KR101568136B1 - Natural leather and manufacture method of the natural leather - Google Patents
Natural leather and manufacture method of the natural leather Download PDFInfo
- Publication number
- KR101568136B1 KR101568136B1 KR1020130150567A KR20130150567A KR101568136B1 KR 101568136 B1 KR101568136 B1 KR 101568136B1 KR 1020130150567 A KR1020130150567 A KR 1020130150567A KR 20130150567 A KR20130150567 A KR 20130150567A KR 101568136 B1 KR101568136 B1 KR 101568136B1
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- leather
- splits
- natural leather
- polyurethane
- Prior art date
Abstract
본 발명은 천연가죽에 관한 것으로, 그 구성은 털을 제거하지 않은 상태인 원료피(rawhide)와, 털을 제거한 상태인 나피(pelt)와, 상기 나피를 크롬탄닝 후 털이 있었던 부위를 할피한 표피층과, 상기 표피층 아래 부분인 스프리트를 포함하는 소가죽에 있어서, 상기 스프리트로 구성되는 본체층과, 상기 본체층의 상면에 위치되며, 접착제로 구성되는 접착층과, 상기 접착층의 상면에 위치되며, 상기 접착층으로 인해 상기 본체층과 접착 결합되며, 폴리우레탄 재질을 가지는 폴리우레탄시트층과, 상기 폴리우레탄시트층의 상면을 코팅하며, 폴리우레탄 재질을 가지는 폴리우레탄코팅층을 포함하는 것을 특징으로 하는 것으로서, 신발류나 가방류나 지갑류나 자동차 시트 등에 사용되는 우피로 이루어지는 천연가죽을 용이하게 제조할 수 있으며, 촉감이 부드러우며, 가죽 질감을 매끄럽게 하고 표면을 보호할 수 있으며, 색상의 표현이 자유로우며, 저렴한 비용으로 천연가죽의 질감을 나타낼 수 있으며, 천연가죽을 저렴한 단가로 제공할 수 있는 효과가 있다. The present invention relates to a natural leather, which comprises a rawhide in which hair is not removed, a pelt in a state in which hair is removed, and a skin layer in which the hairs are present after chrome tanning, And a splice as a lower part of the skin layer, the leather comprising: a body layer composed of the splits; an adhesive layer positioned on an upper surface of the body layer, the adhesive layer being composed of an adhesive; A polyurethane sheet layer having a polyurethane material adhered to the main body layer due to an adhesive layer, and a polyurethane coating layer having a polyurethane material coating the upper surface of the polyurethane sheet layer, It is possible to easily produce natural leather made of leather used for footwear, bags, purses, car seats and the like, Roasting dollars, and to protect the surface smoother skin texture, and color representation are free, of, low cost, and can represent the texture of the leather, there is an effect that can provide the leather with cheap price.
Description
본 발명은 천연가죽 제조방법에 관한 것으로, 더욱 상세하게는 신발류나 가방류나 지갑류나 자동차 시트 등에 사용되는 우피로 이루어지는 천연가죽을 용이하게 제조할 수 있으며, 촉감이 부드러우며, 가죽 질감을 매끄럽게 하고 표면을 보호할 수 있으며, 색상의 표현이 자유로우며, 저렴한 비용으로 천연가죽의 질감을 나타낼 수 있으며, 천연가죽을 저렴한 단가로 제공할 수 있는 천연가죽 제조방법에 관한 것이다. More particularly, the present invention relates to a process for producing a natural leather, which can be easily produced from natural leather used for footwear, bags, purses, car seats, etc., and which has a soft feel, To a method for producing natural leather which can express the texture of natural leather at low cost and can provide natural leather at low cost.
일반적으로 신발류나, 가방류나, 지갑류나, 자동차 시트 등에 사용되는 가죽의 종류에는 우피, 양피, 돈피, 어피, 파충류피 등이 있는데 본 기술에 관한 것은 소가죽인 우피에 한한다. In general, leather used for footwear, bags, purses, car seats, etc. includes leather, sheepskin, sheepskin, apricot, reptile, and the like.
