KR101417983B1 - Interior tile made of aluminum can and manufacturing method thereof - Google Patents
Interior tile made of aluminum can and manufacturing method thereof Download PDFInfo
- Publication number
- KR101417983B1 KR101417983B1 KR1020130153050A KR20130153050A KR101417983B1 KR 101417983 B1 KR101417983 B1 KR 101417983B1 KR 1020130153050 A KR1020130153050 A KR 1020130153050A KR 20130153050 A KR20130153050 A KR 20130153050A KR 101417983 B1 KR101417983 B1 KR 101417983B1
- Authority
- KR
- South Korea
- Prior art keywords
- aluminum
- manufacturing
- interior
- compressor
- present
- Prior art date
Abstract
Description
본 발명은 알루미늄 캔을 소재로 한 인테리어 타일 및 그 제조 방법에 관한 것으로서, 보다 구체적으로는 재활용 알루미늄 캔을 압축하여 소정의 두께와 형상을 갖는 알루미늄 캔 소재 인테리어 타일과 그 제조 방법에 관한 것이다.The present invention relates to an interior tile made of an aluminum can and a method of manufacturing the same. More specifically, the present invention relates to an aluminum tile interior tile having a predetermined thickness and shape by compressing a recycled aluminum can, and a manufacturing method thereof.
최근, 알루미늄 캔은 음료 용기 등으로 널리 사용되고 있다. 이러한 알루미늄 캔은 내용물을 장기간 보관하는 것이 가능하고, 재질이 가벼워서 취급이 용이하므로 갈수록 그 사용량이 늘어나고 있다. 이에 따라 알루미늄 캔을 재활용하기 위한 다양한 시도들이 있어 왔다.
Background Art [0002] Recently, aluminum can is widely used as a beverage container and the like. Such an aluminum can can store the contents for a long period of time and is easy to handle due to its light weight, so that the amount thereof is gradually increasing. Accordingly, various attempts have been made to recycle aluminum cans.
한편, 실내 인테리어를 목적으로 다양한 심미적 특성을 가진 여러 종류의 타일들이 개발되어 있으나, 이러한 인테리어 타일들은 주로 유리, 세라믹, 또는 금속을 재료로 한 고가의 것이 대부분이며, 알루미늄 캔과 같이 재활용 가능한 저가의 소재를 사용한 예는 찾아볼 수 없는 실정이다.
On the other hand, various kinds of tiles having various aesthetic characteristics have been developed for the purpose of interior decoration. However, most of these interior tiles are mainly made of glass, ceramics, or metal. In addition, There are no examples of using materials.
본 발명에서 해결하고자 하는 과제는 재활용이 가능한 알루미늄 캔을 이용하여 알루미늄 캔을 소재로 한 인테리어 타일을 제조하는 방법과 이로부터 제조되는 알루미늄 캔 소재 인테리어 타일을 제공하고자 하는 것이다.An object of the present invention is to provide a method of manufacturing an interior tile made of an aluminum can using an aluminum can that can be recycled and an interior tile of an aluminum can manufactured from the method.
상기와 같은 과제를 해결하기 위하여, 본 발명은 압축기에 다수 개의 알루미늄 캔을 투입하고, 일정한 두께와 형상으로 압축하는 것을 특징으로 하는 알루미늄 캔 소재 인테리어 타일의 제조 방법을 제공한다.
In order to solve the above-described problems, the present invention provides a method of manufacturing an aluminum can material interior tile, wherein a plurality of aluminum cans are put into a compressor and compressed in a predetermined thickness and shape.
상기 제조 방법에는 다수 개의 알루미늄 캔을 압축기에 투입한 후 압축 전에 접착제를 투입하는 공정을 더 포함하는 것이 바람직하다.
It is preferable that the manufacturing method further includes a step of putting a plurality of aluminum cans into a compressor and then injecting the adhesive before compression.
상기 제조 방법에는 압축 후 얻어진 알루미늄 캔 성형체의 표면에 부드러운 요철을 형성시키는 공정을 더 포함하는 것이 바람직하다.
