KR101438656B1 - Casting tape support - Google Patents
Casting tape support Download PDFInfo
- Publication number
- KR101438656B1 KR101438656B1 KR1020120113131A KR20120113131A KR101438656B1 KR 101438656 B1 KR101438656 B1 KR 101438656B1 KR 1020120113131 A KR1020120113131 A KR 1020120113131A KR 20120113131 A KR20120113131 A KR 20120113131A KR 101438656 B1 KR101438656 B1 KR 101438656B1
- Authority
- KR
- South Korea
- Prior art keywords
- support
- casting tape
- load
- dty
- present
- Prior art date
Abstract
본 발명은 정형외과용 캐스팅 테이프의 지지체로서, 상기 지지체는 경사로 폴리에스테르계 섬유와 DTY가 1:1 내지 2:1의 비율(중량기준)로 이루어져 있고, 상기 DTY가 히팅이나 열수에 의해 수축된 상태로 이루어진 편직물을 포함하는 정형외과용 캐스팅 테이프의 지지체를 제공한다. The present invention relates to a support for an orthopedic casting tape, wherein the support comprises a slant polyester fiber and a DTY in a ratio of 1: 1 to 2: 1 (by weight), wherein the DTY is shrunk by heating or hot water The present invention also provides a support for an orthopedic casting tape comprising a knitted fabric made in a state of being knitted.
Description
본 발명은 정형외과용 캐스팅 테이프 지지체에 관한 것으로서, 보다 상세하게는 착용성이 개선된 정형외과용 캐스팅 테이프 지지체에 관한 것이다.
The present invention relates to an orthopedic casting tape support, and more particularly to an orthopedic casting tape support having improved wearability.
일반적으로 정형외과용 캐스팅 테이프는 유리섬유 등으로 짜인 원단에 폴리우레탄 레진이 포함되어 있어 습기나 물 등의 수분에 노출될 경우 화학적 반응을 일으키며 굳기 시작하여 골절상 등 정형외과적 질환에 있어서 종래 석고 몰딩방식을 대체하는 의료기구로서 사용되고 있다. Generally, casting tape for orthopedic surgery is made of fiberglass, and the polyurethane resin is included in the fabric. When it is exposed to moisture such as moisture or water, it causes chemical reaction and starts to harden. In the orthopedic diseases such as fractures, Is being used as a medical device that replaces the system.
종래 유리섬유를 기재로 한 캐스팅 테이프는 가볍고 튼튼하며 빠른 시술시간과 편리한 시술 및 간편한 뒷마무리 등의 장점으로 인해 점차 석고 몰딩방식을 대체해 나가고 있다. 그러나 유리섬유로 이루어진 테이프는 소재 특성에 의해 충격에 의해 파손되거나 유리섬유 분진으로 인해 알러지가 발생하기도 하고, 특히 제조 및 사용을 위한 절단단계에서 유리섬유 분진이 발생하여 호흡기 질환 및 피부 질환을 야기시키는 문제점과 폐기된 테이프가 소각되지 않는 문제점이 있다. Conventionally, casting tapes made of glass fiber are lightweight and durable, and are gradually replacing the plaster molding method due to advantages such as quick procedure time, convenient operation and easy back-end. However, the tape made of glass fiber is damaged by the impact due to the material property, or allergy is caused by the glass fiber dust, and in particular, the glass fiber dust is generated in the cutting step for manufacturing and use, causing respiratory diseases and skin diseases There is a problem that the discarded tape is not burned.
한편 상기 유리섬유의 문제점 때문에 대한민국 특허발명 제201873호에서는 폴리에스테르 섬유와 지지체의 경사방향으로 시장성을 부여하는 섬유가 혼입되어 있는 캐시팅 테이프용 폴리에스테르 지지체에 있어서, 고모듈러스를 지닌 폴리에스테르 섬유와 지지체의 경사방향으로 신장성을 부여하는 탄성섬유로서 폴리에스테르 탄성섬유 단독 또는 폴리에스테르 탄성섬유에 폴리우레탄 탄성섬유가 혼합 편성된 탄성섬유가 혼입되어 있는 캐스팅 테이프용 폴리에스테르 지지체가 제안되었다.On the other hand, Korean Patent No. 201873 discloses a polyester support for a caster tape in which a polyester fiber and a fiber for marketability are mixed in an oblique direction of the support, There has been proposed a polyester support for casting tapes in which polyester elastic fibers alone or elastic fibers mixed with polyurethane elastic fibers mixed with polyester elastic fibers are mixed as elastic fibers for imparting extensibility in the slanting direction of the support.
