Abstract

The present invention relates to a safety sign sheet and a manufacturing method thereof. The safety sign sheet is formed by applying a seat member made of a polyester (PE) material to a safety sign plate of a telephone pole. The sheet member is molded to have a single color; has physical properties reinforced by an electron beam crosslinking process; has improved signal legibility and retro-reflection by a safety indication pattern formed on the surface thereof using a hologram film sheet; and is conveniently installed by a geared band coupling means. As a practical means, the safety sign sheet comprises: a concave-convex coupling part and an auxiliary coupling projection formed on a monochrome sheet member; a concave-convex fixating member prepared as an auxiliary means to fixate the sheet on the outer circumferential surface of a telephone pole; and a hologram film sheet attached to the surface of the sheet. In addition, the manufacturing method thereof comprises processes of: injecting a pigment; stirring the pigment; molding a sheet; forming a connection; cross-linking the sheet; and finishing a product.

Description

[0001] The present invention relates to a sheet for road safety indication,

본 발명은 도로 안전표시용 시트에 관한 것으로, 더욱 상세하게는, 차량 또는, 보행자를 안전하게 유도하기 위해 설치되는 도로 안전표시판의 구성을, 표면에 홀로그램 필름지가 합지되고, 이면에 접착면이 형성된 유동성 시트로 형성되게 하여, 각종 도로안전표시판의 종류, 예컨대, 전신주, 도로경계석, 교통표시판 등은 물론 각종 광고표시판에 이르기까지, 그 표시판의 용도 내지 구조적 특성에 구애받음 없이, 범용적 형태로 적용하여 설치할 수 있도록 한 도로 안전 표시용 시트 및 그 시트의 제조방법에 관한 것이다. BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a road safety indicator sheet, and more particularly, to a road safety indicator panel which is installed for safely guiding a vehicle or a pedestrian by using a hologram film having a surface coated with a hologram film, The present invention can be applied to a variety of road safety display boards such as a telephone pole, a road boundary seat, a traffic signboard, and various advertisement signboards in a universal form without being limited by the use or structural characteristics of the signboard And a method of manufacturing such a sheet.

일반적으로 안전표시판이라 함은, 차량 운전자, 또는 보행자의 주의가 현저히 요구되는 장소, 예컨대, 차도, 인도, 각종 도로 공사구간 등, 위험상황이 예견되는 생활환경 곳곳에, 시인성이 높은 표식형태로 설치되는, 도로 안전 시설물의 일종임을 알 수 있다.Generally, the term "safety sign" refers to a place where a driver or a pedestrian is conspicuously required, such as a road, a road, a road, etc. It is a kind of road safety facilities.

따라서, 이와 같이, 설치되는 도로 안전표시판은, 차량운전자, 혹은, 보행자의 시선을 유도하여, 그들 차량운전자 및 보행자의 주의를 환기되게 함으로써, 안전하고 원활하게 교통 흐름을 확보함과 동시에, 도로구조의 보전(保全)을 도모하고, 아울러, 차량과 차량, 또는, 차량과 보행자 간 충돌, 예컨대, 각종 교통사고 및 안전사고로부터 인명과 재산을 보호하는 역할을 수행하게 되는 것인바;Thus, the road safety signboard thus installed induces the eyes of the vehicle driver or the pedestrian so as to attract the attention of the vehicle driver and the pedestrian, thereby securing the traffic flow safely and smoothly, and at the same time, And also protects people and property from collision between vehicles and vehicles or pedestrians such as various traffic accidents and safety accidents;

이에, 이러한, 특성을 갖는 도로 안전표시판의 종류별 구성을 몇 가지 예로서 살펴보면, 이는, 도로에 설치된 전신주와 차량의 충돌을 예방하기 위한 전신주용 안전표시판, 차량의 주행 경로를 안전하게 유도하여 차선 이탈을 예방토록 하는 도로 경계석, 기타, 안전하고 원활한 교통 흐름 확보를 위한 다양한 표식 형태의 교통 표시판 등이 있음을 알 수 있다. As a result, it is possible to prevent a collision between a telephone pole and a vehicle installed on a road, a safety sign for a telephone pole, a safe driving route of the vehicle, Road barriers to prevent traffic accidents, and traffic sign boards in various forms for securing safe and smooth traffic flow.

