KR101497102B1 - Material for protecting combined-waterproofing layer, produing and installing method thereof - Google Patents
Material for protecting combined-waterproofing layer, produing and installing method thereof Download PDFInfo
- Publication number
- KR101497102B1 KR101497102B1 KR20130092350A KR20130092350A KR101497102B1 KR 101497102 B1 KR101497102 B1 KR 101497102B1 KR 20130092350 A KR20130092350 A KR 20130092350A KR 20130092350 A KR20130092350 A KR 20130092350A KR 101497102 B1 KR101497102 B1 KR 101497102B1
- Authority
- KR
- South Korea
- Prior art keywords
- polypropylene
- polyethylene
- layer
- waterproof layer
- protective material
- Prior art date
Abstract
폴리에틸렌, 폴리프로필렌, 아조디카본아미드계 발포제 및 마스터배치의 성분으로 구성된 방수층 보호재와 그 제조방법 및 시공방법이 소개된다.A waterproof layer protective material composed of polyethylene, polypropylene, azodicarbonamide blowing agent and components of a master batch, and a manufacturing method and a construction method thereof are introduced.
Description
본 발명은 폴리에틸렌의 유연성과 폴리프로필렌의 강인한 특성을 동시에 확보함으로써 보호재 시공시 외력과 충격, 그리고 하중으로부터 방수층을 효과적으로 보호하는 방수층 보호재와 그 제조방법 및 시공방법에 관한 것이다.
The present invention relates to a waterproof layer protecting material that effectively protects a waterproof layer from external forces, impacts, and loads at the time of constructing a protective material by simultaneously ensuring the flexibility of polyethylene and the strong characteristics of polypropylene, and a manufacturing method and a construction method thereof.
기존에는 방수층 보호를 위해 현장 타설 콘크리트, 보호모르타르 등이 타설되고 있으나, 누수부위 발견이 어렵고, 보수 시 철거작업과 이로 인해 발생하는 폐기물의 처리에 어려움이 있다. 이러한 문제점을 개선하기 위해 기존의 보호층을 대체 할 수 있는 건식 구조의 방수층 보호재의 필요성이 증대되고 있다.In the past, site-laundered concrete and protective mortar have been installed to protect the waterproof layer. However, it is difficult to find a leakage site, and it is difficult to dispose of the waste due to demolition work. To overcome such problems, there is a growing need for a dry-type waterproof layer protective material that can replace the existing protective layer.
근래 들어 발포형과 무발포형의 경량화된 구성과 시트 형태로 제품화되고 있으나, 대부분은 발포 가공 처리된 합성고분자계의 보호재가 적용되고 있다. 발포구조를 가지는 보호재는 내부 기포를 활용하여 완충 공간을 확보하여 외력과 충격으로부터 대응할 수 있도록 하고 있고, 무 발포 구조를 가지는 보호재는 플라스틱 고유의 특징인 강인하고 질긴 특성을 이용하고 있다.In recent years, foaming and non-foaming materials have been produced in a light weighted configuration and sheet form, but most of them have been subjected to foamed synthetic polymer based protective materials. Protective materials having a foamed structure utilize internal air bubbles to secure a buffer space to cope with external forces and impacts. Protective materials having a non-foamed structure utilize tough and tough characteristics characteristic of plastics.
그러나 기존 보호재는 상부에 타설되는 보호층(누름 콘크리트, 보호모르타르)의 시공 과정에서 발생하는 충격과 하중, 마찰력 등으로부터 방수층을 보호하는 완충 기능과 손상 방지 기능을 상실하게 되어 누수의 원인을 제공하고 있다.However, existing protective materials provide the cause of leakage by losing the buffering function and damage prevention function protecting the waterproof layer from impact, load, and friction generated in the construction process of the protective layer (push concrete, protective mortar) have.
발포 PE층을 보호재로 사용하는 경우 누름층의 하중을 지지하지 못함으로서 균열 발생과 보호기능 상실의 문제가 있고, 무발포 보호재는 발포에 비해 유연성이 부족함으로 취급하는데 어려움이 있고, 복잡한 부위 처리시 구조물의 복잡한 형상에 대응하기 어렵다는 문제가 있다. 또한 방수층과 충분한 밀착이 되지 않는 경우에는 누름층에 의한 하중으로 변형이 발생하고, 연결부 변형과 파손으로 방수상의 문제가 발생하게 된다.When the foamed PE layer is used as a protective material, there is a problem of generation of cracks and loss of protective function due to failure to support the load of the pressing layer. Since the foam-free protective material is less flexible than foaming, There is a problem that it is difficult to cope with the complicated shape of the structure. Also, when the waterproof layer is not sufficiently adhered to the waterproof layer, deformation occurs due to the load caused by the pressing layer, and waterproof problems arise due to deformation and breakage of the connection portion.
기존에 사용되고 있는 보호재의 재질로는 폴리에틸렌(HDPE, LDPE, LLDPE), 에틸렌 비닐아세테이트(EVA), 폴리프로필렌, ECB 등이 주로 사용되고 있다. 제조 및 생산은 선정된 원료에 발포 또는 저 발포 처리를 하거나, 발포 PE를 여러 층으로 적층하거나, 무발포층과 다양한 보강층을 형성한 구조로 적용되고 있다.Polyethylene (HDPE, LDPE, LLDPE), ethylene vinyl acetate (EVA), polypropylene, ECB and the like are mainly used as protective materials used in the prior art. Manufacturing and production are applied to the selected raw materials by foaming or low foaming treatment, by laminating foamed PE in several layers, or by forming a non-foaming layer and various reinforcing layers.