상기와 같은 방식은 신장률이 향상되는 장점이 있기는 하나 신장된 후 완전 회복이 되는 탄성사의 특성으로 시술단계에서 신장된 지지체가 경화되는 과정에서 과도하게 수축되어 환자의 환부에 압박을 가하게 되어 통증을 유발하는 문제가 있었다.Although the above-mentioned method has the advantage of improving the elongation, it is a characteristic of the elastic fiber which is fully recovered after elongation, which causes excessive shrinkage of the elongated support during the curing process, There was a problem that caused.
이에 탄성회복력이 저감된 원사를 이용한 제품들도 소개되고 있기는 하나 최종 직편물에서 표면적이 늘어나 표면기공이 현저하게 감소되는 문제점이 발생하고 특히 도포되는 경화형 우레탄 수지의 양이 많아져 시술 후 기포가 발생하고 이것이 원단내의 미세기공을 박하 통기성이 나빠져 석고 몰딩 방식의 단점이 동일하게 재연되고 또시술과정에서 경화시간이 늘어나는 문제점이 있었다.Therefore, there is a problem in that the surface area of the final woven fabric is increased and the surface pores are remarkably decreased. Especially, the amount of the curing type urethane resin to be applied is increased, Which causes the micropores in the fabric to have poor ventilating ability, resulting in the same disadvantages of the gypsum molding method, and the curing time is increased during the procedure.
이에 지지체로서의 역할을 수행하면서 시술 후 압박의 정도가 적절하며 통기성까지 확보될 수 있는 캐스팅 테이프의 요구가 대두되었다.
Therefore, there has been a demand for a casting tape which can provide a sufficient degree of compression and ventilation after performing the operation as a support.
상기와 같은 문제점을 해결하기 위하여 본 발명의 목적은 기계적 신장률을 유지하면서 압박에 의한 통증이 완화되는 신장회복률이 확보된 캐스팅 테이프 지지체를 제공하는데 있다.It is an object of the present invention to provide a casting tape support in which the elongation recovery rate is ensured in which the pain caused by compression is relieved while maintaining the mechanical elongation.
또한 본 발명은 위의 특징을 보유하면서 지지체의 기공을 유지하여 통기성이 확보된 캐스팅 테이프 지지체를 제공하는데 있다.
Another object of the present invention is to provide a casting tape support which retains the above characteristics and maintains pores of the support to ensure air permeability.
본 발명은 정형외과용 캐스팅 테이프의 지지체로서, 상기 지지체는 경사로 폴리에스테르계 섬유와 DTY가 1:1 내지 2:1의 비율(중량기준)로 이루어져 있고, 상기 DTY가 히팅이나 열수에 의해 수축된 상태로 이루어진 편직물을 포함하는 정형외과용 캐스팅 테이프의 지지체를 제공한다. The present invention relates to a support for an orthopedic casting tape, wherein the support comprises a slant polyester fiber and a DTY in a ratio of 1: 1 to 2: 1 (by weight), wherein the DTY is shrunk by heating or hot water The present invention also provides a support for an orthopedic casting tape comprising a knitted fabric made in a state of being knitted.
또한 본 발명은 상기 지지체의 탄성계수가 0.02 내지 0.03인 정형외과용 캐스팅 테이프의 지지체를 제공한다. The present invention also provides a support for an orthopedic casting tape having a modulus of elasticity of 0.02 to 0.03.
또한 본 발명은 상기 지지체의 회복계수가 0.07 내지 0.08인 정형외과용 캐스팅 테이프의 지지체를 제공한다. The present invention also provides a support for an orthopedic casting tape wherein the recovery factor of the support is 0.07 to 0.08.