한편, 소가죽은 털을 제거하지 않은 상태를 원료피(rawhide) 라고 하고, 털을 제거한 상태를 나피(pelt) 라고 하며, 나피를 크롬탄닝 후 가죽을 두께 방향과 직각되는 방향으로 할피(가죽을 절단하는 것을 말함) 했을 때 털이 있었던 부위와 인접된 것을 표피층이라고, 표피층 아래 부위를 표피아래층(또는 '스프리트'라고 함) 이라고 하여 소가죽을 구분한다. 본 발명의 소재는 스프리트에 한한다. On the other hand, the cowhide is called a rawhide without hair removal, the state where the hair is removed is called a pelt, and the leather is tanned with chrome tanned leather in a direction perpendicular to the thickness direction, Cut "), the skin adjacent to the area where the hair was present is called the skin layer, and the area below the skin layer is called the epidermal layer (or" splits "). The material of the present invention is limited to the splits.
종래에 천연가죽의 질감을 내기 위해서, 상기 스프리트에는 털을 제거한 표피층이 없으므로 표피층과 유사하게 올리우레탄코팅을 하고 있는데 이를 '폴리우레탄코팅레쟈' 라고 한다. Conventionally, in order to impart a natural leather texture, there is no skin layer on which the hairs are removed, so that the leather is coated with an oily urethane coating similar to a skin layer, which is referred to as a " polyurethane coating ".
한편, 대한민국 특허출원번호 제10-2000-0008825호를 참고하면, 가죽 표면의 질감을 매끄럽게 하고 표면을 보호할 수 있도록 가죽원단의 표면에 폴리우레탄막을 형성하는 방법에 관한 것으로 이형제 등이 필요하고 그 제조공정 또한 복잡하다는 문제점이 있었다.
On the other hand, Korean Patent Application No. 10-2000-0008825 discloses a method for forming a polyurethane film on the surface of a leather fabric so as to smooth the texture of the leather surface and protect the surface, The manufacturing process is also complicated.
본 발명은 상기한 바와 같은 제반 문제점을 해결하기 위하여 제안된 것으로, 그 목적은 신발류나 가방류나 지갑류나 자동차 시트 등에 사용되는 우피로 이루어지는 천연가죽을 용이하게 제조할 수 있으며, 촉감이 부드러우며, 가죽 질감을 매끄럽게 하고 표면을 보호할 수 있으며, 색상의 표현이 자유로우며, 저렴한 비용으로 천연가죽의 질감을 나타낼 수 있으며, 천연가죽을 저렴한 단가로 제공할 수 있는 천연가죽 제조방법을 제공하는데 그 목적이 있다. The present invention has been proposed in order to solve all of the problems as described above. It is an object of the present invention to provide a method for manufacturing a natural leather which is used for footwear, bags, purses and car seats, It is an object of the present invention to provide a method of manufacturing natural leather which can smooth the texture and protect the surface, can express the color freely, can display the texture of natural leather at low cost, and can provide natural leather at low cost. have.
상기와 같은 목적을 달성하기 위한 본 발명에 따른 천연가죽은, 털을 제거하지 않은 상태인 원료피(rawhide)와, 털을 제거한 상태인 나피(pelt)와, 상기 나피를 크롬탄닝 후 털이 있었던 부위를 할피한 표피층과, 상기 표피층 아래 부분인 스프리트를 포함하는 소가죽에 있어서, 상기 스프리트로 구성되는 본체층과, 상기 본체층의 상면에 위치되며, 접착제로 구성되는 접착층과, 상기 접착층의 상면에 위치되며, 상기 접착층으로 인해 상기 본체층과 접착 결합되며, 폴리우레탄 재질을 가지는 폴리우레탄시트층과, 상기 폴리우레탄시트층의 상면을 코팅하며, 폴리우레탄 재질을 가지는 폴리우레탄코팅층을 포함하는 것을 특징으로 한다. According to an aspect of the present invention, there is provided a natural leather comprising a rawhide in which hair is not removed, a pelt in which hair is removed, And a splice which is a portion below the skin layer, wherein the skin layer comprises a body layer composed of the splits, an adhesive layer positioned on the upper surface of the body layer and composed of an adhesive, A polyurethane sheet layer having a polyurethane material adhered to the body layer by the adhesive layer and a polyurethane coating layer having a polyurethane material coating the upper surface of the polyurethane sheet layer .