또한, 여기서, 전술한 바와 같은, 다양한 형태의 도로 안전표시판 중, 특히, 전신주용 안전표시판의 구성을 살펴보면, 이는, 1mm 내외의 두께를 갖는 얇은 금속판재의 표면에 바탕색을 이루는 노란색의 축광 도료를 도색하고, 그 노란색 바탕 위에 검은색 축광 도료를 이용하여, 재차, 빗금형태의 반사 띠를 도색처리에 의해 형성하며, 여기에 더하여, 필요에 따라 "위험"이라는 문자를 표시한 상태하에, 그 금속판재로 이루어진 안전표시판을, 전신주의 형상, 예컨대, 원기둥 형상에 맞도록 밴딩처리한 후, 별도의 금속재 체결밴드를 이용하여, 고정 설치하는 구조를 취하는 것으로, 이는, 대한민국 특허청에 선출원 공개(실용신안공개 제1999-012627호)된 기술 등에 일부 포함되어 개시된 바 있다. Here, among the various types of road safety signboards as described above, in particular, the construction of a safety signboard for a telephone pole will be described. This means that a yellow phosphorescent material that forms a ground color on the surface of a thin metal sheet material having a thickness of about 1 mm And a reflective coating of a hatched shape is again formed by painting using a black phosphorescent paint on the yellow background. In addition, under the condition of displaying the letter "DANGER" if necessary, The safety display panel made of a plate material is subjected to a bending process so as to conform to the shape of a pole, for example, a columnar shape, and then fixed by using a separate metal material fastening band. Open Publication No. 1999-012627) and the like.

하지만, 전술한 바와 같은, 종래 전신주용 안전표시판은, 금속판재를 전신주의 외경형상에 맞추어 밴딩 처리해야 함에 따라, 그 설치작업이 매우 난해하고, 작업중 날카로운 금속판재 모서리 등에 작업자가 상해를 입을 수 있는 등, 일련의 설치과정에 있어 상당한 안전상의 문제점을 주는 것이었으며, 특히, 이러한, 안전표시판은 외부환경에 항상 노출되어 있는 설치 특성을 갖는 것임에도 불구하고, 그 재질이 금속판재로 이루어짐에 따라 눈,비,바람 먼지 등에 의해 쉽게 부식됨은 물론, 도색된 축광도료가 쉽게 벗겨지는 현상을 유발함으로 인해, 유지보수 및 관리 비용이 과다소모될 수밖에 없는 상당한 경제성 저하의 문제점을 주는 것이었다.However, as described above, the conventional safety signboard for a telephone pole has a problem in that the installation work is very difficult due to the bending process of the metal plate material in accordance with the outer diameter of the electric wire, and the worker may be injured in the sharp metal plate corner And the like. In particular, although the safety signboard has the installation characteristic that is always exposed to the external environment, the safety signboard is formed of a metal plate, , Rain, wind dust, and the like, as well as causing a phenomenon in which the painted phosphorescent paint easily peels off, resulting in a problem of a significant economic deterioration which is inevitably excessive in maintenance and management costs.

한편, 또 다르게, 전술한 바와 같은, 안전표시판(전신주용 안전표시판)은, 표면의 반사 띠가, 축광 도료에 의해 형성된 것으로, 이에, 축광 도료의 물질 특성상, 재귀반사 기능이 제한된 각도범위로만 이루어짐에 따라 차량 불빛에 대한 반사력이 상대적으로 낮을 수밖에 없는 단점을 주는 것이었으며, 이로 인해, 특히 야간의 차량운전자에게 피로감을 주어, 사고발생률을 높이게 되는 문제점 또한 상존되게 하는 것이었다. On the other hand, as described above, the safety display panel (safety display panel for a telephone main body) is formed by a phosphorescent coating on the surface thereof, and thus the retroreflective function is limited to the angle range limited by the material properties of the phosphorescent paint. , The reflection power against the vehicle light is relatively low, which causes fatigue to the driver of the vehicle at night, thereby causing the problem of increasing the incidence of accidents.

따라서, 본 발명은 종래 전신주용 안전표시판의 제반적인 문제점을 해결하고자 창안된 것으로;SUMMARY OF THE INVENTION Accordingly, the present invention has been made to solve the conventional problems of the conventional safety pole for a telephone pole,