기존 기술의 이러한 문제점을 해소하기 위해 발포층과 무 발포층, 또는 직조된 보강재를 선택적으로 적층하는 구조로 변형되었으나, 발포층에서 하중과 보호를 대부분 부담해야하기 때문에 현장 적용시 많은 어려움이 있다. 이는 현장의 다양한 외력 또는 충격으로부터 방수층을 안전하게 보호하고 유지하기는 어렵다는 것을 의미한다. 이의 대안으로 발포 또는 무발포 PE 를 적층하는 방식으로 부분적인 문제를 해소하고 있으나, 재료적으로 강인하고, 질긴 특성을 동시에 보유하기는 어렵기 때문에 근본적인 대안이 없는 실정이다.In order to solve this problem of the existing technology, the foamed layer, the non-foamed layer, or the woven reinforcement is selectively laminated. However, since most of the load and the protection are required to be applied to the foamed layer, This means that it is difficult to safely protect and maintain the waterproof layer from various external forces or impacts in the field. As an alternative to this, a partial problem is solved by a method of laminating foamed or non-foamed PE. However, there is no fundamental alternative because it is difficult to have a materially strong and tough characteristic at the same time.
본 발명은 재생폴리에틸렌의 유연한 발포(기포) 부분과 재생 폴리프로필렌의 질긴 무 발포 부분을 동시에 형성된 단일층 구조와 폐플라스틱을 재활용한 방수층 보호재에 관한 것으로, 폴리에틸렌의 유연성과 폴리프로필렌의 강인한 특성을 동시에 확보함으로서, 누름층 타설시 외력과 충격, 그리고 누름층의 하중으로부터 방수층을 효과적으로 보호하는 방수층 보호재의 조성물을 제공하는데 있다.
The present invention relates to a single-layer structure in which a flexible foamed portion (bubble) portion of recycled polyethylene and a rigid non-foamed portion of recycled polypropylene are simultaneously formed, and a waterproof layer protective material recycled from waste plastic. Thereby effectively protecting the waterproof layer from the external force, the impact, and the load of the push layer when the push layer is poured.
상기의 배경기술로서 설명된 사항들은 본 발명의 배경에 대한 이해 증진을 위한 것일 뿐, 이 기술분야에서 통상의 지식을 가진자에게 이미 알려진 종래기술에 해당함을 인정하는 것으로 받아들여져서는 안 될 것이다.
It should be understood that the foregoing description of the background art is merely for the purpose of promoting an understanding of the background of the present invention and is not to be construed as an admission that the prior art is known to those skilled in the art.
본 발명은 폴리에틸렌의 유연성과 폴리프로필렌의 강인한 특성을 동시에 확보함으로써 보호재 시공시 외력과 충격, 그리고 하중으로부터 방수층을 효과적으로 보호하는 방수층 보호재와 그 제조방법 및 시공방법을 제공하는데 그 목적이 있다.
It is an object of the present invention to provide a waterproof layer protecting material that effectively protects a waterproof layer from external force, impact, and load at the time of constructing a protective material by simultaneously ensuring the flexibility of polyethylene and the strong characteristics of polypropylene, and a manufacturing method and a construction method thereof.
상기의 목적을 달성하기 위한 본 발명에 따른 방수층 보호재는, 폴리에틸렌, 폴리프로필렌, 아조디카본아미드계 발포제 및 마스터배치의 성분으로 구성된다.In order to attain the above object, the waterproof layer protective material according to the present invention is composed of components of polyethylene, polypropylene, azodicarbonamide blowing agent and masterbatch.
폴리에틸렌과 폴리프로필렌의 혼합비율은 wt% 기준으로 1:0.11~0.33(폴리에틸렌:폴리프로필렌)일 수 있다.The mixing ratio of polyethylene to polypropylene may be 1: 0.11-0.33 (polyethylene: polypropylene) based on wt%.
아조디카본아미드계 발포제는 wt% 기준으로 폴리에틸렌과 폴리프로필렌을 합한 총 플라스틱 성분을 100wt%로 하였을 때 0.1~0.5wt%가 되도록 혼합될 수 있다.The azodicarbonamide blowing agent may be mixed in an amount of 0.1 to 0.5 wt% based on 100 wt% of the total plastic component of polyethylene and polypropylene based on wt%.
폴리에틸렌과 폴리프로필렌은 재생 폴리에틸렌 및 재생 폴리프로필렌일 수 있다.Polyethylene and polypropylene can be recycled polyethylene and recycled polypropylene.
아조디카본아미드계 발포제에 의해 발포된 폴리에틸렌 발포부 및 발포부를 둘러싸며 발포부의 사이를 채우는 폴리프로필렌 무발포부로 구성될 수 있다. A polyethylene foamed portion blown by the azodicarbonamide blowing agent and a polypropylene nonfoamed portion surrounding the foamed portion and filling the spaces between the foamed portions.