또한, 본 발명에 따른 천연가죽은, 털을 제거하지 않은 상태인 원료피(rawhide)와, 털을 제거한 상태인 나피(pelt)와, 상기 나피를 크롬탄닝 후 털이 있었던 부위를 할피한 표피층과, 상기 표피층 아래 부분인 스프리트를 포함하는 소가죽에 있어서, 상기 스프리트로 구성되는 본체층과, 상기 본체층의 상면에 위치되며, 접착제로 구성되는 접착층과, 상기 접착층의 상면에 위치되며, 상기 접착층으로 인해 상기 본체층과 접착 결합되며, 폴리우레탄 재질을 가지는 폴리우레탄시트층을 포함하되, 상기 폴리우레탄시트층의 상면은 복수 개의 돌출부가 형성되도록 상기 폴리우레탄시트층을 이루는 폴리우레탄시트를 사포가 감겨진 롤러 사이로 통과시켜 표면에 기모가 생기도록 하는 버핑공정을 거친 것을 특징으로 한다. In addition, the natural leather according to the present invention includes a rawhide in which hair is not removed, a pelt in a state in which hair is removed, a skin layer in which the hair is removed after chrome tanning, And a splice which is a lower part of the skin layer, the leather comprising: a main body layer composed of the splits; an adhesive layer positioned on an upper surface of the main body layer, the adhesive layer being positioned on an upper surface of the adhesive layer; And a polyurethane sheet layer having a polyurethane material, the upper surface of the polyurethane sheet layer being wound with a polyurethane sheet constituting the polyurethane sheet layer so as to form a plurality of protrusions, And passing through a gentle roller to form a brushed surface.
또한, 본 발명에 따른 천연가죽의 제조방법은, 털을 제거하지 않은 상태인 원료피(rawhide)와, 털을 제거한 상태인 나피(pelt)와, 상기 나피를 크롬탄닝 후 털이 있었던 부위를 할피한 표피층과, 상기 표피층 아래 부분인 스프리트를 포함하는 소가죽에 있어서, 상기 크롬탄닝은, 드럼에 가죽 100 kg 당 물 50 kg 내지 70 kg과, 크롬분말 3 kg 내지 6 kg과, 세제 1 kg 내지 2 kg 을 수용시키고, 24 시간 교반시키는 것으로 이루어지며, 상기 스프리트를 가공하여, 가공된 스프리트의 상면에 폴리우레탄시트를 접착제로 합지하고, 상기 폴리우레탄시트의 상면에 폴리우레탄코팅을 하되, 상기 스프리트의 가공은, 상기 스프리트를 중화시키는 중화단계와, 상기 중화단계를 거친 스프리트를 50 도씨(℃) 내지 300 도씨(℃)의 온도를 가지는 열판으로 눌러서 건조시기는 건조단계와, 상기 건조단계를 거친 스프리트를 1분에 30 회 내지 300 회의 반복횟수로 봉으로 타격하여 가죽을 부드럽게 하는 바이브레이션단계 및 상기 바이브레이션단계를 거친 스프리트를 사포가 감겨진 롤러에 통과시켜 표면작업을 하는 표면작업단계를 포함하는 것을 특징으로 한다. The method for producing natural leather according to the present invention is characterized in that a rawhide in which hair is not removed, a pelt in a state in which hair is removed, and a napi in which the hair is removed after chrome tanning, Claims 1. A cowhide comprising a skin layer and a splits below the skin layer, wherein the chrome tanning comprises 50 to 70 kg of water, 3 to 6 kg of chromium powder, 1 to 2 kg of detergent per 100 kg of leather, kg, and stirring the mixture for 24 hours. The splits are processed to form a polyurethane sheet on the upper surface of the processed splits with an adhesive, and a polyurethane coating is applied to the upper surface of the polyurethane sheet, The processing is carried out by pressing the neutralized step for neutralizing the spray and the sprayed material through the neutralization step with a hot plate having a temperature of 50 to 300 degrees Celsius, A vibrating step of smoothing the leather by striking the splits having passed through the drying step with a rod at a frequency of 30 to 300 repetitions per minute, and a step of passing the splits having passed through the vibrating step through rollers sandwiched between the surfaces, And a working step.
