KR101491589B1 - Eco-Friendly Concrete Block Composition Using Seaweeds and Manufacturing Methods of Concrete Blocks Using Thereof - Google Patents
Eco-Friendly Concrete Block Composition Using Seaweeds and Manufacturing Methods of Concrete Blocks Using Thereof Download PDFInfo
- Publication number
- KR101491589B1 KR101491589B1 KR20140085071A KR20140085071A KR101491589B1 KR 101491589 B1 KR101491589 B1 KR 101491589B1 KR 20140085071 A KR20140085071 A KR 20140085071A KR 20140085071 A KR20140085071 A KR 20140085071A KR 101491589 B1 KR101491589 B1 KR 101491589B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- concrete block
- block composition
- mixture
- Prior art date
Abstract
Description
본 발명은 콘크리트 블록 조성물에 관한 것으로서, 보다 상세하게는 건축 구조물 또는 도로포장 등에 사용되는 블록, 예를 들면 일반 블록, 보도블록, 호안블록, 식생블록, 축조블록, 조경용 블록 또는 보강토용 블록 등 제반 콘크리트 블록을 제조하기 위한 콘크리트 블록 조성물, 특정적으로 해조류를 이용한 친환경 콘크리트 블록 조성물 및 이를 이용한 블록 제조방법에 관한 것이다.
The present invention relates to a concrete block composition, and more particularly, to a concrete block composition for use in a building structure or road pavement, for example, a general block, a sidewalk block, a shore block, a vegetation block, a building block, A concrete block composition for producing a concrete block, an environmentally friendly concrete block composition using a seaweed, and a method for producing a block using the same.
일반적으로 보도블록은 석재나 콘크리트 등으로 이루어지는 직육면체의 몸체 상면에 각종 색상이나 형태를 가지는 무늬 또는 장식을 형성시킨다. Generally, the sidewalk block forms a pattern or decoration having various colors or shapes on the upper surface of a rectangular parallelepiped body made of stone, concrete, or the like.
그리고 각각의 보도블록을 서로 연이어서 설치하며 보도를 형성하게 되는데, 이 때 각각의 보도블록에 형성된 무늬와 장식이 조합되어 하나의 전체적인 그림 또는 도형을 형성하게 된다. Then, each press block is installed in succession to form a sidewalk. At this time, the pattern and decoration formed on each sidewalk block are combined to form an overall picture or figure.
상기와 같은 블록에 의하여 단순히 도로나 보행통로를 덮는 과거의 블록개념에서 탈피하여 도시와 건물의 미관 향상에 매우 큰 역할을 할 수 있다.By the above-mentioned blocks, it is possible to avoid the concept of the past block simply covering the road or the walkway, and play a very great role in improving the beauty of the city and the building.
한편, 전술한 블록, 특정적으로 보도블록은 통상적으로 지면에 평평한 형태로 모래를 깔고, 그 위에 시멘트와 모래의 혼합체인 몰탈로 성형과 양생과정을 거치며 제작되는 판형의 발판을 일정하게 깔아 보행자들의 보행 또는 차량의 이동에 도움을 주고자 고안된 물품이다.On the other hand, the above-mentioned block, specifically the sidewalk block, is usually laid flat on the ground, and a plate-like footplate, which is formed by molding and curing the mixture with mortar, which is a mixture of cement and sand, It is an item designed to assist in walking or moving the vehicle.
이러한 물품은 일반적으로 백색의 유색층을 가진 보도블록과 다양한 색상을 가진 보도블록으로 나뉘는데, 현행 지면에 깔려진 보도블록중 약 70%정도는 백색의 보도블록이고 나머지 30%정도의 보도블록은 색상을 가진 보도블록이다.These articles are generally divided into a white colored block with colored layers and a colored block with various colors. About 70% of the existing block is covered with white, and the remaining 30% Lt; / RTI >
이때, 상기 보도블록은 그 제작방법에 있어서, 우선 시멘트와 모래를 물과 함께 적당량 섞어 기본층 몰탈을 만들고 이를 일정한 평면형상을 한 형틀, 예를 들면 성형틀에 채우고, 진동을 주며 고압을 이용하여 가압함으로써 기본층을 형성시킨다.At this time, in the manufacturing method of the sidewalk block, cement and sand are mixed with water in an appropriate amount to make a base layer mortar, which is filled in a mold having a predetermined plane shape, for example, a mold, vibration is applied, Thereby forming a base layer.
그 다음, 백시멘트, 모래, 안료 등과 물을 적당량 혼합하여 유색몰탈을 제작하고, 이 유색몰탈을 형틀속의 기본층 상면에 채운 뒤, 진동을 주면서 고압으로 가압하여 완성된 형상을 제조한 후 양생시켜 최종적인 보도블록을 제작한다.Then, an appropriate amount of white cement, sand, pigment, etc. is mixed with water to prepare a colored mortar. The colored mortar is filled on the upper surface of the base layer in the mold, Create the final press block.
이러한 일례로서, 대한민국 특허공개 제2003-0030262호에는 백시멘트, 색소, 물, 혼화제 와 자외선차단제를 구성요소로 사용하며 백운석가루를 모래대용으로 섞어 보도블록의 유색몰탈을 조성하고, 이를 기본층이 형성된 형틀에 채우고, 진동을 주며, 고압으로 가압하여 보도블록을 제작하는 방법이 개시되어 있다.
As an example of this, Korean Patent Laid-Open Publication No. 2003-0030262 discloses a method of preparing a colored mortar of a pedestal block by mixing white dolmene powder with sand as a constituent using white cement, pigment, water, an admixture and an ultraviolet screening agent, Discloses a method for producing a sidewalk block by filling a formed mold, applying vibration, and pressurizing it at a high pressure.
본 발명은 상기와 같은 문제점을 해결하기 위해 창출한 것으로서, 물리/화학적인 영향에 의해 쉽게 노화되지 않으면서도, 외부의 충격에 의해 쉽게 변형되거나 깨지지 않는 고강도와 내구성을 갖는 해조류를 이용한 친환경 콘크리트 블록 조성물 및 이를 이용한 콘크리트 블록의 제조방법을 제공하고자 한다.
The present invention has been made in order to solve the above problems, and it is an object of the present invention to provide an environmentally friendly concrete block composition using seaweeds having high strength and durability that are not easily aged due to physical / chemical influences, And a method for manufacturing a concrete block using the same.
본 발명은
시멘트 100중량부를 기준으로,
가시파래, 홀파래 청태, 해캄, 파래, 청각, 구슬청각, 옥덩굴, 염주말, 미역, 다시마, 헛가지말, 민가지말, 패, 고리매, 미역쇠, 감태, 곰피, 대황, 쇠미역사촌, 모자반, 괭생이 모자반, 지충이, 톳, 김, 우뭇가사리, 불등가사리, 코토니, 개도박, 둥근돌김, 개우무, 새발, 참풀가사리, 꼬시래기, 진두발, 참도박, 가시우무, 비단풀, 단박, 돌가사리, 석목, 지누아리, 또는 이들 중 선택된 적어도 두 개 이상의 혼합물을 포함하는 해조류 2 내지 40중량부;
황토, 모래, 고령토, 점토, 마사토, 규사 또는 이들의 혼합물인 흙 10 내지 70중량부;장석, 흑운모, 백운모, 석영석, 활석, 형석, 제올라이트 또는 이들의 혼합물인 광물 10 내지 70중량부;
알루미늄, 마그네슘, 규소 또는 이들의 혼합물인 금속분말 5 내지 30중량부;
폴리에틸렌옥시드, 폴리비닐파이롤리돈, 셀룰로즈 수지, 폴리비닐알콜, 폴리비닐아세테이트, 에폭시 수지, 실리콘 수지, 우레탄 수지, 아크릴 수지 또는 이들의 혼합물이거나 클로로프렌 고무, 부틸고무, 스티렌부타디엔 고무, 부타디엔 고무 또는 이들의 혼합물인 바인더 10 내지 50중량부;
헥사메틸렌테트라민, 아민류, 폴리아마이드 또는 이들의 혼합물로 이루어진 경화제 2 내지 30중량부;
분말도가 3,000 내지 3,800cm2/g이고, 밀도가 1.5 내지 2.8g/cm3인 미분쇄한 플라이 애시와 분말도가 블레인(blaine) 비표면적으로 4,000 내지 12,000cm2/g인 제지 애시가 1:9 내지 9:1 중량비로 혼합된 애시 20 내지 30중량부;
불포화 폴리에스터 수지로 이루어진 저수축제 1 내지 10중량부;
6PPD(N-(1,3-dimethylutyl)-N'-phenyl-p-phenylenediamine) 및 TAPDT(2,4,6-tris-(N-1,4-dimethylpentyl-p-phenylenediamino)-1,3,5-triazine)가 혼합된 열화방지제 1 내지 5중량부; 및
나프탈렌계 고성능 감수제가 80 내지 95중량%이고, 폴리카르복실산형 고성능 감수제가 5 내지 20중량%인 고성능 감수제 0.01 내지 10중량부를 포함하는 콘크리트 블록 조성물에,
입경이 60 내지 1,130㎛ 크기의 범위를 갖는 석영계 천연석 또는 유리입자인 투명성 논슬립(Non-Slip)입자를 콘크리트 블록 조성물 100중량부를 기준으로 5 내지 15중량부로 더 포함하고,
단섬유, 장섬유, 필라멘트, 위스커(whisker), 토우(tow), 직물, 매트(mat), 펠트(felt) 또는 이들의 혼합물인 파이버를 콘크리트 블록 조성물 100중량부 기준으로 5 내지 20중량부로 더 포함하며,
발포제 또는 기포제로서 코코넛 오일을 콘크리트 블록 조성물 100중량부 기준으로 1 내지 10중량부로 더 포함하고,The present invention
Based on 100 parts by weight of cement,
It is the cousin of the sea bream, the sea bream, the sea bream, the sea bream, the hearing, the bead hearing, the jade, the salt weekend, the seaweed, the kelp, , Goby, horns, horns, trichuris, chrysanthemum, chestnut, chestnut, chestnut, chestnut, chestnut, dog gambling, From 2 to 40 parts by weight of seaweeds comprising a mixture of at least two selected from among rocks, gypsum, guinea pigs, or mixtures thereof;
10 to 70 parts by weight of clay, earth, sand, kaolin, clay, margarine, silica or mixtures thereof 10 to 70 parts by weight of feldspar, biotite, muscovite, quartzite, talc, fluorite, zeolite or mixtures thereof;
5 to 30 parts by weight of a metal powder which is aluminum, magnesium, silicon or a mixture thereof;
Polyvinyl pyrrolidone, cellulose resin, polyvinyl alcohol, polyvinyl acetate, epoxy resin, silicone resin, urethane resin, acrylic resin or a mixture thereof, or chloroprene rubber, butyl rubber, styrene butadiene rubber, butadiene rubber or 10 to 50 parts by weight of a binder which is a mixture thereof;
2 to 30 parts by weight of a curing agent composed of hexamethylenetetramine, amines, polyamide or a mixture thereof;
Pulverized fly ash having a powder viscosity of 3,000 to 3,800 cm 2 / g and a density of 1.5 to 2.8 g / cm 3 and a powdery ash having a blaine specific surface area of 4,000 to 12,000 cm 2 / g : 9 to 9: 1 20 to 30 parts by weight of ash blended;
1 to 10 parts by weight of a water-reducing agent composed of an unsaturated polyester resin;
(2,4,6-tris- (N-1,4-dimethylpentyl-p-phenylenediamino) -1,3,6- 5-triazine) is mixed with 1 to 5 parts by weight of an anti-deterioration agent; And
To 0.01 to 10 parts by weight of a high-performance water reducing agent having a naphthalene-based high-performance water reducing agent in an amount of 80 to 95% by weight and a polycarboxylic acid type high-performance water reducing agent in an amount of 5 to 20%
Further comprising 5 to 15 parts by weight of transparent non-slip particles, which are quartz-type natural stone or glass particles having a particle size ranging from 60 to 1,130 탆, based on 100 parts by weight of the concrete block composition,
The fiber, which is a short fiber, a long fiber, a filament, a whisker, a tow, a fabric, a mat, a felt or a mixture thereof, is added in an amount of 5 to 20 parts by weight based on 100 parts by weight of the concrete block composition ≪ / RTI &
Further comprising 1 to 10 parts by weight of coconut oil as a foaming agent or foaming agent based on 100 parts by weight of the concrete block composition,
스트론튬, 바나듐, 지르코늄, 세륨, 녜어디뮴, 란탄, 바륨, 류비듐, 세슘 또는 갈륨인 음이온 방출물질 및 석영, 몬조나이트, 편마암류 또는 유문암질 응회암인 원적외선 방출물질이 1:1의 중량비로 혼합된 세라믹 파우더를 콘크리트 블록 조성물 100중량부 기준으로 3 내지 10중량부로 더 포함하는 콘크리트 블록 조성물을 제공한다.
