KR101448213B1 - Construction method using silicone sheet - Google Patents

Construction method using silicone sheet Download PDF

Info

Publication number
KR101448213B1
KR101448213B1 KR1020120011931A KR20120011931A KR101448213B1 KR 101448213 B1 KR101448213 B1 KR 101448213B1 KR 1020120011931 A KR1020120011931 A KR 1020120011931A KR 20120011931 A KR20120011931 A KR 20120011931A KR 101448213 B1 KR101448213 B1 KR 101448213B1
Authority
KR
South Korea
Prior art keywords
silicon
sheet
connecting member
nonwoven fabric
adhesive
Prior art date
Application number
KR1020120011931A
Other languages
Korean (ko)
Other versions
KR20130090646A (en
Inventor
최영기
Original Assignee
최영기
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 최영기 filed Critical 최영기
Priority to KR1020120011931A priority Critical patent/KR101448213B1/en
Publication of KR20130090646A publication Critical patent/KR20130090646A/en
Application granted granted Critical
Publication of KR101448213B1 publication Critical patent/KR101448213B1/en

Abstract

본 발명은 실리콘 시트를 이용한 방수공법에 관한 것으로, 더욱 상세하게는 건축물의 옥상에 다수의 실리콘시트를 배열하는 시트배열단계, 상기 시트배열단계를 통해 배열된 실리콘시트 사이의 연접부위와 연접부위의 상부면에 접착제를 도포하는 접착제도포단계 및 상기 접착제도포단계를 통해 접착제가 도포된 실리콘시트 연접부위의 상부면에 제1연결부재를 적층하는 연결부재적층단계로 이루어진다.
전술한 과정을 통해 이루어지는 실리콘 시트를 이용한 방수공법은 실리콘시트가 사용되어 건축물의 옥상에 방수성, 내충격성 및 내화학성이 우수한 방수시트층을 형성할 수 있다.The present invention relates to a waterproofing method using a silicon sheet, and more particularly to a waterproofing method using a silicon sheet, which comprises a sheet arranging step of arranging a plurality of silicon sheets on the roof of a building, And a connecting member laminating step of laminating the first connecting member on the upper surface of the silicone sheet connecting portion to which the adhesive is applied through the adhesive applying step.
The waterproofing method using the silicon sheet through the above-described process can form a waterproof sheet layer having a waterproof property, an impact resistance and a chemical resistance on the roof of a building by using a silicon sheet.

Description

실리콘 시트를 이용한 방수공법 {CONSTRUCTION METHOD USING SILICONE SHEET}{CONSTRUCTION METHOD USING SILICONE SHEET}

본 발명은 실리콘 시트를 이용한 방수공법에 관한 것으로, 더욱 상세하게는 실리콘시트를 이용하여 건축물의 옥상에 방수성, 내충격성 및 내화학성이 우수한 방수시트층을 형성하는 실리콘 시트를 이용한 방수공법에 관한 것이다.
The present invention relates to a waterproofing method using a silicon sheet, and more particularly, to a waterproofing method using a silicone sheet to form a waterproof sheet layer having a waterproof property, an impact resistance and a chemical resistance on the roof of a building .

본 발명은 실리콘 시트를 이용한 방수공법에 관한 것으로, 더욱 상세하게는 실리콘시트를 이용하여 건축물의 옥상에 방수성, 내충격성 및 내화학성이 우수한 방수시트층을 형성하는 실리콘 시트를 이용한 방수공법에 관한 것이다.The present invention relates to a waterproofing method using a silicon sheet, and more particularly, to a waterproofing method using a silicone sheet to form a waterproof sheet layer having a waterproof property, an impact resistance and a chemical resistance on the roof of a building .

일반적으로 콘크리트 건축물들의 옥상은 빗물로 인한 누수를 방지하기 위해 방수처리가 진행되며, 옥상 이외에도 건축물들의 옥외 표면을 통해 우수나 지하수 등의 수분이 유입되는 것을 차단하여 구조체의 균열 및 내구성의 저하를 최소화하기 위해 방수작업을 진행한다.Generally, the roof of concrete buildings is waterproofed to prevent water leakage due to rainwater. In addition to the rooftop, it prevents the inflow of water such as rainwater or ground water through the outdoor surface of the buildings, thereby minimizing the deterioration of the structure crack and durability Waterproofing work is carried out.

콘크리트 건축물들의 통상적인 방수공법은 그 시공방법에 따라 시트방수, 도막방수 및 복합방수 등으로 구분된다.Conventional waterproofing methods for concrete structures are classified into sheet waterproofing, film waterproofing and composite waterproofing according to the construction method.