또한, 본 발명에 따른 천연가죽 제조방법에서, 상기 중화단계는, 상기 스프리트 100 kg 당, 레진 1 kg 내지 5 kg, 개미산 1 kg 내지 4 kg, 중조 5 kg 내지 8 kg, 의산소다 1 kg 내지 3 kg, 크롬 1 kg 내지 3 kg, 가지제 6 kg 내지 8 kg, 바인더 1 kg 내지 5 kg, 신탄 3 kg 내지 5 kg 을 드럼에 함께 혼합하고 상기 드럼을 10 시간 내지 40 시간 교반시키는 것으로 이루어지며, 상기 중화단계와 건조단계 사이에 염료를 첨가하여 색상을 첨가하는 염색단계를 더 포함하는 것을 특징으로 한다. Further, in the method for producing natural leather according to the present invention, the neutralization step may comprise: 1 kg to 5 kg of resin, 1 kg to 4 kg of formic acid, 5 kg to 8 kg of sodium bicarbonate, 1 kg to 3 kg of sodium bicarbonate kg of chromium, 1 kg to 3 kg of chromium, 6 kg to 8 kg of branch, 1 kg to 5 kg of binder, 3 kg to 5 kg of coal, and stirring the drum for 10 to 40 hours, And a dyeing step of adding a color between the neutralization step and the drying step to add a color.
본 발명에 따른 천연가죽 제조방법에 의하면, 신발류나 가방류나 지갑류나 자동차 시트 등에 사용되는 우피로 이루어지는 천연가죽을 용이하게 제조할 수 있으며, 촉감이 부드러우며, 가죽 질감을 매끄럽게 하고 표면을 보호할 수 있으며, 색상의 표현이 자유로우며, 저렴한 비용으로 천연가죽의 질감을 나타낼 수 있으며, 천연가죽을 저렴한 단가로 제공할 수 있는 효과가 있다. According to the method for producing natural leather according to the present invention, it is possible to easily produce natural leather made of leather used for footwear, bags, purses and car seats, and can smoothly soften the leather texture, And is capable of expressing the color of natural leather at a low cost and can provide natural leather at low cost.
본 발명은 첨부된 도면에 도시된 실시예를 참고로 설명되나, 이는 예시적인 것이며, 당해 분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 실시예가 가능하다는 점을 이해할 수 있을 것이다. 따라서 본 발명의 진정한 보호범위는 첨부된 청구범위에 의해서만 정해져야 할 것이다. While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is evident that many alternatives, modifications and variations will be apparent to those skilled in the art. Accordingly, the true scope of protection of the present invention should be determined only by the appended claims.
도 1은 본 발명의 일 실시 예에 따른 천연가죽의 구성을 나타낸 단면도
도 2는 본 발명의 다른 실시 예에 따른 천연가죽의 구성을 나타낸 단면도
도 3은 본 발명의 일 실시예에 따른 천연가죽을 제조하는 방법을 도시한 순서도1 is a cross-sectional view showing the construction of a natural leather according to an embodiment of the present invention;
2 is a cross-sectional view showing the construction of a natural leather according to another embodiment of the present invention
3 is a flow chart illustrating a method of making natural leather according to one embodiment of the present invention.
이하, 본 발명의 바람직한 실시 예에 따른 천연가죽 제조방법을 첨부된 도면에 의거하여 상세히 설명한다. Hereinafter, a method of manufacturing a natural leather according to a preferred embodiment of the present invention will be described in detail with reference to the accompanying drawings.
도 1 내지 도 3은 본 발명의 실시 예에 따른 천연가죽 제조방법을 도시한 것으로, 도 1은 본 발명의 일 실시 예에 따른 천연가죽의 구성을 나타낸 단면도를, 도 2는 본 발명의 다른 실시 예에 따른 천연가죽의 구성을 나타낸 단면도를, 도 3은 본 발명의 일 실시예에 따른 천연가죽을 제조하는 방법을 도시한 순서도를 각각 나타낸 것이다. 1 to 3 illustrate a method of manufacturing a natural leather according to an embodiment of the present invention. FIG. 1 is a sectional view showing the construction of a natural leather according to an embodiment of the present invention. Fig. 3 is a flowchart showing a method of manufacturing a natural leather according to an embodiment of the present invention, and Fig.
