KR101461322B1 - Coating composition for protecting an automobile - Google Patents
Coating composition for protecting an automobile Download PDFInfo
- Publication number
- KR101461322B1 KR101461322B1 KR1020130068906A KR20130068906A KR101461322B1 KR 101461322 B1 KR101461322 B1 KR 101461322B1 KR 1020130068906 A KR1020130068906 A KR 1020130068906A KR 20130068906 A KR20130068906 A KR 20130068906A KR 101461322 B1 KR101461322 B1 KR 101461322B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- automobile
- protecting
- polyurethane
- Prior art date
Abstract
Description
본 발명은 자동차 표면보호용 코팅제 조성물에 관한 것으로, 더욱 상세하게는 차량 표면에 코팅된 후 스크래치가 발생하더라도 자가복원 기능을 나타내어 반영구적인 표면보호 효과를 나타내고, 코팅제 경화 후 상시 연마가 가능하여 부드러운 촉감과 수려한 광택효과를 나타내며, 차량 표면에 이형제 도포 유무에 관계없이 필름형태로 제거가 가능하며, 이형제 도포 및 정도에 따라 제거의 용이성 및 접착성을 조절할 수 있는 자동차 표면보호용 코팅제 조성물에 관한 것이다.
The present invention relates to a coating composition for protecting a surface of an automobile, and more particularly, it relates to a coating composition for protecting a surface of an automobile, more specifically, a self-restoring function even when a scratch is generated after coating on a vehicle surface, The present invention relates to a coating composition for protecting the surface of an automobile, which can be removed in the form of a film regardless of whether or not the release agent is applied on the surface of the vehicle, and can be easily removed and adhered to the surface of the vehicle according to the release agent application and degree.
본 발명은 자동차 표면보호용 코팅제 조성물에 관한 것으로, 더욱 상세하게는 차량 표면에 코팅된 후 스크래치가 발생하더라도 자가복원 기능을 나타내어 반영구적인 표면보호 효과를 나타내고, 코팅제 경화 후 상시 연마가 가능하여 부드러운 촉감과 수려한 광택효과를 나타내며, 차량 표면에 이형제 도포 유무에 관계없이 필름형태로 제거가 가능하며, 이형제 도포 및 정도에 따라 제거의 용이성 및 접착성을 조절할 수 있는 자동차 표면보호용 코팅제 조성물에 관한 것이다.The present invention relates to a coating composition for protecting a surface of an automobile, and more particularly, it relates to a coating composition for protecting a surface of an automobile, more specifically, a self-restoring function even when a scratch is generated after coating on a vehicle surface, The present invention relates to a coating composition for protecting the surface of an automobile, which can be removed in the form of a film regardless of whether or not the release agent is applied on the surface of the vehicle, and can be easily removed and adhered to the surface of the vehicle according to the release agent application and degree.
일반적으로 자동차 도장 공정의 상도도장 중 투명한 클리어 코팅층은 내후성, 내스크래치성, 선영성, 광택성 및 내약품성 등과 같은 물성이 요구되며, 최근에는 대기나 수질의 오염을 최소화하기 위해 분체도장을 실시하거나, 휘발성 유기화합물의 배출을 최소화할 수 있는 수성도료의 이용이 증가하고 있다.Generally, a clear clear coating layer during top coating of an automobile coating process is required to have properties such as weatherability, scratch resistance, glossiness, gloss and chemical resistance, and recently, a powder coating is applied to minimize air and water pollution , The use of water-based paints capable of minimizing the emission of volatile organic compounds is increasing.
종래에 가장 보편적으로 사용되는 자동차용 코팅제는 아크릴과 멜라민의 혼합물을 이용하여 경화시키는 조성물로, 상기와 같은 성분으로 이루어진 조성물은 물에 의한 가수분해가 이루어지며, 코팅막에 스크래치가 쉽게 발생하여 광택의 저하가 빠르게 진행되는 문제점이 있었다.The most commonly used automotive coating agent is a composition which is cured by using a mixture of acrylic and melamine. The composition composed of the above components is hydrolyzed by water, scratches easily occur in the coating film, There is a problem that the deterioration proceeds rapidly.