방수층 보호재를 제조하는 방법은, 고상의 폴리에틸렌, 폴리프로필렌, 아조디카본아미드계 발포제 및 마스터배치를 혼합하는 혼합단계; 220~250℃에서 용융하는 용융단계; 및 필름 형태로 압출하는 압출단계;를 포함한다.The method for producing the waterproofing layer protective material comprises mixing a solid polyethylene, polypropylene, azodicarbonamide blowing agent and master batch; A melting step of melting at 220 to 250 ° C; And an extrusion step of extruding in the form of a film.
본 발명의 또 다른 방수층 보호재는, 폴리에틸렌, 폴리프로필렌, 아조디카본아미드계 발포제 및 마스터배치의 성분으로 구성된 보호층; 보호층 이면에 결합된 접착층; 및 접착층 이면에 결합된 이형층;을 포함한다.Another waterproof layer protective material of the present invention is a protective layer composed of components of polyethylene, polypropylene, azodicarbonamide type foaming agent and master batch; An adhesive layer bonded to the back surface of the protective layer; And a release layer bonded to the back surface of the adhesive layer.
폴리에틸렌과 폴리프로필렌의 혼합비율은 wt% 기준으로 1:0.11~0.33(폴리에틸렌:폴리프로필렌)일 수 있다.The mixing ratio of polyethylene to polypropylene may be 1: 0.11-0.33 (polyethylene: polypropylene) based on wt%.
방수층 보호재를 시공하는 방법은, 방수층 표면의 이물질을 제거하는 준비단계; 방수층 보호재의 이형층을 제거하는 제거단계; 방수층 보호재의 접착층 이면을 방수층에 접착하되, 방수층 보호재의 이음부와 연결부는 방수층 보호재가 일정부분 상호 겹쳐지도록 시공하는 접착단계; 및 방수층 보호재의 겹쳐진 이음부와 연결부 상부에 테이프를 보강하는 보강단계;를 포함한다.
The method of constructing the waterproofing layer protective material comprises: a preparation step of removing foreign matters on the surface of the waterproofing layer; A removal step of removing the release layer of the waterproof layer protection material; A bonding step of adhering the back surface of the adhesive layer of the waterproof layer protective material to the waterproof layer, wherein the joint part and the connection part of the waterproof layer protective material are constructed such that the waterproof layer protective material is partially overlapped with each other; And a reinforcing step of reinforcing the tape on the overlapped joints and the joints of the waterproofing layer protective material.
상술한 바와 같은 구조로 이루어진 방수층 보호재와 그 제조방법 및 시공방법에 따르면, 제조공정상 혼합되는 재생 폴리에틸렌과 재생 폴리프로필렌 중 에틸렌만 발포할 수 있는 발포재를 선택 적용함으로써, 혼합되는 재생폴리프로필렌이 발포된 재생 폴리에틸렌의 기포를 견고하게 유지할 수 있도록 기포와 기포 사이의 표면에 위치되어 보호재의 강도 및 인열 성능과 저온에서의 유연성과 안정성을 향상시키고, 완충효과가 우수한 보호재를 제공할 수 있게 된다.
According to the waterproofing layer protection material having the above-described structure, and the method of manufacturing and the method of manufacturing the same, it is possible to selectively use the regenerated polyethylene that is normally mixed with the manufacturing process and the foamable material that can only expand ethylene among the regenerated polypropylene, Which is located on the surface between the bubbles and the bubbles so as to firmly hold the bubbles of the reclaimed polyethylene, thereby improving the strength and tear performance of the protective material, flexibility and stability at low temperatures, and providing a protective material with excellent buffering effect.
도 1은 본 발명의 일 실시예에 따른 방수층 보호재의 구조를 나타낸 도면.
도 2는 본 발명의 또 다른 실시예에 따른 방수층 보호재의 구조를 나타낸 도면.
도 3은 본 발명의 일 실시예에 따른 방수층 보호재의 시공방법의 순서도.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a view showing a structure of a waterproofing layer protective material according to an embodiment of the present invention. FIG.
2 is a view showing the structure of a waterproof layer protection material according to another embodiment of the present invention.
3 is a flowchart of a method of constructing a waterproof layer protection material according to an embodiment of the present invention.
이하에서는 첨부된 도면을 참조하여 본 발명의 바람직한 실시 예에 따른 방수층 보호재와 그 제조방법 및 시공방법에 대하여 살펴본다.Hereinafter, a waterproof layer protecting material according to a preferred embodiment of the present invention will be described with reference to the accompanying drawings.
도 1은 본 발명의 일 실시예에 따른 방수층 보호재의 구조를 나타낸 도면이고, 도 2는 본 발명의 또 다른 실시예에 따른 방수층 보호재의 구조를 나타낸 도면이며, 도 3은 본 발명의 일 실시예에 따른 방수층 보호재의 시공방법의 순서도이다.FIG. 1 is a view showing a structure of a waterproofing layer protection material according to an embodiment of the present invention, FIG. 2 is a view showing the structure of a waterproofing layer protection material according to another embodiment of the present invention, And a method of constructing a waterproof layer protection material according to the present invention.
