KR101434611B1 - Manufacturing method of soft glitter sheet - Google Patents

Manufacturing method of soft glitter sheet Download PDF

Info

Publication number
KR101434611B1
KR101434611B1 KR1020120023195A KR20120023195A KR101434611B1 KR 101434611 B1 KR101434611 B1 KR 101434611B1 KR 1020120023195 A KR1020120023195 A KR 1020120023195A KR 20120023195 A KR20120023195 A KR 20120023195A KR 101434611 B1 KR101434611 B1 KR 101434611B1
Authority
KR
South Korea
Prior art keywords
thin film
sheet
polyurethane
film sheet
layer
Prior art date
Application number
KR1020120023195A
Other languages
Korean (ko)
Other versions
KR20130102182A (en
Inventor
장순동
Original Assignee
장순동
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 장순동 filed Critical 장순동
Priority to KR1020120023195A priority Critical patent/KR101434611B1/en
Publication of KR20130102182A publication Critical patent/KR20130102182A/en
Application granted granted Critical
Publication of KR101434611B1 publication Critical patent/KR101434611B1/en

Abstract

연질이면서 신축성이 우수한 폴리우레탄 박막필름을 기재층으로 사용하여 우수한 신축성, 굴곡성 및 내구성을 갖도록 한 연질 반짝이시트 제조방법이 개시된다. 개시된 반짝이시트는 폴리우레탄 박막시트와 폴리에틸렌 박막시트를 합지하는 단계와; 상기 폴리에틸렌 박막시트 저면에 접착제를 도포한 다음 종이를 부착하는 지지층 형성단계와; 상기 폴리우레탄 박막시트 상면에 바인더를 도포한 다음 반짝이가루를 분사하여 반짝이층을 형성하고 나서 상기 반짝이층 위로 투명코팅층을 형성하는 장식층 형성단계와; 상기 합지된 폴리우레탄 박막시트와 폴리에틸렌 박막시트에서 폴리에틸렌 박막시트를 분리하는 단계와; 상기 폴리에틸렌 박막시트가 분리된 폴리우레탄 박막시트의 저면에 프라이머층을 형성하는 단계와; 상면에 실리콘 재질의 이형수지와 아크릴 재질의 점착성 수지가 순차적으로 도포된 이형필름을 상기 폴리우레탄 박막시트과 합지한 후 2일 내지 3일간 자연건조하는 단계로 이루어지는 것을 특징으로 한다.Disclosed is a method for producing a soft shiny sheet using a polyurethane thin film having excellent softness and stretchability as a base layer to have excellent stretchability, flexibility and durability. The disclosed sparkling sheet comprises the steps of: laminating a polyurethane thin film sheet and a polyethylene thin film sheet; A support layer forming step of applying an adhesive to the bottom surface of the polyethylene thin film sheet and then attaching the paper; A decorative layer forming step of forming a transparent coating layer on the glitter layer by forming a glitter layer by spraying a glitter powder on a top surface of the polyurethane thin film sheet; Separating the polyethylene foil sheet from the laminated polyurethane foil sheet and the polyethylene foil sheet; Forming a primer layer on a bottom surface of the polyurethane thin film sheet from which the polyethylene thin film sheet is separated; And a releasing film on which a releasing resin of silicone material and an adhesive resin of acrylic material are sequentially coated on the upper surface of the polyurethane thin film sheet, followed by natural drying for 2 to 3 days after laminating the releasing film with the polyurethane thin film sheet.

Description

연질 반짝이시트 제조방법{MANUFACTURING METHOD OF SOFT GLITTER SHEET}TECHNICAL FIELD [0001] The present invention relates to a method for producing a soft shiny sheet,

본 발명은 연질 반짝이시트 제조방법에 관한 것으로, 연질이면서 신축성이 우수한 폴리우레탄 박막필름을 기재층으로 사용하여 우수한 신축성, 굴곡성 및 내구성을 갖도록 함과 동시에 표면에 폴리우레탄 박막필름을 형성하여 시트표면의 손상이나 이물질이 부착되는 것을 방지하도록 한 연질 반짝이시트 제조방법에 관한 것이다.
The present invention relates to a method for producing a soft sparked sheet, which uses a polyurethane thin film having excellent softness and stretchability as a base layer to have excellent stretchability, flexibility and durability, and to form a polyurethane thin film on the surface, Thereby preventing damage or foreign matter from adhering thereto.

반짝이시트란 기재층 위에 반짝이가루로 이루어진 반짝이층을 형성한 시트로서, 일정한 도형, 글자, 숫자 등으로 절단한 후 가방이나 신발, 의류등에 부착하여 반짝거리는 특성에 의해 시각적 효과를 높이고 외적 미려함을 향상시키는 장식 부재이다.
A glittering sheet is a sheet formed with a glitter layer on a substrate layer. It is cut into a certain figure, letter, number, etc., and then attached to a bag, shoes, clothing, etc. to increase visual effect and enhance external beauty .