본 발명의 목적은, 차량 또는, 보행자를 안전하게 유도하기 위해 설치되는 전신주용 안전표시판을, 유동성을 갖는 폴리에스테르(P.E) 소재의 시트 구성으로 형성하되, 그 시트의 구성을 바탕색이 일체로 형성 표출되는 단색 컬러색상으로 성형함과 동시에, 전자선 가교 처리에 의해 물리적 특성을 강화시키고, 여기에, 더하여, 상기 유동성 시트의 표면에, 홀로그램 필름지를 이용한 안전표시 문양의 표현으로서, 시인성과 재귀반사 기능을 향상토록 하며, 아울러, 안전표시판의 설치 형태를, 치합형 밴드체결 수단에 의해 이루어지도록 하여, 설치작업의 편리성 또한 부여되도록 한 도로 안전표시용 시트 및 그 시트의 제조방법을 제공함에 있다. SUMMARY OF THE INVENTION An object of the present invention is to provide a safety panel for a vehicle or pedestrian, which is installed to safely guide a vehicle or a pedestrian, into a sheet structure of a polyester (PE) material having fluidity, And the physical properties are enhanced by electron beam cross-linking treatment. In addition, visibility and retroreflective function are provided on the surface of the fluid sheet as a representation of the safety mark using the holographic film sheet The present invention also provides a road safety indicator sheet and a method of manufacturing the same, which can provide a safety indicator panel with an attachment type band fastening means and also provide convenience of installation work.

한편, 본 발명의 또 다른 목적은, 전신주용 안전표시판의 구성을 유동성 소재의 시트로 형성하여, 그 적용 대상을 어느 하나의 안전표시시설물, 예컨대, 전신주용 안전표시판에 한정함 없이, 필요에 따른 재단작업과, 홀로그램 필름지를 이용한 가변적 안전표시 문양의 표현, 그리고, 부가적 구성인 점착면 형성을 통해 도로경계석, 또는, 기타 다양한 형태의 교통안전표시판, 또는 각종 광고표시판에 범용적으로 이용가능하도록 하여, 사용효율성을 증대되도록 한 도로 안전표시용 시트 및 그 시트의 제조방법을 제공함에 있다. It is still another object of the present invention to provide a safety display panel for a telephone pole, which is formed of a sheet of a fluid material and is applicable to any safety display facility, for example, It can be widely used in various types of traffic safety signboards or various advertisement signboards by cutting work, expression of variable safety mark using hologram film, and adhesion surface formation as an additional constituent. Thereby improving the efficiency of use, and a method of manufacturing such a sheet.

이에, 상기 목적을 달성하기 위한 본 발명에 따른 도로 안전표시용 시트 및 그 시트 제조방법의 바람직한 수단으로는;In order to accomplish the above object, according to a preferred aspect of the present invention,

단색 컬러 색상을 갖는 시트부재에 요철 체결부와 보조 체결돌기를 형성시키고, 상기 시트부재를 전신주 외경면에 설치하기 위한 보조수단으로, 요철고정밴드를 더 마련토록 하며, 재차, 상기 시트부재 표면에 홀로그램 필름지를 더 부착시켜, 전신주용 안전표시판을 형성함으로써, 달성된다. A concave-convex fastening portion and an auxiliary fastening protrusion are formed on the sheet member having a monochromatic color hue, and further provided with a concave-convex fixing band as an auxiliary means for mounting the sheet member on the outer surface of the poles, And further attaching a holographic film sheet to form a safety label for a telephone pole.

또한, 상기 시트부재를 형성하는 방법으로서, 안료투입과정과, 안료 교반과정과, 시트 성형과정과, 체결부 성형과정과, 시트부재 가교처리 과정과, 제품마감과정을 행하도록 하여 달성된다. Further, as a method of forming the sheet member, a pigment input process, a pigment stirring process, a sheet forming process, a fastener forming process, a sheet member crosslinking process, and a product finishing process are performed.

따라서, 상기 본 발명에 따른 도로 안전표시용 시트 및 그 시트의 제조방법은, 전신주용 안전표시판을 유동성 시트부재로 형성하되, 그 시트부재의 구성을 단색 컬러의 바탕색을 갖도록 성형함과 동시에, 전자선 가교 처리에 의해 물리적 특성을 강화시키고, 여기에, 더하여, 홀로그램 필름지를 이용한 안전표시 문양의 표현으로서, 시인성과 재귀반사 기능을 향상되게 한 것임은 물론, 상기 시트부재로 이루어진 안전표시판의 설치 형태를, 치합형 밴드체결 수단에 의해 이루어지도록 하여, 설치작업의 편리성 또한 부여되도록 한 것이며; Accordingly, the present invention provides a road safety indicator sheet and a method of manufacturing the same, wherein the safety indicator plate for a telephone pole is formed of a fluid sheet member, the structure of the sheet member is shaped to have a base color of monochromatic color, The physical property is strengthened by the crosslinking treatment and the visibility and retroreflective function are improved as a representation of the safety mark using the holographic film sheet as well as the installation form of the safety display panel made of the sheet member And a pair of clamping band fastening means so as to provide convenience of installation work;