상기 도면에 도시된 바와 같이, 본 발명의 일 실시 예에 따른 가죽시트(100)는 본체층(10)과, 접착층(20)과, 폴리우레탄시트층(30)과, 폴리우레탄코팅층(40)을 포함하고 있다. A
한편, 소가죽의 털을 제거하지 않은 상태인 원료피(rawhide)와, 털을 제거한 상태인 나피(pelt)와, 상기 나피를 크롬탄닝 후 털이 있었던 부위를 할피한 표피층과, 상기 표피층 아래 부분인 스프리트로 소가죽이 구분됨은 이미 설명하였다. On the other hand, a rawhide in which the hair of the leather is not removed, a pelt in the state where the hair is removed, a skin layer in which the hair after the chrome tanning is avoided, The division of cowhide with splits has already been explained.
상기 본체층(10)은 상기 스프리트로 구성되는 것이다. The body layer (10) consists of the splits.
상기 접착층(20)은 상기 본체층(10)의 상면에 위치되며, 접착제로 구성되는 것이다. The
상기 폴리우레탄시트층(30)은 상기 접착층(20)의 상면에 위치되며, 상기 접착층(20)으로 인해 상기 본체층(10)과 접착 결합되며, 폴리우레탄 재질을 가지는 것이다. The
상기 폴리우레탄코팅층(40)은 상기 폴리우레탄시트층(30)의 상면을 코팅하며, 폴리우레탄 재질을 가지는 것이다.
The
상기와 같은 구성을 가진 본 발명의 일 실시 예에 따른 천연가죽(100)은 다음과 같이 제조된다. The
먼저, 소가죽이 털을 제거하지 않은 상태인 원료피(rawhide)와, 털을 제거한 상태인 나피(pelt)와, 상기 나피를 크롬탄닝 후 털이 있었던 부위를 할피한 표피층과, 상기 표피층 아래 부분인 스프리트로 구분됨은 이미 설명하였다. First, raw hides, which are raw hides without removing hairs, pests which are hairless, hairs that have avoided hairs after chrome tanning of the hides, The division into sprites has already been explained.
여기서 상기 나피를 크롬탄닝하는 방법은, 드럼에 가죽 100 kg 당 물 50 kg 내지 70 kg과, 크롬분말 3 kg 내지 6 kg과, 세제 1 kg 내지 2 kg 을 수용시키고, 24 시간 교반시키는 것으로 이루어진다. Here, the method of chrome tanning the nappe is such that 50 kg to 70 kg of water, 3 kg to 6 kg of the chromium powder and 1 kg to 2 kg of the detergent per 100 kg of leather are accommodated in the drum and stirred for 24 hours.
이어서, 상기 본체층(10, 스프리트)을 가공한다. 상기 본체층(10, 스프리트)을 가공하는 공정에 대해서는 후술한다. Then, the body layer (10, splits) is processed. The process of processing the main body layer 10 (splits) will be described later.
이어서, 가공된 상기 본체층(10, 스프리트)의 상면에 폴리우레탄시트층(30)를 접착제로 합지한다. 이때 상기 폴리우레탄시트층(30)의 상면에는 이미 폴리우레탄코팅을 하여 상기 폴리우레탄코팅층(40)이 형성되어 있는 상태이다. Then, the
이렇게 스프리트에 상면에 폴리우레탄코팅이 미리 되어 있는 폴리우레탄시트를 접착제로 합지한 것을 퍼미어(permea)라고 부른다. In this way, it is called "permea" that a spliced polyurethane sheet with a polyurethane coating on the top surface is laminated with an adhesive.
한편, 상기 본체층(10, 스프리트)을 가공하는 방법은, 중화단계(S1)와, 염색단계(S2)와, 건조단계(S3)와, 바이브레이션단계(S4)와, 표면작업단계(S5)를 포함한다. The method of processing the
상기 중화단계(S1)는 상기 본체층(10, 스프리트)를 중화시키는 공정이다. The neutralization step (S1) is a step of neutralizing the body layer (10, splits).