여기서, 도막방수 공법은 액상형의 방수제를 반복하여 콘크리트 표면에 도포하는 방법으로, 건축물의 평평한 부분은 물론 모서리 등에 적용이 용이한 장점이 있으나, 액상 자체의 퍼짐성으로 인해 건축물 바탕면의 평활도가 좋지 않으면 균일한 두께의 도막 형성이 어렵게 되고, 또한, 바탕의 습기에 의해 부풀림이 쉽게 발생하게 되며, 바탕의 크랙에 대한 대응성이 현저히 떨어지게 되는 단점이 있다.The coating film waterproofing method is a method in which a liquid type water repellent is repeatedly applied to the surface of a concrete, which is advantageous in that it is easily applied to a flat part of a building as well as to an edge. However, since the spreadability of the liquid itself causes poor smoothness It is difficult to form a coating film having a uniform thickness, and furthermore, it is easily inflated by the moisture on the background and the correspondence to cracks on the base is remarkably deteriorated.

전술한 문제점을 해결하기 위해 합성수지 등으로 형성된 시트를 이용한 시트방수 공법이 이용되고 있으며, 종래에 사용되고 있는 시트방수 공법에 가장 적합한 재료는 실리콘시트인데, 전술한 실리콘시트는 우레탄 접착제와의 접착성이 미흡하여, 시공시 별도의 접착과정을 진행해야하며, 접착 후에도 접착부위의 박리나 들뜸현상이 발생하는 문제점이 있었다.
In order to solve the above-mentioned problems, a sheet waterproofing method using a sheet formed of a synthetic resin or the like is used, and the most suitable material for a sheet waterproofing method which is conventionally used is a silicon sheet. It is necessary to carry out a separate bonding process at the time of construction, and there is a problem that peeling or peeling of the bonding portion occurs even after bonding.

본 발명의 목적은 실리콘 시트를 이용하여 방수성, 내충격성 및 내화학성이 우수한 방수층을 제공하는 실리콘 시트를 이용한 방수공법을 제공하는 것이다.An object of the present invention is to provide a waterproofing method using a silicone sheet which provides a waterproof layer excellent in water resistance, impact resistance and chemical resistance by using a silicon sheet.

본 발명의 다른 목적은 실리콘 시트의 표면에 형성된 부직포층으로 인해 우레탄계 접착제에 의해 견고하게 접착되어 들뜸현상 등이 발생하지 않는 실리콘 시트를 이용한 방수공법을 제공하는 것이다.
Another object of the present invention is to provide a waterproofing method using a silicone sheet which is firmly adhered by a urethane-based adhesive due to a nonwoven fabric layer formed on the surface of the silicone sheet and does not cause floating phenomenon.

본 발명의 목적은 건축물의 옥상에 다수의 실리콘시트를 배열하는 시트배열단계, 상기 시트배열단계를 통해 배열된 실리콘시트 사이의 연접부위와 연접부위의 상부면에 접착제를 도포하는 접착제도포단계 및 상기 접착제도포단계를 통해 접착제가 도포된 실리콘시트 연접부위의 상부면에 제1연결부재를 적층하는 연결부재적층단계로 이루어지는 것을 특징으로 하는 실리콘 시트를 이용한 방수공법을 제공함에 의해 달성된다.An object of the present invention is to provide a method of manufacturing a semiconductor device, which comprises a sheet arranging step of arranging a plurality of silicon sheets on the roof of a building, an adhesive applying step of applying an adhesive to the upper surface of the connecting part and the connecting part between the silicon sheets arranged through the sheet arranging step, And a connecting member laminating step of laminating the first connecting member on the upper surface of the silicon sheet connecting portion to which the adhesive is applied through the adhesive applying step.

본 발명의 바람직한 특징에 따르면, 상기 실리콘시트는 상부면 및 하부면에 부직포층이 형성되는 것으로 한다.According to a preferred aspect of the present invention, the nonwoven fabric layer is formed on the upper surface and the lower surface of the silicon sheet.

본 발명의 더 바람직한 특징에 따르면, 상기 실리콘시트는 실리콘을 압출기로 압출하고, 압출된 실리콘의 상부면 및 하부면에 부직포를 적층한 후에 압착성형하여 실리콘의 내부로 부직포의 섬유가닥이 침투한 상태에서 경화하여 제조되는 것으로 한다.According to a more preferred feature of the present invention, the silicon sheet is produced by extruding silicon with an extruder, laminating a nonwoven fabric on the upper and lower surfaces of the extruded silicone, and then press-molding the fibers to infiltrate the fiber strands of the nonwoven fabric into the silicon To be cured.