또 다르게, 전신주용 안전표시판의 구성을 유동성 소재의 시트부재로 형성 함으로써, 그 적용 대상을 어느 하나의 안전시설물, 예컨대, 전신주용 안전표시판에 한정함 없이, 필요에 따른 재단작업과, 홀로그램 필름지를 이용한 가변적 안전표시 문양의 표현, 그리고, 부가적 구성인 점착면 형성을 통해 도로경계석, 또는, 기타 다양한 형태의 교통안전표시판, 또는 광고표시판 등에 범용적으로 이용가능하도록 하여, 사용효율성을 증대되도록 한 것으로, 이는 매우 유용한 기대효과를 제공한다.Alternatively, by forming the structure of the safety signboard for a telephone pole from a sheet member of a fluid material, it is possible to apply a cutting operation as needed, and a hologram film sheet, without limiting the application target to any safety facility, The expression of the variable safety mark used, and the formation of the adhesive surface, which is an additional constituent, can be widely used for road barrier seats, or various other types of traffic safety sign boards or advertisement sign boards, Which provides a very useful anticipatory effect.

도 1은 본 발명에 따른 도로 안전표시용 시트의 분해사시도
도 2는 본 발명에 따른 도로 안전표시용 시트의 결합사시도
도 3은 본 발명에 따른 도로 안전표시용 시트의 설치상태도
도 4는 본 발명에 따른 도로 안전표시용 시트의 또 다른 실시예도
도 5는 본 발명에 따른 도로 안전표시용 시트의 또 다른 제조공정 순서도1 is an exploded perspective view of a road safety indicator sheet according to the present invention.
Fig. 2 is a perspective view showing a combination of a seat for road safety indication according to the present invention
Fig. 3 is a view showing an installation state of a road safety indication sheet according to the present invention
Fig. 4 shows another embodiment of the road safety indication sheet according to the present invention
5 is a flowchart showing another manufacturing process of the road safety indication sheet according to the present invention.

이하, 본 발명에 따른 도로 안전표시용 시트 및 그 시트의 제조방법의 바람직한 실시예 구성을 첨부도면에 의거하여 상세히 설명하기로 한다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, preferred embodiments of a road safety display sheet and a method of manufacturing the same according to the present invention will be described in detail with reference to the accompanying drawings.

이에, 첨부도면을 참고로 하여, 본 발명에 따른 도로 안전표시용 시트의 개략적인 구성을 살펴보면;Hereinafter, with reference to the accompanying drawings, a schematic configuration of a seat for road safety display according to the present invention will be described;

이는, 시트부재(1)와, 요철고정밴드(2), 그리고, 홀로그램 필름지(3)로 구성된다.This is constituted by the sheet member 1, the concave-convex fixing band 2, and the holographic film sheet 3.

여기서, 먼저 상기 시트부재(1)는, 유동성을 갖는 폴리에스테르 소재의 구성으로서, 이에, 이와 같은, 시트부재(1)를 본 발명에 적용함에 있어서는, 시트부재(1) 성형시, 그 시트부재(1) 성형원료에 축광안료를 첨가하여, 단색의 컬러 색상, 예컨대, 노란색, 파란색, 빨간색 등과 같은 다양한 컬러의 바탕색을 일체로 표출되도록 하고, 상기 컬러 색상을 갖으면 형성된 시트부재(1)의 표면 상,하 단부에 도 1 또는 도 2로 도시된 바와 같이, 띠 형상을 이루며, 대칭되는 한쌍의 요철 체결부(11)(11')를 일체로 형성하며, 재차, 상기 시트부재(1)의 중앙 좌,우 양측 단부에 대칭되는 한쌍의 보조 체결돌기(12)(12')를 일체로 더 형성함이 바람직하다.Here, first, the sheet member 1 is made of a polyester material having fluidity, and when such a sheet member 1 is applied to the present invention, at the time of molding the sheet member 1, (1) A phosphorescent pigment is added to a molding material so that a base color of various colors such as a monochromatic color hue, for example yellow, blue, red, etc., is integrally expressed, and the color of the sheet member 1 A pair of symmetrical concavo-convex coupling portions 11 and 11 'are integrally formed on the upper surface and the lower end of the sheet member 1 as shown in Fig. 1 or Fig. 2, And a pair of auxiliary fastening protrusions 12 and 12 'which are symmetrical to both the center left and right end portions of the main body 10 are formed integrally.

이때, 시트부재(1)로 형성되는 요철 체결부(11)(11')는, 평기어 같은 형태, 예컨대, 삼각 또는 사각형상의 돌기가, 규칙적이고 반복적인 형태로 배열되는, 기어의 이빨과 같은 형상으로 구성되는 것이다.
At this time, the concave-convex coupling portions 11 and 11 'formed by the sheet member 1 are formed in a shape of a spur gear, for example, a triangular or quadrangular projection, arranged in a regular and repetitive manner, Shape.