Anion emission materials such as strontium, vanadium, zirconium, cerium, nepheline, lanthanum, barium, rubidium, cesium or gallium and far infrared ray emission materials such as quartz, mononite, gneiss or rhyolitic tuff are mixed at a weight ratio of 1: To 3 to 10 parts by weight based on 100 parts by weight of the concrete block composition.
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
또한, 본 발명은
블록 모양을 갖는 성형틀을 준비하는 성형틀 준비단계;
상기 성형틀 준비단계가 종료된 후 성형틀 내부에 시멘트 100중량부를 기준으로,
가시파래, 홀파래 청태, 해캄, 파래, 청각, 구슬청각, 옥덩굴, 염주말, 미역, 다시마, 헛가지말, 민가지말, 패, 고리매, 미역쇠, 감태, 곰피, 대황, 쇠미역사촌, 모자반, 괭생이 모자반, 지충이, 톳, 김, 우뭇가사리, 불등가사리, 코토니, 개도박, 둥근돌김, 개우무, 새발, 참풀가사리, 꼬시래기, 진두발, 참도박, 가시우무, 비단풀, 단박, 돌가사리, 석목, 지누아리, 또는 이들 중 선택된 적어도 두 개 이상의 혼합물을 포함하는 해조류 2 내지 40중량부, 황토, 모래, 고령토, 점토, 마사토, 규사 또는 이들의 혼합물인 흙 10 내지 70중량부, 장석, 흑운모, 백운모, 석영석, 활석, 형석, 제올라이트 또는 이들의 혼합물인 광물 10 내지 70중량부, 알루미늄, 마그네슘, 규소 또는 이들의 혼합물인 금속분말 5 내지 30중량부, 폴리에틸렌옥시드, 폴리비닐파이롤리돈, 셀룰로즈 수지, 폴리비닐알콜, 폴리비닐아세테이트, 에폭시 수지, 실리콘 수지, 우레탄 수지, 아크릴 수지 또는 이들의 혼합물이거나 클로로프렌 고무, 부틸고무, 스티렌부타디엔 고무, 부타디엔 고무 또는 이들의 혼합물인 바인더 10 내지 50중량부, 헥사메틸렌테트라민, 아민류, 폴리아마이드 또는 이들의 혼합물로 이루어진 경화제 2 내지 30중량부, 분말도가 3,000 내지 3,800cm2/g이고, 밀도가 1.5 내지 2.8g/cm3인 미분쇄한 플라이 애시와 분말도가 블레인(blaine) 비표면적으로 4,000 내지 12,000cm2/g인 제지 애시가 1:9 내지 9:1 중량비로 혼합된 애시 20 내지 30중량부, 불포화 폴리에스터 수지로 이루어진 저수축제 1 내지 10중량부, 6PPD(N-(1,3-dimethylutyl)-N'-phenyl-p-phenylenediamine) 및 TAPDT(2,4,6-tris-(N-1,4-dimethylpentyl-p-phenylenediamino)-1,3,5-triazine)가 혼합된 열화방지제 1 내지 5중량부, 및 나프탈렌계 고성능 감수제가 80 내지 95중량%이고, 폴리카르복실산형 고성능 감수제가 5 내지 20중량%인 고성능 감수제 0.01 내지 10중량부를 포함하는 콘크리트 블록 조성물에, 입경이 60 내지 1,130㎛ 크기의 범위를 갖는 석영계 천연석 또는 유리입자인 투명성 논슬립(Non-Slip)입자를 콘크리트 블록 조성물 100중량부를 기준으로 5 내지 15중량부로 더 포함하고, 단섬유, 장섬유, 필라멘트, 위스커(whisker), 토우(tow), 직물, 매트(mat), 펠트(felt) 또는 이들의 혼합물인 파이버를 콘크리트 블록 조성물 100중량부 기준으로 5 내지 20중량부로 더 포함하며, 발포제 또는 기포제로서 코코넛 오일을 콘크리트 블록 조성물 100중량부 기준으로 1 내지 10중량부로 더 포함하고, 스트론튬, 바나듐, 지르코늄, 세륨, 녜어디뮴, 란탄, 바륨, 류비듐, 세슘 또는 갈륨인 음이온 방출물질 및 석영, 몬조나이트, 편마암류 또는 유문암질 응회암인 원적외선 방출물질이 1:1의 중량비로 혼합된 세라믹 파우더를 콘크리트 블록 조성물 100중량부 기준으로 3 내지 10중량부로 더 포함하는 콘크리트 블록 조성물과 물을 타설하는 타설단계;
상기 타설단계가 종료된 후 콘크리트 블록 조성물을 양생하는 양생단계; 및In addition,
Preparing a mold for preparing a mold having a block shape;
After completion of the forming mold preparation step,
It is the cousin of the sea bream, the sea bream, the sea bream, the sea bream, the hearing, the bead hearing, the jade, the salt weekend, the seaweed, the kelp, , Goby, horns, horns, trichuris, chrysanthemum, chestnut, chestnut, chestnut, chestnut, chestnut, dog gambling, From 2 to 40 parts by weight of seaweeds comprising a mixture of at least two selected from the group consisting of marbled rocks, gypsum, guinea pigs and mixtures of at least two of these selected from the group consisting of clay, sand, kaolin, clay, 5 to 30 parts by weight of a metal powder which is aluminum, magnesium, silicon or a mixture thereof, feldspar, biotite, muscovite, quartzite, talc, fluorite, zeolite or a mixture thereof, Vinyl pyrrolidone, cellulose number 10 to 50 parts by weight of a binder which is a polyvinyl alcohol, a polyvinyl acetate, an epoxy resin, a silicone resin, a urethane resin, an acrylic resin or a mixture thereof or a chloroprene rubber, butyl rubber, styrene butadiene rubber, butadiene rubber or a mixture thereof, tetramine, amine, polyamide curing agent, or a mixture thereof 2 to 30 parts by weight, the fineness of 3,000 to 3,800cm 2 / g and a density of 1.5 to 2.8g / cm 3 of the fly ash and pulverized powder 20 to 30 parts by weight of ash mixed with papermaking ash having a blaine specific surface area of 4,000 to 12,000 cm 2 / g in a weight ratio of 1: 9 to 9: 1, 1 to 10 parts by weight of an unsaturated polyester resin (2,4,6-tris- (N-1,4-dimethylpentyl-p-phenylenediamino) -1, 3,5-triazine) is mixed with 1 to 5 parts by weight of an antioxidant, Based concrete composition comprising 80 to 95% by weight of a phthalene-based high-performance water reducing agent and 0.01 to 10 parts by weight of a high-performance water reducing agent having a polycarboxylic acid type high-performance water reducing agent in an amount of 5 to 20% by weight, And further comprises 5-15 parts by weight of transparent non-slip particles, which are quartz-type natural stone or glass particles, based on 100 parts by weight of the concrete block composition, and further comprising 5-15 parts by weight of short fiber, long fiber, filament, whisker, tow, A fiber, a mat, a felt, or a mixture thereof, in an amount of 5 to 20 parts by weight based on 100 parts by weight of the concrete block composition, wherein the coconut oil as a foaming agent or foaming agent is used in an amount of 100 parts by weight Anion releasing material further comprising 1 to 10 parts by weight of at least one anion selected from the group consisting of strontium, vanadium, zirconium, cerium, nepheline, lanthanum, barium, A concrete block composition further comprising 3 to 10 parts by weight of a ceramic powder having 100 parts by weight of a concrete block composition, wherein the ceramic powder is mixed with a weight ratio of 1: 1 of far-infrared ray emitting material which is quartz, mononite, gneiss or rhyolitic tuff, Casting step;
A curing step of curing the concrete block composition after the pouring step is completed; And
상기 양생단계가 종료된 후 성형틀을 제거하는 성형틀 제거단계를 포함하는 콘크리트 블록 제조방법을 제공한다.
And removing the mold from the mold after the curing step is completed.
삭제delete
삭제delete
삭제delete
본 발명에 따른 콘크리트 블록 조성물은 콘크리트 블록이 요구하는 내구성, 압축강도 등의 물성을 만족하는 콘크리트 블록을 제공한다.
The concrete block composition according to the present invention provides a concrete block satisfying physical properties such as durability and compressive strength required by a concrete block.
이하, 본 발명을 구체적으로 설명한다.Hereinafter, the present invention will be described in detail.