It is preferable that the manufacturing method further includes a step of forming smooth concavities and convexities on the surface of the aluminum can formed body obtained after compression.
상기 제조 방법에는 압축 후 얻어진 알루미늄 캔 성형체의 표면에 투명 실리콘 코팅층을 형성시키는 공정을 더 포함하는 것이 바람직하다.
It is preferable that the manufacturing method further includes a step of forming a transparent silicone coating layer on the surface of the aluminum can formed body obtained after compression.
또한, 본 발명은 상기 본 발명의 제조 방법에 따라 제조되는 것을 특징으로 하는 알루미늄 캔 소재 인테리어 타일을 제공한다.
The present invention also provides an aluminum can material interior tile, which is manufactured according to the manufacturing method of the present invention.
본 발명의 제조 방법에 따라 제조된 알루미늄 캔 소재 인테리어 타일은 저렴한 비용 및 간단한 공정으로도 다양한 형상을 가진 인테리어 타일을 제조할 수 있으므로 각종 요식업 매장 등의 실내에 심미적 인테리어 소재로서 적용이 가능할 것이다.
The aluminum can material interior tile manufactured according to the manufacturing method of the present invention can be used as an aesthetic interior material in various restaurants and the like because it can manufacture various kinds of interior tiles with low cost and simple process.
도 1은 본 발명의 제조 방법에 따라 제조된 사각형상의 알루미늄 캔 소재 인테리어 타일을 나타낸 것이다.
도 2는 본 발명의 제조 방법에 따라 제조된 원형의 알루미늄 캔 소재 인테리어 타일을 나타낸 것이다.
Fig. 1 shows a rectangular aluminum can material interior tile manufactured according to the manufacturing method of the present invention.
Fig. 2 shows a circular aluminum can material interior tile manufactured according to the manufacturing method of the present invention.
이하, 본 발명을 상세하게 설명한다.
Hereinafter, the present invention will be described in detail.
본 발명의 발명자들은 실내 인테리어용 타일로 사용하기에 적합한 소재를 개발하고자 연구를 거듭한 결과, 재활용되는 알루미늄 캔을 비교적 적은 비용으로도 미적 감각이 우수한 독창적인 인테리어 타일로 제조할 수 있음을 확인하고 본 발명을 완성하였다.
The inventors of the present invention have conducted studies to develop a material suitable for use as a tile for interior decorations, and as a result, it has been confirmed that an aluminum can to be recycled can be manufactured as an original interior tile having a good aesthetic sense at a relatively low cost Thus completing the present invention.
따라서, 본 발명은 압축기에 다수 개의 알루미늄 캔을 투입하고, 일정한 두께와 형상으로 압축하는 것을 특징으로 하는 알루미늄 캔 소재 인테리어 타일의 제조 방법을 제공한다.
Accordingly, the present invention provides a method of manufacturing an aluminum can material interior tile, which comprises charging a plurality of aluminum cans into a compressor, and compressing the aluminum cans to a predetermined thickness and shape.
상기 압축기는 알루미늄 캔과 금속 캔 등을 재활용하기 위하여 사용되고 있는 기존의 압축기를 사용할 수 있으며, 원하는 타일의 형상이 있다면 이를 위하여 개별적으로 설계 및 제작된 압축기를 사용할 수도 있다. 이러한 압축기의 설계 및 제작 과정은 본 발명의 기술분야에서 공지되어 있다.
The compressor may be a conventional compressor used for recycling aluminum cans and metal cans, or may be a separately designed and manufactured compressor if desired. The design and fabrication of such a compressor is well known in the art.
상기 알루미늄 캔은 재활용되는 식품 포장용 알루미늄 캔인 것이 바람직하다. 상기 알루미늄 캔은 수거 후 간단한 세척 과정을 거쳐 이용하는 것이 바람직하며, 상기 세척 과정 이외에 다른 추가적인 처리 공정은 필요하지 않다. 준비된 알루미늄 캔들은 표면에 다양한 문자, 도형 및 상표 등이 존재하며, 이들은 압축되어 독특한 형상을 나타내게 됨으로써 실내 인테리어 용도로 우수한 심미감을 나타내게 된다.