본 발명의 더욱 바람직한 특징에 따르면, 상기 제1연결부재는 실리콘시트의 상부면 또는 하부면에 부직포층을 형성하여 이루어지는 것으로 한다.According to a further preferred feature of the present invention, the first connection member is formed by forming a nonwoven fabric layer on the upper surface or the lower surface of the silicon sheet.

본 발명의 더욱 더 바람직한 특징에 따르면, 상기 제1연결부재는 실리콘을 압출기로 압출하고, 압출된 실리콘의 상부면 또는 하부면에 부직포를 적층한 후에 압착성형하여 실리콘의 내부로 부직포의 섬유가닥이 침투한 상태에서 경화하여 제조되는 것으로 한다.According to a further preferred feature of the present invention, the first connecting member is formed by extruding silicon with an extruder, laminating a nonwoven fabric on the upper surface or the lower surface of the extruded silicon, followed by compression molding, And cured in the infiltrated state.

본 발명의 더욱 더 바람직한 특징에 따르면, 상기 시트배열단계 이전에는 제2연결부재를 건축물의 옥상에 배열하고, 상기 제2연결부재의 상부면에 접착제를 도포한 후에, 상기 제2연결부재의 상부면에 실리콘시트의 연접부위가 접착되도록 배열하는 연결부재배열단계가 더 이루어지는 것으로 한다.According to a further preferred feature of the present invention, the second connecting member is arranged on the roof of the building before the sheet arranging step, and after the adhesive is applied to the upper surface of the second connecting member, And a connecting member arranging step of arranging the connecting portion of the silicon sheet so as to be adhered to the surface.

본 발명의 더욱 더 바람직한 특징에 따르면, 상기 제2연결부재는 실리콘시트의 상부면 또는 하부면에 부직포층을 형성하여 이루어지는 것으로 한다.According to a further preferred feature of the present invention, the second connection member is formed by forming a nonwoven fabric layer on the upper surface or the lower surface of the silicon sheet.

본 발명의 더욱 더 바람직한 특징에 따르면, 상기 제2연결부재는 실리콘을 압출기로 압출하고, 압출된 실리콘의 상부면 또는 하부면에 부직포를 적층한 후에 압착성형하여 실리콘의 내부로 부직포의 섬유가닥이 침투한 상태에서 경화하여 제조되는 것으로 한다.According to a further preferred feature of the present invention, the second connecting member is formed by extruding silicon with an extruder, laminating a nonwoven fabric on the upper surface or the lower surface of the extruded silicon, followed by compression molding, And cured in the infiltrated state.

본 발명의 더욱 더 바람직한 특징에 따르면, 상기 접착제는 우레탄계 접착제로 이루어지는 것으로 한다.
According to a further preferred feature of the present invention, the adhesive is made of a urethane-based adhesive.

본 발명에 따른 실리콘 시트를 이용한 방수공법은 실리콘 시트를 이용하여 방수성, 내충격성 및 내화학성이 우수한 방수시트층을 제공하는 탁월한 효과를 나타낸다.The waterproofing method using the silicone sheet according to the present invention exhibits an excellent effect of providing a waterproof sheet layer excellent in water resistance, impact resistance and chemical resistance by using a silicon sheet.

또한, 실리콘 시트의 표면에 형성된 부직포층으로 인해 우레탄계 접착제에 의해 견고하게 접착되어, 들뜸현상 등이 발생하지 않는 방수시트층을 제공하는 탁월한 효과를 나타낸다.
Further, it shows an excellent effect of providing a waterproof sheet layer which is firmly adhered by a urethane-based adhesive due to the nonwoven fabric layer formed on the surface of the silicone sheet, and does not cause floating phenomenon.