한 가지 관점에서, 본 발명은 시멘트 100중량부를 기준으로, 해조류 2 내지 40중량부; 흙 10 내지 70중량부; 광물 10 내지 70중량부; 금속분말 5 내지 30중량부; 바인더 10 내지 50중량부; 경화제 2 내지 30중량부; 애시 20 내지 30중량부; 저수축제 1 내지 10중량부; 열화방지제 1 내지 5중량부; 및 고성능 감수제 0.01 내지 10중량부를 포함하는 콘크리트 블록 조성물을 제공한다.In one aspect, the present invention relates to a cement composition comprising, based on 100 parts by weight of cement, 2 to 40 parts by weight of seaweeds; 10 to 70 parts by weight of soil; 10 to 70 parts by weight of minerals; 5 to 30 parts by weight of a metal powder; 10 to 50 parts by weight of a binder; 2 to 30 parts by weight of a curing agent; 20 to 30 parts by weight of ash; 1 to 10 parts by weight of a water reducing festival; 1 to 5 parts by weight of an anti-deterioration agent; And 0.01 to 10 parts by weight of a high-performance water reducing agent.
다른 관점에서, 본 발명은 블록 모양을 갖는 성형틀을 준비하는 성형틀 준비단계; 상기 성형틀 준비단계가 종료된 후 성형틀 내부에 시멘트 100중량부를 기준으로, 해조류 2 내지 40중량부, 흙 10 내지 70중량부, 광물 10 내지 70중량부, 금속분말 5 내지 30중량부, 바인더 10 내지 50중량부, 경화제 2 내지 30중량부, 애시 20 내지 30중량부, 저수축제 1 내지 10중량부, 열화방지제 1 내지 5중량부, 및 고성능 감수제 0.01 내지 10중량부를 포함하는 콘크리트 블록 조성물과 물을 타설하는 타설단계; 상기 타설단계가 종료된 후 콘크리트 블록 조성물을 양생하는 양생단계; 및 상기 양생단계가 종료된 후 성형틀을 제거하는 성형틀 제거단계를 포함하는 콘크리트 블록 제조방법을 제공한다.According to another aspect of the present invention, there is provided a method of manufacturing a mold, comprising: preparing a mold for preparing a mold having a block shape; After completion of the forming mold preparation step, 2 to 40 parts by weight of seaweed, 10 to 70 parts by weight of earth, 10 to 70 parts by weight of mineral, 5 to 30 parts by weight of metal powder, A concrete block composition comprising 10 to 50 parts by weight of a curing agent, 2 to 30 parts by weight of an ash, 20 to 30 parts by weight of an ash, 1 to 10 parts by weight of a water reducing agent, 1 to 5 parts by weight of a deterioration inhibitor and 0.01 to 10 parts by weight of a high- A pouring step for pouring water; A curing step of curing the concrete block composition after the pouring step is completed; And a mold removing step of removing the mold after the curing step is completed.
본 발명에 따른 콘크리트 블록 조성물, 바람직하게는 해조류를 이용한 친환경 콘크리트 블록 조성물은 건축 구조물 또는 도로포장 등에 사용되는 블록, 예를 들면 일반 블록, 보도블록, 조경용 블록 또는 보강토용 블록을 제조하기 위한 조성물이다.The concrete block composition according to the present invention, preferably an eco-concrete block composition using algae, is a composition for producing blocks used for building structures, road pavement, etc., for example, general blocks, sidewalk blocks, landscape blocks or reinforcing soil blocks .
본 발명에 따른 시멘트는 당업계에서 통상적으로 사용되는 시멘트라면 특별히 한정되지 않지만, 바람직하게는 일반 포틀랜드 시멘트, 백시멘트 또는 고로슬래그시멘트, 초미분말시멘트 등의 특수 시멘트 등을 사용할 수 있다.The cement according to the present invention is not particularly limited as long as it is a cement conventionally used in the art, but it is preferable to use special Portland cement, white cement, blast furnace slag cement, ultra fine powder cement, and other special cements.
상기 시멘트의 바람직한 분말도는 3,200 내지 6,500cm2/g인 것이 좋다.The preferred powder of the cement is preferably 3,200 to 6,500 cm 2 / g.
본 발명에 따른 콘크리트 블록 조성물의 시멘트 외 나머지 성분들의 함량은 시멘트 100중량부를 기준으로 한다.The content of the remaining components other than cement in the concrete block composition according to the present invention is based on 100 parts by weight of cement.
본 발명에 따른 해조류는 콘크리트 블록 조성물, 특정적으로 친환경 콘크리트 블록 조성물에 포함되어 상기 콘크리트 블록 조성물이 건조 및 경화시에 수축이 커서 갈라지거나 굴곡 및 충격강도가 약하여 용이하게 부서지는 것을 방지한다.The seaweed according to the present invention is contained in a concrete block composition, specifically, an environmentally friendly concrete block composition, and prevents the concrete block composition from being easily broken due to a large shrinkage during drying and curing,
또한, 상기 해조류는 콘크리트 블록 조성물을 구성하는 구성성분들의 결합을 촉진시키고, 균열을 방지할 수 있도록 하는 것으로서, 이러한 목적을 갖는 해조류라면 어떠한 것을 사용하여도 무방하다.In addition, the seaweed promotes the binding of constituents of the concrete block composition and prevents cracks, and any seaweed having such a purpose may be used.
여기서, 상기 해조류는 세계적으로 약 8,000 종, 한국 근해에는 약 500여 종이 서식하고 있으므로, 이들 모두를 사용할 수 있지만, 바람직한 해조류로서 녹조류, 갈조류, 홍조류 또는 이들로부터 선택된 적어도 두 개 이상을 사용하는 것이 좋다.Since about 8,000 species of seaweeds exist in the world and about 500 species live in the sea of Korea, all of them can be used, but it is preferable to use at least two selected from green algae, brown algae, red algae or the like as preferable seaweeds .
바람직한 해조류로 대표적인 것은 녹조류로는 가시파래, 홀파래 청태, 해캄, 파래, 청각, 구슬청각, 옥덩굴, 염주말 등이 사용될 수 있으나 이에 한정되는 것은 아니며, 상기 갈조류로는 미역, 다시마, 헛가지말, 민가지말, 패, 고리매, 미역쇠, 감태, 곰피, 대황, 쇠미역사촌, 모자반, 괭생이 모자반, 지충이, 톳 등이 사용될 수 있으나 이에 한정되는 것은 아니며, 상기 홍조류로는 김, 우뭇가사리, 불등가사리, 코토니, 개도박, 둥근돌김, 개우무, 새발, 참풀가사리, 꼬시래기, 진두발, 참도박, 가시우무, 비단풀, 단박, 돌가사리, 석목, 지누아리 등이 사용될 수 있으나 이에 한정되는 것은 아니다.Examples of the preferable algae include green algae such as barnyardgrass, hallucinophyta, sea cucumber, parasites, hearing, beard hearing, jadebug, and salt weekly, but the present invention is not limited thereto, and the brown algae include seaweed, kelp, But the present invention is not limited thereto. Examples of the red algae include red sea bream, red sea bream, red sea bream, red sea bream, red sea bream, It is also possible to use such as, but not limited to, umbrella, umbrella, kotony, dog gambling, round bud, dog umbrella, umbrella, umbrella, crocodile, umbrella, true gambling, But is not limited thereto.
특정 양태로서, 본 발명에 따른 해조류는 건조된 해조류, 분말 형태의 해조류 또는 끊여서 농축시킨 농축액 형태를 사용할 수도 있지만, 추천하기로는 건조 후 분쇄한 분말 형태의 고형분을 사용하는 것이 좋다.As a specific aspect, seaweeds according to the present invention may be used in the form of dried seaweeds, seaweeds in the form of powders or concentrates in concentrated form, but it is advisable to use a solid form of dried powder after being dried.
바람직한 해조류의 사용량은 시멘트 100중량부를 기준으로 2 내지 40중량부인 것이 좋다.The amount of the algae to be used is preferably 2 to 40 parts by weight based on 100 parts by weight of the cement.
본 발명에 따른 흙은 콘크리트 블록 조성물에 포함되어 시멘트와 섞이며 고형화되는 동시에 블록에 일정한 투수성을 제공할 수 있다.The soil according to the present invention is contained in the concrete block composition and is mixed with the cement to be solidified, and at the same time, it can provide a certain permeability to the block.
이때, 상기 흙의 입도를 작게 할수록 투수성이 감소하며, 종국에는 물이 투과할 수 없는 방수성을 제공하게 된다.At this time, as the particle size of the soil is decreased, the water permeability is decreased, and finally, the waterproofing property that water can not permeate is provided.
여기서, 상기 흙은 당업계에서 통상적으로 사용되는 흙이라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 황토, 모래, 고령토, 점토, 마사토, 규사 또는 이들의 혼합물인 것이 좋다.The soil may be any earth soil conventionally used in the art, but it is preferably earth soil, sand, kaolin, clay, marathon, silica or a mixture thereof.
여기서, 상기 규사는 특별히 한정되지 않지만, 추천하기로는 규사2호 또는 규사3호 또는 이들의 혼합물을 사용하는 것을 추천한다.Here, the silica sand is not particularly limited, but it is recommended to use silica sand No. 2 or silica sand No. 3 or a mixture thereof.
바람직한 흙 사용량은 시멘트 100중량부를 기준으로 10 내지 70중량부인 것이 좋다.The amount of the soil used is preferably 10 to 70 parts by weight based on 100 parts by weight of the cement.
본 발명에 따른 광물은 균질한 결정질의 고체로서, 화학조성이 일정하고 원자배열이 규칙적으로 배열되어 콘크리트 블록의 강도를 향상시키고, 변형을 방지할 뿐만 아니라 마찰력을 제공하여 미끄럼을 방지하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 광물이라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 장석, 흑운모, 백운모, 석영석, 활석, 형석, 제올라이트 또는 이들의 혼합물을 사용하는 것이 좋고, 그 사용량은 시멘트 100중량부를 기준으로 10 내지 70중량부인 것이 바람직하다.The mineral according to the present invention is a homogeneous crystalline solid having a uniform chemical composition and regularly arranged atomic arrangement to improve the strength of a concrete block and prevent deformation and provide a frictional force to prevent slipping, It is preferable to use feldspathic, biotite, muscovite, quartzite, talc, fluorite, zeolite, or a mixture thereof, and the amount thereof is preferably in the range of 0.1 to 10 mass% It is preferably 10 to 70 parts by weight based on 100 parts by weight of the polymer.
본 발명에 따른 금속분말은 콘크리트 블록의 전자파차폐효과를 부여하는 동시에 내구성을 향상시키고, 마찰력을 제공하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 금속분말 이라면 특별히 한정되지 않지만, 바람직하게는 알루미늄, 마그네슘, 규소 또는 이들의 혼합물을 사용하는 것이 좋고, 그 사용량은 시멘트 100중량부 기준으로 5 내지 30중량부인 것을 추천한다. The metal powder according to the present invention is for imparting an electromagnetic wave shielding effect to a concrete block, improving durability and providing frictional force, and is not particularly limited as long as it is a typical metal powder in the related art having such an object, , Magnesium, silicon or a mixture thereof is preferably used, and it is recommended that the amount thereof is 5 to 30 parts by weight based on 100 parts by weight of cement.