상기와 같은 반짝이시트는 피부착물에 부착된 상태에서 피부착물과 분리된 느낌이나 뻣뻣한 느낌을 주지 않는 것이 중요하다. 즉, 반짝이시트가 피부착물에 부착된 상태에서 피부착물이 굴곡하거나 신축될 때 이에 추종하여 그대로 굴국되거나 신축되어 피부착물과의 일체감을 주어야 한다.
It is important that such a shiny sheet does not give a feeling of separation or stiffness to the skin complex in the state of being attached to the skin complex. That is, when the skin complex is bent or stretched in a state where the glitter sheet is adhered to the skin complex, the skin complex should be bent or stretched to give a sense of unity with the skin complex.

이러한 관점에서 반짝이시트가 우수한 굴곡성과 신축성을 구비하도록 다양한 연구가 진행되고 있으며, 그 일례로 국내특허 제10-0589735호에서는 "보조 필름 상에 핫멜트를 도포 및 건조시켜 핫멜트층을 형성하는 단계; 상기 핫멜트층 상에 접착제를 도포하여 접착층을 형성하는 단계; 상기 접착층 상에 반짝이를 도포 및 건조시겨 반짝이층을 형성하는 단계; 상기 반짝이층 상에 투명 수지 도료를 도포하여 투명 코팅층을 형성하는 단계; 및 상기 투명 코팅층 상에 투명 필름을 합지하는 것과 동시에 상기 보조 필름을 핫멜트층에서 분리하는 단계를 포함하여 제조된 것을 특징으로 하는 장식용 시트지의 제조방법"을 개시하고 있다.
In this regard, various researches have been conducted to provide a shiny sheet having superior flexibility and stretchability in this respect. For example, Korean Patent No. 10-0589735 discloses a method for producing a hot melt film by coating and drying a hot melt on an auxiliary film to form a hot melt layer, A method for manufacturing a transparent conductive film, comprising: applying an adhesive on a hot melt layer to form an adhesive layer; forming a shiny layer by applying and drying a glitter on the adhesive layer; And a step of laminating a transparent film on the transparent coating layer and at the same time separating the auxiliary film from the hot-melt layer. "

상기 방법에 따라 제조된 장식용 시트지는 기재층이 없이 핫멜트층에 직접 반짝이층이 형성되므로 우수한 굴곡성과 신축성을 갖아 피부착물과의 일체감이 향상되는 잇점이 있다. 하지만, 핫멜트를 사용하기 때문에 피부착물에 부착할 때는 반드시 열이 필요하므로 사용이 제한적이며, 기재층이 없기 때문에 강도가 저하되어 쉽게 찢어지는 단점이 있다.
The decorative sheet produced according to the above method is advantageous in that the shiny layer is directly formed on the hot-melt layer without the substrate layer, so that it has excellent flexibility and stretchability and improves the unity with the skin complex. However, since hot melt is used, adhesion to skin complexes requires heat, which limits the use thereof.

본 발명은 상기 문제점을 해결하기 위해 안출된 것으로, 연질이면서 신축성이 우수한 폴리우레탄 박막필름을 기재층으로 사용하여 우수한 신축성, 굴곡성 및 내구성을 갖도록 동시에 표면에 폴리우레탄 박막필름을 형성하여 시트표면의 손상이나 이물질이 부착되는 것을 방지하도록 한 연질 반짝이시트 제조방법을 제공하는 것이다.
Disclosure of the Invention The present invention has been conceived in order to solve the above problems, and it is an object of the present invention to provide a polyurethane thin film having excellent flexibility, flexibility and durability by using a polyurethane thin film excellent in softness and stretchability as a substrate layer, Or foreign matters from adhering to the surface of the backsheet.

상기 본 발명의 목적은 폴리우레탄 박막시트와 폴리에틸렌 박막시트를 합지하는 단계와; 상기 폴리에틸렌 박막시트 저면에 접착제를 도포한 다음 종이를 부착하는 지지층 형성단계와; 상기 폴리우레탄 박막시트 상면에 바인더를 도포한 다음 반짝이가루를 분사하여 반짝이층을 형성하고 나서 상기 반짝이층 위로 투명코팅층을 형성하는 장식층 형성단계와; 상기 합지된 폴리우레탄 박막시트와 폴리에틸렌 박막시트에서 폴리에틸렌 박막시트를 분리하는 단계와; 상기 폴리에틸렌 박막시트가 분리된 폴리우레탄 박막시트의 저면에 프라이머층을 형성하는 단계와; 상면에 실리콘 재질의 이형수지와 아크릴 재질의 점착성 수지가 순차적으로 도포된 이형필름을 상기 폴리우레탄 박막시트과 합지한 후 2일 내지 3일간 자연건조하는 단계와; 상기 장식층 상면에 접착제를 통해 폴리우레탄 필름을 형성하는 표면보호층 형성단계로 이루어지는 것을 특징으로 하는 연질 반짝이시트 제조방법을 제공함으로써 달성된다.
It is an object of the present invention to provide a method of manufacturing a polyurethane thin film sheet, comprising: laminating a polyurethane thin film sheet and a polyethylene thin film sheet; A support layer forming step of applying an adhesive to the bottom surface of the polyethylene thin film sheet and then attaching the paper; A decorative layer forming step of forming a transparent coating layer on the glitter layer by forming a glitter layer by spraying a glitter powder on a top surface of the polyurethane thin film sheet; Separating the polyethylene foil sheet from the laminated polyurethane foil sheet and the polyethylene foil sheet; Forming a primer layer on a bottom surface of the polyurethane thin film sheet from which the polyethylene thin film sheet is separated; A release film on which an release agent of a silicone material and an acrylic resin are sequentially applied on an upper surface of the polyurethane thin film sheet, followed by natural drying for 2 to 3 days after laminating the release film with the polyurethane thin film sheet; And a surface protective layer forming step of forming a polyurethane film on an upper surface of the decorative layer through an adhesive agent.

