KR101553401B1 - Mnufacturing method of embossing wallpaper and embossing wallpaper thereby the same that - Google Patents
Mnufacturing method of embossing wallpaper and embossing wallpaper thereby the same that Download PDFInfo
- Publication number
- KR101553401B1 KR101553401B1 KR1020150027857A KR20150027857A KR101553401B1 KR 101553401 B1 KR101553401 B1 KR 101553401B1 KR 1020150027857 A KR1020150027857 A KR 1020150027857A KR 20150027857 A KR20150027857 A KR 20150027857A KR 101553401 B1 KR101553401 B1 KR 101553401B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- resin
- wallpaper
- pattern
- impregnated fabric
- Prior art date
Abstract
Description
본 발명은 함침원단을 이용한 엠보싱무늬 벽지의 제조방법 및 이에 의해 제조된 엠보싱무늬 벽지에 관한 것으로서, 보다 상세하게는 변형이 방지되어 시공이 용이하고, 엠보싱무늬가 소실될 우려가 없고 외관도 미려한 새로운 구성의 함침원단을 이용한 엠보싱무늬 벽지의 제조방법 및 이에 의해 제조된 엠보싱무늬 벽지에 관한 것이다.
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method of manufacturing an embossed pattern wallpaper using impregnated fabric and an embossed pattern wallpaper produced by the method. More particularly, the present invention relates to an embossed pattern wall The present invention relates to a method of manufacturing an embossed pattern wallpaper using impregnated fabric of a constitution and an embossed pattern wallpaper produced thereby.
벽지는 크게 재질에 따라 종이벽지, 2장 이상의 종이가 합지된 합지벽지, 합성수지소재의 비닐벽지, 섬유소재 벽지 또는 자연소재 벽지 등으로 나누어지고, 또한 구조에 따라 평면벽지, 엠보무늬 벽지 등으로 나누어진다.The wallpaper can be classified into paper wall paper, laminated wallpaper composed of two or more pieces of paper, vinyl wallpaper of synthetic resin, textile material wallpaper or natural material wallpaper according to the material, and divided into plane wallpaper and embossed wallpaper according to the structure Loses.
엠보무늬 벽지란 벽지 표면에 엠보싱 무늬를 부여하여 제품에 입체적 효과를 부여한 것으로서, 엠보싱 공정을 포함하는 제조방법으로 제조되는데, 엠보무늬벽지 중에서 합지벽지는 벽지원지에 수성접착제층 도포한 벽지용 하지와 상지(박엽지 및 부직포에 무늬를 인쇄한 것)을 서로 접착한 후, 암수 한벌로 되어있는 엠보싱 장치를 이용해 엠보싱을 성형된다. 그런데 이러한 합지벽지는 하지와 상지가 서로 다른 물성, 특히 서로 다른 열수축률 또는 수분수축률을 가지기 때문에, 벽지가 열수축 또는 수분수축이 적은 쪽으로 말리는 말림현상이 발생되고, 또한 이러한 말림현상으로 인해 벽지시공 후에 벽지가 벽체에서 떨어지는 경우가 발생되거나 벽지의 하지와 상지가 분리되기도 한다.Embossed wallpaper is a product that gives embossing effect to a product by giving an embossing pattern to the surface of the wallpaper. It is manufactured by a manufacturing method including an embossing process. Among the embossed wallpaper, the wallpaper is formed by applying a water- After the topsheet (the paper and the non-woven fabric are printed with patterns) are bonded to each other, embossing is performed using an embossing device made of male and female. However, since such backing wallpaper has different physical properties, particularly different heat shrinkage rates or water shrinkage rates, between the lower and upper limbs, a curling phenomenon occurs in which the wallpaper dries to a side with less heat shrinkage or moisture shrinkage. The wallpaper may fall off the wall, or the floor of the wallpaper may be separated from the upper limb.
뿐만 아니라 벽지 시공시에 접착제에 함유된 수분에 의해 벽지가 손상되어 벽지에 형성된 엠보싱무늬가 소실되어 벽지의 입체감이 감소되는 경우도 발생된다. In addition, the wallpaper may be damaged by the moisture contained in the adhesive when the wallpaper is applied, and the embossed pattern formed on the wallpaper may be lost, thereby reducing the stereoscopic effect of the wallpaper.