상기의 문제점을 해결하기 위해 한국등록특허 제10-1052223호 "자동차용 듀얼 경화 이액형 클리어코트 조성물"에는 내스크래치성과 내산성이 개선되며, 코팅과정에서 유해가스의 발생이 없는 조성물이 기재되어 있으나, 상기의 조성물은 차량의 표면에 도포된 후에는 제거가 용이하지 않기 때문에, 상기의 조성물로 이루어진 클리어코트 표면에 스크래치가 다량 발생하여 광택성이 저하되면, 별도로 클리어코트 제거작업을 실시한 후에 다시 클리어코트 조성물을 도포해야하는 문제점이 있었다.
In order to solve the above problems, Korean Patent No. 10-1052223 entitled " Dual Cured Liquid-Type Clearcoat Composition for Automobiles "describes compositions having improved scratch resistance and acid resistance and no generation of noxious gas during the coating process, Since the above composition is not easily removed after being applied to the surface of a vehicle, if a large amount of scratches is generated on the surface of the clear coat made of the composition and the gloss is deteriorated, the clear coat is separately removed, There is a problem that the composition must be applied.
본 발명의 목적은 자동차의 표면에 코팅된 후에 스크래치가 발생하더라도, 자기복원 능력을 나타내어 반영구적인 표면보호 효과를 나타내고, 연마가 가능하여 부드러운 촉감과 수려한 광택효과를 나타내는 코팅막을 제공하는 자동차 표면보호용 코팅제 조성물을 제공하는 것이다.An object of the present invention is to provide a coating film for automobile surface protection which provides a coating film which shows a self-restoring ability even when scratches are generated after coating on the surface of an automobile to exhibit a semi-permanent surface protection effect, To provide a composition.
본 발명의 다른 목적은 자동차의 표면에 필름형태로 형성되기 때문에, 자동차의 도장면으로부터 제거가 용이한 코팅막을 제공하는 자동차 표면보호용 코팅제 조성물을 제공하는 것이다.
Another object of the present invention is to provide a coating composition for automobile surface protection which provides a coating film which is easily removed from a coating surface of an automobile, because it is formed in a film form on the surface of an automobile.
본 발명의 목적은 폴리우레탄이 함유된 주제와 스티렌모노머가 함유된 경화제가 2:1의 중량부 비율로 이루어지는 것을 특징으로 하는 자동차 표면보호용 코팅제 조성물을 제공함에 의해 달성된다.The object of the present invention is achieved by providing a coating composition for protecting an automobile surface which comprises a polyurethane-containing subject and a styrene monomer-containing curing agent in a weight ratio of 2: 1.
본 발명의 바람직한 특징에 따르면, 상기 주제는 폴리우레탄 100 중량부, 아크릴 80 내지 100 중량부, 희석제 120 내지 200 중량부, 광개시제 50 내지 80 중량부, 점도조절제 100 내지 120 중량부 및 레벨링제 3 내지 6 중량부로 이루어지는 것으로 한다.According to a preferred feature of the present invention, the subject matter is a composition comprising 100 parts by weight of polyurethane, 80 to 100 parts by weight of acrylic, 120 to 200 parts by weight of diluent, 50 to 80 parts by weight of photoinitiator, 100 to 120 parts by weight of viscosity adjusting agent, 6 parts by weight.
본 발명의 더 바람직한 특징에 따르면, 상기 폴리우레탄은 경질폴리우레탄과 연질폴리우레탄이 1:0.09 내지 0.1의 중량부로 혼합되어 이루어지는 것으로 한다.According to a further preferred feature of the present invention, the polyurethane is a mixture of a hard polyurethane and a soft polyurethane in a weight ratio of 1: 0.09 to 0.1.