본 발명에 따른 연질 반짝이시트 제조방법에 의하면, 연질이면서 신축성이 우수한 폴리우레탄 박막필름을 기재층으로 사용하기 때문에 우수한 신축성, 굴곡성 및 내구성을 갖는 연질 반짝이시트를 제조할 수 있으며, 이와 같은 연질 반짝이시트를 피부착물에 부착하면 피부착물이 굴곡하거나 신축될 때 이에 추종하여 그대로 굴국되거나 신축되기 때문에 피부착물과 일체감이 향상되는 효과가 있다. 또한, 본 발명에 따라 제조된 연질 반짝이시트는 표면에 형성된 폴리우레탄 박막필름으로 인해 시트표면이 이물질로부터 보호되는 효과가 있다.
According to the method of producing a soft sparked sheet according to the present invention, a soft sparkling sheet having excellent stretchability, flexibility and durability can be produced because a polyurethane thin film having flexibility and excellent stretchability is used as a substrate layer. Is adhered to a skin complex, the skin complex can be improved in unity because the skin complex is flexed or stretched, followed by bending or stretching. Further, the soft sparked sheet produced according to the present invention has an effect that the sheet surface is protected from foreign matter by the polyurethane thin film formed on the surface.

도1(a) 내지 도1(g)는 본 발명에 따른 연질 반짝이시트의 제조방법을 시계열적으로 도시한 도면이며,
도2는 본 발명에 따라 폴리우레탄 박막시트와 폴리에틸렌 박막시트를 합지하는 단계를 설명하기 위한 도면이며,
도3은 본 발명에 따라 제조된 연질 반짝이시트의 단면도이다.Figs. 1 (a) to 1 (g) are views showing a method of manufacturing a flexible glaze sheet according to the present invention in a time-
2 is a view for explaining a step of laminating a polyurethane thin film sheet and a polyethylene thin film sheet according to the present invention,
3 is a cross-sectional view of a soft sparkling sheet made in accordance with the present invention.

이하, 첨부된 도면을 참고하여 본 발명에 따른 연질 반짝이시트 제조방법을 상세하게 설명한다. 도1(a) 내지 도1(g)는 본 발명에 따른 연질 반짝이시트의 제조방법을 시계열적으로 도시한 도면이다.
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, a method of manufacturing a soft sparked sheet according to the present invention will be described in detail with reference to the accompanying drawings. Figs. 1 (a) to 1 (g) are views showing a method of manufacturing a soft glossy sheet according to the present invention in a time-wise manner.

본 발명에 따른 연질 반짝이시트 제조방법는 도1(a)에 도시된 바와 같이 먼저 폴리우레탄 박막시트(110)와 폴리에틸렌 박막시트(120)를 합지하는 단계를 포함한다.
The method of manufacturing a soft sparked sheet according to the present invention includes a step of first joining a polyurethane thin film sheet 110 and a polyethylene thin sheet 120 as shown in FIG. 1 (a).

상기 폴리우레탄 박막시트(110)는 본 발명에 따른 반짝이시트의 기재층으로, 그 상면에 장식층(140)을 형성하고 그 하면에 지지층(130)을 형성한 다음 지지층(130)을 제거함으로써 추후 장식층(140)을 기초해주는 역할을 수행한다.
The polyurethane thin film sheet 110 is a base layer of a sparkling sheet according to the present invention. A decoration layer 140 is formed on an upper surface thereof, a support layer 130 is formed on a lower surface thereof, And serves as a base for the decorative layer 140.

여기서, 기재층으로 사용되는 박막시트(110)는 폴리우레탄 재질이다. 폴리우레탄은 공지된 바와 같이 연질성, 신축성 및 탄성회복성이 매우 우수하다. 또한, 내구성이 우수하여 쉽게 노화되지 않으며 무게가 가볍다는 특성이 있다. 따라서 본 발명에서는, 반짝이시트가 우수한 신축성, 굴곡성 및 내구성을 갖도록 상기와 같은 폴리우레탄 박막시트를 기재층으로 사용하는 것이다.
Here, the thin sheet 110 used as the substrate layer is made of polyurethane. Polyurethanes are very excellent in softness, stretchability and elastic recovery as known. In addition, it has excellent durability and is not easily aged and has a light weight. Therefore, in the present invention, such a polyurethane thin film sheet is used as a substrate layer so that the light-shine sheet has excellent stretchability, flexibility and durability.