또한, 벽지의 상하면이 모두 엠보싱처리되어 벽지의 하면에 요철이 형성되는데, 벽지 시공시에 이러한 요철에 접착제가 채워짐에 따라 접착제가 불필요하게 많이 소모되며, 과다한 접착제로 인해 곰팡이가 발생되는 문제점도 야기된다.In addition, the upper and lower surfaces of the wallpaper are all embossed to form irregularities on the lower surface of the wallpaper. As the adhesive is filled in the irregularities at the time of wallpaper construction, unnecessary adhesive is consumed unnecessarily and mold is generated due to excessive adhesive. do.
한편, 실크벽지의 경우 벽지원지 위에 열가소성수지인 PVC졸을 적층가공한 후 건조 및 엠보싱처리하거나, PVC필름을 합지벽지와 같이 벽지원지 위에 접착한 후 엠보싱 처리함으로써 합지벽지의 치명적단점인 성형된 무늬의 소멸을 극복하고 있다.On the other hand, in the case of silk wallpaper, the PVC film, which is a thermoplastic resin, is laminated on the wallpaper paper and then dried and embossed, or the PVC film is adhered on wallpaper paper such as a ridge wallpaper and embossed, Overcome the disappearance of.
그러나, 이러한 실크벽지 역시 합지벽지와 마찬가지로 시공시 원지와 PVC층이 서로 분리되거나, 수축율이 적은 쪽으로 말려 올라가는 현상은 여전히 상존하고 있다.
However, as with silk wallpaper, silk wallpaper is separated from the original layer and PVC layer at the time of construction, and the phenomenon that the silk wallpaper is curled up toward the shrinkage ratio still exists.
본 발명은 상기와 같은 문제점에 착안하여 제안되는 것으로서, 본 발명의 목적은 벽지가 단일의 층을 이루도록 제조되기 때문에, 벽지가 상하로 분리되거나 또는 물성차이로 인해 말리는 형상이 발생되지 않으며, 엠보싱무늬가 소실될 우려도 없어서 입체감도 우수한 새로운 구성의 함침원단을 이용한 엠보싱무늬 벽지의 제조방법 및 이에 의해 제조된 엠보싱무늬를 제공하는 것이다.
SUMMARY OF THE INVENTION The present invention has been made in view of the above problems, and it is an object of the present invention to provide a wallpaper in which a wallpaper is divided into upper and lower parts, Which is excellent in three-dimensional feeling, and a method of manufacturing the embossed pattern wallpaper using the impregnated fabric.
본 발명의 일 특징에 따르면, 다공성 재질의 기재를 준비하는 과정; 준비된 기재를 열가소성 수지와 발포제를 포함하는 발포수지액에 함침시키는 과정; 발포수지액이 함침된 기재를 건조시켜서 함침원단을 제조하는 과정; 함침원단의 상면에 무늬를 인쇄하는 과정; 및 무늬가 인쇄된 함침원단을 가열가압하여 함침원단의 상면에 엠보싱무늬를 형성하는 과정;을 포함하여 이루어진 것을 특징으로 하는 함침원단을 이용한 엠보싱무늬 벽지의 제조방법 및 이에 의해 제조된 벽지가 제공된다.
According to an aspect of the present invention, there is provided a method of manufacturing a semiconductor device, comprising: preparing a substrate made of a porous material; Impregnating the prepared substrate with a foaming resin solution containing a thermoplastic resin and a foaming agent; Drying the substrate impregnated with the foaming resin solution to prepare an impregnated fabric; Printing the pattern on the top surface of the impregnated fabric; And heating and pressing the impregnated fabric imprinted with the pattern to form an emboss pattern on the impregnated fabric. The method of manufacturing embossed pattern wallpaper using the impregnated fabric and the wallpaper produced thereby are provided .
본 발명의 다른 특징에 따르면, 상기 발포수지액에는 옥, 맥반석, 황토, 게르마늄, 일라이트, 숯 중에서 1종 이상이 더 포함된다.