이때, 상기 금속분말은 콘크리트 블록을 제조하기 위한 양생 또는 소성과정에서 금속산화물로 변형되어 콘크리트 블록에 안료를 첨가하는 경우 착색효과를 더욱 향상시킬 수 있다.At this time, the metal powder is transformed into a metal oxide during the curing or firing process for producing the concrete block, so that the coloring effect can be further improved when the pigment is added to the concrete block.
본 발명에 따른 바인더는 상기 콘크리트 블록 조성물에 포함되어 부착성 및 구성성분들 간의 결합력을 제공하는 동시에 강도를 향상시키고 균열 발생을 억제하기 위한 것으로서, 이러한 목적을 위한 바인더라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 폴리에틸렌옥시드, 폴리비닐파이롤리돈, 셀룰로즈 수지, 폴리비닐알콜, 폴리비닐아세테이트, 에폭시 수지, 실리콘 수지, 우레탄 수지, 아크릴 수지 또는 이들의 혼합물이거나 클로로프렌 고무, 부틸고무, 스티렌부타디엔 고무, 부타디엔 고무 또는 이들의 혼합물을 사용하는 것이 좋다.The binder according to the present invention is included in the concrete block composition so as to provide bonding strength between the adhesive and the constituent components, while improving the strength and suppressing cracking, and any kind of binder may be used for this purpose Polyvinyl alcohol, polyvinyl acetate, an epoxy resin, a silicone resin, a urethane resin, an acrylic resin or a mixture thereof, or a mixture of a chloroprene rubber, a butyl rubber, a styrene butadiene rubber , Butadiene rubber, or a mixture thereof.
특정적으로, 본 발명에 따른 바인더는 콘크리트 블록 조성물을 이용하여 제조되는 콘크리트블록의 치수안정성을 향상시키기 위해 무기물, 금속염 및/또는 금속분말 등을 사용할 수 있으며, 이러한 경우 바람직하는 무기물, 금속염 및/또는 금속분말은 황산칼슘, 규산 염, 규산 알루미나, 칼슘 알루미네이트, 알루미나계 금속분말 또는 이들의 혼합물을 사용하는 것이 좋다.In particular, the binder according to the present invention may be formed of an inorganic material, a metal salt and / or a metal powder to improve the dimensional stability of the concrete block produced using the concrete block composition. In this case, the preferable inorganic material, metal salt and / Or the metal powder is preferably calcium sulfate, silicate, alumina silicate, calcium aluminate, alumina-based metal powder or a mixture thereof.
이때, 상기 바인더의 함량은 특별히 제한되지 않지만, 콘크리트 블록 조성물에 포함된 시멘트 100중량부를 기준으로 10 내지 50중량부를 포함하는 것이 좋다.At this time, the content of the binder is not particularly limited, but it is preferable that the binder includes 10 to 50 parts by weight based on 100 parts by weight of the cement contained in the concrete block composition.
본 발명에 따른 경화제는 콘크리트 블록 조성물을 경화시키기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 경화제, 예를 들면, 헥사메틸렌테트라민, 아민류, 폴리아마이드 또는 이들의 혼합물로 이루어진 경화제라면 어떠한 것을 사용하여도 무방하다.The curing agent according to the present invention is used for curing a concrete block composition, and any curing agent that is conventionally used in the art having such a purpose, for example, a hexamethylenetetramine, an amine, a polyamide, It is also acceptable.
바람직한 경화제의 사용량은 시멘트 100중량부를 기준으로 2 내지 30중량부를 사용하는 것이 좋다.The amount of the hardener to be used is preferably 2 to 30 parts by weight based on 100 parts by weight of the cement.
본 발명에 따른 애시는 콘크리트 블록 조성물에 적량 혼합하여 사용하면 가공성이 개선되고 경화열이 완화됨과 더불어 장기적인 강도 및 수밀성을 향상시킬 수 있다.When the ash according to the present invention is mixed with the concrete block composition in an appropriate amount, the workability is improved and the hardening heat is alleviated, and the long-term strength and water tightness can be improved.
이에, 상기 애시는 전술한 목적으로 사용되는 애시라면 특별히 한정되지 않지만, 바람직하게는 플라이 애시 및/또는 제지 애시를 사용하는 것이 좋다.Thus, the ash is not particularly limited as long as it is used as the above-mentioned purpose, but it is preferable to use fly ash and / or paper ash.
상기 플라이 애시는 미분탄을 연소하는 보일러의 연도 가스로부터 집진기로 채취한 석탄재를 의미하는 것으로서, 구상인 입자 크기는 시멘트와 같은 정도이고, 알루미나와 실리카가 주성분이다.The fly ash refers to coal ash collected from a flue gas of a boiler that burns pulverized coal with a dust collector. The spherical particle size is similar to that of cement, and alumina and silica are the main components.
특정 양태로서, 본 발명에 따른 플라이 애시는 미분쇄한 플라이 애시를 사용할 수 있는바, 상기 미분쇄한 플라이 애시는 미분쇄하지 않은 플라이 애시를 사용하는 것 보다 향상된 고강도성 및/또는 유동성을 제공한다.As a specific aspect, the fly ash according to the present invention can use finely pulverized fly ash, and the finely pulverized fly ash provides improved high strength and / or fluidity than using non-pulverized fly ash .
이때, 본 발명에 따른 미분쇄한 플라이 애시의 분말도는 3,000 내지 3,800cm2/g, 바람직하게는 3,000 내지 3,800cm2/g, 보다 바람직하게는 3,700cm2/g 미만이고, 밀도는 1.5 내지 2.8g/cm3, 바람직하게는 약 2.2g/cm3인 것이 좋다.The fineness of the pulverized fly ash according to the present invention is in the range of 3,000 to 3,800 cm 2 / g, preferably 3,000 to 3,800 cm 2 / g, more preferably 3,700 cm 2 / g, Cm < 2 >, preferably about 2.2 g / cm < 3 >.
한편, 상기 제지 애시는 시멘트의 수화시 발열반응에 의해 형성될 수 있는 수화물과 상온에서 서서히 반응하여 불용성의 화합물을 생성할 수 있도록 한다.On the other hand, the paper ash gradually reacts with the hydrate which can be formed by the exothermic reaction upon hydration of the cement, so as to generate an insoluble compound at room temperature.
이러한 제지 애시는 특별히 한정되지 않지만, 바람직하게는 폐기물로 처리되어 왔던 제지공장 슬러지를 500 내지 1,300℃ 정도의 온도에서 열처리하여 얻은 애시를 분말도가 블레인(blaine) 비표면적으로 4,000 내지 12,000cm2/g인 정도가 되도록 분쇄한 것을 사용하는 것이 좋다.The papermaking ash is not particularly limited, but preferably, the ash obtained by heat-treating the paper mill sludge which has been treated with waste at a temperature of about 500 to 1,300 ° C is blasted at a blaine specific surface area of 4,000 to 12,000 cm 2 / g or less.
특히, 상기 제지 애시는 콘크리트 블록 조성물에 포함되어 고강도성, 고내구성 및 유동성을 향상시킬 수 있다.In particular, the paper ash can be incorporated into a concrete block composition to improve high strength, high durability and fluidity.
특정 양태로서, 본 발명에 따른 애시는 플라이 애시와 제지 애시를 1:9 내지 9:1 중량비, 바람직하게는 2:8 내지 8:2의 중량비로 혼합하여 콘크리트 블록 조성물의 강도, 수밀성 및 보수성뿐만 아니라 내구성과 유동성을 함께 향상시킬 수 있다.As a specific aspect, the ash according to the present invention may be prepared by mixing fly ash and paper ash with a weight ratio of 1: 9 to 9: 1 by weight, preferably 2: 8 to 8: 2 to obtain the strength, water tightness and water retention But also enhance durability and fluidity.
바람직한 애시의 사용량은 시멘트 100중량부를 기준으로 20 내지 30중량부인 것이 좋다.Preferably, the amount of the ash to be used is 20 to 30 parts by weight based on 100 parts by weight of the cement.
본 발명에 따른 저수축제는 콘크리트 블록 조성물이 수축되는 것을 방지하기 위한 것으로서, 이러한 목적을 위한 저숙축제라면 특별히 한정되지 않지만, 바람직하게는 폴리에스터계 저수축제, 특정적으로 불포화 폴리에스터 수지로 이루어진 저수축제를 사용하는 것이 좋고, 그 사용량은 시멘트 100중량부를 기준으로 1 내지 10중량부를 사용하는 것이 바람직하다.The water-reducing agent according to the present invention is for preventing the concrete block composition from being shrunk and is not particularly limited as long as it is a low-melting festival for this purpose, but preferably a polyester- It is preferable to use a festival, and it is preferable to use 1 to 10 parts by weight based on 100 parts by weight of cement.
본 발명에 따른 열화방지제는 콘크리트 블록 조성물의 열화를 방지하기 위한 것이다.The deterioration inhibitor according to the present invention is intended to prevent the deterioration of the concrete block composition.
특히, 상기 열화방지제, 특정적으로 오존열화방지제는 6PPD (N-(1,3-dimethylutyl)-N'-phenyl-p-phenylenediamine) 및/또는 TAPDT(2,4,6-tris-(N-Particularly, the deterioration inhibitor, specifically the ozone deterioration inhibitor, is preferably selected from the group consisting of N- (1,3-dimethylutyl) -N'-phenyl-p-phenylenediamine and / or TAPDT (2,4,6-
1,4-dimethylpentyl-p-phenylenediamino)-1,3,5-triazine)를 포함하여 수중에서 활성화된 오존라디칼의 산화작용에 의한 콘크리트의 촉진열화작용을 오존열화방지제 분자구조에 아민과 결합된 방향족 고리화합물 거대분자의 이중결합부분이 자유전자 이동현상에 의해 활성화된 오존라디칼과 상쇄되어 콘크리트 블록 조성물의 열화 방지 및 열화를 지연시킬 수 있다.The effect of accelerated deterioration of concrete by oxidation of activated ozone radicals in water, including 1,4-dimethylpentyl-p-phenylenediamino) -1,3,5-triazine, The double bond portion of the ring compound macromolecule may be counteracted with the ozone radical activated by the free electron transfer phenomenon, so that deterioration prevention and deterioration of the concrete block composition may be delayed.
즉, 상기 오존열화방지제는 페닐렌디아민(Phenylenediamine-based)계 왁스를 사용할 수 있고, 6PPD와 TAPDT을 포함하는 혼합수지 조성을 사용하거나 라디칼 생성이 활발한 방향족 폴리아민계 등을 사용할 수 있으며, 특히 페닐렌디아민계를 사용하는 것이 바람직하다.That is, the ozone deterioration inhibitor may be a phenylenediamine-based wax, a mixed resin composition containing 6PPD and TAPDT, or an aromatic polyamine system in which radical generation is active. In particular, phenylenediamine- It is preferable to use a system.