상기 폴리우레탄 박막시트(110)의 두께는 40㎛ 내지 60㎛인 것이 바람직한 데, 그 두께가 40㎛ 이하이면 두께가 너무 얇아 제조가 쉽지 않으며, 폴리에틸렌 박막시트와의 합지과정과 분리과정에서 취급이 어려워 곤란하며, 그 두께가 60㎛ 이상이면 두께가 너무 두꺼워 본 발명에서 추구하고자 하는 신축성과 굴곡성을 저해하는 요인이 되어 곤란한다.
The thickness of the polyurethane thin film sheet 110 is preferably 40 to 60 占 퐉. If the thickness of the polyurethane thin film sheet 110 is 40 占 퐉 or less, the thickness of the polyurethane thin film sheet 110 is too thin to be easily manufactured. And if the thickness is 60 m or more, the thickness is too thick, which is a factor that hinders the stretchability and flexibility to be sought in the present invention.

상기 폴리우레탄 박막시트(110)와 폴리에틸렌 박막시트(120)는 도2에 도시된 바와 같이 한쌍의 가압롤러(R1, R2) 사이를 통과하면서 자체 택기, 즉 폴리우레탄 박막시트(110)와 폴리에틸렌 박막시트(120)의 자체 끈적거림으로 서로 합지되는 것이 바람직하다.
The polyurethane thin film sheet 110 and the polyethylene thin film sheet 120 are passed through a pair of pressure rollers R1 and R2 as shown in FIG. 2 to form a polyurethane thin film sheet 110, It is preferable that the sheets 120 are joined to each other by self-sticking.

즉, 폴리우레탄 박막시트(110) 상부에 장식층을 형성한 다음에는 폴리우레탄 박막시트(110)는 폴리에틸렌 박막시트(120)와 다시 분리되는 데, 접착제를 사용하여 폴리우레탄 박막시트(110)와 폴리에틸렌 박막시트(120)를 서로 합지하면 나중에 분리가 곤란하다. 따라서, 본 발명에서는 폴리우레탄 박막시트(110)와 폴리에틸렌 박막시트(120)를 중첩하여 한 쌍의 가압롤러(R1, R2) 사이를 통과시키면 시트 자체에서 발생하는 택기(끈적거림)로 인해 폴리우레탄 박막시트(110)와 폴리에틸렌 박막시트(120)가 서로 합지되며, 접착제를 사용하지 않기 때문에 추후 쉽게 분리될 수 있다.
That is, after the decorative layer is formed on the polyurethane thin film sheet 110, the polyurethane thin film sheet 110 is separated from the polyethylene thin film sheet 120, and the polyurethane thin film sheet 110 If the polyethylene thin sheet 120 is laminated to each other, separation is difficult later. Therefore, in the present invention, when the polyurethane thin film sheet 110 and the polyethylene thin film sheet 120 are stacked and passed between the pair of pressure rollers R1 and R2, the polyurethane The thin film sheet 110 and the polyethylene thin sheet 120 are laminated to each other and can be easily separated later because no adhesive is used.

여기서, 폴리에틸렌 시트(120)는 폴리우레탄 시트(110)보다는 경질이기 때문에 합지된 상태에서 폴리우레탄 시트(110)가 변형하는 것을 막아주는 역할을 수행한다.
Here, since the polyethylene sheet 120 is harder than the polyurethane sheet 110, the polyurethane sheet 110 plays a role of preventing the polyurethane sheet 110 from being deformed in a state of being laminated.

이와 같이, 상기 폴리우레탄 박막시트(110)와 폴리에틸렌 박막시트(120)를 합지한 다음에는, 도1(b)에 도시된 바와 같이 본 발명은 폴리에틸렌 박막시트(120) 저면에 접착제(131)를 도포한 다음 종이(132)를 부착하는 지지층(130)을 형성하게 된다.
1 (b), after the polyurethane thin film sheet 110 and the polyethylene thin film sheet 120 are laminated together, the present invention is characterized in that an adhesive 131 is applied to the bottom surface of the polyethylene thin film sheet 120 Thereby forming a supporting layer 130 to which the paper 132 is attached.

기재층인 폴리우레탄 시트(110)는 박막이기 때문에 지지력이 약해 장식층(140)을 형성하기 어렵고 특히 반짝이가루를 고정하기 위해 열챔버에 유입될 때 폴리우레탄 시트가 변형될 수 있기 때문에, 본 발명에서는 폴리우레탄 시트를 지지하여 작업성을 향상시킬 수 있도록 폴리에틸렌 시트의 저면에 지지층(130)을 형성하는 것이다.
Since the polyurethane sheet 110 as a base layer is a thin film, its supporting force is weak and it is difficult to form the decorative layer 140. In particular, since the polyurethane sheet can be deformed when it enters the heat chamber for fixing the glitter powder, The supporting layer 130 is formed on the bottom surface of the polyethylene sheet so that the polyurethane sheet can be supported and workability can be improved.