본 발명의 더욱 바람직한 특징에 따르면, 상기 희석제는 N-부틸아세테이트 65 내지 100 중량부, 프로필렌글리콜메틸에테르아세테이트 50 내지 80 중량부 및 메탄올 5 내지 20 중량부로 이루어지는 것으로 한다.According to a more preferred feature of the present invention, the diluent comprises 65 to 100 parts by weight of N-butyl acetate, 50 to 80 parts by weight of propylene glycol methyl ether acetate, and 5 to 20 parts by weight of methanol.
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 광개시제는 메틸이소부틸케톤으로 이루어지는 것으로 한다.According to a further preferred feature of the present invention, the photoinitiator is made of methyl isobutyl ketone.
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 점도조절제는 자일렌으로 이루어지는 것으로 한다.According to a further preferred feature of the present invention, the viscosity modifier is made of xylene.
삭제delete
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 경화제는 자일렌, 스티렌모노머 및 이소시아네이트 올리고머로 이루어지는 것으로 한다.According to a further preferred feature of the present invention, the curing agent is composed of xylene, a styrene monomer and an isocyanate oligomer.
본 발명의 더욱 더 바람직한 특징에 따르면, 상기 경화제는 자일렌 100 중량부, 스티렌모노머 5 내지 15 중량부 및 이소시아네이트 올리고머 15 내지 40 중량부로 이루어지는 것으로 한다.
According to a further preferred feature of the present invention, the curing agent comprises 100 parts by weight of xylene, 5 to 15 parts by weight of a styrene monomer and 15 to 40 parts by weight of an isocyanate oligomer.
본 발명에 따른 자동차 표면보호용 코팅제 조성물은 자동차의 표면에 코팅된 후에 스크래치가 발생하더라도, 자기복원 능력을 나타내어 반영구적인 표면보호 효과를 나타내고, 연마가 가능하여 부드러운 촉감과 수려한 광택효과를 나타내는 코팅막을 제공하는 탁월한 효과를 나타낸다.The coating composition for protecting a surface of an automobile according to the present invention provides a coating film which exhibits a self-restoring ability even when scratches occur after being coated on a surface of an automobile to exhibit a semi-permanent surface protecting effect and can be polished to exhibit soft touch and a glossy effect .
또한, 자동차의 표면에 필름형태로 형성되기 때문에, 자동차의 도장면으로부터 제거가 용이한 코팅막을 제공하는 탁월한 효과를 나타낸다.
Further, since it is formed in the form of a film on the surface of an automobile, it exhibits an excellent effect of providing a coating film which can be easily removed from a painted surface of an automobile.
이하에는, 본 발명의 바람직한 실시예와 각 성분의 물성을 상세하게 설명하되, 이는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 발명을 용이하게 실시할 수 있을 정도로 상세하게 설명하기 위한 것이지, 이로 인해 본 발명의 기술적인 사상 및 범주가 한정되는 것을 의미하지는 않는다.
Hereinafter, preferred embodiments of the present invention and physical properties of the respective components will be described in detail with reference to the accompanying drawings. However, the present invention is not limited thereto, And this does not mean that the technical idea and scope of the present invention are limited.
본 발명에 따른 자동차 표면보호용 코팅제 조성물은 폴리우레탄이 함유된 주제와 스티렌모노머가 함유된 경화제가 2:1의 중량부로 혼합되어 이루어진다.
The automotive surface protective coating composition according to the present invention is prepared by mixing a polyurethane-containing subject and a styrene monomer-containing curing agent in a weight ratio of 2: 1.
상기 주제는 폴리우레탄 100 중량부, 아크릴 80 내지 100 중량부, 희석제 120 내지 200 중량부, 광개시제 50 내지 80 중량부, 점도조절제 100 내지 120 중량부 및 레벨링제 3 내지 6 중량부로 이루어진다.The subject matter is comprised of 100 parts by weight of polyurethane, 80 to 100 parts by weight of acrylic, 120 to 200 parts by weight of diluent, 50 to 80 parts by weight of photoinitiator, 100 to 120 parts by weight of viscosity adjusting agent and 3 to 6 parts by weight of leveling agent.