According to another aspect of the present invention, the foaming resin solution further includes at least one of jade, elvan, loess, germanium, ilite and char.
본 발명의 또 다른 특징에 따르면, 상기 엠보싱무늬를 형성하는 과정 후에는 상기 엠보싱무늬가 형성된 함침원단의 상면에 표면보호코팅제를 코팅하는 과정이 더 추가되며, 상기 표면보호코팅제는 우레탄수지, 수성 아크릴수지, 수성 멜라민수지, 수성 생분해성수지 중에서 1종 이상 선택되는 수지 30~60중량%; 물, 메탄올, 에틸알콜 중에서 선택되는 용제 32.8~54.4중량%; 분산제 0.1~0.3중량%; 유화제 0.1~0.3중량%; MEG(Monoethylene Glycol) 3~5중량%; 이산화티타늄 2~5중량%; 수용성 왁스 또는 실리콘계 발수제 2-5중량%;로 이루어진다.
According to still another aspect of the present invention, there is further provided a method for forming an embossing pattern, the method comprising the steps of: coating a surface protection coating agent on an upper surface of the impregnated fabric having the embossing pattern formed thereon; 30 to 60% by weight of a resin selected from a resin, an aqueous melamine resin and an aqueous biodegradable resin; 32.8 to 54.4% by weight of a solvent selected from water, methanol and ethyl alcohol; 0.1 to 0.3% by weight of a dispersant; 0.1 to 0.3% by weight of an emulsifier; 3-5 wt% MEG (Monoethylene Glycol); 2 to 5% by weight of titanium dioxide; 2 to 5% by weight of a water-soluble wax or a silicone-based water-repellent agent.
본 발명의 또 다른 특징에 따르면, 상기 엠보싱무늬를 형성하는 과정 후에는 상기 함침원단의 배면에 배면보호코팅제를 코팅하는 과정이 더 추가되며, 상기 배면보호코팅제는 수성 아크릴수지, 수성 EVA수지, 생분해성수지 중에서 하나 이상으로 선택되는 수지 15~35중량%; 물 10~20중량%; 분산제 0.1~0.2중량%; 이산화티타늄 2~5중량%; 옥, 게르마늄, 맥반석, 일라이트, 황토, 숯분말 중에서 선택되는 하나 이상의 기능성물질 3~5중량%; 탄산칼슘 34.6~69.8중량%; 소포제 0.1~0.2중량%;로 이루어진다.
According to another aspect of the present invention, there is further provided a process for forming a backside protective coating agent on the backside of the impregnated fabric after the process of forming the embossed pattern, wherein the backside protection coating agent is selected from the group consisting of aqueous acrylic resin, aqueous EVA resin, 15 to 35% by weight of a resin selected from at least one of the following resins; 10 to 20% by weight of water; 0.1 to 0.2% by weight of a dispersant; 2 to 5% by weight of titanium dioxide; 3 to 5% by weight of at least one functional material selected from jade, germanium, elvan, ilite, loess, charcoal powder; 34.6 to 69.8% by weight of calcium carbonate; 0.1 to 0.2% by weight of an antifoaming agent.
이상과 같은 구성을 가지는 본 발명은 벽지가 기재에 발포수지액이 함침된 함침원단 단일의 층으로 이루어지기 때문에, 이질의 재료가 적층된 종래의 벽지와 달리 벽지가 재료의 물성차로 인해 말리거나 시공된 벽에서 떨어지는 문제가 발생되지 않는다. In the present invention having the above-described constitution, since wallpaper is made of a single impregnated fabric layer impregnated with a foaming resin solution on a substrate, unlike conventional wallpaper in which a heterogeneous material is laminated, The problem of falling off the wall is not generated.
또한, 본 발명은 기재에 함침된 발포수지액이 발포되어 엠보싱무늬를 형성하기 때문에, 엠보싱무늬의 성형이 용이하고,엠보싱무늬가 소실될 우려가 없고, 엠보싱무늬의 입체감도 우수하다. Further, according to the present invention, since the foamed resin liquid impregnated in the substrate is foamed to form an embossing pattern, the embossing pattern can be easily molded, the embossing pattern is not lost, and the embossing pattern has excellent dimensional accuracy.