본 발명에 따른 방수층 보호재는, 폴리에틸렌, 폴리프로필렌, 아조디카본아미드계 발포제 및 마스터배치의 성분으로 구성된다. 또한 본 발명의 방수층 보호재의 조성물은 폐플라스틱 중에서 폴리에틸렌, 폴리프로필렌 폐기물을 재활용하여, 폐자원의 재활용성을 향상시키는 기술이다. The waterproof layer protective material according to the present invention is composed of components of polyethylene, polypropylene, azodicarbonamide blowing agent and masterbatch. Further, the composition of the waterproof layer protective material of the present invention is a technology for recycling polyethylene and polypropylene waste in waste plastics to improve the recyclability of waste resources.
본 발명은 상기 두 가지 재생 플라스틱을 일정한 비율로 혼합하는 방식과 선택적으로 발포하는 개념을 동시에 적용하고 있다. 구체적으로 설명하면, 제조공정상 혼합되는 재생 폴리에틸렌과 재생 폴리프로필렌 중 에틸렌만 발포할 수 있는 발포재를 선택 적용함으로서, 혼합되는 재생폴리프로필렌이 발포된 재생 폴리에틸렌의 기포를 견고하게 유지할 수 있도록 기포와 기포 사이의 표면에 위치함으로서 보호재의 강도 및 인열 성능과 저온에서의 유연성과 안정성을 향상시키고, 완충효과가 우수한 보호재를 제공하게 된다.The present invention applies both the method of mixing the two reclaimed plastics at a certain ratio and the concept of selective foaming simultaneously. Specifically, by selectively applying the foamed material capable of foaming only the ethylene out of the regenerated polyethylene and the regenerated polypropylene which are normally mixed in the manufacturing process, the regenerated polypropylene to be mixed with the foamed material is foamed so as to firmly retain the foamed foamed polyethylene. It is possible to improve the strength and tear performance of the protective material, flexibility and stability at low temperatures, and provide a protective material with excellent buffering effect.
즉, 본 기술의 방수층 보호재는 재생 폴리에틸렌, 재생 폴리프로필렌, 발포재, 착색용 마스터배치로 구성되어 있다.That is, the waterproof layer protecting material of the present invention is composed of recycled polyethylene, recycled polypropylene, foaming material, and masterbatch for coloring.
재생 폴리에틸렌은 폐플라스틱 중에서 튜브 상의 폐 플라스틱류를, 재생 폴리프로필렌은 폐플라스틱 중 포장용 박스를 각각 용융재생법으로 재생한 것을 사용하는 것이 바람직하다. 다양한 폐플라스틱을 사용하는 경우 품질 변동이 발생함으로, 동일한 폐플라스틱을 재생 원료로 사용하는 것이 균일한 발포 효율과 제품 품질 확보에 용이하다. It is preferable to use recycled polyethylene which is a recycled polypropylene recycled from a waste plastic in a tube and recycled polypropylene which is recycled in a waste plastic recycling method by a packing box. When various waste plastics are used, quality fluctuation occurs. Therefore, using the same waste plastic as a raw material for recycling facilitates uniform foaming efficiency and product quality.
폴리에틸렌과 폴리프로필렌의 혼합비율은 wt% 기준으로 1:0.11~0.33(폴리에틸렌:폴리프로필렌)일 수 있다. 즉, 재생 처리된 폴리에틸렌과 폴리프로필렌의 혼합비율은 1 : 0.11~0.33 이 되도록 혼합하여 사용하여야한다. 폴리프로필렌의 함량이 0.11 이하의 경우 발포 처리 후 인장강도와 인열 강도가 저하되어, 방수층 보호재로서 충분히 성능을 발휘하지 못하게 되고, 0.33 이상의 경우에는 저온 조건에서 외력이나 충격을 받는 경우 보호재가 파괴되어 기능을 상실하게 된다.The mixing ratio of polyethylene to polypropylene may be 1: 0.11-0.33 (polyethylene: polypropylene) based on wt%. That is, the mixing ratio of the regenerated polyethylene and polypropylene should be 1: 0.11 to 0.33. When the content of polypropylene is 0.11 or less, the tensile strength and tear strength are lowered after the foaming treatment, and the performance as a waterproof layer protective material is not sufficiently exhibited. When the polypropylene content is 0.33 or more, .
또한, 재생 폴리에틸렌을 발포하는데 사용하는 발포재는 유기계의 열분해형 아조화합물을 적용한다. 아조디카본아미드계를 사용하는 것은 강도 향상 목적으로 적용되는 재생 폴리 프로필렌가 발포되지 않도록 하기 위함이다. 아조디카본아미드계 발포제는 wt% 기준으로 폴리에틸렌과 폴리프로필렌을 합한 총 플라스틱 성분을 100wt%로 하였을 때 0.1~0.5wt%가 되도록 혼합될 수 있다.The foaming material used for foaming the reclaimed polyethylene is an organic pyrolyzed azo compound. The use of the azodicarbonamide type is intended to prevent the regenerated polypropylene, which is applied for the purpose of strength improvement, from foaming. The azodicarbonamide blowing agent may be mixed in an amount of 0.1 to 0.5 wt% based on 100 wt% of the total plastic component of polyethylene and polypropylene based on wt%.