또한 본 발명은 상기 지지체의 신장-회복계수 0.045 내지 0.055인 정형외과용 캐스팅 테이프의 지지체를 제공한다. The present invention also provides a support for an orthopedic casting tape having an extension-recovery coefficient of from 0.045 to 0.055.
또한 본 발명은 상기 폴리에스테르 섬유가 300 내지 500D의 고강력사이고, DTY가 120 내지 200D로 이루어진 정형외과용 캐스팅 테이프의 지지체를 제공한다.
The present invention also provides a support for an orthopedic casting tape wherein the polyester fiber has a high strength of 300 to 500 D and a DTY of 120 to 200 D.
본 발명은 신장-회복에 관한 최적의 조건을 제시함으로서 기계적 강신도를 유지하면서 압박에 의한 통증이 완화되는 신장회복률이 확보된 장점이 있다.The present invention has the advantage of securing the kidney recovery rate in which the pain due to compression is alleviated while maintaining the mechanical strength and strength by suggesting optimal conditions for kidney-recovery.
또한 본 발명은 위의 특징을 보유하면서 원사 특성 및 구조를 통해 지지체의 기공을 유지하여 통기성이 확보된 특징이 있다.
In addition, the present invention is characterized in that air permeability is secured by maintaining pores of a support through yarn characteristics and structure while retaining the above characteristics.
도 1은 본 발명의 바람직한 일실시예에 의한 하중-신장률 그래프.
도 2는 본 발명의 바람직한 일실시예에 의한 하중-신장회복률 그래프.1 is a load-elongation graph according to a preferred embodiment of the present invention.
2 is a load-elongation recovery graph according to a preferred embodiment of the present invention.
이하 본 발명에 첨부된 도면을 참조하여 본 발명의 바람직한 일실시예를 상세히 설명하기로 한다. 우선, 도면들 중, 동일한 구성요소 또는 부품들은 가능한 한 동일한 참조부호를 나타내고 있음에 유의하여야 한다. 본 발명을 설명함에 있어, 관련된 공지기능 혹은 구성에 대한 구체적인 설명은 본 발명의 요지를 모호하지 않게 하기 위하여 생략한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. First, it should be noted that, in the drawings, the same components or parts have the same reference numerals as much as possible. In the following description of the present invention, a detailed description of known functions and configurations incorporated herein will be omitted so as to avoid obscuring the subject matter of the present invention.
본 명세서에서 사용되는 정도의 용어 "약", "실질적으로" 등은 언급된 의미에 고유한 제조 및 물질 허용오차가 제시될 때 그 수치에서 또는 그 수치에 근접한 의미로 사용되고, 본 발명의 이해를 돕기 위해 정확하거나 절대적인 수치가 언급된 개시 내용을 비양심적인 침해자가 부당하게 이용하는 것을 방지하기 위해 사용된다.The terms "about "," substantially ", etc. used to the extent that they are used herein are intended to be taken to mean an approximation of, or approximation to, the numerical values of manufacturing and material tolerances inherent in the meanings mentioned, Accurate or absolute numbers are used to help prevent unauthorized exploitation by unauthorized intruders of the referenced disclosure.
본 발명의 일실시예에 의한 정형외과용 캐스팅 테이프 지지체는 편물로서 형성될 수 있다. 편물 중에서도 조직자체의 신장성을 고려할 때 경편으로 이루어질 수 있다. An orthopedic casting tape support according to an embodiment of the present invention may be formed as a knitted fabric. Among knitted fabrics, it can be made of warp yarn considering the extensibility of the fabric itself.
본 발명의 일실시예에 의한 지지체는 경편으로서 위사는 일반 소재일 수 있으나 비제한적인 예로서 폴리에스테르계일 수 있다. 기계적 물성과 소수성으로 인해 적합한 것으로 판단된다. 또 경사는 복수의 원사가 사용될 수 있는데, 비제한적인 예로서 2개의 서로 다른 종류일 수 있으며, 하나는 일반 폴리에스테르계 섬유, 다른 하나는 폴리에스테르계 DTY를 이용할 수 있다.The support according to an embodiment of the present invention may be a general material as a warp piece, but may be a polyester material as a non-limiting example. Mechanical properties and hydrophobicity. Also, the warp yarns may be of a plurality of yarns, which may be of two different types as a non-limiting example, one of which may be a polyester-based fiber and the other may be a polyester-based DTY.