상기 중화단계(S1)는, 상기 본체층(10, 스프리트) 100 kg 당, 레진 1 kg 내지 5 kg, 개미산 1 kg 내지 4 kg, 중조 5 kg 내지 8 kg, 의산소다 1 kg 내지 3 kg, 크롬 1 kg 내지 3 kg, 가지제 6 kg 내지 8 kg, 바인더 1 kg 내지 5 kg, 신탄 3 kg 내지 5 kg 을 드럼에 함께 혼합하고 상기 드럼을 10 시간 내지 40 시간 교반시키는 것으로 이루어진다. The neutralization step (S1) comprises, in 100 kg of the body layer (10, splits), 1 kg to 5 kg of resin, 1 kg to 4 kg of formic acid, 5 kg to 8 kg of sodium bicarbonate, 1 kg to 3 kg of sodium bicarbonate, 1 kg to 3 kg, 6 kg to 8 kg of branch, 1 kg to 5 kg of binder and 3 kg to 5 kg of coal are mixed together and the drum is stirred for 10 to 40 hours.
상기 염색단계(S2)는 상기 중화단계(S1)를 거친 상기 본체층(10, 스프리트)에 원하는 색상의 염료를 첨가하여 색상을 첨가시키는 공정이다. The dyeing step S2 is a step of adding a color to the main layer 10 (splits) which has been subjected to the neutralization step S1 by adding a dye of a desired color.
상기 건조단계(S3)는 상기 염색단계(S2)를 거친 상기 본체층(10, 스프리트)를 50 도씨(℃) 내지 300 도씨(℃)의 온도를 가지는 열판으로 눌러서 건조시키는 공정이다. The drying step S3 is a step of pressing the
상기 바이브레이션단계(S4)는 상기 건조단계(S3)를 거친 상기 본체층(10, 스프리트)를 1분에 30 회 내지 300 회의 반복횟수로 봉으로 타격하여 가죽을 부드럽게 하는 공정이다. 이렇게 바이브레이션단계를 거친 스프리트를 카라스터(crust)라도 부른다. The vibration step S4 is a step of softening the leather by striking the main body layer 10 (splits) after the drying step S3 with the
상기 표면작업단계(S5)는 상기 바이브레이션단계(S4)를 거친 상기 본체층(10, 스프리트)를 사포가 감겨진 롤러에 통과시켜 표면작업을 하는 공정이다.
The surface working step S5 is a step of passing the main body layer 10 (splits), which have been subjected to the vibration step S4, through a roller wound with a sandpaper to perform surface working.
한편, 본 발명의 일 실시 예에 따른 천연가죽(100)은 최상면에 폴리우레탄코팅층(40)으로 마감되는 것으로 설명되었으나, 여기에 한정되지는 않는다. Meanwhile, although the
도 2에 본 발명의 다른 실시 예에 따른 천연가죽(200)을 도시하였다. 2 shows a
본 발명의 다른 실시 예에 따른 천연가죽(200)은 본체층(10)과, 접착층(20)과, 폴리우레탄시트층(230)을 포함한다. The
상기 본체층(10)과, 접착층(20)은 이미 설명한 실시예와 동일하므로 자세한 설명은 생략한다. Since the
상기 폴리우레탄시트층(230)은 상기 접착층(20)의 상면에 위치되며, 상기 접착층(20)으로 인해 상기 본체층(10)과 접착 결합되며, 폴리우레탄 재질을 가진다. The
단지, 특이한 것은 상기 폴리우레탄시트층(230)의 상면은 복수 개의 돌출부(232)가 형성되어 있다. It should be noted that the upper surface of the
이를 위해서 상기 바이브레이션단계를 거친 스프리트(이를 크라스터 라고 함은 이미 설명하였다)에, 상기 폴리우레탄시트층(230)을 사포가 감겨진 롤러에 통과시켜 상기 폴리우레탄시트층(230)의 표면에 기모가 생기도록(버핑공정) 작업하고, 이렇게 표면에 기모가 생긴 폴리우레탄시트층(230)을 접착제로 상기 바이브레이션단계를 거친 스프리트에 접착제로 접착하는 것이다. 이를 누벅(nubuck)이라 한다. To this end, the
본 발명의 다른 실시 예에 따른 천연가죽(200)에서 상기 본체층(10, 스프리트)를 가공하는 방법은 앞서 설명한 실시예와 동일하다.