The aluminum can is preferably an aluminum can for food packaging to be recycled. The aluminum can is preferably used after a simple cleaning process after collection, and no additional treatment process other than the cleaning process is required. The prepared aluminum candle has a variety of characters, shapes and trademarks on its surface, and they are compressed and have a unique shape, thereby exhibiting an excellent aesthetic feeling for interior use.
압축기에 수 개의 알루미늄 캔을 투입하고, 일정한 압력으로 상기 알루미늄 캔을 압축하게 되는데, 이때 압축되는 알루미늄의 두께는 인테리어용 타일로서 벽면 또는 천정에 부착하기에 적합한 두께일 수 있다. 상기 두께는 1~20mm인 것이 바람직하고, 5~10mm인 것이 보다 바람직하다.
Several aluminum cans are put into the compressor and the aluminum cans are compressed at a constant pressure. At this time, the thickness of aluminum to be compressed may be a thickness suitable for adhering to a wall surface or a ceiling as an interior tile. The thickness is preferably 1 to 20 mm, and more preferably 5 to 10 mm.
압축되는 알루미늄 캔의 형상은 인테리어에 적합한 것으로 디자인될 수 있으며, 예를 들어 사각형, 원형, 타원형, 삼각형, 다각형 등 다양할 수 있다. 시판되는 압축기를 사용하는 경우에는 사각형, 원형, 타원형 등으로 제조되는 것이 통상적이겠지만, 특별한 형상을 원하는 경우 자체 제작된 압축기를 사용하여 원하는 형상의 압축 알루미늄 캔 형상을 얻을 수 있을 것이다. 한편, 일반적인 압축기를 사용하여 압축 알루미늄 캔을 제조한 후, 외부를 절단함으로써 원하는 형상을 얻을 수도 있다.
The shape of the aluminum can to be compressed may be designed to be suitable for the interior, and may be, for example, rectangular, circular, elliptical, triangular, polygonal, and the like. When a commercially available compressor is used, it is usual that the compressor is made of a square, a circle, an ellipse or the like. However, if a special shape is desired, a compressed aluminum can having a desired shape can be obtained by using a self- On the other hand, after a compressed aluminum can is manufactured by using a general compressor, a desired shape can be obtained by cutting the outside.
상기 제조 방법에는 다수 개의 알루미늄 캔을 압축기에 투입한 후 압축 전에 접착제를 투입하는 공정을 더 포함하는 것이 바람직하다.
It is preferable that the manufacturing method further includes a step of putting a plurality of aluminum cans into a compressor and then injecting the adhesive before compression.
압축기로 성형된 일정한 형상의 알루미늄 캔 성형체는 각 알루미늄 캔들이 압축기의 압력에만 의존하여 서로 결합되어 있어 원하지 않은 외력에 의하여 서로 분리되거나 떨어지는 문제점이 발생할 수 있다.
The aluminum can compact having a certain shape formed by the compressor may have a problem that the aluminum cans are connected to each other depending on only the pressure of the compressor so that they are separated or separated from each other by an undesired external force.
이러한 문제점을 해결하기 위하여, 본 발명은 다수 개의 알루미늄 캔을 압축기에 투입한 후 압축 전에 접착제를 투입하는 공정을 도입할 수 있다. 투입되는 접착제의 양은 압축하려는 알루미늄 캔의 양에 따라 적절히 조절될 수 있을 것이다. 상기 사용되는 접착제의 종류는 특별히 한정되지 않으며, 알루미늄과 같은 금속류의 접착에 적합한 에폭시계 접착제를 사용하는 것이 바람직하다.
In order to solve such a problem, the present invention can introduce a process of putting a plurality of aluminum cans into a compressor and then injecting an adhesive before compression. The amount of adhesive to be introduced may be appropriately adjusted according to the amount of the aluminum can to be compressed. The type of the adhesive used is not particularly limited, and it is preferable to use an epoxy adhesive suitable for bonding metals such as aluminum.
상기 제조 방법에는 압축 후 얻어진 알루미늄 캔 성형체의 표면에 부드러운 요철을 형성시키는 공정을 더 포함하는 것이 바람직하다.