도 1은 본 발명의 일 실시예에 따른 실리콘 시트를 이용한 방수공법을 나타낸 순서도이다.
도 2는 본 발명의 다른 실시예에 따른 실리콘 시트를 이용한 방수공법을 나타낸 순서도이다.
도 3은 본 발명의 일 실시예에 따른 실리콘 시트를 이용한 방수공법으로 시공된 방수시트층을 나타낸 단면도이다.
도 4는 본 발명의 다른 실시예에 따른 실리콘 시트를 이용한 방수공법으로 시공된 방수시트층을 나타낸 단면도이다.
도 5은 본 발명의 또 다른 실시예에 따른 실리콘 시트를 이용한 방수공법으로 시공된 방수시트층을 나타낸 단면도이다. 1 is a flowchart showing a waterproof method using a silicon sheet according to an embodiment of the present invention.
2 is a flowchart illustrating a waterproof method using a silicon sheet according to another embodiment of the present invention.
3 is a cross-sectional view illustrating a waterproof sheet layer formed by a waterproof method using a silicon sheet according to an embodiment of the present invention.
4 is a cross-sectional view showing a waterproof sheet layer formed by a waterproof method using a silicon sheet according to another embodiment of the present invention.
5 is a cross-sectional view illustrating a waterproof sheet layer formed by a waterproof method using a silicon sheet according to another embodiment of the present invention.

이하에는, 본 발명의 바람직한 실시예와 각 성분의 물성을 상세하게 설명하되, 이는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 발명을 용이하게 실시할 수 있을 정도로 상세하게 설명하기 위한 것이지, 이로 인해 본 발명의 기술적인 사상 및 범주가 한정되는 것을 의미하지는 않는다.
Hereinafter, preferred embodiments of the present invention and physical properties of the respective components will be described in detail with reference to the accompanying drawings. However, the present invention is not limited thereto, And this does not mean that the technical idea and scope of the present invention are limited.

본 발명에 따른 실리콘 시트를 이용한 방수공법은 건축물의 옥상에 다수의 실리콘시트(10)를 배열하는 시트배열단계(S103), 전술한 시트배열단계(S103)를 통해 배열된 실리콘시트(10) 사이의 연접부위와 연접부위의 상부면에 접착제(20)를 도포하는 접착제도포단계(S105) 및 전술한 접착제도포단계(S105)를 통해 접착제(20)가 도포된 실리콘시트(10) 연접부위의 상부면에 제1연결부재(30)를 적층하는 연결부재적층단계(S107)로 이루어진다.
The waterproofing method using the silicon sheet according to the present invention is a waterproofing method using a silicon sheet 10 arranged on the roof of a building, a sheet arranging step S103 for arranging a plurality of silicon sheets 10 on the roof of the building, Of the silicon sheet 10 to which the adhesive 20 is applied through the adhesive applying step S105 for applying the adhesive 20 to the upper surface of the connecting portion of the adhesive sheet 20 and the adhesive applying step S105 described above, And a connecting member laminating step (S107) for laminating the first connecting member (30) on the surface.

전술한 시트배열단계(S103)는 건축물의 옥상에 다수의 실리콘시트(10)를 배열하는 단계로, 콘크리트로 이루어진 건축물의 옥상에 다수의 실리콘시트(10)를 배열하되, 다수가 배열되는 실리콘시트(10)가 연접되도록 배열하는 것이 바람직하다.The above-described sheet arranging step (S103) is a step of arranging a plurality of silicon sheets 10 on the roof of a building, in which a plurality of silicon sheets 10 are arranged on the roof of a concrete structure, (10) are connected to each other.

이때, 전술한 실리콘시트(10)는 상부면 및 하부면에 부직포층(11)이 형성되는데, 실리콘시트(10)의 상부면 및 하부면에 부직포층(11)을 형성하는 방법은 경화제가 혼합된 실리콘을 압축기로 압축하고, 압축된 실리콘의 상부면 및 하부면에 부직포를 적층한 후에 압착성형하여 실리콘의 내부로 부직포의 섬유가닥이 침투한 상태에서 경화하여 제조된다.The method of forming the nonwoven fabric layer 11 on the upper and lower surfaces of the silicon sheet 10 may include a method in which the hardener is mixed The non-woven fabric is compressed by compression with a compressor, laminated on the upper and lower surfaces of the compressed silicone, and then compression-molded so as to be cured while the fibers of the nonwoven fabric penetrate into the silicon.

전술한 경화제는 2,5-bis(tert-butylperoxy)-2,5-dimethylhexen으로 이루어진 것을 사용하는것이 바람직하다.The above-mentioned curing agent is preferably composed of 2,5-bis (tert-butylperoxy) -2,5-dimethylhexene.

