product can be applied to the production of a proof grade noble metal product which is produced in small quantities.
상술한 바와 같은, 미사용(UNC)급 귀금속 제품의 제조방법은 백금, 금, 은과 같은 귀금속을 바(bar), 코인, 메달, 엽전, 공표(소전) 형태로 제품화하는데 적용할 수 있으므로 그 사용 및 적용대상이 광범위하다. As described above, the manufacturing method of the unused (UNC) grade precious metal product can be applied to the production of precious metals such as platinum, gold and silver in the form of bar, coin, medal, And a wide range of applications.
도면과 명세서에서 최적의 실시예가 개시되었으며, 여기서 사용된 용어들은 단지 본 발명을 설명하기 위한 목적에서 사용된 것이며, 의미한정이나 특허청구범위에 기재된 본 발명의 범위를 제한하기 위하여 사용된 것은 아니다. 그러므로 본 기술 분야의 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능할 것이며, 따라서, 본 발명의 진정한 기술적 보호 범위는 첨부된 특허청구범위의 기술적 사상에 의해 정해져야 할 것이다.Best Mode for Carrying Out the Invention In the drawings and specification, there have been disclosed preferred embodiments and the terminology used herein is for the purpose of describing the present invention only and not for limiting the scope of the present invention. Therefore, those skilled in the art will appreciate that various modifications and equivalent embodiments may be possible without departing from the scope of the invention.
10 : 압연기 11 : 롤러
12 : 판재 20 : 타발기
30 : 목표대상물(또는 목표대상물이 들어있는 가락지)
31 : 이바리(burr) 40 : 저울
50 : 세척기 51 : 쇠 볼
60 : 금형 70 : 깎기 도구10: rolling mill 11: roller
12: Plate 20: rudder
30: Target object (or target object)
31: burr 40: balance
50: washer 51: iron ball
60: mold 70: clipper
Claims (8)
백금, 금, 은 중에서 선택되는 귀금속 주괴(ingot)를 준비하는 단계(a)와;
상기 준비된 귀금속 주괴가 압연기(rolling mill)의 롤러 사이를 통과할 때, 3 내지 10 마력(hp)의 파워(power)로 수차례 압연을 하여 각 중량별로 판재 작업을 하는 압연 단계(b)와;
상기 압연한 후, 타발기를 사용하여 판재에 0.5 내지 1ton으로 전단응력을 발생시켜 소정의 형상 및 치수로 절단하는 타발 단계(c)와;
상기 타발된 목표대상물의 표면에 손상이 가지 않도록 하면서 가장자리의 이바리(burr)를 제거하면서 저울을 사용하여 중량을 목적 중량으로 맞추는 중량 맞춤 단계(d)와;
상기 맞추어진 목표대상물에 산소토치의 불을 2 내지 3초간 가하여 열처리하는 소둔 단계(e)와;
상기 소둔된 목표대상물인 소전을 볼 형태의 쇠가 들어 있는 세척기에 물과 계면활성제를 넣고 세척기를 회전시켜 쇠 볼과 소전을 마찰시켜 세척하는 세정 단계(f); 을 포함함을 특징으로 하는 미사용(UNC)급 귀금속 제품의 제조방법.A method of manufacturing a UNC grade noble metal product,
(A) preparing a noble metal ingot selected from platinum, gold, and silver;
A rolling step (b) of rolling the noble metal ingot several times at a power of 3 to 10 hp when the noble metal ingot passes between rollers of a rolling mill to perform plate work for each weight;
(C) a step (c) of forming a shear stress at 0.5 to 1 ton on the plate using a rudder after the rolling, and cutting the plate into a predetermined shape and dimensions;
A weight adjusting step (d) of adjusting a weight to a target weight by using a balance while removing burrs of edges while preventing damage to the surface of the punched target object;
An annealing step (e) of applying a heat of an oxygen torch to the aligned target object for 2 to 3 seconds and performing a heat treatment;
(F) a cleaning step (f) in which water and a surfactant are put into a dish-type washing machine having a spherical shape as a target object to be annealed, and the dish was rotated by rotating the dishwasher; (UNC) grade precious metal product.