뿐만 아니라, 벽지의 상면에 표면보호코팅제가 코팅되어 벽지의 내마모성 및 내오염성이 향상되므로 벽지 시공 후에 벽지가 깨끗한 상태로 오래 유지될 수 있으며, 또한, 함침원단을 이루는 발포수지액에 난연물질이 함유되면 벽지의 난연성이 향상되어 화재시 화재가 번지는 것이 방지되는 등 안정성 확보에도 도움이 된다.In addition, since the surface protection coating agent is coated on the top surface of the wallpaper, the wallpaper is improved in abrasion resistance and stain resistance, so that the wallpaper can be maintained in a clean state for a long time after the wallpaper is applied, and the flame retardant material The flame retardancy of the wallpaper is improved, so that the fire is prevented from spreading in the event of a fire.
또, 함침원단을 이루는 발포수지액에 음이온 및 원적외선방출물질, 탈취물질이 함유되면, 벽지에서 음이온과 원적외선이 방출되어 사용자의 건강에 유익하며, 실내 악취가 탈취되므로 쾌적한 실내환경 조성에도 도움이 된다. Also, when the foamed resin liquid constituting the impregnated fabric contains anion and far-infrared ray emitting substance and deodorant substance, anion and far-infrared rays are emitted from the wallpaper, which is beneficial to the health of the user and also helps to create a pleasant indoor environment .
뿐만 아니라 함침원단의 배면에 배면보호코팅제가 코팅되어 배면보호층(300)이 더 구비되면, 벽지가 열에 의해 수축되는 것과 접착풀에 의해 수축되는 것을 방지되는 장점이 있다.
In addition, if the rear protective coating is coated on the rear surface of the impregnated fabric, if the rear
도 1은 본 발명의 제1실시예에 따른 제조과정을 보인 공정도.
도 2는 상기 실시예에 의해 제조된 벽지의 확대단면도.
도 3은 본 발명의 제3실시예에 의해 제조된 벽지의 확대단면도.
도 4는 본 발명의 제4실시예에 의해 제조된 벽지의 확대단면도.
1 is a process diagram showing a manufacturing process according to a first embodiment of the present invention;
2 is an enlarged cross-sectional view of a wallpaper produced by the above embodiment.
3 is an enlarged cross-sectional view of a wallpaper produced by the third embodiment of the present invention.
4 is an enlarged cross-sectional view of a wallpaper manufactured by the fourth embodiment of the present invention.
이하에서 도면을 참조하여 본 발명의 바람직한 실시예를 설명한다. Hereinafter, preferred embodiments of the present invention will be described with reference to the drawings.
도 1은 본 발명의 제1실시예에 따른 제조공정도이고, 도 2는 본 실시예에 의해 제조된 벽지의 단면도이다. FIG. 1 is a manufacturing process diagram according to a first embodiment of the present invention, and FIG. 2 is a cross-sectional view of a wallpaper manufactured by the present embodiment.
이러한 본 발명은 다음과 같이 제조된다.The present invention is produced as follows.
1) 기재를 준비한다.1) Prepare a substrate.
기재는 벌키한 다공성 재질의 것이 사용되는데, 종이 뿐만 아니라 유리섬유 또는 합성섬유로 제조된 펠트 또는 부직포도 사용가능하다.The base material is made of a bulky porous material. Felt or nonwoven fabric made of glass fiber or synthetic fiber as well as paper can be used.
이러한 기재로는 특히, 열과 수분에 의한 수축율이 적어서 치수안정성이 우수한 것이 사용되는데, 바람직하게는 평균 평량이 30~150g/㎡ 이고, 벌키도 3~7인것이 사용된다.
As such a base material, particularly, a base material having an average basis weight of 30 to 150 g / m < 2 > and a bulkiness of 3 to 7 is preferably used because it has a small shrinkage ratio due to heat and moisture and is excellent in dimensional stability.
2) 준비된 기재에 발포수지액을 함침시킨다.2) Impregnate the prepared substrate with the foaming resin solution.