분해온도가 201~205℃, 가스량 160~180ml/g인 아조디카본아미드 (AC 또는 ADCA)계 발포제는 재생 플라스틱 중량 대비 0.1~0.5wt% 범위로 사용하는 것이 바람직하다. 0.1wt% 이하에서는 재생 폴리에틸렌의 발포효과가 저하되어 충분한 완충효과를 얻기 어렵고, 0.5wt% 이상 첨가 시 재생 폴리에틸렌이 과다하게 발포되어 강도 저하와 찢어짐에 대한 저항성, 저온에서의 안정성이 이 낮아지는 문제가 발생한다. The azodicarbonamide (AC or ADCA) based blowing agent having a decomposition temperature of 201 to 205 ° C and a gas volume of 160 to 180 ml / g is preferably used in a range of 0.1 to 0.5 wt% based on the weight of the recycled plastic. When the amount is less than 0.1 wt%, the foaming effect of the recycled polyethylene is lowered, and sufficient buffering effect is hardly obtained. When the amount is more than 0.5 wt%, the recycled polyethylene is excessively foamed to reduce the strength and tear resistance, Lt; / RTI >
마스터배치는 착색효과를 부여하기 위해 사용하는 것으로 제한이 없으나, 재생플라스틱을 원료의 색상을 기준으로 첨가량을 결정하는 것이 바람직하다. 이는 최종 생산품의 색상이 일정하게 유지될 수 있도록 하는 것이 필요하기 때문이다.
The master batch is not limited to be used for imparting a coloring effect, but it is preferable to determine the addition amount of the recycled plastic based on the hue of the raw material. This is because it is necessary to keep the color of the final product constant.
도 1은 본 발명의 일 실시예에 따른 방수층 보호재의 구조를 나타낸 도면으로서, 아조디카본아미드계 발포제에 의해 발포된 폴리에틸렌 발포부(100) 및 발포부(100)를 둘러싸며 발포부(100)의 사이를 채우는 폴리프로필렌 무발포부(200)로 구성될 수 있다.1 shows a structure of a waterproofing layer protective material according to an embodiment of the present invention. The
즉, 본 발명은 두 가지 재생 플라스틱을 일정한 비율로 혼합하는 방식과 선택적으로 발포하는 개념을 동시에 적용하고 있는 것으로서, 제조공정상 혼합되는 재생 폴리에틸렌과 재생 폴리프로필렌 중 에틸렌만 발포할 수 있는 발포재를 선택 적용하여, 혼합되는 재생폴리프로필렌이 발포된 재생 폴리에틸렌의 기포를 견고하게 유지할 수 있도록 기포와 기포 사이의 표면에 위치함으로서 보호재의 강도 및 인열 성능과 저온에서의 유연성과 안정성을 향상시키고, 완충효과가 우수한 보호재를 제공하게 된다.
That is, the present invention applies both the method of mixing two types of regenerated plastics at a certain ratio and the concept of selectively foaming, and it is possible to select a foamed material capable of foaming only ethylene out of the regenerated polyethylene and the regenerated polypropylene, The regenerated polypropylene to be mixed is positioned on the surface between the bubbles and the bubbles so as to firmly maintain the bubbles of the foamed regenerated polyethylene, thereby improving the strength and tear performance of the protective material, flexibility and stability at low temperatures, Thereby providing an excellent protection material.
본 발명의 방수층 보호재를 제조하는 방법은, 고상의 폴리에틸렌, 폴리프로필렌, 아조디카본아미드계 발포제 및 마스터배치를 혼합하는 혼합단계; 220~250℃에서 용융하는 용융단계; 및 필름 형태로 압출하는 압출단계;를 포함한다.The method for producing the waterproof layer protective material of the present invention comprises mixing a solid polyethylene, polypropylene, azodicarbonamide based foaming agent and a master batch; A melting step of melting at 220 to 250 ° C; And an extrusion step of extruding in the form of a film.
구체적으로, 본 발명의 조성물에 대해 제조예를 들어 설명하면 다음과 같다. 재생 폴리에틸렌과 폴리프로필렌을 지정된 비율로 프리믹싱하고, 균일한 착색력을 부여하기 위해 적용되는 마스터배치는 재생플라스틱 중량 대비 0.6wt%를 첨가한다. 재생 폴리에틸렌을 발포시키기 위해 분말형 Azodicarbonamide계 발포제를 재생 플라스틱 전체중량 대비 0.1wt%(Cellcom-AC Series, Normal type)를 첨가하여 건식 혼합기를 사용하여 혼합하고, 융융(220~250℃)된 상태로 T-다이로 이송 압출되고, 카렌더 롤에 의해 일정한 두께(1.00mm)로 발포된 제품을 제조한다.
Specifically, the composition of the present invention is described as follows. The masterbatch applied for pre-mixing the recycled polyethylene and polypropylene at a specified ratio and imparting a uniform tinting strength is to add 0.6 wt% to the weight of recycled plastic. (Cellcom-AC Series, Normal type) was added to the total weight of the regenerated plastic, and the resultant mixture was melt-mixed (220 to 250 ° C) Transferred to a T-die, and a product foamed to a constant thickness (1.00 mm) by a calender roll.