바람직한 열화방지제의 사용량은 시멘트 100중량부를 기준으로 1 내지 5중량부인 것이 좋다.The preferred amount of the deterioration inhibitor to be used is 1 to 5 parts by weight based on 100 parts by weight of the cement.
본 발명에 따른 고성능 감수제는 콘크리트 시공을 할 때 콘크리트 속에 있는 작은 공기 거품을 고르게 하기 위하여 사용하는 혼화제이다. The high performance water reducing agent according to the present invention is an admixture used to adjust small air bubbles in concrete when the concrete is applied.
상기 감수제는 거품을 일으키는 성질이 뛰어난 계면활성제로서, 콘크리트 중에 작은 기포를 고르게 발생시켜 내동결 융해성, 내식성, 내구성 등을 개선한다.The water reducing agent is a surfactant having an excellent bubble-generating property, and generates small bubbles evenly in the concrete to improve freezing-thawing resistance, corrosion resistance, durability and the like.
또한, 상기 감수제는 콘크리트 블록 조성물의 유동성을 좋게 하여 부어 넣기 작업을 용이하게 하고, 굳은 콘크리트의 열전도율을 저하시키며, 수밀성을 향상시키는 등 2차적인 효과도 있다. In addition, the water reducing agent has a secondary effect such as facilitating the pouring work by improving the fluidity of the concrete block composition, lowering the thermal conductivity of hard concrete, and improving water tightness.
이때, 콘크리트 블록 조성물에 사용되는 감수제의 감수율은 일반적으로 10 내지 15%정도이나 그 중 감수율이 20 내지 30%인 것을 본 발명에서는 고성능 감수제라 통칭한다.At this time, the water reducing agent used in the concrete block composition generally has a water reducing rate of about 10 to 15%, but a water reducing rate of 20 to 30% is generally referred to as a high-performance water reducing agent in the present invention.
바람직한 고성능 감수제는 나프탈렌형, 멜라민형, 폴리카르복실산형, 아미노 술폰산형 감수제 또는 이들의 혼합물로 이루어진 것이 좋고, 그 함량은 특별히 제한되지 않고 필요에 따라 적절하게 조절할 수 있으며, 예를 들어 시멘트 100중량부를 기준으로 0.01 내지 10중량부를 사용할 수 있다.The preferred high performance water reducing agent is preferably a naphthalene type, a melamine type, a polycarboxylic acid type, an aminosulfonic acid type water reducing agent or a mixture thereof. The content thereof is not particularly limited and can be appropriately adjusted as required. 0.01 to 10 parts by weight may be used.
이때, 상기 나프탈렌형 감수제로서 대표적인 것은 변성리그닌, 알킬아릴술폰산 및 활성지속폴리머, 폴리알킬아일슬폰산염과 반응성고분자, 알킬아릴술폰산염고축합물, 슬폰산기카르복실기 함유 다원폴리머,리그닌술폰산알카리금속염, 알킬나프탈렌슬폰산염, 알킬아릴술폰산염변성리그닌공축합물과 변성리그닌, 리그닌유도체와 알킬아릴술포네이트 또는 이들로부터 선택된 적어도 하나 이상을 들을 수 있다.Typical examples of the naphthalene-type water reducing agent include modified lignin, alkylaryl sulfonic acid and active persistent polymer, polyalkyl isophosphate and reactive polymer, alkylaryl sulfonic acid salt condensate, sulfonic acid group carboxyl group-containing multi-component polymer, ligninsulfonic acid alkali metal salt, alkyl naphthalene A sulfonate salt, an alkylaryl sulfonate modified lignin co-condensate and modified lignin, a lignin derivative and an alkylaryl sulfonate, or at least one selected from the foregoing.
상기 멜라민형 감수제로서 대표적인 것은 변성메칠멜라민축합물과 수용성특수고분자화합물, 슬폰화멜라민고축합물 또는 이들로부터 선택된 하나 이상의 혼합물을 들을 수 있다.Representative examples of the melamine-type water reducing agent include a modified methylmelamine condensate and a water-soluble special polymer compound, a sulfonated melamine condensate, and a mixture of at least one selected from the foregoing.
상기 폴리카르복실산형 감수제로서 대표적인 것은 불포화 카르복시산 단량체를 단일 성분으로 포함하는 공중합체 또는 그의 염, 예컨대, 폴리모노메타크릴레이트, 폴리(알킬렌 글리콜)모노아크릴레이트, 폴리(알킬렌 글리콜)모노메타크릴레이트, 무수말레인산 및 스티렌의 공중합체, 아크릴레이트나 메타크릴레이트의 공중합체 및 이들 단량체와 공중합가능한 단량체로부터 유도되는 공중합체 등을 포함할 수 있다.Representative examples of the polycarboxylic acid type water reducing agent include a copolymer or a salt thereof containing an unsaturated carboxylic acid monomer as a single component, for example, a polyimonomethacrylate, a poly (alkylene glycol) monoacrylate, a poly (alkylene glycol) Copolymers of acrylate and methacrylate, and copolymers derived from monomers copolymerizable with these monomers, and the like.
상기 아미노 술폰산형 감수제로서 대표적인 것은 방향족아미노슬폰산계 고분자화합물, 방향족고분자축합물과 리그닌슬폰산유도체 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 들을 수 있다.Typical examples of the aminosulfonic acid-based water reducing agent include an aromatic aminosulfonic acid-based polymer compound, an aromatic polymer condensate, a lignin sulfonic acid derivative, and a mixture of at least one selected from the foregoing.
또한, 바람직한 고성능 감수제는 나프탈렌형 고성능 감수제를 단독으로 사용하거나 나프탈렌계 고성능 감수제가 80 내지 95중량%이고, 폴리카르복실산형 고성능 감수제가 5 내지 20중량%로 이루어진 혼합조성을 사용하는 것이 좋다.It is also preferable to use a naphthalene-type high-performance water reducing agent alone or a mixed composition comprising 80 to 95 wt% of a naphthalene-based high-performance water reducing agent and 5 to 20 wt% of a polycarboxylic acid-type high-
상기 고성능 감수제의 사용량은 콘크리트 중의 전 공기량이 용적으로 약 4 내지 6%가 되도록 하는 것이 바람직하다. 너무 많이 사용하면 비경제적일 뿐만 아니라, 압축강도의 감소, 철근과의 부착강도의 저하 등 여러 가지 장애가 일어나므로, 적정 사용량을 엄수해야 한다.The amount of the high-performance water reducing agent is preferably such that the total amount of air in the concrete is about 4 to 6% by volume. If it is used too much, it will not only be economical but also cause various obstacles such as reduction of compressive strength and deterioration of bond strength with reinforcing steel, so proper usage should be strictly observed.
특정 양태로서, 본 발명에 따른 콘크리트 블록 조성물, 특정적으로 친환경 콘크리트 블록 조성물은 유화제를 더 포함할 수 있다.In a particular embodiment, the concrete block composition according to the invention, in particular the environmentally friendly concrete block composition, may further comprise an emulsifier.
여기서, 상기 유화제는 콘크리트 타설을 위해 콘크리트 블록 조성물과 혼합되는 물속에서 콘크리트를 미립자 형태로 분산시키기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 유화제라면 어떠한 것을 사용하여도 무방하다.Herein, the emulsifier is used to disperse concrete in the form of fine particles in water mixed with a concrete block composition for pouring concrete, and any emulsifier that is conventional in the art having such a purpose may be used.
바람직한 유화제로는 수지산나트륨염, 리그닌술폰산알카리금속염, 나프탈렌 설포닉 산(Naphthalene Sulfonic acid) 유도체, 클로로벤젠(Chlorobenzene) 유도체, 고급지방산알카리금속염, 알킬벤젠슬폰산염, 알파-올레핀슬폰산염, 폴리옥시에칠렌알킬페닐에텔류, 알킬아릴슬폰산나트륨류 또는 이들의 혼합물을 사용할 수 있고, 그 사용량은 콘크리트 블록 조성물 100중량부를 기준으로 1 내지 5중량부인 것을 추천한다.Preferred emulsifiers include sodium methacrylate, sodium ligninsulfonate alkali metal salts, naphthalene sulfonic acid derivatives, chlorobenzene derivatives, higher fatty acid alkali metal salts, alkylbenzene sulfonates, alpha-olefin sulfonates, polyoxy Sodium alkylarylsulfonate, or mixtures thereof, and the amount thereof is preferably 1 to 5 parts by weight based on 100 parts by weight of the concrete block composition.
다른 특정 양태로서, 본 발명에 따른 콘크리트 블록 조성물은 부가적으로 자외선 차단제를 더 포함할 수 있다.In another specific embodiment, the concrete block composition according to the present invention may further comprise an ultraviolet screening agent.
이때, 상기 자외선 차단제는 자외선으로부터 콘크리트 블록 조성물을 보호함으로써, 노화를 방지하기 위한 것으로 이러한 목적을 갖는 당업계의 통상적인 자외선 차단제라면 어떠한 것을 사용하여도 무방하다.At this time, the ultraviolet screening agent is used to protect the concrete block composition from ultraviolet rays to prevent aging. Any conventional ultraviolet screening agent having such a purpose may be used.
상기 자외선 차단제의 사용량은 사용자의 선택에 따라 변경 가능하지만, 추천하기로는 콘크리트 블록 조성물 100중량부를 기준으로 1 내지 10중량부를 사용하는 것이 좋다.The use amount of the ultraviolet screening agent may be changed according to the user's choice, but it is recommended to use 1 to 10 parts by weight based on 100 parts by weight of the concrete block composition.
또 다른 특정 양태로서, 본 발명에 따른 콘크리트 블록 조성물은 콘크리트 블록 조성물 100중량부 기준으로 논슬립(Non-Slip)입자 5 내지 15중량부를 더 포함할 수 있다.In another specific embodiment, the concrete block composition according to the present invention may further comprise 5 to 15 parts by weight of non-slip particles based on 100 parts by weight of the concrete block composition.
상기 논슬립입자는 콘크리트 블록 조성물에 포함되어 마찰력을 제공함으로써 차량, 보행자 등이 미끄러지지 않도록 하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 논슬립입자라면 특별히 한정되지 않지만, 바람직하게는 광물분말입자, 세라믹스입자, 유리분말입자, 금속합금분말 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋고, 추천하기로는 규사, 산화알루미늄, 실리콘카바이드, 세라믹골제 또는 이들로부터 선택된 적어도 하나 이상을 사용하는 것이 바람직하다.The non-slip particles are included in the concrete block composition to provide a frictional force to prevent slippage of vehicles, pedestrians and the like. The non-slip particles are not particularly limited as long as they are conventional non-slip particles in the related art. Preferably, Particles, glass powder particles, metal alloy powder or a mixture of at least one selected from these may be preferably used. It is preferable to use at least one selected from silica, aluminum oxide, silicon carbide, ceramic bone, or a mixture thereof.