It is preferable that the manufacturing method further includes a step of forming smooth concavities and convexities on the surface of the aluminum can formed body obtained after compression.
압축기를 사용하여 압축 성형된 알루미늄 캔의 표면은 평평한 것이 일반적이다. 본 발명은 재활용되는 알루미늄 캔을 소재로 하므로 각 알루미늄 캔의 표면에 존재하는 다양한 문자, 무늬 등이 무작위로 결합됨으로써 독특한 심미감을 나타내기는 하지만, 여기에 3차원적인 요철이 도입되면 보다 우수한 미감을 가질 수 있다.
The surface of the aluminum can which is compression molded using a compressor is generally flat. Since the present invention uses a recycled aluminum can as a raw material, various characters, patterns and the like present on the surface of each aluminum can is randomly combined to exhibit a unique aesthetics. However, when three-dimensional unevenness is introduced into the aluminum can, .
상기 요철은 압축 성형체의 일 표면을 부분적으로 압력을 가하거나 두드려서 다양한 형상의 요철을 표면에 형성시킬 수 있다. 표면을 두드리거나 압력을 가하는 경우 날카로운 부분이 생길 수 있으므로 가능한 부드러운 면이 되도록 요철을 형성시키는 것이 바람직하다.
The irregularities may be formed by pressing or pressing one surface of the compression-molded body partially to form irregularities of various shapes on the surface. It is preferable to form the irregularities so as to be as smooth as possible since sharp portions may be generated when the surface is hit or pressure is applied.
상기 제조 방법에는 압축 후 얻어진 알루미늄 캔 성형체의 표면에 투명 실리콘 코팅층을 형성시키는 공정을 더 포함하는 것이 바람직하다.
It is preferable that the manufacturing method further includes a step of forming a transparent silicone coating layer on the surface of the aluminum can formed body obtained after compression.
상기 설명된 바와 같이, 압축기에 의하여 압축된 성형체의 표면은 대체적으로 부드러운 표면을 가지므로 이를 그대로 실내 인테리어 타일용으로 적용하더라도 무리가 없다. 다만, 간혹 발생될 수 있는 날카로운 표면에 의한 안전상의 위험을 최소화하고, 인테리어 타일로서 적용할 때 시각적으로 보다 볼륨감을 나타내게 하기 위하여 성형체의 일면을 투명 실리콘 코팅하는 것이 효과적일 수 있다.
As described above, since the surface of the compacted body compressed by the compressor has a generally smooth surface, it can be applied as it is for indoor interior tiles. However, it may be effective to minimize the safety risk due to the occasional sharp surfaces and to apply a transparent silicone coating on one side of the molded body in order to visually show a sense of volume when applied as an interior tile.
상기 투명 실리콘 코팅은 공지된 실리콘 코팅제를 사용할 수 있으며, 코팅 두께는 2~5mm인 것이 바람직하다. 이러한 코팅층이 형성된 성형체는 인테리어 타일로 적용되어 보는 방향에 따라 상이한 입체감과 볼륨감을 느끼게 할 수 있다.
The transparent silicone coating may be a known silicone coating, and preferably has a thickness of 2 to 5 mm. The formed body having such a coating layer is applied as an interior tile, and it can feel a different sense of depth and volume depending on the viewing direction.
상기 설명된 바와 같은 제조 방법으로 재활용 가능한 알루미늄 캔을 소재로 하는 인테리어 타일을 제조할 수 있으며, 제조된 압축 성형체들은 단독으로 또는 여러 개를 조합하여 인테리어 타일로 실내 벽면 또는 천정에 장식될 수 있다.
As described above, an interior tile can be manufactured using recyclable aluminum can as a manufacturing method, and the manufactured compression molded bodies can be decorated on indoor walls or ceilings as interior tiles, alone or in combination.
따라서, 본 발명은 상기 본 발명의 제조 방법에 따라 제조되는 것을 특징으로 하는 알루미늄 캔 소재 인테리어 타일을 제공한다.