백금, 금, 은 중에서 선택되는 귀금속 주괴(ingot)를 준비하는 단계(a)와;
상기 준비된 귀금속 주괴가 압연기(rolling mill)의 롤러 사이를 통과할 때, 3 내지 10 마력(hp)의 파워(power)로 수차례 압연을 하여 각 중량별로 판재 작업을 하는 압연 단계(b)와;
상기 압연한 후, 타발기를 사용하여 판재에 0.5 내지 1ton으로 전단응력을 발생시켜 소정의 형상 및 치수로 절단하는 타발 단계(c)와;
상기 타발된 목표대상물의 표면에 손상이 가지 않도록 하면서 가장자리의 이바리(burr)를 제거하면서 저울을 사용하여 중량을 목적 중량으로 맞추는 중량 맞춤 단계(d)와;
상기 맞추어진 목표대상물에 산소토치의 불을 2 내지 3초간 가하여 열처리하는 소둔 단계(e)와;
상기 소둔된 목표대상물인 소전을 볼 형태의 쇠가 들어 있는 세척기에 물과 계면활성제를 넣고 세척기를 회전시켜 쇠 볼과 소전을 마찰시켜 세척하는 세정 단계(f)와;
상기 세정된 소전에 압연기(press)를 사용하여 150 내지 500ton의 압력을 가하여 금형에 의해 소전의 표면을 성형하는 압사 단계(g); 을 포함함을 특징으로 하는 미사용(UNC)급 귀금속 제품의 제조방법.A method of manufacturing a UNC grade noble metal product,
(A) preparing a noble metal ingot selected from platinum, gold, and silver;
A rolling step (b) of rolling the noble metal ingot several times at a power of 3 to 10 hp when the noble metal ingot passes between rollers of a rolling mill to perform plate work for each weight;
(C) a step (c) of forming a shear stress at 0.5 to 1 ton on the plate using a rudder after the rolling, and cutting the plate into a predetermined shape and dimensions;
A weight adjusting step (d) of adjusting a weight to a target weight by using a balance while removing burrs of edges while preventing damage to the surface of the punched target object;
An annealing step (e) of applying a heat of an oxygen torch to the aligned target object for 2 to 3 seconds and performing a heat treatment;
(F) a cleaning step (f) in which water and a surfactant are put into a washing machine containing a metal in the shape of a ball and the rinse wheel is rotated to rub and clean the metal balls with each other;
A pressing step (g) of applying a pressure of 150 to 500 ton by using a mill to the cleaned preform to mold the surface of the preform by a mold; (UNC) grade precious metal product.
상기 압사 단계(g) 이후에, 상기 목표대상물인 소전을 마무리 손질하는 마무리 작업 단계(g-1); 을 더 포함함을 특징으로 하는 미사용(UNC)급 귀금속 제품의 제조방법.3. The method of claim 2,
A finishing work step (g-1) for final finishing the target object as the target object after the pressing step (g); Further comprising the steps of: preparing a precious metal product;
상기 목표대상물은 바(bar), 코인, 메달, 엽전, 공표(소전) 형태로 제품화되는 것을 특징으로 하는 미사용(UNC)급 귀금속 제품의 제조방법.3. The method according to claim 1 or 2,
Wherein the target object is commercialized in the form of a bar, a coin, a medal, a pre-warp, or an unprecedented (unprecedented) form.
상기 미사용(UNC)급 귀금속 제품의 제조방법은 소량 생산되는 프루프(proof)급 귀금속 제품의 제조에도 적용할 수 있는 것을 포함함을 특징으로 하는 미사용(UNC)급 귀금속 제품의 제조방법.3. The method according to claim 1 or 2,
A method of manufacturing a UNC grade noble metal product, which is applicable to the production of a proof grade noble metal product produced in small quantities.
상기 단계(d)에서, 상기 이바리(burr)를 제거하는 깎기 도구는 줄(file), 갈기, 연삭기(grinder) 중의 어느 하나인 것을 포함함을 특징으로 하는 미사용(UNC)급 귀금속 제품의 제조방법.3. The method according to claim 1 or 2,
Wherein the cutting tool for removing the burr in the step (d) includes one of a file, a grinder, and a grinder. Way.
상기 단계(g-1)에서, 상기 이바리(burr)를 제거하는 깎기 도구는 줄(file), 갈기, 연삭기(grinder) 중의 어느 하나인 것을 포함함을 특징으로 하는 미사용(UNC)급 귀금속 제품의 제조방법.The method of claim 3,
Wherein the cutting tool for removing the burr in the step (g-1) includes any one of a file, a mane, and a grinder. ≪ / RTI >