또한, 상기 요철고정밴드(2)는, 전술한 시트부재(1)를 전신주의 외경면에 설치 고정하기 위한 별도의 독립적 부품구성으로 마련되는 것인바, 이에, 이와 같은, 요철고정밴드(1)는, 유동성을 갖는 소정길이의 띠 형상을 취하며, 그 요철고정밴드(2) 내측 전면에, 도 1 또는 도 2로 도시된 바와 같이, 치합돌기면(21)을 일체로 형성하고, 요철고정밴드(2)의 좌,우 양측 단부에 한쌍의 고정스톱퍼(22)(22')를 일체로 더 형성하며, 상기 한쌍의 고정스톱퍼(22)(22')를 대칭구조로 밀착되게 한 후, 압착걸림 구조로 연결되게 하는 독립적 부품구성의 체결클립(C)을 더 구비토록 함이 바람직하다.
The concavo-convex fixing band 2 is provided with a separate independent component structure for fixing and fixing the above-described sheet member 1 to the outer diameter surface of the electric pole. 1 and 2, a coupling projecting surface 21 is integrally formed on the entire inner surface of the concave-convex fixing band 2, A pair of fixed stoppers 22 and 22 'are integrally formed on both left and right ends of the band 2 so that the pair of fixed stoppers 22 and 22' It is preferable to further include a fastening clip (C) of an independent component structure for making a connection with a crimp engagement structure.

끝으로, 상기 홀로그램 필름지(3)는, 다양한 각도에서 물체의 모습을 3차원 입체상으로 재생토록 하는 일반적 형태의 물품구성으로서, 이와 같은, 홀로그램 필름지는, 필름지의 표면에 0.2 ~ 0.3 마이크로m의 깊이로 홈을 새기고, 그 미세한 홈에 의해 빛을 굴절되게 하여, 보는 각도에 따라 반사되는 빛의 색깔, 형태를 틀리게 함으로서, 마치 3차원의 영상이 있는 듯한 착각이 일으키게 하는 물품 특성을 갖는 것인바, 이에, 이와 같은, 홀로그램 필름지(3)를 본 발명에 적용함에 있어서는, 그 홀로그램 필름지를 안전표시를 나타내는 문양으로 재단하여 이용함이 바람직하다.Finally, the hologram film sheet 3 is a general form of an article structure for regenerating a three-dimensional stereoscopic image of an object at various angles. Such a hologram film sheet is a film sheet having a thickness of 0.2 to 0.3 μm It is possible to make an illusion that a three-dimensional image is produced by engraving a groove with a depth and refracting the light by the fine groove to make the color and shape of the light reflected according to the viewing angle wrong, Therefore, when such a holographic film sheet 3 is applied to the present invention, it is preferable to cut the holographic film sheet into a pattern indicating a safety mark.

이때, 홀로그램 필름지(3)의 이면은, 일반적인 스티커와 같이, 접착면(31)이 필수 구성요소로 구비되는 것이다.
At this time, the back surface of the holographic film sheet 3 is provided with the adhesive surface 31 as an essential component like a general sticker.

따라서, 전술한 바와 같은, 일련의 구성을 상호 결합하여, 전신주용 안전표시판을 형성, 설치함에 있어서는;Therefore, in forming and installing the safety display panel for a telephone main body by combining a series of components as described above,

먼저, 바탕색을 갖는 시트부재(1)의 표면에, 안전표시판임을 나타내는 문양, 예컨대, 도 2로 도시된 바와 같은, 홀로그램 필름지(3)를 사선형 줄무늬 형상으로 재단하여, 그 재단된 홀로그램 필름지(3)를, 접착면(31)을 이용하여, 상기 시트부재(1) 표면에 배열 부착시킴으로서, 전신주용 안전표시판을 형성한다.First, a hologram film 3 is cut out in a shape of a quadrilateral stripe pattern as shown in Fig. 2, for example, on the surface of the sheet member 1 having a ground color, 3 are arranged on the surface of the sheet member 1 by using the adhesive surface 31 to form a safety sign for a telephone pole.

이어, 상기와 같이, 전신주용 안전표시판 형성된 시트부재(1)를, 전신주에 설치함에 있어서는, 먼저, 유동성을 갖는 시트부재(1)를, 도 3으로 도시된 바와 같이, 전신주 외경면에 감아 돌려 밀착시킨다.Next, as described above, when the seat member 1 having the safety indicator for the telephone pole is installed on the telephone pole, first, the seat member 1 having the fluidity is wound around the outer surface of the telephone main body as shown in Fig. 3 And is brought into close contact.