상기 표는 본 발명의 실시예와 비교예들의 조성에 관한 표이다.
The above table is a table relating to compositions of Examples and Comparative Examples of the present invention.
실시예들과 비교예들의 시험결과를 설명하면 아래와 같다.Test results of Examples and Comparative Examples are as follows.
인장강도와 인열강도는 "폴리에틸렌(PE) 방수층 보호재(LH 공사 전문시방서 / 2012.06)"에 제시되어 있는 시험방법에 따라 평가하였다. 저온 안정성 평가는 영하 20℃ / 24시간 정치 후 180°로 절곡하고, 절곡된 부위의 상태를 육안으로 확인하는 방법을 적용하였다. 제조된 실시예와 비교예에 대한 평가 결과를 제시하면 다음과 같다.
Tensile strength and tear strength were evaluated according to the test methods given in "Polyethylene (PE) waterproof layer protection material (LH Construction Specification / 2012.06)". The low-temperature stability evaluation was carried out at a temperature of minus 20 ° C / 24 hours and then bent at 180 °, and the state of the bent portion was visually confirmed. The evaluation results of the prepared examples and comparative examples are as follows.
상기와 같이, 실시예와 비교예의 평가결과 재생 폴리에틸렌 대비 폴리프로필렌의 함량이 증가함에 따라 인장강도와 인열 강도는 증가되는 것으로 나타났다. 이러한 경향은 발포되지 않은 재생 폴리프로필렌이 발포된 폴리에틸렌의 기포와 기포 사이를 견고하게 고정하고 있기 때문이다. As described above, the evaluation results of Examples and Comparative Examples show that the tensile strength and the tear strength are increased as the content of polypropylene increases with respect to the recycled polyethylene. This tendency is because the unfoamed regenerated polypropylene firmly fixes between the bubbles of foamed polyethylene and the bubbles.
또한, 실시예 1과 2의 경우, 요구되는 조건 성능을 충족할 수 조성물로 나타났다. 이는 현장 적용시 발생할 수 있는 모든 조건에 대응할 수 있는 성능을 가진다는 것을 의미하고 있다.Further, in the case of Examples 1 and 2, the composition showed satisfactory performance of the required condition. This means that it has the capability to cope with all the conditions that can occur in the field application.
반면, 비교예 1은 발포된 재생 폴리에틸렌의 기포의 피막만으로 이루어진 구조임으로 가장 낮은 강도와 인열 성능을 가진 것으로 나타났다. 그리고 비교예 2,3,4의 순서로 발포되지 않은 재생 폴리프로필렌의 함량이 증가하기 때문에 강도는 증가하나, 딱딱한(hard) 특성으로 인해 저온에서의 안정성이 부족하여 파괴 현상이 발생하였다. 재생 폴리프로필렌을 단독으로 적용한 비교예 4는 발포가 거의 되지 않아 비교적 높은 강도를 보유하고 있으나, 유연성 부족으로 현장 설치 작업시 취급이 곤란하고, 굴곡부위에 대한 대응성이 부족하여 누름층 적용시 변형 또는 파괴 등의 문제가 발생하였다.
On the other hand, Comparative Example 1 has the lowest strength and tear performance because it is a structure composed of foamed recycled polyethylene bubble film only. In addition, in the order of Comparative Examples 2, 3, and 4, the content of unrepresented polypropylene was increased, so that the strength was increased. However, due to hard properties, the stability at low temperature was insufficient. Comparative Example 4, in which recycled polypropylene was used singly, had relatively high strength because it was hardly foamed, but it was difficult to handle in field installation work due to lack of flexibility and lack of correspondence to bending portion, Or breakage.
본 발명의 또 다른 방수층 보호재는, 폴리에틸렌, 폴리프로필렌, 아조디카본아미드계 발포제 및 마스터배치의 성분으로 구성된 보호층; 보호층 이면에 결합된 접착층; 및 접착층 이면에 결합된 이형층;을 포함한다.Another waterproof layer protective material of the present invention is a protective layer composed of components of polyethylene, polypropylene, azodicarbonamide type foaming agent and master batch; An adhesive layer bonded to the back surface of the protective layer; And a release layer bonded to the back surface of the adhesive layer.
도 2는 본 발명의 또 다른 실시예에 따른 방수층 보호재의 구조를 나타낸 도면으로서, 폴리에틸렌, 폴리프로필렌, 아조디카본아미드계 발포제 및 마스터배치의 성분으로 구성된 보호층(300)의 하면에 접착층(400)이 결합되고, 접착층(400)의 하면에는 다시 이형층(500)이 결합된다.