이때, 전술한 부직포는 폴리프로필렌으로 이루어지는 것이 바람직하며, 전술한 부직포로 이루어진 부직포층(11)이 형성된 다수의 실리콘시트(10)의 연접부위는 전술한 접착제도포단계(S105)를 통해 도포되는 우레탄계 접착제에 의해 강력하게 접착되며, 들뜸현상이 발생하지 않게 된다.
At this time, it is preferable that the above-mentioned nonwoven fabric is made of polypropylene, and the connecting portion of the plurality of silicon sheets 10 on which the nonwoven fabric layer 11 made of the above-described nonwoven fabric is formed is a urethane- It is strongly adhered by the adhesive, and the lifting phenomenon does not occur.

전술한 접착제도포단계(S105)는 전술한 시트배열단계(S101)를 통해 배열된 실리콘시트(10) 사이의 연접부위와 연접부위의 상부면에 접착제(20)를 도포하는 단계로, 전술한 시트배열단계(S103)를 통해 건축물의 옥상에 다수 배열된 실리콘시트 (10)사이의 연접부위와 연접부위의 상부면에 우레탄계 접착제(20)를 도포하여 다수 배열된 실리콘시트(10)의 연접부위의 실리콘시트(10)를 서로 접착하고, 전술한 제1연결부재(30)를 실리콘시트(10) 사이에 형성되는 연접부위의 상부면에 접착할 수 있도록하는 단계다.
The above-described adhesive applying step (S105) is a step of applying the adhesive 20 to the upper surface of the connecting portion and the connecting portion between the silicon sheets 10 arranged through the sheet arranging step (S101) described above, The urethane adhesive 20 is applied to the upper surface of the connecting portion and the connecting portion between the silicon sheets 10 arranged on the roof of the building through the arranging step S103 and the connecting portions of the plurality of arranged silicon sheets 10 The silicon sheet 10 is adhered to each other and the first connecting member 30 described above can be adhered to the upper surface of the connecting portion formed between the silicon sheets 10. [

전술한 연결부재적층단계(S107)는 전술한 접착제도포단계(S105)를 통해 접착제(20)가 도포된 실리콘시트(10) 연접부위의 상부면에 제1연결부재(30)를 적층하는 단계로, 전술한 제1연결부재(30)가 적층된 실리콘시트(10) 연접부위는 제1연결부재(30)가 실리콘시트(10)를 서로 강력하게 접착할 수 있도록 하는 역할을 하여, 외부의 충격이나 콘크리트의 거동에 따른 외력 발생시 실리콘시트(10) 간의 접착된 부분이 분리되거나 들뜨지 않도록 하기 때문에, 내충격성이 우수한 방수시트층이 제공된다.The above-described connecting member laminating step S107 is a step of laminating the first connecting member 30 on the upper surface of the connecting portion of the silicon sheet 10 to which the adhesive 20 is applied through the above-described adhesive applying step S105 The connecting portion of the silicon sheet 10 in which the first connecting member 30 is laminated can serve to make the first connecting member 30 strongly bond the silicon sheet 10 to each other, The waterproof sheet layer having excellent impact resistance is provided because the bonded portion between the silicon sheets 10 when the external force is generated due to the behavior of the concrete or the concrete is not separated or lifted.

이때, 전술한 제1연결부재(30)는 실리콘시트의 상부면 또는 하부면에 부직포층(31)을 형성하여 이루어지며, 경화제가 혼합된 실리콘을 압축기로 압축하고, 압축된 실리콘의 상부면 또는 하부면에 부직포를 적층한 후에 압착성형하여 실리콘의 내부로 부직포의 섬유가닥이 침투한 상태에서 경화하여 제조된다.The first connecting member 30 is formed by forming a nonwoven fabric layer 31 on the upper surface or the lower surface of the silicon sheet, compressing the silicon mixed with the hardening agent with a compressor, A nonwoven fabric is laminated on the lower surface of the nonwoven fabric, followed by compression molding and curing in a state in which the fiber strands of the nonwoven fabric penetrate into the silicon.

전술한 경화제는 2,5-bis(tert-butylperoxy)-2,5-dimethylhexen으로 이루어진 것을 사용하는것이 바람직하다.The above-mentioned curing agent is preferably composed of 2,5-bis (tert-butylperoxy) -2,5-dimethylhexene.