바람직한 논슬립입자의 다른 일례로서, 본 발명에서는 다이아몬드(Dianmond), 탄화붕소(boron carbide), 에머리(Emery), 알루미나(Alumina), 용융알루미나(Fused alumina), 탄화규소(silicon carbide), 지르코니아(Zirconia), 소결보크사이트(Fused Bauxite), 금강사(Aluminum oxide), 석영(Quartz), 석류석(Garnet) 및/또는 바텀애쉬(Battom ash) 등을 사용할 수 있다.As another example of the preferred non-slip particles, in the present invention, there are used diamond particles such as diamond (Dianmond), boron carbide, emery, alumina, fused alumina, silicon carbide, zirconia Fused Bauxite, Aluminum oxide, Quartz, Garnet and / or Battom ash may be used.
특정적으로, 본 발명에 따른 논슬립입자는 차별적 시인기능을 위해 투명성 논슬립입자를 사용할 수 있다.In particular, the non-slip particles according to the present invention can use transparent non-slip particles for differential visualization.
이러한 투명성 논슬립입자는 콘크리트 블록면의 빛깔에 깊이를 주고, 고휘도의 반사를 가지게 할 수 있어 보다 제어된 색을 연출할 수 있다.These transparency non-slip particles can give a depth to the color of the concrete block surface, have a high brightness reflection, and can produce a more controlled color.
바람직한 투명성 논슬립입자는 투명한 석영계 천연석이나 유리를 분쇄해서 얻은 유리 입자를 사용할 수 있다.Preferable transparent non-slip particles can be transparent quartz-type natural stone or glass particles obtained by grinding glass.
한편, 본 발명에 따른 논슬립입자는 그 크기가 특별히 한정되는 것은 아니지만, 비교적 큰 입경은 60 내지 1,130㎛ 크기의 범위를 가지며, 바람직하게는 140 내지 840㎛의 크기 범위를 갖는 것을 추천한다. On the other hand, the size of the non-slip particles according to the present invention is not particularly limited, but a relatively large particle size is in the range of 60 to 1,130 μm, preferably 140 to 840 μm.
또 다른 특정 양태로서, 본 발명에 따른 콘크리트 블록 조성물은 콘크리트로 제조되는 블록의 균열을 방지하기 위해 콘크리트 블록 조성물 100중량부 기준으로 5 내지 20중량부의 파이버를 더 포함할 수 있다.In another specific embodiment, the concrete block composition according to the present invention may further comprise 5 to 20 parts by weight of fibers based on 100 parts by weight of the concrete block composition to prevent cracking of the block made of concrete.
여기서, 상기 파이버(fiber)는 상기 파이버는 전술한 목적을 갖는 파이버라면 특별히 한정되지 않지만, 바람직하게는 단섬유, 장섬유, 필라멘트, 위스커(whisker), 토우(tow), 직물, 매트(mat) 또는 펠트(felt) 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋다.Here, the fiber is not particularly limited as long as the fiber is the fiber having the above-mentioned purpose, but it is preferably a fiber such as a short fiber, a long fiber, a filament, a whisker, a tow, Or felt, or a mixture of at least one selected from these.
또 다른 특정 양태로서, 본 발명에 따른 콘크리트 블록 조성물은 제조되는 콘크리트 블록의 단열성을 향상시키는 동시에 무게를 감소시키고, 식물 생장을 위한 공극을 제공하기 위하여 콘크리트 블록 조성물 100중량부 기준으로 발포제 또는 기포제 1 내지 10중량부를 더 포함할 수 있다.In another specific embodiment, the concrete block composition according to the present invention is used to improve the heat insulating property of a concrete block to be produced, to reduce weight, and to provide a pore for plant growth. To 10 parts by weight.
여기서, 상기 발포제 또는 기포제는 통상적인 발포제 또는 기포제라면 어떠한 것을 사용하여도 무방하지만, 보다 친환경적인 콘크리트 블록 조성물을 제공하기 위해 동물성 기포제 보다는 식물성 기포제를 사용하는 것이 좋다.Any conventional foaming agent or foaming agent may be used as the foaming agent or foaming agent, but it is preferable to use a vegetable foaming agent rather than an animal foaming agent in order to provide a more environmentally friendly concrete block composition.
바람직한 발포제 또는 기포제로는 코코넛 오일, 왁스, 파라핀유 또는 이들의 혼합물을 사용할 수 있다.Preferred foaming agents or foaming agents include coconut oil, wax, paraffin oil or mixtures thereof.
한편, 상기 발포제 또는 기포제는 그 사용량이 과다하게 첨가되면 콘크리트 블록에 형성되는 공극으로 인하여 강도가 급격히 감소될 수 있으므로, 사용자는 이를 고려하여 부가되는 발포제 또는 기포제의 사용량을 조절하는 것이 바람직하다.On the other hand, if the amount of the foaming agent or foaming agent is excessively added, the strength may be drastically reduced due to the voids formed in the concrete block, so that the user may control the amount of the foaming agent or foaming agent added in consideration of this.
또 다른 특정 양태로서, 본 발명에 따른 콘크리트 블록 조성물은 콘크리트 블록 조성물 100중량부 기준으로 음이온 방출을 제공하는 세라믹 파우더 3 내지 10중량부를 더 포함할 수 있다. In another specific embodiment, the concrete block composition according to the present invention may further comprise 3 to 10 parts by weight of a ceramic powder which provides anion release based on 100 parts by weight of the concrete block composition.
여기서, 상기 세라믹 파우더는 음이온 방출을 제공하는 물질이라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 스트론튬, 바나듐, 지르코늄, 세륨, 녜어디뮴, 란탄, 바륨, 류비듐, 세슘 및/또는 갈륨을 사용하는 것이 좋다.The ceramic powder may be any material as long as it provides anion release. Preferably, the ceramic powder is selected from strontium, vanadium, zirconium, cerium, nepheline, lanthanum, barium, rubidium, cesium and / or gallium It is good to do.
특히, 상기 세라믹 파우더를 구성하는 음이온 방출물질은 원적외선을 방출하는 원적외선 방출물질과 서로 혼합되어 사용될 수 있는바, 이러한 경우 음이온 방출물질과 원적외선 방출물질은 1:1의 중량비로 혼합되는 것이 바람직하지만, 이에 한정되는 것은 아니다.In particular, the anion emitting material constituting the ceramic powder may be mixed with the far-infrared emitting material emitting far-infrared rays. In this case, the anion emitting material and the far-infrared emitting material are preferably mixed at a weight ratio of 1: But is not limited thereto.
바람직한 원적외선 방출물질로는 석영, 몬조나이트, 편마암류 및/또는 유문암질 응회암을 포함한다.Preferred far infrared ray emitting materials include quartz, mononitic, gneissic and / or rhyolitic tuff.
또 다른 특정 양태로서, 본 발명에 따른 콘크리트 블록 조성물은 부가적으로 첨가제를 더 포함할 수 있다.In another specific embodiment, the concrete block composition according to the present invention may additionally comprise additives.
상기 첨가제는 점감제, 안료, 소포제 및/또는 노화방지제일 수 있다.The additive may be a depressant, a pigment, a defoamer and / or an antioxidant.
여기서, 상기 첨가제로 사용되는 점감제, 안료, 소포제 또는 노화방지제는 당업계에서 통상적으로 사용되는 것을 사용하는 것이 바람직하며, 사용량은 전체 콘크리트 블록 조성물 100중량부를 기준으로 1 내지 20중량부를 사용하는 것이 좋다.The amount of the depressant, pigment, antifoaming agent or antioxidant used in the present invention is preferably from 1 to 20 parts by weight based on 100 parts by weight of the total concrete block composition good.
상기 점감제는 트리메산에스테르, 안식향산에스테르, 에틸사이클로헥산, 2,2,4-트리메틸-1,3-펜탄디올디이소부틸레이트 중에서 하나를 사용하는 것이 좋다.It is preferable to use one of dimethic ester, benzoic acid ester, ethylcyclohexane and 2,2,4-trimethyl-1,3-pentanediol diisobutylate as the dimmer.
상기 안료는 무기계 안료 및/또는 유기계 안료를 사용하는 것이 좋다.It is preferable to use an inorganic pigment and / or an organic pigment as the pigment.
상기 무기계 안료는 산화철, 수산화철, 산화크롬, 산화티탄 또는 이들의 혼합물을 포함한다.The inorganic pigments include iron oxide, iron hydroxide, chromium oxide, titanium oxide, or mixtures thereof.
이때, 산화철, 수산화철은 적갈색을 나타내고, 산화크롬은 녹색을 나타내고, 산화티탄은 백색을 나타낸다.At this time, iron oxide and iron hydroxide show reddish brown color, chromium oxide shows green, and titanium oxide shows white.
상기 유기계 안료는 카본 블랙, 아조피그먼트 또는 이들의 혼합물을 사용하는 것이 좋다.The organic pigments may be carbon black, azo pigments or mixtures thereof.
상기 소포제는 저온에서도 소포성, 분산성 및 유화성 등이 탁월한 실리콘계 소포제, 예를 들면 폴리실록산을 주성분으로 하는 소포제를 사용하는 것이 좋다.The antifoaming agent is preferably a defoaming agent containing a silicon-based antifoaming agent, for example, polysiloxane as a main component, which has excellent antifoaming, dispersing and emulsifying properties even at a low temperature.
또한, 상기 노화방지제는 방향족 아민계, 페놀계, 아인산 에스테르계 화합물 또는 이들의 혼합물을 사용하는 것이 좋다.
The antioxidant may be an aromatic amine-based compound, a phenol-based compound, a phosphorous ester-based compound, or a mixture thereof.
전술한 구성을 갖는 본 발명에 따른 콘크리트 블록 조성물, 특정적으로 해조류를 이용한 콘크리트 블록 조성물의 시공방법, 즉 콘크리트 블록 조성물을 이용한 블록 제조방법을 설명하면 다음과 같다.A concrete block composition according to the present invention having the above-mentioned structure, specifically, a method for constructing a concrete block composition using seaweed, that is, a method for producing a block using a concrete block composition will be described below.