상기 폴리우레탄은 100 중량부가 함유되며, 본 발명에 따른 자동차 표면보호용 코팅제 조성물에 접착력과 유연성을 부여하여 내충격성과 내마모성을 향상시키는 역할을 한다.The polyurethane contains 100 parts by weight of the polyurethane, and imparts adhesion and flexibility to the coating composition for protecting a surface of an automobile according to the present invention to improve impact resistance and abrasion resistance.
이때, 상기 폴리우레탄은 경질폴리우레탄과 연질 폴리우레탄이 1:0.09 내지 0.1 중량부로 혼합되어 이루어지는 것이 바람직한데, 연질폴리우레탄의 함량이 0.09 중량부 미만이면, 본 발명에 따른 자동차 표면보호용 코팅제 조성물이 자동차의 표면에 코팅되었을 때, 필름형태의 코팅막 형성이 어렵고, 상기 연질폴리우레탄의 함량이 0.1 중량부를 초과하게 되면 자동차의 표면에 형성된 코팅막의 투명성이 저하된다.At this time, the polyurethane preferably comprises 1: 0.09 to 0.1 part by weight of the hard polyurethane and the soft polyurethane. When the content of the soft polyurethane is less than 0.09 part by weight, When coated on the surface of an automobile, it is difficult to form a film in the form of a film. When the content of the flexible polyurethane exceeds 0.1 part by weight, the transparency of the coating film formed on the surface of the automobile is lowered.
또한, 상기 폴리우레탄 성분이 함유된 자동차 표면보호용 코팅제 조성물은 자기복원력이 향상되어, 미세한 스크래치가 발생한 부분이 복원되는 효과를 나타낸다. In addition, the automotive surface protective coating composition containing the polyurethane component exhibits an effect of improving the self-restoring force and restoring the portion where fine scratches have occurred.
상기 아크릴은 80 내지 100 중량부가 함유되며, 코팅막의 외관 및 기계적 물성, 부착력, 내산성, 내스크래치성 등의 각종 기계적 물성을 부여하는 역할을 한다.The acrylic resin contains 80 to 100 parts by weight of the acrylic resin and imparts various mechanical properties such as appearance, mechanical properties, adhesion, acid resistance and scratch resistance of the coating film.
이때, 상기 아크릴의 함량이 80 중량부 미만일 경우에는 코팅막 형성을 위한 최소한의 경화밀도를 갖지 못해 코팅막의 내산성, 내스크래치성 등의 물성이 저하되며, 아크릴의 함량이 100 중량부를 초과하게 되면, 코팅막 외관의 저하 및 작업성 조절이 어려워지고 코팅막이 지나치게 경화되어, 냉한칩성 및 부착성 등이 저하될 수 있다.If the content of acrylic acid is less than 80 parts by weight, the coating film may not have a minimum curing density to form a coating film, thereby deteriorating physical properties such as acid resistance and scratch resistance of the coating film. If the content of acrylic acid exceeds 100 parts by weight, Deterioration of appearance and workability may be difficult, and the coating film may be excessively cured, resulting in deterioration of cold chipping and adhesion.
상기 희석제는 120 내지 200 중량부가 함유되며, N-부틸아세테이트 65 내지 100 중량부, 프로필렌글리콜메틸에테르아세테이트 50 내지 80 중량부 및 메탄올 5 내지 20 중량부로 이루어지는데, 본 발명에 따른 자동차 표면보호용 코팅제 조성물을 희석시켜 코팅과정에서의 작업성을 개선하며, 희석제 성분 자체도 반응에 참여하여 코팅막의 일부를 구성하는 역할을 한다.The diluent is contained in an amount of 120 to 200 parts by weight, and is composed of 65 to 100 parts by weight of N-butyl acetate, 50 to 80 parts by weight of propylene glycol methyl ether acetate, and 5 to 20 parts by weight of methanol. To improve the workability in the coating process, and the diluent component itself participates in the reaction to form a part of the coating film.