준비된 기재에 발포수지액을 함침시키는데, 기재를 발포수지액에 디핑하거나 또는 발포수지액을 기재에 도포 및 스퀴징하여 발포수지액이 기재에 함침되도록 한다.The prepared base material is impregnated with a foaming resin solution. The base material is dipped in the foaming resin solution, or the foaming resin solution is applied to the substrate and squeezed to impregnate the substrate with the foaming resin solution.
상기 발포수지액은 열가소성 수지와 발포제를 포함하여 이루어진다. 바람직하게는 발포수지액은 수성 폴리에틸렌수지, 수성 아크릴수지, 수성 EVA수지, 생분해성수지, 아크릴수지 중에서 선택되는 1종 이상의 수지 17~37중량%, 수성 아크릴산수지 4~5중량%, 물 7~15중량%, MEG(Monoethylene Glycol) 4~5중량%, 분산제 0.1~0.3중량%, 소포제 0.2~0.5중량%, 유화제 0.1~0.2중량%, 탄산칼슘 37~60중량%, 이산화티타늄 0.1~15중량%, 발포제 0.1~10중량%로 이루어진다. The foamed resin liquid comprises a thermoplastic resin and a foaming agent. Preferably, the foaming resin liquid comprises 17 to 37% by weight of at least one resin selected from an aqueous polyethylene resin, an aqueous acrylic resin, an aqueous EVA resin, a biodegradable resin and an acrylic resin, 4 to 5% by weight of an aqueous acrylic acid resin, 15 to 15 wt%, MEG (Monoethylene Glycol) 4 to 5 wt%, dispersant 0.1 to 0.3 wt%, defoaming agent 0.2 to 0.5 wt%, emulsifier 0.1 to 0.2 wt%, calcium carbonate 37 to 60 wt%, titanium dioxide 0.1 to 15 wt% By weight, and 0.1 to 10% by weight of a blowing agent.
상기 발포제는 가열시 발포되는 것으로서, 공지된 발포제 중에서 선택된다.
The foaming agent is selected from known foaming agents as being foamed upon heating.
3) 발포수지액이 함침된 기재를 건조시킨다.3) Dry the substrate impregnated with the foaming resin solution.
히팅드럼이나 열풍오븐, IR히터 등과 같은 장치를 이용하여 기재를 건조시킨다. 이와 같이 하면 기재에 발포수지액이 함침된 함침원단이 제조된다.
The substrate is dried using a device such as a heating drum, a hot air oven, an IR heater, or the like. In this way, impregnated fabric impregnated with the foaming resin solution is produced on the base material.
4) 함침원단의 상면에 무늬를 인쇄한다.4) Print pattern on top of impregnated fabric.
그라비아 인쇄 등과 같은 공지된 인쇄방법을 이용하여 다양한 형태의 무늬를 인쇄한다.Various types of patterns are printed using a known printing method such as gravure printing or the like.
5) 무늬가 인쇄된 함침원단에 엠보싱무늬를 형성한다.5) Embossing pattern is formed on impregnated fabric printed with pattern.
프레스 또는 엠보롤러를 이용하여 무늬가 인쇄된 함침원단에 엠보싱무늬를 형성한다. 상기 프레스 또는 엠보롤러의 저면에는 함침원단에 형성할 엠보싱무늬에 대응되는 형상의 오목홈이 형성된다. An embossing pattern is formed on impregnated fabric printed with a pattern using a press or emboss roller. A concave groove having a shape corresponding to the embossing pattern to be formed on the impregnated fabric is formed on the bottom surface of the press or emboss roller.
이러한 프레스 또는 엠보롤러로 함침원단을 가열가압하면 상기 발포수지액에 함유된 발포제에 의해 발포수지액이 발포되는데, 이때 프레스 또는 엠보롤러에 형성된 오목홈에 대응되는 부위만 발포되고, 다른 부위는 프레스 또는 엠보롤러에 눌러서 상향으로 돌출되지 않는다. 따라서 프레스 또는 엠보롤러의 오목홈에 대응되는 형상으로 돌출된 엠보싱무늬가 형성된다.When the impregnated fabric is heated and pressed with such a press or emboss roller, the foaming resin solution is foamed by the foaming agent contained in the foaming resin solution. At this time, only the portion corresponding to the concave groove formed in the press or emboss roller is foamed, Or is pressed against the emboss roller and does not protrude upward. Therefore, an embossing pattern protruding in a shape corresponding to the concave groove of the press or emboss roller is formed.