Accordingly, the present invention provides an aluminum can material interior tile, which is manufactured according to the manufacturing method of the present invention.
본 발명의 알루미늄 캔 소재 인테리어 타일은 적은 비용으로 손쉽게 구할 수 있는 재활용 알루미늄 캔을 특별한 처리 공정 없이 실내 인테리어 타일용으로 제조 가능하며, 제조되는 성형체마다 독특한 무늬를 가짐으로써 실내 벽면 또는 천정에 설치하는 경우 독특한 심미감을 나타내는 우수한 효과를 얻을 수 있다.
The aluminum can material interior tile of the present invention can be manufactured for indoor interior tiles without any special treatment process and can be easily obtained at a low cost and has a unique pattern for each of the formed articles to be installed on a wall or ceiling of a room An excellent effect showing a unique aesthetic feeling can be obtained.
이하에서는 실시예를 통하여 본 발명을 더욱 상세하게 설명한다.
Hereinafter, the present invention will be described in more detail by way of examples.
[[
실시예Example
]]
1. 알루미늄 캔의 압축 성형1. Compression molding of aluminum can
재활용 수거되는 음료용 알루미늄 캔을 세척 및 건조한 후 압축기에 투입하고, 에폭시 수지계 접착제를 투입한 후, 두께 5mm가 되도록 압축하여 사각형의 성형체를 제조하였다.
The aluminum beverage for beverage being collected for recycling was washed and dried, then put in a compressor, and an epoxy resin adhesive was put thereinto and compressed to a thickness of 5 mm to prepare a rectangular shaped body.
2. 실리콘 코팅 처리2. Silicon coating treatment
상기 항목 1.로부터 제조된 접착제 처리된 성형체의 일 표면에 두께 5mm로 투명 실리콘 코팅층을 형성시키고 건조시켜 알루미늄 캔 소재 인테리어 타일을 완성하였다.
A transparent silicone coating layer having a thickness of 5 mm was formed on one surface of the adhesive-treated molded article prepared in the above item 1 and dried to complete an aluminum can material interior tile.
3. 실내 벽면 적용3. Interior wall application
상기와 같은 방법으로 제조된 알루미늄 캔 소재 인테리어 타일을 원하는 위치와 간격으로 실내 벽면에 접착제로 단단히 고정시켜 설치하였다.
The aluminum tile interior tile manufactured by the above method was fixed to the wall surface of the room at a desired position and at a desired position with an adhesive.
Claims (5)
(b) 상기 세척 및 건조가 완료된 음료용 알루미늄 캔에 에폭시 수지계 접착제를 투입하는 단계;
(c) 상기 에폭시 수지계 접착제가 투입된 음료용 알루미늄 캔을 압축기에 투입시켜 성형체를 제조하는 단계;
(d) 상기 성형체의 표면에 부드러운 요철을 형성하는 단계; 및
(e) 상기 성형체의 일표면에 투명 실리콘 코팅층을 2~5mm 두께로 도포한 후 건조하는 단계; 를 포함하는 알루미늄 캔 소재 인테리어 타일의 제조방법으로 제조되되,
상기 (c) 단계에서 상기 압축기를 통해 압축되는 알루미늄 두께는 인테리어용 타일로서 벽면 또는 천정에 부착하기에 적합하도록 5~10mm로 제조되는 알루미늄 캔 소재 인테리어 타일.(a) washing and drying an aluminum can for beverage which is collected for recycling and in which various characters, figures and trademarks are present;
(b) injecting an epoxy resin adhesive into the aluminum can for beverage which has been cleaned and dried;
(c) preparing a molded body by injecting the aluminum can for beverage, into which the epoxy resin adhesive is introduced, into a compressor;
(d) forming a soft concavo-convex on the surface of the molded body; And
(e) coating a transparent silicone coating layer on one surface of the molded body to a thickness of 2 to 5 mm and drying the coated body; The method of manufacturing an aluminum tin material according to claim 1,
In the step (c), the thickness of aluminum compressed through the compressor is an interior tile, which is manufactured to have a thickness of 5 to 10 mm suitable to be attached to a wall surface or a ceiling.