상기 희석제의 함량이 120 중량부 미만이면, 본 발명에 따른 자동차 표면보호용 코팅제 조성물의 점도가 지나치게 높아, 코팅과정에서의 작업성이 저하되며, 상기 희석제의 함량이 200 중량부를 초과하게 되면 본 발명에 따른 자동차 표면보호용 코팅제 조성물의 점도가 지나치게 낮아져 작업성이 저하되며, 경화시간이 길어지고, 끈적이는 현상이 발생하게 된다.When the content of the diluent is less than 120 parts by weight, the viscosity of the coating composition for protecting an automobile surface according to the present invention is excessively high, and the workability in the coating process is deteriorated. When the content of the diluent exceeds 200 parts by weight, The viscosity of the coating composition for protecting the surface of the automobile according to the present invention is too low, resulting in deteriorated workability, a long curing time, and a sticky phenomenon.
상기 광개시제는 50 내지 80 중량부가 함유되며, 메틸이소부틸케톤으로 이루어지는데, 자외선을 흡수하여 중합을 개시하도록 하는 역할을 한다.The photoinitiator is contained in an amount of 50 to 80 parts by weight, and is composed of methyl isobutyl ketone, and has a role of absorbing ultraviolet rays to initiate polymerization.
상기 광개시제의 함량이 50 중량부 미만이면 자외선에 의한 반응성이 저하되어 본 발명에 따른 자동차 표면보호용 코팅제 조성물을 자동차의 표면에 코팅했을 때, 경과가 더디게 진행되어 작업성이 저하되며, 상기 광개시제의 함량이 80 중량부를 초과하게 되면 본 발명에 따른 자동차 표면보호용 코팅제 조성물을 자동차의 표면에 도포했을 때, 외관 불량이 발생하게 된다.When the content of the photoinitiator is less than 50 parts by weight, reactivity due to ultraviolet rays is lowered. When the coating composition for automobile surface protection according to the present invention is coated on the surface of an automobile, Is more than 80 parts by weight, when the coating composition for protecting a surface of an automobile according to the present invention is applied to the surface of an automobile, appearance defects may occur.
상기 점도조절제는 100 내지 120 중량부가 함유되며, 자일렌으로 이루어지는데, 본 발명에 따른 자동차 표면보호용 코팅제 조성물의 점도를 일정하게 유지시켜, 작업성을 향상시키는 역할을 한다.The viscosity modifier is contained in an amount of 100 to 120 parts by weight, and is composed of xylene. The viscosity of the coating composition for protecting a surface of an automobile according to the present invention is maintained constant to improve workability.
상기 점도조절제의 함량이 100 중량부 미만이면, 코팅막의 점도가 지나치게 높아 작업성이 저하되며, 상기 점도조절제의 함량이 120 중량부를 초과하게 되면, 코팅막의 점도가 지나치게 낮아져 자동차의 표면으로부터 흘러내림 현상이 발생할 수 있다.If the content of the viscosity modifier is less than 100 parts by weight, the viscosity of the coating film becomes too high to lower the workability. If the content of the viscosity modifier exceeds 120 parts by weight, the viscosity of the coating film becomes excessively low, Can occur.
상기 레벨링제는 3 내지 6 중량부가 함유되며, 본 발명에 따른 자동차 표면보호용 코팅제 조성물로 이루어진 코팅막에 레벨링을 부여하는 역할을 하는데, 더욱 상세하게는, 코팅막의 표면장력을 낮추어 표면에 향상된 젖음(Wetting)성을 부여하고, 이로 인해 안정적인 레벨링을 갖도록 하기 때문에, 수려한 외관을 갖는 코팅막을 형성할 수 있다.The leveling agent contains 3 to 6 parts by weight of the leveling agent. The leveling agent serves to impart leveling to the coating layer composed of the coating composition for protecting a surface of an automobile according to the present invention. More specifically, the surface tension of the coating layer is lowered to improve wetting ), And thus has a stable leveling, so that a coating film having a beautiful appearance can be formed.