전술한 과정을 통해 제조된 제1연결부재(30)를 우레탄계 접착제(20)가 도포된 실리콘시트(10) 사이에 연접부위의 상부면에 적층할 때는, 제1연결부재(30)에 형성된 부직포층(31)이 우레탄계 접착제(20)가 도포되어 있는 방향을 향하도록 하여 적층해야 하는데, 제1연결부재(30) 표면 중에서 부직포층(31)이 형성되지 않은 면이 전술한 실리콘시트(10) 사이의 연접부위에 적층되면, 제1연결부재(30)를 구성하는 실리콘시트와 실리콘시트(10) 사이의 연접부위가 우레탄계 접착제(20)로 직접 접착되기 때문에, 시간의 경과 및 외력 등에 따른 시트 간의 박리 및 들뜸현상이 발생되기 때문이다.When the first connecting member 30 manufactured through the above-described process is laminated on the upper surface of the connecting portion between the silicon sheets 10 to which the urethane adhesive 20 is applied, the nonwoven fabric 30 formed on the first connecting member 30 The surface of the first connecting member 30 on which the nonwoven fabric layer 31 is not formed is the same as the surface of the silicon sheet 10 described above, The adhesiveness between the silicon sheet and the silicon sheet 10 constituting the first connection member 30 is directly adhered to the urethane adhesive 20, And peeling and lifting phenomena occur.

전술한 연결부재적층단계(S107)가 완료되면, 아래 도 3 및 도 5에 나타낸 것과 같은 방수시트층이 형성되며, 이러한 방수시트층은 실리콘시트가 사용되어 형성되기 때문에 방수성, 내충격성 및 내화학성이 우수하며, 실리콘 시트의 표면에 형성된 부직포층으로 인해 우레탄계 접착제에 의해 견고하게 접착되어, 박리 및 들뜸현상 등이 발생하지 않는다.
When the connecting member stacking step S107 described above is completed, a waterproof sheet layer as shown in Figs. 3 and 5 is formed, and since such a waterproof sheet layer is formed by using a silicon sheet, waterproofness, impact resistance and chemical resistance And is firmly adhered by the urethane-based adhesive due to the nonwoven fabric layer formed on the surface of the silicon sheet, so that peeling and lifting phenomenon do not occur.

또한, 전술한 시트배열단계(S103) 이전에는 제2연결부재(40)를 건축물의 옥상에 배열하고, 전술한 제2연결부재(40)의 상부면에 접착제를 도포한 후에, 전술한 제2연결부재(40)의 상부면에 실리콘시트(10)의 연접부위가 접착되도록 배열하는 연결부재배열단계(S101)가 더 이루어지질 수도 있다.Further, before the above-described sheet arranging step (S103), the second connecting member 40 is arranged on the roof of the building, and after the adhesive is applied to the upper surface of the second connecting member 40, A connecting member arranging step S101 may be further arranged to arrange the connecting portion of the silicon sheet 10 to be adhered to the upper surface of the connecting member 40. [

전술한 연결부재배열단계(S101)를 통해 제2연결부재(40)가 더 형성된 방수시트층은 제1연결부제(30)와 제2연결부재(40)가 실리콘시트(10) 연접부위의 상부면 하부면에 형성되어 실리콘시트(10) 간의 접착강도가 더욱 향상된다.The waterproof sheet layer in which the second connection member 40 is further formed through the connection member arranging step S101 described above is formed so that the first connection member 30 and the second connection member 40 are joined to the upper portion of the concave portion of the silicon sheet 10 The adhesion strength between the silicon sheets 10 is further improved.

이때, 전술한 제2연결부재(40)는 실리콘시트의 상부면 또는 하부면에 부직포층(41)을 형성하여 이루어지며, 경화제가 혼합된 실리콘을 압축기로 압축하고, 압축된 실리콘의 상부면 또는 하부면에 부직포를 적층한 후에 압착성형하여 실리콘의 내부로 부직포의 섬유가닥이 침투한 상태에서 경화하여 제조된다.The second connecting member 40 may be formed by forming a nonwoven fabric layer 41 on the upper surface or the lower surface of the silicon sheet, compressing the silicon mixed with the hardening agent with a compressor, A nonwoven fabric is laminated on the lower surface of the nonwoven fabric, followed by compression molding and curing in a state in which the fiber strands of the nonwoven fabric penetrate into the silicon.

전술한 경화제는 2,5-bis(tert-butylperoxy)-2,5-dimethylhexen으로 이루어진 것을 사용하는 것이 바람직하다. The above-mentioned curing agent is preferably composed of 2,5-bis (tert-butylperoxy) -2,5-dimethylhexene.