이에, 상기와 같이 시트부재(1)가 전신주 외경면에 감김된 형태로 밀착될 경우, 시트부재(1)의 중앙 좌,우 양측 단부로 형성된 한쌍의 보조 체결돌기(12)(12')는 서로 맞대어진 형태를 취하게 되는 것인바, 따라서, 이와 같이, 맞대어진 한쌍의 보조체결돌기(12)(12')를 도 3으로 도시된 바와 같이, 별도 마련된 체결클립(C)에 의해 압박 연결고정하여, 시트부재(1)의 가 설치상태를 이루도록 한 상태하에, 재차, 시트부재(1)의 상,하 단부로 형성된 요철 체결부(11)(11')에, 요철고정밴드(2)를 치합구조로 밀착시켜 감아 돌리고, 그와 같이, 감아 돌려진 요철고정밴드(2)의 고정스톱퍼(22)(22'), 예컨대, 도 3으로 도시된 바와 같이, 맞대어진 한쌍의 고정스톱퍼(22)(22')를, 상기 보조체결돌기(12)(12')의 결합구조와 동일한 형태로, 별도 마련된 체결클립(C)에 의해 압박 연결 고정함으로서, 전신주용 안전표시판의 설치상태를 마무리 하게 되는 것이다.
When the sheet member 1 is brought into close contact with the outer surface of the main body of the telephone, as described above, the pair of auxiliary fastening protrusions 12 and 12 'formed at the left and right ends of the center of the sheet member 1 The pair of auxiliary fastening protrusions 12 and 12 'abutted against each other are pressed against each other by a separate fastening clip C as shown in FIG. 3, The uneven fastening band 2 is fixed to the uneven fastening portions 11 and 11 'formed at the upper and lower ends of the sheet member 1 again under the condition that the sheet member 1 is set in a state of being fixed, The fixing stoppers 22 and 22 'of the concave-convex fixing band 2, for example, as shown in Fig. 3, are brought into close contact with each other by a pair of fixed stoppers 22) 22 'are formed in the same shape as the coupling structure of the auxiliary clamping protrusions 12, 12' by a separate clamping clip C, So, that would finish the installation state of safety signs for the telephone pole.

또한, 도 4는 본 발명에 따른 도로 안전표시용 시트의 또 다른 실시예도로서, 이와 같은, 또 다른 실시예로서의 본 발명은, 전술한 일실예 구성에 있어, 시트부재(1)의 이면에 점착면(13)을 형성하고, 상기 점착면(13)을 보호하는 이형지(14)를 더 부착시킨 형태로 구성함이 바람직하다.4 is a view showing still another embodiment of the road safety indication sheet according to the present invention. In the above-described embodiment of the present invention, in the above-described embodiment, (14) for protecting the pressure-sensitive adhesive surface (13) is further attached to the pressure-sensitive adhesive layer (13).

이에, 이와 같은, 이실시예로 형성되는 시트부재(1)는, 전술한 일실예와 같이, 전신주용 안전표시판에 한정됨 없이, 그 시트부재(1)를 다양한 형성과 모양으로 선택적 재단하여, 다양한 형태의 안전표시시설물, 예컨대, 도로경계석, 교통안전표시판, 공사위험 표시판 등에, 이형지(14)를 분리시킨 형태의, 접착식 구조로 설치 이용할 수 있는 것으로, 이 또한 본 발명의 범주에서 벗어나는 것은 아니다. As described above, the sheet member 1 formed in this way is not limited to the safety display panel for a telephone main body, but can be selectively cut in various forms and shapes, Type safety display facility such as a road barrier seat, a traffic safety signboard, a construction hazard signboard, and the like, which are separated from the release paper 14 and which can be used in a sticky structure.

한편, 전술한 바와 같은, 일련의 결합구성 및 설치 이용관계를 갖는, 본 발명에 따른 도로 안전표시용 시트는, 또 다른 차별화된 기술형태의 제조방법으로 형성되는 것인바, 이에, 이와 같은, 도로 안전표시용 시트의 제조방법을 살펴보면;On the other hand, the road safety indication sheet according to the present invention, which has the above-described series of combined construction and installation use relationship, is formed by a manufacturing method of another differentiated technical form, A manufacturing method of the safety indicator sheet will be described.