상기 지지층은 바람직하게 종이(132)이며 접착제(131)를 통해 폴리에틸렌 박막시트(120)에 접착된다. 상기 종이는 지지력과 열변형을 견딜수 있는 두께를 갖는 것이 좋으며 평활성을 갖는 골판지인 것이 바람직하다.
The support layer is preferably paper 132 and adhered to the polyethylene thin sheet 120 through the adhesive 131. The paper preferably has a thickness capable of withstanding the supporting force and thermal deformation, and is preferably a corrugated board having smoothness.

상기와 같이, 폴리우레탄 시트(110)의 저면에 지지층(130)을 형성한 다음에는 도1(c)에 도시된 바와 같이 폴리우레탄 시트(110)의 상면에 장식층(140)을 형성하게 된다. 상기 장식층(140)은 폴리우레탄 박막시트(110) 상면에 도포된 바인더층(141)과; 상기 바인더층(141) 위로 반짝이가루를 분사하여 이루어진 반짝이층(142)과; 반짝이층(142) 상면에 도포되는 투명코팅층(143)으로 구성된다.
As described above, after the support layer 130 is formed on the bottom surface of the polyurethane sheet 110, the decorative layer 140 is formed on the top surface of the polyurethane sheet 110 as shown in FIG. 1 (c) . The decorative layer 140 includes a binder layer 141 applied on the upper surface of the polyurethane thin film sheet 110; A glitter layer 142 formed by spraying glitter powder onto the binder layer 141; And a transparent coating layer 143 applied on the upper surface of the shiny layer 142.

당해분야에 알려진 통상의 방법에 따라 바인더를 도포한 다음 예를 들어, 반짝이를 뿌려주는 반짝이 분사통등을 이용하여 바인더층(141)에 반짝이가루를 도포하여 반짝이층(142)을 형성한다.
The binder is applied according to a conventional method known in the art, and then a glitter layer 142 is formed by applying glitter powder to the binder layer 141 using, for example, a glitter sprayer for spraying glitter.

다음으로, 상기 반짝이층(142)에 투명코팅층(143)을 형성하는 데, 상기 투명코팅층은 우레탄 엘라스토머가 함유된 투명수지도료를 100∼130℃의 온도에서 10초 내지 15초 동안 롤링으로 도포 및 건조시켜 형성한다. 여기서, 투명 수지 도료의 조성은 1.0∼2.0의 산가를 갖는 폴리에스테르 폴리올과 적어도 2 이상의 유리 이소시아네이트기를 함유하는 폴리이소시아네이트의 반응생성물인 우레탄 엘라스토머 60∼80중량%, 분산제 0.1∼1중량%, 레벨링제 0.1∼1중량% 및 나머지는 용매를 포함한다.
Next, a transparent coating layer 143 is formed on the sparkling layer 142. The transparent coating layer is formed by applying a transparent resin coating material containing urethane elastomer by rolling at a temperature of 100 to 130 캜 for 10 seconds to 15 seconds, And dried. Here, the composition of the transparent resin coating material is such that 60 to 80% by weight of a urethane elastomer as a reaction product of a polyester polyol having an acid value of 1.0 to 2.0 and a polyisocyanate containing at least 2 or more free isocyanate groups, 0.1 to 1% 0.1 to 1% by weight, and the remainder comprises a solvent.

상기 우레탄 엘라스토머는 연질 우레탄 고무와 같은 성질을 갖는 물질로서, 내굴곡성이 우수하고 2차 가공성을 용이하게 하며, 수지도료 내에 반짝이 등의 안료 투입시 소재면에 부착성을 부여하는 매개체 역할을 하는 동시에 반복되는 세탁에도 내부의 반짝이층을 보호할 수 있도록 적절한 유연성 및 강도를 부여하는 역할을 한다.
The urethane elastomer is a material having the same properties as the soft urethane rubber and has excellent bending resistance, facilitates secondary processability, serves as an agent for imparting adhesion to the material surface when a pigment such as a glitter is put into the resin coating It also provides adequate flexibility and strength to protect the inner shiny layer from repeated washing.

특히, 본 발명에서는 1.0∼2.0의 산가를 갖는 폴리에스테르 폴리올과 적어도 2 이상의 유리 이소시아네이트기를 함유하는 폴리이소시아네이트의 반응생성물인 우레탄 엘라스토머를 사용하여 상술한 바와 같은 특정 요구물성을 달성할 수 있음을 발견하였다.
Particularly, in the present invention, it has been found that a specific required property as described above can be achieved by using a urethane elastomer which is a reaction product of a polyester polyol having an acid value of 1.0 to 2.0 and a polyisocyanate containing at least two free isocyanate groups .

상기 투명 수지 중 우레탄 엘라스토머의 사용량은 60∼80중량%이다. 상기 우레탄 엘라스토머의 사용량이 60중량% 미만이면 반짝이 원단의 상단 코팅층으로서 목적하는 요구물성을 얻을 수 없고, 80중량%를 초과하면 가공성 및 취급성이 저하되는 문제점이 있다.
The amount of the urethane elastomer in the transparent resin is 60 to 80% by weight. If the amount of the urethane elastomer is less than 60% by weight, desired properties as the upper coating layer of the glitter fabric can not be obtained. If the amount of the urethane elastomer is more than 80% by weight, the processability and handleability are deteriorated.