전술한 과정을 통해 제조된 제2연결부재(40)를 건축물의 옥상에 배열할 때는, 부직포층(41)이 형성된 면이 건축물 옥상 표면의 반대방향인 상부를 향하도록 배열하는 것이 바람직한데, 제2연결부재(40) 표면 중에서 부직포층(41)이 형성되지 않은 면이 상부면을 향하도록 배열하면, 제2연결부재(40)를 구성하는 실리콘시트와 실리콘시트(10) 사이의 연접부위가 우레탄계 접착제(20)로 직접 접착되기 때문에, 시간의 경과 및 외력 등에 따른 시트 간의 박리 및 들뜸현상이 발생되기 때문이다.When the second connection member 40 manufactured through the above-described process is arranged on the roof of the building, it is preferable that the surface on which the nonwoven fabric layer 41 is formed is arranged so as to face the top, which is the opposite direction to the roof surface of the building. When the surface of the connecting member 40 on which the nonwoven fabric layer 41 is not formed is arranged so as to face the upper surface, the connecting portion between the silicon sheet constituting the second connecting member 40 and the silicon sheet 10 The adhesive is directly adhered to the urethane-based adhesive 20, so that peeling and lifting between the sheets occur due to the passage of time and external force.

전술한 연결부재배열단계(S101)가 더 이루어지면, 아래 도 5에 나타낸 것과 같은 방수시트층이 형성되며, 이러한 방수시트층은 실리콘시트가 사용되어 방수성, 내충격성 및 내화학성이 우수하며, 실리콘시트의 표면에 형성된 부직포층으로 인해 우레탄계 접착제에 의해 견고하게 접착되어, 박리 및 들뜸현상 등이 발생하지 않을 뿐만 아니라, 제2연결부재(40)가 더 형성되어 우레탄계 접착제(20)로 접착된 실리콘시트(10) 사이의 연접부위의 접착강도 및 내 충격성은 더욱 향상된다.
When the above-described connection member arranging step (S101) is further performed, a waterproof sheet layer as shown in Fig. 5 is formed. The waterproof sheet layer is made of a silicone sheet and is excellent in water resistance, impact resistance and chemical resistance, The second connecting member 40 is further formed so as not to be peeled off and lifted off due to the adhesion of the urethane-based adhesive 20 due to the nonwoven fabric layer formed on the surface of the sheet, The adhesive strength and the impact resistance of the connecting portion between the sheets 10 are further improved.

이하에서는, 본 발명에 사용된 실리콘시트의 경화전과 경화후의 물성을 측정하여 아래 표 1에 나타내었다.The properties of the silicone sheet used in the present invention before and after curing were measured and are shown in Table 1 below.

(단, 실리콘 99.35 중량%에 2,5-bis(tert-butylperoxy)-2,5-dimethylhexen로 이루어진 경화제를 0.65 중량% 첨가하고, 170℃의 온도에서 10분간 압축성형하고, 200℃의 온도에서 4시간 동안 오븐경화한 실리콘시트를 가로 2mm×세로 2mm의 시편으로 제조하여 측정한 결과로, CTM은 다우코닝 시험 기준이며, JIS는 일본공업규격이고, 선 수축율은 경화제의 종류, 경화온도, 성형제품의 크기와 같은 경화조건에 따라 달라질 수 있다.)
(Except that 0.65 wt% of a curing agent consisting of 2,5-bis (tert-butylperoxy) -2,5-dimethylhexene was added to 99.35 wt% of silicon, compression molded at a temperature of 170 DEG C for 10 minutes, As a result, the CTM is a Dow Corning test standard, the JIS is a Japanese industrial standard, and the linear shrinkage is determined by the type of curing agent, the curing temperature, the molding temperature, It may vary depending on the curing conditions such as the size of the product.)

<표 1><Table 1>

Figure 112012009625469-pat00001
Figure 112012009625469-pat00001

위에 표 1에 나타낸 것처럼 본 발명에 사용되는 실리콘시트는 경화 후에 밀도, 경도, 인장강도, 신율, 인열강도 및 선 수축율이 우수하기 때문에, 이러한 물성을 나타내는 실리콘시트를 이용하여 형성된 방수시트층은 방수성, 내충격성 및 내화학성이 우수한 효과를 나타낸다.As shown in Table 1 above, since the silicone sheet used in the present invention has excellent density, hardness, tensile strength, elongation, tear strength and line shrinkage after curing, the waterproof sheet layer formed using the silicone sheet exhibiting such physical properties Water resistance, impact resistance and chemical resistance.

또한, 전술한 실리콘시트에 부직포층을 형성하여 우레탄계 접착제에 의해 강력하게 접착된 방수시트층을 제공한다.
In addition, a nonwoven fabric layer is formed on the above-mentioned silicone sheet to provide a waterproof sheet layer strongly bonded by a urethane adhesive.