여기서, 상기 콘크리트 블록 조성물을 이용한 콘크리트 블록 제조방법은 특별히 한정되지 않지만, 바람직하게는 블록 모양을 갖는 성형틀을 준비하는 성형틀 준비단계;Here, the method of producing a concrete block using the concrete block composition is not particularly limited, but preferably includes the steps of preparing a mold having a block shape;
상기 성형틀 준비단계가 종료된 후 성형틀 내부에 시멘트 100중량부를 기준으로, 해조류 2 내지 40중량부, 흙 10 내지 70중량부, 광물 10 내지 70중량부, 금속분말 5 내지 30중량부, 바인더 10 내지 50중량부, 경화제 2 내지 30중량부, 애시 20 내지 30중량부, 저수축제 1 내지 10중량부, 열화방지제 1 내지 5중량부, 및 고성능 감수제 0.01 내지 10중량부를 포함하는 콘크리트 블록 조성물과 물을 타설하는 타설단계;After completion of the forming mold preparation step, 2 to 40 parts by weight of seaweed, 10 to 70 parts by weight of earth, 10 to 70 parts by weight of mineral, 5 to 30 parts by weight of metal powder, A concrete block composition comprising 10 to 50 parts by weight of a curing agent, 2 to 30 parts by weight of an ash, 20 to 30 parts by weight of an ash, 1 to 10 parts by weight of a water reducing agent, 1 to 5 parts by weight of a deterioration inhibitor and 0.01 to 10 parts by weight of a high- A pouring step for pouring water;
상기 타설단계가 종료된 후 콘크리트 블록 조성물을 양생하는 양생단계; 및A curing step of curing the concrete block composition after the pouring step is completed; And
상기 양생단계가 종료된 후 성형틀을 제거하는 성형틀 제거단계를 포함한다.And a mold removing step of removing the mold after the curing step is completed.
이때, 상기 콘크리트 블록 조성물을 이용한 블록 제조방법은 필요에 따라, 상기 성형틀 제거단계의 후단으로 성형틀이 제거된 블록을 900 내지 1,200℃의 온도에서 소성하는 소성단계를 더 포함할 수 있다.
In this case, the block manufacturing method using the concrete block composition may further include a firing step of firing the block from which the forming mold has been removed to the downstream end of the forming mold removing step, at a temperature of 900 to 1,200 ° C.
이하에서 실시예를 통하여 본 발명을 구체적으로 설명하기로 한다. 그러나 하기의 실시예는 오로지 본 발명을 구체적으로 설명하기 위한 것으로 이들 실시예에 의해 본 발명의 범위를 한정하는 것은 아니다.
Hereinafter, the present invention will be described in detail by way of examples. However, the following examples are for illustrative purposes only and are not intended to limit the scope of the present invention.
[실시예 1][Example 1]
포틀랜드 시멘트 100g, 가시파래 6g, 모래 25g, 제올라이트 20g, 알루미늄 15g, 우레탄 수지 35g, 헥사메틸렌테트라민으로 이루어진 경화제 10g, 플라이 애시 25g, 불포화 폴리에스터 수지 저수축제 5g, 6PPD 3g, 리그닌술폰산알카리금속염 7g 및 폴리모노메타크릴레이트를 포함하는 고성능 감수제 1g을 혼합하여 콘크리트 블록 조성물을 제조하였다.
10 g of curing agent consisting of hexamethylenetetramine, 25 g of fly ash, 5 g of unsaturated polyester resin water reducing agent, 3 g of 6PPD, 7 g of lignin sulfonic acid alkali metal salt, 7 g of lignin sulfonic acid alkali metal salt, 10 g of coconut oil, 20 g of zeolite, 35 g of urethane resin, And 1 g of a high-performance water reducing agent containing poly-monomethacrylate were mixed to prepare a concrete block composition.
[실시예 2][Example 2]
실시예 1과 동일한 방법으로 실시하되, 가시파래 6g 대신 홀파래 2g, 미역 2g 및 우뭇가사리 2g을 사용하여 실시하였다.
The same procedure as in Example 1 was carried out except that 2 g of HORI PALAE, 2 g of seaweed, and 2 g of marigolds were used instead of 6 g of barnyardgrass.
[실시예 3][Example 3]
실시예 1과 동일한 방법으로 실시하되, 수지산나트륨염를 포함하는 유화제 7g을 더 포함시켜 콘크리트 블록 조성물을 제조하였다.
The concrete block composition was prepared in the same manner as in Example 1 except that 7 g of an emulsifier containing a sodium acid salt of sodium hydroxide was further added.
[실시예 4][Example 4]
실시예 1과 동일한 방법으로 실시하되, 탄화붕소를 포함하는 논슬립입자 20g을 더 포함시켜 콘크리트 블록 조성물을 제조하였다.
The concrete block composition was prepared in the same manner as in Example 1 except that 20 g of non-slip particles containing boron carbide was further included.
[실시예 5][Example 5]
실시예 1과 동일한 방법으로 실시하되, 트리메산에스테르를 포함하는 점감제 5g을 더 포함시켜 콘크리트 블록 조성물을 제조하였다.
The concrete block composition was prepared in the same manner as in Example 1 except that 5 g of a dimer containing trimester was further added.
[실시예 6][Example 6]
실시예 1과 동일한 방법으로 실시하되, 폴리실록산을 주성분으로 하는 소포제 5g을 더 포함시켜 콘크리트 블록 조성물을 제조하였다.
The concrete block composition was prepared in the same manner as in Example 1 except that 5 g of a defoaming agent containing polysiloxane as a main component was further added.
[실시예 7][Example 7]
실시예 1과 동일한 방법으로 실시하되, 장섬유로 구성된 파이버 20g을 더 포함시켜 콘크리트 블록 조성물을 제조하였다.
The same procedure as in Example 1 was carried out except that 20 g of fiber composed of long fibers was further included to prepare a concrete block composition.
[실시예 8][Example 8]
실시예 1과 동일한 방법으로 실시하되, 코코넛 오일로 이루어진 기포제 5g을 더 포함시켜 콘크리트 블록 조성물을 제조하였다.
The concrete block composition was prepared in the same manner as in Example 1 except that 5 g of a foaming agent consisting of coconut oil was further added.
[실시예 9][Example 9]
실시예 1과 동일한 방법으로 실시하되, 바륨을 포함하는 음이온 방출물질 10g을 더 포함시켜 콘크리트 블록 조성물을 제조하였다.
The concrete block composition was prepared in the same manner as in Example 1 except that 10 g of an anion emitting material containing barium was further included.
[실시예 10][Example 10]
실시예 1과 동일한 방법으로 실시하되, 아인산 에스테르계 화합물로 이루어진 노화방지제 5g을 더 포함시켜 콘크리트 블록 조성물을 제조하였다.The concrete block composition was prepared in the same manner as in Example 1 except that 5 g of an antioxidant composed of a phosphorous ester compound was further included.
[실험][Experiment]
실시예에 따라 제조된 조성물을 물과 혼합하여 콘크리트 블록을 제조한 후 저온과 표준상태에서의 변형성, 압축강도 및 건조수축율 등을 측정하여 표 1로 나타냈다.
The compositions prepared according to the examples were mixed with water to prepare concrete blocks, and then the deformability, compressive strength, and shrinkage ratio at low temperature and standard conditions were measured and shown in Table 1.
표 1에 나타난 바와 같이, 실시예 1 내지 실시예 10에 따라 제조된 콘크리트 블록 조성물의 콘크리트 타설로 인해 제조된 블록은 충분한 압축강도를 나타내고, 변형성이 없는 것으로 나타났다.
As shown in Table 1, the blocks produced by the concrete pouring of the concrete block composition prepared according to Examples 1 to 10 showed sufficient compressive strength and no deformability.
이상에서 설명한 바와 같이, 본 발명이 속하는 기술 분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예는 모두 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위의 의미 및 범위 그리고 그 등가개념으로부터 도출되는 모두 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.
As described above, those skilled in the art will understand that the present invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. It is therefore to be understood that the embodiments described above are all illustrative and not restrictive. The scope of the present invention should be construed as being included in the scope of the present invention without departing from the scope of the present invention.
Claims (5)
가시파래, 홀파래 청태, 해캄, 파래, 청각, 구슬청각, 옥덩굴, 염주말, 미역, 다시마, 헛가지말, 민가지말, 패, 고리매, 미역쇠, 감태, 곰피, 대황, 쇠미역사촌, 모자반, 괭생이 모자반, 지충이, 톳, 김, 우뭇가사리, 불등가사리, 코토니, 개도박, 둥근돌김, 개우무, 새발, 참풀가사리, 꼬시래기, 진두발, 참도박, 가시우무, 비단풀, 단박, 돌가사리, 석목, 지누아리, 또는 이들 중 선택된 적어도 두 개 이상의 혼합물을 포함하는 해조류 2 내지 40중량부;
황토, 모래, 고령토, 점토, 마사토, 규사 또는 이들의 혼합물인 흙 10 내지 70중량부;장석, 흑운모, 백운모, 석영석, 활석, 형석, 제올라이트 또는 이들의 혼합물인 광물 10 내지 70중량부;
알루미늄, 마그네슘, 규소 또는 이들의 혼합물인 금속분말 5 내지 30중량부;
폴리에틸렌옥시드, 폴리비닐파이롤리돈, 셀룰로즈 수지, 폴리비닐알콜, 폴리비닐아세테이트, 에폭시 수지, 실리콘 수지, 우레탄 수지, 아크릴 수지 또는 이들의 혼합물이거나 클로로프렌 고무, 부틸고무, 스티렌부타디엔 고무, 부타디엔 고무 또는 이들의 혼합물인 바인더 10 내지 50중량부;
헥사메틸렌테트라민, 아민류, 폴리아마이드 또는 이들의 혼합물로 이루어진 경화제 2 내지 30중량부;
분말도가 3,000 내지 3,800cm2/g이고, 밀도가 1.5 내지 2.8g/cm3인 미분쇄한 플라이 애시와 분말도가 블레인(blaine) 비표면적으로 4,000 내지 12,000cm2/g인 제지 애시가 1:9 내지 9:1 중량비로 혼합된 애시 20 내지 30중량부;
불포화 폴리에스터 수지로 이루어진 저수축제 1 내지 10중량부;
6PPD(N-(1,3-dimethylutyl)-N'-phenyl-p-phenylenediamine) 및 TAPDT(2,4,6-tris-(N-1,4-dimethylpentyl-p-phenylenediamino)-1,3,5-triazine)가 혼합된 열화방지제 1 내지 5중량부; 및
나프탈렌계 고성능 감수제가 80 내지 95중량%이고, 폴리카르복실산형 고성능 감수제가 5 내지 20중량%인 고성능 감수제 0.01 내지 10중량부를 포함하는 콘크리트 블록 조성물에,
입경이 60 내지 1,130㎛ 크기의 범위를 갖는 석영계 천연석 또는 유리입자인 투명성 논슬립(Non-Slip)입자를 콘크리트 블록 조성물 100중량부를 기준으로 5 내지 15중량부로 더 포함하고,
단섬유, 장섬유, 필라멘트, 위스커(whisker), 토우(tow), 직물, 매트(mat), 펠트(felt) 또는 이들의 혼합물인 파이버를 콘크리트 블록 조성물 100중량부 기준으로 5 내지 20중량부로 더 포함하며,
발포제 또는 기포제로서 코코넛 오일을 콘크리트 블록 조성물 100중량부 기준으로 1 내지 10중량부로 더 포함하고,
스트론튬, 바나듐, 지르코늄, 세륨, 녜어디뮴, 란탄, 바륨, 류비듐, 세슘 또는 갈륨인 음이온 방출물질 및 석영, 몬조나이트, 편마암류 또는 유문암질 응회암인 원적외선 방출물질이 1:1의 중량비로 혼합된 세라믹 파우더를 콘크리트 블록 조성물 100중량부 기준으로 3 내지 10중량부로 더 포함하는 콘크리트 블록 조성물.Based on 100 parts by weight of cement,