상기 레벨링제의 함량이 3 중량부 미만이면 레벨링 효과가 미미하며, 상기 레벨링제의 함량이 6 중량부를 초과하게 되면 자동차 표면과의 부착성이 저하된다.
When the content of the leveling agent is less than 3 parts by weight, the leveling effect is insignificant. When the content of the leveling agent exceeds 6 parts by weight, adhesion with the surface of the automobile is decreased.
상기 경화제는 자일렌, 스티렌모노머 및 이소시아네이트 올리고머로 이루어지며, 자일렌 100 중량부, 스티렌모노머 5 내지 15 중량부 및 이소시아네이트 올리고머 15 내지 40 중량부로 이루어지는 것이 바람직하다.The curing agent is composed of xylene, a styrene monomer and an isocyanate oligomer, and is preferably composed of 100 parts by weight of xylene, 5 to 15 parts by weight of a styrene monomer and 15 to 40 parts by weight of an isocyanate oligomer.
상기 경화제는 상기 주제와 혼합되면 주제를 경화시켜 코팅막을 형성시키는 역할을 하는데, 경화제의 함량이 25 중량부 미만이면 가교결합력이 저하되어, 코팅막의 내스크래치성, 내약품성 및 내마모성이 저하되며, 경화제의 함량이 35 중량부를 초과하게 되면 경화제 성분이 과량 잔존하여 경화과정이 느리게 진행되며, 작업성의 저하될 뿐만 아니라, 경화된 코팅막의 경도가 지나치게 증가하여 광택, 평활성, 내약품성 및 내후성이 저하된다.When the content of the curing agent is less than 25 parts by weight, the cross-linking force is lowered and the scratch resistance, chemical resistance and abrasion resistance of the coating film are lowered, and the curing agent Exceeds 35 parts by weight, an excessive amount of the curing agent component remains and the curing process proceeds slowly, and not only the workability is lowered, but also the hardness of the cured coating film is excessively increased, and gloss, smoothness, chemical resistance and weather resistance are lowered.
상기 경화제의 성분 중 이소시아네이트 올리고머는 경도 및 내약품성이 우수하며, 유연성이 우수하기 때문에, 내스크래치성, 내한칩핑성, 내충격성 및 내굴곡성이 우수한 코팅막을 제공하는 역할을 한다.
Among the components of the curing agent, the isocyanate oligomer is excellent in hardness and chemical resistance and excellent in flexibility, thus providing a coating film having excellent scratch resistance, cold chipping resistance, impact resistance and flex resistance.
따라서, 상기의 성분들로 이루어지는 자동차 표면보호용 코팅제 조성물은 차량의 표면에 코팅된 후에 스크래치가 발생하더라도, 자기복원 능력을 나타내어 반영구적인 표면보호 효과를 나타내고, 부드러운 촉감과 수려한 광택효과를 나타낸다.Therefore, even when scratches are generated after coating the surface of a vehicle, the coating composition for protecting an automobile surface comprising the above-mentioned components exhibits a self-restoring ability to exhibit a semi-permanent surface protecting effect, a soft touch and a glossy effect.
또한, 상기의 성분들로 이루어진 자동차 표면보호용 코팅제 조성물은 자동차의 표면에 필름형태로 형성되어, 자동차의 표면으로부터 제거가 용이하며, 코팅막의 제거를 위한 별도의 공정을 거치지 않아도 되기 때문에 우수한 공정효율성을 갖는다.Also, since the coating composition for protecting the surface of automobile, which is composed of the above-mentioned components, is formed in the form of a film on the surface of an automobile, it can be easily removed from the surface of the automobile and the separate process for removing the coating film is not required. .