상기 분산제는 안료 등의 분산을 용이하게 하는 첨가제이고, 레벨링제는 도료 표면 조정제로서 그 함량은 각각 0.1∼1.0중량%인 것이 요구 특성 발현 면에서 가장 적합하다. 상기 용매로는 중비점의 방향족 탄화수소계 용매 및 알코올 등의 저비점, 저취의 용매를 단독 또는 혼합하여 사용할 수 있지만, 특별히 이에 한정되는 것은 아니다. 이외에도 필요에 따라 안료 및 실리카 등의 소광제를 더욱 첨가할 수 있다.
The dispersing agent is an additive that facilitates dispersion of pigments and the like, and the leveling agent is 0.1 to 1.0 wt% each as a surface conditioner of a coating material, and is most suitable from the viewpoint of exhibiting required properties. As the solvent, an aromatic hydrocarbon solvent having a middle boiling point and a solvent having a low boiling point and a low boiling point such as alcohol may be used alone or in combination, but the present invention is not limited thereto. In addition, pigments and quenching agents such as silica may be further added if necessary.

이와 같이, 폴리우레탄 박막시트(110) 위에 장식층(140)이 형성되면, 도1(d)에 도시된 바와 같이 상기 합지된 폴리우레탄 박막시트(110)와 폴리에틸렌 박막시트(120)에서 폴리에틸렌 박막시트(120)를 분리하여, 폴리에틸렌 박막시트(120) 및 그 하부에 형성된 지지층(130)을 제거한다. 이 때, 폴리우레탄 박막시트(110)와 폴리에틸렌 박막시트(120)는 접착제가 아닌 자체 택기, 즉 자체 끈적거림으로 합지된 상태이므로 용이하게 분리될 수 있다.
1 (d), when the decorative layer 140 is formed on the polyurethane thin film sheet 110, the polyurethane thin film sheet 110 and the polyethylene thin film sheet 120, The sheet 120 is separated to remove the polyethylene thin film sheet 120 and the support layer 130 formed thereunder. At this time, the polyurethane thin film sheet 110 and the polyethylene thin film sheet 120 are separated from each other because they are in a state of being laminated by their own adhesive, that is, self-adhesive rather than an adhesive.

이후에는 도1(e)와 같이 상기 폴리에틸렌 박막시트(120)가 분리된 폴리우레탄 박막시트(110)의 저면에 프라이머층(150)을 형성하고, 상면에 실리콘 재질의 이형수지(160)와 아크릴 재질의 점착성수지(170)가 순차적으로 도포된 이형필름(180)을 도1(f)와 같이 상기 폴리우레탄 박막시트(110)과 합지한 다음 2일 내지 3일간 자연건조한다.
Thereafter, as shown in FIG. 1 (e), a primer layer 150 is formed on the bottom surface of the polyurethane thin film sheet 110 from which the polyethylene thin film sheet 120 is separated, and a release resin 160 of silicone, The release film 180 on which the adhesive resin 170 is sequentially applied is lapped with the polyurethane thin film sheet 110 as shown in Fig. 1 (f), followed by natural drying for 2 to 3 days.

여기서, 상기 이형필름(180)은 강도가 우수한 PET필름 또는 폴리에스터 필름을 사용하는 것이 바람직하며, 상기 아크릴 재질의 점착성 수지(170)는 폴리우레탄 박막시트(110)의 저면에 형성된 프라이머층(150)에 고정되며 실리콘 재질의 이형수지(160)는 이형필름(180)에 고정된 상태가 되어, 실제 사용시 이형필름(180)은 이형수지(160)에 의해 본 발명에 따른 시트에서 분리될 수 있으며, 노출된 점착성 수지(170)에 의해 피부착물에 탈착가능하게 점착된다.
The acrylic adhesive resin 170 may be a primer layer 150 formed on the bottom surface of the polyurethane thin film sheet 110, And the releasing film 180 of silicone is fixed to the releasing film 180 so that the releasing film 180 can be separated from the sheet according to the present invention by the releasing resin 160 in actual use , And is detachably adhered to the skin complex by the exposed adhesive resin (170).

여기서, 상기 실리콘 재질의 이형수지(160)는 100g/m2 내지 120g/m2 의 고밀도로 이형필름(150)에 도포되는 것이 2가지 측면에서 바람직하다.
Here, it is preferable that the release agent 160 of the silicone material is applied to the release film 150 at a high density of 100 g / m 2 to 120 g / m 2 in two aspects.