2 illustrates a structure of a waterproofing layer protective material according to another embodiment of the present invention. The
도 3은 본 발명의 일 실시예에 따른 방수층 보호재의 시공방법의 순서도로서, 본 발명의 방수층 보호재를 시공하는 방법은, 방수층 표면의 이물질을 제거하는 준비단계(S100); 보호재를 설치(S200)함에 있어 접착층이 있는 보호재의 경우(S310)에는 보호재를 포설하고(S320) 방수층 보호재의 이형층을 제거하는 제거단계(S330); 방수층 보호재의 접착층 이면을 방수층에 접착하되, 방수층 보호재의 이음부와 연결부는 방수층 보호재가 일정부분 상호 겹쳐지도록 시공하는 접착단계(S340); 및 방수층 보호재의 겹쳐진 이음부와 연결부 상부에 테이프를 보강하는 보강단계(S350);를 포함한다. 즉, 먼저 방수층 표면의 이물질을 제거하고, 접착층 하부의 이형층을 제거한 다음 압착 처리하여 견고하게 접착하고, 보호재의 이음부와 연결부를 겹침 처리하여 접착하되, 그 이음부와 연결부의 상부에는 보강 테이프를 처리하여 마무리하게 되는 것이다. 즉, 복수의 보호재를 연결하면서 발생되는 이음부나 연결부의 경우 겹쳐놓아 접착하되 그 겹치는 부분을 보강함으로써 방수층을 더욱 완벽하게 보호하게 되는 것이다.
FIG. 3 is a flowchart of a method of constructing a waterproofing layer protection material according to an embodiment of the present invention. The method of constructing the waterproofing layer protection material of the present invention includes a preparation step (S100) for removing foreign matters on the waterproofing layer surface; In the case of the protective material having the adhesive layer (S310), the protective material is installed (S320), the removing step (S330) of removing the release layer of the waterproofing layer protective material is performed. A bonding step (S340) of adhering the back surface of the adhesive layer of the waterproof layer protection material to the waterproof layer, wherein the joint part and the connection part of the waterproof layer protection material are constructed such that the waterproof layer protective material overlaps with a certain portion; And a reinforcing step (S350) of reinforcing the tape on the overlapped joint portion of the waterproofing layer protective material and the joint portion. That is, first, the foreign substances on the surface of the waterproof layer are removed, the release layer under the adhesive layer is removed, and the adhesive layer is firmly adhered to the adhesive layer. To finish the process. That is, in the case of joints or joints which are generated while connecting a plurality of protective materials, the waterproof layer is more completely protected by superimposing and bonding the overlapped portions.
한편, 접착층이 없는 경우(S410)에는 방수층 표면의 이물질을 제거하는 준비단계; 방수층 보호재를 방수층에 포설하되, 방수층 보호재의 이음부와 연결부는 방수층 보호재가 일정부분 상호 겹쳐지도록 시공하는 시공단계; 및 방수층 보호재의 겹쳐진 이음부와 연결부 상부에 테이프를 보강하는 보강단계;를 포함한다. 즉, 방수층 보호재를 포설하고(S420) 이음부와 연결부는 방수층 보호재가 일정부분 상호 겹쳐지도록 시공하되(S430), 방수층 보호재의 겹쳐진 이음부와 연결부 상부에 테이프를 보강하도록 한다(S440).
On the other hand, if there is no adhesive layer (S410), a preparation step of removing foreign matters on the surface of the waterproof layer; The waterproof layer protection material is installed on the waterproof layer, and the joint part and the connection part of the waterproof layer protection material are constructed so that the waterproof layer protective material is partially overlapped with each other. And a reinforcing step of reinforcing the tape on the overlapped joints and the joints of the waterproofing layer protective material. That is, the waterproofing layer protection material is installed S420, and the joint portion and the connection portion are constructed such that the waterproofing layer protection material overlaps with each other at a certain time (S430), and the tape is reinforced at the overlapped joint portion and the connection portion of the waterproofing layer protection material at S440.
상술한 바와 같은 구조로 이루어진 방수층 보호재와 그 제조방법 및 시공방법에 따르면, 제조공정상 혼합되는 재생 폴리에틸렌과 재생 폴리프로필렌 중 에틸렌만 발포할 수 있는 발포재를 선택 적용함으로써, 혼합되는 재생폴리프로필렌이 발포된 재생 폴리에틸렌의 기포를 견고하게 유지할 수 있도록 기포와 기포 사이의 표면에 위치되어 보호재의 강도 및 인열 성능과 저온에서의 유연성과 안정성을 향상시키고, 완충효과가 우수한 보호재를 제공할 수 있게 된다.
According to the waterproofing layer protection material having the above-described structure, and the method of manufacturing and the method of manufacturing the same, it is possible to selectively use the regenerated polyethylene that is normally mixed with the manufacturing process and the foamable material that can only expand ethylene among the regenerated polypropylene, Which is located on the surface between the bubbles and the bubbles so as to firmly hold the bubbles of the reclaimed polyethylene, thereby improving the strength and tear performance of the protective material, flexibility and stability at low temperatures, and providing a protective material with excellent buffering effect.
본 발명은 특정한 실시예에 관련하여 도시하고 설명하였지만, 이하의 특허청구범위에 의해 제공되는 본 발명의 기술적 사상을 벗어나지 않는 한도 내에서, 본 발명이 다양하게 개량 및 변화될 수 있다는 것은 당 업계에서 통상의 지식을 가진 자에게 있어서 자명할 것이다.
While the present invention has been particularly shown and described with reference to specific embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the invention as defined by the following claims It will be apparent to those of ordinary skill in the art.