위와 같은 준비과정으로 편직준비과정으로 정의할 수 있고, 위사용 원사와 경사용 원사를 준비할 수 있다. 경사용 원사는 일반 폴리에스테르계 섬유와 DTY가 1:1 내지 2:1(중량기준)로 공급되어 편직될 수 있다. 상기 범위내에서 후술할 DTY와 수축 및 신장에 의해 통기성이 확보되는 장점이 있다.This preparation process can be defined as a knitting preparation process, and the above used yarn and light yarn can be prepared. Yarn yarns can be knitted by feeding common polyester fibers and DTY in a ratio of 1: 1 to 2: 1 (by weight). Within this range, there is an advantage that the DTY to be described later and the air permeability are secured by shrinkage and elongation.
상기와 같이 준비과정이 완료되면 통상의 경편 편직방식으로 편물로 형성될 수있다.(편직과정)When the preparation process is completed as described above, the knitted fabric can be formed into a knitted fabric by a conventional knitting method.
상기 편직된 지지체는 히팅이나 열수에 의해 DTY를 수축시키는 과정으로 거치게 된다.(수축과정) 상기 수축된 DTY로 인해 기공성과 신장성이 보강되는데 DTY는 본래의 포텐셜에 비해 수축된 상태가 유지되어 있고 상기 수축된 포텐셜이 사용시 신장되면서 신장할 수 있는 여력이 더 많아지게 되어 신장성이 향상될 수 있다. 이러한 신장성은 캐스팅 테이프가 사용시 환부를 감싸기 위해 신장되어야 하기 때문이다. The knitted support is subjected to a process of shrinking DTY by heating or hot water (shrinkage process). The shrunk DTY reinforces porosity and extensibility. The DTY is maintained in a contracted state compared to the original potential The contracted potential is elongated at the time of use so that the elongation capability can be increased, and the extensibility can be improved. This extensibility is due to the casting tape being stretched to wrap the affected part in use.
이러한 신장성은 하중(Kgf)-변형률(%)와의 관계에서 탄성계수 0.02 내지 0.03이 바람직함을 발견하였다.(도 1 참조) 상기 범위를 초과하는 경우 테이프를 신장시키는데 하중이 상당히 요구된다. 즉 시술과정에서 환부를 감싸는데 시술자의 과도한 노력이 필요하며 후술할 신장회복률과 관련하여 과도한 압박이 발생될 가능성이 높은 문제점이 있다. 또한 상기 범위 미만인 경우 시술과정에서 적은 하중으로 잘 신장되는 점이 있기는 하나 시술된 후 형태안정성 및 적절한 압박력이 발생하지 못하는 문제점이 있는 것으로 본 발명자는 평가하였다. It has been found that the elongation is preferably in the range of 0.02 to 0.03 in relation to the load (Kgf) - strain (%) (see Fig. 1). That is, an excessive effort of the practitioner is required to wrap the lesion in the procedure, and there is a high possibility that excessive compression is likely to occur in relation to the renal recovery rate to be described later. In addition, the inventors of the present invention evaluated that when the diameter is less than the above range, there is a problem that the elongation is well under a small load during the procedure, but the shape stability and proper pressing force do not occur.
한편 사용(시술)환경에서 상기 신장된 캐스팅 테이프는 다시 수축되어야 하는데 이를 위하여 종래에는 탄성사(스판덱스 또는 고무사 등)를 사용한 것이다. 그러나 위에서 설명한 바와 같이 탄성사는 과도한 수축회복력으로 인해 환부를 강하게 압박하는 단점이 존재한 것이다. 이에 캐스팅 테이프가 환부에 고정될 정도의 수축력을 보유하면서 환부를 압박하여 통증을 유발하지 않을 정도의 수축력이 최적치가 검토되어야 하는 것이다. On the other hand, in the used environment, the stretched casting tape must be retracted again. For this purpose, elastic yarn (such as spandex or rubber yarn) is used. However, as described above, the elastic yarn has a disadvantage that it strongly presses the affected part due to excessive shrinking and restoring force. Therefore, it is necessary to examine the optimum value of the shrinking force not to cause pain by pressing the affected part while holding the shrinking force enough to fix the casting tape to the affected part.