이는, 도 6으로 도시된 바와 같이, 안료투입과정(S1)과, 안료 교반과정(S2)과, 시트 성형과정(S3)과, 체결부 성형과정(S4)과, 시트부재 가교처리 과정(S5)과, 제품마감과정(S6)을 통해 이루어진다.6, the pigment is injected in step S1, pigment agitation step S2, sheet forming step S3, fastening part forming step S4, sheet member crosslinking step S5 ) And a product finishing process (S6).

여기서, 먼저, 상기 안료투입과정(S1)은, 통상의 폴리에스테르 시트의 제조방법, 예컨대, 열가소성 고분자인 폴리에스테르 중합물을 용융 압출과정을 통해 성형하여 유동성 시트를 제조하는 통상의 방법에 있어서, 상기 성형 되기 전의 용융된 폴리에스테르 중합물에, 노란색, 초록색, 빨간색 등, 단색의 컬러색상을 갖는 수지용 축광안료를 첨가하는 과정으로 이루어지도록 함이 바람직하다.Herein, the pigment introduction step (S1) is a conventional method for producing a polyester sheet, for example, a method for producing a fluidized sheet by molding a polyester polymer, which is a thermoplastic polymer, through a melt extrusion process, It is preferable to add a phosphorescent pigment for a resin having a monochromatic hue such as yellow, green, and red to the melted polyester polymer before molding.

여기서, 축광안료는, 내부에 빛을 흡수해 저장하고, 발광,방출하는 성질을 지닌 통상의 안료로서, 이와 같은, 축광안료의 첨가는, 폴리에스테르 중합물의 전체 중량에 대하여, 1~5%의 중량비율로 첨가하도록 한다.
Here, the phosphorescent pigment is a conventional pigment having a property of absorbing and storing light and emitting and emitting light, and the addition of such a phosphorescent pigment is preferably carried out in an amount of 1 to 5% of the total weight of the polyester polymer Weight ratio.

또한, 상기 안료 교반과정(S2)은, 축광안료가 첨가된 용융된 폴리에스테르 중합물을, 전기적 에너지에 의해 고온의 발열작용을 행하는 통상의 산업용 교반기에 투입하여, 30분 이상의 교반작동 관계를 통해, 상기 축광안료와 폴리에스테르 중합물을 균일하게 혼합처리하는 과정으로 이루어지게 함이 바람직하다.
In the pigment agitation step (S2), the molten polyester polymer to which the phosphorescent pigment is added is put into a conventional industrial stirrer for performing a high-temperature exothermic action by electrical energy, and stirred for 30 minutes or more, And a step of mixing the phosphorescent pigment and the polyester polymer uniformly.

또한, 상기 시트 성형과정(S3)은, 전술한 안료 교반과정(S2)을 통해 혼합 교반된, 폴리에스테르 중합물을, 용융압출장치에 투입하여, 압출 성형을 통해 유동성을 갖는 시트부재(1)를 형성하는 과정으로 이루어지게 함이 바람직하다.
The sheet molding process (S3) is a process in which the polyester polymer mixed and stirred through the above-described pigment stirring process (S2) is put into a melt extrusion apparatus and extruded to form a sheet member (1) having fluidity And a process of forming the above-described structure.

또한, 상기 체결부 성형과정(S4)은, 전술한 시트 성형과정(S3)을 통해, 용융압출장치로부터 성형 배출되는 시트부재(1)를 컨베어어 흐름방식에 의해, 통상의 산업용 가압 롤링 성형장치로 투입하고, 이와 같이, 투입된 시트부재(1)를 상기 가압 롤링 성형장치에 의한 압착가공에 하여, 시트부재(1)의 표면 상,하 단부에 상호 대칭되는 한쌍의 요철 체결부(11)(11')를 형성하는 과정으로 이루어지게 함이 바람직하다.The fastening part forming step S4 is a step of forming the sheet member 1 which is formed and discharged from the melt extruding device through the above-described sheet forming step S3 by a conveyor flow method, And a pair of concave-convex fastening portions 11 (hereinafter referred to as " concave fastening portions 11 ") which are symmetrical to each other on the surface and the lower end portion of the sheet member 1 are formed by pressing the inserted sheet member 1 by the above- 11 ').

또한, 상기 시트부재 가교처리 과정(S5)은, 전술한 체결부 성형과정(S4)을 통해 형성된 시트부재(1)를 전자선 가속장치를 이용하여, 전자빔 조사에 의해 가교 처리하는 과정으로 이루어지게 함이 바람직하다.The sheet member cross-linking step S5 is a step of cross-linking the sheet member 1 formed through the above-described joint part forming step S4 by electron beam irradiation using an electron beam accelerator .