100 : 발포부 200 : 무발포부
300 : 보호층 400 : 접착층
500 : 이형층100: foaming part 200: no foaming part
300: protective layer 400: adhesive layer
500:
Claims (10)
폴리에틸렌과 폴리프로필렌의 혼합비율은 wt% 기준으로 1:0.11~0.33(폴리에틸렌:폴리프로필렌)인 것을 특징으로 하는 방수층 보호재.Polyethylene, polypropylene, azodicarbonamide blowing agent and components of a master batch,
Wherein the mixing ratio of polyethylene to polypropylene is 1: 0.11 to 0.33 (polyethylene: polypropylene) based on wt%.
아조디카본아미드계 발포제는 wt% 기준으로 폴리에틸렌과 폴리프로필렌을 합한 총 플라스틱 성분을 100wt%로 하였을 때 0.1~0.5wt%가 되도록 혼합된 것을 특징으로 하는 방수층 보호재.The method according to claim 1,
Wherein the azodicarbonamide blowing agent is mixed so as to have a content of 0.1 to 0.5 wt% based on 100 wt% of total plastic components of polyethylene and polypropylene based on wt%.
폴리에틸렌과 폴리프로필렌은 재생 폴리에틸렌 및 재생 폴리프로필렌인 것을 특징으로 하는 방수층 보호재.The method according to claim 1,
Wherein the polyethylene and the polypropylene are recycled polyethylene and recycled polypropylene.
아조디카본아미드계 발포제에 의해 발포된 폴리에틸렌 발포부 및 발포부를 둘러싸며 발포부의 사이를 채우는 폴리프로필렌 무발포부로 구성된 것을 특징으로 하는 방수층 보호재.The method according to claim 1,
And a polypropylene non-foamed portion surrounding the foamed portion and filling the spaces between the foamed portions, characterized by comprising a polyethylene foam portion foamed by an azodicarbonamide blowing agent and a polypropylene non-foamed portion surrounding the foam portion.
고상의 폴리에틸렌, 폴리프로필렌, 아조디카본아미드계 발포제 및 마스터배치를 혼합하는 혼합단계;
220~250℃에서 용융하는 용융단계; 및
필름 형태로 압출하는 압출단계;를 포함하고,
혼합단계에서의 폴리에틸렌과 폴리프로필렌의 혼합비율은 wt% 기준으로 1:0.11~0.33(폴리에틸렌:폴리프로필렌)인 것을 특징으로 하는 방수층 보호재 제조방법.A method for producing the waterproofing layer protective material of claim 1,
A mixing step of mixing solid polyethylene, polypropylene, azodicarbonamide blowing agent and master batch;
A melting step of melting at 220 to 250 ° C; And
An extrusion step of extruding in the form of a film,
Wherein the mixing ratio of polyethylene to polypropylene in the mixing step is 1: 0.11 to 0.33 (polyethylene: polypropylene) based on wt%.
보호층 이면에 결합된 접착층; 및
접착층 이면에 결합된 이형층;을 포함하고,
폴리에틸렌과 폴리프로필렌의 혼합비율은 wt% 기준으로 1:0.11~0.33(폴리에틸렌:폴리프로필렌)인 것을 특징으로 하는 방수층 보호재.A protective layer composed of components of polyethylene, polypropylene, azodicarbonamide blowing agent and master batch;
An adhesive layer bonded to the back surface of the protective layer; And
And a releasing layer bonded to the back surface of the adhesive layer,
Wherein the mixing ratio of polyethylene to polypropylene is 1: 0.11 to 0.33 (polyethylene: polypropylene) based on wt%.
방수층 표면의 이물질을 제거하는 준비단계;
방수층 보호재의 이형층을 제거하는 제거단계;
방수층 보호재의 접착층 이면을 방수층에 접착하되, 방수층 보호재의 이음부와 연결부는 방수층 보호재가 일정부분 상호 겹쳐지도록 시공하는 접착단계; 및
방수층 보호재의 겹쳐진 이음부와 연결부 상부에 테이프를 보강하는 보강단계;를 포함하는 방수층 보호재 시공방법.A method for constructing a waterproofing layer protective material according to claim 7,
A preparation step of removing foreign matters on the surface of the waterproof layer;
A removal step of removing the release layer of the waterproof layer protection material;
A bonding step of adhering the back surface of the adhesive layer of the waterproof layer protective material to the waterproof layer, wherein the joint part and the connection part of the waterproof layer protective material are constructed such that the waterproof layer protective material is partially overlapped with each other; And
And a reinforcing step of reinforcing the tape on the overlapped joints of the waterproofing layer protective material and the joints.
방수층 표면의 이물질을 제거하는 준비단계;
방수층 보호재를 방수층에 포설하되, 방수층 보호재의 이음부와 연결부는 방수층 보호재가 일정부분 상호 겹쳐지도록 시공하는 시공단계; 및
방수층 보호재의 겹쳐진 이음부와 연결부 상부에 테이프를 보강하는 보강단계;를 포함하는 방수층 보호재 시공방법.A method for constructing a waterproofing layer protective material according to claim 1,
A preparation step of removing foreign matters on the surface of the waterproof layer;
The waterproof layer protection material is installed on the waterproof layer, and the joint part and the connection part of the waterproof layer protection material are constructed so that the waterproof layer protective material is partially overlapped with each other. And
And a reinforcing step of reinforcing the tape on the overlapped joints of the waterproofing layer protective material and the joints.