The method of processing the body layer 10 (splits) in the
10. 본체층 20. 접착층
30. 230. 폴리우레탄시트층 40. 폴리우레탄코팅층
232. 돌출부10.
30. 230.
232. Projection
Claims (4)
상기 크롬탄닝은,
드럼에 가죽 100 kg 당 물 50 kg 내지 70 kg과, 크롬분말 3 kg 내지 6 kg과, 세제 1 kg 내지 2 kg 을 수용시키고, 24 시간 교반시키는 것으로 이루어지며,
상기 스프리트를 가공하여, 가공된 스프리트의 상면에 폴리우레탄시트를 접착제로 합지하고, 상기 폴리우레탄시트의 상면에 폴리우레탄코팅을 하되,
상기 스프리트의 가공은,
상기 스프리트를 중화시키는 중화단계(S1);
상기 중화단계를 거친 스프리트를 50 도씨(℃) 내지 300 도씨(℃)의 온도를 가지는 열판으로 눌러서 건조시기는 건조단계(S3);
상기 건조단계를 거친 스프리트를 1분에 30 회 내지 300 회의 반복횟수로 봉으로 타격하여 가죽을 부드럽게 하는 바이브레이션단계(S4); 및
상기 바이브레이션단계를 거친 스프리트를 사포가 감겨진 롤러에 통과시켜 표면작업을 하는 표면작업단계(S5);를 포함하는 것을 특징으로 하는 천연가죽 제조방법.
1. A method for producing a natural leather including a pelt which is in a state where hair is removed, a skin layer which avoids a hairy portion after chrome tanning of the nappy, and splits which are a portion below the skin layer,
In the chrome tanning,
50 kg to 70 kg of water, 3 kg to 6 kg of chromium powder and 1 kg to 2 kg of detergent per 100 kg of leather are accommodated in the drum and stirred for 24 hours,
The splits are processed to form a polyurethane sheet on the upper surface of the processed splices with an adhesive and a polyurethane coating on the upper surface of the polyurethane sheet,
In the processing of the splits,
A neutralization step (S1) of neutralizing the split;
The spraying step is carried out by pressing the sprayed spit with a hot plate having a temperature of 50 ° C to 300 ° C,
A vibration step (S4) of smoothing the leather by striking the splits having passed through the drying step with a rod at a frequency of 30 to 300 repetitions per minute; And
And a surface working step (S5) of performing a surface work by passing the splits having passed through the vibrating step to rollers sandwiched therebetween.
상기 중화단계(S1)는, 상기 스프리트 100 kg 당, 레진 1 kg 내지 5 kg, 개미산 1 kg 내지 4 kg, 중조 5 kg 내지 8 kg, 의산소다 1 kg 내지 3 kg, 크롬 1 kg 내지 3 kg, 가지제 6 kg 내지 8 kg, 바인더 1 kg 내지 5 kg, 신탄 3 kg 내지 5 kg 을 드럼에 함께 혼합하고 상기 드럼을 10 시간 내지 40 시간 교반시키는 것으로 이루어지며,
상기 중화단계(S1)와 건조단계(S3) 사이에 염료를 첨가하여 색상을 첨가하는 염색단계(S2)를 더 포함하는 것을 특징으로 하는 천연가죽 제조방법.The method of claim 3,
The neutralization step (S1) comprises the steps of: 1 kg to 5 kg of resin, 1 kg to 4 kg of formic acid, 5 kg to 8 kg of sodium bicarbonate, 1 kg to 3 kg of sodium bicarbonate, 1 kg to 3 kg of chromium, Mixing 6 kg to 8 kg of the branch, 1 kg to 5 kg of the binder and 3 kg to 5 kg of the coal to the drum and stirring the drum for 10 to 40 hours,
Further comprising a dyeing step (S2) of adding a dye between the neutralization step (S1) and the drying step (S3) to add a color.