또한, 상기의 성분들로 이루어진 자동차 표면보호용 코팅제 조성물은 코팅막의 탄성과 슬립성이 극대화되어, 외력에 의한 긁힘을 방지하고, 미끄러짐을 유도하여 코팅막이 찢어지는 것이 방지되며, 스크래치가 발생된 경우에는 코팅막에 함유된 탄성체 성분으로 인해 일정시간이 경과하면 원상태로 복원된다.In addition, the coating composition for surface protection of automobile, which is composed of the above-mentioned components, maximizes the elasticity and slipperiness of the coating film, prevents scratching by external force, prevents slipping of the coating film and prevents the coating film from being torn. Due to the elastic component contained in the coating film, it is restored to its original state after a lapse of a predetermined time.
또한, 상기 코팅막은 차량의 표면에 도포된 후에 연마가공을 실시할 수 있을 정도의 경도를 나타내며, 미세한 스크래치 등은 마찰열 및 일상 중 실온에서 발생 할 수 있는 열로써 복원된다.
Further, the coating film shows a hardness enough to be polished after being applied to the surface of the vehicle, and fine scratches and the like are restored as heat which can be generated at frictional heat and at room temperature during normal operation.
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
삭제delete
Claims (9)
Wherein the polyurethane-containing subject and the styrene monomer-containing curing agent are contained in a weight ratio of 2: 1.
상기 주제는 폴리우레탄 100 중량부, 아크릴 80 내지 100 중량부, 희석제 120 내지 200 중량부, 광개시제 50 내지 80 중량부, 점도조절제 100 내지 120 중량부 및 레벨링제 3 내지 6 중량부로 이루어지는 것을 특징으로 하는 자동차 표면보호용 코팅제 조성물.
The method according to claim 1,
The subject matter is characterized by comprising 100 parts by weight of polyurethane, 80 to 100 parts by weight of acrylic, 120 to 200 parts by weight of diluent, 50 to 80 parts by weight of a photoinitiator, 100 to 120 parts by weight of viscosity adjusting agent and 3 to 6 parts by weight of leveling agent A coating composition for protecting an automobile surface.
상기 폴리우레탄은 경질폴리우레탄과 연질폴리우레탄이 1:0.09 내지 0.1의 중량부비율로 혼합되어 이루어지는 것을 특징으로 하는 자동차 표면보호용 코팅제 조성물.
The method according to claim 1 or 2,
Wherein the polyurethane is a mixture of a hard polyurethane and a soft polyurethane in a weight ratio of 1: 0.09 to 0.1.
상기 희석제는 N-부틸아세테이트 65 내지 100 중량부, 프로필렌글리콜메틸에테르아세테이트 50 내지 80 중량부 및 메탄올 5 내지 20 중량부로 이루어지는 것을 특징으로 하는 자동차 표면보호용 코팅제 조성물.
The method of claim 2,
Wherein the diluent comprises 65 to 100 parts by weight of N-butyl acetate, 50 to 80 parts by weight of propylene glycol methyl ether acetate, and 5 to 20 parts by weight of methanol.
상기 광개시제는 메틸이소부틸케톤으로 이루어지는 것을 특징으로 하는 자동차 표면보호용 코팅제 조성물.
The method of claim 2,
Wherein the photoinitiator is methyl isobutyl ketone.
상기 점도조절제는 자일렌으로 이루어지는 것을 특징으로 하는 자동차 표면보호용 코팅제 조성물.
The method of claim 2,
Wherein the viscosity modifier is composed of xylene.
상기 경화제는 자일렌, 스티렌모노머 및 이소시아네이트 올리고머로 이루어지는 것을 특징으로 하는 자동차 표면보호용 코팅제 조성물.
The method according to claim 1,
Wherein the curing agent is composed of xylene, a styrene monomer, and an isocyanate oligomer.
상기 경화제는 자일렌 100 중량부, 스티렌모노머 5 내지 15 중량부 및 이소시아네이트 올리고머 15 내지 40 중량부로 이루어지는 것을 특징으로 하는 자동차 표면보호용 코팅제 조성물.The method according to claim 1 or 8,
Wherein the curing agent comprises 100 parts by weight of xylene, 5 to 15 parts by weight of a styrene monomer, and 15 to 40 parts by weight of an isocyanate oligomer.