10 ; 실리콘시트
11, 31, 41 ; 부직포층
20 ; 접착제
30 ; 제1연결부재
40 ; 제2연결부재10; Silicone sheet
11, 31, 41; Nonwoven fabric layer
20; glue
30; The first connecting member
40; The second connecting member

Claims (9)

건축물의 옥상에 다수의 실리콘시트를 배열하는 시트배열단계;
상기 시트배열단계를 통해 배열된 실리콘시트 사이의 연접부위와 연접부위의 상부면에 접착제를 도포하는 접착제도포단계; 및
상기 접착제도포단계를 통해 접착제가 도포된 실리콘시트 연접부위의 상부면에 제1연결부재를 적층하는 연결부재적층단계;로 이루어지며,
상기 실리콘시트는 실리콘을 압출기로 압출하고, 압출된 실리콘의 상부면 및 하부면에 부직포를 적층한 후에 압착성형하여 실리콘의 내부로 부직포의 섬유가닥이 침투한 상태에서 경화하여 제조되며,
상기 제1연결부재는 실리콘을 압출기로 압출하고, 압출된 실리콘의 상부면 또는 하부면에 부직포를 적층한 후에 압착성형하여 실리콘의 내부로 부직포의 섬유가닥이 침투한 상태에서 경화하여 제조되는 것을 특징으로 하는 실리콘 시트를 이용한 방수공법.
A sheet arranging step of arranging a plurality of silicon sheets on the roof of the building;
An adhesive applying step of applying an adhesive to the upper surface of the connecting portion and the connecting portion between the silicon sheets arranged through the sheet arranging step; And
And a connecting member laminating step of laminating the first connecting member on the upper surface of the silicon sheet connecting portion to which the adhesive is applied through the adhesive applying step,
The silicone sheet is prepared by extruding silicon with an extruder, laminating a nonwoven fabric on the upper and lower surfaces of the extruded silicone, followed by compression molding to cure the fiber strands of the nonwoven fabric into the silicon,
The first connecting member is manufactured by extruding silicon with an extruder, laminating a nonwoven fabric on the upper surface or the lower surface of the extruded silicon, followed by compression molding, and curing in a state in which the fiber strands of the nonwoven fabric penetrate into the silicon A waterproof method using a silicon sheet.
삭제delete 삭제delete 삭제delete 삭제delete 청구항 1에 있어서,
상기 시트배열단계 이전에는 제2연결부재를 건축물의 옥상에 배열하고, 상기 제2연결부재의 상부면에 접착제를 도포한 후에, 상기 제2연결부재의 상부면에 실리콘시트의 연접부위가 접착되도록 배열하는 연결부재배열단계가 더 이루어지는 것을 특징으로 하는 실리콘 시트를 이용한 방수공법.
The method according to claim 1,
The second connecting member is arranged on the roof of the building and the adhesive is applied to the upper surface of the second connecting member so that the connecting portion of the silicon sheet is adhered to the upper surface of the second connecting member Wherein the step of arranging the connecting member further comprises the step of arranging the connecting member.
청구항 6에 있어서,
상기 제2연결부재는 실리콘시트의 상부면 또는 하부면에 부직포층을 형성하여 이루어지는 것을 특징으로 하는 실리콘 시트를 이용한 방수공법.
The method of claim 6,
Wherein the second connecting member is formed by forming a nonwoven fabric layer on an upper surface or a lower surface of the silicon sheet.
청구항 6에 있어서,
상기 제2연결부재는 실리콘을 압출기로 압출하고, 압출된 실리콘의 상부면 또는 하부면에 부직포를 적층한 후에 압착성형하여 실리콘의 내부로 부직포의 섬유가닥이 침투한 상태에서 경화하여 제조되는 것을 특징으로 하는 실리콘 시트를 이용한 방수공법.
The method of claim 6,
The second connecting member is manufactured by extruding silicon with an extruder, laminating a nonwoven fabric on the upper surface or the lower surface of the extruded silicon, followed by compression molding, and curing the fiber in a state where the fiber strands of the nonwoven fabric penetrate into the silicon A waterproof method using a silicon sheet.
청구항 1 또는 6에 있어서,
상기 접착제는 우레탄계 접착제로 이루어지는 것을 특징으로 하는 실리콘 시트를 이용한 방수공법.The method according to claim 1 or 6,
Wherein the adhesive is composed of a urethane-based adhesive.
KR1020120011931A 2012-02-06 2012-02-06 Construction method using silicone sheet KR101448213B1 (en)