It is the cousin of the sea bream, the sea bream, the sea bream, the sea bream, the hearing, the bead hearing, the jade, the salt weekend, the seaweed, the kelp, , Goby, horns, horns, trichuris, chrysanthemum, chestnut, chestnut, chestnut, chestnut, chestnut, dog gambling, From 2 to 40 parts by weight of seaweeds comprising a mixture of at least two selected from among rocks, gypsum, guinea pigs, or mixtures thereof;
10 to 70 parts by weight of clay, earth, sand, kaolin, clay, margarine, silica or mixtures thereof 10 to 70 parts by weight of feldspar, biotite, muscovite, quartzite, talc, fluorite, zeolite or mixtures thereof;
5 to 30 parts by weight of a metal powder which is aluminum, magnesium, silicon or a mixture thereof;
Polyvinyl pyrrolidone, cellulose resin, polyvinyl alcohol, polyvinyl acetate, epoxy resin, silicone resin, urethane resin, acrylic resin or a mixture thereof, or chloroprene rubber, butyl rubber, styrene butadiene rubber, butadiene rubber or 10 to 50 parts by weight of a binder which is a mixture thereof;
2 to 30 parts by weight of a curing agent composed of hexamethylenetetramine, amines, polyamide or a mixture thereof;
Pulverized fly ash having a powder viscosity of 3,000 to 3,800 cm 2 / g and a density of 1.5 to 2.8 g / cm 3 and a powdery ash having a blaine specific surface area of 4,000 to 12,000 cm 2 / g : 9 to 9: 1 20 to 30 parts by weight of ash blended;
1 to 10 parts by weight of a water-reducing agent composed of an unsaturated polyester resin;
(2,4,6-tris- (N-1,4-dimethylpentyl-p-phenylenediamino) -1,3,6- 5-triazine) is mixed with 1 to 5 parts by weight of an anti-deterioration agent; And
To 0.01 to 10 parts by weight of a high-performance water reducing agent having a naphthalene-based high-performance water reducing agent in an amount of 80 to 95% by weight and a polycarboxylic acid type high-performance water reducing agent in an amount of 5 to 20%
Further comprising 5 to 15 parts by weight of transparent non-slip particles, which are quartz-type natural stone or glass particles having a particle size ranging from 60 to 1,130 탆, based on 100 parts by weight of the concrete block composition,
The fiber, which is a short fiber, a long fiber, a filament, a whisker, a tow, a fabric, a mat, a felt or a mixture thereof, is added in an amount of 5 to 20 parts by weight based on 100 parts by weight of the concrete block composition ≪ / RTI &
Further comprising 1 to 10 parts by weight of coconut oil as a foaming agent or foaming agent based on 100 parts by weight of the concrete block composition,
Anion emission materials such as strontium, vanadium, zirconium, cerium, nepheline, lanthanum, barium, rubidium, cesium or gallium and far infrared ray emission materials such as quartz, mononite, gneiss or rhyolitic tuff are mixed at a weight ratio of 1: Wherein the ceramic powder further comprises 3 to 10 parts by weight based on 100 parts by weight of the concrete block composition.
A block comprising a concrete block composition according to claim 1.
상기 성형틀 준비단계가 종료된 후 성형틀 내부에 시멘트 100중량부를 기준으로,
가시파래, 홀파래 청태, 해캄, 파래, 청각, 구슬청각, 옥덩굴, 염주말, 미역, 다시마, 헛가지말, 민가지말, 패, 고리매, 미역쇠, 감태, 곰피, 대황, 쇠미역사촌, 모자반, 괭생이 모자반, 지충이, 톳, 김, 우뭇가사리, 불등가사리, 코토니, 개도박, 둥근돌김, 개우무, 새발, 참풀가사리, 꼬시래기, 진두발, 참도박, 가시우무, 비단풀, 단박, 돌가사리, 석목, 지누아리, 또는 이들 중 선택된 적어도 두 개 이상의 혼합물을 포함하는 해조류 2 내지 40중량부, 황토, 모래, 고령토, 점토, 마사토, 규사 또는 이들의 혼합물인 흙 10 내지 70중량부, 장석, 흑운모, 백운모, 석영석, 활석, 형석, 제올라이트 또는 이들의 혼합물인 광물 10 내지 70중량부, 알루미늄, 마그네슘, 규소 또는 이들의 혼합물인 금속분말 5 내지 30중량부, 폴리에틸렌옥시드, 폴리비닐파이롤리돈, 셀룰로즈 수지, 폴리비닐알콜, 폴리비닐아세테이트, 에폭시 수지, 실리콘 수지, 우레탄 수지, 아크릴 수지 또는 이들의 혼합물이거나 클로로프렌 고무, 부틸고무, 스티렌부타디엔 고무, 부타디엔 고무 또는 이들의 혼합물인 바인더 10 내지 50중량부, 헥사메틸렌테트라민, 아민류, 폴리아마이드 또는 이들의 혼합물로 이루어진 경화제 2 내지 30중량부, 분말도가 3,000 내지 3,800cm2/g이고, 밀도가 1.5 내지 2.8g/cm3인 미분쇄한 플라이 애시와 분말도가 블레인(blaine) 비표면적으로 4,000 내지 12,000cm2/g인 제지 애시가 1:9 내지 9:1 중량비로 혼합된 애시 20 내지 30중량부, 불포화 폴리에스터 수지로 이루어진 저수축제 1 내지 10중량부, 6PPD(N-(1,3-dimethylutyl)-N'-phenyl-p-phenylenediamine) 및 TAPDT(2,4,6-tris-(N-1,4-dimethylpentyl-p-phenylenediamino)-1,3,5-triazine)가 혼합된 열화방지제 1 내지 5중량부, 및 나프탈렌계 고성능 감수제가 80 내지 95중량%이고, 폴리카르복실산형 고성능 감수제가 5 내지 20중량%인 고성능 감수제 0.01 내지 10중량부를 포함하는 콘크리트 블록 조성물에, 입경이 60 내지 1,130㎛ 크기의 범위를 갖는 석영계 천연석 또는 유리입자인 투명성 논슬립(Non-Slip)입자를 콘크리트 블록 조성물 100중량부를 기준으로 5 내지 15중량부로 더 포함하고, 단섬유, 장섬유, 필라멘트, 위스커(whisker), 토우(tow), 직물, 매트(mat), 펠트(felt) 또는 이들의 혼합물인 파이버를 콘크리트 블록 조성물 100중량부 기준으로 5 내지 20중량부로 더 포함하며, 발포제 또는 기포제로서 코코넛 오일을 콘크리트 블록 조성물 100중량부 기준으로 1 내지 10중량부로 더 포함하고, 스트론튬, 바나듐, 지르코늄, 세륨, 녜어디뮴, 란탄, 바륨, 류비듐, 세슘 또는 갈륨인 음이온 방출물질 및 석영, 몬조나이트, 편마암류 또는 유문암질 응회암인 원적외선 방출물질이 1:1의 중량비로 혼합된 세라믹 파우더를 콘크리트 블록 조성물 100중량부 기준으로 3 내지 10중량부로 더 포함하는 콘크리트 블록 조성물과 물을 타설하는 타설단계;
상기 타설단계가 종료된 후 콘크리트 블록 조성물을 양생하는 양생단계; 및
상기 양생단계가 종료된 후 성형틀을 제거하는 성형틀 제거단계를 포함하는 콘크리트 블록 제조방법.Preparing a mold for preparing a mold having a block shape;
After completion of the forming mold preparation step,
It is the cousin of the sea bream, the sea bream, the sea bream, the sea bream, the hearing, the bead hearing, the jade, the salt weekend, the seaweed, the kelp, , Goby, horns, horns, trichuris, chrysanthemum, chestnut, chestnut, chestnut, chestnut, chestnut, dog gambling, From 2 to 40 parts by weight of seaweeds comprising a mixture of at least two selected from the group consisting of marbled rocks, gypsum, guinea pigs and mixtures of at least two of these selected from the group consisting of clay, sand, kaolin, clay, 5 to 30 parts by weight of a metal powder which is aluminum, magnesium, silicon or a mixture thereof, feldspar, biotite, muscovite, quartzite, talc, fluorite, zeolite or a mixture thereof, Vinyl pyrrolidone, cellulose number 10 to 50 parts by weight of a binder which is a polyvinyl alcohol, a polyvinyl acetate, an epoxy resin, a silicone resin, a urethane resin, an acrylic resin or a mixture thereof or a chloroprene rubber, butyl rubber, styrene butadiene rubber, butadiene rubber or a mixture thereof, tetramine, amine, polyamide curing agent, or a mixture thereof 2 to 30 parts by weight, the fineness of 3,000 to 3,800cm 2 / g and a density of 1.5 to 2.8g / cm 3 of the fly ash and pulverized powder 20 to 30 parts by weight of ash mixed with papermaking ash having a blaine specific surface area of 4,000 to 12,000 cm 2 / g in a weight ratio of 1: 9 to 9: 1, 1 to 10 parts by weight of an unsaturated polyester resin (2,4,6-tris- (N-1,4-dimethylpentyl-p-phenylenediamino) -1, 3,5-triazine) is mixed with 1 to 5 parts by weight of an antioxidant, Based concrete composition comprising 80 to 95% by weight of a phthalene-based high-performance water reducing agent and 0.01 to 10 parts by weight of a high-performance water reducing agent having a polycarboxylic acid type high-performance water reducing agent in an amount of 5 to 20% by weight, And further comprises 5-15 parts by weight of transparent non-slip particles, which are quartz-type natural stone or glass particles, based on 100 parts by weight of the concrete block composition, and further comprising 5-15 parts by weight of short fiber, long fiber, filament, whisker, tow, A fiber, a mat, a felt, or a mixture thereof, in an amount of 5 to 20 parts by weight based on 100 parts by weight of the concrete block composition, wherein the coconut oil as a foaming agent or foaming agent is used in an amount of 100 parts by weight Anion releasing material further comprising 1 to 10 parts by weight of at least one anion selected from the group consisting of strontium, vanadium, zirconium, cerium, nepheline, lanthanum, barium, A concrete block composition further comprising 3 to 10 parts by weight of a ceramic powder having 100 parts by weight of a concrete block composition, wherein the ceramic powder is mixed with a weight ratio of 1: 1 of far-infrared ray emitting material which is quartz, mononite, gneiss or rhyolitic tuff, Casting step;
A curing step of curing the concrete block composition after the pouring step is completed; And
And removing the forming mold after the curing step is completed.