이와 같은 본 발명에 의해 제조되는 벽지는 도 3에 도시된 바와 같이 기재와 발포수지액이 함침된 함침원단(100)에 엠보싱무늬(110)가 형성되는 것으로서, 벽지가 단일의 층으로 구성된다. 따라서 종래의 벽지와 같이 벽지를 이루는 소재의 물성차로 인해 벽지가 말리거나 시공된 벽체에서 떨어지거나 하는 문제점이 발생되지 않는다. As shown in FIG. 3, the wallpaper according to the present invention has embossed
또한, 열가소성수지에 발포제가 함유뒨 발포수지액이 발포되어 엠보싱무늬를 형성하기 때문에, 엠보싱무늬가 선명하고 소실될 우려도 없어서 입체감도 우수하다.
Further, since the foamed resin liquid containing the foaming agent is foamed in the thermoplastic resin to form the embossing pattern, the embossing pattern is clear and there is no possibility of disappearing, and the three-dimensional feeling is also excellent.
이하에서는 본 발명의 다른 실시예를 설명하되, 전술한 실시예와 동일한 구성 및 효과에 대해서는 설명을 생략한다.Hereinafter, other embodiments of the present invention will be described, and the same structures and effects as those of the above-described embodiments will not be described.
본 발명의 제2실시예에 따르면, 상기 발포수지액에는 옥, 맥반석, 황토, 게르마늄, 일라이트, 숯 중에서 1종 또는 1종 이상이 더 포함된다. 바람직하게는 이들 성분들은 발포수지액에 1~5중량% 정도 포함된다. According to the second embodiment of the present invention, the foaming resin solution further includes at least one of jade, elvan, loess, germanium, ilite and char. Preferably, these components are contained in the foaming resin solution in an amount of 1 to 5% by weight.
이들 성분들이 더 추가되면 이들 성분들에 의해 벽지에서 음이온 및 원적외선이 방출되어 사용자의 건강이 증진되고, 탈취효과도 얻을 수 있다.
When these components are further added, negative ions and far-infrared rays are emitted from the wallpaper by these components, thereby improving the user's health and obtaining a deodorizing effect.
도 3은 본 발명의 제3실시예에 따른 벽지의 확대단면도이다. 본 발명의 제3실시예에 따르면, 함침원단(100)의 상면에는 벽지의 내마모성 및 내오염성을 향상시키기 위한 표면호보코팅제가 코팅되어 형성된 표면보호층(200)이 더 구비된다. 3 is an enlarged cross-sectional view of a wallpaper according to a third embodiment of the present invention. According to the third embodiment of the present invention, the top surface of the impregnated
이 표면보호코팅제는 우레탄수지, 수성 아크릴수지, 수성 멜라민수지, 수성 생분해성수지 중에서 1종 이상 선택되는 수지 30~60중량%, 물, 메탄올, 에틸알콜 중에서 선택되는 용제 32.8~54.4중량%, 분산제 0.1~0.3중량%, 유화제 0.1~0.3중량%, MEG(Monoethylene Glycol)3~5중%량, 이산화티타늄 2~5중량%, 수용성 왁스 또는실리콘계 발수제 2-5중량%로 이루어진다. The surface protective coating agent is a coating composition containing 30 to 60% by weight of a resin selected from urethane resin, aqueous acrylic resin, aqueous melamine resin and aqueous biodegradable resin, 32.8 to 54.4% by weight of a solvent selected from water, methanol and ethyl alcohol, 0.1 to 0.3% by weight of an emulsifier, 0.1 to 0.3% by weight of an emulsifier, 3 to 5% by weight of MEG (monoethylene glycol), 2 to 5% by weight of titanium dioxide, and 2 to 5% by weight of a water-soluble wax or a silicone-
또한, 본 실시예에서는 상기 발포수지액에 난연성 혼합물이 포함된다. 이 난연성혼합물은 수산화칼슘 계통의 광물질 10~14중량%, 수산화알루미늄 계통의 광물질 27~57.6중량%, 안티몬계통의 광물질1~5중량%, 할로겐화합물 10~30중량%로 이루어지며, 상기 발포수지액에 1~5중량% 포함된다. Further, in this embodiment, the flame-retardant mixture is included in the foamed resin solution. This flame retardant mixture is composed of 10 to 14% by weight of calcium hydroxide-based mineral, 27 to 57.6% by weight of aluminum hydroxide-based mineral, 1 to 5% by weight of antimony-based mineral and 10 to 30% by weight of halogen compound, By weight to 1 to 5% by weight.