첫째, 플로터 커팅시 커팅이 용이하다. 즉, 본 발명에 따른 반짝이시트는 도3에 도시된 바와 같이 상부에서부터 이형필름 이전까지 플로터 커팅기를 통해 소정의 도형, 글자, 숫자등으로 절단(하프커팅, C)되어 판매된다. 따라서, 소비자는 절단된 부분에서 도형, 글자, 숫자등을 띄어 내어 피부착물에 부착하여 사용하는 데, 플로터 커팅시 기재층인 폴리우레탄 박막시트(110)가 연질이기 때문에 커팅되지 않고 밀려 접혀지는 경우가 발생할 수 있다. 그러나, 본 발명에서와 같이 실리콘 재질의 이형수지의 밀도를 100g/m2 내지 120g/m2 와 같이 고밀도로 하게 되면, 이형수지와 점착성 수지와의 결합력이 강해져 폴리우레탄 박막시트가 밀리는 경우를 방지할 수 있다.
First, cutting is easy when plotter cutting. That is, as shown in FIG. 3, the shiny sheet according to the present invention is cut (half-cut, C) by a predetermined shape, letter, number, etc. through the plotter cutter from the top to before the release film. Therefore, the customer places a figure, letter, number, or the like on the cut part and attaches it to the skin complex. In the case where the polyurethane thin film sheet 110 as a substrate layer is soft during the plotter cutting, May occur. However, as in the present invention, if the density of the release agent of silicone material is set to a high density such as 100 g / m 2 to 120 g / m 2 , the bonding force between the release resin and the adhesive resin becomes strong and the polyurethane thin sheet can do.

둘째, 승화염색이 가능하다. 승화인쇄는 대략 섭씨 200도 이상의 고온에서 20초간 수행되는 데 고온의 염색환경에서 이형수지의 밀도가 낮은 경우에는 이형수지와 점착성 수지가 분리되고 그 결과 연질의 폴리우레탄 시트가 쭈글쭈글해지는 문제점이 발생할 수 있다. 하지만, 본 발명에서와 같이 실리콘 재질의 이형수지의 밀도를 100g/m2 내지 120g/m2 와 같이 고밀도로 하게 되면 전술한 바와 같이, 이형수지와 점착성 수지간의 고온의 승화인쇄시에도 폴리우레탄 박막시트가 쭈글쭈글해지는 것을 방지할 수 있다.
Second, sublimation dyeing is possible. Sublimation printing is performed at a high temperature of about 200 degrees Celsius or more for about 20 seconds. When the density of the release resin is low in a high-temperature dyeing environment, the release resin and the adhesive resin are separated from each other. As a result, a problem arises in that the soft polyurethane sheet is wrinkled . However, even polyurethane films When a high density as mentioned above, sublimation printing of the high temperatures between the release resin and the adhesive resin when, as the density of the mold release resin, a silicon material and 100g / m 2 to 120g / m 2 as in the present invention It is possible to prevent the sheet from being squashed.

이후에는 도1(g)에 도시된 바와 같이, 장식층(140) 표면에 투명 폴리우레탄 박막필름(190)을 접착제를 통해 부착한다. 상기 투명 폴리우레탄 박막필름(190)는 장식층의 표면을 이물질로부터 보호하는 역할을 수행하는 데, 좀 더 구체적으로 장식층 표면의 반짝이층(142)는 반짝이가루에 의해 형성되기 때문에 표면이 불규칙하고 반짝이가루와 반짝이가루 사이에 공간이 형성된다. 따라서, 시트 표면을 헝겁으로 닦을 때 헝겁의 실이 돌출된 반짝이가루에 걸려 장식층 표면에 남게 되거나 미세먼지와 같은 이물질이 반짝이가루와 반짝이가루 사이에 공간에 침투하여 시트표면을 오염시키게 된다. 따라서, 본 발명에서는 폴리우레탄 박막필름(190)을 시트표면에 형성하여 장식층(140)표면을 보호하는 것이다. 여기서, 상기 투명 폴리우레탄 박막필름(190) 역시 박막필름으로 그 두께는 40㎛ 내지 50㎛인 것이 본 발명에 따른 연질시트의 특성에 적합하다.
Thereafter, as shown in Fig. 1 (g), a transparent polyurethane thin film 190 is attached to the surface of the decorative layer 140 through an adhesive. The transparent polyurethane thin film 190 serves to protect the surface of the decorative layer from foreign substances. More specifically, since the shiny layer 142 of the decorative layer surface is formed by the glitter powder, the surface is irregular A space is formed between the glitter powder and the glitter powder. Therefore, when the surface of the sheet is wiped, the thread of the fabric is caught by the protruding glitter powder and remains on the surface of the decorative layer, or foreign matter such as fine dust penetrates into the space between the glitter powder and the glitter powder to contaminate the sheet surface. Therefore, in the present invention, the polyurethane thin film 190 is formed on the surface of the sheet to protect the surface of the decorative layer 140. Here, the transparent polyurethane thin film 190 is also a thin film and has a thickness of 40 탆 to 50 탆, which is suitable for the characteristics of the soft sheet according to the present invention.