이에 본 발명자의 다수의 시험결과 신장회복률은 하중(Kgf)-회복률(%)와의 관계에서 미분값을 회복계수로 정의할 때, 상기 회복계수는 0.07 내지 0.08이 바람직함을 발견하였다.(도 2 참조) 상기 회복률이 위 범위임은 시술 후 지나친 회복력으로 인해 환부에 통증을 유발하지 않으면서 형태를 유지하기 위함이다.Accordingly, the inventors of the present invention have found that the elongation recovery rate is preferably 0.07 to 0.08 when the derivative value is defined as a recovery factor in relation to the load (Kgf) - recovery rate (%). The recovery rate is in the upper range to maintain the shape without causing pain in the affected part due to excessive resilience after the procedure.
한편, 신장률과 회복률간의 상관성은 동일 하중(Kgf) 대비 기울기의 편차로서 정의하는데, 본 명세서에서는 이를 신장-회복계수로 명명하기로 한다. 상기 편차는 0.045 내지 0.055임이 바람직하다. 이러한 관계는 시술시 작업의 편리성으로 위하여 신장이 용이하면서, 신장회복시 과도한 회복이 되지 않도록 할 수 있는 상관계수라 할 수 있다. On the other hand, the correlation between the elongation and the recovery rate is defined as the deviation of the slope with respect to the same load (Kgf), which will be referred to as the elongation-recovery coefficient in this specification. The deviation is preferably 0.045 to 0.055. This relationship can be regarded as a correlation coefficient that can be easily elongated for convenience of operation at the time of the procedure and can prevent excessive recovery at the time of renal recovery.
이하 실시예로서 설명하기로 한다.Examples will be described below.
실시예Example
위사로 420/96(D/F) 폴리에스테르사를 사용하고, 경사로 420/96(D/F) 폴리에스테르사와 DTY 150/48(D/F)를 2:1 비율(중량기준)로 사용하여 경편조직으로 제편하였다. 상기 제편 후 150도의 열수에서 DTY를 수축가공한 후 상기 제편된 원단의 신장률과 신장회복률을 측정하였다. 결과는 표 1과 같다
Using a 420/96 (D / F) polyester yarn as a weft yarn and a 420/96 (D / F) polyester yarn as a warp and a DTY 150/48 (D / F) as a 2: 1 ratio And a lightweight tissue. The DTY was shrunk from the hot water at a temperature of 150 degrees Celsius and then the elongation and elongation recovery of the prepared fabric were measured. The results are shown in Table 1
* 신장률(%) 시험방법* Elongation (%) Test Method
- 조건 1 : 0.2Kgf의 하중을 건 상태로 1분간 방치 후 표선 간 거리 측정- Condition 1: Leave a load of 0.2 Kgf in a dry state for 1 minute and measure the distance between the lines
- 조건 2 : 0.4Kgf의 하중을 건 상태로 1분간 방치 후 표선 간 거리 측정- Condition 2: Leave a load of 0.4 Kgf in a dry state for 1 minute, and measure the distance between lines
- 조건 3 : 0.6Kgf의 하중을 건 상태로 1분간 방치 후 표선 간 거리 측정- Condition 3: Leave a load of 0.6 Kgf in a dry state for 1 minute and measure the distance between the lines
- 조건 4 : 0.8Kgf의 하중을 건 상태로 1분간 방치 후 표선 간 거리 측정- Condition 4: Leave a load of 0.8 Kgf in a dry state for 1 minute, and measure the distance between lines
- 조건 5 : 1.0Kgf의 하중을 건 상태로 1분간 방치 후 표선 간 거리 측정- Condition 5: Leave a load of 1.0 Kgf in a dry state for 1 minute, and measure the distance between lines
- 조건 6 : 1.2Kgf의 하중을 건 상태로 1분간 방치 후 표선 간 거리 측정
- Condition 6: After leaving a load of 1.2 Kgf for 1 minute,
* 신장회복율(%) 시험방법* Renal recovery rate (%) Test method
- 조건 1 : 0.2Kgf의 하중을 건 상태로 1분간 방치, 상기 하중을 제거 후 편평한 대 위에 1분간 방치 후 표선 간 거리 측정- Condition 1: Leave a load of 0.2 Kgf in a dry state for 1 minute, remove the load and leave it on a flat surface for 1 minute,
- 조건 2 : 0.4Kgf의 하중을 건 상태로 1분간 방치, 상기 하중을 제거 후 편평한 대 위에 1분간 방치 후 표선 간 거리 측정- Condition 2: Leave a load of 0.4 Kgf in a dry state for 1 minute, remove the load, and leave it on a flat surface for 1 minute.