이와 같이 난연성 혼합물이 발포수지액에 포함되면 벽지의 난연성이 향상되어 화재시 화염이 번지는 것이 방지되는 효과를 얻을 수 있다.
When the flame retardant mixture is contained in the foaming resin solution, the flame retardancy of the wallpaper is improved, and the flame spreading effect is prevented.
도 4는 본 발명의 제3실시예에 따른 벽지의 확대단면도로서, 본 실시예에 따르면, 함침원단(100)의 배면에는 배면보호코팅제가 코팅되어 형성된 배면보호층(300)이 더 구비된다. FIG. 4 is an enlarged cross-sectional view of a wallpaper according to a third embodiment of the present invention. According to this embodiment, a
이 배면보호코팅제는 수성 아크릴수지, 수성 EVA수지, 생분해성수지 중에서 하나 이상으로 선택되는 수지 15~35중량%, 물 10~20중량%, 분산제 0.1~0.2중량%, 이산화티타늄 2~5중량%, 옥, 게르마늄, 맥반석, 일라이트, 황토, 숯분말 중에서 선택되는 하나 이상의 기능성물질 3~5중량%, 탄산칼슘 34.6~69.8중량%, 소포제 0.1~0.2중량%를 혼합된 것이 사용된다. 필요에 따라 이러한 배면보호코팅제에도 상기 난연성 혼합물이 더 포함될 수 있다. Wherein the backside protective coating comprises 15 to 35% by weight of a resin selected from at least one of water-based acrylic resin, aqueous EVA resin and biodegradable resin, 10 to 20% by weight of water, 0.1 to 0.2% by weight of dispersant, 2 to 5% 3 to 5% by weight of at least one functional material selected from the group consisting of jade, germanium, elvan, ilite, loess, and charcoal powder, 34.6 to 69.8% by weight of calcium carbonate and 0.1 to 0.2% by weight of defoamer. If necessary, such a flame-retardant mixture may further be included in such a back-protecting coating.
이러한 보호코팅층은 벽지 시공시에 벽지가 열에 의해 수축되는 것과 접착풀에 의해 수축되는 것을 방지하기 위한 것이다.
Such a protective coating layer is intended to prevent the wallpaper from being shrunk by heat and shrinking by the adhesive pool during wallpapering.
100. 함침원단 110. 엠보싱무늬
200. 표면보호층 300. 배면보호층100.
200.
Claims (5)
준비된 기재를 열가소성 수지와 발포제를 포함하는 발포수지액에 함침시키는 과정;
발포수지액이 함침된 기재를 건조시켜서 함침원단을 제조하는 과정;
함침원단의 상면에 무늬를 인쇄하는 과정; 및
상기 무늬가 인쇄된 함침원단의 발포수지액을 발포시켜서 엠보싱무늬를 형성하는 과정;을 포함하여 이루어지며.
상기 엠보싱무늬를 형성하는 과정은,
오목홈이 형성된 엠보롤러로 상기 무늬가 형성된 함침원단의 상면을 가열가압하여 함침원단의 발포수지액을 발포시키되, 상기 발포수지액이 발포되면서 상기 엠보롤러의 오목홈에 대응되는 부위만 상향으로 돌출되어 엠보싱무늬가 형성되는 것을 특징으로 하는 함침원단을 이용한 엠보싱무늬 벽지의 제조방법.