이때, 전자선 가속장치에 의한 가교는, 폴리에스테르 소재로 이루어진 시트부재(1)의 분자구조, 예컨대, 선형 고분자 구조를 세로로 한번 더 엮어지게 하여, 그물 구조로 바꿔주도록 하는 처리 과정으로서, 이러한, 전자선 가교를 행할 경우, 시트부재(1)는, 내열성, 내화학성, 열수축성, 내유성, 내한성, 내구성, 내마모성 등이 향상되는 물성변화를 일으키게 되는 것이다.
At this time, the crosslinking by the electron beam accelerating apparatus is a treatment process in which the molecular structure of the sheet member 1 made of a polyester material, for example, the linear polymer structure, is weaved once more vertically so as to switch to a net structure, When the electron beam crosslinking is carried out, the sheet member 1 is changed in physical properties such as heat resistance, chemical resistance, heat shrinkability, oil resistance, cold resistance, durability, abrasion resistance and the like.

끝으로, 상기 제품마감과정(S6)은, 전술한 시트부재 가교처리 과정(S5)을 행한 시트부재(1)의 표면에 안전표시 문양으로 재단처리된 홀로그램 필름지(3)를 부착하여, 시트부재(1)를 안전표시판으로 이용할 수 있도록 형성하는 과정으로 이루어지게 함이 바람직하다.Finally, in the product finishing step S6, the hologram film 3 cut with the safety mark is affixed to the surface of the sheet member 1 subjected to the above-described sheet member crosslinking process S5, (1) to be used as a safety display panel.

1 : 시트부재 2 : 요철고정밴드 3 : 홀로그램 필름지
11,11' : 요철체결부 12,12': 보조체결돌기 13 : 점착면
14 : 이형지 21,21': 치합돌기면 22,22': 고정스톱퍼1: sheet member 2: concave-convex fixing band 3: holographic film sheet
11, 11 ': concave and convex fastening portions 12, 12': ancillary fastening projections 13:
14: release papers 21, 21 ': engagement projections 22, 22': fixed stopper

Claims

A pair of concave-convex engaging portions 11 and 11 'symmetrically formed on the surface of the molded sheet member 1 and having a monochromatic color hue by the addition of a phosphorescent pigment, A pair of auxiliary fastening protrusions 12 and 12 'which are symmetrical to both the center left and right end portions of the main body 10;
A pair of upper and lower concave and convex fixing bands 2 which are tightly coupled with the pair of concave-convex concave portions 11 and 11 'in a coupling structure are provided as auxiliary means for installing the sheet member 1 on the outer surface of the pole of the main body, Wherein the concave and convex fixing band 2 is formed with a coupling projection 21 on its inner front surface and a pair of fixed stoppers 22 and 22 'symmetrical to both left and right ends, Further comprising a fastening clip (C) for connecting the stoppers (22) and (22 ') in a crimp engagement structure;
In addition, a hologram film sheet (3) cut with a safety marking pattern is further attached to the surface of the sheet member (Q) having the monochromatic color hue to form a safety signboard for a telephone pole. Sheet.

The method of claim 1, further comprising:
The sheet member (1) has an adhesive surface (13) formed on the back surface thereof;
Wherein a release paper (14) is further attached to the adhesion surface (13) as means for protecting the adhesion surface (13).

The method of claim 1, further comprising:
The sheet member 1 having the safety marking pattern formed by attaching the hologram film sheet 3 is installed in a safety display facility in a safety display facility such as a road boundary seat, a traffic safety signboard, and a hazard warning signboard, Wherein the sheet for road safety display is applied to the road surface.

A process for producing a polyester sheet by melt-extruding a polyester polymer, which is a thermoplastic polymer, comprising:
A pigment injecting step (S1) of adding a phosphorescent pigment for resin to the molten polyester polymer;
A pigment agitation step (S2) of injecting molten polyester polymer added with the phosphorescent pigment into an agitator to homogeneously mix the phosphorescent pigment and the polyester polymer;
A sheet forming step (S3) of forming the sheet member (1) by extruding the mixed and stirred polyester polymer by a melt extrusion apparatus;
The sheet member 1 molded and discharged from the above-described pouring and pressing apparatus is charged into a pressure rolling forming apparatus by a conveyer flow method, and is pressed on the surface of the sheet member 1 at the lower end (S4) of forming a pair of concave-convex engaging portions (11) and (11 ') symmetrical to each other;
A sheet member crosslinking step (S5) of crosslinking the sheet member (1) by electron beam irradiation using an electron beam accelerator;
Characterized in that a hologram film sheet (3) cut with a safety mark is affixed to the surface of the crosslinked sheet member (1) to form a safety signboard for a telephone pole. Gt;