이와 같이 구성된 본 발명에 따른 연질 반짝이시트 제조방법은 연질이면서 신축성이 우수한 폴리우레탄 박막필름을 기재층으로 사용하기 때문에 우수한 신축성, 굴곡성 및 내구성을 갖는 연질 반짝이시트를 제조할 수 있으며, 이와 같은 연질 반짝이시트를 피부착물에 부착하면 피부착물이 굴곡하거나 신축될 때 이에 추종하여 그대로 굴국되거나 신축되기 때문에 피부착물과 일체감이 향상되는 잇점이 있다. 또한, 본 발명에 따라 제조된 연질 반짝이시트는 표면에 형성된 폴리우레탄 박막필름으로 인해 시트표면이 이물질로부터 보호되는 효과가 있다.
In the method of producing a soft sparked sheet according to the present invention having the above-described structure, since a polyurethane thin film having excellent softness and stretchability is used as a base layer, a soft sparkling sheet having excellent stretchability, flexibility and durability can be produced. When the sheet is attached to the skin complex, it is advantageous that the skin complex and the sense of unity are improved because the skin complex is bent or stretched when it is bent or stretched. Further, the soft sparked sheet produced according to the present invention has an effect that the sheet surface is protected from foreign matter by the polyurethane thin film formed on the surface.

110: 폴리우레탄 시트 120: 폴리에틸렌 시트
130: 지지층 140: 장식층
150: 프라이머층 160: 이형수지
170: 점착성수지 180: 이형필름
190: 표면보호필름110: polyurethane sheet 120: polyethylene sheet
130: support layer 140: decorative layer
150: primer layer 160: release resin
170: Adhesive resin 180: Release film
190: Surface protective film

Claims (4)

폴리우레탄 박막시트와 폴리에틸렌 박막시트를 합지하는 단계와;
상기 폴리에틸렌 박막시트 저면에 접착제를 도포한 다음 종이를 부착하는 지지층 형성단계와;
상기 폴리우레탄 박막시트 상면에 바인더를 도포한 다음 반짝이가루를 분사하여 반짝이층을 형성하고 나서 상기 반짝이층 위로 투명코팅층을 형성하는 장식층 형성단계와;
상기 합지된 폴리우레탄 박막시트와 폴리에틸렌 박막시트에서 폴리에틸렌 박막시트를 분리하는 단계와;
상기 폴리에틸렌 박막시트가 분리된 폴리우레탄 박막시트의 저면에 프라이머층을 형성하는 단계와;
상면에 실리콘 재질의 이형수지와 아크릴 재질의 점착성 수지가 순차적으로 도포된 이형필름을 상기 폴리우레탄 박막시트과 합지한 후 2일 내지 3일간 자연건조하는 단계와;
상기 장식층 상면에 접착제를 통해 투명 폴리우레탄 박막필름을 형성하는 표면보호층 형성단계로 이루어지는 것을 특징으로 하는 연질 반짝이시트 제조방법.
Laminating a polyurethane thin film sheet and a polyethylene thin film sheet;
A support layer forming step of applying an adhesive to the bottom surface of the polyethylene thin film sheet and then attaching the paper;
A decorative layer forming step of forming a transparent coating layer on the glitter layer by forming a glitter layer by spraying a glitter powder on a top surface of the polyurethane thin film sheet;
Separating the polyethylene foil sheet from the laminated polyurethane foil sheet and the polyethylene foil sheet;
Forming a primer layer on a bottom surface of the polyurethane thin film sheet from which the polyethylene thin film sheet is separated;
A release film on which an release agent of a silicone material and an acrylic resin are sequentially applied on an upper surface of the polyurethane thin film sheet, followed by natural drying for 2 to 3 days after laminating the release film with the polyurethane thin film sheet;
And a surface protective layer forming step of forming a transparent polyurethane thin film through an adhesive on the upper surface of the decorative layer.
제1항에 있어서,
상기 폴리우레탄 박막시트의 두께는 40㎛ 내지 60㎛인 것을 특징으로 하는 연질 반짝이시트 제조방법.
The method according to claim 1,
Wherein the thickness of the polyurethane thin film sheet is 40 占 퐉 to 60 占 퐉.
제1항 또는 제2항에 있어서,
상기 폴리우레탄 박막시트와 폴리에틸렌 박막시트는 한 쌍의 가압롤러 사이를 통과하면서 폴리우레탄 박막시트와 폴리에틸렌 박막시트의 자체 끈적거림에 의해 서로 합지되는 것을 특징으로 하는 연질 반짝이시트 제조방법.
3. The method according to claim 1 or 2,
Wherein the polyurethane thin film sheet and the polyethylene thin film sheet are bonded to each other by self-sticking of the polyurethane thin film sheet and the polyethylene thin film sheet while passing between the pair of pressure rollers.
제1항 또는 제2항에 있어서,
실리콘 재질의 이형수지는 100g/m2 내지 120g/m2 의 고밀도로 이형필름에 도포되는 것을 특징으로 하는 연질 반짝이시트 제조방법.3. The method according to claim 1 or 2,
Characterized in that the release paper of silicone material is applied to the release film at a high density of from 100 g / m 2 to 120 g / m 2 .
KR1020120023195A 2012-03-07 2012-03-07 Manufacturing method of soft glitter sheet KR101434611B1 (en)