- 조건 3 : 0.6Kgf의 하중을 건 상태로 1분간 방치, 상기 하중을 제거 후 편평한 대 위에 1분간 방치 후 표선 간 거리 측정- Condition 3: Leave a load of 0.6 Kgf in a dry state for 1 minute, remove the load, and leave it on a flat surface for 1 minute.
- 조건 4 : 0.8Kgf의 하중을 건 상태로 1분간 방치, 상기 하중을 제거 후 편평한 대 위에 1분간 방치 후 표선 간 거리 측정- Condition 4: The load of 0.8 Kgf was left in a dry state for 1 minute, the load was removed, and the plate was allowed to stand on a flat surface for 1 minute.
- 조건 5 : 1.0Kgf의 하중을 건 상태로 1분간 방치, 상기 하중을 제거 후 편평한 대 위에 1분간 방치 후 표선 간 거리 측정- Condition 5: Allow a load of 1.0 Kgf to stand for 1 minute, remove the load, and leave it on a flat surface for 1 minute.
- 조건 6 : 1.2Kgf의 하중을 건 상태로 1분간 방치, 상기 하중을 제거 후 편평한 대 위에 1분간 방치 후 표선 간 거리 측정
- Condition 6: The load of 1.2 Kgf was left in a dry state for 1 minute, the load was removed, then left on a flat surface for 1 minute,
이상에서 설명한 본 발명은 전술한 실시예 및 첨부된 도면에 의해 한정되는 것이 아니고, 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 여러 가지 치환, 변형 및 변경이 가능함은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에게 있어서 명백할 것이다.
It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the inventions. It will be clear to those who have knowledge of.
Claims (5)
상기 지지체는 경사로 폴리에스테르계 섬유와 DTY가 1:1 내지 2:1의 비율(중량기준)로 이루어져 있고, 상기 DTY가 히팅이나 열수에 의해 수축된 상태로 이루어진 편직물을 포함하는 정형외과용 캐스팅 테이프의 지지체. As a support for an orthopedic casting tape,
Wherein the support is a casting tape for orthopedic surgery comprising a knitted fabric having a slant polyester fiber and DTY in a ratio of 1: 1 to 2: 1 (by weight) and the DTY being contracted by heating or hot water / RTI >
상기 지지체의 탄성계수가 0.02 내지 0.03인 정형외과용 캐스팅 테이프의 지지체. The method according to claim 1,
Wherein the support has a modulus of elasticity of 0.02 to 0.03.
상기 지지체의 회복계수가 0.07 내지 0.08인 정형외과용 캐스팅 테이프의 지지체. The method according to claim 1,
Wherein the support has a recovery coefficient of 0.07 to 0.08.
상기 지지체의 신장-회복계수 0.045 내지 0.055인 정형외과용 캐스팅 테이프의 지지체. The method according to claim 1,
The support of an orthopedic casting tape having an extension-recovery coefficient of from 0.045 to 0.055.
상기 폴리에스테르 섬유는 300 내지 500D의 고강력사이고, DTY는 120 내지 200D로 이루어진 정형외과용 캐스팅 테이프의 지지체.
The method according to claim 1,
Wherein the polyester fiber has a high tensile strength of 300 to 500D and the DTY is 120 to 200D.