Preparing a substrate made of a porous material;
Impregnating the prepared substrate with a foaming resin solution containing a thermoplastic resin and a foaming agent;
Drying the substrate impregnated with the foaming resin solution to prepare an impregnated fabric;
Printing the pattern on the top surface of the impregnated fabric; And
And foaming the foaming resin solution of the impregnated fabric having the pattern printed thereon to form an embossing pattern.
The process of forming the embossed pattern includes:
The upper surface of the impregnated fabric having the pattern is heated and pressed by the emboss roller provided with the concave groove to foam the foamed resin liquid of the impregnated fabric, and only the portion corresponding to the concave groove of the emboss roller protrudes upward Wherein the embossing pattern is formed on the embossed patterned wallpaper.
상기 발포수지액에는 옥, 맥반석, 황토, 게르마늄, 일라이트, 숯 중에서 1종 이상이 더 포함된 것을 특징으로 하는 함침원단을 이용한 엠보싱무늬 벽지의 제조방법.
The method according to claim 1,
Wherein the foaming resin solution further contains at least one of jade, elvan, loess, germanium, ilite, and char.
상기 엠보싱무늬를 형성하는 과정 후에는,
상기 엠보싱무늬가 형성된 함침원단의 상면에 표면보호코팅제를 코팅하는 과정이 더 추가되며,
상기 표면보호코팅제는 우레탄수지, 수성 아크릴수지, 수성 멜라민수지, 수성 생분해성수지 중에서 1종 이상 선택되는 수지 30~60중량%, 물, 메탄올, 에틸알콜 중에서 선택되는 용제 32.8~54.4중량%, 분산제 0.1~0.3중량%, 유화제 0.1~0.3중량%, MEG(Monoethylene Glycol)3~5중량%, 이산화티타늄 2~5중량%, 수용성 왁스 또는 실리콘계 발수제 2-5중량%로 이루어진 것을 특징으로 하는 함침원단을 이용한 엠보싱무늬 벽지의 제조방법.
3. The method according to claim 1 or 2,
After the process of forming the embossing pattern,
Further comprising the step of coating a surface protective coating agent on the top surface of the impregnated fabric having the emboss pattern,
Wherein the surface protective coating agent comprises 30 to 60% by weight of a resin selected from urethane resin, aqueous acrylic resin, aqueous melamine resin and aqueous biodegradable resin, 32.8 to 54.4% by weight of a solvent selected from water, methanol and ethyl alcohol, 0.1 to 0.3% by weight of an emulsifier, 0.1 to 0.3% by weight of an emulsifier, 3 to 5% by weight of MEG (monoethylene glycol), 2 to 5% by weight of titanium dioxide, and 2-5% by weight of a water- Method of manufacturing embossed pattern wallpaper using.
상기 엠보싱무늬를 형성하는 과정 후에는,
상기 함침원단의 배면에 배면보호코팅제를 코팅하는 과정이 더 추가되며,
상기 배면보호코팅제는 수성 아크릴수지, 수성 EVA수지, 생분해성수지 중에서 하나 이상으로 선택되는 수지 15~35중량%; 물 10~20중량%; 분산제 0.1~0.2중량%; 이산화티타늄 2~5중량%; 옥, 게르마늄, 맥반석, 일라이트, 황토, 숯분말 중에서 선택되는 하나 이상의 기능성물질 3~5중량%; 탄산칼슘 34.6~69.8중량%; 소포제 0.1~0.2중량%;로 이루어진 것을 특징으로하는 함침원단을 이용한 엠보싱무늬 벽지의제조방법.
3. The method according to claim 1 or 2,
After the process of forming the embossing pattern,
Further comprising the step of coating a rear surface protective coating agent on the back surface of the impregnated fabric,
The backside protective coating agent comprises 15 to 35% by weight of a resin selected from at least one of an aqueous acrylic resin, an aqueous EVA resin, and a biodegradable resin; 10 to 20% by weight of water; 0.1 to 0.2% by weight of a dispersant; 2 to 5% by weight of titanium dioxide; 3 to 5% by weight of at least one functional material selected from jade, germanium, elvan, ilite, loess, charcoal powder; 34.6 to 69.8% by weight of calcium carbonate; And 0.1 to 0.2% by weight of an antifoaming agent.